JP5281540B2 - Method for producing polyacetal resin composition - Google Patents
Method for producing polyacetal resin composition Download PDFInfo
- Publication number
- JP5281540B2 JP5281540B2 JP2009246856A JP2009246856A JP5281540B2 JP 5281540 B2 JP5281540 B2 JP 5281540B2 JP 2009246856 A JP2009246856 A JP 2009246856A JP 2009246856 A JP2009246856 A JP 2009246856A JP 5281540 B2 JP5281540 B2 JP 5281540B2
- Authority
- JP
- Japan
- Prior art keywords
- polyacetal resin
- hydrazine derivative
- compound
- melting point
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明は、ポリアセタール樹脂組成物の製造方法に関する。 The present invention relates to a method for producing a polyacetal resin composition.
ポリアセタール樹脂は、機械的強度、耐薬品性及び摺動性のバランスに優れ、且つその加工性が容易である。そこで、ポリアセタール樹脂は、代表的なエンジニアリングプラスチックスとして、電気機器、電気機器の機構部品、自動車部品及びその他の機構部品を中心に広範囲に亘って用いられている。しかしながら、ポリアセタール樹脂は、その利用分野の拡大によって、ホルムアルデヒド発生の抑制、エージング後の寸法安定性、耐モールドデポジット性も要求されている。このように、ポリアセタール樹脂に対する種々の性能の要求レベルがますます高くなっているのが現状である。 Polyacetal resin is excellent in the balance of mechanical strength, chemical resistance and slidability, and easy to process. Therefore, polyacetal resin is used as a typical engineering plastics over a wide range mainly in electrical equipment, mechanical parts of electrical equipment, automobile parts, and other mechanical parts. However, polyacetal resins are also required to suppress formaldehyde generation, have dimensional stability after aging, and mold deposit resistance due to the expansion of their application fields. In this way, the required level of various performances for polyacetal resins is increasing at present.
これらの要求に応えるため、特にホルムアルデヒド発生の抑制という要求に応えるため、ポリアセタール樹脂組成物に、グアナミン及びヒドラジド化合物を添加する方法(例えば特許文献1、5参照。)、カルボン酸ヒドラジド化合物を添加する方法(例えば特許文献2、3、4参照。)、ヒドラジド化合物を添加する方法(例えば特許文献6、7参照。)、芳香族ジヒドラジド及び脂肪族ヒドラジド化合物を添加する方法(例えば特許文献8参照。)が検討されている。
In order to meet these demands, in particular to meet the demand for suppression of formaldehyde generation, a method of adding guanamine and a hydrazide compound to the polyacetal resin composition (see, for example, Patent Documents 1 and 5) and a carboxylic acid hydrazide compound are added. A method (for example, see
しかしながら、それらの一般的にホルムキャッチャーといわれる化合物を添加したポリアセタール樹脂組成物は、ポリアセタールの結晶化状況に影響を与えてしまう。その結果、ポリアセタール樹脂組成物の成形品は、その寸法が安定しなかったり、リサイクル時のホルムアルデヒド放出量が安定しなかったりする他、エージング後の耐繰り返し衝撃性が安定しないという改善すべき点を有する。また、そのポリアセタール樹脂組成物は、金型への充填率が低い条件下での耐モールドデポジット性も改良の余地がある。 However, the polyacetal resin composition to which a compound generally referred to as a form catcher is added affects the crystallization state of the polyacetal. As a result, the molded article of the polyacetal resin composition is not stable in dimensions, the amount of formaldehyde released during recycling is not stable, and the repeated impact resistance after aging is not stable. Have. The polyacetal resin composition also has room for improvement in mold deposit resistance under conditions where the filling rate into the mold is low.
そこで、本発明は上記事情にかんがみてなされたものであり、特にエージング後の耐繰り返し衝撃性、及びリサイクル成形性、すなわちリサイクル時のホルムアルデヒド放出量低減性に優れたポリアセタール樹脂組成物の製造方法を提供することを目的とする。 Therefore, the present invention has been made in view of the above circumstances, and in particular, a method for producing a polyacetal resin composition excellent in repetitive impact resistance after aging and recycle moldability, that is, reduced formaldehyde emission during recycle. The purpose is to provide.
本発明者らは、上述の課題を達成するため鋭意検討した結果、ポリアセタール樹脂と、第1のヒドラジン誘導体と、前記第1のヒドラジン誘導体の融点を低下させる化合物と、を含有する原料組成物から得られるポリアセタール樹脂組成物を特定の工程を経て製造することにより上記課題を解決できることを見出し、本発明を完成させるに至った。
すなわち本発明は下記の通りである。
As a result of intensive studies to achieve the above-mentioned problems, the present inventors have found that a raw material composition containing a polyacetal resin, a first hydrazine derivative, and a compound that lowers the melting point of the first hydrazine derivative. It discovered that the said subject could be solved by manufacturing the polyacetal resin composition obtained through a specific process, and came to complete this invention.
That is, the present invention is as follows.
[1]ポリアセタール樹脂と、第1のヒドラジン誘導体と、前記第1のヒドラジン誘導体の融点を低下させる化合物と、を含有する原料組成物から得られるポリアセタール樹脂組成物の製造方法であって、
下記式(1)及び(2)で表される条件を満足する、前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物との混合物を調製する第1の工程と、前記第1の工程を経て得られた前記混合物を前記ポリアセタール樹脂と溶融混練する第2の工程と、を含むポリアセタール樹脂組成物の製造方法。
T1<T2 (1)
T1<T3 (2)
(式(1)及び(2)中、T1は、示差走査熱量計を用いて前記混合物に対して所定の温度プログラムで加熱及び冷却を施した後に、前記混合物が融解するまで2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T2は、前記示差走査熱量計を用いて前記第1のヒドラジン誘導体に対して所定の温度プログラムで加熱及び冷却を施した後に、前記第1のヒドラジン誘導体に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T3は、前記示差走査熱量計を用いて前記ポリアセタール樹脂に対して所定の温度プログラムで加熱及び冷却を施した後に、前記ポリアセタール樹脂に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)である。)
[2]前記第1の工程を経て得られた前記混合物を溶融する第3の工程を更に含み、前記第3の工程を経て得られた溶融混合物を前記第2の工程に供する、[1]に記載のポリアセタール樹脂組成物の製造方法。
[3]ポリアセタール樹脂と、第1のヒドラジン誘導体と、前記第1のヒドラジン誘導体の融点を低下させる化合物と、を含有する原料組成物から得られるポリアセタール樹脂組成物の製造方法であって、
前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物と前記ポリアセタール樹脂の一部とを混合して予備混合物を得る第1の工程と、前記第1の工程を経て得られた前記予備混合物を残りの前記ポリアセタール樹脂と溶融混練する第2の工程と、を含み、
前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物との混合物が下記式(1)及び(2)で表される条件を満足するものであるポリアセタール樹脂組成物の製造方法。
T1<T2 (1)
T1<T3 (2)
(式(1)及び(2)中、T1は、示差走査熱量計を用いて前記混合物に対して所定の温度プログラムで加熱及び冷却を施した後に、前記混合物が融解するまで2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T2は、前記示差走査熱量計を用いて前記第1のヒドラジン誘導体に対して所定の温度プログラムで加熱及び冷却を施した後に、前記第1のヒドラジン誘導体に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T3は、前記示差走査熱量計を用いて前記ポリアセタール樹脂に対して所定の温度プログラムで加熱及び冷却を施した後に、前記ポリアセタール樹脂に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)である。)
[4]前記第1の工程を経て得られた前記予備混合物を溶融する第3の工程を更に含み、前記第3の工程を経て得られた溶融予備混合物を前記第2の工程に供する、[3]に記載のポリアセタール樹脂組成物の製造方法。
[5]前記第1のヒドラジン誘導体の融点を低下させる前記化合物が、前記第1のヒドラジン誘導体とは異なる1種又は2種以上の第2のヒドラジン誘導体である、[1]〜[4]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[6]前記第1のヒドラジン誘導体がカルボン酸ヒドラジドであり、前記第1のヒドラジン誘導体の融点を低下させる前記化合物が、前記第1のヒドラジン誘導体とは異なる1種又は2種以上のカルボン酸ヒドラジドである、[1]〜[5]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[7]前記第1のヒドラジン誘導体が下記一般式(3)で表されるカルボン酸ジヒドラジドであり、前記第1のヒドラジン誘導体の融点を低下させる前記化合物が、前記第1のヒドラジン誘導体とは異なる1種又は2種以上のカルボン酸ヒドラジドである、[1]〜[6]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[8]前記第1のヒドラジン誘導体が、アジピン酸ジヒドラジド、セバシン酸ジヒドラジド及びドデカン二酸ジヒドラジドからなる群より選ばれる1種又は2種以上のカルボン酸ジヒドラジドである、[1]〜[7]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[9]前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物とが、アジピン酸ジヒドラジド、セバシン酸ジヒドラジド及びドデカン二酸ジヒドラジドからなる群より選ばれる互いに異なるカルボン酸ジヒドラジドを含む、[1]〜[8]いずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[10]前記ポリアセタール樹脂100質量部に対して、前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物との合計の含有量が0.03〜0.2質量部である、[1]〜[9]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[11]前記第1のヒドラジン誘導体と、前記第1のヒドラジン誘導体の融点を低下させる前記化合物との含有比が、質量基準で2:8〜8:2である、[1]〜[10]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[12]前記第1のヒドラジン誘導体と、前記第1のヒドラジン誘導体の融点を低下させる前記化合物との含有比が、質量基準で3:7〜7:3である、[1]〜[11]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[13]前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物との質量比1:1の混合物の吸熱容量が最も大きな吸熱ピークのピーク面積が、前記混合物の全吸熱ピークの総ピーク面積の95%未満である、[1]〜[12]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[14]前記ポリアセタール樹脂が、ポリアセタールコポリマーである、[1]〜[13]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[15]前記ポリアセタール樹脂が、エチレンオキサイド、プロピレンオキサイド、エピクロルヒドリン、1,3−ジオキソラン及び1,4−ブタンジオールホルマールからなる群より選ばれる1種又は2種以上のコモノマーを、トリオキサン1molに対して0.0013〜0.0039mol含有するポリアセタールコポリマーである、[1]〜[14]のいずれか一項に記載のポリアセタール樹脂組成物の製造方法。
[1] A method for producing a polyacetal resin composition obtained from a raw material composition containing a polyacetal resin, a first hydrazine derivative, and a compound that lowers the melting point of the first hydrazine derivative,
A first step of preparing a mixture of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative, satisfying the conditions represented by the following formulas (1) and (2); And a second step of melt-kneading the mixture obtained through the first step with the polyacetal resin.
T1 <T2 (1)
T1 <T3 (2)
(In the formulas (1) and (2), T1 is 2.5 ° C./until the mixture is melted after being heated and cooled with a predetermined temperature program using a differential scanning calorimeter. Among the endothermic peaks obtained when the temperature is increased at a rate of minutes, the temperature (° C.) indicates the peak of the endothermic peak having the largest endothermic capacity, and T2 is the first hydrazine using the differential scanning calorimeter. Among the endothermic peaks obtained when the derivative is heated and cooled by a predetermined temperature program and then heated to a rate of 2.5 ° C./min with respect to the first hydrazine derivative, the endothermic capacity is T3 is the temperature (° C.) indicating the peak of the largest endothermic peak, and T3 is the temperature of the polyacetal resin after heating and cooling the polyacetal resin with a predetermined temperature program using the differential scanning calorimeter. Among the endothermic peak obtained when heated at 2.5 ° C. / min with respect to a temperature (℃) endothermic capacity indicating the vertex of the largest endothermic peak.)
[2] The method further includes a third step of melting the mixture obtained through the first step, and subjecting the molten mixture obtained through the third step to the second step. [1] The manufacturing method of the polyacetal resin composition as described in 1 above.
[3] A method for producing a polyacetal resin composition obtained from a raw material composition comprising a polyacetal resin, a first hydrazine derivative, and a compound that lowers the melting point of the first hydrazine derivative,
A first step of obtaining a premix by mixing the first hydrazine derivative, the compound that lowers the melting point of the first hydrazine derivative, and a part of the polyacetal resin, and obtained through the first step. A second step of melt-kneading the prepared premix with the remaining polyacetal resin,
Production of a polyacetal resin composition in which a mixture of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative satisfies the conditions represented by the following formulas (1) and (2): Method.
T1 <T2 (1)
T1 <T3 (2)
(In the formulas (1) and (2), T1 is 2.5 ° C./until the mixture is melted after being heated and cooled with a predetermined temperature program using a differential scanning calorimeter. Among the endothermic peaks obtained when the temperature is increased at a rate of minutes, the temperature (° C.) indicates the peak of the endothermic peak having the largest endothermic capacity, and T2 is the first hydrazine using the differential scanning calorimeter. Among the endothermic peaks obtained when the derivative is heated and cooled by a predetermined temperature program and then heated to a rate of 2.5 ° C./min with respect to the first hydrazine derivative, the endothermic capacity is T3 is the temperature (° C.) indicating the peak of the largest endothermic peak, and T3 is the temperature of the polyacetal resin after heating and cooling the polyacetal resin with a predetermined temperature program using the differential scanning calorimeter. Among the endothermic peak obtained when heated at 2.5 ° C. / min with respect to a temperature (℃) endothermic capacity indicating the vertex of the largest endothermic peak.)
[4] The method further includes a third step of melting the premix obtained through the first step, and subjecting the melt premix obtained through the third step to the second step. 3] The manufacturing method of the polyacetal resin composition as described in 3].
[5] The compounds according to [1] to [4], wherein the compound that lowers the melting point of the first hydrazine derivative is one or more second hydrazine derivatives different from the first hydrazine derivative. The manufacturing method of the polyacetal resin composition as described in any one of Claims.
[6] The first hydrazine derivative is a carboxylic acid hydrazide, and the compound that lowers the melting point of the first hydrazine derivative is one or more carboxylic acid hydrazides different from the first hydrazine derivative. The method for producing a polyacetal resin composition according to any one of [1] to [5].
[7] The first hydrazine derivative is a carboxylic acid dihydrazide represented by the following general formula (3), and the compound that lowers the melting point of the first hydrazine derivative is different from the first hydrazine derivative. The manufacturing method of the polyacetal resin composition as described in any one of [1]-[6] which is 1 type, or 2 or more types of carboxylic acid hydrazide.
[8] The first hydrazine derivative is one or more carboxylic acid dihydrazides selected from the group consisting of adipic acid dihydrazide, sebacic acid dihydrazide, and dodecanedioic acid dihydrazide. [1] to [7] The manufacturing method of the polyacetal resin composition as described in any one of Claims.
[9] The first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative are different carboxylic acid dihydrazides selected from the group consisting of adipic acid dihydrazide, sebacic acid dihydrazide, and dodecanedioic acid dihydrazide. The manufacturing method of the polyacetal resin composition as described in any one of [1]-[8] containing.
[10] The total content of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative is 0.03 to 0.2 parts by mass with respect to 100 parts by mass of the polyacetal resin. The manufacturing method of the polyacetal resin composition as described in any one of [1]-[9].
[11] The content ratio of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative is 2: 8 to 8: 2 on a mass basis, [1] to [10] The manufacturing method of the polyacetal resin composition as described in any one of these.
[12] The content ratio of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative is 3: 7 to 7: 3 on a mass basis, [1] to [11] The manufacturing method of the polyacetal resin composition as described in any one of these.
[13] The peak area of the endothermic peak having the largest endothermic capacity of the mixture having a mass ratio of 1: 1 between the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative is the total endotherm of the mixture. The manufacturing method of the polyacetal resin composition as described in any one of [1]-[12] which is less than 95% of the total peak area of a peak.
[14] The method for producing a polyacetal resin composition according to any one of [1] to [13], wherein the polyacetal resin is a polyacetal copolymer.
[15] The polyacetal resin contains one or more comonomers selected from the group consisting of ethylene oxide, propylene oxide, epichlorohydrin, 1,3-dioxolane, and 1,4-butanediol formal with respect to 1 mol of trioxane. The method for producing a polyacetal resin composition according to any one of [1] to [14], which is a polyacetal copolymer containing 0.0013 to 0.0039 mol.
本発明によれば、特にエージング後の耐繰り返し衝撃性、及びリサイクル成形性、すなわちリサイクル時のホルムアルデヒド放出量安定性に優れたポリアセタール樹脂組成物の製造方法を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the manufacturing method of the polyacetal resin composition excellent in the repetitive impact resistance especially after aging and recycle moldability, ie, the formaldehyde discharge | release amount stability at the time of recycling, can be provided.
以下、必要に応じて図面を参照しつつ、本発明を実施するための形態(以下、「本実施形態」という。)について詳細に説明する。なお、図面中、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。また、本発明は、下記の本実施形態に限定されるものではなく、その要旨の範囲内で種々変形して実施することができる。本実施形態で製造されるポリアセタール樹脂組成物は、ポリアセタール樹脂(A)と、ヒドラジン誘導体(B)と、ヒドラジン誘導体(B)の融点を低下させる化合物(C)とを含有する原料組成物から得られる。ここで、「原料組成物」とは、上記3つの成分を含む組成物を意味し、その原料組成物に何らかの処理(例えば、混合、溶融、混練など)を施して本実施形態に係るポリアセタール樹脂組成物が得られる。ただし、何らかの処理を施して得られるポリアセタール樹脂組成物は、引き続き、上記3つの成分を含有すると好ましい。 Hereinafter, a form for carrying out the present invention (hereinafter referred to as “the present embodiment”) will be described in detail with reference to the drawings as necessary. In the drawings, positional relationships such as up, down, left and right are based on the positional relationships shown in the drawings unless otherwise specified. Further, the present invention is not limited to the present embodiment described below, and can be implemented with various modifications within the scope of the gist. The polyacetal resin composition produced in the present embodiment is obtained from a raw material composition containing a polyacetal resin (A), a hydrazine derivative (B), and a compound (C) that lowers the melting point of the hydrazine derivative (B). It is done. Here, the “raw material composition” means a composition containing the above three components, and the raw material composition is subjected to some treatment (for example, mixing, melting, kneading, etc.) and the polyacetal resin according to the present embodiment. A composition is obtained. However, it is preferable that the polyacetal resin composition obtained by performing any treatment subsequently contains the above three components.
本実施形態に係るポリアセタール樹脂組成物は、ポリアセタール樹脂(A)と、ヒドラジン誘導体(B)と、ヒドラジン誘導体(B)の融点を低下させる化合物(C)と、を含有する原料組成物から得られるポリアセタール樹脂組成物であって、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物が、下記式(1)及び(2)で表される条件を満足するものである。
T1<T2 (1)
T1<T3 (2)
The polyacetal resin composition according to this embodiment is obtained from a raw material composition containing a polyacetal resin (A), a hydrazine derivative (B), and a compound (C) that lowers the melting point of the hydrazine derivative (B). The polyacetal resin composition, wherein the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) satisfies the conditions represented by the following formulas (1) and (2) Is.
T1 <T2 (1)
T1 <T3 (2)
ここで、式(1)及び(2)中、T1は、示差走査熱量計を用いて上記ヒドラジン誘導体(B)と、ヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物に対して所定の温度プログラムで加熱及び冷却を施した後に、上記混合物が融解するまで2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T2は、上記示差走査熱量計を用いてヒドラジン誘導体(B)に対して所定の温度プログラムで加熱及び冷却を施した後に、2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T3は、上記示差走査熱量計を用いてポリアセタール樹脂(A)に対して所定の温度プログラムで加熱及び冷却を施した後に、2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)である。 Here, in the formulas (1) and (2), T1 represents a mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) using a differential scanning calorimeter. Of the endothermic peak with the largest endothermic capacity among the endothermic peaks obtained when the temperature is raised at a rate of 2.5 ° C./min until the mixture melts after heating and cooling in accordance with a predetermined temperature program. T2 is a temperature of 2.5 ° C./min after heating and cooling the hydrazine derivative (B) with a predetermined temperature program using the above differential scanning calorimeter. Among the endothermic peaks obtained when the temperature is raised, this is the temperature (° C.) indicating the peak of the endothermic peak having the largest endothermic capacity, and T3 is a predetermined value for the polyacetal resin (A) using the differential scanning calorimeter. Temperature program After performing heating and cooling without, among the endothermic peak obtained when temperature was raised at 2.5 ° C. / min, the temperature (℃) endothermic capacity indicating the vertex of the largest endothermic peak.
また、上述の「所定の温度プログラム」とは、上記混合物、ヒドラジン誘導体(B)、ポリアセタール樹脂(A)の吸熱ピークよりも低い温度から上記混合物が融解する温度まで2.5℃/分の速度で昇温し、次いで、2分間その温度で保持し、その次に、100℃まで10℃/分の降温速度で降温する温度プログラムを意味する。 The above-mentioned “predetermined temperature program” means a rate of 2.5 ° C./min from a temperature lower than the endothermic peak of the mixture, the hydrazine derivative (B), and the polyacetal resin (A) to a temperature at which the mixture melts. Temperature program, and then held at that temperature for 2 minutes, and then lowered to 100 ° C. at a rate of temperature decrease of 10 ° C./min.
[ポリアセタール樹脂(A)]
ポリアセタール樹脂(A)としては、従来知られているものであれば特に限定されず、ポリアセタールホモポリマー及びポリアセタールコポリマーが挙げられる。ポリアセタールホモポリマーとしては、例えば、ホルムアルデヒド単量体又はその3量体(トリオキサン)や4量体(テトラオキサン)等のホルムアルデヒドの環状オリゴマーを単独重合して得られる、実質的にオキシメチレン単位のみからなるポリアセタールホモポリマーが挙げられる。また、ポリアセタールコポリマーとしては、ホルムアルデヒド単量体又はその3量体(トリオキサン)若しくは4量体(テトラオキサン)等のホルムアルデヒドの環状オリゴマーと、エチレンオキサイド、プロピレンオキサイド、エピクロルヒドリン、1,3−ジオキソラン及び1,4−ブタンジオールホルマールからなる群より選ばれる1種又は2種以上のコモノマーである、グリコール若しくはジグリコールの環状ホルマール等の環状エーテル又は環状ホルマールとを共重合させて得られたポリアセタールコポリマーが挙げられる。さらに、ポリアセタールコポリマーとして、ホルムアルデヒド単量体又は上記ホルムアルデヒドの環状オリゴマーと、単官能グリシジルエーテルとを共重合させて得られる分岐を有するポリアセタールコポリマー;ホルムアルデヒド単量体又は上記ホルムアルデヒドの環状オリゴマーと、多官能グリシジルエーテルとを共重合させて得られる架橋構造を有するポリアセタールコポリマーも挙げられる。
[Polyacetal resin (A)]
The polyacetal resin (A) is not particularly limited as long as it is conventionally known, and examples thereof include polyacetal homopolymers and polyacetal copolymers. The polyacetal homopolymer, for example, consists essentially of oxymethylene units obtained by homopolymerizing formaldehyde monomers or cyclic oligomers of formaldehyde such as trimers (trioxane) and tetramers (tetraoxane). A polyacetal homopolymer may be mentioned. Polyacetal copolymers include formaldehyde monomers or cyclic oligomers of formaldehyde such as trimer (trioxane) or tetramer (tetraoxane), ethylene oxide, propylene oxide, epichlorohydrin, 1,3-dioxolane and 1,3. Examples thereof include polyacetal copolymers obtained by copolymerizing cyclic ether or cyclic formal such as cyclic formal of glycol or diglycol, which is one or more comonomers selected from the group consisting of 4-butanediol formal. . Furthermore, as a polyacetal copolymer, a polyacetal copolymer having a branch obtained by copolymerizing a formaldehyde monomer or a cyclic oligomer of the above formaldehyde with a monofunctional glycidyl ether; a formaldehyde monomer or a cyclic oligomer of the above formaldehyde, and a polyfunctional A polyacetal copolymer having a crosslinked structure obtained by copolymerization with glycidyl ether is also exemplified.
また、両末端若しくは片末端に水酸基などの官能基を有する化合物、例えば、ポリアルキレングリコールの存在下、ホルムアルデヒド単量体又は上記ホルムアルデヒドの環状オリゴマーを重合して得られるブロック成分を有するポリアセタールホモポリマー;同じく、両末端若しくは片末端に水酸基などの官能基を有する化合物、例えば水素添加ポリブタジエングリコールの存在下、ホルムアルデヒド単量体又は上記ホルムアルデヒドの環状オリゴマーと環状エーテル、環状ホルマールとを共重合させて得られるブロック成分を有するポリアセタールコポリマーも、ポリアセタール樹脂(A)として挙げられる。上述のとおり、ポリアセタール樹脂(A)として、ポリアセタールホモポリマー、ポリアセタールコポリマーのいずれも用いることが可能である。これらの中では熱安定性と機械物性とのバランスの観点から、ポリアセタールコポリマーが好ましい。ポリアセタール樹脂(A)は1種を単独で又は2種以上を組み合わせて用いられる。 In addition, a compound having a functional group such as a hydroxyl group at both ends or one end, for example, a polyacetal homopolymer having a block component obtained by polymerizing a formaldehyde monomer or a cyclic oligomer of formaldehyde in the presence of polyalkylene glycol; Similarly, it is obtained by copolymerizing a compound having a functional group such as a hydroxyl group at both ends or one end, such as a hydrogenated polybutadiene glycol, with a formaldehyde monomer or a cyclic oligomer of formaldehyde and a cyclic ether or cyclic formal. A polyacetal copolymer having a block component is also exemplified as the polyacetal resin (A). As described above, any of a polyacetal homopolymer and a polyacetal copolymer can be used as the polyacetal resin (A). Among these, a polyacetal copolymer is preferable from the viewpoint of a balance between thermal stability and mechanical properties. A polyacetal resin (A) is used individually by 1 type or in combination of 2 or more types.
トリオキサンと上記1,3−ジオキソラン等のコモノマーとのポリアセタールコポリマーである場合、一般的には、トリオキサン1molに対してコモノマーの共重合割合は0.001〜0.6molの範囲であれば、熱安定性が良好となるので好ましい。そのコモノマーの共重合割合は0.001〜0.2molであるとより好ましく、0.0013〜0.1molであると更に好ましく、0.0013〜0.0039molであると特に好ましい。 In the case of a polyacetal copolymer of trioxane and the above-mentioned comonomer such as 1,3-dioxolane, generally, if the copolymerization ratio of the comonomer is in the range of 0.001 to 0.6 mol with respect to 1 mol of trioxane, heat stability This is preferable because the property is improved. The copolymerization ratio of the comonomer is more preferably 0.001 to 0.2 mol, further preferably 0.0013 to 0.1 mol, and particularly preferably 0.0013 to 0.0039 mol.
ポリアセタールコポリマーを共重合により得る際に用いられる重合触媒としては特に制限されないが、ルイス酸、プロトン酸及びそのエステル又は無水物等のカチオン活性触媒が好ましい。ルイス酸としては、例えば、ホウ酸、スズ、チタン、リン、ヒ素及びアンチモンのハロゲン化物が挙げられ、より具体的には、三フッ化ホウ素、四塩化スズ、四塩化チタン、五フッ化リン、五塩化リン、五フッ化アンチモン及びその錯化合物又は塩が挙げられる。ただし、ルイス酸はこれらに限定されない。また、プロトン酸、そのエステル又は無水物の具体例としては、パークロル酸、トリフルオロメタンスルホン酸、パークロル酸−3級ブチルエステル、アセチルパークロラート、トリメチルオキソニウムヘキサフルオロホスフェートが挙げられるが、これらに限定されない。これらのカチオン活性触媒の中でも、三フッ化ホウ素;三フッ化ホウ素水和物;及び酸素原子又は硫黄原子を含む有機化合物と三フッ化ホウ素との配位錯化合物が好ましい。そのようなカチオン活性触媒として、例えば、三フッ化ホウ素ジエチルエーテル、三フッ化ホウ素ジ−n−ブチルエーテル、三フッ化ホウ素ジ−n−ブチルエーテラートが重合収率向上の観点から好適である。また、上記ポリアセタールコポリマーを得る際には、カチオン活性触媒に加えて、メチラール等の重合連鎖剤(連鎖移動剤)を適宜用いてもよい。さらにメチラールを用いる際、含有水分量量が100ppm以下で含有メタノール量が1質量%以下のもの、より好ましくは、含有水分量が50ppm以下で含有メタノール量が0.7質量%以下のメチラールが好ましい。 The polymerization catalyst used when the polyacetal copolymer is obtained by copolymerization is not particularly limited, but cationically active catalysts such as Lewis acids, proton acids and their esters or anhydrides are preferred. Examples of Lewis acids include boric acid, tin, titanium, phosphorus, arsenic and antimony halides. More specifically, boron trifluoride, tin tetrachloride, titanium tetrachloride, phosphorus pentafluoride, Examples thereof include phosphorus pentachloride, antimony pentafluoride, and complex compounds or salts thereof. However, the Lewis acid is not limited to these. Specific examples of the protonic acid, its ester or anhydride include perchloric acid, trifluoromethanesulfonic acid, perchloric acid-tertiary butyl ester, acetyl perchlorate, trimethyloxonium hexafluorophosphate, It is not limited. Among these cationically active catalysts, boron trifluoride; boron trifluoride hydrate; and a coordination complex compound of an organic compound containing an oxygen atom or a sulfur atom and boron trifluoride are preferable. As such a cationically active catalyst, for example, boron trifluoride diethyl ether, boron trifluoride di-n-butyl ether, and boron trifluoride di-n-butyl etherate are preferable from the viewpoint of improving the polymerization yield. Moreover, when obtaining the said polyacetal copolymer, in addition to a cation active catalyst, you may use suitably polymerization chain agents (chain transfer agent), such as methylal. Furthermore, when using methylal, the amount of water content is 100 ppm or less and the amount of methanol contained is 1% by mass or less, more preferably, the methylal content is 50 ppm or less and the amount of methanol contained is 0.7% by mass or less. .
ポリアセタールコポリマーの重合方法としては特に制限されないが、従来公知の方法、例えば、米国特許第3027352号明細書、米国特許第3803094号明細書、独国特許発明第1161421号明細書、独国特許発明第1495228号明細書、独国特許発明第1720358号明細書、独国特許発明第3018898号明細書、特開昭58−98322号公報、特開平7−70267号公報に記載の方法が挙げられる。特公昭55−42085号公報には、洗浄・除去を行う必要のない触媒失活剤として三価のリン化合物が提案されているが、さらに高い熱安定性のポリアセタールコポリマーを得るためには不安定末端の除去が必要となる。 The polymerization method of the polyacetal copolymer is not particularly limited, but conventionally known methods, for example, U.S. Pat. No. 30,273,352, U.S. Pat. No. 3,803,094, German Patent No. 1161412, and German Patent Invention No. No. 1495228, German Patent No. 1720358, German Patent No. 3018898, JP-A-58-98322, JP-A-7-70267. Japanese Patent Publication No. 55-42085 proposes a trivalent phosphorus compound as a catalyst deactivator that does not need to be washed and removed. However, it is unstable to obtain a polyacetal copolymer having higher thermal stability. It is necessary to remove the ends.
上記重合で得られたポリアセタールコポリマーには、熱的に不安定な末端部(−(OCH2)n−OH基)が存在するため、その実用性を向上させるために、下記に示す特定の不安定末端部の分解除去処理を施すと好ましい。 The polyacetal copolymer obtained by the above polymerization has a thermally unstable terminal portion (— (OCH 2 ) n —OH group). Therefore, in order to improve its practicality, the following specific irregularities are required. It is preferable to disassemble and remove the stable end portion.
特定の不安定末端部の分解除去処理(以下、単に「不安定末端部除去処理」という。)とは、例えば下記一般式(7)で表わされる少なくとも1種の第4級アンモニウム化合物の存在下で、ポリアセタールコポリマーの融点以上260℃以下の温度で、ポリアセタールコポリマーを溶融させた状態で熱処理する方法である。 The specific decomposing / removing treatment of unstable terminal portion (hereinafter, simply referred to as “unstable end portion removing treatment”) is, for example, in the presence of at least one quaternary ammonium compound represented by the following general formula (7). In this method, the polyacetal copolymer is heat-treated at a temperature not lower than the melting point of the polyacetal copolymer and not higher than 260 ° C. in a molten state.
[R1R2R3R4N+]nXn- (7)
ここで、式(7)中、R1、R2、R3及びR4は、各々独立して、炭素数1〜30の置換又は非置換アルキル基;炭素数6〜20のアリール基;炭素数1〜30の置換又は非置換アルキル基の少なくとも1個の水素原子が炭素数6〜20のアリール基で置換されたアラルキル基;炭素数6〜20のアリール基の少なくとも1個の水素原子が炭素数1〜30の置換又は非置換アルキル基で置換されたアルキルアリール基を示し、置換又は非置換アルキル基は直鎖状、分岐状、又は環状である。上記置換アルキル基の置換基はハロゲン原子、水酸基、アルデヒド基、カルボキシル基、アミノ基、又はアミド基である。また、上記非置換アルキル基、アリール基、アラルキル基、アルキルアリール基はその水素原子がハロゲン原子で置換されていてもよい。nは1〜3の整数を示す。Xは水酸基、又は炭素数1〜20のカルボン酸、ハロゲン化水素以外の水素酸、オキソ酸、無機チオ酸若しくは炭素数1〜20の有機チオ酸の酸残基を示す。
[R 1 R 2 R 3 R 4 N + ] n X n- (7)
Here, in formula (7), R 1 , R 2 , R 3 and R 4 are each independently a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms; an aryl group having 6 to 20 carbon atoms; carbon An aralkyl group in which at least one hydrogen atom of the substituted or unsubstituted alkyl group having 1 to 30 is substituted with an aryl group having 6 to 20 carbon atoms; at least one hydrogen atom of the aryl group having 6 to 20 carbon atoms is The alkylaryl group substituted by the C1-C30 substituted or unsubstituted alkyl group is shown, and a substituted or unsubstituted alkyl group is linear, branched, or cyclic. The substituent of the substituted alkyl group is a halogen atom, a hydroxyl group, an aldehyde group, a carboxyl group, an amino group, or an amide group. Further, in the above unsubstituted alkyl group, aryl group, aralkyl group, and alkylaryl group, the hydrogen atom may be substituted with a halogen atom. n shows the integer of 1-3. X represents a hydroxyl group or an acid residue of a carboxylic acid having 1 to 20 carbon atoms, a hydrogen acid other than a hydrogen halide, an oxo acid, an inorganic thioacid, or an organic thioacid having 1 to 20 carbon atoms.
上述の第4級アンモニウム化合物は、上記一般式(7)で表わされるものであれば特に制限はないが、一般式(7)におけるR1、R2、R3、及びR4が、各々独立して、炭素数1〜5のアルキル基又は炭素数2〜4のヒドロキシアルキル基であることが好ましく、さらに、R1、R2、R3、及びR4の少なくとも1つが、ヒドロキシエチル基であるものが特に好ましい。具体的には、テトラメチルアンモニウム、テトエチルアンモニウム、テトラプロピルアンモニウム、テトラ−n−ブチルアンモニウム、セチルトリメチルアンモニウム、テトラデシルトリメチルアンモニウム、1,6−ヘキサメチレンビス(トリメチルアンモニウム)、デカメチレン−ビス−(トリメチルアンモニウム)、トリメチル−3−クロロ−2−ヒドロキシプロピルアンモニウム、トリメチル(2−ヒドロキシエチル)アンモニウム、トリエチル(2−ヒドロキシエチル)アンモニウム、トリプロピル(2−ヒドロキシエチル)アンモニウム、トリ−n−ブチル(2−ヒドロキシエチル)アンモニウム、トリメチルベンジルアンモニウム、トリエチルベンジルアンモニウム、トリプロピルベンジルアンモニウム、トリ−n−ブチルベンジルアンモニウム、トリメチルフェニルアンモニウム、トリエチルフェニルアンモニウム、トリメチル−2−オキシエチルアンモニウム、モノメチルトリヒドロキシエチルアンモニウム、モノエチルトリヒドロキシエチルアンモニウム、オクタデシルトリ(2−ヒドロキシエチル)アンモニウム、テトラキス(ヒドロキシエチル)アンモニウム等の水酸化物(Xn-=OH-);塩酸、臭酸、フッ酸等の水素酸塩;硫酸(Xn-=HSO4 -、SO4 2-)、硝酸、燐酸、炭酸(Xn-=HCO3 -、CO3 2-)、ホウ酸(Xn-=B(OH)4 -)、塩素酸、ヨウ素酸、珪酸、過塩素酸、亜塩素酸、次亜塩素酸、クロロ硫酸、アミド硫酸、二硫酸、トリポリ燐酸等のオキソ酸塩;チオ硫酸等のチオ酸塩;蟻酸、酢酸、プロピオン酸、ブタン酸、イソ酪酸、ペンタン酸、カプロン酸、カプリル酸、カプリン酸、安息香酸、シュウ酸等のカルボン酸塩が挙げられる。これらの中でも、水酸化物、硫酸塩、炭酸塩、ホウ酸塩、カルボン酸塩が好ましい。カルボン酸塩のなかでは、蟻酸塩、酢酸塩、プロピオン酸塩が特に好ましい。そのような第4級アンモニウム化合物としては、例えば、水酸化コリン蟻酸塩(トリメチル−2−ヒドロキシエチルアンモニウムフォルメート、トリエチル−2−ヒドロキシエチルアンモニウムフォルメート等)が挙げられる。これら第4級アンモニウム化合物は、1種を単独で用いられてもよいし、また2種以上を組み合わせて用いられてもよい。また、上記第4級アンモニウム化合物に加えて、公知の不安定末端部の分解促進剤であるアンモニアやトリエチルアミン等のアミン類等を併用してもよい。 The quaternary ammonium compound is not particularly limited as long as it is represented by the general formula (7), but R 1 , R 2 , R 3 , and R 4 in the general formula (7) are each independently selected. In addition, the alkyl group is preferably an alkyl group having 1 to 5 carbon atoms or a hydroxyalkyl group having 2 to 4 carbon atoms, and at least one of R 1 , R 2 , R 3 , and R 4 is a hydroxyethyl group. Some are particularly preferred. Specifically, tetramethylammonium, tetoethylammonium, tetrapropylammonium, tetra-n-butylammonium, cetyltrimethylammonium, tetradecyltrimethylammonium, 1,6-hexamethylenebis (trimethylammonium), decamethylene-bis- ( Trimethylammonium), trimethyl-3-chloro-2-hydroxypropylammonium, trimethyl (2-hydroxyethyl) ammonium, triethyl (2-hydroxyethyl) ammonium, tripropyl (2-hydroxyethyl) ammonium, tri-n-butyl ( 2-hydroxyethyl) ammonium, trimethylbenzylammonium, triethylbenzylammonium, tripropylbenzylammonium, tri-n-butylbenzene Such as zirconium ammonium, trimethylphenylammonium, triethylphenylammonium, trimethyl-2-oxyethylammonium, monomethyltrihydroxyethylammonium, monoethyltrihydroxyethylammonium, octadecyltri (2-hydroxyethyl) ammonium, tetrakis (hydroxyethyl) ammonium Hydroxides (X n− = OH − ); hydrogenates such as hydrochloric acid, odorous acid, hydrofluoric acid; sulfuric acid (X n− = HSO 4 − , SO 4 2− ), nitric acid, phosphoric acid, carbonic acid (X n− = HCO 3 − , CO 3 2− ), boric acid (X n− = B (OH) 4 − ), chloric acid, iodic acid, silicic acid, perchloric acid, chlorous acid, hypochlorous acid, chlorosulfuric acid, Oxoacid salts such as amidosulfuric acid, disulfuric acid, tripolyphosphoric acid; thioacid salts such as thiosulfuric acid; formic acid, acetic acid, propionic acid, butanoic acid, iso Acid, pentanoic acid, caproic acid, caprylic acid, capric acid, benzoic acid, carboxylic acid salts such as oxalate. Among these, hydroxide, sulfate, carbonate, borate, and carboxylate are preferable. Among the carboxylates, formate, acetate, and propionate are particularly preferable. Examples of such quaternary ammonium compounds include hydroxy choline formate (trimethyl-2-hydroxyethylammonium formate, triethyl-2-hydroxyethylammonium formate, etc.). These quaternary ammonium compounds may be used individually by 1 type, and may be used in combination of 2 or more type. Further, in addition to the quaternary ammonium compound, amines such as ammonia and triethylamine which are known decomposition accelerators for unstable terminals may be used in combination.
上記熱処理する方法に用いる第4級アンモニウム化合物の量は、ポリアセタールコポリマーと第4級アンモニウム化合物との合計質量に対する下記式(8)で表わされる第4級アンモニウム化合物由来の窒素の量に換算して、0.05〜50質量ppmであると好ましく、1〜30質量ppmであるとより好ましい。 The amount of the quaternary ammonium compound used in the heat treatment method is converted to the amount of nitrogen derived from the quaternary ammonium compound represented by the following formula (8) with respect to the total mass of the polyacetal copolymer and the quaternary ammonium compound. , 0.05 to 50 ppm by mass, and more preferably 1 to 30 ppm by mass.
P×14/Q (8)
ここで、式(8)中、Pは第4級アンモニウム化合物のポリアセタールコポリマーに対する濃度(質量ppm)を示し、14は窒素の原子量であり、Qは第4級アンモニウム化合物の分子量を示す。
P × 14 / Q (8)
Here, in Formula (8), P shows the density | concentration (mass ppm) with respect to the polyacetal copolymer of a quaternary ammonium compound, 14 is the atomic weight of nitrogen, Q shows the molecular weight of a quaternary ammonium compound.
第4級アンモニウム化合物の添加量が、第4級アンモニウム化合物由来の窒素の量に換算して0.05質量ppm未満であると不安定末端部の分解除去速度が低下する傾向にあり、50質量ppmを超えると不安定末端部除去処理後のポリアセタールコポリマーの色調が悪化する傾向にある。 When the addition amount of the quaternary ammonium compound is less than 0.05 ppm by mass in terms of the amount of nitrogen derived from the quaternary ammonium compound, the decomposition and removal rate of the unstable terminal portion tends to decrease, and 50 mass If it exceeds ppm, the color tone of the polyacetal copolymer after the removal of the unstable end portion tends to deteriorate.
ポリアセタールコポリマーの不安定末端部除去処理は、そのポリアセタールコポリマーの融点以上260℃以下の温度でポリアセタールコポリマーを溶融させた状態で熱処理することにより達成される。この熱処理に用いる装置としては特に制限はないが、押出機、ニーダー等を用いて熱処理することが好適である。また、分解により発生したホルムアルデヒドは減圧下で除去される。第4級アンモニウム化合物の添加方法には特に制約はなく、重合触媒を失活する工程にて水溶液として加える方法、重合で生成したポリアセタールコポリマーパウダーに吹きかける方法などが挙げられる。いずれの添加方法を用いても、ポリアセタールコポリマーを熱処理する工程で添加されていればよく、押出機の中に注入してもよい。あるいは、ポリアセタール樹脂組成物に押出機等を用いてフィラーやピグメントの配合を行う場合、樹脂ペレットに該化合物を添着し、その後の配合工程で不安定末端部除去処理を行ってもよい。 The unstable end portion removal treatment of the polyacetal copolymer is achieved by heat-treating the polyacetal copolymer in a melted state at a temperature not lower than the melting point of the polyacetal copolymer and not higher than 260 ° C. The apparatus used for this heat treatment is not particularly limited, but it is preferable to perform heat treatment using an extruder, a kneader or the like. In addition, formaldehyde generated by decomposition is removed under reduced pressure. There are no particular restrictions on the method of adding the quaternary ammonium compound, and examples thereof include a method of adding it as an aqueous solution in the step of deactivating the polymerization catalyst and a method of spraying the polyacetal copolymer powder produced by the polymerization. Whichever addition method is used, it suffices if it is added in the step of heat-treating the polyacetal copolymer, and it may be poured into an extruder. Alternatively, when the filler or pigment is blended into the polyacetal resin composition using an extruder or the like, the compound may be attached to the resin pellet, and the unstable terminal portion may be removed in the subsequent blending step.
不安定末端部除去処理を、重合により得られたポリアセタールコポリマー中の重合触媒を失活させた後に行ってもよく、重合触媒を失活させずに行ってもよい。重合触媒の失活処理としては特に制限されないが、アミン類等の塩基性の水溶液中で重合触媒を中和失活する方法を代表例として挙げることができる。また、重合触媒を失活させずに、ポリアセタールコポリマーの融点以下の温度で不活性ガス雰囲気下にて加熱し、重合触媒を揮発により低減した後、該不安定末端部除去処理を行うことも有効な方法である。 The unstable terminal portion removal treatment may be performed after the polymerization catalyst in the polyacetal copolymer obtained by polymerization is deactivated or may be performed without deactivating the polymerization catalyst. The polymerization catalyst deactivation treatment is not particularly limited, but a representative example is a method of neutralizing and deactivating the polymerization catalyst in a basic aqueous solution such as amines. It is also effective to remove the unstable end after heating in an inert gas atmosphere at a temperature below the melting point of the polyacetal copolymer without deactivating the polymerization catalyst, and reducing the polymerization catalyst by volatilization. It is a simple method.
不安定末端部除去処理を行うことで、窒素雰囲気下、200℃で50分間加熱したときのホルムアルデヒド発生量が、ポリアセタール樹脂の量に対して100ppm以下のポリアセタール樹脂を得ることができる。 By performing the unstable terminal portion removal treatment, a polyacetal resin in which the amount of formaldehyde generated when heated at 200 ° C. for 50 minutes in a nitrogen atmosphere is 100 ppm or less with respect to the amount of the polyacetal resin can be obtained.
[ヒドラジン誘導体(B)]
本実施形態に係るヒドラジン誘導体(B)は、窒素原子間の単結合を有するヒドラジン構造(N−N)を有するものであれば特に限定されず、例えばヒドラジン;ヒドラジン水和物;コハク酸モノヒドラジド、グルタル酸モノヒドラジド、アジピン酸モノヒドラジド、ピメリン酸モノヒドラジド、スペリン酸モノヒドラジド、アゼライン酸モノヒドラジド、セバシン酸モノヒドラジド等のカルボン酸モノヒドラジド;蓚酸ジヒドラジド、マロン酸ジヒドラジド、コハク酸ジヒドラジド、グルタル酸ジヒドラジド、アジピン酸ジヒドラジド、ピメリン酸ジヒドラジド、スペリン酸ジヒドラジド、アゼライン酸ジヒドラジド、セバシン酸ジヒドラジド、ドデカン二酸ジヒドラジド等の飽和脂肪族カルボン酸ジヒドラジド;マレイン酸ジヒドラジド、フマル酸ジヒドラジド、イタコン酸ジヒドラジド等のモノオレフィン性不飽和ジカルボン酸のジヒドラジド;イソフタル酸ジヒドラジド、フタル酸ジヒドラジド、2,6−ナフタレンジカルボジヒドラジド等の芳香族カルボン酸ジヒドラジド;ピロメリット酸のジヒドラジド;トリマー酸トリヒドラジド、シクロヘキサントリカルボン酸トリヒドラジド、ベンゼントリカルボン酸トリヒドラジド、ニトリロトリ酢酸トリヒドラジド、クエン酸トリヒドラジド等のトリヒドラジド;ピロメリット酸テトラヒドラジド、ナフトエ酸テトラヒドラジド、エチレンジアミンテトラ酢酸テトラヒドラジド、1,4,5,8−ナフトエ酸テトラヒドラジド等のテトラヒドラジド;カルボン酸低級アルキルエステル基を有する低重合体をヒドラジン又はヒドラジン水化物(ヒドラジンヒドラート)と反応させてなるポリヒドラジド等のポリヒドラジド;炭酸ジヒドラジド;ビスセミカルバジド;ヘキサメチレンジイソシアネート、イソホロンジイソシアネート等のジイソシアネート及びそれから誘導されるポリイソシアネート化合物にN,N−ジメチルヒドラジン等のN,N−置換ヒドラジン及び/又は上記例示のヒドラジドを過剰に反応させて得られる多官能セミカルバジド;上記ポリイソシアネート化合物とポリエーテルポリオール類又はポリエチレングリコールモノアルキルエーテル類等の親水性基を含む活性水素化合物との反応物中のイソシアネート基に、上記のいずれかのジヒドラジドを過剰に反応させて得られる水系多官能セミカルバジド;上記多官能セミカルバジドと上記水系多官能セミカルバジドとの混合物;ビスアセチルジヒドラゾン等が挙げられる。
[Hydrazine derivative (B)]
The hydrazine derivative (B) according to the present embodiment is not particularly limited as long as it has a hydrazine structure (NN) having a single bond between nitrogen atoms. For example, hydrazine; hydrazine hydrate; succinic monohydrazide , Carboxylic acid monohydrazides such as glutaric acid monohydrazide, adipic acid monohydrazide, pimelic acid monohydrazide, speric acid monohydrazide, azelaic acid monohydrazide, sebacic acid monohydrazide; oxalic acid dihydrazide, malonic acid dihydrazide, succinic acid dihydrazide, glutaric acid Saturated aliphatic carboxylic acid dihydrazides such as dihydrazide, adipic acid dihydrazide, pimelic acid dihydrazide, speric acid dihydrazide, azelaic acid dihydrazide, sebacic acid dihydrazide, dodecanedioic acid dihydrazide; maleic acid dihydrazide Diolefins of monoolefinically unsaturated dicarboxylic acids such as fumarate dihydrazide and itaconic acid dihydrazide; aromatic carboxylic acid dihydrazides such as isophthalic acid dihydrazide, phthalic acid dihydrazide and 2,6-naphthalenedicarbodihydrazide; pyrohydric acid dihydrazide; trimer Trihydrazides such as acid trihydrazide, cyclohexanetricarboxylic acid trihydrazide, benzenetricarboxylic acid trihydrazide, nitrilotriacetic acid trihydrazide, citric acid trihydrazide; pyromellitic acid tetrahydrazide, naphthoic acid tetrahydrazide, ethylenediaminetetraacetic acid tetrahydrazide, 1,4 , 5,8-naphthoic acid tetrahydrazide and the like; a low polymer having a carboxylic acid lower alkyl ester group is converted to hydrazine or hydrazine Polyhydrazide such as polyhydrazide obtained by reaction with hydrazine hydrate (hydrazine hydrate); carbonic dihydrazide; bissemicarbazide; diisocyanate such as hexamethylene diisocyanate and isophorone diisocyanate and polyisocyanate compound derived therefrom, N, N-dimethylhydrazine Polyfunctional semicarbazide obtained by excessively reacting N, N-substituted hydrazine and / or the above-exemplified hydrazide, etc .; including a hydrophilic group such as the polyisocyanate compound and polyether polyols or polyethylene glycol monoalkyl ethers An aqueous polyfunctional semicarbazide obtained by excessively reacting any of the above dihydrazides with an isocyanate group in a reaction product with an active hydrogen compound; the polyfunctional semicarbazide and the aqueous multifunctional compound A mixture with active semicarbazide; bisacetyldihydrazone and the like.
[ヒドラジン誘導体(B)の融点を低下させる化合物(C)]
本発明者らは、種々のヒドラジン誘導体(B)を検討した結果、ヒドラジン誘導体(B)がホルムアルデヒドと効率よく反応するためには、その分子内に複数のヒドラジド基を有する化合物が有効であるものの、ヒドラジド誘導体(B)自体の融点は上昇していく傾向にあり、ポリアセタール樹脂(A)の融点よりも高くなることを知見した。さらに、ポリアセタール樹脂(A)の融点とヒドラジン誘導体(B)の融点との差が広がるとモールドデポジットになりやすいことが判明した。そこで、本発明者らは、ヒドラジン誘導体(B)の融点を低下させる化合物に着目した。
ヒドラジン誘導体(B)の融点を低下させる化合物(C)としては、ヒドラジン誘導体(B)への添加により上記融点を低下できるものであれば特に制限はない。その中でも、化合物(C)が、ヒドラジン誘導体(B)とは異なる1種又は2種以上のヒドラジン誘導体であると好ましい。例えば、ヒドラジン誘導体(B)がモノヒドラジドの場合の化合物(C)は、ヒドラジン誘導体(B)とは異なる1種又は2種以上のモノヒドラジド及び/又はジヒドラジド、ヒドラジン誘導体(B)がジヒドラジドの場合の化合物(C)は、ヒドラジン誘導体(B)とは異なる1種又は2種以上のジヒドラジド及び/又はモノヒドラジドがより好ましい。このように、化合物(C)もヒドラジン誘導体であって、それらヒドラジド誘導体(B)と化合物(C)との組合せが、互いに異種の構造を有するヒドラジド誘導体の組合せであると、ヒドラジド誘導体(B)の融点を低下させるのに効果的である。
[Compound (C) that lowers the melting point of the hydrazine derivative (B)]
As a result of studying various hydrazine derivatives (B), the present inventors have found that a compound having a plurality of hydrazide groups in the molecule is effective for the hydrazine derivative (B) to react efficiently with formaldehyde. It has been found that the melting point of the hydrazide derivative (B) itself tends to increase and is higher than the melting point of the polyacetal resin (A). Further, it has been found that mold deposits tend to occur when the difference between the melting point of the polyacetal resin (A) and the melting point of the hydrazine derivative (B) increases. Therefore, the present inventors have focused on compounds that lower the melting point of the hydrazine derivative (B).
The compound (C) that lowers the melting point of the hydrazine derivative (B) is not particularly limited as long as the melting point can be lowered by addition to the hydrazine derivative (B). Among them, the compound (C) is preferably one or more hydrazine derivatives different from the hydrazine derivative (B). For example, when the hydrazine derivative (B) is a monohydrazide, the compound (C) is one or more monohydrazides and / or dihydrazides and / or hydrazine derivatives (B) different from the hydrazine derivative (B). The compound (C) is more preferably one or more dihydrazides and / or monohydrazides different from the hydrazine derivative (B). Thus, when the compound (C) is also a hydrazine derivative, and the combination of the hydrazide derivative (B) and the compound (C) is a combination of hydrazide derivatives having different structures, the hydrazide derivative (B) It is effective in lowering the melting point.
ヒドラジド誘導体(B)と化合物(C)との好ましい組合せは、ジヒドラジド化合物同士の組合せであり、更に好ましいのは、飽和脂肪族カルボン酸ジヒドラジド化合物同士の組合せ、すなわち、ヒドラジン誘導体(B)が飽和脂肪族カルボン酸ジヒドラジドの場合、ヒドラジン誘導体(B)の融点を低下させる化合物(C)として、ヒドラジン誘導体(B)とは異なる飽和脂肪族カルボン酸ジヒドラジドであると更に好ましい。 A preferred combination of the hydrazide derivative (B) and the compound (C) is a combination of dihydrazide compounds, more preferably a combination of saturated aliphatic carboxylic acid dihydrazide compounds, that is, a hydrazine derivative (B) is saturated fat. In the case of the group carboxylic acid dihydrazide, the compound (C) for lowering the melting point of the hydrazine derivative (B) is more preferably a saturated aliphatic carboxylic acid dihydrazide different from the hydrazine derivative (B).
本発明者らが、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)を種々検討した中の例を以下に示す。本発明者らは、種々の2種のカルボン酸ヒドラジドの質量比1:1の混合物を、示差走査熱量計を用いて昇温速度2.5℃/分で加熱して融解し、融解した温度で2分間保持した後に、降温速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で再び昇温した時に、その混合物の融点が、混合前の各々のカルボン酸ヒドラジドの融点とは異なる挙動となることを見出した。 Examples in which the present inventors have studied various compounds (C) that lower the melting point of the hydrazine derivative (B) and the hydrazine derivative (B) are shown below. The present inventors melted a mixture of various two kinds of carboxylic acid hydrazides in a mass ratio of 1: 1 by heating at a heating rate of 2.5 ° C./min using a differential scanning calorimeter, and the melting temperature. At a rate of temperature decrease of 10 ° C./min to 100 ° C. and then heated again at a rate of temperature increase of 2.5 ° C./min. It was found that the behavior differs from the melting point of acid hydrazide.
例えば、テレフタル酸ジヒドラジドを示差走査熱量計(パーキンエルマー社製、商品名「DSC7」)を用いて速度2.5℃/分で昇温すると、324℃に吸熱ピークの頂点が認められた。同様にしてイソフタル酸ジヒドラジドを昇温すると、226℃に吸熱ピークの頂点が認められた。また、アジピン酸ジヒドラジドでは181℃に、セバシン酸ジヒドラジドでは188℃に、ドデカン二酸ジヒドラジドも188℃に、それぞれ吸熱ピークの頂点が認められた。 For example, when terephthalic acid dihydrazide was heated at a rate of 2.5 ° C./min using a differential scanning calorimeter (trade name “DSC7”, manufactured by Perkin Elmer Co., Ltd.), an endothermic peak peak was observed at 324 ° C. Similarly, when isophthalic acid dihydrazide was heated, an endothermic peak was observed at 226 ° C. Further, the peak of the endothermic peak was observed at 181 ° C. for adipic acid dihydrazide, 188 ° C. for sebacic acid dihydrazide, and 188 ° C. for dodecanedioic acid dihydrazide.
さらに、1種のカルボン酸ヒドラジド、あるいは2種のカルボン酸ヒドラジドを質量比1:1で乳鉢に入れ混合及び粉砕して得られる混合物を、示差走査熱量計(パーキンエルマー社製、商品名「DSC7」)を用いて200℃まで昇温速度2.5℃/分で昇温し、200℃で2分間保持した後に、降温速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で昇温して吸熱ピークの頂点を確認することにより融点を測定した。
例えば、アジピン酸ジヒドラジド単体を、上述のようにして示差走査熱量測定に供したしたところ、2つの吸熱ピークが認められ、それらのピークの頂点から176℃と171℃とに融点が認められた。また、各々の吸熱ピークの面積から算出した吸熱容量(以下「ΔH」という)は、それぞれ5.4J/g、229.2J/gであった。それらのΔHの合計量に対する、171℃の融点を示す吸熱ピークのΔHの割合、すなわち、それらの吸熱ピークの総ピーク面積に対する171℃の融点を示す吸熱ピークのピーク面積の割合は、98%であった(図1参照)。また、セバシン酸ジヒドラジド単体を同様に示差走査熱量測定に供したところ、185℃、180℃及び172℃に融点が認められ、各々のΔHは、5.4J/g、32.4J/g及び16.4J/gであった。さらに、それらのΔHの合計量に対するそれぞれの融点を示す吸熱ピークのΔHの割合は、185℃が10%、180℃が60%、172℃が30%であった(図2参照)。同様にしてドデカン二酸ジヒドラジド単体を測定したところ、183℃、177℃及び171℃に融点が認められ、各々のΔHは、2.4J/g、18.1J/g及び32.4J/gであった。さらに、それらのΔHの合計量に対するそれぞれの融点を示す吸熱ピークのΔHの割合は、183℃が5%、177℃が34%、171℃が61%であった。ΔHが最も大きな吸熱ピークの頂点が示す温度を、ここで「融点のメインピーク温度」と呼ぶと、アジピン酸ジヒドラジドの融点のメインピーク温度は171℃、セバシン酸ジヒドラジドの融点のメインピーク温度は180℃、ドデカン二酸ジヒドラジドの融点のメインピーク温度は171℃であった。
Further, a differential scanning calorimeter (trade name “DSC7”, manufactured by Perkin Elmer Co., Ltd.) was obtained by mixing and pulverizing one carboxylic acid hydrazide or two carboxylic acid hydrazides in a mortar at a mass ratio of 1: 1. The temperature is increased to 200 ° C. at a temperature increase rate of 2.5 ° C./min, held at 200 ° C. for 2 minutes, and then the temperature is decreased to 100 ° C. at a temperature decrease rate of 10 ° C./min. The melting point was measured by raising the temperature at 5 ° C./min and confirming the peak of the endothermic peak.
For example, when adipic acid dihydrazide alone was subjected to differential scanning calorimetry as described above, two endothermic peaks were observed, and melting points were observed at 176 ° C. and 171 ° C. from the peaks. The endothermic capacities (hereinafter referred to as “ΔH”) calculated from the areas of the respective endothermic peaks were 5.4 J / g and 229.2 J / g, respectively. The ratio of ΔH of the endothermic peak showing the melting point of 171 ° C. to the total amount of ΔH, that is, the ratio of the peak area of the endothermic peak showing the melting point of 171 ° C. to the total peak area of those endothermic peaks is 98%. (See FIG. 1). Moreover, when the sebacic acid dihydrazide simple substance was similarly subjected to differential scanning calorimetry, melting points were observed at 185 ° C., 180 ° C. and 172 ° C., and each ΔH was 5.4 J / g, 32.4 J / g and 16 4 J / g. Furthermore, the ratio of ΔH of the endothermic peaks indicating the respective melting points with respect to the total amount of ΔH was 10% at 185 ° C., 60% at 180 ° C., and 30% at 172 ° C. (see FIG. 2). Similarly, when dodecanedioic acid dihydrazide alone was measured, melting points were observed at 183 ° C., 177 ° C. and 171 ° C., and ΔH of each was 2.4 J / g, 18.1 J / g and 32.4 J / g. there were. Furthermore, the ratio of ΔH of the endothermic peaks indicating the respective melting points to the total amount of ΔH was 5% at 183 ° C., 34% at 177 ° C., and 61% at 171 ° C. The temperature indicated by the apex of the endothermic peak having the largest ΔH is referred to herein as the “melting point main peak temperature”. C., the main peak temperature of the melting point of dodecanedioic acid dihydrazide was 171.degree.
アジピン酸ジヒドラジドとセバシン酸ジヒドラジドとの質量比1:1の混合物を上述のようにして示差走査熱量測定に供したところ、融点のメインピーク温度は154℃を示し、そこでのΔHは、ΔHの合計量に対して91%であった(図3参照)。アジピン酸ジヒドラジドとドデカン二酸ジヒドラジドとの質量比1:1の混合物の融点のメインピーク温度は151℃を示し、そこでのΔHは、ΔHの合計量に対して98%であった。セバシン酸ジヒドラジドとドデカン二酸ジヒドラジドとの質量比1:1の混合物の融点のメインピーク温度は144℃を示し、そこでのΔHは、ΔHの合計量に対して80%であった。すなわち、それらの混合物では、上記の質量比1:1の混合物を昇温速度2.5℃/分で加熱して融解し、融解した温度で2分間保持した後に、降温速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で昇温した時に、融点(吸熱ピークの頂点)が存在することが分かった。 When a 1: 1 mass ratio mixture of adipic acid dihydrazide and sebacic acid dihydrazide was subjected to differential scanning calorimetry as described above, the main peak temperature of the melting point was 154 ° C., where ΔH was the sum of ΔH It was 91% with respect to the amount (see FIG. 3). The main peak temperature of the melting point of the 1: 1 mass mixture of adipic acid dihydrazide and dodecanedioic acid dihydrazide was 151 ° C., where ΔH was 98% relative to the total amount of ΔH. The main peak temperature of the melting point of the 1: 1 mass ratio mixture of sebacic acid dihydrazide and dodecanedioic acid dihydrazide was 144 ° C., where ΔH was 80% relative to the total amount of ΔH. That is, in those mixtures, the above-mentioned mixture having a mass ratio of 1: 1 is melted by heating at a heating rate of 2.5 ° C./min, held at the melted temperature for 2 minutes, and then at a cooling rate of 10 ° C./min. It was found that when the temperature was lowered to 100 ° C. and then raised at a rate of temperature rise of 2.5 ° C./min, a melting point (the end of the endothermic peak) was present.
一方、セバシン酸ジヒドラジドとイソフタル酸ジヒドラジドとの質量比1:1の混合物を250℃まで昇温速度2.5℃/分で昇温すると181℃に吸熱ピークが認められた。ところが、引き続き250℃で2分間保持した後に、降温速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で250℃まで昇温したところ、融点(吸熱ピーク)が認められず、最初の融解後に結晶化しなかった(図4参照)。同様にしてアジピン酸ジヒドラジドとイソフタル酸ジヒドラジドとの質量比1:1の混合物、アジピン酸ジヒドラジドとテレフタル酸ジヒドラジドとの質量比1:1の混合物、並びに、テレフタル酸ジヒドラジドとイソフタル酸ジヒドラジドとの質量比1:1の混合物を、350℃まで昇温速度2.5℃/分で昇温し、350℃で2分間保持した後に、降温速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で350℃まで昇温したが、いずれも融点(吸熱ピーク)が認められなかった。このことは、上記の混合物を昇温速度2.5℃/分で加熱して融解し、2分間保持した後に、降温速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で昇温した時に融点(吸熱ピーク)が消失したことを示している。 On the other hand, when a mixture of sebacic acid dihydrazide and isophthalic acid dihydrazide in a mass ratio of 1: 1 was heated to 250 ° C. at a heating rate of 2.5 ° C./min, an endothermic peak was observed at 181 ° C. However, after maintaining at 250 ° C. for 2 minutes, the temperature was decreased to 100 ° C. at a temperature decrease rate of 10 ° C./min, and then increased to 250 ° C. at a temperature increase rate of 2.5 ° C./min. Was not observed and did not crystallize after the first melting (see FIG. 4). Similarly, a 1: 1 mass ratio mixture of adipic acid dihydrazide and isophthalic acid dihydrazide, a 1: 1 mass ratio mixture of adipic acid dihydrazide and terephthalic acid dihydrazide, and a mass ratio of terephthalic acid dihydrazide and isophthalic acid dihydrazide The 1: 1 mixture was heated to 350 ° C. at a heating rate of 2.5 ° C./min, held at 350 ° C. for 2 minutes, then cooled to 100 ° C. at a cooling rate of 10 ° C./min, and then heated Although the temperature was raised to 350 ° C. at a rate of 2.5 ° C./min, no melting point (endothermic peak) was observed. This is because the mixture is heated and melted at a heating rate of 2.5 ° C./min, held for 2 minutes, and then cooled to 100 ° C. at a cooling rate of 10 ° C./min. It shows that the melting point (endothermic peak) disappeared when the temperature was raised at 5 ° C./min.
本発明者らが、更に検討を進めたところ、ポリアセタール樹脂(A)と、ヒドラジン誘導体(B)と、ヒドラジン誘導体(B)の融点を低下させる化合物(C)とを含有する原料組成物から得られるポリアセタール樹脂組成物であって、ヒドラジン誘導体(B)と、ヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物が下記式(1)及び(2)で表される条件を満足するものであるポリアセタール樹脂組成物である場合に、エージング後の寸法安定性、エージング後の耐繰り返し衝撃性、リサイクル成形性、金型への充填率が低い条件下での耐モールドデポジット性に優れたポリアセタール樹脂組成物を提供できることを見出した。
T1<T2 (1)
T1<T3 (2)
ここで、式(1)及び(2)中、T1は、示差走査熱量計を用いて上記ヒドラジン誘導体と、ヒドラジン誘導体の融点を低下させる化合物との混合物に対して所定の温度プログラムで加熱及び冷却を施した後に、上記混合物が融解するまで2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T2は、上記示差走査熱量計を用いてヒドラジン誘導体(B)に対して所定の温度プログラムで加熱及び冷却を施した後に、2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T3は、上記示差走査熱量計を用いてポリアセタール樹脂(A)に対して所定の温度プログラムで加熱及び冷却を施した後に、2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)である。また、上述の「所定の温度プログラム」とは、上記混合物又はヒドラジン誘導体(B)の吸熱ピークよりも低い温度から上記混合物又はヒドラジン誘導体(B)が融解する温度まで2.5℃/分の速度で昇温し、次いで、2分間その温度で保持し、その次に、100℃まで10℃/分の降温速度で降温する温度プログラムを意味する。ポリアセタール樹脂(A)の場合、上述の「所定の温度プログラム」とは、ポリアセタール樹脂(A)の吸熱ピークよりも低い温度から200℃まで速度320℃/分で昇温し、200℃で2分間保持した後に、速度10℃/分で100℃まで降温する温度プログラムを意味する。
As a result of further studies by the present inventors, it was obtained from a raw material composition containing a polyacetal resin (A), a hydrazine derivative (B), and a compound (C) that lowers the melting point of the hydrazine derivative (B). The polyacetal resin composition, wherein the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) satisfies the conditions represented by the following formulas (1) and (2) In the case of a polyacetal resin composition, excellent dimensional stability after aging, repeated impact resistance after aging, recycle moldability, and mold deposit resistance under conditions where the filling rate into the mold is low It has been found that a polyacetal resin composition can be provided.
T1 <T2 (1)
T1 <T3 (2)
Here, in the formulas (1) and (2), T1 is heated and cooled with a predetermined temperature program for a mixture of the hydrazine derivative and a compound that lowers the melting point of the hydrazine derivative using a differential scanning calorimeter. Among the endothermic peaks obtained when the temperature is increased at a rate of 2.5 ° C./min until the mixture is melted, the temperature (° C.) indicating the peak of the endothermic peak having the largest endothermic capacity, T2 is an endothermic peak obtained when the hydrazine derivative (B) is heated and cooled with a predetermined temperature program using the differential scanning calorimeter and then heated at a rate of 2.5 ° C./min. Among these, the temperature (° C.) indicating the peak of the endothermic peak having the largest endothermic capacity, and T3 is heated and cooled with a predetermined temperature program for the polyacetal resin (A) using the differential scanning calorimeter. After performing, among endothermic peaks obtained when temperature was raised at 2.5 ° C. / min, the temperature (℃) endothermic capacity indicating the vertex of the largest endothermic peak. The above-mentioned “predetermined temperature program” means a rate of 2.5 ° C./min from a temperature lower than the endothermic peak of the mixture or hydrazine derivative (B) to a temperature at which the mixture or hydrazine derivative (B) melts. Temperature program, and then held at that temperature for 2 minutes, and then lowered to 100 ° C. at a rate of temperature decrease of 10 ° C./min. In the case of the polyacetal resin (A), the above-mentioned “predetermined temperature program” means that the temperature is raised from a temperature lower than the endothermic peak of the polyacetal resin (A) to 200 ° C. at a rate of 320 ° C./min, and at 200 ° C. for 2 minutes. It means a temperature program that lowers the temperature to 100 ° C. at a rate of 10 ° C./min after being held.
上記検討から好ましいヒドラジン誘導体(B)としては、飽和脂肪族カルボン酸ヒドラジドであり、具体的には、コハク酸モノヒドラジド、グルタル酸モノヒドラジド、アジピン酸モノヒドラジド、ピメリン酸モノヒドラジド、スペリン酸モノヒドラジド、アゼライン酸モノヒドラジド、セバシン酸モノヒドラジド等のカルボン酸モノヒドラジド、コハク酸ジヒドラジド、グルタル酸ジヒドラジド、アジピン酸ジヒドラジド、ピメリン酸ジヒドラジド、スペリン酸ジヒドラジド、アゼライン酸ジヒドラジド、セバシン酸ジヒドラジド、ドデカン二酸ジヒドラジド等のカルボン酸ジヒドラジドである。 Preferred hydrazine derivatives (B) from the above studies are saturated aliphatic carboxylic acid hydrazides, specifically, succinic acid monohydrazide, glutaric acid monohydrazide, adipic acid monohydrazide, pimelic acid monohydrazide, and speric acid monohydrazide. Carboxylic acid monohydrazide such as azelaic acid monohydrazide and sebacic acid monohydrazide, succinic acid dihydrazide, glutaric acid dihydrazide, adipic acid dihydrazide, pimelic acid dihydrazide, speric acid dihydrazide, azelaic acid dihydrazide, sebacic acid dihydrazide, etc. The carboxylic acid dihydrazide.
飽和脂肪族カルボン酸ヒドラジドが、下記一般式(3)で表される飽和脂肪族カルボン酸ジヒドラジドを含むとより好ましい。
ヒドラジン誘導体(B)の融点を低下させる化合物(C)としては、上述のとおり、ヒドラジン誘導体(B)への添加により上記融点を低下できるものであれば特に制限はない。その中でも、好ましくは、ヒドラジン誘導体(B)が飽和脂肪族カルボン酸ヒドラジドの場合の化合物(C)は、ヒドラジン誘導体(B)とは異なる1種又は2種以上の飽和脂肪族カルボン酸ヒドラジドである。ヒドラジン誘導体(B)が飽和脂肪族カルボン酸ジヒドラジドの場合の化合物は(C)は、好ましくは、ヒドラジン誘導体(B)とは異なる1種又は2種以上の飽和脂肪族カルボン酸ジヒドラジド及び/又は飽和脂肪族カルボン酸であり、これらはヒドラジン誘導体(B)の融点を低下させるのに効果的である。 The compound (C) that lowers the melting point of the hydrazine derivative (B) is not particularly limited as long as it can lower the melting point by addition to the hydrazine derivative (B) as described above. Among them, the compound (C) when the hydrazine derivative (B) is a saturated aliphatic carboxylic acid hydrazide is preferably one or more saturated aliphatic carboxylic acid hydrazides different from the hydrazine derivative (B). . When the hydrazine derivative (B) is a saturated aliphatic carboxylic acid dihydrazide, the compound (C) is preferably one or more saturated aliphatic carboxylic acid dihydrazides and / or saturated different from the hydrazine derivative (B). Aliphatic carboxylic acids, which are effective in lowering the melting point of the hydrazine derivative (B).
より具体的な例としては、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とが、アジピン酸ジヒドラジド、セバシン酸ジヒドラジド及びドデカン二酸ジヒドラジドからなる群より選ばれる互いに異なるカルボン酸ジヒドラジドを含むと好ましい。例えば、ヒドラジン誘導体(B)がアジピン酸ジヒドラジドの場合、化合物(C)は、セバシン酸ジヒドラジド及び/又はドデカン二酸ジヒドラジドであり、ヒドラジン誘導体(B)がセバシン酸ジヒドラジドの場合、化合物(C)は、アジピン酸ジヒドラジド及び/又はドデカン二酸ジヒドラジドであると好ましい。エージング後の寸法安定性、エージング後の耐繰り返し衝撃性、リサイクル成形性、耐熱水性、金型への充填率が低い条件下での耐モールドデポジット性の観点から詳細に見ると、ヒドラジン誘導体(B)と化合物(C)との質量比1:1の混合物のΔHが最も大きなメインピーク面積が、全ピークのΔHの95%未満であるものが特に優れる。そのようなヒドラジン誘導体(B)と化合物(C)との組合せとしては、ヒドラジン誘導体(B)としてアジピン酸ジヒドラジド、化合物(C)としてセバシン酸ジヒドラジドの組合せ、ヒドラジン誘導体(B)としてセバシン酸ジヒドラジド、化合物(C)としてドデカン二酸ジヒドラジドの組合せが好ましい。 As a more specific example, the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are selected from the group consisting of adipic acid dihydrazide, sebacic acid dihydrazide, and dodecanedioic acid dihydrazide. It is preferable to include different carboxylic acid dihydrazides. For example, when the hydrazine derivative (B) is adipic acid dihydrazide, the compound (C) is sebacic acid dihydrazide and / or dodecanedioic acid dihydrazide, and when the hydrazine derivative (B) is sebacic acid dihydrazide, the compound (C) is Adipic acid dihydrazide and / or dodecanedioic acid dihydrazide is preferable. From the viewpoints of dimensional stability after aging, repeated impact resistance after aging, recycle moldability, hot water resistance, and mold deposit resistance under low mold filling conditions, hydrazine derivatives (B ) And the compound (C) having a mass ratio of 1: 1, the main peak area having the largest ΔH is less than 95% of the ΔH of all the peaks. As a combination of such a hydrazine derivative (B) and compound (C), adipic acid dihydrazide as hydrazine derivative (B), a combination of sebacic acid dihydrazide as compound (C), sebacic acid dihydrazide as hydrazine derivative (B), A combination of dodecanedioic acid dihydrazide is preferred as the compound (C).
また、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との含有比((B):(C))が、質量基準で2:8〜8:2であると好ましく、より好ましくは3:7〜7:3である。その含有比が、上記範囲内にあることにより、混合物の固化物について、メインピーク温度がポリアセタール樹脂(A)の融点よりも低下する傾向にある。 The content ratio ((B) :( C)) of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) is from 2: 8 to 8: 2 on a mass basis. Preferably, it is 3: 7-7: 3. When the content ratio is within the above range, the main peak temperature tends to be lower than the melting point of the polyacetal resin (A) for the solidified product of the mixture.
また、本実施形態のポリアセタール樹脂組成物を得るための原料組成物におけるヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との合計の含有割合は、ポリアセタール樹脂100質量部に対して0.03〜0.2質量部であると好ましく、より好ましくは0.04〜0.2質量部であり、更に好ましくは0.05〜0.2質量部である。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との合計の含有割合が0.03質量部未満であると、リサイクル成形時のホルムアルデヒド放出量が増加する傾向にあり、0.2質量部よりも多いと、金型への充填率が低い条件下での耐モールドデポジット性と、エージング後の耐繰り返し衝撃性とが低下する傾向にある。 The total content of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) in the raw material composition for obtaining the polyacetal resin composition of the present embodiment is 100 mass of the polyacetal resin. It is preferable that it is 0.03-0.2 mass part with respect to a part, More preferably, it is 0.04-0.2 mass part, More preferably, it is 0.05-0.2 mass part. If the total content of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) is less than 0.03 parts by mass, the amount of formaldehyde released during recycle molding tends to increase. If the amount is more than 0.2 parts by mass, the mold deposit resistance under conditions where the filling rate into the mold is low and the repeated impact resistance after aging tend to be lowered.
[ポリアセタール樹脂組成物の製造方法]
本実施形態のポリアセタール樹脂組成物の製造方法は、その第1の態様として、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物を調製する第1の工程と、第1の工程を経て得られた混合物をポリアセタール樹脂(A)と溶融混練する第2の工程と、を含む製造方法である。上記混合物は、上記式(1)及び(2)で表される条件を満足するものである。
[Production Method of Polyacetal Resin Composition]
As a first aspect of the method for producing a polyacetal resin composition of the present embodiment, a first step of preparing a mixture of a hydrazine derivative (B) and a compound (C) that lowers the melting point of the hydrazine derivative (B). And a second step of melt-kneading the mixture obtained through the first step with the polyacetal resin (A). The mixture satisfies the conditions represented by the above formulas (1) and (2).
この第1の態様の製造方法は、具体的には、まず、第1の工程において、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とをヘンシェルミキサー、タンブラー、V字型ブレンダー等で混合する。次いで、第2の工程において、ポリアセタール樹脂(A)と、第1の工程を経て得られたヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物とをそれぞれ定量フィーダーなどにより1軸又は多軸混錬押出機等に供給し、そこで溶融混錬する。あるいは、第2の工程において、ポリアセタール樹脂(A)と、第1の工程を経て得られたヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物とをヘンシェルミキサー、タンブラー、V字型ブレンダー等で混合した後、得られた混合物を定量フィーダーなどで1軸又は多軸混錬押出機等に供給し、そこで溶融混錬する。第2の工程としては、上述の2つのうちのいずれかが好ましく、それらの中でも、減圧装置を備えた2軸混練押出機を用いる工程が特に好ましい。上述の第1及び第2の工程を経て、本実施形態に係るポリアセタール樹脂組成物が得られる。 Specifically, in the production method of the first aspect, first, in the first step, a hydrazine derivative (B) and a compound (C) that lowers the melting point of the hydrazine derivative (B) are mixed with a Henschel mixer, a tumbler, Mix with a V-shaped blender. Next, in the second step, a polyacetal resin (A) and a mixture of a hydrazine derivative (B) obtained through the first step and a compound (C) that lowers the melting point of the hydrazine derivative (B), respectively. It is supplied to a single-screw or multi-screw kneading extruder or the like by a quantitative feeder or the like and melted and kneaded there. Alternatively, in the second step, the polyacetal resin (A) and a mixture of the hydrazine derivative (B) obtained through the first step and the compound (C) that lowers the melting point of the hydrazine derivative (B) are Henschel. After mixing with a mixer, tumbler, V-shaped blender or the like, the obtained mixture is supplied to a single-screw or multi-screw kneading extruder or the like with a quantitative feeder or the like, and melt kneaded there. As the second step, one of the above-mentioned two is preferable, and among them, a step using a twin-screw kneading extruder equipped with a decompression device is particularly preferable. Through the first and second steps described above, the polyacetal resin composition according to this embodiment is obtained.
この態様の製造方法は、上述の第1の工程を経て得られたヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物を、第2の工程に供する前に加熱手段を用いて溶融する第3の工程を有してもよい。この場合、第2の工程では、例えば、第3の工程を経て得られた溶融混合物を、液体用ポンプを用いて押出機に添加し、溶融したポリアセタール樹脂(A)と混練することも可能である。 In the production method of this embodiment, the mixture of the hydrazine derivative (B) obtained through the first step and the compound (C) that lowers the melting point of the hydrazine derivative (B) is subjected to the second step. There may be a third step of melting using a heating means. In this case, in the second step, for example, the molten mixture obtained through the third step can be added to the extruder using a liquid pump and kneaded with the molten polyacetal resin (A). is there.
本実施形態のポリアセタール樹脂組成物の製造方法は、その第2の態様として、ポリアセタール樹脂(A)の一部とヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを混合して予備混合物を得る第1の工程と、第1の工程を経て得られた予備混合物を残りのポリアセタール樹脂(A)と溶融混練する第2の工程と、を含む製造方法である。ここで、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物は、上記式(1)及び(2)で表される条件を満足するものである。 The method for producing the polyacetal resin composition of the present embodiment includes, as a second aspect, a part of the polyacetal resin (A), a hydrazine derivative (B), and a compound (C) that lowers the melting point of the hydrazine derivative (B). Is a production method including a first step of obtaining a premix by mixing and a second step of melt kneading the premix obtained through the first step with the remaining polyacetal resin (A). Here, the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) satisfies the conditions represented by the above formulas (1) and (2).
この第2の態様の製造方法において、第1の工程における具体的な混合方法は、混合対象となる成分にポリアセタール樹脂(A)の一部をも含む他は、上記第1の態様と同様である。また、第2の工程における具体的な溶融混練方法としては、第1の工程を経て得られたポリアセタール樹脂(A)の一部とヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との予備混合物と、残りのポリアセタール樹脂(A)とを、それぞれ定量フィーダーなどで1軸又は多軸混錬押出機等に供給し、そこで溶融混錬する。あるいは、第2の工程において、ポリアセタール樹脂(A)の一部とヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との予備混合物を押出機のサイドから供給し、溶融した残りのポリアセタール樹脂(A)と溶融混練する。第2の工程としては、上述の2つのうちのいずれかが好ましく、それらの中でも、減圧装置を備えた2軸混練押出機を用いる工程が特に好ましい。 In the manufacturing method of the second aspect, the specific mixing method in the first step is the same as the first aspect except that the component to be mixed also includes a part of the polyacetal resin (A). is there. Moreover, as a specific melt-kneading method in the second step, the melting point of the polyacetal resin (A) obtained through the first step, the hydrazine derivative (B), and the hydrazine derivative (B) is lowered. The preliminary mixture with the compound (C) and the remaining polyacetal resin (A) are respectively supplied to a single-screw or multi-screw kneading extruder or the like with a quantitative feeder or the like, and melt kneaded there. Alternatively, in the second step, a premix of a part of the polyacetal resin (A), the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) is supplied from the side of the extruder, Melt and knead with the remaining melted polyacetal resin (A). As the second step, one of the above-mentioned two is preferable, and among them, a step using a twin-screw kneading extruder equipped with a decompression device is particularly preferable.
また、上記第2の態様の第1の工程において、ポリアセタール樹脂(A)の一部とヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを含む高濃度マスターバッチを予備混合物として作製してもよい。この場合、第2の工程において、押出溶融混練時又は射出成形時にその高濃度マスターバッチを残りのポリアセタール樹脂(A)で希釈してもよく、これによっても本実施形態に係るポリアセタール樹脂組成物が得られる。高濃度のマスターバッチにおいて、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との総量の含有割合は、0.1〜50質量%であると好ましい。 Further, in the first step of the second aspect, a high-concentration masterbatch comprising a part of the polyacetal resin (A), a hydrazine derivative (B), and a compound (C) that lowers the melting point of the hydrazine derivative (B). May be made as a premix. In this case, in the second step, the high-concentration master batch may be diluted with the remaining polyacetal resin (A) at the time of extrusion melt-kneading or injection molding, and thereby the polyacetal resin composition according to this embodiment can be diluted. can get. In the high-concentration masterbatch, the content ratio of the total amount of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) is preferably 0.1 to 50% by mass.
この態様の製造方法は、上述の第1の工程を経て得られたヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との予備混合物を、第2の工程に供する前に加熱手段を用いて溶融する第3の工程を有してもよい。この場合、第2の工程では、例えば、第3の工程を経て得られた溶融混合物を、溶融した残りのポリアセタール樹脂(A)と混練することも可能である。 In the production method of this aspect, a premix of the hydrazine derivative (B) obtained through the first step and the compound (C) that lowers the melting point of the hydrazine derivative (B) is used for the second step. You may have a 3rd process melted previously using a heating means. In this case, in the second step, for example, the molten mixture obtained through the third step can be kneaded with the remaining melted polyacetal resin (A).
第2の態様において、第1の工程を経て得られた予備混合物と残りのポリアセタール樹脂(A)とを第2の工程で溶融混練する場合、第1の工程で用いるポリアセタール樹脂と第2の工程で用いられる残りのポリアセタール樹脂との比率は、1:45〜1:5であることが好ましい。上記比率をこの範囲内に調整することにより、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混練不足を抑制する傾向がある。 In the second aspect, when the preliminary mixture obtained through the first step and the remaining polyacetal resin (A) are melt-kneaded in the second step, the polyacetal resin used in the first step and the second step The ratio with respect to the remaining polyacetal resin used in is preferably 1:45 to 1: 5. By adjusting the ratio within this range, there is a tendency to suppress kneading shortage between the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B).
本実施形態のポリアセタール樹脂組成物の製造方法では、少なくともヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを予め混合した後に、ポリアセタール樹脂と溶融混合(混練)することが必要である。 In the method for producing a polyacetal resin composition of the present embodiment, at least a hydrazine derivative (B) and a compound (C) that lowers the melting point of the hydrazine derivative (B) are mixed in advance and then melt-mixed (kneaded) with the polyacetal resin. It is necessary.
[添加剤]
本実施形態により製造されるポリアセタール樹脂組成物には、用途に応じて適当な添加剤を配合することができる。具体的には、添加剤として、酸化防止剤、ホルムアルデヒド反応性窒素を有する重合体又は化合物、蟻酸捕捉剤、離型剤等が挙げられる。
なお、ポリアセタール樹脂組成物における各添加剤の配合量は、ポリアセタール樹脂100質量部に対して、好ましくは0.001〜0.8質量部、更に好ましくは0.01〜0.7質量部である。
本実施形態の製造方法において、添加剤は、第1、第2及び第3の工程のいずれか1つ又は2つ以上の工程において添加されてもよく、それらの各工程の間で添加されてもよい。
[Additive]
A suitable additive can be mix | blended with the polyacetal resin composition manufactured by this embodiment according to a use. Specific examples of the additive include an antioxidant, a polymer or compound having formaldehyde-reactive nitrogen, a formic acid scavenger, and a mold release agent.
In addition, the compounding quantity of each additive in a polyacetal resin composition becomes like this. Preferably it is 0.001-0.8 mass part with respect to 100 mass parts of polyacetal resin, More preferably, it is 0.01-0.7 mass part. .
In the production method of the present embodiment, the additive may be added in any one or more of the first, second and third steps, and is added between these steps. Also good.
[酸化防止剤]
酸化防止剤としてはヒンダートフェノール系酸化防止剤が好ましい。酸化防止剤としては、例えば、n−オクタデシル−3−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)−プロピオネート、n−オクタデシル−3−(3’−メチル−5’−t−ブチル−4’−ヒドロキシフェニル)−プロピオネート、n−テトラデシル−3−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)−プロピオネート、1,6−ヘキサンジオール−ビス−[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)−プロピオネート]、1,4−ブタンジオール−ビス−[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)−プロピオネート]、トリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]、ペンタエリスリトールテトラキス[メチレン−3−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)プロピオネート]メタンが挙げられる。これらの中で好ましい酸化防止剤は、トリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]及びペンタエリスリトールテトラキス[メチレン−3−(3’,5’−ジ−t−ブチル−4’−ヒドロキシフェニル)プロピオネート]メタンである。これらの酸化防止剤は1種を単独で用いられてもよいし、2種以上を組み合わせて用いられてもよい。
[Antioxidant]
As the antioxidant, a hindered phenol antioxidant is preferable. Examples of the antioxidant include n-octadecyl-3- (3 ′, 5′-di-t-butyl-4′-hydroxyphenyl) -propionate, n-octadecyl-3- (3′-methyl-5 ′). -T-butyl-4'-hydroxyphenyl) -propionate, n-tetradecyl-3- (3 ', 5'-di-t-butyl-4'-hydroxyphenyl) -propionate, 1,6-hexanediol-bis -[3- (3,5-di-tert-butyl-4-hydroxyphenyl) -propionate], 1,4-butanediol-bis- [3- (3,5-di-tert-butyl-4-hydroxy Phenyl) -propionate], triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate], pentaerythritol tetrakis [me Ren-3- (3 ', 5'-di -t- butyl-4'-hydroxyphenyl) propionate], and methane. Among these, preferred antioxidants are triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] and pentaerythritol tetrakis [methylene-3- (3 ′ , 5′-di-t-butyl-4′-hydroxyphenyl) propionate] methane. These antioxidants may be used individually by 1 type, and may be used in combination of 2 or more type.
[ホルムアルデヒド反応性窒素を有する重合体又は化合物]
ホルムアルデヒド反応性窒素を有する重合体又は化合物は、ホルムアルデヒドと反応可能な窒素原子を分子内に有する重合体又は化合物(単量体)であり、その具体例としては、ナイロン4−6、ナイロン6、ナイロン6−6、ナイロン6−10、ナイロン6−12、ナイロン12等のポリアミド樹脂、及びこれらの重合体、例えば、ナイロン6/6−6/6−10、ナイロン6/6−12が挙げられる。また、ホルムアルデヒド反応性窒素を有する重合体又は化合物として、アクリルアミド及びその誘導体、アクリルアミド及びその誘導体と他のビニルモノマーとの共重合体が挙げられる。より具体的には、アクリルアミド及びその誘導体と他のビニルモノマーとを金属アルコラートの存在下で重合して得られたポリ−β−アラニン共重合体が挙げられる。さらに、ホルムアルデヒド反応性窒素を有する重合体又は化合物として、アミド化合物、アミノ置換トリアジン化合物、アミノ置換トリアジン化合物とホルムアルデヒドとの付加物、アミノ置換トリアジン化合物とホルムアルデヒドとの縮合物、尿素、尿素誘導体、イミダゾール化合物、イミド化合物も挙げられる。
[Polymer or compound having formaldehyde-reactive nitrogen]
The polymer or compound having formaldehyde-reactive nitrogen is a polymer or compound (monomer) having a nitrogen atom capable of reacting with formaldehyde in the molecule. Specific examples thereof include nylon 4-6,
アミド化合物の具体例としては、イソフタル酸ジアミドなどの多価カルボン酸アミド、アントラニルアミドが挙げられる。アミノ置換トリアジン化合物の具体例としては、2,4−ジアミノ−sym−トリアジン、2,4,6−トリアミノ−sym−トリアジン、N−ブチルメラミン、N−フェニルメラミン、N,N−ジフェニルメラミン、N,N−ジアリルメラミン、ベンゾグアナミン(2,4−ジアミノ−6−フェニル−sym−トリアジン)、アセトグアナミン(2,4−ジアミノ−6−メチル−sym−トリアジン)、2,4−ジアミノ−6−ブチル−sym−トリアジンが挙げられる。アミノ置換トリアジン化合物とホルムアルデヒドとの付加物の具体例としては、N−メチロールメラミン、N,N’−ジメチロールメラミン、N,N’,N”−トリメチロールメラミンが挙げられる。アミノ置換トリアジン化合物とホルムアルデヒドとの縮合物の具体例としては、メラミン・ホルムアルデヒド縮合物が挙げられる。尿素誘導体としては、例えば、N−置換尿素、尿素縮合体、エチレン尿素、ヒダントイン化合物、ウレイド化合物が挙げられる。N−置換尿素の具体例としては、アルキル基等の置換基が置換したメチル尿素、アルキレンビス尿素、アリール置換尿素が挙げられる。尿素縮合体の具体例としては、尿素とホルムアルデヒドとの縮合体が挙げられる。ヒダントイン化合物の具体例としては、ヒダントイン、5,5−ジメチルヒダントイン、5,5−ジフェニルヒダントインが挙げられる。ウレイド化合物の具体例としては、アラントインが挙げられる。イミド化合物の具体例としてはスクシンイミド、グルタルイミド、フタルイミドが挙げられる。 Specific examples of the amide compound include polycarboxylic acid amides such as isophthalic acid diamide and anthranilamides. Specific examples of the amino-substituted triazine compound include 2,4-diamino-sym-triazine, 2,4,6-triamino-sym-triazine, N-butylmelamine, N-phenylmelamine, N, N-diphenylmelamine, N , N-diallylmelamine, benzoguanamine (2,4-diamino-6-phenyl-sym-triazine), acetoguanamine (2,4-diamino-6-methyl-sym-triazine), 2,4-diamino-6-butyl -Sym-triazine is mentioned. Specific examples of the adduct of an amino-substituted triazine compound and formaldehyde include N-methylol melamine, N, N′-dimethylol melamine, and N, N ′, N ″ -trimethylol melamine. Specific examples of condensates with formaldehyde include melamine / formaldehyde condensates, and examples of urea derivatives include N-substituted urea, urea condensates, ethylene urea, hydantoin compounds, and ureido compounds. Specific examples of the substituted urea include methylurea, alkylenebisurea, and aryl-substituted urea substituted with a substituent such as an alkyl group, etc. Specific examples of the urea condensate include a condensate of urea and formaldehyde. Specific examples of hydantoin compounds include hydantoin, 5, 5 Dimethylhydantoin, specific examples of the 5,5-diphenylhydantoin and the like. Ureido compounds, specific examples of allantoin and the like. Imide compound succinimide, glutarimide, and phthalimide.
これらのホルムアルデヒド反応性窒素原子を有する重合体又は化合物は、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。 These polymers or compounds having formaldehyde-reactive nitrogen atoms may be used alone or in combination of two or more.
[蟻酸捕捉剤]
蟻酸捕捉剤は蟻酸を効率的に中和し得るものであり、例えば、上記のアミノ置換トリアジン化合物、アミノ置換トリアジン化合物とホルムアルデヒドとの縮合物、例えば、メラミン・ホルムアルデヒド縮合物が挙げられる。
[Formic acid scavenger]
The formic acid scavenger is capable of efficiently neutralizing formic acid, and examples thereof include the above-mentioned amino-substituted triazine compounds, condensates of amino-substituted triazine compounds and formaldehyde, such as melamine / formaldehyde condensates.
また、蟻酸捕捉剤として、アルカリ金属又はアルカリ土類金属の水酸化物、無機酸塩、カルボン酸塩又はアルコキシドが挙げられる。例えば、ナトリウム、カリウム、マグネシウム、カルシウム若しくはバリウムなどの金属の水酸化物、上記金属の炭酸塩、リン酸塩、珪酸塩、ホウ酸塩、カルボン酸塩が挙げられる。上記カルボン酸塩のカルボン酸としては、10〜36個の炭素原子を有する飽和又は不飽和脂肪族カルボン酸が好ましく、これらのカルボン酸は水素原子を水酸基で置換されていてもよい。飽和又は不飽和脂肪族カルボン酸塩の具体的な例としては、ジミリスチン酸カルシウム、ジパルミチン酸カルシウム、ジステアリン酸カルシウム、(ミリスチン酸−パルミチン酸)カルシウム、(ミリスチン酸−ステアリン酸)カルシウム、(パルミチン酸−ステアリン酸)カルシウムが挙げられる。これらの中でも好ましくは、ジパルミチン酸カルシウム、ジステアリン酸カルシウム、珪酸マグネシウムである。 Examples of the formic acid scavenger include alkali metal or alkaline earth metal hydroxides, inorganic acid salts, carboxylate salts, and alkoxides. Examples thereof include metal hydroxides such as sodium, potassium, magnesium, calcium, and barium, carbonates, phosphates, silicates, borates, and carboxylates of the above metals. The carboxylic acid of the carboxylate is preferably a saturated or unsaturated aliphatic carboxylic acid having 10 to 36 carbon atoms, and these carboxylic acids may have a hydrogen atom substituted with a hydroxyl group. Specific examples of saturated or unsaturated aliphatic carboxylates include calcium dimyristate, calcium dipalmitate, calcium distearate, (myristic acid-palmitic acid) calcium, (myristic acid-stearic acid) calcium, ( Palmitic acid-stearic acid) calcium. Among these, calcium dipalmitate, calcium distearate, and magnesium silicate are preferable.
[離型剤]
離型剤としては、アルコール、脂肪酸及びそれらの脂肪酸エステルが好ましく用いられるが、特に好ましい離型剤としては、エチレングリコールジステアレートが挙げられる。
[Release agent]
As the releasing agent, alcohol, fatty acid and fatty acid ester thereof are preferably used, and particularly preferable releasing agent includes ethylene glycol distearate.
[その他の添加剤]
本実施形態で製造されるポリアセタール樹脂組成物には、本発明の目的を損なわない範囲で、更に適当な公知の添加剤を必要に応じて配合することができる。具体的には、無機充填剤、結晶核剤、導電材、熱可塑性樹脂及び熱可塑性エラストマー、顔料が挙げられる。
[Other additives]
In the polyacetal resin composition produced in the present embodiment, a suitable known additive can be further blended as necessary within a range not impairing the object of the present invention. Specific examples include inorganic fillers, crystal nucleating agents, conductive materials, thermoplastic resins and thermoplastic elastomers, and pigments.
[無機充填剤]
無機充填剤としては、繊維状、粉粒子状、板状及び中空状の無機充填剤が挙げられる。繊維状無機充填剤としては、例えば、ガラス繊維、炭素繊維、シリコーン繊維、シリカ・アルミナ繊維、ジルコニア繊維、窒化硼素繊維、窒化硅素繊維、硼素繊維、チタン酸カリウム繊維、ステンレス、アルミニウム、チタン、銅、真鍮などの金属繊維等の無機質繊維が挙げられる。また、繊維長の短いチタン酸カリウムウイスカー、酸化亜鉛ウイスカー等のウイスカー類も繊維状無機充填剤として例示される。
[Inorganic filler]
Examples of inorganic fillers include fibrous, powder particle, plate and hollow inorganic fillers. Examples of the fibrous inorganic filler include glass fiber, carbon fiber, silicone fiber, silica / alumina fiber, zirconia fiber, boron nitride fiber, silicon nitride fiber, boron fiber, potassium titanate fiber, stainless steel, aluminum, titanium, copper And inorganic fibers such as metal fibers such as brass. In addition, whiskers such as potassium titanate whisker and zinc oxide whisker having a short fiber length are also exemplified as fibrous inorganic fillers.
粉粒子状無機充填剤としては、例えば、カーボンブラック、シリカ、石英粉末、ガラスビーズ、ガラス粉、珪酸カルシウム、珪酸マグネシウム、珪酸アルミニウム、カオリン、クレー、珪藻土、ウォラストナイトのような珪酸塩、酸化鉄、酸化チタン、アルミナのような金属酸化物、硫酸カルシウム、硫酸バリウムのような金属硫酸塩、炭酸マグネシウム、ドロマイト等の炭酸塩、その他炭化珪素、窒化硅素、窒化硼素、各種金属粉末が挙げられる。 Examples of the powdered inorganic filler include, for example, carbon black, silica, quartz powder, glass beads, glass powder, calcium silicate, magnesium silicate, aluminum silicate, kaolin, clay, diatomaceous earth, wollastonite silicate, oxidation Metal oxides such as iron, titanium oxide, and alumina, metal sulfates such as calcium sulfate and barium sulfate, carbonates such as magnesium carbonate and dolomite, other silicon carbide, silicon nitride, boron nitride, and various metal powders .
板状無機充填剤としては、例えば、マイカ、ガラスフレーク、各種金属箔が挙げられる。中空状無機充填剤としては、ガラスバルーン、シリカバルーン、シラスバルーン、金属バルーンが挙げられる。これらの無機充填剤は、1種を単独で又は2種以上を組み合わせて用いられる。これらの無機充填剤は表面処理を施されていても施されていなくてもよいが、成形表面の平滑性、機械的特性の観点から表面処理を施されたものが好ましい場合がある。無機充填剤の表面処理に用いられる表面処理剤としては従来公知のものが使用可能である。表面処理剤としては、例えば、シラン系、チタネート系、アルミニウム系、ジルコニウム系等の各種カップリング処理剤が挙げられる。より具体的には、表面処理剤として、N−(2−アミノエチル)−3−アミノプロピルトリエトキシシラン、3−グリシドキシプロピルトリメトキシシラン、イソプロピルトリスステアロイルチタネート、ジイソプロポキシアンモニウムエチルアセテート、n−ブチルジルコネートが挙げられる。 Examples of the plate-like inorganic filler include mica, glass flakes, and various metal foils. Examples of the hollow inorganic filler include glass balloons, silica balloons, shirasu balloons, and metal balloons. These inorganic fillers are used alone or in combination of two or more. These inorganic fillers may or may not be subjected to a surface treatment, but those subjected to a surface treatment may be preferable from the viewpoint of the smoothness of the molding surface and mechanical properties. A conventionally well-known thing can be used as a surface treating agent used for the surface treatment of an inorganic filler. Examples of the surface treatment agent include various coupling treatment agents such as silane, titanate, aluminum, and zirconium. More specifically, as a surface treatment agent, N- (2-aminoethyl) -3-aminopropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, isopropyltristearoyl titanate, diisopropoxyammonium ethyl acetate, n-Butyl zirconate is mentioned.
なお、無機充填剤に加えて/代えて、芳香族ポリアミド樹脂、フッ素樹脂、アクリル樹脂等の高融点有機繊維状物質が用いられてもよい。 In addition to / in place of the inorganic filler, a high melting point organic fibrous material such as an aromatic polyamide resin, a fluororesin, or an acrylic resin may be used.
[導電剤]
導電剤としては、例えば、導電性カーボンブラック、金属粉末又は繊維が挙げられる。
[Conductive agent]
Examples of the conductive agent include conductive carbon black, metal powder, or fiber.
[熱可塑性樹脂及び熱可塑性エラストマー]
熱可塑性樹脂としては、例えば、ポリオレフィン樹脂、アクリル樹脂、スチレン樹脂、ポリカーネート樹脂、未硬化のエポキシ樹脂が挙げられる。また、これらの樹脂の変性物も熱可塑性樹脂に含まれる。熱可塑性エラストマーとしては、例えば、ポリウレタン系エラストマー、ポリエステル系エラストマー、ポリスチレン系エラストマー、ポリアミド系エラストマーが挙げられる。
[Thermoplastic resin and thermoplastic elastomer]
Examples of the thermoplastic resin include polyolefin resin, acrylic resin, styrene resin, polycarbonate resin, and uncured epoxy resin. In addition, modified products of these resins are also included in the thermoplastic resin. Examples of the thermoplastic elastomer include polyurethane elastomers, polyester elastomers, polystyrene elastomers, and polyamide elastomers.
[顔料]
顔料としては、無機系顔料及び有機系顔料、メタリック系顔料、蛍光顔料が挙げられる。無機系顔料とは樹脂の着色用として一般的に使用されているものをいい、例えば、硫化亜鉛、酸化チタン、硫酸バリウム、チタンイエロー、コバルトブルー、燃成顔料、炭酸塩、りん酸塩、酢酸塩、カーボンブラック、アセチレンブラック、ランプブラックが挙げられる。有機系顔料としては、例えば、縮合アゾ系、キノン系、フタロシアニン系、モノアゾ系、ジアゾ系、ポリアゾ系、アンスラキノン系、複素環系、ペリノン系、キナクリドン系、チオインジコ系、ペリレン系、ジオキサジン系の顔料が挙げられる。
[Pigment]
Examples of the pigment include inorganic pigments, organic pigments, metallic pigments, and fluorescent pigments. Inorganic pigments are those commonly used for resin coloring, such as zinc sulfide, titanium oxide, barium sulfate, titanium yellow, cobalt blue, combustion pigments, carbonates, phosphates, acetic acid. Examples include salt, carbon black, acetylene black, and lamp black. Examples of organic pigments include condensed azo, quinone, phthalocyanine, monoazo, diazo, polyazo, anthraquinone, heterocyclic, perinone, quinacridone, thioindico, perylene, and dioxazine. Pigments.
[ポリアセタール樹脂組成物の成形方法]
本実施形態により製造されたポリアセタール樹脂組成物を成形する方法は特に制限されるものではない。よって、公知の成形方法、例えば、押出成形、射出成形、真空成形、ブロー成形、射出圧縮成形、加飾成形、他材質成形、ガスアシスト射出成形、発砲射出成形、低圧成形、超薄肉射出成形(超高速射出成形)、金型内複合成形(インサート成形、アウトサート成形)等の成形方法のいずれかによってポリアセタール樹脂組成物を成形することができる。
[Molding method of polyacetal resin composition]
The method for molding the polyacetal resin composition produced according to this embodiment is not particularly limited. Therefore, known molding methods, such as extrusion molding, injection molding, vacuum molding, blow molding, injection compression molding, decorative molding, other material molding, gas assist injection molding, foam injection molding, low pressure molding, ultra-thin injection molding. The polyacetal resin composition can be molded by any one of molding methods such as (ultra-high speed injection molding) and in-mold composite molding (insert molding, outsert molding).
[用途]
本実施形態に係るポリアセタール樹脂組成物を成形して得られる成形品は、成形リサイクル性に優れるため、様々な用途の成形品に用いることが可能である。そのような成形品としては、例えば、ギア、カム、スライダー、レバー、アーム、クラッチ、フェルトクラッチ、アイドラギアー、プーリー、ローラー、コロ、キーステム、キートップ、シャッター、リール、シャフト、関節、軸、軸受け、及びガイド等に代表される機構部品、アウトサート成形の樹脂部品、インサート成形の樹脂部品、シャーシ、トレー、側板、プリンター及び複写機に代表されるオフィスオートメーション機器用部品、VTR(Video Tape Recorder)、ビデオムービー、デジタルビデオカメラ、カメラ及び、デジタルカメラに代表されるカメラ、又はビデオ機器用部品、カセットプレイヤー、DAT、LD(Laser Disk)、MD(Mini Disk)、CD(Compact Disk:CD−ROM(Read Only Memory)、CD−R(Recordable)、CD−RW(Rewritable)を含む)、DVD(Digital Video Disk:DVD−ROM、DVD−R、DVD+R、DVD−RW、DVD+RW、DVD−R DL、DVD+R DL、DVD−RAM(Random Access Memory)、DVD−Audioを含む)、Blu−ray Disc、HD−DVD、その他光デイスクドライブ、MFD、MO、ナビゲーションシステム及びモバイルパーソナルコンピュータに代表される音楽、映像又は情報機器、携帯電話及びファクシミリに代表される通信機器用部品、電気機器用部品、電子機器用部品が挙げられる。また、本実施形態に係る成形品として自動車用の部品も挙げられ、例えば、ガソリンタンク、フュエルポンプモジュール、バルブ類、ガソリンタンクフランジ等に代表される燃料廻り部品、ドアロック、ドアハンドル、ウインドウレギュレータ、スピーカーグリル等に代表されるドア廻り部品、シートベルト用スリップリング、プレスボタン等に代表されるシートベルト周辺部品、コンビスイッチ部品、スイッチ類、及びクリップ類の部品が挙げられる。さらには、本実施形態に係る成形品として、例えば、シャープペンシルのペン先及び、シャープペンシルの芯を出し入れする機構部品、洗面台及び、排水口及び、排水栓開閉機構部品、自動販売機の開閉部ロック機構及び、商品排出機構部品、衣料用のコードストッパー、アジャスター、及びボタン、散水用のノズル、及び散水ホース接続ジョイント、階段手すり部、及び、床材の支持具である建築用品、使い捨てカメラ、玩具、ファスナー、チェーン、コンベア、バックル、スポーツ用品、自動販売機、家具、楽器及び、住宅設備機器に代表される工業部品が挙げられる。その中でも、特に自動車用の内装・機構部品、例えば、ドア、サンルーフ、シートベルト、スイッチ、クリップ、シート及びワイパーが好適であり、より具体的には、インサイド・ハンドル/ベース、キャリアプレート、ウィンドウレギュレーター・プーリー、ドアラッチ部品、スピーカーグリル、サンルーフ部品、プレスボタン、リトラクター部品、シートベルトアジャスタ、ステアリング・コラム、レバー・コントロール、クラスタークリップ、ECUケース、カーテンエアバッグ・クリップ、アシストグリップ・クリップ、スピンドルナット、シートアジャスタ部品、ランバー・サポート、モーターギア部品に好適である。ただし、成形品はこれらに限定されない。
[Usage]
Since a molded product obtained by molding the polyacetal resin composition according to the present embodiment is excellent in molding recyclability, it can be used for molded products for various applications. Examples of such molded products include gears, cams, sliders, levers, arms, clutches, felt clutches, idler gears, pulleys, rollers, rollers, key stems, key tops, shutters, reels, shafts, joints, shafts, bearings. , And mechanical parts such as guides, resin parts for outsert molding, resin parts for insert molding, chassis, trays, side plates, parts for office automation equipment such as printers and copiers, VTR (Video Tape Recorder) , Video movie, digital video camera, camera and camera represented by digital camera, or parts for video equipment, cassette player, DAT, LD (Laser Disk), MD (Mini Disk), CD (Compact Disk: C) -ROM (Read Only Memory), CD-R (Recordable), CD-RW (including Rewriteable), DVD (Digital Video Disk): DVD-ROM, DVD-R, DVD + R, DVD-RW, DVD + RW, DVD-R DL, DVD + R DL, DVD-RAM (including Random Access Memory), DVD-Audio), Blu-ray Disc, HD-DVD, other optical disk drives, MFD, MO, navigation systems, and music represented by mobile personal computers , Parts for communication equipment represented by video or information equipment, mobile phones and facsimiles, parts for electrical equipment, and parts for electronic equipment. Also, automobile parts can be cited as molded articles according to the present embodiment. For example, fuel-related parts such as gasoline tanks, fuel pump modules, valves, gasoline tank flanges, door locks, door handles, window regulators. And door belt parts represented by speaker grills, seat belt slip rings, seat belt peripheral parts represented by press buttons, combination switch parts, switches, and clips. Furthermore, as a molded article according to the present embodiment, for example, a mechanical pencil pen tip and a mechanical part for inserting and removing a mechanical pencil core, a wash basin, a drain outlet, a drain plug opening / closing mechanism part, and a vending machine opening / closing Part locking mechanism, product discharge mechanism parts, cord stopper for clothing, adjuster, and button, nozzle for watering, sprinkling hose connection joint, stair handrail, and building article as a support for flooring, disposable camera , Toys, fasteners, chains, conveyors, buckles, sporting goods, vending machines, furniture, musical instruments, and industrial parts represented by housing equipment. Among them, particularly interior and mechanism parts for automobiles, such as doors, sunroofs, seat belts, switches, clips, seats and wipers are suitable, and more specifically, inside handles / bases, carrier plates, window regulators.・ Pulleys, door latch parts, speaker grills, sunroof parts, press buttons, retractor parts, seat belt adjusters, steering columns, lever controls, cluster clips, ECU cases, curtain airbag clips, assist grip clips, spindle nuts Suitable for seat adjuster parts, lumbar supports, and motor gear parts. However, the molded product is not limited to these.
本実施形態により製造されるポリアセタール樹脂組成物は、特にエージング後の耐繰り返し衝撃性、及びリサイクル成形性に優れた樹脂組成物である。 The polyacetal resin composition produced according to this embodiment is a resin composition that is particularly excellent in repeated impact resistance after aging and recycle moldability.
以下、実施例及び比較例によって本発明をより具体的に説明するが、本発明はこれらによって何ら限定されるものではない。なお、各物性の測定法は下記のとおりである。 EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention more concretely, this invention is not limited at all by these. In addition, the measuring method of each physical property is as follows.
〈エージング後の寸法安定性(2次収縮性)の測定〉
後述のポリアセタール樹脂組成物を射出成形機(住友重機工業株式会社製、商品名「SH−75」)を用いて、シリンダー温度を200℃、金型温度を40℃に設定し、射出圧力70MPa、射出時間60秒、冷却時間15秒の射出条件で成形して、ポリアセタール樹脂成形品として評価用ISOダンベルを得た。成形完了後、23℃、湿度50%の環境下に上記ダンベルを48時間放置した後の流動方向の寸法をD1(mm)とし、成形完了後、23℃、湿度50%の環境下に72時間放置した後、さらに120℃で48時間加熱し、その後23℃で湿度50%の環境下に48時間放置した後の流動方向の寸法をD2(mm)として、下記式(4)にしたがい2次収縮率を求めた。
2次収縮率(%)=(D1−D2)/金型寸法×100 (4)
<Measurement of dimensional stability (secondary shrinkage) after aging>
Using a polyacetal resin composition described later using an injection molding machine (trade name “SH-75” manufactured by Sumitomo Heavy Industries, Ltd.), the cylinder temperature was set to 200 ° C., the mold temperature was set to 40 ° C., and the injection pressure was 70 MPa. Molding was performed under injection conditions of an injection time of 60 seconds and a cooling time of 15 seconds to obtain an evaluation ISO dumbbell as a polyacetal resin molded product. After completion of molding, the dimension in the flow direction after leaving the dumbbell for 48 hours in an environment of 23 ° C. and 50% humidity is D1 (mm), and after completion of molding, it is 72 hours in an environment of 23 ° C. and 50% humidity. After allowing to stand, the sample is further heated at 120 ° C. for 48 hours and then left at 23 ° C. in an environment of 50% humidity for 48 hours, where D2 (mm) is the dimension in the flow direction. Shrinkage was determined.
Secondary shrinkage (%) = (D1-D2) / die size × 100 (4)
〈エージング後の耐繰り返し衝撃性の測定〉
上述のようにして得た評価用ISOダンベルを、160℃に設定されたギアーオーブンに吊るし、240時間加熱した。その後、ギアーオーブンから上記ダンベルを取り出し、23℃で50%の湿度に保たれた恒温室で24時間放置した。上記ダンベルを長さ80mm、幅10mm、厚み4mmの長板状に切削し、長さ方向の中心部にノッチ(先端R=0.25mm、ノッチ幅=8mm、ノッチ深さ=2mm)を形成して試験片を得た。得られた試験片を、図5の符号3に示すように耐繰り返し衝撃性測定装置(東洋精機製作所製、商品名「AT繰り返し衝撃試験機」)にセットし、符号7に示すように160gの重りをセットし、20mmの高さから落下させて試験片に衝突させることにより繰り返し衝撃を与え、試験片が破壊されるまでの衝撃(衝突)回数を測定した。破壊までの衝撃回数が多いほど耐繰り返し衝撃性に優れる。なお、図5中、符号1はプリセットカウンター、符号2は落下高さ調整ボルト、符号3は試験片、符号4はガイド板、符号5はガイド棒、符号6はガイド棒押工、符号7は重り、符号8はツメ、符号9はストッパー、符号10は速度調整ツマミをそれぞれ示す。
<Measurement of repeated impact resistance after aging>
The evaluation ISO dumbbell obtained as described above was suspended in a gear oven set at 160 ° C. and heated for 240 hours. Thereafter, the dumbbell was taken out from the gear oven and left for 24 hours in a temperature-controlled room maintained at 23 ° C. and 50% humidity. The dumbbell is cut into a long plate shape having a length of 80 mm, a width of 10 mm, and a thickness of 4 mm, and a notch (tip R = 0.25 mm, notch width = 8 mm, notch depth = 2 mm) is formed at the center in the length direction. A test piece was obtained. The obtained test piece was set in a repeated impact resistance measuring device (trade name “AT repeated impact tester” manufactured by Toyo Seiki Seisakusho) as shown by
〈リサイクル成形性の評価〉
射出成形機(住友重機工業株式会社製、商品名「SH−75」)を用いて、シリンダー温度を205℃、金型温度を70℃に設定し、射出圧力70MPa、射出時間60秒、冷却時間15秒の射出条件で、後述のポリアセタール樹脂組成物から所定の試験片を成形した。得られた試験片をV型粉砕機で粉砕処理し、その粉砕品を再度成形して成形品を得ることによりリサイクル成形性テストを行った。繰り返し成形回数5回の成形品、及び繰り返し成形回数10回の成形品からのホルムアルデヒド放出量(mg/kg)を導出した。導出方法を下記に示す。
<Evaluation of recyclability>
Using an injection molding machine (trade name “SH-75” manufactured by Sumitomo Heavy Industries, Ltd.), the cylinder temperature is set to 205 ° C., the mold temperature is set to 70 ° C., the injection pressure is 70 MPa, the injection time is 60 seconds, and the cooling time is set. A predetermined test piece was molded from a polyacetal resin composition described later under an injection condition of 15 seconds. The obtained test piece was pulverized with a V-type pulverizer, and the pulverized product was molded again to obtain a molded product. The amount of formaldehyde released (mg / kg) was derived from a molded product with 5 repeated moldings and a molded product with 10 repeated moldings. The derivation method is shown below.
上記成形品をV型粉砕機で粉砕処理し、その粉砕品を、射出成形機(住友重機工業株式会社製、商品名「SH−75」)を用いて、シリンダー温度:220℃、射出圧力:(1次圧力/2次圧力=63.7MPa/50.0MPa)、射出時間:15秒、冷却時間:20秒、金型温度:77℃の条件で成形して試験片を得た。得られた試験片から放出されるホルムアルデヒドを、下記VDA275法により測定し、成形品から放出されるホルムアルデヒドとしてその量を求めた。 The molded product was pulverized with a V-type pulverizer, and the pulverized product was subjected to an injection molding machine (manufactured by Sumitomo Heavy Industries, Ltd., trade name “SH-75”), cylinder temperature: 220 ° C., injection pressure: (Primary pressure / secondary pressure = 63.7 MPa / 50.0 MPa), injection time: 15 seconds, cooling time: 20 seconds, mold temperature: 77 ° C. Molding was performed to obtain a test piece. The formaldehyde released from the obtained test piece was measured by the following VDA275 method, and the amount was determined as formaldehyde released from the molded product.
VDA275法では、まず、ポリエチレン容器に蒸留水50mLと規定されたサイズの試験片(縦100mm×横40mm×厚み3mm)とを収容して密閉した。次いで、60℃で3時間容器を加熱後、蒸留水中のホルムアルデヒドをアンモニウムイオン存在下においてアセチルアセトンと反応させ、その反応物を対象としてUV分光計にて波長412nmの吸収ピークを測定し、ホルムアルデヒド放出量(mg/kg)を求めた。
In the VDA275 method, first, 50 mL of distilled water and a test piece of a specified size (
〈耐モールドデポジット(MD)性の評価〉
射出成形機(東芝機械株式会社製、商品名「IS−100GN」)を用いて、シリンダー温度を170℃、金型温度を60℃に設定し、射出圧力60MPa、射出時間60秒、冷却時間15秒の射出条件で、後述のポリアセタール樹脂組成物から厚さ2mm、幅80mm×80mmのシボ付平板の試験片をショートショット、すなわち金型内に樹脂組成物を完全に充填させない条件にて成形した。この試験片の質量は、金型内に樹脂組成物を完全に充填させて得られる試験片の95質量%であった。本条件で試験片を300ショット成形した後の金型内のモールドデポジット(MD)を目視にて観察した。「A」は、MDが認められないことを示し、「B」は、うっすらとMDが認められることを示し、「C」は、明らかな析出物が認められることを示す。この評価が「A」、「B」、「C」の順で、耐MD性が優れることを示す。
<Evaluation of resistance to mold deposit (MD)>
Using an injection molding machine (trade name “IS-100GN” manufactured by Toshiba Machine Co., Ltd.), the cylinder temperature is set to 170 ° C., the mold temperature is set to 60 ° C., the injection pressure is 60 MPa, the injection time is 60 seconds, and the cooling time is 15 A test piece of a flat plate with a thickness of 2 mm and a width of 80 mm × 80 mm was molded from a polyacetal resin composition described below under short injection conditions, that is, a condition in which the resin composition was not completely filled in the mold. . The mass of this test piece was 95% by mass of the test piece obtained by completely filling the resin composition in the mold. The mold deposit (MD) in the mold after 300 shots of the test piece were molded under these conditions was visually observed. “A” indicates that MD is not observed, “B” indicates that MD is slightly observed, and “C” indicates that obvious precipitate is observed. This evaluation shows that MD resistance is excellent in the order of “A”, “B”, and “C”.
[ポリアセタール樹脂組成物]
実施例、比較例において、ポリアセタール樹脂組成物に含有される成分には下記のものを用いた。
[Polyacetal resin composition]
In Examples and Comparative Examples, the following components were used as components contained in the polyacetal resin composition.
〈ポリアセタール樹脂(a−1)〉
熱媒を通すことができるジャケット付きの2軸セルフクリーニングタイプの重合機(L/D=8)を80℃に調整した。次いで、トリオキサンを4kg/hr、コモノマーとして1,3−ジオキソランを42.8g/hr(トリオキサン1molに対して、0.039mol)、連鎖移動剤としてメチラール(水分量1.3%、メタノール量0.99%)をトリオキサン1molに対して1.50×10-3molにて連続的に添加した。さらに、重合触媒として三フッ化ホウ素ジ−n−ブチルエーテラートをトリオキサン1molに対して1.5×10-5molにて連続的に添加し重合を行った。重合機より排出されたポリアセタールコポリマーをトリエチルアミン0.1%水溶液中に投入し重合触媒の失活を行った。重合触媒が失活したポリアセタールコポリマーを遠心分離機でろ過して分離回収した後、ポリアセタールコポリマー100質量部に対して、第4級アンモニウム化合物として水酸化コリン蟻酸塩(トリエチル−2−ヒドロキシエチルアンモニウムフォルメート)を含有した水溶液1質量部を添加して、均一に混合し、さらに120℃で乾燥した。水酸化コリン蟻酸塩の添加量の調節は、添加する水酸化コリン蟻酸塩を含有した水溶液中の水酸化コリン蟻酸塩の濃度を調整することにより行った。上記式(8)で表される水酸化コリン蟻酸塩由来の窒素の量に換算して20質量ppmとなる量の水酸化コリン蟻酸塩を添加した。乾燥後のポリアセタールコポリマーをベント付き2軸スクリュー式押出機に供給し、押出機中で溶融しているポリアセタールコポリマー100質量部に対して水を0.5質量部添加し、押出機設定温度200℃、押出機における滞留時間7分間で不安定末端部の分解除去処理を行った。不安定末端部が分解されたポリアセタールコポリマーは、ベント真空度20Torrの条件下で脱揮され、押出機ダイス部よりストランドとして押し出され、ペレット化した。こうして、ペレット化したポリアセタール樹脂(a−1)を得た。得られたポリアセタール樹脂(a−1)のメルトインデックスをASTM−D1238に準じて測定したところ、190℃、2169gの条件下で9g/10分であった(メルトインデックスの測定は以下同様。)。また、ポリアセタール樹脂(a−1)について、示唆走査熱量計(パーキンエルマー社製、商品名「DSC7」)を用いて200℃まで速度320℃/分で昇温し、200℃で2分間保持した後に、速度10℃/分で100℃まで降温し、その後、昇温速度2.5℃/分で測定した融点(以下同様。)は165℃であった。
<Polyacetal resin (a-1)>
A biaxial self-cleaning type polymerization machine (L / D = 8) with a jacket capable of passing a heat medium was adjusted to 80 ° C. Then, 4 kg / hr of trioxane, 42.8 g / hr of 1,3-dioxolane as a comonomer (0.039 mol with respect to 1 mol of trioxane), methylal as a chain transfer agent (water content 1.3%, methanol amount 0. 99%) was continuously added at 1.50 × 10 −3 mol with respect to 1 mol of trioxane. Furthermore, polymerization was carried out by continuously adding boron trifluoride di-n-butyl etherate as a polymerization catalyst at 1.5 × 10 −5 mol with respect to 1 mol of trioxane. The polyacetal copolymer discharged from the polymerization machine was put into a 0.1% aqueous solution of triethylamine to deactivate the polymerization catalyst. The polyacetal copolymer in which the polymerization catalyst has been deactivated is separated and recovered by filtration with a centrifugal separator. Then, 100 parts by mass of the polyacetal copolymer is choline hydroxide formate (triethyl-2-hydroxyethylammonium formaldehyde) as a quaternary ammonium compound. 1 part by weight of an aqueous solution containing a mate) was added, mixed uniformly, and further dried at 120 ° C. The addition amount of the hydroxycholine formate was adjusted by adjusting the concentration of the hydroxycholine formate in the aqueous solution containing the added choline formate. An amount of choline formate in an amount of 20 mass ppm in terms of the amount of nitrogen derived from choline formate represented by the above formula (8) was added. The dried polyacetal copolymer is supplied to a vented twin screw extruder, 0.5 parts by mass of water is added to 100 parts by mass of the polyacetal copolymer melted in the extruder, and the extruder set temperature is 200 ° C. Then, the unstable end portion was decomposed and removed in a residence time of 7 minutes in the extruder. The polyacetal copolymer in which the unstable terminal portion was decomposed was devolatilized under a condition of a vent vacuum of 20 Torr, extruded as a strand from the extruder die portion, and pelletized. Thus, a pelletized polyacetal resin (a-1) was obtained. When the melt index of the obtained polyacetal resin (a-1) was measured according to ASTM-D1238, it was 9 g / 10 min under the conditions of 190 ° C. and 2169 g (the measurement of the melt index is the same hereinafter). Further, the polyacetal resin (a-1) was heated up to 200 ° C. at a rate of 320 ° C./min using a suggested scanning calorimeter (trade name “DSC7”, manufactured by Perkin Elmer Co., Ltd.) and held at 200 ° C. for 2 minutes. Later, the temperature was decreased to 100 ° C. at a rate of 10 ° C./min, and then the melting point (hereinafter the same) measured at a rate of temperature increase of 2.5 ° C./min was 165 ° C.
〈ポリアセタール樹脂(a−2)〉
メルトインデックスが40g/10分になるように連鎖移動剤のメチラールの量を変更した以外はポリアセタール樹脂(a−1)と同様にして、ポリアセタール樹脂(a−2)を得た。その融点は165℃であった。
<Polyacetal resin (a-2)>
A polyacetal resin (a-2) was obtained in the same manner as the polyacetal resin (a-1) except that the amount of methylal of the chain transfer agent was changed so that the melt index was 40 g / 10 minutes. Its melting point was 165 ° C.
〈ポリアセタール樹脂(a−3)〉
熱媒を通すことができるジャケット付きの2軸セルフクリーニングタイプの重合機(L/D=8)を80℃に調整し、トリオキサンを4kg/hr、コモノマーとして1,3−ジオキソランを14.3g/hr(トリオキサン1molに対して、0.0013mol)、連鎖移動剤としてメチラール(水分量1.3%、メタノール量0.99%)をトリオキサン1molに対して0.18×10-3mol、連続的に添加した。さらに重合触媒として三フッ化硼素ジ−n−ブチルエーテラートをトリオキサン1molに対して1.5×10-5molで連続的に添加し重合を行った。重合機より排出されたポリアセタールコポリマーをトリエチルアミン0.1%水溶液中に投入し重合触媒の失活を行った。重合触媒が失活したポリアセタールコポリマーを遠心分離機でろ過して分離回収した後、ポリアセタールコポリマー100質量部に対して、第4級アンモニウム化合物として水酸化コリン蟻酸塩(トリエチル−2−ヒドロキシエチルアンモニウムフォルメート)を含有した水溶液1質量部を添加して、均一に混合した後、120℃で乾燥した。水酸化コリン蟻酸塩の添加量の調節は、添加する水酸化コリン蟻酸塩を含有した水溶液中の水酸化コリン蟻酸塩の濃度を調整することにより行った。上記式(8)で表される水酸化コリン蟻酸塩由来の窒素の量に換算して20質量ppmとなる量の水酸化コリン蟻酸塩を添加した。乾燥後のポリアセタールコポリマーをベント付き2軸スクリュー式押出機に供給し、押出機中で溶融しているポリアセタールコポリマー100質量部に対して水を0.5質量部添加し、押出機設定温度200℃、押出機における滞留時間7分間で不安定末端部の分解除去を行った。不安定末端部が分解されたポリアセタールコポリマーは、ベント真空度20Torrの条件下で脱揮され、押出機ダイス部よりストランドとして押し出され、ペレット化した。このようにして得られたポリアセタール樹脂(a−3)の融点は169.5℃であった。
<Polyacetal resin (a-3)>
A twin-screw self-cleaning type polymerization machine (L / D = 8) with a jacket through which a heat medium can pass is adjusted to 80 ° C., 4 kg / hr of trioxane, and 14.3 g / l of 1,3-dioxolane as a comonomer hr (0.0013 mol with respect to 1 mol of trioxane), methylal (water content 1.3%, methanol amount 0.99%) as a chain transfer agent, 0.18 × 10 −3 mol, continuously with respect to 1 mol of trioxane Added to. Further, boron trifluoride di-n-butyl etherate was continuously added as a polymerization catalyst at 1.5 × 10 −5 mol with respect to 1 mol of trioxane to carry out polymerization. The polyacetal copolymer discharged from the polymerization machine was put into a 0.1% aqueous solution of triethylamine to deactivate the polymerization catalyst. The polyacetal copolymer in which the polymerization catalyst has been deactivated is separated and recovered by filtration with a centrifugal separator. Then, 100 parts by mass of the polyacetal copolymer is choline hydroxide formate (triethyl-2-hydroxyethylammonium formaldehyde) as a quaternary ammonium compound. 1 part by mass of an aqueous solution containing a mate) was added and mixed uniformly, and then dried at 120 ° C. The addition amount of the hydroxycholine formate was adjusted by adjusting the concentration of the hydroxycholine formate in the aqueous solution containing the added choline formate. An amount of choline formate in an amount of 20 mass ppm in terms of the amount of nitrogen derived from choline formate represented by the above formula (8) was added. The dried polyacetal copolymer is supplied to a vented twin screw extruder, 0.5 parts by mass of water is added to 100 parts by mass of the polyacetal copolymer melted in the extruder, and the extruder set temperature is 200 ° C. The unstable end portion was decomposed and removed in a residence time of 7 minutes in the extruder. The polyacetal copolymer in which the unstable terminal portion was decomposed was devolatilized under a condition of a vent vacuum of 20 Torr, extruded as a strand from the extruder die portion, and pelletized. The polyacetal resin (a-3) thus obtained had a melting point of 169.5 ° C.
〈ヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)〉
カルボン酸ヒドラジド(bc−1)としてアジピン酸ジヒドラジドを、カルボン酸ヒドラジド(bc−2)としてセバシン酸ジヒドラジドを、カルボン酸ヒドラジド(bc−3)としてドデカン二酸ジヒドラジドを、カルボン酸ヒドラジド(bc−4)としてイソフタル酸ジヒドラジドを、カルボン酸ヒドラジド(bc−5)としてテレフタル酸ジヒドラジドをそれぞれ準備した。これらを、ヒドラジン誘導体(B)及び/又はヒドラジン誘導体(B)の融点を低下させる化合物(C)として用いた。
<Hydrazine derivative (B) and compound (C) which lowers melting point of hydrazine derivative (B)>
Adipic acid dihydrazide as carboxylic acid hydrazide (bc-1), sebacic acid dihydrazide as carboxylic acid hydrazide (bc-2), dodecanedioic acid dihydrazide as carboxylic acid hydrazide (bc-3), and carboxylic acid hydrazide (bc-4) ) And isophthalic acid dihydrazide as carboxylic acid hydrazide (bc-5). These were used as the compound (C) that lowers the melting point of the hydrazine derivative (B) and / or the hydrazine derivative (B).
また、示差走査熱量計(パーキンエルマー社製、商品名「DSC7」)を用いて上記のカルボン酸ヒドラジド単体に対して所定の温度プログラムで加熱及び冷却を施した後に、2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(融点のメインピーク温度)(℃)を測定した。ここで、上述の「所定の温度プログラム」とは、上記化合物の吸熱ピークよりも低い温度から上記化合物が融解する温度まで2.5℃/分の速度で昇温し、次いで、2分間その温度で保持し、その次に、100℃まで10℃/分の降温速度で降温する温度プログラムを意味する。結果を表1に示す。 Further, after heating and cooling the carboxylic acid hydrazide alone with a predetermined temperature program using a differential scanning calorimeter (trade name “DSC7”, manufactured by Perkin Elmer), 2.5 ° C./min Of the endothermic peaks obtained when the temperature was increased at a rate, the temperature (the main peak temperature of the melting point) (° C.) indicating the peak of the endothermic peak having the largest endothermic capacity was measured. Here, the above-mentioned “predetermined temperature program” means that the temperature is raised at a rate of 2.5 ° C./min from a temperature lower than the endothermic peak of the compound to a temperature at which the compound melts, and then the temperature is maintained for 2 minutes. And then the temperature is lowered to 100 ° C. at a temperature lowering rate of 10 ° C./min. The results are shown in Table 1.
〈酸化防止剤(D)〉
酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]を準備した。
<Antioxidant (D)>
Triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] was prepared as an antioxidant (d).
〈蟻酸捕捉剤(E)〉
蟻酸捕捉剤(e−1)としてジステアリン酸カルシウムを準備し、蟻酸捕捉剤(e−2)として珪酸マグネシウムを準備した。
<Formic acid scavenger (E)>
Calcium distearate was prepared as the formic acid scavenger (e-1), and magnesium silicate was prepared as the formic acid scavenger (e-2).
〈離型剤(F)〉
離型剤(f)としてエチレングリコールジステアレートを準備した。
<Release agent (F)>
Ethylene glycol distearate was prepared as a release agent (f).
〈ホルムアルデヒド反応性窒素を有する重合体又は化合物(G)〉
ホルムアルデヒド反応性窒素を有する重合体(g)としてナイロン6−6を準備した。
<Polymer or compound (G) having formaldehyde-reactive nitrogen>
Nylon 6-6 was prepared as a polymer (g) having formaldehyde-reactive nitrogen.
[ベント付2軸押出機]
実施例、比較例において、ベント付2軸押出機として東芝機械社製TEM26SSを用いた。
[Two-screw extruder with vent]
In Examples and Comparative Examples, TEM26SS manufactured by Toshiba Machine Co. was used as a twin screw extruder with a vent.
[実施例1〜14]
表2に示した割合で、カルボン酸ヒドラジド(bc−1)、(bc−2)及び(bc−3)から選ばれたヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)をタンブラーで混合して混合物を得た。次いで、ポリアセタール樹脂(a−1)、(a−2)又は(a−3)100質量部と上記混合物とを、表2に示した割合でベント付2軸押出機にそれぞれ定量フィーダーを用いて供給し、バレル温度200℃、吐出量20kg/hrにて溶融混練することによりポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて、上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。
また、各実施例で用いたヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物を上述の示差走査熱量測定に供した際の融点のメインピーク温度を表2に示した。
[Examples 1 to 14]
Compounds that lower the melting point of hydrazine derivatives (B) and hydrazine derivatives (B) selected from carboxylic acid hydrazides (bc-1), (bc-2) and (bc-3) at the ratios shown in Table 2 ( C) was mixed with a tumbler to obtain a mixture. Next, 100 parts by mass of the polyacetal resin (a-1), (a-2) or (a-3) and the above mixture were respectively used in a biaxial extruder with a vent at a ratio shown in Table 2 using a quantitative feeder. The mixture was melt kneaded at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr to produce polyacetal resin composition pellets. About the obtained pellet, the measurement of the dimensional stability after aging, the measurement of the impact resistance after aging, the evaluation of recycle moldability, and the evaluation of MD resistance were performed as described above.
The main peak temperature of the melting point when the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) used in each example was subjected to the above-mentioned differential scanning calorimetry is shown. It was shown in 2.
[実施例15]
ポリアセタール樹脂(a−3)100質量部に、酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]0.3質量部を添加して、タンブラーで混合し、ポリアセタール樹脂混合物を得た。また、表2に示した割合で、ヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)をタンブラーで混合して混合物を得た。この混合物と上記ポリアセタール樹脂混合物とを、ベント付2軸押出機にそれぞれ定量フィーダーを用いて供給し、バレル温度200℃、吐出量20kg/hrにて溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて、上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 15]
To 100 parts by mass of polyacetal resin (a-3), triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] 0.3 as an antioxidant (d) Mass parts were added and mixed with a tumbler to obtain a polyacetal resin mixture. Moreover, the compound (C) which lowers | hangs melting | fusing point of a hydrazine derivative (B) and a hydrazine derivative (B) in the ratio shown in Table 2 was mixed with the tumbler, and the mixture was obtained. This mixture and the polyacetal resin mixture are respectively fed to a vented twin screw extruder using a quantitative feeder, and melt kneaded at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr. Pellets were produced. About the obtained pellet, the measurement of the dimensional stability after aging, the measurement of the impact resistance after aging, the evaluation of recycle moldability, and the evaluation of MD resistance were performed as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例16]
ポリアセタール樹脂(a−3)100質量部に、酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]0.3質量部と、蟻酸捕捉剤(e−1)としてジステアリン酸カルシウム0.15質量部とを添加して、タンブラーで混合し、ポリアセタール樹脂混合物を得た。また、表2に示した割合で、ヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)をタンブラーで混合して混合物を得た。この混合物と上記ポリアセタール樹脂混合物とを実施例15と同様にして溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて、上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 16]
To 100 parts by mass of polyacetal resin (a-3), triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] 0.3 as an antioxidant (d) Mass part and 0.15 part by mass of calcium distearate as formic acid scavenger (e-1) were added and mixed with a tumbler to obtain a polyacetal resin mixture. Moreover, the compound (C) which lowers | hangs melting | fusing point of a hydrazine derivative (B) and a hydrazine derivative (B) in the ratio shown in Table 2 was mixed with the tumbler, and the mixture was obtained. The mixture and the polyacetal resin mixture were melt-kneaded in the same manner as in Example 15 to produce polyacetal resin composition pellets. About the obtained pellet, the measurement of the dimensional stability after aging, the measurement of the impact resistance after aging, the evaluation of recycle moldability, and the evaluation of MD resistance were performed as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例17]
ポリアセタール樹脂(a−3)100質量部に、酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]0.3質量部と、蟻酸捕捉剤(e−1)としてジステアリン酸カルシウム0.15質量部と、離型剤(f)としてエチレングリコールジステアレート0.03質量部とを添加して、タンブラーで混合し、ポリアセタール樹脂混合物を得た。また、表2に示した割合で、ヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)をタンブラーで混合して混合物を得た。この混合物と上記ポリアセタール樹脂混合物とを実施例15と同様にして溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて、上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 17]
To 100 parts by mass of polyacetal resin (a-3), triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] 0.3 as an antioxidant (d) Add 0.15 parts by mass of calcium distearate as a formic acid scavenger (e-1) and 0.03 parts by mass of ethylene glycol distearate as a mold release agent (f) and mix with a tumbler. A polyacetal resin mixture was obtained. Moreover, the compound (C) which lowers | hangs melting | fusing point of a hydrazine derivative (B) and a hydrazine derivative (B) in the ratio shown in Table 2 was mixed with the tumbler, and the mixture was obtained. The mixture and the polyacetal resin mixture were melt-kneaded in the same manner as in Example 15 to produce polyacetal resin composition pellets. About the obtained pellet, the measurement of the dimensional stability after aging, the measurement of the impact resistance after aging, the evaluation of recycle moldability, and the evaluation of MD resistance were performed as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例18]
ポリアセタール樹脂(a−3)100質量部に、酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]0.3質量部と、蟻酸捕捉剤(e−1)としてジステアリン酸カルシウム0.15質量部と、離型剤(f)としてエチレングリコールジステアレート0.03質量部と、ホルムアルデヒド反応性窒素を有する重合体(g)としてナイロン6−6 0.05質量部とを添加して、タンブラーで混合し、ポリアセタール樹脂混合物を得た。また、表2に示した割合で、ヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)をタンブラーで混合して混合物を得た。この混合物と上記ポリアセタール樹脂混合物とを実施例15と同様にして溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 18]
To 100 parts by mass of polyacetal resin (a-3), triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] 0.3 as an antioxidant (d) Polymer having 0.15 parts by mass of calcium distearate as a formic acid scavenger (e-1), 0.03 parts by mass of ethylene glycol distearate as a release agent (f), and formaldehyde-reactive nitrogen As (g), 0.05-6 parts by mass of nylon 6-6 was added and mixed with a tumbler to obtain a polyacetal resin mixture. Moreover, the compound (C) which lowers | hangs melting | fusing point of a hydrazine derivative (B) and a hydrazine derivative (B) in the ratio shown in Table 2 was mixed with the tumbler, and the mixture was obtained. The mixture and the polyacetal resin mixture were melt-kneaded in the same manner as in Example 15 to produce polyacetal resin composition pellets. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例19]
ポリアセタール樹脂(a−3)100質量部に、酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]0.3質量部と、蟻酸捕捉剤(e−2)として珪酸マグネシウム0.01質量部と、離型剤(f)としてエチレングリコールジステアレート0.03質量部と、ホルムアルデヒド反応性窒素を含む重合体(g)としてナイロン6−6 0.05質量部とを添加して、タンブラーで混合し、ポリアセタール樹脂混合物を得た。また、表2に示した割合で、ヒドラジン誘導体(B)及びヒドラジン誘導体(B)の融点を低下させる化合物(C)をタンブラーで混合して混合物を得た。この混合物と上記ポリアセタール樹脂混合物とを、タンブラーで混合した後に、ベント付2軸押出機に定量フィーダーを用いて供給し、バレル温度200℃、吐出量20kg/hrにて溶融混練することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 19]
To 100 parts by mass of polyacetal resin (a-3), triethylene glycol-bis- [3- (3-tert-butyl-5-methyl-4-hydroxyphenyl) -propionate] 0.3 as an antioxidant (d) A polymer containing 0.01 parts by mass of magnesium silicate as a formic acid scavenger (e-2), 0.03 parts by mass of ethylene glycol distearate as a release agent (f), and formaldehyde-reactive nitrogen ( As g), 0.05 part by mass of nylon 6-6 was added and mixed with a tumbler to obtain a polyacetal resin mixture. Moreover, the compound (C) which lowers | hangs melting | fusing point of a hydrazine derivative (B) and a hydrazine derivative (B) in the ratio shown in Table 2 was mixed with the tumbler, and the mixture was obtained. After this mixture and the polyacetal resin mixture are mixed with a tumbler, the mixture is supplied to a twin screw extruder with a vent using a quantitative feeder, and melt kneaded at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr. Resin composition pellets were produced. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例20]
ポリアセタール樹脂(a−1)15質量部に、表2に示した割合で、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを添加してタンブラーで混合し、ベント付2軸押出機で溶融混錬することにより予備混合物のペレットを製造した。得られたペレットとポリアセタール樹脂(a−1)85質量部とをタンブラーで混合し、ベント付2軸押出機で温度200℃、吐出量20kg/hrにて溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は148℃であった。
[Example 20]
To 15 parts by mass of the polyacetal resin (a-1), the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are added at a ratio shown in Table 2, and mixed by a tumbler. Premixed pellets were produced by melt-kneading with a vented twin screw extruder. The obtained pellets and 85 parts by mass of the polyacetal resin (a-1) are mixed with a tumbler, and melt-kneaded with a vented twin screw extruder at a temperature of 200 ° C. and a discharge rate of 20 kg / hr, thereby producing a polyacetal resin composition. Product pellets were produced. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 148 ° C.
[実施例21]
ポリアセタール樹脂(a−1)15質量部に、表2に示した割合で、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを添加してタンブラーで混合し、予備混合物を製造した。加熱式の小型二軸サイドスクリューフィーダーをつけたベント付2軸押出機で温度200℃、吐出量20kg/hrにて最終処方が表2の割合になるように予備混合物を溶融して、更に残りのポリアセタール樹脂(a−1)と溶融混練することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は148℃であった。
[Example 21]
To 15 parts by mass of the polyacetal resin (a-1), the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are added at a ratio shown in Table 2, and mixed by a tumbler. A premix was made. Melt the premix at a temperature of 200 ° C and discharge rate of 20 kg / hr so that the final formulation is in the ratio shown in Table 2 in a twin screw extruder with a vent equipped with a small heating twin screw side screw feeder. The pellet of the polyacetal resin composition was manufactured by melt-kneading with the polyacetal resin (a-1). The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 148 ° C.
[実施例22]
ポリアセタール樹脂(a−1)3質量部に、表2に示した割合で、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを添加してタンブラーで混合し、ベント付2軸押出機で溶融混錬することにより予備混合物のペレットを製造した。得られたペレットとポリアセタール樹脂(a−1)97質量部とをタンブラーで混合し、ベント付2軸押出機でバレル温度200℃、吐出量20kg/hrにて溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 22]
To 3 parts by mass of the polyacetal resin (a-1), the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are added at a ratio shown in Table 2 and mixed with a tumbler. Premixed pellets were produced by melt-kneading with a vented twin screw extruder. The obtained pellets and 97 parts by mass of the polyacetal resin (a-1) are mixed with a tumbler, and melt-kneaded with a vented twin-screw extruder at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr. A pellet of the composition was produced. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例23]
ポリアセタール樹脂(a−1)3質量部に、表2に示した割合で、ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを添加してタンブラーで混合し、予備混合物を製造した。加熱式の小型二軸サイドスクリューフィーダーをつけたベント付2軸押出機で温度200℃、吐出量200kg/hrにて最終処方が表2の割合になるように予備混合物を溶融して、更に残りのポリアセタール樹脂(a−1)と溶融混練することにより、ポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 23]
To 3 parts by mass of the polyacetal resin (a-1), the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are added at a ratio shown in Table 2 and mixed with a tumbler. A premix was made. Melt the premix with a vented twin screw extruder fitted with a small heating twin screw side screw feeder at a temperature of 200 ° C. and a discharge rate of 200 kg / hr so that the final formulation is the ratio shown in Table 2, and then the rest The pellet of the polyacetal resin composition was manufactured by melt-kneading with the polyacetal resin (a-1). The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[実施例24、25]
ポリアセタール樹脂(a−1)100質量部をベント付2軸押出機でバレル温度200℃、吐出量20kg/hrにて溶融した。また、表2に示した割合のヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを190℃に保温したタンクで溶融した。押出機の出口を始点として押出機混練ゾーンの全長に対して1/10の位置より、上記溶融したヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを液体用ポンプで添加し、溶融したポリアセタール樹脂(a−1)と溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の添加量は、ポリアセタール樹脂(a−1)の押出機への投入量に対して0.15/100(質量比)に調整した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は、実施例24について148℃、実施例25について154℃であった。
[Examples 24 and 25]
100 parts by mass of polyacetal resin (a-1) was melted at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr with a twin screw extruder with a vent. Moreover, the hydrazine derivative (B) in the proportion shown in Table 2 and the compound (C) that lowers the melting point of the hydrazine derivative (B) were melted in a tank kept at 190 ° C. Starting from the exit of the extruder, the molten hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are used for liquids at a position that is 1/10 of the total length of the extruder kneading zone. The pellet of the polyacetal resin composition was manufactured by adding with a pump and melt-kneading with the melted polyacetal resin (a-1). The amount of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) is 0.15 / 100 with respect to the amount of the polyacetal resin (a-1) charged into the extruder. (Mass ratio) was adjusted. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperatures of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) were 148 ° C. for Example 24 and 154 ° C. for Example 25.
[実施例26]
ポリアセタール樹脂(a−1)100質量部に、酸化防止剤(d)としてトリエチレングリコール−ビス−[3−(3−t−ブチル−5−メチル−4−ヒドロキシフェニル)−プロピオネート]0.3質量部と、蟻酸捕捉剤(e−2)として珪酸マグネシウム0.01質量部と、離型剤(f)としてエチレングリコールジステアレート0.03質量部と、ホルムアルデヒド反応性窒素を含む重合体(g)としてナイロン6−6 0.05質量部とを添加してタンブラーで混合し、ベント付2軸押出機でバレル温度200℃、吐出量20kg/hrにて溶融した。また、表2に示した割合でヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを190℃に保温したタンクで溶融した。押出機の出口を始点として押出機混練ゾーンの全長に対して1/10の位置より、上記溶融したヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを液体用ポンプで添加して溶融したポリアセタール樹脂(a−1)と溶融混錬することにより、ポリアセタール樹脂組成物のペレットを製造した。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の添加量は、ポリアセタール樹脂(a−1)の押出機への投入量に対して0.15/100.39(質量比)に調整した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。ヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度は154℃であった。
[Example 26]
To 100 parts by mass of polyacetal resin (a-1), triethylene glycol-bis- [3- (3-t-butyl-5-methyl-4-hydroxyphenyl) -propionate] 0.3 as an antioxidant (d) A polymer containing 0.01 parts by mass of magnesium silicate as a formic acid scavenger (e-2), 0.03 parts by mass of ethylene glycol distearate as a release agent (f), and formaldehyde-reactive nitrogen ( As g), 0.05-6 parts by mass of nylon 6-6 was added and mixed by a tumbler, and melted at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr with a vented twin screw extruder. Further, the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) were melted in a tank kept at 190 ° C. at the ratio shown in Table 2. Starting from the exit of the extruder, the molten hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are used for liquids at a position that is 1/10 of the total length of the extruder kneading zone. Pellets of the polyacetal resin composition were produced by melt kneading with the polyacetal resin (a-1) added and melted by the pump. The amount of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) is 0.15 / 100 with respect to the amount of the polyacetal resin (a-1) charged into the extruder. .39 (mass ratio). The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. The main peak temperature of the melting point of the mixture of the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) was 154 ° C.
[比較例1]
ポリアセタール樹脂(a−1)100質量部を、ベント付2軸押出機でバレル温度200℃、吐出量20kg/hrにて溶融混錬することによりポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。
[Comparative Example 1]
Pellets of the polyacetal resin composition were produced by melt-kneading 100 parts by mass of the polyacetal resin (a-1) with a vented twin-screw extruder at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above.
[比較例2]
ポリアセタール樹脂(a−1)に代えてポリアセタール樹脂(a−2)を用いた以外は比較例1と同様にして、ポリアセタール樹脂組成物のペレットを製造した。
[Comparative Example 2]
A pellet of the polyacetal resin composition was produced in the same manner as in Comparative Example 1 except that the polyacetal resin (a-2) was used instead of the polyacetal resin (a-1).
[比較例3]
ポリアセタール樹脂(a−1)に代えてポリアセタール樹脂(a−3)を用いた以外は比較例1と同様にして、ポリアセタール樹脂組成物のペレットを製造した。
[Comparative Example 3]
A pellet of the polyacetal resin composition was produced in the same manner as in Comparative Example 1 except that the polyacetal resin (a-3) was used instead of the polyacetal resin (a-1).
[比較例4〜7、参考例1]
ポリアセタール樹脂(a−1)100質量部に、表3に示した割合でヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを添加してタンブラーで混合し、ベント付2軸押出機でバレル温度200℃、吐出量20kg/hrにて溶融混錬することによりポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。各比較例、参考例で用いたヒドラジン誘導体(B)の融点、及びヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)との混合物の融点のメインピーク温度を表3に示す。
[Comparative Examples 4-7, Reference Example 1]
To 100 parts by mass of the polyacetal resin (a-1), the hydrazine derivative (B) and the compound (C) that lowers the melting point of the hydrazine derivative (B) are added at a ratio shown in Table 3, and mixed with a tumbler. Polyacetal resin composition pellets were produced by melt kneading at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr with a twin screw extruder. The pellets obtained were measured for dimensional stability after aging, repeated impact resistance after aging, evaluation of recycle moldability, and evaluation of MD resistance as described above. Table 3 shows the melting point of the hydrazine derivative (B) used in each comparative example and reference example, and the main peak temperature of the melting point of the mixture of the compound (C) that decreases the melting point of the hydrazine derivative (B) and the hydrazine derivative (B). Shown in
[比較例8〜12]
表3に示したヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)とを表3に示した割合でタンブラーで混合した。この混合物とポリアセタール樹脂(a−1)100質量部とを表3に示した割合で、ベント付2軸押出機に投入し、バレル温度200℃、吐出量20kg/hrにて溶融混練することによりポリアセタール樹脂組成物のペレットを製造した。得られたペレットについて、上述のようにしてエージング後の寸法安定性の測定、エージング後の耐繰り返し衝撃性の測定、リサイクル成形性の評価及び耐MD性の評価を行った。各比較例で用いたヒドラジン誘導体(B)とヒドラジン誘導体(B)の融点を低下させる化合物(C)の混合物の融点のメインピーク温度を表3に示す。
[Comparative Examples 8-12]
The hydrazine derivative (B) shown in Table 3 and the compound (C) that lowers the melting point of the hydrazine derivative (B) were mixed with a tumbler at the ratio shown in Table 3. By feeding this mixture and 100 parts by mass of polyacetal resin (a-1) into a twin-screw extruder with a vent at the ratio shown in Table 3, and melt-kneading at a barrel temperature of 200 ° C. and a discharge rate of 20 kg / hr. Pellets of polyacetal resin composition were produced. About the obtained pellet, the measurement of the dimensional stability after aging, the measurement of the impact resistance after aging, the evaluation of recycle moldability, and the evaluation of MD resistance were performed as described above. Table 3 shows the main peak temperature of the melting point of the mixture of the compound (C) that lowers the melting point of the hydrazine derivative (B) and the hydrazine derivative (B) used in each comparative example.
上記実施例1〜26、比較例1〜12及び参考例1のポリアセタール樹脂組成物の組成を表2、3に、エージング後の寸法安定性の評価、エージング後の耐繰り返し衝撃性の評価、リサイクル成形性、すなわち成形品からのホルムアルデヒド放出量の評価、及び耐MD性の評価の結果を表4に示す。 The compositions of the polyacetal resin compositions of Examples 1 to 26, Comparative Examples 1 to 12 and Reference Example 1 are shown in Tables 2 and 3, evaluation of dimensional stability after aging, evaluation of repeated impact resistance after aging, recycling Table 4 shows the results of evaluation of moldability, that is, evaluation of formaldehyde emission from the molded article and evaluation of MD resistance.
表2〜4に示す結果より、本発明の製造方法により得られるポリアセタール樹脂組成物は、2次収縮性、金型への充填率が低い条件下での耐モールドデポジット性、及びエージング後の耐繰り返し衝撃性に優れるものであることが分かる。また、本発明の製造方法により得られるポリアセタール樹脂組成物からなる成形品は、リサイクル成形後のホルムアルデヒド放出量を卓越した低いレベルで維持していることから、極めて優れたリサイクル成形性を有していることが分かる。 From the results shown in Tables 2 to 4, the polyacetal resin composition obtained by the production method of the present invention has a secondary shrinkage property, a mold deposit resistance under a low filling rate in the mold, and a resistance after aging. It turns out that it is excellent in repeated impact property. In addition, the molded article made of the polyacetal resin composition obtained by the production method of the present invention maintains an extremely low level of formaldehyde emission after recycling molding, and thus has extremely excellent recycling moldability. I understand that.
本発明により製造されるポリアセタール樹脂組成物は上述のとおり、エージング後の耐繰り返し衝撃性、リサイクル成形性に優れるだけでなく、ポリアセタール樹脂が持つ機械物性バランスを有し、かつ、エージング後の寸法安定性や金型への充填率が低い条件下での耐モールドデポジット性にも優れた樹脂組成物である。したがって、本発明は、自動車、電機電子、その他工業などの分野で好適に利用できるポリアセタール樹脂組成物を得ることのできる製造方法を提供するものである。 As described above, the polyacetal resin composition produced according to the present invention not only has excellent repeated impact resistance after aging and recycle moldability, but also has a mechanical property balance possessed by polyacetal resin, and is dimensionally stable after aging. It is a resin composition that is also excellent in mold deposit resistance under conditions where the properties and the filling rate into the mold are low. Therefore, this invention provides the manufacturing method which can obtain the polyacetal resin composition which can be utilized suitably in field | areas, such as a motor vehicle, electrical machinery electronics, and other industries.
Claims (11)
前記ポリアセタール樹脂が、ポリアセタールコポリマーであって、下記一般式(7)で表わされる少なくとも1種の第4級アンモニウム化合物の存在下で、ポリアセタールコポリマーの融点以上260℃以下の温度で、ポリアセタールコポリマーを溶融させた状態で熱処理されたポリアセタール樹脂であって、
[R1R2R3R4N+]nXn- (7)
(式(7)中、R1、R2、R3及びR4は、各々独立して、炭素数1〜30の置換又は非置換アルキル基;炭素数6〜20のアリール基;炭素数1〜30の置換又は非置換アルキル基の少なくとも1個の水素原子が炭素数6〜20のアリール基で置換されたアラルキル基;炭素数6〜20のアリール基の少なくとも1個の水素原子が炭素数1〜30の置換又は非置換アルキル基で置換されたアルキルアリール基を示し、置換又は非置換アルキル基は直鎖状、分岐状、又は環状である。上記置換アルキル基の置換基はハロゲン原子、水酸基、アルデヒド基、カルボキシル基、アミノ基、又はアミド基である。また、上記非置換アルキル基、アリール基、アラルキル基、アルキルアリール基はその水素原子がハロゲン原子で置換されていてもよい。nは1〜3の整数を示す。Xは水酸基、又は炭素数1〜20のカルボン酸、ハロゲン化水素以外の水素酸、オキソ酸、無機チオ酸若しくは炭素数1〜20の有機チオ酸の酸残基を示す。)
前記第1のヒドラジン誘導体がカルボン酸ヒドラジドであり、前記第1のヒドラジン誘導体の融点を低下させる前記化合物が、前記第1のヒドラジン誘導体とは異なる1種又は2種以上のヒドラジン誘導体であり、
前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物とが、アジピン酸ジヒドラジド及びセバシン酸ジヒドラジドからなる群より選ばれる互いに異なるカルボン酸ジヒドラジドを含み、
下記式(1)及び(2)で表される条件を満足する、前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物との混合物を調製する第1の工程と、前記第1の工程を経て得られた前記混合物を前記ポリアセタール樹脂と溶融混練する第2の工程と、を含むポリアセタール樹脂組成物の製造方法。
T1<T2 (1)
T1<T3 (2)
(式(1)及び(2)中、T1は、示差走査熱量計を用いて前記混合物に対して所定の温度プログラムで加熱及び冷却を施した後に、前記混合物が融解するまで2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T2は、前記示差走査熱量計を用いて前記第1のヒドラジン誘導体に対して所定の温度プログラムで加熱及び冷却を施した後に、前記第1のヒドラジン誘導体に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T3は、前記示差走査熱量計を用いて前記ポリアセタール樹脂に対して所定の温度プログラムで加熱及び冷却を施した後に、前記ポリアセタール樹脂に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)である。) A polyacetal resin, a first hydrazine derivative, a compound that lowers the melting point of the first hydrazine derivative (T2 in the following formula (1)), an alkali metal or alkaline earth metal hydroxide, inorganic acid A method for producing a polyacetal resin composition obtained from a raw material composition containing a salt, carboxylate or alkoxide,
The polyacetal resin is a polyacetal copolymer, and melts at a temperature not lower than the melting point of the polyacetal copolymer and not higher than 260 ° C. in the presence of at least one quaternary ammonium compound represented by the following general formula (7). A polyacetal resin that has been heat-treated in the state of
[R 1 R 2 R 3 R 4 N + ] n X n- (7)
(In the formula (7), R 1 , R 2 , R 3 and R 4 are each independently a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms; an aryl group having 6 to 20 carbon atoms; An aralkyl group in which at least one hydrogen atom of a substituted or unsubstituted alkyl group of -30 is substituted with an aryl group having 6 to 20 carbon atoms; at least one hydrogen atom of the aryl group having 6 to 20 carbon atoms is carbon number 1 represents an alkylaryl group substituted with a substituted or unsubstituted alkyl group having 1 to 30. The substituted or unsubstituted alkyl group is linear, branched, or cyclic, and the substituent of the substituted alkyl group is a halogen atom, A hydroxyl group, an aldehyde group, a carboxyl group, an amino group, or an amide group, and the hydrogen atom of the unsubstituted alkyl group, aryl group, aralkyl group, or alkylaryl group may be substituted with a halogen atom. N represents an integer of 1 to 3. X represents a hydroxyl group, a carboxylic acid having 1 to 20 carbon atoms, a hydrogen acid other than hydrogen halide, an oxo acid, an inorganic thioacid, or an organic thioacid having 1 to 20 carbon atoms. Indicates an acid residue.)
The first hydrazine derivative is a carboxylic acid hydrazide, and the compound that lowers the melting point of the first hydrazine derivative is one or more hydrazine derivatives different from the first hydrazine derivative;
The first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative include different carboxylic acid dihydrazides selected from the group consisting of adipic acid dihydrazide and sebacic acid dihydrazide,
A first step of preparing a mixture of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative, satisfying the conditions represented by the following formulas (1) and (2); And a second step of melt-kneading the mixture obtained through the first step with the polyacetal resin.
T1 <T2 (1)
T1 <T3 (2)
(In the formulas (1) and (2), T1 is 2.5 ° C./until the mixture is melted after being heated and cooled with a predetermined temperature program using a differential scanning calorimeter. Among the endothermic peaks obtained when the temperature is increased at a rate of minutes, the temperature (° C.) indicates the peak of the endothermic peak having the largest endothermic capacity, and T2 is the first hydrazine using the differential scanning calorimeter. Among the endothermic peaks obtained when the derivative is heated and cooled by a predetermined temperature program and then heated to a rate of 2.5 ° C./min with respect to the first hydrazine derivative, the endothermic capacity is T3 is the temperature (° C.) indicating the peak of the largest endothermic peak, and T3 is the temperature of the polyacetal resin after heating and cooling the polyacetal resin with a predetermined temperature program using the differential scanning calorimeter. Among the endothermic peak obtained when heated at 2.5 ° C. / min with respect to a temperature (℃) endothermic capacity indicating the vertex of the largest endothermic peak.)
前記ポリアセタール樹脂が、ポリアセタールコポリマーであって、下記一般式(7)で表わされる少なくとも1種の第4級アンモニウム化合物の存在下で、ポリアセタールコポリマーの融点以上260℃以下の温度で、ポリアセタールコポリマーを溶融させた状態で熱処理されたポリアセタール樹脂であって、
[R1R2R3R4N+]nXn- (7)
(式(7)中、R1、R2、R3及びR4は、各々独立して、炭素数1〜30の置換又は非置換アルキル基;炭素数6〜20のアリール基;炭素数1〜30の置換又は非置換アルキル基の少なくとも1個の水素原子が炭素数6〜20のアリール基で置換されたアラルキル基;炭素数6〜20のアリール基の少なくとも1個の水素原子が炭素数1〜30の置換又は非置換アルキル基で置換されたアルキルアリール基を示し、置換又は非置換アルキル基は直鎖状、分岐状、又は環状である。上記置換アルキル基の置換基はハロゲン原子、水酸基、アルデヒド基、カルボキシル基、アミノ基、又はアミド基である。また、上記非置換アルキル基、アリール基、アラルキル基、アルキルアリール基はその水素原子がハロゲン原子で置換されていてもよい。nは1〜3の整数を示す。Xは水酸基、又は炭素数1〜20のカルボン酸、ハロゲン化水素以外の水素酸、オキソ酸、無機チオ酸若しくは炭素数1〜20の有機チオ酸の酸残基を示す。)
前記第1のヒドラジン誘導体がカルボン酸ヒドラジドであり、前記第1のヒドラジン誘導体の融点を低下させる前記化合物が、前記第1のヒドラジン誘導体とは異なる1種又は2種以上のヒドラジン誘導体であり、
前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物とが、アジピン酸ジヒドラジド及びセバシン酸ジヒドラジドからなる群より選ばれる互いに異なるカルボン酸ジヒドラジドを含み、
前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物と前記ポリアセタール樹脂の一部とを混合して予備混合物を得る第1の工程と、前記第1の工程を経て得られた前記予備混合物を残りの前記ポリアセタール樹脂と溶融混練する第2の工程と、を含み、
前記第1のヒドラジン誘導体と前記第1のヒドラジン誘導体の融点を低下させる前記化合物との混合物が下記式(1)及び(2)で表される条件を満足するものであるポリアセタール樹脂組成物の製造方法。
T1<T2 (1)
T1<T3 (2)
(式(1)及び(2)中、T1は、示差走査熱量計を用いて前記混合物に対して所定の温度プログラムで加熱及び冷却を施した後に、前記混合物が融解するまで2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T2は、前記示差走査熱量計を用いて前記第1のヒドラジン誘導体に対して所定の温度プログラムで加熱及び冷却を施した後に、前記第1のヒドラジン誘導体に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)であり、T3は、前記示差走査熱量計を用いて前記ポリアセタール樹脂に対して所定の温度プログラムで加熱及び冷却を施した後に、前記ポリアセタール樹脂に対して2.5℃/分の速度で昇温したときに得られる吸熱ピークのうち、吸熱容量が最も大きな吸熱ピークの頂点を示す温度(℃)である。) A polyacetal resin, a first hydrazine derivative, a compound that lowers the melting point of the first hydrazine derivative (T2 in the following formula (1)), an alkali metal or alkaline earth metal hydroxide, inorganic acid A method for producing a polyacetal resin composition obtained from a raw material composition containing a salt, carboxylate or alkoxide,
The polyacetal resin is a polyacetal copolymer, and melts at a temperature not lower than the melting point of the polyacetal copolymer and not higher than 260 ° C. in the presence of at least one quaternary ammonium compound represented by the following general formula (7). A polyacetal resin that has been heat-treated in the state of
[R 1 R 2 R 3 R 4 N + ] n X n- (7)
(In the formula (7), R 1 , R 2 , R 3 and R 4 are each independently a substituted or unsubstituted alkyl group having 1 to 30 carbon atoms; an aryl group having 6 to 20 carbon atoms; An aralkyl group in which at least one hydrogen atom of a substituted or unsubstituted alkyl group of -30 is substituted with an aryl group having 6 to 20 carbon atoms; at least one hydrogen atom of the aryl group having 6 to 20 carbon atoms is carbon number 1 represents an alkylaryl group substituted with a substituted or unsubstituted alkyl group having 1 to 30. The substituted or unsubstituted alkyl group is linear, branched, or cyclic, and the substituent of the substituted alkyl group is a halogen atom, A hydroxyl group, an aldehyde group, a carboxyl group, an amino group, or an amide group, and the hydrogen atom of the unsubstituted alkyl group, aryl group, aralkyl group, or alkylaryl group may be substituted with a halogen atom. N represents an integer of 1 to 3. X represents a hydroxyl group, a carboxylic acid having 1 to 20 carbon atoms, a hydrogen acid other than hydrogen halide, an oxo acid, an inorganic thioacid, or an organic thioacid having 1 to 20 carbon atoms. Indicates an acid residue.)
The first hydrazine derivative is a carboxylic acid hydrazide, and the compound that lowers the melting point of the first hydrazine derivative is one or more hydrazine derivatives different from the first hydrazine derivative;
The first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative include different carboxylic acid dihydrazides selected from the group consisting of adipic acid dihydrazide and sebacic acid dihydrazide,
A first step of obtaining a premix by mixing the first hydrazine derivative, the compound that lowers the melting point of the first hydrazine derivative, and a part of the polyacetal resin, and obtained through the first step. A second step of melt-kneading the prepared premix with the remaining polyacetal resin,
Production of a polyacetal resin composition in which a mixture of the first hydrazine derivative and the compound that lowers the melting point of the first hydrazine derivative satisfies the conditions represented by the following formulas (1) and (2): Method.
T1 <T2 (1)
T1 <T3 (2)
(In the formulas (1) and (2), T1 is 2.5 ° C./until the mixture is melted after being heated and cooled with a predetermined temperature program using a differential scanning calorimeter. Among the endothermic peaks obtained when the temperature is increased at a rate of minutes, the temperature (° C.) indicates the peak of the endothermic peak having the largest endothermic capacity, and T2 is the first hydrazine using the differential scanning calorimeter. Among the endothermic peaks obtained when the derivative is heated and cooled by a predetermined temperature program and then heated to a rate of 2.5 ° C./min with respect to the first hydrazine derivative, the endothermic capacity is T3 is the temperature (° C.) indicating the peak of the largest endothermic peak, and T3 is the temperature of the polyacetal resin after heating and cooling the polyacetal resin with a predetermined temperature program using the differential scanning calorimeter. Among the endothermic peak obtained when heated at 2.5 ° C. / min with respect to a temperature (℃) endothermic capacity indicating the vertex of the largest endothermic peak.)