JP3047575B2 - Reflective projection screen - Google Patents
Reflective projection screenInfo
- Publication number
- JP3047575B2 JP3047575B2 JP3314696A JP31469691A JP3047575B2 JP 3047575 B2 JP3047575 B2 JP 3047575B2 JP 3314696 A JP3314696 A JP 3314696A JP 31469691 A JP31469691 A JP 31469691A JP 3047575 B2 JP3047575 B2 JP 3047575B2
- Authority
- JP
- Japan
- Prior art keywords
- polyvinyl chloride
- chloride resin
- projection screen
- soft polyvinyl
- sol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、テレビジョン画像映写
用プロジェクター、あるいはオーバーヘッドプロジェク
ターなどから投影された画像を映写するための反射型映
写スクリーンに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a reflection type projection screen for projecting an image projected from a television image projection projector or an overhead projector.
【０００２】[0002]
【従来の技術】従来、画像投影プロジェクターを用いた
映写用の反射型映写スクリーンとしては、例えば、図２
に示すように、ガラス繊維製の織布１（クロスシート）
の表裏両面に、それぞれ軟質ポリ塩化ビニル樹脂シート
２（例えば厚さ１００μｍ〜２５０μｍ程度）と軟質ポ
リ塩化ビニル樹脂シート３（例えば厚さ７０μｍ〜２５
０μｍ程度）を貼り合わせ、表面の軟質ポリ塩化ビニル
樹脂シート２に、パール顔料を混練した溶剤タイプのグ
ラビア印刷インキなどパール顔料を含む樹脂塗料によっ
て光学反射層４を形成した両面貼り合わせ形式の反射型
映写スリクーンがある。2. Description of the Related Art Conventionally, as a reflection type projection screen for projection using an image projection projector, for example, FIG.
As shown in the figure, a woven cloth 1 made of glass fiber (cross sheet)
The flexible polyvinyl chloride resin sheet 2 (for example, about 100 μm to 250 μm in thickness) and the flexible polyvinyl chloride resin sheet 3 (for example, 70 μm to 25 in thickness)
(Approximately 0 μm), and a double-sided reflection type in which an optical reflection layer 4 is formed on a soft polyvinyl chloride resin sheet 2 on the surface with a resin paint containing a pearl pigment such as a solvent-type gravure printing ink kneaded with a pearl pigment. There is a type-projection scoreline.
【０００３】又、反射型映写スクリーン軽量化のため
に、織布１の片面のみに軟質ポリ塩化ビニル樹脂シート
２を貼り合わせた片面貼り合わせ形式の反射型映写スク
リーン（図示せず）がある。In order to reduce the weight of the reflection type projection screen, there is a single-sided reflection type projection screen (not shown) in which a soft polyvinyl chloride resin sheet 2 is bonded to only one side of the woven fabric 1.
【０００４】上記反射型映写スクリーンは、通常、巻取
り状態で保管されており、使用する場合には、高所より
概略垂直下方に吊り下げて使用されるものである。[0004] The above-mentioned reflection type projection screen is usually stored in a rolled state, and when used, it is used by being suspended substantially vertically downward from a high place.
【０００５】[0005]
【発明が解決しようとする課題】上記の反射型映写スク
リーンは、織布の両面、又は片面に軟質ポリ塩化ビニル
樹脂シートを加熱加圧ラミネートすることによって形成
加工されたものであるため、軟質ポリ塩化ビニルシート
と織布との間のラミネート時のテンションの影響や、ラ
ミネート加工後に残留する加工ストレスや外気温度の変
動などによる収縮が発生し、その収縮率の差によるカー
ル状の変形が生じやすい。The reflection type projection screen is formed by laminating a soft polyvinyl chloride resin sheet on both sides or one side of a woven fabric by heating and pressing. The effect of tension during lamination between the vinyl chloride sheet and the woven fabric, shrinkage due to processing stress remaining after lamination and fluctuations in the outside air temperature occur, and curl-like deformation due to the difference in the shrinkage rate easily occurs .
【０００６】そこで、カール防止のために、予めアクリ
ル樹脂やウレタン樹脂によってディップコート（浸漬塗
布）した織布を軟質ポリ塩化ビニルとラミネートするこ
とが行われるが、映写スクリーン本体の重量が増大する
といったことが考えられる。In order to prevent the curl, a woven cloth previously dip-coated (dip-coated) with an acrylic resin or a urethane resin is laminated with soft polyvinyl chloride. However, the weight of the projection screen body increases. It is possible.
【０００７】本発明は、加熱加圧ラミネート加工の影響
によるカール状の変形を防止し、映写スクリーン本体重
量を軽量化することを目的とするものである。SUMMARY OF THE INVENTION It is an object of the present invention to prevent curl-like deformation due to the influence of heating and pressing lamination and to reduce the weight of a projection screen body.
【０００８】[0008]
【課題を解決するための手段】本発明は、表面にパール
顔料を含有する樹脂塗料による光学反射層を備えた軟質
ポリ塩化ビニル樹脂シート若しくはパール顔料を練り込
んだ軟質ポリ塩化ビニルシート１２の裏面にガラス製若
しくは合成樹脂製の織布１１をフィルムラミネート方式
にて裏打ちし、該軟質ポリ塩化ビニルシート１２と反対
側の前記織布１１面に、コーティング方式により可塑剤
入り塩化ビニル樹脂ゾルをコーティングしてゾルコート
層１３を設けたことを特徴とする反射型映写スクリーン
である。SUMMARY OF THE INVENTION The present invention relates to a back surface of a soft polyvinyl chloride resin sheet or a soft polyvinyl chloride sheet 12 into which a pearl pigment is kneaded. And a woven cloth 11 made of glass or synthetic resin is backed by a film laminating method, and a plasticizer-containing vinyl chloride resin sol is coated by a coating method on the woven cloth 11 opposite to the soft polyvinyl chloride sheet 12. And a sol coating layer 13 is provided.
【０００９】[0009]
【実施例】本発明を、実施例に従って詳細に説明すれ
ば、図１は、本発明の反射型映写スクリーンの側断面図
であり、厚さ１０μｍ〜１００μｍ程度のガラス繊維
製、合成樹脂製の織布１１の一面に、厚さ３０μｍ〜３
００μｍ程度（あるいはそれ以上）の軟質ポリ塩化ビニ
ル樹脂シート１２が加熱加圧によりラミネートされてい
る。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail with reference to the embodiments. FIG. 1 is a side sectional view of a reflection type projection screen according to the present invention, which is made of glass fiber or synthetic resin having a thickness of about 10 to 100 .mu.m. One side of the woven cloth 11 has a thickness of 30 μm to 3 μm.
A soft polyvinyl chloride resin sheet 12 of about 00 μm (or more) is laminated by heating and pressing.
【００１０】軟質ポリ塩化ビニル樹脂シート１２は、ポ
リ塩化ビニル樹脂に適宜量、例えば３０ｗ％（重量％）
〜６０ｗ％（重量％）の可塑剤を混入したものである。The soft polyvinyl chloride resin sheet 12 is formed by adding an appropriate amount, for example, 30 w% (% by weight) to the polyvinyl chloride resin.
６０60 w% (% by weight) of a plasticizer.
【００１１】軟質ポリ塩化ビニル樹脂シート１２の表面
には、パール顔料を含有する樹脂塗料により、スクリー
ンに投影される画像光の反射性能を持たせるために、例
えば厚さ５μｍ〜２０μｍ程度の光学反射層１４が形成
されている。The surface of the soft polyvinyl chloride resin sheet 12 is coated with a resin paint containing a pearl pigment so as to have a reflection performance of image light projected on a screen. A layer 14 is formed.
【００１２】又、軟質ポリ塩化ビニル樹脂シート１２
は、透明乃至白色不透明のいずれであっもよく、又、特
に、光学反射層１４を設ける必要はなく、軟質ポリ塩化
ビニル樹脂シート１２の樹脂本体全体にパール顔料を練
り込むことによって、スクリーン反射性能を持たせるよ
うにしてもよい。Also, a soft polyvinyl chloride resin sheet 12
May be any of transparent to white opaque. In particular, it is not necessary to provide the optical reflection layer 14, and the pearl pigment is kneaded into the entire resin body of the soft polyvinyl chloride resin sheet 12 to obtain the screen reflection performance. May be provided.
【００１３】ガラス繊維製、若しくは合成樹脂製の織布
１１は、ガラス繊維を紡糸して得られたガラス繊維製の
縦糸と横糸、若しくは合成樹脂製の縦糸と横糸とによっ
て織布した織布シートであり、透明乃至不透明いずれで
あってもよく、又、黒色調（光吸収性の色調）に着色さ
れていてもよい。The woven cloth 11 made of glass fiber or synthetic resin is a woven sheet woven with warp and weft made of glass fiber obtained by spinning glass fiber or warp and weft of synthetic resin. And may be transparent or opaque, or may be colored in a black tone (light absorbing color tone).
【００１４】本発明において、前記ガラス繊維製、合成
樹脂製の織布１１には、可塑剤入りの塩化ビニル樹脂ゾ
ルをコーティングしてゾルコート層１３が形成されてい
る。In the present invention, a sol coat layer 13 is formed by coating the woven fabric 11 made of glass fiber or synthetic resin with a vinyl chloride resin sol containing a plasticizer.
【００１５】ゾルコート層１３をコーティングにより形
成するために用いる塩化ビニル樹脂ゾルは、例えば３０
ｗ％〜８０ｗ％の可塑剤（ジオクチルフタレート）を添
加したポリ塩化ビニル樹脂を水性溶媒（水、アルコー
ル）中に分散させた水性エマルジョンタイプの樹脂ゾル
（例えば、ポリ塩化ビニル樹脂微粉末１００ｗ％を、ジ
オクチルフタレート、トリクレジルホスフェート、ジオ
クチルアジペートなどの可塑剤３０ｗ％〜６０ｗ％に溶
解して、水性溶媒中に分散させてゾル化したもの）であ
り、適宜着色顔料によって黒色調（光吸収性の色調）に
着色されていることが望ましい。The vinyl chloride resin sol used to form the sol coat layer 13 by coating is, for example, 30 sol.
An aqueous emulsion-type resin sol (e.g., 100 w% of polyvinyl chloride resin fine powder) in which a polyvinyl chloride resin to which w% to 80 w% of a plasticizer (dioctyl phthalate) is added is dispersed in an aqueous solvent (water, alcohol). Dissolved in a plasticizer such as dioctyl phthalate, tricresyl phosphate, and dioctyl adipate in an amount of 30 w% to 60 w%, and dispersed in an aqueous solvent to form a sol). (Color tone).
【００１６】以下に、本発明の具体的な実施例を示す。 ＜実施例１＞ガラス繊維製織布、又は熱可塑性若しくは
熱硬化性ポリエステル製の織布（均量５０ｇ／ｍ2 〜２
００ｇ／ｍ2 、厚さ４０μｍ〜１５０μｍ程度）の片面
に、黒色など不透明顔料にて着色した塩化ビニル樹脂ゾ
ル（日信化学（株）製；可塑剤３０ｗ％〜４０ｗ％混入
した水性エマルジョンタイプ）を、例えば塗布量１０ｇ
／ｍ2 〜１００ｇ／ｍ2 （厚さ１０μｍ〜１００μｍ）
程度で、ナイフコーター等によって塗布した後に、加熱
温度７０℃〜１６０℃にて固化、乾燥する。Hereinafter, specific embodiments of the present invention will be described. <Example 1> Glass fiber woven fabric or thermoplastic or thermosetting polyester woven fabric (50 g / m 2 to 2
A vinyl chloride resin sol colored by an opaque pigment such as black (manufactured by Nissin Chemical Co., Ltd .; aqueous emulsion type containing 30 w% to 40 w% of a plasticizer) on one surface of 00 g / m 2 and a thickness of about 40 μm to 150 μm) With, for example, an application amount of 10 g
/ M 2 ~100g / m 2 (thickness 10 m - 100 m)
After coating with a knife coater or the like, the mixture is solidified and dried at a heating temperature of 70 ° C to 160 ° C.
【００１７】次に、前記織布の反対面に、パール顔料を
含む樹脂塗布液（ポリ塩化ビニル樹脂バインダーに、パ
ール顔料を１２ｗ％〜３０ｗ％程度混入）を表面にコー
ティングして光学反射層を形成した白色不透明な軟質ポ
リ塩化ビニル樹脂シート（可塑剤３０ｗ％〜６０ｗ％混
入）、又はパール顔料を練り込んだ白色不透明な軟質ポ
リ塩化ビニル樹脂シート、又はパール顔料を含む樹脂塗
布液がコーティングされていない白色不透明な軟質ポリ
塩化ビニル樹脂シート、又はパール顔料が練り込まれて
いない白色不透明な軟質ポリ塩化ビニル樹脂シート（例
えば厚さ３０μｍ〜２００μｍ，可塑剤添加量２０％〜
６０％程度）を加熱（温度８０℃〜１８０℃程度）及び
加圧してラミネートした。これによって、可塑剤入り塩
化ビニル樹脂ゾルと、軟質ポリ塩化ビニル樹脂シート
が、互いに織布の編み目内に入り込んで接合することに
よるブリッジ効果のある反射型映写スクリーンが得られ
た。Next, a resin coating solution containing a pearl pigment (about 12 w% to 30 w% of a pearl pigment mixed with a polyvinyl chloride resin binder) is coated on the opposite surface of the woven fabric to form an optical reflection layer. The formed white opaque soft polyvinyl chloride resin sheet (containing 30 w% to 60 w% of a plasticizer), or a white opaque soft polyvinyl chloride resin sheet into which a pearl pigment is kneaded, or a resin coating solution containing a pearl pigment is coated. White opaque soft polyvinyl chloride resin sheet which is not opaque or white opaque soft polyvinyl chloride resin sheet which is not kneaded with pearl pigment (for example, having a thickness of 30 μm to 200 μm and a plasticizer addition amount of 20% to
(Approximately 60%) and heated (temperature: approximately 80 ° C. to 180 ° C.) and pressurized for lamination. As a result, a reflection type projection screen having a bridging effect due to the plasticizer-containing vinyl chloride resin sol and the soft polyvinyl chloride resin sheet penetrating into and joining the stitches of the woven fabric was obtained.
【００１８】＜実施例２＞ガラス繊維製織布（均量１１
０ｇ／ｍ2 ユーエムグラスＨ−１１６ユニチカ（株）
製）の片面に、ポリ塩化ビニルエマルジョン（ビニブラ
ン３８６、可塑剤３０ｗ％〜４０ｗ％含有、日信化学
（株）製）と、難燃剤と、黒色顔料（カーボンブラッ
ク）とを、８：１：１の割合で配合したポリ塩化ビニル
樹脂ゾルを、ナイフコーターを用いて２０ｇ／ｍ2 ｄｒ
ｙの厚さで塗布し、約１５０℃にて加熱乾燥させる。Example 2 Glass fiber woven fabric (average weight 11
0 g / m 2 U-M Glass H-116 Unitika Ltd.
8: 1: a polyvinyl chloride emulsion (Vinibulan 386, containing 30% to 40% by weight of a plasticizer, manufactured by Nissin Chemical Co., Ltd.), a flame retardant, and a black pigment (carbon black). The polyvinyl chloride resin sol blended at a ratio of 1 was mixed with a knife coater at 20 g / m 2 dr.
Apply with a thickness of y and heat dry at about 150 ° C.
【００１９】続いて、前記ガラス繊維製織布の反対面
に、表面にグラビア印刷にてパール顔料を含む樹脂液を
コーティングして光学反射層を設けた軟質ポリ塩化ビニ
ル樹脂シート（可塑剤４０ｗ％含有、乳白色、厚さ１０
０μｍ、タツノ化学（株）製）を、温度８０℃〜１５０
℃にて加熱加圧ラミネートした。これによって、可塑剤
入り塩化ビニル樹脂ゾルと、軟質ポリ塩化ビニル樹脂シ
ートが、互いに織布の編み目内に入り込んで接合するこ
とによるブリッジ効果のある反射型映写スクリーンが得
られた。Then, a soft polyvinyl chloride resin sheet (40% by weight of plasticizer) is provided with an optical reflection layer by coating a resin liquid containing a pearl pigment on the surface opposite to the woven fabric made of glass fiber by gravure printing. Contained, milky white, thickness 10
0 μm, manufactured by Tatsuno Chemical Co., Ltd.) at a temperature of 80 ° C. to 150 ° C.
The laminate was heated and pressed at ℃. As a result, a reflection type projection screen having a bridging effect due to the plasticizer-containing vinyl chloride resin sol and the soft polyvinyl chloride resin sheet penetrating into and joining the stitches of the woven fabric was obtained.
【００２０】[0020]
【作用】本発明反射型映写スクリーンは、織布１１の一
面の反射表面（映写面）側に反射効果を持たせた軟質ポ
リ塩化ビニル樹脂シート１が貼り合わされ、該織布１１
の他面（裏面）側には、可塑剤入りポリ塩化ビニル樹脂
ゾルを薄膜状にコーティングして形成した軟質ポリ塩化
ビニルによる薄膜状のゾルコート層１３を形成したの
で、織布１１の両面に軟質ポリ塩化ビニルを加熱加圧ラ
ミネート加工した従来の映写スクリーンと比較して、ラ
ミネート加工の影響によるカール状の変形の発生が軽減
でき、又、前記ゾルコート層１３によって、織布１１に
対するディップコートの必要性が解消されて、映写スク
リーン本体の重量を軽量化できる。In the reflection type projection screen of the present invention, a soft polyvinyl chloride resin sheet 1 having a reflection effect is attached to one reflection surface (projection surface) of a woven cloth 11, and the woven cloth 11
On the other side (back side), a thin sol coat layer 13 made of a soft polyvinyl chloride formed by coating a polyvinyl chloride resin sol containing a plasticizer in a thin film is formed. Compared with a conventional projection screen obtained by laminating polyvinyl chloride under heat and pressure, the occurrence of curl-like deformation due to the laminating process can be reduced, and the sol coat layer 13 makes it necessary to dip coat the woven fabric 11. And the weight of the projection screen body can be reduced.
【００２１】又、織布１１本体は、本来的に外的変形応
力に対して追従変形性があり、それに加えて外的変形応
力に対して比較的追従変形性のあるゾルコート層１３が
裏面側に形成されているので、巻かれた状態で保管され
る上記反射型映写スクリーンに生じ易いカール状の巻き
癖が、使用時における巻き戻し及び高所からの吊り下げ
自重によって短時間内で修正できる。The woven fabric 11 has a sol coat layer 13 which inherently has a follow-up deformation property with respect to external deformation stress, and additionally has a sol-coat layer 13 which has relatively follow-up deformation property with respect to external deformation stress. The curl-shaped curl that tends to occur on the reflective projection screen stored in a wound state can be corrected in a short time by rewinding during use and hanging from a high place by its own weight. .
【００２２】[0022]
【発明の効果】本発明の反射型映写スクリーンは、映写
スクリーンの加熱加圧ラミネート加工の影響によるカー
ル状の変形の発生を防止でき、又、映写スクリーン本体
の重量を従来よりも軽量化できる効果がある。According to the reflection type projection screen of the present invention, it is possible to prevent curl-like deformation due to the influence of the heating / pressing lamination of the projection screen and to reduce the weight of the projection screen body as compared with the conventional one. There is.
【００２３】又、巻取り状態から巻き戻して高所より垂
直下方に吊り下げた時に、保管時におけるカール状の巻
き癖による変形が、スクリーンの自重によって短時間に
垂直下方に平坦に修正される効果がある。Further, when the film is unwound from the winding state and hung vertically downward from a high place, the deformation due to the curl-shaped curl during storage is corrected to be flat vertically downward in a short time by the weight of the screen. effective.
【図１】本発明の反射型映写スクリーンの側断面図であ
る。FIG. 1 is a side sectional view of a reflection type projection screen of the present invention.
【図２】従来の反射型映写スクリーンの側断面図であ
る。FIG. 2 is a side sectional view of a conventional reflection type projection screen.
１…織布 ２…軟質ポリ塩化ビニル樹脂シート ３…軟
質ポリ塩化ビニル樹脂シート ４…光学反射層 １１…
織布 １２…軟質ポリ塩化ビニル樹脂シート １３…ゾ
ルコート層 １４…光学反射層DESCRIPTION OF SYMBOLS 1 ... Woven cloth 2 ... Soft polyvinyl chloride resin sheet 3 ... Soft polyvinyl chloride resin sheet 4 ... Optical reflection layer 11 ...
Woven cloth 12 ... Soft polyvinyl chloride resin sheet 13 ... Sol coat layer 14 ... Optical reflection layer
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7，ＤＢ名) G03B 21/60 ──────────────────────────────────────────────────続 き Continued on front page (58) Field surveyed (Int.Cl. 7 , DB name) G03B 21/60
Claims (1)
る光学反射層を備えた軟質ポリ塩化ビニル樹脂シート若
しくはパール顔料を練り込んだ軟質ポリ塩化ビニルシー
ト１２の裏面にガラス製若しくは合成樹脂製の織布１１
をフィルムラミネート方式にて裏打ちし、該軟質ポリ塩
化ビニルシート１２と反対側の前記織布１１面に、コー
ティング方式により可塑剤入り塩化ビニル樹脂ゾルをコ
ーティングしてゾルコート層１３を設けたことを特徴と
する反射型映写スクリーン。1. A soft polyvinyl chloride resin sheet having an optical reflection layer made of a resin paint containing a pearl pigment on its surface or a soft polyvinyl chloride sheet kneaded with a pearl pigment on the back surface of glass or synthetic resin. Woven cloth 11
Is backed by a film lamination method, and a sol coat layer 13 is provided by coating a vinyl chloride resin sol containing a plasticizer on the surface of the woven fabric 11 opposite to the soft polyvinyl chloride sheet 12 by a coating method. Reflective projection screen.