JP3003934B1 - Manufacturing method of insert material and insert molded product - Google Patents

Abstract

[PROBLEMS] An insert material and insert molding that can be molded even with a thin base sheet, have excellent pattern layer formability, have good appearance without cracks, and facilitate alignment of the pattern with the molded product. Provided is a method of manufacturing an article. SOLUTION: A support sheet 3 having good dimensional stability is releasably laminated on one surface of a base sheet 2 excellent in moldability, and an ink having excellent moldability is laminated on the other surface of the base sheet 2. A pattern layer 5 is provided, and a half-cut or broken-line perforation 6 is provided at a boundary between a molded portion and a non-molded portion of the support sheet 3.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an insert material and a method for producing an insert molded product which can be used for decoration of toys, electric appliances, automobile parts and the like.

[0002]

2. Description of the Related Art Conventionally, insert materials have been used to decorate a resin molded product designed in a three-dimensional shape. That is, the insert material provided with the pattern on the base sheet is three-dimensionally processed by a method such as vacuum molding, the three-dimensionally processed insert material is set in a mold for injection molding, the mold is closed, and the molding resin is filled in the cavity. By injecting and solidifying the molding resin, it is possible to form the resin molded product and at the same time integrally bond the insert material to the surface thereof to decorate the resin molded product.

In the above method, a pattern is printed on one surface of a moldable insert material using an ultraviolet curable ink, and the ultraviolet curable ink is cured by irradiation with ultraviolet rays to form a pattern layer. When a normal printing ink is used to form the design layer, the insert material is heated in the ink drying step, and the dimensional stability of the insert material cannot be maintained. Therefore, in order to form a design layer, an ultraviolet curable ink which does not require heating to solidify the ink is used.

[0004]

However, according to the prior art, since the insert material is difficult to handle if the thickness is small,
It was necessary to use an unnecessarily thick sheet as the base sheet, which was uneconomical.

[0005] Further, since the film constituting the design layer formed by the ultraviolet curable ink has poor moldability, there is a problem that cracks occur when the insert material is molded, and the appearance becomes poor.

In addition, dimensional stability of the base sheet cannot be maintained due to preheating at the time of molding, and it is difficult to align the pattern with the molded product. In particular, when the molded product has a design that needs to be squeezed into a deep shape, it is difficult to obtain a product with the same register.

Therefore, the present invention solves the above-mentioned problems and enables molding even with a thin base sheet, has excellent moldability of a design layer, has good appearance without cracks, and has a good appearance. It is an object of the present invention to provide an insert material and a method for manufacturing an insert molded product in which positioning of the molded product is easy.

[0008]

Means for Solving the Problems An insert material and a method of manufacturing the same according to the present invention are configured as follows to achieve the above object.

In other words, the insert material of the present invention is formed by laminating a support sheet having good dimensional stability on one surface of a base sheet excellent in formability so that the support sheet can be peeled off, and forming a mold on the other surface of the base sheet. The support layer is provided with a design layer made of ink, and a half-cut or broken-line perforation is provided at the boundary between the molded portion and the non-molded portion of the support sheet.

[0010] In the above invention, an adhesive sheet excellent in formability may be formed on the surface of the base sheet on which the design layer is formed.

In the above invention, the adhesive sheet may be formed on the surface of the base sheet on which the design layer is formed via an adhesive.

In the above invention, the adhesive sheet may be formed on the surface of the base sheet on which the design layer has been formed by casting the resin in a molten or dissolved state.

Further, in the above invention, the base sheet and the support sheet may be laminated so that they can be peeled off by thermocompression bonding.

Further, in the above invention, the base sheet and the support sheet may be laminated so as to be peelable via an adhesive or a pressure-sensitive adhesive.

Further, in the above invention, the resin in a molten or dissolved state may be cast on the base sheet and the support sheet may be laminated so as to be peelable.

Further, according to a method of manufacturing an insert-molded article of the present invention, the insert material according to any one of claims 1 to 7 is obtained by removing the support sheet at the molded portion and leaving the support sheet laminated at the non-molded portion. As before, using a preforming mold, preforming into a three-dimensional shape that is almost the same as the cavity shape of the molding die, then placing it in the mold cavity, closing the mold, filling the molding resin, opening the mold Then, by taking out the molded product, an insert molded product in which an insert material is integrally bonded to the surface of the molded product is obtained.

Further, in the above invention, before the insert material is preliminarily formed, the molded portion of the support sheet may be removed along the half-cut or broken-line perforations.

Further, in the above-mentioned invention, the remaining portion of the support sheet may be removed between the preforming of the insert material and the arrangement of the preformed insert material in the mold cavity.

[0019]

Embodiments of the present invention will be described in detail with reference to the drawings.

FIGS. 1 and 2 are sectional views showing one embodiment of the insert material of the present invention. 3 to 7 are cross-sectional views showing one step of the method for manufacturing an insert molded product according to the present invention. FIG. 8 is a partial cross-sectional view showing one embodiment of the insert molded product obtained by the method for producing an insert molded product of the present invention. In the figure, 1 is an insert material, 2 is a base sheet, 3
Is a support sheet, 4 is an adhesive sheet, 5 is a design layer, 6 is a half-cut or broken linear perforation, 7 is a preforming die, 8 is a molding die, and 9 is a molding resin.

The insert material 1 of the present invention is laminated on one surface of a base sheet 2 excellent in formability so that a support sheet 3 having good dimensional stability can be peeled off, and is provided on the other surface of the base sheet 2. A pattern layer 5 made of ink having excellent moldability is provided, and a half-cut or broken-line perforation 6 is provided at a boundary between a molded portion and a non-molded portion of the support sheet 3 (FIG. 1). ~ 2).

As the base sheet 2, an acrylic resin,
It is preferable to use a film made of a nylon-based resin, a urethane-based resin, an olefin-based resin, or a mixture of these with a thermoplastic elastomer, a non-stretched or low-stretched polyester film, and the like. The film thickness is 20-3
00 μm is preferred. Further, the base sheet 2 may be transparent or opaque.

As the support sheet 3, a plastic film having excellent dimensional stability and heat resistance, such as a biaxially stretched polyester film, a polyether olefin film, and a polyimide film, paper, and a metal foil can be used. The thickness is preferably from 20 to 300 μm.

The support sheet 3 may be formed by a casting method. That is, the resin as a raw material is heated to a melting point or higher to be in a molten state, and the supporting sheet 3 is formed with a constant film thickness.
It can be coated on top and cooled to form a film-like film. Alternatively, a film-like film may be formed by coating a solution in a solvent and evaporating and drying the solvent.

The base sheet 2 and the support sheet 3 are preferably laminated by thermocompression bonding or an adhesive or a pressure-sensitive adhesive.

In the case of thermocompression bonding, it is preferable that the temperature of the heated base sheet 2 and support sheet 3 is not higher than the softening temperature of base sheet 2 by 30 ° C. or more. If the temperature is higher than the softening temperature of the base sheet 2 by 30 ° C. or more, wrinkles and the like may occur due to expansion and contraction of the base sheet 2.

As the adhesive or pressure-sensitive adhesive, an acrylic resin or a vinyl resin is suitable. It is desirable that the adhesive or the pressure-sensitive adhesive adheres to the support sheet 3 and does not remain on the base sheet 2 after peeling.

When an adhesive is used, a solution dissolved or dispersed in a solvent or the like is applied using a gravure coater, a reverse coater, a lip coater or the like to a thickness of about 0.1 to 30 μm, and is pressed by a laminator. Since the unnecessary support sheet 3 needs to be removed later, the peeling load is 10
Desirably, it is 400 g / cm.

The design layer 5 is a support sheet 3 of the base sheet 2.
Is formed on the non-laminated surface. The design layer 5 needs to be excellent in moldability. Further, it is preferable that the design layer 5 formed as the outermost layer also has an adhesive force to the molding resin 9. As a material of the pattern layer 5, a urethane-based resin, a vinyl-based resin, a polyester-based resin, a vinyl-based resin, a polyester-based resin, an acrylic resin, etc. It is preferable to use a coloring ink containing a pigment or a dye as a coloring agent. As a method for forming the printing layer, a normal printing method such as an offset printing method, a gravure printing method, or a screen printing method may be used. In particular, an offset printing method or a gravure printing method is suitable for performing multicolor printing and gradation expression. In the case of a single color, a coating method such as a gravure coating method, a roll coating method, and a comma coating method can be adopted. Since the base sheet 2 is held by the support sheet 3 so as to be dimensionally stable, even when a heat treatment such as a drying process is performed when the pattern layer 5 is formed, the pattern layer 5 can be overprinted with high registration accuracy. it can.

Further, a metal thin film layer may be used as the design layer 5. The metal thin film layer is for expressing metallic luster, and is formed by a vacuum evaporation method, a sputtering method, an ion plating method, a plating method, or the like. Aluminum, nickel, gold, platinum, chromium, iron, copper, tin, indium, silver, titanium,
Use metals such as lead and zinc, their alloys or compounds. In particular, when a metal thin film layer is provided in a portion stretched by molding, it is preferable to provide a cluster vapor-deposited film of indium or tin. Also, when providing a metal thin film layer,
In order to improve the adhesion of the metal thin film layer, a front anchor layer or a rear anchor layer may be provided. As the material of the front anchor layer and the rear anchor layer, a two-component cured urethane resin,
It is preferable to use a thermosetting urethane resin, a melamine resin, a cellulose ester resin, a chlorine-containing rubber resin, a chlorine-containing vinyl resin, an acrylic resin, an epoxy resin, a vinyl copolymer resin, or the like. Examples of a method for forming the front anchor layer and the rear anchor layer include a coating method such as a gravure coating method, a roll coating method, and a comma coating method, and a printing method such as a gravure printing method and a screen printing method.

The support sheet 3 is provided with a half-cut or broken-line perforation 6 at the boundary between the molded portion and the non-molded portion (see FIGS. 1 and 2). The half-cut here means that the support sheet 3 is cut but the base sheet 2 is cut.
Means notches that do not cut. Further, the perforations in the form of broken lines are cuts in which a number of cuts penetrating the support sheet 3 and a non-penetrating part are continuous and have a shape like a perforation. The half-cut or broken-line perforations 6 may be provided before or after the formation of the symbol layer 5.

To form a half cut, a Thomson method, a laser method, a dice cut method, or the like may be used.
That is, in the case of the Thomson method, a Thomson blade is fixed to a press machine, a film is set at a predetermined position, and then a cut is made from the support sheet 3 side by pressing.
In the case of the laser method or the dice-cut method, a continuous cut is made by scanning the part to be cut with a laser or a dice. By adjusting the cutting depth, only the support sheet 3 can be cut without cutting the base sheet 2. The support sheet 3 to be removed may be a separated pattern or a continuous pattern.

Further, in order to form a break-shaped perforation, a Thomson method, a laser method, or the like may be used. That is,
What is necessary is just to press using the Thomson blade which has a saw blade-shaped edge. Further, in the laser method, a laser scans a portion to be cut and irradiates the laser intermittently.

Half cut or broken line perforations 6
Is preferably provided in a shape surrounding the periphery of the portion to be formed. Further, the shape may surround a part of the portion to be formed.

An adhesive sheet 4 having excellent moldability may be laminated on the surface of the base sheet 2 on which the design layer 5 is formed (see FIG. 2).

As the adhesive sheet 4, a sheet having excellent moldability and excellent adhesiveness with the molding resin 9 may be used. For example, thermoplastic resin sheets such as polymethyl methacrylate, polycarbonate, ABS, vinyl chloride,
A urethane-based thermoplastic elastomer sheet or the like can be used. The thickness is preferably from 20 to 300 μm.

The base sheet 2 and the adhesive sheet 4 are preferably bonded so as to be firmly fixed by thermocompression bonding or an adhesive. In order to perform thermocompression bonding, the base sheet 2 and the adhesive sheet 4 are preferably heated and pressed with a metal roll, a rubber roll, or the like. As the adhesive, a two-component curing type thermosetting resin is suitable.

The adhesive sheet 4 may be formed by a casting method using a resin in a molten or dissolved state.

As described above, the insert material 1 can be obtained. In order to obtain an insert molded product using the insert material 1 having such a configuration, the following should be performed.

First, the insert material 1 is preformed by a preforming mold 7 (see FIGS. 3 to 5). Preforming mold 7
Depending on the shape of the molded product to be molded, select a convex or concave mold, provide a suction hole with a diameter of about 0.3 to 0.6 mm, or divide the mold into multiple parts and partially enter and exit A member formed as possible (see FIGS. 3 and 4) can be used.

In the insert material 1, the non-molded portion of the support sheet 3 may be removed in advance along the half cut or broken line perforations 6 formed in the support sheet 3 (see FIG. 3).

The preforming is performed by heating and softening the insert material 1 with a heat source and bringing the insert material 1 into close contact with the surface of the preforming die 7 by vacuum suction and / or air pressure (see FIG. 4). At this time, if the molded portion of the support sheet 3 having good dimensional stability has been removed in advance, the molded portion of the base sheet 2 is stretched well, and the non-molded portion of the base sheet 2 is preformed without being stretched. Can be. Further, even if the molded portion of the support sheet 3 is not removed, the base sheet 2 is stretched to follow the preforming mold 7, whereas the support sheet 3 does not follow the mold.
The support sheet 3 has half-cut or broken-line perforations 6
, And peeled from the molded portion of the base sheet 2, the molded portion of the base sheet 2 is stretched well, and the non-molded portion of the base sheet 2 can be preformed without being stretched.

Next, the insert material 1 is taken out from the preforming die 7, and the remaining support sheet 3 is removed (FIG. 5).
reference).

In this way, the insert material 1 can be preformed into a three-dimensional shape substantially the same as the cavity shape of the molding die 8.

Next, the preformed insert material 1 is placed in a molding die 8 (see FIG. 6). At this time, the single-piece insert material 1 may be fed one by one, or a necessary portion of the long insert material 1 may be sent intermittently.
When the long insert material 1 is used, the pattern layer 5 of the insert material 1 is used by using a feeder having a positioning mechanism.
It is good to make the register of the mold coincide with that of the mold. When the insert material 1 is intermittently fed, the insert material 1
If the insert material 1 is fixed after the position is detected by the sensor, the insert material 1 can always be fixed at the same position, which is convenient because the design layer 5 does not shift.

Next, the movable mold is closed with respect to the fixed mold, and the molded resin 9 in a molten state is injected into the cavity from the gate portion of the fixed mold, and the molded resin 9 is solidified to form a resin molded product in the cavity. Is formed and the insert material 1 is integrally bonded to the surface.

Thereafter, the insert molded product is removed from the movable mold, and the insert material 1 adhered to the resin molded product can be trimmed as necessary to obtain an insert molded product (see FIGS. 7 and 8). If the insert material 1 is punched into a desired shape in advance, trimming of the insert material 1 is unnecessary.

The movable mold and the fixed mold as injection molds are composed of a fixed mold and a movable mold having a gate for injecting the molding resin 9, and the fixed mold and the movable mold are closed. In this case, one having one or more cavities surrounded by the cavity forming surfaces of the fixed mold and the movable mold may be used. The insert material 1 set in the cavity formed by the movable mold and the fixed mold for injection molding covers the cavity forming surface.

The molding resin 9 is not particularly limited. For example, acrylic resin, polystyrene resin,
A polyacrylonitrile styrene resin, a polyacrylonitrile butadiene styrene resin, or the like can be used.

The present invention can be applied to a horizontal injection molding machine and a vertical injection molding machine. The mold of the injection molding machine can be applied not only to the case of a two-piece mold but also to the case of a three-piece mold.

[0051]

EXAMPLE A polyethylene terephthalate film having a thickness of 50 μm was used as a support sheet, and an adhesive made of a vinyl chloride-vinyl acetate copolymer resin was coated thereon.
A pattern layer was formed on the laminated film obtained by laminating with a 100 μm nylon film by a screen printing method. The support sheet was half-cut by a laser into a shape surrounding the portion including the design layer to obtain an insert material.

Next, when the insert material was preformed by a vacuum pressure molding method into a three-dimensional shape synchronized with the cavity shape of the injection mold, the base sheet was held by the support sheet, so that the workability was very high. The insert material preformed so that the design of the design layer was accurately arranged at a predetermined position of the three-dimensional shape was obtained.

The preformed insert material is placed in the injection mold cavity, and after clamping, the acrylic resin is injected into the mold cavity, filled, cooled and solidified, then opened, and the molded product is opened. When the support sheet was removed, the pattern layer was accurately positioned at the desired position on the surface of the molded product, and because the pattern layer was excellent in formability, no cracks occurred, and the insert material was firmly attached to the surface of the acrylic molded product. A good-looking insert molded product fixed to the surface was obtained.

[0054]

Since the present invention has the above-described structure, it has the following effects.

The insert material of the present invention is laminated on one surface of a base sheet having excellent formability so that a support sheet having good dimensional stability can be peeled off, and has excellent moldability on the other surface of the base sheet. Is provided with a half-cut or broken-line perforation at the boundary between the molded part and the non-molded part of the support sheet, so that the insert material is given rigidity by the support sheet. In addition, molding can be performed even with a thin base sheet. In addition, since the pattern layer has excellent moldability, it follows the elongation of the insert material and has good appearance without cracks. Further, since the base sheet is held by the support sheet so that the dimensions are stable, the alignment between the design and the molded product is easy.

Further, in the method of manufacturing an insert-molded product according to the present invention, the preform is formed by removing the support sheet from the insert material and leaving the support sheet laminated on the non-molded part. Preforming into a three-dimensional shape that is almost the same as the cavity shape of the molding die using it, then placing it in the mold cavity, closing the mold, filling the molding resin, opening the mold, taking out the molded product, molding Since the insert material is integrally bonded to the surface of the product, it can be molded even with a thin base sheet,
An insert molded product in which the pattern layer is excellent in formability and good in appearance without cracks, and in which the alignment between the design and the molded product is accurate can be easily obtained.

[Brief description of the drawings]

FIG. 1 is a sectional view showing one embodiment of an insert material of the present invention.

FIG. 2 is a sectional view showing one embodiment of the insert material of the present invention.

FIG. 3 is a cross-sectional view showing one step of the method for manufacturing an insert molded product according to the present invention.

FIG. 4 is a cross-sectional view showing one step of the method for manufacturing an insert molded product according to the present invention.

FIG. 5 is a cross-sectional view showing one step of the method for manufacturing an insert molded product according to the present invention.

FIG. 6 is a cross-sectional view showing one step of the method for manufacturing an insert molded product according to the present invention.

FIG. 7 is a cross-sectional view showing one step of the method for manufacturing an insert molded product according to the present invention.

FIG. 8 is a partial cross-sectional view showing one embodiment of an insert molded product obtained by the method for producing an insert molded product of the present invention.

[Description of Signs] 1 Insert material 2 Base sheet 3 Support sheet 4 Adhesive sheet 5 Symbol layer 6 Half cut or broken linear perforated hole 7 Pre-forming die 8 Molding die 9 Molding resin

Claims (10)

(57) [Claims] Claims: 1. A pattern comprising a base sheet having excellent formability, a support sheet having good dimensional stability, which is releasably laminated on one side of a base sheet having excellent formability, and an ink having excellent formability on the other side of the base sheet. An insert material comprising a layer, and a half-cut or broken-line perforation provided at a boundary between a molded portion and a non-molded portion of the support sheet. 2. The surface of the base sheet on which the design layer is formed,
The insert material according to claim 1, wherein an adhesive sheet having excellent moldability is formed. 3. The insert material according to claim 2, wherein the adhesive sheet is formed on the surface of the base sheet on which the design layer is formed via an adhesive. 4. The insert material according to claim 2, wherein the adhesive sheet is formed on a surface of the base sheet on which the design layer has been formed by casting a resin in a molten or dissolved state. 5. The base sheet and the support sheet are thermocompressed and laminated so as to be peelable.
Insert material according to any one of the above. 6. The insert material according to claim 1, wherein the base sheet and the support sheet are laminated so as to be peelable via an adhesive or a pressure-sensitive adhesive. 7. The insert according to claim 1, wherein a resin in a molten or dissolved state is cast on the base sheet and the support sheet is laminated so as to be peelable. 8. A preforming die is formed by using the insert material according to claim 1 in such a manner that the support sheet is peeled off at the molded portion and the support sheet is left laminated at the non-molded portion. Preformed into a three-dimensional shape that is almost the same as the cavity shape of the molding die, then placed in a mold cavity, closed with a mold, filled with molding resin, opened the mold, and taken out the molded product. A method for producing an insert molded product, comprising obtaining an insert molded product in which an insert material is integrally bonded to a surface. 9. The method of manufacturing an insert molded product according to claim 8, wherein a molded portion of the support sheet is removed along a half-cut or broken-line perforation before preforming the insert material. 10. The method according to claim 8, wherein a remaining portion of the support sheet is removed between the preforming of the insert material and the placement of the preformed insert material in the mold cavity.