JP3341418B2 - Method for producing foamed propylene-based resin having communicating voids - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a foamed propylene-based resin having communicating voids which can be used mainly as a base material for drainage.

[0002]

2. Description of the Related Art Conventionally, for example, in a riding club, a racetrack of a racetrack, a golf course, and the like, pebbles are laid in the lower layer in order to improve drainage after rain or the like. It is common practice to lay soil on top of it and level the soil to improve drainage, but if clogging occurs in the lower part where pebbles are spread, the drainage that should be exhibited originally In such a case, a large amount of labor was required to perform the work for improving the drainage property, and the work was very difficult. Therefore, in the civil engineering and construction fields,
What is called a geotextile, which is a water-permeable material composed of a fiber material such as a knitted fabric, a woven fabric, or a nonwoven fabric, is widely used to prevent clogging and prevent a decrease in drainage. However, in this case, there is a drawback that the geotextile itself is expensive, the workability is poor, and skill is required at the time of application.

[0003] Conventionally, styrofoam has been used as an ultra-light embankment material as a road base material. However, since styrene is usually impermeable, it may be used after rain or depending on the place where it is used. There is a very serious drawback as a civil engineering structure in which buoyancy is directly received by water circling below the constructed styrene, and the place of use and construction procedures are restricted.

[0004] In recent years, various water-permeable block molded articles made of synthetic resin have been proposed in order to solve the above-mentioned problems. For example, spherical polystyrene foamed particles are solidified with an adhesive and continuous voids are formed. There are known molded articles having a structure provided with (for example, JP-A-52-140569, JP-A-4-153,026). However, in these water-permeable blocks, the adhesion between the foamed particles depends only on the adhesiveness of an adhesive formed in a film form on the surface of the foamed particles, and the film is easily broken and has a sufficient adhesive strength. However, there is a drawback that the strength is fragile, for example, the adhesion between the foamed particles is peeled off. In addition, in the production, foamed particles are not directly filled in a mold and molded, but the foamed particles and an adhesive are mixed, and the mixture is filled in a mold to a temperature lower than the softening point of the foamed particles. There is a problem in productivity, manufacturing cost, and the like because a kind of secondary processing-like manufacturing process of heating and then cooling and solidifying is employed. Moreover, since the polystyrene resin itself is poor in oil resistance and heat resistance, when the molded article of the above-mentioned expanded polystyrene particles is used as a base material for drainage such as a road foundation material, the surface finish of asphalt or the like on the molded article is reduced. It was difficult.

[0005] Further, polystyrene foam molding in which surfaces of extruded chips having a longest portion of 2 cm or more and having a non-spherical shape such as a saddle shape, a curved ball shape, or an eyeglass ring shape are fused together in a mold. Although a method for manufacturing a body is also known (Japanese Patent Publication No. 5-177723), when a foamed molded body is molded using a molded chip having such a shape, the size of a space formed between the chips is increased. Variations tend to occur, and it is difficult to uniformly fill the mold itself, and it is difficult to control the porosity of the obtained foamed molded product, as the filling density tends to be different each time it is filled, There is a drawback that it is difficult even to make the porosity of the molded body constant to some extent at any part. Moreover, in the case of such a molded chip, when the molded chip is filled in the mold, the molded chip to be filled is clogged with a filling feeder, a hose connected to the feeder, and a filling port of the mold. It is easy to reduce the production efficiency, and may cause poor filling of the molded chip in the mold.

On the other hand, in order to efficiently obtain a water-permeable block molded article having excellent water-permeability and compressive strength, the present applicant also has a ratio L / L between the length L of the longest part and the cross-sectional length D of the maximum body. A method of foaming column-shaped expanded polyolefin resin particles in which a specific D is specified in a mold has been previously proposed (Japanese Patent Laid-Open No. 3-2).
No. 24727), the foamed molded article obtained by such a method has good water permeability, good properties in terms of compressive strength and the like, and can sufficiently withstand applications such as drainage base materials. In order to obtain high water permeability,
It is necessary to prevent secondary foaming from occurring as much as possible at the time of molding so that the voids between the foamed particles are not filled.Because of this, the temperature of the steam used for molding cannot be increased. There is a problem that the range is narrow and it is difficult to control the temperature during molding, and further improvement in porosity control has been desired.
Furthermore, since the molding temperature must be lowered in order to suppress secondary foaming during molding as much as possible, there is still room for improvement in the fusion property between foamed particles. Also, when filling the expanded particles into the mold, the expanded particles are filled feeder,
The problem that the hose connected to the feeder is easily clogged has not been completely solved.

The present applicant has conducted intensive studies in view of the above-mentioned problems of the prior art, and as a result, when molding a foamed molded product using a propylene-based resin as a base resin, the volume V and the surface area of the foamed particles to be molded are measured. As long as S satisfies a specific relationship, without suppressing secondary foaming during molding,
Conversely, even in the case of positively secondary foaming, the gap between the foam particles constituting the molded body is not filled, and the problem that the porosity of the obtained foamed molded body is reduced does not occur. Furthermore, if the foamed particles have specific physical properties, it is possible to perform favorable molding without subjecting the particles to a pretreatment of applying an internal pressure when the foamed particles are subjected to molding,
The present inventors have found that control of the porosity of the molded body is also easy, and have completed the present invention.

[0008]

That is, the method of the present invention for producing a foamed propylene-based resin article having communicating voids comprises:
A DSC curve obtained by differential scanning calorimetry of the expanded propylene-based resin particles (a DSC curve obtained when 2 to 6 mg of expanded particles are heated to 220 ° C. at a rate of 10 ° C./min by a differential scanning calorimeter) is represented by propylene. It has a crystal structure in which a high-temperature peak b appears on a higher temperature side than the specific peak a together with the specific peak a of the base resin, and the volume thereof is V
[Mm ³ ], S / S when surface area is S [mm ² ]
(6V ^2/3 ) is 1 to 3, high temperature peak calorie is 5 to 30 J / g, and bulk density is 0.012 to 0.2 g /
propylene-based resin foamed particles having a melting point of ³ cm.
It is characterized by heating in a temperature range of 30 ° C. to the same melting point + 10 ° C. to cause secondary foaming.

In the method of the present invention, the expanded polypropylene resin particles can have a shape satisfying the following formulas. a ≦ b ≦ c 1 ≦ b / a <2 1 ≦ c / a <2 1 , A, b, and c represent the expanded particles in xy on three-dimensional coordinates,
When each of the planes yz and zx is in contact with the foamed particles at at least one point, and the planes are arranged on the first quadrant of three-dimensional coordinates so as not to cut the foamed particles, x, y on the surface of the foamed particles , Z is the minimum coordinate that can be taken by any of the maximum values of the coordinates, and b is the minimum value that can be taken by any of the two maximum coordinate values in the direction orthogonal to the coordinate axis indicating the coordinate value a. , And the maximum value of the remaining coordinate values is c.

In the present invention, a DSC curve obtained by differential scanning calorimetry of expanded propylene resin particles means that 2 to 6 mg of expanded propylene resin particles are measured at 10 ° C./min. Is a DSC curve obtained when the temperature is raised to 220 ° C., and the intrinsic peak a and the high temperature peak b appearing in the DSC curve are, for example, 10 ° C./min. The first DSC curve (an example of which is shown in FIG. 1) obtained when the temperature was raised at a rate of temperature rise of 220 ° C. to 10 ° C./min. At a cooling rate of around 40 ° C,
Again at 10 ° C./min. When the DSC curve obtained when the temperature is raised to 220 ° C. at the temperature raising rate is set as the second DSC curve (an example of which is shown in FIG. 2), the DSC curves can be distinguished by these DSC curves.

That is, the intrinsic peak a in the present invention is:
It is an endothermic peak peculiar to the propylene-based resin constituting the expanded particles, which is considered to be due to an endotherm at the time of so-called melting of the propylene-based resin. Also the second DSC
This is an endothermic peak that also appears in the curve. However, the temperature at the peak of the peak may be slightly different between the first time and the second time.

The high-temperature peak b in the present invention is
This is an endothermic peak that appears on the higher temperature side than the temperature at which the above-mentioned characteristic peak a appears in the first DSC curve, and the second D
Endothermic peaks that do not appear in the SC curve and do not show such a high-temperature peak b in the DSC curve have poor in-mold moldability, making it difficult to obtain a good molded body. It is desirable that the difference between the temperature of the peak of the high-temperature peak b appearing in the first DSC curve and the temperature of the peak of the unique peak a appearing in the second DSC curve is large, and the difference between the two is 5 ° C. or more. , Preferably 10 ° C or higher.

The appearance of the high-temperature peak b in the first DSC curve may be due to the presence of a crystal structure different from the crystal structure of the expanded propylene-based resin particles in which it does not appear. In addition, the unique peak a is the first DS
The high-temperature peak b appears only in the first DSC curve, and appears in the C-curve and the second DSC curve almost in the same manner. Since the high-temperature peak b appears together with the specific peak a, the crystal structure of the expanded propylene-based resin particles in the form of expanded particles is not due to the crystal structure of the base resin itself. It is thought to be due to such as, by producing foamed particles under specific foaming conditions, such as foaming temperature and holding time,
It is possible to obtain expanded propylene resin particles having a crystal structure in which a high-temperature peak b appears together with an intrinsic peak a in a DSC curve.

As means for producing expanded particles, for example, a base resin is melt-kneaded by an extruder and then extruded into strands, and cut into appropriate lengths after cooling, or cut into appropriate lengths and cooled. First, a pellet-shaped resin particle is produced by such means, and then the resin particle is dispersed in a dispersion medium in the presence of a foaming agent in a closed container, and heated to a temperature equal to or higher than the softening temperature of the resin particle. Impregnating the resin particles with a foaming agent,
Thereafter, one end of the container is opened, and the resin particles and the dispersion medium are simultaneously discharged under a lower pressure atmosphere (usually under atmospheric pressure) than the container while maintaining the pressure in the container at a pressure higher than the vapor pressure of the foaming agent. Means such as foaming the resin particles is usually employed, but when heating the resin particles in a closed container,
The heating temperature (foaming temperature) is set to the melting end temperature T of the resin particles.
without raising the temperature above _e , the melting point T _m -20 ° C. or more and the melting end temperature T _e,
It is easy to obtain expanded particles having a crystal structure in which a high-temperature peak b appears on the higher temperature side than the specific peak a along with the specific peak a specific to the propylene-based resin in the C curve. Further, a method of adjusting the expansion temperature within the above temperature range, the melt upon heating of the expanded beads end temperature T _e temperature around a sufficient time (typically, about 5 to 45 minutes) over a temporarily held Thus, the value of the heat absorption amount at the high temperature peak b (high temperature peak heat amount) can be adjusted. When the holding time is compared with the foaming temperature, the adjustment of the high-temperature peak calorific value largely depends on the foaming temperature.

[0015] Incidentally, the above melting point T _m is the temperature at the top of the inherent peak a appearing in the second DSC curve as described above,
The melting completion temperature T _e, is the temperature at which the skirt of the inherent peak a appearing in the second DSC curve is returned to the position of the baseline at a high temperature side.

The base resin used for the expanded propylene resin particles in the present invention includes, for example, polypropylene, ethylene-propylene block copolymer, ethylene-propylene random copolymer, butene-propylene random copolymer, ethylene- Examples thereof include a butene-propylene random copolymer, and among them, an ethylene-propylene random copolymer, a butene-propylene random copolymer, and an ethylene-butene-propylene random copolymer are particularly preferable. Further, the propylene resin is preferably a non-crosslinked resin from the viewpoint of recycling.

In the present invention, the above-mentioned various polymers may be used alone as usual, or may be used in combination such as mixing two or more kinds. Further, in order to impart flexibility, it is preferable to add 5 to 40% by weight of a thermoplastic elastomer such as ethylene-propylene rubber. Furthermore, a biodegradable plastic such as polycaprolactone, β-hydroxybutyric acid, and / or a copolymer thereof, polyvinyl alcohol, and modified starch is mixed with the base resin within a range that does not impair the object, function, and effect of the present invention. It can also be used. When a biodegradable plastic is used, in addition to the method of mixing with the base resin as described above, if necessary, foaming of the biodegradable plastic may be performed within a range that does not impair the object, action, and effect of the present invention. Alternatively, non-foamed resin particles may be mixed with propylene-based resin foamed particles, and a molded article may be obtained from these.

The foaming agent used to obtain the foamed particles is usually propane, butane, pentane, hexane, cyclobutane, cyclohexane, trichlorofluoromethane, dichlorodifluoromethane, chlorofluoromethane, trifluoromethane, 1,2,2, 2,2-tetrafluoroethane, 1-chloro-1,1-difluoroethane, 1,1
Volatile blowing agents such as difluoroethane and 1-chloro-1,2,2,2-tetrafluoroethane, and inorganic gas-based blowing agents such as nitrogen, carbon dioxide, argon, and air are used. Inorganic gas-based blowing agents which do not cause destruction and are inexpensive are preferred, and nitrogen, air and carbon dioxide are particularly preferred. The amount of the foaming agent except nitrogen and air is usually 2 to 50 parts by weight per 100 parts by weight of resin particles. When nitrogen and air are used as the foaming agent, the amount is 20 to 60 kgf / cm. shall be pressed in a sealed container at a pressure range of ² · G, relationships and usage of these blowing agents and the bulk density of the expanded beads to be obtained and the foaming temperature, appropriately selected from the relation between the high temperature peak heat quantity Is done.

The dispersing medium for dispersing the resin particles may be any medium that does not dissolve the resin particles. Examples of such a dispersing medium include water, ethylene glycol, glycerin, methanol, and ethanol. Usually, water is used.

Further, when the resin particles are dispersed in a dispersion medium and heated to a foaming temperature, an anti-fusion agent can be used to prevent fusion between the resin particles. As the anti-fusing agent, any inorganic or organic one can be used as long as it does not dissolve in water or the like and does not melt by heating. In general, an inorganic one is preferable. Powders such as kaolin, talc, mica, aluminum oxide, titanium oxide, and aluminum hydroxide are suitable as the inorganic anti-fusion agent. Anionic surfactants such as sodium dodecylbenzenesulfonate and sodium oleate are preferably used as a dispersing aid. The anti-fusing agent has an average particle size of 0.001 to 100 μm, particularly 0.001 to 30.
μm is preferred. Usually, 0.01 to 10 parts by weight of the anti-fusing agent is preferably added to 100 parts by weight of the resin particles. The surfactant is used per 100 parts by weight of the resin particles.
Usually, 0.001 to 5 parts by weight are preferably added.

The base resin is colored by adding a coloring pigment or dye, for example, black, brown, gray, or the like, for forming water-permeable soil to obtain colored expanded particles. It can also be used to obtain a colored molded product. The color of the above-mentioned coloring pigment or dye can be appropriately selected from yellow, red, pink, blue and the like depending on the application in addition to the above.

When an additive such as a color pigment, a dye or an inorganic substance is added to the base resin, the additive can be kneaded with the base resin as it is. It is preferable to prepare a master batch and knead the master batch with the base resin. The addition amount of the coloring pigment or the dye varies depending on the color.
It is 0.01 to 15 parts by weight based on 00 parts by weight. It is preferable to add 0.001 to 5 parts by weight of the inorganic substance to 100 parts by weight of the base resin. By adding the above amount of the inorganic substance to the base resin, the effect of improving the expansion ratio,
The effect of adjusting the bubble diameter to 50 to 350 μm can be expected.

In the method of the present invention, foamed particles used for molding a foamed propylene resin molded product include:
Assuming that the volume is V [mm ³ ] and the surface area is S [mm ² ], the value of S / (6V ^2/3 ), that is, a cube having the same volume V as the expanded particles is assumed. The surface area S 'of the cube (if the volume of the cube is V, the length of one side is V ^1/3 , the area of one face of the cube is V ^2/3 , and since the cube is a hexahedron, S' = 6 V ^2/3 ) is used so that the ratio of the surface area S of the expanded particles to the surface area S becomes 1 to 3, preferably 1.3 to 2.5.

In selecting the expanded particles in which the above relationship is established between the volume V and the surface area S, the volume V of the expanded particles is selected.
To measure, for example, by measuring the volume increase when submerged any number of expanded particles in a liquid such as alcohol,
The increase may be divided by the number of expanded particles to calculate an average volume per expanded particle. Further, in order to measure the surface area S of the foamed particles, for example, the amount of increase in weight that is increased when a surface of a sample particle having a known surface area is coated with a coating agent such as a low-viscosity dilute silicone rubber on the surface is measured. Based on the relationship between this and the known surface area, a method of calculating the surface area from the weight increase when the same coating agent is similarly coated on the surface of the foamed particles, or a computer graphic using CAD. , A method of applying ink to the surface of the foamed particles, transferring the ink, and calculating the surface area, and the like. In the present invention, it is desirable to use the one that satisfies the above relationship between the volume V and the surface area S in all the individual expanded particles.
As long as the value of / (6V ^2/3 ) does not extremely deviate from the above range, it suffices that the relationship between the volume V and the surface area S is satisfied on average in the whole expanded particles to be subjected to molding.

In the method of the present invention, the volume V and the surface area S
It is particularly important that the propylene-based resin foam molded article is molded using the foamed particles having a specific relationship with the foamed particles, and the foamed particles selected by such a relationship are conventionally used for molding the foamed molded body. If the surface area per unit volume is larger than the normal foamed particles used, and if these foamed particles are filled in a mold so that each of them is randomly oriented and fused together, a molded body is molded. In addition, voids communicating with the foamed particles are formed in the obtained molded body, and exhibit good water permeability. Furthermore, there is no possibility that a problem that the voids between particles are filled by secondary foaming at the time of molding may occur, and it is easy to control the porosity, and it is not necessary to suppress secondary foaming, and molding can be performed at a high temperature. Therefore, the fusibility between particles can be improved. When the value of S / (6V ^2/3 ) is less than 1, even when the high-temperature peak calorific value is adjusted or the heating temperature during molding is adjusted, the voids are filled by secondary foaming during molding. Therefore, it is difficult to control the porosity, and as a result, it is difficult to obtain a predetermined porosity. Also, S
When the value of / (6V ^2/3 ) exceeds 3, there arises a problem that foamed particles having a stable shape cannot be efficiently obtained.

In the present invention, the shape is not particularly limited as long as the expanded particles used for molding the propylene-based resin expanded molded article satisfy the above-mentioned relationship. As shown in FIG. 3, each of the xy, yz, and zx planes on the three-dimensional coordinates has at least one point (the surface p, the line q, and the line r, respectively) on the expanded particle 1 as shown in FIG. Faces and lines are considered as a set of points)
, And when the planes are arranged in all directions on three-dimensional coordinates so as not to cut the foamed particles 1, the absolute value of the absolute value of each coordinate of x, y, z on the surface of the foamed particles 1 Either one may be used, and the coordinate value absolute value which is the smallest among the various directions in which the expanded particles 1 are arranged and which is equal to or less than the value at the portion where the absolute values of the coordinate values in the other two directions are the maximum is determined as When it is assumed that the coordinate axis indicating the coordinate value absolute value a is the x-axis, among the maximum values of the coordinate value absolute values on each of the y-axis and the z-axis, Let b be a small value and c be the rest (a ≦ b ≦ c),
It is preferable that the shape satisfies the relationship of 1 ≦ b / a <2 and 1 ≦ c / a <2. In FIG. 3, the tangent plane p is indicated by oblique lines, and the tangent lines q and r are indicated by two-dot chain lines.

The values of a, b, and c can be measured using computer graphics, a coordinate measuring machine, or the like. The values of a, b, and c of the expanded particles 1 can be determined using computer graphics or the like to design the expanded particle shape.

When b / a ≧ 2 or c / a ≧ 2 in the foamed particles 1, the foamed particles are liable to be clogged in the filling feeder when the foamed particles are filled in the mold, and are insufficiently filled in the mold. Tends to occur. 1> b / a, 1> c / a
Does not exist because the relationship between a, b, and c is defined as a ≦ b ≦ c.

Examples of the expanded particles 1 satisfying the above conditions include, for example, particles having a (substantially) constant shape as shown below in a cross section in a predetermined direction. That is, as shown in FIG. 4, the cross-sectional shapes are (a) a hollow circular shape (a donut shape), (a) a hollow triangular shape, (c) a hollow hexagonal shape, (d) a shape having a partition in a hollow circle, E) a shape in which two hollow circles are arranged side by side, (f) a shape in which three hollow circles are arranged in contact with each other, (g) a hollow circular shape having a tear part d in a part, and (h) a part And a hollow rectangular shape having a tear portion d.

In addition to the above-mentioned hollow structure, that is, a tubular shape, the shape of the foamed particles 1 is also one of the preferred embodiments in which the foamed particles have 3 to 8 limbs. As such a shape, for example, as shown in FIG.
(B) One consisting of three limbs e, (ii) One consisting of five limbs e, (ii) One consisting of eight limbs e, (ii) a solid circle f One having four limbs e at equal positions around the periphery, (G) having six limbs e at equal positions around a solid triangle g, and (T) a solid square h Having four limbs e at equal positions around the perimeter, (h)
One having three limbs e at equal positions around a hollow circle i, (T) having three limbs e at equal positions around a hollow triangle j, and (T) a hollow square one having four limbs e at equal positions around k, (g) one having six limbs e at equal positions around a hollow circle i,
(N) Six limbs e at equal positions around the hollow triangle j, (d) Four limbs e,
(U) Six limbs e and the like.

Among the above-mentioned examples, particularly when the foamed particles are cylindrical without limbs e, there is no clogging of the feeder as in the case of general foamed particles such as spheres. Filling is performed at a uniform density at any position, and in any case, is performed at a constant density. Filling rate(%)
Is a value true volume occupied by the foamed particles (cm ³⁾ indicated as a percentage divided by the mold (cavity) volume (cm ³⁾ when the foamed particles filled into the mold. The filling ratio of the expanded particles is adjusted according to the true density of the expanded particles or, if the expanded particles always have a (substantially) constant shape in the cross section in the predetermined direction as exemplified above, the L / D value is adjusted. It can be performed by a method of appropriately adjusting the air pressure, a method of adjusting the mold opening (cracking) of the mold when filling the foamed particles into the mold, and the like.

The L / D value of a foamed particle is defined as the maximum length (D) of the body section of a given foamed particle having a (almost) constant shape in a cross section in a predetermined direction. Divided by the maximum length (L) in the vertical direction. For example, when the foamed particles are cylindrical, L corresponds to the height of the cylinder, and D corresponds to the outer diameter of the cylinder.

The expanded particles 1 preferably have an L / D of expanded particles of 0.5 to 0.7 or 1.3 to 2.0, and an L / D of expanded particles of 0.5 to 0.7. 0.7 or 1.
With a cylindrical shape of 3 to 2.0, it is possible to give directionality to the cylindrical foamed particles by adjusting the filling air pressure at the time of filling the foamed particles into the mold, so that the porosity, in particular, the direction of the communicating voids Sex can be controlled.

Preferred expanded particles in the present invention are (a) to (h), (h) and (te) in FIGS.
In the case of (d), the outer diameter (corresponding to the above D) is 3 to 12
5 mm, an inner diameter of 1 to 6 mm, and a length of 2 to 20 mm (corresponding to the above L) having a cylindrical shape, an elliptical cylindrical shape or a combined body shape of cylindrical shapes, and FIGS. G) In the case of a limb-shaped part or a limb-shaped part, the thickness of the limb is 1 to 2.5 mm, the height is 1 to 3 mm, and the length (corresponding to the above L). Is 2 to 20 mm, and FIG.
(C) to (ta) solid body diameters (corresponding to D above)
Those having a size of 2.5 to 8 mm are exemplified.

Although the above-mentioned expanded particles always have a (substantially) constant shape in a cross section in a predetermined direction, the expanded particles used in the present invention are not limited to this, and may be somewhat irregular. Good.

When the foamed particles are amorphous, the respective values of a, b, and c defined in the above conditions may be replaced as follows and applied to the foamed particles. That is, assuming that the expanded particles are arranged in the rectangular parallelepiped so that at least one point of the surface of the expanded particles is in contact with all the inner surfaces of a rectangular parallelepiped, when changing the arrangement direction of the expanded particles, When the length of the shortest side is the shortest, the length of the side is defined as a, the length of the shortest side of the two sides orthogonal to the side a is b, and the length of the remaining side is c. Then, a shape having a, b, and c that satisfies the relationship of 1 ≦ b / a <2 and 1 ≦ c / a <2 may be used.

Further, in the present invention, the high-temperature peak calorific value of the expanded particles of the propylene-based resin is set to a specific value so that the expanded particles can be favorably molded without being subjected to a pretreatment for applying an internal pressure. In this case, since the bulk density of the foamed particles affects the value of the high-temperature peak calorie, the high-temperature peak calorie of the foamed particles is 5 to 30 J / g, preferably 12 to 30 J / g.
g and the bulk density of the expanded particles is 0.012 to 0.1 g.
2 g / cm ³ , preferably 0.03 to
0.2 g / cm ³ , more preferably 0.04 to 0.2 g
/ Cm ³ .

When the relationship between the high-temperature peak calorific value and the bulk density is in such a relationship, good molding can be performed without applying an internal pressure to the foamed particles, and the voids in the voids formed in the molded body can be obtained. Rate control becomes easier. That is, the high-temperature peak calorie and the bulk density of the expanded particles are:
It is considered that there is a close relationship between the strength and the film thickness of the film (cell) constituting the expanded particles, and the high-temperature peak calorific value is 30 J
/ G, the cell strength of the expanded particles tends to be unnecessarily high, which lowers the secondary expandability of the expanded particles and requires a high vapor pressure for molding. Problems such as poor appearance of the obtained molded product and poor fusion of the foamed particles occur. If the high-temperature peak calorific value is less than 5 J / g, sufficient cell strength cannot be obtained, and the molded product is removed from the mold. There is a problem in that the molded product has a large shrinkage and it is difficult to control the porosity. On the other hand, when the bulk density of the foamed particles exceeds 0.2 g / cm ³ , the film thickness of the foamed particles tends to be unnecessarily large, and the molded body is molded even when the high temperature peak calorific value is in the above range. In this case, it is necessary to apply an internal pressure to the foamed particles, resulting in poor productivity. On the other hand, if the bulk density is less than 0.012 g / cm ³ , it is difficult to fill the foamed particles into the mold, and furthermore, the resulting molded article has poor compression characteristics, which is not preferable.

The high-temperature peak calorie in the present invention is defined as DSC
The endothermic amount of the high-temperature peak b appearing on the curve. The high-temperature peak b and the specific peak a are divided at the valley portion of the high-temperature peak b and the specific peak a. 1, the area of the high-temperature peak b can be obtained from the area of the high-temperature peak b on the chart by the following equation. : High-temperature peak calorific value [J / g] = (area of the high-temperature peak b on the chart [cm ² ]) × (caloric value per chart ² cm ² [J / cm ² ]) ÷ (mass of sample [g])

The bulk density of the foamed particles is defined as, for example, a value obtained by filling a foamed particle in a measuring cylinder by free fall, then vibrating the measuring cylinder and reading a scale when the volume reaches a constant weight. It is calculated by dividing the total weight of the expanded particles obtained.

[0041] In the method of the present invention, such a propylene-based resin foamed particles, without performing the processing of the inner pressure, but may be opened and closed is filled in the shaping die which can not be closed, the melting point T _m of a foamed particles By heating with steam in a temperature range of −30 ° C. to the same melting point T _m + 10 ° C. to cause the foamed particles to fuse with each other and to cause secondary foaming, and then cool,
A foamed propylene-based resin having communicating voids is obtained. The molded article obtained by the method of the present invention has a foam having a bulk density of 0.012 to 0.2 g / cm ³ , preferably 0.03 to 0.2 g / cm ³ , and more preferably 0.04 to 0.2 g / cm ³ .
It is desirable that the thickness be about 0.2 g / cm ³ .

In the present invention, it is not necessary to suppress the secondary foaming as described above, and it is possible to form the molded body by positively secondary foaming the foamed particles in the mold by increasing the molding temperature. Since it is possible, the molded body is molded in the above-mentioned temperature range, thereby improving the fusion property between the foamed particles and performing good molding. That is, the molding temperature is the melting point T _m
If the temperature is lower than −30 ° C., poor fusion between the foamed particles occurs, and if the molding temperature exceeds the melting point T _m + 10 ° C., the obtained foamed molded product tends to shrink, resulting in poor product appearance and foamed particles. Variations occur in the molten state of the surface, and the fused area between the foamed particles tends to be non-uniform, which makes it difficult to control the porosity.

Further, in the present invention, by setting the high-temperature peak calorific value and the bulk density of the foamed particles to specific values, good molding can be carried out without applying an internal pressure to the foamed particles. This is preferable in terms of simplification and the like, and this also facilitates control of the porosity.

The molded article preferably obtained by the method of the present invention has a communicating void portion having a porosity of 5 to 60%, and the sand of the sample is subjected to foam molding in accordance with JIS-A1218 variable water level permeability test. The value measured in place of the body is 5 × 10 ^-1
１1 × 10 ⁻³ [cm ³ / cm ² · sec. ], And also has excellent characteristics in air permeability and sound absorption. In addition, the porosity A [%] of the polymer particle foam molding is calculated by dividing the apparent volume [cm ³ ] calculated from the outer dimensions of the foam molding by B (the apparent volume B is simply calculated without considering the shrinkage of the molding). In consideration of the above, it is equal to the volume in the mold cavity at the time when the foamed molded body was obtained, and can be calculated from the dimensions of the mold drawing), and the true volume [cm ³ ] excluding the voids of the foamed molded body is represented by C (The true volume C can be determined by measuring the increased volume when the foam molded article is submerged in a liquid such as alcohol), and is calculated by the following equation. : A (%) = [(B−C) / B] × 100

Accordingly, the obtained molded body can be used, for example, for training courses and horse paths such as horseback riding clubs, artificial turf under rooftop gardens, drainage facilities such as dark spots, golf courses, etc. It can be used for various purposes as a wall material, or as a core material for floors and ceilings, making use of its sound-absorbing, air-permeable, and heat-insulating properties. it can.

Hereinafter, examples of use in each of the above applications will be described. In the case described above, a molded body of 30 to 60 mm is placed on the surface of a concrete base on which a drainage groove has been formed, and sand or rubber chips having a thickness of 30 to 100 mm are spread over the molded body. It is preferable that the molded body is colored gray (substantially the same color as the sand or rubber chips) because the horse is not surprised even when the surface of the molded body appears because the surface sand or the like is displaced. In such a case, a molded body of 10 to 30 mm is usually laid on a concrete base provided with a drainage groove as necessary, and artificial grass is laid on the molded body. The artificial turf dries quickly because the water is easily drained through. In such a case, it is used in a state in which the periphery of a drainage pipe having a hole is covered with a molded body, and sand, gravel, soil, and the like are piled thereon. In such a case, a molded body is laid on the ground, and soil, sand, and turf are sequentially provided on the molded body for use. In addition, since styrene foam blocks having no water permeability are usually used as embankment materials, drainage is poor, and when immersed in a large amount of water, the blocks may be pushed up and moved by the buoyancy of water accumulated around the blocks. For this reason, it was necessary to cover with a wedge or a wire mesh. However, the use of the molded body obtained by the method of the present invention promotes drainage and reduces the above-mentioned danger. In other cases, it is used packed between the outer wall and the inner wall. In such a case, it is used by being fixed to the back surface of a floor material or a ceiling material.

[0047]

EXAMPLES Next, examples of the method for producing a foamed propylene-based resin article having open spaces according to the present invention (Examples 1 to 5).
The present invention will be described in more detail with reference to 6) and comparative examples (Comparative Examples 1 to 4). In addition, the base resin and various values regarding the foamed particles formed from the base resin are shown in Table 1, the molding conditions for molding the foamed particles, and the evaluation of the obtained molded body are shown in Table 2. Each example and each comparative example are shown.

After the base resin shown in Table 1 was melted and kneaded in an extruder together with aluminum hydroxide and carbon black (amounts of aluminum hydroxide and carbon black were 0.2% by weight and 0.26% by weight, respectively). Extruded into a strand shape from a die having a similar shape to the desired cross-sectional shape of the foamed particles to be obtained, quenched in water, cut into a predetermined length, and pelletized. After granulating into carbon dioxide as a blowing agent, 100 kg of these pellets were dispersed in 220 liters of water containing 400 g of kaolin as an anti-fusing agent and 30 g of sodium dodecylbenzenesulfonate as a dispersing aid, with stirring in a closed vessel (capacity 400 liters), in Table 1 without heating to the melting completion temperature T _e temperature above the resin After raising the temperature to the foaming temperature and holding for the time shown in Table 1, a back pressure equal to the equilibrium vapor pressure of the foaming agent is applied. One end of the container is released while maintaining the pressure, and the resin particles and water are separated. Simultaneously, the resin particles were released to foam the resin particles, and gray foamed particles having a cross-sectional shape as shown in Table 1 were obtained. In Table 1, symbols (A) to (C) representing cross-sectional shapes are shown.
(Nu) corresponds to the symbols (a) to (nu) in FIGS. In the case of a circular cross section, columnar foamed particles were used.

From the sample group arbitrarily selected from the obtained expanded particles, the volume V, the surface area S of the expanded particles, the values of a, b, and c when the expanded particles are arranged on three-dimensional coordinates,
And the bulk density were measured, and the S /
The results are shown in Table 1 together with the values of (6V ^2/3 ), b / a and c / a. Further, the first DSC curve obtained by the differential scanning calorimetry, the presence or absence of a high-temperature peak from the second DSC curve, the high-temperature peak calorie was calculated from the chart of the first DSC curve, Are also shown in Table 1.

Next, the foamed particles as described above were molded under the molding conditions shown in Table 2 to obtain a molded article of polymer foamed particles. The values obtained by measuring the porosity and the bulk density of the obtained molded body are shown together with the values of the filling property, the fusion property, the moldability, and the water permeability of the molded body at the time of molding. 2 is also shown. The evaluation criteria for the evaluation of the various physical properties are as described below.

The filling property was evaluated by the number of clogging of a filling gun (feeder) with the foamed particles in 10 moldings. The filling gun had a caliber of 25 mm and a drawing air pressure of 5 kg / cm ² (G). ○ ・ ・ ・ 0 times △ ・ ・ ・ 1-2 times × ・ ・ ・ 3 times or more

The fusibility is 50 mm × 100 mm × 5 mm
Five test pieces obtained by cutting the foamed particle molded body were pulled in the longitudinal direction until each of the test pieces was broken so as to obtain (length × width × thickness), and the fractured surfaces were observed and evaluated according to the following criteria. ◎ ・ ・ ・ A lot of broken parts occurred in the foamed particles of the fractured surface in all the test pieces ○ ・ ・ ・ A broken part occurred in the foamed particles of the fractured surface in all the test pieces △ ・ ・ ・ Fracture in some of the test pieces A broken part occurs in the foamed particles of the cross section. × ・ ・ ・ The foamed particles of the broken surface are cut at the fusion surface without being broken in all the test pieces.

The moldability was evaluated based on a molding temperature range in which the molded article did not shrink and a sufficient gap was secured.
The wider the temperature range, the better the moldability.・ ・ ・: The molding temperature range is equal to or higher than that of a normal molded product. Δ: The molding temperature range is narrower than a normal molded product. ×: A molded product cannot be obtained.

The water permeability is such that 1 liter of water is applied to the surface of the molded body.
Minutes were dropped with a funnel to observe the trend of water, and the results were determined as follows.・ ・ ・: Passed through the inside of the molded product and discharged from the lower surface. Δ: After being retained on the surface of the molded product, the product is discharged from the lower surface little by little. ×: Spills from the side without penetrating into the molded body.

[0055]

[Table 1]

[0056]

[Table 2]

[0057]

As described above, according to the method of the present invention, a molded article obtained by molding a foamed propylene resin using foamed particles having a specific relationship between volume V and surface area S is obtained. Shows good water permeability, and there is no possibility that a problem that a void to be formed between particles is filled by secondary foaming at the time of molding may occur, and it is easy to control the porosity. Since molding can be performed at a high temperature without suppressing foaming, it is possible to improve the fusion property between particles and to widen the molding temperature range.

In the method of the present invention, by setting the high-temperature peak calorific value and the bulk density of the foamed particles to be molded to specific values, it is possible to perform good molding without applying an internal pressure to the foamed particles. This is preferable in terms of facilities and costs, simplification of the process, and the like, and this also facilitates control of the porosity.

Further, by specifying the shape of the foamed particles, the porosity can be more easily controlled, and the foamed particles are easily clogged when the foamed particles are filled in the mold, and the filling is not satisfactory. There is no risk of causing trouble.

[Brief description of the drawings]

FIG. 1 is an example of a first DSC curve chart.

FIG. 2 is an example of a second DSC curve chart.

FIG. 3 is an explanatory diagram for explaining respective values of a, b, and c used for specifying a shape of a foamed particle used in a method for producing a foamed propylene-based resin molded article having a communicating void according to the present invention. .

FIG. 4 is a view showing an aspect of a shape of a foamed particle.

FIG. 5 is a view showing an aspect of a shape of a foamed particle.

[Explanation of symbols]

1 Expanded Particles a When the expanded particles are arranged on three-dimensional coordinates, the minimum value that the maximum value of the absolute value of the coordinate value on the surface of the expanded particles can take. B Indicates a when the maximum diameter of the expanded particles indicates a. The smallest one of the absolute values of the coordinate values in the two directions orthogonal to the coordinate axis which is perpendicular to the coordinate axis c The coordinate value in the two directions orthogonal to the coordinate axis indicating a when the maximum diameter of the expanded particles indicates a The remaining value when b is determined among the absolute values. X x-axis y y-axis z z-axis p Contact surface between expanded particles and xy plane q Tangent line between expanded particles and yz plane r Tangent line between expanded particles and zx plane

────────────────────────────────────────────────── (5) References JP-A-63-258939 (JP, A) (58) Fields investigated (Int. Cl. ⁷ , DB name) C08J 9/22

Claims (2)

(57) [Claims] 1. A DSC curve (2 to 6 mg of expanded particles) obtained by differential scanning calorimetry of expanded particles of propylene resin.
By a differential scanning calorimeter at 10 ° C./min. At 220
DSC curve obtained when the temperature is raised to 0 ° C.), has a crystal structure in which a high-temperature peak appears on a higher temperature side than the specific peak of the propylene-based resin in the propylene-based resin, the volume is V [mm ³ ] and the surface area is S / mm when S [mm ² ]
(6V ^2/3 ) is 1 to 3, high temperature peak calorie is 5 to 30 J / g, and bulk density is 0.012 to 0.2 g /
propylene-based resin foamed particles having a melting point of ³ cm.
A method for producing a foamed propylene-based resin article having interconnected voids, wherein the foamed article is heated in a temperature range of 30 ° C. to the same melting point + 10 ° C. to cause secondary foaming. 2. The expanded polypropylene resin particles have the following shape:
2. The method for producing a foamed propylene-based resin having open spaces according to claim 1, which satisfies the following formulas. a ≦ b ≦ c 1 ≦ b / a <2 1 ≦ c / a <2 1 , A, b, and c represent the expanded particles in xy on three-dimensional coordinates,
When each of the planes yz and zx is in contact with the foamed particles at at least one point, and the planes are arranged on the first quadrant of three-dimensional coordinates so as not to cut the foamed particles, x, y on the surface of the foamed particles , Z is the minimum coordinate that can be taken by any of the maximum values of the coordinates, and b is the minimum value that can be taken by any of the two maximum coordinate values in the direction orthogonal to the coordinate axis indicating the coordinate value a. , And the maximum value of the remaining coordinate values is c.