JP3447189B2 - Viscoelastic composition and damping material - Google Patents

Viscoelastic composition and damping material

Info

Publication number
JP3447189B2
JP3447189B2 JP01650397A JP1650397A JP3447189B2 JP 3447189 B2 JP3447189 B2 JP 3447189B2 JP 01650397 A JP01650397 A JP 01650397A JP 1650397 A JP1650397 A JP 1650397A JP 3447189 B2 JP3447189 B2 JP 3447189B2
Authority
JP
Japan
Prior art keywords
ethylene
meth
acrylate
weight
viscoelastic composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP01650397A
Other languages
Japanese (ja)
Other versions
JPH10212330A (en
Inventor
元 野世渓
章 中寿賀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP01650397A priority Critical patent/JP3447189B2/en
Publication of JPH10212330A publication Critical patent/JPH10212330A/en
Application granted granted Critical
Publication of JP3447189B2 publication Critical patent/JP3447189B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【発明の属する技術分野】本発明は、粘弾性組成物及び
それを用いた制振材に関する。
TECHNICAL FIELD The present invention relates to a viscoelastic composition and a vibration damping material using the same.

【0002】[0002]

【従来の技術】従来より、例えば、ブチルゴム等の合成
ゴムを主成分とする粘弾性組成物が、自動車、機械器
具、船舶、建築材料、音響材料等の振動やそれに伴って
発生する騒音等を防止するための制振材、防振材、免振
材等(以下、単に「制振材」と記す)として一般的に用
いられている。
2. Description of the Related Art Conventionally, for example, a viscoelastic composition containing a synthetic rubber such as butyl rubber as a main component has been used to reduce vibrations of automobiles, machinery and equipment, ships, building materials, acoustic materials, etc. It is generally used as a vibration damping material, a vibration damping material, a vibration damping material, etc. (hereinafter, simply referred to as a "vibration damping material") for prevention.

【0003】しかし、上記合成ゴム系粘弾性組成物は、
制振材として用いる場合、制振等を施そうとする対象材
料(以下、単に「被着体」と記す)に対する接着性が十
分でないという問題点があり、この問題点に対応するた
め、近年、アクリル系ポリマーを主成分とする粘弾性組
成物を用いた制振材の検討が行われている。
However, the above synthetic rubber-based viscoelastic composition is
When used as a vibration damping material, there is a problem that the adhesiveness to a target material (hereinafter, simply referred to as “adherent”) to be subjected to vibration damping or the like is not sufficient. , A vibration damping material using a viscoelastic composition containing an acrylic polymer as a main component has been studied.

【0004】上記アクリル系ポリマーを主成分とする粘
弾性組成物の一例として、例えば、特開平4−2025
86号公報では、「アルキル基の炭素数が8〜12のア
クリル酸アルキルエステルを必須とする主モノマー75
〜92重量%と、ホモポリマーのガラス転移温度が50
℃以上であるカルボキシル基含有モノマー25〜8重量
%との共重合ポリマーの架橋構造体を含んでなり、溶剤
不溶分が95重量%以上で、SUS板に対するT剥離強
度が400g/20mm幅以上であることを特徴とする
制振材用感圧性接着剤組成物」が提案されている。
As an example of the viscoelastic composition containing the acrylic polymer as a main component, for example, JP-A-4-2025 is known.
In Japanese Patent Publication No. 86, "A main monomer 75 in which an alkyl acrylate whose alkyl group has 8 to 12 carbon atoms is essential.
˜92% by weight, the homopolymer glass transition temperature is 50
It comprises a crosslinked structure of a copolymerized polymer with 25 to 8% by weight of a carboxyl group-containing monomer having a temperature of ℃ or more, a solvent insoluble content of 95% by weight or more, and a T peel strength to a SUS plate of 400 g / 20 mm width or more. A pressure-sensitive adhesive composition for a vibration damping material, which is characterized by being present, has been proposed.

【0005】しかし、上記提案にあるようなアクリル系
ポリマーを主成分とする粘弾性組成物は、一般的に、被
着体の表面が清浄である場合には良好な接着性を示すも
のの、被着体の表面に例えば切削油等の油類が付着して
いる場合、接着性が乏しくなる、即ち、油面接着性が乏
しくなるという欠点があり、予め被着体表面を洗浄等に
より清浄化したり、油面接着性の良好な別の接着剤を併
用したりする必要が生じ、作業性が著しく悪くなるとい
う問題点がある。
However, the viscoelastic composition containing an acrylic polymer as a main component as proposed above generally shows good adhesiveness when the surface of the adherend is clean, but For example, if oil such as cutting oil adheres to the surface of the adherend, there is a drawback that the adhesiveness becomes poor, that is, the oil surface adhesiveness becomes poor, and the adherend surface is previously cleaned by cleaning or the like. Alternatively, it is necessary to use another adhesive having a good oil surface adhesiveness in combination, resulting in a problem that workability is significantly deteriorated.

【0006】上述の如く、優れた油面接着性と優れた制
振性を兼備する粘弾性組成物及びその粘弾性組成物を用
いた制振材は実用化されていないのが現状である。
As described above, the viscoelastic composition having both excellent oil surface adhesiveness and excellent vibration damping property and the vibration damping material using the viscoelastic composition have not been put into practical use at present.

【0007】[0007]

【発明が解決しようとする課題】本発明は、上記従来の
問題点を解決するため、予め被着体表面を清浄化した
り、別の接着剤を併用したりすることなく、優れた油面
接着性を発揮すると共に、優れた制振性を有する粘弾性
組成物、及び、その粘弾性組成物を用いた制振材を提供
することを課題とする。
SUMMARY OF THE INVENTION In order to solve the above-mentioned conventional problems, the present invention provides excellent oil surface adhesion without cleaning the surface of an adherend in advance or using another adhesive in combination. An object of the present invention is to provide a viscoelastic composition that exhibits excellent vibration damping properties and excellent vibration damping properties, and a vibration damping material using the viscoelastic composition.

【0008】[0008]

【課題を解決するための手段】請求項1記載の発明(以
下、「第1発明」と記す)による粘弾性組成物は、アル
キル基の炭素数が2〜14のアルキル(メタ)アクリレ
ート及び該アルキル(メタ)アクリレートと共重合可能
な極性基含有ビニルモノマーからなるアクリル系モノマ
ーとエチレン−ブチレン系マクロマー及び/又はエチレ
ン−プロピレン系マクロマーとを共重合して得られるア
クリル系共重合体、及び、粘着付与樹脂を含有してな
り、且つ、表面濡れ指数が30dyn/cm以下である
ことを特徴とする。
A viscoelastic composition according to the invention of claim 1 (hereinafter referred to as "first invention") is an alkyl (meth) acrylate having an alkyl group having 2 to 14 carbon atoms and An acrylic copolymer obtained by copolymerizing an acrylic monomer composed of a polar group-containing vinyl monomer copolymerizable with an alkyl (meth) acrylate and an ethylene-butylene macromer and / or an ethylene-propylene macromer, and It is characterized by containing a tackifying resin and having a surface wetting index of 30 dyn / cm or less.

【0009】又、請求項2記載の発明(以下、「第2発
明」と記す)による粘弾性組成物は、上記第1発明によ
る粘弾性組成物において、アクリル系共重合体が、アル
キル基の炭素数が2〜14のアルキル(メタ)アクリレ
ート70〜99.5重量%及び極性基含有ビニルモノマ
ー30〜0.5重量%からなるアクリル系モノマー10
0重量部とエチレン−ブチレン系マクロマー及び/又は
エチレン−プロピレン系マクロマー1〜100重量部と
を共重合して得られるアクリル系共重合体であり、且
つ、上記アクリル系共重合体100重量部に対し、粘着
付与樹脂1〜50重量部が含有されていることを特徴と
する。
The viscoelastic composition according to the invention of claim 2 (hereinafter referred to as the "second invention") is the viscoelastic composition according to the first invention, wherein the acrylic copolymer is an alkyl group. Acrylic monomer 10 comprising 70 to 99.5% by weight of an alkyl (meth) acrylate having 2 to 14 carbon atoms and 30 to 0.5% by weight of a polar group-containing vinyl monomer.
An acrylic copolymer obtained by copolymerizing 0 part by weight with 1 to 100 parts by weight of an ethylene-butylene macromer and / or an ethylene-propylene macromer, and 100 parts by weight of the acrylic copolymer. On the other hand, it is characterized by containing 1 to 50 parts by weight of a tackifying resin.

【0010】さらに、請求項3記載の発明(以下、「第
3発明」と記す)による制振材は、上記第1発明又は第
2発明による粘弾性組成物を用いて製せられていること
を特徴とする。
Further, the vibration damping material according to the invention of claim 3 (hereinafter referred to as "third invention") is made by using the viscoelastic composition according to the first invention or the second invention. Is characterized by.

【0011】第1発明又は第2発明による粘弾性組成物
に用いられるアクリル系共重合体を構成するアルキル基
の炭素数が2〜14のアルキル(メタ)アクリレート
(以下、単に「アルキル(メタ)アクリレート」と記
す)としては、特に限定されるものではないが、例え
ば、エチル(メタ)アクリレート、n−プロピル(メ
タ)アクリレート、イソプロピル(メタ)アクリレー
ト、n−ブチル(メタ)アクリレート、イソブチル(メ
タ)アクリレート、t−ブチル(メタ)アクリレート、
ペンチル(アミル)(メタ)アクリレート、ヘキシル
(メタ)アクリレート、ヘプチル(メタ)アクリレー
ト、2−エチルヘキシル(メタ)アクリレート、n−オ
クチル(メタ)アクリレート、イソオクチル(メタ)ア
クリレート、ノニル(メタ)アクリレート、デシル(メ
タ)アクリレート、ウンデシル(メタ)アクリレート、
ラウリル(ドデシル)(メタ)アクリレート、トリデシ
ル(メタ)アクリレート、テトラデシル(メタ)アクリ
レート等が挙げられ、好適に用いられる。尚、ここで言
う「(メタ)アクリレート」とは「アクリレート」もし
くは「メタクリレート」を意味する。
An alkyl (meth) acrylate having 2 to 14 carbon atoms in the alkyl group constituting the acrylic copolymer used in the viscoelastic composition according to the first or second invention (hereinafter, simply referred to as "alkyl (meth)"). It is not particularly limited, but examples thereof include ethyl (meth) acrylate, n-propyl (meth) acrylate, isopropyl (meth) acrylate, n-butyl (meth) acrylate, isobutyl (meth). ) Acrylate, t-butyl (meth) acrylate,
Pentyl (amyl) (meth) acrylate, hexyl (meth) acrylate, heptyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, n-octyl (meth) acrylate, isooctyl (meth) acrylate, nonyl (meth) acrylate, decyl (Meth) acrylate, undecyl (meth) acrylate,
Lauryl (dodecyl) (meth) acrylate, tridecyl (meth) acrylate, tetradecyl (meth) acrylate, etc. are mentioned and used suitably. The term "(meth) acrylate" used herein means "acrylate" or "methacrylate".

【0012】上記アルキル(メタ)アクリレートは、単
独で用いられても良いし、2種類以上が併用されても良
い。
The above alkyl (meth) acrylates may be used alone or in combination of two or more kinds.

【0013】又、上記アルキル(メタ)アクリレートと
共重合可能な極性基含有ビニルモノマーとしては、特に
限定されるものではないが、例えば、(メタ)アクリル
酸、イタコン酸、クロトン酸、(無水)マレイン酸、
(無水)フマル酸、カルボキシエチルアクリレートのよ
うなカルボキシアルキル(メタ)アクリレート類等のカ
ルボキシル基含有ビニルモノマー;2−ヒドロキシエチ
ル(メタ)アクリレート、2−ヒドロキシプロピル(メ
タ)アクリレート、4−ヒドロキシブチル(メタ)アク
リレート、カプロラクトン変性(メタ)アクリレート、
ポリエチレングリコール(メタ)アクリレート、1,6
−ヘキサンジオールジ(メタ)アクリレート等の水酸基
含有ビニルモノマー;(メタ)アクリロニトリル、N−
ビニルピロリドン、N−ビニルカプロラクタム、N−ビ
ニルラウリロラクタム、(メタ)アクリロイルモルホリ
ン、(メタ)アクリルアミド、ジメチル(メタ)アクリ
ルアミド、N−メチロール(メタ)アクリルアミド、N
−ブトキシメチル(メタ)アクリルアミド、ジメチルア
ミノメチル(メタ)アクリレート等の窒素含有ビニルモ
ノマー等が挙げられ、好適に用いられる。
The polar group-containing vinyl monomer copolymerizable with the above alkyl (meth) acrylate is not particularly limited, and examples thereof include (meth) acrylic acid, itaconic acid, crotonic acid, (anhydrous). Maleic acid,
(Anhydrous) fumaric acid, carboxyl group-containing vinyl monomers such as carboxyalkyl (meth) acrylates such as carboxyethyl acrylate; 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl ( (Meth) acrylate, caprolactone-modified (meth) acrylate,
Polyethylene glycol (meth) acrylate, 1,6
-Hydroxyl group-containing vinyl monomers such as hexanediol di (meth) acrylate; (meth) acrylonitrile, N-
Vinylpyrrolidone, N-vinylcaprolactam, N-vinyllaurylolactam, (meth) acryloylmorpholine, (meth) acrylamide, dimethyl (meth) acrylamide, N-methylol (meth) acrylamide, N
-A nitrogen-containing vinyl monomer such as butoxymethyl (meth) acrylamide, dimethylaminomethyl (meth) acrylate and the like can be mentioned, and they are preferably used.

【0014】上記極性基含有ビニルモノマーは、単独で
用いられても良いし、2種類以上が併用されても良い。
The polar group-containing vinyl monomer may be used alone or in combination of two or more kinds.

【0015】第1発明で用いられるアクリル系モノマー
は、前記アルキル(メタ)アクリレートと上記極性基含
有ビニルモノマーとの混合モノマーであれば良く、その
混合割合は特に限定されるものではない。
The acrylic monomer used in the first invention may be a mixed monomer of the alkyl (meth) acrylate and the polar group-containing vinyl monomer, and the mixing ratio thereof is not particularly limited.

【0016】又、第2発明で用いられるアクリル系モノ
マーは、前記アルキル(メタ)アクリレート70〜9
9.5重量%、好ましくは75〜90重量%、と上記極
性基含有ビニルモノマー30〜0.5重量%、好ましく
は25〜10重量%、とからなることが必要である。
The acrylic monomer used in the second invention is the alkyl (meth) acrylate 70 to 9 described above.
It is necessary to comprise 9.5% by weight, preferably 75 to 90% by weight, and 30 to 0.5% by weight, preferably 25 to 10% by weight, of the above polar group-containing vinyl monomer.

【0017】第2発明で用いられるアクリル系モノマー
中におけるアルキル(メタ)アクリレートの量が70重
量%未満であるか、もしくは、極性基含有ビニルモノマ
ーの量が30重量%を超えると、得られる粘弾性組成物
が硬くなって作業性が悪くなり、逆にアルキル(メタ)
アクリレートの量が99.5重量%を超えるか、もしく
は、極性基含有ビニルモノマーの量が0.5重量%未満
であると、得られる粘弾性組成物の凝集力が低くなって
耐熱性が乏しくなる。
When the amount of the alkyl (meth) acrylate in the acrylic monomer used in the second invention is less than 70% by weight or the amount of the polar group-containing vinyl monomer exceeds 30% by weight, the viscosity obtained is The elastic composition becomes hard and the workability deteriorates, and conversely alkyl (meth)
When the amount of acrylate exceeds 99.5% by weight or the amount of polar group-containing vinyl monomer is less than 0.5% by weight, the resulting viscoelastic composition has low cohesive force and poor heat resistance. Become.

【0018】第1発明又は第2発明による粘弾性組成物
は、上記アクリル系モノマーとエチレン−ブチレン系マ
クロマー及び/又はエチレン−プロピレン系マクロマー
とを共重合して得られるアクリル系共重合体を主成分と
する。
The viscoelastic composition according to the first invention or the second invention is mainly an acrylic copolymer obtained by copolymerizing the above acrylic monomer with an ethylene-butylene macromer and / or an ethylene-propylene macromer. As an ingredient.

【0019】上記エチレン−ブチレン系マクロマーと
は、エチレン−ブチレン骨格の繰り返しから成るポリマ
ー構造を有し、且つ、一方の末端にラジカル重合性の不
飽和結合を有するものである。
The above ethylene-butylene macromer has a polymer structure composed of repeating ethylene-butylene skeletons, and has a radical-polymerizable unsaturated bond at one end.

【0020】上記エチレン−ブチレン系マクロマーの具
体例としては、特に限定されるものではないが、例え
ば、商品名「KRATON LIQUID Polym
erHPVM−1251」(Shell Chemic
al社製)、「KLP L−1203」(油化シェル社
製)等が挙げられ、好適に用いられる。
Specific examples of the ethylene-butylene-based macromer are not particularly limited, but for example, trade name "KRATON LIQUID Polym" may be used.
erHPVM-1251 "(Shell Chemical
Al manufactured by K.K.), “KLP L-1203” (made by Yuka Shell Co., Ltd.) and the like, and are preferably used.

【0021】又、上記エチレン−プロピレン系マクロマ
ーとは、エチレン−プロピレン骨格の繰り返しから成る
ポリマー構造を有し、且つ、一方の末端にラジカル重合
性の不飽和結合を有するものである。
The above ethylene-propylene macromer has a polymer structure composed of repeating ethylene-propylene skeletons and has a radical-polymerizable unsaturated bond at one end.

【0022】前記アクリル系モノマーと共重合される上
記エチレン−ブチレン系マクロマー及び/又は上記エチ
レン−プロピレン系マクロマーは、単独で用いられても
良いし、両者が併用されても良い。
The ethylene-butylene-based macromer and / or the ethylene-propylene-based macromer copolymerized with the acrylic monomer may be used alone or in combination.

【0023】アクリル系モノマーとエチレン−ブチレン
系マクロマー及び/又はエチレン−プロピレン系マクロ
マーとを共重合して得られるアクリル系共重合体は、ポ
リマー中にエチレン−ブチレン骨格及び/又はエチレン
−プロピレン骨格を有するので、後述する粘着付与樹脂
との相溶性が向上し、得られる粘弾性組成物は、吸油性
(油を吸収する性質)に富むものとなり、優れた油面接
着性を発揮すると共に、優れた制振性を示す。
An acrylic copolymer obtained by copolymerizing an acrylic monomer with an ethylene-butylene macromer and / or an ethylene-propylene macromer has an ethylene-butylene skeleton and / or an ethylene-propylene skeleton in the polymer. Since it has, the compatibility with the tackifying resin described below is improved, the resulting viscoelastic composition is rich in oil absorbency (property to absorb oil), exhibits excellent oil surface adhesiveness, and is excellent It exhibits vibration damping properties.

【0024】アクリル系モノマーとエチレン−ブチレン
系マクロマー及び/又はエチレン−プロピレン系マクロ
マーとの共重合方法は、特に限定されるものではなく、
例えば、塊状重合法、溶液重合法、光重合法等を採用し
て、重合触媒の存在下、常法により共重合を行えば良
い。
The copolymerization method of the acrylic monomer and the ethylene-butylene macromer and / or the ethylene-propylene macromer is not particularly limited,
For example, a bulk polymerization method, a solution polymerization method, a photopolymerization method or the like may be adopted, and the copolymerization may be carried out by a conventional method in the presence of a polymerization catalyst.

【0025】第1発明による粘弾性組成物においては、
前述したアクリル系モノマーと上記エチレン−ブチレン
系マクロマー及び/又はエチレン−プロピレン系マクロ
マーとを共重合して得られるアクリル系共重合体が用い
られれば良く、アクリル系モノマーとエチレン−ブチレ
ン系マクロマー及び/又はエチレン−プロピレン系マク
ロマーとの共重合割合は特に限定されるものではない。
In the viscoelastic composition according to the first invention,
An acrylic copolymer obtained by copolymerizing the above-mentioned acrylic monomer and the above ethylene-butylene macromer and / or ethylene-propylene macromer may be used, and the acrylic monomer and the ethylene-butylene macromer and / or Alternatively, the copolymerization ratio with the ethylene-propylene macromer is not particularly limited.

【0026】又、第2発明による粘弾性組成物において
は、前述したアクリル系モノマー100重量部と上記エ
チレン−ブチレン系マクロマー及び/又はエチレン−プ
ロピレン系マクロマー1〜100重量部、好ましくは5
〜90重量部、とを共重合して得られるアクリル系共重
合体が用いられることが必要である。
In the viscoelastic composition according to the second invention, 100 parts by weight of the above-mentioned acrylic monomer and 1 to 100 parts by weight of the above ethylene-butylene macromer and / or ethylene-propylene macromer, preferably 5 parts by weight.
It is necessary to use an acrylic copolymer obtained by copolymerizing with 90 parts by weight.

【0027】第2発明において、アクリル系モノマー1
00重量部に対するエチレン−ブチレン系マクロマー及
び/又はエチレン−プロピレン系マクロマーの共重合量
が1重量部未満であると、アクリル系共重合体の粘着付
与樹脂との相溶性が十分に向上しないので、得られる粘
弾性組成物の油面接着性や制振性等が不十分となる。
In the second invention, the acrylic monomer 1
When the copolymerization amount of the ethylene-butylene-based macromer and / or the ethylene-propylene-based macromer with respect to 00 parts by weight is less than 1 part by weight, the compatibility of the acrylic copolymer with the tackifying resin is not sufficiently improved, The obtained viscoelastic composition has insufficient oil surface adhesion and vibration damping properties.

【0028】逆にアクリル系モノマー100重量部に対
するエチレン−ブチレン系マクロマー及び/又はエチレ
ン−プロピレン系マクロマーの共重合量が100重量部
を超えると、アクリル系共重合体が硬くなって、得られ
る粘弾性組成物の接着性が低下する。
On the contrary, when the copolymerization amount of the ethylene-butylene macromer and / or the ethylene-propylene macromer with respect to 100 parts by weight of the acrylic monomer exceeds 100 parts by weight, the acrylic copolymer becomes hard and the obtained viscosity is increased. The adhesiveness of the elastic composition is reduced.

【0029】第1発明又は第2発明による粘弾性組成物
に用いられる粘着付与樹脂としては、特に限定されるも
のではないが、C5系(脂肪族系)石油樹脂、C9系
(芳香族系)石油樹脂等の石油系樹脂;水添ロジン樹
脂、水添ロジンエステル樹脂、不均化ロジン樹脂、不均
化ロジンエステル樹脂、重合ロジン樹脂、重合ロジンエ
ステル樹脂等のロジン系樹脂;水添テルペン樹脂、水添
テルペンフェノール樹脂等のテルペン系樹脂;水添クマ
ロンインデン樹脂等が挙げられ、好適に用いられるが、
なかでも不飽和結合の少ない粘着付与樹脂がより好適に
用いられる。
The tackifying resin used in the viscoelastic composition according to the first invention or the second invention is not particularly limited, but is C5 (aliphatic) petroleum resin, C9 (aromatic). Petroleum-based resins such as petroleum resins; hydrogenated rosin resins, hydrogenated rosin ester resins, disproportionated rosin resins, disproportionated rosin ester resins, polymerized rosin resins, polymerized rosin ester resins, and other rosin-based resins; hydrogenated terpene resins , Terpene-based resins such as hydrogenated terpene phenolic resin; hydrogenated coumarone indene resin and the like are preferably used.
Above all, a tackifying resin having less unsaturated bonds is more preferably used.

【0030】上記粘着付与樹脂は、単独で用いられても
良いし、2種類以上が併用されても良い。
The above tackifier resins may be used alone or in combination of two or more kinds.

【0031】第1発明による粘弾性組成物においては、
前述したアクリル系モノマーとエチレン−ブチレン系マ
クロマー及び/又はエチレン−プロピレン系マクロマー
とを共重合して得られるアクリル系共重合体と上記粘着
付与樹脂が含有されていれば良く、両者の含有割合は特
に限定されるものではない。
In the viscoelastic composition according to the first invention,
It is sufficient that the acrylic monomer and the acrylic copolymer obtained by copolymerizing the ethylene-butylene-based macromer and / or the ethylene-propylene-based macromer and the above tackifying resin are contained, and the content ratio of the two is the same. It is not particularly limited.

【0032】又、第2発明による粘弾性組成物において
は、前述したアクリル系モノマー100重量部とエチレ
ン−ブチレン系マクロマー及び/又はエチレン−プロピ
レン系マクロマー1〜100重量部とを共重合して得ら
れるアクリル系共重合体100重量部に対し、上記粘着
付与樹脂1〜50重量部、好ましくは10〜40重量
部、が含有されていることが必要である。
The viscoelastic composition according to the second aspect of the present invention is obtained by copolymerizing 100 parts by weight of the above-mentioned acrylic monomer with 1 to 100 parts by weight of ethylene-butylene macromer and / or ethylene-propylene macromer. It is necessary that the tackifying resin is contained in an amount of 1 to 50 parts by weight, preferably 10 to 40 parts by weight, based on 100 parts by weight of the acrylic copolymer.

【0033】上記アクリル系共重合体100重量部に対
する粘着付与樹脂の含有量が1重量部未満であると、得
られる粘弾性組成物の吸油性が不十分となるため、油面
接着性が十分に向上せず、逆にアクリル系共重合体10
0重量部に対する粘着付与樹脂の含有量が50重量部を
超えると、得られる粘弾性組成物の凝集力が低下して、
耐熱性が不十分となる。
If the content of the tackifying resin is less than 1 part by weight based on 100 parts by weight of the acrylic copolymer, the resulting viscoelastic composition will have insufficient oil absorbency, resulting in sufficient oil surface adhesion. Acrylic copolymer 10
When the content of the tackifying resin is more than 50 parts by weight based on 0 parts by weight, the cohesive force of the obtained viscoelastic composition decreases,
The heat resistance becomes insufficient.

【0034】第1発明又は第2発明による粘弾性組成物
は、表面濡れ指数が30dyn/cm以下であることが
必要である。
The viscoelastic composition according to the first or second invention is required to have a surface wetting index of 30 dyn / cm or less.

【0035】上記粘弾性組成物の表面濡れ指数が30d
yn/cmを超えると、接着性が不十分となる。
The surface wetting index of the viscoelastic composition is 30d.
If it exceeds yn / cm, the adhesiveness will be insufficient.

【0036】又、上記粘弾性組成物の表面濡れ指数は、
30dyn/cm以下で小さい方が好ましいが、現実的
には、材質面の制約があり、15dyn/cm未満とす
ることは困難である。
The surface wetting index of the above viscoelastic composition is
It is preferably as small as 30 dyn / cm or less, but in reality, there are restrictions on the material, and it is difficult to make it less than 15 dyn / cm.

【0037】上記粘弾性組成物の表面濡れ指数は、JI
S Z−1529「印刷用粘着フィルム」に規定されて
いるものであり、例えば、自動接触角計(例えば、型式
「G2」、KRUSS社製)を用い、接触角を測定する
ことにより求めることが出来る。
The surface wetting index of the above viscoelastic composition is JI
S Z-1529 "Adhesive film for printing", and can be determined by measuring the contact angle using, for example, an automatic contact angle meter (for example, model "G2", manufactured by KRUSS). I can.

【0038】第1発明又は第2発明による粘弾性組成物
には、本発明の課題達成を阻害しない範囲で必要に応じ
て、充填材、軟化剤、可塑剤、界面活性剤、安定剤、酸
化防止剤、紫外線吸収剤、顔料、染料、架橋剤、有機溶
剤等の各種添加剤の1種もしくは2種以上が含有されて
いても良い。
The viscoelastic composition according to the first invention or the second invention may contain a filler, a softening agent, a plasticizer, a surfactant, a stabilizer, and an oxidizer, if necessary, within a range not hindering the achievement of the object of the present invention. One or more kinds of various additives such as an inhibitor, an ultraviolet absorber, a pigment, a dye, a cross-linking agent and an organic solvent may be contained.

【0039】第1発明又は第2発明による粘弾性組成物
の製造方法は、特別なものではなく、予め、アクリル系
モノマーとエチレン−ブチレン系マクロマー及び/又は
エチレン−プロピレン系マクロマーとを共重合して得ら
れるアクリル系共重合体を前述した重合法のいずれかで
作製した後、ニーダー、プラネタリウムミキサー、バン
バリーミキサー、ロール等の通常の混合装置を使用し
て、常温もしくは加熱下で、必須成分である上記アクリ
ル系共重合体及び粘着付与樹脂、及び、必要に応じて含
有させる各種添加剤の1種もしくは2種以上からなる組
成物を、均一に攪拌混合して、所望の粘弾性組成物を得
れば良い。
The method for producing the viscoelastic composition according to the first or second invention is not special, and the acrylic monomer and the ethylene-butylene macromer and / or the ethylene-propylene macromer are copolymerized in advance. After producing the acrylic copolymer obtained by any of the above-mentioned polymerization methods, using a kneader, a planetarium mixer, a Banbury mixer, a usual mixing device such as a roll, at room temperature or under heating, as an essential component A composition comprising one of the above acrylic copolymer and tackifying resin, and one or two or more of various additives to be contained as necessary is uniformly stirred and mixed to obtain a desired viscoelastic composition. Get it.

【0040】又、上記アクリル系共重合体を光重合法で
作製する場合、アクリル系モノマー、エチレン−ブチレ
ン系マクロマー及び/又はエチレン−プロピレン系マク
ロマー、光重合触媒、粘着付与樹脂、及び、必要に応じ
て含有させる各種添加剤の1種もしくは2種以上からな
る組成物に、例えば、イナートゾーン中で、ケミカルラ
ンプ等を使用して光照射を行い、一挙に所望の粘弾性組
成物を得ても良い。
When the acrylic copolymer is prepared by a photopolymerization method, an acrylic monomer, an ethylene-butylene macromer and / or an ethylene-propylene macromer, a photopolymerization catalyst, a tackifying resin, and, if necessary, The composition containing one or two or more of various additives to be contained is irradiated with light using, for example, a chemical lamp in an inert zone to obtain a desired viscoelastic composition all at once. Is also good.

【0041】次に、第3発明による制振材は、第1発明
又は第2発明による上述の粘弾性組成物を用いて製せら
れていることを特徴とする。
Next, the vibration damping material according to the third aspect of the invention is characterized by being manufactured using the viscoelastic composition according to the first or second aspect of the invention.

【0042】上記制振材には、必須成分である第1発明
又は第2発明による粘弾性組成物以外に、本発明の課題
達成を阻害しない範囲で必要に応じて、制振を施す対象
材料の剛性と制振材の剛性を適合させたり、制振性を向
上させるために、充填材が含有されていても良い。
In the above-mentioned vibration damping material, in addition to the viscoelastic composition according to the first invention or the second invention, which is an essential component, the material to be subjected to vibration damping, if necessary, within the range not hindering the achievement of the object of the present invention. A filler may be contained in order to adapt the rigidity of the above to the rigidity of the vibration damping material or to improve the vibration damping property.

【0043】上記充填材としては、特に限定されるもの
ではないが、例えば、ガラスバルーン、アルミナバルー
ン、シラスバルーン、フライアッシュバルーン等の無機
系中空充填材;ガラスビーズ、シリカビーズ、シリカゲ
ル、アルミナシリカ、フライアッシュ、合成雲母等の無
機系充填材;珪藻土、多孔質シリカ等の多孔質充填材;
ポリメタクリル酸メチル、アクリロニトリル−塩化ビニ
リデン共重合体、ポリスチレン、フェノール樹脂等から
なる有機系中空充填材;ポリメタクリル酸メチルビー
ズ、ポリスチレンビーズ、スチレン−アクリル共重合体
ビーズ、ウレタンビーズ、シリコーンビーズ、ポリプロ
ピレンビーズ、エチレン−酢酸ビニル共重合体ビーズ、
ポリアクリル酸エチルビーズ等の有機系充填材;立方体
アルミナシリカ、ガラスフレーク、ガラス繊維、鎖状粘
土鉱物等が挙げられ、好適に用いられる。
The filler is not particularly limited, but examples thereof include inorganic hollow fillers such as glass balloons, alumina balloons, shirasu balloons and fly ash balloons; glass beads, silica beads, silica gel, alumina silica. , Inorganic fillers such as fly ash and synthetic mica; porous fillers such as diatomaceous earth and porous silica;
Organic hollow fillers composed of polymethylmethacrylate, acrylonitrile-vinylidene chloride copolymer, polystyrene, phenolic resin, etc .; polymethylmethacrylate beads, polystyrene beads, styrene-acrylic copolymer beads, urethane beads, silicone beads, polypropylene Beads, ethylene-vinyl acetate copolymer beads,
Organic fillers such as polyacrylic acid ethyl beads; cubic alumina silica, glass flakes, glass fibers, chain clay minerals and the like can be mentioned and preferably used.

【0044】上記充填材は、単独で用いられても良い
し、2種類以上が併用されても良い。
The above-mentioned fillers may be used alone or in combination of two or more kinds.

【0045】又、第3発明による制振材は、凝集力を上
げて、耐クリープ性や耐熱性等を向上させるために、ア
クリル系モノマーとエチレン−ブチレン系マクロマー及
び/又はエチレン−プロピレン系マクロマーとの共重合
時に予め架橋処理が施されたアクリル系共重合体を用い
ても良いし、又、制振材の成形時に架橋処理が施されて
いても良い。
The vibration damping material according to the third aspect of the present invention comprises an acrylic monomer and an ethylene-butylene macromer and / or an ethylene-propylene macromer in order to increase cohesive force and improve creep resistance and heat resistance. An acrylic copolymer which has been previously subjected to a crosslinking treatment during the copolymerization with may be used, or a crosslinking treatment may be performed during the molding of the vibration damping material.

【0046】第3発明による制振材の成形方法は、特別
なものではなく、必須成分である前記粘弾性組成物と、
必要に応じて含有させる上記充填材の1種もしくは2種
以上とからなる混合組成物を、押出し成形法、プレス成
形法等の成形法を採用して、常法により成形し、所望の
制振材を得れば良い。
The method for molding the vibration damping material according to the third aspect of the invention is not a special one, but the viscoelastic composition as an essential component,
A mixed composition comprising one or more of the above-mentioned fillers to be contained as necessary is molded by a conventional method using a molding method such as an extrusion molding method or a press molding method, and the desired vibration damping is performed. All you have to do is get the materials.

【0047】又、粘弾性組成物を構成する前記アクリル
系共重合体を光重合法で作製する場合、アクリル系モノ
マー、エチレン−ブチレン系マクロマー及び/又はエチ
レン−プロピレン系マクロマー、光重合触媒、粘着付与
樹脂、及び、必要に応じて含有させる上記充填材の1種
もしくは2種以上、並びに、必要に応じて含有させる前
記各種添加剤の1種もしくは2種以上からなる組成物
を、例えば、離型紙上に所望の厚みで塗布し、イナート
ゾーン中で、ケミカルランプ等を使用して光照射を行
い、一挙に所望の制振材を得ても良い。
When the acrylic copolymer constituting the viscoelastic composition is prepared by a photopolymerization method, an acrylic monomer, ethylene-butylene macromer and / or ethylene-propylene macromer, photopolymerization catalyst, adhesive A composition comprising an imparting resin and, if necessary, one or more kinds of the above-mentioned fillers, and one or more kinds of the above-mentioned various additives to be contained, if necessary, The desired damping material may be obtained all at once by applying a desired thickness on the pattern paper and performing light irradiation using a chemical lamp or the like in the inert zone.

【0048】[0048]

【作用】第1発明による粘弾性組成物は、アルキル基の
炭素数が特定されたアルキル(メタ)アクリレート及び
極性基含有ビニルモノマーからなるアクリル系モノマー
とエチレン−ブチレン系マクロマー及び/又はエチレン
−プロピレン系マクロマーとを共重合して得られるアク
リル系共重合体を主成分とするので、粘着付与樹脂との
相溶性が良くなり、吸油性が向上すると共に、表面濡れ
指数が特定されているので、優れた油面接着性を発揮
し、且つ、優れた制振性を有する。
The viscoelastic composition according to the first aspect of the present invention is an acrylic monomer composed of an alkyl (meth) acrylate having a carbon number of an alkyl group specified and a polar group-containing vinyl monomer, an ethylene-butylene macromer and / or ethylene-propylene. Since the main component is an acrylic copolymer obtained by copolymerizing a system macromer, the compatibility with the tackifying resin is improved, the oil absorption is improved, and the surface wetting index is specified. Exhibits excellent oil surface adhesion and has excellent vibration damping properties.

【0049】又、第2発明による粘弾性組成物は、上記
第1発明による粘弾性組成物において、アクリル系モノ
マーとエチレン−ブチレン系マクロマー及び/又はエチ
レン−プロピレン系マクロマーとの共重合割合が特定さ
れており、且つ、得られるアクリル系共重合体に対する
粘着付与樹脂の含有量が特定されているので、一段と優
れた油面接着性と制振性を兼備する。
The viscoelastic composition according to the second aspect of the present invention is the viscoelastic composition according to the first aspect, wherein the copolymerization ratio of the acrylic monomer and the ethylene-butylene macromer and / or the ethylene-propylene macromer is specified. In addition, since the content of the tackifying resin in the resulting acrylic copolymer is specified, it further has both excellent oil surface adhesiveness and vibration damping property.

【0050】さらに、第3発明による制振材は、上記第
1発明又は第2発明による粘弾性組成物を用いて製せら
れているので、優れた油面接着性と制振性を兼備する。
Furthermore, since the vibration damping material according to the third aspect of the present invention is manufactured using the viscoelastic composition according to the first aspect or the second aspect of the present invention, it has both excellent oil surface adhesiveness and vibration damping property. .

【0051】[0051]

【発明の実施の形態】本発明をさらに詳しく説明するた
め以下に実施例を挙げるが、本発明はこれら実施例に限
定されるものではない。尚、実施例中の「部」は「重量
部」を意味する。
BEST MODE FOR CARRYING OUT THE INVENTION The following examples are given to explain the present invention in more detail, but the present invention is not limited to these examples. In addition, "part" in an Example means a "weight part."

【0052】(実施例1)(Example 1)

【0053】(1)光重合性組成物の調製 セパラブルフラスコ中に、2−エチルヘキシルアクリレ
ート90部、アクリル酸10部、1,6−ヘキサンジオ
ールジアクリレート(HDDA)0.08部、エチレン
−ブチレン系マクロマー(商品名「KLP L−120
3」、油化シェル社製)10部、粘着付与樹脂(商品名
「スーパーエステルA140」、荒川化学工業社製)5
部及び光重合触媒(商品名「イルガキュアー651」、
チバガイギー社製)0.1部を投入し、均一に攪拌混合
した後、窒素ガスを30分間パージして系内の溶存酸素
を除去し、光重合性組成物を調製した。
(1) Preparation of Photopolymerizable Composition In a separable flask, 90 parts of 2-ethylhexyl acrylate, 10 parts of acrylic acid, 0.08 part of 1,6-hexanediol diacrylate (HDDA), ethylene-butylene were added. System macromer (trade name "KLP L-120
3 ", manufactured by Yuka Shell Co., Ltd., 10 parts, tackifying resin (trade name" Super Ester A140 ", manufactured by Arakawa Chemical Industry Co., Ltd.) 5
Part and photopolymerization catalyst (trade name "Irgacure 651",
0.1 part (manufactured by Ciba-Geigy Co., Ltd.) was added and uniformly stirred and mixed, and then nitrogen gas was purged for 30 minutes to remove dissolved oxygen in the system to prepare a photopolymerizable composition.

【0054】(2)粘弾性組成物の作製 上記で得られた光重合性組成物を、20℃に維持されて
いるステンレス板に密着させた表面離型性を有するポリ
エチレンテレフタレート(PET)フィルム(厚み50
μm)の離型面上に、塗布厚みが1.5mmとなるよう
に塗布し、その塗布面上に、表面離型性を有するPET
フィルム(厚み50μm)の離型面を積層した。次い
で、ケミカルランプを紫外線の光源として使用し、その
照射面の光強度が2mW/cm2 となるようにケミカル
ランプの高さを設定して、積層されたPETフィルム面
を通して10分間紫外線を照射し、光重合性組成物の光
重合を行って、シート状の粘弾性組成物を作製した。
尚、上記光強度は、波長365nmに最大感度を有する
光強度測定機(型式「UVR−1」、東京光学機械社
製)を用いて測定した光強度である。
(2) Preparation of viscoelastic composition A polyethylene terephthalate (PET) film having surface releasability was obtained by bringing the photopolymerizable composition obtained above into close contact with a stainless steel plate maintained at 20 ° C. Thickness 50
.mu.m) on the release surface so that the coating thickness is 1.5 mm, and PET having the surface release property on the application surface.
The release surfaces of the film (thickness 50 μm) were laminated. Then, the chemical lamp is used as a light source of ultraviolet rays, the height of the chemical lamp is set so that the light intensity of the irradiation surface becomes 2 mW / cm 2, and the ultraviolet rays are irradiated for 10 minutes through the laminated PET film surface. The photopolymerizable composition was photopolymerized to prepare a sheet-shaped viscoelastic composition.
The above-mentioned light intensity is the light intensity measured by using a light intensity measuring device (model “UVR-1”, manufactured by Tokyo Optical Machinery Co., Ltd.) having the maximum sensitivity at a wavelength of 365 nm.

【0055】上記で得られたシート状の粘弾性組成物の
表面濡れ指数を以下の方法で測定したところ、表面濡れ
指数は23.2dyn/cmであった。 〔表面濡れ指数の測定方法〕シート状の粘弾性組成物の
一方の面のPETフィルムを剥離した後、自動接触角計
(型式「G2」、KRUSS社製)を使用し、溶媒とし
て水、cis−ジヨードエチレン、1,1−ジヨードエ
タンを用いて、各々の接触角を測定した。次いで、ヤン
グ・デュプレー式により表面濡れ指数(dyn/cm)
を求めた。
The surface wetting index of the sheet-shaped viscoelastic composition obtained above was measured by the following method, and the surface wetting index was 23.2 dyn / cm. [Measuring Method of Surface Wetting Index] After peeling the PET film on one surface of the sheet-shaped viscoelastic composition, an automatic contact angle meter (model “G2”, manufactured by KRUSS) is used, and water and cis are used as a solvent. -The contact angle of each was measured using diiodoethylene and 1,1-diiodoethane. Next, surface wetting index (dyn / cm) by Young-Duprey formula
I asked.

【0056】(3)制振材の作製 上記で得られたシート状の粘弾性組成物をそのまま制振
材とした。
(3) Preparation of Damping Material The sheet-shaped viscoelastic composition obtained above was used as it was as a damping material.

【0057】(4)評価 上記で得られた制振材の性能(油面接着性、及び、
制振性)を以下の方法で評価した。その結果は表1に示
すとおりであった。尚、評価は、特に記載の無い限り、
23℃−65%RHの雰囲気下で行った。
(4) Evaluation The performance of the damping material obtained above (oil surface adhesion, and
Vibration damping property) was evaluated by the following method. The results are shown in Table 1. In addition, unless otherwise specified, the evaluation is
It was performed in an atmosphere of 23 ° C.-65% RH.

【0058】油面接着性 幅20mm×長さ80mmに裁断された制振材の一方の
面のPETフィルムを剥離した後、JIS H−400
0規定のアルミニウム箔(品番「1100P」、幅20
mm×長さ100mm×厚み0.05mm)を貼り付け
た。次に、予め塗布量6g/m2 で防錆油を塗布し、2
4時間放置して準備した被着体であるJIS H−40
00規定のアルミニウム板(品番「1100P」、幅5
0mm×長さ100mm×厚み2mm)の防錆油塗布面
上に、制振材の他方の面のPETフィルムを剥離して積
層し、2Kgの圧着ローラーを2往復させて接着し、測
定用試験片を作成した。次いで、引張り試験機を使用
し、引張り速度300mm/分の条件で、接着10分後
及び接着24時間後の測定用試験片の90度角剥離強度
(Kg/20mm)を測定した。
Oil surface adhesiveness After peeling off the PET film on one surface of the vibration damping material cut into a width of 20 mm and a length of 80 mm, JIS H-400 is used.
0 standard aluminum foil (Product number "1100P", width 20
(mm × length 100 mm × thickness 0.05 mm) was attached. Next, apply rust-preventive oil at a coating amount of 6 g / m 2 in advance and
JIS H-40 which is an adherend prepared by leaving it for 4 hours
00 standard aluminum plate (product number "1100P", width 5
On the rust-proof oil coated surface (0 mm x length 100 mm x thickness 2 mm), the PET film on the other side of the vibration damping material was peeled off and laminated, and a 2 Kg pressure roller was reciprocated twice to adhere, and a measurement test was performed. Created a piece. Then, using a tensile tester, the 90-degree angle peel strength (Kg / 20 mm) of the test piece for measurement 10 minutes after the adhesion and 24 hours after the adhesion was measured under the condition of the tension speed of 300 mm / min.

【0059】制振性 幅20mm×長さ200mmに裁断された制振材の一方
の面のPETフィルムを剥離した後、予め塗布量6g/
2 で防錆油を塗布して準備した被着体である鋼板(幅
20mm×長さ200mm×厚み1mm)の防錆油塗布
面上に積層し、2Kgの圧着ローラーを2往復させて接
着し、測定用試験片を作成した。次いで、24時間放置
後の測定用試験片をインパルスハンマー法により加振
し、共振周波数及び半値幅から対数減衰率を求めた。
Damping property After the PET film on one surface of the damping material cut to a width of 20 mm and a length of 200 mm was peeled off, the coating amount was 6 g /
Laminated on the surface of the steel plate (width 20 mm x length 200 mm x thickness 1 mm), which is the adherend prepared by applying rust preventive oil at m 2 , and adhering by reciprocating the 2 Kg pressure roller twice. Then, a test piece for measurement was prepared. Then, the test piece for measurement after standing for 24 hours was vibrated by the impulse hammer method, and the logarithmic attenuation rate was obtained from the resonance frequency and the half value width.

【0060】(実施例2〜4、及び、比較例1〜3)表
1に示すような配合組成で、実施例1と同様にして、6
種類の光重合性組成物を調製した。次に、得られた6種
類の光重合性組成物を用い、実施例1と同様にして、6
種類のシート状の粘弾性組成物を作製した。得られた6
種類の粘弾性組成物の表面濡れ指数を実施例1と同様に
して測定したところ、表1に示すような結果であった。
(Examples 2 to 4 and Comparative Examples 1 to 3) The composition was as shown in Table 1 in the same manner as in Example 1 and 6
A variety of photopolymerizable compositions were prepared. Next, using 6 kinds of the obtained photopolymerizable compositions, in the same manner as in Example 1, 6
Various types of sheet-shaped viscoelastic compositions were prepared. Obtained 6
The surface wetting index of each type of viscoelastic composition was measured in the same manner as in Example 1, and the results are shown in Table 1.

【0061】次いで、上記で得られた6種類のシート状
の粘弾性組成物をそのまま制振材として用い、その性能
を実施例1と同様にして評価した。その結果は表1に示
すとおりであった。
Then, the six types of sheet-like viscoelastic compositions obtained above were used as they were as a damping material, and the performance was evaluated in the same manner as in Example 1. The results are shown in Table 1.

【0062】[0062]

【表1】 [Table 1]

【0063】表1に示されるように、本発明による実施
例1〜4の制振材(粘弾性組成物)は、初期(接着10
分後)及び経時後(接着24時間後)のいずれにおいて
も優れた油面接着性を発揮し、且つ、制振性も優れてい
る。
As shown in Table 1, the damping materials (viscoelastic compositions) of Examples 1 to 4 according to the present invention were initially (adhesive 10).
Both after (minutes) and after lapse of time (24 hours after adhesion), excellent oil surface adhesion is exhibited and vibration damping properties are also excellent.

【0064】これに対し、比較例1〜3の制振材(粘弾
性組成物)は、制振性については実施例1〜4の制振材
と比較しても遜色ないが、初期(接着10分後)及び経
時後(接着24時間後)の油面接着性が悪いことがわか
る。
On the other hand, the vibration damping materials (viscoelastic compositions) of Comparative Examples 1 to 3 are comparable in vibration damping property to the vibration damping materials of Examples 1 to 4, but the initial (adhesion It can be seen that the oil surface adhesiveness is poor after 10 minutes) and after lapse of time (24 hours after adhesion).

【0065】[0065]

【発明の効果】以上述べたように、第1発明又は第2発
明による粘弾性組成物は、優れた油面接着性と制振性を
兼備するので、制振材等として好適に用いられる。
As described above, the viscoelastic composition according to the first invention or the second invention has both excellent oil surface adhesiveness and vibration damping property, and thus is suitably used as a vibration damping material or the like.

【0066】又、第3発明による制振材は、優れた油面
接着性を発揮するので、予め被着体表面を清浄化した
り、別の接着剤を併用したりする必要がなく、作業性に
優れると共に、制振性も優れているので、自動車、機械
器具、船舶、建築材料、音響材料等、各種用途の制振材
として好適に用いられる。
Further, since the vibration damping material according to the third aspect of the present invention exhibits excellent oil surface adhesiveness, it is not necessary to clean the surface of the adherend in advance or to use another adhesive in combination, and workability is improved. In addition to being excellent in vibration damping property, it is suitably used as a vibration damping material for various applications such as automobiles, machinery and equipment, ships, building materials, acoustic materials and the like.

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭59−38053(JP,A) 特開 平6−100756(JP,A) 特開 平8−209099(JP,A) 特開 平3−200886(JP,A) 特開 平5−194929(JP,A) 特開 平7−173436(JP,A) 特開 平10−183092(JP,A) (58)調査した分野(Int.Cl.7,DB名) C08L 1/00 - 101/16 F16F 15/02 G10K 11/16 G10K 11/162 C08F 290/00 - 290/14 C08F 299/00 - 299/08 ─────────────────────────────────────────────────── ─── Continuation of the front page (56) Reference JP-A-59-38053 (JP, A) JP-A-6-100756 (JP, A) JP-A-8-209099 (JP, A) JP-A-3- 200886 (JP, A) JP 5-194929 (JP, A) JP 7-173436 (JP, A) JP 10-183092 (JP, A) (58) Fields investigated (Int.Cl. 7 , DB name) C08L 1/00-101/16 F16F 15/02 G10K 11/16 G10K 11/162 C08F 290/00-290/14 C08F 299/00-299/08

Claims (3)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 アルキル基の炭素数が2〜14のアルキ
ル(メタ)アクリレート及び該アルキル(メタ)アクリ
レートと共重合可能な極性基含有ビニルモノマーからな
るアクリル系モノマーとエチレン−ブチレン系マクロマ
ー及び/又はエチレン−プロピレン系マクロマーとを共
重合して得られるアクリル系共重合体、及び、粘着付与
樹脂を含有してなり、且つ、表面濡れ指数が30dyn
/cm以下であることを特徴とする粘弾性組成物。
1. An acrylic monomer comprising an alkyl (meth) acrylate having an alkyl group having 2 to 14 carbon atoms and a polar group-containing vinyl monomer copolymerizable with the alkyl (meth) acrylate, an ethylene-butylene macromer, and / or Alternatively, it contains an acrylic copolymer obtained by copolymerizing an ethylene-propylene macromer and a tackifying resin, and has a surface wetting index of 30 dyn.
/ Cm or less, The viscoelastic composition characterized by the above-mentioned.
【請求項2】 アクリル系共重合体が、アルキル基の炭
素数が2〜14のアルキル(メタ)アクリレート70〜
99.5重量%及び該アルキル(メタ)アクリレートと
共重合可能な極性基含有ビニルモノマー30〜0.5重
量%からなるアクリル系モノマー100重量部とエチレ
ン−ブチレン系マクロマー及び/又はエチレン−プロピ
レン系マクロマー1〜100重量部とを共重合して得ら
れるアクリル系共重合体であり、且つ、上記アクリル系
共重合体100重量部に対し、粘着付与樹脂1〜50重
量部が含有されていることを特徴とする請求項1記載の
粘弾性組成物。
2. The acrylic copolymer is an alkyl (meth) acrylate having an alkyl group having 2 to 14 carbon atoms,
100 parts by weight of an acrylic monomer consisting of 99.5% by weight and 30 to 0.5% by weight of a polar group-containing vinyl monomer copolymerizable with the alkyl (meth) acrylate, and an ethylene-butylene macromer and / or an ethylene-propylene system. It is an acrylic copolymer obtained by copolymerizing 1 to 100 parts by weight of a macromer, and contains 1 to 50 parts by weight of a tackifying resin with respect to 100 parts by weight of the above acrylic copolymer. The viscoelastic composition according to claim 1, wherein
【請求項3】 請求項1又は請求項2記載の粘弾性組成
物を用いて製せられていることを特徴とする制振材。
3. A vibration damping material, characterized by being produced using the viscoelastic composition according to claim 1.
JP01650397A 1997-01-30 1997-01-30 Viscoelastic composition and damping material Expired - Fee Related JP3447189B2 (en)