JP4418766B2 - Method for making a photosensitive lithographic printing plate - Google Patents

Description

  The present invention relates to a method for making a photosensitive lithographic printing plate. In particular, the present invention relates to a plate making method of a negative photosensitive lithographic printing plate having excellent storage stability, high sensitivity and high printing durability.

  In general, a negative photosensitive lithographic printing plate is obtained by coating a photosensitive composition on a support such as a roughened aluminum plate, exposing a desired image, and polymerizing or crosslinking the exposed portion of the photosensitive layer. Image formation is performed by a process of insolubilizing in a developer and eluting unexposed portions of the photosensitive layer with the developer. Conventionally, as a photosensitive composition used for such a purpose, a photopolymerizable composition is well known, and a part thereof is put into practical use. In addition, recent high-sensitivity photopolymers incorporating a photoinitiating technology that is highly sensitive to visible light have been increased in sensitivity to an area used for direct plate-making with a visible laser, and are widely used as so-called CTP plates.

  In order to respond to the improvement in drawing speed as a pursuit of higher productivity, not only higher sensitivity is required, but also in terms of workability, it is easy to handle under a yellow or white light instead of a dark room. ) Is also increasing. Furthermore, a photopolymerization initiator or a photopolymerization initiation system has been designed and developed to increase the sensitivity, and the hexaarylbiimidazole photopolymerization initiator attracts attention as a highly sensitive photopolymerization initiator. . Many of such hexaarylbiimidazole photopolymerization initiators do not absorb visible light, and photosensitive compositions containing them include ultraviolet-violet lasers with wavelengths of 300 nm to 450 nm and infrared lasers with wavelengths of 800 to 1200 nm. A bright room is also possible by combining with the exposure method.

  However, the sensitivity of the hexaarylbiimidazole photopolymerization initiator alone is not sufficient, and it is necessary to add a co-sensitizer. As this co-sensitizer, a thiol compound is generally used (see Patent Document 1). Unfortunately, the thiol compound not only has a specific odor but is also volatile. When used in the photosensitive layer of a photosensitive lithographic printing plate, the thiol compound evaporates from the photosensitive layer during storage, and in other layers. There is a problem that the sensitivity is reduced by diffusion.

On the other hand, in the plate-making method of a photosensitive lithographic printing plate, heating of the lithographic printing plate precursor after exposure and before development processing (preheating) promotes curing of the image area of the photosensitive material, and improves printing durability. Although conventionally known, on the other hand, there was a problem that the developability of the non-image area was lowered and the printed matter was stained. In particular, hexaarylbisimidazole compounds used as polymerization initiators have poor heat stability, and improvements are desired.
Furthermore, even when a polymer binder having a crosslinkable group is used for the purpose of improving printing durability, it is desired to improve the handleability because the thermal stability tends to deteriorate.
US Pat. No. 5,256,520

  An object of the present invention is to provide a plate-making method for a lithographic printing plate which is excellent in light room handling property and printing durability, has good solubility in a developer, and does not cause stains on printed matter in a highly sensitive radical polymerization type photosensitive material. It is to provide.

  The above-mentioned subject is achieved by the following composition. That is, the present invention is as follows.

式中、Ｒは置換基を有してもよいアルキル基、又は置換基を有してもよいアリール基を表
し、ＡはＮ＝Ｃ−Ｎ部分と共に炭素原子を有する５員環又は６員環のヘテロ環を形成す
る原子団を表し、Ａはさらに置換基を有してもよい。
２．前記連鎖移動剤が、下記一般式（Ｉ）および一般式（ＩＩ）で表される化合物で
あること特徴とする上記１に記載の感光性平版印刷版の製版方法。

〔一般式（Ｉ）および一般式（ＩＩ）中、Ｒは置換基を有してもよいアルキル基、又は置換基を有してもよいアリール基を表し、Ｘはハロゲン基、アルコキシル基、置換基を有してもよいアルキル基、または置換基を有してもよいアリール基を表す。〕
３． 高分子バインダーが、側鎖に架橋性基を有する（メタ）アクリルバインダーおよび側鎖に架橋性基を有するポリウレタンバインダーからなる群から選択される少なくとも１種であることを特徴とする前記１又は２に記載の感光性平版印刷版の製版方法。
４． 高分子バインダーが、側鎖に架橋性基を有するポリウレタンバインダーから選択される少なくとも１種であることを特徴とする前記１〜３のいずれかに記載の感光性平版印刷版の製版方法。 1. On a hydrophilic support, a hexaarylbisimidazole compound, a chain transfer agent represented by the following general formula (A), a compound having an ethylenically unsaturated double bond, a polymer binder having a crosslinkable group, and 300 to 500 nm have a photosensitive layer containing a sensitizing dye having an absorption maximum in a wavelength range of the content of the hexaarylbisimidazole compound, the lithographic printing plate precursor is not more than 6.5 mass% of non-volatile components of the photosensitive layer Is subjected to heating and development after scanning exposure with a laser beam, the heating is performed for 5 to 30 seconds, the plate surface temperature at the time of heating is 80 to 150 ° C., and polyoxyethylene naphthyl ether (oxy A method for making a photosensitive lithographic printing plate, comprising developing with a developer containing ethylene repeating unit number n = 13).

In the formula, R represents an alkyl group which may have a substituent, or an aryl group which may have a substituent, and A represents a 5-membered or 6-membered ring having a carbon atom together with an N = CN moiety. The atomic group which forms the heterocyclic ring of A, and A may further have a substituent.
2. 2. The plate making method of a photosensitive lithographic printing plate as described in 1 above , wherein the chain transfer agent is a compound represented by the following general formula (I) and general formula (II).

[In general formula (I) and general formula (II), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and X represents a halogen group, an alkoxyl group, a substituted group. An alkyl group which may have a group, or an aryl group which may have a substituent. ]
3. Said polymeric binder, characterized in that at least one member selected from the group consisting of polyurethane binder having a crosslinkable group in (meth) acrylic binder and a side chain having a crosslinkable group in a side chain one or two A process for making a photosensitive lithographic printing plate as described in 1 above.
4). 4. The process for making a photosensitive lithographic printing plate as described in any one of 1 to 3 above, wherein the polymer binder is at least one selected from polyurethane binders having a crosslinkable group in the side chain.

  According to the present invention, there is provided a plate making method for a lithographic printing plate which is excellent in light room handling properties and printing durability, has good solubility in a developer and does not cause stains on printed matter.

Hereinafter, the plate making method of the photosensitive lithographic printing plate in the present invention will be described in detail.
In addition, although this invention is invention concerning said 1-4 , the other matter was also described for reference.
The photosensitive lithographic printing plate in the present invention is image-exposed with a conventionally known actinic ray such as a helium cadmium laser, an argon ion laser, an FD / YAG laser, a helium neon laser, a semiconductor laser (350 to 600 nm), and then developed. By doing so, an image can be formed on the support.
Heat treatment (preheating) is performed for the purpose of enhancing the curing of the photosensitive layer after image exposure and before development. In order to obtain good printing durability in the present invention, it is preferable to heat the plate so that the temperature reached 80 to 150 ° C., more preferably 90 to 130 ° C., and even more preferably 100 to 125 ° C. after exposure. . If the temperature is too high, the developability of the non-image area is lowered, and if the temperature is too low, sufficient printing durability cannot be obtained. The heating time is 5 to 60 seconds, preferably 5 to 30 seconds, and more preferably 5 to 15 seconds. If the heating time is extremely long, it is not preferable from the viewpoint of workability, and if it is extremely short, sufficient printing durability cannot be obtained.
Further, preheating is preferably performed within 10 minutes after exposure, and more preferably within 1 minute. If the time from exposure to preheating is remarkably long, the radicals generated by exposure disappear and crosslinking does not proceed sufficiently, so that the printing durability tends to deteriorate.

On the photosensitive layer of the photosensitive lithographic printing plate in the present invention, a protective layer may be provided for the purpose of blocking oxygen that inhibits the polymerization. A method of simultaneously removing an unexposed portion of a layer, or a method of removing a protective layer first with water and warm water and then removing a photosensitive layer of an unexposed portion by development, is known. Can contain preservatives described in JP-A-10-10754, organic solvents described in JP-A-8-278636, and the like. A detailed description of the protective layer will be described later.
The development of the photosensitive lithographic printing plate in the present invention with the developer is performed at a temperature of about 0 to 60 ° C., preferably about 15 to 40 ° C., for example, using a light-sensitive photosensitive lithographic printing plate as a developer according to a conventional method. It is performed by dipping and rubbing with a brush.
Further, when developing using an automatic developing machine, the developing solution becomes fatigued according to the amount of processing, so that the processing capability may be restored using a replenishing solution or a fresh developing solution. The photosensitive lithographic printing plate thus developed is washed with water, surface active as described in JP-A Nos. 54-8002, 55-1115045 and 59-58431. It is post-treated with a rinsing solution containing an agent and the like, a desensitizing solution containing gum arabic, starch derivatives and the like. In the present invention, these treatments can be used in various combinations for the post-treatment of the photosensitive lithographic printing plate.
The printing plate obtained by the above treatment can be improved in printing durability by post-exposure treatment or heating treatment such as burning according to the method described in JP-A-2000-89478.

  Next, the photosensitive layer and the planographic printing plate precursor (photosensitive planographic printing plate) having the same in the plate making method of the present invention will be described in detail.

  The photosensitive layer in the present invention contains (A) a hexaarylbisimidazole compound, (B) a chain transfer agent, (C) a compound having an ethylenically unsaturated double bond, and (D) a polymer binder having a crosslinkable group. Contains as an essential component. Each component will be described.

[Hexaarylbisimidazole compound]
In the present invention, a hexaarylbisimidazole compound is used as a polymerization initiator.

  Examples of the hexaarylbiimidazole polymerization initiator include lophine dimers described in JP-B Nos. 45-37377 and 44-86516, such as 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-bromophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o, p-dichlorophenyl) ) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-chlorophenyl) -4,4', 5,5'-tetra (m-methoxyphenyl) biimidazole, 2 , 2'-bis (o, o'-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-nitrophenyl) -4,4', 5,5 ′ − Traphenylbiimidazole, 2,2'-bis (o-methylphenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-trifluorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole and the like.

The hexaarylbisimidazole compound in the present invention is preferably used alone or in combination of two or more.
The amount of the hexaarylbisimidazole compound used in the photosensitive layer in the present invention is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, based on the total solid content of the photosensitive layer. More preferably, it is 1.0 mass%-10 mass%.
Moreover, it is preferable that content of a hexaarylbisimidazole compound is 6.5 mass% or less of the non-volatile component of a photosensitive layer.

  As long as the effects of the present invention are not impaired, a conventionally known polymerization initiator may be used in addition to the hexaarylbisimidazole compound.

[Chain transfer agent]
As the chain transfer agent used in the photosensitive layer of the present invention, a thiol compound represented by the following formula is preferable. By using this thiol compound as a chain transfer agent, it avoids odor problems and sensitivity reduction due to evaporation from the photosensitive layer and diffusion to other layers, and it has excellent storage stability and high sensitivity and high printing durability. A photosensitive lithographic printing plate is obtained.

  In the formula, R represents an alkyl group which may have a substituent, or an aryl group which may have a substituent, and A represents a 5-membered or 6-membered ring having a carbon atom together with an N = CN moiety. The atomic group which forms the heterocyclic ring of A, and A may further have a substituent.

  More preferably, it is at least one selected from the group consisting of compounds represented by the following general formula (I) and general formula (II).

  In general formula (I) and general formula (II), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and X represents a halogen group, an alkoxyl group, a substituent. Represents an alkyl group which may have a substituent or an aryl group which may have a substituent.

  Specific examples of the chain transfer agent (thiol compound) used in the present invention are shown below, but the present invention is not limited thereto.

  The amount of the chain transfer agent used is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, based on the total solid content of the photosensitive layer. More preferably, it is 1.0-10 mass%.

[Compound having an ethylenically unsaturated double bond]
A compound having an ethylenically unsaturated double bond (hereinafter also referred to as an ethylenically unsaturated compound) is an addition polymerized, crosslinked and cured by the action of a polymerization initiator when the photosensitive layer is irradiated with actinic rays. Such a compound having an ethylenically unsaturated bond. The compound containing an ethylenically unsaturated bond capable of addition polymerization can be arbitrarily selected from compounds having at least one, preferably two or more terminal ethylenically unsaturated bonds. For example, those having chemical forms such as monomers, prepolymers, that is, dimers, trimers and oligomers, or mixtures thereof.

Examples of monomers include esters of unsaturated carboxylic acids (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.) and aliphatic polyhydric alcohol compounds, unsaturated carboxylic acids and aliphatic Examples include amides with polyvalent amine compounds.
Specific examples of the monomer of an ester of an aliphatic polyhydric alcohol compound and an unsaturated carboxylic acid include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol Diacrylate, tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, polyester acrylate There are oligomers and the like.

  Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, dipentaerythritol pentamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [p (3-methacryloxy-2-hydroxypropoxy) phenyl] dimethyl methane, bis - [p-(methacryloxyethoxy) phenyl] dimethyl methane.

  Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,5-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate. Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate.

  Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate. Furthermore, the mixture of the above-mentioned ester monomer can also be mentioned. Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylenebisacrylamide, xylylenebismethacrylamide and the like.

  As another example, the polyisocyanate compound having two or more isocyanate groups in one molecule described in JP-B-48-41708 contains a hydroxyl group represented by the following general formula (A). Examples thereof include a vinyl urethane compound containing two or more polymerizable vinyl groups in one molecule to which a vinyl monomer is added.

_{CH 2 = C (R) COOCH} 2 CH (R ') (A)
(However, R and R ′ represent H or CH _3. )

  Further, urethane acrylates as described in JP-A-51-37193 and JP-B-2-32293, JP-A-48-64183, JP-B-49-43191, JP-B-52-30490 And polyfunctional acrylates and methacrylates such as polyester acrylates and epoxy acrylates obtained by reacting an epoxy resin with (meth) acrylic acid, as described in each publication. Further, those introduced as photo-curable monomers and oligomers in the Japan Adhesion Association magazine Vo 1.20, No. 7, pages 300 to 308 (1984) can also be used. In addition, the usage-amount of these ethylenically unsaturated bond containing compounds is 5-80 mass% normally with respect to the total mass of a photosensitive layer, Preferably it is used in 30-70 mass%.

[Polymer binder having a crosslinkable group in the side chain]
For the photosensitive layer in the invention, a polymer binder having a crosslinkable group in the side chain is used.
Here, the crosslinkable group is a group that crosslinks the polymer binder in the course of radical polymerization reaction that occurs in the photosensitive layer when the photosensitive lithographic printing plate is exposed. Although it will not specifically limit if it is a group of such a function, For example, an ethylenically unsaturated bond group, an amino group, an epoxy group etc. are mentioned as a functional group which can be addition-polymerized. Moreover, the functional group which can become a radical by light irradiation may be sufficient, and as such a crosslinkable group, a thiol group, a halogen group, an onium salt structure etc. are mentioned, for example. Especially, an ethylenically unsaturated bond group is preferable and the functional group represented by the following general formula (1)-(3) is especially preferable.

In the general formula (1), R ^{1 to} R ³ each independently represents a monovalent organic group, but R ¹
Preferred examples include a hydrogen atom or an alkyl group which may have a substituent. Among them, a hydrogen atom and a methyl group are preferable because of high radical reactivity. R ² ,
R ³ each independently has a hydrogen atom, a halogen atom, an amino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an alkyl group that may have a substituent, or a substituent. Aryl group which may have a substituent, aryloxy group which may have a substituent, alkylamino group which may have a substituent, arylamino which may have a substituent Group, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group and a substituent may be mentioned. A good alkyl group and an aryl group which may have a substituent are preferable because of high radical reactivity.

X represents an oxygen atom, a sulfur atom, or —N (R ¹² ) —, and R ¹² represents a hydrogen atom or a monovalent organic group. Here, examples of R ¹² include an alkyl group which may have a substituent. Among them, a hydrogen atom, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

  Here, examples of the substituent that can be introduced include an alkyl group, an alkenyl group, an alkynyl group, an aryl group, an alkoxy group, an aryloxy group, a halogen atom, an amino group, an alkylamino group, an arylamino group, a carboxyl group, an alkoxycarbonyl group, A sulfo group, a nitro group, a cyano group, an amide group, an alkylsulfonyl group, an arylsulfonyl group and the like can be mentioned.

In the general formula (2), R ⁴ to R ⁸ is each independently a monovalent organic group, R ⁴
To R ⁸ is preferably a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an alkyl group which may have a substituent, An aryl group that may have a substituent, an alkoxy group that may have a substituent, an aryloxy group that may have a substituent, an alkylamino group that may have a substituent, and a substituent Arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, a substituent may be mentioned. The alkyl group which may have and the aryl group which may have a substituent are preferable.

Examples of the substituent that can be introduced are the same as those in the general formula (1). Y represents an oxygen atom, a sulfur atom, or —N (R ¹² ) —. R ¹² has the same meaning as R ¹² in general formula (1), and preferred examples are also the same.

In the general formula (3), R ⁹ is preferably a hydrogen atom or an alkyl group which may have a substituent, among which a hydrogen atom or a methyl group has high radical reactivity. preferable. R ¹⁰ and R ¹¹ are each independently a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, or an alkyl group which may have a substituent. An aryl group which may have a substituent, an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, a substituent An arylamino group that may have, an alkylsulfonyl group that may have a substituent, an arylsulfonyl group that may have a substituent, and the like, among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

Here, examples of the substituent that can be introduced are the same as those in the general formula (1). Further, Z is an oxygen atom, a sulfur atom, -N (R ¹³⁾ -, or a phenylene group which may have a substituent. Examples of R ¹³ include an alkyl group which may have a substituent. Among them, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

The polymer binder having the crosslinkable group in the side chain of the present invention not only functions as a film-forming agent for the photosensitive layer but also needs to be dissolved in a developer, preferably an alkali developer, so that it is soluble in alkaline water. Or it is preferable that it is a swelling organic polymer. Therefore, the polymer binder of the present invention preferably has an alkali-soluble group such as a carboxyl group in the side chain in addition to the crosslinkable group.
When the polymer binder having a crosslinkable group in the side chain is a water-soluble organic polymer, water development is possible.

Examples of the polymer binder of the present invention include those described in JP-A-59-53836 and JP-A-59-71048, that is, allyl groups in the side chain, (meth) acryloyl groups, and the like. Examples include (meth) acrylic acid copolymers, itaconic acid copolymers, crotonic acid copolymers, maleic acid copolymers, partially esterified maleic acid copolymers having a crosslinkable group.
In addition, as the polymer binder of the present invention, there are also those obtained by adding a cyclic acid anhydride to an addition polymer having a crosslinkable group and a carboxyl group in the side chain, a polyurethane, an acidic cellulose derivative, and a hydroxyl group. Useful.
Among the above, (meth) acrylic acid copolymer and polyurethane are more preferable. In particular, the polyurethane resin can suppress the development damage of the exposed area without lowering the developability of the unexposed area even if the acid value of the photosensitive layer is low, and has both good stain resistance and high printing durability. It is preferable in that
The polyurethane resin having a crosslinkable group in the side chain will be described in more detail below.

The polyurethane resin having a crosslinkable group in the side chain particularly preferably used in the present invention includes (i) a diisocyanate compound, (ii) a diol compound having a carboxyl group, (iii) a diisocyanate compound having a crosslinkable group, and if necessary. (Iv) It can be obtained by subjecting a diol compound having no carboxyl group to a polyaddition reaction.
The diisocyanate compound and diol compound, which are raw materials for the polyurethane resin, will be described below.

(I) Diisocyanate Compound Examples of the diisocyanate compound include a diisocyanate compound represented by the formula (4).

          OCN-L-NCO (4)

  In the formula, L represents a divalent aliphatic or aromatic hydrocarbon group which may have a substituent. If necessary, L may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, and ureido groups. More specifically, L is a divalent aliphatic or aromatic hydrocarbon group which may have a single bond or a substituent (for example, an alkyl, aralkyl, aryl, alkoxy or halogeno group is preferred). Indicates. Preferably an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 15 carbon atoms, and more preferably an alkylene group having 1 to 8 carbon atoms is shown. If necessary, L may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, ureido, and ether groups.

  Specific examples include the following. That is, 2,4-tolylene diisocyanate, dimer of 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, p-xylylene diisocyanate, m-xylylene diisocyanate, 4,4′-diphenylmethane diisocyanate Aromatic diisocyanate compounds such as 1,5-naphthylene diisocyanate, 3,3′-dimethylbiphenyl-4,4′-diisocyanate; hexamethylene diisocyanate, trimethylhexamethylene diisocyanate, lysine diisocyanate, dimer acid diisocyanate, etc. Aliphatic diisocyanate compounds; isophorone diisocyanate, 4,4′-methylenebis (cyclohexyl isocyanate), methylcyclohexane-2,4 (or 2,6) diisocyanate Alicyclic diisocyanate compounds such as 1,3- (isocyanatomethyl) cyclohexane, etc .; a reaction product of diol and diisocyanate such as an adduct of 1 mol of 1,3-butylene glycol and 2 mol of tolylene diisocyanate The diisocyanate compound etc. which are are mentioned.

  A diisocyanate compound may be used independently and may be used in combination of 2 or more type. It is preferable to use a combination of two or more in terms of the balance between printing durability and stain resistance, and at least one aromatic diisocyanate compound (L is an aromatic group) and aliphatic diisocyanate compound (L is an aliphatic group). It is particularly preferred to use each species.

  The amount of diisocyanate used is preferably 0.8 to 1.2, more preferably 0.9 to 1.1 in terms of molar ratio to the diol compound. If the diisocyanate compound is used in excess relative to the diol compound, and the isocyanate group remains at the polymer end, the isocyanate group finally remains by treating with an alcohol or amine after completion of the urethanization reaction. It is preferable that they are synthesized in such a manner.

(Ii) Diol compound having at least one carboxyl group As the diol compound having at least one carboxyl group, formulas (5) and (6)
(7) and / or a compound obtained by ring-opening tetracarboxylic dianhydride with a diol compound. The diol compound used to ring-open the carboxylic dianhydride can be used.

R ₁ represents a hydrogen atom, a substituent (for example, cyano, nitro, halogen atom (—F, —Cl, —
_{Br, -I), - CONH 2} , -COOR 113, -OR 113, -NHCONHR 113, -NHCOOR 113, -NHCOR 113, -OCONHR 113 ( wherein, R ₁₁₃ is an alkyl group having 1 to 10 carbon atoms, carbon Each group such as an aralkyl group of 7 to 15) is included. ) May be an alkyl, aralkyl, aryl, alkoxy or aryloxy group, preferably a hydrogen atom, an alkyl having 1 to 8 carbon atoms or an aryl group having 6 to 15 carbon atoms. L ₁₀ , L ₁₁ and L ₁₂ may be the same or different, and may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy and halogeno groups are preferred). A divalent aliphatic or aromatic hydrocarbon group is shown. Preferably an alkylene group having 1 to 20 carbon atoms, an arylene group having 6 to 15 carbon atoms, and more preferably an alkylene group having 1 to 8 carbon atoms is shown. If necessary, L ₁₀ , L ₁₁ , and L ₁₂ may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, ureido, and ether groups. A ring may be formed by 2 or 3 of R ₁ , L ₁₀ , L ₁₁ and L ₁₂ . Ar represents a trivalent aromatic hydrocarbon group which may have a substituent, preferably an aromatic group having 6 to 15 carbon atoms.

  Specific examples of the diol compound having a carboxyl group represented by the formula (5), (6) or (7) include those shown below.

  3,5-dihydroxybenzoic acid, 2,2-bis (hydroxymethyl) propionic acid, 2,2-bis (2-hydroxyethyl) propionic acid, 2,2-bis (3-hydroxypropyl) propionic acid, Bis (hydroxymethyl) acetic acid, bis (4-hydroxyphenyl) acetic acid, 2,2-bis (hydroxymethyl) butyric acid, 4,4-bis (4-hydroxyphenyl) pentanoic acid, tartaric acid, N, N-dihydroxyethylglycine N, N-bis (2-hydroxyethyl) -3-carboxy-propionamide and the like.

  Moreover, as a preferable tetracarboxylic dianhydride used in the production | generation of the at least 1 sort (s) of diol compound which has an at least 1 carboxyl group, what is shown by Formula (8), (9), (10) is mentioned.

In the formula, L ₂₁ is a divalent aliphatic or aromatic hydrocarbon which may have a single bond or a substituent (for example, alkyl, aralkyl, aryl, alkoxy, halogeno, ester, amide groups are preferred). A group, —CO—, —SO—, —SO ₂ —, —O— or —S—; Preferably a single bond, a divalent aliphatic hydrocarbon group having 1 to 15 carbon _{atoms, -CO -, - SO 2 -} ,
-O- or -S- is shown. R ₂ and R ₃ may be the same or different and each represents a hydrogen atom, alkyl, aralkyl, aryl, alkoxy, or halogeno group. Preferably, a hydrogen atom, a C1-C8 alkyl, a C6-C15 aryl, a C1-C8 alkoxy, or a halogeno group is shown. _{Two of} L ₂₁ , R ₂ and R ₃ may be bonded to form a ring. R ₄ and R ₅ may be the same or different and each represents a hydrogen atom, alkyl, aralkyl, aryl or halogeno group. Preferably a hydrogen atom, a C1-C8 alkyl, or a C6-C15 aryl group is shown. Two of L ₂₁ , R ₄ and R ₅ may be bonded to form a ring. L ₂₂ and L ₂₃ may be the same or different and each represents a single bond, a double bond, or a divalent aliphatic hydrocarbon group. Preferably a single bond, a double bond, or a methylene group is shown. A represents a mononuclear or polynuclear aromatic ring. An aromatic ring having 6 to 18 carbon atoms is preferable.

  Specific examples of the compound represented by the formula (8), (9) or (10) include those shown below.

That is, pyromellitic dianhydride, 3,3 ′, 4,4′-benzophenone tetracarboxylic dianhydride, 3,3 ′, 4,4′-diphenyltetracarboxylic dianhydride, 2,3,6 , 7-Naphthalenetetracarboxylic dianhydride, 1,4,5,8-naphthalenetetracarboxylic dianhydride, 4,4′-sulfonyldiphthalic dianhydride, 2,2-bis (3,4 Dicarboxyphenyl) propane dianhydride, bis (3,4-dicarboxyphenyl) ether dianhydride, 4,4 ′-[3,3 ′-(alkylphosphoryldiphenylene) -bis (iminocarbonyl)] diphthalic acid Aromatic tetracarboxylic dianhydrides such as dianhydrides, adducts of hydroquinone diacetate and trimetic anhydride, diacetyldiamine and trimetic anhydride; 5- (2,5-dioxote Trahydrofuryl) -3-methyl-3-cyclohexene-1,2-dicarboxylic anhydride (Dainippon Ink Chemical Co., Ltd., Epicron B-4400), 1,2,3,4-cyclopentanetetracarboxylic Alicyclic tetracarboxylic dianhydrides such as acid dianhydride, 1,2,4,5-cyclohexanetetracarboxylic dianhydride, tetrahydrofuran tetracarboxylic dianhydride; 1,2,3,4-butanetetra Aliphatic tetracarboxylic dianhydrides such as carboxylic dianhydride and 1,2,4,5-pentanetetracarboxylic dianhydride may be mentioned.

By ring-opening these tetracarboxylic dianhydrides with a diol compound, (ii) at least one diol compound having at least one carboxyl group can be synthesized. However, it is also possible to synthesize the polyurethane resin of the present invention by first reacting the diol compound with (i) the diisocyanate compound and reacting this reactant with the tetracarboxylic dianhydride. Methods are also encompassed by aspects of the present invention. That is, as a method for introducing a structural unit derived from tetracarboxylic dianhydride and a diol compound into a polyurethane resin, there are the following methods.

a) A method of reacting an alcohol-terminated compound obtained by ring-opening tetracarboxylic dianhydride with a diol compound and a diisocyanate compound.
b) A method of reacting an alcohol-terminated urethane compound obtained by reacting a diisocyanate compound under an excess of a diol compound with tetracarboxylic dianhydride.

  Of the at least one diol compound having at least one carboxyl group, the compound represented by the general formula (5) is more preferable because of high solvent solubility and easy synthesis. Further, at least one diol compound having at least one carboxyl group, the polyurethane resin binder has a carboxyl group of 0.2 to 4.0 meq / g, preferably 0.3 to 3.0 meq / g, more preferably Introduced into the polyurethane resin binder in such an amount as having a range of 0.4 to 2.0 meq / g, particularly preferably 0.5 to 1.5 meq / g, most preferably 0.6 to 1.2 meq / g. . Accordingly, the content in the polyurethane resin binder having a structure derived from at least one diol compound having at least one carboxyl group is the number of carboxyl groups, what is used as the other diol component, and the acid of the polyurethane resin binder obtained. Although it is appropriately selected depending on the value, molecular weight, developer composition, pH, etc., for example, it is 5 to 45 mol%, preferably 10 to 40 mol%, more preferably 15 to 35 mol%.

(Iii) Diisocyanate compound having a crosslinkable group As the diisocyanate compound having a crosslinkable group, for example, a triisocyanate compound and a monofunctional alcohol or monofunctional amine compound having a crosslinkable group are subjected to an addition reaction. There is a product obtained.
Examples of the triisocyanate compound include those shown below, but are not limited thereto.

  Examples of the monofunctional alcohol or monofunctional amine compound having a crosslinkable group include those shown below, but are not limited thereto.

  Here, as a method for introducing a crosslinkable group into the side chain of the polyurethane resin, a method using a diisocyanate compound containing a crosslinkable group in the side chain as a raw material for producing the polyurethane resin is suitable. As a diisocyanate compound obtained by addition reaction of a triisocyanate compound and a monofunctional alcohol having a crosslinkable group or 1 equivalent of a monofunctional amine compound having a crosslinkable group in the side chain, for example, Although the following are mentioned, it is not limited to this.

(Iv) Other diol compound As a method for introducing an unsaturated group into the side chain of the polyurethane resin, in addition to the above-described method, a diol compound containing an unsaturated group in the side chain is used as a raw material for polyurethane resin production. A method is also suitable. Such a diol compound may be a commercially available one such as trimethylolpropane monoallyl ether, a halogenated diol compound, a triol compound, an aminodiol compound, a carboxylic acid containing an unsaturated group, and an acid. It may be a compound that is easily produced by a reaction with a chloride, isocyanate, alcohol, amine, thiol, or alkyl halide compound. Specific examples of these compounds include, but are not limited to, the compounds shown below.

  Still another diol compound includes an ethylene glycol compound represented by the following general formula (A ′).

HO— (CH ₂ CH ₂ O) _n —H (A ′)
(In the formula, n represents an integer of 1 or more.)

  Moreover, the random copolymer and block copolymer of ethylene oxide and propylene oxide which have a hydroxyl group at the terminal are also mentioned.

  Furthermore, bisphenol A ethylene oxide adduct (addition number of ethylene oxide 27 to 100), bisphenol F ethylene oxide adduct (ethylene oxide addition number 22 to 100), hydrogenated bisphenol A ethylene oxide adduct (addition of ethylene oxide) The ethylene oxide adduct of hydrogenated bisphenol F (the number of addition of ethylene oxide is 18 or more and 100 or less) can also be used. More specifically, the ethylene glycol compound represented by the general formula (A ′) is preferable in terms of soiling property, n is more preferably an ethylene glycol compound having 2 to 50, and n is an ethylene glycol compound having 3 to 30. More preferably, an ethylene glycol compound having n of 4 to 10 is particularly preferable.

Specifically, 1,2-propylene glycol, di-1,2-propylene glycol, tri-1,2-propylene glycol, tetra-1,2-propylene glycol, hexa-1,2-propylene glycol, 1, 3-propylene glycol, di-1,3-propylene glycol, tri-1,3-propylene glycol, tetra-1,3-propylene glycol, 1,3-butylene glycol, di-1,3-butylene glycol, tri- 1,3-butylene glycol, hexa-1,3-butylene glycol, polypropylene glycol having an average molecular weight of 400, polypropylene glycol having an average molecular weight of 700, polypropylene glycol having an average molecular weight of 1000, polypropylene glycol having an average molecular weight of 2000, and polypropylene having an average molecular weight of 3000 Glycol, average molecular weight 4000 polypropylene glycol, neopentyl glycol, 2-butene-1,4-diol, 2,2,4-trimethyl-1,3-pentanediol, 1,4-bis-β-hydroxyethoxycyclohexane 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,7-heptanediol, 1,8-octanediol, cyclohexanedimethanol, tricyclodecane dimethanol, hydrogenated bisphenol A , Hydrogenated bisphenol F, ethylene oxide adduct of bisphenol A (ethylene oxide addition number of 26 or less), ethylene oxide adduct of bisphenol F (ethylene oxide addition number of 21 or less), hydrogenated bisphenol A ethylene oxide adduct (ethyleneoxy ), Hydrogenated bisphenol F ethylene oxide adduct (ethylene oxide addition number 17 or less), bisphenol A propylene oxide adduct, bisphenol F propylene oxide adduct, hydrogenated bisphenol A propylene oxide Adduct, propylene oxide adduct of hydrogenated bisphenol F, hydroquinone dihydroxyethyl ether, p-xylylene glycol, dihydroxyethyl sulfone, bis (2-hydroxyethyl) -2,4-tolylene dicarbamate, 2,4-tolylene- Examples thereof include bis (2-hydroxyethylcarbamide), bis (2-hydroxyethyl) -m-xylylene dicarbamate, and bis (2-hydroxyethyl) isophthalate.

  Moreover, the polyether diol compound of the compound represented by Formula (A), (B), (C), (D), (E) can also be used suitably.

In the formula, R ₆ represents a hydrogen atom or a methyl group. However, in formula (A), R ₆ represents a methyl group. X represents the following group.

  a, b, c, d, e, f, and g each represent an integer of 2 or more. Preferably it is an integer of 2-100.

  Furthermore, the polyester diol compound represented by Formula (11), (12) can also be mentioned as a specific example.

In the formula, L ₁ , L ₂ and L ₃ may be the same or different and each represents a divalent aliphatic or aromatic hydrocarbon group, and L ₄ represents a divalent aliphatic hydrocarbon group. Preferably, L ₁ , L ₂ and L ₃ each represent an alkylene group, an alkenylene group, an alkynylene group or an arylene group, and L ₄ represents an alkylene group. In L ₁ , L ₂ , L ₃ and L ₄ , there are other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom. May be. n1 and n2 are each an integer of 2 or more, preferably an integer of 2 to 100.

  Furthermore, the polycarbonate diol compound represented by Formula (13) can also be mentioned as a specific example.

In the formula, L ₅ may be the same or different and each represents a divalent aliphatic or aromatic hydrocarbon group. Preferably, L ₅ represents an alkylene group, an alkenylene group, an alkynylene group or an arylene group. In addition, other functional groups that do not react with the isocyanate group, such as ether, carbonyl, ester, cyano, olefin, urethane, amide, ureido group or halogen atom may be present in L ₅ . n3 is an integer of 2 or more, preferably 2 to 1
Indicates an integer of 00.

  Specific examples of the diol compound represented by the formula (11), (12) or (13) include those shown below. N in the specific examples is an integer of 2 or more.

  Furthermore, a diol compound that does not have a carboxyl group and may have another substituent that does not react with isocyanate can also be used.

Examples of such diol compounds include those shown below.
_{HO-L 6 -O-CO-} L 7 -CO-O-L 6 -OH (14)
_{HO-L 7 -CO-O-} L 6 -OH (15)

In the formula, L ₆ and L ₇ may be the same as or different from each other, and a substituent (eg, alkyl, aralkyl, aryl, alkoxy, aryloxy, halogen atom (—F, —Cl, —Br, —I), A divalent aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group which may have a group. If necessary, L ₆ and L ₇ may have another functional group that does not react with an isocyanate group, for example, carbonyl, ester, urethane, amide, ureido group and the like. Note that L ₆ and L ₇ may form a ring.

  Specific examples of the compound represented by the formula (14) or (15) include those shown below.

  Moreover, the diol compound shown below can also be used conveniently.

In the formula, R ₇ and R ₈ may be the same or different, and may be an alkyl group which may have a substituent, preferably cyano, nitro, halogen atom (—F, —Cl, —Br, —I _{), - CONH 2, -COOR,} -OR, ( wherein, R represents may be the same or different from each other,
An alkyl group having 1 to 10 carbon atoms, an aryl group having 7 to 15 carbon atoms, and an aralkyl group are shown. ) And the like, and an alkyl group having 1 to 10 carbon atoms which may have a substituent.

  Specific examples of the diol compound represented by the formula (16) include those shown below.

As the formula (17), 2-butyne-1,4-diol, and as the formula (18), cis-2
-Butene-1,4-diol, trans-2-butene-1,4-diol and the like.
Moreover, the diol compound shown to following formula (19), (20) can also be used conveniently.
_{HO-L 8 -NH-CO-} L 9 -CO-NH-L 8 -OH (19)
_{HO-L 9 -CO-NH-} L 8 -OH (20)

In the formula, L ₈ and L ₉ may be the same as or different from each other, and a substituent (eg, alkyl, aralkyl, aryl, alkoxy, aryloxy, halogen atom (—F, —Cl, —Br, —I), A divalent aliphatic hydrocarbon group, an aromatic hydrocarbon group or a heterocyclic group which may have a group. If necessary, L ₈ and L ₉ may have other functional groups that do not react with isocyanate groups, such as carbonyl, ester, urethane, amide, ureido groups and the like. Note that L ₈ and L ₉ may form a ring.

  Specific examples of the compound represented by the formula (19) or (20) include those shown below.

Furthermore, diol compounds represented by the following formulas (21) and (22) can also be suitably used.
_{HO-Ar 2 - (L 16} -Ar 3) n -OH (21)
_{HO-Ar 2 -L 16 -OH (} 22)

In the formula, L ₁₆ represents a divalent aliphatic hydrocarbon group which may have a substituent (eg, alkyl, aralkyl, aryl, alkoxy, aryloxy and halogeno groups are preferable). If necessary, L ₁₆ may have another functional group that does not react with an isocyanate group, such as an ester, urethane, amide, or ureido group.

Ar ₂ and Ar ₃ may be the same or different and each represents a divalent aromatic hydrocarbon group which may have a substituent, preferably an aromatic group having 6 to 15 carbon atoms. n represents an integer of 0 to 10.
Specific examples of the diol compound represented by the formula (21) or (22) include those shown below.

  That is, catechol, resorcin, hydroquinone, 4-methylcatechol, 4-t-butylcatechol, 4-acetylcatechol, 3-methoxycatechol, 4-phenylcatechol, 4-methylresorcin, 4-ethylresorcin, 4-t-butyl Resorcin, 4-hexyl resorcin, 4-chlororesorcin, 4-benzyl resorcin, 4-acetyl resorcin, 4-carbomethoxy resorcin, 2-methyl resorcin, 5-methyl resorcin, t-butyl hydroquinone, 2,5-di-t -Butylhydroquinone, 2,5-di-t-amylhydroquinone, tetramethylhydroquinone, tetrachlorohydroquinone, methylcarboaminohydroquinone, methylureidohydroquinone, methylthiohydroquinone, benzonor Runene-3,6-diol, bisphenol A, bisphenol S, 3,3′-dichlorobisphenol S, 4,4′-dihydroxybenzophenone, 4,4′-dihydroxybiphenyl, 4,4′-thiodiphenol, 2, 2′-dihydroxydiphenylmethane, 3,4-bis (p-hydroxyphenyl) hexane, 1,4-bis (2- (p-hydroxyphenyl) propyl) benzene, bis (4-hydroxyphenyl) methylamine, 1,3 -Dihydroxynaphthalene, 1,4-dihydroxynaphthalene, 1,5-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 1,5-dihydroxyanthraquinone, 2-hydroxybenzyl alcohol, 4-hydroxybenzyl alcohol, 2-hydroxy-3, 5-di-t-butylbenzyl Alcohol, 4-hydroxy-3,5-di-t-butylbenzyl alcohol, 4-hydroxyphenethyl alcohol, 2-hydroxyethyl-4-hydroxybenzoate, 2-hydroxyethyl-4-hydroxyphenyl acetate, resorcin mono-2- And hydroxyethyl ether. The diol compound shown below can also be used conveniently.

(V) Other amino group-containing compound In the polyurethane resin binder in the present invention, the amino group-containing compound represented by the following formulas (31) and (32) is further combined and reacted with a diisocyanate compound to form a urea structure to form a polyurethane resin. It may be incorporated into the structure.

In the formula, R ₁₀₆ and R _{106 ′} may be the same or different from each other, and may be a hydrogen atom, a substituent (for example, alkoxy, halogen atom (—F, —Cl, —Br, —I), ester, carboxyl group, etc. An alkyl group, an aralkyl group and an aryl group which may have a hydrogen atom, a C 1-8 alkyl which may have a carboxyl group as a substituent, An aryl group having 6 to 15 carbon atoms is shown. L ₁₇ has a substituent (for example, each group such as alkyl, aralkyl, aryl, alkoxy, aryloxy, halogen atom (—F, —Cl, —Br, —I), carboxyl group and the like is included). And a divalent aliphatic hydrocarbon group, aromatic hydrocarbon group or heterocyclic group. If necessary, L ₁₇ may have another functional group that does not react with an isocyanate group, such as a carbonyl, ester, urethane, or amide group. Two of R ₁₀₆ , L ₁₇ and R _{106 ′} may form a ring.

  Specific examples of the compounds represented by the formulas (31) and (32) include those shown below.

  That is, ethylenediamine, propylenediamine, tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, heptamethylenediamine, octamethylenediamine, dodecamethylenediamine, propane-1,2-diamine, bis (3-aminopropyl) methylamine, 1 , 3-bis (3-aminopropyl) tetramethylsiloxane, piperazine, 2,5-dimethylpiperazine, N- (2-aminoethyl) piperazine, 4-amino-2,2-6,6-tetramethylpiperidine, N , N-dimethylethylenediamine, lysine, L-cystine, isophoronediamine, and the like; o-phenylenediamine, m-phenylenediamine, p-phenylenediamine, 2,4-tolylenediamine, benzidine, o- Toluidine, o-dianisidine, 4-nitro-m-phenylenediamine, 2,5-dimethoxy-p-phenylenediamine, bis- (4-aminophenyl) sulfone, 4-carboxy-o-phenylenediamine, 3-carboxy-m -Aromatic diamine compounds such as phenylenediamine, 4,4'-diaminophenyl ether, 1,8-naphthalenediamine, etc .; 2-aminoimidazole, 3-aminotriazole, 5-amino-1H-tetrazole, 4-aminopyrazole 2-aminobenzimidazole, 2-amino-5-carboxy-triazole, 2,4-diamino-6-methyl-S-triazine, 2,6-diaminopyridine, L-histidine, DL-tryptophan, adenine, etc. Heterocyclic amine compounds; ethanolamine, N- Tylethanolamine, N-ethylethanolamine, 1-amino-2-propanol, 1-amino-3-propanol, 2-aminoethoxyethanol, 2-aminothioethoxyethanol, 2-amino-2-methyl-1-propanol P-aminophenol, m-aminophenol, o-aminophenol, 4-methyl-2-aminophenol, 2-chloro-4-aminophenol, 4-methoxy-3-aminophenol, 4-hydroxybenzylamine, 4 -Amino-1-naphthol, 4-aminosalicylic acid, 4-hydroxy-N-phenylglycine, 2-aminobenzyl alcohol, 4-aminophenethyl alcohol, 2-carboxy-5-amino-1-naphthol, L-tyrosine, etc. Such as amino alcohol or amino Lumpur compound.

As the polymer binder of the present invention, in addition to the above-mentioned polyurethane resin obtained by introducing a crosslinkable group into the side chain during the polyurethane synthesis, a polyurethane having a carboxyl group as described in JP-A-2003-270775 is highly effective. Polyurethane resins obtained by introducing crosslinkable groups by molecular reaction can also be used.

  The molecular weight of the polymer binder in the present invention is appropriately determined from the viewpoint of image formability and printing durability. The molecular weight is preferably in the range of 2,000 to 1,000,000, more preferably 5,000 to 500,000, and still more preferably 10,000 to 200,000.

  The polymer binder used in the present invention may be used alone or in combination of two or more. Further, one or more other binder polymers having no crosslinkable group may be used in combination as a mixture. As the binder polymer that can be used in combination, a conventionally known alkali-soluble or swellable binder can be used without limitation, and specifically, an acrylic main chain binder, a urethane binder, or the like often used in the industry is preferably used.

  The total amount of the polymer binder in the photosensitive layer and the binder polymer that may be used in combination can be determined as appropriate, but is usually 10 to 90% by mass with respect to the total mass of nonvolatile components in the photosensitive layer. , Preferably it is 20-80 mass%, More preferably, it is the range of 30-70 mass%.

[Sensitizing dye]
The photosensitive layer of the present invention can contain a sensitizing dye corresponding to the wavelength of the exposure light source in addition to the above-described essential components.
First, a sensitizing dye having an absorption maximum in the wavelength range of 300 nm to 500 nm will be described. Examples of such a sensitizing dye include merocyanine dyes represented by the following general formula (V), benzopyrans and coumarins represented by the following general formula (VI), and fragrances represented by the following general formula (VII). And anthracenes represented by the following general formula (VIII).

(In the formula, A represents an S atom or NR ₆ , R ₆ represents a monovalent non-metallic atomic group, Y represents a basic nucleus of the dye in cooperation with the adjacent A and the adjacent carbon atom. A non-metallic atomic group, X ₁ and X ₂ each independently represent a monovalent non-metallic atomic group, and X ₁ and X ₂ may combine with each other to form an acidic nucleus of the dye.)

(In the formula, = Z represents a carbonyl group, a thiocarbonyl group, an imino group or an alkylidene group represented by the partial structural formula (1 ′), and X ₁ and X ₂ have the same meanings as in the general formula (V). R _{7 to} R ₁₂ each independently represents a monovalent nonmetallic atomic group.)

(In the formula, Ar ₃ represents an aromatic group or a heteroaromatic group which may have a substituent, and R ₁₃ represents a monovalent nonmetallic atomic group. More preferred R ₁₃ represents an aromatic group or It is a heteroaromatic group, and Ar ₃ and R ₁₃ may be bonded to each other to form a ring.)

(In the formula, X ₃ , X ₄ and R _{14 to} R ₂₁ each independently represent a monovalent non-metallic atomic group, and more preferable X ₃ and X ₄ are electron donating groups having a negative Hammett's substituent constant. .)

In the general formulas (V) to (VIII), preferred examples of the monovalent nonmetallic atomic group represented by X ₁ to X ₄ and R ₆ to R ₂₁ include a hydrogen atom, an alkyl group (for example, a methyl group, Ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, hexadecyl group, octadecyl group, eicosyl group, isopropyl group, isobutyl group , S-butyl group, t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group, 2-norbornyl group, chloromethyl group , Bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxymethyl group, methoxyethoxy Ethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-cyclohexylcarbamoyloxyethyl Group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, allyloxycarbonylbutyl group, chloro Phenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl Tyl-N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoyl group Propyl group, N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphine group Onatobutyl group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonatoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p-methylbenzyl group, Namyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc.), aryl group (for example , Phenyl group, biphenyl group, naphthyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, Acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylaminophenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, Phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group, cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl group, phosphonatophenyl group, etc.), heteroaryl group (for example, thiophene, Thiathrene, furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indoyl, indazole, purine, quinolidine, isoquinoline, Phthalazine, naphthyridine, quinazoline, cynoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthroline, phthalazine, phenazazine, fu Noxazine, furazane, phenoxazine, etc.), alkenyl groups (eg, vinyl, 1-propenyl, 1-butenyl, cinnamyl, 2-chloro-1-ethenyl, etc.), alkynyl (eg, ethynyl, 1 -Propynyl group, 1-butynyl group, trimethylsilylethynyl group, etc.), halogen atom (-F, -Br, -Cl, -I), hydroxyl group, alkoxy group, aryloxy group, mercapto group, alkylthio group, arylthio group, alkyl Dithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group, N-alkyl-N-arylamino group, acyloxy group , Carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamo Ruoxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, arylsulfoxy group, acylthio group, acylamino group, N- Alkylacylamino group, N-arylacylamino group, ureido group, N′-alkylureido group, N ′, N′-dialkylureido group, N′-arylureido group, N ′, N′-diarylureido group, N '-Alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido group, N'-alkyl-N-arylureido group, N', N ' -Dialkyl-N-alkylureido groups, N ', N'-dialkyl-N-arylureido groups N'-aryl-N-alkylureido group, N'-aryl-N-arylureido group, N ', N'-diaryl-N-alkylureido group, N', N'-diaryl-N-arylureido group N'-alkyl-N'-aryl-N-alkylureido group, N'-alkyl-N'-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl-N- Alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, formyl group, acyl group, carboxyl group, alkoxy Carbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkyl group Vamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkylsulfinyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group , Sulfo group (—SO ₃ H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N-alkylsulfinamoyl group, N, N-dialkylsulfina Moyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfur group Famoyl group, N-ary A sulfamoyl group, N, N- diaryl sulfamoyl group, N- alkyl -N- arylsulfamoyl group, a phosphono group (-PO ₃ H ₂₎ and its conjugated base group (hereinafter referred to as phosphonato group), dialkyl Phono group (—PO ₃ (alkyl) ₂ ), diaryl phosphono group (—PO ₃ (aryl) ₂ ), alkylaryl phosphono group (—PO ₃ (alkyl) (aryl)), monoalkyl phosphono group (— PO ₃ H (alkyl)) and its conjugate base group (hereinafter referred to as alkyl phosphonate group), monoaryl phosphono group (—PO ₃ H (aryl)) and its conjugate base group (hereinafter referred to as aryl phosphonate group) referred), phosphonooxy group (-OPO ₃ H ₂₎ and its conjugated base group (hereinafter referred to as phosphonophenyl group), dialkyl phosphonooxy group (-OPO ₃ (alkyl) _2), di Reel phosphonooxy group _{(-OPO 3 (aryl) 2)} , alkylaryl phosphonooxy group _{(-OPO 3 (alkyl) (aryl} )), monoalkyl phosphonooxy group (-OPO ₃ H (alkyl)) and its A conjugated base group (hereinafter referred to as an alkylphosphonatooxy group), a monoarylphosphonooxy group (—OPO ₃ H (aryl)) and a conjugated base group (hereinafter referred to as an arylphosphonatooxy group), a cyano group, A nitro group, and the like. Among these substituents, a hydrogen atom, an alkyl group, an aryl group, a halogen atom, an alkoxy group, and an acyl group are particularly preferable.

  Examples of the basic nucleus of the dye formed together with A adjacent to Y in the general formula (V) and the adjacent carbon atom include 5-, 6-, and 7-membered nitrogen-containing or sulfur-containing heterocycles. A 5- or 6-membered heterocyclic ring is preferable.

Examples of nitrogen-containing heterocycles constitute the basic nucleus in merocyanine dyes described in, for example, LGBrooker et al., J. Am. Chem. Soc., 73, 5326-5358 (1951). Any known material can be suitably used. Specific examples include thiazoles (for example, thiazole, 4-methylthiazole, 4-phenylthiazole, 5-methylthiazole, 5-phenylthiazole, 4,5-dimethylthiazole, 4,5-diphenylthiazole, 4,5- Di (p-methoxyphenylthiazole), 4- (2-thienyl) thiazole, etc.), benzothiazoles (for example, benzothiazole, 4-chlorobenzothiazole, 5-chlorobenzothiazole, 6-chlorobenzothiazole, 7- Chlorobenzothiazole, 4-methylbenzothiazole, 5-methylbenzothiazole, 6-methylbenzothiazole, 5-bromobenzothiazole, 4-phenylbenzothiazole, 5-phenylbenzothiazole, 4-methoxybenzothiazole, 5-methoxybenzo Cheer , 6-methoxybenzothiazole, 5-iodobenzothiazole, 6-iodobenzothiazole, 4-ethoxybenzothiazole, 5-ethoxybenzothiazole, tetrahydrobenzothiazole, 5,6-dimethoxybenzothiazole, 5,6-di Oxymethylenebenzothiazole, 5-hydroxybenzothiazole, 6-hydroxybenzothiazole, 6-dimethylaminobenzothiazole, 5-ethoxycarbonylbenzothiazole, etc.), naphthothiazoles (for example, naphtho [1,2] thiazole, naphtho [2 , 1] thiazole, 5-methoxynaphtho [2,1] thiazole, 5-ethoxynaphtho [2,1] thiazole, 8-methoxynaphtho [1,2] thiazole, 7-methoxynaphtho [1,2] thiazole, etc.) , Chianafuteno 7 ′, 6 ′, 4,5-thiazole (for example, 4′-methoxythianaphtheno-7 ′, 6 ′, 4,5-thiazole, etc.), oxazole (for example, 4-methyloxazole, 5-methyloxazole) 4-phenyloxazole, 4,5-diphenyloxazole, 4-ethyloxazole, 4,5-dimethyloxazole, 5-phenyloxazole, etc.), benzoxazoles (benzoxazole, 5-chlorobenzoxazole, 5-methylbenzoxazole) , 5-phenylbenzoxazole, 6-methylbenzoxazole, 5,6-dimethylbenzoxazole, 4,6-dimethylbenzoxazole, 6-methoxybenzoxazole, 5-methoxybenzoxazole, 4-ethoxybenzoxazole, 5-chloro Benzoki Sol, 6-methoxybenzoxazole, 5-hydroxybenzoxazole, 6-hydroxybenzoxazole, etc.), naphthoxazoles (eg, naphtho [1,2] oxazole, naphtho [2,1] oxazole, etc.), selenazoles (eg, , 4-methylselenazole, 4-phenylselenazole, etc.), benzoselenazoles (for example, benzoselenazole, 5-chlorobenzoselenazole, 5-methoxybenzoselenazole, 5-hydroxybenzoselenazole, tetrahydrobenzoselena) Sol etc.), naphthoselenazoles (eg naphtho [1,2] selenazole, naphtho [2,1] selenazole etc.), thiazolines (eg thiazoline, 4-methylthiazoline etc.), 2-quinolines (eg Quinoline, 3-methyl Norin, 5-methylquinoline, 7-methylquinoline, 8-methylquinoline, 6-chloroquinoline, 8-chloroquinoline, 6-methoxyquinoline, 6-ethoxyquinoline, 6-hydroxyquinoline, 8-hydroxyquinoline, etc.), 4 -Quinolines (eg, quinoline, 6-methoxyquinoline, 7-methylquinoline, 8-methylquinoline, etc.), 1-isoquinolines (eg, isoquinoline, 3,4-dihydroisoquinoline, etc.), 3-isoquinolines (eg, , Isoquinoline, etc.), benzimidazoles (eg, 1,3-diethylbenzimidazole, 1-ethyl-3-phenylbenzimidazole, etc.), 3,3-dialkylindolenins (eg, 3,3-dimethylindolenin, 3,3,5, -trimethylindolenine, 3,3,7,- Trimethylindolenine etc.), 2-pyridines (eg pyridine, 5-methylpyridine etc.), 4-pyridine (eg pyridine etc.) and the like.

Examples of the sulfur-containing heterocycle include a dithiol partial structure in dyes described in JP-A-3-296759.
Specific examples include benzodithiols (for example, benzodithiol, 5-t-butylbenzodithiol, 5-methylbenzodithiol, etc.), naphthodithiols (for example, naphtho [1,2] dithiol, naphtho [2,1] Dithiol etc.), dithiols (for example, 4,5-dimethyldithiols, 4-phenyldithiols, 4-methoxycarbonyldithiols, 4,5-dimethoxycarbonylbenzodithiols, 4,5-ditrifluoromethyldithiol, 4 , 5-dicyanodithiol, 4-methoxycarbonylmethyldithiol, 4-carboxymethyldithiol and the like.

As mentioned above, for the sake of convenience, the description used in the description of the heterocyclic ring has conventionally used the name of the heterocyclic mother skeleton, but when forming the basic skeleton partial structure of the sensitizing dye, for example, in the case of the benzothiazole skeleton It is introduced in the form of an alkylidene type substituent with one degree of unsaturation, such as a 3-substituted-2 (3H) -benzothiazolidene group.

  Of the sensitizing dyes having an absorption maximum in a wavelength range of 360 nm to 450 nm, a dye more preferable from the viewpoint of high sensitivity is a dye represented by the following general formula (IX).

(In the general formula (IX), A represents an aromatic ring or a hetero ring which may have a substituent, and X represents an oxygen atom, a sulfur atom or N- (R ₃ ). R ₁ , R ₂ and R ₃ each independently represents a hydrogen atom or a monovalent nonmetallic atomic group, and A and R ₁ and R ₂ and R ₃ are bonded to each other to form an aliphatic or aromatic ring. May be.)

General formula (IX) will be described in more detail. R ₁ , R ₂ and R ₃ are each independently
A hydrogen atom or a monovalent nonmetallic atomic group, preferably a substituted or unsubstituted alkyl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted aryl group, a substituted or unsubstituted aromatic heterocyclic ring It represents a residue, a substituted or unsubstituted alkoxy group, a substituted or unsubstituted alkylthio group, a hydroxyl group, or a halogen atom.

Preferable examples of R ₁ , R ₂ and R ₃ will be specifically described. Examples of preferable alkyl groups include linear, branched, and cyclic alkyl groups having 1 to 20 carbon atoms. Specific examples thereof include a methyl group, an ethyl group, a propyl group, Butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, hexadecyl, octadecyl, eicosyl, isopropyl, isobutyl, s-butyl, Examples thereof include t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group and 2-norbornyl group. Of these, linear alkyl groups having 1 to 12 carbon atoms, branched alkyl groups having 3 to 12 carbon atoms, and cyclic alkyl groups having 5 to 10 carbon atoms are more preferable.

As the substituent of the substituted alkyl group, a monovalent nonmetallic atomic group excluding hydrogen is used, and preferred examples include a halogen atom (—F, —Br, —Cl, —I), a hydroxyl group, an alkoxy group, Aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, Reelsulfoxy group, acylthio group, acylamino group, N-alkylacylamino group, N-arylacylamino group, ureido group, N'-alkylureido group, N ', N'-dialkylureido group, N'-arylureido Group, N ′, N′-diarylureido group, N′-alkyl-N′-arylureido group, N-alkylureido group, N-arylureido group, N′-alkyl-N-alkylureido group, N′- Alkyl-N-arylureido group, N ', N'-dialkyl-N-alkylureido group, N', N'-dialkyl-N-arylureido group, N'-aryl-N-alkylureido group, N'- Aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-ary Luureido group, N′-alkyl-N′-aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl- N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, formyl group, acyl group, carboxyl group , Alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group , Alkylsul Finyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group, sulfo group (—SO ₃ H) and its conjugate base group (hereinafter referred to as sulfonate group), alkoxysulfonyl group, aryloxysulfonyl group, sulfinamoyl group, N -Alkylsulfinamoyl group, N, N-dialkylsulfinamoyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N-arylsulfamoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (-PO ₃ H ₂₎ and its conjugated base group (hereinafter, phospho Referred to as bets group), dialkyl phosphono group _{(-PO 3 (alkyl) 2)} , diaryl phosphono group _{(-PO 3 (aryl) 2)} , alkyl aryl phosphono group _{(-PO 3 (alkyl) (aryl} )) , Monoalkylphosphono group (—PO ₃ H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonate group), monoarylphosphono group (—PO ₃ H (aryl)) and its conjugate base group (Hereinafter referred to as arylphosphonate group), phosphonooxy group (—OPO ₃ H ₂ ) and its conjugate base group (hereinafter referred to as phosphonateoxy group), dialkylphosphonooxy group (—OPO ₃ (alkyl)) ₂ ), diarylphosphonooxy group (—OPO ₃ (aryl) ₂ ), alkylarylphosphonooxy group (—OPO ₃ (alkyl) (aryl)), monoalkylphosphonooxy group (—OPO ₃ H (alkyl)) )and The conjugated base group (hereinafter referred to as alkyl phosphonophenyl group), monoaryl phosphonooxy group (-OPO ₃ H (aryl)) and its conjugated base group (hereinafter referred to as aryl phosphite Hona preparative group), a cyano group , A nitro group, an aryl group, a heteroaryl group, an alkenyl group, and an alkynyl group.

  Specific examples of the alkyl group in these substituents include the above-described alkyl groups, and specific examples of the aryl group include a phenyl group, a biphenyl group, a naphthyl group, a tolyl group, a xylyl group, a mesityl group, and a cumenyl group. , Chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylamino Phenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group Cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl phenyl group, phosphonophenyl phenyl group and the like.

As the preferred heteroaryl group as R ₁ , R ₂ and R ₃ , a monocyclic or polycyclic aromatic ring containing at least one of nitrogen, oxygen and sulfur atoms is used. Examples of particularly preferred heteroaryl groups Is, for example, thiophene, thiathrene, furan, pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indolizine, indazole, indazole, Purine, quinolidine, isoquinoline, phthalazine, naphthyridine, quinazoline, sinoline, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthrolin, phthalazine, phenalazine, phenoxazine, flaza And phenoxazine and the like. These may be further benzo-fused and may have a substituent.

Examples of preferred alkenyl groups for R ₁ , R ₂ and R ₃ include vinyl groups, 1-
A propenyl group, a 1-butenyl group, a cinnamyl group, a 2-chloro-1-ethenyl group, and the like. Examples of the alkynyl group include an ethynyl group, a 1-propynyl group, a 1-butynyl group, and a trimethylsilylethynyl group. Can be mentioned. Examples of G ₁ in the acyl group (G ₁ CO—) include hydrogen and the above alkyl groups and aryl groups. Of these substituents, halogen atoms (—F, —Br, —Cl, —I), alkoxy groups, aryloxy groups, alkylthio groups, arylthio groups, N-alkylamino groups, N, N— Dialkylamino group, acyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, acylamino group, formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, sulfo group, sulfonate group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group Group, N-arylsulfa Yl group, N-alkyl-N-arylsulfamoyl group, phosphono group, phosphonate group, dialkyl phosphono group, diaryl phosphono group, monoalkyl phosphono group, alkyl phosphonate group, monoaryl phosphono group, aryl phosphine group Examples include an onato group, a phosphonooxy group, a phosphonateoxy group, an aryl group, and an alkenyl group.

  On the other hand, examples of the alkylene group in the substituted alkyl group include divalent organic residues obtained by removing any one of the hydrogen atoms on the alkyl group having 1 to 20 carbon atoms. Can include linear alkylene groups having 1 to 12 carbon atoms, branched chains having 3 to 12 carbon atoms, and cyclic alkylene groups having 5 to 10 carbon atoms.

Specific examples of preferable substituted alkyl groups as R ₁ , R ₂ and R ₃ obtained by combining the substituent and the alkylene group include chloromethyl group, bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxy Methyl group, methoxyethoxyethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group, tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N -Cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbo Nylethyl group, allyloxycarbonylbutyl group, chlorophenoxycarbonylmethyl group, carbamoylmethyl group, N-methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl- N- (sulfophenyl) carbamoylmethyl group, sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group N-methyl-N- (phosphonophenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobu Group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, phosphonateoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p -Methylbenzyl group, cinnamyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, etc. Can be mentioned.

Specific examples of preferred aryl groups as R ₁ , R ₂ and R ₃ include those in which 1 to 3 benzene rings form a condensed ring, and those in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Specific examples include a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, and a fluorenyl group. Among these, a phenyl group and a naphthyl group are more preferable. .

Specific examples of preferred substituted aryl groups as R ₁ , R ₂ and R ₃ include those having a monovalent non-metallic atomic group excluding hydrogen as a substituent on the ring-forming carbon atom of the aryl group described above. . Examples of preferred substituents include the aforementioned alkyl groups, substituted alkyl groups, and those previously shown as substituents in the substituted alkyl group. Preferred examples of such a substituted aryl group include a biphenyl group, a tolyl group, a xylyl group, a mesityl group, a cumenyl group, a chlorophenyl group, a bromophenyl group, a fluorophenyl group, a chloromethylphenyl group, and a trifluoromethylphenyl group. Hydroxyphenyl group, methoxyphenyl group, methoxyethoxyphenyl group, allyloxyphenyl group, phenoxyphenyl group, methylthiophenyl group, tolylthiophenyl group, ethylaminophenyl group, diethylaminophenyl group, morpholinophenyl group, acetyloxyphenyl group, Benzoyloxyphenyl group, N-cyclohexylcarbamoyloxyphenyl group, N-phenylcarbamoyloxyphenyl group, acetylaminophenyl group, N-methylbenzoylaminophenyl group, carbo Cyphenyl group, methoxycarbonylphenyl group, allyloxycarbonylphenyl group, chlorophenoxycarbonylphenyl group, carbamoylphenyl group, N-methylcarbamoylphenyl group, N, N-dipropylcarbamoylphenyl group, N- (methoxyphenyl) carbamoylphenyl group N-methyl-N- (sulfophenyl) carbamoylphenyl group, sulfophenyl group, sulfonatophenyl group, sulfamoylphenyl group, N-ethylsulfamoylphenyl group, N, N-dipropylsulfamoylphenyl group, N-tolylsulfamoylphenyl group, N-methyl-N- (phosphonophenyl) sulfamoylphenyl group, phosphonophenyl group, phosphonatophenyl group, diethylphosphonophenyl group, diphenylphosphono Enyl group, methylphosphonophenyl group, methylphosphonatophenyl group, tolylphosphonophenyl group, tolylphosphonatophenyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallylphenyl group, 2- Examples thereof include a methylpropenylphenyl group, a 2-propynylphenyl group, a 2-butynylphenyl group, and a 3-butynylphenyl group.

Next, A in the general formula (IX) will be described. A represents an aromatic ring or a hetero ring which may have a substituent. Specific examples of the aromatic ring or hetero ring which may have a substituent include R ₁ and R in the general formula (IX). similar to those described in ₂ and R ₃ can be exemplified.

  The sensitizing dye represented by the general formula (IX) of the present invention includes an acidic nucleus as shown above, an acidic nucleus having an active methylene group, a substituted or unsubstituted aromatic ring or heterocyclic ring, and These can be synthesized by referring to Japanese Patent Publication No. 59-28329.

  Preferred specific examples (D1) to (D38) of the compound represented by the general formula (IX) are shown below. In addition, an isomer with a double bond connecting an acidic nucleus and a basic nucleus is not limited to either isomer.

  The addition amount of the sensitizing dye is preferably 0.05 to 30% by mass, more preferably 0.1 to 20% by mass, and still more preferably 0.2 to 10% by mass with respect to the total solid content constituting the photosensitive layer. It is.

[Thermal polymerization inhibitor]
In the present invention, a small amount of a thermal polymerization inhibitor is added to prevent unnecessary thermal polymerization of the polymerizable ethylenically unsaturated bond-containing compound during the production or storage of the photosensitive lithographic printing plate. Is desirable. Suitable thermal polymerization inhibitors include haloid quinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4-thiobis (3-methyl-6-t-butylphenol) 2,2′-methylenebis (4-methyl-6-tert-butylphenol), N-nitrosophenylhydroxylamine primary cerium salt, N-nitrosophenylhydroxylamine aluminum salt and the like.
The amount of the thermal polymerization inhibitor added is about 0.01% by mass to about 5% with respect to the total solid content constituting the photosensitive layer.
Mass% is preferred.

[Other additives]
If necessary, a higher fatty acid derivative such as behenic acid or behenic acid amide is added to the photosensitive layer of the present invention to prevent polymerization inhibition due to oxygen, and the surface of the photosensitive layer is dried during the coating process. May be unevenly distributed. The addition amount of the higher fatty acid derivative or the like is preferably about 0.5% by mass to about 10% by mass with respect to the total solid content constituting the photosensitive layer.
Further, a coloring agent may be added for the purpose of coloring the photosensitive layer. Examples of the colorant include phthalocyanine pigments (CIPigment Blue 15: 3, 15: 4, 15: 6, etc.), azo pigments, pigments such as carbon black and titanium oxide, ethyl violet, crystal violet, azo dyes, anthraquinones. There are dyes and cyanine dyes. The addition amount of the dye and the pigment is preferably about 0.5% by mass to about 20% by mass based on the total solid content of the photosensitive layer. In addition, in order to improve the physical properties of the cured film, an additive such as an inorganic filler or a plasticizer such as dioctyl phthalate, dimethyl phthalate, or tricresyl phosphate may be added. These addition amounts are preferably 10% by mass or less based on the total solid content of the photosensitive layer.

[Support]
As the hydrophilic support of the present invention, a conventionally known hydrophilic support used in a lithographic printing plate can be used without limitation. The support used is preferably a dimensionally stable plate, for example, paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum, zinc). , Copper, etc.), plastic films (for example, cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.) Paper or plastic film, etc., laminated or vapor-deposited with such metals is included, and appropriate physical and chemical treatments are applied to these surfaces for the purpose of imparting hydrophilicity and improving strength as necessary. You may give it.

  In particular, preferred supports include paper, polyester film or aluminum plate, among which dimensional stability is good, relatively inexpensive, and a surface with excellent hydrophilicity and strength is provided by surface treatment as required. An aluminum plate which can be used is particularly preferred. A composite sheet in which an aluminum sheet is bonded on a polyethylene terephthalate film as described in Japanese Patent Publication No. 48-18327 is also preferable.

  The aluminum substrate is a metal plate mainly composed of dimensionally stable aluminum. In addition to a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of foreign elements, or aluminum (alloy) is laminated or Selected from vapor-deposited plastic film or paper.

In the following description, the above-mentioned substrates made of aluminum or an aluminum alloy are generically used as an aluminum substrate. Examples of the foreign element contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of the foreign element in the alloy is 10% by mass or less. In the present invention, a pure aluminum plate is suitable, but since completely pure aluminum is difficult to manufacture in the refining technique, it may contain a slightly different element.
Thus, the composition of the aluminum plate applied to the present invention is not specified, and conventionally known and used materials such as JIS A 1050, JIS A 1100, JIS A 3103, and JIS A 3005 are appropriately used. It can be used. The thickness of the aluminum substrate used in the present invention is about 0.1 mm to 0.6 mm, preferably 0.15 mm to 0.4 mm, particularly preferably 0.2 mm to 0.3 mm. This thickness can be appropriately changed according to the size of the printing press, the size of the printing plate, and the user's desire. The aluminum substrate may be subjected to a substrate surface treatment described later as necessary. Of course, it may not be applied.

The aluminum substrate is usually roughened. Examples of the roughening treatment method include mechanical roughening, chemical etching, and electrolytic grain as disclosed in JP-A-56-28893. Electrochemical roughening method that further electrochemically roughens in hydrochloric acid or nitric acid electrolyte solution, and a wire brush grain method in which the aluminum surface is scratched with a metal wire, and a pole in which the aluminum surface is grained with a polishing ball and an abrasive. A mechanical roughening method such as a grain method or a brush grain method in which the surface is roughened with a nylon brush and an abrasive can be used, and the above roughening methods can be used alone or in combination. Among them, a method usefully used for roughening is an electrochemical method in which roughening is chemically carried out in hydrochloric acid or nitric acid electrolyte, and a suitable anodic electricity is 50 C / dm ^{2 to} 400 C / dm ² . It is a range. More specifically, in the electrolytic solution containing from 0.1 to 50% by weight hydrochloric acid or nitric acid, the temperature 20 to 80 ° C., for 1 second to 30 minutes, at a current density of 100C / dm ² ~400C / dm ² It is preferable to perform alternating current and / or direct current electrolysis.

  The roughened aluminum substrate may be chemically etched with acid or alkali. Etching agents suitably used are caustic soda, sodium carbonate, sodium aluminate, sodium metasilicate, sodium phosphate, potassium hydroxide, lithium hydroxide, etc., and preferred ranges of concentration and temperature are 1 to 50% by mass, 20 to 100 ° C. Pickling is performed to remove dirt (smut) remaining on the surface after etching. As the acid used, nitric acid, sulfuric acid, phosphoric acid, chromic acid, hydrofluoric acid, borohydrofluoric acid and the like are used. In particular, as a method for removing smut after the electrochemical surface roughening treatment, it is preferably brought into contact with 15 to 65 mass% sulfuric acid at a temperature of 50 to 90 ° C. as described in JP-A-53-12739. Examples thereof include an alkali etching method described in Japanese Patent Publication No. 48-28123. After the processing as described above, the method condition is not particularly limited as long as the center line average group Ra Ra of the processing surface is 0.2 to 0.5 μm.

The aluminum substrate that has been roughened as described above is then anodized to form an oxide film. In the anodizing treatment, sulfuric acid, phosphoric acid, oxalic acid, or an aqueous solution of boric acid / sodium borate is used alone or in combination as a main component of an electrolytic bath. In this case, the electrolyte solution may of course contain at least components normally contained in at least an Al alloy plate, an electrode, tap water, groundwater and the like. Further, the second and third components may be added. Here, the second and third components are, for example, metal ions such as Na, K, Mg, Li, Ca, Ti, Al, V, Cr, Mn, Fe, Co, Ni, Cu, and Zn, and ammonium ions. Examples include cations, nitrate ions, carbonate ions, chloride ions, phosphate ions, fluorine ions, sulfite ions, titanate ions, silicate ions, borate ions and the like, and the concentration is 0 to 10,000 ppm. May be included. There are no particular limitations on the conditions for the anodizing treatment, but the treatment is preferably performed by direct current or alternating current electrolysis at a treatment liquid temperature of 10 to 70 ° C. and a current density of 0.1 to 40 A / m ² at 30 to 500 g / liter. . The thickness of the formed anodic oxide film is in the range of 0.5 to 1.5 μm. Preferably it is the range of 0.5-1.0 micrometer.

  Further, after these treatments, a water-soluble resin such as polyvinyl phosphonic acid, a polymer or copolymer having a sulfo group in the side chain, polyacrylic acid, a water-soluble metal salt (for example, zinc borate) or yellow Also suitable are those primed with dyes, amine salts and the like. Further, a sol-gel treated substrate in which a functional group capable of causing an addition reaction by a radical as disclosed in JP-A-7-159983 is covalently used.

  As another preferred example, a substrate provided with a water-resistant hydrophilic layer as a surface layer on an arbitrary support can be raised. Examples of such a surface layer include a layer composed of an inorganic pigment and a binder described in US Pat. No. 3,055,295 and JP-A-56-13168, and a hydrophilic swelling described in JP-A-9-80744. A layer, a sol-gel film made of titanium oxide, polyvinyl alcohol, silicic acid or the like described in JP-A-8-507727 can be raised. These hydrophilic treatments are performed to make the surface of the support hydrophilic, in order to prevent harmful reactions of the photosensitive layer provided thereon, and to improve the adhesion of the photosensitive layer, etc. It is to be given.

[Middle layer]
The photosensitive lithographic printing plate according to the invention may be provided with an intermediate layer for the purpose of improving adhesion between the photosensitive layer and the support and soiling. Specific examples of such an intermediate layer include JP-B-50-7481, JP-A-54-72104, JP-A-59-101651, JP-A-60-149491, JP-A-60-232998, JP-A-3-56177, JP-A-4-282737, JP-A-5-16558, JP-A-5-246171, JP-A-7-159983, JP-A-7-314937, JP-A-8-202025, Special Kaihei 8-320551, JP 9-34104, JP 9-236911, JP 9-269593, JP 10-69092, JP 10-115931, JP 10-161317, JP 10-260536, JP-A-10-282682, JP-A-11-84684, JP-A-11-38635, JP-A-11-38629, JP 10-282645, JP 10-301262, JP 11-24277, JP 11-109641, JP 10-319600, JP 11-327152, JP 2000-10292, JP Examples described in JP 2000-235254 A, JP 2000-352824 A, JP 2001-209170 A, and the like.

[Coating solution]
In coating the photosensitive layer, the above components are dissolved in a solvent to prepare a coating solution. Solvents used here include acetone, methyl ethyl ketone, cyclohexane, ethyl acetate, ethylene dichlorite, tetrahydrofuran, toluene, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol dimethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether. , Acetylacetone, cyclohexanone, diacetone alcohol, ethylene glycol monomethyl ether acetate, ethylene glycol ethyl ether acetate, ethylene glycol monoisopropyl ether, ethylene glycol monobutyl ether acetate, 3-methoxypropanol, methoxymethoxyethanol, diethylene glycol monomethyl ether, di Ethylene glycol monoethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate-3-methoxypropyl acetate, N, N-dimethylformamide, dimethyl sulfoxide, γ-butyrolactone, methyl lactate, lactic acid There are organic solvents such as ethyl. These solvents can be used alone or in combination.
The density | concentration of the solid content in a coating solution is 1-50 mass% normally.

  In addition, a surfactant can be added to improve the coating surface quality.

The coating amount of the photosensitive layer is the mass after drying, and is usually about 0.1 to about 10 g / m ² , preferably 0.3 to
5 g / m ^2, more preferably from 0.5 to 3 g / m ^2.

[Protective layer (oxygen barrier layer)]
In the photosensitive lithographic printing plate of the present invention, it is preferable to provide a protective layer (oxygen blocking layer) on the photosensitive layer in order to block the diffusion and penetration of oxygen that hinders the polymerization reaction during exposure. The protective layer used in the present invention has an oxygen permeability A at 25 ° C. and 1 atm of 1.0 ≦ A ≦ 20 (cc / m ² · da
y) is preferred. If the oxygen permeability A is less than 1.0 (cc / m ² · day) and is extremely low, unnecessary polymerization reaction may occur during production and raw storage, and unnecessary fogging and image lines may occur during image exposure. The problem that fatness arises arises. Conversely, when the oxygen permeability A exceeds 20 (cc / m ² · day) and is too high, the sensitivity is lowered. In addition to the oxygen permeability described above, the properties desired for the protective layer further do not substantially impede the transmission of light used for exposure, have excellent adhesion to the photosensitive layer, and are easy in the development process after exposure. It is desirable that it can be removed. Such a protective layer has been conventionally devised and described in detail in US Pat. No. 3,458,311 and Japanese Patent Publication No. 55-49729.

  As a material that can be used for the protective layer, for example, a water-soluble polymer compound having relatively excellent crystallinity is preferably used. Specifically, polyvinyl alcohol, vinyl alcohol / vinyl phthalate copolymer, vinyl acetate / vinyl are used. Examples include water-soluble polymers such as alcohol / vinyl phthalate copolymer, vinyl acetate / crotonic acid copolymer, polyvinyl pyrrolidone, acidic celluloses, gelatin, gum arabic, polyacrylic acid, and polyacrylamide. Or they can be mixed. Of these, the use of polyvinyl alcohol as the main component gives the best results in terms of basic properties such as oxygen barrier properties and development removability.

The polyvinyl alcohol used for the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains an unsubstituted vinyl alcohol unit for having necessary oxygen barrier properties and water solubility. Similarly, some of them may have other copolymer components. Specific examples of polyvinyl alcohol include those that are hydrolyzed by 71 to 100 mol% and have a polymerization repeating unit in the range of 300 to 2400. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA
-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405 , PVA-420, PVA-613, L-8 and the like, and these can be used alone or in combination. As a preferable aspect, the content rate in the protective layer of polyvinyl alcohol is 20-95 mass%, More preferably, it is 30-90 mass%.

  As a component used by mixing with polyvinyl alcohol, polyvinyl pyrrolidone or a modified product thereof is preferable from the viewpoint of oxygen barrier properties and development removability, and the content in the protective layer is 3.5 to 80% by mass, preferably 10 to 60%. It is 15 mass%, More preferably, it is 15-30 mass%.

Components of the protective layer (selection of PVA, use of additives), coating amount, and the like are selected in consideration of fogging, adhesion, and scratch resistance in addition to oxygen barrier properties and development removability. In general, the higher the hydrolysis rate of the PVA used (the higher the content of the unsubstituted vinyl alcohol unit in the protective layer), the thicker the film thickness, the higher the oxygen barrier property, which is advantageous in terms of sensitivity. However, when the oxygen barrier property is extremely increased, there arises a problem that unnecessary polymerization reaction occurs during production and raw storage, and unnecessary fogging and image line thickening occur during image exposure. The oxygen permeability A of the protective layer in the present invention at 25 ° C. and 1 atm must be 1.0 ≦ A ≦ 20 (cc / m ² · day), preferably 1.5 ≦ A ≦ 12 ( cc / m ² · day), more preferably 2.0 ≦ A ≦ 8.0 (cc / m ² · day). The molecular weight of the (co) polymer such as polyvinyl alcohol (PVA) can be in the range of 2000 to 10 million, preferably in the range of 20,000 to 3 million.

  As another composition of the protective layer, glycerin, dipropylene glycol and the like can be added in an amount corresponding to several mass% with respect to the (co) polymer to provide flexibility. Anionic surfactants such as sodium acid salts; amphoteric surfactants such as alkylaminocarboxylates and alkylaminodicarboxylates; nonionic surfactants such as polyoxyethylene alkylphenyl ethers to the (co) polymer Mass% can be added. The thickness of the protective layer is suitably 0.5 to 5 μm, particularly 1 to 3 μm.

  In addition, adhesion to the image area and scratch resistance are extremely important in handling the plate. That is, when a hydrophilic layer made of a water-soluble polymer is laminated on an oleophilic polymer layer, film peeling due to insufficient adhesion tends to occur, and the peeled part causes defects such as poor film hardening due to inhibition of oxygen polymerization. On the other hand, various proposals have been made to improve the adhesion between these two layers. For example, in U.S. Patent Application No. 292,501 and U.S. Patent Application No. 44,563, an acrylic emulsion or a water-insoluble vinyl pyrrolidone-vinyl acetate copolymer is contained in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesiveness can be obtained by mixing 20 to 60% by mass and laminating on a polymerization layer. Any of these known techniques can be applied to the protective layer in the present invention. Such a coating method for the protective layer is described in detail in, for example, US Pat. No. 3,458,311 and Japanese Patent Publication No. 55-49729.

The coating amount of the protective layer is generally 0.1 to 10 g / m ² as a dry mass, preferably 0.00.
5 to 5 g / m ² .

[Developer]
Below, the developing solution used for the plate making method of this invention is demonstrated.
The developer used in the plate making method of the photosensitive lithographic printing plate of the present invention is not particularly limited. For example, it contains an inorganic alkali salt and a nonionic surfactant, and usually has a pH of 11.0 to 12.7. Some are preferably used.

  The inorganic alkali salt can be used as appropriate. For example, sodium hydroxide, potassium, ammonium, lithium, sodium silicate, potassium, ammonium, lithium, tribasic sodium phosphate, potassium, ammonium Inorganic alkaline agents such as sodium carbonate, potassium, ammonium, sodium hydrogencarbonate, potassium, ammonium, sodium borate, potassium, and ammonium. These may be used alone or in combination of two or more.

In the case of using silicate, developability is achieved by adjusting the mixing ratio and concentration of silicon oxide SiO ₂ which is a component of silicate and alkali oxide M ₂ O (M represents an alkali metal or ammonium group). Can be easily adjusted. Among the alkaline aqueous solutions, those having a mixing ratio (SiO ₂ / M ₂ O: molar ratio) of the silicon oxide SiO ₂ and the alkali oxide M ₂ O of 0.5 to 3.0 are preferable, and 1.0 to 2 0.0 is preferred. The addition amount of the SiO ₂ / M ₂ O is preferably 1 to 10% by mass, more preferably 3 to 8% by mass, and most preferably 4 to 7% by mass with respect to the mass of the alkaline aqueous solution. When this concentration is within the above-mentioned range, there is no decrease in developability and processing capacity, no precipitation or crystal formation, no gelation during neutralization during waste liquid, and no trouble in waste liquid processing.

  In addition, an organic alkali agent may be supplementarily used in order to finely adjust the alkali concentration and supplement the solubility of the photosensitive layer. Examples of the organic alkali agent include monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropylamine, diisopropylamine, triisopropylamine, n-butylamine, monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, Examples thereof include diisopropanolamine, ethyleneimine, ethylenediamine, pyridine, tetramethylammonium hydroxide and the like. These alkali agents are used alone or in combination of two or more.

  The surfactant can be used as appropriate. For example, nonionic surfactants having a polyoxyalkylene ether group, polyoxyethylene alkyl esters such as polyoxyethylene stearate, sorbitan monolaurate, sorbitan monostearate Nonionic surfactants such as sorbitan alkyl esters such as sorbitan distearate, sorbitan monooleate, sorbitan sesquioleate, sorbitan trioleate, and monoglyceride alkyl esters such as glycerol monostearate and glycerol monooleate; Alkyl benzene sulfonates such as sodium acetate, sodium butyl naphthalene sulfonate, sodium pentyl naphthalene sulfonate, sodium hexyl naphthalene sulfonate Anion interfaces such as alkyl naphthalene sulfonates such as sodium, sodium octyl naphthalene sulfonate, alkyl sulfates such as sodium lauryl sulfate, alkyl sulfonates such as sodium dodecyl sulfonate, and sulfosuccinate esters such as sodium dilauryl sulfosuccinate Activators: Alkyl betaines such as lauryl betaine and stearyl betaine, amphoteric surfactants such as amino acids, and the like can be mentioned. Particularly preferred are nonionic surfactants having a polyoxyalkylene ether group.

  As the surfactant containing a polyoxyalkylene ether group, those having the structure of the following general formula (X) are preferably used.

R ₄₀ —O— (R ₄₁ —O) _pH (X)

In the formula, R ₄₀ is an alkyl group having 3 to 15 carbon atoms, an aromatic hydrocarbon group having 6 to 15 carbon atoms, or a heteroaromatic ring group having 4 to 15 carbon atoms (in addition, the substituent is 1 to 20 carbon atoms). An alkylene group, a halogen atom such as Br, Cl, or I, an aromatic hydrocarbon group having 6 to 15 carbon atoms, an aralkyl group having 7 to 17 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, or an alkyl group having 2 to 20 carbon atoms An alkoxy-carbonyl group and an acyl group having 2 to 15 carbon atoms.), R ₄₁ represents an alkylene group having 1 to 100 carbon atoms, and p represents an integer of 1 to 100. Each of these groups may have a substituent, and examples of the substituent include an alkyl group having 1 to 20 carbon atoms and an aromatic hydrocarbon group having 6 to 15 carbon atoms.

  In the definition of the above formula (X), specific examples of the “aromatic hydrocarbon group” include phenyl group, tolyl group, naphthyl group, anthryl group, biphenyl group, phenanthryl group and the like, and “heteroaromatic ring” Specific examples of the “group” include furyl group, thionyl group, oxazolyl group, imidazolyl group, pyranyl group, pyridinyl group, acridinyl group, benzofuranyl group, benzothionyl group, benzopyranyl group, benzooxazolyl group, benzoimidazolyl group, and the like. It is done.

In addition, the part of (R ₄₁ —O) p in the formula (X) may be two or three groups within the above range. Specific examples include a combination of random or block combinations of ethyleneoxy and propyleneoxy, ethyleneoxy and isopropyloxy, ethyleneoxy and butyleneoxy, ethyleneoxy and isobutylene, and the like. . In the present invention, the surfactant having a polyoxyalkylene ether group is used alone or in a composite system, and it is effective to add 1 to 30% by mass, preferably 2 to 20% by mass in the developer. If the addition amount is small, the developability may be deteriorated. On the other hand, if the amount is too large, the development damage becomes strong and the printing durability of the printing plate may be deteriorated.

  Examples of the nonionic surfactant having a polyoxyalkylene ether group represented by the formula (X) include polyoxyethylene alkyl ethers such as polyoxyethylene lauryl ether, polyoxyethylene cetyl ether, and polyoxyethylene stearyl ether. Polyoxyethylene aryl ethers such as polyoxyethylene phenyl ether and polyoxyethylene naphthyl ether, polyoxyethylene alkyl aryl ethers such as polyoxyethylene methyl phenyl ether, polyoxyethylene octyl phenyl ether and polyoxyethylene nonyl phenyl ether Kind.

  These surfactants can be used alone or in combination. Further, the content of these surfactants in the developer is preferably in the range of 0.1 to 20% by mass in terms of active ingredients.

  The pH of the developer used in the plate making method of the present invention is usually 11.0 to 12.7, preferably 11.5 to 12.5, from the viewpoint of damage during image formation and development of the exposed area.

  Moreover, it is preferable that the electrical conductivity of the developing solution used by this invention is 3-30 mS / cm. If the ratio is lower than normal, the elution of the photosensitive layer components on the surface of the aluminum plate support becomes difficult and printing may be accompanied by stains. Conversely, if the range is exceeded, the salt concentration is high, so the elution rate of the photosensitive layer is increased. This is because the film is extremely slow and a remaining film may be formed in the unexposed area. Particularly preferred conductivity is in the range of 5-20 mS / cm.

  EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these.

[Examples 1-8 and Comparative Examples 1-3]
(Method for producing aluminum support)
An aluminum plate having a thickness of 0.3 mm was etched by being immersed in 10% by mass sodium hydroxide at 60 ° C. for 25 seconds, washed with running water, neutralized and washed with 20% by mass nitric acid, and then washed with water. This was subjected to an electrolytic surface roughening treatment in a 1% by mass nitric acid aqueous solution using a sinusoidal alternating waveform current at an anode time electricity of 300 coulomb / dm ² . Subsequently, after dipping in a 1% by mass aqueous sodium hydroxide solution at 40 ° C. for 5 seconds and then in a 30% by mass sulfuric acid aqueous solution and desmutting at 60 ° C. for 40 seconds, the current density in a 20% by mass sulfuric acid aqueous solution was 2A / current density. Anodization was performed for 2 minutes so that the thickness of the anodized film was 2.7 g / m ² under the condition of dm ² . When the surface roughness was measured, it was 0.3 μm (Ra display according to JIS B0601).

(Formation of intermediate layer)
The aluminum plate thus treated was first coated with the next intermediate layer solution using a bar coater and then dried at 80 ° C. for 20 seconds. A coating amount of the intermediate layer after drying was 10 mg / m ^2.

Intermediate layer solution ・ 100g of the following sol solution
・ Methanol 900g

Sol solution ・ Phosmer PE (Unichemical Co., Ltd.) 5g
・ Methanol 45g
・ Water 10g
・ 85% phosphoric acid 5g
・ Tetraethoxysilane 20g
・ 3-Methacryloxypropyltrimethoxysilane 15g

[Formation of photosensitive layer]
A high-sensitivity photopolymerizable composition P-1 having the following composition was applied so that the dry coating mass was 1.4 g / m ² and dried at 100 ° C. for 1 minute to form a photosensitive layer.
(Photopolymerizable composition P-1)
Ethylenically unsaturated bond-containing compound (A-1) 4.3 parts by mass Linear organic polymer (polymer binder) (B-1) 3.5 parts by mass Sensitizing dye (C-1) 0.31 Part by mass Polymerization initiator (D-1) (Amount described in Table 1)
Chain transfer agent (E-1) 0.35 parts by mass N-nitrosophenylhydroxylamine aluminum salt 0.025 parts by mass
ε-phthalocyanine dispersion 0.75 parts by mass Fluorine nonionic surfactant Megafac F780 0.014 parts by mass (Dainippon Ink Chemical Co., Ltd.)
Methyl ethyl ketone 63 parts by mass Propylene glycol monomethyl ether 55 parts by mass

[Comparative Example 4]
A photosensitive lithographic printing plate of Comparative Example 4 was obtained in the same manner as in Example 1 except that the linear organic polymer (polymer binder) B-1 in Example 1 was changed to B-2.

[Evaluation]
(1) Printing durability The photosensitive lithographic printing plate obtained was adjusted with a Vx9600CTP (light source wavelength: 405 nm) manufactured by Fuji Photo Film Co., Ltd. so that the exposure amount on the photosensitive material was 0.05 mJ / cm ^2. I drew the image. Within 30 seconds, G & J PS processor Inter Plater 850HD charged with an alkaline developer having the following composition was used for preheating so as to reach the plate surface arrival temperature and heat treatment time shown in Table 1, followed by development with a developer at 25 ° C. . The resulting lithographic printing plate was DIC manufactured by Dainippon Ink & Chemicals, Inc. using a Lithrone printing machine manufactured by Komori Corporation. Printing was performed using GEOS (N) black ink, and printing durability was evaluated based on the number of printed sheets when it was visually recognized that the density of the solid image started to decrease.

(Alkali developer composition)
Potassium hydroxide 0.15g
Polyoxyethylene naphthyl ether (n = 13) 5.0 g
Kirest 400 (chelating agent) 0.1 g
94.75 g of water
The results are shown in Table 1.

Example 9
A photosensitive lithographic printing plate of Example 9 was obtained in the same manner as in Example 1 except that the linear organic polymer (polymer binder) B-1 in Example 1 was changed to B-3. And it evaluated by the method similar to Example 1, and the result was shown in Table 2.
Example 10
A photosensitive lithographic printing plate of Example 10 was obtained in the same manner as in Example 1 except that the linear organic polymer (polymer binder) B-1 in Example 1 was changed to B-4. And it evaluated by the method similar to Example 1, and the result was shown in Table 2.
[Comparative Example 5]
A photosensitive lithographic printing plate of Comparative Example 6 was obtained in the same manner as in Comparative Example 2 except that the linear organic polymer (polymer binder) B-1 in Comparative Example 2 was changed to B-3. And it evaluated by the method similar to Example 1, and the result was shown in Table 2.
[Comparative Example 6]
A photosensitive lithographic printing plate of Comparative Example 7 was obtained in the same manner as in Comparative Example 3 except that the linear organic polymer (polymer binder) B-1 in Comparative Example 3 was changed to B-4. And it evaluated by the method similar to Example 1, and the result was shown in Table 2.
[Comparative Example 7]
A photosensitive lithographic printing plate of Comparative Example 8 was obtained in the same manner as in Comparative Example 3 except that the linear organic polymer (polymer binder) B-1 of Comparative Example 3 was changed to B-5. And it evaluated by the method similar to Example 1, and the result was shown in Table 2.

  As is apparent from the results of Tables 1 and 2, the present invention can provide a plate making method of a lithographic printing plate that is excellent in printing durability and has no stain on the printed matter.

Claims (4)

On a hydrophilic support, a hexaarylbisimidazole compound, a chain transfer agent represented by the following general formula (A), a compound having an ethylenically unsaturated double bond, a polymer binder having a crosslinkable group, and 300 to 500 nm A lithographic printing plate precursor having a photosensitive layer containing a sensitizing dye having an absorption maximum in the wavelength region of which the hexaarylbisimidazole compound content is 6.5% by mass or less of the non-volatile component of the photosensitive layer Is subjected to heating and development after scanning exposure with a laser beam, the heating is performed for 5 to 30 seconds, the plate surface temperature at the time of heating is 80 to 150 ° C., and polyoxyethylene naphthyl ether (oxy A method for making a photosensitive lithographic printing plate, comprising developing with a developer containing ethylene repeating unit number n = 13).

In the formula, R represents an alkyl group which may have a substituent, or an aryl group which may have a substituent, and A represents a 5-membered or 6-membered ring having a carbon atom together with an N = CN moiety. The atomic group which forms the heterocyclic ring of A, and A may further have a substituent. 2. The photosensitive lithographic printing according to claim 1, wherein the chain transfer agent is at least one selected from the group consisting of compounds represented by the following general formula (I) and general formula (II): Plate making method.

[In general formula (I) and general formula (II), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and X represents a halogen group, an alkoxyl group, a substituted group. An alkyl group which may have a group, or an aryl group which may have a substituent. ] Polymeric binder, claim, characterized in that at least one member selected from the group consisting of polyurethane binder having a crosslinkable group in (meth) acrylic binder and a side chain having a crosslinkable group in a side chain one or 2. A process for making a photosensitive lithographic printing plate as described in 2 above. The method of making a photosensitive lithographic printing plate according to any one of claims 1 to 3, wherein the polymer binder is at least one selected from polyurethane binders having a crosslinkable group in the side chain.