JP3239782U - Adhesive material for shoe inner repair - Google Patents
Adhesive material for shoe inner repair Download PDFInfo
- Publication number
- JP3239782U JP3239782U JP2022003031U JP2022003031U JP3239782U JP 3239782 U JP3239782 U JP 3239782U JP 2022003031 U JP2022003031 U JP 2022003031U JP 2022003031 U JP2022003031 U JP 2022003031U JP 3239782 U JP3239782 U JP 3239782U
- Authority
- JP
- Japan
- Prior art keywords
- layer
- adhesive
- shoe
- nonwoven fabric
- repairing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】靴の内側を簡単に補修できて、かつ補修箇所が、長期の使用に耐えられ、さらに、違和感なく良好な履き心地となる靴内側補修用貼着材を提供する。【解決手段】粘着剤層2と、該粘着剤層より上方の不織布層3A又は樹脂フィルム層3Bと、該不織布層又は樹脂フィルム層より上方の表面層4とを備えてなる靴内側補修用貼着材1であって、前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記樹脂フィルム層の厚みが0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材。【選択図】図1[PROBLEMS] To provide an adhesive material for repairing the inner side of a shoe, which can easily repair the inner side of the shoe, the repaired portion can withstand long-term use, and the wearer can wear the shoe without discomfort. A patch for repairing the inner side of a shoe comprising an adhesive layer 2, a nonwoven fabric layer 3A or resin film layer 3B above the adhesive layer, and a surface layer 4 above the nonwoven fabric layer or resin film layer. In the adhesive material 1, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the resin film layer has a thickness of The adhesive strength of the patch for repairing the inner side of a shoe, which has a thickness of 0.1 mm to 3.0 mm, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237:2009. is 2.5N to 30N. [Selection drawing] Fig. 1
Description
本考案は、靴内側補修用貼着材に関する。詳しくは、粘着剤層、不織布層又は樹脂フィルム層及び表面層を含むことにより、十分な粘着力を有することを特徴とする靴内側補修用貼着材に関する。 TECHNICAL FIELD The present invention relates to an adhesive material for repairing the inner side of a shoe. More specifically, it relates to an adhesive material for repairing the inner side of a shoe, characterized by having sufficient adhesive strength by including an adhesive layer, a nonwoven fabric layer or a resin film layer, and a surface layer.
革製などのビジネスシューズやスポーツシューズ等のほとんどの靴においては、足にフィットさせて履き心地を良くすること等を目的としてクッション材例えば表素材と裏素材との間にウレタンスポンジなどの軟質弾性体を使用したクッション材を配する構成が採用されている。さらに靴の底や外側には靴を長く履けるように耐久性を著しく高める靴部品が開発、採用されたことで、近年では、良い靴について耐久消費財のように長期間に亘って履こうとする傾向が見られる。 In most shoes such as business shoes and sports shoes made of leather, a soft elastic material such as urethane sponge is placed between the front material and the back material for the purpose of fitting the foot and improving comfort. A configuration is adopted in which a cushion material using the body is arranged. In addition, the development and adoption of shoe parts that significantly increase the durability of the sole and outside of the shoe so that the shoe can be worn for a long time has led to the recent trend to wear good shoes for a long time like durable consumer goods. There is a tendency to
しかしながら、靴を履いているうちにやがて靴の外側に傷がついてしまうことが多い。しかし、多少傷ができただけで、靴を捨ててしまうというのは良い靴であるか否かにかかわらず非常に不経済である。
そこで、簡易に靴を補修するためのテープ等が報告されている(特許文献1乃至特許文献4)。
However, it is often the case that the outside of the shoe is eventually damaged while the shoe is being worn. However, it is very uneconomical to throw away the shoes just because they are slightly damaged, regardless of whether they are good shoes or not.
Therefore, tapes and the like for easily repairing shoes have been reported (
特許文献1乃至特許文献4に記載の発明又は考案は、靴の外側を補修するための物又は方法である。
しかし、実際は靴の内側、特に踵内側部分が摩耗して破れや擦れ跡などが生じてしまうことが長期間に亘って靴を履く場合の問題として生じやすいことが少なくとも靴業界において知られている。すなわち、靴の内側、特に踵内側部分は、長く履いていると、足と強く当る部分のクッション部の耐久性が特に乏しいために、その部分が磨耗して破れたり一部欠落して見苦しくなったり、靴の硬い素材と足、特に踵が直接接触して擦れることによって、履いている靴下が短期間で部分的に薄くなったり、破けたり、足に圧痕が出来たり、靴の内側と足の表面との間にガタと言われる空隙部が生じ一体感が乏しくなって履き心地が悪くなる等の多くの問題が発現する。
The inventions or devices described in
However, it is known at least in the shoe industry that wear of the inner side of the shoe, particularly the inner side of the heel, resulting in tears and abrasion marks is likely to occur as a problem when wearing the shoe for a long period of time. . That is, when the shoe is worn for a long time, especially the inner part of the heel, the durability of the cushion part of the part that strongly contacts with the foot is particularly poor, so that part is worn and torn or partly missing, making it unsightly. In addition, due to direct contact between the hard material of the shoe and the foot, especially the heel, the socks may be partially thinned or torn in a short period of time, the foot may be indented, and the inside of the shoe and the foot may be damaged. There are many problems such as a lack of sense of unity and poor wearing comfort due to the formation of a space called looseness between the surface of the shoe and the shoe.
本考案は、斯かる事情を考慮してなされたものであって、その目的とするところは、靴の内側を簡単に補修できて、かつ補修箇所が、長期の使用に耐えられ、さらに、違和感のない良好な履き心地を再び得ることができる靴内側補修用貼着材を提供することにある。 The present invention has been made in consideration of such circumstances, and the purpose thereof is to easily repair the inside of the shoe, to make the repaired part durable for a long period of time, and to prevent discomfort. To provide an adhesive material for repairing the inner side of a shoe capable of obtaining good comfort in wearing again.
本考案者は、上記課題を解決するために鋭意検討を行った結果、靴内側補修用貼着材が0.01mm乃至1.0mmの厚さの粘着剤層、0.1mm乃至3.0mmの厚さの表面層の間に0.1mm乃至3.0mmの厚さの不織布層又は0.1mm乃至3.0mmの樹
脂フィルム層を含むことで、2.5N乃至30Nの十分な粘着力を持ち、かつ当該靴内側補修用貼着材は簡単に貼着できるうえに、当該靴内側補修用貼着材を貼着した靴を履いても違和感なく良好な履き心地となることを見出し、本考案を完成させた。
As a result of intensive studies to solve the above problems, the inventors of the present invention have found that the adhesive layer for repairing the inner side of the shoe has a thickness of 0.01 mm to 1.0 mm and a pressure-sensitive adhesive layer of 0.1 mm to 3.0 mm. By including a nonwoven fabric layer with a thickness of 0.1 mm to 3.0 mm or a resin film layer with a thickness of 0.1 mm to 3.0 mm between the thick surface layers, it has a sufficient adhesive strength of 2.5 N to 30 N. Moreover, the adhesive material for repairing the inner side of the shoe can be easily attached, and the shoes to which the adhesive material for repairing the inner side of the shoe is attached are comfortable to wear without discomfort. completed.
即ち、本考案は、以下の態様からなる。
(1)粘着剤層と、該粘着剤層より上方の不織布層又は樹脂フィルム層と、該不織布層又は樹脂フィルム層より上方の表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記樹脂フィルム層の厚みが0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材。
(2)前記粘着剤層は、アクリル系粘着剤、ウレタン系粘着剤、シリコン系粘着剤及びゴム系粘着剤からなる群から選ばれる少なくとも一種の粘着剤を含む、(1)に記載の靴内側補修用貼着材。
(3)前記不織布層は、ポリエチレン不織布、ポリプロピレン不織布、ポリエステル不織布、アラミド不織布、ガラス不織布、セルロース不織布、ナイロン不織布、ビニロン不織布及びレーヨン不織布からなる群から選ばれる少なくとも一種の不織布からなる、(1)又は(2)に記載の靴内側補修用貼着材。
(4)前記樹脂フィルム層は、ポリウレタンフィルム、ポリプロピレンフィルム及びポリエステルフィルムからなる群から選ばれる少なくとも一種の樹脂フィルムからなる、(1)乃至(3)のうち何れか一に記載の靴内側補修用貼着材。
(5)前記表面層は、天然皮革、合成皮革、人工皮革、天然繊維及び合成繊維からなる群から選ばれる少なくとも一種の布地からなる、(1)乃至(4)のうち何れか一に記載の靴内側補修用貼着材。
(6)前記天然皮革が、スエードである、(5)に記載の靴内側補修用貼着材。
(7)前記合成繊維が、ナイロン樹脂又はポリエステル樹脂からなり、網目状に織られている、(5)に記載の靴内側補修用貼着材。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤を含み、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布、ポリプロピレン不織布及びポリエステル不織布からなる群から選ばれる少なくとも一種の不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革及び合成繊維からなる群から選ばれる少なくとも一種の布地からなり、該合成皮革がポリ塩化ビニル又はポリウレタンからなり、該合成繊維がナイロン樹脂又はポリエステル樹脂からなり、該ナイロン樹脂又はポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層
と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS
Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の
外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3
.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの
厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層
と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS
Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の
外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の不織布層と、該不織布層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009
に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
ここで、本考案の好ましい態様の一つは、粘着剤層と、該粘着剤層より上方の樹脂フィルム層と、該樹脂フィルム層より上方の表面層とを備えてなり、上辺が弓形の長方形状である、靴内側補修用貼着材であって、
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材に関する。
That is, this invention consists of the following aspects.
(1) An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer or resin film layer above the adhesive layer, and a surface layer above the nonwoven fabric layer or resin film layer. ,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the resin film layer has a thickness of 0.1 mm to 3.0 mm. The surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive strength of the adhesive for repairing the inner side of the shoe measured in accordance with JIS Z0237:2009 is 2.5 N to 30 N. There is an adhesive material for repairing the inside of shoes.
(2) The shoe inner according to (1), wherein the pressure-sensitive adhesive layer contains at least one pressure-sensitive adhesive selected from the group consisting of an acrylic pressure-sensitive adhesive, a urethane-based pressure-sensitive adhesive, a silicon-based pressure-sensitive adhesive, and a rubber-based pressure-sensitive adhesive. Adhesive for repair.
(3) The nonwoven fabric layer is made of at least one kind of nonwoven fabric selected from the group consisting of polyethylene nonwoven fabric, polypropylene nonwoven fabric, polyester nonwoven fabric, aramid nonwoven fabric, glass nonwoven fabric, cellulose nonwoven fabric, nylon nonwoven fabric, vinylon nonwoven fabric and rayon nonwoven fabric. Or the adhesive material for repairing the inside of a shoe according to (2).
(4) The shoe inner repairing material according to any one of (1) to (3), wherein the resin film layer is made of at least one resin film selected from the group consisting of polyurethane film, polypropylene film and polyester film. adhesive.
(5) The surface layer according to any one of (1) to (4), wherein the surface layer is made of at least one fabric selected from the group consisting of natural leather, synthetic leather, artificial leather, natural fibers and synthetic fibers. Adhesive for repairing the inside of shoes.
(6) The adhesive material for shoe inner repair according to (5), wherein the natural leather is suede.
(7) The adhesive material for repairing the inner side of a shoe according to (5), wherein the synthetic fibers are made of nylon resin or polyester resin and are woven in a mesh shape.
Here, one of the preferred embodiments of the present invention is an adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer. There is
The pressure-sensitive adhesive layer contains a urethane-based pressure-sensitive adhesive, the pressure-sensitive adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the non-woven fabric layer is at least one selected from the group consisting of polyethylene non-woven fabric, polypropylene non-woven fabric and polyester non-woven fabric. The nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, the surface layer is made of at least one fabric selected from the group consisting of synthetic leather and synthetic fibers, and the synthetic leather is polychlorinated It is made of vinyl or polyurethane, the synthetic fiber is made of nylon resin or polyester resin, the nylon resin or polyester resin is woven in a mesh shape, and the surface layer has a thickness of 0.1 mm to 3.0 mm, The present invention also relates to an adhesive for repairing the inner side of a shoe, wherein the adhesive strength of the adhesive for repairing the inner side of the shoe is 2.5N to 30N as measured according to JIS Z0237:2009.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. The adhesive material for repairing the inner side of a shoe is attached with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. It relates to an adhesive material for repairing the inner side of a shoe, which is attached with a cut line of
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and JIS
The adhesive strength of the adhesive material for shoe inner repair measured according to Z0237:2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and an adhesive material is attached to the release layer for each shoe size. An adhesive material for repairing the inner side of a shoe with a plurality of cut lines matching the outer shape of the shoe.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. It relates to an adhesive material for repairing the inner side of a shoe, which is attached with a cut line of
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. The adhesive material for repairing the inner side of a shoe is attached with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. It relates to an adhesive material for repairing the inner side of a shoe, which is attached with a cut line of
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3
. The adhesive material for repairing the inner side of shoes has a thickness of 0 mm and an adhesive force of 2.5 N to 30 N measured according to JIS Z0237:2009, and a release layer is adhered to the adhesive layer, and the release layer To provide an adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each shoe size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009. A shoe having an adhesive force of 2.5 N to 30 N, a release layer adhered to the adhesive layer, and a plurality of cut lines corresponding to the outer shape of the adhesive material for each shoe size. It relates to an adhesive material for inner repair.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive strength of the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of cut lines are attached to the release layer according to the outer shape of the adhesive material for each shoe size. It relates to an adhesive material for
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. The present invention relates to an adhesive material for repairing the inner side of a shoe with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. The present invention relates to an adhesive material for repairing the inner side of a shoe with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. The adhesive material for repairing the inner side of a shoe is attached with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. It relates to an adhesive material for repairing the inner side of a shoe, which is attached with a cut line of
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and JIS
The adhesive strength of the adhesive material for shoe inner repair measured according to Z0237:2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and an adhesive material is attached to the release layer for each shoe size. An adhesive material for repairing the inner side of a shoe with a plurality of cut lines matching the outer shape of the shoe.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. It relates to an adhesive material for repairing the inner side of a shoe, which is attached with a cut line of
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. The adhesive material for repairing the inner side of a shoe is attached with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. It relates to an adhesive material for repairing the inner side of a shoe, which is attached with a cut line of
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention comprises an adhesive layer, a non-woven fabric layer above the adhesive layer, and a surface layer above the non-woven fabric layer, and has a rectangular shape with an arched upper side. An adhesive material for repairing the inside of a shoe,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009. A shoe having an adhesive force of 2.5 N to 30 N, a release layer adhered to the adhesive layer, and a plurality of cut lines corresponding to the outer shape of the adhesive material for each shoe size. It relates to an adhesive material for inner repair.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and JIS Z0237: 2009
The adhesive strength of the adhesive material for repairing the inner side of the shoe measured according to the method is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the outer shape of the adhesive material for each shoe size. The present invention relates to an adhesive material for repairing the inner side of a shoe attached with a plurality of cut lines that are aligned with each other.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. The present invention relates to an adhesive material for repairing the inner side of a shoe with a plurality of cut lines.
Here, one of the preferred embodiments of the present invention is provided with an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and has a rectangular shape with an arcuate upper side. An adhesive material for repairing the inside of a shoe, which has a shape,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of a polyester resin, the polyester resin is woven into a mesh, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. The present invention relates to an adhesive material for repairing the inner side of a shoe with a plurality of cut lines.
本考案の靴内側補修用貼着材は、粘着剤層、表面層の間に不織布層又は樹脂フィルム層を含むので、十分に強い強度で靴本体に簡単に貼着できる貼着材が提供される。従って、補修部分が剥がれることなく靴をより長く履くことが可能となり、経済的である。
また、本考案の靴内側補修用貼着材は、その厚み等の性状について、靴内側補修用貼着材として用いるに最適な数値範囲を決定したことで、靴を履いたときに補修部の違和感もなく良好な履き心地を提供することができる。
Since the adhesive material for repairing the inner side of the shoe of the present invention includes a nonwoven fabric layer or a resin film layer between the adhesive layer and the surface layer, the adhesive material has sufficiently high strength and can be easily attached to the shoe body. be. Therefore, the shoe can be worn for a longer period of time without peeling off of the repaired portion, which is economical.
In addition, in the adhesive material for repairing the inner side of the shoe of the present invention, the optimum numerical range for use as an adhesive material for repairing the inner side of the shoe was determined for the properties such as thickness, so that when the shoe was worn, the repaired part It is possible to provide good wearing comfort without any sense of incongruity.
以下、本考案の好ましい態様を示す図面を挙げて、本考案を更に説明する。
図1は本考案の靴内側補修用貼着材1の一実施態様を示す図である。
図1(c)に示すように、本考案の靴内側補修用貼着材1は、粘着剤層2と、該粘着剤層2より上方の不織布層3A又は樹脂フィルム層3Bと、該不織布層3A又は樹脂フィルム層3Bより上方の表面層4とからなる。
また、実際に販売するにあたっては、図1(b)に示すような粘着剤層2に剥離層5を接着した構成をとる。
本考案の靴内側補修用貼着材1は、靴内側の補修部を覆えれば、どのような大きさ、形状でもかまわない。例えば、靴の踵内側部分の補修部、内側側面部の補修部、内側底部の補修部を覆うことができ、特に踵内側部分の補修部を覆えることが好ましい。
実際に製品にするにあたっては、例えば、おおよそ一般的な靴の踵内側部分の湾曲及び大きさに合わせて、図1(a)に示すような長辺100mm、短辺60mm程度の上辺が弓形の長方形状のものが好ましい。また、さらに靴のサイズごとに合わせた複数のカット線が剥離層5に付けてあると好ましい。例えば、靴のサイズが25cmの場合、25cmの靴の踵内側部分の湾曲及び大きさに合わせたサイズに調整できるカット線(例えばカット線上に25cmと表記しておく)が剥離層5に付けてあればこれに合わせて切り取ることができるので、より簡便に本考案の靴内側補修用貼着材1を使用することができる。
The invention will now be further described with reference to the drawings showing preferred embodiments of the invention.
FIG. 1 is a diagram showing one embodiment of an
As shown in FIG. 1(c), the shoe inner repair
For actual sales, a configuration in which a
The shoe inner repair
When actually making a product, for example, according to the curvature and size of the inner side of the heel of a general shoe, the upper side is arched with a long side of 100 mm and a short side of 60 mm as shown in Fig. 1 (a). A rectangular shape is preferred. Further, it is preferable that a plurality of cut lines are attached to the
本考案の靴内側補修用貼着材1の使用方法(ここでは被貼着面である靴の踵内側への貼着方法)は、例えば以下のとおりである(図2参照)。
靴の踵内側の形状に合わせて、靴内側補修用貼着材1を適当な大きさに鋏等を用いてカットする。なお、上記のように、靴のサイズに合わせた複数のカット線が剥離層5に付けてある場合は、消費者は、自分が使用している靴のサイズに適合するカット線に合わせてカットすればよい。
そして、踵内側にある摩耗欠損部9に付着している埃や汚れを落とし、貼り付けしやすくした後、粘着剤層2から剥離層5を少し剥がし、貼り付ける位置を決めて摩耗欠損部9を覆うように貼り付ける。その後、粘着剤層2から剥離層5を完全に剥がし、摩耗欠損部9に靴内側補修用貼着材1全体を貼り付ける。仮に、少し貼り付けた後で貼り付ける位置を調整したい場合は、ゆっくりと摩耗欠損部9から靴内側補修用貼着材1を剥がした後に調整すればよい。
The method of using the
The
Then, after removing the dust and dirt adhering to the wear-damaged
本考案において、「補修」とは、「修繕する」意味を表す。 In the present invention, "repair" means "to repair".
本考案の靴内側補修用貼着材1に用いられる粘着剤層2は、アクリル系粘着剤、ウレタン系粘着剤、シリコン系粘着剤及びゴム系粘着剤からなる群から選ばれる少なくとも一種の粘着剤を含む。好ましくは、ウレタン系粘着剤及びゴム系粘着剤であり、より好ましくは、ウレタン系粘着剤である。
粘着剤層の厚みは、0.01mm乃至1.0mmであり、好ましくは0.01mm乃至0.7mmmであり、より好ましくは、0.01mm乃至0.5mmであり、特に好ましくは0.01mm乃至0.4mmであり、さらに特に好ましくは、0.01mm乃至0.3mmである。
The
The thickness of the adhesive layer is 0.01 mm to 1.0 mm, preferably 0.01 mm to 0.7 mm, more preferably 0.01 mm to 0.5 mm, particularly preferably 0.01 mm to 0.5 mm. 0.4 mm, more preferably 0.01 mm to 0.3 mm.
本考案の靴内側補修用貼着材1に用いられる不織布層3Aは、ポリエチレン(PE)不織布、ポリプロピレン(PP)不織布、ポリエステル不織布、アラミド不織布、ガラス不織布、セルロース不織布、ナイロン不織布、ビニロン不織布及びレーヨン不織布からなる群から選ばれる少なくとも一種の不織布である。好ましくはポリエチレン不織布、ポリプロピレン不織布及びポリエステル不織布であり、より好ましくは、ポリプロピレン不織布である。ポリエステル不織布としては、ポリエチレンテレフタレート(PET)不織布が好ましい。
The
本考案の靴内側補修用貼着材1に用いられる樹脂フィルム層3Bは、ポリウレタン(PU)フィルム、ポリプロピレン(PP)フィルム及びポリエステルフィルムからなる群からなる群から選ばれる少なくとも一種の樹脂フィルムである。ポリエステルフィルムとしては、ポリエチレンテレフタレート(PET)フィルムが好ましい。
粘着剤層2、表面層4の間に不織布層3A又は樹脂フィルム層3Bを含むので、後述の実施例にも示されるが、粘着剤層2及び表面層5の二層からなる比較例の靴内側補修用貼着材に比べて格段に強い粘着力を有する。しかも、本考案の靴内側補修用貼着材1は、不織布層3A又は樹脂フィルム層3Bを含むことで靴を履いている際の靴の踵内側部分に対する足による押圧力や、靴を履く際に指で引っ掛けて履く際に生じる摩擦に対しても十分な強度を有することができる。
不織布層3Aの厚みは、0.1mm乃至3.0mmであり、好ましくは0.1mm乃至2.5mmmであり、より好ましくは、0.1mm乃至2.0mmであり、特に好ましくは0.1mm乃至1.5mmであり、さらに特に好ましくは、0.1mm乃至1.0mmである。
樹脂フィルム層3Bの厚みは、通常0.1mm乃至3.0mmであるが、これより薄くてもかまわない。
The
Since the
The thickness of the
The thickness of the
粘着力の測定方法は、後述するJIS Z0237:2009に従い測定される。本考案の靴内側補修用貼着材1の粘着力は、2.5N乃至30Nが好ましい。より好ましくは、3N乃至25Nであり、さらに好ましくは、4乃至23Nであり、特に好ましくは、5乃至20Nであり、さらに特に好ましくは、7乃至18Nである。上記範囲に粘着力があるとき、十分に強い強度で靴本体に本考案の靴内側補修用貼着材1が貼着し、かつ、貼り付ける位置の再調整を行うことも可能となる。粘着力が2.5N以下になると靴の脱ぎ履きで靴内側補修用貼着材1が容易に剥がれてしまう虞がある一方、粘着力が30N以上であると、製品としたときに剥離層5が剥がれにくくなる虞があり、さらに、少し貼り付けた後で貼り付ける位置を再調整することが難しくなる虞がある。
The adhesive force is measured according to JIS Z0237:2009, which will be described later. The adhesive force of the
本考案の靴内側補修用貼着材1に用いられる表面層4は、天然皮革、合成皮革、人工皮革、天然繊維及び合成繊維からなる群から選ばれる少なくとも一種の布地からなる。
表面層4は、靴の踵内側の材質及び靴の外側の材質に対応して、色、材質等を合わせることができる。革靴の場合は、例えば、天然皮革、合成皮革又は人口皮革の布地からなるものが好ましく、特に天然皮革としては、例えば、アニリン革、厚物革、ウールスキン、ウォッシャブルレザー、薄物革、馬革、エキゾチックレザー、エナメル革、エルク革、オイルレザー、カーフスキン、カウハイド、ガラスレザー、キッドスキン、キップスキン、クロム革、グローブレザー、ゴートスキン、コードバン、サドルレザー、シープスキン、スエード、スティングレイ、スムースレザー、成牛革、ディアスキン、ヌバック、ヌメ革、豚革、ベロア及びラムスキン等を挙げることができる。一方、スポーツシューズの場合は、合成繊維の布地からなるものが好ましく、例えば、ナイロン樹脂又はポリエステル樹脂からなり、網目状に織られているものがより好ましい。また、合成皮革又は人工皮革としては、例えば、ポリ塩化ビニル(PVC)及びポリウレタン(PU)のものを挙げることができる。
表面層4の厚みは、0.1mm乃至3.0mmであり、好ましくは0.1mm乃至2.5mmmであり、より好ましくは、0.1mm乃至2.0mmであり、特に好ましくは0.1mm乃至1.5mmであり、さらに特に好ましくは、0.1mm乃至1.0mmである。
The
The color and material of the
The thickness of the
本考案の靴内側補修用貼着材1は、実際の販売品においては、粘着剤層2に剥離層5を接着した構成をとることが好ましい。そのような剥離層5としては、粘着剤層2から所定の力で剥離可能なものであれば特に限定されず、例えば、ポリプロピレン、ポリ塩化ビニル、ポリカーボネート(PC)、若しくはポリエチレンテレフタレート(PET)等から
なる離型フィルム、又は離型紙等が使用され、なかでも離型紙は安価に製造できる観点から本考案の靴内側補修用貼着材1に使用するにおいて好ましい。
The
本考案の靴内側補修用貼着材1は、粘着剤層2と、該粘着剤層2より上方の不織布層3A又は樹脂フィルム層3Bと、該不織布層3A又は樹脂フィルム層3Bより上方の表面層4とを備えるが、各層の間に本考案の効果を損なわない限り、別の層があってもよい。例えば、発泡層(クッション層)を設けることが好ましい。上記発泡層としては、例えば、熱可塑性樹脂や熱硬化性樹脂及びゴム等が使用できるがこれらに限定されない。より具体的には、軟質ポリウレタンフォーム、硬質ポリウレタンフォーム、ポリスチレンフォーム、ポリエチレンフォーム、ポリプロピレンフォーム、エチレン酢酸ビニル共重合体(EVA)架橋発泡体、PET樹脂発泡体、フェノールフォーム、シリコーンフォーム、ポリ塩化ビニルフォーム、ユリアフォーム、アクリルフォーム、ポリイミドフォーム及びエチレンプロピレンジエンゴム(EPDM)フォーム等を挙げることができるがこれらに限定されない。好ましくは、軟質ポリウレタンフォーム、硬質ポリウレタンフォーム及びアクリルフォームを使用できる。
発泡層の厚みは、0.1mm乃至4.0mmであり、好ましくは0.1mm乃至3.5mmmであり、より好ましくは、0.1mm乃至3.0mmである。
The shoe inner repair
The foam layer has a thickness of 0.1 mm to 4.0 mm, preferably 0.1 mm to 3.5 mm, more preferably 0.1 mm to 3.0 mm.
本考案において「層」とは、単層だけでなく、複数の層(複層)であってもよい。従って、本考案の靴内側補修用貼着材1を構成する粘着剤層2と、該粘着剤層2より上方の不織布層3A又は樹脂フィルム層3Bと、該不織布層3A又は樹脂フィルム層3Bより上方の表面層4は、いずれも単層だけでなく、複層であってもよい。例えば、粘着剤層2が同一又は異なった種類の複数の層であってもよい。さらに例えば、表面層4が同一又は異なった種類の複数の層であってもよい。さらに例えば、不織布層3Aが、同一又は異なった種類の複数の層であってもよい。さらに例えば、樹脂フィルム層3Bが、同一又は異なった種類の複数の層であってもよい。さらに例えば、複層中に不織布層3A及び樹脂フィルム層3Bがあってもよい。さらに例えば、粘着剤層2の上方に不織布層3Aが設けられ、その上方に粘着剤層2が設けられ、その上方に表面層4が設けられるような靴内側補修用貼着材1であっても本考案に包含される。
In the present invention, "layer" may be not only a single layer but also a plurality of layers (multilayer). Therefore, the
本考案の靴内側補修用貼着材1の全体の厚みは、0.21mm乃至9.0mmであり、好ましくは、0.21mm乃至8.0mmであり、より好ましくは、0.21mm乃至6.0mmであり、特に好ましくは0.21mm乃至5.0mmであり、さらに特に好ましくは、0.21mm乃至4.0mmである。
本考案の靴内側補修用貼着材1の全体の厚みが9.0mm以上であると、後述する実施例の(靴の履き心地評価)でも示されるように、靴の履き心地が悪くなる虞がある。
The overall thickness of the shoe inner repair
If the overall thickness of the shoe inner repair
ここで、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Here, one particularly preferred embodiment of the present invention is an adhesive layer containing a urethane-based adhesive, a nonwoven fabric layer containing a polypropylene nonwoven fabric above the adhesive layer, and a mesh-like fabric above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a nylon resin,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の天然皮革のスエードを含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm
乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
In addition, one of the particularly preferred embodiments of the present invention is a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a non-woven fabric layer containing a polypropylene non-woven fabric above the pressure-sensitive adhesive layer, and natural leather suede above the non-woven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer has a thickness of 0.1 mm.
3.0 mm in thickness, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive strength of the adhesive for repairing the inner side of the shoe measured according to JIS Z0237:2009 is 2.0 mm. An adhesive material for repairing the inner side of a shoe with a thickness of 5N to 30N.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方のポリ塩化ビニルの合成皮革を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is a synthesis of an adhesive layer containing a urethane-based adhesive, a nonwoven fabric layer containing a polypropylene nonwoven fabric above the adhesive layer, and polyvinyl chloride above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing leather,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方のポリウレタンの合成皮革を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
In one particularly preferred embodiment of the present invention, a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a non-woven fabric layer containing a polypropylene non-woven fabric above the pressure-sensitive adhesive layer, and a polyurethane synthetic leather above the non-woven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and an adhesive force of 2.5N to 30N, measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の天然皮革のクロム革を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
In addition, one of the particularly preferred embodiments of the present invention is an adhesive layer containing a urethane-based adhesive, a nonwoven fabric layer containing a polypropylene nonwoven fabric above the adhesive layer, and a chrome leather of natural leather above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の天然皮革の薄物革を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
In addition, one of the particularly preferred embodiments of the present invention is an adhesive layer containing a urethane-based adhesive, a nonwoven fabric layer containing a polypropylene nonwoven fabric above the adhesive layer, and a thin leather of natural leather above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and an adhesive force of 2.5N to 30N, measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ゴム系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferable embodiments of the present invention is an adhesive layer containing a rubber-based adhesive, a nonwoven fabric layer containing a polypropylene nonwoven fabric above the adhesive layer, and a mesh woven above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a nylon resin with
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の網目状に織られているナイロン樹脂からなる表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至0.3mmの厚さであり、前記不織布層が0.1mm乃至1.0mmの厚さであり、前記表面層が0.1mm乃至1.0mmの厚さであり、そ
してJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至20Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is an adhesive layer containing a urethane-based adhesive, a nonwoven fabric layer containing a polypropylene nonwoven fabric above the adhesive layer, and a mesh woven above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer made of a nylon resin containing
The adhesive layer has a thickness of 0.01 mm to 0.3 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 1.0 mm, and the surface layer has a thickness of 0.1 mm to 1.0 mm. and has an adhesive strength of 2.5N to 20N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレン不織布を含む不織布層と、該不織布層より上方の天然皮革のスエードを含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至0.4mmの厚さであり、前記不織布層が0.1mm乃至1.5mmの厚さであり、前記表面層が0.1mm乃至1.5mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至21Nである、靴内側補修用貼着材である。
In addition, one of the particularly preferred embodiments of the present invention is a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a non-woven fabric layer containing a polypropylene non-woven fabric above the pressure-sensitive adhesive layer, and natural leather suede above the non-woven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing
The adhesive layer has a thickness of 0.01 mm to 0.4 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 1.5 mm, and the surface layer has a thickness of 0.1 mm to 1.5 mm. and has an adhesive force of 2.5 N to 21 N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリエチレンテレフタレート不織布を含む不織布層と、該不織布層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a non-woven fabric layer containing polyethylene terephthalate non-woven fabric above the pressure-sensitive adhesive layer, and a mesh-like fabric above the non-woven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a nylon resin,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリエチレン不織布を含む不織布層と、該不織布層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is an adhesive layer containing a urethane-based adhesive, a nonwoven fabric layer containing polyethylene nonwoven fabric above the adhesive layer, and a mesh woven above the nonwoven fabric layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a nylon resin with
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリウレタンフィルムを含む樹脂フィルム層と、該樹脂フィルム層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a resin film layer containing a polyurethane film above the pressure-sensitive adhesive layer, and a network above the resin film layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a woven nylon resin,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリプロピレンフィルムを含む樹脂フィルム層と、該樹脂フィルム層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a resin film layer containing a polypropylene film above the pressure-sensitive adhesive layer, and a network above the resin film layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a woven nylon resin,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
また、本考案の特に好ましい態様の一つは、ウレタン系粘着剤を含む粘着剤層と、該粘着剤層より上方のポリエステルフィルムを含む樹脂フィルム層と、該樹脂フィルム層より上方の網目状に織られているナイロン樹脂を含む表面層とを備えてなる靴内側補修用貼着材であって、
前記粘着剤層が、0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層が0.1mm乃至3.0mmの厚さであり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nである、靴内側補修用貼着材である。
Further, one of the particularly preferred embodiments of the present invention is a pressure-sensitive adhesive layer containing a urethane-based pressure-sensitive adhesive, a resin film layer containing a polyester film above the pressure-sensitive adhesive layer, and a network above the resin film layer. An adhesive material for repairing the inner side of a shoe, comprising a surface layer containing a woven nylon resin,
The adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer has a thickness of 0.1 mm to 3.0 mm, and the surface layer has a thickness of 0.1 mm to 3.0 mm. and has an adhesive strength of 2.5N to 30N as measured according to JIS Z0237:2009.
以下に本考案の実施例を示し、さらに具体的に説明するが、本考案は、これらに限定されるものではなく、本考案の技術的思想を逸脱しない範囲内で種々の応用が可能である。 Examples of the present invention will be shown below and described more specifically, but the present invention is not limited to these, and various applications are possible without departing from the technical idea of the present invention. .
[実施例1]
実施例1の靴内側補修用貼着材1は、粘着剤層2、不織布層3A及び表面層4を備える。粘着剤層2は、ポリウレタン(PU)系粘着剤が塗布された粘着剤層であって、その厚みは、0.05mmであり、不織布層3Aは、ポリプロピレン(PP)不織布であって、その厚みは、0.5mmであり、表面層4は、ナイロン樹脂が網目状に織られた生地であって、その厚みは、0.5mmである。
[Example 1]
The shoe inner repair
[実施例2]
実施例2の靴内側補修用貼着材1は、実施例1と同じく粘着剤層2、不織布層3A及び表面層4を備える。粘着剤層2は、ポリウレタン系粘着剤が塗布された粘着剤層であって、その厚みは、0.05mmであり、不織布層3は、ポリプロピレン不織布であって、その厚みは、0.5mmであり、表面層4は、豚革のスエードであって、その厚みは、0.5mmである。
[Example 2]
The shoe inner repair
[実施例3]
実施例3の靴内側補修用貼着材1は、実施例1と同じく粘着剤層2、不織布層3A及び表面層4を備える。粘着剤層2は、ポリウレタン系粘着剤が塗布された粘着剤層であって、その厚みは、0.05mmであり、不織布層3は、ポリプロピレン不織布であって、その厚みは、0.5mmであり、表面層4は、ポリ塩化ビニル(PVC)製の合成皮革であって、その厚みは、0.5mmである。
[Example 3]
The shoe inner repair
実施例4乃至実施例9の靴内側補修用貼着材1について、各層の種類及び後述する方法で測定した粘着力を併せて表1に示す。
Table 1 shows the type of each layer and the adhesive force measured by the method described later for the shoe inner repair
[比較例1]
比較例1の靴内側補修用貼着材は、粘着剤層2及び表面層4を備える。粘着層2は、ポリウレタン系粘着剤が塗布された粘着剤層であって、その厚みは、0.05mmであり、表面層4は、ナイロン樹脂が網目状に織られた生地であって、その厚みは、0.5mmである。
[Comparative Example 1]
The shoe inner repair adhesive material of Comparative Example 1 includes an
[比較例2]
比較例2の靴内側補修用貼着材は、実施例1と同じく粘着剤層2、不織布層3A及び表面層4を備える。粘着剤層2は、ポリウレタン系粘着剤が塗布された粘着剤層であって、その厚みは、3.0mmであり、不織布層3は、ポリプロピレン不織布であって、その厚みは、4.0mmであり、表面層4は、ポリ塩化ビニル(PVC)製の合成皮革であって、その厚みは、4.0mmである。
[Comparative Example 2]
The shoe inner repair adhesive material of Comparative Example 2 includes the pressure-
[比較例3]
比較例3の靴内側補修用貼着材は、実施例1と同じく粘着剤層2、不織布層3A及び表面層4を備える。粘着剤層2は、ポリウレタン系粘着剤が塗布された粘着剤層であって、その厚みは、4.0mmであり、不織布層3は、ポリプロピレン不織布であって、その厚
みは、5.0mmであり、表面層4は、ポリ塩化ビニル(PVC)製の合成皮革であって、その厚みは、5.0mmである。
[Comparative Example 3]
The shoe inner repair adhesive material of Comparative Example 3 includes the
(粘着力評価)
粘着力の測定方法は、JIS Z0237:2009に従い測定した。靴内側補修用貼着材から幅24mm、長さ300mmの試験片を切断した。そして、該試験片をステンレス板に貼り付け、試験片の上から圧着ローラを用いて圧着した。その後、試験片を、表面層4が重なるように試験片の端を持って180度に折り返し、ステンレス板から25mm剥がし、試験機に設置した下側の治具にその試験片をはがした部分の試験板の片端を固定し,上側の治具に試験片を固定した。300mm/minの負荷速度で試験を実施した。測定開始後,最初の25mmの長さの測定値は無視し,その後,試験板から引きはがされた50mmの長さの粘着力測定値を平均し,粘着力の値とした。上記した実施例1乃至実施例9及び比較例1乃至比較例3の靴内側補修用貼着材の粘着力を表1に示す。
(Adhesive strength evaluation)
The adhesive force was measured according to JIS Z0237:2009. A test piece having a width of 24 mm and a length of 300 mm was cut from the shoe inner repair adhesive material. Then, the test piece was attached to a stainless steel plate, and pressed from above using a pressing roller. After that, the test piece is folded back at 180 degrees with the end of the test piece so that the
(靴の脱ぎ履き試験評価)
実施例1乃至実施例9及び比較例1乃至比較例3の靴内側補修用貼着材を貼り付けた靴の脱ぎ履き試験を評価した。まず、スポーツシューズの踵内側に縦1cm、横1cmに十字に傷をつけ、ヒールカウンターを露出させ、次に、実施例1乃至実施例9及び比較例1乃至比較例3の靴内側補修用貼着材を傷部分が覆えるように長辺60mm、短辺40mm程度の上辺が弓形の長方形状にカットし、傷部分に貼りつけた。このスポーツシューズの脱ぎ履きを300回行った。そして以下の要領で評価した。結果を表2に示す。
○:靴内側補修用貼着材が靴の踵内側から剥がれない。
×:靴内側補修用貼着材の一部が靴の踵内側から剥がれる。
(Evaluation of putting on and taking off shoes)
The shoes to which the adhesive materials for repairing the inner side of shoes of Examples 1 to 9 and Comparative Examples 1 to 3 were attached were evaluated in a putting on and taking off test. First, a 1 cm long and 1 cm wide cross-shaped scratch was made on the inside of the heel of the sports shoe to expose the heel counter. The adhesive material was cut into a rectangular shape having a long side of 60 mm and a short side of 40 mm so that the upper side was arched so as to cover the damaged part, and the rectangular shape was attached to the damaged part. Put on and take off these sports shoes 300 times. Then, it was evaluated in the following manner. Table 2 shows the results.
◯: The adhesive material for repairing the inner side of the shoe did not come off from the inner side of the heel of the shoe.
x: Part of the adhesive material for repairing the inner side of the shoe is peeled off from the inner side of the heel of the shoe.
(靴の履き心地評価)
実施例1乃至実施例9及び比較例1乃至比較例3の靴内側補修用貼着材を貼り付けた靴の履き心地を以下の方法で評価した。靴の履き心地については<靴の履きやすさ>、<靴を履いて歩いた際の足の踵部への感触>及び<靴の脱ぎやすさ>の3つの指標を勘案して評価した。靴内側補修用貼着材が実際に使用に耐えるかは、靴内側補修用貼着材を使用しても良好な履き心地であるかが非常に重要である。<靴の履きやすさ>とは、靴を履く際に靴内側補修用貼着材に踵が引っかかるような違和感がなく履きやすいか否かである。<靴を履いて歩いた際の足の踵部への感触>とは、靴を履いて歩いている際に靴内側補修用貼着材が踵を圧迫するような違和感があるか否かである。<靴の脱ぎやすさ>とは、靴を脱ぐ際に靴内側補修用貼着材に踵が引っかかるような違和感がなく脱ぎやすいか否かである。これら3つの点をいずれも5段階で被験者に評価させ、いずれの点も優れていなければ消費者が使用するには適さないと考えた。より具体的には、下記の方法を採用して評価を行った。まず、スポーツシューズの踵内側に縦1cm、横1cmに十字に傷をつけ、ヒールカウンターを露出させ、次に、実施例1乃至実施例9及び比較例1乃至比較例3の靴内側補修用貼着材を傷部分が覆えるように長辺60mm、短辺40mm程度の上辺が弓形の長方形状にカットし、傷部分に貼りつけた。そして、該スポーツシューズを成人男女10人の被験者に履かせ、各人に<靴の履きやすさ>、<靴を履いて歩いた際の足の踵部への感触>及び<靴の脱ぎやすさ>を5段階のスコアリングに照らして評価させた。そして、10人の3つの項目の平均値を算出し、3つの項目の平均点が全て4点以上であるものを◎(靴の履き心地が非常に優れる)とし、3点以上4点が含まれるものを〇(靴の履き心地が優れる)とし、2点以上3点未満が含まれるものを△(靴の履き心地がよくない)とし、2点未満が含まれるものを×(靴の履き心地として不適格)とした。ここで、例えば、<靴の履きやすさ>の平均点が3点以上4点であり、<靴を履いて歩いた際の足の踵部への感触>の平均点が3点以上4点であり、<靴の脱ぎやすさ>の平均が2点以上3点未満である場合は、靴の履き心地については△とした。
<靴の履きやすさ>
5 : 履きやすい
4 : やや履きやすい
3 : どちらともいえない
2 : やや履きにくい
1 : 履きにくい
<靴を履いて歩いた際の足の踵部への感触>
5 : 気にならない
4 : ほぼ気にならない
3 : どちらともいえない
2 : やや違和感がある
1 : 違和感がある
<靴の脱ぎやすさ>
5 : 脱ぎやすい
4 : やや脱ぎやすい
3 : どちらともいえない
2 : やや脱ぎにくい
1 : 脱ぎにくい
(Shoe comfort evaluation)
The comfort of the shoes to which the adhesive materials for repairing the shoe inner side of Examples 1 to 9 and Comparative Examples 1 to 3 were attached was evaluated by the following method. The wearing comfort of shoes was evaluated by taking into consideration the following three indicators: <ease of wearing shoes>, <feel on the heel of the foot when walking in shoes>, and <ease of taking off shoes>. It is very important whether the adhesive material for repairing the inner side of the shoe is actually usable and whether the adhesive material for repairing the inner side of the shoe is comfortable to wear. <Ease of wearing shoes> refers to whether or not the shoes are comfortable to wear without causing discomfort such as the heel being caught by the adhesive material for repairing the inner side of the shoe. <Feeling on the heel of the foot when walking in shoes> refers to whether or not there is a sense of incongruity, such as pressure on the heel by the adhesive material for repairing the inner side of the shoe, when walking in the shoes. be. <Ease of taking off the shoes> refers to whether or not the shoes are easy to take off without discomfort such as the heel being caught by the adhesive material for repairing the inner side of the shoe. All of these three points were evaluated by subjects on a 5-point scale, and if they were not excellent in any of the points, they were considered unsuitable for use by consumers. More specifically, evaluation was carried out using the following method. First, a 1 cm long and 1 cm wide cross-shaped scratch was made on the inside of the heel of the sports shoe to expose the heel counter. The adhesive material was cut into a rectangular shape having a long side of 60 mm and a short side of 40 mm so that the upper side was arched so as to cover the damaged part, and the rectangular shape was attached to the damaged part. Then, 10 adult male and female subjects were asked to wear the sports shoes, and each subject was asked for <ease of putting on the shoes>, <feeling of the heel of the foot when walking in shoes>, and <ease of taking off the shoes>. > was evaluated in light of 5-grade scoring. Then, the average value of the three items of 10 people was calculated, and those with an average score of 4 points or more for all three items were marked as ◎ (the shoes are extremely comfortable to wear), and 3 points or more and 4 points were included. Those with 2 or more but less than 3 points were given △ (not comfortable to wear shoes), and those with less than 2 points were given × (comfortable shoes). unsuitable for comfort). Here, for example, the average score for <ease of wearing shoes> is 3 to 4 points, and the average score for <touch on the heel of the foot when walking in shoes> is 3 to 4 points. When the average score of <easiness of taking off shoes> was 2 or more and less than 3, the comfort of wearing shoes was evaluated as Δ.
<Ease of wearing shoes>
5: Easy to wear 4: Somewhat easy to wear 3: Neither 2: Somewhat difficult to wear 1: Difficult to wear
5: Not bothering me 4: Almost not bothering me 3: Neither 2: Somewhat uncomfortable 1: Feeling uncomfortable <Easy to take off shoes>
5: Easy to take off 4: Somewhat easy to take off 3: Neither 2: Somewhat difficult to take off 1: Difficult to take off
表1に示すように、実施例1乃至実施例9の靴内側補修用貼着材にあっては、粘着力が2.5N乃至30Nの範囲にあって、靴の脱ぎ履き試験において、靴内側補修用貼着材が靴の踵内側から剥がれないとの結果が得られた。さらに、靴の履き心地が優れるとの結果が得られた。
一方、比較例1にあっては、靴の脱ぎ履き試験において、補修用貼着材の一部が靴の踵内側から剥がれる結果となり、比較例2及び比較例3にあっては、履き心地試験において、靴の履き心地がよくない又は靴の履き心地として不適格との結果が得られた。
As shown in Table 1, in the adhesive materials for repairing the inner side of shoes of Examples 1 to 9, the adhesive strength was in the range of 2.5 N to 30 N, A result was obtained that the patch for repair did not come off from the inside of the heel of the shoe. Furthermore, the results indicated that the shoes were more comfortable to wear.
On the other hand, in Comparative Example 1, part of the repair adhesive material was peeled off from the inner side of the heel in the shoe putting on and taking off test, and in Comparative Examples 2 and 3, the wearing comfort test was performed. , the result was that the shoes were not comfortable to wear, or that the shoes were not comfortable to wear.
1 靴内側補修用貼着材
2 粘着剤層
3A 不織布層
3B 樹脂フィルム層
4 表面層
5 剥離層
6 外革
7 クッション材
8 裏革
9 摩耗欠損部
10 靴
11 ロゴ
1 Adhesive material for repairing shoe
Claims (32)
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. An adhesive material for repairing the inside of a shoe with a cut line attached.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS
Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. , the surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and JIS
The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to Z0237:2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and an adhesive material is attached to the release layer for each shoe size. An adhesive material for repairing the inside of a shoe with a plurality of cut lines that match the outer shape of the shoe.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, and a release layer is adhered to the adhesive layer, and a plurality of adhesive materials are attached to the release layer according to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a cut line attached.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至
3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. An adhesive material for repairing the inside of a shoe with a cut line attached.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009. A shoe having an adhesive strength of 2.5 N to 30 N, a release layer adhered to the adhesive layer, and a plurality of cut lines corresponding to the outer shape of the adhesive material for each shoe size. Adhesive material for inner repair.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive strength of the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of cut lines are attached to the release layer according to the outer shape of the adhesive material for each shoe size. adhesive.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a plurality of cut lines.
前記粘着剤層がアクリル系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of an acrylic adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of a polyester resin, the polyester resin is woven into a mesh, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a plurality of cut lines attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of adhesive materials matching the outer shape of the adhesive material are attached to the adhesive layer for each shoe size. An adhesive material for repairing the inside of a shoe with a cut line attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエチレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of polyethylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber cloth, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS
Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and JIS
The adhesive strength of the adhesive material for shoe inner repair measured according to Z0237:2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and an adhesive material is attached to the release layer for each shoe size. An adhesive material for repairing the inside of a shoe with a plurality of cut lines that match the outer shape of the shoe.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, and a release layer is adhered to the adhesive layer, and a plurality of adhesive materials are attached to the release layer according to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a cut line attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリプロピレン不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定され
る前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the nonwoven fabric layer is made of a polypropylene nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and according to JIS Z0237: 2009 The adhesive strength of the adhesive material for repairing the inner side of the shoe to be measured is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is fitted to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic leather fabric, the synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009. The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, and a release layer is adhered to the adhesive layer, and a plurality of adhesive materials are attached to the release layer according to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a cut line attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記不織布層がポリエステル不織布からなり、該不織布層が0.1mm乃至3.0mmの厚さであり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe, comprising an adhesive layer, a nonwoven fabric layer above the adhesive layer, and a surface layer above the nonwoven fabric layer, and having a rectangular shape with an arched upper side,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, and the nonwoven fabric layer is made of a polyester nonwoven fabric, and the nonwoven fabric layer has a thickness of 0.1 mm to 3.0 mm. The surface layer is made of synthetic fiber fabric, the synthetic fiber is made of polyester resin, the polyester resin is woven in a mesh shape, and the surface layer is 0.1 mm to 3.0 mm. The adhesive strength of the adhesive material for repairing the inner side of shoes measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is attached to the shoe. An adhesive material for repairing the inner side of a shoe, to which a plurality of cut lines are attached according to the outer shape of the adhesive material for each size.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムから
なり、前記表面層が合成皮革の布地からなり、該合成皮革がポリ塩化ビニルからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyvinyl chloride, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009. A shoe having an adhesive force of 2.5 N to 30 N, a release layer adhered to the adhesive layer, and a plurality of cut lines corresponding to the outer shape of the adhesive material for each shoe size. Adhesive material for inner repair.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成皮革の布地からなり、該合成皮革がポリウレタンからなり、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is synthetic leather. The synthetic leather is made of polyurethane, the surface layer has a thickness of 0.1 mm to 3.0 mm, and the adhesive strength of the adhesive material for repairing the inner side of the shoe is measured according to JIS Z0237: 2009 is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and a plurality of cut lines are attached to the release layer according to the outer shape of the adhesive material for each shoe size. adhesive.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がナイロン樹脂からなり、該ナイロン樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of nylon resin, the nylon resin is woven in a mesh shape, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a plurality of cut lines attached.
前記粘着剤層がウレタン系粘着剤からなり、該粘着剤層が0.01mm乃至1.0mmの厚さであり、前記樹脂フィルム層がポリエチレンテレフタレート(PET)フィルムからなり、前記表面層が合成繊維の布地からなり、該合成繊維がポリエステル樹脂からなり、該ポリエステル樹脂が網目状に織られており、前記表面層が0.1mm乃至3.0mmの厚さであり、そしてJIS Z0237:2009に従い測定される前記靴内側補修用貼着材の粘着力が2.5N乃至30Nであり、前記粘着剤層に剥離層が接着され、該剥離層に靴のサイズごとに貼着材の外形に合わせた複数のカット線が付けられている、靴内側補修用貼着材。 An adhesive material for repairing the inner side of a shoe comprising an adhesive layer, a resin film layer above the adhesive layer, and a surface layer above the resin film layer, and having a rectangular shape with an arched upper side. hand,
The adhesive layer is made of a urethane-based adhesive, the adhesive layer has a thickness of 0.01 mm to 1.0 mm, the resin film layer is made of a polyethylene terephthalate (PET) film, and the surface layer is a synthetic fiber. The synthetic fiber is made of a polyester resin, the polyester resin is woven into a mesh, the surface layer has a thickness of 0.1 mm to 3.0 mm, and is measured according to JIS Z0237: 2009 The adhesive force of the adhesive material for repairing the inner side of the shoe is 2.5 N to 30 N, a release layer is adhered to the adhesive layer, and the release layer is matched to the outer shape of the adhesive material for each shoe size. An adhesive material for repairing the inside of a shoe with a plurality of cut lines attached.