JP3904984B2 - Coated metal material and non-chromium metal surface treatment method - Google Patents
Coated metal material and non-chromium metal surface treatment method Download PDFInfo
- Publication number
- JP3904984B2 JP3904984B2 JP2002174741A JP2002174741A JP3904984B2 JP 3904984 B2 JP3904984 B2 JP 3904984B2 JP 2002174741 A JP2002174741 A JP 2002174741A JP 2002174741 A JP2002174741 A JP 2002174741A JP 3904984 B2 JP3904984 B2 JP 3904984B2
- Authority
- JP
- Japan
- Prior art keywords
- surface treatment
- water
- phosphorus
- zirconium
- polyallylamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【0001】
【発明の属する技術分野】
本発明は、被覆金属材料、及び、ノンクロム金属表面処理方法に関する。
【従来の技術】
【0002】
従来、アルミニウム板の表面処理としては、スプレー法によって短時間にて化成処理を施すことができるリン酸クロメート系化成処理剤が使用されてきた。
リン酸クロメート系化成処理剤を用いて形成されるリン酸クロメート化成皮膜は、各種樹脂系塗料を塗装した後の耐食性、密着性に優れているため、建材向け、家電向け、フィン材向け、カーエバポレーター向け、飲料缶蓋材向け等、アルミ材の広範囲な用途において使用されている。
【0003】
しかし、近年、環境保全の目的から、塗料及びラミネートに対して、リン酸クロメートと同等の高い耐食性、密着性を付与することができ、かつ、リン酸クロメート化成処理と同様、短時間のスプレー法により化成皮膜を形成することができるノンクロム系化成処理の要求が高まってきている。
【0004】
スプレー法によるノンクロム化成処理剤としては、例えば、飲料缶ボディ用等のものとして、ジルコニウム化合物又はチタン化合物とリン酸化合物とを併用した系が使用されている。
【0005】
しかしながら、これらの系の処理剤により形成される化成皮膜は、リン酸クロメート化成皮膜と比べて、塗料の塗装後及びラミネートフィルム貼付け後における耐食性及び密着性に劣るため、広範囲な用途に使用できるものではなかった。
【0006】
【発明が解決しようとする課題】
本発明は、上記現状に鑑み、塗料の塗装後及びラミネートフィルム貼付け後における耐食性及び密着性に優れ、リン酸クロメート化成処理を施したものと同等以上の性能を有する被覆金属材料、及び、ノンクロム金属表面処理方法を提供することを目的とするものである。
【0007】
【課題を解決するための手段】
本発明は、アルミニウム又はアルミニウム合金上に、水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンに由来するジルコニウム及び/又はチタンとリンとを含んでなる表面処理層(A)を有し、更に、上記表面処理層(A)上に、ポリアリルアミンを含んでなる樹脂層(B)を有することを特徴とする被覆金属材料である。
【0008】
上記ジルコニウム及び/又は上記チタンは、水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンに由来するものであることが好ましい。
上記リンは、オルソリン酸に由来するものであることが好ましい。
上記リンは、ホスホン基を構成するリン原子が炭素原子と結合した有機ホスホン酸化合物に由来するものであることが好ましい。
【0009】
上記表面処理層(A)は、乾燥後の片面当たりの質量で、ジルコニウム及び/又はチタンの含有量が3〜30mg/m2、リンの含有量が0.5〜5mg/m2であり、上記樹脂層(B)は、乾燥後の片面当たりの質量で、ポリアリルアミンに由来する炭素の含有量が1.6〜200mg/m2であることが好ましい。
【0010】
上記金属製基材は、アルミニウム又はアルミニウム合金であることが好ましい。上記被覆金属材料は、ラミネート材の製造に用いられるものであることが好ましい。
【0011】
本発明は、水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンとリン化合物とを含むノンクロム金属表面処理剤(C)でアルミニウム又はアルミニウム合金を処理する工程(I)、並びに、上記工程(I)を行ったアルミニウム又はアルミニウム合金をポリアリルアミン水溶液(D)で処理する工程(II)を含むことを特徴とするノンクロム金属表面処理方法である。
【0012】
上記水溶性ジルコニウム化合物及び/又は上記水溶性チタン化合物は、水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンであることが好ましい。
【0013】
上記ノンクロム金属表面処理剤(C)は、水溶性錯フッ化ジルコニウム化合物及び/又は水溶性錯フッ化チタン化合物の含有量がジルコニウム及び/又はチタン原子換算で40〜1000ppm、リン化合物の含有量がリン原子換算で20〜500ppmであり、上記ポリアリルアミン水溶液(D)は、ポリアリルアミンの含有量が質量基準で80〜10000ppmであることが好ましい。
以下に、本発明を詳細に説明する。
【0014】
本発明の被覆金属材料は、塗料塗装後、ラミネートフィルム等の樹脂フィルム接着後において、耐食性に優れるものであり、また、塗料塗装後における塗膜密着性、ラミネートフィルム等の樹脂フィルム接着後におけるフィルム密着性にも優れる金属材料である。
【0015】
本発明の被覆金属材料は、金属製基材上に、ジルコニウム及び/又はチタンとリンとを含んでなる表面処理層(A)を有するものである。
本発明の被覆金属材料は、金属製基材上にジルコニウム及び/又はチタンとリンとを含んでなる層が形成されたものであることから、優れた耐食性を付与されたものである。上記表面処理層(A)は、例えば、金属製基材を水溶性ジルコニウム化合物及び/又は水溶性チタン化合物とリン化合物とを含むノンクロム金属表面処理剤で処理することにより形成することができる。
【0016】
上記ジルコニウム及び/又は上記チタンは、水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンに由来するものであることが好ましい。即ち、上記水溶性錯フッ化ジルコニウム及び/又は上記水溶性錯フッ化チタンをジルコニウム及び/又はチタン供給源とする場合が好ましい。例えば、水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンを含有するノンクロム金属表面処理剤を用いて処理を行う場合には、短時間での皮膜化成性に優れるため、より効率的に表面処理層(A)を形成することができる。
【0017】
上記水溶性錯フッ化ジルコニウムとしては特に限定されず、例えば、H2ZrF6、(NH4)2ZrF6、K2ZrF6、Na2ZrF6、Li2ZrF6等を挙げることができる。これらは、単独で用いてもよく、2種以上を併用してもよい。
【0018】
上記水溶性錯フッ化チタンとしては特に限定されず、例えば、H2TiF6、(NH4)2TiF6、K2TiF6、Na2TiF6等を挙げることができる。これらは、単独で用いてもよく、2種以上を併用してもよい。
【0019】
上記表面処理層(A)は、乾燥後の片面当たりの質量で、ジルコニウム及び/又はチタンの含有量が、下限3mg/m2、上限30mg/m2であることが好ましい。3mg/m2未満であると、塗装後、ラミネート後の密着性、耐食性が低下する。30mg/m2を超えると、塗装後、ラミネート後の密着性が低下し、耐食性の改善は見られない。上記下限は、8mg/m2であることがより好ましく、上記上限は、20mg/m2であることがより好ましい。
【0020】
上記リンの供給源であるリン化合物としては特に限定されず、例えば、オルソリン酸、リン酸アンモニウム、第一リン酸ナトリウム、第ニリン酸ナトリウム、第三リン酸ナトリウム、亜リン酸、次亜リン酸、次亜リン酸ナトリウム、有機リン化合物、有機ホスホン酸化合物等を挙げることができる。
【0021】
上記リンは、オルソリン酸に由来するものであることが好ましい。即ち、上記オルソリン酸をリン供給源とする場合が好ましい。例えば、オルソリン酸を含有するノンクロム金属表面処理剤を用いて処理を行う場合には、短時間での皮膜化成性に優れるため、より効率的に表面処理層(A)を形成することができる。
【0022】
上記リンは、ホスホン基を構成するリン原子が炭素原子と結合した有機ホスホン酸化合物に由来するものであることが好ましい。即ち、上記ホスホン基を構成するリン原子が炭素原子と結合した有機ホスホン酸化合物をリン供給源とする場合が好ましい。例えば、上記有機ホスホン酸化合物を含有するノンクロム金属表面処理剤を用いて処理を行う場合には、短時間での皮膜化成性に優れるため、より効率的に表面処理層(A)を形成することができるとともに、形成した皮膜は耐食性に優れる。
【0023】
上記有機ホスホン酸化合物は、ホスホン基(−PO3H2)を化合物中に有し、化合物中の炭素原子にホスホン基(−PO3H2)が結合した化合物である。
上記有機ホスホン酸化合物としては特に限定されず、例えば、下記式(a)で表されるアミノトリ(メチレンホスホン酸)、下記式(b)で表される1−ヒドロキシエチリデン−1,1−ジホスホン酸、下記式(c)で表される2−ホスホブタノン1,2,4−トリカルボン酸等を挙げることができる。
【0024】
【化1】
【0025】
上記有機ホスホン酸化合物としてはまた、下記式(d)で表されるエチレンジアミンテトラ(メチレンホスホン酸)、下記式(e)で表されるジエチレントリアミンペンタ(メチレンホスホン酸)等も挙げることができる。
【0026】
【化2】
【0027】
上記有機ホスホン酸化合物のなかでも、皮膜析出性、塗装後における耐食性及び塗膜密着性、ラミネート貼り付け後における耐食性及びフィルム密着性に優れることから、上記式(a)で表されるアミノトリ(メチレンホスホン酸)、上記式(b)で表される1−ヒドロキシエチリデン−1,1−ジホスホン酸、上記式(c)で表される2−ホスホブタノン1,2,4−トリカルボン酸が好ましい。
【0028】
上記有機ホスホン酸化合物は、水溶性であることが好ましい。水溶性の化合物である場合には、有機溶媒を用いる必要がなくなり、環境に対する負荷を軽減することができる。
【0029】
上記有機ホスホン酸化合物は、単独で用いてもよく、2種以上を併用してもよい。なお、ホスホン基に含まれる水素原子をアルカリ金属又はアンモニウム等で置換した有機ホスホン酸化合物塩をノンクロム金属表面処理剤に含有させることは、形成される皮膜の耐食性が低下することから好ましくない。
【0030】
上記表面処理層(A)は、乾燥後の片面当たりの質量で、リンの含有量が、下限0.5mg/m2、上限5mg/m2であることが好ましい。0.5mg/m2未満であると、塗装後、ラミネート後の密着性、耐食性が低下する。5mg/m2を超えると、塗装後、ラミネート後の密着性が低下する。上記下限は、1mg/m2であることがより好ましく、上記上限は、3mg/m2であることがより好ましい。
【0031】
本発明の被覆金属材料は、上記表面処理層(A)上に、ポリアリルアミンを含んでなる樹脂層(B)を有するものである。
上記樹脂層(B)は、上記被覆金属材料における表面処理層(A)上に形成されるポリアリルアミンを含んでなる層である。これにより、上記樹脂層(B)上に、塗膜を形成する場合には、塗膜形成後の塗膜密着性を向上させることができ、また、ラミネートフィルムを貼り付ける場合には、ラミネートフィルム貼り付け後のフィルム密着性を向上させることができる。上記樹脂層(B)は、例えば、上記表面処理層(A)が形成された金属製基材をポリアリルアミンを含む水溶液で処理することによって形成することができる。
【0032】
本発明の被覆金属材料においては、ポリアリルアミンを含んでなる樹脂層(B)を有するものであることにより、特異的に塗膜形成後の塗膜密着性、ラミネートフィルム貼り付け後のフィルム密着性を向上させることができる。即ち、下記一般式(1);
【0033】
【化3】
【0034】
で表されるポリアリルアミンを含んでなる樹脂層を有する場合には、塗膜密着性、フィルム密着性を向上させる効果が見られるが、例えば、下記一般式(2)、下記一般式(3)、下記一般式(4)で表されるポリビニルアミン、ポリアクリルアミド、ポリエチレンイミンを含んでなる樹脂層を有する場合には、塗膜密着性、フィルム密着性を向上させる効果は見られない。
【0035】
【化4】
【0036】
【化5】
【0037】
【化6】
【0038】
また、例えば、下記一般式(5)で表されるポリアリルアミンの強酸塩を含んでなる樹脂層を有する場合にも、塗膜密着性、フィルム密着性を向上させる効果は見られない。このように、ポリアリルアミンを含んでなる樹脂層を有する場合に、特異的に塗膜形成後の塗膜密着性、ラミネートフィルム貼り付け後のフィルム密着性を向上させることができることが本発明の被覆金属材料の特徴的な点である。
【0039】
【化7】
【0040】
上記樹脂層(B)におけるポリアリルアミンとしては特に限定されず、例えば、PAA−01、PAA−03、PAA−05、PAA−15、PAA−15B、PAA−10C、PAA−H−10C(いずれも日東紡績社製)等の市販品を用いることができる。これらは、単独で用いてもよく、2種以上を併用してもよい。
上記ポリアリルアミンは、本発明の効果を損なわない範囲で、少量の他のモノマーを共重合したものであってもよい。
【0041】
上記ポリアリルアミンの重量平均分子量は、下限1000、上限150000であることが好ましい。この範囲内であることにより、塗装後の塗膜密着性、ラミネートフィルム貼り付け後のフィルム密着性を優れたものとすることができる。上記下限は、1000であることがより好ましく、上記上限は、5000であることがより好ましい。
【0042】
上記樹脂層(B)におけるポリアリルアミンは、上記樹脂層(B)を形成する際にポリアリルアミン水溶液を用いる場合には、水溶液のpHを調整するため、含有する1級アミンを酸で中和することもできる。中和剤としては、強酸で中和した場合には、例えば、上記一般式(5)で表されるポリアリルアミンの強酸塩となり、塗装後の塗膜密着性、ラミネートフィルム貼り付け後のフィルム密着性が低下するため好ましくなく、酢酸等の弱酸を使用することが好ましい。
【0043】
上記樹脂層(B)は、乾燥後の片面当たりの質量で、ポリアリルアミンに由来する炭素の含有量が下限1.6mg/m2、上限200mg/m2であることが好ましい。1.6mg/m2未満であると、塗装後、ラミネート後の密着性が低下する。200mg/m2を超えると、密着性、耐食性は向上せず、コスト高となる。上記下限は、10mg/m2であることがより好ましく、上記上限は、100mg/m2であることがより好ましい。
【0044】
本発明の被覆金属材料に形成される皮膜(上記表面処理層(A)及び上記樹脂層(B)からなる皮膜)中のジルコニウム及び/又はチタンの含有量は、蛍光X線分析装置により測定することができ、上記ポリアリルアミンに由来する炭素の含有量は、形態別炭素/水分析装置によって測定される有機炭素量により測定することができる。
【0045】
上記金属製基材は、アルミニウム又はアルミニウム合金であることが好ましい。即ち、上記被覆金属材料がアルミニウム又はアルミニウム合金である金属製基材上に上記表面処理層(A)を有し、更に表面処理層(A)上に上記樹脂層(B)を有するものであることが好ましい。また、上記金属製基材は板状であることが好ましい。アルミニウム又はアルミニウム合金を金属製基材として用いて得られる被覆金属材料は、塗装後の耐食性及び塗膜密着性に優れるものであることから、飲料物用容器向け、家電向け、住宅建材向け等の用途に好適に用いることができる。
【0046】
上記アルミニウム合金としては特に限定されず、例えば、アルミニウム合金5182材、アルミニウム合金5021材、アルミニウム合金5022材、アルミニウム合金5052材、アルミニウム合金3004材、アルミニウム合金3005材、アルミニウム合金1050材、アルミニウム合金1100材等が好適に用いられる。
【0047】
本発明の被覆金属材料は、上記被覆金属材料に、更に塗装を施してもよい。上記被覆金属材料における樹脂層(B)上に、更に、塗装を行った材料は、塗装後の耐食性及び塗膜密着性に優れるものである。これにより、塗装が施された被覆金属材料は、金属缶蓋材、電気製品、金属家具用の金属材料等に好適に使用することができる。
【0048】
本発明の被覆金属材料は、ラミネート材の製造に用いられるものであることが好ましい。即ち、上記被覆金属材料にラミネートフィルムを被覆することにより、ラミネートフィルムで被覆された被覆金属材料を製造することができ、得られた材料は、ラミネートフィルムによって表面が保護されたものであり、耐食性、フィルム密着性にも優れるものである。これにより、ラミネートフィルムで被覆された被覆金属材料は、金属缶、電気製品、金属家具用の金属材料等に好適に使用することができる。
【0049】
上記ラミネートフィルムを構成する樹脂としては特に限定されないが、例えば、上記熱可塑性ポリエステル系樹脂等を挙げることができる。
上記熱可塑性ポリエステル系樹脂としては特に限定されず、例えば、エチレンテレフタレート単位、エチレンナフタレート単位、エチレンイソフタレート単位、ブチレンテレフタレート単位、1,4−シクロヘキサンジメタノールテレフタレート単位等の構成単位からなる熱可塑性ポリエステル系樹脂を挙げることができる。2以上の上記構成単位を有する共重合熱可塑性ポリエステル系樹脂であってもよい。エチレンテレフタレート単位からなるポリエチレンテレフタレート樹脂又はナフタレンテレフタレート単位からなるポリエチレンナフタレート樹脂がより好ましい。
【0050】
上記熱可塑性ポリエステル樹脂は、フィルムを形成した後金属にラミネートするものであっても、加熱溶融した上記熱可塑性ポリエステル樹脂を押出し成形機の押出し幅の狭いスリットによってフィルム状に押出し、直接金属板上にラミネートするダイレクトラミネーションによるものであってもよい。上記フィルムを形成した後でラミネートする場合、上記フィルムとしては特に限定されず、例えば、未延伸フィルムであっても一軸延伸フィルムであっても二軸延伸フィルムであってもよい。
【0051】
本発明のノンクロム金属表面処理方法は、クロムを含有しない表面処理剤を用いて被処理物を処理し、次いでポリアリルアミンの水溶液で処理する方法が好ましい。本発明のノンクロム金属表面処理方法による処理を行った被処理物に塗装を施すと、優れた塗装後耐食性、塗膜密着性を付与することができ、ラミネートフィルムを接着すると、接着後において優れた耐食性、フィルム密着性を付与することができる。特に、アルミニウム又はアルミニウム合金に対して、好適に適用することができるものであり、例えば、金属缶、電気製品、金属家具用のアルミニウム又はアルミニウム合金に適用することにより優れた耐食性、塗膜密着性、フィルム密着性を付与することができるものである。
【0052】
本発明のノンクロム金属表面処理方法は、先ず、水溶性ジルコニウム化合物及び/又は水溶性チタン化合物とリン化合物とからなるノンクロム金属表面処理剤(C)で被処理物を処理する工程(工程(I))を行うものである。上記工程(I)を行うことにより、金属製基材上に、ジルコニウム及び/又はチタンとリンとを含んでなる表面処理層を形成することができる。
【0053】
上記工程(I)において使用するノンクロム金属表面処理剤(C)は、水溶性ジルコニウム化合物及び/又は水溶性チタン化合物を含有するものである。これにより、耐食性、密着性に優れる被覆金属材料を得ることができる。
【0054】
上記水溶性ジルコニウム化合物としては、水溶性であるジルコニウム含有化合物であれば特に限定されないが、短時間での皮膜形成性に優れることから、水溶性錯フッ化ジルコニウムであることが好ましい。
上記水溶性錯フッ化ジルコニウムとしては特に限定されず、例えば、上述したフッ化ジルコニウム水素酸を挙げることができる。
【0055】
上記水溶性チタン化合物としては、水溶性であるチタン含有化合物であれば特に限定されないが、短時間での皮膜形成性に優れることから、水溶性錯フッ化チタンであることが好ましい。
上記水溶性錯フッ化チタンとしては特に限定されず、例えば、上述したフッ化チタン水素酸を挙げることができる。
【0056】
上記ノンクロム金属表面処理剤(C)は、上記水溶性錯フッ化ジルコニウム及び/又は上記水溶性錯フッ化チタンの含有量がジルコニウム及び/又はチタン原子換算で、下限40ppm、上限1000ppmであることが好ましい。40ppm未満であると、短時間処理で充分なジルコニウム又はチタン皮膜量が得られず、密着性、耐食性が低下するおそれがある。1000ppmを超えると、塗膜密着性、フィルム密着性が低下するおそれがあり、また、性能向上、処理時間の短縮は認められず、コスト高となるおそれもある。上記下限は、100ppmであることがより好ましく、上記上限は、300ppmであることがより好ましい。なお、上記水溶性錯フッ化ジルコニウム及び/又は上記水溶性錯フッ化チタンの含有量とは、ノンクロム金属表面処理剤(C)中に含まれるジルコニウムとチタンとの合計の含有量である。
【0057】
上記工程(I)において使用するノンクロム金属表面処理剤(C)は、リン化合物を含有するものである。これにより、耐食性、密着性に優れる被覆金属材料を得ることができる。
【0058】
上記リン化合物としては、水溶性であるリン含有化合物であれば特に限定されないが、短時間での皮膜形成性に優れることから、オルソリン酸、ホスホン基を構成するリン原子が炭素原子と結合した有機ホスホン酸化合物であることが好ましい。
上記有機ホスホン酸化合物としては特に限定されず、例えば、上述した有機ホスホン酸化合物を挙げることができる。
【0059】
上記ノンクロム金属表面処理剤(C)は、上記リン化合物の含有量が、リン原子換算で、下限20ppm、上限500ppmであることが好ましい。20ppm未満であると、短時間処理で充分なリン皮膜量が得られず、密着性が低下するおそれがある。500ppmを超えても、皮膜形成速度は向上せず、過剰に存在することになるだけで密着性、耐食性を向上させる効果は見られず、コスト高となるおそれがある。上記下限は、50ppmであることがより好ましく、上記上限は、200ppmであることがより好ましい。
【0060】
上記工程(I)で使用されるノンクロム金属表面処理剤(C)は、上記成分の他に必要に応じて、更に、皮膜形成促進剤、エッチング助剤、キレート剤、pH調整剤を使用することができる。
【0061】
上記皮膜形成促進剤としては特に限定されず、例えば、硼酸を挙げることができる。
上記エッチング助剤としては、例えば、フッ化水素酸、フッ化水素酸塩、フッ化硼素酸等を挙げることができる。なお、フッ素イオンの供給源として、上記水溶性錯フッ化ジルコニウム、上記水溶性錯フッ化チタンを用いる場合には、生成するフッ素イオンの量が不充分であるので、上記フッ素化合物を併用することが好ましい。
【0062】
上記キレート剤としては、例えば、クエン酸、酒石酸、グルコン酸等、アルミニウムと錯体を形成する酸及びそれらの金属塩等を挙げることができる。
【0063】
上記pH調整剤としては、例えば、硝酸、過塩素酸、硫酸、硝酸ナトリウム、水酸化アンモニウム、水酸化ナトリウム、アンモニア等の表面処理に悪影響を与えない酸又は塩基を挙げることができる。
【0064】
上記工程(I)で使用されるノンクロム金属表面処理剤(C)は、pHの下限が1.4、上限が4.0であることが好ましい。1.4未満であると、金属表面のエッチングが促進され過ぎるため、充分な皮膜量が得られないとともに、皮膜外観不良の原因ともなる。4.0を超えると、化成反応が満足に進行せず、充分な皮膜量が得られないおそれがある。上記下限は、1.8であることがより好ましく、2.0であることが更に好ましい。上記上限は、3.2であることがより好ましく、3.0であることが更に好ましい。
【0065】
上記工程(I)において、上記被処理物としては、例えば、上述した金属製基材を挙げることができる。
上記工程(I)において、上記被処理物を処理する方法としては、上記被処理物を上記ノンクロム金属表面処理剤(C)に接触させる方法であれば特に限定されず、スプレー法、浸漬法等の通常の方法を挙げることができる。なかでも、スプレー法で行うことが好ましい。
【0066】
上記工程(I)において、上記ノンクロム金属表面処理剤(C)の処理温度としては、好ましい下限は30℃、好ましい上限は80℃であり、より好ましい下限は40℃、より好ましい上限は60℃である。30℃未満であると、反応性が低く、皮膜の析出性が悪くなり、耐食性が低下するおそれがある。80℃を超えても、反応性は向上せず、エネルギーのロスが大きくなるおそれがある。
【0067】
上記工程(I)において、スプレー法で処理する場合には、上記ノンクロム金属表面処理剤(C)の処理時間は、好ましい下限は1秒、好ましい上限は20秒であり、より好ましい下限は3秒、より好ましい上限は8秒である。1秒未満であると、形成される皮膜量が充分でないおそれがあり、20秒を超えると、皮膜形成時のエッチングが過度に進行し、密着性、耐食性が低下するおそれがある。
【0068】
上記工程(I)の後、必要に応じて水洗処理を行うことができる。
上記化成後水洗処理は、塗膜外観等に悪影響を及ぼさないようにするために、1回又はそれ以上により行われるものである。この場合、最終の水洗は、純水で行われることが適当である。この水洗処理においては、スプレー水洗又は浸漬水洗のどちらでもよく、これらの方法を組み合わせて水洗することもできる。
【0069】
本発明のノンクロム金属表面処理方法は、上記工程(I)を行った被処理物をポリアリルアミン水溶液(D)で処理する工程(工程(II))を行うものである。上記工程(II)で使用するポリアリルアミンは、上述したポリアリルアミンを用いることができる。即ち、上述したポリアリルアミンを水に溶解したものをポリアリルアミン水溶液(D)として使用し、処理することによって行うことができる。上記工程(II)を行うことにより、ポリアリルアミンを含んでなる樹脂層を形成することができる。
【0070】
上記ポリアリルアミン水溶液(D)は、ポリアリルアミンの含有量が質量基準で、下限100ppm、上限10000ppmであることが好ましい。100ppm未満であると、塗装後、ラミネート後の密着性が低下するおそれがある。10000ppmを超えると、耐食性は向上せず、コスト高となるおそれがある。上記下限は、500ppmであることがより好ましく、上記上限は、5000ppmであることがより好ましい。
【0071】
上記ポリアリルアミン水溶液(D)は、特にpHを調整する必要は無く、適宜設定するポリアリルアミン量を溶解した水溶液を用いることができる。上記ポリアリルアミン水溶液(D)のpHは、特にpHを調整しない水溶液を用いる場合には、通常、10〜12程度である。
【0072】
上記工程(II)において、上記ポリアリルアミン水溶液(D)で処理する方法としては、上記工程(I)を行った被処理物を上記ポリアリルアミン水溶液(D)に接触させる方法であれば特に限定されず、スプレー法、浸漬法、ロールコート法等の通常の方法を挙げることができる。なかでも、スプレー法で行うことが好ましい。ポリアリルアミンの付着量を均一にするため、スプレー処理後は、ゴムロール絞り、エアブロー等により、被処理物表面に残った過剰の液を取り除くことが好ましい。被処理物が板状である場合、ゴムロール絞り法が好ましい。
【0073】
上記工程(II)において、上記ポリアリルアミン水溶液(D)の処理温度は、皮膜形成性が温度の影響を受けないので、特に処理温度の調整を行う必要はないが、処理後の乾燥を容易にするため、下限20℃であることが好ましく、また、エネルギーロスが大きくなる可能性があるので、上限60℃であることが好ましい。
【0074】
上記工程(II)において、スプレー法で処理する場合には、上記ポリアリルアミン水溶液(D)の処理時間は、好ましい下限は1秒、好ましい上限は10秒であり、より好ましい下限は2秒、より好ましい上限は6秒である。1秒未満であると、形成される皮膜量が充分でなく、塗装後、ラミネート後の密着性が低下するおそれがある。10秒を超えても、皮膜形成性に影響を与えず、生産性を低下させるおそれがある。上記工程(II)を行った後は、ゴムロール等を用いて素材表面の過剰な液を除去し、水洗は行わないことが好ましい。水洗を行った場合、工程(II)によって付着したポリアリルアミンが洗い流されてしまうおそれがあるためである。
【0075】
上記工程(I)及び上記工程(II)を行うことにより、金属製基材上に、ジルコニウム及び/又はチタンとリンとを含んでなる表面処理層及びポリアリルアミンを含んでなる樹脂層が形成された被覆金属材料を得ることができ、得られた被覆金属材料は、更に、塗装する場合には、塗装後耐食性、塗膜密着性に優れるものであり、また、更に、ラミネートフィルムを貼り付ける場合には、フィルム貼り付け後における耐食性、フィルム密着性に優れるものである。
【0076】
本発明のノンクロム金属表面処理方法において、上記工程(I)及び上記工程(II)を行った後に、乾燥することが好ましい。乾燥方法としては、加熱乾燥が好ましく、例えば、オーブン乾燥及び/又は熱空気の強制的循環による加熱乾燥を挙げることができる。
【0077】
上記乾燥において、乾燥温度は、素材温度として、下限40℃、上限120℃であることが好ましい。上記下限は、60℃であることがより好ましく、上記上限は、80℃であることがより好ましい。また、乾燥時間は、乾燥方法により適宜設定することができ、通常、下限6秒、上限60秒である。
【0078】
本発明のノンクロム金属表面処理方法は、上記ノンクロム金属表面処理剤(C)による処理が行われる前に酸で洗浄する工程が行われることが好ましい。更に、酸で洗浄する工程の前にアルカリで洗浄する工程が行われることが好ましい。より好ましい態様は、アルカリ洗浄、水洗、酸洗浄、水洗、ノンクロム金属表面処理剤(C)による処理(工程(I))、水洗、純水洗、ポリアリルアミン水溶液(D)による処理(工程(II))、ゴムロール絞り、乾燥の各工程を順次行う方法、又は、酸洗浄、水洗、ノンクロム金属表面処理剤(C)による処理(工程(I))、水洗、純水洗、ポリアリルアミン水溶液(D)による処理(工程(II))、ゴムロール絞り、乾燥の各工程を順次行う方法である。
【0079】
上記アルカリ洗浄処理としては特に限定されず、例えば、従来アルミニウムやアルミニウム合金等の金属のアルカリ洗浄処理に用いられてきたアルカリ洗浄を行うことができる。上記アルカリ洗浄処理において、通常、アルカリ洗浄はアルカリ性クリーナーを用いて行われる。また、上記酸洗浄は酸性クリーナーを用いて行われる。
【0080】
上記アルカリ性クリーナーとしては特に限定されず、例えば、通常のアルカリ洗浄に用いられるものを用いることができ、例えば、日本ペイント社製「サーフクリーナーEC370」等を挙げることができる。上記酸性クリーナーとしては特に限定されず、例えば、硫酸、硝酸、塩酸等の無機酸;日本ペイント社製「サーフクリーナーST160」等を挙げることができる。
【0081】
上記酸洗浄及びアルカリ洗浄処理は、通常、スプレー法で行われる。上記酸洗浄又はアルカリ洗浄処理を行った後は、基材表面に残存する酸洗浄液又はアルカリ洗浄剤を除去するために、水洗処理を行う。
【0082】
本発明のノンクロム金属表面処理方法により得られる皮膜において、各成分の皮膜量は、ノンクロム金属表面処理剤(C)の組成、ポリアリルアミン水溶液(D)の組成、それぞれの処理温度、処理時間を適宜設定することによって所望の皮膜量を得ることができる。
【0083】
本発明の被覆金属材料は、金属製基材上に、ジルコニウム及び/又はチタンとリンとを含んでなる表面処理層(A)を有し、更に、上記表面処理層(A)上に、ポリアリルアミンを含んでなる樹脂層(B)を有するものであることから、塗装後における耐食性及び塗膜密着性に優れるものであり、また、ラミネートフィルム貼り付け後における耐食性及びフィルム密着性にも優れるものである。特に、上記被覆金属材料における金属製基材としてアルミニウム又はアルミニウム合金を用い、ジルコニウム及び/又はチタンが水溶性錯フッ化ジルコニウム及び/又は水溶性錯フッ化チタンに由来するものであり、リンはオルソリン酸又は有機ホスホン酸化合物に由来するものである場合に得られるものは、密着性、耐食性により優れるものである。また、本発明のノンクロム金属表面処理方法は、耐食性及び密着性に優れる被覆金属材料を得ることができる方法である。従って、上記ノンクロム金属表面処理方法を適用することにより得られる被覆金属材料は、塗装後における耐食性及び密着性に優れるものであり、ラミネートフィルム貼り付け後における耐食性及びフィルム密着性に優れるものであることから、例えば、金属缶、電気製品、金属家具等の用途に好適に用いることができるものである。
【実施例】
以下本発明について実施例を掲げて更に詳しく説明するが、本発明はこれらの実施例のみに限定されるものではない。また実施例中、「部」は特に断りのない限り「質量部」を意味する。
【0084】
(水溶性錯フッ化ジルコニウム及びリン酸含有ノンクロム金属表面処理剤の調製)
イオン交換水9996.7部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、日本軽金属社製「フッ化ジルコニウム水素酸」(Zrとして17.6%含有)2.3部を徐々に添加した。更に、攪拌しながら、75%リン酸0.8部を徐々に添加した。次いで、攪拌しながら、フッ化水素酸0.2部を徐々に添加した。続いて、攪拌しながら、アンモニアを添加し、処理剤のpHを2.6に調整した。10分攪拌を継続し、フッ化ジルコニウム水素酸をジルコニウムとして40ppm含有し、リン酸をリンとして20ppm含有する無色透明のノンクロム金属表面処理剤を得た。同様の方法で、表1、2に実施例、比較例として示された配合比率で、フッ化ジルコニウム水素酸のジルコニウムとリン酸のリンとを含有するノンクロム金属表面処理剤を得た。
【0085】
(水溶性錯フッ化ジルコニウム及び有機ホスホン酸化合物含有ノンクロム金属表面処理剤の調製)
イオン交換水9996.8部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、日本軽金属社製「フッ化ジルコニウム水素酸」(Zrとして17.6%含有)2.3部を徐々に添加した。更に、攪拌しながら、1−ヒドロキシエチリデン−1,1−ジホスホン酸0.7部を徐々に添加した。次いで、攪拌しながら、フッ化水素酸0.2部を徐々に添加した。続いて、攪拌しながら、アンモニアを添加し、処理剤のpHを2.6に調整した。10分攪拌を継続し、フッ化ジルコニウム水素酸をジルコニウムとして40ppm含有し、1−ヒドロキシエチリデン−1,1−ジホスホン酸をリンとして20ppm含有する無色透明のノンクロム金属表面処理剤を得た。同様の方法で、表1、2に実施例、比較例として示された配合比率で、フッ化ジルコニウム水素酸のジルコニウムと1−ヒドロキシエチリデン−1,1−ジホスホン酸のリンとを含有するノンクロム金属表面処理剤を得た。
【0086】
(水溶性錯フッ化チタン及びリン酸含有ノンクロム金属表面処理剤の調製)
イオン交換水9997.6部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、森田化学工業社製「フッ化チタン水素酸」(Tiとして29.3%含有)1.4部を徐々に添加した。更に、攪拌しながら、75%リン酸0.8部を徐々に添加した。次いで、攪拌しながら、フッ化水素酸0.2部を徐々に添加した。続いて、攪拌しながら、アンモニアを添加し、処理剤のpHを2.6に調整した。10分攪拌を継続し、フッ化チタン水素酸をチタンとして40ppm含有し、リン酸をリンとして20ppm含有する無色透明のノンクロム金属表面処理剤を得た。同様の方法で、表1、2に実施例、比較例として示された配合比率で、フッ化チタン水素酸のチタンとリン酸のリンとを含有するノンクロム金属表面処理剤を得た。
【0087】
(水溶性錯フッ化チタン及び有機ホスホン酸化合物含有ノンクロム金属表面処理剤の調製)
イオン交換水9997.7部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、森田化学工業社製「フッ化チタン水素酸」(Tiとして29.3%含有)1.4部を徐々に添加した。更に、攪拌しながら、1−ヒドロキシエチリデン−1,1−ジホスホン酸0.7部を徐々に添加した。次いで、攪拌しながら、フッ化水素酸0.2部を徐々に添加した。続いて、攪拌しながら、アンモニアを添加し、処理剤のpHを2.6に調整した。10分攪拌を継続し、フッ化チタン水素酸をチタンとして40ppm含有し、1−ヒドロキシエチリデン−1,1−ジホスホン酸をリンとして20ppm含有する無色透明のノンクロム金属表面処理剤を得た。同様の方法で、表1、2に実施例、比較例として示された配合比率で、フッ化チタン水素酸のチタンと1−ヒドロキシエチリデン−1,1−ジホスホン酸のリンとを含有するノンクロム金属表面処理剤を得た。
【0088】
(水溶性錯フッ化ジルコニウム、水溶性錯フッ化チタン及びリン酸含有ノンクロム金属表面処理剤の調製)
イオン交換水9997.1部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、フッ化ジルコニウム水素酸1.2部、続いてフッ化チタン水素酸0.7部を徐々に添加した。更に、攪拌しながら、75%リン酸0.8部を徐々に添加した。次いで、攪拌しながら、フッ化水素酸0.2部を徐々に添加した。続いて、攪拌しながら、アンモニアを添加し、処理剤のpHを2.6に調整した。10分攪拌を継続し、フッ化ジルコニウム水素酸をジルコニウムとして20ppm、フッ化チタン水素酸をチタンとして20ppm、リン酸をリンとして20ppm含有する無色透明のノンクロム金属表面処理剤を得た。同様の方法で、表1、2に実施例、比較例として示された配合比率で、フッ化ジルコニウム水素酸のジルコニウムとフッ化チタン水素酸のチタンとリン酸のリンとを含有するノンクロム金属表面処理剤を得た。
【0089】
(水溶性錯フッ化ジルコニウム、水溶性錯フッ化チタン及び有機ホスホン酸化合物含有ノンクロム金属表面処理剤の調製)
イオン交換水9997.2部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、フッ化ジルコニウム水素酸1.2部、続いてフッ化チタン水素酸0.7部を徐々に添加した。更に、攪拌しながら、1−ヒドロキシエチリデン−1,1−ジホスホン酸0.7部を徐々に添加した。次いで、攪拌しながら、フッ化水素酸0.2部を徐々に添加した。続いて、攪拌しながら、アンモニアを添加し、処理剤のpHを2.6に調整した。10分攪拌を継続し、フッ化ジルコニウム水素酸をジルコニウムとして20ppm、フッ化チタン水素酸をチタンとして20ppm、1−ヒドロキシエチリデン−1,1−ジホスホン酸をリンとして20ppm含有する無色透明のノンクロム金属表面処理剤を得た。同様の方法で、表1、2に実施例、比較例として示された配合比率で、フッ化ジルコニウム水素酸のジルコニウムとフッ化チタン水素酸のチタンと1−ヒドロキシエチリデン−1,1−ジホスホン酸のリンとを含有するノンクロム金属表面処理剤を得た。
【0090】
(ポリアリルアミン水溶液の調製)
イオン交換水9996部を攪拌装置付きベッセルに仕込んだ。常温にて攪拌しながら、日東紡績社製「PAA−05」(ポリアリルアミン、不揮発分20%含有)4部を徐々に添加した。10分攪拌を継続し、塩構造を持たないポリアリルアミンを80ppm含有する無色透明のポリアリルアミン水溶液を得た。同様の方法で、ポリアリルアミンを1000ppm、5000ppm、10000ppm含有する無色透明のポリアリルアミン水溶液を得た。
【0091】
(アミノ基含有樹脂水溶液の調製(比較樹脂成分))
ポリアリルアミンの代わりに、三菱化学社製「PVAM−0595B」(ポリビニルアミン)、和光純薬工業社製「アクリルアミドポリマー水溶液」(ポリアクリルアミド)、日本触媒社製「エポミンP−1000」(ポリエチレンイミン)を用い、上記ポリアリルアミン水溶液の調製と同様の方法で、それぞれ樹脂分を1000ppm含有するアミノ基含有樹脂水溶液を得た。
また、ポリアリルアミンの強酸塩として、日東紡績社製「PAA−HCl−3L」(PAA−10Cの塩酸塩)を用い、同様の方法で、樹脂分を1000ppm含有するアミノ基含有樹脂水溶液を得た。
【0092】
実施例1〜24、比較例1〜4
(ノンクロム金属表面処理材の作成)
板厚0.30mmのアルミニウム合金3004板材両面を、日本ペイント社製アルカリクリーナー「サーフクリーナーEC370」の1%希釈液を用いて洗浄し(65℃×3秒)、水洗し、続いて硫酸1%希釈液を用いて洗浄し(50℃×3秒)、水洗し、得られたアルミニウム材に、上記方法により調製され、表1及び表2に示した成分を有するノンクロム金属表面処理剤をスプレー装置により化成処理し(50℃×5秒)、水洗し、純水洗し、室温のポリアリルアミン水溶液又はアミノ基含有樹脂水溶液をスプレー装置によりそれぞれ2秒間処理を行った後、ゴムロールを用いて素材表面に付着した過剰な樹脂水溶液を絞りとった。その後、素材温度80℃にて30秒間乾燥させ、ノンクロム金属表面処理材を得た。
【0093】
比較例5〜7
上記ノンクロム金属表面処理材の作成において、室温のアミノ基含有樹脂水溶液で処理しなかった以外は同様の方法で処理し、ノンクロム金属表面処理材を得た。
【0094】
比較例8〜9
(ポリアリルアミン表面処理材の作成)
上記ノンクロム金属表面処理材の作成において、アルカリ脱脂、酸洗浄、水洗、純水洗の後、金属表面処理剤による化成処理を行わずに室温のポリアリルアミン水溶液を同様の方法で処理し、ポリアリルアミン表面処理材を得た。
【0095】
比較例10
(クロメート処理材の作成)
ノンクロム金属表面処理剤で化成処理し、ポリアリルアミン水溶液で処理を行う代わりに、日本ペイント社製「アルサーフ401/45」を用いた以外は、上記ノンクロム金属表面処理材の作成と同様にして、リン酸クロメート処理を施したクロメート処理材を作成した。
【0096】
(皮膜質量測定)
実施例及び比較例によって得られたノンクロム金属表面処理材、クロメート処理材における乾燥皮膜中のジルコニウム、チタン、クロムの質量を、島津製作所社製 蛍光X線分析装置「XRF−1700」を用いて測定した。
ノンクロム金属表面処理材、ポリアリルアミン表面処理材における乾燥皮膜中のポリアリルアミン及び各比較樹脂の質量は、米国LECO社製 形態別炭素/水分分析装置「RC412」を用いて各樹脂由来の有機炭素質量を測定した。
上記測定により得られたジルコニウム化合物中のジルコニウムの質量をZrとして、チタン化合物中のチタンの質量をTiとして、リン酸又は1−ヒドロキシエチリデン−1,1−ジホスホン酸中のリンの質量をPとして、ポリアリルアミン又は各比較樹脂に由来する有機炭素質量をCとして、それぞれ表1、2に示した。
【0097】
(アルミ塗装材の作成)
得られたノンクロム金属表面処理材、ポリアリルアミン表面処理材、クロメート処理材に、日本ファインコーティングス社製ポリエステル系塗料「フレキコート#5000ホワイト」(不揮発分50%)を、リバースロールコーターを用いて、片面当たりウェット塗布量15g/m2なるよう塗布し、コンベアー式オーブンを用いて素材温度230℃で60秒間焼付けを行い、塗料の乾燥塗装質量が7.5g/m2であるアルミ塗装材をそれぞれ得た。
【0098】
(ラミネート材の作成)
得られたノンクロム金属表面処理材、ポリアリルアミン表面処理材、クロメート処理材に、ポリエチレンテレフタレート(PET)フィルムを乗せ、加熱ローラーを用いて、ロール温度260℃(素材温度240℃)、ロール速度30m/分にて熱圧着した直後、水冷し、ラミネート材を得た。
【0099】
(評価方法)
得られたアルミ塗装材、ラミネート材のそれぞれに対して、下記評価を行い、結果を表1、2に示した。
【0100】
1.塗装材の密着性
アルミ塗装材を100℃の沸騰水に60分間浸漬した。アルミ塗装材を沸騰水より取り出し後直ちに、1mm幅で100個のクロスカットを施し、粘着テープ剥離を行い、剥離個数を測定した。剥離個所が無いことを合格レベルとした。
【0101】
2.塗装材の耐食性
アルミ塗装材の塗装面を凸となるよう、図1に示したカップ加工を行った。カップ加工材を、50℃に保持した、2%クエン酸、2%食塩の混合水溶液に72時間浸潰し、取り出し後、図1に示した平面部1、エッジ部2及び側面部3の各部位の腐食状態を5点満点にて評価し、その平均点を算出した。
5点:腐食無し
4点:微少腐食(側面部0.5mm、腐食10ヶ所以下、エッジ部:0.5mm腐食5ヶ所以下)
3点:腐食(側面部:1mm腐食20ヶ所以下、エッジ部:1mm腐食10ヶ所以下)
2点:腐食(側面部:3mm腐食20ヶ所以下、エッジ部:3mm腐食10ヶ所以下)
1点:全面腐食(側面部、エッジ部とも半分以上腐食)
評点平均値がリン酸クロメート処理へのアルミ塗装材と同等以上の数値を示すことを合格レベルとした。
【0102】
3.ラミネート材の密着性
図2のように50mm×50mmのラミネート材のうち、ラミネート貼り付け面の裏側22(ラミネート非被覆面)にNTカッターでV字切り込み21をb−c−bのように入れ、このV字切り込み21の裾をラミネート材の端から5mmの所までa−bのように金切鋏で切断した。次いで、図3のようにV字切り込み部の裾とその両端部とを逆方向に、東洋ボールドウィン社製「テンシロン引張り試験機」にて50mm/分の速度で引っ張り、切断面のラミネートフィルム残存状態を図4に示す目視5段階評価基準に従って5点満点で評価した。
【0103】
4.ラミネート材の密着性
ラミネート材のラミネート被覆面を合わせ、ホットプレス試験機を用いて、250℃、10kg/cm2にて1分間熱圧着させた。貼り合わせたラミネート材を5mm幅に切り出し、東洋ボールドウィン社製「テンシロン引張り試験機」にて200mm/分の速度で引き剥がした際にかかる力を測定した。リン酸クロメート処理へのラミネート材と同等以上の数値(密着強度)を示すことを合格レベルとした。
【0104】
5.ラミネート材の耐食性
ラミネート材のラミネート被覆面を凸となるように図1に示したカップ加工を行い、図5に示したように円周状にカットを施した。加工材を、50℃に保持した2%クエン酸、2%食塩の混合水溶液に144時間浸漬し、取り出し後、カット部からの腐食の広がり長さを測定した。
【0105】
【表1】
【0106】
【表2】
【0107】
実施例により得られた被覆金属材料は、塗装後の密着性及び耐食性に優れ、ラミネート材の密着性及び耐食性に優れるものであり、リン酸クロメート処理を行ったものと同等以上の性能を示すものであった。
【0108】
これに対して、比較樹脂成分として、ポリビニルアミン、ポリアクリルアミド、ポリエチレンイミン、ポリアリルアミンの強酸塩を用いた場合、化成処理を行わなかった場合に得られたものは、塗装後の密着性及び耐食性、並びに、ラミネート材の密着性及び耐食性に劣るものであった。
【0109】
【発明の効果】
本発明の被覆金属材料は、上述した構成よりなるので、塗装後における塗膜密着性及び耐食性に優れるものであり、また、ラミネートフィルム貼り付け後のフィルム密着性及び耐食性にも優れるものである。また、本発明のノンクロム金属表面処理方法は、上記被覆金属材料を得ることができる方法である。従って、上記ノンクロム金属表面処理方法を適用することによって得られる被覆金属材料は、密着性、耐食性に優れるものであることから、例えば、飲料缶、家電向け等の用途に好適に使用することができるものである。
【図面の簡単な説明】
【図1】 塗装材の耐食性評価のための被検物の形状の模式図を示す。
【図2】 密着性評価のための切り込みを入れたラミネート材のラミネート非被覆面の概略図を示す。
【図3】 テンシロン引張り試験機による引っ張り方向の模式図を示す。
【図4】 密着性評価における目視5段階評価基準を示す切り込み部の拡大図を示す。
【図5】 ラミネート材の耐食性評価のための被検物の形状の模式図を示す。
【符号の説明】
1 平面部
2 エッジ部
3 側面部
21 切り込み
22、31 非被覆面
23 圧延目
32 円周状カット部[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a coated metal material and a non-chromium metal surface treatment method.
[Prior art]
[0002]
Conventionally, as a surface treatment of an aluminum plate, a phosphate chromate-based chemical conversion treatment agent that can be subjected to chemical conversion treatment in a short time by a spray method has been used.
The phosphate chromate conversion coating formed using a phosphate chromate conversion treatment agent has excellent corrosion resistance and adhesion after coating various resin paints, so it is suitable for building materials, home appliances, fin materials, cars It is used in a wide range of aluminum materials, such as for evaporators and beverage can lids.
[0003]
However, in recent years, for the purpose of environmental protection, paints and laminates can be given high corrosion resistance and adhesion equivalent to those of phosphate chromate, and in the same manner as phosphate chromate conversion treatment, a short spray method Therefore, there is an increasing demand for a non-chromium chemical conversion treatment capable of forming a chemical conversion film.
[0004]
As the non-chromic chemical conversion treatment agent by the spray method, for example, a system in which a zirconium compound or a titanium compound and a phosphoric acid compound are used in combination is used for a beverage can body or the like.
[0005]
However, conversion coatings formed with these types of treatment agents are inferior in corrosion resistance and adhesion after coating of paint and pasting a laminate film compared to phosphoric acid chromate conversion coatings, so that they can be used in a wide range of applications. It wasn't.
[0006]
[Problems to be solved by the invention]
In view of the current situation, the present invention is a coated metal material having excellent corrosion resistance and adhesion after coating of a paint and after laminating a film, and having a performance equal to or higher than that of a phosphate chromate conversion treatment, and a non-chromium metal The object is to provide a surface treatment method.
[0007]
[Means for Solving the Problems]
The present invention Aluminum or aluminum alloy above, Derived from water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride It has a surface treatment layer (A) containing zirconium and / or titanium and phosphorus, and further has a resin layer (B) containing polyallylamine on the surface treatment layer (A). It is a covering metal material.
[0008]
The zirconium and / or titanium is preferably derived from water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride.
The phosphorus is preferably derived from orthophosphoric acid.
The phosphorus is preferably derived from an organic phosphonic acid compound in which a phosphorus atom constituting a phosphonic group is bonded to a carbon atom.
[0009]
The surface treatment layer (A) is a mass per one side after drying, and the content of zirconium and / or titanium is 3 to 30 mg / m. 2 The phosphorus content is 0.5-5 mg / m 2 The resin layer (B) has a mass per one side after drying, and the content of carbon derived from polyallylamine is 1.6 to 200 mg / m. 2 It is preferable that
[0010]
The metal substrate is preferably aluminum or an aluminum alloy. It is preferable that the said covering metal material is what is used for manufacture of a laminate material.
[0011]
The present invention Water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride And phosphorus compounds including With non-chromium metal surface treatment agent (C) Aluminum or aluminum alloy The step (I) of treating the above and the above step (I) were performed. Aluminum or aluminum alloy Step (II) of treating with a polyallylamine aqueous solution (D) including This is a non-chromium metal surface treatment method.
[0012]
The water-soluble zirconium compound and / or the water-soluble titanium compound is preferably water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride.
[0013]
In the non-chromium metal surface treatment agent (C), the content of the water-soluble complex zirconium fluoride compound and / or the water-soluble complex titanium fluoride compound is 40 to 1000 ppm in terms of zirconium and / or titanium atoms, and the content of the phosphorus compound is It is 20 to 500 ppm in terms of phosphorus atom, and the polyallylamine aqueous solution (D) preferably has a polyallylamine content of 80 to 10,000 ppm on a mass basis.
The present invention is described in detail below.
[0014]
The coated metal material of the present invention is excellent in corrosion resistance after coating a paint and after bonding a resin film such as a laminate film. Also, the film adhesion after coating a paint film, a film after bonding a resin film such as a laminate film, etc. It is a metal material with excellent adhesion.
[0015]
The coated metal material of the present invention has a surface treatment layer (A) comprising zirconium and / or titanium and phosphorus on a metal substrate.
The coated metal material of the present invention is provided with excellent corrosion resistance because a layer containing zirconium and / or titanium and phosphorus is formed on a metal substrate. The surface treatment layer (A) can be formed, for example, by treating a metal substrate with a water-soluble zirconium compound and / or a non-chromium metal surface treatment agent containing a water-soluble titanium compound and a phosphorus compound.
[0016]
The zirconium and / or titanium is preferably derived from water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride. That is, the case where the water-soluble complex zirconium fluoride and / or the water-soluble complex titanium fluoride is used as a zirconium and / or titanium supply source is preferable. For example, when the treatment is performed using a non-chromium metal surface treatment agent containing water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride, it is more efficient because it is excellent in film formation in a short time. A surface treatment layer (A) can be formed.
[0017]
The water-soluble complex zirconium fluoride is not particularly limited, for example, H 2 ZrF 6 , (NH 4 ) 2 ZrF 6 , K 2 ZrF 6 , Na 2 ZrF 6 , Li 2 ZrF 6 Etc. These may be used alone or in combination of two or more.
[0018]
The water-soluble complex titanium fluoride is not particularly limited. For example, H 2 TiF 6 , (NH 4 ) 2 TiF 6 , K 2 TiF 6 , Na 2 TiF 6 Etc. These may be used alone or in combination of two or more.
[0019]
The surface treatment layer (A) is a mass per one side after drying, and the content of zirconium and / or titanium is 3 mg / m at the lower limit. 2 , Upper limit 30mg / m 2 It is preferable that 3mg / m 2 If it is less than the range, adhesion and corrosion resistance after coating and lamination will be reduced. 30 mg / m 2 If it exceeds 1, adhesion after coating and lamination will be reduced, and no improvement in corrosion resistance will be seen. The lower limit is 8 mg / m 2 More preferably, the upper limit is 20 mg / m 2 It is more preferable that
[0020]
The phosphorus compound as the phosphorus source is not particularly limited. For example, orthophosphoric acid, ammonium phosphate, sodium monophosphate, sodium diphosphate, sodium triphosphate, phosphorous acid, hypophosphorous acid And sodium hypophosphite, organic phosphorus compounds, and organic phosphonic acid compounds.
[0021]
The phosphorus is preferably derived from orthophosphoric acid. That is, it is preferable to use the orthophosphoric acid as a phosphorus source. For example, when the treatment is performed using a non-chromium metal surface treatment agent containing orthophosphoric acid, the surface treatment layer (A) can be formed more efficiently because of excellent film formation in a short time.
[0022]
The phosphorus is preferably derived from an organic phosphonic acid compound in which a phosphorus atom constituting a phosphonic group is bonded to a carbon atom. That is, it is preferable to use an organic phosphonic acid compound in which a phosphorus atom constituting the phosphonic group is bonded to a carbon atom as a phosphorus supply source. For example, when the treatment is performed using the non-chromium metal surface treatment agent containing the organic phosphonic acid compound, the surface treatment layer (A) can be more efficiently formed because of excellent film formation in a short time. The formed film is excellent in corrosion resistance.
[0023]
The organic phosphonic acid compound has a phosphonic group (—PO 3 H 2 ) In the compound, and the phosphone group (—PO 3 H 2 ) Is a bonded compound.
The organic phosphonic acid compound is not particularly limited. For example, aminotri (methylenephosphonic acid) represented by the following formula (a), 1-hydroxyethylidene-1,1-diphosphonic acid represented by the following formula (b) And 2-
[0024]
[Chemical 1]
[0025]
Examples of the organic phosphonic acid compound include ethylenediaminetetra (methylenephosphonic acid) represented by the following formula (d), diethylenetriaminepenta (methylenephosphonic acid) represented by the following formula (e), and the like.
[0026]
[Chemical 2]
[0027]
Among the above organic phosphonic acid compounds, aminotri (methylene) represented by the above formula (a) is excellent in film deposition, corrosion resistance and coating film adhesion after coating, corrosion resistance and film adhesion after laminating. (Phosphonic acid), 1-hydroxyethylidene-1,1-diphosphonic acid represented by the above formula (b), and 2-
[0028]
The organic phosphonic acid compound is preferably water-soluble. In the case of a water-soluble compound, it is not necessary to use an organic solvent, and the burden on the environment can be reduced.
[0029]
The said organic phosphonic acid compound may be used independently and may use 2 or more types together. In addition, it is not preferable to add an organic phosphonic acid compound salt in which a hydrogen atom contained in a phosphonic group is substituted with an alkali metal or ammonium to the non-chromium metal surface treatment agent because the corrosion resistance of the formed film is lowered.
[0030]
The surface treatment layer (A) is the mass per one side after drying, and the phosphorus content has a lower limit of 0.5 mg / m. 2 , Upper limit 5mg / m 2 It is preferable that 0.5mg / m 2 If it is less than the range, adhesion and corrosion resistance after coating and lamination will be reduced. 5mg / m 2 If it exceeds, the adhesion after coating and after lamination will decrease. The lower limit is 1 mg / m 2 More preferably, the upper limit is 3 mg / m 2 It is more preferable that
[0031]
The coated metal material of the present invention has a resin layer (B) comprising polyallylamine on the surface treatment layer (A).
The resin layer (B) is a layer comprising polyallylamine formed on the surface treatment layer (A) in the coated metal material. Thereby, when forming a coating film on the said resin layer (B), the coating-film adhesiveness after coating-film formation can be improved, When laminating a laminate film, a laminate film The film adhesion after pasting can be improved. The resin layer (B) can be formed, for example, by treating the metal substrate on which the surface treatment layer (A) is formed with an aqueous solution containing polyallylamine.
[0032]
The coated metal material of the present invention has a resin layer (B) containing polyallylamine, so that the coating film adhesion after forming the coating film specifically, the film adhesion after pasting the laminated film. Can be improved. That is, the following general formula (1);
[0033]
[Chemical 3]
[0034]
In the case of having a resin layer comprising polyallylamine represented by the formula, the effect of improving coating film adhesion and film adhesion can be seen. In the case of having a resin layer comprising polyvinylamine, polyacrylamide, and polyethyleneimine represented by the following general formula (4), the effect of improving coating film adhesion and film adhesion is not observed.
[0035]
[Formula 4]
[0036]
[Chemical formula 5]
[0037]
[Chemical 6]
[0038]
In addition, for example, even when a resin layer containing a polyallylamine strong acid salt represented by the following general formula (5) is included, the effect of improving coating film adhesion and film adhesion is not observed. Thus, when it has a resin layer containing polyallylamine, the coating of the present invention can specifically improve the coating film adhesion after forming the coating film and the film adhesion after laminating the laminated film. This is a characteristic point of metal materials.
[0039]
[Chemical 7]
[0040]
The polyallylamine in the resin layer (B) is not particularly limited. For example, PAA-01, PAA-03, PAA-05, PAA-15, PAA-15B, PAA-10C, PAA-H-10C (all Commercial products such as Nitto Boseki Co., Ltd.) can be used. These may be used alone or in combination of two or more.
The polyallylamine may be one obtained by copolymerizing a small amount of other monomers within a range not impairing the effects of the present invention.
[0041]
The weight average molecular weight of the polyallylamine is preferably 1000 as the lower limit and 150,000 as the upper limit. By being in this range, the coating film adhesion after coating and the film adhesion after applying the laminate film can be made excellent. The lower limit is more preferably 1000, and the upper limit is more preferably 5000.
[0042]
The polyallylamine in the resin layer (B) neutralizes the primary amine contained with an acid in order to adjust the pH of the aqueous solution when a polyallylamine aqueous solution is used when forming the resin layer (B). You can also. As a neutralizing agent, when neutralized with a strong acid, for example, it becomes a polyallylamine strong acid salt represented by the above general formula (5), and the coating film adhesion after coating, film adhesion after laminating film sticking It is not preferable because the properties are lowered, and it is preferable to use a weak acid such as acetic acid.
[0043]
The resin layer (B) is the mass per one side after drying, and the content of carbon derived from polyallylamine is the lower limit of 1.6 mg / m. 2 , Upper limit 200mg / m 2 It is preferable that 1.6mg / m 2 If it is less than the range, the adhesion after coating and laminating decreases. 200 mg / m 2 If it exceeds 1, adhesion and corrosion resistance are not improved, and the cost is increased. The lower limit is 10 mg / m 2 More preferably, the upper limit is 100 mg / m 2 It is more preferable that
[0044]
The content of zirconium and / or titanium in the film formed on the coated metal material of the present invention (the film comprising the surface treatment layer (A) and the resin layer (B)) is measured by a fluorescent X-ray analyzer. The carbon content derived from the polyallylamine can be measured by the amount of organic carbon measured by the carbon / water analyzer classified by form.
[0045]
The metal substrate is preferably aluminum or an aluminum alloy. That is, the coating metal material has the surface treatment layer (A) on a metal substrate made of aluminum or an aluminum alloy, and further has the resin layer (B) on the surface treatment layer (A). It is preferable. The metal substrate is preferably plate-shaped. The coated metal material obtained by using aluminum or an aluminum alloy as a metal base material is excellent in corrosion resistance and paint film adhesion after coating, so it is suitable for beverage containers, home appliances, residential building materials, etc. It can use suitably for a use.
[0046]
The aluminum alloy is not particularly limited, and for example, aluminum alloy 5182 material, aluminum alloy 5021 material, aluminum alloy 5022 material, aluminum alloy 5052 material, aluminum alloy 3004 material, aluminum alloy 3005 material, aluminum alloy 1050 material, aluminum alloy 1100 A material etc. are used suitably.
[0047]
The coated metal material of the present invention may be further coated on the coated metal material. The material further coated on the resin layer (B) in the coated metal material is excellent in corrosion resistance after coating and coating film adhesion. Thereby, the coated metal material to which the coating has been applied can be suitably used for metal can lid materials, electrical products, metal materials for metal furniture, and the like.
[0048]
The coated metal material of the present invention is preferably used for the production of a laminate material. That is, a coated metal material coated with a laminate film can be produced by coating the above coated metal material with a laminate film, and the obtained material has a surface protected by the laminate film and has a corrosion resistance. Also, the film adhesion is excellent. Thereby, the coating | coated metal material coat | covered with the laminate film can be used conveniently for the metal material for metal cans, an electric product, metal furniture, etc.
[0049]
Although it does not specifically limit as resin which comprises the said laminate film, For example, the said thermoplastic polyester-type resin etc. can be mentioned.
The thermoplastic polyester-based resin is not particularly limited. For example, a thermoplastic resin composed of structural units such as an ethylene terephthalate unit, an ethylene naphthalate unit, an ethylene isophthalate unit, a butylene terephthalate unit, and a 1,4-cyclohexanedimethanol terephthalate unit. Mention may be made of polyester resins. It may be a copolymerized thermoplastic polyester resin having two or more of the above structural units. A polyethylene terephthalate resin composed of ethylene terephthalate units or a polyethylene naphthalate resin composed of naphthalene terephthalate units is more preferred.
[0050]
Even if the thermoplastic polyester resin is laminated on a metal after forming a film, the thermoplastic polyester resin heated and melted is extruded into a film shape by a narrow slit of an extrusion machine and directly on a metal plate. It may be by direct lamination which is laminated on. When laminating after forming the film, the film is not particularly limited, and may be, for example, an unstretched film, a uniaxially stretched film, or a biaxially stretched film.
[0051]
The non-chromium metal surface treatment method of the present invention is preferably a method of treating an object to be treated with a surface treatment agent containing no chromium and then treating with an aqueous solution of polyallylamine. When the object treated by the non-chromium metal surface treatment method of the present invention is coated, excellent post-coating corrosion resistance and coating film adhesion can be imparted. When the laminate film is adhered, it is excellent after adhesion. Corrosion resistance and film adhesion can be imparted. In particular, it can be suitably applied to aluminum or aluminum alloys. For example, excellent corrosion resistance and coating film adhesion by applying to aluminum or aluminum alloys for metal cans, electrical products, and metal furniture. , Film adhesion can be imparted.
[0052]
In the non-chromium metal surface treatment method of the present invention, first, a treatment of an object to be treated with a non-chromium metal surface treatment agent (C) comprising a water-soluble zirconium compound and / or a water-soluble titanium compound and a phosphorus compound (step (I) ). By performing the above step (I), a surface treatment layer containing zirconium and / or titanium and phosphorus can be formed on the metal substrate.
[0053]
The non-chromium metal surface treating agent (C) used in the step (I) contains a water-soluble zirconium compound and / or a water-soluble titanium compound. Thereby, the coating metal material which is excellent in corrosion resistance and adhesiveness can be obtained.
[0054]
The water-soluble zirconium compound is not particularly limited as long as it is a water-soluble zirconium-containing compound, but is preferably water-soluble complex zirconium fluoride because it is excellent in film formation in a short time.
The water-soluble complex zirconium fluoride is not particularly limited, and examples thereof include the above-described zirconium hydrofluoric acid.
[0055]
The water-soluble titanium compound is not particularly limited as long as it is a titanium-containing compound that is water-soluble, but water-soluble complex titanium fluoride is preferable because it is excellent in film formation in a short time.
The water-soluble complex titanium fluoride is not particularly limited, and examples thereof include the above-described titanium hydrofluoric acid.
[0056]
In the non-chromium metal surface treating agent (C), the content of the water-soluble complex zirconium fluoride and / or the water-soluble complex titanium fluoride is 40 ppm and the upper limit is 1000 ppm in terms of zirconium and / or titanium atoms. preferable. If it is less than 40 ppm, a sufficient amount of zirconium or titanium film cannot be obtained by short-time treatment, and adhesion and corrosion resistance may be lowered. When it exceeds 1000 ppm, the coating film adhesion and the film adhesion may be lowered, and the performance improvement and the shortening of the processing time are not recognized, and the cost may be increased. The lower limit is more preferably 100 ppm, and the upper limit is more preferably 300 ppm. The content of the water-soluble complex zirconium fluoride and / or the water-soluble complex titanium fluoride is a total content of zirconium and titanium contained in the non-chromium metal surface treatment agent (C).
[0057]
The non-chromium metal surface treating agent (C) used in the step (I) contains a phosphorus compound. Thereby, the coating metal material which is excellent in corrosion resistance and adhesiveness can be obtained.
[0058]
The phosphorus compound is not particularly limited as long as it is a water-soluble phosphorus-containing compound, but since it is excellent in film-forming properties in a short time, an organic compound in which the phosphorus atoms constituting orthophosphoric acid and phosphonic groups are bonded to carbon atoms. A phosphonic acid compound is preferred.
It does not specifically limit as said organic phosphonic acid compound, For example, the organic phosphonic acid compound mentioned above can be mentioned.
[0059]
In the non-chromium metal surface treatment agent (C), the content of the phosphorus compound is preferably a lower limit of 20 ppm and an upper limit of 500 ppm in terms of phosphorus atoms. If it is less than 20 ppm, a sufficient amount of phosphorus film cannot be obtained by short-time treatment, and adhesion may be reduced. Even if it exceeds 500 ppm, the film formation rate is not improved, and the effect of improving the adhesion and corrosion resistance is not seen only by being present in excess, which may increase the cost. The lower limit is more preferably 50 ppm, and the upper limit is more preferably 200 ppm.
[0060]
The non-chromium metal surface treatment agent (C) used in the step (I) may further use a film formation accelerator, an etching aid, a chelating agent, and a pH adjuster in addition to the above components, as necessary. Can do.
[0061]
The film formation accelerator is not particularly limited, and examples thereof include boric acid.
Examples of the etching aid include hydrofluoric acid, hydrofluoric acid salt, and boronic acid fluoride. When the above water-soluble complex zirconium fluoride or the above water-soluble complex titanium fluoride is used as a fluorine ion supply source, the amount of fluorine ions produced is insufficient. Is preferred.
[0062]
Examples of the chelating agent include citric acid, tartaric acid, gluconic acid and the like, acids that form a complex with aluminum, and metal salts thereof.
[0063]
Examples of the pH adjuster include acids or bases that do not adversely affect the surface treatment, such as nitric acid, perchloric acid, sulfuric acid, sodium nitrate, ammonium hydroxide, sodium hydroxide, and ammonia.
[0064]
The non-chromium metal surface treatment agent (C) used in the step (I) preferably has a lower pH limit of 1.4 and an upper limit of 4.0. If it is less than 1.4, the etching of the metal surface is promoted too much, so that a sufficient amount of film cannot be obtained and also causes the appearance of the film to be defective. If it exceeds 4.0, the chemical conversion reaction does not proceed satisfactorily, and there is a possibility that a sufficient film amount cannot be obtained. The lower limit is more preferably 1.8, and still more preferably 2.0. The upper limit is more preferably 3.2, and still more preferably 3.0.
[0065]
In the said process (I), as said to-be-processed object, the metal base material mentioned above can be mentioned, for example.
In the step (I), the method for treating the object to be treated is not particularly limited as long as it is a method for bringing the object to be treated into contact with the non-chromium metal surface treating agent (C). The usual method can be mentioned. Of these, the spray method is preferred.
[0066]
In the said process (I), as a processing temperature of the said chromium-free metal surface treating agent (C), a preferable minimum is 30 degreeC, a preferable upper limit is 80 degreeC, a more preferable minimum is 40 degreeC, and a more preferable upper limit is 60 degreeC. is there. When the temperature is lower than 30 ° C., the reactivity is low, the film depositability is deteriorated, and the corrosion resistance may be lowered. Even if it exceeds 80 degreeC, the reactivity may not improve and there is a possibility that the loss of energy may become large.
[0067]
In the step (I), when the treatment is performed by a spray method, the treatment time of the non-chromium metal surface treatment agent (C) is preferably 1 second, preferably 20 seconds, and more preferably 3 seconds. A more preferred upper limit is 8 seconds. If the time is less than 1 second, the amount of the formed film may not be sufficient, and if it exceeds 20 seconds, the etching during the formation of the film may proceed excessively, and the adhesion and corrosion resistance may be reduced.
[0068]
After the step (I), a water washing treatment can be performed as necessary.
The post-chemical conversion rinsing treatment is performed once or more so as not to adversely affect the appearance of the coating film. In this case, it is appropriate that the final water washing is performed with pure water. In this water washing treatment, either spray water washing or immersion water washing may be used, and these methods may be combined for water washing.
[0069]
The non-chromium metal surface treatment method of the present invention performs a step (step (II)) of treating the workpiece to which the above step (I) has been performed with an aqueous polyallylamine solution (D). The polyallylamine mentioned above can be used for the polyallylamine used at the said process (II). That is, the above-described polyallylamine dissolved in water can be used as the polyallylamine aqueous solution (D) and treated. By performing the step (II), a resin layer containing polyallylamine can be formed.
[0070]
The polyallylamine aqueous solution (D) preferably has a polyallylamine content on a mass basis with a lower limit of 100 ppm and an upper limit of 10,000 ppm. If it is less than 100 ppm, the adhesiveness after coating and after lamination may decrease. If it exceeds 10,000 ppm, the corrosion resistance is not improved and the cost may increase. The lower limit is more preferably 500 ppm, and the upper limit is more preferably 5000 ppm.
[0071]
The polyallylamine aqueous solution (D) is not particularly required to adjust the pH, and an aqueous solution in which an appropriately set amount of polyallylamine can be used. The pH of the polyallylamine aqueous solution (D) is usually about 10 to 12 when an aqueous solution that does not adjust the pH is used.
[0072]
In the step (II), the method for treating with the polyallylamine aqueous solution (D) is not particularly limited as long as it is a method for bringing the treatment object subjected to the step (I) into contact with the polyallylamine aqueous solution (D). Ordinary methods such as a spray method, a dipping method, and a roll coating method can be used. Of these, the spray method is preferred. In order to make the adhesion amount of polyallylamine uniform, it is preferable to remove excess liquid remaining on the surface of the object to be treated by rubber roll squeezing, air blowing, or the like after spraying. When the workpiece is plate-shaped, the rubber roll drawing method is preferable.
[0073]
In the step (II), the treatment temperature of the polyallylamine aqueous solution (D) is not affected by the temperature because the film-forming property is not affected by the temperature. Therefore, the lower limit is preferably 20 ° C., and energy loss may increase, so the upper limit is preferably 60 ° C.
[0074]
In the step (II), when the treatment is performed by a spray method, the treatment time of the polyallylamine aqueous solution (D) is preferably 1 second, preferably 10 seconds, and more preferably 2 seconds. A preferred upper limit is 6 seconds. If it is less than 1 second, the amount of film formed is not sufficient, and adhesion after coating and after lamination may decrease. Even if it exceeds 10 seconds, there is a possibility that the productivity is not affected without affecting the film forming property. After performing the above step (II), it is preferable to remove excess liquid on the surface of the material using a rubber roll or the like and not wash with water. This is because when washing with water, the polyallylamine adhering to the step (II) may be washed away.
[0075]
By performing the step (I) and the step (II), a surface treatment layer containing zirconium and / or titanium and phosphorus and a resin layer containing polyallylamine are formed on a metal substrate. The coated metal material obtained is excellent in post-coating corrosion resistance and coating film adhesion when it is further applied, and when a laminate film is further applied. It has excellent corrosion resistance and film adhesion after the film is attached.
[0076]
In the non-chromium metal surface treatment method of the present invention, it is preferable to dry after performing the step (I) and the step (II). The drying method is preferably heat drying, and examples thereof include oven drying and / or heat drying by forced circulation of hot air.
[0077]
In the drying, the drying temperature is preferably the lower limit of 40 ° C. and the upper limit of 120 ° C. as the material temperature. The lower limit is more preferably 60 ° C., and the upper limit is more preferably 80 ° C. The drying time can be appropriately set depending on the drying method, and is usually a lower limit of 6 seconds and an upper limit of 60 seconds.
[0078]
In the non-chromium metal surface treatment method of the present invention, it is preferable that a step of washing with an acid is performed before the treatment with the non-chromium metal surface treatment agent (C). Further, it is preferable that a step of washing with an alkali is performed before the step of washing with an acid. More preferable embodiments are alkali washing, water washing, acid washing, water washing, treatment with non-chromium metal surface treatment agent (C) (step (I)), water washing, pure water washing, treatment with polyallylamine aqueous solution (D) (step (II)). ), Rubber roll squeezing and drying, or a method of sequentially performing each step, acid washing, water washing, treatment with non-chromium metal surface treatment agent (C) (step (I)), water washing, pure water washing, polyallylamine aqueous solution (D) This is a method of sequentially performing each step of treatment (step (II)), rubber roll squeezing and drying.
[0079]
The alkali cleaning treatment is not particularly limited, and for example, alkali cleaning that has been conventionally used for alkali cleaning treatment of metals such as aluminum and aluminum alloys can be performed. In the alkali cleaning treatment, the alkali cleaning is usually performed using an alkaline cleaner. The acid cleaning is performed using an acidic cleaner.
[0080]
The alkaline cleaner is not particularly limited, and for example, those used for normal alkali cleaning can be used, and examples thereof include “Surf Cleaner EC370” manufactured by Nippon Paint Co., Ltd. The acidic cleaner is not particularly limited, and examples thereof include inorganic acids such as sulfuric acid, nitric acid and hydrochloric acid; “Surf Cleaner ST160” manufactured by Nippon Paint Co., Ltd.
[0081]
The acid washing and alkali washing treatment is usually performed by a spray method. After performing the acid cleaning or alkali cleaning treatment, a water washing treatment is performed to remove the acid cleaning liquid or the alkali cleaning agent remaining on the substrate surface.
[0082]
In the film obtained by the non-chromium metal surface treatment method of the present invention, the film amount of each component is determined appropriately by the composition of the non-chromium metal surface treatment agent (C), the composition of the polyallylamine aqueous solution (D), the respective treatment temperature, and treatment time. By setting, a desired coating amount can be obtained.
[0083]
The coated metal material of the present invention has a surface treatment layer (A) comprising zirconium and / or titanium and phosphorus on a metal substrate, and further, a polycrystal on the surface treatment layer (A). Since it has a resin layer (B) containing allylamine, it has excellent corrosion resistance and coating film adhesion after coating, and also has excellent corrosion resistance and film adhesion after laminating film attachment. It is. In particular, aluminum or an aluminum alloy is used as a metal substrate in the above coated metal material, and zirconium and / or titanium is derived from water-soluble complex zirconium fluoride and / or water-soluble complex titanium fluoride, and phosphorus is ortholine. What is obtained when it is derived from an acid or an organic phosphonic acid compound is superior in adhesion and corrosion resistance. The non-chromium metal surface treatment method of the present invention is a method by which a coated metal material having excellent corrosion resistance and adhesion can be obtained. Therefore, the coated metal material obtained by applying the above-mentioned non-chromium metal surface treatment method is excellent in corrosion resistance and adhesion after coating, and excellent in corrosion resistance and film adhesion after laminating the film. For example, it can be used suitably for uses, such as a metal can, an electric product, and metal furniture.
【Example】
EXAMPLES Hereinafter, although an Example is hung up and demonstrated in more detail, this invention is not limited only to these Examples. In the examples, “parts” means “parts by mass” unless otherwise specified.
[0084]
(Preparation of water-soluble complex zirconium fluoride and phosphoric acid-containing non-chromium metal surface treatment agent)
9996.7 parts of ion-exchanged water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 2.3 parts of Nippon Light Metal Co., Ltd. “zirconium hydrofluoric acid” (containing 17.6% as Zr) was gradually added. Further, 0.8 part of 75% phosphoric acid was gradually added while stirring. Next, 0.2 part of hydrofluoric acid was gradually added while stirring. Subsequently, ammonia was added while stirring to adjust the pH of the treatment agent to 2.6. Stirring was continued for 10 minutes to obtain a colorless and transparent non-chromium metal surface treatment agent containing 40 ppm of zirconium hydrofluoric acid as zirconium and 20 ppm of phosphoric acid as phosphorus. By the same method, the non-chromium metal surface treating agent containing the zirconium hydrofluoric acid zirconium and the phosphoric acid phosphorus was obtained with the compounding ratios shown in Tables 1 and 2 as examples and comparative examples.
[0085]
(Preparation of water-soluble complex zirconium fluoride and organophosphonic acid compound-containing non-chromium metal surface treatment agent)
9996.8 parts of ion-exchanged water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 2.3 parts of Nippon Light Metal Co., Ltd. “zirconium hydrofluoric acid” (containing 17.6% as Zr) was gradually added. Further, 0.7 part of 1-hydroxyethylidene-1,1-diphosphonic acid was gradually added while stirring. Next, 0.2 part of hydrofluoric acid was gradually added while stirring. Subsequently, ammonia was added while stirring to adjust the pH of the treatment agent to 2.6. Stirring was continued for 10 minutes to obtain a colorless and transparent non-chromium metal surface treating agent containing 40 ppm of hydrofluoric zirconium hydroacid as zirconium and 20 ppm of 1-hydroxyethylidene-1,1-diphosphonic acid as phosphorus. Non-chromium metal containing zirconium hydrofluoric acid zirconium and phosphorus 1-hydroxyethylidene-1,1-diphosphonic acid in the same manner at the blending ratios shown in Tables 1 and 2 as examples and comparative examples A surface treating agent was obtained.
[0086]
(Preparation of water-soluble complex titanium fluoride and phosphoric acid-containing non-chromium metal surface treatment agent)
9997.6 parts of ion exchange water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 1.4 parts of “Titanium hydrofluoric acid” (containing 29.3% as Ti) by Morita Chemical Co., Ltd. was gradually added. Further, 0.8 part of 75% phosphoric acid was gradually added while stirring. Next, 0.2 part of hydrofluoric acid was gradually added while stirring. Subsequently, ammonia was added while stirring to adjust the pH of the treatment agent to 2.6. Stirring was continued for 10 minutes to obtain a colorless and transparent non-chromium metal surface treatment agent containing 40 ppm of titanium hydrofluoric acid as titanium and 20 ppm of phosphoric acid as phosphorus. By the same method, the non-chromium metal surface treating agent containing the titanium hydrofluoric acid titanium and the phosphoric acid phosphorus was obtained with the compounding ratios shown in Tables 1 and 2 as examples and comparative examples.
[0087]
(Preparation of water-soluble complex titanium fluoride and organic phosphonic acid compound-containing non-chromium metal surface treatment agent)
9997.7 parts of ion-exchanged water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 1.4 parts of “Titanium hydrofluoric acid” (containing 29.3% as Ti) by Morita Chemical Co., Ltd. was gradually added. Further, 0.7 part of 1-hydroxyethylidene-1,1-diphosphonic acid was gradually added while stirring. Next, 0.2 part of hydrofluoric acid was gradually added while stirring. Subsequently, ammonia was added while stirring to adjust the pH of the treatment agent to 2.6. Stirring was continued for 10 minutes to obtain a colorless and transparent non-chromium metal surface treating agent containing 40 ppm of titanium hydrofluoric acid as titanium and 20 ppm of 1-hydroxyethylidene-1,1-diphosphonic acid as phosphorus. In the same manner, the non-chromium metal containing titanium of hydrofluoric titanate and phosphorus of 1-hydroxyethylidene-1,1-diphosphonic acid in the mixing ratios shown in Tables 1 and 2 as examples and comparative examples A surface treating agent was obtained.
[0088]
(Preparation of water-soluble complex zirconium fluoride, water-soluble complex titanium fluoride and phosphoric acid-containing non-chromium metal surface treatment agent)
9997.1 parts of ion exchange water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 1.2 parts of zirconium hydrofluoric acid and then 0.7 parts of titanium hydrofluoric acid were gradually added. Further, 0.8 part of 75% phosphoric acid was gradually added while stirring. Next, 0.2 part of hydrofluoric acid was gradually added while stirring. Subsequently, ammonia was added while stirring to adjust the pH of the treatment agent to 2.6. Stirring was continued for 10 minutes to obtain a colorless and transparent non-chromium metal surface treating agent containing 20 ppm of zirconium hydrofluoric acid as zirconium, 20 ppm of titanium hydrofluoric acid as titanium, and 20 ppm of phosphoric acid as phosphorus. In the same manner, the surface of the non-chromium metal containing zirconium fluoride hydrofluoric acid, titanium fluorotitanium hydroacid titanium and phosphoric acid phosphorus at the mixing ratios shown in Tables 1 and 2 as examples and comparative examples A treating agent was obtained.
[0089]
(Preparation of water-soluble complex zirconium fluoride, water-soluble complex titanium fluoride and organic phosphonic acid compound-containing non-chromium metal surface treatment agent)
9997.2 parts of ion-exchanged water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 1.2 parts of zirconium hydrofluoric acid and then 0.7 parts of titanium hydrofluoric acid were gradually added. Further, 0.7 part of 1-hydroxyethylidene-1,1-diphosphonic acid was gradually added while stirring. Next, 0.2 part of hydrofluoric acid was gradually added while stirring. Subsequently, ammonia was added while stirring to adjust the pH of the treatment agent to 2.6. A colorless and transparent non-chromium metal surface containing 10 ppm of zirconium hydrofluoric acid as zirconium, 20 ppm of titanium hydrofluoric acid as titanium, and 20 ppm of 1-hydroxyethylidene-1,1-diphosphonic acid as phosphorus. A treating agent was obtained. In the same manner, the zirconium fluoride of zirconium hydrofluoric acid, titanium of titanium hydrofluoric acid, and 1-hydroxyethylidene-1,1-diphosphonic acid were mixed at the compounding ratios shown in Tables 1 and 2 as examples and comparative examples. A non-chromium metal surface treatment agent containing phosphorus was obtained.
[0090]
(Preparation of polyallylamine aqueous solution)
9996 parts of ion exchange water was charged into a vessel equipped with a stirrer. While stirring at room temperature, 4 parts of “PAA-05” (polyallylamine, containing 20% non-volatile content) manufactured by Nitto Boseki Co., Ltd. was gradually added. Stirring was continued for 10 minutes to obtain a colorless and transparent polyallylamine aqueous solution containing 80 ppm of polyallylamine having no salt structure. By the same method, a colorless and transparent polyallylamine aqueous solution containing 1000 ppm, 5000 ppm and 10,000 ppm of polyallylamine was obtained.
[0091]
(Preparation of amino group-containing resin aqueous solution (comparative resin component))
Instead of polyallylamine, “PVAM-0595B” (polyvinylamine) manufactured by Mitsubishi Chemical Corporation, “acrylamide polymer aqueous solution” (polyacrylamide) manufactured by Wako Pure Chemical Industries, Ltd., “Epomin P-1000” (polyethyleneimine) manufactured by Nippon Shokubai Co., Ltd. In the same manner as in the preparation of the polyallylamine aqueous solution, an amino group-containing resin aqueous solution containing 1000 ppm of resin was obtained.
Moreover, as a strong acid salt of polyallylamine, “PAA-HCl-3L” (hydrochloric acid salt of PAA-10C) manufactured by Nitto Boseki Co., Ltd. was used to obtain an amino group-containing resin aqueous solution containing 1000 ppm of resin by the same method. .
[0092]
Examples 1-24, Comparative Examples 1-4
(Creation of non-chromium metal surface treatment material)
Both sides of aluminum alloy 3004 plate with a thickness of 0.30 mm were washed with a 1% diluted solution of alkali cleaner “Surf Cleaner EC370” manufactured by Nippon Paint Co., Ltd. (65 ° C. × 3 seconds), then washed with water, followed by 1% sulfuric acid. Washing using a diluting solution (50 ° C. × 3 seconds), washing with water, and spraying a non-chromium metal surface treatment agent having the components shown in Tables 1 and 2 to the aluminum material obtained by the above method. (50 ° C x 5 seconds), washed with water, washed with pure water, treated with an aqueous polyallylamine solution or amino group-containing resin solution at room temperature for 2 seconds using a spray device, and then applied to the surface of the material using a rubber roll. The excess resin aqueous solution adhered was squeezed out. Then, it was dried at a material temperature of 80 ° C. for 30 seconds to obtain a non-chromium metal surface treatment material.
[0093]
Comparative Examples 5-7
In preparation of the said chromium-free metal surface treatment material, it processed by the same method except not having processed with the amino group containing resin aqueous solution of room temperature, and obtained the chromium-free metal surface treatment material.
[0094]
Comparative Examples 8-9
(Preparation of polyallylamine surface treatment material)
In the preparation of the above-mentioned non-chromium metal surface treatment material, after alkali degreasing, acid washing, water washing, and pure water washing, a polyallylamine surface at room temperature was treated in the same manner without subjecting it to chemical conversion treatment with a metal surface treatment agent. A treated material was obtained.
[0095]
Comparative Example 10
(Chromate treatment material creation)
In the same manner as in the preparation of the above-mentioned non-chromium metal surface treatment material, except that chemical conversion treatment with a non-chromium metal surface treatment agent and treatment with a polyallylamine aqueous solution were used, “Alsurf 401/45” manufactured by Nippon Paint Co., Ltd. was used. A chromate-treated material subjected to acid chromate treatment was prepared.
[0096]
(Film mass measurement)
The mass of zirconium, titanium, and chromium in the dry film in the non-chromium metal surface treatment material and chromate treatment material obtained in Examples and Comparative Examples was measured using a fluorescent X-ray analyzer “XRF-1700” manufactured by Shimadzu Corporation. did.
The mass of the polyallylamine in the dry film in the non-chromium metal surface treatment material, the polyallylamine surface treatment material, and the mass of each comparison resin are the mass of organic carbon derived from each resin using a carbon / moisture analyzer by type “RC412” manufactured by LECO USA. Was measured.
The mass of zirconium in the zirconium compound obtained by the above measurement is Zr, the mass of titanium in the titanium compound is Ti, and the mass of phosphorus in phosphoric acid or 1-hydroxyethylidene-1,1-diphosphonic acid is P. Table 1 and 2 show the mass of organic carbon derived from polyallylamine or each comparative resin as C.
[0097]
(Creation of aluminum paint)
Using the obtained non-chromium metal surface treatment material, polyallylamine surface treatment material and chromate treatment material, Nippon Fine Coatings polyester-based paint “Flexcoat # 5000 White” (non-volatile content 50%) using a reverse roll coater , Wet application amount per side 15g / m 2 Then, using a conveyor oven, baking is performed at a material temperature of 230 ° C. for 60 seconds, and the dry coating weight of the paint is 7.5 g / m. 2 Each aluminum coating material was obtained.
[0098]
(Making laminate material)
A polyethylene terephthalate (PET) film is placed on the obtained non-chromium metal surface treatment material, polyallylamine surface treatment material, and chromate treatment material, and using a heating roller, a roll temperature of 260 ° C. (material temperature of 240 ° C.) and a roll speed of 30 m / Immediately after thermocompression bonding in minutes, it was cooled with water to obtain a laminate material.
[0099]
(Evaluation methods)
The following evaluation was performed on each of the obtained aluminum coating material and laminate material, and the results are shown in Tables 1 and 2.
[0100]
1. Paint adhesion
The aluminum coating material was immersed in boiling water at 100 ° C. for 60 minutes. Immediately after taking out the aluminum coating material from boiling water, 100 crosscuts with a width of 1 mm were made, and the adhesive tape was peeled off, and the number of peeled pieces was measured. An acceptable level was that there were no peeling points.
[0101]
2. Corrosion resistance of paint
The cup processing shown in FIG. 1 was performed so that the painted surface of the aluminum coating material became convex. The cup processed material was immersed in a mixed aqueous solution of 2% citric acid and 2% sodium chloride held at 50 ° C. for 72 hours, and after removal, each part of the
5 points: No corrosion
4 points: Slight corrosion (side 0.5mm, corrosion 10 or less, edge: 0.5
3 points: Corrosion (side part: 1mm corrosion 20 places or less, edge part: 1mm corrosion 10 places or less)
2 points: Corrosion (Side: 20 mm or less of 3 mm corrosion, Edge: 10 mm or less of 3 mm corrosion)
1 point: Overall corrosion (more than half of the side and edge portions are corroded)
An acceptable score was obtained when the average score was equal to or greater than that of aluminum coating material treated with phosphate chromate.
[0102]
3. Adhesion of laminate material
As shown in FIG. 2, among the laminate material of 50 mm × 50 mm, a V-shaped
[0103]
4). Adhesion of laminate material
Match the laminate-coated surfaces of the laminates and use a hot press tester at 250 ° C. and 10 kg / cm. 2 For 1 minute. The bonded laminate was cut into a width of 5 mm, and the force applied when it was peeled off at a rate of 200 mm / min was measured with a “Tensilon tensile tester” manufactured by Toyo Baldwin. The acceptable level was a value (adhesion strength) equal to or greater than that of the laminate material for the phosphoric acid chromate treatment.
[0104]
5). Corrosion resistance of laminate material
The cup processing shown in FIG. 1 was performed so that the laminate-coated surface of the laminate material was convex, and cut in a circumferential shape as shown in FIG. The processed material was immersed in a mixed aqueous solution of 2% citric acid and 2% sodium chloride held at 50 ° C. for 144 hours, and after taking out, the length of corrosion spread from the cut portion was measured.
[0105]
[Table 1]
[0106]
[Table 2]
[0107]
The coated metal materials obtained by the examples are excellent in adhesion and corrosion resistance after painting, excellent in adhesion and corrosion resistance of laminate materials, and exhibit performance equal to or better than that subjected to phosphoric acid chromate treatment. Met.
[0108]
On the other hand, when a strong acid salt of polyvinylamine, polyacrylamide, polyethyleneimine, polyallylamine is used as a comparative resin component, what is obtained when the chemical conversion treatment is not performed is the adhesion and corrosion resistance after coating. In addition, the adhesion and corrosion resistance of the laminate material were inferior.
[0109]
【The invention's effect】
Since the coated metal material of the present invention has the above-described configuration, it is excellent in coating film adhesion and corrosion resistance after painting, and also excellent in film adhesion and corrosion resistance after laminating a laminated film. Further, the non-chromium metal surface treatment method of the present invention is a method by which the above coated metal material can be obtained. Therefore, since the coated metal material obtained by applying the above-mentioned non-chromium metal surface treatment method is excellent in adhesion and corrosion resistance, it can be suitably used for applications such as beverage cans and home appliances. Is.
[Brief description of the drawings]
FIG. 1 shows a schematic diagram of the shape of a test object for evaluating the corrosion resistance of a coating material.
FIG. 2 is a schematic view of a non-laminated surface of a laminate material with a cut for evaluation of adhesion.
FIG. 3 is a schematic diagram of a tensile direction by a Tensilon tensile tester.
FIG. 4 is an enlarged view of a cut portion showing a visual five-level evaluation standard in adhesion evaluation.
FIG. 5 shows a schematic diagram of the shape of a test object for evaluating the corrosion resistance of a laminate material.
[Explanation of symbols]
1 Plane section
2 Edge part
3 Sides
21 notches
22, 31 Uncoated surface
23 Rolling eyes
32 Circumferential cut
Claims (7)
樹脂層(B)は、乾燥後の片面当たりの質量で、ポリアリルアミンに由来する炭素の含有量が1.6〜200mg/m2である請求項1、2又は3記載の被覆金属材料。The surface treatment layer (A) is a mass per one side after drying, the content of zirconium and / or titanium is 3 to 30 mg / m 2 , and the content of phosphorus is 0.5 to 5 mg / m 2 ,
Resin layer (B) is a mass per surface after drying, coated metal material according to claim 1, wherein the content of carbon derived from polyallylamine is 1.6~200mg / m 2.
ポリアリルアミン水溶液(D)は、ポリアリルアミンの含有量が質量基準で80〜10000ppmである請求項6記載のノンクロム金属表面処理方法。The non-chromium metal surface treatment agent (C) has a water-soluble complex zirconium fluoride compound and / or water-soluble complex titanium fluoride compound content of 40 to 1000 ppm in terms of zirconium and / or titanium atoms, and a phosphorus compound content of phosphorus. 20 to 500 ppm in terms of atoms,
The non-chromium metal surface treatment method according to claim 6 , wherein the polyallylamine aqueous solution (D) has a polyallylamine content of 80 to 10,000 ppm on a mass basis.