JP3220954B2 - Golf club head - Google Patents
Golf club headInfo
- Publication number
- JP3220954B2 JP3220954B2 JP35412492A JP35412492A JP3220954B2 JP 3220954 B2 JP3220954 B2 JP 3220954B2 JP 35412492 A JP35412492 A JP 35412492A JP 35412492 A JP35412492 A JP 35412492A JP 3220954 B2 JP3220954 B2 JP 3220954B2
- Authority
- JP
- Japan
- Prior art keywords
- head
- golf club
- face
- club head
- maximum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Description
【0001】[0001]
【産業上の利用分野】この発明は、ソール幅がフェース
高さ以上あるゴルフクラブヘッド、所謂ウッドクラブと
呼ばれるゴルフクラブヘッドに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf club head having a sole width equal to or larger than a face height, that is, a golf club head called a so-called wood club.
【0002】[0002]
【従来の技術】従来のウッドクラブのヘッドは、形成材
料としてステンレス鋼,アルミニウム合金,チタン合
金,マグネシウム合金等のメタル材料や繊維強化プラス
チック(FRP)材料等が使用され、強度,重量,重心
位置,コスト面等の配慮から各種の大きさのものが開発
されている。2. Description of the Related Art A conventional wood club head is made of a metal material such as stainless steel, aluminum alloy, titanium alloy, magnesium alloy, or fiber reinforced plastic (FRP) as a forming material, and has strength, weight, and center of gravity. Various sizes have been developed in consideration of cost and cost.
【0003】最近は、ドライバーのヘッドの大型化が図
られ、スィートエリアを拡大し、慣性モーメントを高く
する試みがなされている。ヘッドのスィートスポットで
ボールをヒットした場合に最大飛距離が得られるが、実
際にはスポットをはずしてヒットすることが多い。アマ
チュアゴルファーはヘッドのフェースの幾何学的中心で
ボールを打とうとするが、幾何学的中心とスィートスポ
ットとが必ずしも一致していないヘッドが多く、スィー
トスポットをはずしてヒットすることとなる。スィート
スポットをはずしてヒットしても飛距離の低下を最小限
におさえるため、スィートエリアの拡大が望まれてい
る。ここで、スィートエリアとは、スィートスポットで
ヒットしたときのボールの落下点から左右に最大飛距離
の2.5%ずつ離れた点と、落下点より打撃点方向に最
大飛距離の5%戻った点から左右に最大飛距離の2.5
%ずつ離れた点とを頂点とする正方領域内にボールが落
下するクラブヘッドのフェース上の全ての集合エリアを
いう。In recent years, attempts have been made to increase the size of the driver's head, enlarge the sweet area, and increase the moment of inertia. The maximum flight distance is obtained when hitting the ball at the sweet spot of the head, but in practice, the hit is often taken off the spot. Amateur golfers try to hit the ball at the geometric center of the face of the head, but many of the heads do not always coincide with the geometric center and the sweet spot. In order to minimize the drop in flight distance even if a hit is made without the sweet spot, it is desired to expand the sweet area. Here, the sweet area is a point that is 2.5% of the maximum flight distance left and right from the ball drop point when hitting at the sweet spot, and 5% of the maximum flight distance in the direction of the hit point from the drop point. The maximum flight distance of 2.5 from left to right from the point
All the collective areas on the face of the club head where the ball falls into a square area having a vertex at a point separated by%.
【0004】[0004]
【発明が解決しようとする課題】従来の所謂デカヘッド
と呼ばれるものでは、ヘッド体積が200cc前後であ
る。このようなデカヘッドよりもさらに易しく打て、オ
フセンターヒット時にも飛距離の減少を最小にとどめる
ことができるものが望まれている。そのためには、スィ
ートエリアのさらなる拡大を図り、重心位置とフェース
面との距離をさらに長くし、しかも強度面での問題も生
じない必要がある。A conventional so-called deca head has a head volume of about 200 cc. There is a demand for a head that can be hit more easily than such a deca head and that minimizes the decrease in flight distance even during an off-center hit. For this purpose, it is necessary to further enlarge the sweet area, further increase the distance between the position of the center of gravity and the face surface, and not cause a problem in strength.
【0005】そこで、この発明は、スィートエリアのさ
らなる拡大を図り、重心を深くし、強度面で問題の生じ
ないゴルフクラブヘッドを提供することを目的とする。Accordingly, an object of the present invention is to provide a golf club head which further enlarges the sweet area, deepens the center of gravity, and has no problem in strength.
【0006】[0006]
【課題を解決するための手段】上述の目的を達成するた
め、この発明は、ソール幅がフェース高さ以上あるゴル
フクラブヘッドであって、フェース面の形成材料とフェ
ース面を除くヘッド形成材料として夫々比強度140以
上のマグネシウム合金を使用してヘッドを形成し、フェ
ース面のヘッド最大高さを48mm以上、シャフト基準ヘ
ッド長さを86mm以上、ヘッド最大幅を85mm以上とし
たものである。SUMMARY OF THE INVENTION In order to achieve the above-mentioned object, the present invention provides a golf club head having a sole width equal to or greater than a face height, wherein the golf club head has a face surface and a head material other than the face surface. The head is formed by using a magnesium alloy having a specific strength of 140 or more, and the maximum head height of the face surface is 48 mm or more, the shaft reference head length is 86 mm or more, and the maximum head width is 85 mm or more.
【0007】[0007]
【作用】この発明では、比強度140以上の材料でフェ
ース面とフェース面を除くヘッドを形成するため、強度
面での問題がなく、ヘッドを大きくすることができ、ヘ
ッドが大きくなることによりスィートエリアの拡大が図
れる。例えば、ヘッド体積250cc以上のものであれ
ば、スィートエリアが著しく拡大し、重心も深くなり、
ボールの左右方向の弾道安定性を向上させる。According to the present invention, since the face and the head excluding the face are formed from a material having a specific strength of 140 or more, there is no problem in the strength, and the head can be made larger. The area can be enlarged. For example, if the head volume is 250 cc or more, the sweet area is significantly expanded and the center of gravity is deepened,
Improves ballistic stability in the horizontal direction of the ball.
【0008】[0008]
【実施例】以下に、この発明の好適な実施例を図面を参
照にして説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below with reference to the drawings.
【0009】図1は、このゴルフクラブヘッドの正面図
を示し、フェース面1のヘッド最大高さHを48mm以上
とし、シャフト基準ヘッド長さLを86mm以上としてあ
る。このシャフト基準ヘッド長さLは、シャフト2の中
心軸を通る平面とその平面に平行でヘッドのトウ側に接
する平面との距離をいう。フェース面1とフェース面1
を除くヘッド形成材料としては、比強度140以上のマ
グネシウム合金を用いる。比強度とは、引張り強度(M
Pa)を密度(g/cm3)で割った値をいう。メタル材
料の比強度は、比強度の大きい方からチタン,ステンレ
ス,アルミニウムおよびマグネシウムとなる。したがっ
て、比強度のみで材料を考慮するとチタンが最適である
が、チタンはコスト面で問題があった。また、ステンレ
スは比重の面からヘッドの軽量化を図るには問題があっ
た。また、アルミニウムはマグネシウムと比較して比重
の面で劣る。このようなメタル材料中フェース面1を含
むヘッド全体をマグネシウム合金から形成することで、
ヘッド重量を従来ヘッドの重量と同程度としつつ、より
大型化し、強度面の問題も生じない。FIG. 1 shows a front view of the golf club head, wherein the maximum head height H of the face surface 1 is 48 mm or more, and the shaft reference head length L is 86 mm or more. The shaft reference head length L refers to a distance between a plane passing through the center axis of the shaft 2 and a plane parallel to the plane and in contact with the toe side of the head. Face 1 and Face 1
A magnesium alloy having a specific strength of 140 or more is used as a head forming material except for. The specific strength is the tensile strength (M
Pa) divided by the density (g / cm 3 ). The specific strength of the metal material is titanium, stainless steel, aluminum, and magnesium in the order of higher specific strength. Therefore, titanium is optimal when considering the material only with the specific strength, but titanium has a problem in cost. In addition, stainless steel has a problem in reducing the weight of the head in terms of specific gravity. Aluminum is inferior in specific gravity as compared with magnesium. By forming the entire head including the face surface 1 in such a metal material from a magnesium alloy,
The weight of the head is about the same as the weight of the conventional head, while the head is made larger and the problem of strength does not occur.
【0010】図2はヘッドの側面図であり、ヘッド最大
幅Wを85mm以上とした。図1および図2に示すゴルフ
クラブヘッドは全体を比強度140以上のマグネシウム
合金とし、フェース面1のヘッド最大高さHを51.3
mm、シャフト基準ヘッド長さLを89.5mm、ヘッド最
大幅Wを86mmとし、ヘッド体積を260ccとした。ま
た、ヘッドのクラウン部3は厚さを1mmとし、その他の
厚さを3.5mmとした。これにより軽量化および低重心
化が図れた。このヘッドの内部は空洞あるいは内部にウ
レタンフォーム等を充填する。ヘッドのフェース面1と
クラウン部3との間には、補強のためにそれぞれ端部か
ら15mmの位置まで三角形状のリブ4を取付けた。FIG. 2 is a side view of the head, in which the maximum head width W is 85 mm or more. The golf club head shown in FIGS. 1 and 2 is entirely made of a magnesium alloy having a specific strength of 140 or more, and the head maximum height H of the face surface 1 is set to 51.3.
mm, the shaft reference head length L was 89.5 mm, the head maximum width W was 86 mm, and the head volume was 260 cc. The crown 3 of the head had a thickness of 1 mm, and the other thicknesses were 3.5 mm. As a result, the weight and the center of gravity were reduced. The inside of this head is filled with urethane foam or the like in the cavity or inside. Triangular ribs 4 were attached between the face 1 of the head and the crown 3 to a position 15 mm from each end for reinforcement.
【0011】このようなヘッドを有するゴルフクラブで
50m/sの速度でボールを3000発ヒットしたが、
ヘッドに異常はなく強度面での問題のないことが判明し
た。A golf club having such a head hits 3000 balls at a speed of 50 m / s.
It was found that there was no abnormality in the head and no problem in strength.
【0012】上述したようなサイズを有するマグネシウ
ム合金から成るヘッドを有するゴルフクラブを12名の
プロゴルファーと、6名のアシスタントプロゴルファー
と、11名のアマチュアゴルファーに実打させたときの
評価を次表に示す。The following table shows the evaluation results when golf clubs having a head made of a magnesium alloy having the above-mentioned size were actually hit by 12 professional golfers, 6 assistant professional golfers, and 11 amateur golfers. Show.
【0013】[0013]
【表1】 [Table 1]
【0014】表1から評価良いの比率が約60〜70
%、評価普通の比率が約20〜30%、評価悪いの比率
が約10〜20%で実打したゴルファーの大半が満足し
ていることが判明した。From Table 1, the ratio of good evaluation is about 60 to 70.
%, The average rating was about 20 to 30%, and the poor rating was about 10 to 20%, indicating that most golfers who hit the ball were satisfied.
【0015】実打試験を行なったものは、比強度140
以上のマグネシウム合金によりヘッドを形成したので、
ヘッド体積は250cc以上〜300cc超とすることも可
能である。なお、ゴルファーがスィートエリアを拡大
し、使い易いと感じるのは、スィートエリアが従来に比
べて2割以上拡大したときであることが判明している。
2割以下であると効果が実感として感じられない。[0015] An actual hit test was carried out to obtain a specific strength of 140.
Since the head was formed with the above magnesium alloy,
The head volume can be 250 cc or more to more than 300 cc. It has been found that the golfer enlarges the sweet area and feels easy to use when the sweet area is enlarged by 20% or more compared to the conventional art.
If it is less than 20%, the effect is not felt as real.
【0016】[0016]
【発明の効果】以上説明したように、この発明では、フ
ェース面の形成材料とフェース面を除くヘッド形成材料
として夫々比強度140以上のマグネシウム合金を使用
してヘッドを形成し、フェース面のヘッド最大高さを4
8mm以上、シャフト基準ヘッド長さを86mm以上、ヘッ
ド最大幅を85mm以上としたので、スィートエリアの著
しい拡大が可能となり、重心も深くなり、スィートスポ
ットを外してヒットしても飛距離の減少を最小限に抑え
ることができ、しかもボールの左右方向の弾道安定性を
向上させることができる。また、強度面での問題もな
く、ヘッド全体を大きくすることができる。さらに、ヘ
ッドの肉厚による周辺重量配分により低重心化や慣性モ
ーメントの向上を図ることができる。As described above, according to the present invention, a head is formed using a magnesium alloy having a specific strength of 140 or more as a material for forming the face surface and a head forming material excluding the face surface. Maximum height is 4
8mm or more, the shaft reference head length is 86mm or more, and the maximum head width is 85mm or more. The trajectory stability in the left-right direction of the ball can be improved while minimizing it. In addition, the entire head can be enlarged without any problem in strength. Further, a lower center of gravity and an improved moment of inertia can be achieved by allocating the peripheral weight by the thickness of the head.
【図1】この発明のゴルフクラブヘッドの正面図。FIG. 1 is a front view of a golf club head according to the present invention.
【図2】側面図。FIG. 2 is a side view.
1 フェース面 2 シャフト 1 face side 2 shaft
フロントページの続き (56)参考文献 特開 平4−12772(JP,A) (58)調査した分野(Int.Cl.7,DB名) A63B 53/00 - 53/16 Continuation of the front page (56) References JP-A-4-12772 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) A63B 53/00-53/16
Claims (1)
クラブヘッドであって、 フェース面の形成材料とフェース面を除くヘッド形成材
料として夫々比強度140以上のマグネシウム合金を使
用してヘッドを形成し、 フェース面のヘッド最大高さを48mm以上、シャフト基
準ヘッド長さを86mm以上、ヘッド最大幅を85mm以上
としたことを特徴とするゴルフクラブヘッド。1. A golf club head having a sole width equal to or greater than a face height, wherein the head is formed using a magnesium alloy having a specific strength of 140 or more as a material for forming the face surface and a head forming material excluding the face surface. A golf club head having a maximum face height of 48 mm or more on a face surface, a standard shaft length of 86 mm or more, and a maximum head width of 85 mm or more.