JP3942185B2 - Cylindrical case manufacturing method - Google Patents

Description

  The present invention relates to a cylindrical case manufacturing method.

  A condenser microphone is used in a cellular phone. This condenser microphone has a cylindrical case. In recent years, the condenser microphone has been downsized (compact). Specifically, an aluminum plate having a thickness of about 0.3 mm was used in the conventional cylindrical case, whereas a white plate having a thickness of about 0.1 mm was used in a recent cylindrical case. Downsizing. That is. In recent years, since the size has been reduced, the material is white to ensure product strength.

  By the way, in order to maintain the characteristics (electric distortion, sensitivity) of the microphone, it is necessary to provide an insulating film on the inner side of the cylindrical case. And as this insulating film, it was unnecessary for the inner surface of the top wall, and it was necessary only for the inner surface (inner peripheral surface) of the peripheral wall.

When manufacturing such a cylindrical case, for example, a progressive press device is used to sequentially punch from a plate-shaped material. In this case, the insulating material constituting the insulating film on the one surface of the plate-like material was applied, so are those punched in this state, the cylindrical case 50 punched, as shown in FIG. 9, the insulating over its entire inner surface 51 A film 52 is formed. In addition, the progressive press apparatus is used for the manufacturing method of a flange, for example (for example, refer patent document 1).
Japanese Patent Laid-Open No. 2004-11981

  For this reason, in the cylindrical case 50 formed as shown in FIG. For this reason, it is necessary to peel off the insulating material of the unnecessary portions 53 and 54. In this case, for example, the insulating material of the unnecessary portions 53 and 54 is peeled off by shot blasting or processing with a blade. However, the work accuracy of this peeling work is low, and a large number of defective products are generated, and after punching, such a peeling work is required and the number of manufacturing processes is large and the productivity is poor.

Further, as shown in FIG. 10 , a vibration motor used for a cellular phone or the like includes a shaft 55, a winding portion 56 fixed to the shaft 55, and a motor case 57 in which the winding portion 56 is housed. Etc. The motor case 57 includes a cylindrical case main body 59 having an upper wall 58 and a magnet 62 attached to the inner peripheral surface 61 of the peripheral wall 60 of the case main body 59. A shaft 55 is inserted through a bearing 64.

By the way, conventionally, the motor case 57 is configured by the following method. That is, as shown in FIGS. 11 and 12 , first, the case main body 59 is formed by performing press working and cutting, etc., and sintering and cutting are performed to obtain a ring-shaped magnetic body (for example, ferrite). Or a neodymium compound (lanthanoid compound etc.) M is formed. Thereafter, the magnetic body M is fixed to the inner peripheral surface 61 of the peripheral wall 60 of the case main body 59 using an adhesive or the like, and then the magnetic body M is magnetized to form a magnet 62.

  Thus, conventionally, a process for manufacturing the case body 59, a process for processing the magnetic body M constituting the magnet 62, an assembly process for mounting the magnetic body M on the case body 59, and the like are required. For this reason, there were many work steps and it was inferior to production.

  The present invention has been made to solve the above-mentioned conventional drawbacks, and the purpose thereof is to prevent the unnecessary part of the film part to be an insulating film from being generated and to attach the film part to be a magnet part after the punching process. An object of the present invention is to provide a cylindrical case manufacturing method that does not require a process to be performed and has excellent productivity.

Therefore, in the cylindrical case manufacturing method of the first aspect, the plate-shaped material 11 provided with the guide holes 12 at a predetermined pitch along the longitudinal direction is sequentially fed by the progressive press device 8 while being guided by the guide holes 12. A cylindrical case manufacturing method in which the cylindrical case 1 is punched, and after the coating portion 13 is formed on the plate-shaped material 11 with the guide hole 12 as a reference, an inspection process such as positional deviation of the coating portion 13 is performed. In addition, the range H that becomes the cylindrical case 1 including the defective film portion 25 such as displacement when punched by the progressive press apparatus 8 is punched before being supplied to the progressive press apparatus 8, and then the above-mentioned A feeding process of the plate-shaped material 11 by the progressive press device 8 is performed, and the cylindrical case 1 having the coating portion 13 is sequentially punched out.

In the cylindrical case manufacturing method according to claim 2, the progressive press device 8 sequentially feeds the plate-like material 11 provided with the guide holes 12 at a predetermined pitch along the longitudinal direction while guiding the guide holes 12 to the cylinder. A cylindrical case manufacturing method for punching a cylindrical case 1, wherein a ring-shaped film portion 13 is formed on the plate-shaped material 11 with reference to a guide hole 12, and then an inspection process such as positional deviation of the film portion 13 is performed. Next, the range H that becomes the cylindrical case 1 including the defective film portion 25 such as displacement when punched by the progressive press apparatus 8 is punched before being supplied to the progressive press apparatus 8, and thereafter The step of feeding the plate-shaped material 11 by the progressive press device 8 is performed, and the cylindrical case 1 in which the film portion 13 is disposed on the inner peripheral surface 5 is sequentially punched.

In the cylindrical case manufacturing method according to the third aspect of the present invention, the progressive press device 8 sequentially feeds the plate-shaped material 11 provided with the guide holes 12 at a predetermined pitch along the longitudinal direction while guiding the guide holes 12 into the cylinder. A cylindrical case manufacturing method for punching a cylindrical case 1, in which a plate-shaped material 11 having a ring-shaped film portion 13 formed on the basis of a guide hole 12 is subjected to an inspection process such as positional deviation of the film portion 13. Next, the range H that becomes the cylindrical case 1 including the defective film portion 25 such as displacement when punched by the progressive press apparatus 8 is punched before being supplied to the progressive press apparatus 8, and thereafter the plate-like material 11, is characterized in that performs step feed are supplied to the order of feeding the press device 8, are sequentially punched cylindrical case 1 in which the coating unit 13 is disposed on the inner peripheral surface 5

The cylindrical case manufacturing method of claim 4 is a case in which the punched cylindrical case 1 is used for a condenser microphone, and the coating portion 13 is printed on the plate-shaped material 11 so as to cover the insulating film 6 of the condenser microphone case. It is characterized by comprising.

The cylindrical case manufacturing method according to the fifth aspect is characterized in that the punched cylindrical case 1 is a motor case, and the coating portion 13 is formed of a magnetic body M to become a magnet portion 34 of the motor case.

According to the cylindrical case manufacturing method of the first aspect, the cylindrical case is sequentially punched by performing the feeding process of the plate-like material by the progressive press device. And a coating part will be arranged on the inner peripheral surface of this cylindrical case, but this coating part is formed on the basis of the guide hole used as a guide at the time of the feeding process of the plate-shaped material by a progressive press device. Has been. For this reason, in the punching process by the progressive press device, the arrangement position of the coating portion with respect to the punching position of the progressive press device is not displaced, and the punched cylindrical case is formed with a coating portion at a regular position. It will be. That is, a coating part is not formed in an unnecessary part, a coating part is formed only in a necessary part, a peeling process of the coating part after the punching process is not required, and the productivity is excellent. Moreover, since the range that becomes a cylindrical case including a defective film portion such as a displacement when punched by the progressive press device is punched before being supplied to the progressive press device, The cylindrical case including the coating part is not punched out. For this reason, defective products are not mixed in non-defective products, product inspection for detecting defective products from non-defective products is not required, and productivity can be improved. In addition, it is possible to prevent the use of defective products as products and to provide stable non-defective products.

According to the cylindrical case manufacturing method of the second aspect, as in the cylindrical case manufacturing method of the first aspect, the coating portion is based on a guide hole that serves as a guide during the feeding process of the plate-shaped material by the progressive press device. Is formed. For this reason, the arrangement | positioning position of the coating | coated part with respect to the punching position of a progressive press apparatus does not shift | deviate, but a coating | coated part is formed only in the internal peripheral surface in the punched cylindrical case. That is, a coating part is not formed in an unnecessary part, a coating part is formed only in a necessary part, a peeling process of the coating part after the punching process is not required, and the productivity is excellent. Moreover, since the range that becomes a cylindrical case including a defective film portion such as a displacement when punched by the progressive press device is punched before being supplied to the progressive press device, The cylindrical case including the coating part is not punched out. For this reason, defective products are not mixed in non-defective products, product inspection for detecting defective products from non-defective products is not required, and productivity can be improved. In addition, it is possible to prevent the use of defective products as products and to provide stable non-defective products.

According to the cylindrical case manufacturing method of the third aspect , similarly to the second aspect, the coating part is formed with reference to a guide hole that serves as a guide in the step of feeding the plate-shaped material by the progressive press device. For this reason, the arrangement | positioning position of the coating | coated part with respect to the punching position of a progressive press apparatus does not shift | deviate, but a coating | coated part is formed only in the internal peripheral surface in the punched cylindrical case. That is, a coating part is not formed in an unnecessary part, a coating part is formed only in a necessary part, a peeling process of the coating part after the punching process is not required, and the productivity is excellent. Moreover, since the range that becomes a cylindrical case including a defective film portion such as a displacement when punched by the progressive press device is punched before being supplied to the progressive press device, The cylindrical case including the coating part is not punched out. For this reason, defective products are not mixed in non-defective products, product inspection for detecting defective products from non-defective products is not required, and productivity can be improved. In addition, it is possible to prevent the use of defective products as products and to provide stable non-defective products.

According to the cylindrical case manufacturing method of the fourth aspect , the punched cylindrical case is a condenser microphone case, and an insulating film is formed only on the inner peripheral surface thereof. For this reason, an insulating film is not formed in an unnecessary area such as the inner surface of the top wall, and capacitor microphone cases excellent in microphone characteristics (electric distortion, sensitivity, etc.) can be sequentially manufactured. In addition, the coating portion constituting the insulating coating can be formed on a plate-like material by printing, and the processing can be performed easily and accurately. Further, since a defective product in which a positional deviation or the like has occurred is not used in the condenser microphone case, it is possible to provide a condenser microphone case that can prevent the occurrence of a short-circuit phenomenon due to the positional deviation of the insulating film.

According to the cylindrical case manufacturing method of the fifth aspect , the punched cylindrical case is a motor case, and a magnet portion made of a magnetic material is formed only on the inner peripheral surface thereof. For this reason, a cylindrical case that forms a magnet part on the inner peripheral surface but has a magnetic body can be formed in a punching process by a progressive press device, and after the punching process, the magnetic body that constitutes the magnet part is The operation | work etc. which are mounted | worn on the internal peripheral surface of a body can be abbreviate | omitted, and the improvement of the productivity of a motor can be aimed at.

  Next, a specific embodiment of the cylindrical case manufacturing method of the present invention will be described in detail with reference to the drawings. FIG. 3 is an enlarged cross-sectional view of the cylindrical case 1 manufactured by this cylindrical case manufacturing method. The cylindrical case 1 is a case used for a condenser microphone, and as shown in FIGS. 3 and 4, a case main body 3 composed of a cylindrical body having an upper wall 2 and a peripheral wall 4 of the case main body 3. And an insulating film 6 formed on the inner peripheral surface 5. The cylindrical case 1 has an outer diameter of about 4φ to 6φ and a thickness (length in the axial direction) of about 1 mm. At this time, the material of the case main body 3 is made of, for example, white or the like having a thickness of about 0.1 mm, and the insulating film 6 is made of, for example, an epoxy polyester resin or the like as a main component. The case body 3 is provided with a through hole 7 in the upper wall 2. As described above, when the case body 3 is made of white and white, the strength of the product can be ensured even if the case is downsized as in the case of the condenser microphone case.

  In this cylindrical case manufacturing method, a progressive press apparatus 8 as shown in FIG. 5 is used. The progressive press device 8 includes an upper die 9 that moves up and down and a lower die 10 that receives the upper die 9. A plate-like material from which the cylindrical case 1 is punched between the upper die 9 and the lower die 10. (Press material) 11 is supplied. That is, the upper die 9 has a plurality of types of punch portions (not shown), and the progressive press device 8 is configured with a plurality of processing stages. Further, the plate-shaped material 11 is provided with a plurality of guide holes 12 (see FIG. 1) at a predetermined pitch along the longitudinal direction, and the plate-shaped material 11 is sequentially fed out by being guided by the guide holes 12. For this reason, the plate-shaped material 11 is sequentially fed to different processing stages as indicated by arrows by this sequential feeding, and the cylindrical case 1 as a product is punched out at the final stage. The plate-like material 11 supplied to the progressive press apparatus 8 is a long strip wound around the supply drum 14 in a roll shape. That is, the plate-like material 11 is made of a metal plate or a metal foil.

  Next, this cylindrical case manufacturing method will be described with reference to FIG. First, from the plate-like material (strip plate) 11 as shown in FIG. 1A, as shown in FIG. 1B, the guide holes 12.・ To penetrate. Next, as shown in FIG. 1C, the ring-shaped film portion 13 (in this case, the insulating film 6) is printed on the basis of the formed guide holes 12. The film part 13 is performed by, for example, silk printing. In other words, the reference pin is inserted into the guide hole 12 for positioning, and the coating portion 13 is printed in this positioned state. Program control controls the reference pin insertion / removal timing, number of vacuums, and forward / reverse tension in the direction of travel.

  And the plate-shaped raw material 11 of the state of FIG.1 (c) is supplied to the progressive press apparatus 8. FIG. In this case, the progressive press apparatus 8 includes a first stage 15, a second stage 16, a third stage 17, a fourth stage 18, and a fifth stage 19, as shown in FIG. The first stage 15 is a stage for forming a ruled line portion K (see FIG. 1 (d)) for punching the cylindrical case 1, and the second stage 16 is an outer ring 20 as shown in FIG. 2 (a). 3 and the third stage 17, as shown in FIG. 2B, is a stage that forms a concave section 22 having a rectangular cross section, and the fourth stage 18. FIG. 2 (c) shows a stage in which the through hole 7 is provided in the bottom wall 23 of the recess 22, and the fifth stage 19 constitutes the recess 22 as shown in FIG. 2 (d). It is a stage that punches out the wall part. For this reason, the plate-shaped material 11 is provided with a through hole 24, and the punched wall portion becomes the cylindrical case 1. At this time, the coating portion 13 is formed on the inner peripheral surface 5 of the peripheral wall 4, but is disposed on the upper wall 2 side with a slight gap S from the upper wall 2 as shown in FIG. 3.

  Thus, according to the said cylindrical case manufacturing method, the feeding process of the plate-shaped raw material 11 by the progressive press apparatus 8 is performed, and the cylindrical case 1 is sequentially punched out. And the coating | coated part 13 will be arrange | positioned at the internal peripheral surface 5 of this cylindrical case 1, This coating | coated part 13 becomes a guide at the time of the delivery process of the plate-shaped raw material 11 by the progressive press apparatus 8. FIG. The guide hole 12 is formed as a reference. For this reason, in the punching process by the progressive press device 8, the arrangement position of the coating portion 13 with respect to the punching position of the progressive press device 8 is not displaced, and the punched cylindrical case 1 has only the inner peripheral surface 5. A film portion 13 is formed on the surface. That is, the film part 13 is not formed in an unnecessary part, the film part 13 is formed only in a necessary part, and a peeling process of the film part 13 after the punching process is not required, and the productivity is excellent. In particular, the punched cylindrical case 1 is a condenser microphone case, and the insulating film 6 is formed only on the inner peripheral surface 5 thereof. For this reason, the insulating film 6 is not formed in unnecessary areas such as the inner surface of the top wall (upper wall 2), and capacitor microphone cases having excellent microphone characteristics (electric distortion, sensitivity, etc.) are sequentially manufactured. Can do. Furthermore, since the insulating film 6 has a slight gap S between the inner surface of the top wall 2, a more accurate condenser microphone case is obtained. Moreover, the film portion 13 constituting the insulating film 6 can be formed on the plate-shaped material 11 by printing, and the processing can be performed easily and accurately. Further, since a defective product in which a positional deviation or the like has occurred is not used in the condenser microphone case, it is possible to provide a condenser microphone case that can prevent the occurrence of a short-circuit phenomenon due to the positional deviation of the insulating film 6.

  Incidentally, in the above embodiment, the steps from FIG. 1A to FIG. 1D are sequentially performed. However, in the present invention, only the step of FIG. 1D may be used. That is, the process from FIG. 1A to FIG. 1C may be manufactured in another factory, and the product in the state of FIG. .

Further, in the state of FIG. 1C, before supplying the progressive press apparatus 8, an inspection such as the presence or absence of a print missing portion where the film portion 13 is disposed at a predetermined position or not printed (for example, It intends line inspection) process by the image processing machine or the like. By the inspection process line Ukoto, if any defective film portion 25, to ensure that the plate-shaped material 11 having a defective film portion 25 so as not to supply the progressive press device 8, without causing defective Can do.

That is, if there is defective film portion 25 such as a positional deviation, as shown in FIG. 6, that form a Onuki holes 26 punched out the defective film portion 25 is larger than the range H including the defective film portion 25. As shown in FIG. 6, if the plate-shaped material 11 from which the defective film portion 25 is punched is supplied to the progressive press device 8 and the cylindrical case 1 is punched, the cylindrical case including the defective film portion 25. No one is punched out. That is, since the range H of the large through hole 26 is a range that becomes the cylindrical case 1 including the defective film portion 25 such as displacement when punched, the defective film portion 25 is removed when the punching process is performed. The containing cylindrical case 1 is not punched out. For this reason, defective products are not mixed in non-defective products, product inspection such as detecting defective products from non-defective products is not required, and productivity can be improved. In addition, it is possible to prevent the use of defective products as products and to provide stable non-defective products.

By the way, in the said embodiment, although the cylindrical case 1 was a capacitor | condenser microphone case, a motor case may be sufficient. In this case, as shown in FIG. 7 , the magnetic body M is used as the film portion 13, and the film portion 13 made of the magnetic body M may be formed on the plate-shaped material 11. As the magnetic substance M, for example, ferrite or neodymium compound (lanthanoid compound) can be used.

That is, the coating portion 13 made of the magnetic material M is coated on the basis of the guide holes 12 of the plate-like material 11. Therefore, the cylindrical case 1 as shown in FIG. 8 can be punched out by supplying the plate-like material 11 having such a coating portion 13 formed to the progressive press 8. At this time, in FIG. 7 , the film portions 13... Are arranged at the center in the width direction of the plate-like material 11 along the longitudinal direction. For this reason, the progressive press apparatus 8 to be used also has a plurality of stages 15..., And each stage 15 has a number of punch portions corresponding to the film portions 13 of the plate-like material 11. Even in this case, as shown in FIG. 1A, the film portions 13... May be arranged along the longitudinal direction on both side edges 11a and 11b of the plate-like material 11, respectively. Good.

The progressive cylindrical case 1 which is punched by a press apparatus 8, as shown in FIG. 8, a case body 31 having a top wall 30, disposed on the inner peripheral surface 33 of the peripheral wall 32 of the case body 31 And a film portion 13 to be a magnet portion 34. An axial hole 35 is provided through the upper wall 30. In this case, since the magnetic force is not magnetized in the film part 13 constituting the magnet part 34, the motor case is completed by magnetizing the magnetic material M as the film part 13.

  For this reason, the cylindrical case (motor case) in which the coating | coated part 13 used as the magnet part 34 was formed in the internal peripheral surface 33 can be formed in the punching process by the progressive press apparatus 8, and this kind of conventional Unlike the manufacturing method, the operation | work etc. which attach the magnetic body which comprises a magnet part to the internal peripheral surface of a cylinder can be abbreviate | omitted, and the improvement of the productivity of a motor can be aimed at. In the above manufacturing method, the film thickness of the magnetic body M to be the film portion 13 may not be so large. However, since ferrite or a neodymium compound is used as the magnetic body M, a sufficient magnetic force can be magnetized for a vibration motor of a mobile phone even if the film thickness of the magnetic body M cannot be increased. For this reason, even if it uses the cylindrical case 1 manufactured with the said manufacturing method as a motor case, the stable performance can be exhibited as this kind of motor.

Even when manufacturing such a motor case, before supplying the plate-shaped material 11 to the progressive press apparatus 8, intends rows inspection process of the film unit 13. Then, by performing the inspection process, if there is defective film portion 25, as shown in FIG. 6, it is possible Contact Ku by punching a defective film portion 25 before being fed to the progressive press apparatus 8. Thus, if to perform the inspection process, defective products without contamination Some good, that do not require product inspection for detecting a defective among the non-defective.

  By the way, although the membrane | film | coat part 13 formed in said each embodiment was ring shape (annular), as the cylindrical case 1 manufactured, the membrane | film | coat part which consists of an insulating material, a magnetic material (magnetic body), etc. However, the present invention is not limited to the condenser microphone case or the motor case. For this reason, the shape of the film part 13 is not limited to an annular shape, and various other shapes such as a circle and a rectangle are possible, and the upper wall (top wall) of the punched cylindrical case 1 is also possible. The film part 13 may be arrange | positioned on the inner surface of 2. FIG. Thus, even if the film part 13 is not ring-shaped and the position of the film part 13 to be formed is not the inner peripheral surface 5 of the peripheral wall 4 of the cylindrical case 1, it is formed according to this manufacturing method. In the product to be manufactured, it is possible to manufacture the cylindrical case 1 in which the film portion 13 is disposed at a regular position.

Although specific embodiments of the present invention have been described above, the present invention is not limited to the above embodiments, and various modifications can be made within the scope of the present invention. For example, the increase / decrease in the number of punch portions at each stage 15 of the progressive press device 8 is arbitrary, and the feed pitch of the plate-like material 11 is also one time as the arrangement pitch of the guide holes 12 and the coating portions 13. Can be changed according to the size of the cylindrical case 1 that forms the size of the film portion 13 and the like. Furthermore, although the film | membrane part 13 is arrange | positioned in 2 rows in FIG. 1, and is arrange | positioned in 1 row in FIG. 7 , 3 or more rows may be sufficient, and the increase / decrease in the number of stages of the progressive press apparatus 8 is arbitrary. is there. By the way, in the said embodiment, although the plate-shaped raw material 11 supplied to the progressive press apparatus 8 is made into the elongate strip wound by the supply drum 14 at roll shape, it differs from this. It may be a plate material of a predetermined size (fixed size). Also, the material of the plate-like material 11 is not limited to the white, and various metals such as aluminum that can be used for the progressive press device 8 can be used. Further, in the above embodiment, when manufacturing a condenser microphone case, the coating portion 13 is made of an insulating material mainly composed of epoxy polyester resin, and when manufacturing a motor case, the coating portion 13 is made of ferrite or using magnetic body M neodymium compounds, etc., but of course not limited to these, Ru can be variously changed depending on the application or the like of the tubular case 1 to be manufactured.

It is a simple process figure of the cylindrical case manufacturing method of this invention. The plate-shaped raw material used for the said cylindrical case manufacturing method is shown, (a) is a principal part simplified expanded sectional view of the plate-shaped raw material in a 2nd stage, (b) is the plate-shaped raw material in a 3rd stage. It is a principal part simple expanded sectional view, (c) is a principal part simplified enlarged sectional view of the plate-like material in the 4th stage, (d) is a principal part simplified enlarged sectional view of the plate-like material in the 5th stage. It is. It is an expanded sectional view of the cylindrical case manufactured with the said cylindrical case manufacturing method. It is an enlarged plan view of the cylindrical case manufactured with the said cylindrical case manufacturing method. It is a simplification figure of the progressive press apparatus used for the said cylindrical case manufacturing method. It is a simplified view of just before supply to the progressive press the Help rate like material be used for the cylindrical case manufacturing method. It is a simplified process drawing of the other cylindrical case manufacturing method of this invention. It is a simplified sectional view of the cylindrical case manufactured with the above-mentioned cylindrical case manufacturing method. It is sectional drawing of the cylindrical case in the middle of manufacture of the conventional cylindrical case manufacturing method. It is a simplified sectional view of a vibration motor used for a cellular phone or the like. It is a simplified diagram which shows the manufacturing process of the said vibration motor. It is a simplified view of the motor case of the vibration motor.

Explanation of symbols

1 .... Cylinder case, 5 .... Inner peripheral surface, 6 .... Insulating coating, 8 .... Progressive press machine, 11 .... Plate material, 12 .... Guide hole, 13 .... Section part, ... Defective film part, 27 ... Defect mark, 34 ... Magnet part, H ... Range, M ... Magnetic material

Claims (5)

In the progressive press device (8), the plate-shaped material (11) provided with the guide holes (12) at a predetermined pitch along the longitudinal direction is sequentially fed out while being guided by the guide holes (12), and is then cylindrically-shaped ( 1) A cylindrical case manufacturing method in which punching is performed, and after the coating portion (13) is formed on the plate-shaped material (11) with reference to the guide hole (12), the positional deviation of the coating portion (13), etc. The inspection process is performed, and then the range (H) that becomes the cylindrical case (1) including the defective film portion (25) such as misalignment when punched by the progressive press device (8) is progressively pressed. It is punched before being supplied to the apparatus (8), and thereafter the plate-shaped material (11 ) is fed out by the progressive press apparatus (8), and the cylindrical case (1) having the coating part (13) A cylinder characterized by sequentially punching Case production method. In the progressive press device (8), the plate-shaped material (11) provided with the guide holes (12) at a predetermined pitch along the longitudinal direction is sequentially fed out while being guided by the guide holes (12), and is then cylindrically-shaped ( 1) A cylindrical case manufacturing method in which a ring-shaped film part (13) is formed on the plate-shaped material (11) with reference to a guide hole (12), and then the position of the film part (13) A range (H) that becomes a cylindrical case (1) including a defective film part (25) such as a positional deviation when performing an inspection process such as a deviation and then punching with a progressive press device (8), It punches out before supplying to a progressive press apparatus (8), Then, the feed process of the plate-shaped raw material (11) by the said progressive press apparatus (8) is performed, and the said film | membrane part (5) is carried out to an internal peripheral surface (5). 13) Sequentially strike the cylindrical case (1) where the Cylindrical case manufacturing method characterized by Iteiku. In the progressive press device (8), the plate-shaped material (11) provided with the guide holes (12) at a predetermined pitch along the longitudinal direction is sequentially fed out while being guided by the guide holes (12), and is then cylindrically-shaped ( 1) A cylindrical case manufacturing method for punching out a plate-shaped material (11) having a ring-shaped film part (13) formed with reference to a guide hole (12), and the position of the film part (13). A range (H) that becomes a cylindrical case (1) including a defective film part (25) such as a positional deviation when performing an inspection process such as a deviation and then punching with a progressive press device (8), It punches out before supplying to a progressive press apparatus (8), Then, a plate-shaped raw material (11) is supplied to the said progressive press apparatus (8), a delivery process is performed, and it is made to an internal peripheral surface (5) A cylindrical case in which the film part (13) is disposed ( Cylindrical case manufacturing method characterized by) are successively punched. The punched cylindrical case (1) is a case used for a condenser microphone, and the coating part (13) is printed on a plate-like material (11) to constitute an insulating film (6) of the condenser microphone case. The cylindrical case manufacturing method according to any one of claims 1 to 3 . The punched cylindrical case (1) is a motor case, and the film portion (13) is made of a magnetic body (M) to become a magnet portion (34) of the motor case. The cylindrical case manufacturing method in any one of Claim 3 .