JP3194914B2 - Detergent composition for clothing - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to a phosphorus-free detergent composition for clothing. More specifically, the present invention relates to a detergent composition for clothing that can be used in a low amount, has a low surfactant concentration in a washing liquid, and can obtain excellent detergency.

[0002]

2. Description of the Related Art Many chelators, ion exchange agents, alkali agents, dispersants and the like have been reported to builders incorporated in detergents. Previously, for the reason of being water-soluble and having a good detergency, a formulation using a phosphoric acid-based chelating agent mainly containing tripolyphosphate was mainly used.

[0003] In recent years, however, tripolyphosphates have
Due to concerns about eutrophication of closed water bodies such as lakes and marshes, their use has been reduced, and crystalline aluminosilicates (zeolites) as typified by JP-A-50-12381 have come to be widely used. In such a formulation using zeolite, the standard amount of detergent used was about 40 g / 30 L in Japan. Further, the powder detergent at that time had a low bulk density (0.20 to 0.45) from the viewpoint of solubility in cold water.
g / ml). As a result, the standard working volume is about 90
It was as large as ~ 200 ml / 30 L, which was very inconvenient to handle in logistics, stores, homes, and the like.

[0004] Therefore, intensive studies have been made to reduce the size of the detergent. For example, JP-A-62-1
67396, JP-A-62-167399,
As seen in JP-A-62-253699, a crystalline inorganic salt which is a powdering aid conventionally contained in detergents,
For example, a large reduction in sodium sulfate,
No. 7, JP-A-61-69899, JP-A-61-69989
-69900, JP-A-5-209200, etc., the bulk density of the detergent is increased by 0.60 to 1.00 g / ml due to the invention of the manufacturing technology for increasing the bulk density of the detergent.
In addition, the standard amount of detergent is 25-30g / 30L,
As a result, the standard working volume was reduced to 25-50 ml / 30L.

However, the conventional concept of cleaning has been focused on achieving solubilization of oil in dirt with a surfactant, so that a large amount of a surfactant must be added. . That is, taking as an example the sebum dirt derived from the human body, which is the most typical dirt adhering to clothing (easy to be observed on the collar and sleeves), the sebum dirt is
Oils such as free fatty acids and glycerides are contained in the soil at a high content of 70% or more (Kashiwa Ichiro et al., Oil Chemistry, 19 ,
1095 (1969) etc.), these are carbon and mud in dust,
The exfoliated keratin and the like are trapped and observed as dirt. However, conventionally, in cleaning them, carbon and mud are mainly removed by solubilizing and removing these oils by micelles of a surfactant. In addition, it was designed to wash keratin with a mechanism for dropping it off clothing. This concept has been widely established among those skilled in the art, and there was no change in the surfactant concentration in the washing liquid even when the conventional detergent was changed to the compact detergent. These are described in the encyclopedia of detergents and cleaning by Haruhiko Okuyama et al., P.42 of the first edition (Asakura Shoten, 1990).
8, it can be said that the concentration of components other than sodium sulfate in the washing liquid is basically unchanged.

Based on these washing theories, it is necessary to increase the concentration of the surfactant in the washing liquid in order to obtain a high detergency. Therefore, it is necessary to incorporate a large amount of the surfactant in the detergent composition. Thus, it has been practically difficult to drastically reduce the standard amount of detergent. In addition, the bulk density is around 1.00 g / ml in a practical production method, and as a result, it has been considered that further reduction of the standard working volume is a technically very difficult task.

On the other hand, crystalline silicates having a specific structure described in JP-A-5-184946, JP-A-60-74595, and the like exhibit the action of an alkali agent (alkali ability) in addition to the ion exchange ability. In order to show, the function of the two components of sequestering agents such as zeolite used in conventional detergents and alkali agents such as sodium carbonate can be fulfilled only by these crystalline silicates. Approaches have been made on the potential of new detergents.

For example, JP-A-6-116588 discloses that
The present invention relates to a detergent composition containing a crystalline silicate.
There is disclosed a more compact detergent capable of obtaining the same detergency even when the amount is reduced by 5%. However, since the composition is based on the conventional cleaning theory, the surfactant concentration is high,
Further, the alkali ability and the ion exchange ability were almost exclusively expressed by the crystalline silicate. In this case, since the function of the crystalline silicate as an alkali agent precedes, the function as a sequestering agent becomes insufficient, and the detergency is not always satisfactory. Therefore, if the amount used was further reduced, the cleaning power could not be maintained.

Further, several patent applications relating to crystalline silicates have been filed in Japanese Patent Application Laid-Open No. 60-74595. For example, JP-A-6-502199 discloses that no film is formed on a fiber in which a layered crystalline silicate, zeolite and polycarboxylate are blended at a specific blending ratio.
Detergents exhibiting excellent detergency and bleach stability are disclosed. However, under these mixing conditions, when the amount added during washing is small, the alkali ability is insufficient due to the small amount of silicate in the builder composition, and the detergency cannot be maintained. Further, there is no idea at all that a good detergency is exhibited with a small amount of use.

[0010] In addition, Japanese Patent Publication No. 6-500141,
JP-A-2-178398 or JP-A-2-1783
The same applies to patent publications in which crystalline silicates such as Japanese Patent Publication No. 99 are disclosed, and it is not related to a detergent used in a small amount as in the present invention. Detergency decreases.

[0011]

SUMMARY OF THE INVENTION It is an object of the present invention to substantially review the concept of washing as described above, so that the detergent has excellent detergency even when the concentration of surfactant is low. Is to provide a phosphorus-free detergent composition for clothing that can be washed with a smaller amount than conventional compact detergent compositions for clothing (25 to 30 g / 30 L).

[0012]

Means for Solving the Problems As a result of intensive studies, the present inventors have found out the relationship between the washing conditions of clothes and the washability from an extremely simple washing system, and specified the washing conditions with high alkali and low hardness. By analyzing the reasons for the excellent detergency in the above, we have developed a detergent that requires less use.

That is, the present inventors have conducted intensive studies on the effects of the pH of the washing liquid and the hardness of the washing liquid on washing, and have found the following. The higher the pH and the lower the hardness, the lower the dependency of the detergency on the surfactant concentration, and the better the detergency is obtained. Also, in the case of high hardness even at high pH,
Extremely low cleaning power. Also, without blending an alkaline agent,
In the case of washing with a surfactant alone, the washing power at a low hardness is low, but the dependency of the washing power on the hardness is sufficiently smaller than that of a system containing an alkali agent. The present inventors have paid attention to the relationship between the washing liquid and the stain regarding the result obtained.

As described in the section of the prior art, sebum soil, which is a typical soil adhering to clothing, contains fatty acids and glycerides. The soil is composed of a mixture of these organic substances and carbon, mud or keratin. It is thought that it was done.
In the case of a high pH, the fatty acid content increases due to the hydrolysis of glyceride, while the reaction of converting the fatty acid into an alkali salt proceeds. Alkali metal salts of fatty acids are soaps, which promote the release of dirt into the wash liquor. However, this reaction is a competitive reaction with calcium and magnesium etc. in hard water, and fatty acid alkali metal salts form scum with calcium and magnesium, so when the hardness is high, the dirt solidifies without releasing from the fabric interface. Resulting in. From the above, it is considered that a high pH and low hardness showed excellent cleaning power, and a high hardness showed low cleaning power. When no alkaline agent is blended, the sebum dirt is washed only by the surfactant, so it is considered that the dependence on hardness was smaller than that of the alkaline compound blended system.

From these phenomena, the inventors of the present invention concluded that one of the reasons why the surfactant concentration was lower than that of the conventional detergent, but that the detergency was equal to or higher than that of the conventional detergent was obtained.
Noticing that the soap obtained by progressing the saponification of fatty acids in the soil due to low hardness and high pH is acting on the detergency,
We have now found phosphorus-free clothing detergent compositions that use less standard amounts than conventional detergents that rely on surfactants.

That is, the gist of the present invention is to provide the following components: a) a surfactant, b) an alkali metal silicate, and c) a Ca ion trapping ability of 200 CaCO ₃ mg / g or more.
A sequestering agent other than the component b, wherein the sequestering agent of the component c is a carboxylate polymer, an aluminosilicate, aminotri (methylenephosphonic acid) and a salt thereof, 1-hydroxyethylidene-
1,1-diphosphonic acid and its salt, ethylenediaminetetra (methylenephosphonic acid) and its salt, diethylenetriaminepenta (methylenephosphonic acid) and its salt, phosphonocarboxylic acid salt, amino acid salt, aminopolyacetate, and citric acid At least one selected from the group consisting of trisodium salts, wherein the total amount of the components a, b, and c accounts for 70 to 100% by weight of the total composition, and the ratio of the component b to a is a weight ratio. And b / a = 9/1 to 9/11, and the ratio of the b component to the c component is b / c = 5/1 to 1/15.

[0017]

BEST MODE FOR CARRYING OUT THE INVENTION The washing method of the present invention comprises a surfactant, an alkali metal silicate, and a sequestering agent other than the alkali metal silicate. 5/1 salt weight ratio
The following phosphorus-free detergent composition for clothing is used to provide the following washing conditions when clothing is not put in. The pH of the washing liquid is 10.60 or more. A substance having an ion-capturing ability necessary to reduce the hardness of the washing water to 0.5 ° DH or less in calculation is present in the washing liquid. Surfactant concentration of 0.07 to 0.17 g /
L.

By adopting such washing conditions, the washing power is excellent even when the concentration of the surfactant is low, so that the standard amount of the detergent can be reduced as compared with the conventional case.

The weight ratio of the alkali metal silicate to the sequestering agent other than the alkali metal silicate is 5%.
When the ratio exceeds / 1, sufficient cleaning power cannot be obtained even when the above-mentioned cleaning conditions are satisfied.

In the washing method of the present invention, more preferable washing conditions include the following, corresponding to the above conditions (1) to (4). 'The pH of the washing liquid is 10.85 to 11.00, more preferably 10.90 to 11.00. 'It is preferable that a substance having an ion-capturing ability necessary to make the hardness of the washing water to be 0 ° DH in calculation is present in the washing liquid, more preferably, it is not more than -1 (-1) ° DH in calculation. This is where the quantity is present in the wash liquor. 'The surfactant concentration in the washing liquid is 0.08-0.1
4 g / L, preferably 0.08 to 0.11 g / L
L is more preferred.

Although those satisfying all of these preferred ranges are particularly preferred, the effects of the present invention become more remarkable when at least one of these preferred ranges is satisfied.

The weight ratio of the alkali metal silicate to the sequestering agent other than the alkali metal silicate is as follows:
4/1 to 1/15 are preferred, and 3/1 to 1/15 are more preferred.

The specific amount of use, in other words, the concentration of the detergent in the washing liquid, depends on the hardness of the washing liquid, and the amount of increase or decrease is caused by a change in the amount of the sequestering agent. Basically, the surfactant concentration in the washing liquid does not change.

The standard amount of detergent used varies from country to country in the world. This is because tap water hardness varies from country to country.
For example, in Japan it is usually around 4 ° DH,
In the United States, water with a high hardness of 6 ° DH or more and in Europe exceeding 10 ° DH is used as washing water. This changes the absolute amount of sequestering agent, and consequently the standard usage is adjusted accordingly. Although the amount of the sequestering agent added in the present invention varies depending on the hardness, the concentration of the surfactant in the washing liquid is basically the same, and the standard amount used is smaller than in the past.

Accordingly, the detergent concentration when the initial hardness of the washing liquid is different is as follows. 1) For washing water of 2 to 6 ° DH, the concentration of the detergent composition in the washing liquid is 0.33 to 0.67 g / L, preferably 0.33 to 0.50 g / L. 2) For washing water of 6 to 10 ° DH, the concentration of the detergent composition in the washing liquid is 0.50 to 1.20 g / L, preferably 0.50 to 1.00 g / L. 3) For washing water of 10 to 20 ° DH, the concentration of the detergent composition in the washing liquid is 0.80 to 2.50 g / L, preferably 1.00 to 2.00 g / L.

Here, each of the above washing conditions is measured and the like as follows. The pH of the washing liquid is measured at 25 ° C. using a normal glass electrode pH meter or the like. The amount of a substance having an ion-capturing ability to be present in the washing liquid (referred to as an alkali metal silicate and a sequestering agent other than the alkali metal silicate) is calculated as follows.

For example, the hardness of the washing water is calculated to be 0.5 °
The amount corresponding to the ion trapping capacity required to make DH is calculated from the hardness of the washing water used (for example, about 4 ° DH in Japan) and the concentration of Ca, Mg ions corresponding to the difference in the hardness. The total Ca ion capturing ability corresponding to the ion concentration is calculated in units of concentration. In this case, the amount of the washing water and the amount of the detergent composition to be added are determined by the surfactant concentration (0.0%).
7 to 0.17 g / L).
The DH hardness was measured by an ion coupling plasma method (IC
P method).

At this time, the method of measuring the ion capturing ability of the sequestering substance differs depending on whether the sequestering substance to be used is an ion exchanger or a chelating agent. The measuring method for each substance is as follows.

In the case of an ion exchanger, 0.1 g of a sample is precisely weighed and added to 100 ml of an aqueous solution of calcium chloride (concentration: 500 ppm as CaCO ₃ ).
After stirring at 25 ° C. for 60 minutes, the mixture is filtered using a membrane filter having a pore size of 0.2 μm (manufactured by Advantech, nitrocellulose), and the amount of Ca contained in 10 ml of the filtrate is measured by EDTA titration. From that value, the calcium ion exchange capacity (cation exchange capacity) of the sample is determined.

For example, in the present invention, an inorganic substance such as a crystalline alkali metal silicate or an aluminosilicate (such as zeolite) is measured as an ion exchanger.

In the case of a chelating agent, the ability to capture Ca ions is measured as follows using a calcium ion electrode. In addition, all the solutions are prepared using the following buffers. Buffer; 0.1M-NH ₄ Cl-
NH ₄ OH buffer (pH 10.0) (1) Preparation of calibration curve A standard calcium ion solution is prepared, and a calibration curve showing the relationship between the logarithm of calcium ion concentration and the potential as shown in FIG. 1 is prepared. (2) Measurement of Capability of Capturing Calcium Ions About 0.1 g of a sample is weighed in a 100 ml volumetric flask, and the volume is increased with the above buffer solution. In addition, 2000
A CaCl ₂ aqueous solution (pH 10.0) corresponding to 0 ppm (CaCO ₃ conversion) is dropped from the burette (blanks are also measured). For the dropwise addition, use a CaCl ₂ aqueous solution of 0.1 to
0.2 ml at a time, read the potential at that time,
The calcium ion concentration is determined from the calibration curve of FIG. FIG.
The calcium ion concentration at the dropping amount A of the sample inside becomes the calcium ion trapping ability of the sample. For example, in the present invention, polycarboxylates such as citrate and carboxylate polymers such as acrylic acid-maleic acid copolymer are measured as chelating agents.

The washing method of the present invention is as follows: 1) 2 to 6 °
In the case of DH washing water, 2) in the case of 6-10 ° DH washing water, and 3) in the case of 10-20 ° DH washing water, the present invention can be applied. in this case,~
Are the same, and only the detergent concentration is selected and determined so as to satisfy the condition (1).

As described above in the washing method of the present invention,
In order to realize a high-pH and low-hardness washing liquid capable of obtaining excellent detergency, the following conditions are required. (B) Excess sequestering agent is present. (B) The presence of an alkaline agent that buffers at high pH.

Of these, crystalline silicates satisfying both (a) and (b) are known, but care must be taken in using crystalline silicates. The reason for this is that if the amount of the crystalline silicate is increased to reduce the hardness, the alkali capacity also increases. In this case, the exchange rate of Ca or Mg with respect to the fatty acid naturally increases, which is not preferable.
Therefore, in order to satisfy more preferable conditions, it is necessary to mix other sequestering agents in a specific ratio, and if the ratio is outside these ranges, it becomes difficult to reduce the amount of the detergent used.

Accordingly, the phosphorus-free detergent composition for clothing of the present invention comprises: a) a surfactant, b) an alkali metal silicate, and c) a sequestering agent other than the b component. , C component occupies 70 to 100% by weight of the total composition, and the ratio of b component to a is b / a = 9/1 to 1/2, preferably 9 /
1 to 9/11, and the ratio of the component b to the component c is b
/ C = 5/1 to 1/15, preferably 4/1 to 1/15
It is something that is.

More preferably, the above-mentioned components a) to c) are contained, and the total amount of the components a, b and c is 80 to 80% in the total composition.
Occupies 100% by weight, and the ratio of the b component to a is b / a = 9/1 to 1/1 in weight ratio, and the ratio of the b component to the c component is b / c = 3/1 to 1/15. It is something that is. Most preferably, the water used has a hardness of 2 to 6 ° DH.
Is 3/1 to 3/7, 4/3 to 1/6 when the hardness is 6 to 10 ° DH, and 1 when the hardness is 10 to 20 ° DH.
/ 1 to 1/15. In the present invention, by adopting such a composition, a detergent composition having a smaller standard usage amount for washing water having different hardness can be obtained.

Hereinafter, each of these components will be described. a) Surfactant The surfactant used in the present invention is generally used in a detergent as long as it preferably contains 50 to 100% by weight, more preferably 65 to 100% by weight of a nonionic surfactant. What is used can be used without particular limitation. Specifically, it is at least one selected from the group consisting of nonionic surfactants, anionic surfactants, cationic surfactants and amphoteric surfactants exemplified below.
For example, the same type may be selected only from a plurality of non-ionic surfactants, or various types from anionic surfactants and non-ionic surfactants. May be selected plurally.

Examples of the nonionic surfactant include the following.

That is, polyoxyethylene alkyl ether, polyoxyethylene alkyl phenyl ether, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene sorbite fatty acid ester, polyethylene glycol fatty acid ester, polyoxyethylene glycol fatty acid alkyl ester, polyoxyethylene polyoxy Propylene alkyl ether, polyoxyethylene castor oil, polyoxyethylene alkylamine, glycerin fatty acid ester, higher fatty acid alkanolamide,
Examples thereof include alkyl glucoside, alkyl glucose amide, and alkylamine oxide.

Among them, ethylene oxide adducts of linear or branched primary or secondary alcohols having 10 to 18 carbon atoms, particularly as nonionic surfactants,
It is desirable to use a polyoxyethylene alkyl ether having an average number of added moles of 5 to 15. More preferably, it is an ethylene oxide adduct of a linear or branched primary or secondary alcohol having 12 to 14 carbon atoms, and it is desirable to use a polyoxyethylene alkyl ether having an average addition mole number of 6 to 10. .

Examples of the anionic surfactant include alkyl benzene sulfonate, alkyl or alkenyl ether sulfate, alkyl or alkenyl sulfate, α-olefin sulfonate, α-sulfofatty acid salt or ester salt, alkyl or alkenyl ether carboxylate. Examples thereof include acid salts, amino acid type surfactants, N-acyl amino acid type surfactants, and the like, preferably alkyl benzene sulfonate, alkyl or alkenyl ether sulfate, alkyl or alkenyl sulfate and the like.

Examples of the cationic surfactant include quaternary ammonium salts such as alkyltrimethylamine salts. Examples of the amphoteric surfactant include carboxy type and sulfobetaine type amphoteric surfactants.

The content of the surfactant is preferably 1 to 45% by weight in the whole composition, and particularly 1) when using 2 to 6 ° DH washing water, 15 to 30% by weight.
2) When washing water of 6 to 10 ° DH is used, 8 to 25% is used.
3) When using 10 to 20 ° DH washing water, 5 to 2%
It is preferable to add 0% by weight.

If the amount is less than the above range, sufficient detergency tends to be difficult to obtain. If the amount exceeds this range, the amounts of the alkali agent and the sequestering agent are relatively reduced, and sufficient detergency is obtained. Tends to be difficult.

The detergent composition for clothing of the present invention can be used in such a manner that the surfactant concentration in the washing liquid is 0.0
When the detergent composition is added to the washing water so as to have a concentration of 7 to 0.17 g / L, the concentration of the detergent composition in the washing liquid is as follows. The concentration of the detergent composition therein becomes 0.33 to 0.67 g / L, preferably 0.33 to 0.50 g / L. 2) For washing water of 6 to 10 ° DH, The concentration of the detergent composition is 0.50 to 1.20 g / L, preferably 0.50 to 1.00 g / L. 3) For washing water of 10 to 20 ° DH, the detergent composition in the washing liquid The concentration of the product is 0.80 to 2.50 g / L, preferably 1.00 to 2.00 g / L, and the standard usage amount of the detergent composition for obtaining sufficient detergency is smaller than that of the conventional one. Yes.

B) Alkali metal silicate As the alkali metal silicate used in the present invention, either crystalline or amorphous metal silicate can be used. Without
It is preferable to use a crystalline one because it can provide ion exchange ability and further reduce the standard usage of the detergent composition.

As the crystalline alkali metal silicate used in the present invention, the alkali metal silicate SiO ₂ / M
₂ O (where M represents an alkali metal) is from 0.5 to
What is 2.6 is used. On the other hand, the crystalline silicate used in the patent publication described in the prior art is Si
Although the O ₂ / Na ₂ O ratio (S / N ratio) is 1.9 to 4.0, a silicate having an S / N ratio exceeding 2.6 in the present invention cannot obtain the effects of the present invention. However, it is impossible to produce a detergent which can obtain excellent detergency with a small amount of use.

Among the crystalline alkali metal silicates used in the present invention, those having the following composition are preferably exemplified. _{xM 2 O · ySiO 2 · zMe} m O n · wH 2 O (1) ( wherein, M is Group Ia elements of the periodic table, Me represents IIa, II
b, IIIa, IVa or VIII, represents one or a combination of two or more elements, wherein y / x = 0.5 to 2.
6, z / x = 0.01-1.0, n / m = 0.5-2.
0 and w = 0 to 20. _{) M 2 O · x'SiO 2 ·} y'H 2 O (2) ( wherein, M represents an alkali metal, x '= 1.5~2.
6, y ′ = 0 to 20. )

First, the crystalline alkali metal silicate having the above composition will be described.

In the general formula (1), M is I in the periodic table.
The element is selected from group a elements, and examples of the group Ia element include Na and K. These may be used alone or, for example, a mixture of Na ₂ O and K ₂ O to form the M ₂ O component.

Me is selected from Group IIa, IIb, IIIa, IVa or VIII elements of the periodic table, for example, Mg, Ca, Zn,
Y, Ti, Zr, Fe and the like can be mentioned. These are not particularly limited, but are preferably Mg and Ca from the viewpoint of resources and safety. These may be used alone or as a mixture of two or more. For example, MgO, CaO
Like are mixed may constitute the Me _m O _n component.

In the present invention, the crystalline alkali metal silicate may be a hydrate, and the hydration amount in this case is in the range of w = 0 to 20.

In the general formula, y / x is 0.5 to
2.6, and preferably 1.5 to 2.2. y /
When x is less than 0.5, the water resistance is insufficient and the physical properties of the powder of the detergent composition such as caking property and solubility are adversely affected. If y / x exceeds 2.6, the alkalinity becomes low and becomes insufficient as an alkali agent, and the ion exchange ability also becomes low, making it insufficient as an ion exchanger. z
/ X is 0.01 to 1.0, preferably 0.02 to
0.9. When z / x is less than 0.01, the water resistance is insufficient, and when it exceeds 1.0, the ion exchange capacity is lowered and the ion exchange is insufficient. x, y, and z are not particularly limited as long as they have the relationship shown in the above y / x and z / x. As described above, when xM ₂ O is, for example, x′Na ₂ O · x ″ K ₂ O, x is x ′ + x ″. Such a relationship is represented by zMe
The same applies to z in the case _{where m} O _n component consist of two or more kinds. Also, n / m = 0.5 to 2.0
Represents the number of oxygen ions coordinated to the element, and is substantially selected from values of 0.5, 1.0, 1.5, and 2.0.

Crystalline alkali metal silicic acid according to the present invention
The salt is M as shown in the above general formula._TwoO, Si
O_Two, Me_mO_nIt consists of three components. Accordingly
To produce the crystalline alkali metal silicate of the present invention.
To do this, each component is required as a raw material.
In the light, known compounds are not particularly limited,
Used as appropriate. For example, M_TwoO component, Me_mO_ncomponent
Is the oxidation of each element alone or in combination
Substances, hydroxides, salts, and minerals containing the element are used.
Specifically, for example, M_TwoThe raw material of the O component is NaO
H, KOH, Na_TwoCO _Three, K_TwoCO_Three, Na_TwoSO_Four
Etc. are Me_mO_nThe raw material of the component is CaCO _Three, M
gCO_Three, Ca (OH)_Two, Mg (OH)_Two, MgO,
ZrO_TwoAnd dolomite. SiO_TwoIngredients
Silicate, kaolin, talc, fused silica, sodium silicate
And the like.

In the method for preparing a crystalline alkali metal silicate according to the present invention, the above-mentioned raw material components are mixed at a predetermined quantitative ratio so as to obtain the desired values of x, y and z of the crystalline alkali metal silicate. Mixing, usually 300 to 1500 ° C, preferably 500 to 1000 ° C, more preferably 600 to 900 ° C.
A method of firing and crystallization in the range of ° C. is exemplified. In this case, if the heating temperature is lower than 300 ° C., the crystallization is insufficient and the water resistance is poor. If the heating temperature exceeds 1500 ° C., coarse particles are formed and the ion exchange ability is lowered. The heating time is usually 0.1 to 24 hours. Such firing can be usually performed in a heating furnace such as an electric furnace or a gas furnace.

The thus obtained crystalline alkali metal silicate of the present invention shows a pH of 11 or more in a 0.1% by weight dispersion and shows excellent alkalinity.
Also, the alkali buffering effect is particularly excellent, and the alkali buffering effect is superior to that of sodium carbonate or potassium carbonate.

The crystalline alkali metal silicate of the present invention has an ion exchange capacity of at least 100 CaCO 3.
₃ mg / g or more, preferably 200 to 600 CaCO ₃
mg / g, and is one of the substances having an ion-capturing ability in the present invention.

The amount of Si eluted in water is usually 110 mg / g or less in terms of SiO ₂ , and is substantially insoluble in water. In the present invention, “insoluble in water” means that 2 g of a sample is added to 100 g of ion-exchanged water,
Is usually less than 110 mg / g in terms of SiO ₂ when the mixture is stirred for 30 minutes, but in the present invention, 100 mg / g or less is more preferable to satisfy the present effect.

The crystalline alkali metal silicate according to the present invention has an alkali function and an alkali buffering effect as described above, and furthermore has an ion exchange function. Conditions can be suitably adjusted.

In the present invention, the crystalline alkali metal silicate preferably has an average particle size of 0.1 to 50 μm, more preferably 1 to 30 μm, and still more preferably 1 to 10 μm. If the average particle size exceeds this range, the rate of onset of ion exchange tends to be slow, leading to a decrease in detergency. Further, when the amount is less than this range, the hygroscopicity and the CO ₂ absorption increase due to the increase in the specific surface area,
The quality tends to deteriorate significantly. Here, the average particle size is the median size of the particle size distribution.

The crystalline alkali metal silicate having such average particle size and particle size distribution can be prepared by pulverizing using a pulverizer such as a vibration mill, a hammer mill, a ball mill, a roller mill and the like. For example, HB
It can be easily obtained by pulverizing with an -O type vibration mill (manufactured by Chuo Kakoki Co., Ltd.).

The content of the crystalline alkali metal silicate is
It is preferable to mix 4 to 75% by weight of the total composition. Particularly, 1) When 2 to 6 ° DH washing water is used, 25 to 55% by weight is used.
2) When washing water of 6 to 10 ° DH is used, 10 to 4% is used.
3) 5 to 3% when using 10 to 20 ° DH washing water.
It is preferable to add 0% by weight.

If the amount is outside this range, it becomes difficult to satisfy the above-mentioned washing conditions.

Next, the crystalline alkali metal silicate having the above composition will be described.

This crystalline alkali metal silicate has the general formula (2) M ₂ O.x'SiO ₂ .y'H ₂ O (2) (where M represents an alkali metal and x '= 1) 0.5-2.
6, y ′ = 0 to 20. ), Wherein x ′ and y ′ in the general formula (2) are 1.7 ≦ x ′ ≦ 2.
2, y ′ = 0 is preferred, and the cation exchange capacity is at least 100 CaCO ₃ mg / g or more, preferably 20
A substance having a capacity of 0 to 400 CaCO ₃ mg / g can be used and is one of the substances having an ion capturing ability in the present invention.

The crystalline alkali metal silicate according to the present invention has an alkali function and an alkali buffering effect, and furthermore has an ion exchange function. Can be suitably adjusted.

The crystalline alkali metal silicate is preferably incorporated in the composition in an amount of 4 to 75% by weight. Particularly, 1) when 2 to 6 ° DH washing water is used, 25 to 55% by weight.
2) When washing water of 6 to 10 ° DH is used, 10 to 4% is used.
3) 5 to 3% when using 10 to 20 ° DH washing water.
It is preferable to add 0% by weight.

If the amount is outside this range, it becomes difficult to satisfy the above-mentioned washing conditions.

The production method of such a crystalline alkali metal silicate is described in Japanese Patent Application Laid-Open No. 60-227895.
It is obtained by firing at ~ 1000 ° C to make it crystalline. For details of the synthesis method, see, for example, Phys. Chem. Glasses.
7, 127-138 (1966), Z. Kristallogr., 129 , 396-404 (19
69) etc. Further, this crystalline alkali metal silicate is, for example, a trade name “Na-SKS-6” from Hoechst.
As (δ-Na ₂ Si ₂ O ₅ ), powdery and granular forms are available.

In the present invention, the crystalline alkali metal silicate having the following composition preferably has an average particle diameter of 0.1 to 50 μm, more preferably 1 to 30 μm, as in the case of the composition. More preferably, it is 1 to 10 μm.

In the present invention, the crystalline alkali metal silicates of the above and the above compositions may be used alone or in combination of two or more, and may account for 50 to 100% by weight of the alkali agent. Preferably, it occupies 70 to 100% by weight.

In the present invention, an amorphous alkali metal silicate can also be used.
No. sodium silicate, Britesil C20,
Britesil H20, Britesil C2
4, Britesil H24 (both are registered trademarks, T
he PQ Corporation) and NABI
ON 15 (registered trademark, RHONE-BOULENC)
Commercially available products, such as those manufactured by Toshiba Corporation.

C) Sequestering Agent Other than Alkali Metal Silicate The sequestering agent other than the alkali metal silicate in the present invention has a Ca ion capturing ability of 200 CaCO ₃ mg / mg.
g or more.

Particularly, those containing 10% by weight or more of a carboxylate polymer are preferable. Specific examples of such a polymer include a polymer or a copolymer having a repeating unit represented by the general formula (4). Is mentioned.

[0075]

Embedded image

(Wherein X ₁ is methyl, H or COOX
₃ , X ₂ represents methyl, H or OH, and X ₃ represents H, an alkali metal, an alkaline earth metal, NH ₄ or ethanolamine. )

In the general formula (4), examples of the alkali metal include Na, K, and Li, and examples of the alkaline earth metal include Ca and Mg.

The polymer or copolymer used in the present invention may be, for example, a polymerization reaction of acrylic acid, (anhydride) maleic acid, methacrylic acid, α-hydroxyacrylic acid, crotonic acid, isocrotonic acid, and salts thereof, or It is synthesized by a copolymerization reaction of each monomer or a copolymerization reaction with another polymerizable monomer. Examples of other copolymer monomers used for copolymerization at this time include, for example, aconitic acid, itaconic acid, citraconic acid, fumaric acid, vinylphosphonic acid, sulfonated maleic acid, diisobutylene, styrene, methyl vinyl ether, ethylene, propylene , Isobutylene, pentene, butadiene, isoprene, vinyl acetate (and vinyl alcohol when hydrolyzed after copolymerization), acrylate, and the like, but are not particularly limited. In addition,
The polymerization reaction is not particularly limited, and a generally known method can be used.

Further, a polyacetal carboxylic acid polymer such as polyglyoxylic acid described in JP-A-54-52196 can also be used.

In the present invention, as the above-mentioned polymer and copolymer, those having a weight average molecular weight of 800 to 1,000,000 are used, and those having a weight average molecular weight of 5000 to 200,000 are preferably used.

The copolymerization ratio of the repeating unit of the general formula (4) to another copolymerizable monomer in the case of copolymerization is not particularly limited, but is preferably the repeating unit of the general formula (4) / other copolymerization. Monomer = copolymerization ratio in the range of 1/100 to 90/10.

In the present invention, the above-mentioned polymer or copolymer accounts for 1 to 50% by weight, preferably 2% by weight, of the total composition.
-30% by weight, more preferably 5-15% by weight. If it is less than 1% by weight, the effects of the present invention cannot be obtained, and
If the amount exceeds 0% by weight, the effect of addition becomes saturated, and the cost is unnecessarily increased without any meaning.

Further, (c) is contained in the sequestering agent of the component c.
-I) The above-mentioned Ca ion trapping ability is 200 CaCO ₃ m
g / g or more carboxylate polymer, and (c-ii)
The ion exchange capacity represented by the following formula (3) is 200 CaC
Containing O ₃ mg / g or more _{aluminosilicate, x "(M 2 O)} · Al 2 O 3 · y" (SiO 2) · w "(H 2 O) (3) ( in the formula, M Alkali metals such as sodium and potassium,
x ″, y ″, w ″ represent the number of moles of each component, and generally 0.7 ≦ x ″ ≦ 1.5, 0.8 ≦ y ″ ≦ 6, w ″
20. ) The ratio of the ci component to the c-ii component is ci / c-ii = 1/20 to 4/1, preferably 1/9 to 4/1 by weight ratio, and ci and c- Those in which the total amount of ii accounts for 70 to 100% by weight of the sequestering agent of the component c are more preferable.

Examples of the aluminosilicate described above include crystalline ones and amorphous ones. The crystalline ones are particularly preferably those represented by the following general formula.

[0085] _{Na 2 O · Al 2 O 3} · ySiO 2 · wH
₂ O (in the formula, y represents a number of 1.8 to 3.0 and w represents a number of 1 to 6.) As the crystalline aluminosilicate (zeolite), type A,
Average primary particle size of 0.1 represented by X-type and P-type zeolites.
1-10 μm synthetic zeolites are preferably used. The zeolite may be used as zeolite agglomerated dry particles obtained by drying the powder and / or the zeolite slurry or the slurry.

The above-mentioned crystalline aluminosilicate can be produced by a conventional method. For example, JP-A-50-123
81 and JP-A-51-12805 can be used.

On the other hand, an amorphous aluminosilicate represented by the same general formula as that of the above-mentioned crystalline aluminosilicate can be produced by a conventional method. For example, SiO ₂ and M ₂ O
(M means an alkali metal) molar ratio of SiO ₂ /
An M ₂ O = 1.0~4.0, the molar ratio of between H ₂ O and M ₂ O is using alkali metal silicate solution is a _{H 2 O / M 2 O =} 12~200, M to The molar ratio of ₂ O to Al ₂ O ₃ is M ₂ O / Al ₂ O ₃ = 1.0 to 2.0;
The molar ratio of ₂ O to M ₂ O is H ₂ O / M ₂ O = 6.0 to 50
The aqueous solution of a low alkali alkali metal aluminate, which is 0, is usually added under a strong stirring at a temperature of 15 to 60 ° C, preferably 30 to 50 ° C.

Next, the resulting white precipitate slurry is heated at a temperature of usually 70 to 100 ° C., preferably 90 to 100 ° C.
It can be advantageously obtained by performing a heat treatment usually for 10 minutes or more and 10 hours or less, preferably 5 hours or less, followed by filtration, washing and drying. At this time, the addition method may be a method of adding an aqueous solution of an alkali metal silicate to an aqueous solution of a low alkali alkali metal aluminate.

The ion exchange capacity of 100 CaC
An amorphous aluminosilicate oil-absorbing carrier having an O ₃ mg / g or more and an oil absorption capacity of 80 ml / 100 g or more can be easily obtained (Japanese Patent Application Laid-Open Nos. 62-191417 and 62-19).
No. 1419).

Other sequestering agents include aminotri (methylenephosphonic acid), 1-hydroxyethylidene-1,1-diphosphonic acid, ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylenephosphonic acid), and the like. Salts, salts of phosphonocarboxylic acids such as 2-phosphonobutane-1,2-dicarboxylic acid, salts of amino acids such as aspartic acid and glutamic acid, and aminopolyacetates such as nitrilotriacetate and ethylenediaminetetraacetate.

Other components in the present invention include, as alkali agents, crystalline and amorphous alkali metal silicates, alkali metal salts such as carbonates and sulfites, and organic amines such as alkanolamines. One.

Further, it may be incorporated in detergents such as non-dissociated polymers such as polyethylene glycol, polyvinyl alcohol and polyvinylpyrrolidone, builders such as salts of organic acids such as diglycolic acid and oxycarboxylate, and carboxymethyl cellulose. Known examples include an anti-fading agent and an anti-redeposition agent.

In addition, the detergent composition of the present invention can also contain the following components. That is, enzymes such as protease, lipase, cellulase, and amylase,
Anticaking agents such as lower alkylbenzene sulfonates, sulfosuccinates, talc, calcium silicate, etc. of about 4, antioxidants such as tertiary butylhydroxytoluene and distyrenated cresol, bleaching agents such as sodium percarbonate and tetraacetylethylenediamine, etc. , A bleach activator, a fluorescent dye, a bluing agent, a fragrance, etc., but these are not particularly limited, and may be blended according to the purpose.

The detergent composition of the present invention contains the above-mentioned components. The method for producing the detergent composition is not particularly limited, and a conventionally known method can be used. For example, as a method for obtaining a high bulk density detergent,
JP-A-61-69897, JP-A-61-6989
9, JP-A-61-69900, JP-A-5-69900
209200 and Japanese Patent Application No. 7-174440 can be used.

[0095]

EXAMPLES The present invention will be described in more detail with reference to Preparation Examples and Test Examples, but the present invention is not limited to these Preparation Examples and the like.

The measured value was measured by the following method.

(1) pH of Washing Liquid The pH of the washing liquid was measured at 25 ° C. by adding a detergent composition to washing water and using a glass electrode pH meter (manufactured by Horiba, Ltd.). At this time, the pH shown in the washing liquid was a value at which the indicated value was sufficiently stable.

(2) Amount of Substance Having Ion-Capturing Ability The ion-capturing ability was measured by the following method, depending on whether the sequestering substance used was an ion exchanger or a chelating agent. In addition, as a method of indicating the ion-capturing ability of the sequestering agent, it is represented by CEC (calcium ion exchange capacity) in the table of the examples, similarly to the alkali metal silicate. The DH hardness was measured by an ion coupling plasma method (ICP method).

In the case of an ion exchanger, 0.1 g of a sample was precisely weighed and added to 100 ml of an aqueous calcium chloride solution (concentration: 500 ppm as CaCO ₃ ).
After stirring at 25 ° C. for 60 minutes, filtration was carried out using a membrane filter having a pore size of 0.2 μm (manufactured by Advantech, nitrocellulose), and the amount of Ca contained in 10 ml of the filtrate was measured by EDTA titration. The calcium ion exchange capacity (cation exchange capacity) of the sample was determined from the value.

In the case of a chelating agent, the ability to capture Ca ions was measured as follows using a calcium ion electrode. All the solutions were prepared using the following buffers. _{Buffer; 0.1M-NH 4 Cl-NH} 4 OH buff
er (pH 10.0) (i) Preparation of calibration curve A standard calcium ion solution was prepared, and a calibration curve showing the relationship between the logarithm of calcium ion concentration and the potential as shown in FIG. 1 was prepared. (Ii) Measurement of Calcium Ion Capturing Capacity About 0.1 g of a sample is weighed in a 100 ml volumetric flask, and the volume is increased with the above buffer solution. In addition, 2000
A CaCl ₂ aqueous solution (pH 10.0) corresponding to 0 ppm (CaCO ₃ equivalent) was dropped from the burette (blanks were also measured). For the dropwise addition, use a CaCl ₂ aqueous solution of 0.1 to
0.2 ml at a time, read the potential at that time,
The calcium ion concentration was determined from the calibration curve of FIG. FIG.
The calcium ion concentration at the drop amount A of the sample in the middle was defined as the calcium ion trapping ability of the sample.

When calculating the amount of a substance having an ion capturing ability, for example, at 4 ° DH used in Test Example 1, the ion concentration is 71.6 CaCO ₃ mg / L (2148 CaCO ₃
mg / 30 L), and 0.5 ° DH is 9.0 CaC
Since it is equivalent to O ₃ mg / L (270 CaCO ₃ mg / 30 L), at least 62.6 CaCO ₃ mg / L is calculated in order to reduce the washing water at 4 ° DH to 0.5 ° DH or less.
(1878 CaCO ₃ mg / 30 L) is required in an amount corresponding to the ion trapping ability. Therefore, in the table showing the results, the amount of the substance having the ion trapping ability is shown in the corresponding unit (CaCO ₃ mg / L).

(3) Average Particle Size and Particle Size Distribution of Alkali Metal Silicate The average particle size and particle size distribution were measured using a laser diffraction type particle size distribution analyzer. That is, about 200 ml of ethanol was injected into a measurement cell of a laser diffraction type particle size distribution analyzer LA-700 type (manufactured by Horiba, Ltd.), and about 0.5 to 5 mg of a sample was suspended. Subsequently, the mixture was stirred for 1 minute while being irradiated with ultrasonic waves, and after sufficiently dispersing the sample, a He-Ne laser (632.8 nm) was incident, and the particle size distribution was measured from its diffraction / scattering pattern.
The analysis uses both the Fraunhofer diffraction theory and the Mie scattering theory to reduce the particle size distribution of suspended particles in the liquid from 0.04 to
It was measured in the range of 262 μm. The average particle size was the median size of the particle size distribution.

Preparation Example 1 (Crystalline alkali metal silicate A
To E) No. 2 sodium silicate (SiO ₂ / Na ₂ O = 2.5) 100
To 5 parts by weight of sodium hydroxide, 55.9 parts by weight of sodium hydroxide and 8.5 parts by weight of potassium hydroxide were added, and the mixture was stirred with a homomixer to dissolve sodium hydroxide and potassium hydroxide. 5.23 parts by weight of finely dispersed anhydrous calcium carbonate and 0.13 parts by weight of magnesium nitrate hexahydrate were added thereto, and mixed using a homomixer. An appropriate amount of the mixture was placed in a nickel crucible, fired in air at a temperature of 700 ° C. for 1 hour, quenched, and then the fired body was pulverized to obtain an alkali metal silicate A of the present invention. The ion exchange capacity of this powder was as high as 305 CaCO ₃ mg / g.

Similarly, alkali metal silicates B, C, D and E having the compositions shown in Table 1 were obtained.

[0105]

[Table 1]

Preparation Example 2 (Amorphous Aluminosilicate) Sodium carbonate was dissolved in ion-exchanged water to prepare a 6% by weight aqueous solution. 132 g of this aqueous solution and 38.28 g of aqueous sodium aluminate solution (Conc.
Placed in a 00 ml baffled reaction vessel. No. 3 water glass 20 diluted with 2 times water was added to the obtained mixed solution under strong stirring.
The reaction was carried out at 40 ° C. while dropping 1.4 g over 20 minutes. At this time, the pH of the reaction system was controlled by blowing CO ₂ gas (pH = 10.5) to optimize the reaction rate. Subsequently, the reaction system was heated to 50 ° C. and stirred at the same temperature for 30 minutes. After that, CO
₂ Gas was blown in to neutralize excess alkali (pH =
9.0). The obtained neutralized slurry was filtered under reduced pressure using filter paper (No. 5C manufactured by Toyo Roshi Kaisha, Ltd.). The filter cake is washed with water 1000 times and filtered and dried (105
C., 300 torr, 10 hours), and the remainder was dried under the same conditions (without washing). Further, crushing was performed to obtain an amorphous aluminosilicate powder of the present invention. The aqueous sodium aluminate solution was placed in a 1000 cc four-necked flask with 243 g of Al (OH) ₃ and a 48% NaOH aqueous solution 2.
98.7 g was added and mixed, heated to 110 ° C. with stirring, and dissolved for 30 minutes to prepare.

The composition of the obtained amorphous aluminosilicate is as follows:
As a result of atomic absorption analysis and plasma emission analysis, Al ₂ O ₃
= 29.6% by weight, SiO ₂ = 52.4% by weight, Na ₂
O = 18.0% by weight (1.0 Na ₂ O.Al ₂
O ₃ · 3.10 SiO ₂ ). Further, the Ca ion trapping ability is 185 CaCO ₃ mg / g, and the oil absorbing ability is 285 ml / 10
0 g, the ratio of the pore volume having a pore diameter of less than 0.1 μm is 9.4%, and the ratio of the pore volume having the pore diameter of 0.1 μm or more and 2.0 μm or less is 76.3%. Is 11.
It was 2% by weight.

Preparation Example 3 (detergent composition) The crystalline alkali metal silicate A obtained in the above Preparation Example
To E, an amorphous aluminosilicate, and other components shown in Tables 2 to 11, detergent compositions having the compositions shown in Tables 2 to 11 were produced by the following methods.

That is, Examples 1-1 to 15 and Examples 1-17 to 20
In the above, an aqueous component (LAS-Na, A
S-Na, No. 1 sodium silicate, maleic acid acrylate copolymer, sodium polyglyoxylate, sodium polyacrylate,
(Citrate sodium, sodium carbonate, sodium sulfate, sodium sulfite) is made into a 60% solids slurry, and the particles obtained by spray-drying the slurry are put into a Loedige mixer. The mixture was granulated while gradually adding the ionic surfactant. In Example 1-16, a 60% solids slurry composed of components other than zeolite was spray-dried, and the obtained particles were put into a high-speed mixer, and further, zeolite equivalent to the blending amount was added and granulated.

[0110] For TAED, PC and enzymes in each example, granular raw materials were blended.

In this way, the average particle size is 300 to 600
A powdery detergent composition having a bulk density of 0.6 to 1.0 g / ml of μm was obtained.

Test Example 1 Using the detergent composition obtained in the above Preparation Example, a cleaning test was performed under the following conditions. (Preparation of an artificially stained cloth) An artificially stained cloth having the following composition was adhered to the cloth to prepare an artificially stained cloth. The artificial contaminant was attached to the cloth by printing the artificial contaminant on the cloth using a gravure roll coater. The step of making the artificially contaminated cloth by adhering the artificially contaminated liquid to the cloth is performed using a gravure roll having a cell capacity of 5
The drying was performed at 8 cm ³ / cm ² , a coating speed of 1.0 m / min, a drying temperature of 100 ° C., and a drying time of 1 minute. Cloth is cotton gold width 20
03 cloth (manufactured by Tanito Shoten) was used. [Composition of artificial contaminated liquid] Lauric acid 0.44% by weight Myristic acid 3.09% by weight 2.31% by weight pentadecanoic acid 6.18% by weight Heptadecanoic acid 0.44% by weight Stearic acid 1.57% by weight Olein 7.75% by weight of acid 13.06% by weight of triolein 2.18% by weight of n-hexadecyl palmitate 6.53% by weight of squalene 1.94% by weight of egg white lecithin liquid crystal material 8.11% by weight of Kanuma red soil 8.11% by weight of carbon black 0.01 Weight% tap water balance

(Washing conditions) Using a tergotometer, rotation speed 100 rpm, washing time 10 minutes, temperature 20
° C, use water 4 ° DH (Ca / Mg = 3/1), Table 2
Washing was performed with the detergents and detergent concentrations shown in Table 11. Usually, the hardness components of the washing water are represented by Ca ²⁺ and Mg ²⁺ , and the weight ratio thereof is Ca / Mg = (60-85) / (40
-15), but here, Ca /
Mg = 3/1 was used. Further, 4 ° DH is the hardness when an equimolar amount of Mg ions is replaced by Ca.

(Calculation of cleaning rate) 55% of original cloth and before and after cleaning
The reflectance at 0 μm was measured with a self-recording colorimeter (manufactured by Shimadzu Corporation), and the cleaning rate D (%) was calculated by the following equation. The results are shown in Tables 3, 5, 7, 9, and 11.

D = (L ₂ −L ₁ ) / (L ₀ −L ₁ ) × 100 (%) L ₀ : reflectance of original cloth L ₁ : reflectance of contaminated cloth before cleaning L ₂ : contaminated cloth after cleaning Reflectance

The abbreviations in Tables 2 to 15 are as follows. POE: Average ethylene oxide addition mole number LAS-Na: Sodium linear alkyl benzene sulfonate AS-Na: Sodium alkyl sulfate Acrylic maleic acid copolymer: "Sokalan
CP5 "(manufactured by BASF Actchenge Shell Shaft,
A copolymer of acrylic acid-maleic acid as a monomer, an average molecular weight of 70000, a sodium polyacrylate: a polymer of sodium acrylate,
Average molecular weight 10,000 Citric acid Na: Trisodium citrate TAED: Tetraacetylethylenediamine PC: Sodium percarbonate Protease: Alkaline protease K-16 cellulase described in JP-A-5-25492: JP-A-63-264699 Alkaline cellulase K lipase: Lipolase NOVO Nordisk Bioindustry LTD

[0117]

[Table 2]

[0118]

[Table 3]

[0119]

[Table 4]

[0120]

[Table 5]

[0121]

[Table 6]

[0122]

[Table 7]

[0123]

[Table 8]

[0124]

[Table 9]

[0125]

[Table 10]

[0126]

[Table 11]

As shown by the above results, when the clothes are not put in, the washing liquid which gives the above-mentioned washing conditions (Example 1)
1, when Examples 1-9 to 1-15 and 1-20) were used, a high cleaning rate was obtained. In particular, the ratio of the crystalline alkali metal silicate to the other sequestering agent is 5/1 to 1/1.
Those having a value of 15 showed a high cleaning rate of 60% or more.
Further, for example, as shown in Example 1-1 of Table 3, it was shown that even when the detergent composition concentration was as low as 0.33 to 0.67 g / L, a cleaning rate of 60% or more was maintained. This means that the standard amount for one use is 25-30 g / 3 for conventional products.
0L, about 0.4% of conventional compact detergent
This indicates that the size is further reduced by 0.7 times.

On the other hand, the washing liquids not given the above-mentioned washing conditions (Examples 1-2 to 1-8, Examples 1-16 to 1-1)
In 9), the detergent composition concentration is from 0.33 to 0.67 g /
At a low concentration of L, only a low cleaning rate was obtained.

Test Example 2 Using the detergent compositions shown in Table 12, a cleaning test was performed under the following conditions.

In the same manner as in Test Example 1, except that the washing temperature was changed to 30 ° C. and the water used was changed to 8 ° DH (Ca / Mg = 3/1), the detergent concentrations shown in Table 13 were changed. Did the laundry. Table 13 shows the results.

[0131]

[Table 12]

[0132]

[Table 13]

As is clear from Table 13, when no clothes are put in, the washing liquid giving the above-mentioned washing conditions (Example 2)
When -1) was used, a high cleaning rate was obtained. On the other hand, the washing liquid not giving the above-mentioned washing conditions (Example 2-
In 2), the detergent composition concentration is 0.50 to 1.20 g /
At a low concentration of L, only a low cleaning rate was obtained.

Test Example 3 A cleaning test was performed using the detergent compositions shown in Table 14 under the following conditions.

In Test Example 1, the washing time was changed to 30 minutes, the washing temperature was changed to 40 ° C., and the water used was changed to 15 ° DH (Ca / M
g = 3/1), except that Table 1 was used in the same manner as in Test Example 1.
Washing was performed at the detergent concentration shown in FIG. Table 15 shows the results.
Shown in

[0136]

[Table 14]

[0137]

[Table 15]

As is clear from Table 15, when no clothes are put in, a washing liquid giving the above-mentioned washing conditions (Example 3)
When -1) was used, a high cleaning rate was obtained. On the other hand, the washing liquid not giving the above-mentioned washing conditions (Example 3)
In 2), the detergent composition concentration is 0.80 to 2.50 g /
At a low concentration of L, only a low cleaning rate was obtained.

[0139]

According to the detergent composition for clothing of the present invention, the detergent is excellent even if the concentration of the surfactant is low, so that the standard amount of the detergent can be smaller than that of the ordinary compact detergent composition for clothing. . Further, since the detergent composition is phosphorus-free, there are few environmental problems.

[Brief description of the drawings]

FIG. 1 is a diagram showing a calibration curve showing a relationship between a logarithm of calcium ion concentration and a potential.

FIG. 2 is a diagram illustrating a relationship between a dropping amount of a sample and a calcium ion concentration.

──────────────────────────────────────────────────の Continued on the front page (72) Inventor Katsuhiko Kasai 1334 Minato, Wakayama City Kao Corporation Research Laboratory (72) Inventor Masaki Tsumori 1334 Minato Wakayama City Research Laboratory Kao Corporation Research Laboratory (72) Inventor Hiroyuki Yamashita Wakayama City 1334 Minato, Kao Corporation Research Institute (56) References JP-A-2-178398 (JP, A) JP-A-6-10000 (JP, A) JP-A-7-53992 (JP, A) Table 6 -501737 (JP, A) (58) Field surveyed (Int. Cl. ⁷ , DB name) C11D 3/08 C11D 3/12-3/37 C11D 17/06

Claims (11)

(57) [Claims] 1. The following components: a) a surfactant, b) an alkali metal silicate, and c) a Ca ion trapping ability of 200 CaCO ₃ mg / g or more.
A sequestering agent other than the component b, wherein the sequestering agent of the component c is a carboxylate polymer, an aluminosilicate, aminotri (methylenephosphonic acid) and a salt thereof, 1-hydroxyethylidene-
1,1-diphosphonic acid and its salt, ethylenediaminetetra (methylenephosphonic acid) and its salt, diethylenetriaminepenta (methylenephosphonic acid) and its salt, phosphonocarboxylic acid salt, amino acid salt, aminopolyacetate, and citric acid At least one selected from the group consisting of trisodium salts, wherein the total amount of the components a, b and c accounts for 70 to 100% by weight of the total composition, and And b / a = 9/1 to 9/11, and the ratio of the b component to the c component is b / c = 5/1 to 1/15. 2. The ratio of the b component to a is b / b in weight ratio.
The detergent composition for clothing according to claim 1, wherein a = 9/1 to 9/11 and the ratio of the component b to the component c is b / c = 4/1 to 1/15. 3. A nonionic surfactant in the surfactant,
3. The detergent composition for clothing according to claim 1, which is contained in an amount of 50 to 100% by weight. 4. The detergent for clothing according to claim 3, wherein the nonionic surfactant is a polyoxyethylene alkyl ether obtained by adding an average of 5 to 15 mol of ethylene oxide to an alcohol having an alkyl group having an average carbon number of 10 to 18. Composition. 5. The detergent composition for clothing according to claim 1, wherein the alkali agent comprises 50 to 100% by weight of the alkali metal silicate. 6. An alkali metal silicate, SiO ₂ / M _2.
O (however, M represents an alkali metal) is 0.5 to
The detergent composition for clothing according to any one of claims 1 to 5, which is 2.6. 7. The detergent composition for clothing according to claim 1, wherein the alkali metal silicate is crystalline. 8. The detergent composition for clothing according to claim 7, wherein the crystalline alkali metal silicate has a composition represented by the following formula (1). _{xM 2 O · ySiO 2 · zMe} m O n · wH 2 O (1) ( wherein, M is Group Ia elements of the periodic table, Me represents IIa, II
b, IIIa, IVa or VIII, represents one or a combination of two or more elements, wherein y / x = 0.5 to 2.
6, z / x = 0.01-1.0, n / m = 0.5-2.
0 and w = 0 to 20. ) 9. The detergent composition for clothing according to claim 7, wherein the crystalline alkali metal silicate has a composition represented by the following formula (2). _{M 2 O · x'SiO 2 · y'H} 2 O (2) ( wherein, M represents an alkali metal, x '= 1.5~2.
6, y ′ = 0 to 20. ) 10. The sequestering agent of component c contains 10% by weight or more of a carboxylate polymer having a Ca ion trapping ability of 200 CaCO ₃ mg / g or more.
The detergent composition for clothing according to any one of the above. 11. The sequestering agent of component c contains (ci) a Ca ion trapping ability of 200 CaCO ₃ mg /
g or more of a carboxylate polymer, and (c-ii) an ion exchange capacity represented by the following formula (3) of 2
Containing 00CaCO ₃ mg / g or more _{aluminosilicate, x "(M 2 O)} · Al 2 O 3 · y" (SiO 2) · w "
(H ₂ O) (3) (where M is an alkali metal, x ″,
y ″, w ″ represents the number of moles of each component, and 0.7 ≦ x ″ ≦
1.5, 0.8 ≦ y ″ ≦ 6, w ″ is 0-20. )
The ratio of the ci component to the c-ii component is ci by weight ratio.
/ C-ii = 1/20 to 4/1, and ci and c-ii
The detergent composition for clothing according to any one of claims 1 to 10, wherein the total amount of the detergent composition accounts for 70 to 100% by weight of the sequestering agent of the component c.