JP3860346B2 - Non-eluting biodegradable resin extrusion foam molded article, biodegradable resin foam molded article using the same, and production method thereof - Google Patents
Non-eluting biodegradable resin extrusion foam molded article, biodegradable resin foam molded article using the same, and production method thereof Download PDFInfo
- Publication number
- JP3860346B2 JP3860346B2 JP28197998A JP28197998A JP3860346B2 JP 3860346 B2 JP3860346 B2 JP 3860346B2 JP 28197998 A JP28197998 A JP 28197998A JP 28197998 A JP28197998 A JP 28197998A JP 3860346 B2 JP3860346 B2 JP 3860346B2
- Authority
- JP
- Japan
- Prior art keywords
- biodegradable resin
- foam
- molded article
- polycaprolactone
- extrusion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【発明の属する技術分野】
本発明は、非溶出性の生分解性樹脂押出発泡成形体、及びこれを用いた生分解性樹脂発泡成型品、並びにそれらの製造方法に関し、さらに詳しくは、熱賦形等により容易に食品包装容器、水質浄化材、断熱材、緩衝材等の各種形態の成形体に成形することが可能であるばかりでなく、非溶出性のため、水と接触しても成形体内部から水溶性成分の溶出がなく、しかも得られた成形体の寸法安定性や機械的特性が良好な生分解性樹脂押出発泡成形体、及びこれを用いた生分解性樹脂発泡成型品、並びにそれらの製造方法に関する。
【0002】
【従来の技術】
従来、合成樹脂からなる発泡体は、多種多様のものが製造され、食品包装容器、水質浄化材、断熱材、緩衝材等の幅広い分野で活用されてきた。近年、これら合成樹脂発泡体の需要は、年々増加する傾向にあり、このため廃棄される量も年々増加して、環境問題、公害問題として、大きく社会的にクローズアップされてきている。しかし、廃棄合成樹脂発泡体を再生利用するには、社会的規模の様々な対応が求められ、一方、焼却処分するには、有害ガスの発生防止、高熱発生による焼却炉の劣化防止など、山積されている問題が多く、廃棄処理が容易である発泡体の開発が強く望まれている。
【0003】
このような要求に対して、これら合成樹脂を生分解性樹脂で置き換えた発泡体が種々提案されている。例えば、特開平5−306349号公報、特開平5−269875号公報などには、水を含浸させた生分解性樹脂チップを、油で加熱して発泡ビーズ又は発泡ペレットをいったん成形した後、これを型に詰めて熱賦形する方法、及び水を含浸させた生分解性樹脂を型に詰め込み、型全体を油で加熱して発泡させ、発泡体成形物を得る方法が開示されている。しかし、これらの方法では、粒子間の接着性に乏しく成型物の機械的特性が低いという問題がある。さらに、加熱媒体として油を使用しているため、発泡体粒子間に油が残存しやすく、これが徐々にしみ出して汚染するという問題もある。
【0004】
この発泡体粒子間の接着を改善するため、接着剤を用いて成形する方法も提案されているが、接着剤は生分解性を有していないものが多く、このような接着剤で、発泡体粒子を被覆すると、生分解性が阻害されることになる。一方、澱粉や膠などに代表される天然物由来の接着剤は、生分解性の点では良好であるが、親水性であるため、湿度の影響を受けやすく、吸湿・吸水により接着性が極端に低下するため、使用環境の制限を受けるという問題がある。
【0005】
また、特開平5−320405号公報、特開平6−32928号公報には、ペンジル化セルロースやセルロースアセテートなどのセルロース誘導体からなる発泡体粒子の製造方法が開示され、得られた発泡体粒子を型内に詰めて蒸気加熱により発泡体粒子間を融着せしめて成形体となすことも開示されている。しかし、セルロース誘導体に可塑剤が配合されていない場合には、蒸気加熱では十分に発泡体粒子間を融着させることは困難である。一方、セルロース誘導体に可塑剤が配合されている場合には、発泡体粒子間を融着させるに十分な量の可塑剤が存在すると、熱融着処理の際に発泡体粒子全体が可塑化されるため、発泡体粒子が逆に収縮して得られる成形体の寸法安定性が悪化し、機械的特性も低下し、さらには可塑剤が多価アルコール等の場合は、成形体使用時に水分に接触すると、可塑剤が水溶性のため溶出して汚染するという問題がある。また可塑剤の使用量を減らすと、セルロース誘導体の可塑化が難しくなって、成形時の発泡体粒子間の融着が困難になるという問題がある。
【0006】
一方、特開平7−126537号公報には、融点が100℃以上の生分解性樹脂と、例えばポリカプロラクトンのような融点が100℃以下の低融点生分解性樹脂とからなる生分解性樹脂配合物を水発泡させることにより生分解性樹脂発泡体を製造する方法が開示されている。しかし、この方法は、射出成形によるものであって、低融点生分解性樹脂は、成形体の内部全体に分布し、射出時にノズルから蜷局を巻くように吐出し集合する生分解性樹脂発泡体間の接着に作用し、得られた成形体製品の空洞や巣によって生じる不連続境界の発生を防止するのに役立つのみであり、成形体の表面平滑性に欠けると問題がある。しかも、低融点生分解性樹脂のみでは生分解性樹脂配合物の可塑性が不充分である場合には、可塑剤をさらに添加する必要が生じるが、可塑剤として水溶性の多価アルコール等を用いた際には、前記したと同様な可塑剤の溶出による汚染という問題がある。
また、特開平10−100264号公報には、セルロース誘導体からなる発泡体粒子を型内に充填して熱賦形するに際し、予め該セルロース誘導体の可塑剤を発泡体粒子表面に付着させておいて、発泡体粒子の表面を熱可塑化して融着させて成形体にすることも開示されている。しかし、この場合には、可塑剤を予め発泡体粒子表面に付着させる工程が入り、工程が煩雑になるという問題がある。
このように、セルロース誘導体からなる生分解性樹脂発泡成形体に対する研究・開発は、数多く試みられてきたが、未だ充分な、発泡体の成形が簡単で、成形体の寸法安定性や機械的特性が良好である生分解性発泡体は少なかった。そのため、生分解性でかつ、成型品に賦形する際の型内成形が容易であり、しかも機械的特性の良好な生分解性発泡体の技術開発が強く望まれてきた。
【0007】
【発明が解決しようとする課題】
本発明の目的は、上記従来の発泡体がもつ問題点を解消し、熱賦形等により容易に食品包装容器、水質浄化材、断熱材、緩衝材等の各種形態の成型品に成形することが可能であるばかりでなく、非溶出性のため、水と接触しても成形体内部から水溶性成分の溶出がなく、しかも寸法安定性や機械的特性が良好な生分解性樹脂押出発泡成形体及びその製造方法、さらには、この押出発泡成形体を用いた生分解性樹脂発泡成型品及びその製造方法を提供することにある。
【0008】
【課題を解決するための手段】
本発明者は、上記課題に対し鋭意研究を重ねた結果、セルロース・アセテート系樹脂と、該樹脂の軟化点より低い温度の融点を有するポリカプロラクトンと、発泡剤としての水分とを含有する特定の発泡性生分解性樹脂組成物を、押出成形すると同時に水分の気化膨張力により発泡させることにより、表面が実質的にポリカプロラクトンからなる層で覆われ、非溶出性でかつ表面平滑性に富んだ生分解性樹脂押出発泡成形体が得られること、さらには、この生分解性樹脂押出発泡成形体を用いることにより、食品包装容器、水質浄化材、断熱材、緩衝材等の各種成型品に賦形する際の型内成形が容易で、かつ寸法安定性や機械的特性が良好であることを見出した。本発明は、これらの知見に基づいて完成に至ったものである。
【0009】
すなわち、本発明によれば、セルロース・アセテート系樹脂100重量部と、該樹脂の軟化点より低い温度の融点を有するポリカプロラクトン5〜70重量部と、発泡剤としての水分とを含有する発泡性生分解性樹脂組成物を、押出成形すると同時に水分の気化膨張力により発泡させることにより製造されることを特徴とする、非溶出性の生分解性樹脂押出発泡成形体が提供される。
さらに、本発明によれば、上記発泡性生分解性樹脂組成物は、セルロース・アセテート系樹脂、ポリカプロラクトン、タルク、及び水分からなることを特徴とする上記の生分解性樹脂発泡体、ポリカプロラクトンは、押出発泡成形体の芯部よりも表層部に偏在し、かつ押出発泡成形体の表面を実質的に覆っていることを特徴とする上記の生分解性樹脂押出発泡成形体が提供される。
【0010】
さらにまた、本発明によれば、上記の生分解性樹脂押出発泡成形体を所望の形状に熱賦形、真空成形、又は圧空成形することを特徴とする生分解性樹脂発泡成型品が提供される。
【0011】
一方、また、本発明によれば、前方に押出ノズル又はダイを有する筒状容器内に、セルロース・アセテート系樹脂100重量部と、該樹脂の軟化点より低い温度の融点を有するポリカプロラクトン5〜70重量部と、発泡剤としての水分とを含有する発泡性生分解性樹脂組成物を投入し、該生分解性樹脂組成物を前記押出ノズルに押送する間は、昇温させて流動状の加熱加圧状態とし、その後前記押出ノズル又はダイから押し出して、発泡、成形させることを特徴とする上記の生分解性樹脂押出発泡成形体の製造方法が提供される。
さらに、本発明によれば、上記発泡性生分解性樹脂組成物は、セルロース・アセテート系樹脂、ポリカプロラクトン、タルク、及び水分からなることを特徴とする上記の製造方法が提供される。
【0012】
さらにまた、本発明によれば、上記生分解性樹脂押出発泡成形体は、ビーズ状又はペレット状に切断した後、所望の成形型に詰めて熱賦形されることを特徴とする前記の生分解性樹脂発泡成型品の製造方法、および上記生分解性樹脂押出発泡成形体は、シート状に押し出して、発泡、成形させた後、所望の形状に真空成形又は圧空成形されることを特徴とする前記の生分解性樹脂発泡成型品の製造方法が提供される。
【0013】
【発明の実施の形態】
以下、本発明について詳細に説明する。
【0014】
1.セルロース・アセテート系樹脂
本発明の生分解性樹脂押出発泡成形体(以下、単に「生分解性樹脂発泡体」という。)に用いられるセルロース・アセテート系樹脂は、セルロース・アセテートを主成分として含むものである。副成分として配合してもよい生分解性樹脂は、水分との接触によって溶出しなければ、特に限定されるものではなく、一般に非水溶性の生分解性樹脂として用いられているものならば何でも使用することができる。これらに該当するものとしては、例えば、スターチ系、セルロース系などが挙げられる。
セルロース・アセテート系樹脂中で主成分として含まれるセルロース・アセテートは、通常、綿の実から得られるリンター、又は木材パルプのセルロースに酢酸を反応させることにより製造される。本発明の生分解性樹脂発泡体に用いられるセルロース・アセテートとしては、通常「酢酸セルロース」として市販されているグレードのものならば何でもよいが、その中でも、セルロースの酢酸エステル化度が、セルロースに結合している酢酸の重量割合で表される酢化度でいって45%以上であるようなものがよく、特に酢化度が47〜60%(セルロース1単位当たりの結合アセチル基の数は1.9〜2.8)のものが好ましい。酢化度が45%未満の場合には、溶融温度が高くなりすぎるため、安定して発泡体に溶融成形することが困難となる。
セルロース・アセテートは、物性面では、軟質又は中硬質のものがよく、表面硬度がロックウェル硬さで、HR=80〜100のもの、衝撃強度が20〜30kg−cm/cmのものが好ましく用いられる。さらに、成形加工性の観点から、軟化して流動を始める軟化点(流出温度)が150〜170℃のもの、ASTM D 648に規定された荷重18.6kgf/cm2の条件での熱変形温度が、44〜55℃のものが好ましく用いられる。一方、硬質のものでは、安定して発泡体に溶融成形することが困難となる。
また、本発明の生分解性樹脂発泡体に用いられるセルロース・アセテート系樹脂には、単に酢酸基をもつアセテートの他に、プロピオン酸或いは酪酸を混合使用したセルロース・アセトプロピオネートや、セルロース・アセトブチレートも含まれ、溶融点、吸水率、溶剤に対する溶解性等の観点から酸の混合比率を適宜選択して使用できる。
【0015】
2.ポリカプロラクトン成分
本発明の生分解性樹脂発泡体に用いられるポリカプロラクトン成分は、前記セルロース・アセテート系樹脂の軟化点より低い温度の融点を有するポリカプロラクトンからなる。
このようなポリカプロラクトンとしては、次の一般式で表される脂肪族ポリエステルが挙げられるが、この脂肪族ポリエステルの市販品としては、例えば、日本ユニカー株式会社販売の「トーン」(商品名)がある。
【0016】
【化1】
(式中、Rは、脂肪族部分を表し、nは正の整数である。)
【0017】
本発明に用いられるポリカプロラクトンは、生分解性であるばかりでなく、非水溶性であり、さらに、好都合なことには、加熱によりセルロース・アセテート系樹脂を可塑化する働きがあるため、通常生分解性樹脂発泡体を製造する際に必要な可塑剤を何ら添加しなくても、表面平滑性に富んだ良好な生分解性樹脂発泡体が得られ、その上、水溶性可塑剤を用いていないため、水分との接触による可塑剤の溶出といった弊害をも回避することができる。しかも、驚くべきことには、配合されたポリカプロラクトンは、セルロース・アセテート系樹脂に較べて低融点であるため、生分解性樹脂発泡体の内部に均一に分布するのではなく、ポリカプロラクトンを含有する生分解性樹脂組成物が加熱溶融され、押出ノズル又はダイに押送される間に、中心部より周辺部、すなわち芯部より表層部に移行して生分解性樹脂発泡体の表層部に偏在する傾向がある。
また、本発明に用いられるポリカプロラクトンは、上記のように、融点がセルロース・アセテート系樹脂の軟化点以下であることが必要である。そのうち、好ましい融点は、100℃以下、特に好ましい融点は、60℃近傍である。このような融点を有するポリカプロラクトンを用いることにより、発泡体の表層部にポリカプロラクトンを偏在させることができる。このポリカプロラクトンは、種々な樹脂との相溶性がよく、耐衝撃性を向上させ、熱賦形した成型品の寸法安定性を向上させる。
一方、融点がセルロース・アセテート系樹脂の軟化点以上であるポリカプロラクトンを用いると、生分解性であっても、可塑化する働きをしないため、表面平滑性に富んだ良好な生分解性樹脂発泡体が得られない。
【0018】
本発明において、ポリカプロラクトンの配合量は、セルロース・アセテート系樹脂100重量部に対して、5〜70重量部、好ましくは10〜40重量部の範囲である。配合量が5重量部未満であると、発泡体表層部でのポリカプロラクトンの割合が少なく、熱賦形時、発泡体表面の熱可塑化効果が不十分となり、得られた成型品の機械的強度が悪化し、一方70重量部を超えると、その添加効果が現れず、また、ポリカプロラクトンの発泡体表層部への偏在が過度となり、却って仕上げ外観や成形加工性が悪化するようになる。
【0019】
3.発泡性生分解性樹脂組成物
本発明の生分解性樹脂発泡体に用いられる発泡性生分解性樹脂組成物は、前記した如く、セルロース・アセテート系樹脂に、所定量のポリカプロラクトンと、発泡剤としての水分を配合することにより調製される。発泡剤としての水分の配合割合は、セルロース・アセテート系樹脂とポリカプロラクトンとの生分解性樹脂配合物100重量部に対して、3〜100重量部、好ましくは5〜50重量部である。
本発明の生分解性樹脂組成物には、前述したように、ポリカプロラクトンがセルロース・アセテート系樹脂を可塑化する働きをするため、他の可塑剤を添加しなくても、良好な生分解性樹脂発泡体を得ることができるが、さらに必要に応じて、本発明の目的を損なわない範囲で、非水溶性の可塑剤ならば、他の可塑剤を配合してもよい。
【0020】
さらに、上記生分解性樹脂配合物には、本発明の目的を損なわない範囲で、他の添加剤等を配合してもよく、例えば、熱安定剤、発泡調整剤、発泡助剤、増量材等が挙げられる。なかでも、タルク、酸化珪素、酸化チタン、酸化マグネシウム、酸化アルミニウム、珪酸カルシウム等の無機系微粒子、セルロース粉末、キチン、キトサン、木粉、ステアリン酸金属塩等の有機系微粒子などの発泡調整剤、特にタルクは、該生分解性樹脂配合物に、好適な発泡性を付与することができるので、均一でかつ高度に発泡した発泡体が容易に得られる。このような発泡調整剤は、それぞれ単独で用いてもよく、2種類以上を併用してもよい。さらに発泡性を向上させたり、発泡体製造時に副生される酸性物質を中和させると共にガスを発生させる目的で、例えば炭酸水素ナトリウム、炭酸水素カリウム、炭酸ナトリウム、炭酸カリウム、炭酸カルシウム等の無機微粒子を併用してもよい。また、増量材として、オカラ、木粉、麩(小麦の皮)、米粉、古紙等を添加することもできる。
本発明の生分解性樹脂組成物の好ましい態様として、セルロース・アセテート系樹脂に、ポリカプロラクトンと、発泡調整剤としてタルク、及び発泡剤としての水分からなる生分解性樹脂組成物が挙げられ、また、この生分解性樹脂組成物には、上記した増量材を添加してもよい。
この発泡調整剤としてタルクの生分解性樹脂組成物に対する配合量は、セルロース・アセテート系樹脂100重量部に対して、5〜50重量部、好ましくは10〜30重量部の範囲である。配合量が5重量部未満であると、タルクを配合した効果が現れず、不均一で粗い発泡体が形成されやすく、一方50重量部を超えると、タルクの2次凝集が起こりやすくなるため、やはり不均一で粗い発泡体が形成されやすくなる。
【0021】
4.生分解性樹脂発泡体(押出発泡成形体)及びその製造方法
本発明の生分解性樹脂発泡体は、前記の発泡性生分解性樹脂組成物を、押出成形すると同時に水分の気化膨張力により発泡させることにより製造される。
そのため、本発明の生分解性樹脂発泡体は、次の特徴を有している。
▲1▼水によって発泡させている。
▲2▼素材がすべて生分解性であるため、汎用プラスチック発泡体に比べて様々な廃棄処理に対処できる。
▲3▼非溶出性のため、水分と接触しても可塑剤等の溶出といった問題がない。
▲4▼表面がポリカプロラクトンの層で覆われているため、熱賦形等の二次成形 が容易である。
▲5▼スターチ系の生分解性樹脂発泡体などに比べて雰囲気湿度によって衝撃性能が変動しなくて、強度的に優れている。
▲6▼表面平滑性に優れている。
さらに、前記したように、本発明の生分解性樹脂発泡体は、発泡体の表層部にポリカプロラクトンが偏在することを特徴としている。ここで、発泡体表層部とは、発泡体の短軸方向の切断面積を円に換算したとき、直径の外側部分で数mm以内の部分を指す。ポリカプロラクトンは、発泡性生分解性樹脂組成物を押出成形する際、セルロース・アセテート系樹脂と共に加熱溶融され、押出ノズル又はダイに押送される間に、中心部より表層部に移行する傾向があるため、発泡体の中心部、すなわち芯部には、ポリカプロラクトンが比較的少なく、外側の表層部部分にポリカプロラクトンが比較的多く存在することとなる。
ポリカプロラクトンが発泡体の表層部に偏在し、その結果、表面が実質的にポリカプロラクトンからなる層で覆われていないと、熱賦形等の二次成形において溶融、相互融着することが困難となって、成形加工性が悪化する。このように、ポリカプロラクトンが発泡体の表層部に偏在することによって、実用上支障のない曲げ強度等の機械的強度を有する発泡体成型品が得られる。
【0022】
上記生分解性樹脂発泡体は、前述の如く、発泡性生分解性樹脂組成物を押出成形すると同時に水分の気化膨張力により発泡させることにより製造されるが、さらに、この製法を詳記すると、以下のようになる。
セルロース・アセテート系樹脂、ポリカプロラクトンおよび水分(発泡剤)を含有する発泡性生分解性樹脂組成物は、所定の割合で調製された後、前方に押出ノズル又はダイを有する筒状容器内(例えば、混練押出機)に投入される。筒状容器内に水分を投入する方法としては、発泡用の生分解性樹脂組成物に予め所定量の水分を含有させるようにしてもよいし、或いは生分解性樹脂やポリカプロラクトンの生分解性樹脂配合物と共に水そのものをホッパ内に直接添加してもよく、生分解性樹脂配合物と水分とが一緒に供給されさえすればよい。また、その投入割合は、前記したように、生分解性樹脂配合物100重量部に対して水分が3〜100重量部、好ましくは5〜50重量部であることが望ましい。
次いで、この生分解性樹脂組成物は、前記押出ノズルに押送するまでの間に、120〜250℃、好ましくは180〜220℃の温度で加熱溶融混練され、その結果、流動状の加熱加圧状態とされた後、細孔の、例えば径0.5〜5mmのノズル又はダイから押し出される。溶融混練時間は、単位時間当たりの吐出量、溶融混練温度などにより異なってくるので一概に決定することはできないが、該混合物が均一に溶融混練されるに十分な時間であればよい。また、吐出部のノズル又はダイの温度は、前記溶融混練温度と同じでもよいが、吐出できる範囲内で該温度よりも低温にしてもよい。ここで、溶融混練に使用される押出機は、高温高圧下となって水分がセルロースアセテート中に無理やり溶解されるようになっている限り、どのようなタイプの押出機でもよいが、通常は1軸又は2軸のスクリュータイプの押出機が用いられる。
その後、ノズル又はダイ細孔から吐出された溶融生分解性樹脂組成物は、その温度及び水分量によって発泡開始位置は異なってくるが、通常ノズル又はダイ部より0.1mm離れた位置から発泡が開始され、発泡を終えた後、押出し口の形状に合った形態に成形される。押出すノズル又はダイ細孔の形状は、丸、三角、四角、矩形、星形、中空などいずれであってもよく、目的に応じて適宜選択すればよい。
【0023】
得られた生分解性樹脂発泡体は、二次成形のために、通常はビーズ状又はペレット状に切断されて利用されるが、その切断は、発泡過程にある状態の生分解性樹脂発泡体を切断するのが好ましい。その理由は、このようにセルロース・アセテート樹脂配合物が固化する前の溶融可塑化状態で切断することにより、新たに形成される切断面は、切断後さらに膨化する過程でその表面が滑らかとなるため、表面が滑らかで、しかも発泡体も角が丸まったものが得られ、型内充填性が向上するからである。そのため、該押出物がノズル又はダイ細孔直径の3倍を超えて膨化する前の段階、好ましくは1.5倍を超えて膨化する前の段階で切断する。この切断長は、得られるビーズ状又はペレット状発泡体の長軸と短軸の比(長軸/短軸)が1〜10、好ましくは1〜3の範囲にとなるように切断する。
長軸/短軸比が10を超えると、棒又は紐状となるため、型内に均一に充填することが難しくなり、得られる成形体に密度斑が生じやすい。なお、ここでいう長軸/短軸比は、発泡体の最も長い軸方向と最も短い軸方向の長さの比である。
また、ビーズ状又はペレット状発泡体の大きさは、短軸方向の切断面積を円に換算したときの直径が3〜20mm、好ましくは5〜10mmの範囲にあることが好ましい。この範囲未満であると、発泡体が小さくなりすぎて取扱い性が悪化し、一方これより大きくなりすぎると、型内に充填・熱賦形して得られる成形物に大きな空洞部ができやすくなる。
【0024】
5.生分解性樹脂発泡成型品及びその製造方法
本発明により得られた生分解性樹脂発泡体は、前記したように、押出すノズル又はダイの形状により種々の形態を有するが、その押出された原材を所定の寸法に切断してそのまま使用する場合や、板状発泡体を所望の形状に真空成形する場合を除き、通常は、生分解性樹脂発泡体をビーズ状又はペレット状に切断した後、熱賦形等により各種用途に応じた形態に二次成形し、生分解性樹脂発泡成型品として利用される。
発泡体の二次成形方法は、従来から公知の熱賦形方法が好適である。この方法には、例えば、熱プレスによる方法、加熱バス中で加熱する方法、熱風乾燥処理機により熱風を吹き付ける方法、水蒸気又は加熱水蒸気を型内に導入する方法などがあり、これらの方法を選択することやその際の加熱状況を最適化とすることによっては、二次発泡を期待することもできる。
発泡体を型内に充填して熱賦形する際の温度は、表層部に偏在するポリカプロラクトンの量により最適温度が変化するが、あまりに低温すぎると、発泡体間の接着不良が発生しやすく、逆にあまりに高温すぎると、ポリカプロラクトンの熱劣化、着色、発泡体の収縮などが生じやすいため、通常は120〜200℃の範囲であることが望ましい。
さらに、熱賦形させる際に、バインダーを発泡体に付着せしめて発泡体間の接着強度を増すことも、必要に応じて用いられる。その際、バインダーは、生分解性であり非水溶性であることが、本発明の目的からして望ましい。
【0025】
本発明の生分解性樹脂発泡成型品は、前記した特徴を有している。すなわち、生分解性であって、焼却処理をしても有毒ガスや焼却炉劣化の問題がなく、しかも、非溶出性であるため、水と接触しても成型品の内部から水溶性成分の溶出がなく、その上、寸法安定性や機械的特性にも優れている。したがって、その特徴を生かした各種用途に用いられ、用途としては、特に限定されないが、具体的用途としては、例えば、食品包装容器、水質浄化材、断熱材、緩衝材等を例示することができる。
【0026】
【実施例】
以下に、本発明について実施例及び比較例を挙げてさらに詳細に説明するが、本発明は、これらの実施例に特に限定されるものではない。
【0027】
実施例1[発泡体の製造と成型品の加工と評価]
生分解性樹脂として、軟質の帝人株式会社製セルロース・ジアセテート(表面硬度(HR):85、衝撃強度:25kgf・cm/cm2、流出温度:155℃、熱変形温度:48℃、酢化度:57%)(基準:100重量部)と、日本ユニカー株式会社販売のポリカプロラクトン(商品名:TONEポリマー P−787、融点:60℃、密度:1.145g/cm3 、分子量:8万)(15重量部)とを用い、発泡調整剤として、タルク(14重量部)を添加して、生分解性樹脂配合物とし、これに、発泡剤として、水分(31重量部)を添加して、溶融混練押出機のホッパーに供給し、180℃の温度で加熱溶融混練した後、口径1.5mmを有するノズル部から押し出して、該押出物がノズル口径の1.5倍を超えて膨化する前の段階で切断して、生分解性樹脂の発泡体を得た。
そしてこの得た生分解性樹脂の発泡体は、長軸/短軸比が1.5、短軸方向の切断面積が円換算で直径約10mmであった。
次に、この発泡体を型内に充填して、熱風乾燥処理機により熱風を吹き付ける方法により、150℃で20分間熱賦形させ、評価試験に供することができる大きさの発泡成型品を得た。得られた成型品について、以下の評価試験を実施した。結果を表1に示す。
曲げ強度:JIS K7221(硬質発泡プラスチックの曲げ試験方法)に準拠し、寸法、有効長:200mm、幅:50mm、高さ:40mmの試験片について、曲げ強度を測定する。曲げ強度が0.8Kg/cm2以上を合格とした。
溶出性:成型品について、寸法、長さ:60mm、幅:30mm、高さ:10mmの試験片を作製し、2Lのビーカーの水1L中に浸漬し、室温において48時間静置して、可塑剤の溶出性試験を行う。試験後、試験片を乾燥して、試験片の重量変化とビーカーの水の水質変化とを測定、観察して、可塑剤の溶出の有無を評価する。
押出発泡性:押し出し、発泡、成形する際の、作業性や条件設定の難易度、仕上げ外観、発泡度合い等に支障、不利があるかを評価し総合判断する。
【0028】
【表1】
【0029】
実施例2〜4
実施例1と同様に、表1に示すセルロース・ジアセテートとポリカプロラクトン、発泡調整剤成分(タルク)を同表に示す割合で配合し、生分解性樹脂配合物を調製した。これに、発泡剤として、水分を同表に示す割合で添加して、実施例1と同様の方法で、生分解性樹脂の発泡体を得、得られた発泡体を熱賦形させて、発泡成型品を得た。得られた成型品について、評価試験を実施した。結果を表1に示す。
【0030】
比較例1、2
比較例1は、ポリカプロラクトンの替わりに、可塑剤として、平均分子量400のポリエチレングリコール(35重量部)を用いた以外は、実施例1と同様に実施し、発泡体と発泡成型品を得た。得られた成型品について、評価試験を実施した。結果を表1に示す。
比較例2は、実施例1と同様に、セルロース・ジアセテートとポリカプロラクトン、発泡調整剤成分(タルク)を用い、配合量を表1に示す割合にした以外は、実施例1と同様に実施し、発泡体と発泡成型品を得た。得られた成型品について、評価試験を実施した。結果を表1に示す。
【0031】
これらの評価結果から、セルロース・アセテート系樹脂に対して、該樹脂の軟化点より低い温度の融点を有するポリカプロラクトンの添加量が少なすぎると、実質的にポリカプロラクトンの層で発泡体の表面を覆う程にはならず、その後の成形加工性に劣り、成型品に機械的強度が得られないことは勿論、押出発泡自体に支障が出ることが判明した。また、ポリカプロラクトンを用いた場合には、水と接触しても成型品の内部から水溶性成分が溶出することはなく、食品トレイ等の用途に有利となることが判明した。一方、可塑剤としてポリエチレングリコールを用いた場合は、成型品の内部からポリエチレングリコールの溶出が観察された。さらに、発泡調整材として適当量のタルクを添加した方が、押出発泡性、延いては成形加工性及び成型品の機械的強度を得る上で有利となることが確認された。
【0032】
【発明の効果】
本発明の生分解性樹脂発泡体は、セルロース・アセテート系樹脂に、該樹脂の軟化点より低い融点を有するポリカプロラクトンを配合してなる生分解性樹脂配合物を原料とし、かつ発泡剤として水分を用いる特殊な発泡体製法を適用したことにより、従来の生分解性樹脂に比較して生分解性能に優れ、環境にも優しく、焼却処理しても有毒ガスや焼却炉劣化の問題が少ないばかりでなく、非溶出性であるため、水と接触しても成形体内部から水溶性成分が溶出するといった問題がない。しかも発泡体の表面は、実質的にポリカプロラクトンからなる層で覆われているため、表面平滑性に優れ、熱賦形等により二次成形する際、容易に発泡体間を融着させることができ、機械的特性に優れた発泡成形体が得られる。したがって、本発明の生分解性樹脂発泡体は、その特徴を生かし、食品包装容器、水質浄化材、断熱材、緩衝材等の各種分野に使用することができる。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a non-eluting biodegradable resin extrusion foam molded article, a biodegradable resin foam molded article using the same, and a method for producing the same, and more specifically, food packaging easily by heat shaping or the like. Not only can it be molded into molded products of various forms such as containers, water purification materials, heat insulating materials, buffer materials, etc. The present invention relates to a biodegradable resin extruded foam molded article having no leaching and having good dimensional stability and mechanical properties of the obtained molded article, a biodegradable resin foam molded article using the same, and a production method thereof.
[0002]
[Prior art]
Conventionally, a wide variety of foams made of synthetic resin have been manufactured and used in a wide range of fields such as food packaging containers, water purification materials, heat insulating materials, and cushioning materials. In recent years, the demand for these synthetic resin foams has been increasing year by year. For this reason, the amount of discarded plastics has been increasing year by year, and it has been greatly raised socially as an environmental problem and a pollution problem. However, in order to recycle the waste synthetic resin foam, various measures on a social scale are required. On the other hand, incineration disposal involves a pile of measures such as prevention of harmful gas generation and deterioration of the incinerator due to high heat generation. Development of a foam that has many problems and can be easily disposed of is strongly desired.
[0003]
In response to such demands, various foams in which these synthetic resins are replaced with biodegradable resins have been proposed. For example, in JP-A-5-306349 and JP-A-5-269875, a biodegradable resin chip impregnated with water is heated with oil to form foam beads or foam pellets once. A method is disclosed in which a foam is molded by filling a mold with a biodegradable resin impregnated with water and heating the entire mold with oil for foaming. However, these methods have a problem in that the adhesion between particles is poor and the mechanical properties of the molded product are low. Furthermore, since oil is used as the heating medium, there is a problem that the oil tends to remain between the foam particles, and this gradually oozes out and becomes contaminated.
[0004]
In order to improve the adhesion between the foam particles, a method of molding using an adhesive has also been proposed, but many adhesives are not biodegradable. Coating body particles will inhibit biodegradability. On the other hand, natural product-derived adhesives such as starch and glue are good in terms of biodegradability, but they are hydrophilic, so they are easily affected by humidity and have extremely high adhesion due to moisture absorption and water absorption. Therefore, there is a problem that the usage environment is limited.
[0005]
JP-A-5-320405 and JP-A-6-32928 disclose a method for producing foam particles made of cellulose derivatives such as pendylated cellulose and cellulose acetate, and the obtained foam particles are molded. It has also been disclosed that the foam particles are fused together by steam heating to form a molded body. However, when a plasticizer is not blended in the cellulose derivative, it is difficult to sufficiently fuse the foam particles by steam heating. On the other hand, when a plasticizer is blended in the cellulose derivative, if there is a sufficient amount of plasticizer to fuse the foam particles, the entire foam particles are plasticized during the heat fusion treatment. Therefore, the dimensional stability of the molded product obtained by the shrinkage of the foam particles on the contrary is deteriorated, the mechanical properties are also deteriorated, and when the plasticizer is a polyhydric alcohol or the like, moisture is lost when the molded product is used. When contacted, there is a problem that the plasticizer dissolves and becomes contaminated because it is water-soluble. Further, when the amount of the plasticizer used is reduced, it becomes difficult to plasticize the cellulose derivative, and it becomes difficult to fuse the foam particles during molding.
[0006]
On the other hand, JP-A-7-126537 discloses a biodegradable resin composition comprising a biodegradable resin having a melting point of 100 ° C. or higher and a low melting point biodegradable resin having a melting point of 100 ° C. or lower, such as polycaprolactone. A method for producing a biodegradable resin foam by water foaming a product is disclosed. However, this method is based on injection molding, and the low-melting-point biodegradable resin is distributed throughout the interior of the molded body, and the biodegradable resin foams that are discharged and gathered around the nozzle at the time of injection. It only serves to prevent the occurrence of discontinuous boundaries caused by cavities and nests of the obtained molded product, which acts on the adhesion between the bodies, and there is a problem if the surface smoothness of the molded product is lacking. In addition, if the low-melting-point biodegradable resin alone is insufficient in plasticity of the biodegradable resin composition, it is necessary to add a plasticizer. However, a water-soluble polyhydric alcohol or the like is used as the plasticizer. In such a case, there is a problem of contamination due to elution of the plasticizer as described above.
Japanese Patent Application Laid-Open No. 10-1000026 discloses that a plasticizer of the cellulose derivative is previously attached to the surface of the foam particles when the foam particles made of the cellulose derivative are filled into the mold and thermally shaped. Further, it is also disclosed that the surface of the foam particles is thermoplasticized and fused to form a molded body. However, in this case, there is a problem in that a process of previously attaching a plasticizer to the surface of the foam particles is included, and the process becomes complicated.
As described above, many researches and developments on biodegradable resin foam molded articles made of cellulose derivatives have been attempted, but sufficient foam molding is still easy, and the dimensional stability and mechanical properties of the molded articles are still satisfactory. There were few biodegradable foams that were good. For this reason, there has been a strong demand for the development of a biodegradable foam that is biodegradable and that can be easily molded in-mold when it is molded into a molded product, and that has good mechanical properties.
[0007]
[Problems to be solved by the invention]
The object of the present invention is to eliminate the problems of the above-mentioned conventional foams, and to easily mold them into molded products of various forms such as food packaging containers, water purification materials, heat insulating materials, cushioning materials, etc. by heat shaping or the like. In addition, because it is non-eluting, it does not elute water-soluble components from the inside of the molded body even when it comes in contact with water, and it is a biodegradable resin extrusion foam molding with good dimensional stability and mechanical properties. Another object of the present invention is to provide a biodegradable resin foam molded article using the extruded foam molded body and a method for producing the same.
[0008]
[Means for Solving the Problems]
As a result of earnest research on the above problems, the present inventor has found that the cellulose-acetate-based resin, a polycaprolactone having a melting point lower than the softening point of the resin, and a specific content containing water as a blowing agent. The foamable biodegradable resin composition is extruded and foamed by the vapor expansion force of moisture at the same time, so that the surface is covered with a layer made of polycaprolactone, which is non-eluting and rich in surface smoothness. The biodegradable resin extrusion foam molding can be obtained, and furthermore, by using this biodegradable resin extrusion foam molding, it can be applied to various molded products such as food packaging containers, water purification materials, heat insulating materials, and cushioning materials. It has been found that in-mold molding is easy when forming, and that dimensional stability and mechanical properties are good. The present invention has been completed based on these findings.
[0009]
That is, according to the present invention, cellulose acetate resin100 parts by weightAnd polycaprolactone having a melting point lower than the softening point of the resin5 to 70 parts by weightAnd a foamable biodegradable resin composition containing water as a foaming agent, which is produced by extruding and foaming by the vapor expansion force of water, and is non-eluting biodegradable A resin-extruded foamed molded article is provided.
Furthermore, according to the present invention, the foamable biodegradable resin composition comprises a cellulose / acetate-based resin, polycaprolactone, talc, and water. The biodegradable resin foam, polycaprolactone, Is provided with the biodegradable resin extruded foam molded article characterized by being unevenly distributed in the surface layer part rather than the core part of the extruded foam molded article and substantially covering the surface of the extruded foam molded article. .
[0010]
Furthermore, according to the present invention, there is provided a biodegradable resin foam molded article characterized by heat-molding, vacuum molding, or pressure forming the above-described biodegradable resin extruded foam molded body into a desired shape. The
[0011]
On the other hand, according to the present invention, a cellulose acetate resin is provided in a cylindrical container having an extrusion nozzle or die in front.100 parts by weightAnd polycaprolactone having a melting point lower than the softening point of the resin5 to 70 parts by weightAnd a foamable biodegradable resin composition containing water as a foaming agent, and while the biodegradable resin composition is pushed to the extrusion nozzle, the temperature is raised and fluidized by heating and pressing. There is provided a method for producing the above-described biodegradable resin extruded foamed product, which is made into a state and then extruded and extruded from the extrusion nozzle or die.
Further, according to the present invention, there is provided the above production method, wherein the foamable biodegradable resin composition comprises a cellulose / acetate resin, polycaprolactone, talc, and moisture.
[0012]
Furthermore, according to the present invention, the biodegradable resin extruded foam molded body is cut into beads or pellets, and then packed in a desired mold and thermally shaped. The method for producing a degradable resin foam molded article, and the biodegradable resin extrusion foam molded article are characterized in that they are extruded into a sheet, foamed and molded, and then vacuum molded or compressed air molded into a desired shape. A method for producing the biodegradable resin foam molded article is provided.
[0013]
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, the present invention will be described in detail.
[0014]
1. Cellulose acetate resin
The cellulose-acetate resin used in the biodegradable resin extruded foamed product of the present invention (hereinafter simply referred to as “biodegradable resin foam”) contains cellulose acetate as a main component. The biodegradable resin that may be blended as an accessory component is not particularly limited as long as it does not elute by contact with moisture, and any material that is generally used as a water-insoluble biodegradable resin can be used. Can be used. Examples of these include starch and cellulose.
Cellulose acetate contained as a main component in a cellulose acetate resin is usually produced by reacting acetic acid with linter obtained from cottonseed or cellulose of wood pulp. The cellulose acetate used in the biodegradable resin foam of the present invention may be any grade as long as it is normally marketed as “cellulose acetate”. The degree of acetylation expressed by the weight ratio of bound acetic acid is preferably 45% or more, and particularly the degree of acetylation is 47 to 60% (the number of bound acetyl groups per unit of cellulose is Those of 1.9 to 2.8) are preferred. When the degree of acetylation is less than 45%, the melting temperature becomes too high, and it becomes difficult to stably melt-mold the foam.
Cellulose acetate is preferably soft or medium-hard in terms of physical properties, surface hardness is Rockwell hardness, HR= 80 to 100 and those having an impact strength of 20 to 30 kg-cm / cm are preferably used. Furthermore, from the viewpoint of moldability, the softening point (outflow temperature) at which softening starts to flow (flow temperature) is 150 to 170 ° C., and the load specified by ASTM D 648 is 18.6 kgf / cm.2Those having a thermal deformation temperature of 44 to 55 ° C. under the above conditions are preferably used. On the other hand, in the case of a hard material, it is difficult to stably melt and form the foam.
In addition, the cellulose acetate resin used in the biodegradable resin foam of the present invention includes cellulose acetate acetopropionate using a mixture of propionic acid or butyric acid in addition to acetate having an acetic acid group, cellulose acetate Acetobutyrate is also included, and the mixing ratio of the acid can be appropriately selected and used from the viewpoints of the melting point, water absorption, solubility in the solvent, and the like.
[0015]
2. Polycaprolactone component
The polycaprolactone component used in the biodegradable resin foam of the present invention is made of polycaprolactone having a melting point lower than the softening point of the cellulose acetate resin.
Examples of such polycaprolactone include aliphatic polyesters represented by the following general formula. Examples of commercially available aliphatic polyesters include “Tone” (trade name) sold by Nippon Unicar Co., Ltd. is there.
[0016]
[Chemical 1]
(In the formula, R represents an aliphatic moiety, and n is a positive integer.)
[0017]
The polycaprolactone used in the present invention is not only biodegradable but also water-insoluble, and advantageously, it has the function of plasticizing the cellulose acetate resin by heating, so that it is usually biodegradable. A good biodegradable resin foam rich in surface smoothness can be obtained without adding any plasticizer necessary for producing a degradable resin foam, and a water-soluble plasticizer is used. Therefore, adverse effects such as elution of the plasticizer due to contact with moisture can be avoided. Moreover, surprisingly, the blended polycaprolactone has a lower melting point than the cellulose acetate resin, so it contains polycaprolactone instead of being uniformly distributed inside the biodegradable resin foam. While the biodegradable resin composition to be heated is melted and fed to the extrusion nozzle or die, it shifts from the central part to the peripheral part, that is, from the core part to the surface layer part, and is unevenly distributed in the surface layer part of the biodegradable resin foam Tend to.
Further, as described above, the polycaprolactone used in the present invention needs to have a melting point equal to or lower than the softening point of the cellulose acetate resin. Among these, a preferable melting point is 100 ° C. or less, and a particularly preferable melting point is around 60 ° C. By using polycaprolactone having such a melting point, polycaprolactone can be unevenly distributed in the surface layer portion of the foam. This polycaprolactone has good compatibility with various resins, improves the impact resistance, and improves the dimensional stability of the heat-shaped molded product.
On the other hand, if polycaprolactone with a melting point higher than the softening point of cellulose acetate resin is used, even if it is biodegradable, it does not function to plasticize, so it is a good biodegradable resin foam with excellent surface smoothness I can't get a body.
[0018]
In this invention, the compounding quantity of polycaprolactone is 5-70 weight part with respect to 100 weight part of cellulose acetate type-resins, Preferably it is the range of 10-40 weight part. When the blending amount is less than 5 parts by weight, the proportion of polycaprolactone in the foam surface layer is small, and the thermoplastic effect on the foam surface becomes insufficient during heat forming, and the mechanical properties of the resulting molded product When the strength is deteriorated and exceeds 70 parts by weight, the effect of addition does not appear, and the uneven distribution of polycaprolactone in the foam surface layer becomes excessive, and on the contrary, the finished appearance and moldability are deteriorated.
[0019]
3. Foamable biodegradable resin composition
As described above, the foamable biodegradable resin composition used in the biodegradable resin foam of the present invention is obtained by blending a predetermined amount of polycaprolactone and moisture as a foaming agent into a cellulose acetate resin. Prepared. The blending ratio of water as a foaming agent is 3 to 100 parts by weight, preferably 5 to 50 parts by weight, with respect to 100 parts by weight of the biodegradable resin blend of cellulose / acetate resin and polycaprolactone.
In the biodegradable resin composition of the present invention, as described above, since polycaprolactone functions to plasticize the cellulose acetate resin, good biodegradability can be obtained without adding other plasticizers. A resin foam can be obtained, but if necessary, other plasticizers may be blended as long as they are water-insoluble plasticizers as long as the object of the present invention is not impaired.
[0020]
Furthermore, the above biodegradable resin composition may be blended with other additives and the like within a range not impairing the object of the present invention. For example, a heat stabilizer, a foaming modifier, a foaming aid, an extender. Etc. Among them, foam regulators such as inorganic fine particles such as talc, silicon oxide, titanium oxide, magnesium oxide, aluminum oxide, calcium silicate, organic fine particles such as cellulose powder, chitin, chitosan, wood powder, metal stearate, In particular, talc can impart suitable foaming properties to the biodegradable resin composition, so that a uniform and highly foamed foam can be easily obtained. Such foaming modifiers may be used alone or in combination of two or more. Further, for the purpose of improving foamability or neutralizing acidic substances by-produced during foam production and generating gas, inorganics such as sodium bicarbonate, potassium bicarbonate, sodium carbonate, potassium carbonate, calcium carbonate, etc. Fine particles may be used in combination. Further, as an extender, okara, wood flour, rice bran (wheat skin), rice flour, waste paper, and the like can be added.
A preferred embodiment of the biodegradable resin composition of the present invention includes a biodegradable resin composition comprising a cellulose-acetate-based resin, polycaprolactone, talc as a foaming modifier, and moisture as a foaming agent. The above-described extender may be added to the biodegradable resin composition.
The blending amount of talc with respect to the biodegradable resin composition as the foam regulator is in the range of 5 to 50 parts by weight, preferably 10 to 30 parts by weight, with respect to 100 parts by weight of the cellulose / acetate resin. When the blending amount is less than 5 parts by weight, the effect of blending talc does not appear, and a non-uniform and coarse foam tends to be formed. On the other hand, when the blending amount exceeds 50 parts by weight, secondary aggregation of talc tends to occur. Again, a non-uniform and rough foam is likely to be formed.
[0021]
4). Biodegradable resin foam (extruded foam) and method for producing the same
The biodegradable resin foam of the present invention is produced by foaming the foamable biodegradable resin composition by the vaporization expansion force of moisture simultaneously with extrusion molding.
Therefore, the biodegradable resin foam of the present invention has the following characteristics.
(1) Foamed with water.
(2) Since all the materials are biodegradable, it is possible to deal with various disposal treatments compared to general-purpose plastic foams.
(3) Due to non-elution, there is no problem of elution of plasticizers even when it comes into contact with moisture.
(4) Since the surface is covered with a polycaprolactone layer, secondary molding such as heat shaping is easy.
(5) Compared to starch-based biodegradable resin foams, etc., the impact performance does not fluctuate depending on the atmospheric humidity and is excellent in strength.
(6) Excellent surface smoothness.
Furthermore, as described above, the biodegradable resin foam of the present invention is characterized in that polycaprolactone is unevenly distributed in the surface layer portion of the foam. Here, the foam surface layer portion refers to a portion within several mm in the outer portion of the diameter when the cut area in the short axis direction of the foam is converted into a circle. When a foamable biodegradable resin composition is extruded, polycaprolactone is heated and melted together with a cellulose / acetate-based resin and tends to move from the center to the surface layer while being fed to an extrusion nozzle or die. Therefore, there is relatively little polycaprolactone in the center of the foam, that is, the core, and relatively much polycaprolactone is present in the outer surface layer portion.
If polycaprolactone is unevenly distributed in the surface layer of the foam, and the surface is not covered with a layer made of substantially polycaprolactone, it will be difficult to melt and fuse with each other in secondary molding such as heat forming. As a result, moldability deteriorates. As described above, the polycaprolactone is unevenly distributed in the surface layer portion of the foam, so that a foam molded product having mechanical strength such as bending strength that does not impede practical use can be obtained.
[0022]
As described above, the biodegradable resin foam is produced by foaming the foamable biodegradable resin composition at the same time as extrusion molding with the vaporization expansion force of moisture. It becomes as follows.
A foamable biodegradable resin composition containing a cellulose / acetate-based resin, polycaprolactone, and moisture (foaming agent) is prepared at a predetermined ratio, and is then placed in a cylindrical container having an extrusion nozzle or die in front (for example, , And kneading extruder). As a method for introducing water into the cylindrical container, a predetermined amount of water may be included in the biodegradable resin composition for foaming in advance, or the biodegradability of the biodegradable resin or polycaprolactone may be included. Water itself may be added directly into the hopper along with the resin blend, as long as the biodegradable resin blend and moisture are supplied together. Further, as described above, the charging ratio is 3 to 100 parts by weight, preferably 5 to 50 parts by weight, based on 100 parts by weight of the biodegradable resin composition.
Subsequently, this biodegradable resin composition is heated and melt-kneaded at a temperature of 120 to 250 ° C., preferably 180 to 220 ° C., until it is pushed to the extrusion nozzle, and as a result, it is heated and pressurized in a fluid state. After being brought into a state, it is extruded from a nozzle or die having a diameter of 0.5 to 5 mm, for example. The melt-kneading time varies depending on the discharge amount per unit time, the melt-kneading temperature, and the like, and thus cannot be determined unconditionally. However, the melt-kneading time may be sufficient as long as the mixture is uniformly melt-kneaded. The temperature of the nozzle or die of the discharge unit may be the same as the melt kneading temperature, but may be lower than the temperature within a dischargeable range. Here, the extruder used for the melt-kneading may be any type of extruder as long as the water is forcibly dissolved in the cellulose acetate under high temperature and high pressure. A screw or twin screw type extruder is used.
After that, the melt biodegradable resin composition discharged from the nozzle or die pore has a foaming start position that varies depending on its temperature and moisture content, but usually foams from a position 0.1 mm away from the nozzle or die part. After starting and finishing foaming, it is formed into a shape that matches the shape of the extrusion port. The shape of the nozzle or die pore to be extruded may be any of a circle, a triangle, a square, a rectangle, a star, and a hollow, and may be appropriately selected according to the purpose.
[0023]
The obtained biodegradable resin foam is usually used after being cut into beads or pellets for secondary molding, but the biodegradable resin foam is in the process of foaming. Is preferably cut. The reason for this is that, by cutting in the melt plasticized state before the cellulose acetate resin compound is solidified, the newly formed cut surface becomes smooth in the process of further swelling after cutting. Therefore, the surface is smooth and the foam has rounded corners, and the in-mold filling property is improved. Therefore, the extrudate is cut at a stage before it expands more than 3 times the nozzle or die pore diameter, preferably at a stage before it expands more than 1.5 times. This cutting length is cut so that the ratio of the major axis to the minor axis (major axis / minor axis) of the obtained bead-like or pellet-like foam is in the range of 1 to 10, preferably 1 to 3.
When the major axis / minor axis ratio exceeds 10, it becomes a rod or string shape, so that it is difficult to uniformly fill the mold, and density spots are likely to occur in the obtained molded body. The major axis / minor axis ratio here is the ratio of the longest axial direction and the shortest axial length of the foam.
In addition, the size of the bead-like or pellet-like foam is preferably in the range of 3 to 20 mm, preferably 5 to 10 mm in diameter when the cut area in the minor axis direction is converted into a circle. If it is less than this range, the foam becomes too small and the handleability deteriorates. On the other hand, if it becomes too large, it becomes easy to form a large cavity in the molded product obtained by filling and heat forming in the mold. .
[0024]
5). Biodegradable resin foam molded product and method for producing the same
As described above, the biodegradable resin foam obtained by the present invention has various forms depending on the shape of the nozzle or die to be extruded, and the extruded raw material is cut into a predetermined size and used as it is. In general, the biodegradable resin foam is cut into beads or pellets and then subjected to various applications by thermal shaping etc., except when vacuum forming the plate-like foam into a desired shape. Secondary molded into a shape and used as a biodegradable resin foam molded product.
As the secondary molding method of the foam, a conventionally known heat shaping method is suitable. This method includes, for example, a method using a hot press, a method of heating in a heating bath, a method of blowing hot air using a hot air dryer, and a method of introducing water vapor or heated water vapor into a mold. It is also possible to expect secondary foaming by optimizing the heating conditions at that time.
The optimum temperature for heat forming by filling the foam into the mold varies depending on the amount of polycaprolactone unevenly distributed in the surface layer, but if it is too low, poor adhesion between the foams is likely to occur. On the other hand, if the temperature is too high, the polycaprolactone is likely to be thermally deteriorated, colored, or shrinkage of the foam. Therefore, it is usually preferably in the range of 120 to 200 ° C.
Furthermore, it is also used as needed to increase the adhesive strength between the foams by attaching the binder to the foams when heat forming. In that case, it is desirable for the purpose of the present invention that the binder is biodegradable and water-insoluble.
[0025]
The biodegradable resin foam molded article of the present invention has the characteristics described above. In other words, it is biodegradable, has no problem of toxic gas or incinerator deterioration even when incinerated, and is non-eluting, so even if it comes into contact with water, There is no elution, and in addition, it has excellent dimensional stability and mechanical properties. Therefore, it is used for various applications that make use of its characteristics, and the application is not particularly limited. Examples of specific applications include food packaging containers, water purification materials, heat insulating materials, cushioning materials, and the like. .
[0026]
【Example】
Hereinafter, the present invention will be described in more detail with reference to examples and comparative examples, but the present invention is not particularly limited to these examples.
[0027]
Example 1[Manufacture of foam and processing and evaluation of molded products]
As a biodegradable resin, soft Teijin Limited cellulose diacetate (surface hardness (HR): 85, impact strength: 25 kgf · cm / cm2Outflow temperature: 155 ° C., heat distortion temperature: 48 ° C., acetylation degree: 57% (standard: 100 parts by weight) and polycaprolactone (trade name: TONE polymer P-787, sold by Nippon Unicar Co., Ltd., melting point: 60 ° C., density: 1.145 g / cmThree , Molecular weight: 80,000) (15 parts by weight), talc (14 parts by weight) is added as a foaming modifier to obtain a biodegradable resin composition, and as a foaming agent, water (31 weights) Part) is fed to the hopper of the melt-kneading extruder, heated and melt-kneaded at a temperature of 180 ° C., and then extruded from a nozzle part having a diameter of 1.5 mm. It cut | disconnected in the stage before expanding more than double | fold, and the foam of the biodegradable resin was obtained.
The obtained biodegradable resin foam had a major axis / minor axis ratio of 1.5 and a cut area in the minor axis direction of about 10 mm in diameter in terms of a circle.
Next, this foam is filled into a mold, and hot foam is blown by a hot air drying processor, and heat molded at 150 ° C. for 20 minutes to obtain a foam molded product having a size that can be used for an evaluation test. It was. The following evaluation tests were performed on the obtained molded products. The results are shown in Table 1.
Bending strength: According to JIS K7221 (bending test method for rigid foam plastic), the bending strength is measured for a test piece having dimensions, effective length: 200 mm, width: 50 mm, and height: 40 mm. Bending strength is 0.8Kg / cm2The above was regarded as passing.
Dissolution: For molded products, test pieces with dimensions, length: 60 mm, width: 30 mm, and height: 10 mm were prepared, immersed in 1 L of water in a 2 L beaker, and allowed to stand at room temperature for 48 hours to plasticize. Perform dissolution test of the agent. After the test, the test piece is dried, and the change in the weight of the test piece and the change in the water quality of the beaker are measured and observed to evaluate whether or not the plasticizer is eluted.
Extrusion foamability: Comprehensive judgment is made by evaluating whether there are any obstacles or disadvantages in workability, difficulty in setting conditions, finished appearance, foaming degree, etc. during extrusion, foaming and molding.
[0028]
[Table 1]
[0029]
Examples 2-4
In the same manner as in Example 1, cellulose diacetate, polycaprolactone and foaming modifier component (talc) shown in Table 1 were blended in the proportions shown in the same table to prepare a biodegradable resin blend. To this, as a foaming agent, water was added at a ratio shown in the same table, and in the same manner as in Example 1, a biodegradable resin foam was obtained, and the resulting foam was thermally shaped, A foam molded product was obtained. An evaluation test was performed on the obtained molded product. The results are shown in Table 1.
[0030]
Comparative Examples 1 and 2
Comparative Example 1 was carried out in the same manner as in Example 1 except that polyethylene glycol (35 parts by weight) having an average molecular weight of 400 was used as a plasticizer instead of polycaprolactone to obtain a foam and a foam molded product. . An evaluation test was performed on the obtained molded product. The results are shown in Table 1.
Comparative Example 2 was carried out in the same manner as in Example 1 except that cellulose diacetate, polycaprolactone, and a foaming modifier component (talc) were used in the same manner as in Example 1 except that the blending amounts were as shown in Table 1. Thus, a foam and a foam molded product were obtained. An evaluation test was performed on the obtained molded product. The results are shown in Table 1.
[0031]
From these evaluation results, when the amount of polycaprolactone having a melting point lower than the softening point of the resin is too small for the cellulose acetate resin, the surface of the foam is substantially covered with the polycaprolactone layer. It was found that the extrusion foaming itself was hindered as well as not being covered, inferior in molding processability thereafter and not being able to obtain mechanical strength in the molded product. In addition, when polycaprolactone was used, it was found that water-soluble components did not elute from the inside of the molded product even when contacted with water, and this was advantageous for uses such as food trays. On the other hand, when polyethylene glycol was used as the plasticizer, elution of polyethylene glycol was observed from the inside of the molded product. Furthermore, it has been confirmed that the addition of an appropriate amount of talc as a foam adjusting material is advantageous in obtaining extrusion foaming properties, as well as molding processability and mechanical strength of a molded product.
[0032]
【The invention's effect】
The biodegradable resin foam of the present invention is made from a biodegradable resin blend obtained by blending cellulose acetate resin with polycaprolactone having a melting point lower than the softening point of the resin, and water as a foaming agent. By applying a special foam manufacturing method using, it has superior biodegradability compared to conventional biodegradable resins, is environmentally friendly, and has few problems of toxic gas and incinerator degradation even after incineration. In addition, since it is non-eluting, there is no problem that water-soluble components are eluted from the inside of the molded article even when it comes into contact with water. Moreover, since the surface of the foam is substantially covered with a layer made of polycaprolactone, it has excellent surface smoothness and can be easily fused between the foams when secondary molding is performed by heat shaping or the like. And a foamed molded article having excellent mechanical properties can be obtained. Therefore, the biodegradable resin foam of the present invention can be used in various fields such as a food packaging container, a water purification material, a heat insulating material, and a cushioning material, taking advantage of its characteristics.
Claims (9)