JP3511133B2 - Adhesive silicone molded product with separator - Google Patents
Adhesive silicone molded product with separatorInfo
- Publication number
- JP3511133B2 JP3511133B2 JP2001033385A JP2001033385A JP3511133B2 JP 3511133 B2 JP3511133 B2 JP 3511133B2 JP 2001033385 A JP2001033385 A JP 2001033385A JP 2001033385 A JP2001033385 A JP 2001033385A JP 3511133 B2 JP3511133 B2 JP 3511133B2
- Authority
- JP
- Japan
- Prior art keywords
- separator
- molded article
- water
- silicone
- silicone molded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、粘着面がセパレー
ターにより保護され、このため現場施工においても優れ
た取り扱い性を有する粘着性シリコーン成形品に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive silicone molded article having an adhesive surface protected by a separator and therefore having excellent handleability even in the field.
【０００２】[0002]
【従来の技術及び発明が解決しようとする課題】シリコ
ーン製品は、耐熱性、耐候性、電気絶縁性等に優れると
ともに、ポッティング性、シール性にも優れるため、電
子機器、家電、自動車、建築物等のポッティング材、シ
ール材として広く使用されている。2. Description of the Related Art Silicone products are excellent in heat resistance, weather resistance, electric insulation, etc., as well as in potting property and sealing property, so that electronic products, home appliances, automobiles, buildings It is widely used as potting material and sealing material.
【０００３】しかし、これらに使用されるシリコーンゲ
ル等の強い粘着性を有するシリコーン材料は、取り扱い
性が極めて悪いため、使用する部分に流し込んでから固
める（ゲル化させる）等のポッティングやシールを行う
のに専用の装置が必要とされていた。そのため、大型の
機械部品のシール等についてはこれらのシリコーン材料
の使用が制限されていた。However, since silicone materials having a strong adhesive property such as silicone gel used for these have extremely poor handleability, potting or sealing such as pouring into a portion to be used and hardening (gelation) is performed. A dedicated device was needed for this. Therefore, the use of these silicone materials has been restricted for sealing large machine parts.
【０００４】一方、既に架橋したシリコーンゲル等の粘
着性シリコーン成形品は、その粘着面にポリエチレンや
ポリプロピレン等のセパレーター（保護フィルム）を貼
付、保護することも行われているが、これらのセパレー
ターを用いた場合、セパレーターを剥がそうとすると、
シリコーン成形品が軟らかく強度もないため、成形品の
形状を維持することができなかった。On the other hand, a pressure-sensitive adhesive silicone molded article such as a cross-linked silicone gel is attached and protected with a separator (protective film) such as polyethylene or polypropylene on the adhesive surface. When used, when trying to peel off the separator,
Since the silicone molded product is soft and has no strength, the shape of the molded product could not be maintained.
【０００５】本発明は、上記問題点を解決するためにな
されたもので、セパレーターを剥がした場合でも、粘着
性シリコーン成形品の表面粘着層を荒すことなくセパレ
ーターを剥がすことができ、粘着性シリコーン成形品に
微細加工を施した場合でも、微細加工部分にストレスを
かけずにセパレーターを剥がすことができる、現場施工
に好適な粘着性を有するシリコーン成形品を提供するこ
とを目的とする。The present invention has been made to solve the above problems, and even when the separator is peeled off, the separator can be peeled off without roughening the surface adhesive layer of the adhesive silicone molded article. An object of the present invention is to provide a silicone molded product having adhesiveness suitable for on-site construction, which enables the separator to be peeled off without applying stress to the finely processed portion even when the molded product is subjected to fine processing.
【０００６】[0006]
【課題を解決するための手段及び発明の実施の形態】本
発明者は、上記目的を達成するため鋭意検討を行った結
果、粘着性シリコーン成形品の粘着面に剥離可能に貼
付、保護するセパレーターとして、水分を保有する保水
材にて形成されたセパレーターを使用することにより、
シリコーンゲル等の軟らかく、強度の低い粘着性シリコ
ーン成形品の粘着面の状態を損うことなく、また粘着面
に微細加工を施した場合もこれにストレスをかけること
なく、スムーズにセパレーターを剥離除去し得ることを
見出し、本発明をなすに至った。Means for Solving the Problems and Modes for Carrying Out the Invention As a result of intensive studies to achieve the above object, the present inventor has found that a separator for releasably attaching and protecting the adhesive surface of an adhesive silicone molded article. As, by using a separator formed of a water retaining material that retains water,
Adhesive surface of soft and low-strength silicone molded products such as silicone gel is not damaged, and even when microfabrication is applied to the adhesive surface, the separator is peeled off smoothly without stress. The inventors have found that this is possible and have completed the present invention.
【０００７】従って、本発明は、粘着性シリコーン成形
品の少なくとも一方の面に、多価アルコールを含有させ
た、水分を保有する保水材を貼着面とするセパレーター
が剥離可能に貼付されてなることを特徴とするセパレー
ターを有する粘着性シリコーン成形品を提供する。Therefore, according to the present invention, a separator having a water-retaining material containing water containing polyhydric alcohol as an adhering surface is releasably attached to at least one surface of an adhesive silicone molded article. An adhesive silicone molded article having a separator is provided.
【０００８】以下、本発明につき更に詳しく説明する。The present invention will be described in more detail below.
【０００９】本発明の粘着性を有するシリコーン成形品
は、少なくとも一方の面に、水分を保有する保水材を用
いて形成されたセパレーターを剥離可能に貼着してなる
ものである。The adhesive silicone molded article of the present invention comprises a separator formed of a water retaining material retaining water on at least one surface thereof so as to be releasable.
【００１０】ここで、粘着性を有するシリコーン成形品
としては、シリコーンゲル、表面粘着性の強い低硬度シ
リコーンゴム、シリコーン粘着剤等の成形品が挙げら
れ、これらが他の材料と複合化されたものであってもよ
い。中でもシリコーンゲル及びシリコーンゲルを用いた
複合品の場合に有効である。Examples of the adhesive silicone molded article include silicone gel, low surface hardness silicone rubber having strong surface tackiness, silicone adhesive and the like, which are compounded with other materials. It may be one. Above all, it is effective in the case of a silicone gel and a composite product using a silicone gel.
【００１１】保水材としては、デンプン、ポリアクリル
酸、ポリビニルアルコール、ポリエチレンオキシド等の
水溶性高分子を架橋によって水に不溶化して得られる吸
水性高分子、コンニャク等があげられ、吸水性高分子が
好ましい。Examples of the water retention material include water-absorbent polymers obtained by insolubilizing water-soluble polymers such as starch, polyacrylic acid, polyvinyl alcohol, and polyethylene oxide in water by crosslinking, konjak, and the like. Is preferred.
【００１２】セパレーターは、この保水材に水を含有さ
せたものから形成されるが、この場合、水の含有量は保
水材１００重量部に対して１〜５００重量部、特に５〜
１００重量部が好ましい。The separator is formed by adding water to the water retaining material. In this case, the content of water is 1 to 500 parts by weight, especially 5 to 100 parts by weight of the water retaining material.
100 parts by weight is preferred.
【００１３】また、セパレーターは、取り扱い性を向上
させるために、内部にポリエチレンやＰＥＴ等の樹脂フ
ィルム、ナイロン等の不織布、Ａｌ箔等の金属フィル
ム、ガラスクロス等の無機不織布などの補強材を存在さ
せることが好ましい。この場合、セパレーターは、補強
材に水分を含有する保水材をコーティング等により塗布
し、保水材の層を設けることによって形成することがで
きる。Further, the separator has a reinforcing material such as a resin film such as polyethylene and PET, a non-woven fabric such as nylon, a metal film such as Al foil, and an inorganic non-woven fabric such as glass cloth in order to improve the handling property. Preferably. In this case, the separator can be formed by applying a water retaining material containing water to the reinforcing material by coating or the like and providing a layer of the water retaining material.
【００１４】保水材には、水と共にグリセリン等の多価
アルコールを含有させることが好ましい。多価アルコー
ルを含有させることにより、離型耐久性が向上する。多
価アルコールの量は、保水材１００重量部に対して１〜
５００重量部、特に５〜１００重量部が好ましい。The water retention material preferably contains polyhydric alcohol such as glycerin together with water. By containing a polyhydric alcohol, the release durability is improved. The amount of polyhydric alcohol is 1 to 100 parts by weight of the water retaining material.
500 parts by weight, especially 5 to 100 parts by weight are preferred.
【００１５】本発明は、粘着性を有するシリコーン成形
品を所定の形状とした後、上記セパレーターを貼り付け
ることにより容易に製造することができる。セパレータ
ーは粘着性を有するシリコーン成形品の少なくとも一面
に設けられていればよく、他の面はＰＥＴやポリエチレ
ン等のフィルムであってもよい。なお、セパレーターの
厚さは、０．１〜５ｍｍ、特に０．１〜２ｍｍであるこ
とが好ましい。The present invention can be easily manufactured by forming an adhesive silicone molded product into a predetermined shape and then attaching the above-mentioned separator. The separator may be provided on at least one surface of the adhesive silicone molded product, and the other surface may be a film such as PET or polyethylene. The thickness of the separator is preferably 0.1 to 5 mm, especially 0.1 to 2 mm.
【００１６】本発明の上記セパレーターを有する粘着性
シリコーン成形品は、セパレーターを剥がした場合でも
粘着性シリコーン成形品の表面粘着層を荒らすことがな
く、粘着性シリコーン成形品に微細加工を施した場合で
も微細加工部分にストレスをかけずにセパレーターを剥
がすことができるため、取り扱い性に優れ、現場施工に
好適である。また、本発明のセパレーターを有する粘着
性シリコーン成形品は、打ち抜き加工性にも優れ、所定
の形状に打ち抜き加工することができる。The pressure-sensitive adhesive silicone molded article having the above-mentioned separator of the present invention does not roughen the surface pressure-sensitive adhesive layer of the pressure-sensitive adhesive silicone molded article even when the separator is peeled off. However, since the separator can be peeled off without applying stress to the microfabricated portion, it has excellent handleability and is suitable for on-site construction. Further, the adhesive silicone molded product having the separator of the present invention is excellent in punching workability and can be punched into a predetermined shape.
【００１７】[0017]
【実施例】以下、実施例を示して本発明を具体的に説明
するが、本発明は下記の実施例に制限されるものではな
い。EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to the following examples.
【００１８】[実施例１]シリコーンゲルＫＥ１０５１Ａ
／Ｂ（信越化学工業（株）製品名）のＡ液とＢ液を等量
混合して１００ミクロンの厚さのＰＥＴフィルムに０．
５ｍｍの厚みでコーティングし、硬化成形した。[Example 1] Silicone gel KE1051A
/ B (Shin-Etsu Chemical Co., Ltd. product name) liquids A and B are mixed in equal amounts to form a PET film having a thickness of 100 microns.
It was coated with a thickness of 5 mm and cured and molded.
【００１９】ついで、アクリル系高分子吸水ポリマー１
００重量部にグリセリンと水を１対１で混合した混合液
２０重量部を充填し、不織布に０．５ｍｍの厚みでコー
ティングしたセパレーターを貼り付けた。これを、所定
の形状に打ち抜き加工したところ、任意の形に打ち抜き
加工ができた。また、上記セパレーターは、シリコーン
ゲル硬化物（成形品）からスムーズに、その表面状態を
損うことなく剥離することができた。Then, the acrylic polymer water-absorbing polymer 1
20 parts by weight of a mixed solution in which 100 parts by weight of glycerin and water were mixed in a ratio of 1: 1 was filled, and a separator coated with a thickness of 0.5 mm was attached to the nonwoven fabric. When this was punched into a predetermined shape, it could be punched into an arbitrary shape. Further, the separator was able to be smoothly peeled from the silicone gel cured product (molded product) without impairing the surface condition.
【００２０】[実施例２]５０ミクロンの厚さのＰＥＴフ
ィルムに、アクリル系高分子吸水ポリマー１００重量部
にグリセリンと水を１対１で混合した混合液２０重量部
を充填したものを０．５ｍｍの厚みでコーティングした
セパレーターの上に、ＫＥ１０５１Ａ／Ｂ（信越化学工
業（株）製品名）のＡ液とＢ液を等量混合したものを１
ｍｍの厚みでコーティングし、硬化成形した。ついで、
このシリコーンゲル硬化物（成形品）の表面に上記と同
じセパレーターを貼り付けた。これを所定の形状に打ち
抜き加工したところ、任意の形に打ち抜き加工ができ
た。また、電子機器の基板パッキング状に打ち抜いたも
のをパッキングとして使用したところ、上記セパレータ
ーで表面粘着面が保護されているので取り扱い性もよ
く、また使用に際してセパレーターを表面粘着面を損う
ことなくスムーズに剥離除去することができ、セパレー
ターを除去して用いたパッキング（シリコーンゲル成形
品）はパッキング機能も十分であった。[Example 2] A PET film having a thickness of 50 microns was filled with 20 parts by weight of a mixed solution prepared by mixing 100 parts by weight of an acrylic polymer water-absorbing polymer with glycerin and water in a ratio of 1: 1. On a separator coated with a thickness of 5 mm, mix 1 and 1 parts of KE1051A / B (product name of Shin-Etsu Chemical Co., Ltd.) A and B liquids.
It was coated with a thickness of mm and cured and molded. Then,
The same separator as described above was attached to the surface of this silicone gel cured product (molded product). When this was punched into a predetermined shape, it could be punched into an arbitrary shape. In addition, when punched into a packing shape for electronic equipment, it was used as packing, and because the surface adhesive surface was protected by the separator, it was easy to handle, and the separator was smooth when used without damaging the surface adhesive surface. The packing (silicone gel molded product) used after removing the separator had a sufficient packing function.
【００２１】[0021]
【発明の効果】本発明のセパレーターを有する粘着性シ
リコーン成形品は、成形品のセパレーター貼着面の状態
を損うことなく、セパレーターをスムーズに剥離除去す
ることができる。The pressure-sensitive adhesive silicone molded article having the separator of the present invention can be smoothly peeled off and removed without impairing the condition of the surface of the molded article to which the separator is attached.
Claims (5)
方の面に、多価アルコールを含有させた、水分を保有す
る保水材を貼着面とするセパレーターが剥離可能に貼付
されてなることを特徴とするセパレーターを有する粘着
性シリコーン成形品。1. A separator comprising a polyhydric alcohol-containing water retaining material having a water-retaining material as an attachment surface is releasably attached to at least one surface of an adhesive silicone molded article. An adhesive silicone molded article having a separator.
部に対して１〜５００重量部である請求項１記載のシリ
コーン成形品。2. The silicone molded article according to claim 1, wherein the amount of polyhydric alcohol is 1 to 500 parts by weight with respect to 100 parts by weight of the water retaining material.
ルコールを含有させた、水分を保有する保水材の層を形
成してなるものである請求項１又は２記載のシリコーン
成形品。3. The silicone molded article according to claim 1, wherein the separator is formed by forming a layer of a water retaining material containing a polyhydric alcohol and retaining water on the reinforcing material.
１、２又は３記載のシリコーン成形品。4. The silicone molded article according to claim 1, 2 or 3, wherein the water retaining material is a water-absorbing polymer substance.
ル成形品である請求項１乃至４のいずれか１項記載のシ
リコーン成形品。5. The silicone molded article according to claim 1, wherein the adhesive silicone molded article is a silicone gel molded article.