JP4722545B2 - Water-absorbing resin composition and method for producing the same - Google Patents

Description

  The present invention relates to a water-absorbent resin composition suitably used for sanitary materials such as disposable diapers and sanitary napkins, so-called incontinence pads, and a method for producing the same.

  For sanitary materials such as disposable diapers, sanitary napkins, and incontinence pads, absorbents comprising hydrophilic fibers such as pulp and water-absorbing resin are widely used for the purpose of absorbing body fluids.

  In recent years, these sanitary materials have become highly functional and thin, and the amount of water-absorbing resin used per sanitary material and the ratio of water-absorbing resin to the entire absorbent body composed of water-absorbing resin and hydrophilic fibers have increased. Tend to. In other words, by reducing the number of hydrophilic fibers with a small bulk specific gravity, and using many water absorbent resins with excellent water absorption and a large bulk specific gravity, the ratio of the water absorbent resin in the absorbent body can be increased and the amount of water absorbed can be reduced. The sanitary material is made thinner.

  However, a hygienic material having a low ratio of hydrophilic fibers and a high ratio of water-absorbing resin is preferable from the viewpoint of simply storing the liquid, but the liquid in the actual use situation as a diaper or the like is preferable. When distribution and diffusion are considered, problems arise rather. For example, a large amount of water-absorbing resin becomes a soft gel by absorbing water, causing a phenomenon of gel blocking and dramatically reducing the diffusibility of the liquid in the sanitary material. In order to avoid such problems and maintain the absorption characteristics of the absorbent body, the ratio between the hydrophilic fiber and the water-absorbent resin is naturally limited, and there has been a limit to the thinning of sanitary materials.

  As a means for obtaining a water-absorbing resin excellent in liquid permeability and diffusibility by suppressing gel blocking, a technique of adding a metal compound (polyvalent metal salt, metal cation, etc.) to the water-absorbing resin is known.

  In the technique of adding a metal compound in an aqueous solution state (for example, see Patent Documents 1 to 10), the metal component easily penetrates into the water absorbent resin. For this reason, the effect of improving liquid permeability and diffusibility corresponding to the amount added is not sufficient. In addition, since the metal component penetrates into the water-absorbent resin, the absorption capacity under no pressure and the absorption capacity under pressure have been reduced.

In the technique of adding a binder such as water after dry blending the water absorbent resin and the metal compound (see, for example, Patent Documents 11 to 12), the metal component dissolves in the binder such as water and penetrates into the water absorbent resin. For this reason, the effect of improving liquid permeability and diffusibility was not sufficient. In addition, there is a problem that dust is often generated due to damage such as impact and friction during the process.
JP-A-62-2745 Japanese Unexamined Patent Publication No. 63-270741 JP-A 64-56707 JP-A-9-124879 JP 2001-96151 A International Publication No. 98/49221 Pamphlet International Publication No. 2000/53644 Pamphlet International Publication No. 2000/53664 Pamphlet International Publication No. 2001/74913 Pamphlet US Patent Application Publication No. 2002/0128618 JP-A-61-257235 International Publication No. 98/48857 Pamphlet

  The problem to be solved by the present invention is excellent in the absorption capacity indicated by the centrifuge retention capacity (CRC) and the absorption capacity (AAP) with respect to the pressure of 4.83 kPa, and is indicated by the saline flow conductivity (SFC) and the like. Water-absorbent resin particles and metal compounds that have excellent liquid permeability and diffusibility, excellent fluidity during moisture absorption, high damage resistance, excellent dust suppression effects, and are less likely to segregate added metal compounds. The object is to provide a water-absorbing resin composition containing the same and a method for producing the same.

  The present inventor has intensively studied to solve the above problems. As a result, the water-absorbing resin particles, the divalent and / or trivalent water-soluble polyvalent metal salt as the metal compound, and the nitrogen-containing ketone compound are mixed, preferably, the water-absorbing resin particles are divalent and In addition to adding a trivalent water-soluble polyvalent metal salt and further using a nitrogen-containing ketone compound, the divalent and / or trivalent water-soluble polyvalent metal salt and the nitrogen-containing ketone compound for the water-absorbent resin particles The present inventors have found that the above problem can be solved by setting the total use amount to a specific range of a small amount equal to or less than the same amount, and have completed the present invention.

  A water-absorbing polymer composition comprising at least one of alum, aluminum sulfate, dry alum, and dry aluminum sulfate, urea, and a water-absorbing polymer is known (Japanese Patent Laid-Open No. 2003). No. 306609)), and this technology is intended to impart antibacterial and deodorizing properties to the water-absorbing polymer. For this reason, in the water-absorbing polymer composition, alum, aluminum sulfate, dry alum, and The total content of at least one of the dry aluminum sulfate and urea is a large amount of 50 to 95% by weight (that is, at least equal to the weight of the water-absorbing polymer), and such a composition ratio The problem of the present invention cannot be achieved at all.

  The water-absorbent resin composition according to the present invention includes water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a nitrogen-containing ketone compound having a structure represented by the general formula (1) (A) a water-absorbing resin composition comprising (but not having a carboxyl group) and a divalent and / or trivalent water-soluble polyvalent metal salt, with respect to 100 parts by mass of the water-absorbing resin particles The total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass.

  The method for producing a water-absorbent resin composition according to the present invention has water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a structure represented by the general formula (1). A method for producing a water-absorbent resin composition comprising mixing a nitrogen-containing ketone compound (A) (but not having a carboxyl group) with a divalent and / or trivalent water-soluble polyvalent metal salt, The nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt are mixed so that the total amount is 0.01 to 100 parts by mass with respect to 100 parts by mass of the conductive resin particles.

  The method for producing a water-absorbent resin composition according to the present invention has water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a structure represented by the general formula (1). The nitrogen-containing ketone compound (A) (but not having a carboxyl group) and a divalent and / or trivalent water-soluble polyvalent metal salt powder are mixed.

  Another method for producing a water-absorbent resin composition according to the present invention includes a water-absorbent resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer, and a structure represented by the general formula (1). A nitrogen-containing ketone compound (A) having a carboxyl group (but not having a carboxyl group) and a liquid containing a divalent and / or trivalent water-soluble polyvalent metal salt.

  Another method for producing a water-absorbent resin composition according to the present invention includes a water-absorbent resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer, and a structure represented by the general formula (1). An aqueous solution containing a nitrogen-containing ketone compound (A) having no carboxylic acid (but not having a carboxyl group) and an aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt are mixed.

  Another method for producing a water-absorbent resin composition according to the present invention includes a water-absorbent resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer, and a structure represented by the general formula (1). One of the nitrogen-containing ketone compound (A) having no carboxylic acid (but not having a carboxyl group) and a divalent and / or trivalent water-soluble polyvalent metal salt is mixed as an aqueous solution, and the other is dry blended. .

  The water absorbent resin composition according to the present invention includes water absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water soluble unsaturated monomer, a hydrophilic organic compound, and a water soluble polyvalent metal salt. A water-absorbent resin composition having a liquid diffusion rate (LDV) of 2.1 to 10.0 mm / s.

  According to the present invention, the absorption capacity indicated by the centrifuge retention capacity (CRC) and the absorption capacity (AAP) with respect to the pressure of 4.83 kPa is excellent, and the liquid permeability indicated by the saline flow conductivity (SFC) and the like.・ Excellent diffusibility, excellent fluidity during moisture absorption, high damage resistance, excellent dust suppression effect, prevents penetration of added metal compounds into water-absorbent resin particles, and added metal compounds It is possible to provide a water-absorbent resin composition containing water-absorbent resin particles and a metal compound, and a method for producing the same.

  Hereinafter, the present invention will be described in detail. However, the scope of the present invention is not limited to these descriptions, and modifications other than the following examples can be made as appropriate without departing from the spirit of the present invention.

[Water-absorbent resin particles]
The water-absorbent resin particles used in the present invention are particles of a water-insoluble water-swellable hydrogel-forming polymer (hereinafter also referred to as a water-absorbent resin) that can be obtained by polymerizing a water-soluble unsaturated monomer, It has a spherical or indeterminate particle shape in which at least the physiological saline (0.90 mass% NaCl aqueous solution) has an absorption ratio of 5 times or more. In the present invention, the water absorbent resin particles may be simply referred to as a water absorbent resin.

  Specific examples of water-insoluble water-swellable hydrogel-forming polymers include partially neutralized crosslinked polyacrylic acid polymers (US Pat. No. 4,462,001, US Pat. No. 4,654,039, US Pat. No. 5,250,640, US Pat. No. 5,275,773, European Patent 456136, etc.) Cross-linked and partially neutralized starch-acrylic acid graft polymer (US Pat. No. 4,076,663), isobutylene-maleic acid copolymer Copolymer (US Pat. No. 4,389,513), saponified vinyl acetate-acrylic acid copolymer (US Pat. No. 4,124,748), hydrolyzate of acrylamide (co) polymer (US Pat. No. 3,959,569) ), Hydrolyzate of acrylonitrile polymer (US Pat. No. 3,935,099), etc. .

  The water-absorbent resin particles used in the present invention are polyacrylic acid (salt) -based crosslinked polymers containing acrylic acid and / or acrylate as structural units obtained by polymerizing a monomer containing acrylic acid and / or a salt thereof. It is preferable that it is the particle | grains of the water absorbing resin which consists of. In the present invention, the polyacrylic acid (salt) -based cross-linked polymer means a single unit containing 50 mol% or more, preferably 70 mol% or more, more preferably 90 mol% or more of acrylic acid and / or a salt thereof in all structural units. It is a crosslinked polymer obtained by polymerizing a monomer. Further, the acid group in the polymer is preferably neutralized by 50 to 90 mol%, more preferably 60 to 80 mol%, and the salt includes sodium, potassium and lithium. Examples thereof include alkali metal salts such as ammonium salts and amine salts. A sodium salt is preferable. Neutralization for forming a salt may be performed in a monomer state before polymerization, or may be performed in a polymer state during polymerization or after polymerization, or may be used in combination.

  The polyacrylic acid (salt) -based crosslinked polymer that is a water-absorbent resin particle preferably used in the present invention may be used in combination with a monomer (acrylic acid and / or a salt thereof) used as a main component, if necessary. These monomers may be copolymerized. Specific examples of other monomers include methacrylic acid, maleic acid, vinyl sulfonic acid, styrene sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid, 2- (meth) acryloyloxyethane sulfonic acid Anionic unsaturated monomers such as 2- (meth) acryloyloxypropanesulfonic acid and salts thereof; acrylamide, methacrylamide, N-ethyl (meth) acrylamide, Nn-propyl (meth) acrylamide, N-isopropyl (Meth) acrylamide, N, N-dimethyl (meth) acrylamide, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, methoxypolyethylene glycol (meth) acrylate, polyethylene glycol mono (meth) acrylate, Nonionic hydrophilic group-containing unsaturated monomers such as Nylpyridine, N-vinylpyrrolidone, N-acryloylpiperidine, N-acryloylpyrrolidine and N-vinylacetamide; N, N-dimethylaminoethyl (meth) acrylate, N, N -Cationically unsaturated monomers such as diethylaminoethyl (meth) acrylate, N, N-dimethylaminopropyl (meth) acrylate, N, N-dimethylaminopropyl (meth) acrylamide and quaternary salts thereof Can do. As for the usage-amount of monomers other than these acrylic acid and / or its salt, 0-30 mol% is preferable in all the monomers, More preferably, it is 0-10 mol%.

  The water-absorbent resin particles used in the present invention are cross-linked polymers having an internal cross-linked structure.

  As a method of introducing an internal cross-linked structure into the water-absorbent resin particles used in the present invention, a method of introducing by self-cross-linking without using a cross-linking agent, two or more polymerizable unsaturated groups and / or two in one molecule Examples thereof include a method of introducing the internal crosslinking agent having the above reactive group by copolymerization or reaction. Preferably, the internal cross-linking agent is introduced by copolymerization or reaction.

  Specific examples of these internal crosslinking agents include, for example, N, N′-methylenebis (meth) acrylamide, (poly) ethylene glycol di (meth) acrylate, (poly) propylene glycol di (meth) acrylate, trimethylolpropane tri (Meth) acrylate, trimethylolpropane di (meth) acrylate, glycerin tri (meth) acrylate, glycerin acrylate methacrylate, ethylene oxide modified trimethylolpropane tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol hexa ( (Meth) acrylate, triallyl cyanurate, triallyl isocyanurate, triallyl phosphate, triallylamine, poly (meth) allyloxyalkane, (poly) ethyl Glycol diglycidyl ether, glycerol diglycidyl ether; polyhydric alcohols such as ethylene glycol, polyethylene glycol, 1,4-butanediol, propylene glycol, glycerin, pentaerythritol; ethylenediamine, polyethyleneimine, glycidyl (meth) acrylate, etc. I can list them. These internal crosslinking agents may be used alone or in combination of two or more. Among them, it is preferable to use a compound having two or more polymerizable unsaturated groups as an internal crosslinking agent from the viewpoint of water absorption properties of the water-absorbent resin particles obtained, and the amount used is based on the total amount of monomers. 0.005-3 mol% is preferable, More preferably, it is 0.01-1.5 mol%.

  In the polymerization, hydrophilic polymers such as starch-cellulose, starch-cellulose derivatives, polyvinyl alcohol, polyacrylic acid (salt), cross-linked polyacrylic acid (salt), and chains such as hypophosphorous acid (salt) A transfer agent may be added.

  In order to obtain the water-absorbent resin particles used in the present invention, the above-described monomer containing acrylic acid and / or a salt thereof as a main component is subjected to bulk polymerization, reverse phase suspension polymerization, and precipitation polymerization. However, from the viewpoint of performance and ease of control of polymerization, it is preferable to perform aqueous solution polymerization using the monomer as an aqueous solution. Such polymerization methods are described, for example, in US Pat. No. 462501, US Pat. No. 4,769,427, US Pat. No. 4,873,299, US Pat. No. 4,093,763, US Pat. No. 4,367,323, US Pat. U.S. Pat. No. 4,446,261, U.S. Pat. No. 4,683,274, U.S. Pat.No. 4,690,996, U.S. Pat. No. 4,721,647, U.S. Pat. No. 4,738,867, U.S. Pat. It is described in the description.

  In performing the polymerization, radical polymerization initiators such as potassium persulfate, ammonium persulfate, sodium persulfate, t-butyl hydroperoxide, hydrogen peroxide, 2,2'-azobis (2-amidinopropane) dihydrochloride, ultraviolet rays And active energy rays such as electron beam can be used. Moreover, when using a radical polymerization initiator, it is good also as redox polymerization combining reducing agents, such as sodium sulfite, sodium hydrogensulfite, ferrous sulfate, and L-ascorbic acid. The amount of these polymerization initiators used is preferably 0.001 to 2 mol%, more preferably 0.01 to 0.5 mol%, based on all monomers.

  The shape of the water-absorbing resin particles obtained by the above polymerization is generally an irregularly crushed shape, a spherical shape, a fiber shape, a rod shape, a substantially spherical shape, a flat shape, etc., but the water-absorbing resin particles used in the present invention are Since it is in the form of particles, it is preferable to use an irregularly pulverized product obtained by pulverization after drying because the effect of the present invention is further increased.

  The water-absorbent resin particles used in the present invention are preferably those in which the vicinity of the surface is subjected to surface crosslinking treatment.

  The surface cross-linking treatment may be performed using a surface cross-linking agent or other known surface cross-linking treatment methods.

  Examples of the surface cross-linking agent that can be used for the surface cross-linking treatment include organic surface cross-linking agents and polyvalent metal compounds having two or more functional groups that can react with the carboxyl group, in particular, the functional groups of the water-absorbent resin particles. . For example, ethylene glycol, diethylene glycol, propylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, 1,3-propanediol, dipropylene glycol, 2,2,4-trimethyl-1,3-pentanediol, polypropylene glycol, Glycerin, polyglycerol, 2-butene-1,4-diol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,2-cyclohexanedimethanol 1,2-cyclohexanol, trimethylolpropane, diethanolamine, triethanolamine, polyoxypropylene, oxyethylene-oxypropylene block copolymer, pentaerythritol, sorbitol Polyhydric alcohols of: ethylene glycol diglycidyl ether, polyethylene glycol diglycidyl ether, glycerol polyglycidyl ether, diglycerol polyglycidyl ether, polyglycerol polyglycidyl ether, propylene glycol diglycidyl ether, polypropylene glycol diglycidyl ether, glycidol etc. Compound; polyvalent amine compounds such as ethylenediamine, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, pentaethylenehexamine, and polyethyleneimine, and inorganic or organic salts thereof (for example, azetidinium salt); 2,4-tolylene Polyisocyanate compounds such as isocyanate and hexamethylene diisocyanate; 1,2-ethylene bi Polyvalent oxazoline compounds such as oxazoline; carbonic acid derivatives such as urea, thiourea, guanidine, dicyandiamide and 2-oxazolidinone; 1,3-dioxolan-2-one, 4-methyl-1,3-dioxolan-2-one, 4 , 5-dimethyl-1,3-dioxolan-2-one, 4,4-dimethyl-1,3-dioxolan-2-one, 4-ethyl-1,3-dioxolan-2-one, 4-hydroxymethyl- 1,3-dioxolan-2-one, 1,3-dioxan-2-one, 4-methyl-1,3-dioxan-2-one, 4,6-dimethyl-1,3-dioxan-2-one, Alkylene carbonate compounds such as 1,3-dioxopan-2-one; haloepoxidation of epichlorohydrin, epibromohydrin, α-methylepichlorohydrin, etc. , And polyvalent amine adducts thereof (for example, Hercules Kaimen: registered trademark); silane coupling agents such as γ-glycidoxypropyltrimethoxysilane and γ-aminopropyltriethoxysilane; 3-methyl-3- Oxetanemethanol, 3-ethyl-3-oxetanemethanol, 3-butyl-3-oxetanemethanol, 3-methyl-3-oxetaneethanol, 3-ethyl-3-oxetaneethanol, 3-butyl-3-oxetaneethanol, 3- Oxetane compounds such as chloromethyl-3-methyloxetane, 3-chloromethyl-3-ethyloxetane, and polyvalent oxetane compounds; These surface cross-linking agents may be used alone or in combination of two or more. Of these, polyhydric alcohols are preferred because they are highly safe and can improve the hydrophilicity of the surface of the water-absorbent resin particles. Further, by using a polyhydric alcohol, familiarity with the divalent and / or trivalent water-soluble polyvalent metal salt on the surface of the water-absorbent resin particles is improved, and the polyhydric alcohol residue and the divalent and / or 3 Due to the interaction with the surface of the water-soluble polyvalent metal salt having a valence, it becomes possible to make the water-soluble resin particle surface more uniformly present with a divalent and / or trivalent water-soluble metal salt.

  As for the usage-amount of a surface crosslinking agent, 0.001-5 mass parts is preferable with respect to 100 mass parts of solid content of a water absorbing resin particle.

  Water may be used in mixing the surface cross-linking agent and the water-absorbent resin particles. The amount of water used is more than 0.5, preferably 10 parts by mass or less, and more preferably in the range of 1 part by mass to 5 parts by mass with respect to 100 parts by mass of the solid content of the water absorbent resin particles.

  When mixing the surface cross-linking agent or its aqueous solution, a hydrophilic organic solvent or a third substance may be used as a mixing aid.

  When a hydrophilic organic solvent is used, for example, lower alcohols such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, isobutyl alcohol, and t-butyl alcohol; ketones such as acetone; Ethers such as dioxane, tetrahydrofuran and methoxy (poly) ethylene glycol; Amides such as ε-caprolactam and N, N-dimethylformamide; Sulphoxides such as dimethyl sulfoxide; Ethylene glycol, diethylene glycol, propylene glycol, triethylene glycol, tetra Ethylene glycol, polyethylene glycol, 1,3-propanediol, dipropylene glycol, 2,2,4-trimethyl-1,3-pentanediol, polypropylene Glycol, glycerol, polyglycerol, 2-butene-1,4-diol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,2-cyclohexane Examples include dimethanol, 1,2-cyclohexanol, trimethylolpropane, diethanolamine, triethanolamine, polyoxypropylene, oxyethylene-oxypropylene block copolymers, polyhydric alcohols such as pentaerythritol and sorbitol. The amount of the hydrophilic organic solvent used is preferably 10 parts by mass or less with respect to 100 parts by mass of the solid content of the water-absorbent resin particles, although it depends on the type, particle size, water content and the like of the water-absorbent resin particles. A range of 1 part by mass to 5 parts by mass is more preferable. In addition, inorganic acids, organic acids, polyamino acids and the like shown in European Patent No. 0668080 may be present as the third substance. These mixing aids may act as a surface cross-linking agent, but those that do not deteriorate the water absorption performance of the water-absorbent resin particles after surface cross-linking are preferred. In particular, volatile alcohols having a boiling point of less than 150 ° C. are volatilized during the surface cross-linking treatment, and therefore it is desirable that no residue remains.

  In order to mix the water-absorbent resin particles and the surface cross-linking agent more uniformly, non-crosslinkable water-soluble inorganic bases (preferably alkali metal salts, ammonium salts, alkali metal hydroxides, and ammonia or hydroxide thereof) Product) and non-reducing alkali metal salt pH buffer (preferably hydrogen carbonate, dihydrogen phosphate, hydrogen phosphate, etc.) are allowed to coexist when the water absorbent resin particles and the surface cross-linking agent are mixed. May be. These use amounts depend on the type and particle size of the water-absorbent resin particles, but are preferably in the range of 0.005 to 10 parts by mass with respect to 100 parts by mass of the solid content of the water-absorbent resin particles. Within the range of ˜5 parts by mass is more preferable.

  The mixing method for mixing the water-absorbent resin particles and the surface cross-linking agent is not particularly limited. For example, the water-absorbent resin particles are immersed in a hydrophilic organic solvent and dissolved in water and / or the hydrophilic organic solvent as necessary. Examples thereof include a method of mixing a surface cross-linking agent and a method of directly mixing water-absorbent resin particles with a surface cross-linking agent dissolved in water and / or a hydrophilic organic solvent by spraying or dropping.

  After mixing the water-absorbent resin particles and the surface cross-linking agent, it is usually preferable to perform a heat treatment to carry out the cross-linking reaction. Although the said heat processing temperature is based also on the surface crosslinking agent to be used, 40 to 250 degreeC is preferable and 150 to 250 degreeC is more preferable. When the heat treatment temperature is less than 40 ° C., absorption characteristics such as absorption capacity under pressure may not be sufficiently improved. When the heat treatment temperature exceeds 250 ° C., the water absorbent resin particles are deteriorated, and various performances may be deteriorated. The heat treatment time is preferably 1 minute to 2 hours, more preferably 5 minutes to 1 hour.

  When the water-absorbent resin particles in the present invention are heat-treated, the heat treatment method is described in, for example, European Patent No. 530517, European Patent No. 603292, International Publication No. 95/05856. A method of further heating the water-absorbent resin particles after drying is mentioned.

  There is no particular limitation on the particle size and particle size distribution of the water-absorbent resin particles used in the present invention, but if the particle size distribution is relatively small and the particle size distribution has many small particle size components, the absorption performance such as the absorption capacity This is preferable because the improvement in the resistance is remarkable.

  The water absorbent resin particles used in the present invention preferably have a mass average particle diameter of 100 to 600 μm. More preferably, it is 200-500 micrometers. When the mass average particle size is out of the range of 100 to 600 μm, the liquid permeability and diffusibility are remarkably reduced or the absorption rate is greatly reduced. For example, when used for diapers, there is a risk of causing liquid leakage and the like. . In addition, fine particles of water-absorbent resin particles having a particle diameter of 300 μm or less may be granulated and adjusted in particle size, and primary particles obtained by pulverization may be formed into irregularly crushed particles of fine particles. Alternatively, water-absorbing resin particles partially mixed with may be used. When a part of the granulated product of water-absorbing resin particles is mixed, a water-absorbing resin composition having further excellent absorption characteristics such as water absorption speed and capillary absorption capacity can be obtained. The mixing amount of the granulated fine powder is preferably 5% by mass or more, more preferably 10% by mass or more, and further preferably 15% by mass or more.

  As a method for producing a fine granulated product, a known technique for regenerating fine powder can be used. For example, a method in which warm water and fine powder of water absorbent resin particles are mixed and dried (US Pat. No. 6,228,930), or a method in which fine powder of water absorbent resin particles is mixed with an aqueous monomer solution and polymerized (US Pat. No. 5,264,495). Description), a method of adding water to fine powder of water-absorbent resin particles and granulating at a specific surface pressure or higher (European Patent No. 844270), an amorphous gel that sufficiently wets the fine powder of water-absorbent resin particles It is possible to use a method of forming and drying / pulverizing (US Pat. No. 4,950,692), a method of mixing fine particles of water-absorbent resin particles and a polymer gel (US Pat. No. 5,478,879), etc. Preferably, a method in which the warm water and fine powder of water-absorbent resin particles are mixed and dried is used. The particle diameter is indicated by the sieve diameter to be classified.

  The water-absorbent resin particles used in the present invention have a centrifuge retention capacity (CRC) of preferably 5 (g / g) or more, more preferably 10 (g / g) or more, and still more preferably 20 ( g / g) or more, and particularly preferably 25 (g / g) or more. Although an upper limit is not specifically limited, Preferably it is 50 (g / g) or less, More preferably, it is 45 (g / g) or less, More preferably, it is 40 (g / g) or less. When the centrifuge retention capacity (CRC) is less than 10 (g / g), the amount of absorption is too small and it is not suitable for the use of sanitary materials such as diapers. Moreover, when the centrifuge retention capacity (CRC) is larger than 50 (g / g), there is a possibility that a water absorbent resin composition having excellent liquid permeability cannot be obtained.

  The water-absorbent resin particles used in the present invention have an absorptivity (AAP) with respect to a pressure of 4.83 kPa, preferably 18 (g / g) or more, more preferably 20 (g / g) or more, and still more preferably. Is 22 (g / g) or more. When the absorptive power (AAP) with respect to the pressure of 4.83 kPa is less than 18 (g / g), there is a possibility that a water absorbent resin composition having excellent liquid permeability cannot be obtained.

Water absorbent resin particles used in the present invention, saline flow conductivity (SFC), preferably ^{10 (× 10 -7 · cm 3} · s · g -1) or more, more preferably 30 (× 10 ^{- 7} · cm ³ · s · g ⁻¹ ) or more, more preferably 50 (× 10 ⁻⁷ · cm ³ · s · g ⁻¹ ) or more. When the saline flow conductivity (SFC) is less than 10 (× 10 ⁻⁷ · cm ³ · s · g ⁻¹ ), a divalent and / or trivalent water-soluble polyvalent metal salt and a nitrogen-containing ketone compound (A ) May not improve liquid permeability.

  The water-absorbent resin particles used in the present invention preferably have a water-soluble content of 35% by mass or less, more preferably 25% by mass or less, and further preferably 15% by mass or less. When the water-soluble content exceeds 35% by mass, the gel strength is weak and the liquid permeability may be inferior. In addition, when used for a long time in a diaper, the absorption characteristics (such as CRC and AAP) may deteriorate over time.

[Water-absorbing resin composition]
The water-absorbent resin composition according to the present invention includes water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a nitrogen-containing ketone compound having a structure represented by the general formula (1) (A) a water-absorbing resin composition comprising (but not having a carboxyl group) and a divalent and / or trivalent water-soluble polyvalent metal salt, with respect to 100 parts by mass of the water-absorbing resin particles The total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass.

  The water-absorbent resin composition according to the present invention comprises a water-absorbent resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer, a hydrophilic organic compound, and a divalent and / or trivalent water-soluble. A water-absorbent resin composition containing a polyvalent metal salt, wherein a liquid diffusion rate (LDV) is 2.1 to 10.0 mm / s.

  Examples of the hydrophilic organic compound include water-soluble organic compounds. Although not particularly limited, more specifically, the surface cross-linking agents exemplified above, nitrogen-containing ketone compounds (A), organic acids and the like can be mentioned. Particularly preferred as the hydrophilic organic compound is a nitrogen-containing ketone compound (A). Only one hydrophilic organic compound may be used, or two or more hydrophilic organic compounds may be used in combination.

  The hydrophilic organic compound has a solubility in 100 g of water at 1 atm and 25 ° C. of preferably 10 g or more, more preferably 20 g or more, and further preferably 40 g or more.

  As a hydrophilic organic compound, molecular weight becomes like this. Preferably it is 45-10000 g / mol, More preferably, it is 59-1000 g / mol, More preferably, it is 60-150 g / mol.

  In the water absorbent resin composition according to the present invention, the total amount of the hydrophilic organic compound and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water absorbent resin particles. 100 parts by mass, preferably 0.05 to 50 parts by mass, more preferably 0.1 to 10 parts by mass, and particularly preferably 0.5 to 5 parts by mass. If the total amount of the hydrophilic organic compound and the divalent and / or trivalent water-soluble polyvalent metal salt is less than 0.01 parts by mass, the effect of improving liquid permeability / diffusibility and blocking rate may not be sufficient. If it is more than 100 parts by mass, the absorption characteristics such as CRC and AAP may be remarkably deteriorated.

  In the water-absorbent resin composition according to the present invention, the ratio of the content of the hydrophilic organic compound and the content of the divalent and / or trivalent water-soluble polyvalent metal salt is preferably a mass ratio, preferably 1: 10 to 10: 1, more preferably 3: 7 to 7: 3. If the ratio of the content of the hydrophilic organic compound and the content of the divalent and / or trivalent water-soluble polyvalent metal salt is outside the range of 1:10 to 10: 1 by mass ratio, There is a possibility that the effect of improving the diffusibility and the blocking rate is not sufficient, or the absorption characteristics such as CRC and AAP are remarkably deteriorated.

  In the water-absorbent resin composition according to the present invention, at least a part of the surface of the water-absorbent resin particles is composed of a hydrophilic organic compound and a divalent and / or trivalent water-soluble solution in order to sufficiently exhibit the effects of the present invention. It is preferable to coat with a functional polyvalent metal salt. Furthermore, it is more preferable that the coating is not a coating on the entire surface of the water-absorbent resin particles. If the entire surface of the water-absorbent resin particles is coated, the absorption rate (for example, the centrifuge retention capacity (CRC) or the absorption capacity (AAP) with respect to the pressure of 4.83 kPa) may be greatly reduced.

  In the water-absorbent resin composition according to the present invention, the hydrophilic organic compound preferably contains a polyhydric alcohol (exemplified as the above-mentioned surface cross-linking agent).

  In the water-absorbent resin composition according to the present invention, the hydrophilic organic compound preferably contains a nitrogen-containing ketone compound (A).

  The water-absorbing resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer are as described above, and are preferably subjected to surface cross-linking treatment.

  The nitrogen-containing ketone compound (A) is a nitrogen-containing ketone compound (A) having a structure represented by the general formula (1) (however, having no carboxyl group), for example, methyl carbamate, carbamic acid Carbamic acid alkyl such as ethyl; carbazic acid alkyl such as ethyl carbazate; fatty acid amide such as formamide, acetamide and propionamide; nitrogen of amide group such as N, N-dimethylacetamide and N-methylacetamide is substituted with an alkyl group Compounds; acrylamides such as (meth) acrylamide, N-isopropylacrylamide, N, N-dimethylacrylamide; 2-oxazolidone; 3-methyl-2-oxazolidinone, 3-alkyl-2-oxazolidinone, 4-methyl-2- Oxazolidinone, 4-al 2-Oxazolidinones such as lu-2-oxazolidinone; Oxazolidinones such as 2,5-oxazolidinedinone; 2-pyrrolidinone, 3-hydroxymethyl-2-pyrrolidinone, 3-alkyl-2-pyrrolidinone; 4-alkyl-2 -2-pyrrolidinones such as pyrrolidinone and 5-alkyl-2-pyrrolidinone; pyrrolidinedinones such as 2,5-pyrrolidinedinone; urea having a structure represented by the general formula (2) and / or a derivative thereof; Can be mentioned. Preferred is urea and / or a derivative thereof having a structure represented by the general formula (2). The urea having a structure represented by the general formula (2) and / or a derivative thereof has a structure in which the interaction with the divalent and / or trivalent water-soluble polyvalent metal salt is represented by the general formula (1). It is preferable because it is considered to be stronger than the nitrogen-containing ketone compound (A).

  The nitrogen-containing ketone compound (A) (preferably urea having a structure represented by the general formula (2) and / or a derivative thereof) is preferably water-soluble and has a solubility in 100 g of water at 1 atm and 25 ° C. , Preferably 10 g or more, more preferably 20 g or more, and even more preferably 40 g or more.

  The nitrogen-containing ketone compound (A) (preferably urea having a structure represented by the general formula (2) and / or a derivative thereof) preferably has a molecular weight of 45 to 10,000 g / mol, more preferably 59 to 1000 g. / Mol, more preferably 60 to 150 g / mol.

  The nitrogen-containing ketone compound (A) (preferably urea having a structure represented by the general formula (2) and / or a derivative thereof) is preferably highly safe and stable.

  Specific examples of urea and / or derivatives thereof having the structure represented by the general formula (2) include urea; N-methylurea, N-ethylurea, N, N′-dimethylurea, and ethyleneurea. , N, N-dimethylurea and other urea derivatives having an alkyl group bonded to urea nitrogen; hydroxyurea, N, N′-dihydroxyurea, N-hydroxy-N′-methylurea, N-hydroxy-N-methyl Urea derivatives such as urea having a hydroxyl group bonded to the nitrogen of urea; urea having a cyano group bonded to the nitrogen of urea, such as cyanourea, N-cyano-N′-methylurea, N-cyano-N-methylurea Hydroxymethylurea; Cyanomethylurea; Nitrosourea; Hydrazinecarboxamide; Carbonic dihydrazide; Formylurea; 1-aziridinecarboxa A urea derivative in which boron is bonded to urea nitrogen, such as N, N′-diborylurea; a urea derivative in which silicon is bonded to urea nitrogen, such as silylurea; 1,3-diazetidin-2-one; Preferred examples include urea; 2-propynylurea; phosphoranilidene urea; ethenylurea; methyleneurea; carbonicyanocyanidamide; 1,2,4-oxadiazetidin-3-one; aminomethylurea; ethynylurea; . More preferably, urea; urea derivatives in which an alkyl group is bonded to nitrogen of urea, such as N-methylurea, N-ethylurea, N, N′-dimethylurea, ethyleneurea, N, N-dimethylurea; N, N′-dihydroxyurea, N-hydroxy-N′-methylurea, N-hydroxy-N-methylurea, and the like, and more preferably urea derivatives having a hydroxyl group bonded to the nitrogen of urea. A urea derivative in which an alkyl group is bonded to nitrogen of urea, such as N-methylurea, N-ethylurea, N, N′-dimethylurea, ethyleneurea, N, N-dimethylurea; Among these, urea is particularly preferable because it has a particularly strong interaction with a divalent and / or trivalent water-soluble polyvalent metal salt and is considered to have a strong affinity with water.

  Further, the nitrogen-containing ketone compound (A) having the structure represented by the general formula (1) and the urea and / or its derivative having the structure represented by the general formula (2) are divalent and / or trivalent. When mixed with a water-soluble polyvalent metal salt in an aqueous solution, a stable homogeneous solution is preferred.

  The divalent and / or trivalent water-soluble polyvalent metal salt is a metal salt having a divalent and / or trivalent valence, and is preferably in a powder form. Considering that the water-absorbent resin composition according to the present invention is used as an absorbent material for sanitary materials such as diapers, it is preferable to select a water-absorbent resin composition that does not color the water-absorbent resin composition and has low toxicity to the human body.

  In order to maintain the effect of the divalent and / or trivalent water-soluble polyvalent metal salt more efficiently for a long time at the time of liquid absorption, the divalent and / or soluble in pure water at room temperature at a concentration of 5% by mass or more Alternatively, it is preferable to select a trivalent water-soluble polyvalent metal salt, more preferably 10% by mass or more, and still more preferably 20% by mass or more.

  Examples of divalent and / or trivalent water-soluble polyvalent metal salts that can be used in the present invention include aluminum chloride, polyaluminum chloride, aluminum sulfate, aluminum nitrate, potassium aluminum bissulfate, sodium aluminum bissulfate, and potassium alum. , Ammonium alum, sodium alum, sodium aluminate, calcium chloride, calcium nitrate, magnesium chloride, magnesium sulfate, magnesium nitrate, zinc chloride, zinc sulfate, zinc nitrate, iron (III) chloride, cerium (III) chloride, ruthenium chloride ( III), yttrium chloride (III), chromium chloride (III) and the like can be exemplified. Moreover, it is preferable to use the salt which has these crystal waters also from the point of solubility with absorption liquids, such as urine. Particularly preferred are aluminum compounds, among which aluminum chloride, polyaluminum chloride, aluminum sulfate, aluminum nitrate, potassium aluminum bissulfate, sodium aluminum bissulfate, potassium alum, ammonium alum, sodium alum, sodium aluminate are preferred, aluminum sulfate Is particularly preferable, and powders of hydrous crystals such as aluminum sulfate 18 hydrate and aluminum sulfate 14-18 hydrate can be most preferably used. These may be used alone or in combination of two or more.

  The divalent and / or trivalent water-soluble polyvalent metal salt that can be used in the present invention is preferably in the form of particles, and the particle size of the water-absorbent resin particles is from the viewpoint of mixing properties. Preferably it is smaller. The mass average particle diameter is preferably 500 μm or less, and more preferably 400 μm or less. From the viewpoint of performance, it is more preferably a particle containing particles having a particle diameter of 150 μm or less in an amount of 20% by mass or more based on the total of the divalent and / or trivalent water-soluble polyvalent metal salt, most preferably Particles containing 30% by mass or more.

  In the water absorbent resin composition according to the present invention, the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0 with respect to 100 parts by mass of the water absorbent resin particles. 0.01 to 100 parts by mass, preferably 0.05 to 50 parts by mass, more preferably 0.1 to 10 parts by mass, and particularly preferably 0.5 to 5 parts by mass. When the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is less than 0.01 parts by mass, the effect of improving liquid permeability / diffusibility and blocking rate is sufficient. If the amount is more than 100 parts by mass, absorption characteristics such as CRC and AAP may be remarkably deteriorated.

  In the water absorbent resin composition according to the present invention, the ratio of the content of the nitrogen-containing ketone compound (A) and the content of the divalent and / or trivalent water-soluble polyvalent metal salt is preferably a mass ratio. Is 1:10 to 10: 1, more preferably 3: 7 to 7: 3. When the ratio of the content of the nitrogen-containing ketone compound (A) and the content of the divalent and / or trivalent water-soluble polyvalent metal salt is outside the range of 1:10 to 10: 1 by mass ratio, There is a possibility that the effect of improving liquidity / diffusibility and blocking rate is not sufficient, and absorption characteristics such as CRC and AAP are remarkably deteriorated.

  In the water-absorbent resin composition according to the present invention, at least a part of the surface of the water-absorbent resin particles is the nitrogen-containing ketone compound (A) and the divalent and / or in order to fully exhibit the effects of the present invention. It is preferably coated with a trivalent water-soluble polyvalent metal salt. Furthermore, it is more preferable that the coating is not a coating on the entire surface of the water-absorbent resin particles. If the entire surface of the water-absorbent resin particles is coated, the absorption rate (for example, the centrifuge retention capacity (CRC) or the absorption capacity (AAP) with respect to the pressure of 4.83 kPa) may be greatly reduced.

  The water-absorbent resin composition according to the present invention preferably has a mass average particle diameter of 100 to 600 μm. More preferably, it is 200-500 micrometers. When the mass average particle size is out of the range of 100 to 600 μm, the liquid permeability and diffusibility are remarkably reduced or the absorption rate is greatly reduced. For example, when used for diapers, there is a risk of causing liquid leakage and the like. .

  The water-absorbent resin composition according to the present invention preferably has 90% by mass or more of particles having a particle size of 150 to 850 μm, and more preferably 90% by mass or more of particles having a particle size of 150 to 600 μm. preferable.

  The water-absorbent resin composition according to the present invention preferably has a logarithmic standard deviation (σζ) of particle size distribution of 0.25 to 0.45, more preferably 0.27 to 0.43, and most preferably 0.30. ~ 0.40 mm / s. The logarithmic standard deviation (σζ) of the particle size distribution is a numerical value indicating the spread of the particle size distribution. The smaller the logarithmic standard deviation (σζ) of the particle size distribution, the narrower the particle size distribution. When the logarithmic standard deviation (σζ) of the particle size distribution is less than 0.25, the particle size distribution is too narrow, and the balance between liquid diffusion / liquid permeability and capillary force may be deteriorated. If it exceeds 0.45, there may be a problem in handleability, or the balance between liquid diffusion / liquid permeability and capillary force may be deteriorated.

  The water-absorbent resin composition according to the present invention has a centrifuge retention capacity (CRC) of preferably 5 (g / g) or more, more preferably 10 (g / g) or more, and even more preferably 15 (G / g) or more, more preferably 20 (g / g) or more, and most preferably 25 (g / g) or more. Although an upper limit is not specifically limited, Preferably it is 50 (g / g) or less, More preferably, it is 40 (g / g) or less, More preferably, it is 35 (g / g) or less. When the centrifuge retention capacity (CRC) is less than 5 (g / g), the amount of absorption is too small and it is not suitable for the use of sanitary materials such as diapers. Moreover, when centrifuge retention capacity (CRC) is larger than 50 (g / g), there exists a possibility that gel strength is weak and cannot obtain the water absorbing resin composition excellent in liquid permeability.

  The water absorbent resin composition according to the present invention has an absorptive power (AAP) with respect to a pressure of 4.83 kPa, preferably 10 (g / g) or more, more preferably 15 (g / g) or more, Preferably it is 20 (g / g) or more. When the absorbency (AAP) for pressure of 4.83 kPa is less than 10 (g / g), for example, when used for a diaper, the amount of return, so-called Re-wet, may increase and cause baby skin roughness .

The water-absorbent resin composition according to the present invention has a saline flow conductivity (SFC) of preferably 30 (× 10 ⁻⁷ · cm ³ · s · g ⁻¹ ) or more, more preferably 70 (× 10). ⁻⁷ · cm ³ · s · g ⁻¹ ) or more, more preferably 100 (× 10 ⁻⁷ · cm ³ · s · g ⁻¹ ) or more, and particularly preferably 130 (× 10 ⁻⁷ · cm). ³ · s · g ⁻¹ ) or more. When the saline flow conductivity (SFC) is less than 30 (× 10 ⁻⁷ · cm ³ · s · g ⁻¹ ), the concentration of the water-absorbent resin particles in the diaper core is 30% by mass or more, preferably 50 In the case of mass% or more, the absorption rate of urine becomes slow and may cause leakage.

  The water-absorbent resin composition according to the present invention has a water-soluble content of preferably 35% by mass or less, more preferably 25% by mass or less, and further preferably 15% by mass or less. When the water-soluble content exceeds 35% by mass, the gel strength is weak and the liquid permeability may be inferior. In addition, when used for a long time in a diaper, the absorption capacity (CRC, AAP, etc.) may decrease over time.

The water-absorbent resin composition according to the present invention is excellent in dust suppression effect. Dust generation amount is preferably 1.00 mg / ^{m 3} or less, more preferably 0.30 mg / ^{m 3} or less.

  The water-absorbent resin composition according to the present invention is excellent in blocking rate (BR). The blocking rate (BR) is preferably 35% or less, more preferably 10% or less.

  The water-absorbent resin composition according to the present invention preferably has an excellent liquid diffusion rate (LDV). LDV is a parameter indicating “liquid suction property”. In the performance of absorbent articles such as disposable diapers and sanitary napkins, or the water absorbing body, LDV relates to the speed at which the liquid in the water absorbing body diffuses, and in particular to the speed at which the initial liquid is absorbed. That is, the water-absorbent resin composition having excellent LDV can remarkably improve liquid diffusibility during actual use of diapers and the like. In the water absorbent resin composition according to the present invention, the lower limit value of LDV is preferably 2.1 mm / s or more, more preferably 2.3 mm / s or more, and most preferably 2.5 mm / s or more. In the water-absorbent resin composition according to the present invention, the upper limit of LDV is not particularly limited, but is preferably 10 mm / s or less, more preferably 5 mm / s or less. In the numerical range of the LDV of the water absorbent resin composition according to the present invention, an upper limit value and a lower limit value can be appropriately combined. As a more specific numerical range, the water-absorbent resin composition according to the present invention preferably has a liquid diffusion rate (LDV) of 2.1 to 10 mm / s, more preferably 2.3 to 10 mm / s. More preferably, it is 2.5-10 mm / s, Most preferably, it is 2.5-5 mm / s.

  The water content of the water absorbent resin composition according to the present invention is preferably 0.1% by mass or more, more preferably less than 10% by mass, and particularly preferably less than 5% by mass.

[Method for producing water-absorbing resin composition]
Water-absorbing resin particles comprising water-absorbing resin particles having an internal crosslinking structure obtained by polymerizing a water-soluble unsaturated monomer, a nitrogen-containing ketone compound (A), and a divalent and / or trivalent water-soluble polyvalent metal salt Although the method to manufacture a resin composition is not specifically limited, Preferably the following manufacturing methods 1-4 are mentioned.

(Manufacturing method 1)
A first production method (production method 1) of a water-absorbent resin composition according to the present invention comprises a nitrogen-containing ketone compound on water-absorbent resin particles having an internal crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer. (A) and a divalent and / or trivalent water-soluble polyvalent metal salt powder are mixed.

  In the above, the powder is particularly preferably mixed under heating or heated after mixing (in the following description, this is referred to as heat fusion).

  The heat-sealing of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt to the water-absorbent resin particles is performed by using the nitrogen-containing ketone compound (A) and the divalent and / or trivalent The water-soluble polyvalent metal salt may be heat-sealed simultaneously, or the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt may be heat-sealed separately.

  The nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt are used in an amount of 100 parts by mass of the water-absorbent resin particles, and the nitrogen-containing ketone compound (A) and the divalent and / or Alternatively, the total amount of the trivalent water-soluble polyvalent metal salt is preferably 0.01 to 100 parts by mass, more preferably 0.05 to 50 parts by mass, still more preferably 0.1 to 10 parts by mass, particularly Preferably it is 0.5-5 mass parts. When the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is less than 0.01 parts by mass, the effect of improving liquid permeability / diffusibility and blocking rate is sufficient. If the amount is more than 100 parts by mass, absorption characteristics such as CRC and AAP may be remarkably deteriorated.

  The ratio between the amount of the nitrogen-containing ketone compound (A) used and the amount of the divalent and / or trivalent water-soluble polyvalent metal salt is, in mass ratio, preferably 1:10 to 10: 1, more preferably 3: 7-7: 3. When the ratio of the amount of nitrogen-containing ketone compound (A) used to the amount of divalent and / or trivalent water-soluble polyvalent metal salt is outside the range of 1:10 to 10: 1 by mass ratio, There is a possibility that the effect of improving liquidity / diffusibility and blocking rate is not sufficient, and absorption characteristics such as CRC and AAP are remarkably deteriorated.

  The heat fusion in the present invention means that the nitrogen-containing ketone compound (A) and at least part of the divalent and / or trivalent water-soluble polyvalent metal salt become softer than the molten or solid state by heat, and absorbs water. A method of adhering to the surface of resin particles.

That is, it is not particularly limited as long as it is the above method, but for example, there are the following methods (a) to (d).
(A) Nitrogen-containing ketone compound (A) and water-absorbent resin particles heated to a melting point or higher of the divalent and / or trivalent water-soluble polyvalent metal salt and nitrogen-containing ketone compound (A) and divalent and / or 3 A method of mixing a valent water-soluble polyvalent metal salt.
(B) Nitrogen-containing ketone compound (A) heated above the melting point of the nitrogen-containing ketone compound (A) and divalent and / or 3 heated above the melting point of the divalent and / or trivalent water-soluble polyvalent metal salt. A method of mixing a valent water-soluble polyvalent metal salt and water-absorbent resin particles.
(C) After mixing the water-absorbing resin particles, the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt, the mixture is mixed with the nitrogen-containing ketone compound (A) and the divalent and / or Or the method of heating more than melting | fusing point of trivalent water-soluble polyvalent metal salt.
(D) The water-absorbing resin particles heated above the melting point of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt, and heated above the melting point of the nitrogen-containing ketone compound (A). A method of mixing a nitrogen-containing ketone compound (A) and a divalent and / or trivalent water-soluble polyvalent metal salt heated to a melting point or higher of a divalent and / or trivalent water-soluble polyvalent metal salt.

  These methods are preferred, but other methods can be used.

  Examples of the heating means include heaters, microwaves, ultrasonic waves, and far infrared rays.

  When heating, it is preferable to heat above the melting point of the nitrogen-containing ketone compound (A) and the water-soluble polyvalent metal. The temperature range of heating is preferably 100 to 200 ° C, more preferably 120 to 180 ° C, and most preferably 130 to 150 ° C.

  The addition / mixing method is not particularly limited, and a known powder addition / mixing method may be used. A method of adding a predetermined amount of the nitrogen-containing ketone compound (A) and a divalent and / or trivalent water-soluble polyvalent metal salt to the water-absorbent resin particles all at once or in a divided or continuous manner is preferred.

  The addition / mixing is preferably performed with stirring. Further, it is preferable that at least a part of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is fused to the surface of the water-absorbent resin particles with stirring.

  As a stirring apparatus, a paddle blender, a ribbon mixer, a rotary blender, a jar tumbler, a plow jar mixer, a mortar mixer, or the like can be used. These stirring devices may be devices that can be heated, or may be devices that cool the heated mixture.

  Although stirring time is not specifically limited, Preferably it is 60 minutes or less, More preferably, it is 30 minutes or less.

  When heat-sealing, it is preferable to pressurize a mixture of water-absorbing resin particles, a nitrogen-containing ketone compound (A), and a divalent and / or trivalent water-soluble polyvalent metal salt. By applying pressure, heat fusion is promoted.

(Manufacturing method 2)
A second production method (production method 2) of a water-absorbent resin composition according to the present invention comprises water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a nitrogen-containing ketone compound (A) and a liquid containing a divalent and / or trivalent water-soluble polyvalent metal salt are mixed.

  Use amount of nitrogen-containing ketone compound (A) and divalent and / or trivalent water-soluble polyvalent metal salt, use amount of nitrogen-containing ketone compound (A) and divalent and / or trivalent water-soluble polyvalent metal The ratio to the amount of salt used is the same as in Production Method 1 described above.

  Examples of the liquid substance containing the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt include, for example, the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt. The liquid substance which consists only of a valent metal salt may be sufficient, and the liquid substance in which liquids, such as water and a polyhydric alcohol (preferably what was illustrated previously), may be contained in these. In particular, the present inventor completed the present invention to form a liquid material by mixing a nitrogen-containing ketone compound (A) (preferably urea (solid at normal temperature)) and aluminum sulfate hydrate (solid at normal temperature). I found out.

  The content ratio of the nitrogen-containing ketone compound (A) (preferably urea) in the liquid containing the nitrogen-containing ketone compound (A) (preferably urea) and the divalent and / or trivalent water-soluble polyvalent metal salt is 10 to 80% by mass, preferably 20 to 70% by mass, and more preferably 30 to 60% by mass.

  Inclusion of divalent and / or trivalent water-soluble polyvalent metal salt in liquid containing nitrogen-containing ketone compound (A) (preferably urea) and divalent and / or trivalent water-soluble polyvalent metal salt The ratio is preferably 10 to 80% by mass, more preferably 20 to 70% by mass, and further preferably 30 to 60% by mass.

  When the liquid is highly viscous, a solvent or the like may be used. As the solvent, organic solvents, alcohols, water and the like can be preferably used, but water is particularly preferable. The usage-amount of a solvent is the ratio in a liquid substance, Preferably it is 0-80 mass%, More preferably, it is 10-60 mass%, More preferably, it is 20-40 mass%.

  The amount of the liquid containing the nitrogen-containing ketone compound (A) (preferably urea) and the divalent and / or trivalent water-soluble polyvalent metal salt is nitrogen-containing ketone with respect to 100 parts by mass of the water-absorbent resin particles. The amount of the liquid substance containing the compound (A) (preferably urea) and the divalent and / or trivalent water-soluble polyvalent metal salt is preferably 0.01 to 100 parts by mass, It is more preferable that it is a mass part, and it is still more preferable that it is 1.0-10 mass parts.

  The addition / mixing method is the same as the manufacturing method 1 described above.

(Manufacturing method 3)
The third production method (production method 3) of the water-absorbent resin composition according to the present invention comprises water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a nitrogen-containing ketone compound. An aqueous solution containing (A) and an aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt are added.

  Use amount of nitrogen-containing ketone compound (A) and divalent and / or trivalent water-soluble polyvalent metal salt, use amount of nitrogen-containing ketone compound (A) and divalent and / or trivalent water-soluble polyvalent metal The ratio to the amount of salt used is the same as in Production Method 1 described above.

  The concentration of the nitrogen-containing ketone compound (A) in the aqueous solution containing the nitrogen-containing ketone compound (A) is preferably 50% or more with respect to the saturated concentration in order to prevent penetration and diffusion into the water-absorbent resin particles. Preferably it is 60% or more, more preferably 70% or more, further preferably 80% or more, and particularly preferably 90% or more. Of course, it may be used at a saturated concentration.

  The concentration of the divalent and / or trivalent water-soluble polyvalent metal salt in the aqueous solution containing the divalent and / or trivalent water-soluble polyvalent metal salt is to prevent penetration and diffusion into the water-absorbent resin particles. The saturated concentration is preferably 50% or more, more preferably 60% or more, still more preferably 70% or more, still more preferably 80% or more, and particularly preferably 90% or more. Of course, it may be used at a saturated concentration.

  The aqueous solution containing the nitrogen-containing ketone compound (A) may contain an aqueous liquid such as a polyhydric alcohol (preferably exemplified above).

  The aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt may contain, for example, an aqueous liquid such as a polyhydric alcohol (preferably those exemplified above). An aqueous liquid such as the polyhydric alcohol (preferably exemplified above) may act as a mixing aid or a surface cross-linking agent.

  The amount of the aqueous solution containing the nitrogen-containing ketone compound (A) is such that the amount of the aqueous solution containing the nitrogen-containing ketone compound (A) is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbing resin particles. Is preferably 0.1 to 50 parts by mass, and more preferably 1.0 to 10 parts by mass.

  The amount of the aqueous solution containing the divalent and / or trivalent water-soluble polyvalent metal salt is an aqueous solution containing the divalent and / or trivalent water-soluble polyvalent metal salt with respect to 100 parts by mass of the water-absorbent resin particles. Is preferably 0.01 to 100 parts by mass, more preferably 0.1 to 50 parts by mass, and still more preferably 1.0 to 10 parts by mass.

  The order of addition of the aqueous solution containing the nitrogen-containing ketone compound (A) and the aqueous solution containing the divalent and / or trivalent water-soluble polyvalent metal salt is not particularly limited, and may be simultaneous, or start adding one of them first May be. Preferably, after adding an aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt, an aqueous solution containing a nitrogen-containing ketone compound (A) is added. In this case, the surface treatment (preferably surface crosslinking treatment) of the water-absorbent resin particles is more preferably performed by adding an aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt. The surface treatment (preferably surface crosslinking treatment) is preferably performed at a temperature of 150 to 250 ° C.

  The addition / mixing method is the same as the manufacturing method 1 described above.

(Manufacturing method 4)
A fourth production method (production method 4) of the water-absorbent resin composition according to the present invention comprises water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, and a nitrogen-containing ketone compound. Either (A) or a divalent and / or trivalent water-soluble polyvalent metal salt is mixed as an aqueous solution, and the other is dry blended.

  Use amount of nitrogen-containing ketone compound (A) and divalent and / or trivalent water-soluble polyvalent metal salt, use amount of nitrogen-containing ketone compound (A) and divalent and / or trivalent water-soluble polyvalent metal The ratio to the amount of salt used is the same as in Production Method 1 described above.

  The concentration of the nitrogen-containing ketone compound (A) in the aqueous solution containing the nitrogen-containing ketone compound (A) is preferably 50% or more with respect to the saturated concentration in order to prevent penetration and diffusion into the water-absorbent resin particles. Preferably it is 60% or more, more preferably 70% or more, further preferably 80% or more, and particularly preferably 90% or more. Of course, it may be used at a saturated concentration.

  The concentration of the divalent and / or trivalent water-soluble polyvalent metal salt in the aqueous solution containing the divalent and / or trivalent water-soluble polyvalent metal salt is to prevent penetration and diffusion into the water-absorbent resin particles. The saturated concentration is preferably 50% or more, more preferably 60% or more, still more preferably 70% or more, still more preferably 80% or more, and particularly preferably 90% or more. Of course, it may be used at a saturated concentration.

  When using the aqueous solution containing the nitrogen-containing ketone compound (A), the aqueous solution containing the nitrogen-containing ketone compound (A) includes, for example, an aqueous liquid such as a polyhydric alcohol (preferably those exemplified above). May be.

  When an aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt is used, the aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt includes, for example, a polyhydric alcohol (preferably An aqueous liquid such as those exemplified above may be included.

  When mixing the water-absorbent resin particles, the nitrogen-containing ketone compound (A) and any one of the divalent and / or trivalent water-soluble polyvalent metal salts as an aqueous solution, And dry blending may be performed simultaneously, or one of them may be added first.

  The addition / mixing method is the same as the manufacturing method 1 described above.

[Water absorber]
The water-absorbent resin composition in the present invention can be made into a water-absorbing body suitable as an absorbent layer for sanitary materials, for example, by combining with an appropriate material. Hereinafter, a water absorption body is demonstrated.

  A water absorbent is a molded composition composed of a water absorbent resin composition and other materials used for sanitary materials such as disposable diapers, sanitary napkins, incontinence pads, and medical pads that absorb blood, body fluids, urine, etc. An example of a material used is a cellulose fiber. Specific examples of cellulose fibers include wood pulp fibers such as mechanical pulp, chemical pulp, semi-chemical pulp, and dissolved pulp from wood, and artificial cellulose fibers such as rayon and acetate. A preferred cellulose fiber is wood pulp fiber. These cellulose fibers may partially contain synthetic fibers such as nylon and polyester. When the water absorbent resin composition in the present invention is used as a part of the water absorbent, the mass of the water absorbent resin composition in the present invention contained in the water absorbent is preferably 20% by mass or more, more preferably 30%. It is in the range of not less than mass%, more preferably not less than 40 mass%. If the mass of the water absorbent resin composition in the present invention contained in the water absorbent is less than 20% by mass, sufficient effects may not be obtained.

  In order to obtain a water absorbent from the water absorbent resin composition and cellulose fiber in the present invention, for example, a method of spraying the water absorbent resin composition on paper or mat made of cellulose fiber, and sandwiching between them, if necessary, cellulose fiber and water absorbent Well-known means for obtaining a water-absorbing body, such as a method of uniformly blending the functional resin composition, can be appropriately selected. Preferably, the water-absorbing resin composition and the cellulose fiber are mixed in a dry manner and then compressed. By this method, it is possible to remarkably suppress the dropping of the water absorbent resin composition from the cellulose fiber. The compression is preferably performed under heating, and the temperature range is, for example, 50 to 200 ° C. Moreover, in order to obtain a water absorption body, the method described in Japanese translations of PCT publication No. 9-509591 and Unexamined-Japanese-Patent No. 9-290000 is also used preferably.

  The water-absorbent resin composition in the present invention is excellent in various physical properties when used in a water-absorbing body, so that the liquid can be taken up quickly, and the remaining amount of liquid on the surface of the water-absorbing body is small. can get.

  Since the water-absorbent resin composition in the present invention has excellent water absorption properties, it can be used as a water-absorbing water retention agent for various applications. For example, water absorbent water absorbents for absorbent articles such as disposable diapers, sanitary napkins, incontinence pads, and medical pads; moss substitutes, soil modification improvers, water retention agents, water retention agents for agricultural and horticultural use such as agrochemical potency retention agents; interior walls Anti-condensation agent for materials, water retention agent for construction such as cement additive; release control agent, cold insulation agent, disposable body warmer, sludge coagulant, food freshness preservation agent, ion exchange column material, sludge or oil dehydrating agent, desiccant Can be used as a humidity control material. In addition, the water-absorbent resin composition in the present invention is particularly preferably used for sanitary materials for absorbing feces, urine or blood, such as paper diapers and sanitary napkins.

  When the absorbent body is used for sanitary materials such as disposable diapers, sanitary napkins, incontinence pads, medical pads, etc., (a) a liquid permeable top sheet placed adjacent to the wearer's body, (b) worn A liquid impervious backsheet disposed far from the wearer's body and adjacent to the wearer's clothing, and (c) a water absorbent disposed between the topsheet and the backsheet It is preferable to be used in a configuration consisting of Two or more water absorbent bodies may be used, or a water absorbent body may be used together with a pulp layer.

  Hereinafter, the present invention will be described more specifically by way of examples. However, the present invention is not limited to these examples. Hereinafter, for convenience, “mass part” may be simply referred to as “part”, and “liter” may be simply referred to as “L”. In addition, “mass%” may be described as “wt%”.

  Various performances of the water absorbent resin particles or the water absorbent resin composition were measured by the following methods. Unless otherwise specified, the following measurements are performed under conditions of room temperature (20 to 25 ° C.) and humidity of 50 RH%.

  In the case of a water absorbent resin composition used as a final product such as sanitary materials, the water absorbent resin composition absorbs moisture. Therefore, the water absorbent resin composition is appropriately separated from the final product and dried under reduced pressure at low temperature. The measurement may be performed later (for example, 1 mmHg or less, 12 hours at 60 ° C.). Moreover, the water content of the water-absorbent resin compositions used in the examples and comparative examples of the present invention was all 6% by mass or less.

<Centrifuge retention capacity (CRC)>
The centrifuge retention capacity (CRC) shows an absorption capacity of 30 minutes under no pressure with respect to 0.90 mass% saline. CRC is sometimes referred to as absorption capacity without pressure.

  Put 0.200 g of water-absorbent resin particles or water-absorbent resin composition uniformly into a bag (85 mm x 60 mm) made of nonwoven fabric (Nangoku Pulp Industries Co., Ltd., trade name: Heaton paper, model: GSP-22). After heat sealing, it was immersed in a large excess (usually about 500 ml) of 0.90% by mass saline (aqueous sodium chloride solution) at room temperature. After 30 minutes, the bag was pulled up and drained for 3 minutes with a centrifugal force (250 G) described in edana ABSORBENCY II 441.1-99 using a centrifuge (manufactured by Kokusan Co., Ltd., centrifuge: model H-122). After that, the mass W1 (g) of the bag was measured. Further, the same operation was performed without using the water absorbent resin particles or the water absorbent resin composition, and the mass W0 (g) at that time was measured. The centrifuge retention capacity (CRC) (g / g) was calculated from these W1 and W0 according to the following formula.

Centrifuge retention capacity (CRC) (g / g)
= (W1 (g) -W0 (g)) / (mass of water absorbent resin particles or water absorbent resin composition (g))-1
<Absorptive power against pressure (AAP)>
Absorptive power against pressure (AAP) is 4.83 kPa with respect to 0.90% by mass saline solution, indicating an absorption capacity of 60 minutes. AAP is sometimes referred to as absorption capacity under pressure at 4.83 kPa.

  Using the apparatus shown in FIG. 1, a stainless steel 400 mesh wire mesh 101 (mesh size 38 μm) is fused to the bottom of a plastic support cylinder 100 having an inner diameter of 60 mm, and room temperature (20 to 25 ° C.), humidity 50 RH%. Under these conditions, 0.900 g of water-absorbing resin particles or water-absorbing resin composition is uniformly dispersed on the net, and 4.83 kPa (0 The piston 103 and the load 104, which have been adjusted so that a load of .7 psi) can be applied uniformly, have an outer diameter slightly smaller than 60 mm and do not cause a gap with the support cylinder and do not hinder vertical movement. It mounted in order and measured mass Wa (g) of this measuring device set.

  A glass filter 106 having a diameter of 90 mm (manufactured by Mutual Riken Glass Co., Ltd., pore diameter: 100 to 120 μm) is placed inside a petri dish 105 having a diameter of 150 mm, and 0.90 mass% saline 108 (20 to 25 ° C.). Was added to the same level as the upper surface of the glass filter. On top of that, a sheet of filter paper 107 having a diameter of 90 mm (ADVANTEC Toyo Co., Ltd., product name: (JIS P 3801, No. 2), thickness 0.26 mm, reserved particle diameter 5 μm) was placed so that the entire surface was wetted. Excess liquid was removed.

  The set of measuring devices was placed on the wet filter paper, and the liquid was absorbed under load. After 1 hour, the measuring device set was lifted and its mass Wb (g) was measured. And the absorptive power (AAP) (g / g) with respect to pressure was computed from Wa and Wb according to the following formula.

Absorptive power against pressure (AAP)
= (Wb (g) -Wa (g)) / (mass of water absorbent resin particles or water absorbent resin composition (0.900 g))
<Saline flow conductivity (SFC)>
The saline flow conductivity (SFC) is a value indicating the liquid permeability during swelling of the water absorbent resin particles or the water absorbent resin composition. It shows that it has high liquid permeability, so that the value of SFC is large.

  This was performed according to the saline flow conductivity (SFC) test described in JP-T 9-509591.

  Using the apparatus shown in FIG. 2, the water-absorbent resin particles or the water-absorbent resin composition (0.900 g) uniformly placed in the container 40 is pressurized in an artificial urine (1) at 0.3 psi (2.07 kPa). Swell for 60 minutes, record the height of the gel layer of gel 44, then swell 0.69 wt% saline 33 from tank 31 with constant hydrostatic pressure under pressure of 0.3 psi (2.07 kPa). The gel layer was passed through. The SFC test was performed at room temperature (20-25 ° C.). Using a computer and a balance, the amount of liquid passing through the gel layer at 20 second intervals as a function of time was recorded for 10 minutes. The flow rate Fs (T) passing through the swollen gel 44 (mainly between the particles) was determined in units of g / s by dividing the increased mass (g) by the increased time (s). Let Ts be the time at which a constant hydrostatic pressure and a stable flow rate were obtained, use only the data obtained between Ts and 10 minutes for the flow rate calculation, and use the flow rate obtained between Ts and 10 minutes. The value of Fs (T = 0), ie the initial flow rate through the gel layer, was calculated. Fs (T = 0) was calculated by extrapolating the result of the least squares method of Fs (T) versus time to T = 0.

Saline flow conductivity (SFC)
= (Fs (t = 0) × L0) / (ρ × A × ΔP)
= (Fs (t = 0) × L0) / 139506
here,
Fs (t = 0): flow rate expressed in g / s L0: height of gel layer expressed in cm ρ: density of NaCl solution (1.003 g / cm ³ )
A: Area above the gel layer in the cell 41 (28.27 cm ² )
ΔP: hydrostatic pressure applied to the gel layer (4920 dyne / cm ² )
The unit of the SFC value is (10 ⁻⁷ · cm ³ · s · g ⁻¹ ).

  In the apparatus shown in FIG. 2, a glass tube 32 is inserted into the tank 31, and the lower end of the glass tube 32 is 5 cm from the bottom of the swollen gel 44 in the cell 41 with 0.69 mass% saline 33. It was arranged so that it could be maintained at the upper height. The 0.69 mass% saline solution 33 in the tank 31 was supplied to the cell 41 through the L-shaped tube 34 with a cock. Under the cell 41, a container 48 for collecting the passed liquid is disposed, and the collection container 48 is installed on an upper pan balance 49. The inner diameter of the cell 41 is 6 cm. A 400 stainless steel wire mesh (aperture 38 μm) 42 was installed. The bottom of the piston 46 has a hole 47 sufficient for the liquid to pass through, and the bottom has a glass with good permeability so that the water-absorbing resin particles or the water-absorbing resin composition or its swelling gel does not enter the hole 47. A filter 45 was attached. The cell 41 was placed on a table on which the cell was placed, and the surface of the table in contact with the cell was placed on a stainless steel wire mesh 43 that did not prevent liquid permeation.

  Artificial urine (1) is calcium chloride dihydrate 0.25 g, potassium chloride 2.0 g, magnesium chloride hexahydrate 0.50 g, sodium sulfate 2.0 g, ammonium dihydrogen phosphate 0.85 g, What added 0.15 g of hydrogen ammonium diphosphate and 994.25 g of pure waters was used.

<Mass average particle diameter (D50) and logarithmic standard deviation of particle size distribution (σζ)>
The water-absorbent resin particles or the water-absorbent resin composition were sieved with JIS standard sieves having openings of 850 μm, 710 μm, 600 μm, 500 μm, 425 μm, 300 μm, 212 μm, 150 μm, 45 μm, etc., and the residual percentage R was plotted on logarithmic probability paper. . Thereby, the particle diameter corresponding to R = 50 mass% was read as the mass average particle diameter (D50). Further, the logarithmic standard deviation (σζ) of the particle size distribution is expressed by the following equation, and the smaller the value of σζ, the narrower the particle size distribution.

σζ = 0.5 × ln (X2 / X1)
(X1 is R = 84.1%, X2 is each particle size when R = 15.9%)
The classification method for measuring the mass average particle diameter (D50) and the logarithmic standard deviation (σζ) of the particle size distribution is as follows: 10.0 g of water-absorbent resin particles or water-absorbent resin composition, room temperature (20 to 25 ° C.), humidity Under a condition of 50 RH%, a JIS standard sieve (THE IIDA TESTING SIEVE: diameter 8 cm) having an aperture of 850 μm, 710 μm, 600 μm, 500 μm, 425 μm, 300 μm, 212 μm, 150 μm, 45 μm was charged, and a vibration classifier (IIDA SIEVE SHAK, (TYPE: ES-65 type, SER No. 0501), classification was performed for 5 minutes.

<Blocking rate (BR)>
It shows the blocking rate (Blocking Ratio) at the time of 25 degreeC, relative humidity 70%, and 1 hour passage.

  A constant temperature and humidity chamber (2,000 g of water absorbent resin particles or water absorbent resin composition) was uniformly sprayed on the bottom of a polypropylene cup having an inner diameter of 50 mm and a height of 10 mm and adjusted to 25 ° C. and a relative humidity of 70% in advance ( The product was quickly put into PLATIIOUS LUCIFER PL-2G manufactured by Tabay Espec and left for 60 minutes. Thereafter, the moisture-absorbing water-absorbing resin particles or the water-absorbing resin composition was transferred to a JIS standard sieve having a diameter of 7.5 cm and an opening of 2000 μm, and a vibration classifier (IIDA SIEVE SHAKER, TYPE: ES-65 type, SER. No. 0501). ) To measure the mass W4 (g) of the water absorbent resin particles or the water absorbent resin composition remaining on the sieve and the mass W5 (g) of the water absorbent resin particles or the water absorbent resin composition that passed through the sieve. did.

Blocking ratio (BR) (%) = mass W4 (g) / (mass W4 (g) + mass W5 (g)) × 100
Was used to calculate the blocking rate (%). The lower the moisture absorption blocking rate, the better the fluidity during moisture absorption.

<Amount of water-soluble component (water-soluble component)>
Weigh out 184.3 g of 0.90 mass% saline solution in a 250 ml lidded plastic container, add 1.00 g of water-absorbent resin particles or water-absorbent resin composition to the aqueous solution, and stir for 16 hours by rotating the stirrer. As a result, the soluble component in the resin was extracted. Filtration of this extract using one sheet of filter paper (ADVANTEC Toyo Co., Ltd., product name: (JIS P 3801, No. 2), thickness 0.26 mm, retained particle diameter 5 μm) gave 50. 0 g was measured and used as a measurement solution.

  First, only 0.90% by mass saline is titrated with 0.1N NaOH aqueous solution to pH 10, and then titrated with 0.1N HCl aqueous solution to pH 2.7 to perform empty titration ([bNaOH] ml). [BHCl] ml).

  The titration ([NaOH] ml, [HCl] ml) was determined by performing the same titration operation on the measurement solution.

  For example, in the case of a water-absorbing resin particle or water-absorbing resin composition comprising a known amount of acrylic acid and its sodium salt, the water-absorbing resin particle or the water-absorbing resin is based on the average molecular weight of the monomer and the titration amount obtained by the above operation. The soluble content in the conductive resin composition can be calculated by the following formula. In the case of an unknown amount, the average molecular weight of the monomer is calculated using the neutralization rate obtained by titration.

Soluble content (mass%) = 0.1 × (average molecular weight) × 184.3 × 100 × ([HCl] − [bHCl]) / 1000 / 1.0 / 50.0
Neutralization rate (mol%) = (1 − ([NaOH] − [bNaOH]) / ([HCl] − [bHCl])) × 100
<Dust amount>
A water absorbent resin or a water absorbent resin composition was placed in a PE bag (No. 13, 0.03 × 260 × 380 mm) previously coated with an antistatic agent. After the bag was shaken 30 times, the bag was opened and measured with a DIGITAL DUST INDICATOR P-5L (manufactured by SHIBATA) for 1 minute. This measurement was performed 10 times, and the average value was obtained. The unit of dust amount is mg / m ³ .

<Paint shaker test>
The paint shaker test (PS) is a paint shaker (Toyo Seiki Seisakusho Co., Ltd.) in which a glass container having a diameter of 6 cm and a height of 11 cm is charged with 10 g of glass beads having a diameter of 6 mm and water absorbent resin particles or a water absorbent resin composition. No. 488) and shake at 800 cycle / min (CPM), and details of the apparatus are disclosed in Japanese Patent Laid-Open No. 9-235378.

  Paint shaker test 1 is the shake time of 30 minutes and paint shake test 2 is the test shake time of 10 minutes.

  After permeation, the glass beads are removed with a JIS standard sieve having an opening of 2 mm to obtain damaged water absorbent resin particles or a water absorbent resin composition.

<Liquid diffusion rate (LDV)>
The liquid diffusion rate (LDV) was measured using a suction index measuring device described in JP-A-5-200068 (EP532002). The trough sheet was made of SUS304 with a stainless steel grade 2B finish.

  In the trough groove of the trough sheet installed at an angle of 20 °, 1.00 g ± 0.005 g of the water-absorbent resin composition was evenly spread between 0 to 20 cm. Furthermore, the water-absorbent resin composition was more evenly dispersed using a spatula.

  The liquid used for liquid suction was a liquid colored at a ratio of 0.01 g of edible blue No. 1 (Tokyo Kasei Kogyo Co., Ltd.) to 1 L of 0.9% by weight saline solution (sodium chloride aqueous solution).

  The liquid suction time (WT) is adjusted so that the liquid level of the liquid storage tank is 0.5 cm above the lowest position of the trough, and then the stainless steel screen mesh (400 mesh) comes into contact with the liquid. Measurement started. The liquid sucking time (WT) represents the time (sec) when the liquid is sucked up to the 10 cm scale position. In addition, the speed at which the liquid in the liquid storage tank and the stainless steel screen mesh are immersed from the lowest position of the trough to 0.5 cm above is 1.35 to 1.40 mm / s in the vertical direction from the liquid surface. It was.

  The liquid diffusion rate (LDV) is calculated by the following equation.

LDV (mm / s) = 100 (mm) / WT (s)
(Production Example 1)
In a reactor formed by covering a 10-liter jacketed stainless steel double-armed kneader with two sigma-shaped blades with a lid, 505.6 g of acrylic acid, 4430.8 g of 37 mass% sodium acrylate aqueous solution, pure 497.0 g of water and 12.79 g of polyethylene glycol diacrylate (molecular weight 523) were dissolved to prepare a reaction solution. Next, this reaction solution was degassed for 20 minutes in a nitrogen gas atmosphere. Subsequently, 29.34 g of a 10% by mass aqueous sodium persulfate solution and 24.45 g of a 0.1% by mass L-ascorbic acid aqueous solution were added to the reaction solution with stirring, and polymerization started about 1 minute later. Then, polymerization was performed at 20 to 95 ° C. while pulverizing the generated gel, and a hydrogel crosslinked polymer was taken out 30 minutes after the polymerization started. The obtained hydrogel crosslinked polymer was subdivided to have a diameter of about 5 mm or less.

  This finely divided hydrogel cross-linked polymer is spread on a 50-mesh wire mesh, dried with hot air at 180 ° C. for 50 minutes, and the dried product is pulverized using a roll mill, and further, a JIS having an opening of 600 μm and an opening of 150 μm. By classifying with a standard sieve, amorphous crushed water-absorbent resin particles (1) having a mass average particle diameter of 350 μm were obtained. The centrifuge retention capacity (CRC) of the water absorbent resin particles (1) was 33.0 g / g, and the water-soluble content was 9.0% by mass.

  A surface treatment agent comprising a mixed liquid of 0.4 parts by mass of 1,4-butanediol, 0.6 parts by mass of propylene glycol and 3.0 parts by mass of pure water to 100 parts by mass of the obtained water absorbent resin particles (1). After mixing uniformly, the mixture was heat-treated at 200 ° C. for 30 minutes. Further, the particles were pulverized until passing through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 1 was performed on the particles. Thus, water-absorbing resin particles (A) having a crosslinked surface were obtained.

Example 1
An aqueous solution (A) comprising 1 part by mass of aluminum sulfate 14-18 hydrate, 1.5 parts by mass of urea and 1 part by mass of pure water was added to 100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1. It added uniformly and was dried at 60 degreeC for 1 hour. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 2 was performed on this composition. Thus, a water absorbent resin composition (1d) was obtained.

(Example 2)
The same operation as in Example 1 was performed except that the amount of urea in the aqueous solution (A) in Example 1 was changed to 1.0 part by mass to obtain a water absorbent resin composition (2d).

(Example 3)
A water-absorbent resin composition (3d) was obtained in the same manner as in Example 1 except that the amount of urea in the aqueous solution (A) in Example 1 was changed to 2.0 parts by mass.

Example 4
Example 1 except that the composition of the aqueous solution (A) in Example 1 was changed to an aqueous solution consisting of 1 part by mass of aluminum sulfate 14-18 hydrate, 1 part by mass of urea, and 0.22 part by mass of pure water. The same operation was performed to obtain a water absorbent resin composition (4d).

(Example 5)
1 part by mass of aluminum sulfate 14-18 hydrate and 1 part by mass of urea were mixed. After 24 hours, the mixture was liquid. The same operation as in Example 1 was performed except that the aqueous solution (A) in Example 1 was changed to 2 parts by mass of this liquid to obtain a water absorbent resin composition (5d).

(Example 6)
The same composition as in Example 1 except that the composition of the aqueous solution (A) in Example 1 was changed to an aqueous solution consisting of 11 parts by mass of aluminum sulfate 14-18 hydrate, 11 parts by mass of urea, and 11 parts by mass of pure water. Operation was performed to obtain a water absorbent resin composition (6d).

(Example 7)
The composition of the aqueous solution (A) in Example 1 was changed to an aqueous solution consisting of 1 part by weight of aluminum sulfate 14-18 hydrate, 1 part by weight of urea, 1 part by weight of pure water, and 0.05 part by weight of propylene glycol. Except for this, the same operation as in Example 1 was performed to obtain a water absorbent resin composition (7d).

(Example 8)
The composition of the aqueous solution (A) in Example 1 was changed to an aqueous solution consisting of 1 part by weight of aluminum sulfate 14-18 hydrate, 1 part by weight of urea, 0.25 part by weight of pure water, and 0.25 part by weight of propylene glycol. Except having changed, operation similar to Example 1 was performed and the water absorbing resin composition (8d) was obtained.

Example 9
An aqueous solution (A) comprising 1 part by mass of aluminum sulfate 14-18 hydrate, 1.5 parts by mass of urea and 1 part by mass of pure water was added to 100 parts by mass of the water-absorbent resin particles (1) obtained in Production Example 1. It added uniformly and was dried at 60 degreeC for 1 hour. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 2 was performed on this composition. Thus, a water absorbent resin composition (9d) was obtained.

(Example 10)
100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1 are heated to 150 ° C., and 1 part by mass of aluminum sulfate 14-18 hydrate (having a particle diameter of 600 μm or less) and urea (particle diameter) 0.5 parts by mass) was uniformly added and fused. The mixture was further heated at 100 ° C. for 30 minutes, and the resulting composition was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Thus, a water absorbent resin composition (10) was obtained. Next, the paint shaker test 2 was performed on the water absorbent resin composition (10). Thus, a water absorbent resin composition (10d) was obtained.

(Example 11)
The same operation as in Example 10 was performed except that the amount of urea in Example 10 was changed to 1.0 part by mass. Thus, a water absorbent resin composition (11) and a water absorbent resin composition (11d) were obtained.

(Example 12)
The same operation as in Example 10 was performed except that the amount of urea in Example 10 was changed to 1.5 parts by mass. Thus, a water absorbent resin composition (12) and a water absorbent resin composition (12d) were obtained.

(Example 13)
100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1, 1 part by mass of aluminum sulfate 14-18 hydrate (having a particle diameter of 600 μm or less), urea (having a particle diameter of 600 μm or less) 1 Mass parts were mixed. The mixture was fused by heating to 140 ° C. and stirring for 5 minutes. The obtained composition was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Thus, a water absorbent resin composition (13) was obtained.

(Example 14)
The same operation as in Example 13 was performed except that the amount of aluminum sulfate 14-18 hydrate of Example 13 was changed to 11 parts by mass and the amount of urea was changed to 11 parts by mass. Thus, a water absorbent resin composition (14) was obtained.

(Example 15)
The same operation as in Example 13 was performed except that the amount of urea in Example 13 was changed to 11 parts by mass. Thus, a water absorbent resin composition (15) was obtained.

(Example 16)
The same operation as in Example 13 was performed except that the amount of aluminum sulfate 14-18 hydrate of Example 13 was changed to 11 parts by mass. Thus, a water absorbent resin composition (16) was obtained.

(Example 17)
The same operation as in Example 13 was performed except that the water absorbent resin particles (A) of Example 13 were changed to water absorbent resin particles (1). Thus, a water absorbent resin composition (17) was obtained.

(Example 18)
The same procedure as in Example 1 was performed except that the aluminum sulfate 14-18 hydrate of the aqueous solution (A) in Example 1 was changed to iron (III) chloride hexahydrate, and a water absorbent resin composition ( 18d) was obtained.

(Example 19)
To 100 parts by mass of the water-absorbent resin particles (1) obtained in Production Example 1, 0.3 part by mass of 1,4-butanediol, 0.5 part by mass of propylene glycol, 2.7 parts by mass of pure water, and aluminum sulfate 14 After uniformly mixing a surface treating agent consisting of a mixed solution of 1.0 part by weight of -18 hydrate, the mixture was heated at 200 ° C. for 30 minutes. After the heat treatment, the composition was cooled to 60 ° C., and 2 parts by mass of 50 mass% urea aqueous solution was uniformly mixed. This was dried at 60 ° C. for 1 hour. This dried product was pulverized until it passed through a JIS standard sieve having an opening of 600 μm. Thus, a water absorbent resin composition (19) was obtained.

(Example 20)
To 100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1, 1 part by mass of aluminum sulfate 14-18 hydrate (having a particle diameter of 600 μm or less) is dry-mixed, and 50 parts by mass is added to this composition. 2 parts by mass of an aqueous urea solution was uniformly mixed. This was dried at 60 ° C. for 1 hour. This dried product was pulverized until it passed through a JIS standard sieve having an opening of 600 μm. Thus, a water absorbent resin composition (20) was obtained.

(Example 21)
100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1 are dry-mixed with 1 part by mass of urea (particle size of 600 μm or less), and this composition is mixed with aluminum sulfate 14-18 hydrate. An aqueous solution consisting of 1 part by mass and 1 part by mass of pure water was uniformly mixed. This was dried at 60 ° C. for 1 hour. This dried product was pulverized until it passed through a JIS standard sieve having an opening of 600 μm. Thus, a water absorbent resin composition (21) was obtained.

(Example 22)
To 100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1, an aqueous solution consisting of 1 part by mass of aluminum sulfate 14-18 hydrate and 1 part by mass of pure water and 2 parts by mass of 50% by mass urea aqueous solution Mixed. This was dried at 60 ° C. for 1 hour. This dried product was pulverized until it passed through a JIS standard sieve having an opening of 600 μm. Thus, a water absorbent resin composition (22) was obtained.

(Production Example 2)
185.4 g acrylic acid, 0.942 g polyethylene glycol diacrylate (molecular weight 523) (0.07 mol%: acrylic acid) in a polypropylene container with an inner diameter of 80 mm and a capacity of 1 liter covered with polystyrene foam as a heat insulating material , And a solution (A) obtained by mixing 1.13 g of 1.0 mass% diethylenetriaminepentaacetic acid-5 sodium aqueous solution, 148.53 g of 48.5 mass% sodium hydroxide aqueous solution, and ion-exchanged water 159 adjusted to 50 ° C. The solution (B) in which 0.71 g was mixed was quickly added to (A) in an open system and mixed with stirring with a magnetic stirrer. A monomer aqueous solution having a liquid temperature increased to about 100 ° C. by heat of neutralization and heat of dissolution was obtained.

  After adding 4.29 g of 3 mass% sodium persulfate aqueous solution to the obtained monomer aqueous solution and stirring for several seconds, the surface temperature was adjusted to 100 ° C. with a hot plate (NEO HOTPLATE H1-1000, manufactured by Inoue Seieido Co., Ltd.). Was poured in an open system into a 250 × 250 mm bottom stainless steel bat-shaped container with Teflon (registered trademark) attached to the inner surface. The stainless bat-shaped container had a bottom surface of 250 × 250 mm, a top surface of 640 × 640 mm, a height of 50 mm, a central cross section of a trapezoid, and an open top surface.

  Polymerization started soon after the aqueous monomer solution was poured into the vat. Polymerization proceeded while generating water vapor and expanding and foaming vertically and horizontally, and then contracted to a size slightly larger than the bottom surface. This expansion and contraction was completed within about 1 minute, and after holding in the polymerization vessel for 4 minutes, the water-containing polymer was taken out.

  The obtained water-containing polymer was pulverized by a meat chopper (ROYAL MEAT CHOPPER VR400K, manufactured by Iizuka Kogyo Co., Ltd.) having a die diameter of 9.5 mm to obtain a finely divided water-containing polymer.

  This finely divided hydrogel cross-linked polymer is spread on a 50 mesh wire net, dried with hot air at 180 ° C. for 50 minutes, and the dried product is pulverized using a roll mill. By classifying with a standard sieve, amorphous crushed water-absorbent resin particles (2) having a mass average particle diameter of 450 μm were obtained. The centrifuge retention capacity (CRC) of the water absorbent resin particles (2) was 36.0 g / g, and the water-soluble content was 12.0% by mass.

  A surface treatment agent comprising a mixed solution of 0.4 parts by mass of 1,4-butanediol, 0.6 parts by mass of propylene glycol and 3.0 parts by mass of pure water to 100 parts by mass of the obtained water absorbent resin particles (2). After mixing uniformly, the mixture was heat treated at 200 ° C. for 40 minutes. Further, the particles were pulverized until passing through a JIS standard sieve having an opening of 850 μm. Next, the paint shaker test 1 was performed on the particles. Thus, water-absorbing resin particles (B) whose surfaces were cross-linked were obtained.

  Moreover, the surface treatment which consists of a liquid mixture of 0.4 mass part of 1, 4- butanediol, 0.6 mass part of propylene glycol, and 3.0 mass part of pure waters to 100 mass parts of obtained water absorbent resin particles (2). After the agent was uniformly mixed, the mixture was heat-treated at 200 ° C. for 30 minutes. Further, the particles were pulverized until passing through a JIS standard sieve having an opening of 850 μm. Next, the paint shaker test 1 was performed on the particles. Thus, water-absorbing resin particles (C) having a cross-linked surface were obtained.

(Example 23)
An aqueous solution (A) composed of 1 part by mass of aluminum sulfate 14-18 hydrate, 1.5 parts by mass of urea and 1 part by mass of pure water was added to 100 parts by mass of the water-absorbent resin particles (B) obtained in Production Example 2. It added uniformly and was dried at 60 degreeC for 1 hour. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 2 was performed on this composition. Thus, a water absorbent resin composition (23d) was obtained.

(Example 24)
An aqueous solution (A) comprising 1 part by mass of aluminum sulfate 14-18 hydrate, 1.5 parts by mass of urea and 1 part by mass of pure water was added to 100 parts by mass of the water-absorbent resin particles (C) obtained in Production Example 2. It added uniformly and was dried at 60 degreeC for 1 hour. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 2 was performed on this composition. Thus, a water absorbent resin composition (24d) was obtained.

(Example 25)
100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1 are composed of 1 part by mass of aluminum sulfate 14-18 hydrate, 0.2 part by mass of N, N-dimethylacetamide, and 1 part by mass of pure water. An aqueous solution (a precipitate appeared and became cloudy after several hours) was added uniformly and dried at 60 ° C. for 1 hour. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 2 was performed on this composition. Thus, a water absorbent resin composition (25d) was obtained.

(Example 26)
An aqueous solution comprising 1 part by mass of aluminum sulfate 14-18 hydrate, 0.2 part by mass of ethylene urea and 1 part by mass of pure water is uniformly applied to 100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1. Added and dried at 60 ° C. for 1 hour. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. Next, the paint shaker test 2 was performed on this composition. Thus, a water absorbent resin composition (26d) was obtained.

(Comparative Example 1)
The water absorbent resin particles (A) obtained in Production Example 1 were used as comparative water absorbent resin particles (1).

(Comparative Example 2)
The water absorbent resin particles (B) obtained in Production Example 2 were used as comparative water absorbent resin particles (2).

(Comparative Example 3)
The water absorbent resin particles (C) obtained in Production Example 2 were used as comparative water absorbent resin particles (3).

(Comparative Example 4)
An aqueous solution consisting of 1 part by mass of aluminum sulfate 14-18 hydrate and 1 part by mass of pure water is uniformly added to 100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1, and the mixture is heated at 60 ° C. for 1 hour. Dried. The obtained dried product was crushed until it passed through a JIS standard sieve having an opening of 600 μm. In this way, a comparative water absorbent resin composition (4) was obtained. Next, the paint shaker test 2 was performed on the comparative water absorbent resin composition (4). In this way, a comparative water absorbent resin composition (4d) was obtained.

(Comparative Example 5)
To 100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1, 1 part by mass of aluminum sulfate 14-18 hydrate (having a particle diameter of 600 μm or less) was uniformly dry-mixed. In this way, a comparative water absorbent resin composition (5) was obtained. Next, the paint shaker test 2 was performed on the comparative water absorbent resin composition (5). In this way, a comparative water absorbent resin composition (5d) was obtained.

(Comparative Example 6)
100 parts by mass of the water-absorbent resin particles (A) obtained in Production Example 1 are heated to 150 ° C., and 1.6 parts by mass of potassium aluminum sulfate dodecahydrate (having a particle diameter of 600 μm or less) are uniformly added thereto. And fused. The mixture was further heated at 100 ° C. for 30 minutes, and the resulting composition was crushed until it passed through a JIS standard sieve having an opening of 600 μm. In this way, a comparative water absorbent resin composition (6) was obtained. Next, the paint shaker test 2 was performed on the comparative water absorbent resin composition (6). In this way, a comparative water absorbent resin composition (6d) was obtained.

(Comparative Example 7)
7.5 g of dry potassium aluminum sulfate (baked potassium alum) powder was added to 30 g of a hot solution of potassium aluminum sulfate (potash alum) (content of aluminum component converted to aluminum oxide is 10.75 mass%). Thereafter, the mixture is stirred to obtain a uniformly dispersed white slurry liquid. Next, after adding 26.2 g of urea to the slurry liquid and dissolving it, 34.2 g of the water-absorbent resin particles (1) obtained in Production Example 1 are added, and the slurry liquid obtained by uniformly dispersing the slurry liquid. Was poured into a drying dish, and hot air drying was performed at a temperature around 60 ° C. while loosening at an appropriate time. After drying, it was pulverized to obtain 93 g of a white / odorless solid. In this way, a comparative water absorbent resin composition (7) was obtained.

(Comparative Example 8)
The same operation as Comparative Example 7 was performed except that the water absorbent resin particles (1) of Comparative Example 7 were changed to the water absorbent resin (A) obtained in Production Example 1. In this way, a comparative water absorbent resin composition (8) was obtained.

(Comparative Example 9)
To 100 parts by mass of the water-absorbent resin particles (1) obtained in Production Example 1, 0.3 part by mass of 1,4-butanediol, 0.5 part by mass of propylene glycol, 2.7 parts by mass of pure water, and aluminum sulfate 14 After uniformly mixing a surface treating agent consisting of a mixed solution of 1.0 part by weight of -18 hydrate, the mixture was heated at 200 ° C. for 30 minutes. After the heat treatment, the composition was pulverized until it passed through a JIS standard sieve having an opening of 600 μm. In this way, a comparative water absorbent resin composition (9) was obtained.

  The water-absorbent resin compositions, comparative water-absorbent resin particles, centrifuge retention capacity (CRC) of comparative water-absorbent resin compositions, absorbency against pressure (AAP), saline solution obtained in the above Examples and Comparative Examples The results of measuring the flow conductivity (SFC) are shown in Tables 1 and 2.

  Table 3 shows the results of measuring the dust amounts of the water absorbent resin compositions (1d) and (11d), the comparative water absorbent resin particles (1), and the comparative water absorbent resin compositions (4d), (5d) and (6d). Show.

  Table 4 shows the results of measuring the dust amount of the water absorbent resin composition (19) and the comparative water absorbent resin composition (9).

  Table 5 shows the results of measuring the blocking rate (BR) of the water absorbent resin compositions (1d), (8d), (11d) and the comparative water absorbent resin particles (1), (2), (3).

  Table 6 shows the mass average particle diameter (D50) and the logarithmic standard deviation (σζ) of the water absorbent resin particles (A) and (C), the water absorbent resin compositions (1d) and (24d).

  Table 7 shows the results of measuring the liquid diffusion rate (LDV) of the water absorbent resin composition (1d), the comparative water absorbent resin particles (1), and the comparative water absorbent resin composition (4d).

  Since the water-absorbent resin composition in the present invention has excellent water absorption characteristics and the like, it can be used as a water-absorbing water retaining agent for various applications. For example, water absorbent water absorbents for absorbent articles such as disposable diapers, sanitary napkins, incontinence pads, and medical pads; moss substitutes, soil modification improvers, water retention agents, water retention agents for agricultural and horticultural use such as agrochemical potency retention agents; interior walls Anti-condensation agent for materials, water retention agent for construction such as cement additive; release control agent, cold insulation agent, disposable body warmer, sludge coagulant, food freshness preservation agent, ion exchange column material, sludge or oil dehydrating agent, desiccant Can be used as a humidity control material. In addition, the water-absorbent resin composition in the present invention is particularly preferably used for sanitary materials for absorbing feces, urine or blood, such as paper diapers and sanitary napkins.

It is the schematic of the measuring apparatus of AAP. It is the schematic of the measuring apparatus of SFC.

Explanation of symbols

31 Tank 32 Glass tube 33 0.69 mass% salt solution 34 L-shaped tube with cock 35 Cock 40 Container 41 Cell 42 Stainless steel wire mesh 43 Stainless steel wire mesh 44 Swelling gel 45 Glass filter 46 Piston 47 Hole 48 in piston Additional container 49 Upper plate balance 100 Plastic support cylinder 101 Stainless steel 400 mesh wire mesh 102 Swelling gel 103 Piston 104 Load (weight)
105 Petri dish 106 Glass filter 107 Filter paper 108 0.90 mass% saline

Claims (15)

A water-absorbing resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer , a nitrogen-containing ketone compound (A) , and a divalent compound that can be dissolved in pure water at room temperature at a concentration of 5% by mass or more. A water-absorbent resin composition comprising a trivalent water-soluble polyvalent metal salt,
The nitrogen-containing ketone compound (A) is urea,
The total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbent resin particles.
A water absorbent resin composition characterized by the above. The water absorbing property according to claim 1 , wherein at least a part of the surface of the water absorbing resin particle is coated with the nitrogen-containing ketone compound (A) and a divalent and / or trivalent water-soluble polyvalent metal salt. Resin composition. The water-absorbent resin composition according to claim 1 or 2, wherein the water-absorbent resin particles have been subjected to a surface crosslinking treatment or a heat treatment. The water-absorbent resin composition according to any one of claims 1 to 3, wherein the water-absorbent resin composition has an absorptivity (AAP) to a pressure of 4.83 kPa of 15 (g / g) or more. The water absorbent resin composition, saline flow conductivity (SFC) is the ^{30 (× 10 -7 · cm 3} · s · g -1) or more, according to any one of claims 1 4 Water absorbent resin composition. A water-absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer, a nitrogen-containing ketone compound (A), 2-valent which can dissolve in a concentration of 5% by mass or more in pure water at room temperature And / or a method for producing a water-absorbent resin composition comprising mixing a trivalent water-soluble polyvalent metal salt,
The nitrogen-containing ketone compound (A) is urea,
Mixing so that the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbent resin particles. ,
A method for producing a water-absorbent resin composition, comprising: It can be dissolved at a concentration of 5% by mass or more in a water-absorbing resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer , a nitrogen-containing ketone compound (A) that is urea, and pure water at room temperature. A divalent and / or trivalent water-soluble polyvalent metal salt powder,
Mixing so that the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbent resin particles. ,
A method for producing a water-absorbent resin composition, comprising: It can be dissolved at a concentration of 5% by mass or more in a water-absorbing resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer , a nitrogen-containing ketone compound (A) that is urea, and pure water at room temperature. A liquid containing a divalent and / or trivalent water-soluble polyvalent metal salt,
Mixing so that the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbent resin particles. ,
A method for producing a water-absorbent resin composition, comprising: Water absorbent resin particles having an internal cross-linked structure obtained by polymerizing a water-soluble unsaturated monomer , an aqueous solution containing a nitrogen-containing ketone compound (A) that is urea, and a concentration of 5% by mass or more in pure water at room temperature An aqueous solution containing a divalent and / or trivalent water-soluble polyvalent metal salt that can be dissolved in
Mixing so that the total amount of the nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbent resin particles. ,
A method for producing a water-absorbent resin composition, comprising: It can be dissolved at a concentration of 5% by mass or more in a water-absorbing resin particle having an internally crosslinked structure obtained by polymerizing a water-soluble unsaturated monomer , a nitrogen-containing ketone compound (A) that is urea, and pure water at room temperature. A divalent and / or trivalent water-soluble polyvalent metal salt,
The nitrogen-containing ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt are contained in an amount of 0.01 to 100 parts by mass with respect to 100 parts by mass of the water-absorbent resin particles. Either one of the nitrogen ketone compound (A) and the divalent and / or trivalent water-soluble polyvalent metal salt is mixed as an aqueous solution, and the other is dry-blended.
A method for producing a water-absorbent resin composition, comprising: The water-absorbing resin composition according to any one of claims 1 to 5 , wherein a liquid diffusion rate (LDV) is 2.1 to 10.0 mm / s. The water absorbent resin composition is
90% by mass or more of particles having a particle size of 150 to 850 μm, and
The water absorbent resin composition according to claim 11, wherein the logarithmic standard deviation (σζ) of the particle size distribution is 0.25 to 0.45. The water absorbent resin composition according to claim 11 or 12, wherein the water absorbent resin particles contained in the water absorbent resin composition are surface-treated. The water absorbent resin composition according to any one of claims 11 to 13, wherein the water content of the water absorbent resin composition is 0.1 to 10% by mass. The water absorbent resin composition according to any one of claims 11 to 14, wherein a centrifuge retention capacity (CRC) of the water absorbent resin composition is 25 to 40 g / g.