JP3742402B2 - Animal excrement disposal material and method for producing the same - Google Patents
Animal excrement disposal material and method for producing the same Download PDFInfo
- Publication number
- JP3742402B2 JP3742402B2 JP2003128449A JP2003128449A JP3742402B2 JP 3742402 B2 JP3742402 B2 JP 3742402B2 JP 2003128449 A JP2003128449 A JP 2003128449A JP 2003128449 A JP2003128449 A JP 2003128449A JP 3742402 B2 JP3742402 B2 JP 3742402B2
- Authority
- JP
- Japan
- Prior art keywords
- waste wood
- particles
- less
- particle size
- excrement disposal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【産業上の利用分野】
本発明は、動物、特に猫科及び犬科動物並びにその他愛玩動物等の動物の粒状の排泄物処理材及びその製造方法に関し、特に、建築現場などで既に使用済みの廃木材の有効利用を図る、動物、特に猫科及び犬科動物並びにその他愛玩動物等の動物の粒状の排泄物処理材及びその製造方法に関する。
【０００２】
【従来の技術】
家畜、愛玩動物等の動物の排泄物処理材、特に屋内での排泄物処理材としては、砂、ベントナイト、ゼオライト、製紙用パルプ、パルプスラッジなどを小塊状に成形して使用されている。
この種の愛玩動物の排泄物処理材は、例えば室内で使用されるところから、清潔で、衛生的であることが望まれ、使用後、清潔さ及び衛生上の点から、廃棄処理され易いのが望まれる。しかし、砂、ゼオライト、ベントナイトなどの無機物の場合は、使用時、砕けて埃となり易く、また、使用後放置する間に汚臭を発生しても、非可燃物であるため焼却処理を行うことができず、また下水等に流すこともできない。そこで、消臭効果が低く、価格が高いが、吸水能に優れ、可燃物であるところから、製紙用パルプ及び紙粉の小塊状成形物が使用されている。
【０００３】
【発明が解決しようとする課題】
廃木材は、建築産業、その他木材産業などからかなりの量で発生し、その量は膨大な量に上っており、その多くが、産業廃棄物として捨てられ、その殆どは、焼却処理されており、その扱いが建築産業やその他木材産業の課題の一となっている。
従来、廃木材の粉砕物は、その侭では粒状化することが難しいために、紙粉又は紙パルプ及び高吸水性樹脂と混合して、造粒して粒状の動物用排泄物処理材を製造している。しかし紙粉及び紙パルプは、比較的高価であり、量的に少なく廃木材処理の上で問題とされている。
本発明は、従来の廃木材処理に係る問題点を解決することを目的としている。
【０００４】
【課題を解決するための手段】
本発明者は、廃木材を、粗粉砕して解繊することにより得られる廃木材の繊維状の粒子は、高吸水性樹脂及び水と混合して押出し造粒等の造粒手段により、紙粉及び紙パルプを混合しないでも、容易に造粒できることを発見して本発明に至った。
即ち、本発明は、製材所から発生する大量のおが屑、建築現場等から発生する廃木材を、紙粉や紙パルプを混合しないで、造粒して製造できる動物用廃木材処理材及びその製造方法を提供する。
【０００５】
即ち、本発明は、５ｍｍ以下の粒度で、粒子の短軸の長さ１に対し粒子の長軸の長さが４以上の寸法比を有する繊維状の廃木材粒子を主として含有する廃木材粉砕物及び前記廃木材粉砕物より少ない量の接着剤を含む混合物により形成されている粒状物であることを特徴とする動物の排泄物処理材にあり、また、本発明は、５ｍｍ以下の粒度で、粒子の短軸の長さ１に対し粒子の長軸の長さが４以上の寸法比を有する繊維状の廃木材粒子を主として含有する廃木材粉砕物並びに前記廃木材粉砕物より少ない量の接着剤及び配合物質を含む混合物により形成されている粒状物であることを特徴とする動物の排泄物処理材。
にある。
【０００６】
これらの他に、本発明は、廃木材を、粗粉砕することにより、５ｍｍ以下の粒度で、粒子の短軸の長さ１に対し粒子の長軸の長さが４以上の寸法比を有する繊維状の廃木材粒子に解繊して、前記繊維状の廃木材粒子を主として含有する廃木材粉砕物を形成し、この形成された前記繊維状の廃木材粒子を主として含有する廃木材粉砕物に、接着剤及び水を加えて、造粒用混合物を形成し、この形成された造粒用混合物を造粒して、造粒物粒子を形成することを特徴とする廃木材からの動物の排泄物処理材の製造方法にある。
【０００７】
【発明の実施の形態】
本発明の動物の排泄物処理材において、接着剤は、粒状物に対し、粒状物に対し、５重量パーセント未満の含有率の一種以上の高吸水性樹脂及び粒状物に対し１０重量パーセント以下の含有率の一種以上の糊剤であるのが好ましい。しかし５重量パーセント未満の含有率の一種以上の高吸水性樹脂若しくは粒状物に対し５重量パーセント以下の含有率の一種以上の糊剤又はこれらの組み合わせとすることができる。また、接着剤を、高吸水性樹脂とする場合には、粒状物に対し、３０重量パーセント以下の含有率の一種以上の高吸水性樹脂であるのが好ましいが、粒状物に対し、５重量パーセント未満の含有率の一種以上の高吸水性樹脂とすることができる。
【０００８】
また、接着剤として、高吸水性樹脂を使用する場合は、高吸水性樹脂は、３０μｍ以下の粒度を有するものであるのが好ましい。しかし、２０μｍ以下の粒度を有するものとすることができる。本発明の動物の排泄物処理材において、糊剤としては、ポリアクリルアミド、α−澱粉、ポリビニルアルコール、コンスターチ、小麦粉若しくはカルボキシメチルセルロース又はこれら二以上のものを組み合わせたものを使用することができる。
【０００９】
本発明の動物の排泄物処理材において、造粒物の吸水速度を増すために、陽イオン界面活性剤、陰イオン界面活性剤、中性イオン界面活性剤及び非イオン界面活性剤等の界面活性剤を使用することができる。廃木材が松等の水を弾く材料である場合、界面活性剤の使用は、水を弾く材料を濡れさせることができ、廃木材粉砕物の吸水性及び保水性を増加させると共に、また、本発明の動物の排泄物処理材において、使用される繊維状の廃木材粉砕物は、粒度が５ｍｍ以下、好ましくは３ｍｍ以下、さらに好ましくは２ｍｍ以下とすると、吸水性能及び保水性能が大きくなり、また造粒することが容易となるので好ましい。
本発明の動物の排泄物処理材の粒状物の粒度は、２ｍｍ以上であるのが、粉状物が少なくなるので好ましいが、６ｍｍ以下とするのが使用上好ましい。
【００１０】
本発明の動物の排泄物処理材は、芯部と芯部を被覆する被覆層部で形成することができる。この場合、被覆層部は、濡れた粒子相互が付着しあって塊状を形成するように付着性を有するように形成され、芯部は、吸水した尿等の排泄物を保持できるように、吸水性及び保水性を有するように形成されれる。芯部は、排泄物処理材粒子の７５乃至９５重量パーセントであり、被覆層部は、５乃至２５重量パーセントであるのが、該排泄物処理材としての吸水及び保水性能及び排泄物処理材粒子の付着性能を達成する上で好ましい。
本発明の、芯部及び被覆層部の二層からなる動物の排泄物処理材においても、一層の造粒物からなる動物の排泄物処理材と同様に、接着剤は、一種以上の高吸水性樹脂若しくは一種以上の糊剤又はこれらの組み合わせとすることができる。本発明の動物の排泄物処理材の芯部においては、造粒が容易に行えるように、接着剤は、例えば、５重量パーセント未満の含有率で含有される一種以上の高吸水性樹脂及び１０重量パーセント以下の含有率で含有される一種以上の糊剤とすることができるが、芯部における接着剤は、５重量パーセント未満の含有率で含有される一種以上の高吸水性樹脂若しくは５重量パーセント以下の含有率で含有される一種以上の糊剤又はこれらを組み合わせたものとすることができる。芯部における接着剤は、高吸水性樹脂を単独で接着剤とする場合には、高吸水性樹脂は、３０重量パーセント以下の含有率で含有させることができる。高吸水性樹脂及び糊剤を一緒に接着剤として使用する場合は、解繊された木粉に、別個に又は予め混合して配合することができる。
【００１１】
本発明の動物の排泄物処理材において、被覆層部における接着剤は、３５重量パーセント以下の含有率で含有される一種以上の高吸水性樹脂とすることができる。被覆層部において、接着剤は、５重量パーセント未満の含有率で含有される一種以上の高吸水性樹脂若しくは５重量パーセント以下の含有率で含有される糊剤又はこれらを組み合わせたものとすることができる。本発明において、高吸水性樹脂は、３０μｍ以下の粒度を有するものであるのが好ましいが、２０μｍ以下の粒度を有するものとすると、さらに好ましい。
本発明において、芯部及び／又は被覆層部に使用される接着剤は、造粒物に使用される接着剤と同様であり、即ち、一種以上の高吸水性樹脂及び／又は糊剤とすることができる。本発明において、糊剤についても同様に、ポリアクリルアミド、α−澱粉、ポリビニルアルコール若しくはカルボキシメチルセルロース又はこれらの二以上の組み合わせたものである。
本発明において、芯部及び／又は被覆層部に使用される配合物質としては、一種以上の着色物質若しくは一種以上の殺菌作用を有する物質又はこれらの組み合わせである。本発明において、芯部若しくは被覆層部又はこれら双方に、界面活性剤を含有させると、吸水性能を増加できるので好ましい。界面活性剤は、造粒物単独の場合と同様であり、陽イオン界面活性剤、陰イオン界面活性剤、中性イオン界面活性剤及び非イオン界面活性剤等の界面活性剤を使用することができる。陽イオン界面活性剤の場合は、殺菌効果があるので、殺菌作用を有する物質として使用することができる。
【００１２】
本発明において、芯部の廃木材粉砕物は、主として、２乃至５ｍｍの粒度の繊維状の廃木材粒子を含有する廃木材粉砕物である。本発明において、芯部の廃木材粉砕物は、主として、５ｍｍ以下の粒度、好ましくは、３ｍｍ以下の粒度、さらに好ましくは２ｍｍ以下の粒度の繊維状の廃木材粒子を含有するものである。被覆層部において、繊維化された廃木材粉砕物は、例えば０．５ｍｍ以下の粒度に細かくすることにより、被覆することを容易にさせることができ、例えば０．１ｍｍ以下の粒度の繊維状の廃木材粒子を主として含有する繊維化された廃木材粉砕物とするのが好ましい。細かい微粒子は、保存時において剥落し易いので、被覆層部の繊維化されたの廃木材粉砕物が、０．１乃至０．５ｍｍの粒度、好ましくは、繊維状の廃木材粒子を含有する廃木材粉砕物とするのが好ましい。本発明において、芯部は、２ｍｍ以上の粒度、好ましくは３ｍｍ以上の粒度とすることができる。動物の排泄物処理材は、３ｍｍ以上の粒度に形成することができ、また６ｍｍ以下の粒度に形成することができる。
【００１３】
本発明において、廃木材は、剪定枝、木材の樹皮、木材の建築現場からの使用済み建築資材、製材所から発生する木片及び木屑並びにおが屑などの廃木材は、例えば５０乃至３００ｍｍの大きさに破砕される。破砕された廃木材片は、金属を有するものを分離するために、静電分離、磁力選別される。静電分離及び磁力選別により鉄片及び／又は金属片が分離された５０乃至３００ｍｍの大きさの廃木材片は、５乃至３０ｍｍの大きさの粒子に粗粉砕される。粗粉砕された廃木材粒には、可成の量の金属粒が夾雑されるので、夾雑される金属粒を、風力選別（風簸）又は磁力選別（磁選）により分離し、金属粒が分離された廃木材粒は、解繊機により、３乃至５ｍｍの粒度で繊維化される。本発明において、繊維化された廃木材粉砕物は、繊維状粒子を含有するものであり、繊維化されない廃木材粉砕物に比して、吸水性及び保水性に優れる。ここで繊維状の粒子は、粒子の短軸の長さ即ち粒子の幅１に対する粒子の長軸の長さ即ち粒子の長さが４以上のものであり、好ましくは、６以上である。本発明において、繊維化された廃木材粉砕物は、このような寸法比を有する繊維状粒子を５０重量％以上、好ましくは７０重量％以上含有するのが好ましい。
【００１４】
本発明において、５ｍｍ以下の粒度、３乃至５ｍｍの粒度及び３ｍｍ以下の粒度の廃木材の繊維状粒子は、高吸水性樹脂及び水と混合して、押出し造粒される。繊維化されない廃木材粉砕物は、高吸水性樹脂との混合物としても、粒状に造粒することが困難である。本発明において、木粉を繊維化することにより、高吸水性樹脂の使用を減少させることができる。本発明において、高吸水性樹脂の使用量は、排泄物処理材としての吸水能力、保水能力及び濡れた造粒された粒子相互の付着能力を保持するに足りればよい。造粒粒子相互の付着及び繊維状粒子の付着を容易にするためには、高吸水性樹脂に代えて糊剤を使用することができる。このような糊剤としては、ポリアクリルアミド、α−澱粉、ポリビニルアルコール（ＰＶＡ）、カルボキシメチルセルロース（ＣＭＣ）などの接着剤を使用することができる。本発明においては、ポリアクリルアミド及びα−澱粉を繊維状に粒子の付着に使用するのが好ましい。
【００１５】
本発明において、押出し造粒には、繊維化された廃木材粉砕物の繊維状粒子を、高吸水性樹脂及び水と混合した混合物が使用される。繊維化されないで単に３乃至５ｍｍの粒度に粉砕された廃木材粉砕物の粒子の場合には、前記繊維状粒子の含有率が２０重量％以下であり、高吸水性樹脂及び水と混合した混合物では、押出し造粒により粒状にすることが難しい。
本発明において、繊維化された廃木材粒を形成するために、粉砕された廃木材の粒子は、解繊機、例えば市販の乾式紙片解繊機により、繊維化及び粉砕される。解繊機により解繊された、粒度が３乃至５ｍｍの廃木材粉砕物には、繊維状粒子が７０重量％以上の含有率で含有される。おが屑等の木粉は、解繊機で解繊して使用するのが、紙粉等の紙材を混ぜないで造粒する場合に、造粒作業が円滑に行えるので好ましい。
本発明において、動物用の粒状の排泄物処理材は、粒度が２ｍｍ以上、例えば２ｍｍ、３ｍｍ、４ｍｍ又は５ｍｍ以上の粒子に造粒することにより製造され、例えば、水分が１０％以下、好ましくは、５％以下の乾燥状態で保存される。
本発明において、粒状の動物用排泄物処理材は、水分含有率を１５重量％以下、好ましくは１０重量％となるように乾燥することにより、保管時の黴の発生を防止することができるので、２０重量％以上の含水率で造粒するときは、最終段階で１０重量％以下の含水率になるまで乾燥するのが好ましい。
【００１６】
本発明において、建築現場及び製材所から発生する廃木材は、針葉樹及び広葉樹の何れの廃木材も使用することができる。
本発明において、動物の排泄物処理材に使用される廃木材は、保存時の黴の発生を避けるために、ヒノキチオールを成分として含有する廃木材が好ましい。
ヒノキチオールはヒノキ科の木材に含まれていおり、このような、ヒノキ科の木材としては、例えば、アスナロ属ではアスナロ、ヒノキアスナロ（ひば）があり、ネズミサシ属の木材としては、イブキ、ハイネズミがあり、クロベ属の木材としては、クロベ（ネズコ）、ウエスタンレッドシーダーがあり、またインセンスシーダ属では、インセンスシーダーがあり、ヒノキ属としてタイワンヒノキがある。
【００１７】
本発明において、排泄物処理材は、使用時に、動物に乾燥したさらさらした感触を与えると共に、排泄物処理材の保存時の黴等の発生を防止するために、乾燥状態で保存される。
本発明において、排泄物処理材とされる廃木材粉砕物の造粒物は、乾燥状態でにされて保存される。そこで、本発明においては、着色された繊維化された廃木材粉砕物の造粒物は、好ましくは含有水分が１０重量％以下、さらに好ましくは５重量％以下になるまで乾燥して、動物の排泄物処理材とされる。しかし、比較的多湿の雰囲気下で使用される動物用の排泄物処理材の場合、殺菌作用を有する物質を前記繊維状の木粉に配合して、廃木材粉砕物を造粒すると、長期に亙って、黴などの発生を避けて動物用排泄物処理材として保存することができるので好ましい。しかし、繊維化された廃木材粉砕物としては、ヒノキチオールを採取した採取滓を廃木材として使用する場合には、ヒノキチオールが僅かながら廃木材粉砕物中に残留するので、その残留量に応じて、前記殺菌作用を有する物質の使用を減少又は省略することができる。
【００１８】
本発明において、繊維化された廃木材粉砕物の造粒物の表面は、該廃木材粉砕物の本来有する色彩を呈しており、造粒物をその侭、排泄物処理材として使用できるが、特別に着色物質により着色して、廃木材粉砕物の造粒物の本来の色彩を着色物質により隠して、各種の色彩の排泄物処理材とすることができる。本発明において、着色された木粉の造粒物は、その侭、排泄物処理材として使用することができるが、この場合、埃となるのを避けるために、例えば１ｍｍより小さい粒径の細かい粉状部分を分離しておくのが好ましい。
【００１９】
本発明において、排泄物処理材を使用雰囲気に調和させる目的で、木粉造粒物は着色物質により着色される。本発明において、着色物質は、顔料及び染料を使用することができる。このような顔料及び染料には、例えば、白色のものとして、炭酸カルシウム、酸化チタン及び合成パールがあり、青色の顔料及び染料としては、シアニンブルー、アゾブルー及びパテントブルーがあり、緑色の顔料及び染料としては、シアニングリーン及びエメラルドグリーンがあり、黄色の顔料及び染料としては、アゾイエロー、アシッドイエロー及びハンサイエローがある。
【００２０】
本発明において、排泄物処理材粒子は、尿に触れた部分が互いに付着し合って集合体を形成して、尿に触れた部分を取り出し易くさせることができる。この場合、繊維化された廃木材の粉砕物には、混合される高吸水性樹脂の他に、ポリアクリルアミド及び／又はα−澱粉を配合することができる。しかし、これら以外にも、尿に触れて粉体粒子相互を接着させて、容易に塊状物とするような接着機能を有する材料を選択することができる。
また、本発明において、使用時の排泄物処理材の粉化を避けるために、廃木材粉砕物に、接着機能を有する物質を配合するのが好ましい。このような接着機能を有する物質としては、水溶性又は水分散性のものとして、ポリビニルアルコール（ＰＶＡ）、小麦粉、澱粉、コーンスターチ、カルボキシメチルセルロース（ＣＭＣ）、プルラン又はゼラチンなどがあり、これらは、単独で使用されるか、又はこれら２種以上を混合して配合物質として使用することができる。また、アルコール溶解性の配合物質としては、ヒドロキシエチルセルロース（ＨＥＣ）、ヒドロキシプロピルセルロース（ＨＰＣ）又はポリビニルピロリドン或（ＰＶＰ）などがあり、この場合も同様に、これらは夫々単独で使用されるか、又はこれらの２種以上を混合して使用することができる。
【００２１】
また本発明の排泄物処理材において、高吸水性樹脂は、動物用の排泄物処理材の吸水機能、保水機能及び使用後の粒子相互の付着機能を高めるために配合され、その使用量は３０重量パーセント以下であるのが好ましい。本発明において、動物用の排泄物処理材中の高吸水性樹脂の配合割合は、５乃至３０重量％であるが、付着機能を接着剤により行うときは、高吸水性樹脂の量は５重量パーセント以下とすることができる。本発明において、高吸水性樹脂の用語は、３０倍程度の水を吸収する吸水性樹脂をも意味する。本発明においては、木粉を繊維化させることしにより、このような高吸水性樹脂とはいえない吸水樹脂の使用を容易にさせる。
本発明において配合される高吸水性樹脂は、一般に、自重の数十倍から二千倍程度の水を吸収しても、形を保持できる樹脂であり、例えば、ビニルエステルとエチレン系不飽和カルボン酸又はその誘導体との共重合体鹸化物、澱粉とアクリル酸のグラフト重合体、ポリアクリル酸の架橋物、ビニルアルコールとアクリル酸の共重合体、ポリアクリロニトリルの部分加水分解物、カルボキシメチルセルロースの架橋物、ポリエチレングリコールの架橋物、キトサンの塩又はプルランのゲルなどがあり、これらは、繊維化された廃木材粉砕物に、単独で又は２種以上の混合物として配合することができる。
【００２２】
本発明において、排泄物処理材を排泄物指示薬として兼用することができる。この場合には、着色物質及び配合物質の色彩を例えば白一色に揃えると、その指示薬の発色の確認が容易となり、適宜の排泄物検査用指示薬を配合して、動物の排泄物による検診を簡単に行うことができることとなり好ましい。本発明において使用される動物用の尿検査用指示薬は、従来の動物用の尿検査用指示薬と同様に、人の尿検査用指示薬、即ち尿ｐＨ指示薬、尿蛋白指示薬、尿糖指示薬、尿ヘモグロビン指示薬及びその他の人の尿検査用指示薬を使用することができる。
【００２３】
本発明において、このような尿検査用の指示薬を配合するなどのために、廃木材粉砕物の造粒乾燥粒子の表面を白色に着色する場合、指示薬が添加され又は添加されない白色乃至略白色の着色物質を繊維状の廃木材粉砕物に配合することができる。この場合、白色乃至略白色を呈する物質を、上記の白色の顔料及び染料に代えて使用することができる。したがって、例えば上に列記の、例えば、ベントナイト、ゼオライト、炭酸カルシウム及び石膏等の鉱物質の白色物質、並びに小麦粉及びＣＭＣ等の白色物質を、繊維状の廃木材粉砕物粒子の表面を白色にする着色物質として、使用することができる。
尿ｐＨ指示薬の場合は、使用される着色物質はｐＨに影響を与えないものとされる。例えば、チタン白等を使用することができる。
【００２４】
また、本発明において、繊維状の廃木材粉砕物の造粒乾燥物は、それ自体脱臭能を有していないので、動物が排泄した尿等が分解して汚臭となるのを極力避けるために、本発明の動物の排泄物処理材には、補助脱臭剤として、１０重量％以下の量で、吸着能を有するコーヒー液抽出残渣、ベントナイト又はゼオライト
本発明においては、繊維状の廃木材粉砕物と共に、動物の排泄物処理材の主たる成分として、１０重量％以下の量で使用することができる。
本発明において、使用時の排泄物処理材の粉化を避けるために、繊維化された廃木材粉砕物に、接着機能を有する物質を配合するのが好ましい。
【００２５】
本発明において、排泄物処理材は、原料の繊維状の廃木材粉砕物及び高吸水性樹脂の微細な粉塵の存在を極力避けるために、１ｍｍ以上の粒度（例えば、１ｍｍ篩上）の造粒物に造粒されるのが好ましいが、２ｍｍ以上の粒度の粒子に造粒すると、例えば動物のトイレ用の箱から室内に散り難くなり、仮令散ったとしても、粒子を拾い集めるのが容易であり、室内の衛生を保つ上で好ましい。しかし、これらの場合、１ｍｍ以下の粒度の粒子の存在や、２ｍｍ以下の粒度の粒子の存在を完全に排斥するものではない。造粒物は、球状、柱状、粒状、顆粒状等各種形状に形成することができる。
【００２６】
本発明において、廃木材粉砕物と高吸水性樹脂の混合物は、造粒装置により造粒される。造粒装置としては、従来周知の、押出し造粒装置を使用することができる。しかし、この他に、パン型、ドラム型、流動層型及び錠剤成形機などの各種造粒装置を使用することができる。これらの造粒装置において、造粒成形された造粒物の表面への白色粉末等の着色物質の付着は、造粒物が形成されたところで、造粒物表面に、例えば白色粉末を直接接触させて付着させたり、又は白色粉末を溶液又は懸濁液にして、噴霧等により付着させることによって行うことができる。
【００２７】
本発明において、界面活性剤は、廃木材の表面を覆うプラスチック被膜の濡れを良くして、廃木材粉砕物の造粒物の水の吸水速度を大きくするために、塗布されるものであり、陽イオン界面活性剤、非イオンか界面活性剤、陰イオン界面活性剤又は両性イオン界面活性剤を使用することができる。
陰イオン界面活性剤としては、例えば、ドデシルベンゼンスルホン酸、スルホこはく酸型陰イオン界面活性剤などがあり、非イオン界面活性剤としては、オクチルフェニルエーテル、ポリオキシエチレン誘導体などがあり、陽イオン界面活性剤としては、ラウリルトリメチルアンモニウムクロライド、ステアリルトリメチルアンモニウムクロライド、ココナットアミンアセテートなどがある。
【００２８】
本発明においては、繊維化された廃木材粉砕物、高吸水性樹脂及び水の混合物が造粒されるが、この造粒過程で、又は造粒後に、更に繊維状の廃木材粉砕物の造粒粒子を粒子として安定させるために、接着能、吸水能を有する高吸水性繊維、高吸水性樹脂、殺菌作用を有する物質等を、前記造粒粒子の上にまぶすなどして、造粒粒子の表面にこれら吸着機能又は殺菌作用を有する物質を付着させ、その後乾燥することにより、吸着機能及び／又は殺菌機能を有する付着物質が、造粒粒子の表面から容易に剥落しないようにするのが好ましい。このような吸着機能及び殺菌機能を有する物質としては、カテキン、パンシル及びスメルナーク（商品名）がある。本発明において、被覆用混合物に使用される廃木材粉砕物は、例えば、篩を通して、０．５ｍｍ以下の粒度、好ましくは、０．１ｍｍ以下の粒度の微細な粉砕物とされるのが好ましい。このように微細な粉砕物を被覆用混合物として使用すると、使用時に尿により一部洗い流されて流失して、芯部の色調を外部から見えるようにすることができ、使用された箇所が外から容易に知ることができる。
【００２９】
【作用】
本発明において、動物の排泄物処理材は、５ｍｍ以下の粒度の繊維状の廃木材粒子を主として含有する廃木材粉砕物及び前記廃木材粉砕物より少ない量の接着剤を含む混合物により形成されている粒状物であるので、廃木材粉砕物を繊維化することにより得られた繊維状の廃木材粉砕物を、接着剤及び水と混合して簡単に造粒することができ、高吸水性樹脂を多量に使用しないで造粒することができる。また、繊維化された廃木材粉砕物を含む造粒物表面を着色物質で着色する場合には、廃木材粉砕物の特有の色を隠すことができ、着色物質を選ぶことにより、排泄物処理材を、例えば使用される室内の調度との調和、衛生感、使用者の好み及び色彩雰囲気等に応じた色調に着色することが可能となり、動物の排泄物処理材を多色化させることができる。
本発明において、動物の排泄物処理材は、廃木材粉砕物を含む造粒物表面が、廃木材粉砕物及び接着剤を含む接着性混合物で被覆することができるので、排泄物処理材中に排泄された排泄物は、排泄物処理材を上から掛けるなどして簡単に包まれるので、排泄物の汚臭等は、排泄物処理材に吸着されて周囲に放散されることはない。
【００３０】
しかも、本発明において、解繊された木粉は、それ自体、吸水性及び保水性を有するが、それに吸水性及び／又は脱臭性を有する物質を配合して、吸水性及び脱臭性を付与することができ、動物の排泄物処理材として使用して、動物の排泄した尿の吸収性及び消臭性が良好である。
さらに、本発明の排泄物処理材は、特に白色物質で着色できるので、尿検査用指示薬を配合しても、その発色を際立たせることができ、動物の排泄した尿の色を検査して、動物の健康状態を監視することが容易となる。
【００３１】
本発明において、ポリアクリルアミド、α−澱粉、ポバール及び／又は小麦粉等の糊剤は、被覆層の１０重量％以下の量で、廃木材粉砕物５５重量％以上の量及び高吸水性樹脂３５重量％以下の量の混合物に混合される。この場合には、動物の排泄物に付着して、排泄物処理材粒子相互が付着して、排泄物を包み込んで塊状となり、塊状の部分のみを取り出すことにより動物の排泄物の後始末ができ、後始末が簡単かつ容易である。また、動物の排泄処理材中に補助脱臭剤及び／又は高吸水性樹脂が混合されている場合には、排泄物処理材として更に優れた脱臭性並びに吸水性及び保水性を発揮する。
本発明は、従来、廃物とされて、その処理が問題とされていた建築現場で使用された廃木材や製材所から発生する廃木材を、動物の排泄物処理材として有効に利用するので、廃棄処理が容易である。
【００３２】
本発明の動物の排泄物処理材は、産業廃棄物の繊維化された廃木材粉砕物を主として含有し、１ｍｍ以上、好ましくは、３ｍｍ以上の粒径の造粒物に、吸水性及び／又は脱臭性の物質と共に成形されるので、動物の尿について吸収性が良く、また保水性が良く、しかも、木粉は木の香りを周囲に与えるので、消臭性が良好である。
また、本発明の排泄物処理材には、例えば、高吸水性樹脂、又は小麦粉、ポバール、α−澱粉若しくはその他接着能を有する配合物質、又は殺菌作用を有する物質或はこれら配合物質の二以上のものを混合して配合できるので、動物の排泄物に付着して、排泄物を包み込んで塊状にすることができ、後始末が簡単かつ容易である。また、脱臭剤及び／又は吸水剤が混合されている場合には、排泄物処理材として更に優れた脱臭性及び吸水性を発揮する。さらにまた、殺菌作用を有する物質が混合されている場合には、排泄物処理材は、黴などの発生がなく長期間に亙って保存することができる
【００３３】
【実施例】
以下、本発明の実施の態様の例を説明するが、本発明は、以下の説明及び例示によって何等制限されるものではない。
図１は、本発明の一実施例を本例に使用される廃木材粉砕物を造粒して排泄物処理材とする装置の一例を示す概念図である。
図１において、建築現場から集められ、１０ｃｍの大きさに裁断されいる各種廃木材が使用された。本例において、廃木材は、柱、梁、貫き等の木の廃材を破砕機１で破砕して、５０乃至１００ｍｍの径の塊状物に破砕する。破砕機１で破砕された廃木材の塊状物は、磁選機２に送られる。磁選機２では、比較的大きな鉄片及び該鉄片を有する廃木材の塊状物が、磁石に吸い付けられて除去され、比較的大きな鉄片及び該鉄片を有する廃木材の塊状物が除去された廃木材の塊状物は粗粉砕機３に送られる。粗粉砕機３で、５０乃至１００ｍｍの大きさの廃木材の塊状物は、５乃至３０ｍｍの大きさの廃木材片に粗粉砕され、５乃至３ｍｍの大きさに粗粉砕された廃木材片は、磁選機４に送られる。磁選機４では、比較的小さい鉄片及び小さな鉄片を有する廃木材片が、磁石に吸い付けられて除去される。小さい鉄片及び小さな鉄片を有する廃木材片が除去された廃木材片は、解繊機５に送られて、解繊されながら３乃至５ｍｍの粒度の繊維状の廃木材粒子を含む廃木材粒子に粉砕される。解繊されて３乃至５ｍｍの粒度の繊維状の廃木材粒子を含む廃木材粉砕物は、第一ホッパー６に集められる。第一ホッパー６に集められた３乃至５ｍｍの粒度の繊維状の廃木材粒子を含む廃木材粉砕物は、二分されて、一方の３乃至５ｍｍの粒度の繊維状の廃木材粒子を含む粉砕物は、押出し造粒機７に搬送する第一スクリューフィーダー８に供給される。第一スクリューフィーダー８には、押出し造粒機７に至る間に、高吸水性樹脂供給ホッパー９に接続する高吸水性樹脂供給部１０及び水供給タンク１１に接続する水供給部１２が設けられている。高吸水性樹脂供給部１０では、前記繊維状の廃木材粒子を含む粉砕物に高吸水性樹脂が供給され、混合される。水供給部１２では、高吸水性樹脂が供給された繊維状の廃木材粒子を含む粉砕物に水が供給され混合され、造粒物用混合物が形成される。本例において、造粒物用混合物は、廃木材粒子が７０乃至９５重量部であり、高吸水性樹脂が５乃至３０重量部である。本例において、押出し造粒機７は、３ｍｍの孔径を有する２５ｍｍ厚さのダイスを備えており、造粒物用混合物は、押出し造粒機７において、３ｍｍ以上の粒径で長さ５ｍｍ以上の円柱形状の廃木材造粒物に造粒される。押出し造粒機７のダイスの孔径は、造粒物粒子の径に対応して選択される。３ｍｍ以上の粒径で長さ５ｍｍ以上の円柱形状の廃木材造粒物は、円形の篩機１３に送られて、２ｍｍの目の開きを有する篩により、２ｍｍ以下の粒度の廃木材造粒物の粉状物が篩分けられて分離される。
【００３４】
ホッパー６に集められた３乃至５ｍｍの粒度の繊維状の廃木材粒子を含む廃木材粉砕物の、二分された、もう一方の３乃至５ｍｍの粒度の繊維状の廃木材粒子を含む廃木材粉砕物は、第二スクリューフィーダー１４により一次微粉砕解繊機１５に送られて０．５乃至１ｍｍの粒度の繊維状の廃木材粒子を含む粉砕物に解繊され、続いて二次微粉砕解繊機１６に送られて、０．３５ｍｍの粒度の繊維状の廃木材粒子を含む廃木材粉砕物に解繊される。０．１乃至０．５ｍｍの粒度に解繊された繊維状の廃木材粒子を含む廃木材粉砕物は、第二ホッパー１７に集められる。第二ホッパー１７に集められた、０．１乃至０．５ｍｍの粒度に解繊された繊維状の廃木材粒子を含む粉砕物は、被覆用高吸水性樹脂供給ホッパー１８及び被覆用ポリアクリルアミド供給ホッパー１９に接続する第三スクリューフィーダー２０が接続する混合機２１に送られる。該混合機２１において、０．１乃至０．５ｍｍの粒度で５５重量部以上の量の繊維状の廃木材粒子を含む粉砕物は、被覆用高吸水性樹脂供給ホッパー１８からの３５重量部以下の量の被覆用高吸水性樹脂及び被覆用ポリアクリルアミド供給ホッパー１９からの１０重量部以下の被覆用ポリアクリルアミドと混合されて、被覆用混合物が形成される。本例において、被覆用混合物は、廃木材粉砕物の５５重量％以上、被覆用高吸水性樹脂の３５重量％以上及び被覆用アクリルアミドの１０重量％以下の混合物である。円形篩機１３の篩上部は、搬送路２２により被覆装置２３に接続し、また前記混合機２１は、前記被覆装置２３の上方に位置して、被覆装置２３に、前記被覆用混合物を散布できるように設けられており、粒度２ｍｍ以上の粒度の廃木材造粒物は、搬送路２２から被覆装置２３に供給され、そこで、被覆用混合物が散布され、廃木材造粒物の上に前記被覆用混合物により被覆される。本例において、被覆された造粒物は、廃木材造粒物が８０乃至９５重量％であり、被覆用混合物が５乃至２０重量％である。
【００３５】
被覆装置２３の出口は、円形篩機２４に接続しており、被覆用混合物により被覆された、排泄物処理材用の造粒物は、被覆装置２３から円形篩機２４に供給されて粒度２ｍｍ以下の造粒物が篩分けされて分離される。円形篩機２４の出口は、乾燥機２５に接続するベルトコンベヤ２６に接続しており、粒度２ｍｍ以上の排泄物処理材用の造粒物は、ベルトコンベヤ２６により乾燥機２５に送られ、水分が５重量％以下になるまで乾燥される。乾燥機２５の出口は、製品ホッパー２７に接続するベルトコンベヤ２８に接続しており、製品ホッパー２７の出口は、篩機２９に接続するベルトコンベヤ３０に接続する。乾燥機２５で水分が５重量％以下に乾燥された排泄物処理材用の造粒物は、ベルトコンベヤ２８を介して製品ホッパー２７に集められ、ベルトコンベヤ３０を介して篩機２９に送られ、そこで、粒度２ｍｍ以下の排泄物処理材用の造粒物が篩分けされて分離される。篩機２９の出口はベルトコンベヤ３１を介して自動包装機３２に接続している。篩機２９により篩分けされた、粒度２ｍｍ以上の篩上粒子の排泄物処理材用の造粒物は、ベルトコンベヤ３１から、自動包装機３２に送られて、包装され出荷される。
【００３６】
例１．
建築現場から集められ、破砕機で５０〜１００ｍｍの粒度に破砕され、粗砕機で５〜３０ｍｍ粒度に粉砕されたたヒバ系廃木材を、解繊機により、３．５ｍｍ以下の粒度に粉砕し、繊維化した。この繊維化されたヒバ系廃木材粉砕物を、第一ホッパー６に入れ、その中の８ｋｇを第一スクリューフィーダー８に供給し、高吸水性樹脂供給部１０で高吸水性樹脂２ｋｇを混合し、水供給部１２で水２リットルを混合して形成された造粒用混合物を、第一スクリューフィーダー８から、押出し造粒機７に送り、押出し造粒する。押出し造粒された繊維化された廃木材粉砕物は円形篩機１３で２ｍｍ以下の粒度の造粒物が篩分けられた。円形篩機１３の篩上は、少量の水が噴霧されて、被覆装置２３に送られた。
他方、３．５ｍｍ以下の粒度の繊維化されたヒバ系廃木材粉砕物の中の１．５ｋｇを第一ホッパー６から、一次微粉砕解繊機１５に供給し０．５ｍｍ以下の粒度に解繊し、次いで二次微粉砕解繊機１６で０．３５ｍｍ以下の粒度に解繊した。０．３５ｍｍ以下の粒度に解繊された廃木材粉砕物を第二ホッパー１７に集め、混合機２１に供給した。一方、高吸水性樹脂７００ｇを被覆用高吸水性樹脂供給ホッパー１８からスクリューフィーダー２０に供給すると共に、ポリアクリルアミド２００ｇを被覆用ポリアクリルアミド供給ホッパー１９から、前記スクリューフィーダー２０に供給し、前記混合機２１に供給し、繊維化された廃木材粉砕物と混合した。
繊維化された廃木材粉砕物、被覆用高吸水性樹脂及び被覆用ポリアクリルアミドの被覆用混合物は、被覆装置２３に送られて、繊維化された廃木材粉砕物の造粒物の上に散布された。本例においては、この被覆作業は数段に分けて行われた。被覆工程を終えた被覆造粒物は、円形篩機２４で２ｍｍ以下の粒度の被覆造粒物を除去した。円形篩機２４の篩上は、乾燥機２５に送られて乾燥され、篩分けられ、猫のトイレ砂として製品化された。
【００３７】
室内において、このように製造された猫のトイレ用の砂１００ｇに、３８℃の温度の疑似尿３０ミリリットルを加えたが、非常に吸水性及び脱臭性が良好であり、アンモニア臭が消臭された後、木の香りが認められた。本実施例において、疑似尿は、食塩１０ｇ、アンモニア水（ＮＨ3９．５〜１０．５重量％）１０ミリリットルを水１リットルに溶解することにより調製した。
この猫のトイレ用の砂は、猫のトイレに厚さ１０ｃｍの厚さに敷いて使用されたが、猫は普段と同様にトイレとして使用しており、使用の上で何等支障がなかった。
本例のトイレ用の砂は、排泄物の周囲に容易に付着して、排泄物の取り出しを容易にする。しかも本例のトイレ用の砂は、使用後、木の香りを漂わせるので、脱臭性が優れる上に、消臭性も優れるので、屋内に不快な臭いを発生するのを避けることができた。
本例において、建築現場から集められたヒバ系木材の廃木材粉砕物を使用しているが、これ以外の異なった種類の木材の各種木粉を使用しても同様の結果を得ることができる。
【００３８】
例２．
建築現場から集められ、破砕機で５０〜１００ｍｍの粒度に破砕され、粗砕機で５〜３０ｍｍ粒度に粉砕されたた杉材の廃木材を、解繊機により、３．５ｍｍ以下の粒度に粉砕し、繊維化した。この解繊機により繊維化された杉材の廃木材粉砕物を、第一ホッパー６に入れ、その中の９．５ｋｇを第一スクリューフィーダー８に供給した。高吸水性樹脂供給部１０で高吸水性樹脂（アロンザップ：東亜合成株式会社製、商品名）０．５ｋｇを混合し、この混合物に水供給部１２で水１．４リットルを混合して形成された造粒用混合物（含水率１２％）を、第一スクリューフィーダー８から、３ｍｍの孔を有するダイスを備える押出し造粒機７に送り、３ｍｍ径の粒状物に押出し造粒する。押出し造粒された廃木材粉砕物の造粒物は、円形篩機１３に送られて、３ｍｍ以下の粒度の造粒物を篩分けにより分離する。円形篩機１３の篩上の粒子には、少量の水が噴霧されて、被覆装置２３に送られた。
他方、３ｍｍ以下の粒度の繊維化された杉材の廃木材粉砕物の中の１．５ｋｇを第一ホッパー６から、一次微粉砕解繊機１５に送って、１ｍｍ以下の粒度に解繊し、次いで二次微粉砕解繊機１６に送って、０．３５ｍｍ以下の粒度に解繊し、被覆用廃木材粉砕物とした。一方、０．３５ｍｍ以下の粒度の解繊された廃木材粉砕物を第二ホッパー１７に集め、その５５重量部を混合機２１に供給した。一方、高吸水性樹脂としては、ハイモ株式会社製の２５μｍ以下の粒度を有するものを使用し、その４０重量部を被覆用高吸水性樹脂供給ホッパー１８からスクリューフィーダー２０を経て混合機２１に供給した。また、ポリアクリルアミドは、三菱化学株式会社製であり、２５μｍ以下の粒度を有しており、その５重量部を、被覆用ポリアクリルアミド供給ホッパー１９から、前記スクリューフィーダー２０を経て混合機２１に供給した。前記混合機２１に供給された被覆用高吸水性樹脂、被覆用ポリアクリルアミド及び繊維化された被覆用廃木材粉砕物は、混合機２１で混合された。
繊維化された被覆用廃木材粉砕物、被覆用高吸水性樹脂及び被覆用ポリアクリルアミドの被覆用混合物は、前記造粒物１００重量部に対し１６重量部の割合で、被覆装置２３に送られて、廃木材粉砕物の造粒物の上に散布された。本例においては、この被覆作業は数段に分けて行われた。被覆工程を終えた被覆造粒物は、円形篩機２４で、２ｍｍ以下の粒度の被覆造粒物を除去した。円形篩機２４の篩上は、乾燥機２５に送られて乾燥され、篩分けられ、猫のトイレ砂として製品化された。
室内において、このように製造された猫のトイレ用の砂を猫のトイレに厚さ１０ｃｍに敷いて使用した。この猫のトイレ用の砂に、３８℃の温度の疑似尿３０ミリリットルを注入したが、非常に吸水性及び脱臭性が良好であり、アンモニア臭は消臭され、ほとんど感知されなかつた。猫は従来の砂と同様に使用し、屋内での使用においても臭いの点で何の問題もなく、排尿部分は塊状を呈し、排泄物の取出しも容易である。
【００３９】
例３．
建築現場から集められ、破砕機で５０〜１００ｍｍの粒度に破砕され、粗砕機で５〜３０ｍｍ粒度に粉砕されたた杉材の廃木材を、解繊機により、３．５ｍｍ以下の粒度に粉砕し、繊維化した。この解繊機により繊維化された杉材の廃木材粉砕物を、第一ホッパー６に入れ、その中の９．５ｋｇを第一スクリューフィーダー８に供給した。
本例においては、接着剤として高吸水性樹脂に代えてポリアクリルアミド（三菱化学株式会社製）が使用され、ホッパー９に入れられた。
ポリアクリルアミド０．５ｋｇが、第一スクリューフィーダ８により送られてくる繊維化された杉材の廃木材粉砕物に、ホッパー９から供給部１０で混合された。この混合物に水供給部１２で水１．４リットルを混合して形成された造粒用混合物（含水率１２％）を、第一スクリューフィーダー８から、３ｍｍの孔を有するダイスを備える押出し造粒機７に送り、３ｍｍ径の粒状物に押出し造粒する。押出し造粒された廃木材粉砕物の造粒物は、円形篩機１３に送られて、３ｍｍ以下の粒度の造粒物を篩分けにより分離する。円形篩機１３の篩上の造粒物粒子には、少量の水が噴霧されて、被覆装置２３に送られた。
他方、３ｍｍ以下の粒度の繊維化された杉材の廃木材粉砕物の中の１．５ｋｇを第一ホッパー６から、一次微粉砕解繊機１５に送って、１ｍｍ以下の粒度に解繊し、次いで二次微粉砕解繊機１６に送って、０．３５ｍｍ以下の粒度に解繊し、被覆用廃木材粉砕物とした。一方、０．３５ｍｍ以下の粒度の解繊された廃木材粉砕物を第二ホッパー１７に集め、その５５重量部を混合機２１に供給した。一方、高吸水性樹脂としては、ハイモ株式会社製の２５μｍ以下の平均粒度を有するものを使用し、その２７重量部を被覆用高吸水性樹脂供給ホッパー１８からスクリューフィーダー２０を経て混合機２１に供給した。また、ポリアクリルアミド（三菱化学株式会社製）は、２５μｍ以下の平均粒度を有しており、その１８重量部を、被覆用ポリアクリルアミド供給ホッパー１９から、前記スクリューフィーダー２０を経て混合機２１に供給した。前記混合機２１に供給された被覆用高吸水性樹脂、被覆用ポリアクリルアミド及び繊維化された被覆用廃木材粉砕物を含む被覆用混合物は混合された。
繊維化された被覆用廃木材粉砕物、被覆用高吸水性樹脂及び被覆用ポリアクリルアミドの被覆用混合物は、造粒物１００重量部に対し１５重量部の割合で、被覆装置２３に送られて、廃木材粉砕物の造粒物の上に散布された。本例においては、この被覆作業は数段階に分けて行われた。被覆工程を終えた被覆造粒物は、円形篩機２４で、２ｍｍ以下の粒度の被覆造粒物を除去した。円形篩機２４の篩上は、乾燥機２５に送られて乾燥され、篩分けられ、猫のトイレ砂として製品化された。
室内において、このように製造された猫のトイレ用の砂を猫のトイレに厚さ１０ｃｍに敷いて使用した。この猫のトイレ用の砂に、３８℃の温度の疑似尿３０ミリリットルを注入したが、非常に吸水性及び脱臭性が良好であり、アンモニア臭は消臭され、ほとんど感知されなかつた。猫は従来の砂と同様に使用し、屋内での使用においても臭いの点で何の問題もなく、排尿部分は塊状を呈し、排泄物の取出しも容易である。
例４．
建築現場から集められ、破砕機で５０〜１００ｍｍの粒度に破砕され、粗砕機で５〜３０ｍｍ粒度に粉砕されたた栂材の廃木材を、解繊機により、３ｍｍ以下の粒度に粉砕し、繊維化した。この解繊機により繊維化された栂材の廃木材粉砕物の７０重量部に、粒度２５μｍの高吸水性樹脂（商品名Ｈｓ１１００：ハイモ株式会社製）５重量部と粒度１５０μｍの高吸水性樹脂（商品名Ｈｓ１１００：ハイモ株式会社製）５０重量部の高吸水性樹脂混合物２５重量部を混合し、この混合物に、平均粒度２５μｍのアクリルアミド（三菱化学株式会社製）５重量部を混合し、この混合物に、１１．１重量部の水を混合して形成された造粒用混合物（含水率１０％）を製造した。この造粒用混合物を、５ｍｍの孔を有するダイスを備える押出し造粒機により押出し造粒して、直径５ｍｍ、長さ１０ｍｍ以下の柱状の造粒物を製造した。
このように製造された猫のトイレ用の砂を、室内の猫のトイレに厚さ１０ｃｍに敷いて使用した。この猫のトイレ用の砂に、３８℃の温度の疑似尿３０ミリリットルを注入したが、非常に吸水性及び脱臭性が良好であり、アンモニア臭は消臭され、ほとんど感知されなかつた。猫は従来の砂と同様に使用し、屋内での使用においても臭いの点で何の問題もなく、排尿部分は塊状を呈し、排泄物の取出しも容易である。
例５．
建築現場から集められ、破砕機で５０〜１００ｍｍの粒度に破砕され、粗砕機で５〜３０ｍｍ粒度に粉砕されたた栂材の廃木材を、解繊機により、３ｍｍ以下の粒度に粉砕し、繊維化した。この解繊機により繊維化された栂材の廃木材粉砕物の９２重量部に、平均粒度２５μｍの高吸水性樹脂（商品名Ｈｓ１１００：ハイモ株式会社製）５重量部と平均粒度１５０μｍの高吸水性樹脂（商品名Ｈｓ１１００：ハイモ株式会社製）５０重量部の高吸水性樹脂混合物４重量部を混合し、この混合物に、平均粒度２５μｍのアクリルアミド（三菱化学株式会社製）４重量部を混合し、この混合物に、１１．１重量部の水を混合して形成された造粒用混合物（含水率１０％）を製造した。この造粒用混合物を、５ｍｍの孔を有するダイスを備える押出し造粒機により押出し造粒して、直径５ｍｍ、長さ１０ｍｍ以下の柱状の造粒物を製造した。
このように製造された猫のトイレ用の砂を、室内の猫のトイレに厚さ１０ｃｍに敷いて使用した。この猫のトイレ用の砂に、３８℃の温度の疑似尿３０ミリリットルを注入したが、非常に吸水性及び脱臭性が良好であり、アンモニア臭は消臭され、ほとんど感知されなかつた。猫は従来の砂と同様に使用し、屋内での使用においても臭いの点で何の問題もなく、排尿部分は塊状を呈し、排泄物の取出しも容易である。
本例においては、ヒバ材、杉材及び栂材の廃木材の粉砕物を使用しているが、これ以外の異なった種類の木材の各種木粉を使用しても同様の結果を得ることができる。
【００４０】
【発明の効果】
本発明において、動物の排泄物処理材は、５ｍｍ以下の粒度の繊維状の廃木材粒子を主として含有する廃木材粉砕物及び該廃木材粉砕物に比して小量の高吸水性樹脂を含む混合物により形成されている粒状物であるので、柔らかい木粉の色を呈し、またそれ以外の色に着色することが容易であるので、従来の動物の排泄物処理材に比して、使用場所の色調に合わせて、種々の色調、即ち適宜の色彩の排泄物処理材を選ぶことが可能となり、衛生的な雰囲気はもとより、室内の色彩の調和を保つことができる。
しかも廃木材粉砕物は、固有の香りを有するので、例えば室内に放置して、トイレ特有の臭いを消して、室内の環境を改善する。またそれ自体保水性を有するので、従来の動物の排泄物処理材に比して、検尿用指示薬の使用が容易となり、動物の健康状態を把握することが容易となる。
本発明は、従来、建築現場から発生し、廃物とされていた廃木材を、繊維化された粒子とするので、紙パルプや紙製品などを使用しないで高吸水性樹脂のみで、造粒物とするものであり、低廉に動物の排泄物処理材として有効に利用することができ、しかも、主として可燃物で構成するので、廃棄処理が容易である。 しかも、本発明は、繊維化された廃木材粉砕物の乾燥造粒物を適宜着色させて、動物の排泄物処理材とできるので、室内の調度に合わせた、又は好みに合わせた色調の動物排泄物処理材とすることができる。
以上のように、本発明は、従来の動物の廃棄物処理材に比して、建築現場から発生する産業廃棄物の廃木材の廃棄に係る問題点と、従来の使用済みの動物の排泄物処理材の非可燃性に係る廃棄処理に係る問題点を一挙に解決するものであり、資源の有効利用及び環境廃棄物の処理の軽減等の点で有意義なものである。
【図面の簡単な説明】
【図１】本発明の一実施例を本例に使用される廃木材粉砕物を造粒して排泄物処理材とする装置の一例を示す概念図である。
【符号の説明】
１ 破砕機
２、４ 磁選機
３ 粗粉砕機
５ 解選機
６ 第一ホッパー
７ 押出し造粒機
８ 第一スクリューフィーダー
９ 高吸水性樹脂供給ホッパー、アクリルアミド供給ホッパー
１０ 高吸水性樹脂供給部、アクリルアミド供給部
１１ 水供給ホッパー
１２ 水供給部
１３ 円形の篩機
１４ 第二スクリューフイーダー
１５ 一次微粉砕解繊機
１６ 二次微粉砕解繊機
１７ 第二ホッパー
１８ 被覆用高吸水性樹脂供給ホッパー
１９ 被覆用ポリアクリルアミド供給ホッパー
２０ 第三エクリューフィーダー
２１ 混合機
２２ 搬送路
２３ 被覆装置
２４ 円形篩機
２５ 乾燥機
２６、２８、３０、３１ ベルトコンベヤ
２７ 製品ホッパー
２９ 篩機
３２ 自動包装機[0001]
[Industrial application fields]
The present invention relates to a granular excrement disposal material for animals such as cats, canines, and other pet animals, and a method for producing the same, and more particularly, to effectively use waste wood already used at construction sites. Further, the present invention relates to a granular excrement disposal material for animals such as cats, canines, and other pet animals, and a method for producing the same.
[0002]
[Prior art]
Sand, bentonite, zeolite, pulp for papermaking, pulp sludge and the like are used in the form of small blocks for excrement disposal materials for animals such as livestock and pets, especially for indoor excrement disposal materials.
This kind of pet animal excrement disposal material is desired to be clean and hygienic because it is used indoors, for example, and is easy to be disposed of after use because of its cleanliness and hygiene. Is desired. However, in the case of inorganic substances such as sand, zeolite, bentonite, etc., they are crushed and become dusty during use. Cannot be drained into sewage. Therefore, although the deodorizing effect is low and the price is high, the water-absorbing ability is excellent, and since it is a flammable material, a paper-making pulp and a small-sized molded product of paper powder are used.
[0003]
[Problems to be solved by the invention]
Waste wood is generated in a considerable amount from the construction industry and other wood industries, and the amount is enormous. Most of it is discarded as industrial waste, and most of it is incinerated. This is one of the challenges of the construction industry and other timber industries.
Conventionally, pulverized waste wood is difficult to granulate with its straw, so it is mixed with paper powder or paper pulp and super absorbent resin, and granulated to produce granular animal excrement disposal materials. is doing. However, paper dust and paper pulp are relatively expensive and are low in quantity, and are problematic in treating waste wood.
The object of the present invention is to solve the problems associated with conventional waste wood treatment.
[0004]
[Means for Solving the Problems]
The present inventor made the waste wood fibrous particles obtained by coarsely pulverizing and defibrating waste wood into a paper by mixing with a superabsorbent resin and water and by a granulating means such as extrusion granulation. It discovered that it could granulate easily, without mixing a powder and paper pulp, and came to this invention.
That is, the present invention is a waste wood treatment material for animals that can be produced by granulating a large amount of sawdust generated from a sawmill, waste wood generated from a construction site, etc. without mixing paper powder or paper pulp, and its production. Provide a method.
[0005]
That is, the present invention is a waste wood pulverization mainly containing fibrous waste wood particles having a particle size of 5 mm or less and a length ratio of the major axis of the particles of 4 or more to the
It is in.
[0006]
In addition to these, the present invention By roughly crushing waste wood, The fiber-like waste wood particles having a particle size of 5 mm or less and having a dimensional ratio of the major axis length of the particles to 4 or more with respect to the
[0007]
DETAILED DESCRIPTION OF THE INVENTION
In the animal excrement disposal material of the present invention, the adhesive is less than 10% by weight based on one or more superabsorbent resins and particulates having a content of less than 5% by weight relative to the particulates. It is preferable that the content is one or more pastes. However, it can be one or more pastes having a content of 5% by weight or less or a combination thereof with respect to one or more superabsorbent resins or granules having a content of less than 5% by weight. When the adhesive is a highly water-absorbing resin, it is preferably one or more highly water-absorbing resins having a content of 30% by weight or less based on the granular material, but 5% by weight based on the granular material. One or more superabsorbent resins with a content of less than a percent can be obtained.
[0008]
Moreover, when using a highly water absorbent resin as an adhesive agent, it is preferable that the highly water absorbent resin has a particle size of 30 μm or less. However, it can have a particle size of 20 μm or less. In the animal excrement disposal material of the present invention, as the paste, polyacrylamide, α-starch, polyvinyl alcohol, starch, wheat flour or carboxymethylcellulose, or a combination of two or more of these can be used.
[0009]
In the animal excrement disposal material of the present invention, in order to increase the water absorption rate of the granulated product, surface activity such as a cationic surfactant, an anionic surfactant, a neutral ionic surfactant and a nonionic surfactant is used. Agents can be used. If the waste wood is a water repellent material such as pine, the use of surfactants can wet the water repellent material, increase the water absorption and water retention of the waste wood ground product, and In the animal excrement disposal material of the invention, the fibrous waste wood pulverized material used has a water absorption performance and a water retention performance that are large when the particle size is 5 mm or less, preferably 3 mm or less, more preferably 2 mm or less. Since granulation becomes easy, it is preferable.
The particle size of the animal excrement disposal material according to the present invention is preferably 2 mm or more because the amount of powder is reduced, but is preferably 6 mm or less.
[0010]
The animal excrement disposal material of the present invention can be formed of a core part and a covering layer part covering the core part. In this case, the coating layer portion is formed to have adhesive properties such that wet particles adhere to each other and form a lump shape, and the core portion absorbs water so that excrement such as absorbed urine can be retained. It is formed to have properties and water retention. The core portion is 75 to 95 percent by weight of the excrement disposal material particles, and the coating layer portion is 5 to 25 percent by weight. It is preferable to achieve the adhesion performance.
In the animal excrement disposal material consisting of two layers of the core part and the covering layer part of the present invention, as in the animal excrement disposal material consisting of a single granulated product, the adhesive is one or more superabsorbents. Resin, one or more types of glue, or a combination thereof. In the core part of the animal excrement disposal material of the present invention, the adhesive contains, for example, one or more superabsorbent resins contained at a content of less than 5 weight percent and 10 so that granulation can be easily performed. The adhesive in the core may be one or more superabsorbent resins or 5% by weight contained at a content of less than 5% by weight. One or more kinds of pastes contained in a percentage or less content or a combination thereof can be used. When the superabsorbent resin is used alone as the adhesive in the core, the superabsorbent resin can be contained at a content of 30 weight percent or less. When the superabsorbent resin and the paste are used together as an adhesive, they can be blended separately or in advance with the defibrated wood flour.
[0011]
In the animal excrement disposal material of the present invention, the adhesive in the covering layer portion may be one or more superabsorbent resins contained at a content of 35 weight percent or less. In the coating layer part, the adhesive shall be one or more superabsorbent resins contained at a content of less than 5 weight percent, a paste contained at a content of 5 weight percent or less, or a combination thereof. Can do. In the present invention, the superabsorbent resin preferably has a particle size of 30 μm or less, but more preferably has a particle size of 20 μm or less.
In the present invention, the adhesive used for the core and / or the coating layer is the same as the adhesive used for the granulated product, that is, one or more superabsorbent resins and / or adhesives. be able to. In the present invention, the sizing agent is similarly polyacrylamide, α-starch, polyvinyl alcohol, carboxymethyl cellulose, or a combination of two or more thereof.
In this invention, as a compounding substance used for a core part and / or a coating layer part, it is a 1 or more types of coloring substance, a 1 or more types of substance which has bactericidal action, or these combination. In the present invention, it is preferable to add a surfactant to the core portion, the coating layer portion, or both, because the water absorption performance can be increased. The surfactant is the same as that of the granulated product alone, and a surfactant such as a cationic surfactant, an anionic surfactant, a neutral ionic surfactant and a nonionic surfactant may be used. it can. In the case of a cationic surfactant, since it has a bactericidal effect, it can be used as a substance having a bactericidal action.
[0012]
In the present invention, the waste wood pulverized product in the core is mainly a waste wood pulverized product containing fibrous waste wood particles having a particle size of 2 to 5 mm. In the present invention, the waste wood pulverized product of the core mainly contains fibrous waste wood particles having a particle size of 5 mm or less, preferably 3 mm or less, and more preferably 2 mm or less. In the coating layer portion, the pulverized waste wood pulverized product can be easily coated by making it finer to a particle size of 0.5 mm or less, for example, a fibrous material having a particle size of 0.1 mm or less. A fiberized waste wood pulverized product mainly containing waste wood particles is preferable. Since fine fine particles are easy to peel off during storage, the pulverized waste wood pulverized material of the coating layer portion has a particle size of 0.1 to 0.5 mm, preferably waste containing fibrous waste wood particles. It is preferable to use a pulverized wood. In the present invention, the core can have a particle size of 2 mm or more, preferably 3 mm or more. Animal excrement disposal materials can be formed to a particle size of 3 mm or more, and can be formed to a particle size of 6 mm or less.
[0013]
In the present invention, waste wood is pruned branches, bark of wood, used building materials from the construction site of wood, pieces of wood and wood chips and sawdust generated from sawmills, and waste wood such as sawdust has a size of 50 to 300 mm, for example. It is crushed. The crushed waste wood pieces are subjected to electrostatic separation and magnetic separation in order to separate those having metal. Waste wood pieces having a size of 50 to 300 mm from which iron pieces and / or metal pieces have been separated by electrostatic separation and magnetic separation are coarsely pulverized into particles having a size of 5 to 30 mm. The coarsely pulverized waste wood grains are contaminated with a viable amount of metal grains, so the contaminated metal grains are separated by wind sorting (wind folding) or magnetic sorting (magnetic sorting) to separate the metal grains. The waste wood grain thus obtained is fibrillated with a particle size of 3 to 5 mm by a defibrating machine. In the present invention, the pulverized waste wood pulverized product contains fibrous particles, and is superior in water absorption and water retention compared to the waste wood pulverized product that is not fiberized. Here, the fibrous particles have a length of the short axis of the particle, that is, a length of the long axis of the particle with respect to a
[0014]
In the present invention, fibrous particles of waste wood having a particle size of 5 mm or less, a particle size of 3 to 5 mm, and a particle size of 3 mm or less are mixed with a superabsorbent resin and water and extruded and granulated. It is difficult to granulate waste wood pulverized material that is not fiberized, even as a mixture with a superabsorbent resin. In the present invention, the use of superabsorbent resin can be reduced by making wood flour into a fiber. In the present invention, the amount of the superabsorbent resin used may be sufficient to maintain the water absorption capability, water retention capability, and wet granulated particle adhesion capability as a waste treatment material. In order to facilitate adhesion between the granulated particles and fibrous particles, a paste can be used instead of the superabsorbent resin. As such a paste, an adhesive such as polyacrylamide, α-starch, polyvinyl alcohol (PVA), carboxymethyl cellulose (CMC) can be used. In the present invention, it is preferable to use polyacrylamide and α-starch in the form of fibers for adhesion of particles.
[0015]
In the present invention, a mixture obtained by mixing fibrous particles of a pulverized waste wood pulverized product with a superabsorbent resin and water is used for extrusion granulation. In the case of particles of pulverized waste wood that is not fibrillated and is simply pulverized to a particle size of 3 to 5 mm, the content of the fibrous particles is 20% by weight or less, and the mixture is mixed with a superabsorbent resin and water. Then, it is difficult to granulate by extrusion granulation.
In the present invention, in order to form fiberized waste wood particles, the pulverized waste wood particles are fiberized and pulverized by a defibrating machine, for example, a commercially available dry paper piece defibrating machine. The pulverized waste wood having a particle size of 3 to 5 mm, which has been defibrated by a defibrator, contains fibrous particles at a content of 70% by weight or more. Wood powder such as sawdust is preferably defibrated using a defibrator because granulation can be performed smoothly when granulating without mixing paper materials such as paper powder.
In the present invention, the granular excrement disposal material for animals is produced by granulating particles having a particle size of 2 mm or more, for example, 2 mm, 3 mm, 4 mm or 5 mm or more. For example, moisture is 10% or less, preferably Stored in a dry state of 5% or less.
In the present invention, since the granular animal excrement disposal material is dried so that the moisture content is 15% by weight or less, preferably 10% by weight, generation of wrinkles during storage can be prevented. When granulating at a moisture content of 20% by weight or more, it is preferable to dry until the moisture content is 10% by weight or less in the final stage.
[0016]
In the present invention, waste wood generated from a construction site and a sawmill can be any of softwood and hardwood.
In the present invention, waste wood used for animal excrement disposal materials is preferably waste wood containing hinokitiol as a component in order to avoid generation of soot during storage.
Hinokithiol is contained in the wood of the cypress family, and as such wood of the cypress family, for example, Asunaro genus includes Asunaro and Hinokiakisunaro (Hiba). As the wood of the genus Kurobe, there are Kurobe (Nezuko) and Western red cedar, and in the genus Seeda genus there is an incense seeder, and the cypress genus is Taiwan cypress.
[0017]
In the present invention, the excrement disposal material is stored in a dry state in order to give a dry and dry feel to the animal during use and to prevent generation of wrinkles and the like during storage of the excrement disposal material.
In this invention, the granulated material of the waste wood ground material used as the excrement disposal material is made dry and stored. Therefore, in the present invention, the colored fiberized waste wood pulverized granulated product is preferably dried until the water content is 10% by weight or less, more preferably 5% by weight or less. It is considered as a waste disposal material. However, in the case of animal excrement disposal materials used in a relatively humid atmosphere, if a substance having a bactericidal action is blended with the fibrous wood flour and granulated waste wood is granulated for a long time. It is preferable because it can be stored as an animal excrement disposal material while avoiding the occurrence of wrinkles. However, as the fiberized waste wood pulverized product, when using the harvested culm collected hinokitiol as waste wood, hinokitiol remains in the waste wood pulverized product a little, so depending on the residual amount, The use of the substance having the bactericidal action can be reduced or omitted.
[0018]
In the present invention, the surface of the granulated product of the pulverized waste wood pulverized product exhibits the original color of the pulverized waste wood product, and the granulated product can be used as a soot and excrement treatment material, By specially coloring with a coloring substance, the original color of the granulated product of the waste wood pulverized material can be hidden with the coloring substance, and excrement disposal materials of various colors can be obtained. In the present invention, the granulated product of colored wood powder can be used as a soot and excrement treatment material, but in this case, in order to avoid dust, the fine particle size is smaller than 1 mm, for example. It is preferable to separate the powdery part.
[0019]
In the present invention, for the purpose of harmonizing the excrement disposal material with the use atmosphere, the wood powder granulated product is colored with a coloring substance. In the present invention, pigments and dyes can be used as the coloring substance. Such pigments and dyes include, for example, calcium carbonate, titanium oxide, and synthetic pearls as white ones, and blue pigments and dyes include cyanine blue, azo blue, and patent blue, and green pigments and dyes Are cyanine green and emerald green, and yellow pigments and dyes are azo yellow, acid yellow and hansa yellow.
[0020]
In the present invention, the excrement disposal material particles can make it easy to take out the portions that have been in contact with urine by forming the aggregate by the portions that have been in contact with urine adhering to each other. In this case, polyacrylamide and / or α-starch can be blended in the pulverized waste wood fiberized product in addition to the superabsorbent resin to be mixed. However, besides these, it is possible to select a material having an adhesion function that allows powder particles to adhere to each other by touching urine to easily form a lump.
Moreover, in this invention, in order to avoid powdering of the excrement disposal material at the time of use, it is preferable to mix | blend the substance which has an adhesive function with waste wood ground material. Examples of substances having such an adhesive function include water-soluble or water-dispersible materials such as polyvinyl alcohol (PVA), wheat flour, starch, corn starch, carboxymethyl cellulose (CMC), pullulan, and gelatin. Or two or more of these can be mixed and used as a compounding substance. Further, as alcohol-soluble compounding substances, there are hydroxyethyl cellulose (HEC), hydroxypropyl cellulose (HPC), polyvinylpyrrolidone or (PVP), etc., and in this case as well, these are each used alone, Or these 2 or more types can be mixed and used.
[0021]
In the excrement disposal material of the present invention, the superabsorbent resin is blended in order to enhance the water absorption function, the water retention function and the particle adhesion function after use of the animal excrement disposal material, and the amount used is 30. It is preferably less than or equal to weight percent. In the present invention, the mixing ratio of the superabsorbent resin in the animal excrement disposal material is 5 to 30% by weight. However, when the adhesion function is performed by an adhesive, the superabsorbent resin is 5% by weight. It can be less than a percent. In the present invention, the term superabsorbent resin also means a superabsorbent resin that absorbs about 30 times as much water. In the present invention, the use of a water-absorbing resin that cannot be said to be such a highly water-absorbing resin is facilitated by fiberizing the wood flour.
The superabsorbent resin blended in the present invention is generally a resin that can retain its shape even when it absorbs several tens to 2,000 times its own weight of water, for example, vinyl ester and ethylenically unsaturated carboxylic acid. Copolymer saponified product with acid or its derivatives, graft polymer of starch and acrylic acid, cross-linked product of polyacrylic acid, copolymer of vinyl alcohol and acrylic acid, partial hydrolyzate of polyacrylonitrile, cross-linked carboxymethyl cellulose Products, polyethylene glycol cross-linked products, chitosan salts or pullulan gels, etc., and these can be blended into the fiberized waste wood pulverized material alone or as a mixture of two or more.
[0022]
In the present invention, the excrement disposal material can also be used as an excrement indicator. In this case, if the color of the coloring substance and the compounding substance is aligned to, for example, a single white color, it will be easy to confirm the color of the indicator, and an appropriate excrement inspection indicator will be blended to facilitate screening with animal excrement. This is preferable. The urinalysis indicator for animals used in the present invention is a urinalysis indicator for humans, that is, a urine pH indicator, a urine protein indicator, a urine sugar indicator, and a urine hemoglobin, as in the case of conventional urinalysis indicators for animals. Indicators and other indicators for human urinalysis can be used.
[0023]
In the present invention, when the surface of the granulated dry particles of the waste wood pulverized product is colored white for the purpose of blending such an indicator for urinalysis, the white or substantially white color with or without the addition of the indicator is added. The coloring substance can be blended in the fibrous waste wood pulverized product. In this case, a white or substantially white substance can be used in place of the white pigment and dye. Thus, for example, white materials such as those listed above, such as bentonite, zeolite, calcium carbonate and gypsum, and white materials such as flour and CMC, make the surface of the fibrous waste wood ground particles white. It can be used as a coloring substance.
In the case of a urine pH indicator, the coloring substance used is not supposed to affect the pH. For example, titanium white or the like can be used.
[0024]
In addition, in the present invention, the granulated dried product of fibrous waste wood pulverized product itself does not have a deodorizing ability, so that urine excreted by animals is decomposed to avoid odor as much as possible. In addition, the animal excrement disposal material of the present invention has, as an auxiliary deodorant, a coffee liquid extraction residue, bentonite or zeolite having an adsorption capacity in an amount of 10% by weight or less.
In the present invention, together with the fibrous waste wood pulverized product, it can be used in an amount of 10% by weight or less as the main component of the animal excrement disposal material.
In the present invention, in order to avoid pulverization of the excrement disposal material at the time of use, it is preferable to blend a substance having an adhesive function into the pulverized waste wood ground material.
[0025]
In the present invention, the excrement disposal material is granulated with a particle size of 1 mm or more (for example, on a 1 mm sieve) in order to avoid the presence of fine fibrous waste wood pulverized material and fine water absorbent resin as much as possible. It is preferable to be granulated into a product, but when granulated into particles having a particle size of 2 mm or more, for example, it becomes difficult to disperse into the room from an animal toilet box. Yes, it is preferable for maintaining indoor hygiene. However, in these cases, the presence of particles having a particle size of 1 mm or less or the presence of particles having a particle size of 2 mm or less is not completely excluded. The granulated product can be formed into various shapes such as a spherical shape, a columnar shape, a granular shape, and a granular shape.
[0026]
In the present invention, the waste wood pulverized product and the superabsorbent resin mixture are granulated by a granulator. As the granulator, a conventionally known extrusion granulator can be used. However, in addition to this, various granulation apparatuses such as a bread mold, a drum mold, a fluidized bed mold, and a tablet molding machine can be used. In these granulators, the adhesion of colored substances such as white powder to the surface of the granulated product that has been granulated is brought into direct contact with, for example, white powder on the surface of the granulated product when the granulated product is formed. It can be carried out by adhering by spraying or the like by making white powder into a solution or suspension.
[0027]
In the present invention, the surfactant is applied to improve the wetting of the plastic film covering the surface of the waste wood and increase the water absorption rate of the granulated product of the waste wood pulverized product, Cationic surfactants, nonionic or surfactants, anionic surfactants or zwitterionic surfactants can be used.
Examples of anionic surfactants include dodecylbenzenesulfonic acid and sulfosuccinic acid type anionic surfactants, and examples of nonionic surfactants include octylphenyl ether and polyoxyethylene derivatives. Surfactants include lauryl trimethyl ammonium chloride, stearyl trimethyl ammonium chloride, coconut amine acetate and the like.
[0028]
In the present invention, a mixture of pulverized waste wood pulverized material, a superabsorbent resin and water is granulated. In this granulation process or after granulation, further production of fibrous waste wood pulverized material is performed. In order to stabilize the granulated particles as particles, the granulated particles are coated with a superabsorbent fiber having a bonding ability and a water absorbing ability, a superabsorbent resin, a substance having a bactericidal action, etc. on the granulated particles. By adhering a substance having an adsorption function or a bactericidal action to the surface of the powder and then drying it, the adhered substance having an adsorption function and / or a bactericidal function is prevented from easily peeling off from the surface of the granulated particles. preferable. Examples of the substance having such an adsorption function and a sterilization function include catechin, pancil, and sumernak (trade name). In the present invention, the waste wood pulverized product used in the coating mixture is preferably made into a fine pulverized product having a particle size of 0.5 mm or less, preferably 0.1 mm or less, through a sieve, for example. When such a finely pulverized product is used as a coating mixture, it is washed away by urine during use and washed away, so that the color of the core can be seen from the outside. It is easy to know.
[0029]
[Action]
In the present invention, the animal excrement disposal material is formed of a waste wood pulverized product mainly containing fibrous waste wood particles having a particle size of 5 mm or less and a mixture containing a smaller amount of adhesive than the waste wood pulverized product. Because it is a granular material, the fibrous waste wood pulverized material obtained by fiberizing the waste wood pulverized material can be easily granulated by mixing it with an adhesive and water. Can be granulated without using a large amount. In addition, when coloring the granulated surface containing fiberized waste wood pulverized material with a coloring substance, the unique color of the waste wood pulverized material can be hidden, and excrement disposal can be performed by selecting the coloring material. For example, it is possible to color the material in a color according to the harmony with the indoor furniture used, hygiene, user preference, color atmosphere, etc., and to increase the color of animal excrement disposal materials. it can.
In the present invention, the animal excrement disposal material can be coated with the adhesive mixture containing the waste wood pulverized material and the adhesive on the surface of the granulated material containing the waste wood pulverized material. Since the excreted excrement is easily wrapped by, for example, hanging the excrement disposal material from above, the foul odor of the excrement is not adsorbed by the excrement disposal material and diffused to the surroundings.
[0030]
Moreover, in the present invention, the defibrated wood flour itself has water absorbency and water retention, but it is mixed with a material having water absorbency and / or deodorization property to impart water absorbency and deodorization property. It can be used as an animal excrement disposal material, and has good absorbability and deodorant property of animal excreted urine.
Furthermore, since the excrement disposal material of the present invention can be colored with a white substance in particular, even if an indicator for urinalysis is added, the color development can be highlighted, and the color of urine excreted by an animal is examined, It becomes easy to monitor the health status of animals.
[0031]
In the present invention, the paste such as polyacrylamide, α-starch, poval and / or wheat flour is an amount of 10% by weight or less of the coating layer, an amount of 55% by weight or more of pulverized waste wood, and 35% by weight of a superabsorbent resin. % Or less of the mixture. In this case, it adheres to the excrement of the animal, the excrement treatment material particles adhere to each other, wraps up the excrement and forms a lump, and only the lump part is removed to clean up the excrement of the animal. Cleaning up is simple and easy. In addition, when an auxiliary deodorizing agent and / or a highly water-absorbing resin are mixed in the animal excrement treating material, it exhibits further excellent deodorizing property, water absorbing property and water retaining property as the excrement treating material.
Since the present invention is effectively used as waste material for animal excrement treatment, waste wood generated from a lumber mill or waste wood used in a construction site that has been considered a problem in the past. Disposal processing is easy.
[0032]
The animal excrement disposal material of the present invention mainly contains industrial waste fibrillated waste wood pulverized material, and absorbs water and / or granulated material having a particle diameter of 1 mm or more, preferably 3 mm or more. Since it is molded together with a deodorizing substance, it has good absorbability for animal urine, good water retention, and wood flour gives the scent of wood to the surroundings, so it has good deodorizing properties.
Further, the excrement disposal material of the present invention includes, for example, a superabsorbent resin, wheat flour, poval, α-starch or other compounding substance having adhesive ability, a substance having bactericidal action, or two or more of these compounding substances Since it can be mixed and mixed, it can adhere to the excrement of animals, wrap the excrement into a lump, and clean up easily and easily. Moreover, when the deodorizing agent and / or the water-absorbing agent are mixed, the deodorizing agent and the water-absorbing property which are further excellent as the excrement treating material are exhibited. Furthermore, when a substance having a bactericidal action is mixed, the excrement disposal material can be stored for a long time without generation of soot and the like.
[0033]
【Example】
Examples of embodiments of the present invention will be described below, but the present invention is not limited to the following descriptions and examples.
FIG. 1 is a conceptual diagram showing an example of an apparatus for granulating waste wood pulverized material used in this example according to an embodiment of the present invention to form a waste disposal material.
In FIG. 1, various kinds of waste wood collected from a construction site and cut to a size of 10 cm were used. In this example, the waste wood is crushed by a
[0034]
Waste wood pulverized material containing fibrous waste wood particles having a particle size of 3 to 5 mm collected in the
[0035]
The outlet of the
[0036]
Example 1.
Hiba-based waste wood collected from a construction site, crushed to a particle size of 50 to 100 mm by a crusher, and crushed to a particle size of 5 to 30 mm by a crusher, pulverized to a particle size of 3.5 mm or less by a defibrator, Fiberized. This fiberized hiba waste wood pulverized product is put into the
On the other hand, 1.5 kg of fiberized hiba waste wood pulverized material having a particle size of 3.5 mm or less is supplied from the
The coating mixture of the fiberized waste wood pulverized product, the coating superabsorbent resin and the coating polyacrylamide is sent to the
[0037]
In the room, 30 milliliters of simulated urine at a temperature of 38 ° C. was added to 100 g of cat toilet sand produced in this way, but the water absorption and deodorizing properties were very good, and the ammonia odor was eliminated. After that, the smell of wood was recognized. In this example, simulated urine was prepared by dissolving 10 g of sodium chloride and 10 ml of aqueous ammonia (NH3 9.5 to 10.5 wt%) in 1 liter of water.
This cat litter sand was used with a thickness of 10 cm on the cat litter, but the cat was used as a litter as usual, and there was no problem in its use.
The toilet sand in this example easily adheres to the surroundings of the excrement and facilitates the removal of the excrement. Moreover, the toilet sand in this example drifts the scent of wood after use, so it has excellent deodorizing properties and deodorizing properties, so it was possible to avoid generating unpleasant odors indoors. .
In this example, hiba-based waste wood pulverized material collected from the construction site is used, but the same result can be obtained even if various types of wood powder of different types of wood are used. .
[0038]
Example 2.
The timber waste wood collected from the construction site, crushed to a particle size of 50 to 100 mm by a crusher, and crushed to a particle size of 5 to 30 mm by a crusher is pulverized to a particle size of 3.5 mm or less by a defibrator. , Fiberized. The crushed waste wood of cedar wood fiberized by this defibrating machine was put into the
On the other hand, 1.5 kg of the waste wood pulverized material of fiberized cedar wood having a particle size of 3 mm or less is sent from the
The coating mixture of the fiberized waste wood ground for coating, the superabsorbent resin for coating and the polyacrylamide for coating is sent to the
In the room, the cat toilet sand produced in this way was laid on the cat toilet in a thickness of 10 cm. 30 milliliters of simulated urine at a temperature of 38 ° C. was injected into the sand for the toilet of the cat, but the water absorption and deodorizing properties were very good, and the ammonia odor was deodorized and hardly perceived. Cats are used in the same manner as conventional sand, and there is no problem in odor even when used indoors. The urination portion is agglomerated and the excrement can be easily taken out.
[0039]
Example 3
The timber waste wood collected from the construction site, crushed to a particle size of 50 to 100 mm by a crusher, and crushed to a particle size of 5 to 30 mm by a crusher is pulverized to a particle size of 3.5 mm or less by a defibrator. , Fiberized. The crushed waste wood of cedar wood fiberized by this defibrating machine was put into the
In this example, polyacrylamide (manufactured by Mitsubishi Chemical Corporation) was used as the adhesive instead of the superabsorbent resin, and was put into the
0.5 kg of polyacrylamide was mixed with the pulverized waste wood of cedar wood sent by the
On the other hand, 1.5 kg of the waste wood pulverized material of fiberized cedar wood having a particle size of 3 mm or less is sent from the
The coating mixture of the fiberized waste wood ground for coating, the superabsorbent resin for coating, and the polyacrylamide for coating is sent to the
In the room, the cat toilet sand produced in this way was laid on the cat toilet in a thickness of 10 cm. 30 milliliters of simulated urine at a temperature of 38 ° C. was injected into the sand for the toilet of the cat, but the water absorption and deodorizing properties were very good, and the ammonia odor was deodorized and hardly perceived. Cats are used in the same manner as conventional sand, and there is no problem in odor even when used indoors. The urination portion is agglomerated and the excrement can be easily taken out.
Example 4
Waste wood made of firewood collected from a construction site, crushed to a particle size of 50 to 100 mm by a crusher, and crushed to a particle size of 5 to 30 mm by a crusher is pulverized to a particle size of 3 mm or less by a defibrating machine. Turned into. 70 parts by weight of the waste wood pulverized material made into fiber by this defibrating machine, 5 parts by weight of a superabsorbent resin having a particle size of 25 μm (trade name Hs1100: manufactured by Hymo Co., Ltd.) and a superabsorbent resin having a particle size of 150 μm ( (Trade name Hs1100: manufactured by Hymo Co., Ltd.) 50 parts by weight of
The sand for cat toilets manufactured in this way was used on a cat toilet in a room with a thickness of 10 cm. 30 milliliters of simulated urine at a temperature of 38 ° C. was injected into the sand for the toilet of the cat, but the water absorption and deodorizing properties were very good, and the ammonia odor was deodorized and hardly perceived. Cats are used in the same manner as conventional sand, and there is no problem in odor even when used indoors. The urination portion is agglomerated and the excrement can be easily taken out.
Example 5.
Waste wood made of firewood collected from a construction site, crushed to a particle size of 50 to 100 mm by a crusher, and crushed to a particle size of 5 to 30 mm by a crusher is pulverized to a particle size of 3 mm or less by a defibrating machine. Turned into. 92 parts by weight of the waste wood pulverized material of fiber made by this defibrating machine, 5 parts by weight of a superabsorbent resin (trade name Hs1100: manufactured by Hymo Co., Ltd.) with an average particle size of 25 μm and a superabsorbent with an average particle size of 150 μm Resin (trade name Hs1100: manufactured by Hymo Co., Ltd.) 50 parts by weight of a
The sand for cat toilets manufactured in this way was used on a cat toilet in a room with a thickness of 10 cm. 30 milliliters of simulated urine at a temperature of 38 ° C. was injected into the sand for the toilet of the cat, but the water absorption and deodorizing properties were very good, and the ammonia odor was deodorized and hardly perceived. Cats are used in the same manner as conventional sand, and there is no problem in odor even when used indoors. The urination portion is agglomerated and the excrement can be easily taken out.
In this example, crushed waste wood of cedar, cedar and firewood is used, but the same result can be obtained even if various wood powders of different types of wood are used. it can.
[0040]
【The invention's effect】
In the present invention, the animal excrement disposal material contains a waste wood pulverized product mainly containing fibrous waste wood particles having a particle size of 5 mm or less, and a small amount of superabsorbent resin compared to the waste wood pulverized product. Since it is a granular material formed of a mixture, it exhibits a soft wood powder color and can be easily colored in other colors, so it is used in comparison with conventional animal excrement disposal materials. According to the color tone, it is possible to select various color tones, that is, an excrement disposal material having an appropriate color, and it is possible to maintain harmony of indoor colors as well as a sanitary atmosphere.
Moreover, since the waste wood pulverized product has a unique scent, it is left in the room, for example, to eliminate the smell peculiar to the toilet and improve the indoor environment. In addition, since it itself has water retention, the use of a urinalysis indicator becomes easier and the health condition of the animal can be grasped more easily than conventional animal excrement disposal materials.
In the present invention, waste wood that has conventionally been generated from a construction site and used as waste is converted into fiberized particles, so that only a superabsorbent resin and a granulated product without using paper pulp or paper products are used. It can be used effectively as an animal excrement disposal material at low cost, and is mainly composed of combustible material, so that it can be easily disposed of. In addition, the present invention can appropriately color the dried granulated product of the pulverized waste wood and use it as an animal excrement disposal material. Therefore, the animal has a color tone adapted to the indoor furniture or to the taste. It can be used as a waste disposal material.
As described above, the present invention has a problem related to the disposal of waste wood of industrial waste generated from a construction site as compared with conventional animal waste treatment materials, and conventional used animal excrement. It solves problems related to the disposal of non-flammable materials at once, and is significant in terms of effective use of resources and reduction of treatment of environmental waste.
[Brief description of the drawings]
BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is a conceptual diagram showing an example of an apparatus for granulating waste wood pulverized material used in this example to produce an excrement disposal material.
[Explanation of symbols]
1 Crusher
2, 4 Magnetic separator
3 Coarse grinder
5 answering machines
6 First hopper
7 extrusion granulator
8 First screw feeder
9 Super absorbent polymer supply hopper, acrylamide supply hopper
10 Superabsorbent resin supply section, acrylamide supply section
11 Water supply hopper
12 Water supply section
13 Round sieve
14 Second screw feeder
15 Primary fine grinding defibrator
16 Secondary fine grinding and defibrating machine
17 Second hopper
18 Super absorbent polymer supply hopper for coating
19 Polyacrylamide supply hopper for coating
20 Third Ecru Feeder
21 Mixer
22 Transport path
23 Coating equipment
24 round sieve
25 Dryer
26, 28, 30, 31 Belt conveyor
27 Product hopper
29 Sieve machine
32 Automatic packaging machine
Claims (18)