JP5290715B2

JP5290715B2 - ball

Info

Publication number: JP5290715B2
Application number: JP2008304438A
Authority: JP
Inventors: 邦彦山田; 敦司山口; 啓一武田
Original assignee: Molten Corp
Current assignee: Molten Corp
Priority date: 2008-11-28
Filing date: 2008-11-28
Publication date: 2013-09-18
Anticipated expiration: 2028-11-28
Also published as: JP2010125152A

Abstract

<P>PROBLEM TO BE SOLVED: To improve the commercial value of a ball by making the rebound characteristic of the ball in a low-temperature atmosphere approximate to that in an ordinary temperature atmosphere so that a user hardly feels incompatibility and by relieving user's pain when he uses the ball in the low-temperature atmosphere. <P>SOLUTION: A facing panel includes a plurality of members 40-44 stacked one on the other. These members 40-44 are adhesively bonded to each other by a binder A containing an adhesive except natural rubber latex. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、表皮パネルを備えたボールに関し、特に、表皮パネルを、複数の部材を積層して得る構造の技術分野に属する。 The present invention relates to a ball having a skin panel, and particularly belongs to a technical field of a structure obtained by laminating a plurality of members.

従来より、球形中空状のチューブで構成された内部部材を表皮パネルで被覆してなるボールが知られている。表皮パネルは、その表面層を構成する皮革部材と、裏面の補強層を構成する複数の布部材とを積層してなる。本技術分野においては、一般に、複数の布部材同士の接着及び布部材と皮革部材との接着の際には、天然ゴムラテックス接着剤が用いられている（例えば、特許文献１〜４参照）。
特開２０００−２４５８７５号公報特開２００１−１７０２１６号公報特開２００３−３３４４８号公報特開２００３−４９３７０号公報 2. Description of the Related Art Conventionally, there has been known a ball formed by covering an inner member composed of a spherical hollow tube with a skin panel. The skin panel is formed by laminating a leather member constituting the surface layer and a plurality of cloth members constituting the reinforcing layer on the back surface. In the present technical field, a natural rubber latex adhesive is generally used for bonding a plurality of cloth members and bonding a cloth member and a leather member (see, for example, Patent Documents 1 to 4).
JP 2000-245875 A JP 2001-170216 A JP 2003-33448 A JP 2003-49370 A

ところで、ボールは、四季を通じて使用されるとともに、屋内及び屋外で使用され、また、気候が異なる世界の各地でも使用されるので、その使用環境は、常温雰囲気から例えば１０℃以下の低温雰囲気まで様々である。 By the way, the ball is used throughout the seasons, indoors and outdoors, and also used in various parts of the world where the climate is different, so the usage environment varies from a normal temperature atmosphere to a low temperature atmosphere of 10 ° C. or lower, for example. It is.

しかしながら、今までのように、表皮パネルを構成する部材を天然ゴムラテックス接着剤を用いて接着するようにすると、天然ゴムは温度が低下すると弾性率が低下して硬くなるものなので、低温雰囲気下で表皮パネルが硬くなってしまい、ひいては、ボールの弾性率が低下する。こうなると、ボールを低温雰囲気下で使用した場合と、常温雰囲気下で使用した場合とで、リバウンド特性が大きく異なって使用者が違和感を感じる。また、ボールを低温雰囲気下で使用した場合には、表皮パネルが硬くなっていることにより、使用者が蹴ったときや使用者の体に当たったときに強い痛みを感じることがある。 However, as before, when the members constituting the skin panel are bonded using natural rubber latex adhesive, natural rubber has a lower elastic modulus and becomes harder when the temperature is lowered. As a result, the skin panel becomes hard, and as a result, the elastic modulus of the ball decreases. In this case, the rebound characteristics are greatly different between the case where the ball is used in a low temperature atmosphere and the case where the ball is used in a normal temperature atmosphere, and the user feels uncomfortable. Further, when the ball is used in a low temperature atmosphere, the skin panel is hard, so that a strong pain may be felt when the user kicks or hits the user's body.

本発明は斯かる点に鑑みてなされたものであり、その目的とするところは、低温雰囲気下でのボールのリバウンド特性を常温雰囲気下でのリバウンド特性に近づけて使用者が違和感を感じるのを抑制するとともに、低温雰囲気下での使用時に使用者が感じる痛みを緩和することで、ボールの商品性を高めることにある。 The present invention has been made in view of such points, and the object of the present invention is to make the user feel uncomfortable by bringing the rebound characteristics of the ball under a low temperature atmosphere closer to the rebound characteristics under a normal temperature atmosphere. In addition to reducing the pain felt by the user when used in a low-temperature atmosphere, the product of the ball is improved.

上記目的を達成するために、第１の発明では、内部部材と、該内部部材を被覆するように形成された表皮パネルとを備えたボールであって、上記表皮パネルは、互いに積層された第１の部材と第２の部材とを備え、上記第１の部材と上記第２の部材とは、でんぷん系接着剤を含有した結合剤により接着されており、上記結合剤には、上記表皮パネルの重量を調整するための添加剤として、硫酸バリウム、酸化ケイ素及びクレーの少なくとも一つが混入されている構成とする。 In order to achieve the above object, according to a first aspect of the present invention, there is provided a ball comprising an internal member and a skin panel formed so as to cover the internal member, wherein the skin panel is laminated on each other. 1 member and a second member, wherein the first member and the second member are bonded by a binder containing a starch adhesive, and the skin panel is attached to the binder. As an additive for adjusting the weight, at least one of barium sulfate, silicon oxide and clay is mixed.

この構成によれば、表皮パネルを構成する第１の部材と第２の部材とが天然ゴムラテックスを除く接着剤を含む接合剤で接着されるので、低温雰囲気下で表皮パネルが硬くなりにくく、ボールの弾性率の低下が抑制される。 According to this configuration, since the first member and the second member constituting the skin panel are bonded with a bonding agent including an adhesive excluding natural rubber latex, the skin panel is not easily hardened in a low temperature atmosphere. A decrease in the elastic modulus of the ball is suppressed.

また、例えば、球技に使用されるボールは規定重量とする必要があるが、この構成によれば、結合剤を利用してボールの重量を容易に調整することが可能になる。 In addition, for example, a ball used for ball games needs to have a specified weight, but according to this configuration, the weight of the ball can be easily adjusted using a binder.

第２の発明では、第１の発明において、結合剤には、接着力を調整する添加物が混入されている構成とする。 In 2nd invention, it is set as the structure in which the additive which adjusts adhesive force is mixed in the binder in 1st invention.

この構成によれば、例えば添加物により第１の部材と第２の部材との接着力を低下させることにより、表皮パネルが柔らかくなる。つまり、添加剤によってボールの硬さを容易に変更することが可能になる。 According to this configuration, for example, the skin panel is softened by reducing the adhesive force between the first member and the second member with an additive. In other words, the hardness of the ball can be easily changed by the additive.

第３の発明では、第１または２の発明において、添加物は、粉末状をなしている構成とする。 In 3rd invention, it is set as the structure which has comprised the powder form in 1st or 2nd invention.

この構成によれば、添加物を結合剤に均一に混入させることが可能になる。 According to this configuration, the additive can be uniformly mixed in the binder.

第４の発明では、第１から３のいずれか１つの発明において、結合剤には、柔軟剤が混入されている構成とする。 In 4th invention, it is set as the structure by which the softener is mixed in the binder in any one invention of 1st-3.

したがって、表皮パネルの柔軟性が高まることにより、使用者が感じる痛みをより一層低減することが可能になる。 Therefore, it becomes possible to further reduce the pain felt by the user by increasing the flexibility of the skin panel .

本発明によれば、表皮パネルを構成する第１の部材と第２の部材とを、天然ゴムラテックスを除く接着剤を含有した結合剤により接着するようにしたので、低温雰囲気下において表皮パネルが硬くなりにくく、低温雰囲気下のリバウンド特性を常温雰囲気下のリバウンド特性に近づけることができるとともに、使用者が使用時に感じる痛みを軽減でき、よって、ボールの商品性を高めることができる。 According to the present invention, the first member and the second member constituting the skin panel are bonded by the binder containing the adhesive excluding the natural rubber latex. It is hard to become hard, and the rebound characteristic under a low temperature atmosphere can be made close to the rebound characteristic under a normal temperature atmosphere, and the pain that the user feels at the time of use can be reduced, so that the merchantability of the ball can be improved.

以下、本発明の実施形態を図面に基づいて詳細に説明する。尚、以下の好ましい実施形態の説明は、本質的に例示に過ぎず、本発明、その適用物或いはその用途を制限することを意図するものではない。 Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings. It should be noted that the following description of the preferred embodiment is merely illustrative in nature, and is not intended to limit the present invention, its application, or its use.

図１は、本発明の実施形態に係るボール１を示すものである。このボール１は、サッカーボールであり、内部部材としてのチューブ２（図２に示す）と、チューブ２の外面を覆う六角形の表皮パネル３及び五角形の表皮パネル４とを備えている。 FIG. 1 shows a ball 1 according to an embodiment of the present invention. The ball 1 is a soccer ball, and includes a tube 2 (shown in FIG. 2) as an internal member, and a hexagonal skin panel 3 and a pentagonal skin panel 4 that cover the outer surface of the tube 2.

上記チューブ２は、ブチルゴム又はラテックスゴム等の空気低透過性を有する弾性材料で構成されており、周知の構造のゴム等の弾性材からなるバルブ５を有している。このバルブ５は、表皮パネル３を貫通してボール１の外面に露出している。バルブ５を介してチューブ２内に圧縮空気が注入されるようになっている。尚、バルブ５の構造は上記に限定されるものではない。 The tube 2 is made of an elastic material having low air permeability such as butyl rubber or latex rubber, and has a valve 5 made of an elastic material such as rubber having a known structure. The valve 5 penetrates the skin panel 3 and is exposed on the outer surface of the ball 1. Compressed air is injected into the tube 2 through the valve 5. The structure of the valve 5 is not limited to the above.

図２に示すように、各表皮パネル３，４の周縁部は、チューブ２側へ向けて折り曲げられており、この折り曲げられた部分同士が糸６により縫い合わされている。表皮パネル３，４を縫い合わせる際には、手縫いであってもよいし、ミシン縫い（機械縫い）であってもよい。 As shown in FIG. 2, the peripheral portions of the skin panels 3 and 4 are bent toward the tube 2, and the bent portions are sewn together by a thread 6. When the skin panels 3 and 4 are sewn together, they may be hand-sewn or machine-sewn (machine-sewn).

六角形の表皮パネル３と五角形の表皮パネル４とは同じ構造であるため、以下、図３に示す五角形の表皮パネル４の構造について説明する。表皮パネル４は、図２に示すように、表面層を構成する皮革部材４０と、裏面層を構成する補強用の第１〜第４布部材４１〜４４とを備えている。皮革部材４０は、天然皮革または人工皮革からなるものである。皮革部材４０の厚さは、例えば、約２ｍｍであるが、この厚さは皮革部材４０の物性、第１〜第４布部材４１〜４４の物性、ボール１の用途等によって任意に設定することができる。また、皮革部材４０の表面を樹脂フィルム等でコーティングしてもよいし、皮革部材４０の表面に模様等を印刷するようにしてもよい。 Since the hexagonal skin panel 3 and the pentagonal skin panel 4 have the same structure, the structure of the pentagonal skin panel 4 shown in FIG. 3 will be described below. As shown in FIG. 2, the skin panel 4 includes a leather member 40 constituting a surface layer and reinforcing first to fourth cloth members 41 to 44 constituting a back surface layer. The leather member 40 is made of natural leather or artificial leather. The thickness of the leather member 40 is, for example, about 2 mm. This thickness is arbitrarily set depending on the physical properties of the leather member 40, the physical properties of the first to fourth cloth members 41 to 44, the use of the ball 1, and the like. Can do. Further, the surface of the leather member 40 may be coated with a resin film or the like, or a pattern or the like may be printed on the surface of the leather member 40.

第１布部材（第１の部材）４１は、皮革部材４０の裏面に接着され、第２布部材（第２の部材）４２は、第１布部材４１の裏面に接着され、第３布部材４３は、第２布部材４２の裏面に接着され、第４布部材４４は、第３布部材４３の裏面に接着されている。第１〜第４布部材４１〜４４を積層した状態でのトータルの厚さは、約２ｍｍであるが、皮革部材４０と同様に任意に設定することができる。 The first cloth member (first member) 41 is bonded to the back surface of the leather member 40, the second cloth member (second member) 42 is bonded to the back surface of the first cloth member 41, and the third cloth member is bonded. 43 is bonded to the back surface of the second cloth member 42, and the fourth cloth member 44 is bonded to the back surface of the third cloth member 43. The total thickness in the state where the first to fourth cloth members 41 to 44 are laminated is about 2 mm, but can be arbitrarily set similarly to the leather member 40.

第１〜第４布部材４１〜４４は、織布からなるものである。織布としては、綿布や、綿とポリエステルの混紡布が好ましいが、織布の材質はこれらに限られるものではない。また、織布を用いずに不織布を用いてもよく、この場合、第１布部材４１及び第４布部材４４の一方、または両方を不織布とし、他の布部材４２，４３は織布にするのが好ましい。また、第１〜第４布部材４１〜４４の材質や厚みは、互いに異ならせてもよい。 The first to fourth cloth members 41 to 44 are made of woven cloth. As the woven fabric, a cotton fabric or a blended fabric of cotton and polyester is preferable, but the material of the woven fabric is not limited to these. Further, a non-woven fabric may be used without using a woven fabric. In this case, one or both of the first fabric member 41 and the fourth fabric member 44 are non-woven fabric, and the other fabric members 42 and 43 are woven fabric. Is preferred. The materials and thicknesses of the first to fourth cloth members 41 to 44 may be different from each other.

皮革部材４０、第１〜第４布部材４１〜４４は、天然ゴムラテックスを除く接着剤を含有した結合剤Ａ（図４にのみ示す）により接着されている。この実施形態では、接着剤がでんぷん系接着剤である場合について説明する。でんぷん系接着剤の原料としては、例えば、コーンスターチ等が挙げられるが、原料は他のものであってもよい。でんぷん系接着剤にすることで、結合剤Ａを安価にすることができるとともに、安全性を確保できる。 The leather member 40 and the first to fourth cloth members 41 to 44 are bonded by a binder A (shown only in FIG. 4) containing an adhesive excluding natural rubber latex. In this embodiment, a case where the adhesive is a starch-based adhesive will be described. Examples of the raw material for the starch-based adhesive include corn starch, but other raw materials may be used. By using a starch-based adhesive, the binder A can be made inexpensive and safety can be ensured.

結合剤Ａには、でんぷん系接着剤の他に、表皮パネル４の重量を調整する添加物と、柔軟剤とが混入されている。この実施形態では、添加物は、硫酸バリウムを粉末にしたものであり、柔軟剤は、グリセリンである。さらに、結合剤Ａには、他にも防カビ剤が混入されている。結合剤Ａは、各部材４０，４１〜４４に塗布する前は液状である。 In addition to the starch-based adhesive, the binder A is mixed with an additive for adjusting the weight of the skin panel 4 and a softening agent. In this embodiment, the additive is powdered barium sulfate, and the softening agent is glycerin. Further, the anti-mold agent is mixed in the binder A. The binder A is in a liquid state before being applied to the members 40 and 41 to 44.

硫酸バリウムの比重は、乾燥したでんぷん系接着剤の比重よりも大きいので、硫酸バリウムの混入量を増減させることで、乾燥後の結合剤Ａの比重を変更することが可能である。結合剤Ａの比重は、ボール１が規定重量となるように設定されている。 Since the specific gravity of barium sulfate is larger than the specific gravity of the dried starch-based adhesive, it is possible to change the specific gravity of the binder A after drying by increasing or decreasing the amount of barium sulfate mixed therein. The specific gravity of the binder A is set so that the ball 1 has a specified weight.

硫酸バリウムの混入割合は、結合剤Ａが液状態にあるときに、結合剤Ａに占める硫酸バリウムの重量割合が８０重量部以下となるようにするのが好ましい。硫酸バリウムの混入割合を８０重量部以下としたのは、８０重量部よりも多いと、硫酸バリウムには接着力が無いため、結合剤Ａの接着力が十分に確保されなくなるからである。このように、硫酸バリウムの混入割合によって結合剤Ａの接着力を調整することも可能であり、硫酸バリウムは、本発明の接着力を調整する添加物に相当する。 The mixing ratio of barium sulfate is preferably set so that the weight ratio of barium sulfate in the binder A is 80 parts by weight or less when the binder A is in a liquid state. The reason why the mixing ratio of barium sulfate is set to 80 parts by weight or less is that when it is more than 80 parts by weight, barium sulfate has no adhesive force, so that the adhesive force of the binder A cannot be sufficiently secured. Thus, it is also possible to adjust the adhesive force of the binder A by the mixing ratio of barium sulfate, and barium sulfate corresponds to the additive for adjusting the adhesive force of the present invention.

また、グリセリンは、粘性液体であり、このグリセリンの混入割合を多くすると表皮パネル４の柔軟性が高まる。グリセリンの混入割合を多くしすぎるとでんぷん系接着剤の接着成分が薄まることになって接着力が低下するので、グリセリンの混入割合は、結合剤Ａに占めるグリセリンの重量割合が１５重量部以下となるようにするのが好ましい。また、他の混入物としての防カビ剤等の混入割合は、結合剤Ａに占める防カビ剤等の重量割合が２重量部以下となるようにするのが好ましい。尚、他の混入物には、防カビ剤以外の薬剤を含めてもよい。また、防カビ剤は添加しなくてもよい。 Glycerin is a viscous liquid, and the flexibility of the skin panel 4 increases when the mixing ratio of the glycerin is increased. If the mixing ratio of glycerin is increased too much, the adhesive component of the starch-based adhesive will be thinned and the adhesive strength will be reduced. Therefore, the mixing ratio of glycerin is 15 parts by weight or less by weight of glycerin in the binder A. It is preferable to do so. Moreover, it is preferable that the mixing ratio of the antifungal agent or the like as the other contaminant is such that the weight ratio of the antifungal agent or the like in the binder A is 2 parts by weight or less. In addition, you may include chemical | medical agents other than a fungicide in other contaminants. Moreover, it is not necessary to add a fungicide.

次に、上記ボール１の製造要領について説明する。まず、図４（ａ）に示すように、皮革部材４０の裏面に上記結合剤Ａを塗布する。結合剤Ａの塗布量は、皮革部材４０の種類や第１布部材４１の種類及び厚み等で調整することになるが、例えば、でんぷん系接着剤の固定分量で３グラム／１平方メートル以上となるように塗布するのが好ましい。でんぷん系接着剤の固定分量が１平方メートルあたり３グラムよりも少ないと、接着力が低下してしまい、後述する縫製作業の際に第１布部材４１が皮革部材４０から剥がれてしまうことがあるためである。 Next, the manufacturing procedure of the ball 1 will be described. First, as shown in FIG. 4A, the binder A is applied to the back surface of the leather member 40. The coating amount of the binder A is adjusted by the type of the leather member 40, the type and thickness of the first cloth member 41, and the fixed amount of the starch-based adhesive is, for example, 3 grams / 1 square meter or more. It is preferable to apply as described above. If the fixed amount of the starch-based adhesive is less than 3 grams per square meter, the adhesive strength is reduced, and the first cloth member 41 may be peeled off from the leather member 40 during the sewing operation described later. It is.

皮革部材４０に結合剤Ａを塗布した後に、第１布部材４１を皮革部材４０の裏面に重ねる。その後、第１布部材４１の裏面に、皮革部材４０に塗布したのと同様に結合剤Ａを塗布する。そして、第２布部材４２を第１布部材４１の裏面に重ねる。同様にして、図４（ｂ）に示すように、第３布部材４３を第２布部材４２に接着し、第４布部材４４を第３布部材４３に接着する。その後、図４（ｃ）に示すように、第４布部材４４の裏面に結合剤Ａを塗布しておく。 After the binder A is applied to the leather member 40, the first cloth member 41 is overlaid on the back surface of the leather member 40. Thereafter, the binder A is applied to the back surface of the first cloth member 41 in the same manner as applied to the leather member 40. Then, the second cloth member 42 is overlaid on the back surface of the first cloth member 41. Similarly, as shown in FIG. 4B, the third cloth member 43 is bonded to the second cloth member 42, and the fourth cloth member 44 is bonded to the third cloth member 43. Thereafter, as shown in FIG. 4C, the binder A is applied to the back surface of the fourth cloth member 44.

結合剤Ａが乾燥すると、皮革部材４０と、第１〜第４布部材４１〜４４とが積層されて一体化して表皮パネル３，４の材料が得られる。この材料を裁断して表皮パネル３，４が得られる。 When the binder A is dried, the leather member 40 and the first to fourth cloth members 41 to 44 are laminated and integrated to obtain the materials of the skin panels 3 and 4. The skin panels 3 and 4 are obtained by cutting this material.

このようにして得られた表皮パネル３，４の周縁部同士を糸６で縫うことによって球をなすように連結していく。このとき、第１〜第４布部材４１〜４４は、皮革部材４０に十分な接着力で接着されているので、第１〜第４布部材４１〜４４が皮革部材４０から剥がれることはない。また、第１〜第４布部材４１〜４４の各々も剥がれることはない。そして、チューブ２を収容するように表皮パネル３，４を縫い合わせることでボール１が得られる。 The peripheral portions of the skin panels 3 and 4 obtained in this way are connected to form a sphere by sewing with the thread 6. At this time, since the first to fourth cloth members 41 to 44 are bonded to the leather member 40 with sufficient adhesive force, the first to fourth cloth members 41 to 44 are not peeled off from the leather member 40. Also, each of the first to fourth cloth members 41 to 44 is not peeled off. And the ball | bowl 1 is obtained by sewing up the skin panels 3 and 4 so that the tube 2 may be accommodated.

このボール１は、表皮パネル３，４の皮革部材４０及び第１〜第４布部材４１〜４４をでんぷん系接着剤で接着している。でんぷん系接着剤は、天然ゴムラテックスに比べて、低温雰囲気下において硬くなりにくい。よって、本実施形態のボール１と従来例との弾性率及びバウンド高さを比較すると、表１に示すように、本実施形態のボール１の方が有利な結果となった。 In this ball 1, the leather member 40 and the first to fourth cloth members 41 to 44 of the skin panels 3 and 4 are bonded with a starch-based adhesive. Starch-based adhesives are harder to harden in a low temperature atmosphere than natural rubber latex. Therefore, when comparing the elastic modulus and the bounce height between the ball 1 of this embodiment and the conventional example, as shown in Table 1, the ball 1 of this embodiment has a more advantageous result.

尚、表１において、常温とは、ボール１の表面温度が２５℃となる雰囲気温度であり、低温とは、ボール１の表面温度が５℃となる雰囲気温度である。また、弾性率は、ボール１表面の値である。さらに、バウンド高さとは、ボール１を、水平な硬い板から鉛直上方に２００ｃｍ離れた所から自由落下させた際に板から跳ねた高さを測定した値である。 In Table 1, the normal temperature is an ambient temperature at which the surface temperature of the ball 1 is 25 ° C., and the low temperature is an ambient temperature at which the surface temperature of the ball 1 is 5 ° C. The elastic modulus is a value on the surface of the ball 1. Further, the bounce height is a value obtained by measuring the height at which the ball 1 is bounced off the plate when it is freely dropped from a horizontal hard plate vertically 200 cm away from the place.

試験結果について、詳しくは、従来例の弾性率は、常温で６８．０％で、低温で５８．０％であり、その差は１０．０％もある。これに対し、本実施形態のボール１は、常温で６７．０％であり、従来例と殆ど変わらないが、低温では従来例に比べて高く、６０．５％もあり、その差は６．５％に過ぎない。また、リバウンド高さについては、従来例では、常温で１３６．０ｃｍで、低温で１１６．０ｃｍであり、その差は２０．０ｃｍもある。これに対し、本実施形態のボール１は、常温では従来例と殆ど変わらない１３４．０ｃｍであり、低温では１２１．０ｃｍも跳ね返っており、その差は１３．０ｃｍに過ぎないものとなっている。 Specifically, the elastic modulus of the conventional example is 68.0% at room temperature, 58.0% at low temperature, and the difference is 10.0%. On the other hand, the ball 1 of this embodiment is 67.0% at room temperature, which is almost the same as the conventional example, but is higher than the conventional example at a low temperature, which is 60.5%, and the difference is 6. Only 5%. As for the rebound height, in the conventional example, it is 136.0 cm at normal temperature and 116.0 cm at low temperature, and the difference is 20.0 cm. On the other hand, the ball 1 of the present embodiment is 134.0 cm which is almost the same as the conventional example at room temperature, rebounds by 121.0 cm at low temperature, and the difference is only 13.0 cm. .

この試験結果からも明らかなように、本実施形態のボール１では、低温雰囲気下でのリバウンド特性が常温雰囲気下でのリバウンド特性に近づき、その結果、常温雰囲気下でのバウンド高さと低温雰囲気下でのバウンド高さとの差が小さくなっていることが分かる。また、本実施形態のボール１は従来例に比べて低温雰囲気で弾性率が高いので、使用者が蹴った際や体に当たった際にボール１が弾性変形し易く、よって、使用者が感じる痛みが緩和される。 As is apparent from this test result, in the ball 1 of this embodiment, the rebound characteristics in a low temperature atmosphere approach the rebound characteristics in a normal temperature atmosphere, and as a result, the bounce height in a normal temperature atmosphere and the low temperature atmosphere It can be seen that the difference between the bounce height and the height is small. Further, since the ball 1 of this embodiment has a higher elastic modulus in a low temperature atmosphere than the conventional example, the ball 1 is easily elastically deformed when the user kicks or hits the body, and thus the user feels. Pain is relieved.

以上説明したように、この実施形態によれば、表皮パネル２を構成する部材４０、４１〜４４を、でんぷん系接着剤を含有する結合剤Ａで接着するようにしたので、低温雰囲気下のリバウンド特性を常温雰囲気下のリバウンド特性に近づけることができるとともに、低温雰囲気下において使用者が感じる痛みを軽減でき、よって、ボール１の商品性を高めることができる。 As explained above, according to this embodiment, since the members 40 and 41 to 44 constituting the skin panel 2 are bonded with the binder A containing the starch-based adhesive, the rebound in a low-temperature atmosphere. The characteristics can be made close to the rebound characteristics in a normal temperature atmosphere, the pain felt by the user in a low temperature atmosphere can be reduced, and the merchantability of the ball 1 can be improved.

また、結合剤Ａへの添加物である硫酸バリウムの混入割合によって、ボール１の重量を容易に調整して規定重量とすることができる。 Further, the weight of the ball 1 can be easily adjusted to a specified weight by the mixing ratio of barium sulfate as an additive to the binder A.

また、硫酸バリウムの混入割合によって結合剤Ａの接着力を低下させることにより、表皮パネル３，４をより一層柔らかくすることが可能になる。 Moreover, it becomes possible to make skin panel 3 and 4 still softer by reducing the adhesive force of the binder A by the mixing rate of barium sulfate.

また、硫酸バリウムを粉末にしているので、結合剤Ａの中に均一に分散させることができる。 Further, since the barium sulfate powder can be uniformly dispersed in the binder A.

また、本発明の添加物としては、シリカ（酸化ケイ素）、クレーが好ましい。上記添加物は、いずれも粉末に加工したものが好ましい。添加物の比重が接着剤の比重よりも大きいものを選べば、その添加物を結合剤Ａに混入することで、ボール１を重くすることが可能になり、また、小さいものを選べば、ボール１を軽くすることが可能になる。上記添加物は１種類のみ混入するようにしてもよいし、複数種を混入するようにしてもよい。 Further, as the additive of the present invention, silica (silicon oxide) and clay are preferable. The above additives are preferably processed into powder. If the specific gravity of the additive is larger than the specific gravity of the adhesive, the ball 1 can be made heavy by mixing the additive into the binder A, and if the small one is selected, the ball 1 can be lightened. Only one type of the additive may be mixed, or a plurality of types of additives may be mixed.

また、本発明の柔軟剤としては、例えば、アルコール類としてジエチレングリコール等が挙げられ、パラフィン類として流動パラフィンが挙げられるが、これに限られるものではなく、表皮パネル３，４を柔軟にするものであればよい。 In addition, examples of the softener of the present invention include diethylene glycol and the like as alcohols, and liquid paraffin as paraffins. However, the softener is not limited to this, and softens the skin panels 3 and 4. I just need it.

また、結合剤Ａを生成する際には、上記のような添加物を一切添加せずに生成してもよいし、柔軟剤を一切添加せずに生成してもよい。すなわち、でんぷん系接着剤のみで結合剤Ａを構成してもよいし、該接着剤と上記添加物とで結合剤Ａを構成してもよいし、該接着剤と柔軟材とで結合剤Ａを構成してもよい。 Moreover, when producing | generating binder A, you may produce | generate without adding the above additives at all, and you may produce | generate without adding a softening agent at all. That is, the binder A may be composed only of the starch-based adhesive, the binder A may be composed of the adhesive and the additive, or the binder A may be composed of the adhesive and the flexible material. May be configured.

また、上記実施形態では、皮革部材４０、第１〜第４布部材４１〜４４の全てを、でんぷん系接着剤を含有した結合剤Ａにより接着するようにしているが、これに限らず、例えば、第２布部材４２と第３布部材４３とを結合剤Ａにより接着し、他の部材４０，４１，４４は従来の天然ゴムラテックス接着剤で接着するようにしてもよい。この場合も、従来例のものに比べて、天然ゴムラテックス接着剤の使用料が減る分、同様な作用効果が得られる。結合剤Ａにより接着する部材は任意に設定することができる。 Moreover, in the said embodiment, although it is made to adhere | attach all the leather members 40 and the 1st-4th cloth members 41-44 with the binder A containing the starch-type adhesive agent, it is not restricted to this, For example, The second cloth member 42 and the third cloth member 43 may be bonded with the binder A, and the other members 40, 41, and 44 may be bonded with a conventional natural rubber latex adhesive. In this case as well, the same effect can be obtained as the amount of use of the natural rubber latex adhesive is reduced as compared with the conventional example. The member bonded by the binder A can be arbitrarily set.

また、皮革部材４０と第１布材４１との間にクッション材を設けてもよい。この場合、クッション材（第１の部材となる）と皮革部材（第２の部材となる）４０とを結合剤Ａで接着することや、クッション材（第１の部材となる）と第１布材（第２の部材となる）４１とを結合剤Ａで接着することも可能である。クッション材は、天然ゴムラテックス接着剤で接着するようにしてもよい。皮革部材４０と第１布材４１との間には、クッション材以外の部材を設け、同様に結合剤Ａや天然ゴムラテックス接着剤で接着するようにしてもよい。 A cushion material may be provided between the leather member 40 and the first cloth material 41. In this case, the cushion material (being the first member) and the leather member (being the second member) 40 are bonded with the binder A, or the cushion material (being the first member) and the first cloth. It is also possible to bond the material (which becomes the second member) 41 with the binder A. The cushion material may be bonded with a natural rubber latex adhesive. A member other than the cushion material may be provided between the leather member 40 and the first cloth material 41, and may be similarly bonded with a binder A or a natural rubber latex adhesive.

また、皮革部材（第１の部材となる）４０と１枚の布材（第２の部材となる）とを結合剤Ａで接着するようにしてもよい。 Further, the leather member (being the first member) 40 and one cloth material (being the second member) may be bonded with the binder A.

また、上記実施形態では４枚の布部材４１〜４４を設けたが、布部材の枚数は３枚以下であってもよいし、５枚以上であってもよい。布部材の間にクッション材を挟むようにしてもよい。 In the above embodiment, the four cloth members 41 to 44 are provided. However, the number of cloth members may be three or less, or may be five or more. A cushion material may be sandwiched between the cloth members.

また、本発明は、サッカーボール以外にも、例えば、ハンドボール、バスケットボール、バレーボール、ビーチバレーボール、ラグビーボール、アメリカンフットボール等の各種球技に用いられるボールに適用できるとともに、遊戯用のボールにも適用できる。 In addition to the soccer ball, the present invention can be applied to balls used in various ball games such as handball, basketball, volleyball, beach volleyball, rugby ball, American football and the like, as well as a game ball.

また、表皮パネル３，４の形状は、五角形や六角形に限られるものではない。 Moreover, the shape of the skin panels 3 and 4 is not restricted to a pentagon or a hexagon.

また、ボール１の直径や重量も各競技の規格に合うようにすることが可能である。 Also, the diameter and weight of the ball 1 can be adapted to the standards of each competition.

また、上記実施形態では、本発明の内部部材をチューブ２で構成しているが、内部部材は、中空構造のもの以外にも、スポンジやゲル等からなる中実構造のものであってもよい。また、内部部材の材料は、上記したものに限られず、様々な種類のものを用いることができる。また、内部部材の形状は、球形以外にも、例えばラグビーボールのような形状であってもよい。 Moreover, in the said embodiment, although the internal member of this invention is comprised with the tube 2, the internal member may be a thing of the solid structure which consists of sponge, gel, etc. besides the thing of a hollow structure. . Further, the material of the internal member is not limited to the above, and various kinds of materials can be used. Further, the shape of the internal member may be, for example, a shape like a rugby ball in addition to the spherical shape.

以上説明したように、本発明に係るボールは、例えば、サッカーボールに適している。 As described above, the ball according to the present invention is suitable for a soccer ball, for example.

実施形態に係るボールの正面図である。It is a front view of the ball concerning an embodiment. 図１のII−II線断面図である。It is the II-II sectional view taken on the line of FIG. 表皮パネルの平面図である。It is a top view of a skin panel. 表皮パネルの製造要領を示す図である。It is a figure which shows the manufacture point of a skin panel.

１ボール
２チューブ
３，４表皮パネル
４０皮革部材
４１第１布材（第１の部材）
４２第２布材（第２の部材）
４３第３布材
４４第４布材
Ａ結合剤 1 Ball 2 Tube 3, 4 Skin panel 40 Leather member 41 First cloth material (first member)
42 Second cloth material (second member)
43 3rd cloth material 44 4th cloth material A Binder

Claims

A ball comprising an inner member and a skin panel formed to cover the inner member,
The skin panel includes a first member and a second member stacked on each other,
The first member and the second member are bonded by a binder containing a starch-based adhesive,
A ball characterized in that the binder contains at least one of barium sulfate, silicon oxide and clay as an additive for adjusting the weight of the skin panel.

The ball according to claim 1,
A ball characterized in that an additive for adjusting adhesive strength is mixed in the binder.

The ball according to claim 1 or 2,
A ball characterized in that the additive is in the form of a powder.

In the ball according to any one of claims 1 to 3,
A ball characterized in that a softener is mixed in the binder.