JP4420211B2

JP4420211B2 - Identification sheet

Info

Publication number: JP4420211B2
Application number: JP2004185723A
Authority: JP
Inventors: 敬一朗中谷; 晴夫草島
Original assignee: Shiga Prefectural Government.
Current assignee: Shiga Prefectural Government.
Priority date: 2004-06-24
Filing date: 2004-06-24
Publication date: 2010-02-24
Anticipated expiration: 2024-06-24
Also published as: JP2006008784A

Description

本発明は、指紋や足跡、タイヤ跡等の採取に用いる鑑識用シートに関する。 The present invention relates to an identification sheet used for collecting fingerprints, footprints, tire marks, and the like.

犯罪捜査において、指紋採取の一般的な方法は、犯人の指が接触したと思われる箇所に、アルミの微粉末や、アルミと４三酸化鉄の混合微粉末等を、刷毛を用いて撒布し、穂先で軽く払うようにして指紋の隆線を視覚化した後、ここに、ベースフィルム層と、このベースフィルム層の片面に設けられた粘着剤層とから構成される鑑識用シートを貼付し、粘着剤層に指紋の隆線を転写した後に剥離して行われる。 In criminal investigations, the general method of fingerprint collection is to distribute fine powder of aluminum or a mixed powder of aluminum and iron trioxide using a brush at the place where the finger of the criminal is supposed to have touched. After visualizing the ridges of the fingerprint as if it was lightly swollen with the tip of the fingerprint, a discriminating sheet composed of a base film layer and an adhesive layer provided on one side of the base film layer was affixed here. The ridges of the fingerprint are transferred to the adhesive layer and then peeled off.

かかる指紋採取は、犯人割り出しのための有力な手段となるため、これまでに、指紋採取に好適に用いられる鑑識用シートがいくつか開発されてきた（例えば、特許文献１乃至３）。
特開平３−８０８３３号公報（特許請求の範囲）特開２００１−４０２９９号公報（特許請求の範囲）特開２００２−２０００６０号公報（特許請求の範囲） Since such fingerprint collection is an effective means for determining a criminal, several identification sheets that have been suitably used for fingerprint collection have been developed so far (for example, Patent Documents 1 to 3).
Japanese Patent Laid-Open No. 3-80833 (Claims) JP 2001-40299 A (Claims) JP 2002-200060 A (Claims)

しかしながら、かかる従来の鑑識用シートにあっては、指紋の付着した箇所が、車のダッシュボードや革製品等、表面が微細な凹凸構造から構成されている場合に、かかる箇所にアルミ等の微粉末を撒布することによって、指紋の視覚化はできるものの、かかる視覚化された指紋の隆線を鑑識用シートに転写しようとしても、転写された指紋は斑模様となって、指紋の隆線を上手く転写することができなかった。すなわち、従来の鑑識用シートでは、指紋が付着した箇所によっては、指紋鑑識に耐え得る程度に鑑識用シートに指紋を転写することができない場合があった。 However, in such a conventional forensic sheet, when the part where the fingerprint is attached is composed of a concave and convex structure with a fine surface such as a car dashboard or leather product, a fine powder such as aluminum is applied to the part. Although the fingerprint can be visualized by distributing the fingerprint, even if the visualized fingerprint ridge is transferred to the identification sheet, the transferred fingerprint becomes a mottled pattern, and the fingerprint ridge is improved. Could not be transcribed. That is, in the conventional identification sheet, depending on the location where the fingerprint is attached, the fingerprint may not be transferred to the identification sheet to the extent that it can withstand the fingerprint identification.

本発明の目的は、従来の鑑識用シートでは指紋採取を十分に行うことができなかった車のダッシュボード等の、微細な凹凸構造を有する表面からも高い精度で指紋の隆線を転写することができる、鑑識用シートを提供することにある。 An object of the present invention is to transfer fingerprint ridges with high accuracy even from a surface having a fine concavo-convex structure, such as a dashboard of a car, which could not sufficiently perform fingerprint collection with a conventional identification sheet. It is to provide a sheet for identification.

本発明の要旨とするところは、ベースフィルム層と、該ベースフィルム層の片面に設けられた粘着剤層とを備え、前記ベースフィルム層が、引張弾性率４〜５０ＭＰａ、伸長回復率９０％以上を示す鑑識用シートにある。 The gist of the present invention includes a base film layer and an adhesive layer provided on one side of the base film layer, and the base film layer has a tensile elastic modulus of 4 to 50 MPa and an elongation recovery rate of 90% or more. It is in the sheet for identification.

かかる構成により、車のダッシュボード等の、微細な凹凸構造を有する表面に、本発明にかかる鑑識用シートを貼付しても、鑑識用シートが備える粘着剤層が凹部にも到達することとなる。すなわち、本発明の鑑識用シートは、表面追従性に優れたものとなる。また、指紋の付着した箇所への鑑識用シートの貼付、指紋の転写、及び、かかる箇所からの鑑識用シートの剥離操作を経た後にあっても、鑑識用シートが変形することが防がれることとなる。 With this configuration, even if the forensic sheet according to the present invention is applied to a surface having a fine uneven structure, such as a dashboard of a car, the adhesive layer included in the forensic sheet reaches the recess. . That is, the forensic sheet of the present invention has excellent surface followability. In addition, it is possible to prevent the forensic sheet from being deformed even after the pasting of the forensic sheet to the part where the fingerprint is attached, the transfer of the fingerprint, and the peeling operation of the forensic sheet from the part. It becomes.

また、本発明の要旨とするところは、ベースフィルム層と、該ベースフィルム層の片面に設けられた粘着剤層と、該ベースフィルム層の他の片面に設けられた支持体層とを備え、前記ベースフィルム層が、引張弾性率４〜５０ＭＰａ、伸長回復率９０％以上を示し、前記支持体層が、引張弾性率１００〜３００ＭＰａを示す鑑識用シートにある。 The gist of the present invention includes a base film layer, a pressure-sensitive adhesive layer provided on one side of the base film layer, and a support layer provided on the other side of the base film layer, The base film layer has a tensile elastic modulus of 4 to 50 MPa, an elongation recovery rate of 90% or more, and the support layer is in a forensic sheet having a tensile elastic modulus of 100 to 300 MPa.

かかる構成により、本発明の鑑識用シートは、微細な凹凸構造を有する表面に対する優れた追従性を保持しつつ、指紋の採取の際に、ベースフィルム層が風でなびいたり、よれたり、ダレて変形したりすることが防がれる。 With this configuration, the forensic sheet of the present invention has excellent followability to a surface having a fine concavo-convex structure, and the base film layer flutters in the wind, twists or sags when collecting fingerprints. It can be prevented from being deformed.

また、本発明の要旨とするところは、前記支持体層が、前記ベースフィルム層に着脱自在に設けられたことにある。 Further, the gist of the present invention is that the support layer is detachably provided on the base film layer.

かかる構成により、本発明の鑑識用シートは、指紋の付着した箇所に鑑識用シートを貼付する際には、支持体層を設けたまま行うことが可能となる一方、かかる貼付の後、粘着剤層への指紋の隆線の転写をするために、鑑識用シートを上から押圧する際には、かかる支持体層を除去した後に行うことが可能となる。また、押圧の後、指紋が転写された鑑識用シートを、指紋が付着した箇所から剥離する操作を、かかる支持体層を再度ベースフィルム層に設けた後に行うことが可能となる。 With this configuration, the identification sheet according to the present invention can be performed with the support layer provided when the identification sheet is applied to the portion where the fingerprint is attached. In order to transfer the fingerprint ridges to the layer, it is possible to remove the support layer after pressing the identification sheet from above. In addition, after pressing, the operation of peeling the identification sheet on which the fingerprint is transferred from the place where the fingerprint is attached can be performed after the support layer is provided again on the base film layer.

また、本発明の要旨とするところは、前記支持体層が、ポリエステル系樹脂を主成分として構成されることにある。 The gist of the present invention is that the support layer is composed mainly of a polyester resin.

かかる構成によって、本発明の鑑識用シートは、支持体層を光透過性の優れたものとすることが可能となる。 With this configuration, the identification sheet of the present invention can make the support layer excellent in light transmittance.

また、本発明の要旨とするところは、前記ベースフィルム層が、シリコーン系樹脂を主成分として構成されることにある。 Further, the gist of the present invention is that the base film layer is composed mainly of a silicone resin.

かかる構成により、本発明の鑑識用シートは、ベースフィルム層の表面追従性がより優れたものとなる。 With this configuration, the forensic sheet of the present invention is more excellent in surface followability of the base film layer.

また、本発明の要旨とするところは、前記粘着剤層が、ポリウレタン系接着剤を主成分として構成されることにある。 The gist of the present invention is that the pressure-sensitive adhesive layer is composed mainly of a polyurethane-based adhesive.

かかる構成により、本発明の鑑識用シートの粘着剤層が、耐熱性、撥水性に優れたものとなる。 With this configuration, the pressure-sensitive adhesive layer of the identification sheet of the present invention is excellent in heat resistance and water repellency.

また、本発明の要旨とするところは、前記粘着剤層が、シリコーン系接着剤を主成分として構成されることにある。 The gist of the present invention is that the pressure-sensitive adhesive layer is composed mainly of a silicone-based adhesive.

かかる構成により、ベースフィルム層がシリコーン系樹脂を主成分として構成された場合の、ベースフィルム層と粘着剤層との接着性が優れたものとなる。 With this configuration, the adhesiveness between the base film layer and the pressure-sensitive adhesive layer is excellent when the base film layer is composed mainly of a silicone resin.

また、本発明の要旨とするところは、前記粘着剤層の表面に、さらに台紙が設けられたことにある。 Further, the gist of the present invention is that a mount is further provided on the surface of the pressure-sensitive adhesive layer.

かかる構成により、粘着剤層が台紙によって保護されることとなる。 With this configuration, the pressure-sensitive adhesive layer is protected by the mount.

本発明の鑑識用シートは、鑑識用シートが備える粘着剤層が、微細な凹凸表面の凹部にも到達することとなる。このため、従来、指紋の隆線を十分に転写することが困難であった微細な凹凸面から構成される表面上からでも、指紋鑑識に耐え得る程度に、指紋の隆線を鑑識用シートに転写することができる。また、指紋採取後において、鑑識用シートが変形することが少ないため、鑑識用シートに転写された指紋が大きく変形することを防ぐことができる。 In the forensic sheet of the present invention, the pressure-sensitive adhesive layer provided in the forensic sheet reaches the concave portion of the fine uneven surface. For this reason, fingerprint ridges can be applied to the identification sheet to the extent that it can withstand fingerprint identification even from a surface composed of fine uneven surfaces, which has conventionally been difficult to transfer sufficiently. Can be transferred. In addition, since the inspection sheet is rarely deformed after the fingerprint is collected, it is possible to prevent the fingerprint transferred to the inspection sheet from being largely deformed.

また、本発明の鑑識用シートは、支持体層を備えることにより、鑑識用シートが風でなびいたり、よれたりすることが防がれる。このため、本発明の鑑識用シートは、指紋採取の際の操作性に優れたものとなる。また、指紋の付着した箇所に本発明の鑑識用シートを貼付する際に、鑑識用シートがダレたりして、変形した状態で貼付されることが防がれるため、鑑識用シートが変形した状態で指紋が鑑識用シートに転写されることを防ぐことができる。 Moreover, the forensic sheet of the present invention is provided with a support layer, whereby the forensic sheet can be prevented from fluttering or twisting in the wind. For this reason, the identification sheet of the present invention is excellent in operability during fingerprint collection. In addition, when sticking the identification sheet of the present invention to the place where the fingerprint is attached, the identification sheet is prevented from being damaged and stuck in a deformed state. This prevents the fingerprint from being transferred to the identification sheet.

本発明の鑑識用シートは、支持体層がベースフィルム層に着脱自在に設けられることにより、指紋が付着した箇所に本発明の鑑識用シートを貼付する際には、ベースフィルム層に支持体層を設けたままで行うことにより、貼付の際にベースフィルム層が風でなびいたり、変形することが防がれるため、貼付の際の鑑識用シートの操作性を優れたものとすることができる。また、鑑識用シートの貼付後の押圧を、支持体層を除去した後に行うことにより、鑑識用シートは、優れた表面追従性を発揮することができる。そして、かかる押圧後、支持体層を再度ベースフィルム層に装着し、次いで、指紋の付着した箇所から鑑識用シートを剥離することにより、かかる剥離操作の際にベースフィルム層が変形して、鑑識用シートに転写された指紋が変形することを防ぐことができる。 The discriminating sheet of the present invention is provided so that the support layer is detachably provided on the base film layer, so that when the discriminating sheet of the present invention is applied to a place where a fingerprint is attached, the support layer is attached to the base film layer. Since the base film layer is prevented from being blown or deformed by wind during sticking, it is possible to improve the operability of the identification sheet during sticking. Moreover, by performing the pressing after the application of the identification sheet after removing the support layer, the identification sheet can exhibit excellent surface followability. Then, after such pressing, the support layer is attached to the base film layer again, and then the inspection sheet is peeled off from the place where the fingerprint is attached, whereby the base film layer is deformed during the peeling operation, It is possible to prevent the fingerprint transferred on the sheet for use from being deformed.

本発明の鑑識用シートは、支持体層、ベースフィルム層、粘着剤層を、それぞれ光透過性に優れたものから構成することが可能であるため、指紋の採取の際、鑑識用シートの粘着剤層表面の略中央に指紋の隆線を転写することが容易になる。また、指紋転写後は、支持体層側から指紋を明確に鑑識することが可能になる。 In the identification sheet of the present invention, the support layer, the base film layer, and the pressure-sensitive adhesive layer can each be composed of a material having excellent light transmittance. It becomes easy to transfer the fingerprint ridge to the approximate center of the surface of the agent layer. In addition, after the fingerprint is transferred, the fingerprint can be clearly identified from the support layer side.

本発明の鑑識用シートは、ベースフィルム層がシリコーン系樹脂を主成分として構成されることにより、ベースフィルム層の表面追従性がより優れたものとなる。このため、微細な凹凸構造から構成される表面からも、アルミの微粉末等で視覚化された指紋の隆線を、より高精度に鑑識用シートの粘着剤層に転写することができる。 In the identification sheet of the present invention, the base film layer is composed mainly of a silicone-based resin, so that the surface followability of the base film layer is more excellent. Therefore, fingerprint ridges visualized with fine aluminum powder or the like can be transferred to the pressure-sensitive adhesive layer of the identification sheet with higher accuracy even from the surface constituted by a fine concavo-convex structure.

本発明の鑑識用シートは、粘着剤層がポリウレタン系接着剤を主成分として構成されることにより、耐熱性、撥水性に優れることとなる。このため、例えば、真夏に屋外に放置される等して、表面が高温となっている部材からでも、指紋を採取することができる。また、屋外等にあって、降雨等で表面が濡れている部材からでも、かかる表面から完全に水分を除去しなくとも、指紋を採取することができる。 The identification sheet of the present invention is excellent in heat resistance and water repellency because the pressure-sensitive adhesive layer is mainly composed of a polyurethane-based adhesive. For this reason, for example, fingerprints can be collected even from a member whose surface is hot, such as being left outdoors in midsummer. In addition, fingerprints can be collected even from a member that is outdoors or the like and whose surface is wet due to rain or the like without completely removing moisture from the surface.

本発明の鑑識用シートは、粘着剤層がシリコーン系接着剤を主成分として構成されることにより、ベースフィルム層がシリコーン系樹脂を主成分として構成された場合において、かかる粘着剤層とベースフィルム層との接着性が優れたものとなるため、ベースフィルム層に粘着剤層を設ける際、ベースフィルム層表面に特別な処理を施すことが必須ではなくなる。このため、本発明の鑑識用シートの製造コストを低く抑えることができる。 The identification sheet of the present invention has a pressure-sensitive adhesive layer and a base film when the pressure-sensitive adhesive layer is composed mainly of a silicone-based adhesive, so that the base film layer is composed mainly of a silicone-based resin. Since the adhesiveness to the layer is excellent, it is not essential to perform a special treatment on the surface of the base film layer when the pressure-sensitive adhesive layer is provided on the base film layer. For this reason, the manufacturing cost of the identification sheet of the present invention can be kept low.

本発明にかかる鑑識用シートについて、以下に詳しく説明する。 The inspection sheet according to the present invention will be described in detail below.

図１は、本発明の鑑識用シートの第１実施形態を示す。図２は、本発明の鑑識用シートの第２実施形態を示す。図３は、本発明の鑑識用シートの第３実施形態を示す。 FIG. 1 shows a first embodiment of the identification sheet of the present invention. FIG. 2 shows a second embodiment of the identification sheet of the present invention. FIG. 3 shows a third embodiment of the identification sheet of the present invention.

図１に従えば、本発明の鑑識用シート１０は、ベースフィルム層２０と、このベースフィルム層２０の片面に設けられた粘着剤層２４とを含んで構成される。 According to FIG. 1, the identification sheet 10 of the present invention includes a base film layer 20 and an adhesive layer 24 provided on one side of the base film layer 20.

本発明にかかるベースフィルム層２０、及び粘着剤層２４は、光透過性に優れていることが好ましい。かかる構成により、本発明にかかる鑑識用シート１０は、鑑識用シート１０の片方の面に転写された指紋の形状を、鑑識用シート１０のもう片方の面から観察して指紋鑑識を行うことが可能となる。 The base film layer 20 and the pressure-sensitive adhesive layer 24 according to the present invention are preferably excellent in light transmittance. With this configuration, the forensic sheet 10 according to the present invention can perform fingerprint inspecting by observing the shape of the fingerprint transferred to one side of the forensic sheet 10 from the other side of the forensic sheet 10. It becomes possible.

本発明にかかるベースフィルム層２０は、引張弾性率が４〜５０ＭＰａであることが好ましく、４〜１０ＭＰａであることがより好ましく、６〜８ＭＰａであることがさらに好ましい。また、伸長回復率が８０％以上であることが好ましく、９０％以上であることがより好ましい。 The base film layer 20 according to the present invention preferably has a tensile modulus of 4 to 50 MPa, more preferably 4 to 10 MPa, and even more preferably 6 to 8 MPa. The elongation recovery rate is preferably 80% or more, and more preferably 90% or more.

ベースフィルム層２０の引張弾性率が５０ＭＰａより大きい場合には、ベースフィルム層２０の伸縮性が劣ることとなる。このため、本発明にかかる鑑識用シート１０は、優れた表面追従性を発揮することが困難となって、微細な凹凸表面から鑑識用シート１０へ、十分に指紋を転写することができない。また、ベースフィルム層２０の引張弾性率が４ＭＰａ未満である場合には、ベースフィルム層２０の自己支持性が劣ることとなって、鑑識用シート１０が風でなびいたり、よれる等するおそれがある。このため、本発明にかかる鑑識用シート１０は、指紋採取の際の操作性、作業性が悪くなる。また、ベースフィルム層２０の伸長回復率が８０％未満の場合には、鑑識用シート１０への指紋の転写後、指紋の付着した箇所から鑑識用シート１０を剥離する際、鑑識用シート１０が延びて変形した場合に、延びたままの状態で維持され易くなるため、鑑識用シート１０に転写された指紋の形状が変形して保持されるおそれがある。このため、本発明にかかる鑑識用シート１０は、鑑識用シート１０に転写された指紋を、好適に指紋鑑定に用いることができないおそれがある。 When the tensile elastic modulus of the base film layer 20 is greater than 50 MPa, the stretchability of the base film layer 20 is inferior. For this reason, it becomes difficult for the forensic sheet 10 according to the present invention to exhibit excellent surface followability, and the fingerprint cannot be sufficiently transferred from the fine uneven surface to the forensic sheet 10. Moreover, when the tensile elastic modulus of the base film layer 20 is less than 4 MPa, the self-supporting property of the base film layer 20 is inferior, and there is a possibility that the forensic sheet 10 may be swung or swung. is there. For this reason, the forensic sheet 10 according to the present invention has poor operability and workability when collecting fingerprints. Further, when the elongation recovery rate of the base film layer 20 is less than 80%, after the fingerprint is transferred to the identification sheet 10, the identification sheet 10 is removed when the identification sheet 10 is peeled off from the portion where the fingerprint is attached. When it is extended and deformed, it is easily maintained in an extended state, and therefore the shape of the fingerprint transferred to the identification sheet 10 may be deformed and held. For this reason, the identification sheet 10 according to the present invention may not be able to suitably use the fingerprint transferred to the identification sheet 10 for fingerprint identification.

本発明にかかるベースフィルム層２０は、シリコーン系樹脂を主成分として構成されることが好ましい。かかる構成により、本発明にかかる鑑識用シート１０は、指紋鑑識により好適に用いることができる。 The base film layer 20 according to the present invention is preferably composed mainly of a silicone resin. With this configuration, the inspection sheet 10 according to the present invention can be suitably used for fingerprint identification.

本発明にかかるベースフィルム層２０の厚みは、０．１〜１ｍｍであることが好ましく、０．２〜０．６ｍｍであることがより好ましい。かかる構成により、本発明にかかる鑑識用シート１０は、指紋を採取する際の操作性、及び指紋採取後の鑑識用シート１０の保存性に優れたものとなる。かかる厚みが０．１ｍｍ未満の場合には、指紋採取の際にフィルムがよれたりして、操作性が悪くなる。また、指紋が付着した箇所への鑑識シートの貼付、及び、かかる箇所からの鑑識用シート１０の剥離の際に、鑑識用シート１０が伸長して薄肉化して、鑑識用シート１０が破損するおそれがある。また、指紋採取の際に、鑑識用シート１０に裂けが生じる場合がある。また、かかる厚みが１ｍｍより厚い場合には、鑑識用シート１０に採取された指紋をベースフィルム層２０を通して観察する際に、指紋の形状が屈折するおそれがある。また、鑑識用シート１０を保存する際に嵩張ることとなる。 The thickness of the base film layer 20 according to the present invention is preferably 0.1 to 1 mm, and more preferably 0.2 to 0.6 mm. With this configuration, the forensic sheet 10 according to the present invention is excellent in operability when collecting a fingerprint and preservability of the forensic sheet 10 after the fingerprint is collected. If the thickness is less than 0.1 mm, the film may be twisted during fingerprint collection, resulting in poor operability. In addition, when the identification sheet is attached to the part where the fingerprint is attached and when the identification sheet 10 is peeled off from the part, the identification sheet 10 is elongated and thinned, and the identification sheet 10 may be damaged. There is. Further, when collecting fingerprints, the identification sheet 10 may be torn. When the thickness is greater than 1 mm, the fingerprint shape may be refracted when the fingerprint collected on the identification sheet 10 is observed through the base film layer 20. Moreover, it will be bulky when the identification sheet 10 is stored.

本発明にかかる粘着剤層２４は、前述の通り、光透過性に優れていることが好ましい。また、付着した指紋を視覚化するために従来から一般的に用いられる、アルミ等の微粉末を吸着し得る程度の粘着力を有していることが好ましい。その一方、かかる粘着力は、粘着剤層２４への指紋の転写後、指紋が付着した箇所から鑑識用シート１０を剥離する際に、かかる箇所の塗装の剥離等、原状破損が生じない程度の粘着力であることが好ましい。本発明にかかる粘着剤層２４は、かかる性質を併せ有する接着剤から構成されるものであれば、特に限定されるものではなく、具体的には、かかる粘着剤層２４は、ゼラチンやポリウレタン系接着剤等、従来の鑑識用シートの粘着剤層を構成するために用いられる接着剤のみならず、エポキシ樹脂系接着剤やシリコーン系接着剤から構成されてもよい。また、これらの接着剤を二以上選択して構成される接着剤から構成されてもよい。 As described above, the pressure-sensitive adhesive layer 24 according to the present invention is preferably excellent in light transmittance. Moreover, it is preferable to have an adhesive force that can adsorb fine powders such as aluminum, which is generally used in the past for visualizing attached fingerprints. On the other hand, the adhesive strength is such that after the fingerprint is transferred to the adhesive layer 24, when the identification sheet 10 is peeled off from the place where the fingerprint is attached, the original damage such as peeling of the paint on the place is not caused. The adhesive strength is preferred. The pressure-sensitive adhesive layer 24 according to the present invention is not particularly limited as long as it is composed of an adhesive having such properties. Specifically, the pressure-sensitive adhesive layer 24 is made of gelatin or polyurethane. The adhesive may be composed of not only an adhesive used for constituting a pressure-sensitive adhesive layer of a conventional identification sheet but also an epoxy resin adhesive or a silicone adhesive. Moreover, you may comprise from the adhesive comprised by selecting 2 or more of these adhesives.

なお、かかる粘着剤層２４は、ポリウレタン系接着剤を含んで構成されることが好ましい。かかる構成により、本発明にかかる粘着剤層２４は、耐熱性、撥水性に優れるものとなる。このため、本発明にかかる鑑識用シート１０は、表面が高温を有していたり、あるいは表面が水で濡れている箇所からでも、好適に指紋を採取することができる。 In addition, it is preferable that this adhesive layer 24 is comprised including a polyurethane-type adhesive agent. With this configuration, the pressure-sensitive adhesive layer 24 according to the present invention has excellent heat resistance and water repellency. For this reason, the forensic sheet 10 according to the present invention can suitably collect fingerprints even from the surface having a high temperature or the surface being wet with water.

また、ベースフィルム層２０が、シリコーン系樹脂を含んで構成される場合には、かかる粘着剤層２４は、シリコーン系接着剤を含んで構成されてもよい。かかる構成により、本発明にかかる粘着剤層２４は、耐熱性に優れるものとなるため、本発明にかかる鑑識用シート１０は、表面が高温を有している箇所からでも、好適に指紋を採取することができる。また、ベースフィルム層２０と粘着剤層２４との接着性が優れるものとなって、ベースフィルム層２０の表面に粘着剤層２４を設ける際に、ベースフィルム層２０の表面にコロナ処理やプラズマ処理等の特別な処理を施すことが必要なくなるため、鑑識用シート１０の製造コストを低く抑えることができる。 Moreover, when the base film layer 20 is comprised including a silicone type resin, this adhesive layer 24 may be comprised including a silicone type adhesive agent. With this configuration, the pressure-sensitive adhesive layer 24 according to the present invention is excellent in heat resistance. Therefore, the forensic sheet 10 according to the present invention suitably collects fingerprints even from a location where the surface has a high temperature. can do. Further, the adhesiveness between the base film layer 20 and the pressure-sensitive adhesive layer 24 becomes excellent, and when the pressure-sensitive adhesive layer 24 is provided on the surface of the base film layer 20, the surface of the base film layer 20 is subjected to corona treatment or plasma treatment. Therefore, it is not necessary to perform a special process such as this, so that the manufacturing cost of the identification sheet 10 can be kept low.

本発明にかかる粘着剤層２４は、その厚みが０．０５〜０．５ｍｍであることが好ましく、０．０５〜０．２ｍｍであることがより好ましい。かかる構成により、本発明にかかる鑑識用シート１０は、優れた表面追従性を保持しつつ、十分な指紋転写能力を発揮することができる。かかる厚みが０．０５ｍｍ未満では、本発明にかかる鑑識用シート１０を凹凸面や湾曲面に貼付した際に、鑑識用シート１０が伸長して粘着剤層２４が薄肉化して、粘着力が低下する場合がある。また、かかる厚みが０．５ｍｍより厚い場合には、本発明にかかる鑑識用シート１０の、優れた表面追従性を維持できないおそれがある。 The pressure-sensitive adhesive layer 24 according to the present invention preferably has a thickness of 0.05 to 0.5 mm, and more preferably 0.05 to 0.2 mm. With this configuration, the forensic sheet 10 according to the present invention can exhibit a sufficient fingerprint transfer capability while maintaining excellent surface followability. When the thickness is less than 0.05 mm, when the forensic sheet 10 according to the present invention is affixed to an uneven surface or a curved surface, the forensic sheet 10 is stretched and the adhesive layer 24 is thinned, resulting in a decrease in adhesive strength. There is a case. Moreover, when this thickness is thicker than 0.5 mm, there exists a possibility that the outstanding surface followable | trackability of the sheet 10 for identification concerning this invention cannot be maintained.

以上、本発明の鑑識用シート１０の実施態様を詳述したが、本発明は上述の実施態様に限定されるものではなく、その他の態様でも実施しうるものである。 As mentioned above, although the embodiment of the identification sheet 10 of this invention was explained in full detail, this invention is not limited to the above-mentioned embodiment, It can implement also in another aspect.

本発明にかかるベースフィルム層２０は、シリコーン系樹脂を含んで構成される態様に限られるものではなく、引張弾性率が４〜５０ＭＰａで、伸長回復率が８０％以上を示すものであれば、いずれの樹脂を含んで構成されてもよい。具体的には、ポリエステル系エラストマーやポリオレフィン系エラストマーを含んで構成される態様を挙げることができる。また、天然ゴムや合成ゴムを含んで構成されてもよい。なお、いずれの場合にあっても、ベースフィルム層２０は、前述の通り、光透過性に優れていることが好ましい。 The base film layer 20 according to the present invention is not limited to an embodiment configured to contain a silicone resin, as long as the tensile elastic modulus is 4 to 50 MPa and the elongation recovery rate is 80% or more. Any resin may be included. Specifically, the aspect comprised including a polyester-type elastomer and a polyolefin-type elastomer can be mentioned. Moreover, you may comprise including natural rubber and synthetic rubber. In any case, the base film layer 20 is preferably excellent in light transmittance as described above.

また、図２に従えば、本発明にかかる鑑識用シート１０は、粘着剤層２４が備えられたベースフィルム層２０のもう片方の面に、支持体層２８が備えられて構成されてもよい。かかる構成により、本発明にかかる鑑識用シート１０は、自己支持性に優れたものとなるため、指紋の採取の際に、ベースフィルム層２０が風でなびいたり、よれたり、ダレて変形したりすることが防がれて、その操作を円滑に行うことができる。特に、指紋採取に熟練した技術を有していない者にも、本発明にかかる鑑識用シート１０を用いた指紋採取を的確に行うことを可能にする。 Further, according to FIG. 2, the forensic sheet 10 according to the present invention may be configured such that a support layer 28 is provided on the other surface of the base film layer 20 provided with the pressure-sensitive adhesive layer 24. . With this configuration, the forensic sheet 10 according to the present invention has excellent self-supporting properties, and therefore, when the fingerprint is collected, the base film layer 20 flutters in the wind, is distorted, and is deformed. It is prevented and the operation can be performed smoothly. In particular, even those who do not have skills skilled in fingerprint collection can accurately perform fingerprint collection using the identification sheet 10 according to the present invention.

本発明にかかる支持体層２８は、引張弾性率が１００〜３００ＭＰａであることが好ましく、１２０〜２００ＭＰａであることがより好ましく、１３０〜１５０ＭＰａであることがより好ましい。かかる構成により、支持体層２８がベースフィルム層２０の優れた表面追従性を抑制することが防がれるため、本発明にかかる鑑識用シート１０は、優れた操作性と、優れた表面追従性とを併せ有することができる。 The support layer 28 according to the present invention preferably has a tensile modulus of 100 to 300 MPa, more preferably 120 to 200 MPa, and more preferably 130 to 150 MPa. With this configuration, the support layer 28 is prevented from suppressing the excellent surface followability of the base film layer 20, so that the forensic sheet 10 according to the present invention has excellent operability and excellent surface followability. Can also be included.

本発明にかかる支持体層２８は、厚みが０．０２〜０．１ｍｍであることが好ましく、０．０３〜０．０８ｍｍであることがより好ましい。かかる構成により、本発明にかかる鑑識用シート１０は、指紋を採取する際の操作性、作業性を優れたものとすることができるのみならず、指紋採取後の鑑識用シート１０の保存性にも優れたものとすることができる。かかる厚みが０．０２ｍｍ未満の場合には、本発明にかかる鑑識用シート１０に、十分な自己支持性を付与することができず、指紋採取の際にベースフィルム層２０がよれたりすることを十分に防ぐことができない。また、指紋が付着した箇所への鑑識シートの貼付、及び、かかる箇所からの鑑識用シート１０の剥離の際に、鑑識用シート１０が伸長して薄肉化して、鑑識用シート１０が破損することを防ぐことができないおそれがある。また、かかる厚みが０．１ｍｍより厚い場合には、鑑識用シート１０の優れた操作性、作業性、及び指紋転写能力を阻害するおそれがある。また、鑑識用シート１０を保存する際に嵩張ることとなる。 The support layer 28 according to the present invention preferably has a thickness of 0.02 to 0.1 mm, and more preferably 0.03 to 0.08 mm. With this configuration, the forensic sheet 10 according to the present invention can not only have excellent operability and workability when collecting fingerprints, but also can improve the storability of the forensic sheet 10 after fingerprint collection. Can also be excellent. When the thickness is less than 0.02 mm, the self-supporting sheet 10 according to the present invention cannot be provided with sufficient self-supporting property, and the base film layer 20 may be twisted during fingerprint collection. It cannot be prevented sufficiently. In addition, when the identification sheet is attached to the part where the fingerprint is attached and when the identification sheet 10 is peeled off from the part, the identification sheet 10 is elongated and thinned, and the identification sheet 10 is damaged. May not be prevented. Moreover, when this thickness is thicker than 0.1 mm, there exists a possibility of inhibiting the operativity, workability | operativity, and fingerprint transfer capability which were excellent in the sheet | seat 10 for identification. Moreover, it will be bulky when the identification sheet 10 is stored.

本発明にかかる支持体層２８は、引張弾性率が１００〜３００ＭＰａを有するものであれば、いずれの部材から構成されてもよく、具体的には、シリコーン系樹脂やポリエステルやポリオレフィンを含んで構成される態様を挙げることができる。なお、かかる支持体層２８は、粘着剤層２４に転写された指紋の隆線が、支持体層２８及びベースフィルム層２０を通して観察できる程度に、光透過性に優れることが好ましい。 The support layer 28 according to the present invention may be composed of any member as long as it has a tensile modulus of 100 to 300 MPa, and specifically includes a silicone resin, polyester, or polyolefin. Can be mentioned. The support layer 28 is preferably excellent in light transmittance so that the ridges of the fingerprint transferred to the adhesive layer 24 can be observed through the support layer 28 and the base film layer 20.

なお、本発明にかかる支持体層２８は、ベースフィルム層２０に着脱自在に備えられてもよい。かかる構成により、本発明にかかる鑑識用シート１０は、指紋の付着した箇所に鑑識用シート１０を貼付し、また、かかる箇所から剥離する際には支持体層２８を装着して行い、また、指紋の付着した箇所に鑑識用シート１０を貼付した後、粘着剤層２４への指紋の隆線の転写を確実にするために鑑識用シート１０を押圧する際には、かかる支持体層２８を除去して行うことが可能となる。このため、本発明にかかる鑑識用シート１０は、指紋の採取のための貼付操作、及び剥離操作の際には自己支持性を備えて、その操作性を優れたものとすることができる一方、押圧操作の際には本発明にかかる鑑識用シート１０の優れた表面追従性を発揮させて、指紋鑑識に十分に耐え得る精度で指紋の採取を行うことができる。 The support layer 28 according to the present invention may be detachably provided on the base film layer 20. With such a configuration, the forensic sheet 10 according to the present invention is performed by attaching the forensic sheet 10 to a place where a fingerprint is attached, and attaching the support layer 28 when peeling from the place, When the identification sheet 10 is affixed to the location where the fingerprint is attached, and when the identification sheet 10 is pressed to ensure the transfer of the fingerprint ridges to the adhesive layer 24, the support layer 28 is used. It is possible to carry out by removing. For this reason, the forensic sheet 10 according to the present invention has a self-supporting property at the time of a sticking operation for collecting fingerprints and a peeling operation, and can have excellent operability, In the pressing operation, the excellent surface followability of the inspection sheet 10 according to the present invention can be exhibited, and fingerprints can be collected with an accuracy sufficient to withstand fingerprint identification.

本発明にかかる支持体層２８は、ベースフィルム層２０に着脱自在に設けるために、接着剤層３２を介して支持体層２８をベースフィルム層２０に貼付してもよい。なお、ベースフィルム層２０が、シリコーン系樹脂を主成分として構成される場合には、かかる接着剤層３２を設けなくとも、支持体層２８はベースフィルム層２０に着脱自在となる場合がある。 The support layer 28 according to the present invention may be attached to the base film layer 20 via the adhesive layer 32 in order to be detachably provided on the base film layer 20. When the base film layer 20 is composed mainly of a silicone-based resin, the support layer 28 may be detachable from the base film layer 20 without providing the adhesive layer 32.

本発明にかかる支持体層２８が、ベースフィルム層２０に着脱自在に備えられている場合には、かかる支持体層２８は、いずれの部材から構成されてもよく、また、引張弾性率や膜厚についても、特に限定されるものではなく、具体的には、紙や不織布等から構成されてもよいが、鑑識用シート１０表面の略中央に指紋を転写することが可能となるように、支持体層２８は光透過性に優れることが好ましい。したがって、かかる接着剤層３２は、具体的には、ポリエステルやポリオレフィンやウレタン系樹脂等を含んで構成されることがより好ましい。また、支持体層２８の引張弾性率や、厚みについても、指紋採取の際の操作性、及び、指紋採取後の鑑識用シート１０の保存性を考慮して、引張弾性率が１５０〜５００ＭＰａ、厚みが０．０５〜１ｍｍであることが好ましい。 When the support layer 28 according to the present invention is detachably provided on the base film layer 20, the support layer 28 may be composed of any member, and may have a tensile elastic modulus or a membrane. The thickness is not particularly limited, and specifically may be composed of paper, nonwoven fabric, etc., so that the fingerprint can be transferred to the approximate center of the surface of the forensic sheet 10, The support layer 28 is preferably excellent in light transmittance. Therefore, specifically, the adhesive layer 32 is more preferably configured to include polyester, polyolefin, urethane resin, or the like. Further, regarding the tensile modulus and thickness of the support layer 28, the tensile modulus is 150 to 500 MPa in consideration of the operability during fingerprint collection and the preservability of the identification sheet 10 after fingerprint collection. The thickness is preferably 0.05 to 1 mm.

図３に従えば、本発明にかかる鑑識用シート１０は、粘着剤層２４に台紙３６が設けられて構成されることが好ましい。かかる構成により、本発明の鑑識用シート１０は、指紋採取前において、粘着剤層２４に指紋以外のゴミ等が付着することを防ぐことができる。また、鑑識用シート１０をかかる台紙３６から剥離して指紋を採取した後は、鑑識用シート１０を再度かかる台紙３６に貼付することによって、時間の経過と伴に粘着剤層２４に転写された指紋の形状が消失することを防ぐことができる。 According to FIG. 3, the forensic sheet 10 according to the present invention is preferably configured by providing the backing layer 36 on the adhesive layer 24. With this configuration, the forensic sheet 10 of the present invention can prevent dust other than fingerprints from adhering to the adhesive layer 24 before fingerprint collection. Further, after the identification sheet 10 was peeled off from the mount 36 and fingerprints were collected, the identification sheet 10 was applied to the mount 36 again to be transferred to the adhesive layer 24 over time. The disappearance of the fingerprint shape can be prevented.

なお、かかる台紙３６の裏面には、予め、事件番号記入欄、指紋採取日時の記入欄、採取物件記入欄等、本発明にかかる鑑識用シート１０を用いて採取した指紋を、犯人割り出しのために役立てることができる事項が記入できる記載欄が印刷されていることが好ましい。 In addition, on the back surface of the mount 36, fingerprints collected using the identification sheet 10 according to the present invention, such as a case number entry field, a fingerprint collection date and time entry field, a collection property entry field, etc., are preliminarily determined for the criminal. It is preferable to print a description column in which items that can be used for writing can be entered.

本発明にかかる鑑識用シート１０の製造方法は、特に限定されるものではなく、例えば、従来公知の方法でシリコーン系樹脂等からベースフィルム層２０を構成し、次いで、かかるベースフィルム層２０の片面に粘着剤を流延塗布し、粘着剤を硬化させることによって作製することもできる。 The method for producing the identification sheet 10 according to the present invention is not particularly limited. For example, the base film layer 20 is formed from a silicone-based resin or the like by a conventionally known method, and then one side of the base film layer 20 is formed. It can also be produced by casting and applying an adhesive to the adhesive.

その他、本発明はその趣旨を逸脱しない範囲内で、当業者の知識に基づき種々なる改良、修正、変形を加えた態様で実施しうるものである。 In addition, the present invention can be carried out in a mode in which various improvements, modifications, and variations are added based on the knowledge of those skilled in the art without departing from the spirit of the present invention.

以下に本発明を実施例に基づいて説明するが、本発明はこれらの実施例に限定されるものではない。 The present invention will be described below based on examples, but the present invention is not limited to these examples.

（参考例） ( Reference example)

シリコーン樹脂から、厚さ０．４ｍｍのシリコーン樹脂フィルムを作製した。かかるシリコーン樹脂フィルムは、引張弾性率７ＭＰａ、伸長回復率９０％であった。なお、かかるシリコーン樹脂フィルムについての引張弾性率、伸長回復率については、ＪＩＳＫ６２４９に基づいて測定した。 A silicone resin film having a thickness of 0.4 mm was prepared from the silicone resin. Such a silicone resin film had a tensile elastic modulus of 7 MPa and an elongation recovery rate of 90%. In addition, about the tensile elasticity modulus about this silicone resin film and the expansion | restoration recovery rate, it measured based on JISK6249.

かかるシリコーン樹脂フィルムをベースフィルム層として用い、かかるベースフィルム層の片面に、ポリウレタン系接着剤からなる、厚さ０．１ｍｍの粘着剤層を設けて、本発明にかかる鑑識用シートを得た。 Using such a silicone resin film as a base film layer, a pressure sensitive adhesive layer made of a polyurethane adhesive and having a thickness of 0.1 mm was provided on one side of the base film layer to obtain a forensic sheet according to the present invention.

表面が微細な凹凸構造を有する、車のダッシュボード上に指紋を付着させ、かかる箇所にアルミの粉末を撒布して指紋の隆線を視覚化した後、かかる鑑識用シートを用いて指紋の転写（採取）を行った。その結果、本発明にかかる鑑識用シートは、その粘着剤層に、指紋鑑識に十分に耐え得る精度で、指紋の隆線を転写できることがわかった。
（実施例１） A fingerprint is deposited on the dashboard of a car with a fine rugged structure on the surface, and aluminum powder is spread on the spot to visualize the ridges of the fingerprint, and then the fingerprint is transferred using the identification sheet. (Collecting) was performed. As a result, it was found that the forensic sheet according to the present invention can transfer fingerprint ridges to the pressure-sensitive adhesive layer with an accuracy sufficient to withstand fingerprint discrimination.
(Example 1 )

ポリエステル樹脂を用いて、厚さ０．０５ｍｍのポリエステル樹脂フィルムを作製した。かかるポリエステル樹脂フィルムは、引張弾性率１３０〜１５０ＭＰａであった。なお、かかるポリエステル樹脂フィルムについての引張弾性率については、ＪＩＳＣ２３１８に基づいて測定した。 A polyester resin film having a thickness of 0.05 mm was prepared using the polyester resin. Such a polyester resin film had a tensile modulus of 130 to 150 MPa. In addition, about the tensile elasticity modulus about this polyester resin film, it measured based on JISC2318.

かかるポリエステル樹脂フィルムを、参考例で作製した鑑識用シートにあって、粘着剤層が設けられていないベースフィルム層の片面に貼付して支持体層とし、本発明にかかる鑑識用シートを得た。 Such a polyester resin film is in the forensic sheet produced in the reference example, and is attached to one side of the base film layer not provided with the pressure-sensitive adhesive layer as a support layer to obtain the forensic sheet according to the present invention. .

かかる鑑識用シートを用いて、参考例と同様にして、ダッシュボード上から指紋の転写（採取）を行った。なお、かかる指紋の採取は、鑑識用シートの貼付・剥離操作時は支持体層をベースフィルム層に設けたまま行い、鑑識用シート上からの押圧時には支持体層をベースフィルム層から除去して行った。その結果、本発明にかかる鑑識用シートは、実施例１の鑑識用シートと同様の指紋転写能力を有する上に、ベースフィルム層がヨレたりしないため、鑑識用シートの貼付・剥離の操作性、作業性が向上することが分かった。
（比較例１） Using this forensic sheet, the fingerprint was transferred (collected) from the dashboard in the same manner as in the reference example . Such fingerprint collection is performed with the support layer provided on the base film layer at the time of sticking / peeling of the forensic sheet, and the support layer is removed from the base film layer during pressing from the forensic sheet. went. As a result, the forensic sheet according to the present invention has the same fingerprint transfer ability as the forensic sheet of Example 1, and the base film layer is not twisted. It was found that workability was improved.
(Comparative Example 1)

ＪＰシート（日東電工株式会社製）を用いて、参考例と同様にて、ダッシュボード上から指紋の採取（転写）を行った。その結果、粘着剤層に転写された指紋の隆線は、斑模様となった。

Using a JP sheet (manufactured by Nitto Denko Corporation), fingerprints were collected (transferred) from the dashboard in the same manner as in the reference example . As a result, the ridges of the fingerprint transferred to the adhesive layer became a spotted pattern.

本発明にかかる鑑識用シートの第１実施形態を示す。1st Embodiment of the identification sheet concerning this invention is shown. 本発明にかかる鑑識用シートの第２実施形態を示す。2nd Embodiment of the sheet for identification concerning this invention is shown. 本発明にかかる鑑識用シートの第３実施形態を示す。3rd Embodiment of the identification sheet concerning this invention is shown.

Explanation of symbols

１０：鑑識用シート
２０：ベースフィルム層
２４：粘着剤層
２８：支持体層
３２：接着剤層
３６：台紙
10: Sheet for identification 20: Base film layer 24: Adhesive layer 28: Support layer 32: Adhesive layer 36: Mount

Claims

A base film layer, a pressure-sensitive adhesive layer provided on one side of the base film layer, and a support layer provided on the other side of the base film layer,
The base film layer exhibits a tensile elastic modulus of 4 to 50 MPa, an elongation recovery rate of 90% or more,
It said support layer is a tensile elastic modulus 100~300MPa shows, the support layer, the base film for identification sheet detachably provided in the layer.

The forensic sheet according to claim 1 , wherein the support layer is composed of a polyester-based resin as a main component.

The base film layer, for identification sheet according to claim 1 or 2 constructed of a silicone-based resin as a main component.

The forensic sheet according to any one of claims 1 to 3 , wherein the pressure-sensitive adhesive layer is composed mainly of a polyurethane-based adhesive.

The identification sheet according to any one of claims 1 to 3 , wherein the pressure-sensitive adhesive layer is composed mainly of a silicone-based adhesive.

The forensic sheet according to any one of claims 1 to 5 , wherein a mount is further provided on the surface of the pressure-sensitive adhesive layer.