JP4284975B2 - container - Google Patents
container Download PDFInfo
- Publication number
- JP4284975B2 JP4284975B2 JP2002332569A JP2002332569A JP4284975B2 JP 4284975 B2 JP4284975 B2 JP 4284975B2 JP 2002332569 A JP2002332569 A JP 2002332569A JP 2002332569 A JP2002332569 A JP 2002332569A JP 4284975 B2 JP4284975 B2 JP 4284975B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- lid
- opening
- container
- overcap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】
【発明の属する技術分野】
本発明は、容器内が陽圧化した状態で内容物が保存される容器に関し、特に初期開封時の内容物の飛び散りを防止する容器に関する。
【0002】
【従来の技術】
レギュラーコーヒー缶詰は、通常真空脱臭や窒素置換を行っているが、このような方法ではコーヒーから炭酸ガスが発生すると同時に香りも飛散し、香りの少ないコーヒーとなってしまう。そこで、従来からドライアイスなどで容器内を炭酸ガスで充満させて陽圧化し、コーヒーからの香りの飛散を防止して香りの強いコーヒーを得るようになっている。
しかしながら、缶内が陽圧のため、開封時に炭酸ガスと共にコーヒーの粉末が吹き出してくる。これを防止するため、従来からタブの開口部にフィルターなどを取り付けた吹き出し防止蓋が考案されている(特許文献1,2参照)。
【0003】
【特許文献1】
実開昭63−144428号公報
【特許文献2】
特開平3−133744号公報
これら特許文献1,2には、初期破断される開口用タブの固定部周縁にフィルタや濾紙を取付け、初期開封時にガスのみ逃がして内容物の吹き出しを防止する技術が記載されている。
【0004】
【発明が解決しようとする課題】
しかしながら上記した従来の吹き出し防止蓋の場合には、開口用タブをゆっくり持ち上げる場合は内容物の吹き出しを防止できるものの、勢いよく開口用タブを持ち上げるとフィルタからガスが抜けきれない内にフィルタと蓋体間に隙間が生じる。この隙間から内容物が吹き出し、フィルタを付けた効果が失われてしまうという問題があった。
【0005】
本発明は上記した従来技術の問題点を解決するためになされたもので、その目的とするところは、陽圧状態を確実に保持でき、しかも開封時の内容物の吹き出しを防止できる容器を提供することにある。
【0006】
【課題を解決するための手段】
上記目的を達成するために、本発明にあっては、容器本体と、該容器本体の上端に巻き締め固定される吹き出し防止蓋と、吹き出し防止蓋を覆い容器本体に対して着脱自在に装着されるオーバーキャップと、を備え、
前記吹き出し防止蓋は、部分的に開口部が形成された金属製の蓋体と、該蓋体の内面に取り付けられ開口部を覆う樹脂製のフィルムと、を備えた容器であって、
容器内はガス圧によって陽圧となり、ガス圧によってフィルムが膨張して開口部から蓋体上面より上方に張り出す構成で、前記開口部の開口縁は上方に向けてめくり返されたカール部となっており、
前記フィルムと蓋体内面との間には開口部を取り囲むシール部が設けられ、該シール部はフィルムを蓋体内面に熱溶着するヒートシールによって構成され、
前記フィルムは、ガスバリア層としてのアルミ箔の内面及び外面にPETフィルムが積層され、さらに内側のPETフィルムには、ヒートシール用のPE層が積層された構成で、前記蓋体は、金属材の内外面が合成樹脂製の塗膜によってコーティングされ、さらに外面の塗膜の上にヒートシール用のPE層がコーティングされた構成であり、
前記オーバーキャップには、フィルムを破断する破断手段としてカッターが折り畳まれた状態で装着され、開封する場合には、オーバーキャップを外し、カッターをスコア部にて内側に折り曲げて下方に突出させ、オーバーキャップを再び装着して前記カッターを吹き出し防止蓋のフィルムに押し込んでフィルムを突き破り陽圧を解消する構成となっていることを特徴とする。
【0007】
また、フィルムの外径端部が蓋体外縁の巻締部に固定されることを特徴とする。
【0009】
【発明の実施の形態】
以下に本発明を図示の実施の形態に基づいて説明する。
図1は、本発明の実施の形態に係る吹き出し防止蓋が用いられた容器を示している。
すなわち、この容器1は、容器本体10と、容器本体10の上端に巻締固定される吹き出し防止蓋20と、吹き出し防止蓋20を覆い容器本体10に対して着脱自在に装着されるオーバーキャップ30とを備えた構成となっている。
容器本体10は有底円筒形状の金属製容器で、上端部外周にオーバーキャップ30とねじ係合する雄ねじ部11が形成されている。
【0010】
吹き出し防止蓋20は、部分的に開口部21が形成された蓋体22と、蓋体22の内面に取り付けられ開口部21を覆う樹脂製のフィルム23とを備え、フィルム23と蓋体22内面との間には開口部21を取り囲むシール部24が設けられている。蓋体22の外径端部と容器本体10の上端との巻締部12は、雄ねじ部11よりも小径に絞られている。
【0011】
蓋体22の外周は円形で、開口部21は蓋体外周と同心円状の円形となっている。開口部21の開口縁は上方に向けてめくり返された円環状のカール部25となっている。
シール部24はフィルム23を蓋体22の内側に位置する面に熱溶着するヒートシールによって構成されている。
フィルム23はアルミ箔等のガスバリア層と樹脂層を含む多層樹脂フィルムで構成される。フィルム23には、容器本体10内が陽圧になってもシール部24が剥離しないように充分なシール強度を持つフィルムが使用される。
【0012】
図2(C)には、蓋体22とフィルム23の層構成の一例が示されている。
図示例では、蓋体22は、ブリキ(SPTE)等の金属材22aの内外面が合成樹脂製の塗膜22b,22cによってコーティングされ、さらに外面の塗膜22bの上にヒートシール用のPE層22dがコーティングされた構成となっている。
フィルム23は、ガスバリア層としてのアルミ箔23aの内面及び外面にPETフィルム23b,23cが積層され、さらに内側のPETフィルム23bには、ヒートシール用のPE層23dが積層された構成となっている。
【0013】
オーバーキャップ30には、フィルム23を破断する破断手段としてのカッター31が備えられている。この例では、図1(B)に示すように、キャップ30の天板部32の裏にカッター31が折り畳まれた状態で装着されている。この場合には、まず、オーバーキャップ30を開封し、オーナーキャップ30内面に折り畳まれているカッター31を爪で起こした後、再度、オーバーキャップ30を装着する。このとき、カッター31によりフィルム23が破断される。
【0014】
上記構成の容器の製造手順は、容器本体10にドライアイスを供給後レギュラーコーヒー等の内容物を充填し、ドライアイスが未昇華の状態で吹き出し防止蓋を巻締密封する。
これにより、容器内の空気が炭酸ガスにより追い出されてコーヒー等の酸化劣化が防止できると共に、ドライアイスが昇華すると容器内は陽圧となる。
ガス圧によってシール部24が開口部21に向かって引っ張られるが、ガス圧がフィルム23を蓋体22裏面に対して押し付けてシール部24のシール強度を高める方向に作用しているので、シール部24の剥離が防止される。
【0015】
また、ガス圧によってフィルム23は膨張し、図3に示すように、開口部21から蓋体22上面より上方に張り出す外観となる。開封前の膨張した容器外観は一般的には好ましくないが、レギュラーコーヒーの場合は陽圧となっている外観がコーヒーの香りを保持している証拠となり、新鮮な香りの高いコーヒーの外観を示していることになる。この張り出しは、オーバーキャップ30によって覆われている。
【0016】
開封する場合には、オーバーキャップ30を外し、オーバーキャップ30の天板部32に設けられたカッター31のスコア部31aを内側に折り曲げて下方に突出させ、オーバーキャップ30を再び装着してカッター31を吹き出し防止蓋20のフィルム23に押し込む。
これにより、図4に示すように、カッター31がフィルム23を突き破り、容器内のガスが抜けて陽圧が解消される。フィルム23の破損部23aはカッター31が入り込んでいるため、勢いよく開封してもカッター31と破損部23aの隙間からガスのみが解放され、コーヒーの粉末は飛び散ることはない。
そして、オーバーキャップ30を回転することにより、カッター31が開口部21の開口縁に沿って円周上にフィルム23をカットすることになり、1回転するとフィルム23を全周にわたりカットできる。開口面積が広くなるために、スプーンで一定量のコーヒーを軽量することが可能となり、常に一定濃度のコーヒーを飲用することができる。
【0017】
開口部21の形状としては、図5(A)に示すような半月形状としてもよい。すなわち、蓋体22の外周と同心円状の円弧部21bと、円弧部21bの両端を結ぶ直線部21aとを備え、円弧部21bと直線部21aとの角部は円弧形状となっている。
このように半月形状とすれば、直線部21aをスプーンの擦り切り部として利用可能であり便利である。半月形状の場合のフィルム23の開封は、オーバーキャップ30を半回転することにより開口部21の円弧部21bに沿ってフィルム23を半円形状にカットすることができる。
初期開封した後は、オーバーキャップ30を装着して開口部21を閉塞する。オーバーキャップ30締め込み時に、天板部32を開口部21のカール部25上端に圧接させてリシールすることも可能である。
【0018】
図5(B),(C)は、フィルムの他の取付例を示している。このうち、(C)は参考例である。
図5(B)は、フィルム23の外径端を巻締部12まで延ばし、巻締部12に巻き込んで固定したものである。
このようにすれば、シール部24のせん断方向のずれを防止することができ、シール部24 の剥れ防止効果を高めることができる。
図5(C)に示す参考例は、シール部24を設けないでフィルム23の外径端部を蓋体22の巻締部12に密封状態で巻き込み、巻締部12をシール部24としたものである。
なお、上記実施の形態では内容物としてレギュラーコーヒーを例にとって説明したが、レギュラーコーヒーの他に抹茶など非常に細かい粉体を充填した容器などに広く応用可能である。
【0019】
【実施例】
吹き出し防止蓋の試作蓋として、メガネ蓋の内側にアルミ箔入り多層フィルムをヒートシールした。多層フィルムの層構成は、38μのPETフィルム層、20μのアルミ箔、20μのPE層、30μのPE層の4層構造とした。
陽圧化条件として粉末状ドライアイス2.5gを空き缶に供給後、レギュラーコーヒー150gを充填し、直ちに巻き締めた。
これにより、缶内圧は0.177〜0.196MPa(1.8〜2.0kg・cm2)となった。このように缶内が陽圧となっても、シール部は剥離することなく陽圧状態が保たれた。そして、約0.2MPaの缶内圧によりフィルム23が膨らんだ状態となった。
【0020】
図6は、吹き出し防止蓋20の張り(平坦なパネル部20aからの高さ)状態の比較図である。
開口部21の形状が円形で、開口径Dを25φ、40φ、60φとしたものと、開口部21の形状が図5(A)に示したような半月形状で、直線部21aと円弧部21b間の間隔Rが30mmの吹き出し防止蓋を用意し、フィルム23が巻締部の上端から張り出す高さhを張りの高さとして測定した。開口径Dが25φでは張りの高さhは0mmで(図6(A)参照)、40φでは張りの高さhは4mm(図6(B)参照)、60φでは張りの高さhは10mm(図6(C)参照)、半月形状では張りの高さhが5mmであった(図6(D)参照)。
【0021】
【発明の効果】
以上説明したように、本発明によれば次のような効果が得られる。
本発明によれば、容器本体の上端に巻締固定されると共に部分的に開口部が形成された蓋体と、蓋体の内面に取り付けられ開口部を覆う樹脂製のフィルムとを備え、フィルムと蓋体内面との間には開口部を取り囲むシール部が設けられる構成となっているので、フィルムによって確実にシールすることができる。
また、フィルムを破断する際に、カッター等の破断手段をフィルムに突き刺した瞬間にガスが抜けて陽圧が解消されるが、その瞬間には突き刺して破れた部分は破断手段で塞がれており、破断手段と破れ目の隙間からガスのみが解放され、内容物の吹き出しは破れ部に入り込んでい破断手段によって阻止される。
また、フィルムが圧力によって外側に膨張するので、陽圧状態が維持されていることが、フィルムの膨張状態で一目で確認することができ、内容物の品質保持の証明となる。
【0022】
シール部はフィルムを蓋体内面に熱溶着するヒートシールによって構成されているので、シールが確実にできる。さらに、容器内の圧力によってフィルムが開口部に向かって引っ張られても、フィルムの外径端部が蓋体外縁の巻締部に固定されているので、シール部に作用するせん断力が小さく剥離するおそれがない。
【0024】
フィルムはガスバリア層を含む多層構成の樹脂フィルムで構成されるので、シールがより一層確実になる。
また、吹き出し防止蓋を覆い容器本体に対して着脱自在に装着されるオーバーキャップを備えたので、開封後のリシールと共に、陽圧によって蓋体から張り出したフィルムの膨張部分を覆い隠すことができる。
さらに、オーバーキャップには、フィルムを破断する破断手段が備えられているので、開封のためにナイフ等を用意する必要がなく便利である。
【図面の簡単な説明】
【図1】図1(A)は本発明の実施の形態に係る吹き出し防止蓋を取り付けた容器の概略斜視図、同図(B)は同図(A)のオーバーキャップの縦断面図、同図(C)は同図(A)の容器の吹き出し防止蓋の平面図、同図(D)は同図(A)の吹き出し防止蓋の裏面図である。
【図2】図2(A)は図1の容器の吹き出し防止蓋の断面図、同図(B)は同図(A)の開口部の要部拡大断面図、同図(C)は蓋体とフィルムの層構成を示す断面図である。
【図3】図3(A)は図1の容器のフィルムが膨張した状態の要部斜視図、同図(B)は同図(A)の断面図である。
【図4】図4(A)乃至(C)は図1の容器の吹き出し防止蓋の開封例を示す説明図である。
【図5】 図5(A)は図1の吹き出し防止蓋の開口形状の他の形状例を示す平面図、同図(B),(C)は図1の吹き出し防止蓋の他の取付例及び参考例を示す裏面図である。
【図6】図6(A)乃至(D)は図1の吹き出し防止蓋の開口部の大きさおよび形状を異ならせた場合のフィルムの張り状態を比較した試験結果を示す図である。
【符号の説明】
1 容器
10 容器本体
12 巻締部
20 吹き出し防止蓋
21 開口部、22 蓋体、23 フィルム、
23aアルミ箔(ガスバリア層)、24 シール部、25 カール部
30 オーバーキャップ
31 カッター(破断手段)、31a スコア、32 天板部[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a container vessel contents while positive pressurization is stored, the container relates in particular that to prevent scattering of the contents of the time of initial opening.
[0002]
[Prior art]
Regular canned coffee is usually vacuum deodorized and nitrogen-substituted. However, in such a method, carbon dioxide gas is generated from the coffee, and at the same time, the scent is scattered and the coffee becomes less scented. Therefore, conventionally, the inside of a container is filled with carbon dioxide gas with dry ice to make positive pressure, preventing the scattering of the scent from the coffee and obtaining a strong scented coffee.
However, since the inside of the can has a positive pressure, coffee powder is blown out together with carbon dioxide gas when opened. In order to prevent this, conventionally, a blowout prevention lid has been devised in which a filter or the like is attached to the opening of the tab (see
[0003]
[Patent Document 1]
Japanese Utility Model Publication No. 63-144428 [Patent Document 2]
In JP-A-3-133744, these
[0004]
[Problems to be solved by the invention]
However, in the case of the conventional blowout prevention lid described above, when the opening tab is slowly lifted, the contents can be prevented from being blown out. However, when the opening tab is lifted up vigorously, the filter and lid cannot be removed from the filter. There is a gap between the bodies. There was a problem that the contents were blown out from this gap and the effect of attaching the filter was lost.
[0005]
The present invention has been made to solve the problems of the prior art described above, it is an object of the positive pressure state can be reliably held, moreover container that can prevent blowout of the contents of the time of unsealing Is to provide.
[0006]
[Means for Solving the Problems]
To achieve the above object, according to the present invention, a container body, a blowout prevention lid being seaming fixed to the upper end of the container body, it is detachably attached to cover the container body to prevent closure balloon And an overcap
The blowout prevention lid is a container provided with a metal lid having a partially formed opening, and a resin film attached to the inner surface of the lid and covering the opening ,
The inside of the container becomes a positive pressure due to the gas pressure, and the film expands due to the gas pressure and projects upward from the upper surface of the lid body from the opening, and the opening edge of the opening is curled and turned upward. And
Between the film and the lid inner surface is provided a seal portion surrounding the opening, the seal portion is constituted by a heat seal that thermally welds the film to the lid inner surface,
The film has a configuration in which a PET film is laminated on the inner and outer surfaces of an aluminum foil as a gas barrier layer, and further, a PE layer for heat sealing is laminated on the inner PET film, and the lid is made of a metal material. The inner and outer surfaces are coated with a synthetic resin coating, and the heat sealing PE layer is coated on the outer coating.
The overcap is attached in a state where the cutter is folded as a breaking means for breaking the film, and when opening, the overcap is removed, the cutter is bent inward at the score portion, and protrudes downward. The cap is mounted again and the cutter is pushed into the film of the blowout prevention lid to break through the film and eliminate the positive pressure .
[0007]
Also, the outer diameter end of the film characterized in that it is fixed to the seamed portion of the lid outer edge.
[0009]
DETAILED DESCRIPTION OF THE INVENTION
The present invention will be described below based on the illustrated embodiments.
FIG. 1 shows a container using a blowout prevention lid according to an embodiment of the present invention.
That is, the
The container
[0010]
The
[0011]
The outer periphery of the
The
The
[0012]
FIG. 2C shows an example of the layer structure of the
In the illustrated example, the
The
[0013]
The
[0014]
In the manufacturing procedure of the container having the above-described structure, the container
Thereby, the air in the container is expelled by the carbon dioxide gas to prevent oxidative deterioration of coffee and the like, and when the dry ice sublimates, the inside of the container becomes positive pressure.
The
[0015]
Moreover, the
[0016]
When opening, the
Thereby, as shown in FIG. 4, the
Then, by rotating the
[0017]
The shape of the
In this way, the half-moon shape is convenient because the
After the initial opening, the
[0018]
5B and 5C show other examples of film attachment. Among these, (C) is a reference example.
FIG. 5B shows an example in which the outer diameter end of the
By doing so, it is possible to prevent the
In the reference example shown in FIG. 5C, the outer diameter end portion of the
In the above embodiment, regular coffee is described as an example of the contents, but the present invention can be widely applied to containers filled with very fine powder such as matcha in addition to regular coffee.
[0019]
【Example】
As a prototype lid for the blowout prevention lid, a multilayer film containing aluminum foil was heat sealed inside the glasses lid. The multilayer film had a four-layer structure of a 38 μ PET film layer, a 20 μ aluminum foil, a 20 μ PE layer, and a 30 μ PE layer.
As a positive pressure condition, 2.5 g of powdered dry ice was supplied to an empty can, and then 150 g of regular coffee was charged and immediately wound.
Thereby, the internal pressure of the can became 0.177 to 0.196 MPa (1.8 to 2.0 kg · cm 2 ). Thus, even if the inside of the can was at a positive pressure, the positive pressure state was maintained without peeling off the seal portion. Then, the
[0020]
FIG. 6 is a comparative view of the tension (height from the
The shape of the
[0021]
【The invention's effect】
As described above, according to the present invention, the following effects can be obtained.
According to the present invention, there is provided a lid body that is wound and fixed to the upper end of the container body and partially formed with an opening, and a resin film that is attached to the inner surface of the lid and covers the opening. Since the seal part surrounding the opening is provided between the cover and the inner surface of the lid, the film can be reliably sealed with the film.
Also, when breaking the film, the gas escapes and the positive pressure is eliminated at the moment when the breaker such as a cutter is pierced into the film, but at that moment the portion that was pierced and broken is blocked by the breaker. Thus, only the gas is released from the gap between the breaking means and the break, and the blowout of the contents is prevented by the breaking means that cannot enter the broken portion.
In addition, since the film expands outward due to pressure, it can be confirmed at a glance that the positive pressure state is maintained in the expanded state of the film, which is a proof of maintaining the quality of the contents.
[0022]
Since sheet Lumpur portion is constituted by a heat seal to heat seal the film to cover the inner surface, the seal can be reliably. Furthermore, even if the film is pulled toward the opening due to the pressure in the container, the outer diameter end of the film is fixed to the tightening portion on the outer edge of the lid, so that the shearing force acting on the seal portion is small and peels off. There is no fear.
[0024]
Off Irumu so is a resin film having a multilayer structure including a gas barrier layer, the seal is more reliable.
In addition , since the overcap that covers the blowout prevention cover and is detachably attached to the container body is provided, the expanded portion of the film protruding from the cover body by the positive pressure can be covered together with the reseal after opening.
Further , since the overcap is provided with a breaking means for breaking the film, it is convenient that a knife or the like is not required for opening.
[Brief description of the drawings]
FIG. 1 (A) is a schematic perspective view of a container equipped with a blowout prevention lid according to an embodiment of the present invention, FIG. 1 (B) is a longitudinal sectional view of the overcap of FIG. Fig. (C) is a plan view of the blowout prevention lid of the container of Fig. (A), and Fig. (D) is a back view of the blowout prevention lid of Fig. (A).
2A is a cross-sectional view of the container blowing prevention lid of FIG. 1, FIG. 2B is an enlarged cross-sectional view of the main part of the opening of FIG. 1A, and FIG. It is sectional drawing which shows the layer structure of a body and a film.
3A is a perspective view of a main part in a state where a film of the container in FIG. 1 is expanded, and FIG. 3B is a cross-sectional view of FIG. 3A.
4A to 4C are explanatory views showing an example of opening the blowout prevention lid of the container of FIG.
5A is a plan view showing another example of the opening shape of the blowout prevention lid of FIG. 1, and FIGS. 5B and 5C are other examples of attachment of the blowout prevention lid of FIG. It is a back view which shows a reference example .
6 (A) to 6 (D) are diagrams showing test results comparing film tension when the size and shape of the opening of the blowout prevention lid of FIG. 1 are varied.
[Explanation of symbols]
DESCRIPTION OF
23a aluminum foil (gas barrier layer), 24 seal part, 25
Claims (2)
前記吹き出し防止蓋は、部分的に開口部が形成された金属製の蓋体と、該蓋体の内面に取り付けられ開口部を覆う樹脂製のフィルムと、を備えた容器であって、
容器内はガス圧によって陽圧となり、ガス圧によってフィルムが膨張して開口部から蓋体上面より上方に張り出す構成で、前記開口部の開口縁は上方に向けてめくり返されたカール部となっており、
前記フィルムと蓋体内面との間には開口部を取り囲むシール部が設けられ、該シール部はフィルムを蓋体内面に熱溶着するヒートシールによって構成され、
前記フィルムは、ガスバリア層としてのアルミ箔の内面及び外面にPETフィルムが積層され、さらに内側のPETフィルムには、ヒートシール用のPE層が積層された構成で、前記蓋体は、金属材の内外面が合成樹脂製の塗膜によってコーティングされ、さらに外面の塗膜の上にヒートシール用のPE層がコーティングされた構成であり、
前記オーバーキャップには、フィルムを破断する破断手段としてカッターが折り畳まれた状態で装着され、開封する場合には、オーバーキャップを外し、カッターをスコア部にて内側に折り曲げて下方に突出させ、オーバーキャップを再び装着して前記カッターを吹き出し防止蓋のフィルムに押し込んでフィルムを突き破り陽圧を解消する構成となっていることを特徴とする容器。 Comprising a container body, a blowout prevention lid being seaming fixed to the upper end of the container body, and overcap which is detachably attached to the container body covering the blow-out preventing cover, and
The blowout prevention lid is a container provided with a metal lid having a partially formed opening, and a resin film attached to the inner surface of the lid and covering the opening ,
The inside of the container becomes a positive pressure due to the gas pressure, and the film expands due to the gas pressure and projects upward from the upper surface of the lid body from the opening, and the opening edge of the opening is curled and turned upward. And
Between the film and the lid inner surface is provided a seal portion surrounding the opening, the seal portion is constituted by a heat seal that thermally welds the film to the lid inner surface,
The film has a configuration in which a PET film is laminated on the inner and outer surfaces of an aluminum foil as a gas barrier layer, and further, a PE layer for heat sealing is laminated on the inner PET film, and the lid is made of a metal material. The inner and outer surfaces are coated with a synthetic resin coating, and the heat sealing PE layer is coated on the outer coating.
The overcap is attached in a state where the cutter is folded as a breaking means for breaking the film, and when opening, the overcap is removed, the cutter is bent inward at the score portion, and protrudes downward. A container having a configuration in which a cap is attached again and the cutter is pushed into the film of the blowout prevention lid to break through the film and eliminate the positive pressure .