JP3424521B2 - Diffraction grating pattern transfer foil - Google Patents
Diffraction grating pattern transfer foilInfo
- Publication number
- JP3424521B2 JP3424521B2 JP25360297A JP25360297A JP3424521B2 JP 3424521 B2 JP3424521 B2 JP 3424521B2 JP 25360297 A JP25360297 A JP 25360297A JP 25360297 A JP25360297 A JP 25360297A JP 3424521 B2 JP3424521 B2 JP 3424521B2
- Authority
- JP
- Japan
- Prior art keywords
- diffraction grating
- transparent
- layer
- opaque
- grating pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えばクレジット
カード、パスポート、有価証券などに転写される回折格
子パターン転写箔に係わり、特に透明回折格子パターン
と不透明回折格子パターンとを重ね合わせて複雑なパタ
ーンを表示することにより、偽造防止性及び装飾性を向
上し得る回折格子パターン転写箔に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a diffraction grating pattern transfer foil which is transferred to, for example, a credit card, a passport, securities, and the like, and in particular, a transparent diffraction pattern and an opaque diffraction pattern are superposed to form a complicated pattern. The present invention relates to a diffraction grating pattern transfer foil capable of improving anti-counterfeiting property and decorative property by displaying.
【０００２】[0002]
【従来の技術】近年、光の干渉を用いて立体画像を再生
し得る回折格子パターンの開発が進められている。この
回折格子パターンは高度な製造技術を要し、且つ箔状に
形成可能なことから、偽造防止手段としてクレジットカ
ード、有価証券、証明書等の一部に貼着して使用されて
いる。そして、回折格子パターンをこれらの物品に貼着
するための方法として従来から回折格子パターン転写箔
を用いて回折格子パターンを転写する方法が用いられて
いる。2. Description of the Related Art In recent years, development of a diffraction grating pattern capable of reproducing a stereoscopic image by using light interference has been advanced. Since this diffraction grating pattern requires a high-level manufacturing technique and can be formed into a foil shape, it is used by being attached to a part of a credit card, a securities, a certificate, etc. as a forgery preventing means. Then, as a method for attaching the diffraction grating pattern to these articles, a method of transferring the diffraction grating pattern using a diffraction grating pattern transfer foil has been conventionally used.
【０００３】図９はこの種の回折格子パターン転写箔の
一例の構成を示す断面図である。この回折格子パターン
転写箔は、支持体としての基材（１）上に透明剥離性保
護膜層（２）が形成され、透明剥離性保護膜層（２）上
に透明回折格子形成層（３）が形成されている。透明回
折格子形成層（３）上に、この透明回折格子形成層とは
異なる屈折率をもつ透明薄膜層（４）、及び透明接着層
（６）が形成されている。この図９に示す回折格子パタ
ーン転写箔が使用される際には、例えば、予め文字、絵
柄などが印刷されたクレジットカード、パスポート、有
価証券などに転写され、基材（１）が剥離された状態の
ものとなる。FIG. 9 is a sectional view showing the structure of an example of this type of diffraction grating pattern transfer foil. In this diffraction grating pattern transfer foil, a transparent peelable protective film layer (2) is formed on a base material (1) as a support, and a transparent diffraction grating forming layer (3) is formed on the transparent peelable protective film layer (2). ) Has been formed. A transparent thin film layer (4) having a refractive index different from that of the transparent diffraction grating forming layer (3) and a transparent adhesive layer (6) are formed on the transparent diffraction grating forming layer (3). When the diffraction grating pattern transfer foil shown in FIG. 9 is used, it is transferred to, for example, a credit card, passport, securities, etc. on which characters, patterns, etc. are printed in advance, and the base material (1) is peeled off. It will be in the state.
【０００４】このような回折格子パターンは、入射光の
一部分が反射する方向へ回折光パターンを発生させ、入
射光の大部分が透明剥離性保護膜層（２）、透明回折格
子形成層（３）、透明薄膜層（４）、及び透明接着層
（６）を透過してしまう為に、透明感のある回折格子パ
ターンとなっている。このような透明感のある回折格子
パターンを透明回折格子パターンと称している。Such a diffraction grating pattern generates a diffracted light pattern in a direction in which a part of the incident light is reflected, and most of the incident light is a transparent peelable protective film layer (2) and a transparent diffraction grating forming layer (3). ), The transparent thin film layer (4), and the transparent adhesive layer (6) are transmitted, so that the diffraction grating pattern has a transparent feeling. Such a transparent diffraction grating pattern is called a transparent diffraction grating pattern.
【０００５】この透明回折格子パターンは、透明感があ
るために、例えば、クレジットカード、パスポート、有
価証券などに使用した際には、クレジットカード、パス
ポート、有価証券などに予め印刷された文字、絵柄など
の印刷内容と回折格子パターンの表示内容との両者を視
認することが可能となるものである。Since this transparent diffraction grating pattern has a sense of transparency, when it is used in a credit card, passport, securities, etc., for example, characters and patterns printed in advance on the credit card, passport, securities, etc. It is possible to visually recognize both the printed contents such as the above and the displayed contents of the diffraction grating pattern.
【０００６】一方、図１０はこの種の回折格子パターン
転写箔の他の一例の構成を示す断面図である。この回折
格子パターン転写箔は、支持体としての基材（４１）上
に透明剥離性保護膜層（４２）が形成され、透明剥離性
保護膜層（４２）上に透明回折格子形成層（４３）が形
成されている。透明回折格子形成層（４３）上に、反射
性不透明薄膜層（４７）、及び接着層（４６）が形成さ
れている。この図１０に示す回折格子パターン転写箔が
使用される際には、例えば、予め文字、絵柄などが印刷
されたクレジットカード、パスポート、有価証券などに
転写され、基材（４１）が剥離された状態のものとな
る。On the other hand, FIG. 10 is a sectional view showing the structure of another example of this type of diffraction grating pattern transfer foil. In this diffraction grating pattern transfer foil, a transparent peelable protective film layer (42) is formed on a base material (41) as a support, and a transparent diffraction grating forming layer (43) is formed on the transparent peelable protective film layer (42). ) Has been formed. A reflective opaque thin film layer (47) and an adhesive layer (46) are formed on the transparent diffraction grating forming layer (43). When the diffraction grating pattern transfer foil shown in FIG. 10 is used, it is transferred to, for example, a credit card, passport, securities, etc. on which characters and pictures are printed in advance, and the base material (41) is peeled off. It will be in the state.
【０００７】このような回折格子パターンは、入射光の
一部分が反射する方向へ回折光パターンを発生させ、入
射光の大部分が反射性不透明薄膜層（４７）により反射
されてしまい、入射光は殆ど透過しない為に、不透明感
のある回折格子パターンとなっている。このような不透
明感のある回折格子パターンを不透明回折格子パターン
と称している。Such a diffraction grating pattern generates a diffracted light pattern in the direction in which a part of the incident light is reflected, and most of the incident light is reflected by the reflective opaque thin film layer (47), so that the incident light is Since it hardly transmits light, it has an opaque diffraction grating pattern. Such an opaque diffraction grating pattern is called an opaque diffraction grating pattern.
【０００８】この不透明回折格子パターンは、不透明で
あるために、例えば、クレジットカード、パスポート、
有価証券などに使用した際には、この不透明回折格子パ
ターンが転写された箇所の、クレジットカード、パスポ
ート、有価証券などに予め印刷された文字、絵柄などの
印刷内容は視認することが不可能となり、この箇所は回
折格子パターンの表示内容のみが視認することが可能と
なるものである。Since the opaque diffraction grating pattern is opaque, for example, a credit card, a passport,
When used for securities, etc., the printed contents such as letters and patterns printed on credit cards, passports, securities, etc. at the location where this opaque diffraction grating pattern is transferred are not visible. At this point, only the display content of the diffraction grating pattern can be visually recognized.
【０００９】これら透明回折格子パターン及び不透明回
折格子パターンが、例えば、クレジットカード、パスポ
ート、有価証券などに使用される際には、クレジットカ
ード、パスポート、有価証券などの上に透明回折格子パ
ターン箔を転写し、或いは不透明回折格子パターン箔を
転写するものであって、透明回折格子パターン或いは不
透明回折格子パターン各々が単独で使用されているもの
である。When these transparent diffraction grating pattern and opaque diffraction grating pattern are used in, for example, credit cards, passports, securities, etc., a transparent diffraction grating pattern foil is placed on credit cards, passports, securities, etc. Transfer or transfer of an opaque diffraction grating pattern foil, wherein each transparent diffraction grating pattern or opaque diffraction grating pattern is used alone.
【００１０】このような使用方法は、これら透明回折格
子パターン及び不透明回折格子パターンの製造には高度
な製造技術を要することからして、クレジットカード、
パスポート、有価証券などの偽造防止手段として有用な
ものとなっている。また、装飾性を向上する手段として
有用なものとなっている。Such a method of use requires a high-level manufacturing technique for manufacturing the transparent diffraction grating pattern and the opaque diffraction grating pattern.
It has become a useful tool for preventing forgery of passports and securities. It is also useful as a means for improving decorativeness.
【００１１】[0011]
【発明が解決しようとする課題】本発明においては、こ
のようなクレジットカード、パスポート、有価証券など
の偽造防止手段としての回折格子パターンの偽造防止性
及び装飾性を、更に一段と向上させた回折格子パターン
箔を提供することを目的とするものである。また、偽造
防止性及び装飾性を、更に一段と向上させた回折格子パ
ターン箔をクレジットカード、パスポート、有価証券な
どに転写する際に、転写工程を増やすことなく使用する
ことの出来る転写箔を提供することを目的とするもので
ある。DISCLOSURE OF THE INVENTION In the present invention, a diffraction grating having further improved anti-counterfeiting property and decorative property of a diffraction grating pattern as a means for preventing forgery of such credit cards, passports, securities, etc. It is intended to provide a patterned foil. Further, the present invention provides a transfer foil that can be used without increasing the number of transfer steps when transferring a diffraction grating pattern foil having improved anti-counterfeiting property and decorative property to a credit card, passport, securities, etc. That is the purpose.
【００１２】[0012]
【課題を解決するための手段】本発明の請求項１の発明
は、支持体上の片面に少なくとも、（ａ）透明剥離性保
護膜層、（ｂ）回折格子パタ−ンを有する透明回折格子
形成層、（ｃ）この透明回折格子形成層とは異なる屈折
率をもつ透明薄膜層、（ｄ）透明接着層、反射性不透明
薄膜層、回折格子形成層、剥離性保護膜層の順に順次積
層して形成され回折格子パタ−ンを有する不透明回折格
子層、（ｅ）透明接着層を順次積層したことを特徴とす
る回折格子パタ−ン転写箔である。According to a first aspect of the present invention, a transparent diffraction grating having at least (a) a transparent peelable protective film layer and (b) a diffraction grating pattern on one surface of a support. Forming layer, (c) a transparent thin film layer having a refractive index different from that of the transparent diffraction grating forming layer, (d) a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer, and a peelable protective film layer in this order. An opaque diffraction grating layer having a diffraction grating pattern formed as described above, and (e) a transparent adhesive layer are sequentially laminated, which is a diffraction grating pattern transfer foil.
【００１３】また、本発明の請求項２の発明は、支持体
上の片面に少なくとも、（ａ）透明剥離性保護膜層、
（ｂ）透明接着層、反射性不透明薄膜層、回折格子形成
層、剥離性保護膜層の順に順次積層して形成され回格子
パターンを有する不透明回折格子層、（ｃ）回折格子パ
ターンを有する透明回折格子形成層、（ｄ）この透明回
折格子形成層とは異なる屈折率をもつ透明薄膜層、
（ｅ）透明接着層を順次積層したことを特徴とする回折
格子パターン転写箔である。Further, the invention of claim 2 of the present invention comprises at least (a) a transparent peelable protective film layer on one surface of a support,
(B) An opaque diffraction grating layer having a diffraction grating pattern formed by sequentially laminating a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer, and a peelable protective film layer, and (c) a transparent having a diffraction grating pattern. A diffraction grating forming layer, (d) a transparent thin film layer having a refractive index different from that of the transparent diffraction grating forming layer,
(E) A diffraction grating pattern transfer foil, wherein transparent adhesive layers are sequentially laminated.
【００１４】また、本発明の請求項３の発明は、支持体
上の片面に少なくとも、（ａ）透明剥離性保護膜層、
（ｂ）透明接着層、反射性不透明薄膜層、回折格子形成
層、剥離性保護膜層の順に順次積層して形成され回格子
パターンを有する第一不透明回折格子層、（ｃ）回折格
子パターンを有する透明回折格子形成層、（ｄ）この透
明回折格子形成層とは異なる屈折率をもつ透明薄膜層、
（ｅ）透明接着層、反射性不透明薄膜層、回折格子形成
層、剥離性保護膜層の順に順次積層して形成され回格子
パターンを有する第二不透明回折格子層、（ｆ）透明接
着層を順次積層してなり、前記第一不透明回折格子層及
び前記第二不透明回折格子層の面積を前記透明回折格子
形成層の面積より小さく形成したことを特徴とする回折
格子パターン転写箔である。Further, the invention of claim 3 of the present invention comprises at least (a) a transparent peelable protective film layer on one surface of a support,
(B) a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer, and a peelable protective film layer, which are sequentially laminated in this order to form a first opaque diffraction grating layer having a diffraction grating pattern, and (c) a diffraction grating pattern. A transparent diffraction grating forming layer having (d) a transparent thin film layer having a refractive index different from that of the transparent diffraction grating forming layer,
(E) a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer, a peelable protective film layer, and a second opaque diffraction grating layer formed in this order and having a diffraction grating pattern, and (f) a transparent adhesive layer. The diffraction grating pattern transfer foil is characterized in that the first opaque diffraction grating layer and the second opaque diffraction grating layer are sequentially laminated and have an area smaller than that of the transparent diffraction grating forming layer.
【００１５】また、本発明の請求項４の発明は、上記請
求項１の発明の回折格子パターン転写箔において、前記
不透明回折格子層の面積を前記透明回折格子形成層の面
積より小さく形成したことを特徴とする回折格子パター
ン転写箔である。According to a fourth aspect of the present invention, in the diffraction grating pattern transfer foil according to the first aspect of the present invention, the area of the opaque diffraction grating layer is smaller than the area of the transparent diffraction grating forming layer. Is a diffraction grating pattern transfer foil.
【００１６】また、本発明の請求項５の発明は、上記請
求項２の発明の回折格子パターン転写箔において、前記
不透明回折格子層の面積を前記透明回折格子形成層の面
積より小さく形成したことを特徴とする回折格子パター
ン転写箔である。According to a fifth aspect of the present invention, in the diffraction grating pattern transfer foil according to the second aspect of the invention, the area of the opaque diffraction grating layer is smaller than the area of the transparent diffraction grating forming layer. Is a diffraction grating pattern transfer foil.
【００１７】[0017]
【発明の実施の形態】以下に本発明による回折格子パタ
ーン転写箔を、その一実施形態に基づいて説明する。図
１は、本発明による回折格子パターン転写箔の一実施例
の構成を示す断面図である。図１に示すように、回折格
子パターン転写箔は、支持体としての基材（１１）の上
に透明剥離性保護膜層（１２）が形成され、透明剥離性
保護膜層（１２）の上には透明回折格子形成層（１３）
が形成され、透明回折格子形成層（１３）の上には透明
回折格子形成層とは異なる屈折率をもつ透明薄膜層（１
４）が形成され、更に透明薄膜層（１４）の上には不透
明回折格子層（１５）及び透明接着層（１６）が形成さ
れている。透明薄膜層（１４）の上に形成されている不
透明回折格子層（１５）の面積は、透明回折格子形成層
（１３）の面積より小さなものとなっている。BEST MODE FOR CARRYING OUT THE INVENTION A diffraction grating pattern transfer foil according to the present invention will be described below based on one embodiment thereof. FIG. 1 is a sectional view showing the structure of an embodiment of a diffraction grating pattern transfer foil according to the present invention. As shown in FIG. 1, in the diffraction grating pattern transfer foil, a transparent peelable protective film layer (12) is formed on a base material (11) as a support, and a transparent peelable protective film layer (12) is formed. A transparent diffraction grating forming layer (13)
And a transparent thin film layer (1) having a refractive index different from that of the transparent diffraction grating forming layer (1) is formed on the transparent diffraction grating forming layer (13).
4) is formed, and an opaque diffraction grating layer (15) and a transparent adhesive layer (16) are further formed on the transparent thin film layer (14). The area of the opaque diffraction grating layer (15) formed on the transparent thin film layer (14) is smaller than the area of the transparent diffraction grating forming layer (13).
【００１８】また、図４は、図１において透明薄膜層
（１４）の上に形成される不透明回折格子層（１５）の
構成を拡大して示す断面図である。図４に示すように、
不透明回折格子層（１５）は図４の上方より透明接着層
（３６）、反射性不透明薄膜層（３４）、回折格子形成
層（３３）、剥離性保護膜層（３２）の順に順次積層し
て形成されている。FIG. 4 is an enlarged sectional view showing the structure of the opaque diffraction grating layer (15) formed on the transparent thin film layer (14) in FIG. As shown in FIG.
The opaque diffraction grating layer (15) is formed by sequentially stacking the transparent adhesive layer (36), the reflective opaque thin film layer (34), the diffraction grating forming layer (33) and the peelable protective film layer (32) in this order from the top of FIG. Is formed.
【００１９】この不透明回折格子層（１５）は図４、及
び図１に示すように、不透明回折格子層（１５）の上方
にある透明接着層（３６）側の面を透明薄膜層（１４）
に接して、本発明による回折格子パターン転写箔を形成
している。また、図５は、図４に示す不透明回折格子層
（１５）が図１の透明薄膜層（１４）の上に転写して形
成される前の、基材（３１）に支持された不透明回折格
子箔の構成を拡大して示す断面図である。As shown in FIG. 4 and FIG. 1, the opaque diffraction grating layer (15) has a transparent thin film layer (14) on the surface on the side of the transparent adhesive layer (36) above the opaque diffraction grating layer (15).
To form a diffraction grating pattern transfer foil according to the present invention. In addition, FIG. 5 shows that the opaque diffraction grating layer (15) shown in FIG. 4 is transferred onto the transparent thin film layer (14) of FIG. It is sectional drawing which expands and shows the structure of a lattice foil.
【００２０】本発明による回折格子パターン転写箔は上
記のような構成であるので、例えばクレジットカード、
パスポート、有価証券などに転写された際の回折格子パ
ターンは、その全面積が透明感のある前記透明回折格子
パターンであり、また、透明回折格子形成層より小さな
面積の不透明回折格子は、不透明感のある前記不透明回
折格子パターンであり、また、部分的に２種の回折格子
パターンが層状に組み合わされたものとなっている。Since the diffraction grating pattern transfer foil according to the present invention has the above-mentioned structure, for example, a credit card,
The diffraction grating pattern when transferred to a passport, securities, etc. is the above-mentioned transparent diffraction grating pattern that has a transparent feeling in its entire area, and an opaque diffraction grating having an area smaller than the transparent diffraction grating forming layer has an opaque feeling. The above-mentioned opaque diffraction grating pattern is provided, and two kinds of diffraction grating patterns are partially combined in a layered form.
【００２１】図６は、図１に示すような構成による回折
格子パターン転写箔を、例えばクレジットカードや有価
証券などに使用した際の視認状態を説明する平面図であ
る。図６において、この全面積がクレジットカード、パ
スポート、有価証券など（５１）であり、その上の全面
積に図１に示す回折格子パターン転写箔の基材（１１）
が剥離されて転写されいる。５２はクレジットカード、
パスポート、有価証券（５１）などに予め印刷された文
字、絵柄などを示すものであり、５３は透明回折格子パ
ターン、５５は不透明回折格子パターンの視認状態を示
している。FIG. 6 is a plan view for explaining a visually recognized state when the diffraction grating pattern transfer foil having the structure shown in FIG. 1 is used for, for example, a credit card or securities. In FIG. 6, this entire area is a credit card, passport, securities, etc. (51), and the entire area above it is the base material (11) of the diffraction grating pattern transfer foil shown in FIG.
Is peeled off and transferred. 52 is a credit card,
Characters and pictures printed in advance on a passport, securities (51), etc. are shown, 53 is a transparent diffraction grating pattern, and 55 is an opaque diffraction grating pattern.
【００２２】図６において、クレジットカード、パスポ
ート、有価証券（５１）などに予め印刷された文字、絵
柄（５２）などは鮮明に視認され可読されるものであ
り、また、透明回折格子パターン（５３）はその全面積
において、そのパターンが視認され、また、不透明回折
格子パターン（５５）は不透明回折格子層が形成された
その箇所において、そのパターンが視認されるものであ
る。更に、この不透明回折格子層が形成されたその箇所
においては、不透明回折格子パターン（５５）と透明回
折格子パターン（５３）が重なった状態で視認されるも
のである。In FIG. 6, characters, patterns (52), etc. preprinted on credit cards, passports, securities (51), etc. are clearly visible and readable, and a transparent diffraction grating pattern (53). ) Shows the pattern in the entire area, and the opaque diffraction grating pattern (55) shows the pattern in the place where the opaque diffraction grating layer is formed. Further, at the place where the opaque diffraction grating layer is formed, the opaque diffraction grating pattern (55) and the transparent diffraction grating pattern (53) are visually recognized in an overlapping state.
【００２３】上記のように、本発明による回折格子パタ
ーン転写箔による回折格子パターンは、例えばクレジッ
トカード、パスポート、有価証券などに使用した際に
は、クレジットカード、パスポート、有価証券などに予
め印刷された、例えば文字、絵柄などの印刷内容と、透
明回折格子パターンの表示内容と、不透明回折格子パタ
ーンの表示内容と、更に不透明回折格子パターンと透明
回折格子パターンが重なった状態とが視認可能となる複
雑なパターンを表示することになるものであり、クレジ
ットカード、パスポート、有価証券などの偽造防止性を
更に一段と向上させたものとなる。また、クレジットカ
ード、パスポート、有価証券などの装飾性を更に一段と
向上させたものとなる。As described above, when the diffraction grating pattern transfer foil according to the present invention is used for a credit card, passport, securities, etc., it is printed in advance on the credit card, passport, securities, etc. Further, for example, it is possible to visually recognize the print contents such as characters and patterns, the display contents of the transparent diffraction grating pattern, the display contents of the opaque diffraction grating pattern, and the overlapping state of the opaque diffraction grating pattern and the transparent diffraction grating pattern. Since the complicated pattern is displayed, the anti-counterfeit property of credit cards, passports, securities, etc. is further improved. In addition, the decorativeness of credit cards, passports, securities, etc. will be further improved.
【００２４】上記のように、本発明による回折格子パタ
ーン転写箔を使用したクレジットカード、パスポート、
有価証券などは、その偽造防止性及び装飾性を更に一段
と向上させたものであるが、図２及び図３は本発明によ
る他の実施例における構成を示す断面図である。ここに
おいて、透明回折格子形成層、透明薄膜層と、不透明回
折格子層の積層の順序、及び不透明回折格子層の数を、
図２及び図３に示すようにすることにより、同様な目的
を達成させるものとなっている。As described above, a credit card, passport, or the like using the diffraction grating pattern transfer foil according to the present invention,
Securities have improved anti-counterfeiting properties and decorative properties, and FIGS. 2 and 3 are cross-sectional views showing the configuration of another embodiment according to the present invention. Here, the order of stacking the transparent diffraction grating forming layer, the transparent thin film layer, and the opaque diffraction grating layer, and the number of the opaque diffraction grating layers are
2 and 3, the same purpose is achieved.
【００２５】なお、図１、図２、及び図３の何れにおい
ても、不透明回折格子層（１５、２５、３５）の個数、
箇所などは、例えば、一枚のクレジットカード、パスポ
ート、有価証券などにおいて特に制限されるものではな
い。また、透明回折格子形成層（１３）は、その表示内
容に特に制限されるものではなく、例えば、一枚のクレ
ジットカード、パスポート、有価証券などにおいて、異
なった複数のパターンを組み合わせてもよい。In each of FIG. 1, FIG. 2 and FIG. 3, the number of opaque diffraction grating layers (15, 25, 35),
The location is not particularly limited to, for example, one credit card, passport, securities, or the like. Further, the transparent diffraction grating forming layer (13) is not particularly limited in its display content, and for example, a plurality of different patterns may be combined in one credit card, passport, securities, etc.
【００２６】以下に本発明による回折格子パターン転写
箔の製造方法について説明する。基材（１１）は厚さ２
５μｍの透明なポリエチレンテレフタレートフィルムを
用いた。なお、基材（１１）としては、他にポリ塩化ビ
ニル、ポリエステル、ポリカーボネート、ポリメタクリ
ル酸メチル、ポリスチレン等の合成樹脂、天然樹脂、
紙、合成紙などを単独で又は組合わせた複合体が使用可
能なものである。The method of manufacturing the diffraction grating pattern transfer foil according to the present invention will be described below. Substrate (11) has a thickness of 2
A 5 μm transparent polyethylene terephthalate film was used. In addition, as the base material (11), other synthetic resins such as polyvinyl chloride, polyester, polycarbonate, polymethylmethacrylate, polystyrene, natural resins,
It is possible to use a composite of paper, synthetic paper, etc. alone or in combination.
【００２７】透明剥離性保護膜層（１２）は、透明回折
格子形成層（１３）をより効果的に被転写体（図示せ
ず）に転写するために設けられるものであり、例えば、
以下の配合比からなる組成物を用いグラビア法により、
厚さ１．５μｍに形成される。
アクリル樹脂 …３０部
ポリエステル樹脂 … ５部
トルエン …４０部
メチルエチルケトン …４０部
メチルイソブチルケトン …２０部The transparent peelable protective film layer (12) is provided in order to more effectively transfer the transparent diffraction grating forming layer (13) to a transfer target (not shown).
By the gravure method using the composition consisting of the following blending ratio,
It is formed to a thickness of 1.5 μm. Acrylic resin 30 parts Polyester resin 5 parts Toluene 40 parts Methyl ethyl ketone 40 parts Methyl isobutyl ketone 20 parts
【００２８】また、透明剥離性保護膜層（１２）として
は、他に熱可塑性アクリル樹脂、塩化ゴム系樹脂、塩化
ビニル−酢酸ビニル共重合樹脂、セルロース系樹脂、塩
素化ポリプロピレン樹脂あるいはこれらにオイルシリコ
ン、脂肪酸アミド、ステアリン酸亜鉛を添加したものが
使用可能となっている。また、無機物を使用してもよ
い。Further, as the transparent peelable protective film layer (12), thermoplastic acrylic resin, chlorinated rubber type resin, vinyl chloride-vinyl acetate copolymer resin, cellulose type resin, chlorinated polypropylene resin or oil thereof may be used. It is possible to use those containing silicon, fatty acid amide, and zinc stearate. Moreover, you may use an inorganic substance.
【００２９】透明回折格子形成層（１３）はエンボス成
形性が良好で、プレスムラが生じ難く、明るい再生像が
得られ、透明剥離性保護膜層（１２）及び透明回折格子
形成層とは異なる屈折率をもつ透明薄膜層（１４）との
接着性が良好である樹脂であって、例えば、以下の配合
比からなる組成物を用いグラビア法により、厚さ１．０
μｍに形成される。
塩化ビニル−酢酸ビニル共重合体 …２５部
ウレタン樹脂 …１０部
メチルエチルケトン …７０部
トルエン …３０部The transparent diffraction grating forming layer (13) has a good embossing moldability, is less likely to cause uneven press, produces a bright reproduced image, and has a refraction different from those of the transparent peelable protective film layer (12) and the transparent diffraction grating forming layer. A resin having good adhesiveness with the transparent thin film layer (14) having a ratio of 1.0 to 1.0 and a thickness of 1.0 by a gravure method using a composition having the following compounding ratio.
formed to a thickness of μm. Vinyl chloride-vinyl acetate copolymer 25 parts Urethane resin 10 parts Methyl ethyl ketone 70 parts Toluene 30 parts
【００３０】また、透明回折格子形成層（１３）として
は、他にポリカーボネート樹脂、ポリスチレン樹脂、ポ
リ塩化ビニル樹脂などの熱可塑性樹脂、不飽和ポリエス
テル樹脂、メラミン樹脂、エポキシ樹脂、ウレタン（メ
タ）アクリレート、ポリエステル（メタ）アクリレー
ト、エポキシ（メタ）アクリレート、ポリオール（メ
タ）アクリレート、メラミン（メタ）アクリレート、ト
リアジン（メタ）アクリレートなどの熱硬化性樹脂ある
いはこれらの混合物、さらにはラジカル重合性不飽和基
を有する熱成型性材料などが使用可能である。Further, as the transparent diffraction grating forming layer (13), thermoplastic resins such as polycarbonate resin, polystyrene resin, polyvinyl chloride resin, unsaturated polyester resin, melamine resin, epoxy resin, urethane (meth) acrylate are also used. , Polyester (meth) acrylate, epoxy (meth) acrylate, polyol (meth) acrylate, melamine (meth) acrylate, triazine (meth) acrylate and other thermosetting resins or mixtures thereof, and further radically polymerizable unsaturated groups. It is possible to use a thermoformable material having the same.
【００３１】透明回折格子形成層（１３）は透明剥離性
保護膜層（１２）とは反対側の面に回折格子形成面を有
し、回折格子形成面上に透明回折格子形成層とは異なる
屈折率をもつ透明薄膜層（１４）が蒸着、スパッタリン
グ等により形成されている。なお、この回折格子形成面
は、微細な凹凸パターンが形成されたニッケル製のプレ
ス版を透明回折格子形成層（１３）上に加熱押圧するこ
とにより形成可能である。The transparent diffraction grating forming layer (13) has a diffraction grating forming surface on the side opposite to the transparent peelable protective film layer (12) and is different from the transparent diffraction grating forming layer on the diffraction grating forming surface. A transparent thin film layer (14) having a refractive index is formed by vapor deposition, sputtering or the like. In addition, this diffraction grating formation surface can be formed by heating and pressing a nickel press plate on which a fine concavo-convex pattern is formed on the transparent diffraction grating formation layer (13).
【００３２】透明薄膜層（１４）は透明回折格子形成層
（１３）とは異なる屈折率をもつ材料を用いる。透明回
折格子形成層（１３）の屈折率は１．１〜１．６程度で
あるので、これより屈折率の大きなものが好ましい。こ
こでは厚さ５０ｎｍのＺｎＳが真空蒸着法により形成さ
れている。その他に、例えば、次に示す無機材料が使用
可能となっている。Ｓｂ2 Ｓ3 、Ｆｅ2 Ｏ3 、Ｔｉ
Ｏ2 、ＣｄＳ、ＣｅＯ2 、ＰｂＣｌ2 、ＣｄＯ、Ｓｂ2
Ｏ3 、ＷＯ3 、ＳｉＯ、Ｓｉ2 Ｏ3 。The transparent thin film layer (14) is made of a material having a refractive index different from that of the transparent diffraction grating forming layer (13). Since the transparent diffraction grating forming layer (13) has a refractive index of about 1.1 to 1.6, a material having a larger refractive index than this is preferable. Here, ZnS having a thickness of 50 nm is formed by a vacuum evaporation method. In addition, for example, the following inorganic materials can be used. Sb 2 S 3 , Fe 2 O 3 , Ti
O 2 , CdS, CeO 2 , PbCl 2 , CdO, Sb 2
O 3 , WO 3 , SiO, Si 2 O 3 .
【００３３】また、透明薄膜層（１４）の膜厚は薄膜表
裏からの回折光が互いに干渉して、その強度が大きくな
る範囲が好ましく、膜厚としては１０ｎｍ〜１０００ｎ
ｍの範囲のものとなる。また、このような透明薄膜層
（１４）を形成する方法としては、真空蒸着法の他にス
パッタリング法、イオンプレーティング法等の成膜手段
が適用可能である。The thickness of the transparent thin film layer (14) is preferably in a range in which the diffracted lights from the front and back of the thin film interfere with each other to increase the intensity, and the film thickness is 10 nm to 1000 n.
It will be in the range of m. As a method for forming such a transparent thin film layer (14), a film forming means such as a sputtering method, an ion plating method or the like can be applied in addition to the vacuum vapor deposition method.
【００３４】透明接着層（１６）は、例えば、以下の配
合比からなる組成物を用いてグラビア法により、厚さ１
０．０μｍに形成される。
塩化ビニル−酢酸ビニル共重合体 …３０部
ポリエステル樹脂 …２０部
メチルエチルケトン …５０部
トルエン …５０部The transparent adhesive layer (16) has a thickness of 1 by a gravure method using a composition having the following compounding ratio.
It is formed to 0.0 μm. Vinyl chloride-vinyl acetate copolymer 30 parts Polyester resin 20 parts Methyl ethyl ketone 50 parts Toluene 50 parts
【００３５】また、透明接着層（１６）としては、他に
も、透明薄膜層（１４）を変質させたり冒すものでなけ
れば通常用いられるものでよく、例えばアクリル系接着
剤、ポリエステル系ポリアミドなどが使用可能である
が、これらに限定されるものではない。Further, as the transparent adhesive layer (16), other than the ones which are usually used as long as they do not deteriorate or affect the transparent thin film layer (14), for example, acrylic adhesives, polyester polyamides, etc. Can be used, but is not limited thereto.
【００３６】次に、本発明においては、透明薄膜層（１
４）と透明接着層（１６）の間にアンカー層（図示せ
ず）を設けることもできる。アンカー層は、透明薄膜層
（１４）と透明接着層（１６）との接着性を向上させる
ためのものであり、例えば、以下の配合比からなる組成
物を用いグラビア法により、厚さ２．０μｍに形成され
る。
ポリエステル樹脂 …１５部
ウレタン樹脂 …２５部
メチルエチルケトン …５０部
トルエン …５０部Next, in the present invention, the transparent thin film layer (1
An anchor layer (not shown) may be provided between 4) and the transparent adhesive layer (16). The anchor layer is for improving the adhesiveness between the transparent thin film layer (14) and the transparent adhesive layer (16), and for example, has a thickness of 2. by a gravure method using a composition having the following compounding ratio. It is formed to 0 μm. Polyester resin: 15 parts Urethane resin: 25 parts Methyl ethyl ketone: 50 parts Toluene: 50 parts
【００３７】また、アンカー層としては、他にも、前述
した接着性を向上させるものであって、且つ両層１４，
１６を変質させたり、冒すものでなければ種々の材料が
使用可能であり、例えば飽和共重合ポリエステル等のポ
リエステル樹脂、ポリ塩化ビニル樹脂、塩化ビニル−酢
酸ビニル共重合体、塩化ビニル−酢酸ビニル−ビニルア
ルコール共重合体、塩化ビニル−酢酸ビニル−マレイン
酸共重合体、塩化ビニル−アクリレート共重合体等の塩
化ビニル共重合体、ポリ塩化ビニリデン樹脂、塩化ビニ
リデン−塩化ビニル共重合体、塩化ビニリデン−アクリ
ロニトリル共重合体等の塩化ビニリデン共重合体、ポリ
アミド樹脂、シリコン樹脂、ポリアクリレートもしくは
ポリメタクリレート樹脂又はこれらの共重合体等の熱可
塑性樹脂があり、これらを単独あるいは２種類以上混合
して適用することができる。Further, as the anchor layer, other than the above, the above-mentioned adhesion is improved, and both layers 14,
Various materials can be used as long as they do not deteriorate or damage 16. For example, polyester resin such as saturated copolymerized polyester, polyvinyl chloride resin, vinyl chloride-vinyl acetate copolymer, vinyl chloride-vinyl acetate- Vinyl alcohol copolymers, vinyl chloride-vinyl acetate-maleic acid copolymers, vinyl chloride copolymers such as vinyl chloride-acrylate copolymers, polyvinylidene chloride resins, vinylidene chloride-vinyl chloride copolymers, vinylidene chloride- There are thermoplastic resins such as vinylidene chloride copolymers such as acrylonitrile copolymers, polyamide resins, silicone resins, polyacrylates or polymethacrylate resins, or copolymers thereof, and these are used alone or in combination of two or more. be able to.
【００３８】また、フェノール樹脂、尿素樹脂、メラミ
ン樹脂、不飽和ポリエステル樹脂、エポキシ樹脂等の熱
硬化性樹脂を、単独あるいは２種類以上混合して適用す
ることができる。Further, a thermosetting resin such as a phenol resin, a urea resin, a melamine resin, an unsaturated polyester resin or an epoxy resin may be used alone or in combination of two or more kinds.
【００３９】さらに、上記熱可塑性樹脂と熱硬化性樹脂
との混合物であっても適用することができる。上記樹脂
は塗料化し、バーコート、ブレードコート、エアナイフ
コート、ロールコートなどのソルベントコート法、ある
いはスクリーン印刷方法など従来公知の塗布・印刷方法
により形成することができる。Further, a mixture of the above-mentioned thermoplastic resin and thermosetting resin can also be applied. The above resin can be formed into a paint and formed by a conventionally known coating / printing method such as a solvent coating method such as bar coating, blade coating, air knife coating, or roll coating, or a screen printing method.
【００４０】次に、本発明における不透明回折格子層
（１５）を形成する際に使用する不透明回折格子箔は、
前記のように図５に示す構成をしているものであり、こ
の不透明回折格子箔を製造する際に使用する材料、工程
は、上記透明回折格子パターンにおける透明回折格子箔
を製造する際に使用する材料、工程と略同一なものであ
る。反射性不透明薄膜層（３４）は入射光を反射する層
であって、厚さ１００ｎｍ程度のＡｌが真空蒸着法によ
り形成されている。なお、反射性不透明薄膜層（３４）
としては、他に銀、金、スズ、窒化チタン（ＴｉＮｘ）
が使用可能である。Next, the opaque diffraction grating foil used for forming the opaque diffraction grating layer (15) of the present invention is
As described above, the structure and structure shown in FIG. 5 are used, and the materials and processes used when manufacturing this opaque diffraction grating foil are used when manufacturing the transparent diffraction grating foil in the above transparent diffraction grating pattern. The material and process used are substantially the same. The reflective opaque thin film layer (34) is a layer that reflects incident light, and Al having a thickness of about 100 nm is formed by a vacuum deposition method. The reflective opaque thin film layer (34)
Others include silver, gold, tin, titanium nitride (TiNx)
Can be used.
【００４１】[0041]
【実施例】以下に本発明の実施例を説明する。EXAMPLES Examples of the present invention will be described below.
【００４２】＜実施例１＞図２は、本発明による回折格
子パターン転写箔の一例の構成を示す断面図である。図
２に示すように、回折格子パターン転写箔は、支持体と
しての基材（１１）の上に透明剥離性保護膜層（１２）
が形成され、透明剥離性保護膜層（１２）の上には不透
明回折格子層（１５）及び透明回折格子形成層（１３）
が形成され、透明回折格子形成層（１３）の上には透明
回折格子形成層とは異なる屈折率をもつ透明薄膜層（１
４）が形成され、更に透明薄膜層（１４）の上には透明
接着層（１６）が形成されている。透明剥離性保護膜層
（１２）の上に形成されている不透明回折格子層（１
５）の面積は、透明回折格子形成層（１３）の面積より
小さなものとなっている。Example 1 FIG. 2 is a sectional view showing the structure of an example of the diffraction grating pattern transfer foil according to the present invention. As shown in FIG. 2, the diffraction grating pattern transfer foil comprises a transparent peelable protective film layer (12) on a base material (11) as a support.
Is formed, and an opaque diffraction grating layer (15) and a transparent diffraction grating forming layer (13) are formed on the transparent peelable protective film layer (12).
And a transparent thin film layer (1) having a refractive index different from that of the transparent diffraction grating forming layer (1) is formed on the transparent diffraction grating forming layer (13).
4) is formed, and a transparent adhesive layer (16) is further formed on the transparent thin film layer (14). An opaque diffraction grating layer (1 formed on the transparent peelable protective film layer (12).
The area of 5) is smaller than the area of the transparent diffraction grating forming layer (13).
【００４３】また、図２おける不透明回折格子層（１
５）は図１おける不透明回折格子層（１５）と同一のも
のである。図４に示すように、不透明回折格子層（１
５）は図４の上方より透明接着層（３６）、反射性不透
明薄膜層（３４）、回折格子形成層（３３）、剥離性保
護膜層（３２）の順に順次積層して形成されている。Further, the opaque diffraction grating layer (1
5) is the same as the opaque diffraction grating layer (15) in FIG. As shown in FIG. 4, the opaque diffraction grating layer (1
5) is formed by stacking the transparent adhesive layer (36), the reflective opaque thin film layer (34), the diffraction grating forming layer (33), and the peelable protective film layer (32) in this order from the top of FIG. .
【００４４】この不透明回折格子層（１５）は図４、及
び図２に示すように、不透明回折格子層（１５）の上方
にある透明接着層（３６）側の面を透明剥離性保護膜層
（１２）に接して、本発明による回折格子パターン転写
箔を形成している。また、図５は、図４に示す不透明回
折格子層（１５）が図２の透明剥離性保護膜層（１２）
の上に転写して形成される前の、基材（３１）に支持さ
れた不透明回折格子箔の構成を拡大して示す断面図であ
る。As shown in FIGS. 4 and 2, the opaque diffraction grating layer (15) has a transparent peelable protective film layer on the surface on the transparent adhesive layer (36) side above the opaque diffraction grating layer (15). The diffraction grating pattern transfer foil according to the present invention is formed in contact with (12). In addition, in FIG. 5, the opaque diffraction grating layer (15) shown in FIG. 4 is the transparent peelable protective film layer (12) of FIG.
It is sectional drawing which expands and shows the structure of the opaque diffraction grating foil supported by the base material (31) before being transferred and formed on.
【００４５】本発明による回折格子パターン転写箔は上
記のような構成であるので、例えばクレジットカード、
パスポート、有価証券などに転写された際の回折格子パ
ターンは、不透明回折格子の箇所を除くその全面積が透
明感のある前記透明回折格子パターンであり、また、不
透明回折格子は、不透明感のある前記不透明回折格子パ
ターンとなっている。Since the diffraction grating pattern transfer foil according to the present invention has the above-mentioned structure, for example, a credit card,
The diffraction grating pattern when transferred to a passport, securities, etc. is the transparent diffraction grating pattern whose entire area is transparent except for the opaque diffraction grating, and the opaque diffraction grating is opaque. It is the opaque diffraction grating pattern.
【００４６】図７は、図２に示すような構成による回折
格子パターン転写箔を、例えばクレジットカード、パス
ポート、有価証券などに使用した際の視認状態を説明す
る平面図である。 図７において、この全面積がクレジ
ットカード、パスポート、有価証券など（５１）であ
り、その上の全面積に図２に示す回折格子パターン転写
箔の基材（１１）が剥離されて転写されいる。５２はク
レジットカード、パスポート、有価証券など（５１）に
予め印刷された文字、絵柄などを示すものであり、５３
は透明回折格子パターン、６５は不透明回折格子パター
ンの視認状態を示している。FIG. 7 is a plan view for explaining a visually recognized state when the diffraction grating pattern transfer foil having the structure shown in FIG. 2 is used for a credit card, a passport, securities, etc. In FIG. 7, this entire area is a credit card, passport, securities, etc. (51), and the base material (11) of the diffraction grating pattern transfer foil shown in FIG. . Reference numeral 52 denotes a character, a pattern, etc. preprinted on the credit card, passport, securities, etc. (51), 53
Is a transparent diffraction grating pattern, and 65 is an opaque diffraction grating pattern.
【００４７】図７において、クレジットカード、パスポ
ート、有価証券（５１）などに予め印刷された文字、絵
柄（５２）などは鮮明に視認され可読されるものであ
り、また、透明回折格子パターン（５３）は、不透明回
折格子層の箇所を除くその全面積において、そのパター
ンが視認され、また、不透明回折格子パターン（６５）
は不透明回折格子層が形成されたその箇所において、そ
のパターンが視認されるものである。 更に、この不透
明回折格子層が形成されたその箇所においては、不透明
回折格子パターン（６５）のみが視認され、不透明回折
格子パターン（６５）と透明回折格子パターン（５３）
が重なった状態は視認されないものである。In FIG. 7, characters, patterns (52), etc. preprinted on credit cards, passports, securities (51), etc. are clearly visible and readable, and a transparent diffraction grating pattern (53) is also provided. ), The pattern is visible in the entire area except the location of the opaque diffraction grating layer, and the opaque diffraction grating pattern (65)
The pattern is visible at the location where the opaque diffraction grating layer is formed. Further, only the opaque diffraction grating pattern (65) is visually recognized at the location where the opaque diffraction grating layer is formed, and the opaque diffraction grating pattern (65) and the transparent diffraction grating pattern (53) are visible.
The overlapping state is not visible.
【００４８】上記のように、本発明による回折格子パタ
ーン転写箔による回折格子パターンは、例えばクレジッ
トカード、パスポート、有価証券などに使用した際に
は、クレジットカード、パスポート、有価証券などに予
め印刷された文字、絵柄などは不透明回折格子層の箇所
を除く印刷内容と、不透明回折格子の箇所を除く透明回
折格子パターンの表示内容と、不透明回折格子パターン
の表示内容とが視認可能となる複雑なパターンを表示す
ることになるものであり、クレジットカード、パスポー
ト、有価証券などの偽造防止性を更に一段と向上させた
ものとなる。また、クレジットカード、パスポート、有
価証券などの装飾性を更に一段と向上させたものとな
る。As described above, when the diffraction grating pattern transfer foil according to the present invention is used for a credit card, passport, securities, etc., it is printed in advance on the credit card, passport, securities, etc. Characters, pictures, etc. are complicated patterns that make it possible to see the printed contents excluding the opaque diffraction grating layer, the display contents of the transparent diffraction grating pattern excluding the opaque diffraction grating part, and the display contents of the opaque diffraction grating pattern. Is displayed, and the anti-counterfeit property of credit cards, passports, securities, etc. is further improved. In addition, the decorativeness of credit cards, passports, securities, etc. will be further improved.
【００４９】図２に示す回折格子パターン転写箔を製造
する際に使用する材料、工程は、前記実施例と同一であ
り、積層順序の相違による製造工程の順序の相違のみで
ある。The materials and processes used for manufacturing the diffraction grating pattern transfer foil shown in FIG. 2 are the same as those in the above-mentioned embodiment, and only the order of the manufacturing process is different due to the difference in the stacking order.
【００５０】＜実施例２＞図３は、本発明による回折格
子パターン転写箔の一例の構成を示す断面図である。図
３に示すように、回折格子パターン転写箔は、支持体と
しての基材（１１）の上に透明剥離性保護膜層（１２）
が形成され、透明剥離性保護膜層（１２）の上には第一
不透明回折格子層（２５）及び透明回折格子形成層（１
３）が形成され、透明回折格子形成層（１３）の上には
透明回折格子形成層とは異なる屈折率をもつ透明薄膜層
（１４）が形成され、更に透明薄膜層（１４）の上には
第二不透明回折格子層（３５）及び透明接着層（１６）
が形成されている。透明剥離性保護膜層（１２）の上に
形成されている第一不透明回折格子層（２５）、及び透
明薄膜層（１４）の上に形成されている第二不透明回折
格子層（３５）の面積は、透明回折格子形成層（１３）
の面積より小さなものとなっている。<Embodiment 2> FIG. 3 is a sectional view showing the structure of an example of a diffraction grating pattern transfer foil according to the present invention. As shown in FIG. 3, the diffraction grating pattern transfer foil comprises a transparent peelable protective film layer (12) on a base material (11) as a support.
And the first opaque diffraction grating layer (25) and the transparent diffraction grating forming layer (1) are formed on the transparent peelable protective film layer (12).
3) is formed, a transparent thin film layer (14) having a refractive index different from that of the transparent diffraction grating forming layer (13) is formed on the transparent diffraction grating forming layer (13), and further on the transparent thin film layer (14). Is a second opaque diffraction grating layer (35) and a transparent adhesive layer (16)
Are formed. A first opaque diffraction grating layer (25) formed on the transparent peelable protective film layer (12) and a second opaque diffraction grating layer (35) formed on the transparent thin film layer (14). Area is the transparent diffraction grating forming layer (13)
It is smaller than the area of.
【００５１】また、図３おける第一不透明回折格子層
（２５）及び第二不透明回折格子層（３５）は図１おけ
る不透明回折格子層（１５）と同一のものである。図４
に示すように、第一不透明回折格子層（２５）及び第二
不透明回折格子層（３５）は図４の上方より透明接着層
（３６）、反射性不透明薄膜層（３４）、回折格子形成
層（３３）、剥離性保護膜層（３２）の順に順次積層し
て形成されている。The first opaque diffraction grating layer (25) and the second opaque diffraction grating layer (35) in FIG. 3 are the same as the opaque diffraction grating layer (15) in FIG. Figure 4
As shown in FIG. 4, the first opaque diffraction grating layer (25) and the second opaque diffraction grating layer (35) are the transparent adhesive layer (36), the reflective opaque thin film layer (34), and the diffraction grating forming layer from the top of FIG. (33) and the peelable protective film layer (32) are sequentially laminated in this order.
【００５２】この第一不透明回折格子層（２５）及び第
二不透明回折格子層（３５）は図４、及び図３に示すよ
うに、第一不透明回折格子層（２５）及び第二不透明回
折格子層（３５）の上方にある透明接着層（３６）側の
面を各々透明剥離性保護膜層（１２）、透明薄膜層（１
４）に接して、本発明による回折格子パターン転写箔を
形成している。また、図５は、図４に示す第一不透明回
折格子層（２５）及び第二不透明回折格子層（３５）が
図３の透明剥離性保護膜層（１２）、及び透明薄膜層
（１４）の上に転写して形成される前の、基材（３１）
に支持された不透明回折格子箔の構成を拡大して示す断
面図である。The first opaque diffraction grating layer (25) and the second opaque diffraction grating layer (35) are, as shown in FIGS. 4 and 3, the first opaque diffraction grating layer (25) and the second opaque diffraction grating. The transparent adhesive layer (36) side surface above the layer (35) is covered with a transparent peelable protective film layer (12) and a transparent thin film layer (1), respectively.
In contact with 4), the diffraction grating pattern transfer foil according to the present invention is formed. In addition, in FIG. 5, the first opaque diffraction grating layer (25) and the second opaque diffraction grating layer (35) shown in FIG. 4 are the transparent peelable protective film layer (12) and the transparent thin film layer (14) of FIG. (31) before being transferred and formed on
It is sectional drawing which expands and shows the structure of the opaque diffraction grating foil supported by FIG.
【００５３】本発明による回折格子パターン転写箔は上
記のような構成であるので、例えばクレジットカード、
パスポート、有価証券などに転写された際の回折格子パ
ターンは、第一不透明回折格子の箇所を除くその全面積
が透明感のある前記透明回折格子パターンであり、ま
た、第一不透明回折格子層及び第二不透明回折格子層
は、不透明感のある前記不透明回折格子パターンとなっ
ている。また、部分的に２種の回折格子パターンが層状
に組み合わされたものとなっている。Since the diffraction grating pattern transfer foil according to the present invention has the above-mentioned structure, for example, a credit card,
The diffraction grating pattern when transferred to a passport, securities, etc. is the transparent diffraction grating pattern having a transparent feeling over the entire area except for the first opaque diffraction grating, and the first opaque diffraction grating layer and The second opaque diffraction grating layer has the opaque diffraction grating pattern having an opaque feeling. In addition, two kinds of diffraction grating patterns are partially combined in a layered form.
【００５４】図８は、図３に示すような構成による回折
格子パターン転写箔を、例えばクレジットカード、パス
ポート、有価証券などに使用した際の視認状態を説明す
る平面図である。 図８において、この全面積がクレジ
ットカード、パスポート、有価証券（５１）などであ
り、その上の全面積に図３に示す回折格子パターン転写
箔の基材（１１）が剥離されて転写されいる。５２はク
レジットカード、パスポート、有価証券（５１）などに
予め印刷された文字、絵柄などを示すものであり、５３
は透明回折格子パターン、７５及び８５は不透明回折格
子パターンの視認状態を示している。FIG. 8 is a plan view for explaining a visually recognized state when the diffraction grating pattern transfer foil having the structure shown in FIG. 3 is used for a credit card, a passport, securities, etc. In FIG. 8, the entire area is a credit card, passport, securities (51), etc., and the base material (11) of the diffraction grating pattern transfer foil shown in FIG. 3 is peeled off and transferred onto the entire area. . Reference numeral 52 denotes a character, a design, etc., which is printed in advance on a credit card, passport, securities (51), etc., and 53
Shows a transparent diffraction grating pattern, and 75 and 85 show an opaque diffraction grating pattern.
【００５５】図８において、クレジットカード、パスポ
ート、有価証券（５１）などに予め印刷された文字、絵
柄（５２）などは鮮明に視認され可読されるものであ
り、また、透明回折格子パターン（５３）は、第一不透
明回折格子層の箇所を除くその全面積において、そのパ
ターンが視認され、また、第一不透明回折格子パターン
（７５）は不透明回折格子層が形成されたその箇所にお
いて、そのパターンが視認されるものである。更に、こ
の第一不透明回折格子層が形成されたその箇所において
は、第一不透明回折格子パターン（７５）のみが視認さ
れ、不透明回折格子パターン（７５）と透明回折格子パ
ターン（５３）が重なった状態は視認されないものであ
る。更にまた、この第二不透明回折格子層（３５）が形
成されたその箇所においては、第二不透明回折格子パタ
ーン（８５）と透明回折格子パターン（５３）が重なっ
た状態で視認されるものである。In FIG. 8, characters, patterns (52), etc., preprinted on credit cards, passports, securities (51), etc. are clearly visible and readable, and a transparent diffraction grating pattern (53). ), The pattern is visible in the entire area except the location of the first opaque diffraction grating layer, and the first opaque diffraction grating pattern (75) shows the pattern in the location where the opaque diffraction grating layer is formed. Is visible. Further, only the first opaque diffraction grating pattern (75) is visually recognized at the location where the first opaque diffraction grating layer is formed, and the opaque diffraction grating pattern (75) and the transparent diffraction grating pattern (53) overlap each other. The state is invisible. Furthermore, at the location where the second opaque diffraction grating layer (35) is formed, the second opaque diffraction grating pattern (85) and the transparent diffraction grating pattern (53) are visually recognized in an overlapping state. .
【００５６】上記のように、本発明による回折格子パタ
ーン転写箔による回折格子パターンは、例えばクレジッ
トカード、パスポート、有価証券などに使用した際に
は、クレジットカード、パスポート、有価証券などに予
め印刷された、例えば文字、絵柄などは第一及び第二不
透明回折格子層の箇所を除く印刷内容と、第一不透明回
折格子層の箇所を除く透明回折格子パターンの表示内容
と、第一及び第二不透明回折格子パターンの表示内容
と、更に第二不透明回折格子パターンと透明回折格子パ
ターンが重なった状態とが視認可能となる複雑なパター
ンを表示することになるものであり、クレジットカー
ド、パスポート、有価証券などの偽造防止性を更に一段
と向上させたものとなる。また、クレジットカード、パ
スポート、有価証券などの装飾性を更に一段と向上させ
たものとなる。As described above, when the diffraction grating pattern transfer foil according to the present invention is used for a credit card, passport, securities, etc., it is printed in advance on the credit card, passport, securities, etc. In addition, for example, characters and pictures are printed contents except for the first and second opaque diffraction grating layers, display contents of the transparent diffraction grating pattern except for the first opaque diffraction grating layer, and first and second opaque The display contents of the diffraction grating pattern and the complicated pattern that allows the second opaque diffraction grating pattern and the transparent diffraction grating pattern to be overlapped with each other are visually displayed, such as credit cards, passports, and securities. For example, the anti-counterfeiting property is further improved. In addition, the decorativeness of credit cards, passports, securities, etc. will be further improved.
【００５７】図３に示す回折格子パターン転写箔を製造
する際に使用する材料、工程は、前記実施例と同一であ
り、積層の数、積層順序の相違による製造工程の数、順
序の相違のみである。The materials and steps used to manufacture the diffraction grating pattern transfer foil shown in FIG. 3 are the same as those in the above-mentioned embodiment, and only the number of manufacturing steps and the difference in order due to the difference in the number of layers and the order of lamination. Is.
【００５８】[0058]
【発明の効果】本発明による回折格子パターン転写箔
は、基材、透明剥離性保護膜層、透明回折格子形成層、
透明薄膜層、不透明回折格子層、及び透明接着層で形成
されており、また、不透明回折格子層の面積は透明回折
格子形成層の面積より小さなものとなっているので、本
発明による回折格子パターン転写箔による回折格子パタ
ーンは、例えばクレジットカード、パスポート、有価証
券などに使用した際には、文字、絵柄などの印刷内容
と、透明回折格子パターンの表示内容と、不透明回折格
子パターンの表示内容と、更に不透明回折格子パターン
と透明回折格子パターンが重なった状態とが視認可能と
なる複雑なパターンを表示するものであり、クレジット
カード、パスポート、有価証券などの偽造防止性を更に
一段と向上させたものとなる。また、クレジットカー
ド、パスポート、有価証券などの装飾性を更に一段と向
上させたものとなる。The diffraction grating pattern transfer foil according to the present invention comprises a substrate, a transparent peelable protective film layer, a transparent diffraction grating forming layer,
Since the transparent thin film layer, the opaque diffraction grating layer, and the transparent adhesive layer are formed, and the area of the opaque diffraction grating layer is smaller than the area of the transparent diffraction grating forming layer, the diffraction grating pattern according to the present invention. When used for credit cards, passports, securities, etc., the diffraction grating pattern formed by the transfer foil is used for printing contents such as characters and pictures, displaying contents of a transparent grating pattern, and displaying contents of an opaque grating pattern. In addition, the opaque diffraction grating pattern and the transparent diffraction grating pattern overlap each other to display a complicated pattern that can be visually recognized, and the anti-counterfeit property of credit cards, passports, securities, etc. is further improved. Becomes In addition, the decorativeness of credit cards, passports, securities, etc. will be further improved.
【００５９】また、本発明による回折格子パターン転写
箔は、基材、透明剥離性保護膜層、不透明回折格子層、
透明回折格子形成層、透明薄膜層、及び透明接着層が形
成されており、また、不透明回折格子層の面積は透明回
折格子形成層の面積より小さなものとなっているので、
本発明による回折格子パターン転写箔による回折格子パ
ターンは、例えばクレジットカード、パスポート、有価
証券などに使用した際には、文字、絵柄などは不透明回
折格子層の箇所を除く印刷内容と、不透明回折格子層の
箇所を除く透明回折格子パターンの表示内容と、不透明
回折格子パターンの表示内容とが視認可能となる複雑な
パターンを表示するものであり、クレジットカード、パ
スポート、有価証券などの偽造防止性を更に一段と向上
させたものとなる。また、クレジットカード、パスポー
ト、有価証券などの装飾性を更に一段と向上させたもの
となる。The diffraction grating pattern transfer foil according to the present invention comprises a substrate, a transparent peelable protective film layer, an opaque diffraction grating layer,
Since the transparent diffraction grating forming layer, the transparent thin film layer, and the transparent adhesive layer are formed, and the area of the opaque diffraction grating layer is smaller than the area of the transparent diffraction grating forming layer,
The diffraction grating pattern formed by the diffraction grating pattern transfer foil according to the present invention, when used in, for example, a credit card, passport, securities, etc., prints the characters and pictures except the opaque diffraction grating layer and the opaque diffraction grating. It displays a complicated pattern that makes it possible to see the display contents of the transparent diffraction grating pattern excluding the layers and the display contents of the opaque diffraction grating pattern, and prevents the forgery of credit cards, passports, securities, etc. It will be further improved. In addition, the decorativeness of credit cards, passports, securities, etc. will be further improved.
【００６０】また、本発明による回折格子パターン転写
箔は、基材、透明剥離性保護膜層、第一不透明回折格子
層、透明回折格子形成層、透明薄膜層、第二不透明回折
格子層、及び透明接着層が形成されており、第一不透明
回折格子層、及び第二不透明回折格子層の面積は透明回
折格子形成層の面積より小さなものとなっているので、
本発明による回折格子パターン転写箔による回折格子パ
ターンは、例えばクレジットカード、パスポート、有価
証券などに使用した際には、文字、絵柄などは第一及び
第二不透明回折格子層の箇所を除く印刷内容と、第一不
透明回折格子層の箇所を除く透明回折格子パターンの表
示内容と、第一及び第二不透明回折格子パターンの表示
内容と、更に第二不透明回折格子パターンと透明回折格
子パターンが重なった状態とが視認可能となる複雑なパ
ターンを表示するものであり、クレジットカード、パス
ポート、有価証券などの偽造防止性を更に一段と向上さ
せたものとなる。また、クレジットカード、パスポー
ト、有価証券などの装飾性を更に一段と向上させたもの
となる。Further, the diffraction grating pattern transfer foil according to the present invention comprises a substrate, a transparent peelable protective film layer, a first opaque diffraction grating layer, a transparent diffraction grating forming layer, a transparent thin film layer, a second opaque diffraction grating layer, and Since the transparent adhesive layer is formed and the areas of the first opaque diffraction grating layer and the second opaque diffraction grating layer are smaller than the area of the transparent diffraction grating forming layer,
The diffraction grating pattern formed by the diffraction grating pattern transfer foil according to the present invention, when used in, for example, a credit card, passport, securities, etc., prints characters and patterns except the portions of the first and second opaque diffraction grating layers. And the display contents of the transparent diffraction grating pattern excluding the portion of the first opaque diffraction grating layer, the display contents of the first and second opaque diffraction grating patterns, and the second opaque diffraction grating pattern and the transparent diffraction grating pattern overlapped. The state displays a complicated pattern that makes it visible, and further improves the forgery resistance of credit cards, passports, securities, and the like. In addition, the decorativeness of credit cards, passports, securities, etc. will be further improved.
【００６１】また、本発明による回折格子パターン転写
箔は、透明回折格子形成層と不透明回折格子層とが層状
に構成されているので、例えばクレジットカード、パス
ポート、有価証券などに使用した際に、従来の方法に比
べ転写工程を増やすことなく使用することの出来る。す
なわち、一回の転写により透明回折格子パターンと不透
明回折格子パターンが視認可能となるクレジットカー
ド、パスポート、有価証券などが得られる。Further, since the diffraction grating pattern transfer foil according to the present invention has a transparent diffraction grating forming layer and an opaque diffraction grating layer which are layered, when it is used for a credit card, passport, securities, etc., It can be used without increasing the transfer process as compared with the conventional method. That is, a credit card, passport, securities, etc., in which the transparent diffraction grating pattern and the opaque diffraction grating pattern can be visually confirmed by one transfer, can be obtained.
【図１】本発明による回折格子パターン転写箔の一実施
例の構成を示す断面図である。FIG. 1 is a sectional view showing a configuration of an embodiment of a diffraction grating pattern transfer foil according to the present invention.
【図２】本発明による回折格子パターン転写箔の一例の
構成を示す断面図である。FIG. 2 is a sectional view showing a configuration of an example of a diffraction grating pattern transfer foil according to the present invention.
【図３】本発明による回折格子パターン転写箔の一例の
構成を示す断面図である。FIG. 3 is a sectional view showing a configuration of an example of a diffraction grating pattern transfer foil according to the present invention.
【図４】不透明回折格子の構成を拡大して示す断面図で
ある。FIG. 4 is a cross-sectional view showing an enlarged configuration of an opaque diffraction grating.
【図５】不透明回折格子箔の構成を拡大して示す断面図
である。FIG. 5 is a cross-sectional view showing an enlarged configuration of an opaque diffraction grating foil.
【図６】図１に示すような構成による回折格子パターン
転写箔を使用した際の視認状態を説明する平面図であ
る。FIG. 6 is a plan view illustrating a visual recognition state when the diffraction grating pattern transfer foil having the configuration shown in FIG. 1 is used.
【図７】図２に示すような構成による回折格子パターン
転写箔を使用した際の視認状態を説明する平面図であ
る。FIG. 7 is a plan view illustrating a visually recognized state when the diffraction grating pattern transfer foil having the configuration shown in FIG. 2 is used.
【図８】図３に示すような構成による回折格子パターン
転写箔を使用した際の視認状態を説明する平面図であ
る。FIG. 8 is a plan view illustrating a visually recognized state when the diffraction grating pattern transfer foil having the configuration shown in FIG. 3 is used.
【図９】回折格子パターン転写箔の一例の構成を示す断
面図である。FIG. 9 is a cross-sectional view showing a configuration of an example of a diffraction grating pattern transfer foil.
【図１０】回折格子パターン転写箔の他の一例の構成を
示す断面図である。FIG. 10 is a cross-sectional view showing the configuration of another example of the diffraction grating pattern transfer foil.
１、１１…基材 ２、１２…透明剥離性保護膜層 ３、１３…透明回折格子形成層 ４、１４…透明薄膜層 １５…不透明回折格子層 ６、１６…透明接着層 ２５…第一不透明回折格子層 ３１、４１…基材 ３２、４２…剥離性保護膜層 ３３、４３…回折格子形成層 ３４、４７…反射性不透明薄膜層 ３５…第二不透明回折格子層 ３６、４６…透明接着層 ５１…クレジットカード、パスポート、有価証券 ５２…予め印刷された文字、絵柄 ５３…透明回折格子パターン ５５、６５…不透明回折格子パターン ７５…第一不透明回折格子パターン ８５…第二不透明回折格子パターン 1, 11 ... Base material 2, 12 ... Transparent peelable protective film layer 3, 13 ... Transparent diffraction grating forming layer 4, 14 ... Transparent thin film layer 15 ... Opaque diffraction grating layer 6, 16 ... Transparent adhesive layer 25 ... First opaque diffraction grating layer 31, 41 ... Base material 32, 42 ... Releasable protective film layer 33, 43 ... Diffraction grating forming layer 34, 47 ... Reflective opaque thin film layer 35 ... Second opaque diffraction grating layer 36, 46 ... Transparent adhesive layer 51 ... Credit card, passport, securities 52 ... Preprinted characters and patterns 53 ... Transparent diffraction grating pattern 55, 65 ... Opaque diffraction grating pattern 75 ... First opaque diffraction grating pattern 85 ... Second opaque diffraction grating pattern
Claims (5)
剥離性保護膜層、（ｂ）回折格子パタ−ンを有する透明
回折格子形成層、（ｃ）この透明回折格子形成層とは異
なる屈折率をもつ透明薄膜層、（ｄ）透明接着層、反射
性不透明薄膜層、回折格子形成層、剥離性保護膜層の順
に順次積層して形成され回折格子パタ−ンを有する不透
明回折格子層、（ｅ）透明接着層を順次積層したことを
特徴とする回折格子パタ−ン転写箔。1. A transparent diffraction grating forming layer having (a) a transparent peelable protective film layer, (b) a diffraction grating pattern, and (c) this transparent diffraction grating forming layer on at least one surface of a support. An opaque diffraction grating having a diffraction grating pattern formed by sequentially laminating a transparent thin film layer having a different refractive index, (d) a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer, and a peelable protective film layer. Layer, and (e) a transparent adhesive layer are sequentially laminated, a diffraction grating pattern transfer foil.
剥離性保護膜層、（ｂ）透明接着層、反射性不透明薄膜
層、回折格子形成層、剥離性保護膜層の順に順次積層し
て形成され回格子パターンを有する不透明回折格子層、
（ｃ）回折格子パターンを有する透明回折格子形成層、
（ｄ）この透明回折格子形成層とは異なる屈折率をもつ
透明薄膜層、（ｅ）透明接着層を順次積層したことを特
徴とする回折格子パターン転写箔。2. A support having a transparent peelable protective film layer, (b) a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer and a peelable protective film layer, which are laminated in this order on one surface of the support. An opaque diffraction grating layer having a diffraction grating pattern formed by
(C) a transparent diffraction grating forming layer having a diffraction grating pattern,
(D) A diffraction grating pattern transfer foil comprising a transparent thin film layer having a refractive index different from that of the transparent diffraction grating forming layer, and (e) a transparent adhesive layer sequentially laminated.
剥離性保護膜層、（ｂ）透明接着層、反射性不透明薄膜
層、回折格子形成層、剥離性保護膜層の順に順次積層し
て形成され回格子パターンを有する第一不透明回折格子
層、（ｃ）回折格子パターンを有する透明回折格子形成
層、（ｄ）この透明回折格子形成層とは異なる屈折率を
もつ透明薄膜層、（ｅ）透明接着層、反射性不透明薄膜
層、回折格子形成層、剥離性保護膜層の順に順次積層し
て形成され回格子パターンを有する第二不透明回折格子
層、（ｆ）透明接着層を順次積層してなり、前記第一不
透明回折格子層及び前記第二不透明回折格子層の面積を
前記透明回折格子形成層の面積より小さく形成したこと
を特徴とする回折格子パターン転写箔。3. A transparent peelable protective film layer (a), a transparent adhesive layer (b), a reflective opaque thin film layer, a diffraction grating forming layer, and a peelable protective film layer are sequentially laminated on at least one surface of a support. A first opaque diffraction grating layer having a diffraction grating pattern formed by the above, (c) a transparent diffraction grating forming layer having a diffraction grating pattern, (d) a transparent thin film layer having a refractive index different from that of the transparent diffraction grating forming layer, (E) a transparent adhesive layer, a reflective opaque thin film layer, a diffraction grating forming layer, a peelable protective film layer, and a second opaque diffraction grating layer formed in this order and having a diffraction grating pattern, and (f) a transparent adhesive layer. A diffraction grating pattern transfer foil, wherein the first opaque diffraction grating layer and the second opaque diffraction grating layer are sequentially laminated and are formed to have an area smaller than that of the transparent diffraction grating forming layer.
折格子形成層の面積より小さく形成したことを特徴とす
る請求項１記載の回折格子パターン転写箔。4. The diffraction grating pattern transfer foil according to claim 1, wherein the area of the opaque diffraction grating layer is smaller than the area of the transparent diffraction grating forming layer.
折格子形成層の面積より小さく形成したことを特徴とす
る請求項２記載の回折格子パターン転写箔。5. The diffraction grating pattern transfer foil according to claim 2, wherein the area of the opaque diffraction grating layer is smaller than the area of the transparent diffraction grating forming layer.