JP3062399B2 - Method for producing nubuck leather-like sheet - Google Patents
Method for producing nubuck leather-like sheetInfo
- Publication number
- JP3062399B2 JP3062399B2 JP6162913A JP16291394A JP3062399B2 JP 3062399 B2 JP3062399 B2 JP 3062399B2 JP 6162913 A JP6162913 A JP 6162913A JP 16291394 A JP16291394 A JP 16291394A JP 3062399 B2 JP3062399 B2 JP 3062399B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- leather
- polyether
- polyurethane resin
- skin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は外観及び風合が天然皮革
ヌバック（スェード）に類似したヌバック調皮革様シー
トの製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a nubuck-like leather-like sheet similar in appearance and feel to natural leather nubuck (suede).
And a method for manufacturing the same.
【０００２】[0002]
【従来の技術】従来、ヌバック調皮革様シートとして
は、表皮表面に極細繊維の立毛を形成し、サンドペーパ
ーなどにより研削（バフィング）して毛足を短く整毛し
たもの、または、ポリウレタン樹脂を含浸あるいはコー
トにより基材に塗布し、湿式法により微多孔質皮膜を形
成した表面のスキン層を研削除去したものが実用化され
ている。一般に、ヌバック調は後者の工程によるものを
指していることが多い。しかしながら、この方法は製造
工程に長時間を要すること、使用する製造設備が限定さ
れていること、従って製品の値段も高くなるため、品質
は良好であっても販売量には結びついてない面がある。
一方、離型紙に表皮層及び接着層を塗布し、これを基材
に貼り合わせて製造する、いわゆる乾式法（微多孔質皮
膜を形成しない）のものは、湿式法を使用しないことか
ら、湿式法の製造設備が不用でコスト上は有利である
が、その最終製品は外観及び表面のタッチにおいて同等
とはならず、品質上での問題がある。2. Description of the Related Art Conventionally, as a nubuck leather-like sheet, a nap of fine fibers is formed on the surface of the skin and ground (buffing) with a sandpaper or the like to shorten the hair length, or a polyurethane resin is used. A material in which a skin layer on the surface on which a microporous film is formed by a wet method, which is applied to a substrate by impregnation or coating, is ground and practically used. Generally, nubuck tone often refers to the latter process. However, this method requires a long time in the manufacturing process, uses only limited manufacturing equipment, and increases the price of the product. is there.
On the other hand, the so-called dry method (which does not form a microporous film) in which a skin layer and an adhesive layer are applied to a release paper and bonded to a substrate, which is manufactured by using a wet method, does not use a wet method. Although the production equipment of the method is unnecessary and cost-effective, the final product is not equal in appearance and surface touch, and there is a quality problem.
【０００３】[0003]
【発明が解決しようとする課題】本発明は湿式法の製造
設備に限定されず、乾式法に近い製造コストで製造可能
な、品質は湿式法と同様の良好なヌバック調皮革様シー
トの製造方法を提供するものである。The present invention is not limited to the production equipment of the wet method, but can be produced at a production cost close to that of the dry method, and has a quality similar to that of the wet method.
The present invention provides a method for manufacturing a semiconductor device.
【０００４】[0004]
【課題を解決するための手段】本発明によれば、表面に
マット調の凹凸模様を有するポリエーテル系ポリウレタ
ン樹脂からなる表皮層を基材に接着させた後、該表皮層
表面の凸部を研削してヌバック調皮革様シートを製造す
る方法において、ポリエーテル系ポリウレタン樹脂が、
ポリオール成分としてポリエーテルを５０重量％以上含
有し、１００％モジュラスが１５０ｋｇ／ｃｍ 2 以下の
ポリウレタン樹脂であることを特徴とするヌバック調皮
革様シートの製造方法が提供される。According to the present invention SUMMARY OF], after bonding the skin layer made of polyether-based polyurethane resin having an uneven pattern matte on the front surface to the substrate, convex portions of said surface skin layer surface To produce nubuck-like leather-like sheets
In the method, the polyether polyurethane resin is
Contains 50% by weight or more of polyether as a polyol component
Has a 100% modulus of 150 kg / cm 2 or less
Nubuck method for producing a leather-like sheet, wherein a polyurethane resin der Rukoto is provided.
【０００５】[0005]
【作用】表皮層表面のマット調凹凸模様の凸部表面が研
削されることにより凹部と凸部の艶が近接し、表皮層表
面全体がマット調で濃色感が強くなる。また、表皮層を
柔軟性を有するポリエーテル系ポリウレタン樹脂で形成
することにより、弾性に富み、且つ、ウェット性もあ
り、しっとりとしたヌメリ感のある感触を有する、表面
強度に優れたヌバック調皮革様シートが得られる。The gloss of the concave portion and the convex portion becomes close to each other by grinding the surface of the convex portion of the mat-like uneven pattern on the surface of the skin layer, and the entire surface of the skin layer becomes matte and has a strong dark color. In addition, by forming the skin layer from a polyether polyurethane resin having flexibility, the nubuck leather is rich in elasticity, has wettability, has a moist and slimy feel, and has excellent surface strength. -Like sheet is obtained.
【０００６】[0006]
【好ましい実施態様】以下に好ましい実施態様を挙げて
本発明を詳細に説明する。本発明で得られるヌバック調
皮革様シートは、基材に表皮層を接着させた構造を有
し、表皮層表面にはマット調の凹凸模様が形成され、該
模様の凸部のみが研削されたものである。本発明で使用
する基材は、従来から皮革様シートに用いられている天
然繊維及び合成繊維の織布や不織布等を用いることがで
き特に限定されない。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail with reference to preferred embodiments. The nubuck leather-like sheet obtained in the present invention has a structure in which a skin layer is adhered to a base material, a mat-like uneven pattern is formed on the surface of the skin layer, and only the projections of the pattern are ground. Things. The substrate used in the present invention can be a woven or nonwoven fabric of natural fibers and synthetic fibers conventionally used for leather-like sheets, and is not particularly limited.
【０００７】また、表皮層は微多孔質被膜を形成せずに
被膜形成したものであり、表面のマット調の凹凸模様の
形成性及び製品の弾性、ウェット感やヌメリ感等の品質
の点からポリエーテル系ポリウレタン樹脂の被膜が特に
適している。このような品質を付与するためには、ポリ
ウレタン樹脂は１００％モジュラスが１５０ｋｇ／ｃｍ
2以下のものが用いられる。ポリエーテル系ポリウレタ
ン樹脂としてはポリエーテル／エステル系又はポリエー
テル／カーボネート系のポリウレタン樹脂が好ましく、
さらに好ましくはポリエーテルがポリウレタン中に少な
くとも５０重量％以上含まれているのものである。表皮
層の厚さは、通常２０〜４０μｍである。ポリエーテル
系ポリウレタン樹脂には着色のための種々の顔料やその
他の配合剤を添加することができる。[0007] The skin layer is formed without forming a microporous film, and it is difficult to form a mat-like uneven pattern on the surface and to improve the quality of the product such as elasticity, wet feeling and slimy feeling. Polyether polyurethane resin coatings are particularly suitable. In order to provide such a quality, the polyurethane resin has a 100% modulus of 150 kg / cm.
2 or less are used . As the polyether-based polyurethane resin, a polyether / ester-based or polyether / carbonate-based polyurethane resin is preferable,
More preferably, the polyurethane contains at least 50% by weight or more of the polyether. The thickness of the skin layer is usually 20 to 40 μm. Various pigments for coloring and other compounding agents can be added to the polyether-based polyurethane resin.
【０００８】表皮層表面にマット調の凹凸模様を形成す
る方法は特に限定されない。好ましい方法は、マット調
の凹凸模様を有する離型紙を用い、この離型紙上にポリ
エーテル系ポリウレタン樹脂溶液をコート等により塗布
する方法、離型紙上で該ポリウレタン樹脂を生成させる
方法等で該ポリウレタン樹脂被膜を形成させた後、離型
紙を剥すことによってマット調の模様を被膜表面に転写
する方法である。本発明で得られる皮革様シートでは、
表皮層表面のマット調の凹凸模様の凸部のみが研削され
たものであり、該凸部のみが研削されるためには凹凸の
高低差（シボの深さ）は少なくとも５μｍであることが
好ましい。The method of forming a mat-like uneven pattern on the surface of the skin layer is not particularly limited. A preferred method is to use a release paper having a mat-like uneven pattern, apply a polyether-based polyurethane resin solution on the release paper by coating or the like, or form the polyurethane resin on a release paper by a method such as this. This is a method in which a mat-like pattern is transferred to the coating surface by peeling off the release paper after forming the resin coating. In the leather-like sheet obtained in the present invention,
Only the convex portions of the mat-like uneven pattern on the surface of the skin layer are ground, and in order to grind only the convex portions, the height difference (depth of the grain) of the unevenness is preferably at least 5 μm. .
【０００９】かくして得られた表皮層は基材に接着され
る。使用する接着剤は両者を強固に接着し得、製品の品
質を損なわないものであれば特に限定されないが、好ま
しい接着剤ポリウレタン系接着剤である。表皮層と接着
剤層の合計の厚さは皮革様シートの風合や強度等の点か
ら少なくとも４０μｍは必要であるが、８０μｍを越え
ると風合が悪くなり好ましくない。[0009] The skin layer thus obtained is adhered to a substrate. The adhesive to be used is not particularly limited as long as the two can firmly adhere to each other and do not impair the quality of the product, but preferred adhesives are polyurethane-based adhesives. The total thickness of the skin layer and the adhesive layer is required to be at least 40 μm from the viewpoint of the feeling and strength of the leather-like sheet, but if it exceeds 80 μm, the feeling deteriorates, which is not preferable.
【００１０】最後に、表皮層表面の凹凸模様の凸部表面
のスキン層のみを研削する。研削は通常サンドペーパー
等で行われるが、これ以外の方法でも構わない。凸部表
面のみを研削することにより凹部と凸部の艶が近ずき、
表皮層全表面がマット調に仕上げられる。本発明で得ら
れる皮革様シートの概略図を図１に示した。[0010] Finally, only the skin layer on the surface of the convex portion of the uneven pattern on the surface of the skin layer is ground. Grinding is usually performed with sandpaper or the like, but other methods may be used. By grinding only the surface of the convex part, the gloss of the concave part and the convex part approach,
The entire surface of the skin layer is finished in a matte tone. Obtained by the present invention
FIG. 1 shows a schematic view of the leather-like sheet to be obtained.
【００１１】[0011]
【実施例】以下に実施例及び比較例を挙げて本発明を更
に詳細に説明する。特に断りのない限り、以下の実施例
及び比較例の部及び％は重量基準である。The present invention will be described in more detail with reference to the following Examples and Comparative Examples. Unless otherwise specified, parts and percentages in the following Examples and Comparative Examples are based on weight.
【００１２】実施例１ １００％モジュラスが２０ｋｇ／ｃｍ2 のポリエーテル
系ポリウレタン樹脂溶液〔固形分３０％のメチルエチル
ケトン（ＭＥＫ）／ジメチルホルムアミド（ＤＭＦ）＝
１／１の溶液〕１００部に、黒の着色剤（カーボンブラ
ック含有量１５％）２０部と希釈溶剤としてＤＭＦ及び
ＭＥＫをそれぞれ２５部混合した溶液を、離型紙（旭リ
リース社製、ウルトラスェード）に約１５０ｇｒ／ｍ2
（ウェット基準）塗布し、乾燥させて表皮形成用の厚み
３０μｍの被膜を得た。更に、その上に接着剤としてポ
リエーテル系２液型ポリウレタン〔固形分４０％のＭＥ
Ｋ／トルエン／ＤＭＦ〕１００部に架橋剤１０部を添加
したものを約１２０ｇｒ塗布し、基材と貼り合わせた。
架橋が完了後、離型紙を剥離した（基材の上に塗布され
た乾燥後の表皮層及び接着剤層のポリウレタンの合計皮
膜厚は約６０μｍであった）。 このようにして得られ
た皮革様シートの表皮の凸部を２４０号サンドペーパー
で研削して最終製品を得た。得られた製品は外観がマッ
ト調で黒度感があり、表面タッチもしっとりとしたヌメ
リ感をもっていた。Example 1 A polyether-based polyurethane resin solution having a 100% modulus of 20 kg / cm 2 [methyl ethyl ketone (MEK) / dimethylformamide (DMF) having a solid content of 30% =
A solution obtained by mixing 20 parts of a black colorant (carbon black content: 15%) and 25 parts of DMF and MEK as diluting solvents in 100 parts of a release paper (Ultra Sued, manufactured by Asahi Release Co., Ltd.) ) To about 150 gr / m 2
(Wet standard) It was applied and dried to obtain a film having a thickness of 30 μm for forming a skin. Further, a polyether-based two-component polyurethane [ME having a solid content of 40%] is further provided thereon as an adhesive.
[K / toluene / DMF] 100 parts and a cross-linking agent 10 parts added thereto was applied in an amount of about 120 gr and bonded to a substrate.
After the crosslinking was completed, the release paper was peeled off (the total thickness of the polyurethane of the skin layer and the adhesive layer after drying applied on the base material was about 60 μm). The convex portion of the skin of the leather-like sheet thus obtained was ground with No. 240 sandpaper to obtain a final product. The resulting product had a matte appearance, a blackness, and a moist slimy touch on the surface.
【００１３】実施例２ １００％モジュラスが５０ｋｇ／ｃｍ2 のポリエーテル
／エステル（６／４）系ポリウレタン樹脂溶液（固形分
３０％のＭＥＫ／ＤＭＦ＝１／１の溶液）を用いた他は
上記実施例１と同様にしてヌバック調皮革様シートを得
た。Example 2 A polyether / ester (6/4) polyurethane resin solution having a 100% modulus of 50 kg / cm 2 (MEK / DMF = 1/1 with a solid content of 30%) was used. A nubuck leather-like sheet was obtained in the same manner as in Example 1.
【００１４】実施例３ １００％モジュラスが９０ｋｇ／ｃｍ2 のポリエーテル
系ポリウレタン樹脂溶液（固形分３０％のＭＥＫ／ＤＭ
Ｆ＝１／１の溶液）を用いた他は実施例１と同様にして
ヌバック調皮革様シートを作成した。Example 3 A polyether polyurethane resin solution having a 100% modulus of 90 kg / cm 2 (MEK / DM having a solid content of 30%)
A nubuck leather-like sheet was prepared in the same manner as in Example 1 except that F = 1/1 solution was used.
【００１５】実施例４ １００％モジュラスが５０ｋｇ／ｃｍ2 のポリエーテル
／エステル（７／３）系ポリウレタン樹脂溶液（固形分
３０％のＭＥＫ／ＤＭＦ＝１／１の溶液）を用い、離型
紙としてリンテック社製 ＥＶ１３０ＴＰＤ（Ｒ−８）
を使用した他は実施例１と同様にしてヌバック調皮革様
シートを得た。Example 4 A 100% modulus polyether / ester (7/3) -based polyurethane resin solution having a modulus of 50 kg / cm 2 (a 30% solids solution of MEK / DMF = 1/1) was used as a release paper. Lintec EV130TPD (R-8)
Was used in the same manner as in Example 1 to obtain a nubuck leather-like sheet.
【００１６】比較例１ １００％モジュラスが９０ｋｇ／ｃｍ2 のポリエステル
系ポリウレタン樹脂溶液（固形分３０％のＭＥＫ／ＤＭ
Ｆ＝１／１の溶液）を用い、離型紙としてリンテック社
製 ＥＶ１３０ＴＰＤ（Ｒ−８）を使用した他は実施例
１と同様にしてヌバック調皮革様シートを得た。Comparative Example 1 A polyester polyurethane resin solution having a 100% modulus of 90 kg / cm 2 (MEK / DM having a solid content of 30%)
F = 1/1 solution), and a nubuck-like leather-like sheet was obtained in the same manner as in Example 1 except that EV130TPD (R-8) manufactured by Lintec Corporation was used as release paper.
【００１７】比較例２ １００％モジュラスが３０ｋｇ／ｃｍ2 のポリエステル
系ポリウレタン樹脂溶液（固形分３０％のＤＭＦ溶液）
１００部に着色剤（カーボンブラック含有量１５％）２
０部、成膜助剤を適量、ＤＭＦを４０部加えた溶液を基
材に約１０００ｇｒ／ｍ2 塗布し、水に約１５分間浸積
して脱ＤＭＦ化してポリウレタンを凝固させた。更に、
約５０℃の温水にて１時間洗浄し脱ＤＭＦを完全に行な
い、更に脱水乾燥することにより微多孔質のポリウレタ
ン皮膜が得られた。その全表面をサンドペーパーで研削
することによりヌバック調皮革様シートが得られた。Comparative Example 2 Polyester polyurethane resin solution having a 100% modulus of 30 kg / cm 2 (DMF solution having a solid content of 30%)
Colorant (carbon black content 15%) 2 in 100 parts
A solution obtained by adding 0 part, an appropriate amount of a film forming aid and 40 parts of DMF was applied to a substrate at about 1000 gr / m 2, and immersed in water for about 15 minutes to remove DMF and coagulate the polyurethane. Furthermore,
The resultant was washed with warm water of about 50 ° C. for 1 hour, completely removed from DMF, and dehydrated and dried to obtain a microporous polyurethane film. The whole surface was ground with sandpaper to obtain a nubuck leather-like sheet.
【００１８】[0018]
【評価結果】上記の各実施例及び比較例のヌバック調皮
革様シートについて、風合、黒度及び製造コストを下記
の評価基準に従って評価した。結果を表１に示す。評価基準 （１）風合い ◎ 極めてソフトなヌメリ感を有する手触りで実用価
値が非常に高い。 ○ ソフトなややヌメリ感を有する手触りで実用可
能。 △ ソフトな手触りがなく実用不可。 × ガサツキの手触りであり全く実用不可。 （２）黒度 ◎ マット調で非常に黒度があり実用価値が非常に高
い。 ○ マット調で黒度があり実用可能。 △ マット調であるが、黒度が不足し実用不可。 × マット調が不足、黒度も不足し全く実用不可。 （３）製造コスト ◎ 比較例１の乾式法のものを◎とする。 ○ 比較例１と比較例２の中間で実用可能。 × 比較例２の湿式法のものを×とする。[Evaluation Results] The texture, blackness and production cost of the nubuck leather-like sheets of the above Examples and Comparative Examples were evaluated according to the following evaluation criteria. Table 1 shows the results. Evaluation Criteria (1) Texture ◎ Extremely practical value due to extremely soft slimy feel. ○ It is practical with a soft, slimy feel. △ No practical use due to lack of soft touch. × Unsatisfactory because of the rough touch. (2) Blackness ◎ Matte tone, very blackness, and very high practical value. ○ Matt-tone blackness and practical. △ Matte tone, but blackness was insufficient and not practical. × Insufficient matte tone and blackness, making it impractical at all. (3) Manufacturing cost 乾 The dry method of Comparative Example 1 is indicated by ◎. ○ It is practically possible between Comparative Example 1 and Comparative Example 2. × The wet method of Comparative Example 2 is designated as x.
【００１９】[0019]
【表１】 [Table 1]
【００２０】[0020]
【発明の効果】本発明により得られるヌバック調皮革様
シートは、弾性に富み、ウェット性及びヌメリ感のある
感触を有し、外観はマット調で濃色感を呈する表面強度
に優れたものであり、種々の衣料品の素材として有用で
ある。また、このヌバック調皮革様シートは、表皮表面
層のマット調の凹凸模様の凸部のみを研削することによ
って容易に、且つ低コストで製造することができる。The nubuck leather-like sheet obtained according to the present invention is rich in elasticity, has a wet and slimy feel, has a matte appearance, and has an excellent surface strength exhibiting a dark color. Yes, it is useful as a material for various clothing items. Further, this nubuck leather-like sheet can be easily and inexpensively manufactured by grinding only the projections of the mat-like uneven pattern on the surface layer of the skin.
【図１】本発明のヌバック調皮革様シートの製造例を示
す。FIG. 1 shows a production example of a nubuck leather-like sheet of the present invention.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 佐藤 浩正 東京都中央区日本橋馬喰町１丁目７番６ 号 大日精化工業株式会社内 (72)発明者 近藤 功 東京都中央区日本橋馬喰町１丁目７番６ 号 大日精化工業株式会社内 (56)参考文献 特開 平５−71078（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) D06N 3/14 B32B 27/40 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Hiromasa Sato 1-7-6 Nihombashi Bakurocho, Chuo-ku, Tokyo Inside Dainippon Seika Kogyo Co., Ltd. (72) Inventor Isao Kondo 1-7-7 Nihombashi Bakurocho, Chuo-ku, Tokyo No. 6 Inside Dainichi Seika Kogyo Co., Ltd. (56) References JP-A-5-71078 (JP, A) (58) Fields investigated (Int. Cl. 7 , DB name) D06N 3/14 B32B 27/40
Claims (2)
エーテル系ポリウレタン樹脂からなる表皮層を基材に接
着させた後、該表皮層表面の凸部を研削してヌバック調
皮革様シートを製造する方法において、ポリエーテル系
ポリウレタン樹脂が、ポリオール成分としてポリエーテ
ルを５０重量％以上含有し、１００％モジュラスが１５
０ｋｇ／ｃｍ 2 以下のポリウレタン樹脂であることを特
徴とするヌバック調皮革様シートの製造方法。1. A skin layer made of a polyether-based polyurethane resin having a mat-like uneven pattern on a surface thereof is adhered to a base material, and a convex portion on the surface of the skin layer is ground to obtain a nubuck tone.
In a method for producing a leather-like sheet, a polyether-based sheet
Polyurethane resin is polyether as a polyol component
At least 50% by weight and a 100% modulus of 15%.
0 kg / cm 2 or less of nubuck method for producing leather-like sheet, wherein a polyurethane resin der Rukoto.
ウレタン樹脂溶液を塗布して作製した表皮層を基材に接
着させる請求項１に記載のヌバック調皮革様シートの製
造方法。Wherein Ma Tsu preparative ChoHanare nubuck method for producing a leather-like sheet according to claim 1 which paper onto the skin layer produced by coating of a polyether-based polyurethane resin solution adhering to the substrate.