JP4844898B2 - Cooling method of recovered mold sand - Google Patents

Description

The present invention relates to a cooling how the collection molding sand produced by strip apart the casting is finished sand.

  Conventionally, after cooling the sand mold for cooling the recovered mold sand, the sand temperature of the recovered mold sand is detected, and cooling water proportional to the temperature is added on the belt conveyor (see Patent Document 1). A method of enhancing the cooling effect by stirring the mold sand sprinkled by the stirring device and preventing the sand from adhering to the charging chute and the occurrence of sand lumps is known.

JP-A-11-221649

  However, since the method described in Patent Document 1 requires a sand layer of 70 mm or more in order to measure the sand temperature of the mold sand, it may segregate and cause lumps when water is poured onto the surface of the high temperature sand. . Moreover, since water was poured on the belt conveyor, there was a problem that the molding sand adhered to the belt conveyor and the atmosphere deteriorated (see FIG. 7). Furthermore, there have been many requests to improve the cooling efficiency of the recovered mold sand.

  The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a cooling method of recovered mold sand that can reduce the segregation of water, and is environmentally friendly and can be efficiently cooled.

The method for cooling the recovered mold sand in the present invention is a method for cooling the recovered mold sand that cools the recovered mold sand after pouring, and communicates with the sand cooler charging chute into which the recovered mold sand is charged and the inlet side. in sand and cooler rotating drum, provided with, and, sand cooler configured as a semi-sealed space has been scraped the collection molding sand that is introduced through the sand cooler chute has a sand scooping plate to drop In the sand cooler, a step of spraying mist-like water onto the recovered casting sand that has been repeatedly dropped from the spraying means installed on the rear side of the outlet side of the sand cooler rotating drum, with the sand scraping plate . And a step of collecting the sand cooler by dust collecting means on the inlet side of the sand cooler rotating drum .

  The following is a confirmation test of the principle discovered by the present inventors that allows the recovered mold sand to be cooled efficiently by bringing the mist water into contact with the recovered mold sand in a dispersed flow state. Based on

FIG. 5 shows a schematic diagram of the sand cooling confirmation test apparatus. As shown in FIG. 5, the test apparatus includes a spray device A including an air supply device 101 and a water container 102, an upstream tray 103, a downstream tray 104, and a thermometer 105 that measures sand temperature. Here, the spray device A is a 2-fluid nozzle type BIMV manufactured by Ikeuchi, the spray pattern is fan-shaped, and the spray angle is 110 degrees. The size of the “mist-like water” sprayed at this time was 10 μm to 100 μm.

In the test using the test apparatus, first, sand heated to a high temperature from the upstream tray 103 was dropped onto the downstream tray 104 in a May rain type, and sprayed toward the falling sand. Next, dropping and spraying were performed 5 times, and the temperature of the sand was measured with the thermometer 105 each time, and the residual moisture of the sand for the fifth time was measured.

Table 1 and FIG. 6 show the conditions and results obtained by the above test method. As shown in FIG. 6, it is understood that the temperature drop is larger when spraying than just dropping sand, and the temperature drop increases as the amount of spray water increases. In this case, no segregation or lumps of water occurred.
With five sprays of water, the sand temperature became about 20 degrees, and it was found that this principle has sufficient sand cooling ability.

The present invention is a cooling method for recovered mold sand, wherein the recovered mold sand is cooled after pouring, and the sand cooler input chute into which the recovered mold sand is input, and the sand cooler input connected to the inlet side. A sand cooler rotating drum having a sand scraping plate for scraping and dropping the recovered casting sand introduced through a chute, and the sand cooler rotating drum in the sand cooler configured as a semi-enclosed space A step of spraying mist-like water onto the recovered casting sand that has been repeatedly dropped from the spraying means installed at the rear portion of the outlet side , and the sand cooler rotating drum of the sand cooler And a step of collecting the sand cooler by the dust collecting means on the inlet side, so that the recovered casting sand can be efficiently cooled.

The cooling method of the recovery mold sand of the present invention is a cooling method of the recovery mold sand, which cools the recovery mold sand recovered after pouring, with respect to the recovery mold sand that is in a dispersed flow state in the semi-enclosed space. It is characterized by contacting mist-like water.

Here, “recovered mold sand” refers to mold sand that has been unpacked after pouring and separated from the casting in casting using mold sand, and is stored for reuse. In some cases, kneading and adjusting by adding moisture, caking additive, and fresh sand.

“Cooling of mold sand” refers to lowering the temperature of mold sand that has become hot due to pouring for use in molding. While the molten metal poured into the mold is cooled and solidified in the mold, the heat from the casting is transferred to the mold and the sand and partially becomes high temperature. In order to reduce the thermal effect, heat may be actively transferred to the sand after mixing by mixing the material and sand.

Here, the recovery mold sand temperature is generally about 90 to 120 ° C. on average, and the sand temperature at the time of recovery of the unpoured mold is low. The recovered mold sand is subjected to sieving, magnetic separation, cooling, storage, and kneading processes, and then sent to the molding process as kneaded sand (also referred to as molding sand. Mold sand adjusted for molding), which is molded by a molding machine or the like to become a mold. When the molding sand is high in temperature, the molded mold surface is not stable, which may cause defects (sand sand etc.). Therefore, it is generally necessary to set the temperature to about 40 to 50 ° C. or less. For this reason, sand treatment facilities usually have a sand cooling process.

The sand is generally cooled by adding water and taking away the heat retained by the sand by the latent heat of vaporization during vaporization. Moreover, the water | moisture content which the sand after cooling cools may be adjusted simultaneously with cooling. In addition, since clay cannot exhibit binding force at high temperature, cooling is necessary.

“Semi-enclosed space” refers to a semi-enclosed space such as a hopper or casing. Since heat is exchanged by providing moisture and evaporating it, it is expected that the amount of steam generated will be large and harm the environment. For this reason, a semi-enclosed space is used. A dust collection function is also provided if necessary. In addition, in order to improve heat exchange efficiency, it is preferable that it is close to a closed state.

“Dispersed flow state” refers to a state in which sand particles are separated from each other. It means that sand particles are separated from each other by blowing gas or the like into sand or dropping it by gravity. Any method may be used for dispersion and fluidization. For example, a vertical tubular sand passage may be formed and dispersed and fluidized by rotating blades.

In addition, it is fine powder (a group of sand grains of 44 μm or less) that becomes a problem at the time of kneading, and it is preferable that the fine powder is separated from the larger sand grains because they are less likely to become lumps when sprayed with moisture.

The “mist-like water” used in the present invention refers to a water droplet having a diameter equal to or smaller than that of foundry sand. This is because if it is larger than the sand grains, sand lumps are likely to occur. That is, since the single ceramic particles constituting the foundry sand are about 200 μm, water droplets having a size equal to or less than that size are preferable. Preferably, the average particle size of the water droplets is smaller than 100 μm, more preferably 50 to 10 μm.

Further, the amount of water sprayed varies depending on the cooling position, but needs to be 500 liters / hour to 3000 liters / hour. Furthermore, the spray pattern is preferably a fan shape. In addition, the spray angle is preferably about 20 to 100 degrees.

In the present invention, the foundry sand refers to a single ceramic particle used for adjusting the mold sand. In general, silica is used.

“Making mist-like water in contact with the recovery mold sand” means that mist-like water droplets come into contact with the sand grains to evaporate. Since the water droplets are small, they contact the sand and evaporate instantly without receiving heat. In addition, since contact and evaporation are repeated instantaneously, heat is exchanged efficiently. It can be estimated that heat conduction is good because the heat transfer surface is constantly exposed. Furthermore, since the water droplets are small, they contact with the entire sand particles, the contact efficiency is high, and heat is uniformly exchanged.

As the spraying means of the present invention, a so-called “fog spray nozzle” is preferable, and according to this nozzle, water droplets of 100 μm or less and 10 μm or more can be reliably obtained.

Hereinafter, the cooling method of the recovery casting mold sand of the present invention is explained based on an accompanying drawing.

FIG. 1 shows an overall system diagram of a process for treating recovered casting sand. As shown in FIG. 1, a sand treatment system according to an embodiment of the present invention includes a conveyor unit using belt conveyors 1, 3, 6, 8, 11, 15 and bucket elevators 7, 12, and a sieve using a rotary screen 4. There are provided a separating unit, a sand cooling and sieving unit by the sand cooler 9, a storage unit by the hoppers 5 and 14 and the sand bottle 10, and a kneading unit by the kneader 13.

The belt conveyor 1 conveys the recovered mold sand and is transferred to the belt conveyor 3 via a belt conveyor tip chute 2 (chute is also attached to future belt conveyors and bucket elevators, not shown).

After that, the sand is sieved with the rotary screen 4 which is the rotary drum having the pores, the sand is put into the hopper 5, the sand is conveyed from the belt conveyor 6 through the bucket elevator 7 and further by the belt conveyor 8. The sand cooler 9 cools and sifts the sand.

Next, the sand is stored in the sand bin 10, the sand is conveyed by the belt conveyor 11, the sand is kneaded by the kneader 13 through the bucket elevator 12, and the sand is collected by the hopper 14. 15 is conveyed to the molding line.

Here, the cooling method of the recovery mold sand of the present invention can be applied to a plurality of locations such as a belt conveyor transfer section, a rotary screen section, and a sand cooler section. Details will be described below.

FIG. 2 shows a schematic diagram in which the present invention is applied to the belt conveyor transfer section. In FIG. 2, the belt conveyor 1 conveys the recovered casting sand S. At the front end 1a of the belt conveyor 1, the recovered casting sand S falls downward due to gravity. When the recovered casting sand S falls, the sand naturally disperses and fluidizes. However, as the sand dispersal fluidizing means, a separation plate that divides the sand flow may be provided.

A belt conveyor 3 is located below the front end 1 a of the belt conveyor 1, and the recovered casting sand S that has dropped from the front end 1 a of the belt conveyor 1 is transferred to the belt conveyor 3. In this collected sand transfer portion, a semi-enclosed space partition that is shielded by the belt conveyor tip chute 2 is configured.

Further, spray means for spraying mist-like water in the semi-enclosed space from the outside of the belt conveyor tip chute 2 as a semi-enclosed space partition is directed to the falling recovered casting sand S.

The operation of the mold sand cooling device configured as described above will be described below.
The sand falling from the front end 1a of the belt conveyor 1 is transferred to the belt conveyor 3 via the belt conveyor front end chute 2 and water is sprayed in the form of mist by the fog spray nozzle B1. Thereby, sand cooling is performed by the falling sand and mist-like water contacting.

According to the present embodiment, sand is dispersed and fluidized by using the fall of sand in the collected sand transfer section of the belt conveyors 1 and 3, and efficient sand cooling can be performed by the above-described principle. Furthermore, since this transfer part is contained in the semi-enclosed space partition, the sand can be stably cooled, and the environment is not deteriorated.

FIG. 3 shows a schematic diagram in which the present invention is applied to a rotary screen portion. In FIG. 3, the belt conveyor 3 conveys the recovered casting sand S. At the front end 3a of the belt conveyor 3, the recovered casting sand S falls downward due to gravity. A rotary screen charging chute 16 is positioned below the front end 3 a of the belt conveyor 3, and the rotary screen charging chute 16 communicates with a rotary screen rotating drum 17.

The recovered casting sand S that has fallen from the front end 3 a of the belt conveyor 3 is input to the rotary screen rotating drum 17 through the rotary screen input chute 16. The rotary screen rotating drum 17 is rotated by an electric motor and sifts the collected casting sand S. The recovered casting sand S that has been sieved passes through the sieve and falls by gravity onto the hopper 5 positioned below the rotary screen rotating drum 17.

When the recovered casting sand S is sieved and dropped, the sand naturally disperses and fluidizes. Here, the hopper 5 is configured as a semi-enclosed space partition, and from the outside of the hopper 5 serving as a semi-enclosed space partition, spraying means for spraying mist-like water in the semi-enclosed space drops the recovery. It is directed to the mold sand S.

The operation of the mold sand cooling device configured as described above will be described below. The recovered casting sand S is fed into the rotary screen rotating drum 17 from the tip 3a of the belt conveyor 3 via the rotary screen charging chute 16 and passes through the sieve of the rotating rotary screen rotating drum 17 to rotate. Fall into Water is sprayed into the sand that has passed through the sieve and falling by the fog spray nozzle B2.

According to the present embodiment, the rotary screen unit disperses and fluidizes sand by using the sand falling in the sieving of the rotary screen rotating drum, and can efficiently cool the sand by the above-described principle. Furthermore, since this rotary screen part is contained in the semi-enclosed space partition by the hopper 5, the sand can be cooled stably, and the environment is not deteriorated.

FIG. 4 shows a schematic diagram in which the invention is applied to the sand cooler section. In FIG. 4, the belt conveyor 8 conveys the recovered casting sand S. At the front end 8a of the belt conveyor 8, the recovered casting sand S falls downward due to gravity.

The sand cooler 9 is composed of a sand cooler charging chute 18 and a sand cooler rotating drum 19. The sand cooler charging chute 18 is located below the front end 8 a of the belt conveyor 8. The chute 18 communicates with the sand cooler rotating drum 19.

The recovered casting sand S that has fallen from the front end 8a of the belt conveyor 8 is put into the sand cooler rotating drum 19 through the sand cooler throwing chute 18. The sand cooler rotating drum 19 has a sand scooping plate 20 and is rotated by an electric motor to scoop up and collect the collected recovery sand S. The sand cooler rotating drum 19 has a lead 20a arranged in a screw shape so as to generate a thrust. The recovered casting sand S that has been sieved passes through the sieve and falls to the sand bin 10 located below the sand cooler rotating drum 19 by gravity.

When the recovered casting sand S is scraped up and dropped by the scraping plate 20, the sand is naturally dispersed and fluidized. Alternatively, the recovered casting sand S dropped from the scraping plate 20 is sent along the lead 20a, and is again lifted by the scraping plate 20 and dropped. Here, the sand cooler 9 is configured as a semi-enclosed space, and spraying means for spraying mist of water in the semi-enclosed space from the rear and outside of the sand cooler 9 in the semi-enclosed space, It is directed to the recovery mold sand S falling by the plate 20. Further, dust collecting means is provided on the inlet side of the sand cooler 9.

The operation of the mold sand cooling device configured as described above will be described below.
The recovered casting sand S is fed from the belt conveyor 8 through the sand cooler charging chute 18 into the sand cooler rotating drum 19. The recovered casting sand S is scraped up by the sand scraping plate 20 of the sand cooler rotating drum 19, then passes through a sieve and falls into the sand bin 10. From fog spray nozzle B3 installed in a rear portion of the sand click over la 9, to injection atomized water in sand that repeatedly dropping scooping. The contact frequency of sand and mist-like water reaches about 10 times in an actual machine. The sand cooler 9 collects dust with an appropriate amount of air from the inlet side to create a mist flow and increase the heat exchange efficiency of the sand.

According to the present embodiment, the sand cooler unit disperses and fluidizes the sand using the sand falling by the scraping plate of the sand cooler rotating drum, and can efficiently cool the sand by the above-described principle. Furthermore, since this sand cooler part is a semi-enclosed space, the sand can be cooled stably, and the environment is not deteriorated.

  As mentioned above, although the Example of this invention was described, this invention is not limited to this Example.

It is a system diagram of the whole process of processing recovery mold sand. It is the schematic which applied this invention to the belt conveyor transfer part. It is the schematic which applied this invention to the rotary screen part. It is the schematic which applied this invention to the sand cooler part. It is a schematic diagram of a sand cooling confirmation test device. It is the figure which put together the result of the sand cooling confirmation test. It is a schematic diagram of the conventional mold sand cooling water cooling system.

Explanation of symbols

1, 3, 6, 8, 11, 15 Belt conveyor 1a Belt conveyor 1 tip 2 Belt conveyor tip chute 3a Belt conveyor 3 tip 4 Rotary screen 9 Sand cooler 202 Spraying means (water injection nozzle)
210
Belt conveyor A Spraying means (spraying device)
B1, B2, B3 Spraying means (fog spray nozzle)
S Recovery mold sand

Claims (1)

A cooling method for recovered mold sand, which cools the recovered mold sand after pouring,
Sand cooler rotation having a sand cooler charging chute into which the recovered mold sand is charged, and a sand scraping plate for scraping and dropping the recovered mold sand charged through the sand cooler charging chute communicated with the inlet side A spraying means installed at the rear side of the outlet side of the sand cooler rotating drum in a sand cooler configured as a semi-enclosed space, and is repeatedly scraped and dropped by the sand scraping plate Spraying mist-like water onto the recovery mold sand, and collecting the sand cooler with dust collecting means on the inlet side of the sand cooler rotating drum in the sand cooler. Cooling method of recovered mold sand.