JP3055188U - Document case or card case made of synthetic resin - Google Patents
Document case or card case made of synthetic resinInfo
- Publication number
- JP3055188U JP3055188U JP1998004488U JP448898U JP3055188U JP 3055188 U JP3055188 U JP 3055188U JP 1998004488 U JP1998004488 U JP 1998004488U JP 448898 U JP448898 U JP 448898U JP 3055188 U JP3055188 U JP 3055188U
- Authority
- JP
- Japan
- Prior art keywords
- ethylene
- case
- sheet
- resin
- document
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
(57)【要約】
【課題】 エチレン−メチルメタクリレート共重合樹脂
やエチレン−酢酸ビニル共重合樹脂等からなる単層のシ
ート状物を素材とした書類ケース、カードケースの欠点
を解消する。
【解決手段】 書類ケースやカードケースの素材とし
て、エチレン−（メタ）アクリル酸エステル共重合樹脂
及びエチレン−酢酸ビニル共重合樹脂の中から選ばれる
一種以上の樹脂を主体とする組成物からなる中間層の両
面に、密度が０．９１〜０．９３ｇ／ｍ3 のエチレン−
ヘキセン共重合体又は／及びエチレン−オクテン共重合
体を主体とする外層を形成してなるオレフィン系樹脂製
多層シート状物を使用する。
PROBLEM TO BE SOLVED: To solve the drawbacks of a document case and a card case made of a single-layer sheet made of an ethylene-methyl methacrylate copolymer resin, an ethylene-vinyl acetate copolymer resin or the like. SOLUTION: As a material for a document case or a card case, an intermediate made of a composition mainly composed of at least one resin selected from ethylene- (meth) acrylate copolymer resin and ethylene-vinyl acetate copolymer resin. Ethylene with a density of 0.91 to 0.93 g / m 3 on both sides of the layer
An olefin-based resin multilayer sheet having an outer layer mainly composed of a hexene copolymer and / or an ethylene-octene copolymer is used.
Description
【０００１】[0001]
本考案は、合成樹脂からなるシート状物を袋状に成形加工して得られる書類ケ ース又はカードケースに関するものである。 The present invention relates to a document case or a card case obtained by molding a synthetic resin sheet into a bag.
【０００２】[0002]
従来より、書類やカード（キャッシュカード、クレジットカード、テレホンカ ード等）を収納するケースとして、合成樹脂からなるシート状物を袋状に成形加 工して得られる合成樹脂製の書類ケースやカードケースが使用されている。 また、上記の書類ケースやカードケースの素材となる合成樹脂製シート状物の 一つとして、エチレン−メチルメタクリレート共重合樹脂やエチレン−酢酸ビニ ル共重合樹脂からなる単層のシート状物が知られている。 2. Description of the Related Art Conventionally, as a case for storing documents and cards (cash card, credit card, telephone card, etc.), a synthetic resin document case or card obtained by molding a synthetic resin sheet into a bag shape. A case has been used. Also, as one of the synthetic resin sheets used as the material of the above-mentioned document case and card case, a single-layer sheet made of an ethylene-methyl methacrylate copolymer resin or an ethylene-vinyl acetate copolymer resin is known. Have been.
【０００３】[0003]
上記の書類ケースやカードケースを得る場合、例えば、所望の大きさ、形状に 裁断した二枚の合成樹脂製シート状物を重ね合わせ、開口部（書類やカードを出 し入れする箇所）となる部分を除いた周辺部を接合して袋状とするが、この接合 するための加工としては、得られる製品の外観、加工のし易さ、加工のためのコ スト、等の観点から、特に高周波ウエルダー加工が好適である。 従って、上記したエチレン−メチルメタクリレート共重合樹脂やエチレン−酢 酸ビニル共重合樹脂等からなる単層のシート状物は、高周波ウエルダー適性に優 れるという理由から、袋状に加工する上では好適なものであるということができ る。 When the above-mentioned document case or card case is obtained, for example, two synthetic resin sheets cut into a desired size and shape are overlapped to form an opening (a place where documents and cards are taken in and out). The peripheral parts excluding the parts are joined to form a bag, and the joining process is performed in particular from the viewpoint of the appearance of the resulting product, ease of processing, cost for processing, etc. High frequency welding is preferred. Therefore, a single-layer sheet made of the above-described ethylene-methyl methacrylate copolymer resin, ethylene-vinyl acetate copolymer resin, or the like is suitable for processing into a bag shape because of its suitability for high-frequency welding. It can be said that it is.
【０００４】 しかしながら、このエチレン−メチルメタクリレート共重合樹脂やエチレン− 酢酸ビニル共重合樹脂からなる単層のシート状物は、その表面に傷が付き易い（ 即ち、耐傷性に劣る）ため、これらのシート状物を素材とした書類ケースやカー ドケースは、使用しているうちに見栄えが悪くなるという欠点を有していた。However, a single-layer sheet made of the ethylene-methyl methacrylate copolymer resin or the ethylene-vinyl acetate copolymer resin is easily scratched on its surface (that is, poor in scratch resistance). Document cases and card cases made from sheet-like materials have the drawback that their appearance deteriorates during use.
【０００５】 また、エチレン−メチルメタクリレート共重合樹脂やエチレン−酢酸ビニル共 重合樹脂からなる単層のシート状物は、耐熱性に劣るため、これらのシート状物 を素材とした書類ケースやカードケースは、８０〜９０℃程度の温度でも変形し てしまうという欠点や、エチレン−メチルメタクリレート共重合樹脂やエチレン −酢酸ビニル共重合樹脂からなる単層のシート状物は、裁断性にも劣るため、書 類ケースやカードケースを得るのに必要不可欠な裁断加工時において、端部（裁 断することにより生じる端部）近傍が変形してしまい易く、この裁断加工時には 細心の注意を払わなければならない等、これらのシート状物を成形加工して書類 ケースやカードケースを得るときの作業性は、必ずしも良好であるとは言い難い ものであった。A single-layer sheet made of an ethylene-methyl methacrylate copolymer resin or an ethylene-vinyl acetate copolymer resin is inferior in heat resistance. Therefore, a document case or a card case made of such a sheet material is used. Is a disadvantage that it is deformed even at a temperature of about 80 to 90 ° C., and a single-layer sheet made of an ethylene-methyl methacrylate copolymer resin or an ethylene-vinyl acetate copolymer resin is inferior in cutting property. At the time of cutting which is indispensable to obtain a document case or a card case, the vicinity of the end (the end generated by cutting) tends to be deformed, and great care must be taken during this cutting. However, the workability of forming and processing these sheets to obtain document cases and card cases is not always satisfactory. It was.
【０００６】 本考案は、エチレン−メチルメタクリレート共重合樹脂やエチレン−酢酸ビニ ル共重合樹脂からなるシート状物を素材とする書類ケースやカードケースが抱え る欠点を解消するものであり、袋状に成形加工する際の作業性が良好であり、か つ、使用中に見栄えの悪化が起こり難い書類ケース、カードケースを提供するも のである。The present invention solves the drawbacks of a document case and a card case made of a sheet made of an ethylene-methyl methacrylate copolymer resin or an ethylene-vinyl acetate copolymer resin. The purpose of the present invention is to provide a document case and a card case which have good workability in forming into a shape and are hardly deteriorated in appearance during use.
【０００７】[0007]
上記課題を解決するためになされた本考案の書類ケース又はカードケースは、 袋状に成形加工して書類ケースやカードケースとする合成樹脂製シート状物とし て、エチレン−（メタ）アクリル酸エステル共重合樹脂及びエチレン−酢酸ビニ ル共重合樹脂の中から選ばれる一種以上の樹脂を主体とする組成物からなる中間 層の両面に、密度が０．９１〜０．９３ｇ／ｍ3 の範囲にある、エチレン−ヘキ セン共重合体又は／及びエチレン−オクテン共重合体を主体とする組成物からな る外層を形成してなるオレフィン系樹脂製多層シート状物を用いたことを特徴と するものである。The document case or card case of the present invention made in order to solve the above-mentioned problem is made of a synthetic resin sheet which is formed into a bag shape to form a document case or card case, and is made of ethylene- (meth) acrylate. Density is in the range of 0.91 to 0.93 g / m 3 on both surfaces of an intermediate layer composed of a composition mainly composed of one or more resins selected from a copolymer resin and an ethylene-vinyl acetate copolymer resin. A multi-layer sheet made of an olefin resin having an outer layer formed of a composition mainly composed of an ethylene-hexene copolymer or / and an ethylene-octene copolymer. It is.
【０００８】 本考案の書類ケース、カードケースは、オレフィン系樹脂製多層シート状物を 素材として使用するものである。そして、このオレフィン系樹脂製多層シート状 物は、エチレン−（メタ）アクリル酸エステル共重合樹脂及びエチレン−酢酸ビ ニル共重合樹脂の中から選ばれる一種以上の樹脂を主体とする組成物からなる中 間層と、その両面に形成される、密度が０．９１〜０．９３ｇ／ｍ3 の範囲にあ る、エチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体を主体 とする組成物からなる外層とから構成されるものである。The document case and the card case of the present invention use a multilayer sheet made of an olefin resin as a material. The olefin resin multilayer sheet is composed of a composition mainly composed of one or more resins selected from ethylene- (meth) acrylate copolymer resins and ethylene-vinyl acetate copolymer resins. Composition mainly composed of an ethylene-hexene copolymer and / or an ethylene-octene copolymer having a density in the range of 0.91 to 0.93 g / m 3 formed on the intermediate layer and on both surfaces thereof. And an outer layer made of a material.
【０００９】 エチレン−（メタ）アクリル酸エステル共重合樹脂は、エチレンと、アクリル 酸エステル又は／及びメタクリル酸エステルを共重合させたものであり、具体的 には、上記したエチレン−メチルメタクリレート共重合樹脂の他、エチレン−メ チルアクリレート共重合樹脂、エチレン−エチルアクリレート共重合樹脂、等が 使用できる。The ethylene- (meth) acrylate copolymer resin is obtained by copolymerizing ethylene with an acrylate ester and / or a methacrylate ester. Specifically, the above-mentioned ethylene-methyl methacrylate copolymer resin is used. In addition to the resin, an ethylene-methyl acrylate copolymer resin, an ethylene-ethyl acrylate copolymer resin, and the like can be used.
【００１０】 また、このエチレン−（メタ）アクリル酸エステル共重合樹脂としては、（メ タ）アクリル酸エステル成分が５〜３０重量％のもの、特に、得られたシート状 物を袋状に成形加工する際の高周波ウエルダー適性の観点から１５〜３０重量％ のものが好適である。The ethylene- (meth) acrylate copolymer resin has a (meth) acrylate component in an amount of 5 to 30% by weight, and in particular, the obtained sheet is formed into a bag. From the viewpoint of suitability for high-frequency welding at the time of processing, 15 to 30% by weight is suitable.
【００１１】 勿論、このエチレン−（メタ）アクリル酸エステル共重合樹脂としては、エチ レンと共重合する（メタ）アクリル酸エステルの種類や、その含有量が異なるも のを混合したものであってもよい。 また、得られたシート状物、及びそれを袋状に成形加工して得られる書類ケー スやカードケースの特性を損なわない範囲であれば、エチレン及び（メタ）アク リル酸エステル以外の単量体成分が共重合したものであっても差し支えない。Needless to say, the ethylene- (meth) acrylate copolymer resin is a mixture of (meth) acrylic esters copolymerized with ethylene and those having different contents. Is also good. In addition, as long as the properties of the obtained sheet-like material and the document case or card case obtained by forming the same into a bag shape are not impaired, a single material other than ethylene and (meth) acrylic acid ester may be used. The body component may be copolymerized.
【００１２】 エチレン−酢酸ビニル共重合樹脂としては、酢酸ビニル成分が５〜３０重量％ のもの、特に、得られたシート状物を袋状に成形加工する際の高周波ウエルダー 適性の観点から、１５〜３０重量％のものが好適である。As the ethylene-vinyl acetate copolymer resin, a resin having a vinyl acetate component of 5 to 30% by weight, particularly from the viewpoint of suitability for a high-frequency welder when forming the obtained sheet into a bag, is preferred. Those having a concentration of about 30% by weight are suitable.
【００１３】 勿論、このエチレン−酢酸ビニル共重合樹脂としては、酢酸ビニル成分含有量 が異なるものを混合したものであってもよい。 また、得られるシート状物、及びそれを加工して得られる書類ケースやカード ケースの特性を損なわない範囲であれば、エチレン及び酢酸ビニル以外の単量体 成分が共重合したものであっても差し支えない。[0013] Of course, the ethylene-vinyl acetate copolymer resin may be a mixture of resins having different vinyl acetate component contents. In addition, as long as the properties of the obtained sheet-like material and the document case and card case obtained by processing the same are not impaired, even if a monomer component other than ethylene and vinyl acetate is copolymerized. No problem.
【００１４】 シート状物の中間層を形成するエチレン−（メタ）アクリル酸エステル共重合 樹脂及びエチレン−酢酸ビニル共重合樹脂の中から選ばれる一種以上の樹脂には 、必要に応じて、帯電防止剤、酸化防止剤、ヒンダードアミン系化合物等の光安 定剤、滑剤、紫外線吸収剤、無機充填剤、顔料等の着色剤、等の各種添加剤を添 加してもよい。One or more resins selected from an ethylene- (meth) acrylate copolymer resin and an ethylene-vinyl acetate copolymer resin forming an intermediate layer of the sheet-like material may have, if necessary, an antistatic property. Various additives such as a coloring agent such as an agent, an antioxidant, a light stabilizer such as a hindered amine compound, a lubricant, an ultraviolet absorber, an inorganic filler, and a pigment may be added.
【００１５】 また、得られるシート状物、及びそれを袋状に成形加工して得られる書類ケー スやカードケースの特性を損なわない範囲であれば、上記以外の重合体、具体的 には、低密度ポリエチレン、線状低密度ポリエチレン、中密度ポリエチレン、高 密度ポリエチレン等のポリエチレン；ポリプロピレン（プロピレンとエチレン等 とのランダム、ブロック共重合体、即ち、ランダムポリプロピレンやブロックポ リプロピレン等も含む）；ポリブテン；ブテン−α−オレフィン共重合体；オレ フィン系ゴム；水素添加ゴム；エチレン系エラストマー；等を混合しても差し支 えない。Further, as long as the properties of the obtained sheet-like material and the document case or card case obtained by forming it into a bag shape are not impaired, polymers other than those described above, specifically, Polyethylene such as low-density polyethylene, linear low-density polyethylene, medium-density polyethylene, and high-density polyethylene; polypropylene (including random and block copolymers of propylene and ethylene, such as random polypropylene and block polypropylene); polybutene Butene-α-olefin copolymer; olefin rubber; hydrogenated rubber; ethylene elastomer; and the like.
【００１６】 上記の中間層の両面には、密度が０．９１〜０．９３ｇ／ｍ3 の範囲にある、 エチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体を主体とす る組成物からなる外層が形成される。A composition mainly composed of an ethylene-hexene copolymer and / or an ethylene-octene copolymer having a density in the range of 0.91 to 0.93 g / m 3 on both surfaces of the intermediate layer. An outer layer of the object is formed.
【００１７】 本考案において使用する上記のエチレン−ヘキセン共重合体又は／及びエチレ ン−オクテン共重合体の密度は、上記した通り、０．９１〜０．９３ｇ／ｍ3 の 範囲にある。 このエチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体の密 度が０．９１ｇ／ｍ3 未満であると、得られるシート状物の表面がべたつくとい う問題があり、このエチレン−ヘキセン共重合体又は／及びエチレン−オクテン 共重合体の密度が０．９３ｇ／ｍ3 を超える場合では、得られるシート状物の柔 軟性を損なうと共に、当該シート状物が着色剤を含まない或いはその添加量場合 の透明性を損なうという問題がある。The density of the ethylene-hexene copolymer and / or the ethylene-octene copolymer used in the present invention is in the range of 0.91 to 0.93 g / m 3 as described above. If the density of the ethylene-hexene copolymer and / or ethylene-octene copolymer is less than 0.91 g / m 3 , there is a problem that the surface of the obtained sheet-like material is sticky. When the density of the copolymer and / or the ethylene-octene copolymer exceeds 0.93 g / m 3 , the flexibility of the obtained sheet is impaired, and the sheet does not contain a coloring agent. There is a problem that the transparency is impaired when the amount is added.
【００１８】 上記のエチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体に は、必要に応じて、帯電防止剤、酸化防止剤、ヒンダードアミン系化合物等の光 安定剤、滑剤、紫外線吸収剤、無機充填剤、顔料等の着色剤、等の各種添加剤を 添加してもよい。 また、得られるシート状物、及びそれを袋状に成形加工して得られた書類ケー スやカードケースの特性を損なわない範囲であれば、上記以外の重合体、具体的 には、低密度ポリエチレン、線状低密度ポリエチレン、中密度ポリエチレン、高 密度ポリエチレン等のポリエチレン；エチレン−（メタ）アクリル酸エステル共 重合体、エチレン−酢酸ビニル共重合体等のエチレン系共重合体；ポリプロピレ ン（プロピレンとエチレン等とのランダム、ブロック共重合体、即ち、ランダム ポリプロピレンやブロックポリプロピレン等の含む）；ポリブテン；ブテン−α −オレフィン共重合体；オレフィン系ゴム；水素添加ゴム；エチレン系エラスト マー；等を混合しても差し支えない。If necessary, the ethylene-hexene copolymer and / or ethylene-octene copolymer may contain an antistatic agent, an antioxidant, a light stabilizer such as a hindered amine compound, a lubricant, and an ultraviolet absorber. Various additives such as an inorganic filler, a coloring agent such as a pigment, and the like may be added. In addition, as long as the properties of the obtained sheet-like material and the document case or card case obtained by forming it into a bag shape are not impaired, polymers other than those described above, specifically, a low-density polymer may be used. Polyethylene such as polyethylene, linear low-density polyethylene, medium-density polyethylene, and high-density polyethylene; ethylene-based copolymers such as ethylene- (meth) acrylate copolymer and ethylene-vinyl acetate copolymer; and polypropylene (propylene) Random and block copolymers of ethylene with ethylene and the like, that is, including random polypropylene and block polypropylene); polybutene; butene-α-olefin copolymer; olefin rubber; hydrogenated rubber; ethylene elastomer; Mixing is not a problem.
【００１９】 上記した中間層の両面に上記した外層を形成するに当たっては、中間層の両表 面に直接外層を積層するようにして形成してもよいし、この中間層と外層との間 に接着性層を介在させ、積層することも可能であるが、上記のような層構成から なるシート状物は、中間層と外層との層間接着性に優れるため、一般的には、接 着性層を介在させる必要はない。In forming the outer layer on both surfaces of the intermediate layer, the outer layer may be formed by directly laminating the outer layer on both surfaces of the intermediate layer, or between the intermediate layer and the outer layer. Although it is possible to laminate with an adhesive layer interposed, the sheet-like material having the above-mentioned layer structure generally has excellent adhesiveness between the intermediate layer and the outer layer. No intervening layers are required.
【００２０】 本考案において素材として使用するオレフィン系樹脂製多層シート状物の成形 方法として好ましくは、製造工程が簡略である共押出法や共押出インフレーショ ン法（中間層と外層とを直接積層する場合には二種三層の共押出、中間層と外層 との間に接着性層を介在させる場合には、三種五層の共押出となる）である。 但し、中間層と外層とを、カレンダー法、押出法、インフレーション法等の手 段によって別々に成形し、それらを熱ラミネートや適宜の接着剤による接着等の 手段で積層するなどの手段によっても得ることは可能である。In the present invention, the method of forming a multi-layered sheet made of an olefin resin used as a material is preferably a co-extrusion method or a co-extrusion inflation method (a method of directly laminating an intermediate layer and an outer layer) in which the production process is simple. In this case, two types and three layers are co-extruded, and when an adhesive layer is interposed between the intermediate layer and the outer layer, three types and five layers are co-extruded. However, the intermediate layer and the outer layer are separately formed by a method such as a calendering method, an extrusion method, an inflation method, and the like, and are also obtained by laminating them by means such as heat lamination or bonding with an appropriate adhesive. It is possible.
【００２１】 本考案において使用されるオレフィン系樹脂製多層シート状物の厚さについて は、特に限定されるものではないが、上記用途として一般的には、０．０５〜１ ．０ｍｍ程度である。The thickness of the multilayer sheet made of an olefin resin used in the present invention is not particularly limited, but is generally 0.05 to 1. It is about 0 mm.
【００２２】 また、オレフィン系樹脂製多層シート状物における中間層と各外層との厚さの 比は、それぞれ２：１〜４０：１程度の範囲であるのが望ましい。中間層と外層 との厚さの比が、上記範囲を著しく逸脱した場合には、本考案で解決しようとす る課題を解決するには至らない。 尚、両外層の厚さは、必ずしも同じであることは要しない。The ratio of the thickness of the intermediate layer to the thickness of each outer layer in the multilayer sheet made of an olefin resin is preferably in the range of about 2: 1 to 40: 1. If the thickness ratio between the intermediate layer and the outer layer deviates significantly from the above range, the problem to be solved by the present invention cannot be solved. Note that the thicknesses of both outer layers do not necessarily have to be the same.
【００２３】 本考案において使用されるオレフィン系樹脂製多層シート状物は、片面もしく は両面に、梨地や絹目等のエンボス絞を形成することもできるし、箔押しや通常 の印刷によるプリント模様を形成することもできる。 また、水系、溶剤系、紫外線硬化型等の各種塗料による塗膜を形成することも 可能であるが、塗膜を形成した部分は、高周波ウエルダー適性が著しく低下する ので、シート状物表面に塗膜を形成する場合で、かつ、成形加工するのに高周波 ウエルダー加工を行う場合には、例えば、得られる書類ケースやカードケースの 外表面となる面には塗膜を形成するが、内表面となる面には塗膜を形成しない、 等の配慮が必要である。勿論、プリント模様を形成する場合も同様である。 更にまた、シート状物の耐傷性の更なる向上、シート状物のブロッキングを抑 制すること等を目的として、シート状物の表面にシリコンオイルもしくはフッ素 オイルを塗布してもよい。The multilayer sheet made of an olefin resin used in the present invention can form an embossed squeezed pattern such as satin or silk on one or both sides, and can print a pattern by foil stamping or ordinary printing. Can also be formed. It is also possible to form a coating film of various paints such as water-based, solvent-based, and ultraviolet-curing types. When forming a film and performing high-frequency welding at the time of molding, for example, a coating film is formed on the outer surface of the obtained document case or card case, but the inner surface is It is necessary to consider that no coating film is formed on the surface. Of course, the same applies to the case of forming a print pattern. Furthermore, silicone oil or fluorine oil may be applied to the surface of the sheet for the purpose of further improving the scratch resistance of the sheet and suppressing blocking of the sheet.
【００２４】 上記のシート状物を用いて本考案の書類ケース、カードケースを得る方法とし ては、例えば、所望の大きさ、形状に裁断した二枚のシート状物を重ね合わせ、 開口部となる部分を除いた周辺部を高周波ウエルダー加工により接合して袋状に 成形する方法、所望の大きさ、形状に裁断したシート状物を所定箇所で折り曲げ て、重なり合った両端辺部を高周波ウエルダー加工により接合して袋状に成形す る方法、等が採用される。As a method of obtaining the document case and the card case of the present invention by using the above-mentioned sheet-like material, for example, two sheet-like materials cut into a desired size and shape are overlapped, A method of forming a bag by joining the peripheral parts excluding the part that is not formed by high-frequency welding, forming a sheet-like material cut into a desired size and shape at predetermined locations, and applying high-frequency welding to the overlapping side edges And a method of forming into a bag-like shape by joining.
【００２５】 尚、本考案において素材として使用するシート状物は、高周波ウエルダー適性 に優れているので、上記の成形加工に際しては、得られる製品の外観、加工のし 易さ、加工のためのコスト、等に優れる高周波ウエルダー加工を採用するのが有 利であるが、それ以外の手段による接合、例えば、適宜の接着剤を用いての接合 、熱溶着による接合、超音波溶着による接合、等を採用することも不可能なこと ではない。Since the sheet material used as a material in the present invention has excellent suitability for high-frequency welding, the appearance of the obtained product, the ease of processing, and the cost for processing are required during the above-mentioned forming. It is advantageous to employ high-frequency welding, which is excellent in such methods as joining, but joining by other means, such as joining using an appropriate adhesive, joining by thermal welding, joining by ultrasonic welding, etc. It is not impossible to adopt.
【００２６】 上記のようにして得られた本考案の書類ケースやカードケースは、従来より知 られている書類ケースやカードケースと同様に、その商品価値を更に高めるため に、例えば、書類やカードを出し入れする部分（開口部）に、ファスナー等の開 閉具を設けるなどすることも、勿論可能である。The document case and the card case of the present invention obtained as described above are, for example, a document and a card case in order to further increase their commercial value, similarly to the conventionally known document cases and card cases. Of course, it is also possible to provide an opening / closing tool such as a fastener at a portion (opening) into / out of the device.
【００２７】[0027]
以下、図面に基づいて本考案の実施例について説明する。 図１は、本考案のカードケースの一例であり、図２はカードケースの素材とし て用いたオレフィン系樹脂製多層シート状物の部分拡大断面図である。 また、図１中の符号１は本考案のカードケースを示し、図２中の符号２はカー ドケース１の素材となるオレフィン系樹脂製多層シート状物、符号２１はその中 間層、符号２２（ａ）、（ｂ）はその外層をそれぞれ示している。 Hereinafter, embodiments of the present invention will be described with reference to the drawings. FIG. 1 is an example of a card case of the present invention, and FIG. 2 is a partially enlarged cross-sectional view of an olefin-based resin multilayer sheet used as a material of the card case. Reference numeral 1 in FIG. 1 indicates the card case of the present invention, reference numeral 2 in FIG. 2 indicates a multilayer sheet made of an olefin resin as a material of the card case 1, reference numeral 21 indicates an intermediate layer, and reference numeral 22. (A) and (b) show the outer layers, respectively.
【００２８】 図２に示す多層シート状物は、中間層形成用として、エチレン−酢酸ビニル共 重合樹脂（住友化学社製「エバテートＨ−２０３１」）、外層形成用として、エ チレン−オクテン共重合体（ダウケミカル社製「エリート５４００」；密度０． ９１６ｇ／ｍ3 ）を用い、これらの中間層形成用組成物と外層形成用組成物を、 三層Ｔダイ押出機で共押出して得られたものである。 また、この多層シート状物２全体の厚さは０．３ｍｍであり、中間層２１の厚 さが０．２５ｍｍ、各外層２２（ａ）、（ｂ）の厚さがそれぞれ０．０２５ｍｍ である。The multilayer sheet shown in FIG. 2 has an ethylene-vinyl acetate copolymer resin (“Evatate H-2031” manufactured by Sumitomo Chemical Co., Ltd.) for forming an intermediate layer, and an ethylene-octene copolymer for forming an outer layer. By using a united product (“Elite 5400” manufactured by Dow Chemical Company; density: 0.916 g / m 3 ), the composition for forming an intermediate layer and the composition for forming an outer layer are co-extruded with a three-layer T-die extruder. It is a thing. The overall thickness of the multilayer sheet 2 is 0.3 mm, the thickness of the intermediate layer 21 is 0.25 mm, and the thickness of each of the outer layers 22 (a) and (b) is 0.025 mm. .
【００２９】 図１に示すカードケース１は、多層シート状物２を所定の大きさ、形状に裁断 して得た二枚の裁断片（いずれも略方形であるが、一方の裁断片は、カードケー スとしたときにカードＣの出し入れがスムーズに行えるよう、開口部１２となる 部分の略中央部を半円状に切り欠いてある）を重ね合わせ、開口部となる部分を 除く周辺を高周波ウエルダー加工により溶着し、接合して得られたものである（ 高周波ウエルダー加工による溶着部を符号１１で示す）。The card case 1 shown in FIG. 1 has two cut pieces obtained by cutting a multilayer sheet 2 into a predetermined size and shape (both are substantially rectangular, one of the cut pieces is In order to facilitate the insertion and removal of the card C when the card case is formed, a substantially central portion of the portion to be the opening 12 is cut out in a semicircular shape). This is obtained by welding and joining by high-frequency welding (the welded portion by high-frequency welding is indicated by reference numeral 11).
【００３０】 尚、図２に示す多層シート状物２を成形加工して図１に示すカードケース１を 得る際の作業性、具体的には、所定の大きさ、形状に裁断する際の作業性、及び 裁断片を高周波ウエルダー加工により溶着する際の作業性は、いずれも良好であ った。 また、得られたカードケース１は、従来のエチレン−メチルメタクリレート共 重合樹脂やエチレン−酢酸ビニル共重合樹脂等からなる単層シート状物を素材と したカードケースよりも、表面に傷が付き難いものであった。It should be noted that workability when molding and processing the multilayer sheet-like material 2 shown in FIG. 2 to obtain the card case 1 shown in FIG. 1, specifically, work for cutting into a predetermined size and shape. The workability and the workability when welding the cut pieces by high-frequency welding were both good. In addition, the obtained card case 1 is less likely to be scratched on the surface than a card case made of a single-layer sheet made of a conventional ethylene-methyl methacrylate copolymer resin or ethylene-vinyl acetate copolymer resin or the like. Was something.
【００３１】[0031]
本考案の書類ケース又はカードケースは、特定のオレフィン系樹脂製多層シー ト状物を素材としているため、従来のエチレン−メチルメタクリレート共重合樹 脂やエチレン−酢酸ビニル共重合樹脂からなる単層シート状物を素材としたもの のように、使用中に傷が付いて見栄えが悪化するようなことが生じにくく、しか も、８０〜９０℃程度の温度では変形も生じない。 Since the document case or card case of the present invention is made of a specific multi-layer sheet made of an olefin resin, a single-layer sheet made of a conventional ethylene-methyl methacrylate copolymer resin or ethylene-vinyl acetate copolymer resin is used. It is unlikely that the appearance is deteriorated due to scratches during use, as in the case of using a material as a material, but no deformation occurs at a temperature of about 80 to 90 ° C.
【００３２】 また、素材として、高周波ウエルダー適性に優れ、かつ、従来のエチレン−メ チルメタクリレート共重合樹脂やエチレン−酢酸ビニル共重合樹脂からなる単層 シート状物のように、裁断時に端部近傍が変形したりすることのないオレフィン 系樹脂製多層シート状物を使用しているので、シート状物を成形加工する際の作 業性にも優れるものである。The material is excellent in high-frequency welder suitability, and is near the edge portion at the time of cutting, such as a single-layer sheet made of a conventional ethylene-methyl methacrylate copolymer resin or ethylene-vinyl acetate copolymer resin. Since it uses a multi-layer sheet made of an olefin-based resin that does not deform, the workability in forming the sheet is excellent.
【００３３】 更にまた、本考案の書類ケース又はカードケースの素材として使用するオレフ ィン系樹脂製多層シート状物は、着色剤を含まない或いはその添加量が少ない場 合、透明性にも優れるものであり、収納してある書類やカードをケースから出さ ずとも、その内容を容易に視認することが可能であるようなケースを、という要 望にも十分に応え得るものである。Further, the olefin resin multilayer sheet used as a material of the document case or the card case of the present invention is excellent in transparency when it does not contain a coloring agent or its amount is small. It can sufficiently meet the demand for a case in which the contents of a stored document or card can be easily visually recognized without taking it out of the case.
【提出日】平成１０年７月３日[Submission date] July 3, 1998
【手続補正２】[Procedure amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００７[Correction target item name] 0007
【補正方法】変更[Correction method] Change
【０００７】[0007]
上記課題を解決するためになされた本考案の書類ケース又はカードケースは、 袋状に成形加工して書類ケースやカードケースとする合成樹脂製シート状物とし て、エチレン−（メタ）アクリル酸エステル共重合樹脂及びエチレン−酢酸ビニ ル共重合樹脂の中から選ばれる一種以上の樹脂を主体とする組成物からなる中間 層の両面に、密度が０．９１〜０．９３ｇ／ｃｍ3 の範囲にある、エチレン−ヘ キセン共重合体又は／及びエチレン−オクテン共重合体を主体とする組成物から なる外層を形成してなるオレフィン系樹脂製多層シート状物を用いたことを特徴 とするものである。The document case or card case of the present invention made in order to solve the above-mentioned problem is made of a synthetic resin sheet which is formed into a bag shape to be a document case or a card case, and is made of ethylene- (meth) acrylate. copolymer resin and ethylene - on both sides of one or more resins selected from among acetate vinyl Le copolymer resin comprising the composition mainly intermediate layer, the range density of 0.91~0.93g / c m 3 A multi-layer sheet made of an olefin-based resin having an outer layer formed of a composition mainly composed of an ethylene-hexene copolymer or / and an ethylene-octene copolymer. It is.
【手続補正３】[Procedure amendment 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００８[Correction target item name] 0008
【補正方法】変更[Correction method] Change
【０００８】 本考案の書類ケース、カードケースは、オレフィン系樹脂製多層シート状物を 素材として使用するものである。そして、このオレフィン系樹脂製多層シート状 物は、エチレン−（メタ）アクリル酸エステル共重合樹脂及びエチレン−酢酸ビ ニル共重合樹脂の中から選ばれる一種以上の樹脂を主体とする組成物からなる中 間層と、その両面に形成される、密度が０．９１〜０．９３ｇ／ｃｍ3 の範囲に ある、エチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体を主 体とする組成物からなる外層とから構成されるものである。The document case and the card case of the present invention use a multilayer sheet made of an olefin resin as a material. The olefin resin multilayer sheet is composed of a composition mainly composed of one or more resins selected from ethylene- (meth) acrylate copolymer resins and ethylene-vinyl acetate copolymer resins. a middle-layer is formed on both surfaces, the density is in the range of 0.91~0.93g / c m 3, ethylene - and octene copolymer main body - hexene copolymer or / and ethylene And an outer layer made of the composition.
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１６[Correction target item name] 0016
【補正方法】変更[Correction method] Change
【００１６】 上記の中間層の両面には、密度が０．９１〜０．９３ｇ／ｃｍ3 の範囲にある 、エチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体を主体と する組成物からなる外層が形成される。[0016] On both surfaces of the intermediate layer, the density is in the range of 0.91~0.93g / c m 3, ethylene - composition mainly octene copolymer - hexene copolymer or / and ethylene An outer layer of the object is formed.
【手続補正５】[Procedure amendment 5]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１７[Correction target item name] 0017
【補正方法】変更[Correction method] Change
【００１７】 本考案において使用する上記のエチレン−ヘキセン共重合体又は／及びエチレ ン−オクテン共重合体の密度は、上記した通り、０．９１〜０．９３ｇ／ｃｍ3 の範囲にある。 このエチレン−ヘキセン共重合体又は／及びエチレン−オクテン共重合体の密 度が０．９１ｇ／ｃｍ3 未満であると、得られるシート状物の表面がべたつくと いう問題があり、このエチレン−ヘキセン共重合体又は／及びエチレン−オクテ ン共重合体の密度が０．９３ｇ／ｃｍ3 を超える場合では、得られるシート状物 の柔軟性を損なうと共に、当該シート状物が着色剤を含まない或いはその添加量 場合の透明性を損なうという問題がある。[0017] the use in the present invention ethylene - hexene copolymer or / and ethylene emissions - Density octene copolymers, as described above, in the range of 0.91~0.93g / c m 3. The ethylene - hexene copolymer or / and an ethylene - the density of octene copolymer is less than 0.91 g / c m 3, there is a problem that the surface of the sheet resulting sticky, the ethylene - hexene copolymer or / and ethylene - in the case where the density of the octenyl down copolymer exceeds 0.93 g / c m 3, with impair the flexibility of the sheet obtained, the sheet is free of colorants There is a problem that the transparency is lost when the amount is not added or the amount is added.
【手続補正６】[Procedure amendment 6]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００２８[Correction target item name] 0028
【補正方法】変更[Correction method] Change
【００２８】 図２に示す多層シート状物は、中間層形成用として、エチレン−酢酸ビニル共 重合樹脂（住友化学社製「エバテートＨ−２０３１」）、外層形成用として、エ チレン−オクテン共重合体（ダウケミカル社製「エリート５４００」；密度０． ９１６ｇ／ｃｍ3 ）を用い、これらの中間層形成用組成物と外層形成用組成物を 、三層Ｔダイ押出機で共押出して得られたものである。 また、この多層シート状物２全体の厚さは０．３ｍｍであり、中間層２１の厚 さが０．２５ｍｍ、各外層２２（ａ）、（ｂ）の厚さがそれぞれ０．０２５ｍｍ である。The multilayer sheet shown in FIG. 2 has an ethylene-vinyl acetate copolymer resin (“Evatate H-2031” manufactured by Sumitomo Chemical Co., Ltd.) for forming an intermediate layer, and an ethylene-octene copolymer for forming an outer layer. polymer (Dow Chemical Co. "Elite 5400"; density 0. 916g / c m 3) used, these composition for forming an intermediate layer and an outer layer forming composition, resulting coextruding a three-layer T-die extruder It was done. The overall thickness of the multilayer sheet 2 is 0.3 mm, the thickness of the intermediate layer 21 is 0.25 mm, and the thickness of each of the outer layers 22 (a) and (b) is 0.025 mm. .
【図１】本考案の一実施例（カードケースとしたもの）
を示す図である。FIG. 1 shows an embodiment of the present invention (a card case).
FIG.
【図２】図１に示す例において素材として使用したオレ
フィン系樹脂製多層シート状物の部分拡大断面図であ
る。FIG. 2 is a partially enlarged cross-sectional view of an olefin-based resin multilayer sheet used as a material in the example shown in FIG.
１・・・カードケース ２・・・オレフィン系樹脂製多層シート状物 ２１・・・中間層 ２２（ａ）、（ｂ）・・・外層 DESCRIPTION OF SYMBOLS 1 ... Card case 2 ... Multilayer sheet made of olefin resin 21 ... Intermediate layer 22 (a), (b) ... Outer layer
─────────────────────────────────────────────────────
────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成１０年７月３日[Submission date] July 3, 1998
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】請求項１[Correction target item name] Claim 1
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｇ０６Ｋ 19/00 Ｇ０６Ｋ 19/00 Ｙ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI G06K 19/00 G06K 19/00 Y
Claims (1)
形加工して得られる書類ケース又はカードケースであっ
て、 合成樹脂からなるシート状物が、エチレン−（メタ）ア
クリル酸エステル共重合樹脂及びエチレン−酢酸ビニル
共重合樹脂から選ばれる一種以上を主体とする組成物か
らなる中間層の両面に、密度が０．９１〜０．９３ｇ／
ｍ3 の範囲にある、エチレン−ヘキセン共重合体又は／
及びエチレン−オクテン共重合体を主体とする組成物か
らなる外層を形成してなるオレフィン系樹脂製多層シー
ト状物である、合成樹脂製書類ケース又はカードケー
ス。1. A document case or card case obtained by forming a sheet of synthetic resin into a bag, wherein the sheet of synthetic resin is an ethylene- (meth) acrylate copolymer. A density of 0.91 to 0.93 g /
in the range of m 3, an ethylene - hexene copolymer or /
And a synthetic resin document case or card case, which is an olefin-based resin multi-layer sheet formed by forming an outer layer composed of a composition mainly composed of an ethylene-octene copolymer.