JP5268137B2 - Adhesive composition for optical film, adhesive optical film, and image display device - Google Patents
Adhesive composition for optical film, adhesive optical film, and image display device Download PDFInfo
- Publication number
- JP5268137B2 JP5268137B2 JP2008105962A JP2008105962A JP5268137B2 JP 5268137 B2 JP5268137 B2 JP 5268137B2 JP 2008105962 A JP2008105962 A JP 2008105962A JP 2008105962 A JP2008105962 A JP 2008105962A JP 5268137 B2 JP5268137 B2 JP 5268137B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- optical film
- weight
- acrylate
- sensitive adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明は、剥離容易性、再利用性、および耐久性等が必要とされる光学フィルム用粘着剤組成物および当該粘着剤組成物により光学フィルムの少なくとも片面に粘着剤層が形成されている粘着型光学フィルムに関する。さらには、本発明は、前記粘着型光学フィルムを用いた液晶表示装置、有機ＥＬ表示装置等の画像表示装置に関する。前記光学フィルムとしては、偏光板、位相差板、光学補償フィルム、輝度向上フィルム、さらにはこれらが積層されているものを用いることができる。 The present invention relates to an optical film pressure-sensitive adhesive composition that requires ease of peeling, reusability, durability, and the like, and a pressure-sensitive adhesive composition having an adhesive layer formed on at least one surface of the optical film. Type optical film. Furthermore, the present invention relates to an image display device such as a liquid crystal display device and an organic EL display device using the adhesive optical film. As the optical film, a polarizing plate, a phase difference plate, an optical compensation film, a brightness enhancement film, and a film in which these are laminated can be used.
液晶ディスプレイ等は、その画像形成方式から液晶セルの両側に偏光素子を配置することが必要不可欠であり、一般的には偏光板が貼着されている。また液晶パネルには偏光板の他に、ディスプレイの表示品位を向上させるために様々な光学素子が用いられるようになってきている。例えば、着色防止としての位相差板、液晶ディスプレイの視野角を改善するための視野角拡大フィルム、さらにはディスプレイのコントラストを高めるための輝度向上フィルム等が用いられる。これらのフィルムは総称して光学フィルムと呼ばれる。 In a liquid crystal display or the like, it is indispensable to dispose polarizing elements on both sides of a liquid crystal cell because of its image forming method, and generally a polarizing plate is attached. In addition to polarizing plates, various optical elements have been used for liquid crystal panels in order to improve the display quality of displays. For example, a retardation plate for preventing coloring, a viewing angle widening film for improving the viewing angle of a liquid crystal display, and a brightness enhancement film for increasing the contrast of the display are used. These films are collectively called optical films.
前記光学フィルムなどの光学部材を液晶セルに貼着する際には、通常、粘着剤が使用される。また、光学フィルムと液晶セル、または光学フィルム間の接着は、通常、光の損失を低減するため、それぞれの材料は粘着剤を用いて密着されている。このような場合に、光学フィルムを固着させるのに乾燥工程を必要としないこと等のメリットを有することから、粘着剤は、光学フィルムの片側に予め粘着剤層として設けられた粘着型光学フィルムが一般的に用いられる。 When an optical member such as the optical film is attached to a liquid crystal cell, an adhesive is usually used. In addition, the adhesion between the optical film and the liquid crystal cell, or the optical film is usually in close contact with each other using an adhesive in order to reduce the loss of light. In such a case, since the adhesive has the merit that a drying step is not required for fixing the optical film, the adhesive is an adhesive optical film provided in advance as an adhesive layer on one side of the optical film. Generally used.
前記粘着剤に要求される必要特性としては、光学フィルムを液晶セルに貼り合わせる際、貼り合わせ位置を誤ったり、貼合せ面に異物が噛み込んだりしたような場合にも光学フィルムを液晶パネルから剥離し、液晶セルを再利用する場合がある。かかる剥離工程において、液晶パネルから糊残りなく光学フィルムを容易に剥がすことができる再剥離性（リワーク性）が求められる。特に、近年では、従来のパネル作成工程に加え、ケミカルエッチング処理されたガラスを用いた薄型の液晶パネルの使用が増え、当該薄型の液晶パネルからの光学フィルムのリワーク性、加工性の維持が困難になっている。また、前記粘着剤には、光学フィルムに粘着剤層を形成した後に、粘着剤の汚れや欠落などを生じることなく加工できる加工性、さらには、環境促進試験として通常行われる加熱および加湿等による耐久試験に対して粘着剤に起因する剥がれや浮きなどの不具合が発生しないことが求められる。 Necessary characteristics required for the pressure-sensitive adhesive include that when the optical film is bonded to the liquid crystal cell, the optical film is removed from the liquid crystal panel even when the bonding position is wrong or a foreign object is caught in the bonding surface. The liquid crystal cell may be reused by peeling off. In such a peeling step, re-peelability (reworkability) that can easily peel off the optical film from the liquid crystal panel without adhesive residue is required. In particular, in recent years, in addition to conventional panel manufacturing processes, the use of thin liquid crystal panels using chemically etched glass has increased, making it difficult to maintain reworkability and workability of optical films from the thin liquid crystal panels. It has become. In addition, the pressure-sensitive adhesive can be processed without forming a pressure-sensitive adhesive layer after the pressure-sensitive adhesive layer is formed on the optical film, and further by heating and humidification normally performed as an environmental promotion test. For the durability test, it is required that defects such as peeling and floating due to the adhesive do not occur.
従来、液晶パネルのリワーク性の課題を解消する方法として、アクリル系粘着剤のベースポリマーであるアクリル系ポリマーに、可塑剤やオリゴマー成分を含有させることが提案されている（特許文献１）。しかし、このアクリル系粘着剤では、前記薄型の液晶パネルに対しては、リワーク性、加工性を満足できているとはいえなかった。 Conventionally, as a method for solving the problem of reworkability of a liquid crystal panel, it has been proposed that an acrylic polymer which is a base polymer of an acrylic pressure-sensitive adhesive contains a plasticizer or an oligomer component (Patent Document 1). However, this acrylic pressure-sensitive adhesive does not satisfy reworkability and workability with respect to the thin liquid crystal panel.
上記の他、光学フィルムに用いられるアクリル系粘着剤としては、アクリル系ポリマーのモノマー成分として、アルキル（メタ）アクリレートに加えて、分子内に水酸基を有する単量体と分子内にカルボキシル基、アミド基、アミノ基等の官能基を有する単量体を用いたもの（特許文献２および３）、アクリル系ポリマーのモノマー成分として、アルキル（メタ）アクリレートに加えて、イミド基含有モノマー、アミド基含有モノマー等の窒素含有モノマーを用い、さらに、過酸化物およびイソシアネート化合物を用いたもの（特許文献４）が提案されている。また、芳香族モノマーを特定量含有させる方法（特許文献５）も提案されている。しかし、これら特許文献に記載のアクリル系粘着剤は、いずれも、耐久性や接着性能を向上させるものではあるが、リワーク性、加工性を十分に満足できるものではなかった。 In addition to the above, the acrylic pressure-sensitive adhesive used for the optical film includes, as a monomer component of the acrylic polymer, in addition to alkyl (meth) acrylate, a monomer having a hydroxyl group in the molecule, and a carboxyl group or amide in the molecule. In addition to alkyl (meth) acrylate, those containing monomers having functional groups such as groups and amino groups (Patent Documents 2 and 3), and monomer components of acrylic polymers, containing imide groups and amide groups A nitrogen-containing monomer such as a monomer and a peroxide and an isocyanate compound (Patent Document 4) have been proposed. A method (Patent Document 5) in which a specific amount of an aromatic monomer is contained has also been proposed. However, although the acrylic pressure-sensitive adhesives described in these patent documents all improve durability and adhesion performance, they have not fully satisfied reworkability and workability.
耐久性向上およびリワーク性の向上の為に、アクリル系ポリマーに、メチル水素シリコーンオイルを添加した粘着剤組成物も提案されている（特許文献６および７）が、より優れた特性を有する粘着剤組成物が求められている。
本発明は、液晶パネル等から糊残りなく光学フィルムを容易に剥がすことができるリワーク性、および、光学フィルムに粘着剤層を形成した後、粘着剤の汚れ、剥がれや浮きなどを生じることなく加工できる加工性あるいは耐久性を満足できる粘着剤層を形成することができる光学フィルム用粘着剤組成物を提供することを目的とする。 The present invention is a rework property that allows an optical film to be easily peeled off from a liquid crystal panel or the like without adhesive residue, and after forming an adhesive layer on the optical film, the adhesive film is processed without causing dirt, peeling or floating. It aims at providing the adhesive composition for optical films which can form the adhesive layer which can satisfy the workability or durability which can be performed.
また本発明は、前記光学フィルム用粘着剤組成物により形成された粘着剤層を有する粘着型光学フィルムを提供すること、さらには前記粘着型光学フィルムを用いた画像表示装置を提供することを目的とする。 Another object of the present invention is to provide a pressure-sensitive adhesive optical film having a pressure-sensitive adhesive layer formed from the pressure-sensitive adhesive composition for optical films, and further to provide an image display device using the pressure-sensitive adhesive optical film. And
本発明者らは前記課題を解決すべく鋭意検討を重ねた結果、下記光学フィルム用粘着剤組成物を見出し、本発明を完成するに至った。 As a result of intensive studies to solve the above problems, the present inventors have found the following pressure-sensitive adhesive composition for optical films and have completed the present invention.
すなわち本発明は、モノマー単位として、アルキル（メタ）アクリレートを５０重量％以上含有してなり、ゲルパーミエーションクロマトグラフィーによる重量平均分子量が、１５０万以上の（メタ）アクリル系ポリマー；並びに、
該（メタ）アクリル系ポリマー１００重量部に対して、シランカップリング剤を０．０１〜１重量部、下記構造式（１）で表わされるシロキサン化合物を０．０１〜１０重量部、および架橋剤を０．０１〜５重量部含有してなることを特徴とする光学フィルム用粘着剤組成物：
0.01 to 1 part by weight of a silane coupling agent, 0.01 to 10 parts by weight of a siloxane compound represented by the following structural formula (1), and a crosslinking agent with respect to 100 parts by weight of the (meth) acrylic polymer 0.01 to 5 parts by weight of a pressure-sensitive adhesive composition for optical films,
上記光学フィルム用粘着剤組成物において、上記シロキサン化合物が、下記構造式（２）で表わされることが好ましい。
上記光学フィルム用粘着剤組成物において、上記（メタ）アクリル系ポリマーは、ゲルパーミエーションクロマトグラフィーによる分析において、分子量が１０万以下のポリマーを、１５エリア％以下の割合で含むことが好ましい。 In the optical film pressure-sensitive adhesive composition, the (meth) acrylic polymer preferably contains a polymer having a molecular weight of 100,000 or less at a ratio of 15 area% or less in analysis by gel permeation chromatography.
上記光学フィルム用粘着剤組成物において、上記（メタ）アクリル系ポリマーは、芳香環含有（メタ）アクリレートを１０〜４５重量％の割合で含むことが好ましい。 In the optical film pressure-sensitive adhesive composition, the (meth) acrylic polymer preferably contains an aromatic ring-containing (meth) acrylate in a proportion of 10 to 45% by weight.
上記光学フィルム用粘着剤組成物において、上記シランカップリング剤は、分子構造中に芳香環を有することが好ましい。 In the optical film pressure-sensitive adhesive composition, the silane coupling agent preferably has an aromatic ring in the molecular structure.
本発明はまた、上記のいずれかに記載の光学フィルム用粘着剤組成物を塗工して架橋反応させることによって得られる光学フィルム用粘着剤層、に関する。 The present invention also relates to an optical film pressure-sensitive adhesive layer obtained by applying the above-described optical film pressure-sensitive adhesive composition and performing a crosslinking reaction.
本発明はまた、光学フィルムの少なくとも片側に、上記の光学フィルム用粘着剤層が形成されている粘着型光学フィルム、に関する。 The present invention also relates to an adhesive optical film in which the optical film adhesive layer is formed on at least one side of the optical film.
本発明はまた、上記の粘着型光学フィルムを少なくとも１つ用いる画像表示装置に関する。 The present invention also relates to an image display device using at least one of the above adhesive optical films.
本発明の光学フィルム用粘着剤組成物は、ベースポリマーである（メタ）アクリル系ポリマーとして、アルキル(メタ)アクリレートモノマーを含む。そして、シランカップリング剤と、特定の置換基を有するシロキサン化合物とを含有する。かかる構成を採用することにより、このような光学フィルム用粘着剤組成物は、加工性、リワーク性、および耐久性に優れ、加工時における粘着剤の剥がれ、汚れ、または浮きなどの不具合が抑制され、また、光学フィルムを薄型の液晶パネル、特にケミカルエッチングされたガラスを用いた液晶パネルから剥離する場合にも、糊残りなく剥離を容易に行うことができる。 The pressure-sensitive adhesive composition for an optical film of the present invention contains an alkyl (meth) acrylate monomer as a (meth) acrylic polymer that is a base polymer. Then, containing a siloxane compound having a silane-coupling agent, a specific substituent. By adopting such a configuration, such an adhesive composition for an optical film is excellent in processability, reworkability, and durability, and problems such as peeling, dirt, or floating of the adhesive during processing are suppressed. Also, when the optical film is peeled off from a thin liquid crystal panel, particularly a liquid crystal panel using chemically etched glass, the peeling can be easily performed without adhesive residue.
本発明の光学フィルム用粘着剤組成物は、モノマー単位として、アルキル（メタ）アクリレートを５０重量％以上含有し、さらに任意に芳香族含有（メタ）アクリレートを１０〜４５重量％含有していてもよい（メタ）アクリル系ポリマーをベースポリマーとして含む。 The pressure-sensitive adhesive composition for an optical film of the present invention contains 50% by weight or more of an alkyl (meth) acrylate as a monomer unit, and optionally further contains 10 to 45% by weight of an aromatic-containing (meth) acrylate. A good (meth) acrylic polymer is included as a base polymer.
本明細書で、単に、「アルキル（メタ）アクリレート」と言うときは、炭素数が２〜１８の直鎖あるいは分岐鎖のアルキル基を有する（メタ）アクリレートを指し、芳香環をその構造中に含むものは除外される。前記アルキル基の平均炭素数は２〜１４であるのが好ましく、さらには平均炭素数３〜１２が好ましく、さらには平均炭素数４〜９のものが好ましい。なお、（メタ）アクリレートはアクリレートおよび／またはメタクリレートをいい、本発明の（メタ）とは同様の意味である。 In this specification, the term “alkyl (meth) acrylate” simply refers to a (meth) acrylate having a linear or branched alkyl group having 2 to 18 carbon atoms, and an aromatic ring in the structure. Including is excluded. The alkyl group preferably has an average carbon number of 2 to 14, more preferably an average carbon number of 3 to 12, and further preferably an average carbon number of 4 to 9. (Meth) acrylate refers to acrylate and / or methacrylate, and (meth) of the present invention has the same meaning.
アルキル（メタ）アクリレートの具体例としては、エチル（メタ）アクリレート、ｎ−ブチル（メタ）アクリレート、ｓ−ブチル（メタ）アクリレート、ｔ−ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｎ−ペンチル（メタ）アクリレート、イソペンチル（メタ）アクリレート、へキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、イソアミル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレート、ｎ−オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ｎ−ノニル（メタ）アクリレート、イソノニル（メタ）アクリレート、ｎ−デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ｎ−ドデシル（メタ）アクリレート、イソミリスチル（メタ）アクリレート、ｎ−トリデシル（メタ）アクリレート、ｎ−テトラデシル（メタ）アクリレート、ステアリル（メタ）アクリレート、イソステアリル（メタ）アクリレートなどがあげられる。なかでも、ｎ−ブチル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレートなどを例示でき、これらは単独または組み合わせて使用できる。 Specific examples of the alkyl (meth) acrylate include ethyl (meth) acrylate, n-butyl (meth) acrylate, s-butyl (meth) acrylate, t-butyl (meth) acrylate, isobutyl (meth) acrylate, and n-pentyl. (Meth) acrylate, isopentyl (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, isoamyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, n-octyl (meth) acrylate, isooctyl (meth) Acrylate, n-nonyl (meth) acrylate, isononyl (meth) acrylate, n-decyl (meth) acrylate, isodecyl (meth) acrylate, n-dodecyl (meth) acrylate, isomyristyl (meth) acrylate n- tridecyl (meth) acrylate, n- tetradecyl (meth) acrylate, stearyl (meth) acrylate, isostearyl (meth) acrylate. Especially, n-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, etc. can be illustrated and these can be used individually or in combination.
本発明において、前記アルキル（メタ）アクリレートは、（メタ）アクリル系ポリマーの全モノマー成分に対して、５０重量％以上であり、５０〜９９重量％であることが好ましく、さらには６０〜９９重量％、より好ましくは、７２〜８５重量％である。上記（メタ）アクリル系モノマーが少なすぎると接着性に乏しくなり好ましくない。 In this invention, the said alkyl (meth) acrylate is 50 weight% or more with respect to all the monomer components of a (meth) acrylic-type polymer, It is preferable that it is 50 to 99 weight%, Furthermore, 60 to 99 weight% %, More preferably 72 to 85% by weight. If the amount of the (meth) acrylic monomer is too small, the adhesiveness is poor, which is not preferable.
本発明において、「芳香環含有（メタ）アクリレート」と言うときは、その構造中に芳香族基を含む共重合可能な（メタ）アクリレートである。芳香環含有（メタ）アクリレートの例としては、フェニルアクリレート、フェノキシ（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、ベンジル（メタ）アクリレート、フェノキシジエチレングリコール（メタ）アクリレート、エチレンオキサイド変性ノニルフェノール（メタ）アクリレート、ヒドロキシエチル化β−ナフトールアクリレート、ビフェニル（メタ）アクリレート等が挙げられる。さらに、例えば、フェノールエチレンオキサイド変性（メタ）アクリレート、２−ナフトエチル（メタ）アクリレート、2−ナフトキシエチルアクリレート、２−（４−メトキシ−１−ナフトキシ）エチル（メタ）アクリレート、フェノキシプロピル（メタ）アクリレート、フェノキシジエチレングリコール（メタ）アクリレート、チオールアクリレート、ピリジルアクリレート、ピロールアクリレート、フェニルアクリレート、ポリスチリル（メタ）アクリレート等があげられる。 In the present invention, “aromatic ring-containing (meth) acrylate” is a copolymerizable (meth) acrylate containing an aromatic group in its structure. Examples of aromatic ring-containing (meth) acrylates include phenyl acrylate, phenoxy (meth) acrylate, phenoxyethyl (meth) acrylate, benzyl (meth) acrylate, phenoxydiethylene glycol (meth) acrylate, ethylene oxide modified nonylphenol (meth) acrylate, Examples thereof include hydroxyethylated β-naphthol acrylate and biphenyl (meth) acrylate. Further, for example, phenol ethylene oxide modified (meth) acrylate, 2-naphthoethyl (meth) acrylate, 2-naphthoxyethyl acrylate, 2- (4-methoxy-1-naphthoxy) ethyl (meth) acrylate, phenoxypropyl (meth) Examples include acrylate, phenoxydiethylene glycol (meth) acrylate, thiol acrylate, pyridyl acrylate, pyrrole acrylate, phenyl acrylate, and polystyryl (meth) acrylate.
本発明において、前記芳香環含有（メタ）アクリレートは、含まれる場合には、（メタ）アクリル系ポリマーの全モノマー成分に対して、１０〜４５重量％であることが好ましい。さらには１０〜４０重量％であることがより好ましく、２０〜３５重量％であることが最も好ましい。このように本発明の（メタ）アクリル系ポリマーが芳香環含有（メタ）アクリレートを含む場合には、芳香環含有（メタ）アクリレートとアルキル(メタ)アクリレートの含有比率のバランスを取る必要がある。 In this invention, when the said aromatic ring containing (meth) acrylate is contained, it is preferable that it is 10 to 45 weight% with respect to all the monomer components of a (meth) acrylic-type polymer. Furthermore, it is more preferably 10 to 40% by weight, and most preferably 20 to 35% by weight. Thus, when the (meth) acrylic polymer of the present invention contains an aromatic ring-containing (meth) acrylate, it is necessary to balance the content ratio of the aromatic ring-containing (meth) acrylate and the alkyl (meth) acrylate.
また本発明には、これ以外にも任意に、アミノ基含有（メタ）アクリレートを含ませることが可能である。このようなアミノ基含有（メタ）アクリレートの例としては、第３級アミノ基含有（メタ）アクリレート以外のモノマーとして、Ｎ−（メタ）アクリロイルオキシメチレンスクシンイミドやＮ−（メタ）アクリロイル−６−オキシヘキサメチレンスクシンイミド、Ｎ−（メタ）アクリロイル−８−オキシオクタメチレンスクシンイミドなどのスクシンイミド系モノマー；（メタ）アクリルアミド、Ｎ，Ｎ−ジメチル（メタ）アクリルアミド、Ｎ，Ｎ−ジエチル（メタ）アクリルアミド、Ｎ，Ｎ−ジエチルメタクリルアミド、Ｎ−イソプロピル（メタ）アクリルアミド、Ｎ−メチロール（メタ）アクリルアミド、Ｎ−メトキシメチル（メタ）アクリルアミド、Ｎ−ブトキシメチル（メタ）アクリルアミド等のＮ−置換アミド系モノマー；、（メタ）アクリル酸ｔ−ブチルアミノエチル等の第２級アミノ基を有するモノマー、ダイアセトン（メタ）アクリルアミド、Ｎ，Ｎ’−メチレンビス（メタ）アクリルアミド、Ｎ−アクリロイルモルホリン、Ｎ−アクリロイルピペリジン、Ｎ−メタクリロイルピペリジン、Ｎ−アクリロイルピロリジンなどを用いることができる。しかしながら、特に第３級アミノ基含有（メタ）アクリレートが好ましく、様々な第３級アミノ基および（メタ）アクリロイル基を含有するものが好ましく使用できる。第３級アミノ基としては、第３級アミノアルキル基であることが好ましい。かかる第３級アミノ基含有（メタ）アクリレートとしては、Ｎ，Ｎ−ジアルキルアミノアルキル（メタ）アクリルアミド、Ｎ，Ｎ−ジアルキルアミノアルキル（メタ）アクリレートがあげられる。第３級アミノ基含有（メタ）アクリレートの具体例としては、例えば、Ｎ，Ｎ−ジメチルアミノエチル（メタ）アクリルアミド、Ｎ，Ｎ−ジメチルアミノプロピル（メタ）アクリルアミド、Ｎ，Ｎ−ジエチルアミノエチル（メタ）アクリルアミド、Ｎ，Ｎ−ジエチルアミノプロピル（メタ）アクリルアミド、Ｎ，Ｎ−ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ−ジメチルアミノプロピル（メタ）アクリレート、Ｎ，Ｎ−ジエチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ−ジエチルアミノプロピル（メタ）アクリルアミドがあげられる。 In addition to the above, the present invention can optionally contain an amino group-containing (meth) acrylate. Examples of such amino group-containing (meth) acrylates include N- (meth) acryloyloxymethylene succinimide and N- (meth) acryloyl-6-oxy as monomers other than tertiary amino group-containing (meth) acrylates. Succinimide monomers such as hexamethylene succinimide and N- (meth) acryloyl-8-oxyoctamethylene succinimide; (meth) acrylamide, N, N-dimethyl (meth) acrylamide, N, N-diethyl (meth) acrylamide, N, N-substituted amide monomers such as N-diethylmethacrylamide, N-isopropyl (meth) acrylamide, N-methylol (meth) acrylamide, N-methoxymethyl (meth) acrylamide, N-butoxymethyl (meth) acrylamide; Me ) Monomers having secondary amino groups such as t-butylaminoethyl acrylate, diacetone (meth) acrylamide, N, N′-methylenebis (meth) acrylamide, N-acryloylmorpholine, N-acryloylpiperidine, N-methacryloyl Piperidine, N-acryloylpyrrolidine and the like can be used. However, tertiary amino group-containing (meth) acrylates are particularly preferred, and those containing various tertiary amino groups and (meth) acryloyl groups can be preferably used. The tertiary amino group is preferably a tertiary aminoalkyl group. Examples of such tertiary amino group-containing (meth) acrylates include N, N-dialkylaminoalkyl (meth) acrylamide and N, N-dialkylaminoalkyl (meth) acrylate. Specific examples of the tertiary amino group-containing (meth) acrylate include, for example, N, N-dimethylaminoethyl (meth) acrylamide, N, N-dimethylaminopropyl (meth) acrylamide, N, N-diethylaminoethyl (meta) ) Acrylamide, N, N-diethylaminopropyl (meth) acrylamide, N, N-dimethylaminoethyl (meth) acrylate, N, N-dimethylaminopropyl (meth) acrylate, N, N-diethylaminoethyl (meth) acrylate, N , N-diethylaminopropyl (meth) acrylamide.
アミノ基含有（メタ）アクリレートは、（メタ）アクリル系ポリマーを形成するモノマー成分の全量に対して０．０１〜０．５重量％の割合で用いられる。アミノ基含有（メタ）アクリレートの割合は、０．０１〜０．３重量％であるのが好ましく、さらには０．０５〜０．１５重量％であるのがより好ましい。 The amino group-containing (meth) acrylate is used in a proportion of 0.01 to 0.5% by weight based on the total amount of monomer components forming the (meth) acrylic polymer. The ratio of the amino group-containing (meth) acrylate is preferably 0.01 to 0.3% by weight, more preferably 0.05 to 0.15% by weight.
また、本発明の（メタ）アクリル系ポリマーには、この他に、カルボキシル基含有（メタ）アクリレートを含ませることも可能である。このようなモノマーの例としては、（メタ）アクリロイル基の不飽和二重結合を有する重合性の官能基を有し、かつカルボキシル基を有するものを特に制限なく用いることができる。カルボキシル基含有（メタ）アクリレートとしては、例えば、(メタ)アクリル酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレート等があげられる。 In addition, the (meth) acrylic polymer of the present invention can also contain a carboxyl group-containing (meth) acrylate. As an example of such a monomer, those having a polymerizable functional group having an unsaturated double bond of a (meth) acryloyl group and having a carboxyl group can be used without particular limitation. Examples of the carboxyl group-containing (meth) acrylate include (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, and the like.
また、本発明の（メタ）アクリル系ポリマーには、この他に、水酸基含有（メタ）アクリレートを含ませることも可能である。このようなモノマーとして、（メタ）アクリロイル基の不飽和二重結合を有する重合性の官能基を有し、かつヒドロキシル基を有するものを特に制限なく用いることができる。水酸基含有（メタ）アクリレートとしては、例えば、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシブチル（メタ）アクリレート、３−ヒドロキシプロピル（メタ）アクリレート、４−ヒドロキシブチル（メタ）アクリレート、６−ヒドロキシヘキシル（メタ）アクリレート、８−ヒドロキシオクチル（メタ）アクリレート、１０−ヒドロキシデシル（メタ）アクリレート、１２−ヒドロキシラウリル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレート；ヒドロキシエチル（メタ）アクリルアミド、その他、（４−ヒドロキシメチルシクロへキシル）メチルアクリレート、Ｎ−メチロール（メタ）アクリルアミド、Ｎ−ヒドロキシ（メタ）アクリルアミド、などがあげられる。 In addition, the (meth) acrylic polymer of the present invention can also contain a hydroxyl group-containing (meth) acrylate. As such a monomer, those having a polymerizable functional group having an unsaturated double bond of a (meth) acryloyl group and having a hydroxyl group can be used without particular limitation. Examples of the hydroxyl group-containing (meth) acrylate include 2-hydroxyethyl (meth) acrylate, 2-hydroxybutyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, and 6-hydroxy. Hexyl (meth) acrylate, 8-hydroxyoctyl (meth) acrylate, 10-hydroxydecyl (meth) acrylate, hydroxyalkyl (meth) acrylate such as 12-hydroxylauryl (meth) acrylate; hydroxyethyl (meth) acrylamide, etc. (4-hydroxymethylcyclohexyl) methyl acrylate, N-methylol (meth) acrylamide, N-hydroxy (meth) acrylamide, and the like.
水酸基含有（メタ）アクリレートは、（メタ）アクリル系ポリマーを形成するモノマー成分の全量に対して、０．０５〜２重量％の割合で用いられる。水酸基含有（メタ）アクリレートの割合は、好ましくは、０．０５〜１．５重量％、より好ましくは、０．１〜１重量％ある。 The hydroxyl group-containing (meth) acrylate is used in a proportion of 0.05 to 2% by weight with respect to the total amount of monomer components forming the (meth) acrylic polymer. The proportion of the hydroxyl group-containing (meth) acrylate is preferably 0.05 to 1.5% by weight, more preferably 0.1 to 1% by weight.
前記（メタ）アクリル系ポリマーを形成するモノマー成分としては、前記モノマーの他に、本発明の目的を損なわない範囲で、前記以外のモノマーを、用いることができる。本発明における任意モノマーの割合は、さらには４０重量％以下であるのが好ましい。かかる任意モノマーとしては、無水マレイン酸、無水イタコン酸などの酸無水物基含有モノマー；アクリル酸のカプロラクトン付加物；スチレンスルホン酸やアリルスルホン酸、２−（メタ）アクリルアミド−２−メチルプロパンスルホン酸、（メタ）アクリルアミドプロパンスルホン酸、スルホプロピル（メタ）アクリレート、（メタ）アクリロイルオキシナフタレンスルホン酸などのスルホン酸基含有モノマー；２−ヒドロキシエチルアクリロイルホスフェートなどの燐酸基含有モノマー；（メタ）アクリル酸メトキシエチル、（メタ）アクリル酸エトキシエチルなどの（メタ）アクリル酸アルコキシアルキル系モノマー；などあげられる。 As the monomer component for forming the (meth) acrylic polymer, monomers other than those described above can be used in addition to the monomers as long as the object of the present invention is not impaired. The ratio of the optional monomer in the present invention is further preferably 40% by weight or less. Examples of such optional monomers include maleic anhydride, itaconic anhydride and other acid anhydride group-containing monomers; acrylic acid caprolactone adducts; styrene sulfonic acid, allyl sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid Sulfonic acid group-containing monomers such as (meth) acrylamide propane sulfonic acid, sulfopropyl (meth) acrylate, (meth) acryloyloxynaphthalene sulfonic acid; phosphoric acid group-containing monomers such as 2-hydroxyethyl acryloyl phosphate; (meth) acrylic acid (Meth) acrylic acid alkoxyalkyl monomers such as methoxyethyl and ethoxyethyl (meth) acrylate;
さらに、酢酸ビニル、プロピオン酸ビニル、スチレン、α−メチルスチレン、Ｎ−ビニルカプロラクタムなどのビニル系モノマー；（メタ）アクリル酸グリシジルなどのエポキシ基含有アクリル系モノマー；（メタ）アクリル酸ポリエチレングリコール、（メタ）アクリル酸ポリプロピレングリコール、（メタ）アクリル酸メトキシエチレングリコール、（メタ）アクリル酸メトキシポリプロピレングリコールなどのグリコール系アクリルエステルモノマー；（メタ）アクリル酸テトラヒドロフルフリル、フッ素（メタ）アクリレート、シリコーン（メタ）アクリレートや２−メトキシエチルアクリレートなどのアクリル酸エステル系モノマーなども使用することができる。 Furthermore, vinyl monomers such as vinyl acetate, vinyl propionate, styrene, α-methylstyrene, N-vinylcaprolactam; epoxy group-containing acrylic monomers such as glycidyl (meth) acrylate; polyethylene glycol (meth) acrylate, ( Glycol acrylic ester monomers such as (meth) acrylic acid polypropylene glycol, (meth) acrylic acid methoxyethylene glycol, (meth) acrylic acid methoxypolypropylene glycol; (meth) acrylic acid tetrahydrofurfuryl, fluorine (meth) acrylate, silicone (meta ) Acrylic acid ester monomers such as acrylate and 2-methoxyethyl acrylate can also be used.
さらに、上記以外の共重合可能なモノマーとして、ケイ素原子を含有するシラン系モノマーなどがあげられる。シラン系モノマーとしては、例えば、３−アクリロキシプロピルトリエトキシシラン、ビニルトリメトキシシラン、ビニルトリエトキシシラン、４−ビニルブチルトリメトキシシラン、４−ビニルブチルトリエトキシシラン、８−ビニルオクチルトリメトキシシラン、８−ビニルオクチルトリエトキシシラン、１０−メタクリロイルオキシデシルトリメトキシシラン、１０−アクリロイルオキシデシルトリメトキシシラン、１０−メタクリロイルオキシデシルトリエトキシシラン、１０−アクリロイルオキシデシルトリエトキシシランなどがあげられる。 Furthermore, examples of copolymerizable monomers other than the above include silane monomers containing silicon atoms. Examples of the silane monomer include 3-acryloxypropyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, 4-vinylbutyltrimethoxysilane, 4-vinylbutyltriethoxysilane, and 8-vinyloctyltrimethoxysilane. 8-vinyloctyltriethoxysilane, 10-methacryloyloxydecyltrimethoxysilane, 10-acryloyloxydecyltrimethoxysilane, 10-methacryloyloxydecyltriethoxysilane, 10-acryloyloxydecyltriethoxysilane, and the like.
本発明の（メタ）アクリル系ポリマーは、耐久性、特に耐熱性を考慮し、重量平均分子量（ＭＷ）が１５０万以上の範囲である。好ましくは、１６０万〜３００万の範囲のものが用いられる。さらに、１８０万〜２８０万であることがより好ましく、２００万〜２６０万であることがさらに好ましい。重量平均分子量が１５０万よりも小さいと、耐熱性の点で好ましくない。また、重量平均分子量が大きくなりすぎると貼り合せ性、粘着力が低下する場合がある。なお、重量平均分子量は、ＧＰＣ（ゲル・パーミエーション・クロマトグラフィー）により測定し、ポリスチレン換算により算出された値をいう。 The (meth) acrylic polymer of the present invention has a weight average molecular weight (M w ) in the range of 1.5 million or more in consideration of durability, particularly heat resistance. Preferably, the thing of the range of 1.6 million-3 million is used. Furthermore, it is more preferable that it is 1.8 million to 2.8 million, and it is further more preferable that it is 2 million to 2.6 million. A weight average molecular weight of less than 1,500,000 is not preferable in terms of heat resistance. Moreover, when a weight average molecular weight becomes large too much, bondability and adhesive force may fall. The weight average molecular weight is a value measured by GPC (gel permeation chromatography) and calculated in terms of polystyrene.
本発明の（メタ）アクリル系ポリマーは、さらに、ＧＰＣ（ゲル・パーミエーション・クロマトグラフィー）により測定し、ポリスチレン換算により算出された値での重量平均分子量において、分子量１０万以下のポリマーを、ポリマー全体の１５エリア％以下で含むことが好ましい。重量平均分子量の分布において、分子量１０万以下のポリマーのような低分子量成分が粘着剤層にある一定量以下であれば、ポリマーの凝集力の低下防止、耐久性の低下防止、あるいはリワーク性の維持に効果的である。低分子量成分の割合を小さくするには、ポリマーを重合する際のモノマー濃度、開始剤種、開始剤量、重合温度を制御することで達成できる。モノマー濃度は高く、重合温度を低くする方が良い。具体的には開始剤として、アゾイソブチロニトリルやベンゾイルパーオキサイドを用いた場合は重合温度５０〜６０℃で８時間程度反応することで達成できる。重合温度が低すぎると重合反応は開始せず、高すぎると低分子成分が増加し、耐久性の低下を招く場合がある。 The (meth) acrylic polymer of the present invention is further measured by GPC (gel permeation chromatography) and a polymer having a molecular weight of 100,000 or less in terms of a weight average molecular weight calculated by polystyrene conversion It is preferable to include it in 15 area% or less of the whole. In the distribution of the weight average molecular weight, if a low molecular weight component such as a polymer having a molecular weight of 100,000 or less is not more than a certain amount in the pressure-sensitive adhesive layer, the polymer cohesive strength is prevented from being lowered, the durability is prevented from being lowered, or the reworkability is reduced. It is effective for maintenance. The ratio of the low molecular weight component can be reduced by controlling the monomer concentration, initiator type, initiator amount, and polymerization temperature when polymerizing the polymer. The monomer concentration is high, and it is better to lower the polymerization temperature. Specifically, when azoisobutyronitrile or benzoyl peroxide is used as an initiator, this can be achieved by reacting at a polymerization temperature of 50 to 60 ° C. for about 8 hours. When the polymerization temperature is too low, the polymerization reaction does not start. When the polymerization temperature is too high, the low molecular components increase, and the durability may be lowered.
このような（メタ）アクリル系ポリマーの製造は、溶液重合、塊状重合、乳化重合、各種ラジカル重合などの公知の製造方法を適宜選択できる。また、得られる（メタ）アクリル系ポリマーは、ランダム共重合体、ブロック共重合体、グラフト共重合体などいずれでもよい。 The production of such a (meth) acrylic polymer can be appropriately selected from known production methods such as solution polymerization, bulk polymerization, emulsion polymerization, and various radical polymerizations. Further, the (meth) acrylic polymer obtained may be any of a random copolymer, a block copolymer, a graft copolymer, and the like.
なお、溶液重合においては、重合溶媒として、例えば、酢酸エチル、トルエンなどが用いられる。具体的な溶液重合例としては、反応は窒素などの不活性ガス気流下で、重合開始剤を加え、通常、５０〜７０℃程度で、５〜３０時間程度の反応条件で行われる。 In solution polymerization, for example, ethyl acetate, toluene or the like is used as a polymerization solvent. As a specific example of solution polymerization, the reaction is performed under an inert gas stream such as nitrogen, and a polymerization initiator is added, and the reaction is usually performed at about 50 to 70 ° C. under reaction conditions of about 5 to 30 hours.
ラジカル重合に用いられる重合開始剤、連鎖移動剤、乳化剤などは特に限定されず適宜選択して使用することができる。なお、（メタ）アクリル系ポリマーの重量平均分子量は、重合開始剤、連鎖移動剤の使用量、反応条件により制御可能であり、これらの種類に応じて適宜のその使用量が調整される。 The polymerization initiator, chain transfer agent, emulsifier and the like used for radical polymerization are not particularly limited and can be appropriately selected and used. In addition, the weight average molecular weight of a (meth) acrylic-type polymer can be controlled by the usage-amount of a polymerization initiator and a chain transfer agent, and reaction conditions, The usage-amount is suitably adjusted according to these kinds.
重合開始剤としては、例えば、２，２’−アゾビスイソブチロニトリル、２，２’−アゾビス（２−アミジノプロパン）ジヒドロクロライド、２，２’−アゾビス［２−（５−メチル−２−イミダゾリン−２−イル）プロパン］ジヒドロクロライド、２，２’−アゾビス（２−メチルプロピオンアミジン）二硫酸塩、２，２’−アゾビス（Ｎ，Ｎ’−ジメチレンイソブチルアミジン）、２，２’−アゾビス［Ｎ−（２−カルボキシエチル）−２−メチルプロピオンアミジン］ハイドレート（和光純薬社製、ＶＡ−０５７）などのアゾ系開始剤、過硫酸カリウム、過硫酸アンモニウムなどの過硫酸塩、ジ（２−エチルヘキシル）パーオキシジカーボネート、ジ（４−ｔ−ブチルシクロヘキシル）パーオキシジカーボネート、ジ−ｓｅｃ−ブチルパーオキシジカーボネート、ｔ−ブチルパーオキシネオデカノエート、ｔ−ヘキシルパーオキシピバレート、ｔ−ブチルパーオキシピバレート、ジラウロイルパーオキシド、ジ−ｎ−オクタノイルパーオキシド、１，１，３，３−テトラメチルブチルパーオキシ−２−エチルヘキサノエート、ジ（４−メチルベンゾイル）パーオキシド、ジベンゾイルパーオキシド、ｔ−ブチルパーオキシイソブチレート、１，１−ジ（ｔ−ヘキシルパーオキシ）シクロヘキサン、ｔ−ブチルハイドロパーオキシド、過酸化水素などの過酸化物系開始剤、過硫酸塩と亜硫酸水素ナトリウムの組み合わせ、過酸化物とアスコルビン酸ナトリウムの組み合わせなどの過酸化物と還元剤とを組み合わせたレドックス系開始剤などをあげることができるが、これらに限定されるものではない。 Examples of the polymerization initiator include 2,2′-azobisisobutyronitrile, 2,2′-azobis (2-amidinopropane) dihydrochloride, 2,2′-azobis [2- (5-methyl-2). -Imidazolin-2-yl) propane] dihydrochloride, 2,2'-azobis (2-methylpropionamidine) disulfate, 2,2'-azobis (N, N'-dimethyleneisobutylamidine), 2,2 '-Azobis [N- (2-carboxyethyl) -2-methylpropionamidine] hydrate (manufactured by Wako Pure Chemical Industries, VA-057) and other azo initiators, and persulfates such as potassium persulfate and ammonium persulfate , Di (2-ethylhexyl) peroxydicarbonate, di (4-t-butylcyclohexyl) peroxydicarbonate, di-sec-butyl -Oxydicarbonate, t-butylperoxyneodecanoate, t-hexylperoxypivalate, t-butylperoxypivalate, dilauroyl peroxide, di-n-octanoyl peroxide, 1,1,3 , 3-tetramethylbutylperoxy-2-ethylhexanoate, di (4-methylbenzoyl) peroxide, dibenzoyl peroxide, t-butylperoxyisobutyrate, 1,1-di (t-hexylperoxy) ) Peroxides such as cyclohexane, t-butyl hydroperoxide, hydrogen peroxide, peroxides and sodium bisulfite, peroxides and sodium ascorbate Redox initiators combined with Not intended to be.
前記重合開始剤は、単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量はモノマー１００重量部に対して、０．００５〜１重量部程度であることが好ましく、０．０２〜０．５重量部程度であることがより好ましい。 The polymerization initiator may be used alone or in combination of two or more, but the total content is 0.005 to 1 part by weight with respect to 100 parts by weight of the monomer. Is preferably about 0.02 to 0.5 parts by weight.
なお、重合開始剤として、例えば、２，２’−アゾビスイソブチロニトリルを用いて、前記重量平均分子量の（メタ）アクリル系ポリマーを製造するには、重合開始剤の使用量は、モノマー成分の全量１００重量部に対して、０．０６〜０．２重量部程度とするのが好ましく、さらには０．０８〜０．１７５重量部程度とするのが好ましい。 In order to produce the (meth) acrylic polymer having the weight average molecular weight using, for example, 2,2′-azobisisobutyronitrile as the polymerization initiator, the amount of the polymerization initiator used is a monomer. The amount is preferably about 0.06 to 0.2 part by weight, more preferably about 0.08 to 0.175 part by weight with respect to 100 parts by weight of the total amount of the components.
連鎖移動剤としては、例えば、ラウリルメルカプタン、グリシジルメルカプタン、メルカプト酢酸、２−メルカプトエタノール、チオグリコール酸、チオグルコール酸２−エチルヘキシル、２，３−ジメルカプト−１−プロパノールなどがあげられる。連鎖移動剤は、単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量はモノマー成分の全量１００重量部に対して、０．１重量部程度以下である。 Examples of the chain transfer agent include lauryl mercaptan, glycidyl mercaptan, mercaptoacetic acid, 2-mercaptoethanol, thioglycolic acid, 2-ethylhexyl thioglycolate, and 2,3-dimercapto-1-propanol. The chain transfer agent may be used alone or in combination of two or more, but the total content is 0.1 parts by weight with respect to 100 parts by weight of the total amount of monomer components. Less than or equal to
また、乳化重合する場合に用いる乳化剤としては、例えば、ラウリル硫酸ナトリウム、ラウリル硫酸アンモニウム、ドデシルベンゼンスルホン酸ナトリウム、ポリオキシエチレンアルキルエーテル硫酸アンモニウム、ポリオキシエチレンアルキルフェニルエーテル硫酸ナトリウムなどのアニオン系乳化剤、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレン脂肪酸エステル、ポリオキシエチレン−ポリオキシプロピレンブロックポリマーなどのノニオン系乳化剤などがあげられる。これらの乳化剤は、単独で用いてもよく２種以上を併用してもよい。 Examples of the emulsifier used in emulsion polymerization include anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzenesulfonate, ammonium polyoxyethylene alkyl ether sulfate, sodium polyoxyethylene alkyl phenyl ether sulfate, and polyoxy Nonionic emulsifiers such as ethylene alkyl ether, polyoxyethylene alkyl phenyl ether, polyoxyethylene fatty acid ester, and polyoxyethylene-polyoxypropylene block polymer are listed. These emulsifiers may be used alone or in combination of two or more.
さらに、反応性乳化剤として、プロペニル基、アリルエーテル基などのラジカル重合性官能基が導入された乳化剤として、具体的には、例えば、アクアロンＨＳ−１０、ＨＳ−２０、ＫＨ−１０、ＢＣ−０５、ＢＣ−１０、ＢＣ−２０（以上、いずれも第一工業製薬社製）、アデカリアソープＳＥ１０Ｎ（旭電化工社製）などがある。反応性乳化剤は、重合後にポリマー鎖に取り込まれるため、耐水性がよくなり好ましい。乳化剤の使用量は、モノマー成分の全量１００重量部に対して、０．３〜５重量部、重合安定性や機械的安定性から０．５〜１重量部がより好ましい。 Further, as reactive emulsifiers, as emulsifiers into which radical polymerizable functional groups such as propenyl groups and allyl ether groups are introduced, specifically, for example, Aqualon HS-10, HS-20, KH-10, BC-05 BC-10, BC-20 (all of which are manufactured by Daiichi Kogyo Seiyaku Co., Ltd.), Adekaria soap SE10N (manufactured by Asahi Denka Kogyo Co., Ltd.), and the like. Reactive emulsifiers are preferable because they are incorporated into the polymer chain after polymerization and thus have improved water resistance. The amount of the emulsifier used is more preferably 0.3 to 5 parts by weight and 0.5 to 1 part by weight from the viewpoint of polymerization stability and mechanical stability with respect to 100 parts by weight of the total amount of monomer components.
本発明の粘着剤組成物は、シランカップリング剤および特定の置換基を有するシロキサン化合物を含む。 The pressure-sensitive adhesive composition of the present invention contains a silane coupling agent and a siloxane compound having a specific substituent.
シランカップリング剤を用いることにより、接着力および耐久性があがる。シランカップリング剤としては、具体的には、たとえば、３−グリシドキシプロピルトリメトキシシラン、３−グリシドキシプロピルトリエトキシシラン、３−グリシドキシプロピルメチルジエトキシシラン、２−（３，４−エポキシシクロヘキシル）エチルトリメトキシシランなどのエポキシ基含有シランカップリング剤、３−アミノプロピルトリメトキシシラン、Ｎ−２−（アミノエチル）−３−アミノプロピルメチルジメトキシシラン、３−トリエトキシシリル−Ｎ−（１，３−ジメチルブチリデン）プロピルアミン、Ｎ−フェニル−γ−アミノプロピルトリメトキシシランなどのアミノ基含有シランカップリング剤、３−アクリロキシプロピルトリメトキシシラン、３−メタクリロキシプロピルトリエトキシシランなどの（メタ）アクリル基含有シランカップリング剤、３−イソシアネートプロピルトリエトキシシランなどのイソシアネート基含有シランカップリング剤などがあげられる。このうち、加湿時の耐久性およびリワーク性の向上につながる為、特に芳香環含有シランカップリング剤を使用することが好ましいが、限定はされず、他のシランカップリング剤でも、耐久性の向上などに好ましい。 By using a silane coupling agent, the adhesive strength and durability are improved. Specific examples of the silane coupling agent include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 2- (3, Epoxy group-containing silane coupling agents such as 4-epoxycyclohexyl) ethyltrimethoxysilane, 3-aminopropyltrimethoxysilane, N-2- (aminoethyl) -3-aminopropylmethyldimethoxysilane, 3-triethoxysilyl- Amino group-containing silane coupling agents such as N- (1,3-dimethylbutylidene) propylamine, N-phenyl-γ-aminopropyltrimethoxysilane, 3-acryloxypropyltrimethoxysilane, 3-methacryloxypropyltri (Meth) a, such as ethoxysilane Lil group-containing silane coupling agents, such as isocyanate group-containing silane coupling agents such as 3-isocyanate propyl triethoxysilane and the like. Among them, it is preferable to use an aromatic ring-containing silane coupling agent because it leads to improvement in durability and reworkability during humidification, but there is no limitation, and other silane coupling agents can also improve durability. This is preferable.
前記シランカップリング剤は、単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は前記（メタ）アクリル系ポリマー１００重量部に対し、前記シランカップリング剤０．０１〜１重量部含有してなることが好ましく、０．０２〜１重量部含有してなることがより好ましく、０．０５〜０．６重量部含有してなることがさらに好ましい。耐久性を向上させ、液晶セル等の光学部材への接着力を適度に保持する量である。 The silane coupling agent may be used alone or in combination of two or more, but the total content is 100 parts by weight of the (meth) acrylic polymer. It is preferable to contain 0.01-1 part by weight of a silane coupling agent, more preferably 0.02-1 part by weight, and 0.05-0.6 part by weight. Further preferred. It is an amount that improves durability and appropriately maintains the adhesive force to an optical member such as a liquid crystal cell.
本発明の特定の置換基を有するシロキサン化合物とは、具体的には、下記構造を有するシロキサン化合物を指す。
特に、Ｒがメチル基またはフェニル基を表し、同一分子中にその両方の基をランダムな配置で、あるいはブロックとしてまとまった配置で含むようなシロキサン化合物が好ましい。 In particular, a siloxane compound in which R represents a methyl group or a phenyl group and includes both groups in the same molecule in a random arrangement or in a block arrangement.
シロキサン化合物は、前記（メタ）アクリル系ポリマー１００重量部に対して、０．０１〜１０重量部含有される。好ましくは、０．３〜３．０重量部であり、より好ましくは、０．５〜２．５重量部である。 The siloxane compound is contained in an amount of 0.01 to 10 parts by weight with respect to 100 parts by weight of the (meth) acrylic polymer. Preferably, it is 0.3-3.0 weight part, More preferably, it is 0.5-2.5 weight part.
さらに、本発明では、任意に、他の架橋剤として、イソシアネート系架橋剤を含有する。このような架橋剤の例としては、トリレンジイソシアネート、クロルフェニレンジイソシアナート、テトラメチレンジイソシアナート、キシリレンジイソシアネート、ジフェニルメタンジイソシアネート、水添されたジフェニルメタンジイソシアネートなどのイソシアネートモノマー及びこれらイソシアネートモノマーをトリメチロールプロパンなどと付加したイソシアネート化合物やイソシアヌレート化物、ビュレット型化合物、さらにはポリエーテルポリオールやポリエステルポリオール、アクリルポリオール、ポリブタジエンポリオール、ポリイソプレンポリオールなど付加反応させたウレタンプレポリマー型のイソシアネートなどを挙げることができる。特に好ましくは、ポリイソシアネート化合物であり、ヘキサメチレンジイソシアネート、水添キシリレンジイソシアネート、およびイソホロンジイソシアネートからなる群より選択される1種またはそれに由来するポリイソシアネート化合物である。ここで、ヘキサメチレンジイソシアネート、水添キシリレンジイソシアネート、およびイソホロンジイソシアネートからなる群より選択される1種またはそれに由来するポリイソシアネート化合物には、ヘキサメチレンジイソシアネート、水添キシリレンジイソシアネート、イソホロンジイソシアネート、ポリオール変性ヘキサメチレンジイソシアネート、ポリオール変性水添キシリレンジイソシアネート、トリマー型水添キシリレンジイソシアネート、およびポリオール変性イソホロンジイソシアネートなどが含まれる。例示したポリイソシアネート化合物は、水酸基との反応が、特にポリマーに含まれる酸、塩基を触媒のようにして、迅速に進む為、特に架橋の早さに寄与し、好ましい。 Furthermore, in this invention, an isocyanate type crosslinking agent is contained arbitrarily as another crosslinking agent. Examples of such cross-linking agents include isocyanate monomers such as tolylene diisocyanate, chlorophenylene diisocyanate, tetramethylene diisocyanate, xylylene diisocyanate, diphenylmethane diisocyanate, hydrogenated diphenylmethane diisocyanate and trimethylol. Examples include isocyanate compounds added with propane, isocyanurates, burette type compounds, and urethane prepolymer type isocyanates such as polyether polyols, polyester polyols, acrylic polyols, polybutadiene polyols and polyisoprene polyols that have undergone addition reaction. it can. Particularly preferred is a polyisocyanate compound, which is one or a polyisocyanate compound derived from one selected from the group consisting of hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate. Here, hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, isophorone diisocyanate, polyol-modified is selected from the group consisting of hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate or a polyisocyanate compound derived therefrom. Examples include hexamethylene diisocyanate, polyol-modified hydrogenated xylylene diisocyanate, trimer-type hydrogenated xylylene diisocyanate, and polyol-modified isophorone diisocyanate. The exemplified polyisocyanate compound is preferable because the reaction with a hydroxyl group proceeds rapidly, particularly using an acid or base contained in the polymer as a catalyst, and thus contributes to the speed of crosslinking.
上記イソシアネート系架橋剤は１種を単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、前記（メタ）アクリル系ポリマー１００重量部に対し、前記ポリイソシアネート化合物架橋剤を０．０１〜２重量部含有してなることが好ましく、０．０２〜２重量部含有してなることがより好ましく、０．０５〜１．５重量部含有してなることがさらに好ましい。凝集力、耐久性試験での剥離の阻止などを考慮して適宜含有させることが可能である。 The isocyanate-based crosslinking agent may be used alone or in combination of two or more, but the total content is 100 parts by weight of the (meth) acrylic polymer. On the other hand, it is preferable to contain 0.01-2 weight part of the said polyisocyanate compound crosslinking agent, It is more preferable to contain 0.02-2 weight part, 0.05-1.5 weight part containing More preferably, It can be appropriately contained in consideration of cohesive force and prevention of peeling in a durability test.
本発明においては、架橋剤として、過酸化物を加えることも可能である。過酸化物としては、加熱または光照射によりラジカル活性種を発生して粘着剤組成物のベースポリマーの架橋を進行させるものであれば適宜使用可能であるが、作業性や安定性を勘案して、１分間半減期温度が８０℃〜１６０℃である過酸化物を使用することが好ましく、９０℃〜１４０℃である過酸化物を使用することがより好ましい。 In the present invention, a peroxide can be added as a crosslinking agent. As the peroxide, any radical active species can be used as long as it generates radical active species by heating or light irradiation to advance the crosslinking of the base polymer of the pressure-sensitive adhesive composition. However, in consideration of workability and stability. It is preferable to use a peroxide having a one-minute half-life temperature of 80 ° C. to 160 ° C., and more preferable to use a peroxide having a 90 ° C. to 140 ° C.
用いることができる過酸化物としては、たとえば、ジ（２−エチルヘキシル）パーオキシジカーボネート（１分間半減期温度：９０．６℃）、ジ（４−ｔ−ブチルシクロヘキシル）パーオキシジカーボネート（１分間半減期温度：９２．１℃）、ジ−ｓｅｃ−ブチルパーオキシジカーボネート（１分間半減期温度：９２．４℃）、ｔ−ブチルパーオキシネオデカノエート（１分間半減期温度：１０３．５℃）、ｔ−ヘキシルパーオキシピバレート（１分間半減期温度：１０９．１℃）、ｔ−ブチルパーオキシピバレート（１分間半減期温度：１１０．３℃）、ジラウロイルパーオキシド（１分間半減期温度：１１６．４℃）、ジ−ｎ−オクタノイルパーオキシド（１分間半減期温度：１１７．４℃）、１，１，３，３−テトラメチルブチルパーオキシ−２−エチルヘキサノエート（１分間半減期温度：１２４．３℃）、ジ（４−メチルベンゾイル）パーオキシド（１分間半減期温度：１２８．２℃）、ジベンゾイルパーオキシド（１分間半減期温度：１３０．０℃）、ｔ−ブチルパーオキシイソブチレート（１分間半減期温度：１３６．１℃）、１，１−ジ（ｔ−ヘキシルパーオキシ）シクロヘキサン（１分間半減期温度：１４９．２℃）などがあげられる。なかでも特に架橋反応効率が優れることから、ジ（４−ｔ−ブチルシクロヘキシル）パーオキシジカーボネート（１分間半減期温度：９２．１℃）、ジラウロイルパーオキシド（１分間半減期温度：１１６．４℃）、ジベンゾイルパーオキシド（１分間半減期温度：１３０．０℃）などが好ましく用いられる。 Examples of peroxides that can be used include di (2-ethylhexyl) peroxydicarbonate (1 minute half-life temperature: 90.6 ° C.), di (4-t-butylcyclohexyl) peroxydicarbonate (1 Minute half-life temperature: 92.1 ° C.), di-sec-butyl peroxydicarbonate (1 minute half-life temperature: 92.4 ° C.), t-butyl peroxyneodecanoate (1 minute half-life temperature: 103 0.5 ° C), t-hexyl peroxypivalate (1 minute half-life temperature: 109.1 ° C), t-butyl peroxypivalate (1 minute half-life temperature: 110.3 ° C), dilauroyl peroxide ( 1 minute half-life temperature: 116.4 ° C.), di-n-octanoyl peroxide (1 minute half-life temperature: 117.4 ° C.), 1,1,3,3-tetramethylbutyl Oxy-2-ethylhexanoate (1 minute half-life temperature: 124.3 ° C), di (4-methylbenzoyl) peroxide (1 minute half-life temperature: 128.2 ° C), dibenzoyl peroxide (half-minute for 1 minute) Period temperature: 130.0 ° C.), t-butyl peroxyisobutyrate (1 minute half-life temperature: 136.1 ° C.), 1,1-di (t-hexylperoxy) cyclohexane (1 minute half-life temperature: 149.2 ° C.). Especially, since the crosslinking reaction efficiency is excellent, di (4-t-butylcyclohexyl) peroxydicarbonate (1 minute half-life temperature: 92.1 ° C.), dilauroyl peroxide (1 minute half-life temperature: 116. 4 ° C), dibenzoyl peroxide (1 minute half-life temperature: 130.0 ° C) and the like are preferably used.
なお、過酸化物の半減期とは、過酸化物の分解速度を表す指標であり、過酸化物の残存量が半分になるまでの時間をいう。任意の時間で半減期を得るための分解温度や、任意の温度での半減期時間に関しては、メーカーカタログなどに記載されており、たとえば、日本油脂株式会社の「有機過酸化物カタログ第９版（２００３年５月）」などに記載されている。 The peroxide half-life is an index representing the decomposition rate of the peroxide, and means the time until the remaining amount of peroxide is reduced to half. The decomposition temperature for obtaining a half-life at an arbitrary time and the half-life time at an arbitrary temperature are described in the manufacturer catalog, for example, “Organic peroxide catalog 9th edition by Nippon Oil & Fats Co., Ltd.” (May 2003) ".
前記過酸化物は１種を単独で使用してもよく、また２種以上を混合して使用してもよいが、全体としての含有量は、前記（メタ）アクリル系ポリマー１００重量部に対し、前記過酸化物０．０１〜２重量部であり、０．０４〜１．５重量部含有してなることが好ましく、０．０５〜１重量部含有してなることがより好ましい。加工性、リワーク性、架橋安定性、剥離性などの調整の為に、この範囲内で適宜選択される。 The peroxide may be used alone or as a mixture of two or more, but the total content is based on 100 parts by weight of the (meth) acrylic polymer. The peroxide is 0.01 to 2 parts by weight, preferably 0.04 to 1.5 parts by weight, and more preferably 0.05 to 1 part by weight. In order to adjust processability, reworkability, cross-linking stability, peelability, and the like, it is appropriately selected within this range.
なお、反応処理後の残存した過酸化物分解量の測定方法としては、たとえば、ＨＰＬＣ（高速液体クロマトグラフィー）により測定することができる。 In addition, as a measuring method of the peroxide decomposition amount which remained after the reaction process, it can measure by HPLC (high performance liquid chromatography), for example.
より具体的には、たとえば、反応処理後の粘着剤組成物を約０．２ｇずつ取り出し、酢酸エチル１０ｍｌに浸漬し、振とう機で２５℃下、１２０ｒｐｍで３時間振とう抽出した後、室温で３日間静置する。次いで、アセトニトリル１０ｍｌ加えて、２５℃下、１２０ｒｐｍで３０分振とうし、メンブランフィルター（０．４５μｍ）によりろ過して得られた抽出液約１０μｌをＨＰＬＣに注入して分析し、反応処理後の過酸化物量とすることができる。 More specifically, for example, about 0.2 g of the pressure-sensitive adhesive composition after the reaction treatment is taken out, immersed in 10 ml of ethyl acetate, extracted by shaking at 25 ° C. and 120 rpm for 3 hours with a shaker, and then at room temperature. Leave for 3 days. Next, 10 ml of acetonitrile was added, shaken at 120 rpm at 25 ° C. for 30 minutes, and about 10 μl of the extract obtained by filtration through a membrane filter (0.45 μm) was injected into the HPLC for analysis. The amount of peroxide can be set.
また、さらに、前記架橋剤としては、他の有機系架橋剤や多官能性金属キレートを用いることができる。有機系架橋剤としては、エポキシ系架橋剤、イミン系架橋剤などがあげられる。多官能性金属キレートは、多価金属が有機化合物と共有結合または配位結合しているものである。多価金属原子としては、Ａｌ、Ｃｒ、Ｚｒ、Ｃｏ、Ｃｕ、Ｆｅ、Ｎｉ、Ｖ、Ｚｎ、Ｉｎ、Ｃａ、Ｍｇ、Ｍｎ、Ｙ、Ｃｅ、Ｓｒ、Ｂａ、Ｍｏ、Ｌａ、Ｓｎ、Ｔｉ等があげられる。共有結合または配位結合する有機化合物中の原子としては酸素原子等があげられ、有機化合物としてはアルキルエステル、アルコール化合物、カルボン酸化合物、エーテル化合物、ケトン化合物等があげられる。 Furthermore, as said crosslinking agent, another organic type crosslinking agent and polyfunctional metal chelate can be used. Examples of the organic crosslinking agent include an epoxy crosslinking agent and an imine crosslinking agent. A polyfunctional metal chelate is one in which a polyvalent metal is covalently or coordinately bonded to an organic compound. Examples of polyvalent metal atoms include Al, Cr, Zr, Co, Cu, Fe, Ni, V, Zn, In, Ca, Mg, Mn, Y, Ce, Sr, Ba, Mo, La, Sn, Ti, and the like. can give. Examples of the atom in the organic compound that is covalently or coordinately bonded include an oxygen atom, and the organic compound includes an alkyl ester, an alcohol compound, a carboxylic acid compound, an ether compound, a ketone compound, and the like.
前記架橋剤により、粘着剤層を形成するが、粘着剤層の形成にあたっては、架橋剤全体の添加量を調整することとともに、架橋処理温度や架橋処理時間の影響を十分考慮する必要がある。 The pressure-sensitive adhesive layer is formed by the crosslinking agent. In forming the pressure-sensitive adhesive layer, it is necessary to adjust the addition amount of the entire crosslinking agent and sufficiently consider the influence of the crosslinking treatment temperature and the crosslinking treatment time.
使用する架橋剤によって架橋処理温度や架橋処理時間は、調整が可能である。架橋処理温度は１７０℃以下であることが好ましい。 The crosslinking treatment temperature and the crosslinking treatment time can be adjusted depending on the crosslinking agent used. The crosslinking treatment temperature is preferably 170 ° C. or lower.
また、かかる架橋処理は、粘着剤層の乾燥工程時の温度で行ってもよいし、乾燥工程後に別途架橋処理工程を設けて行ってもよい。 Moreover, this crosslinking process may be performed at the temperature at the time of the drying process of an adhesive layer, and may be performed by providing a crosslinking process process separately after a drying process.
また、架橋処理時間に関しては、生産性や作業性を考慮して設定することができるが、通常０．２〜２０分間程度であり、０．５〜１０分間程度であることが好ましい。 The crosslinking treatment time can be set in consideration of productivity and workability, but is usually about 0.2 to 20 minutes, preferably about 0.5 to 10 minutes.
さらに本発明の粘着剤組成物には、その他の公知の添加剤を含有していてもよく、たとえば、着色剤、顔料などの粉体、染料、界面活性剤、可塑剤、粘着性付与剤、表面潤滑剤、レベリング剤、軟化剤、酸化防止剤、老化防止剤、光安定剤、紫外線吸収剤、重合禁止剤、無機または有機の充填剤、金属粉、粒子状、箔状物などを使用する用途に応じて適宜添加することができる。また、制御できる範囲内で、還元剤を加えてのレドックス系を採用してもよい。 Furthermore, the pressure-sensitive adhesive composition of the present invention may contain other known additives, such as powders such as colorants and pigments, dyes, surfactants, plasticizers, tackifiers, Use surface lubricants, leveling agents, softeners, antioxidants, anti-aging agents, light stabilizers, UV absorbers, polymerization inhibitors, inorganic or organic fillers, metal powders, particles, foils, etc. It can be added appropriately depending on the application. Moreover, you may employ | adopt the redox system which added a reducing agent within the controllable range.
本発明の粘着型光学フィルムなどの粘着型光学部材は、光学フィルムの少なくとも片面に、前記粘着剤により粘着剤層を形成したものである。 The pressure-sensitive adhesive optical member such as the pressure-sensitive adhesive optical film of the present invention has a pressure-sensitive adhesive layer formed on at least one surface of the optical film with the pressure-sensitive adhesive.
粘着剤層を形成する方法としては、例えば、前記粘着剤組成物を剥離処理したセパレーターなどに塗布し、重合溶剤などを乾燥除去して粘着剤層を形成した後に光学フィルムに転写する方法、または光学フィルムに前記粘着剤組成物を塗布し、重合溶剤などを乾燥除去して粘着剤層を光学フィルムに形成する方法などにより作製される。なお、粘着剤の塗布にあたっては、適宜に、重合溶剤以外の一種以上の溶剤を新たに加えてもよい。 As a method for forming the pressure-sensitive adhesive layer, for example, a method in which the pressure-sensitive adhesive composition is applied to a release-treated separator, and the polymerization solvent is dried and removed to form a pressure-sensitive adhesive layer, and then transferred to an optical film, or The pressure-sensitive adhesive composition is prepared by applying the pressure-sensitive adhesive composition to an optical film, drying and removing a polymerization solvent, and the like to form a pressure-sensitive adhesive layer on the optical film. In applying the pressure-sensitive adhesive, one or more solvents other than the polymerization solvent may be added as appropriate.
剥離処理したセパレーターとしては、シリコーン剥離ライナーが好ましく用いられる。このようなライナー上に本発明の接着剤組成物を塗布、乾燥させて粘着剤層を形成する工程において、粘着剤を乾燥させる方法としては、目的に応じて、適宜、適切な方法が採用され得る。好ましくは、上記塗布膜を過熱乾燥する方法が用いられる。加熱乾燥温度は、好ましくは４０℃〜２００℃であり、さらに好ましくは、５０℃〜１８０℃であり、特に好ましくは７０℃〜１７０℃である。加熱温度を上記の範囲とすることによって、優れた粘着特性を有する粘着剤を得ることができる。 A silicone release liner is preferably used as the release-treated separator. In the step of applying the adhesive composition of the present invention on such a liner and drying to form a pressure-sensitive adhesive layer, a method for drying the pressure-sensitive adhesive is appropriately employed depending on the purpose. obtain. Preferably, a method of heating and drying the coating film is used. The heat drying temperature is preferably 40 ° C to 200 ° C, more preferably 50 ° C to 180 ° C, and particularly preferably 70 ° C to 170 ° C. By setting the heating temperature within the above range, an adhesive having excellent adhesive properties can be obtained.
乾燥時間は、適宜、適切な時間が採用され得る。上記乾燥時間は、好ましくは５秒〜２０分、さらに好ましくは５秒〜１０分、特に好ましくは、１０秒〜５分である。 As the drying time, an appropriate time can be adopted as appropriate. The drying time is preferably 5 seconds to 20 minutes, more preferably 5 seconds to 10 minutes, and particularly preferably 10 seconds to 5 minutes.
また、光学フィルムの表面に、アンカー層を形成したり、コロナ処理、プラズマ処理などの各種易接着処理を施した後に粘着剤層を形成することができる。また、粘着剤層の表面には易接着処理をおこなってもよい。 Moreover, an adhesive layer can be formed after forming an anchor layer on the surface of an optical film, or performing various easy-adhesion treatments, such as a corona treatment and a plasma treatment. Moreover, you may perform an easily bonding process on the surface of an adhesive layer.
粘着剤層の形成方法としては、各種方法が用いられる。具体的には、例えば、ロールコート、キスロールコート、グラビアコート、リバースコート、ロールブラッシュ、スプレーコート、ディップロールコート、バーコート、ナイフコート、エアーナイフコート、カーテンコート、リップコート、ダイコーターなどによる押出しコート法などの方法があげられる。 Various methods are used as a method of forming the pressure-sensitive adhesive layer. Specifically, for example, roll coat, kiss roll coat, gravure coat, reverse coat, roll brush, spray coat, dip roll coat, bar coat, knife coat, air knife coat, curtain coat, lip coat, die coater, etc. Examples thereof include an extrusion coating method.
粘着剤層の厚さは、特に制限されず、例えば、１〜１００μｍ程度である。好ましくは、２〜５０μｍ、より好ましくは２〜４０μｍであり、さらに好ましくは、５〜３５μｍである。 The thickness in particular of an adhesive layer is not restrict | limited, For example, it is about 1-100 micrometers. Preferably, it is 2-50 micrometers, More preferably, it is 2-40 micrometers, More preferably, it is 5-35 micrometers.
前記粘着剤層が露出する場合には、実用に供されるまで剥離処理したシート（セパレーター）で粘着剤層を保護してもよい。 When the pressure-sensitive adhesive layer is exposed, the pressure-sensitive adhesive layer may be protected with a sheet (separator) that has been subjected to a release treatment until practical use.
セパレーターの構成材料としては、例えば、ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート、ポリエステルフィルムなどのプラスチックフィルム、紙、布、不織布などの多孔質材料、ネット、発泡シート、金属箔、およびこれらのラミネート体などの適宜な薄葉体などをあげることができるが、表面平滑性に優れる点からプラスチックフィルムが好適に用いられる。 Examples of the constituent material of the separator include, for example, plastic films such as polyethylene, polypropylene, polyethylene terephthalate, and polyester films, porous materials such as paper, cloth, and nonwoven fabric, nets, foam sheets, metal foils, and laminates thereof. A thin film can be used, but a plastic film is preferably used because of its excellent surface smoothness.
そのプラスチックフィルムとしては、前記粘着剤層を保護し得るフィルムであれば特に限定されず、例えば、ポリエチレンフィルム、ポリプロピレンフィルム、ポリブテンフィルム、ポリブタジエンフィルム、ポリメチルペンテンフイルム、ポリ塩化ビニルフィルム、塩化ビニル共重合体フィルム、ポリエチレンテレフタレートフィルム、ポリブチレンテレフタレートフィルム、ポリウレタンフィルム、エチレン−酢酸ビニル共重合体フィルムなどがあげられる。 The plastic film is not particularly limited as long as it can protect the pressure-sensitive adhesive layer. For example, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a polymethylpentene film, a polyvinyl chloride film, and a vinyl chloride co-polymer are used. Examples thereof include a polymer film, a polyethylene terephthalate film, a polybutylene terephthalate film, a polyurethane film, and an ethylene-vinyl acetate copolymer film.
前記セパレーターの厚みは、通常５〜２００μｍ、好ましくは５〜１００μｍ程度である。前記セパレーターには、必要に応じて、シリコーン系、フッ素系、長鎖アルキル系もしくは脂肪酸アミド系の離型剤、シリカ粉などによる離型および防汚処理や、塗布型、練り込み型、蒸着型などの帯電防止処理もすることもできる。特に、前記セパレーターの表面にシリコーン処理、長鎖アルキル処理、フッ素処理などの剥離処理を適宜おこなうことにより、前記粘着剤層からの剥離性をより高めることができる。 The thickness of the separator is usually about 5 to 200 μm, preferably about 5 to 100 μm. For the separator, if necessary, mold release and antifouling treatment with a silicone type, fluorine type, long chain alkyl type or fatty acid amide type release agent, silica powder, etc., coating type, kneading type, vapor deposition type It is also possible to carry out antistatic treatment such as. In particular, when the surface of the separator is appropriately subjected to a release treatment such as silicone treatment, long-chain alkyl treatment, or fluorine treatment, the peelability from the pressure-sensitive adhesive layer can be further improved.
なお、上記の粘着型光学フィルムの作製にあたって用いた、剥離処理したシートは、そのまま粘着型光学フィルムのセパレーターとして用いることができ、工程面における簡略化ができる。 In addition, the sheet | seat which carried out the peeling process used in preparation of said adhesive type optical film can be used as a separator of an adhesive type optical film as it is, and can simplify in the surface of a process.
光学フィルムとしては、液晶表示装置等の画像表示装置の形成に用いられるものが使用され、その種類は特に制限されない。例えば、光学フィルムとしては偏光板があげられる。偏光板は偏光子の片面または両面には透明保護フィルムを有するものが一般に用いられる。 As an optical film, what is used for formation of image display apparatuses, such as a liquid crystal display device, is used, and the kind in particular is not restrict | limited. For example, the optical film includes a polarizing plate. A polarizing plate having a transparent protective film on one or both sides of a polarizer is generally used.
偏光子は、特に限定されず、各種のものを使用できる。偏光子としては、例えば、ポリビニルアルコール系フィルム、部分ホルマール化ポリビニルアルコール系フィルム、エチレン・酢酸ビニル共重合体系部分ケン化フィルム等の親水性高分子フィルムに、ヨウ素や二色性染料の二色性物質を吸着させて一軸延伸したもの、ポリビニルアルコールの脱水処理物やポリ塩化ビニルの脱塩酸処理物等ポリエン系配向フィルム等があげられる。これらの中でも、ポリビニルアルコール系フィルムとヨウ素などの二色性物質からなる偏光子が好適である。これらの偏光子の厚さは特に制限されないが、一般的に５〜８０μｍ程度である。 The polarizer is not particularly limited, and various types can be used. Examples of polarizers include dichroic iodine and dichroic dyes on hydrophilic polymer films such as polyvinyl alcohol films, partially formalized polyvinyl alcohol films, and ethylene / vinyl acetate copolymer partially saponified films. Examples thereof include polyene-based oriented films such as those obtained by adsorbing substances and uniaxially stretched, polyvinyl alcohol dehydrated products and polyvinyl chloride dehydrochlorinated products. Among these, a polarizer composed of a polyvinyl alcohol film and a dichroic material such as iodine is preferable. The thickness of these polarizers is not particularly limited, but is generally about 5 to 80 μm.
ポリビニルアルコール系フィルムをヨウ素で染色し一軸延伸した偏光子は、例えば、ポリビニルアルコールをヨウ素の水溶液に浸漬することによって染色し、元長の３〜７倍に延伸することで作成することができる。必要に応じてホウ酸や硫酸亜鉛、塩化亜鉛等を含んでいても良いヨウ化カリウムなどの水溶液に浸漬することもできる。さらに必要に応じて染色前にポリビニルアルコール系フィルムを水に浸漬して水洗してもよい。ポリビニルアルコール系フィルムを水洗することでポリビニルアルコール系フィルム表面の汚れやブロッキング防止剤を洗浄することができるほかに、ポリビニルアルコール系フィルムを膨潤させることで染色のムラなどの不均一を防止する効果もある。延伸はヨウ素で染色した後に行っても良いし、染色しながら延伸しても良いし、また延伸してからヨウ素で染色しても良い。ホウ酸やヨウ化カリウムなどの水溶液や水浴中でも延伸することができる。 A polarizer obtained by dyeing a polyvinyl alcohol film with iodine and uniaxially stretching it can be prepared, for example, by immersing polyvinyl alcohol in an aqueous solution of iodine and stretching it 3 to 7 times the original length. If necessary, it can be immersed in an aqueous solution such as potassium iodide which may contain boric acid, zinc sulfate, zinc chloride or the like. Further, if necessary, the polyvinyl alcohol film may be immersed in water and washed before dyeing. In addition to washing the polyvinyl alcohol film surface with dirt and anti-blocking agents by washing the polyvinyl alcohol film with water, it also has the effect of preventing unevenness such as uneven coloring by swelling the polyvinyl alcohol film. is there. Stretching may be performed after dyeing with iodine, may be performed while dyeing, or may be dyed with iodine after stretching. The film can be stretched even in an aqueous solution such as boric acid or potassium iodide or in a water bath.
透明保護フィルムを構成する材料としては、例えば透明性、機械的強度、熱安定性、水分遮断性、等方性などに優れる熱可塑性樹脂が用いられる。このような熱可塑性樹脂の具体例としては、トリアセチルセルロース等のセルロース樹脂、ポリエステル樹脂、ポリエーテルスルホン樹脂、ポリスルホン樹脂、ポリカーボネート樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリオレフィン樹脂、（メタ）アクリル樹脂、環状ポリオレフィン樹脂（ノルボルネン系樹脂）、ポリアリレート樹脂、ポリスチレン樹脂、ポリビニルアルコール樹脂、およびこれらの混合物があげられる。なお、偏光子の片側には、透明保護フィルムが接着剤層により貼り合わされるが、他の片側には、透明保護フィルムとして、（メタ）アクリル系、ウレタン系、アクリルウレタン系、エポキシ系、シリコーン系等の熱硬化性樹脂または紫外線硬化型樹脂を用いることができる。透明保護フィルム中には任意の適切な添加剤が１種類以上含まれていてもよい。添加剤としては、例えば、紫外線吸収剤、酸化防止剤、滑剤、可塑剤、離型剤、着色防止剤、難燃剤、核剤、帯電防止剤、顔料、着色剤などがあげられる。透明保護フィルム中の上記熱可塑性樹脂の含有量は、好ましくは５０〜１００重量％、より好ましくは５０〜９９重量％、さらに好ましくは６０〜９８重量％、特に好ましくは７０〜９７重量％である。透明保護フィルム中の上記熱可塑性樹脂の含有量が５０重量％以下の場合、熱可塑性樹脂が本来有する高透明性等が十分に発現できないおそれがある。 As a material constituting the transparent protective film, for example, a thermoplastic resin excellent in transparency, mechanical strength, thermal stability, moisture barrier property, isotropy and the like is used. Specific examples of such thermoplastic resins include cellulose resins such as triacetyl cellulose, polyester resins, polyethersulfone resins, polysulfone resins, polycarbonate resins, polyamide resins, polyimide resins, polyolefin resins, (meth) acrylic resins, cyclic Examples thereof include polyolefin resins (norbornene resins), polyarylate resins, polystyrene resins, polyvinyl alcohol resins, and mixtures thereof. A transparent protective film is bonded to one side of the polarizer by an adhesive layer. On the other side, as a transparent protective film, (meth) acrylic, urethane-based, acrylurethane-based, epoxy-based, silicone A thermosetting resin such as a system or an ultraviolet curable resin can be used. One or more kinds of arbitrary appropriate additives may be contained in the transparent protective film. Examples of the additive include an ultraviolet absorber, an antioxidant, a lubricant, a plasticizer, a release agent, a coloring inhibitor, a flame retardant, a nucleating agent, an antistatic agent, a pigment, and a coloring agent. The content of the thermoplastic resin in the transparent protective film is preferably 50 to 100% by weight, more preferably 50 to 99% by weight, still more preferably 60 to 98% by weight, and particularly preferably 70 to 97% by weight. . When content of the said thermoplastic resin in a transparent protective film is 50 weight% or less, there exists a possibility that the high transparency etc. which a thermoplastic resin originally has cannot fully be expressed.
また、透明保護フィルムとしては、特開２００１−３４３５２９号公報（ＷＯ０１／３７００７）に記載のポリマーフィルム、例えば、（Ａ）側鎖に置換および／または非置換イミド基を有する熱可塑性樹脂と、（Ｂ）側鎖に置換および／または非置換フェニルならびにニトリル基を有する熱可塑性樹脂を含有する樹脂組成物があげられる。具体例としてはイソブチレンとＮ−メチルマレイミドからなる交互共重合体とアクリロニトリル・スチレン共重合体とを含有する樹脂組成物のフィルムがあげられる。フィルムは樹脂組成物の混合押出品などからなるフィルムを用いることができる。これらのフィルムは位相差が小さく、光弾性係数が小さいため偏光板の歪みによるムラなどの不具合を解消することができ、また透湿度が小さいため、加湿耐久性に優れる。 Moreover, as a transparent protective film, the polymer film as described in Unexamined-Japanese-Patent No. 2001-343529 (WO01 / 37007), for example, (A) thermoplastic resin which has a substituted and / or unsubstituted imide group in a side chain, ( B) Resin compositions containing thermoplastic resins having substituted and / or unsubstituted phenyl and nitrile groups in the side chains. A specific example is a film of a resin composition containing an alternating copolymer composed of isobutylene and N-methylmaleimide and an acrylonitrile / styrene copolymer. As the film, a film made of a mixed extruded product of the resin composition or the like can be used. Since these films have a small phase difference and a small photoelastic coefficient, problems such as unevenness due to the distortion of the polarizing plate can be eliminated, and since the moisture permeability is small, the humidification durability is excellent.
透明保護フィルムの厚さは、適宜に決定しうるが、一般には強度や取扱性等の作業性、薄層性などの点より１〜５００μｍ程度である。特に１〜３００μｍが好ましく、５〜２００μｍがより好ましい。透明保護フィルムは、５〜１５０μｍの場合に特に好適である。 Although the thickness of a transparent protective film can be determined suitably, generally it is about 1-500 micrometers from points, such as workability | operativity, such as intensity | strength and handleability, and thin layer property. 1-300 micrometers is especially preferable, and 5-200 micrometers is more preferable. The transparent protective film is particularly suitable when the thickness is 5 to 150 μm.
なお、偏光子の両側に透明保護フィルムを設ける場合、その表裏で同じポリマー材料からなる保護フィルムを用いてもよく、異なるポリマー材料等からなる保護フィルムを用いてもよい。 In addition, when providing a transparent protective film on both sides of a polarizer, the protective film which consists of the same polymer material may be used by the front and back, and the protective film which consists of a different polymer material etc. may be used.
本発明の透明保護フィルムとしては、セルロース樹脂、ポリカーボネート樹脂、環状ポリオレフィン樹脂および（メタ）アクリル樹脂から選ばれるいずれか少なくとも１つを用いるのが好ましい。 As the transparent protective film of the present invention, it is preferable to use at least one selected from cellulose resin, polycarbonate resin, cyclic polyolefin resin, and (meth) acrylic resin.
セルロース樹脂は、セルロースと脂肪酸のエステルである。このようセルロースエステル系樹脂の具体例としでは、トリアセチルセルロース、ジアセチルセルロース、トリプロピオニルセルロース、ジプロピオニルセルロース等があげられる。これらのなかでも、トリアセチルセルロースが特に好ましい。トリアセチルセルロースは多くの製品が市販されており、入手容易性やコストの点でも有利である。トリアセチルセルロースの市販品の例としては、富士フィルム社製の商品名「ＵＶ−５０」、「ＵＶ−８０」、「ＳＨ−８０」、「ＴＤ−８０U」、「ＴＤ−ＴＡＣ」、「ＵＺ−ＴＡＣ」や、コニカ社製の「ＫＣシリーズ」等があげられる。一般的にこれらトリアセチルセルロースは、面内位相差（Ｒｅ）はほぼゼロであるが、厚み方向位相差（Ｒｔｈ）は、〜６０ｎｍ程度を有している。 Cellulose resin is an ester of cellulose and fatty acid. Specific examples of the cellulose ester resin include triacetyl cellulose, diacetyl cellulose, tripropionyl cellulose, dipropionyl cellulose and the like. Among these, triacetyl cellulose is particularly preferable. Many products of triacetylcellulose are commercially available, which is advantageous in terms of availability and cost. Examples of commercial products of triacetyl cellulose include trade names “UV-50”, “UV-80”, “SH-80”, “TD-80U”, “TD-TAC”, “UZ” manufactured by Fuji Film Co., Ltd. -TAC "and" KC series "manufactured by Konica. In general, these triacetyl celluloses have an in-plane retardation (Re) of almost zero, but a thickness direction retardation (Rth) of about 60 nm.
なお、厚み方向位相差が小さいセルロース樹脂フィルムは、例えば、上記セルロース樹脂を処理することにより得られる。例えばシクロペンタノン、メチルエチルケトン等の溶剤を塗工したポリエチレンテレフタレート、ポリプロピレン、ステンレスなどの基材フィルムを、一般的なセルロース系フィルムに貼り合わせ、加熱乾燥（例えば８０〜１５０℃で３〜１０分間程度）した後、基材フィルムを剥離する方法；ノルボルネン系樹脂、（メタ）アクリル系樹脂などをシクロペンタノン、メチルエチルケトン等の溶剤に溶解した溶液を一般的なセルロース樹脂フィルムに塗工し加熱乾燥（例えば８０〜１５０℃で３〜１０分間程度）した後、塗工フィルムを剥離する方法などがあげられる。 In addition, the cellulose resin film with a small thickness direction phase difference is obtained by processing the said cellulose resin, for example. For example, a base film such as polyethylene terephthalate, polypropylene, and stainless steel coated with a solvent such as cyclopentanone and methyl ethyl ketone is bonded to a general cellulose film and dried by heating (for example, at 80 to 150 ° C. for about 3 to 10 minutes). ) And then peeling the base film; a solution obtained by dissolving norbornene resin, (meth) acrylic resin, etc. in a solvent such as cyclopentanone, methyl ethyl ketone, etc. is applied to a general cellulose resin film and dried by heating ( For example, a method of peeling the coated film after 80 to 150 ° C. for about 3 to 10 minutes is mentioned.
また、厚み方向位相差が小さいセルロース樹脂フィルムとしては、脂肪置換度を制御した脂肪酸セルロース系樹脂フィルムを用いることができる。一般的に用いられるトリアセチルセルロースでは酢酸置換度が２．８程度であるが、好ましくは酢酸置換度を１．８〜２．７に制御することによってＲｔｈを小さくすることができる。上記脂肪酸置換セルロース系樹脂に、ジブチルフタレート、ｐ−トルエンスルホンアニリド、クエン酸アセチルトリエチル等の可塑剤を添加することにより、Ｒｔｈを小さく制御することができる。可塑剤の添加量は、脂肪酸セルロース系樹脂１００重量部に対して、好ましくは４０重量部以下、より好ましくは１〜４０重量部、さらに好ましくは１〜１５重量部である。 Moreover, as a cellulose resin film with a small thickness direction retardation, the fatty acid cellulose resin film which controlled the fat substitution degree can be used. Generally used triacetyl cellulose has an acetic acid substitution degree of about 2.8. Preferably, the Rth can be reduced by controlling the acetic acid substitution degree to 1.8 to 2.7. Rth can be controlled to be small by adding a plasticizer such as dibutyl phthalate, p-toluenesulfonanilide, acetyltriethyl citrate to the fatty acid-substituted cellulose resin. The addition amount of the plasticizer is preferably 40 parts by weight or less, more preferably 1 to 40 parts by weight, and still more preferably 1 to 15 parts by weight with respect to 100 parts by weight of the fatty acid cellulose resin.
環状ポリオレフィン樹脂の具体的としては、好ましくはノルボルネン系樹脂である。環状オレフィン系樹脂は、環状オレフィンを重合単位として重合される樹脂の総称であり、例えば、特開平１−２４０５１７号公報、特開平３−１４８８２号公報、特開平３−１２２１３７号公報等に記載されている樹脂があげられる。具体例としては、環状オレフィンの開環（共）重合体、環状オレフィンの付加重合体、環状オレフィンとエチレン、プロピレン等のα−オレフィンとその共重合体（代表的にはランダム共重合体）、および、これらを不飽和カルボン酸やその誘導体で変性したグラフト重合体、ならびに、それらの水素化物などがあげられる。環状オレフィンの具体例としては、ノルボルネン系モノマーがあげられる。 Specific examples of the cyclic polyolefin resin are preferably norbornene resins. The cyclic olefin-based resin is a general term for resins that are polymerized using a cyclic olefin as a polymerization unit, and is described in, for example, JP-A-1-240517, JP-A-3-14882, JP-A-3-122137, and the like. Resin. Specific examples include ring-opening (co) polymers of cyclic olefins, addition polymers of cyclic olefins, cyclic olefins and α-olefins such as ethylene and propylene (typically random copolymers), And graft polymers obtained by modifying them with an unsaturated carboxylic acid or a derivative thereof, and hydrides thereof. Specific examples of the cyclic olefin include norbornene monomers.
環状ポリオレフィン樹脂としては、種々の製品が市販されている。具体例としては、日本ゼオン株式会社製の商品名「ゼオネックス」、「ゼオノア」、ＪＳＲ株式会社製の商品名「アートン」、ＴＩＣＯＮＡ社製の商品名「トーパス」、三井化学株式会社製の商品名「ＡＰＥＬ」があげられる。 Various products are commercially available as the cyclic polyolefin resin. As specific examples, trade names “ZEONEX” and “ZEONOR” manufactured by ZEON CORPORATION, product names “ARTON” manufactured by JSR Corporation, “TOPAS” manufactured by TICONA, and product names manufactured by Mitsui Chemicals, Inc. “APEL”.
（メタ）アクリル系樹脂としては、Ｔｇ（ガラス転移温度）が好ましくは１１５℃以上、より好ましくは１２０℃以上、さらに好ましくは１２５℃以上、特に好ましくは１３０℃以上である。Ｔｇが１１５℃以上であることにより、偏光板の耐久性に優れたものとなりうる。上記（メタ）アクリル系樹脂のＴｇの上限値は特に限定きれないが、成形性当の観点から、好ましくは１７０℃以下である。（メタ）アクリル系樹脂からは、面内位相差（Ｒｅ）、厚み方向位相差（Ｒｔｈ）がほぼゼロものフィルムを得ることができる。 The (meth) acrylic resin preferably has a Tg (glass transition temperature) of 115 ° C. or higher, more preferably 120 ° C. or higher, still more preferably 125 ° C. or higher, and particularly preferably 130 ° C. or higher. When Tg is 115 ° C. or higher, the polarizing plate can be excellent in durability. Although the upper limit of Tg of the (meth) acrylic resin is not particularly limited, it is preferably 170 ° C. or less from the viewpoint of moldability. From (meth) acrylic resin, a film having in-plane retardation (Re) and thickness direction retardation (Rth) of almost zero can be obtained.
（メタ）アクリル系樹脂としては、本発明の効果を損なわない範囲内で、任意の適切な（メタ）アクリル系樹脂を採用し得る。例えば、ポリメタクリル酸メチルなどのポリ（メタ）アクリル酸エステル、メタクリル酸メチル−（メタ）アクリル酸共重合、メタクリル酸メチル−（メタ）アクリル酸エステル共重合体、メタクリル酸メチル−アクリル酸エステル−（メタ）アクリル酸共重合体、（メタ）アクリル酸メチル−スチレン共重合体（ＭＳ樹脂など）、脂環族炭化水素基を有する重合体（例えば、メタクリル酸メチル−メタクリル酸シクロヘキシル共重合体、メタクリル酸メチル−（メタ）アクリル酸ノルボルニル共重合体など）があげられる。好ましくは、ポリ（メタ）アクリル酸メチルなどのポリ（メタ）アクリル酸Ｃ１−６アルキルがあげられる。より好ましくはメタクリル酸メチルを主成分（５０〜１００重量％、好ましくは７０〜１００重量％）とするメタクリル酸メチル系樹脂があげられる。 As the (meth) acrylic resin, any appropriate (meth) acrylic resin can be adopted as long as the effects of the present invention are not impaired. For example, poly (meth) acrylic acid ester such as polymethyl methacrylate, methyl methacrylate- (meth) acrylic acid copolymer, methyl methacrylate- (meth) acrylic acid ester copolymer, methyl methacrylate-acrylic acid ester- (Meth) acrylic acid copolymer, (meth) methyl acrylate-styrene copolymer (MS resin, etc.), polymer having an alicyclic hydrocarbon group (for example, methyl methacrylate-cyclohexyl methacrylate copolymer, Methyl methacrylate- (meth) acrylate norbornyl copolymer, etc.). Preferably, poly (meth) acrylate C1-6 alkyl such as poly (meth) acrylate methyl is used. More preferred is a methyl methacrylate resin containing methyl methacrylate as a main component (50 to 100% by weight, preferably 70 to 100% by weight).
（メタ）アクリル系樹脂の具体例として、例えば、三菱レイヨン株式会社製のアクリペットＶＨやアクリペットＶＲＬ２０Ａ、特開２００４−７０２９６号公報に記載の分子内に環構造を有する（メタ）アクリル系樹脂、分子内架橋や分子内環化反応により得られる高Ｔｇ（メタ）アクリル樹脂系があげられる。 Specific examples of (meth) acrylic resins include (meth) acrylic resins having a ring structure in the molecule described in, for example, Acrypet VH and Acrypet VRL20A manufactured by Mitsubishi Rayon Co., Ltd., and JP-A-2004-70296. And a high Tg (meth) acrylic resin system obtained by intramolecular crosslinking or intramolecular cyclization reaction.
（メタ）アクリル系樹脂として、ラクトン環構造を有する（メタ）アクリル系樹脂を用いることもできる。高い耐熱性、高い透明性、二軸延伸することにより高い機械的強度を有するからである。 As the (meth) acrylic resin, a (meth) acrylic resin having a lactone ring structure can also be used. It is because it has high mechanical strength by high heat resistance, high transparency, and biaxial stretching.
ラクトン環構造を有する（メタ）アクリル系樹脂としては、特開２０００−２３００１６号公報、特開２００１−１５１８１４号公報、特開２００２−１２０３２６号公報、特開２００２−２５４５４４号公報、特開２００５−１４６０８４号公報などに記載の、ラクトン環構造を有する（メタ）アクリル系樹脂があげられる。 Examples of the (meth) acrylic resin having a lactone ring structure include JP 2000-230016, JP 2001-151814, JP 2002-120326, JP 2002-254544, and JP 2005. Examples thereof include (meth) acrylic resins having a lactone ring structure described in Japanese Patent No. 146084.
ラクトン環構造を有する（メタ）アクリル系樹脂は、好ましくは下記一般式（化６）で表される環擬構造を有する。 The (meth) acrylic resin having a lactone ring structure preferably has a ring pseudo structure represented by the following general formula (Formula 6).
式中、Ｒ１、Ｒ２およびＲ３は、それぞれ独立に、水素原子または炭素原子数１〜４０の有機残基を示す。なお、有機残基は酸素原子を含んでいてもよい。 Wherein, R 1, R 2 and R 3 each independently represent a hydrogen atom or an organic residue having 1 to 40 carbon atoms. The organic residue may contain an oxygen atom.
ラクトン環構造を有する（メタ）アクリル系樹脂の構造中の一般式（化６）で表されるラクトン環構造の含有割合は、好ましくは５〜９０重量％、より好ましくは１０〜７０重量％、さらに好ましくは１０〜６０重量％、特に好ましくは１０〜５０重量％である。ラクトン環構造を有する（メタ）アクリル系樹脂の構造中の一般式（化６）で表されるラクトン環構造の含有割合が５重量％よりも少ないと、耐熱性、耐溶剤性、表面硬度が不十分になるおそれがある。ラクトン環構造を有する（メタ）アクリル系樹脂の構造中の一般式（化６）で表されるラクトン環構造の含有割合が９０重量％より多いと、成形加工性に乏しくなるおそれがある。 The content ratio of the lactone ring structure represented by the general formula (Formula 6) in the structure of the (meth) acrylic resin having a lactone ring structure is preferably 5 to 90% by weight, more preferably 10 to 70% by weight, More preferably, it is 10 to 60% by weight, and particularly preferably 10 to 50% by weight. When the content of the lactone ring structure represented by the general formula (Chem. 6) in the structure of the (meth) acrylic resin having a lactone ring structure is less than 5% by weight, the heat resistance, solvent resistance, and surface hardness are low. May be insufficient. When the content ratio of the lactone ring structure represented by the general formula (Chemical Formula 6) in the structure of the (meth) acrylic resin having a lactone ring structure is more than 90% by weight, molding processability may be poor.
ラクトン環構造を有する（メタ）アクリル系樹脂は、質量平均分子量（重量平均分子量と称することも有る）が、好ましくは１０００〜２００００００、より好ましくは５０００〜１００００００、さらに好ましくは１００００〜５０００００、特に好ましくは５００００〜５０００００である。質量平均分子量が上記範囲から外れると、成型加工性の点から好ましくない。 The (meth) acrylic resin having a lactone ring structure has a mass average molecular weight (sometimes referred to as a weight average molecular weight) of preferably 1,000 to 2,000,000, more preferably 5,000 to 1,000,000, still more preferably 10,000 to 500,000, and particularly preferably. Is 50,000 to 500,000. If the mass average molecular weight is out of the above range, it is not preferable from the viewpoint of moldability.
ラクトン環構造を有する（メタ）アクリル系樹脂は、Ｔｇが好ましくは１１５℃以上、より好ましくは１２０℃以上、さらに好ましくは１２５℃以上、特に好ましくは１３０℃以上である。Ｔｇが１１５℃以上であることから、例えば、透明保護フィルムとして偏光板に組み入れた場合に、耐久性に優れたものとなる。上記ラクトン環構造を有する（メタ）アクリル系樹脂のＴｇの上限値は特に限定されないが、成形性などの観点から、好ましくは１７０℃以下である。 The (meth) acrylic resin having a lactone ring structure preferably has a Tg of 115 ° C. or higher, more preferably 120 ° C. or higher, still more preferably 125 ° C. or higher, and particularly preferably 130 ° C. or higher. Since Tg is 115 ° C. or higher, for example, when incorporated into a polarizing plate as a transparent protective film, it has excellent durability. Although the upper limit of Tg of the (meth) acrylic resin having the lactone ring structure is not particularly limited, it is preferably 170 ° C. or less from the viewpoint of moldability and the like.
ラクトン環構造を有する（メタ）アクリル系樹脂は、射出成形により得られる成形品の、ＡＳＴＭ−Ｄ−１００３に準じた方法で測定される全光線透過率が、高ければ高いほど好ましく、好ましくは８５％以上、より好ましくは８８％以上、さらに好ましくは９０％以上である。全光線透過率は透明性の目安であり、全光線透過率が８５％未満であると、透明性が低下するおそれがある。 The (meth) acrylic resin having a lactone ring structure is preferably as the total light transmittance of a molded product obtained by injection molding measured by a method according to ASTM-D-1003 is higher, preferably 85. % Or more, more preferably 88% or more, and still more preferably 90% or more. The total light transmittance is a measure of transparency. If the total light transmittance is less than 85%, the transparency may be lowered.
前記透明保護フィルムは、接着剤を塗工する前に、偏光子との接着性を向上させるために、表面改質処理を行ってもよい。具体的な処理としては、コロナ処理、プラズマ処理、フレーム処理、オゾン処理、プライマー処理、グロー処理、ケン化処理、カップリング剤による処理などがあげられる。また適宜に帯電防止層を形成することができる。 The transparent protective film may be subjected to surface modification treatment in order to improve adhesiveness with the polarizer before applying the adhesive. Specific examples of the treatment include corona treatment, plasma treatment, flame treatment, ozone treatment, primer treatment, glow treatment, saponification treatment, and treatment with a coupling agent. Further, an antistatic layer can be appropriately formed.
前記透明保護フィルムの偏光子を接着させない面には、ハードコート層や反射防止処理、スティッキング防止や、拡散ないしアンチグレアを目的とした処理を施したものであってもよい。 The surface of the transparent protective film to which the polarizer is not adhered may be subjected to a hard coat layer, an antireflection treatment, an antisticking treatment, or a treatment for diffusion or antiglare.
また光学フィルムとしては、例えば反射板や反透過板、前記位相差板（１／２や１／４等の波長板を含む）、視覚補償フィルム、輝度向上フィルムなどの液晶表示装置等の形成に用いられることのある光学層となるものがあげられる。これらは単独で光学フィルムとして用いることができる他、前記偏光板に、実用に際して積層して、１層または２層以上用いることができる。 In addition, as an optical film, for example, for formation of a liquid crystal display device such as a reflection plate, an anti-transmission plate, the retardation plate (including wavelength plates such as 1/2 and 1/4), a visual compensation film, and a brightness enhancement film. The optical layer which may be used is mentioned. These can be used alone as an optical film, or can be laminated on the polarizing plate for practical use and used as one layer or two or more layers.
本発明の粘着型光学フィルムは液晶表示装置等の各種画像表示装置の形成などに好ましく用いることができる。液晶表示装置の形成は、従来に準じて行いうる。すなわち液晶表示装置は一般に、液晶セルと粘着型光学フィルム、及び必要に応じての照明システム等の構成部品を適宜に組み立てて駆動回路を組み込むことなどにより形成されるが、本発明においては本発明による粘着型光学フィルムを用いる点を除いて特に限定は無く、従来に準じうる。液晶セルについても、例えばＴＮ型やＳＴＮ型、π型、ＶＡ型、ＩＰＳ型などの任意なタイプなどの任意なタイプのものを用いうる。 The pressure-sensitive adhesive optical film of the present invention can be preferably used for forming various image display devices such as liquid crystal display devices. The liquid crystal display device can be formed according to the conventional method. That is, a liquid crystal display device is generally formed by appropriately assembling components such as a liquid crystal cell, an adhesive optical film, and an illumination system as necessary, and incorporating a drive circuit. There is no particular limitation except that an adhesive optical film is used. As the liquid crystal cell, an arbitrary type such as an arbitrary type such as a TN type, STN type, π type, VA type, or IPS type can be used.
液晶セルの片側又は両側に粘着型光学フィルムを配置した液晶表示装置や、照明システムにバックライトあるいは反射板を用いたものなどの適宜な液晶表示装置を形成することができる。その場合、本発明による光学フィルムは液晶セルの片側又は両側に設置することができる。両側に光学フィルムを設ける場合、それらは同じものであっても良いし、異なるものであっても良い。さらに、液晶表示装置の形成に際しては、例えば拡散板、アンチグレア層、反射防止膜、保護板、プリズムアレイ、レンズアレイシート、光拡散板、バックライトなどの適宜な部品を適宜な位置に１層又は２層以上配置することができる。 An appropriate liquid crystal display device such as a liquid crystal display device in which an adhesive optical film is disposed on one side or both sides of a liquid crystal cell, or a backlight or a reflector used in an illumination system can be formed. In that case, the optical film according to the present invention can be installed on one side or both sides of the liquid crystal cell. When optical films are provided on both sides, they may be the same or different. Further, when forming a liquid crystal display device, for example, a single layer or a suitable part such as a diffusing plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusing plate, a backlight, etc. Two or more layers can be arranged.
以下に、実施例によって本発明を具体的に説明するが、本発明はこれら実施例によって限定されるものではない。なお、各例中の部および％はいずれも重量基準である。以下に特に規定のない室温放置条件は全て２３℃６５％RH（1時間あるいは1週間）である。実施例等における評価項目は下記のようにして測定を行った。 EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. In addition, all the parts and% in each example are based on weight. The room temperature standing conditions not specifically defined below are all 23 ° C. and 65% RH (1 hour or 1 week). Evaluation items in Examples and the like were measured as follows.
＜重量平均分子量の測定＞
得られた（メタ）アクリル系ポリマーの重量平均分子量は、ＧＰＣ（ゲル・パーミエー
ション・クロマトグラフィー）により測定した。サンプルは、試料をジメチルホルムアミドに溶解して０．１重量％の溶液とし、これを一晩静置した後、０．４５μｍのメンブレンフィルターで濾過した濾液を用いた。
・分析装置：東ソー社製、ＨＬＣ−８１２０ＧＰＣ
・カラム：東ソー社製、Ｇ７０００ＨＸＬ＋ＧＭＨＸＬ＋ＧＭＨＸＬ
・カラムサイズ；各７．８ｍｍφ×３０ｃｍ 計９０ｃｍ
・溶離液：テトラヒドロフラン
・流量：０．８ｍｌ／ｍｉｎ
・検出器：示差屈折計（ＲＩ）
・カラム温度：４０℃
・ 注入量：１００μｌ
・ 標準試料：ポリスチレン
分子量１０万以下のエリア％は、ＧＰＣ測定結果に基づきデータ処理装置（東ソー社製、ＧＰＣ８０２０）により算出した。
<Measurement of weight average molecular weight>
The weight average molecular weight of the obtained (meth) acrylic polymer was measured by GPC (gel permeation chromatography). The sample was prepared by dissolving the sample in dimethylformamide to give a 0.1% by weight solution, which was allowed to stand overnight and then filtered through a 0.45 μm membrane filter.
・ Analyzer: HLC-8120GPC manufactured by Tosoh Corporation
Column: G7000HXL + GMHXL + GMHXL, manufactured by Tosoh Corporation
・ Column size: 7.8mmφ × 30cm each 90cm in total
-Eluent: Tetrahydrofuran-Flow rate: 0.8 ml / min
・ Detector: Differential refractometer (RI)
-Column temperature: 40 ° C
・ Injection volume: 100 μl
Standard sample: polystyrene Area% having a molecular weight of 100,000 or less was calculated by a data processing device (GPC8020, manufactured by Tosoh Corporation) based on the GPC measurement result.
（偏光板の作成）
厚さ８０μｍのポリビニルアルコールフィルムを、速度比の異なるロール間において、３０℃、０．３％濃度のヨウ素溶液中で１分間染色しながら、３倍まで延伸した。その後、６０℃、４％濃度のホウ酸、１０％濃度のヨウ化カリウムを含む水溶液中に０．５分間浸漬しながら総合延伸倍率が６倍まで延伸した。次いで、３０℃、１．５％濃度のヨウ化カリウムを含む水溶液中に１０秒間浸漬することで洗浄した後、５０℃で４分間乾燥を行い偏光子を得た。当該偏光子の両面に、けん化処理した厚さ８０μｍのトリアセチルセルロースフィルムをポリビニルアルコール系接着剤により貼り合せて偏光板を作成した。
(Creation of polarizing plate)
A polyvinyl alcohol film having a thickness of 80 μm was stretched up to 3 times while being dyed for 1 minute in an iodine solution of 0.3% concentration at 30 ° C. between rolls having different speed ratios. Thereafter, the total draw ratio was stretched to 6 times while being immersed in an aqueous solution containing 60% at 4% concentration of boric acid and 10% concentration of potassium iodide for 0.5 minutes. Next, after washing by immersing in an aqueous solution containing potassium iodide at 30 ° C. and 1.5% concentration for 10 seconds, drying was performed at 50 ° C. for 4 minutes to obtain a polarizer. A saponified 80 μm thick triacetyl cellulose film was bonded to both surfaces of the polarizer with a polyvinyl alcohol-based adhesive to prepare a polarizing plate.
製造例１
＜アクリル系ポリマーの調製＞
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた４つ口フラスコに、ブチルアクリレート（ＢＡ）６４ｇ、ベンジルアクリレート（BｚＡ）３５ｇ、４−ヒドロキシブチルアクリレート（ＨＢＡ）１ｇ、重合開始剤として２，２’−アゾビスイソブチロニトリル０．１ｇを酢酸エチル１００ｇと共に仕込み、緩やかに攪拌しながら窒素ガスを導入して窒素置換した後、フラスコ内の液温を５５℃付近に保って８時間重合反応を行い、重量平均分子量１８０万のアクリル系ポリマー溶液を調製した。
Production Example 1
<Preparation of acrylic polymer>
In a four-necked flask equipped with a stirring blade, thermometer, nitrogen gas inlet tube and condenser, butyl acrylate (BA) 64 g, benzyl acrylate (BzA) 35 g, 4-hydroxybutyl acrylate (HBA) 1 g, as a polymerization initiator After charging 0.1 g of 2,2′-azobisisobutyronitrile with 100 g of ethyl acetate and introducing nitrogen gas with gentle stirring to replace nitrogen, the liquid temperature in the flask was kept at around 55 ° C. A time polymerization reaction was carried out to prepare an acrylic polymer solution having a weight average molecular weight of 1,800,000.
実施例１
（粘着剤層付偏光板の作製）
製造例１で得られたアクリル系ポリマー溶液の固形分１００部に対して、架橋剤として０．３０部のイソシアネート架橋剤（日本ポリウレタン製、Ｃ／Ｌ）と０．２部のシランカップリング剤（信越化学工業（株）製、ＫＢＭ５７３）、１部のシロキサン化合物（信越シリコーン製、ＫＦ−５４）を配合したアクリル系粘着剤溶液を調製した。
Example 1
(Preparation of polarizing plate with adhesive layer)
With respect to 100 parts of the solid content of the acrylic polymer solution obtained in Production Example 1, 0.30 parts of an isocyanate crosslinking agent (manufactured by Nippon Polyurethane, C / L) and 0.2 parts of a silane coupling agent are used as a crosslinking agent. (Shin-Etsu Chemical Co., Ltd., KBM573) An acrylic pressure-sensitive adhesive solution containing 1 part of a siloxane compound (manufactured by Shin-Etsu Silicone, KF-54) was prepared.
次いで、上記アクリル系粘着剤溶液を、シリコーン処理を施した、３８μｍのポリエチレンテレフタレート（ＰＥＴ）フィルム（三菱化学ポリエステルフィルム（株）製，ＭＲＦ３８）の片面に、乾燥後の粘着剤層の厚さが２５μｍになるように塗布し、１３０℃で３分間乾燥を行い、偏光板（日東電工製、ＳＥＧ）に転写し、粘着剤層付偏光板を作製した。 Next, the acrylic adhesive solution was subjected to silicone treatment on one side of a 38 μm polyethylene terephthalate (PET) film (MRF38, manufactured by Mitsubishi Chemical Polyester Film Co., Ltd.), and the thickness of the adhesive layer after drying was It apply | coated so that it might become 25 micrometers, it dried at 130 degreeC for 3 minute (s), and it transcribe | transferred to the polarizing plate (Nitto Denko make, SEG), and produced the polarizing plate with an adhesive layer.
実施例２〜８、比較例１〜６
実施例１において、アクリル系粘着剤溶液の調製に用いたアクリル系ポリマー溶液の種類、架橋剤の種類もしくは使用量、シランカップリング剤の種類もしくは使用量を表１に示すように変えたこと以外は、実施例１と同様にして、粘着剤層付偏光板を作製した。
Examples 2-8, Comparative Examples 1-6
In Example 1, except that the type of acrylic polymer solution used for the preparation of the acrylic pressure-sensitive adhesive solution, the type or amount of crosslinking agent, and the type or amount of silane coupling agent were changed as shown in Table 1. Produced a polarizing plate with an adhesive layer in the same manner as in Example 1.
上記実施例および比較例で得られた、粘着剤層付偏光板（サンプル）について以下の評価を行った。評価結果を表１に示す。 The following evaluation was performed about the polarizing plate (sample) with an adhesive layer obtained by the said Example and comparative example. The evaluation results are shown in Table 1.
＜リワーク性＞
実施例および比較例で得られたサンプルを、幅２５ｍｍ×長さ１００ｍｍに裁断し、厚さ０．５ｍｍの無アクリルガラス板（コーニング社製、１７３７）に、ラミネーターを用いて貼り付け、次いで５０℃、５ａｔｍで１５分間オートクレーブ処理して完全に密着させた後、６０℃乾燥条件下で３００時間加熱処理を施した。かかるサンプルの接着力を測定し、リワーク性の評価を以下の基準で行った。
◎：接着力１０Ｎ／２５ｍｍ未満
○：接着力１０Ｎ／２５ｍｍ〜２０Ｎ／２５ｍｍ
×：接着力２０Ｎ／２５ｍｍより大
<Reworkability>
Samples obtained in Examples and Comparative Examples were cut into a width of 25 mm and a length of 100 mm, and attached to a 0.5 mm-thick acrylic glass plate (Corning Corp., 1737) using a laminator, and then 50 After autoclaving for 15 minutes at 5 ° C. at 5 ° C. for complete adhesion, heat treatment was performed for 300 hours under dry conditions at 60 ° C. The adhesive strength of the sample was measured, and reworkability was evaluated according to the following criteria.
A: Adhesive force less than 10 N / 25 mm B: Adhesive force 10 N / 25 mm to 20 N / 25 mm
X: Adhesive strength greater than 20N / 25mm
ここで、接着力は、かかるサンプルを、引張り試験機（オートグラフSHIMAZU AG-1 1OKN）にて、剥離角度９０°、剥離速度３００ｍｍ／ｍｉｎで引き剥がす際の接着力（Ｎ／２５ｍｍ、測定時８０ｍ長）を測定することにより求めた。測定は、１回／０．５sの間隔でサンプリングし、その平均値を測定値とした。 Here, the adhesive strength is measured when the sample is peeled off with a tensile tester (Autograph SHIMAZU AG-1 1OKN) at a peeling angle of 90 ° and a peeling speed of 300 mm / min (N / 25 mm, when measured). 80 m long). The measurement was sampled at an interval of 1 time / 0.5 s, and the average value was taken as the measurement value.
＜耐久性＞
実施例および比較例で得られたサンプルを、１５インチサイズとし、厚さ０．７ｍｍの無アクリルガラス（コーニング社製、１７３７）の両面にクロスニコル状態になるようにラミネーターを用いて貼着した。次いで、５０℃、０．５ＭＰaで１５分間オートクレーブ処理して、上記サンプルを完全に無アクリルガラスに密着させた。かかる処理の施されたサンプルに、９０℃（乾燥状態下）、６０℃／９５％ＲＨの条件で５００時間処理を施した後、発泡、剥がれ、浮きの状態を下記基準で目視にて評価した。
◎：発泡、剥がれ、浮きなしなどの外観上の変化が全くなし。
○：端部に剥がれあるが、実用上問題なし。
△：端部に剥がれあり、実用上問題あり。
×：端部に著しい剥がれあり。
<Durability>
Samples obtained in Examples and Comparative Examples were 15 inches in size, and were attached to both surfaces of 0.7 mm thick acrylic-free glass (Corning Corp., 1737) using a laminator so as to be in a crossed Nicol state. . Subsequently, the sample was autoclaved at 50 ° C. and 0.5 MPa for 15 minutes to completely adhere the sample to the acrylic-free glass. The sample subjected to such treatment was treated for 500 hours under the conditions of 90 ° C. (under dry conditions) and 60 ° C./95% RH, and then the foamed, peeled, and floated state was visually evaluated according to the following criteria. .
A: No change in appearance such as foaming, peeling, or no floating.
○: There is no problem in practical use although there is peeling at the end.
(Triangle | delta): There exists peeling in an edge part and there is a problem practically.
X: Remarkable peeling at the end.
表１中、ＢＡ：ブチルアクリレート、ＨＢＡ：４‐ヒドロキシブチルアクリレート、ＢＺＡ：ベンジルアクリレートを示す。イソシアネート系架橋剤は、ポリオール変性トリレンジイソシアネート（日本ポリウレタン工業（株）製、トリメチロールプロパントリレンジイソシアネート Ｃ／Ｌ）である。シランカップリング剤は、信越化学工業（株）製のＫＢＭ５７３またはＫＢＭ４０３である。シロキサン化合物は、Ｒがフェニル基の場合として、ＫＦ−５４（メチルフェニルシリコーンオイル：信越シリコーン製）、Ｒがメチル基の場合として、ＫＦ−９６Ｌ−１００ｃｓ（ジメチルシリコーンオイル：信越シリコーン製）、Ｒがカルボキシル基の場合として、ｘ−２２−３７０１Ｅ（カルボキシル基変性シリコーンオイル：信越シリコーン製）、Ｒがポリエーテルの場合として、ｘ−２２−４２７２（ポリエーテル変性シリコーンオイル：信越シリコーン製）である。 In Table 1, BA: butyl acrylate, HBA: 4-hydroxybutyl acrylate, BZA: benzyl acrylate are shown. The isocyanate-based crosslinking agent is polyol-modified tolylene diisocyanate (manufactured by Nippon Polyurethane Industry Co., Ltd., trimethylolpropane tolylene diisocyanate C / L). The silane coupling agent is KBM573 or KBM403 manufactured by Shin-Etsu Chemical Co., Ltd. The siloxane compound is composed of KF-54 (methylphenyl silicone oil: Shin-Etsu Silicone) when R is a phenyl group, KF-96L-100cs (dimethyl silicone oil: Shin-Etsu Silicone) when R is a methyl group, R When x is a carboxyl group, x-22-3701E (carboxyl group-modified silicone oil: made by Shin-Etsu Silicone), and when R is a polyether, x- 2 2-4272 (polyether-modified silicone oil: made by Shin-Etsu Silicone) is there.
Claims (8)
該（メタ）アクリル系ポリマー１００重量部に対して、シランカップリング剤を０．０１〜１重量部、下記構造式（１）で表わされるシロキサン化合物を０．０１〜１０重量部、およびイソシアネート系架橋剤を０．０１〜５重量部含有してなることを特徴とする光学フィルム用粘着剤組成物：
0.01 to 1 part by weight of a silane coupling agent, 0.01 to 10 parts by weight of a siloxane compound represented by the following structural formula (1), and an isocyanate system with respect to 100 parts by weight of the (meth) acrylic polymer A pressure-sensitive adhesive composition for an optical film comprising 0.01 to 5 parts by weight of a crosslinking agent: