JP3209713B2 - Lubricant for injection sleeve - Google Patents
Lubricant for injection sleeveInfo
- Publication number
- JP3209713B2 JP3209713B2 JP1268898A JP1268898A JP3209713B2 JP 3209713 B2 JP3209713 B2 JP 3209713B2 JP 1268898 A JP1268898 A JP 1268898A JP 1268898 A JP1268898 A JP 1268898A JP 3209713 B2 JP3209713 B2 JP 3209713B2
- Authority
- JP
- Japan
- Prior art keywords
- wax
- oil
- injection sleeve
- lubricant
- injection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Description
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【発明の属する技術分野】本発明は潤滑剤に関し、特に
鋳造装置における射出スリーブ内へ投入してプランジャ
ーチップの動作をスムーズに行うための射出スリーブ用
潤滑剤に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lubricant, and more particularly, to a lubricant for an injection sleeve which is introduced into an injection sleeve of a casting apparatus to smoothly operate a plunger tip.
【０００２】[0002]
【従来の技術】周知の如く、ダイカストマシンの射出ス
リーブ用の潤滑剤は油性潤滑剤と水性潤滑剤とに大別さ
れる。しかし、油性潤滑剤は引火の危険や発煙による作
業環境上の問題がある。一方、水性潤滑剤は、油性潤滑
剤に比べて引火の危険や発煙による作業環境上の問題は
ないが、潤滑性能に劣る。そこで、水性潤滑剤において
は、潤滑性能を向上させるために黒鉛やボロン等の粉末
を混入させている。しかし、この場合作業環境が低下す
るという問題がある。2. Description of the Related Art As is well known, lubricants for injection sleeves of die casting machines are roughly classified into oil-based lubricants and aqueous lubricants. However, oil-based lubricants have problems in working environment due to danger of ignition and smoking. On the other hand, the aqueous lubricant has no danger of ignition or a problem in working environment due to smoking compared to the oil-based lubricant, but is inferior in lubricating performance. Therefore, powders such as graphite and boron are mixed in the aqueous lubricant to improve the lubrication performance. However, in this case, there is a problem that the working environment is reduced.
【０００３】また、潤滑剤は通常液状あるいはペースト
状であるため、ダイカストマシン周辺に容易に付着して
機械を汚染したり、廃液に混入して排水処理を繁雑にす
る等の弊害がある。Further, since the lubricant is usually in the form of a liquid or a paste, there is a problem that the lubricant easily adheres to the periphery of the die-casting machine and contaminates the machine, or is mixed with the waste liquid to complicate wastewater treatment.
【０００４】[0004]
【発明が解決しようとする課題】この発明はこうした事
情を考慮してなされたもので、ステアリン酸、脂肪酸ア
ミド、ポリエチレン、酸化ポリエチレン、酸化ポリエチ
レンワックス、パラフィン、植物性ワックス、ポリプロ
ピレン、鉱物油、植物油、合成油、石油系ワックス、石
油系樹脂、合成樹脂、アルカアミド、蜜ろう、シリコン
オイル、シリコンワックス、ポリブテン、オレフィン系
合成炭化水素、から選ばれた１種若しくは２種以上の自
己潤滑性を有する粉体又は混合体であり、常温において
粉状あるいは粒状の固体で、かつダイカストマシンの射
出スリーブ内へ投入後、射出スリーブ内面の７０℃〜１
３０℃の温度の熱あるいは前記射出スリーブに給湯され
る溶湯の熱によって液化する性質を有する構成とするこ
とによって、潤滑性能が優れていることは勿論のこと、
周辺の機械を汚染するなどの弊害のない作業環境の点で
優れた射出スリーブ用潤滑剤を提供することを目的とす
る。SUMMARY OF THE INVENTION The present invention has been made in view of such circumstances, and has been developed in consideration of stearic acid, fatty acid amide, polyethylene, polyethylene oxide, polyethylene oxide wax, paraffin, vegetable wax, polypropylene, mineral oil, vegetable oil. Having one or more self-lubricating properties selected from synthetic oil, petroleum wax, petroleum resin, synthetic resin, alkamide, beeswax, silicone oil, silicone wax, polybutene, olefinic synthetic hydrocarbon a powder or mixture, in powder or granular solid at ordinary temperature, and elevation of the die casting machine
After charging into the ejection sleeve, the inner surface of the injection sleeve is 70 ° C to 1
30 ° C heat or hot water supplied to the injection sleeve
By having a structure that liquefies by the heat of the molten metal, it is obvious that lubrication performance is excellent,
It is an object of the present invention to provide a lubricant for an injection sleeve which is excellent in a working environment which does not adversely affect peripheral machines.
【０００５】[0005]
【課題を解決するための手段】本発明は、ステアリン
酸、脂肪酸アミド、ポリエチレン、酸化ポリエチレン、
酸化ポリエチレンワックス、パラフィン、植物性ワック
ス、ポリプロピレン、鉱物油、植物油、合成油、石油系
ワックス、石油系樹脂、合成樹脂、アルカアミド、密ろ
う、シリコンオイル、シリコンワックス、ポリブテン、
オレフィン系合成炭化水素、から選ばれた１種若しくは
２種以上の自己潤滑性を有する粉体又は混合体であり、
常温において粉状あるいは粒状の固体で、かつダイカス
トマシンの射出スリーブ内へ投入後、射出スリーブ内面
の７０℃〜１３０℃の温度の熱あるいは前記射出スリー
ブに給湯される溶湯の熱によって液化する性質を有する
ことを特徴とする射出スリーブ用潤滑剤である。SUMMARY OF THE INVENTION The present invention provides stearic acid, fatty acid amide, polyethylene, polyethylene oxide,
Polyethylene oxide wax, paraffin, vegetable wax, polypropylene, mineral oil, vegetable oil, synthetic oil, petroleum-based wax, petroleum-based resin, synthetic resin, alkamide, beeswax, silicone oil, silicone wax, polybutene,
An olefinic synthetic hydrocarbon, one or more powders or mixtures having self-lubricating properties selected from the group consisting of:
In powdered or granular solid at ordinary temperature, and Daikasu
After injection into the injection sleeve of the machine,
Heat at a temperature of 70 ° C to 130 ° C or the injection three
Has the property of being liquefied by the heat of the molten metal supplied to the pipe
A lubricant for an injection sleeve, characterized in that:
【０００６】本発明において、熱によって液化する例と
しては、ダイカストマシンの射出スリーブ内へ投入後、
射出スリーブ内面の熱あるいは前記射出スリーブに給湯
される溶湯の熱によって液化する場合が挙げられる。こ
こで、前記粉体が液状化する温度は大体７０℃〜１３０
℃である。In the present invention, as an example of liquefaction by heat, after injection into an injection sleeve of a die casting machine,
The liquid may be liquefied by the heat of the inner surface of the injection sleeve or the heat of the molten metal supplied to the injection sleeve. Here, the temperature at which the powder liquefies is approximately 70 ° C. to 130 ° C.
° C.
【０００７】本発明において、自己潤滑性を有する上記
粉体は少なくとも１種用いるが、２種以上用いる場合は
その配合割合を用途に応じて適宜決定する。 ［作用］本発明に係る潤滑剤は、例えばダイカストマシ
ンの射出用として用いた場合、常温においては粉状ある
いは粒状の固体であるので、従来と比べダイカストマシ
ン周辺に付着して機械を汚染させることが極めて少な
い。一方、ダイカストマシンの射出スリーブ内へ投入し
た後、射出スリーブ内面の熱あるいは前記射出スリーブ
に給湯される溶湯の熱によって液化してフィルム状とな
ってスリーブ内に伸展し、従来の液状潤滑剤と同様の潤
滑性能を発揮する。In the present invention, at least one kind of the above-mentioned powder having self-lubricating properties is used, but when two or more kinds are used, the mixing ratio is appropriately determined according to the application. [Function] When the lubricant according to the present invention is used, for example, for injection of a die-casting machine, it is a powdery or granular solid at normal temperature. Is extremely small. On the other hand, after being injected into the injection sleeve of the die casting machine, it is liquefied by the heat of the inner surface of the injection sleeve or the heat of the molten metal supplied to the injection sleeve, becomes a film, and extends into the sleeve. Exhibits similar lubrication performance.
【０００８】[0008]
【発明の実施の形態】以下、本発明の各実施例１〜６に
ついて説明する。 （実施例１）本実施例１に係る潤滑剤は、下記表１に示
すように、酸化ポリエチレン２５〜４５％、植物油系ワ
ックス３５〜４５％、蜜ろう０〜３％、亜鉛オクタエイ
ト１〜５％、アルカアミド１５〜３０％、石油系樹脂３
〜１０％からなる粉体を混ぜ合わせてなる。前記潤滑剤
は、常温において粉状あるいは粒状の固体で、ダイカス
トマシンの射出スリーブ内へ投入後、射出スリーブ内面
の熱あるいは前記射出スリーブに給湯される溶湯の熱に
よって液化する性質を有している。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments 1 to 6 of the present invention will be described below. (Example 1) As shown in Table 1 below, the lubricant according to Example 1 was composed of 25 to 45% of polyethylene oxide, 35 to 45% of vegetable oil-based wax, 0 to 3% of beeswax, and 1 to 5 of zinc octaate. %, 15-30% of alkamide, petroleum resin 3
-10% powder. The lubricant is a powdery or granular solid at room temperature, and has a property of being liquefied by the heat of the inner surface of the injection sleeve or the heat of the molten metal supplied to the injection sleeve after being put into the injection sleeve of the die casting machine. .
【０００９】こうした潤滑剤は、常温では粉状あるいは
粒状の固体であるが、ダイカストマシンの射出スリーブ
内へ投入した後、射出スリーブ内面の熱あるいは前記射
出スリーブに給湯される溶湯の熱によって液化し、フィ
ルム状となってスリーブ内に伸展し、従来の液状潤滑剤
と比べ高潤滑性能、高温で溶解するという性質を有す
る。Such a lubricant is a powdery or granular solid at room temperature, but after being poured into an injection sleeve of a die casting machine, it is liquefied by the heat of the inner surface of the injection sleeve or the heat of the molten metal supplied to the injection sleeve. It has the property of extending into a sleeve in the form of a film, dissolving at high temperature and having higher lubricating performance than conventional liquid lubricants.
【００１０】上記実施例に係る潤滑剤によれば、以下の
ような効果を有する。 (1) 従来の油性潤滑剤と比べ、その組成の違いから溶湯
の注湯後の発煙、発火を大幅に抑制でき、作業環境の点
で優れている。The lubricant according to the above embodiment has the following effects. (1) Compared to conventional oil-based lubricants, smoke and ignition after pouring of molten metal can be significantly suppressed due to the difference in composition, and it is excellent in work environment.
【００１１】(2) 優れた潤滑性を保有するため、従来の
油性あるいは水性潤滑剤に添加されていた黒鉛の添加を
廃止することができ、作業環境の点で優れている。 (3) 従来の潤滑剤は液状であり、射出スリーブ・チップ
塗布後ダイカストマシン周辺に付着し機械を汚染させて
いたが、本実施例ではスリーブ内へ投入する前は常温に
おいて粉状あるいは粒状の固体であるので、大幅な汚染
の削減が可能となる。(2) Since it has excellent lubricity, the addition of graphite which has been added to conventional oil-based or water-based lubricants can be eliminated, which is excellent in working environment. (3) The conventional lubricant is liquid and adheres to the periphery of the die casting machine after application of the injection sleeve / chip to contaminate the machine.However, in this embodiment, the powdery or granular material is added at room temperature before being charged into the sleeve. Being a solid, a significant reduction in contamination is possible.
【００１２】(4) 廃液に混入しても固体状であるので、
液状であった従来の潤滑剤に比べて排水処理を容易にで
きる。 (5) 従来の液体の潤滑剤に比べ、原材料の品質等から少
量塗布、使用が可能となり、周辺機器等の汚れが低減で
き、環境面で優れている。また、少量で使用可能なた
め、液体潤滑剤による火災も大きく改善される。(4) Even if mixed into the waste liquid, it is solid,
Wastewater treatment can be facilitated as compared with a conventional liquid lubricant. (5) Compared to conventional liquid lubricants, it can be applied and used in small quantities due to the quality of raw materials, etc., and can reduce dirt on peripheral devices and is environmentally superior. In addition, since it can be used in a small amount, fire caused by the liquid lubricant is greatly improved.
【００１３】[0013]
【表１】 [Table 1]
【００１４】（実施例２〜６）本実施例２〜６に係る潤
滑剤の原料となる粉体の組成は、上記表１に示す通りで
ある。なお、実施例２〜６に係る潤滑剤も、上記実施例
１と略同様な効果を有する。但し、各実施例２〜６は粉
体を構成する組成の違いにより下記のような性質を有し
ている。Examples 2 to 6 The compositions of powders used as raw materials for lubricants according to Examples 2 to 6 are as shown in Table 1 above. Note that the lubricants according to the second to sixth embodiments also have substantially the same effects as the first embodiment. However, Examples 2 to 6 have the following properties depending on the difference in the composition of the powder.
【００１５】実施例２：中潤滑性能、低温溶解。 実施例３：高い潤滑性能、低温溶解。植物油系ワックス
を使用していることからコスト低減が図れる。また、低
温で融解するのは融点の低い蜜ろうを用いているためで
ある。Example 2: Medium lubrication performance, low temperature melting. Example 3: High lubrication performance, low temperature melting. Cost reduction can be achieved by using vegetable oil-based wax. The melting at a low temperature is due to the use of beeswax having a low melting point.
【００１６】実施例４：極上潤滑性能、焼付き性向上、
広範囲の条件下で使用可能。 実施例５：高温下での濡れ性向上品。 実施例６：高広がり・伸展性、高離型性。Embodiment 4: Improvement of superb lubrication performance and seizure performance
Can be used under a wide range of conditions. Example 5: Product with improved wettability under high temperature. Example 6: High spread / extensibility, high release properties.
【００１７】なお、潤滑剤を構成する粉体の材料は上記
実施例に記載された例に限らず、ステアリン酸、脂肪酸
アミド、ポリエチレン、酸化ポリエチレン、酸化ポリエ
チレンワックス、パラフィン、植物性ワックス、ポリプ
ロピレン、鉱物油、植物油、合成油、石油系ワックス、
石油系樹脂、合成樹脂、アルカアミド、亜鉛オクトエイ
ト、蜜ろう、シリコンオイル、シリコンワックス、ポリ
ブテン、オレフィン系合成炭化水素、から選ばれた任意
の１種若しくは２種以上の自己潤滑性を有する粉体を用
いてもよい。The material of the powder constituting the lubricant is not limited to the examples described in the above embodiments, but may be stearic acid, fatty acid amide, polyethylene, polyethylene oxide, polyethylene oxide wax, paraffin, vegetable wax, polypropylene, Mineral oil, vegetable oil, synthetic oil, petroleum wax,
One or more self-lubricating powders selected from petroleum resin, synthetic resin, alkaamide, zinc octoate, beeswax, silicon oil, silicon wax, polybutene, olefinic synthetic hydrocarbon It may be used.
【００１８】また、上記実施例では、潤滑剤をダイカス
トマシンの射出スリーブ内へ投入する場合について述べ
たが、これに限らず、潤滑性を有する例えばスピンド
ル、冷凍機、コンプレッサーなど種々の用途に用いるこ
とができる。In the above embodiment, the case where the lubricant is injected into the injection sleeve of the die-casting machine has been described. However, the present invention is not limited to this, and the lubricant is used for various uses such as a spindle, a refrigerator, a compressor, etc. be able to.
【００１９】[0019]
【発明の効果】以上詳述したように、本発明によれば、
ステアリン酸、脂肪酸アミド、ポリエチレン、酸化ポリ
エチレン、酸化ポリエチレンワックス、パラフィン、植
物性ワックス、ポリプロピレン、鉱物油、植物油、合成
油、石油系ワックス、石油系樹脂、合成樹脂、アルカア
ミド、蜜ろう、シリコンオイル、シリコンワックス、ポ
リブテン、オレフィン系合成炭化水素、から選ばれた１
種若しくは２種以上の自己潤滑性を有する粉体又は混合
体であり、常温において粉状あるいは粒状の固体で、か
つダイカストマシンの射出スリーブ内へ投入後、射出ス
リーブ内面の７０℃〜１３０℃の温度の熱あるいは前記
射出スリーブに給湯される溶湯の熱によって液化する性
質を有する構成とすることにより、潤滑性能が優れてい
ることは勿論のこと、周辺の機械を汚染するなどの弊害
のない作業環境の点で優れた射出スリーブ用潤滑剤を提
供できる。As described in detail above, according to the present invention,
Stearic acid, fatty acid amide, polyethylene, polyethylene oxide, polyethylene oxide wax, paraffin, vegetable wax, polypropylene, mineral oil, vegetable oil, synthetic oil, petroleum wax, petroleum resin, synthetic resin, alkamide, beeswax, silicon oil, 1 selected from silicon wax, polybutene, and olefinic synthetic hydrocarbon
Powder or mixture of two or more kinds of self-lubricating properties
A body, in powdered or granular solid at room temperature, and after turning into the injection sleeve of the die casting machine, injection scan
Heat at a temperature of 70 ° C to 130 ° C on the inner surface of the leave or
Liquefaction by the heat of the molten metal supplied to the injection sleeve
By having a high quality structure, it is possible to provide a lubricant for an injection sleeve which is excellent in lubricating performance and in a working environment free from adverse effects such as contamination of peripheral machines.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ｃ１０Ｍ 107/22 Ｃ１０Ｍ 107/22 107/50 107/50 Ｃ１０Ｎ 10:04 Ｃ１０Ｎ 10:04 40:02 40:02 50:08 50:08 (72)発明者 ロバート・ジエイ・ダイラ アメリカ合衆国、 ミシガン州 48209、 デトロイト、 ウッドメア・アベニユ ー 134、 クロス・ケミカル・カンパ ニー内 (56)参考文献 特開 平７−62376（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C10M 101/00,105/04,105/24 C10M 105/68,107/00 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification code FI C10M 107/22 C10M 107/22 107/50 107/50 C10N 10:04 C10N 10:04 40:02 40:02 50:08 50 : 08 (72) Inventor Robert J. Dyla, United States 48209, Michigan, Detroit, Woodmare Avenue 134, Cross Chemical Company (56) References JP-A-7-62376 (JP, A) ( 58) Field surveyed (Int. Cl. 7 , DB name) C10M 101/00, 105/04, 105/24 C10M 105/68, 107/00
Claims (1)
レン、酸化ポリエチレン、酸化ポリエチレンワックス、
パラフィン、植物性ワックス、ポリプロピレン、鉱物
油、植物油、合成油、石油系ワックス、石油系樹脂、合
成樹脂、アルカアミド、密ろう、シリコンオイル、シリ
コンワックス、ポリブテン、オレフィン系合成炭化水
素、から選ばれた１種若しくは２種以上の自己潤滑性を
有する粉体又は混合体であり、常温において粉状あるい
は粒状の固体で、かつダイカストマシンの射出スリーブ
内へ投入後、射出スリーブ内面の７０℃〜１３０℃の温
度の熱あるいは前記射出スリーブに給湯される溶湯の熱
によって液化する性質を有することを特徴とする射出ス
リーブ用潤滑剤。1. Stearic acid, fatty acid amide, polyethylene, polyethylene oxide, polyethylene oxide wax,
Selected from paraffin, vegetable wax, polypropylene, mineral oil, vegetable oil, synthetic oil, petroleum wax, petroleum resin, synthetic resin, alkamide, beeswax, silicone oil, silicone wax, polybutene, olefin synthetic hydrocarbon One or more kinds of powders or mixtures having self-lubricating properties, which are powdery or granular solids at room temperature, and are injection sleeves for die casting machines.
After the injection, the temperature of the inner surface of the injection sleeve is 70 ° C to 130 ° C.
Or the heat of the molten metal supplied to the injection sleeve
Characterized in that it has the property of being liquefied by
Lube lubricant .