JP2948952B2 - Carbon coated optical fiber - Google Patents
Carbon coated optical fiberInfo
- Publication number
- JP2948952B2 JP2948952B2 JP3195681A JP19568191A JP2948952B2 JP 2948952 B2 JP2948952 B2 JP 2948952B2 JP 3195681 A JP3195681 A JP 3195681A JP 19568191 A JP19568191 A JP 19568191A JP 2948952 B2 JP2948952 B2 JP 2948952B2
- Authority
- JP
- Japan
- Prior art keywords
- optical fiber
- resin
- acrylate
- coating material
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は遮水性の高いアモルファ
スカーボンを薄くコートした、ハーメチックコート光フ
ァイバの一種であるがカーボンコート光ファイバに関す
るもので、特にテープ心線にした場合一括被覆除去性が
良好で、しかも安定して接続できるカーボンコート光フ
ァイバ心線に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a type of hermetic-coated optical fiber in which amorphous carbon having high water barrier properties is thinly coated, but relates to a carbon-coated optical fiber. The present invention relates to a carbon-coated optical fiber that can be connected stably and stably.
【０００２】[0002]
【従来の技術】一般に石英系光ファイバの被覆材として
は紫外線硬化樹脂（以下ＵＶ樹脂という）系、特にウレ
タン−アクリレート系ＵＶ樹脂が数多く使用されてい
る。2. Description of the Related Art In general, ultraviolet curable resin (hereinafter referred to as "UV resin"), particularly urethane-acrylate UV resin, is widely used as a coating material for a quartz optical fiber.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、このよ
うなウレタン−アクリレート系ＵＶ樹脂を一次被覆材に
用いてカーボンコート光ファイバを被覆した素線、或い
はこの素線によってつくられたテープ心線は、治具を用
いて被覆を除去しようとしても、被覆材のカス等がファ
イバに付着して除去できなかったり、無理に除去しよう
とするとファイバが破損して、融着接続が出来なくな
る。これは、ウレタン−アクリレート系ＵＶ樹脂とカー
ボンコート光ファイバとの接着力が高いためである。However, a wire coated with a carbon-coated optical fiber using such a urethane-acrylate UV resin as a primary coating material, or a tape core made of the wire, Even if it is attempted to remove the coating using a jig, scum of the coating material adheres to the fiber and cannot be removed, or if it is forcibly removed, the fiber is damaged and fusion splicing cannot be performed. This is because the adhesive strength between the urethane-acrylate UV resin and the carbon-coated optical fiber is high.
【０００４】本発明者らは、適度な接着力を有するＵＶ
樹脂を得べく種々検討した結果、ウレタン−アクリレー
ト系ＵＶ樹脂を用いると石英ファイバ裸線よりも、カー
ボンコートした光ファイバとの接着性が高くなることを
知見した。The present inventors have developed a UV light having a moderate adhesive strength.
As a result of various investigations to obtain a resin, it was found that the use of a urethane-acrylate UV resin has higher adhesiveness to a carbon-coated optical fiber than a bare quartz fiber.
【０００５】これに対してシリコーン−アクリレート系
ＵＶ樹脂をカーボンコート光ファイバに使用すると接着
性が低くなり、公知の方法で測定した引抜力（特願平１
−１４８００６号）が所望の範囲となることを知見し
た。On the other hand, when a silicone-acrylate UV resin is used for a carbon-coated optical fiber, the adhesiveness is reduced, and the pull-out force measured by a known method (Japanese Patent Application No. Hei.
148006) in the desired range.
【０００６】本発明は上記の事情に鑑みてなされたもの
で一次被覆材との接着性を低め、被覆材の除去を容易に
行うことができるカーボンコート光ファイバ心線を提供
することを目的とする。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and has as its object to provide a carbon coated optical fiber which can reduce adhesion to a primary coating material and can easily remove the coating material. I do.
【０００７】[0007]
【課題を解決するための手段】本発明に係るカーボンコ
ート光ファイバ心線においては、一次被覆材として、引
抜力測定法によって測定した引抜力が５〜５０ｇ／ｍｍ
の範囲にある紫外線硬化型シリコーン−アクリレート樹
脂を使用することを問題解決の手段とした。In the carbon coated optical fiber according to the present invention, the primary coating material has a pulling force measured by a pulling force measuring method of 5 to 50 g / mm.
The use of an ultraviolet-curable silicone-acrylate resin in the range of (1) was used as a means for solving the problem.
【０００８】[0008]
【作用】本発明は上記の構成となっているので、光ファ
イバ裸線と一次被覆との接着性が好適なものとなり、一
括接続の際に不揃いとなったり或いは、一括被覆除去が
困難となったり、切断カスが残ったりすることがない。Since the present invention has the above-mentioned structure, the adhesiveness between the bare optical fiber and the primary coating is favorable, and the connection becomes uneven at the time of collective connection, or the collective coating is difficult to remove. No cutting residue remains.
【０００９】以下本発明を詳しく説明する。本発明での
シリコーン−アクリレート系ＵＶ樹脂とは、オリゴマー
成分中に少なくとも１〜５０％のシリコーン骨格を有す
るものを言い、モノマー成分として、種々のアクリレー
トモーマを含むものであり、骨格の割合によってその接
着力が変る。Hereinafter, the present invention will be described in detail. The silicone-acrylate UV resin in the present invention refers to a resin having at least 1 to 50% of a silicone skeleton in an oligomer component, and contains various acrylate momers as a monomer component. Its adhesive strength changes.
【００１０】ＵＶ樹脂の硬化は、通常アクリルモノマー
の付加重合によって、三次元の網目構造が形成されるこ
とで進行する。The curing of the UV resin proceeds by forming a three-dimensional network structure usually by addition polymerization of an acrylic monomer.
【００１１】したがって、この硬化に伴なって、網目構
造を作る架橋点の数、すなわちゲル分率が増加すること
が知られている。そしてゲル分率の増加に伴い、この被
覆材と光ファイバとの接着性が高くなって、光ファイバ
との引抜力が大きくなる。Therefore, it is known that the number of cross-linking points forming the network structure, that is, the gel fraction increases with the curing. Then, as the gel fraction increases, the adhesiveness between the coating material and the optical fiber increases, and the pulling force with the optical fiber increases.
【００１２】上記光ファイバの引抜力は、硬化の進行に
伴って一義的に決まるパラメータで、引抜力によって接
着性を代表することができる。The pulling force of the optical fiber is a parameter that is uniquely determined with the progress of curing, and adhesiveness can be represented by the pulling force.
【００１３】上記引抜力の測定は通常の方法によって行
われる。例えば、図１に示すように、試料となる光ファ
イバ１を一部の被覆層２を残した状態で口出しし、この
被覆層２を適宜の治具３に固定するとともに、口出しさ
れた裸線部分４を上記治具３の外部下方に設けられたチ
ャック５にセットする。この状態で、上記治具３は不動
のままチャック５を一定速度で下降させる。この時光フ
ァイバ１の裸線部分４と被覆層２との間に張力（引抜
力）が作用し、ついには裸線部分４が被覆層２より滑り
抜ける。この時の負荷荷重を求めれば、両者間の接着
力、すなわち引抜力が求められる。The measurement of the pull-out force is performed by a usual method. For example, as shown in FIG. 1, an optical fiber 1 serving as a sample is exposed while leaving a part of a coating layer 2, and the coating layer 2 is fixed to an appropriate jig 3, and the exposed bare wire is exposed. The part 4 is set on a chuck 5 provided below and below the jig 3. In this state, the jig 3 moves down the chuck 5 at a constant speed without being moved. At this time, tension (pull-out force) acts between the bare wire portion 4 of the optical fiber 1 and the coating layer 2, and finally the bare wire portion 4 slips out of the coating layer 2. If the applied load at this time is determined, the adhesive force between the two, that is, the pull-out force, is determined.
【００１４】この場合、引抜力が５ｇ／ｍｍ未満では、
一括接続的に先端が不揃となる不都合が発生し、また５
０ｇ／ｍｍを超えると、一括被覆除去が困難となり、無
理に除去しようとすると光ファイバが破損する。In this case, if the drawing force is less than 5 g / mm,
Inconveniences such as unbalanced tips occur due to batch connection.
If it exceeds 0 g / mm, it will be difficult to remove the coating at once, and if it is forcibly removed, the optical fiber will be damaged.
【００１５】このように、本発明のカーボンコート光フ
ァイバは、一次被覆材として引抜力が５〜５０ｇ／ｍｍ
の範囲にすることができる、シリコーン−アクリレート
系ＵＶ樹脂を用いることを特徴とする心線である。As described above, the carbon coated optical fiber of the present invention has a drawing force of 5 to 50 g / mm as a primary coating material.
, Wherein a silicone-acrylate UV resin is used.
【００１６】上記のように一次被覆材はシリコーン−ア
クリレート系ＵＶ樹脂であることが必要だが、その上に
被覆する二次被覆材は、ウレタン−アクリレート、ＵＶ
シリコーン樹脂、エポキシ−アクリレート等いずれも使
用できる。As described above, the primary coating material needs to be a silicone-acrylate UV resin, but the secondary coating material to be coated thereon is urethane-acrylate, UV
Any of silicone resin, epoxy-acrylate and the like can be used.
【００１７】[0017]
【実施例】次に実施例を示して本発明を見体的に説明す
る。光ファイバとして石英光ファイバおよびこの光ファ
イバにカーボンコートしたものを用い、これらに一次被
覆材を被覆した。これをさらに二次被覆材としてすべて
共通のウレタン−アクリレート系ＵＶ樹脂を被覆し表１
に示す試料〜を作製した。Next, the present invention will be described by way of examples. As the optical fiber, a quartz optical fiber and one obtained by coating this optical fiber with carbon were used, and these were coated with a primary coating material. This was further coated with a common urethane-acrylate UV resin as a secondary coating material.
Samples (1) to (4) were prepared.
【００１８】[0018]
【表１】 [Table 1]
【００１９】記の試料〜を用いて、それぞれ４心テ
ープ心線を作成し、ホットストリッパを用いて、一括被
覆除去力を測定するとともに除去後の状態を調査した。
結果を表２に示す。なお、光ファイバの径：１２５μ
ｍ、一次被覆材を被覆した径：２００μｍ、二次被覆材
を被覆した径：２５０μｍとした。Using each of the above-mentioned samples, a four-core tape cord was prepared, and the collective coating removing force was measured using a hot stripper, and the condition after the removal was examined.
Table 2 shows the results. The diameter of the optical fiber: 125 μm
m, diameter coated with the primary coating material: 200 μm, diameter coated with the secondary coating material: 250 μm.
【００２０】[0020]
【表２】 注）カスとは、被覆除去後にファイバに付着した被覆材
の残留物。[Table 2] Note) Scrap is the residue of the coating material attached to the fiber after removing the coating.
【００２１】表２において、試料は一次被覆材として
ウレタン−アクリレート系ＵＶ樹脂を使用しているが、
石英光ファイバを直接被覆しているため接着力は低く、
引抜力は４１ｇ／ｍｍを示し、一括被覆除去性は良好で
ある。In Table 2, the sample used a urethane-acrylate UV resin as the primary coating material.
Adhesive strength is low because it covers silica optical fiber directly,
The drawing force is 41 g / mm, and the collective coating removal property is good.
【００２２】試料はカーボンコート石英光ファイバを
使用しているため、ウレタン−アクリレート系ＵＶ樹脂
との接着力を高く、引抜力が大きく、一括被覆除去性は
極めて悪い。Since the sample uses a carbon-coated quartz optical fiber, it has a high adhesive strength to a urethane-acrylate UV resin, a large pull-out force, and extremely poor collective coating removal.
【００２３】試料は石英光ファイバを用いているがシ
リコーン−アクリレート系ＵＶ樹脂を一次被覆材として
いるので接着性はよく、引抜力も５０ｇ／ｍｍを超えカ
ス発生するが、その付着は除去することができる程度で
ある。Although the sample uses a quartz optical fiber, since the silicone-acrylate UV resin is used as a primary coating material, the adhesiveness is good and the pull-out force exceeds 50 g / mm, and scum is generated. It is possible.
【００２４】試料はカーボンコート石英光ファイバ
に、一次被覆材としてこれに対する接着力の低いシリコ
ーン−アクリレート系ＵＶ樹脂を被覆しているので、一
括被覆除去性は良好である。Since the sample is a carbon-coated quartz optical fiber coated as a primary coating material with a silicone-acrylate UV resin having low adhesion to the optical fiber, the collective coating removal property is good.
【００２５】このようにウレタン−アクリレート系ＵＶ
樹脂の場合、石英光ファイバよりもカーボンコート光フ
ァイバに対するが接着性が高く、またシリコーン−アク
リレート系ＵＶ樹脂の場合は接着性が下がる。これは、
それぞれの樹脂と石英表面、およびカーボンコート表面
との親和性の違いが反映しているものと思料する。Thus, urethane-acrylate UV
In the case of a resin, the adhesion to a carbon coated optical fiber is higher than that of a quartz optical fiber, and in the case of a silicone-acrylate UV resin, the adhesion is reduced. this is,
It is considered that the difference in affinity between each resin and the quartz surface and the carbon coat surface is reflected.
【００２６】[0026]
【発明の効果】以上説明したように、本発明に係るカー
ボンコート光ファイバ心線は、シリコン−アクリレート
系ＵＶ樹脂を一次被覆材として用いることより一括被覆
除去性が良好となるなど、敷設作業の効率が大幅に向上
する利点がある。As described above, the carbon-coated optical fiber core wire according to the present invention can be used in a laying operation such as improving collective coating removal properties by using a silicon-acrylate UV resin as a primary coating material. There is an advantage that the efficiency is greatly improved.
【図１】 引抜力測定装置の一例を示す概略図である。FIG. 1 is a schematic diagram showing an example of a pull-out force measuring device.
１…光ファイバ、２…被覆層、３…治具、４…裸線部
分、５…チャックDESCRIPTION OF SYMBOLS 1 ... Optical fiber, 2 ... Coating layer, 3 ... Jig, 4 ... Bare wire part, 5 ... Chuck
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭63−132138（ＪＰ，Ａ) 特開 平２−309308（ＪＰ，Ａ) 特開 平２−248346（ＪＰ，Ａ) 特開 平３−12343（ＪＰ，Ａ) 特開 平１−260406（ＪＰ，Ａ) 特開 昭59−83107（ＪＰ，Ａ) (58)調査した分野(Int.Cl.6，ＤＢ名) G02B 6/44 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-63-132138 (JP, A) JP-A-2-309308 (JP, A) JP-A-2-248346 (JP, A) JP-A-3- 12343 (JP, A) JP-A-1-260406 (JP, A) JP-A-59-83107 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB name) G02B 6/44
Claims (1)
て測定した引抜力が５〜５０ｇ／ｍｍの範囲にある紫外
線硬化型シリコーン−アクリレート系樹脂を使用したこ
とを特徴とするカーボンコート光ファイバ心線。1. A carbon-coated optical fiber core comprising, as a primary coating material, an ultraviolet-curable silicone-acrylate resin having a pulling force measured by a pulling force measurement method in a range of 5 to 50 g / mm. line.