JP2948505B2 - Radio wave absorption wall - Google Patents
Radio wave absorption wallInfo
- Publication number
- JP2948505B2 JP2948505B2 JP16787095A JP16787095A JP2948505B2 JP 2948505 B2 JP2948505 B2 JP 2948505B2 JP 16787095 A JP16787095 A JP 16787095A JP 16787095 A JP16787095 A JP 16787095A JP 2948505 B2 JP2948505 B2 JP 2948505B2
- Authority
- JP
- Japan
- Prior art keywords
- ferrite
- radio wave
- field direction
- plate
- electric field
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、TVゴースト防止等の
建造物の電波反射防止策として、建造物の壁面に用いら
れる建材用の電波吸収壁に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a radio wave absorbing wall for a building material used for a wall surface of a building as a measure for preventing a radio wave reflection of a building such as a TV ghost prevention.
【0002】[0002]
【従来の技術】一般に、フェライトを用いたTVゴース
ト防止用電波吸収壁は、図9及び図10に示す如く、フ
ェライト板を到来電波に対し磁界方向に連続に、電界方
向に一定の間隔を設けて配置しコンクリートを打設した
プレキャスト・カーテンウォール構造で構成されてい
る。すなわち、図9及び図10に示すように、金属反射
メッシュ(電波反射体)をなす鉄筋2の前面にフェライ
ト板1(例えば縦横寸法10cm×10cmのフェライトタ
イル)を磁界方向に連続に、電界方向に不連続となるよ
うに配置し、フェライト板1の落下防止のための特殊足
付き外装タイル3をフェライト板1の前面に被せ、背面
側にコンクリート4を打設した構造となっている。な
お、コンクリート打設の際にフェライト板1が機械振動
で動いて磁界方向に隙間が生じないように、図11の如
くフェライト板1の背面にコンクリート等からなる長尺
のフェライト抑え板5を接着し、コンクリート打設時の
フェライト板1の動きを防止している。2. Description of the Related Art Generally, as shown in FIGS. 9 and 10, a TV ghost preventing radio wave absorbing wall using ferrite is provided so that a ferrite plate is provided continuously with an incoming radio wave in a magnetic field direction and at a constant interval in an electric field direction. It consists of a precast curtain wall structure that is placed and cast concrete. That is, as shown in FIGS. 9 and 10, a ferrite plate 1 (for example, a ferrite tile of 10 cm × 10 cm in length and width) is continuously provided in front of a reinforcing bar 2 forming a metal reflection mesh (radio wave reflector) in a magnetic field direction and in an electric field direction. The ferrite plate 1 is covered with a specially-fitted exterior tile 3 for preventing the ferrite plate 1 from falling, and concrete 4 is cast on the back side. In order to prevent the ferrite plate 1 from moving due to mechanical vibration when concrete is cast and no gap is formed in the direction of the magnetic field, a long ferrite suppressing plate 5 made of concrete or the like is adhered to the back of the ferrite plate 1 as shown in FIG. In addition, the movement of the ferrite plate 1 during concrete casting is prevented.
【0003】この種のフェライトを用いた電波吸収壁の
電波吸収特性は、使用周波数帯におけるフェライトの磁
気損失が主体的に支配し、如何にフェライトのもつ固有
の磁気特性を劣化させることなく実用化するかによって
その電波吸収特性が決定される。このため、この種の電
波吸収壁では、フェライト板は到来電波の磁界方向に連
続化し、フェライト板間の空隙によって生ずる反磁界に
よる特性劣化を防止する必要がある。特にプレキャスト
・カーテンウォール構造においては、コンクリートを打
設する際に、機械振動等によりフェライト板に空隙が生
じ特性を大幅に劣化させる問題がある。その対策とし
て、図9及び図10に示した電波吸収壁では、図11に
示したように、フェライト板1の背面にフェライト抑え
板5を接着し、コンクリート打設時のフェライト板1の
動きを防止し、フェライト板1間の空隙発生を防止した
構造が採用されている。[0003] The electromagnetic wave absorption characteristics of the electromagnetic wave absorbing wall using this type of ferrite are mainly controlled by the magnetic loss of the ferrite in the operating frequency band, and are practically used without deteriorating the inherent magnetic characteristics of the ferrite. The radio wave absorption characteristics are determined depending on whether the operation is performed. For this reason, in this type of radio wave absorbing wall, the ferrite plate needs to be continuous in the direction of the magnetic field of the arriving radio wave, and it is necessary to prevent the characteristic deterioration due to the demagnetizing field caused by the gap between the ferrite plates. In particular, in the precast curtain wall structure, there is a problem in that, when concrete is poured, voids are formed in the ferrite plate due to mechanical vibration or the like, and the characteristics are significantly deteriorated. As a countermeasure, in the radio wave absorbing wall shown in FIGS. 9 and 10, as shown in FIG. 11, a ferrite pressing plate 5 is adhered to the back of the ferrite plate 1 to prevent the movement of the ferrite plate 1 during concrete casting. A structure that prevents the occurrence of a gap between the ferrite plates 1 is adopted.
【0004】他方、電波吸収壁に用いるフェライトの誘
電率はできるだけ小さい方が電波吸収特性の周波数特性
上望ましいが、フェライト自身固有の誘電率が約10あ
り、現状ではこの固有誘電率を基に電波吸収壁が設計さ
れている。図9及び図10に示した電波吸収壁の場合、
到来電波の電界方向からみたフェライト板と該フェライ
ト板間の物質からなるフェライト含有層の実効誘電率
は、フェライトの固有誘電率より低い約7程度の誘電率
を持つコンクリートとの組み合わせとなり、設計上は有
利な方向になりほとんど問題化されていない。On the other hand, the dielectric constant of ferrite used for the radio wave absorbing wall is desirably as small as possible in view of the frequency characteristics of the radio wave absorption characteristics. Absorbing walls are designed. In the case of the radio wave absorbing wall shown in FIGS. 9 and 10,
The effective dielectric constant of the ferrite plate and the ferrite-containing layer made of the material between the ferrite plates viewed from the direction of the electric field of the arriving radio wave is a combination of concrete having a dielectric constant of about 7 lower than the intrinsic dielectric constant of ferrite, and Is in a favorable direction and hardly a problem.
【0005】図9及び図10に示した構造は、現在広く
VHF帯用のTVゴースト対策用電波吸収壁として、建
造物に実用化されている。The structure shown in FIGS. 9 and 10 is currently widely used in buildings as a radio wave absorption wall for TV ghost countermeasures for the VHF band.
【0006】近年、建造物の外壁に対し軽量化、薄型化
の流れとしてカーボン繊維をコンクリートに混入したカ
ーボン繊維強化コンクリート(以下、CFRCと称す
る)の実用化が試みられるようになってきた。当然電波
吸収壁に対してもCFRCを用いたプレキャスト・カー
テンウォール構造の電波吸収壁が要望されている。In recent years, carbon fiber reinforced concrete (hereinafter, referred to as CFRC) in which carbon fiber is mixed into concrete has been tried to be put to practical use as a flow of reducing the weight and thickness of the outer wall of a building. Naturally, there is a demand for a radio wave absorbing wall having a precast curtain wall structure using CFRC.
【0007】しかし、現状では、図9及び図10に示す
様な従来構造での電波吸収壁は電波吸収特性の問題で実
用化されていない。また、実公平6−48951号で提
案されているプレキャスト壁板として、プラスチック
系、ガラス系の繊維を混入したコンクリートを用い電波
吸収壁部分を構成し、これをCFRCで構成されるプレ
キャスト・カーテンウォールと組み合わせ軽量化を計っ
た構成があるが、製造工程が複雑で軽量化の目的は多少
達成されてもコスト的に高価となり、広く実用化される
には至っていない。However, at present, a radio wave absorbing wall having a conventional structure as shown in FIGS. 9 and 10 has not been put into practical use due to a problem of radio wave absorbing characteristics. Also, as a precast wall plate proposed in Japanese Utility Model Publication No. 6-48951, a radio wave absorbing wall portion is formed by using concrete mixed with plastic or glass fibers, and this is a precast curtain wall formed of CFRC. However, there is a configuration in which the weight is reduced in combination with the above, but the manufacturing process is complicated, and even if the purpose of the weight reduction is somewhat achieved, the cost is high and it has not been widely used.
【0008】[0008]
【発明が解決しようとする課題】CFRCはカーボン繊
維をコンクリートに混合したもので、コンクリートの強
度を上げ軽量、薄型化が計られる等、現状は多少コスト
面で課題が有るも高層建造物の建材として、とりわけ外
壁材料として将来期待される建材である。SUMMARY OF THE INVENTION CFRC is a mixture of carbon fiber and concrete, and although it has some problems in terms of cost at present, such as increasing the strength of the concrete and reducing the weight and thickness, it is a building material for high-rise buildings. In particular, it is a building material expected in the future as an outer wall material.
【0009】このCFRCは建築材料としての特性面で
は従来のコンクリートと比較し優れた特性を有する一
方、電気特性面からみると、電気伝導性の良いカーボン
を混合することによりコンクリートの誘電率を大幅に増
加させ高誘電率材料となる。図12にカーボン添加量に
対するコンクリートの誘電率変化特性を示す(複素誘電
率で示す。)。カーボン混入量わずか1vol%でもコン
クリートの誘電率は約2倍になり現在CFRCとして強
度等から最適混合量とされる2〜3vol%のカーボン量
では40〜100程度の誘電率となる。[0009] This CFRC has excellent properties as a building material compared to conventional concrete, but from the electrical properties side, the dielectric constant of concrete is greatly increased by mixing carbon with good electrical conductivity. To a high dielectric constant material. FIG. 12 shows the dielectric constant change characteristics of concrete with respect to the amount of carbon added (indicated by complex dielectric constant). Even if the carbon content is only 1 vol%, the dielectric constant of concrete is about double, and the carbon content of 2 to 3 vol%, which is currently the optimum mixing amount from the strength and the like as CFRC, is about 40 to 100.
【0010】図9及び図10の電波吸収壁のコンクリー
ト部分をこのCFRCで構成する場合、CFRCの誘電
率が大きな問題となる。図13に電波吸収壁のコンクリ
ート部分の誘電率を変化させたときの電波吸収特性を示
す。普通コンクリートの誘電率約7に近い誘電率、例え
ば5〜10では200MHzで反射減衰量(電波吸収
量)約20dBに対し、誘電率40では10dB程度ま
で大幅に劣化する。このことが現在CFRCだけで電波
吸収壁のコンクリート部分を構成できない理由である。When the concrete part of the radio wave absorbing wall shown in FIGS. 9 and 10 is made of the CFRC, the dielectric constant of the CFRC becomes a serious problem. FIG. 13 shows the radio wave absorption characteristics when the dielectric constant of the concrete portion of the radio wave absorption wall is changed. A dielectric constant close to about 7 of ordinary concrete, for example, a return loss (radiation absorption) of about 20 dB at 200 MHz for 5 to 10 and a deterioration of about 10 dB for a dielectric constant of 40 at 200 MHz. This is the reason why the concrete part of the radio wave absorption wall cannot be formed by CFRC alone.
【0011】本発明は、従来製造技術を用いてコンクリ
ート部分をCFRC等の繊維強化コンクリートで構成
し、プレキャスト・カーテンウォール構造に適した電波
吸収壁を提供しようとするものであり、その課題は(1)
複合誘電体の考え方で到来電波の電界方向からみたフェ
ライト板と該フェライト板間の物質からなるフェライト
含有層の実効誘電率を下げること、(2)現状一般のコン
クリートを用いたプレキャスト・カーテンウォール電波
吸収壁構造から前記フェライト含有層の実効誘電率低減
の可能性を見いだすことである。An object of the present invention is to provide a radio wave absorbing wall suitable for a precast curtain wall structure by using a conventional manufacturing technique to construct a concrete portion with fiber reinforced concrete such as CFRC. 1)
To reduce the effective dielectric constant of the ferrite plate and the ferrite-containing layer made of the material between the ferrite plates as viewed from the direction of the electric field of the arriving radio wave based on the concept of a composite dielectric, (2) Precast curtain wall radio waves using ordinary concrete at present It is to find a possibility of reducing the effective dielectric constant of the ferrite-containing layer from the absorption wall structure.
【0012】本発明の第1の目的は、CFRC等の高誘
電率の繊維強化コンクリートを用いた場合でも普通コン
クリートの場合と同等の電波吸収特性を実現可能で、軽
量化、薄型化に適した電波吸収壁を提供することにあ
る。A first object of the present invention is to realize a radio wave absorption characteristic equivalent to that of ordinary concrete even when using fiber reinforced concrete having a high dielectric constant such as CFRC, which is suitable for weight reduction and thickness reduction. To provide a radio wave absorbing wall.
【0013】本発明の第2の目的は、CFRC等の高誘
電率の繊維強化コンクリートを用いた場合でも普通コン
クリートの場合と同様の製造技術を用いて製造可能で、
構造の複雑化を招くことのない電波吸収壁を提供するこ
とにある。A second object of the present invention is that even when fiber reinforced concrete having a high dielectric constant such as CFRC is used, it can be manufactured using the same manufacturing technology as that for ordinary concrete.
An object of the present invention is to provide a radio wave absorbing wall which does not cause a complicated structure.
【0014】本発明のその他の目的や新規な特徴は後述
の実施例において明らかにする。Other objects and novel features of the present invention will be clarified in the embodiments described later.
【0015】[0015]
【課題を解決するための手段】上記目的を達成するため
に、本発明の電波吸収壁は、到来電波の磁界方向に連
続、かつ電界方向に不連続にフェライト板を配置し、繊
維強化材を混入した繊維強化コンクリートに前記フェラ
イト板を固定してなる構成において、前記フェライト板
を前記磁界方向に連続した状態に保持する低誘電率材料
のフェライト抑え部材を前記フェライト板に接着し、か
つ当該フェライト抑え部材の少なくとも一部を前記フェ
ライト板間の電界方向間隙部分に位置させている。In order to achieve the above object, a radio wave absorbing wall according to the present invention comprises a ferrite plate which is arranged continuously in a magnetic field direction of an incoming radio wave and discontinuously in an electric field direction, and is provided with a fiber reinforced material. In a configuration in which the ferrite plate is fixed to the mixed fiber-reinforced concrete, a ferrite suppressing member made of a low dielectric constant material for holding the ferrite plate in a continuous state in the magnetic field direction is bonded to the ferrite plate, and At least a part of the suppressing member is located in a gap in the electric field direction between the ferrite plates.
【0016】また、前記フェライト抑え部材が前記フェ
ライト板の背面及び前記電界方向間隙部分に臨む側面に
対接する構成としてもよい。Further, the ferrite suppressing member may be configured to be in contact with a back surface of the ferrite plate and a side surface facing the gap portion in the electric field direction.
【0017】さらに、前記フェライト抑え部材が前記フ
ェライト板の前面を覆う外装材を兼ねるものであっても
よい。Further, the ferrite suppressing member may also serve as an exterior material covering a front surface of the ferrite plate.
【0018】[0018]
【作用】現状の普通コンクリートを用いたプレキャスト
・カーテンウォール構造の電波吸収壁において、コンク
リート打設時にフェライト板(フェライトタイル)の入
射電波磁界方向での連続性を保つ目的でフェライト板背
面がコンクリート等からなる抑え板で固定されているこ
とに着目し、さらにフェライト板の見かけの誘電率は入
射電波電界方向での特性であり、フェライト板とフェラ
イト板間の電界方向間隙部分に入り込んだコンクリート
等との組合わされた複合的材料としての特性として与え
られることに着目した。すなわち、フェライト板と該フ
ェライト板間のコンクリート等の物質からなるフェライ
ト含有層の実効誘電率は、普通コンクリートを用いた場
合、普通コンクリートの誘電率が7〜10であり、フェ
ライト板の誘電率が約10であることから、電波吸収壁
としての実効誘電率は8〜9程度となり、フェライト電
波吸収体設計条件が成立ち、フェライト単体と同等の特
性が得られていることに着目した。[Function] In the current wave absorbing wall of the precast curtain wall structure using ordinary concrete, the back surface of the ferrite plate (concrete) is used to maintain the continuity of the ferrite plate (ferrite tile) in the direction of the incident electromagnetic field when casting concrete. Note that the apparent permittivity of the ferrite plate is a characteristic in the direction of the electric field of the incident radio wave, and the apparent permittivity of the ferrite plate is the same as that of concrete that has entered the gap between the ferrite plate and the ferrite plate in the direction of the electric field. It is noted that it is given as a property as a combined composite material. That is, the effective dielectric constant of the ferrite plate and the ferrite-containing layer made of a substance such as concrete between the ferrite plates is such that when ordinary concrete is used, the dielectric constant of ordinary concrete is 7 to 10, and the dielectric constant of the ferrite plate is Since it is about 10, the effective permittivity as a radio wave absorbing wall is about 8 to 9, and the design conditions of the ferrite radio wave absorber are satisfied, and attention is paid to the fact that the same characteristics as the ferrite alone are obtained.
【0019】本発明はこの2つの条件を同時に満足させ
るもので、CFRC等の高誘電率の繊維強化コンクリー
トを用いた電波吸収壁でも普通コンクリートを用いた電
波吸収壁と同等の電波吸収特性を得ようとするものであ
る。The present invention satisfies these two conditions at the same time, and a radio wave absorbing wall using fiber reinforced concrete having a high dielectric constant such as CFRC can obtain radio wave absorbing characteristics equivalent to those of a radio wave absorbing wall using ordinary concrete. It is to try.
【0020】フェライト板を到来電波の磁界方向に連続
に、電界方向に間隙を設けて配列したTVゴースト対策
用電波吸収壁において、電波吸収壁設計上問題となるの
は電界方向からみたフェライト板の見かけの誘電率であ
る。この誘電率をほぼフェライト板の誘電率と同等にす
ることが必要条件であり、この条件を満足させるために
は複合材料の取り扱いにより、フェライト板間に充填さ
れたコンクリート等の物質とフェライト板からなるフェ
ライト含有層の実効誘電率をほぼ10程度に抑える必要
がある。このため、(1)フェライト板間の間隙に10程
度の誘電率特性を持った材料を充填する、(2)一部空気
層を設ける、等のことが考えられる。In a radio wave absorbing wall for TV ghost countermeasures in which a ferrite plate is arranged continuously in a magnetic field direction of an incoming radio wave and a gap is provided in an electric field direction, a problem in designing a radio wave absorbing wall is that the ferrite plate is viewed from the electric field direction. The apparent permittivity. It is a necessary condition that this dielectric constant be approximately equal to the dielectric constant of the ferrite plate, and in order to satisfy this condition, by handling the composite material, the material such as concrete filled between the ferrite plates and the ferrite plate It is necessary to suppress the effective dielectric constant of the ferrite-containing layer to about 10. For this reason, it is conceivable to (1) fill a gap between ferrite plates with a material having a dielectric constant of about 10, or (2) provide a partial air layer.
【0021】このどちらの構成においても、高層建造物
の外壁材として用いられる電波吸収壁としては、電波吸
収特性もさることながら、まず建材としての性能条件を
満足させることが第一である。このためには従来のプレ
キャスト・カーテンウォールの製造方法では困難で、例
えば、(1)の場合は電波吸収体部分を予め作りこれを外
壁材を作るとき一体化させる等、複雑な製造工程が求め
られ、製造方法においても、コスト的にも課題が多すぎ
る。(2)の場合は建材としての特性をどう確保するか、
構造的検討を含めやはり大きな課題が残されている。In either of these configurations, the radio wave absorbing wall used as the outer wall material of the high-rise building must first satisfy the performance conditions as a building material, in addition to the radio wave absorbing property. This is difficult with the conventional method of manufacturing a precast curtain wall.For example, in the case of (1), a complicated manufacturing process is required, such as preparing a radio wave absorber in advance and integrating it when making an outer wall material. However, there are too many problems in the manufacturing method and the cost. In the case of (2), how to secure the characteristics as a building material,
There are still significant issues, including structural considerations.
【0022】従って、フェライト板の見かけの誘電率を
調整する構造としては、現状の電波吸収壁構造を構成す
る部材の一部を利用しCFRC等の高誘電率の繊維強化
コンクリートとの共存のなかで誘電率を調整することが
望まれる。Therefore, as a structure for adjusting the apparent dielectric constant of the ferrite plate, a part of the members constituting the current electromagnetic wave absorbing wall structure is used and coexists with fiber-reinforced concrete having a high dielectric constant such as CFRC. It is desired that the dielectric constant be adjusted by the above method.
【0023】本発明は、現状では図11のようにフェラ
イト板背面に配設されているフェライト抑え板に着目
し、このフェライト抑え板と同様の機能を持つフェライ
ト抑え部材の少なくとも一部が電界方向のフェライト板
間の間隙部分に位置するようにフェライト板に取り付
け、かつフェライト抑え部材の材質も低誘電率の例えば
発泡コンクリート、軽量コンクリート等を用い、抑え板
としての作用と同時にフェライト板間の誘電率を制御す
る役割をも持たせるものである。At present, the present invention focuses on a ferrite holding plate provided on the back of the ferrite plate as shown in FIG. 11, and at least a part of the ferrite holding member having the same function as the ferrite holding plate is provided in the electric field direction. The ferrite plate is attached to the ferrite plate so that it is located in the gap between the ferrite plates, and the material of the ferrite suppressor is low dielectric constant, such as foamed concrete or lightweight concrete. It also has the role of controlling the rate.
【0024】このような構成であれば、従来の製造方法
で製作可能であり、コスト的にも、建材としての性能に
おいても従来と同等以上のものが得られる。With such a configuration, it can be manufactured by a conventional manufacturing method, and a cost and a performance as a building material which are equal to or higher than the conventional one can be obtained.
【0025】[0025]
【実施例】以下、本発明に係る電波吸収壁の実施例を図
面に従って説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the radio wave absorbing wall according to the present invention will be described below with reference to the drawings.
【0026】図1は本発明の第1実施例であって、プレ
キャスト・コンクリート一体型電波吸収壁の平断面図で
あり、図2はフェライト板をフェライト抑え部材で抑え
る構造部分の斜視図である。これらの図において、フェ
ライト板1は、例えば10cm×10cmの方形で厚みは9
mmのフェライト・タイル形状のものであり、各フェライ
ト板1が到来電波の磁界方向に連続した状態に保持され
るように、図2の如く各フェライト板1の両側に発泡コ
ンクリート、軽量コンクリート等で形成されたの低誘電
率材料の断面略L字状フェライト抑え部材10が接着固
定されている。すなわち、フェライト抑え部材10はフ
ェライト板1に比して長尺であって、磁界方向に連続配
置された各フェライト板1の背面及び到来電波の電界方
向に形成された隣り合うフェライト板同士の電界方向間
隙部分に臨む(対面する)側面に対接状態で固着されて
いる。図2のように、到来電波の磁界方向に連続するよ
うにフェライト抑え部材10で保持され、かつ電界方向
に所要の間隔をおいて配列された各フェライト板1、及
びフェライト抑え部材10の背後にはCFRC11が打
設され、打設されたCFRC11の背面には、金属板、
金属メッシュ、鉄筋等の電波反射体12が配設(一体
化)されている。なお、CFRC11の一部はフェライ
ト抑え部材10同士の隙間にも充填されている。FIG. 1 is a plan view of a first embodiment of the present invention, in which a radio wave absorbing wall integrated with precast concrete is shown, and FIG. 2 is a perspective view of a structure for suppressing a ferrite plate with a ferrite suppressing member. . In these figures, the ferrite plate 1 has a square shape of, for example, 10 cm × 10 cm and a thickness of 9 mm.
mm ferrite tiles, foamed concrete, lightweight concrete, etc., on both sides of each ferrite plate 1 as shown in FIG. 2 so that each ferrite plate 1 is maintained in a continuous state in the magnetic field direction of the incoming radio wave. The formed ferrite suppressing member 10 having a substantially L-shaped cross section made of a low dielectric constant material is adhered and fixed. That is, the ferrite suppressing member 10 is longer than the ferrite plate 1 and the electric field between adjacent ferrite plates formed in the back surface of each ferrite plate 1 continuously arranged in the magnetic field direction and the electric field direction of the incoming radio wave. It is fixed in contact with the side face (facing) facing the gap in the direction. As shown in FIG. 2, each ferrite plate 1 is held by the ferrite suppressing member 10 so as to be continuous in the magnetic field direction of the arriving radio wave and arranged at a required interval in the direction of the electric field, and behind the ferrite suppressing member 10. CFRC11 is cast, and a metal plate,
A radio wave reflector 12 such as a metal mesh or a reinforcing bar is provided (integrated). Note that a part of the CFRC 11 is also filled in the gap between the ferrite suppressing members 10.
【0027】本実施例では、例えばフェライト板1の電
界方向の長さを10cm、フェライト板1の側面に位置す
るフェライト抑え部材10の電界方向の厚みを2cm、隣
り合うフェライト抑え部材10間に充填されたCFRC
11の電界方向の厚みを2cmとした(隣り合うフェライ
ト板間の隙間は6cm)。In this embodiment, for example, the length of the ferrite plate 1 in the electric field direction is 10 cm, the thickness of the ferrite suppressing member 10 located on the side surface of the ferrite plate 1 in the electric field direction is 2 cm, and the space between the adjacent ferrite suppressing members 10 is filled. CFRC
11 was 2 cm in the electric field direction (a gap between adjacent ferrite plates was 6 cm).
【0028】この第1実施例の場合、フェライト板1を
磁界方向に連続した状態に保持する低誘電率材料のフェ
ライト抑え部材10が隣り合うフェライト板同士の電界
方向間隙部分に延在しているので、電界方向からみたフ
ェライト板と該フェライト板間の物質からなるフェライ
ト含有層を想定したとき、該フェライト含有層の実効誘
電率はフェライト板同士の電界方向間隙部分が全てCF
RC11で充たされている場合に比べて相当低くなる。
例えば、10cmのフェライト板同士の電界方向間隙部分
が、フェライト抑え部材の一部である2cmの発泡コンク
リート(誘電率約4)と、2cmのCFRC(誘電率約4
0)と、フェライト抑え部材の一部である2cmの発泡コ
ンクリートとから構成されている場合、前記フェライト
含有層の実効誘電率はそれらの混合材料としての値を示
し、約9である。In the case of the first embodiment, the ferrite suppressing member 10 made of a low dielectric constant material for holding the ferrite plate 1 continuously in the direction of the magnetic field extends in the gap between the adjacent ferrite plates in the electric field direction. Therefore, assuming a ferrite plate and a ferrite-containing layer made of a material between the ferrite plates viewed from the direction of the electric field, the effective dielectric constant of the ferrite-containing layer is such that the gap in the electric field direction between the ferrite plates is CF.
It is considerably lower than the case where it is filled with RC11.
For example, the gap between the ferrite plates of 10 cm in the electric field direction is a part of the ferrite suppressing member, 2 cm of foamed concrete (dielectric constant of about 4) and 2 cm of CFRC (dielectric constant of about 4).
0) and a 2 cm foamed concrete that is a part of the ferrite suppressing member, the effective dielectric constant of the ferrite-containing layer is about 9 as a value as a mixed material thereof.
【0029】この第1実施例によれば、次の通りの効果
を得ることができる。According to the first embodiment, the following effects can be obtained.
【0030】(1) 隣り合うフェライト板同士の電界方
向間隙部分に、フェライト板1を磁界方向に連続状態に
保持するための低誘電率のフェライト抑え部材10が延
在するようにしており、前記電界方向間隙部分の全てに
CFRC11が充填されている場合に比べて、電界方向
からみたフェライト板と該フェライト板間の物質からな
るフェライト含有層の実効誘電率を相当低くし、実効誘
電率10以下を実現できる。この結果、高誘電率のCF
RC11で打設したプレキャスト・コンクリート一体型
の電波吸収壁であるのにもかかわらず、普通コンクリー
トで打設したものと同等の電波吸収特性とすることがで
きる。(1) A ferrite suppressing member 10 having a low dielectric constant for holding the ferrite plate 1 in a continuous state in a magnetic field direction extends in a gap between the adjacent ferrite plates in the electric field direction. The effective permittivity of the ferrite plate and the ferrite-containing layer made of a material between the ferrite plates is considerably reduced as viewed from the direction of the electric field, and the effective permittivity is 10 or less, as compared with the case where the entire gap portion in the electric field direction is filled with CFRC11. Can be realized. As a result, a high dielectric constant CF
Despite being a precast / concrete integrated radio wave absorbing wall cast with RC11, it can have the same radio wave absorption characteristics as those cast with ordinary concrete.
【0031】(2) 従来の普通コンクリートを打設した
プレキャスト・コンクリート一体型の電波吸収壁におい
ても使用しているフェライト抑え板と同様の機能を持つ
フェライト抑え部材10を用いればよく、従来のプレキ
ャスト・コンクリート一体型の電波吸収壁の製造技術を
用いることができ、製造工程の複雑化や、構造の複雑化
を招くことがなく、CFRCの特長を生かした軽量、薄
型の電波吸収壁が得られる。(2) A ferrite holding member 10 having the same function as the ferrite holding plate used in the conventional radio wave absorbing wall of the precast / concrete integrated type in which ordinary concrete is cast may be used.・ A technology for manufacturing a radio wave absorbing wall integrated with concrete can be used, and a lightweight and thin radio wave absorbing wall utilizing the features of CFRC can be obtained without complicating the manufacturing process and the structure. .
【0032】(3) フェライト抑え部材10がフェライ
ト板1の背面及びフェライト板間の電界方向間隙部分に
臨む側面に対接するように断面略L字状であり、フェラ
イト板1の接着固定を確実に実行できる。(3) The ferrite suppressing member 10 has a substantially L-shaped cross section so as to be in contact with the rear surface of the ferrite plate 1 and the side surface facing the gap in the electric field direction between the ferrite plates 1. I can do it.
【0033】図3は本発明の第2実施例であって、フェ
ライト板1の落下防止を兼ねた外装材としてシヤーコネ
クタ付き外装タイル(磁器タイル等)を用いたプレキャ
スト・カーテンウォール電波吸収壁の平断面図である。
この場合、金属反射メッシュ(電波反射体)をなす鉄筋
22の前面にフェライト板1を到来電波の磁界方向に連
続に、電界方向に不連続となるように配置し、シヤーコ
ネクタ付き外装タイル23をフェライト板1の前面に被
せている。ここで、シヤーコネクタ付き外装タイル23
は外装タイル本体の両端部に金属等のシヤーコネクタ2
3aを差し込む等して一体化したものであり、シヤーコ
ネクタ23aは外装タイル23の背後方向に延長してい
る。外装タイル23の電界方向の寸法は、フェライト板
1の電界方向の寸法よりも十分長く、フェライト板1の
両端に残った部分に発泡コンクリート、軽量コンクリー
ト等で形成された低誘電率材料の断面略L字状フェライ
ト抑え部材20が配置され、フェライト板1の背面及び
電界方向間隙部分に臨む側面に接着固定されている。フ
ェライト抑え部材20はフェライト板1よりも十分長尺
であり、CFRC打設時にフェライト板1が機械振動等
で動いて磁界方向に隙間が生じるのを防止する。そし
て、フェライト板1、シヤーコネクタ付き外装タイル2
3及びフェライト抑え部材20の背面側にCFRC11
を打設することで、フェライト板1、シヤーコネクタ付
き外装タイル23、フェライト抑え部材20及び鉄筋2
2を一体化している。その際、シヤーコネクタ23aが
CFRC11中に埋没して外装タイル23の落下を防止
している。なお、CFRC11の一部はフェライト抑え
部材20同士の隙間及びシヤーコネクタ付き外装タイル
23の隙間にも充填されている。FIG. 3 shows a second embodiment of the present invention, in which a precast curtain wall radio wave absorption wall using an exterior tile (such as a porcelain tile) with a shear connector as an exterior material also serving to prevent the ferrite plate 1 from dropping. It is a plane sectional view.
In this case, the ferrite plate 1 is disposed on the front surface of the reinforcing bar 22 forming a metal reflection mesh (radio wave reflector) so as to be continuous in the magnetic field direction of the incoming radio wave and discontinuous in the electric field direction. It covers the front surface of the ferrite plate 1. Here, the exterior tile 23 with the shear connector
Is a shear connector 2 made of metal or the like at both ends of the exterior tile body.
The shear connector 23a extends in the rear direction of the exterior tile 23. The dimension of the exterior tile 23 in the direction of the electric field is sufficiently longer than the dimension of the ferrite plate 1 in the direction of the electric field. An L-shaped ferrite suppressing member 20 is arranged and bonded and fixed to the back surface of the ferrite plate 1 and the side surface facing the gap portion in the electric field direction. The ferrite suppressing member 20 is sufficiently longer than the ferrite plate 1 and prevents the ferrite plate 1 from moving due to mechanical vibration or the like at the time of driving the CFRC, so that a gap is generated in the magnetic field direction. And a ferrite plate 1, an exterior tile 2 with a shear connector
3 and CFRC11 on the back side of the ferrite suppressing member 20.
By installing a ferrite plate 1, an exterior tile 23 with a shear connector, a ferrite suppressing member 20, and a reinforcing bar 2
2 are integrated. At this time, the shear connector 23a is buried in the CFRC 11 to prevent the exterior tile 23 from dropping. Note that a part of the CFRC 11 is also filled in the gap between the ferrite suppressing members 20 and the gap between the exterior tiles 23 with the shear connector.
【0034】本実施例では、例えばフェライト板1の電
界方向の長さを10cm、フェライト板1の側面に位置す
るフェライト抑え部材20の電界方向の厚みを2cm、隣
り合うフェライト抑え部材20間に充填されたCFRC
11の電界方向の厚みを2cmとた(隣り合うフェライト
板間の隙間は6cm)。In this embodiment, for example, the length of the ferrite plate 1 in the electric field direction is 10 cm, the thickness of the ferrite suppressing member 20 located on the side surface of the ferrite plate 1 in the electric field direction is 2 cm, and the space between the adjacent ferrite suppressing members 20 is filled. CFRC
11 was 2 cm in the electric field direction (the gap between adjacent ferrite plates was 6 cm).
【0035】図4は、本発明の第2実施例において、1
0cmのフェライト板同士の電界方向間隙部分が、フェラ
イト抑え部材の一部である2cmの発泡コンクリート(誘
電率約4)と、2cmのCFRC(誘電率約40)と、フ
ェライト抑え部材の一部である2cmの発泡コンクリート
とから構成されている場合の電波吸収特性を示す。この
図から、前記電界方向間隙部分の全てにCFRCが充填
されている場合(図13グラフ中の誘電率40の曲線参
照)よりも大幅に改善されていることが判る。FIG. 4 shows a second embodiment of the present invention.
The gap between the 0 cm ferrite plates in the direction of the electric field is 2 cm foamed concrete (dielectric constant about 4), 2 cm CFRC (dielectric constant about 40), which is a part of the ferrite suppressing member, and a part of the ferrite suppressing member. 5 shows the radio wave absorption characteristics in the case of being composed of a certain 2 cm foam concrete. From this figure, it can be seen that it is much improved compared to the case where the entire electric field direction gap is filled with CFRC (see the curve of the dielectric constant 40 in the graph of FIG. 13).
【0036】この第2実施例の場合、外装タイル23を
シヤーコネクタ23aで確実にCFRC11側に固定す
ることでフェライト板1及び外装タイル23の落下を防
止でき、建材としての要求特性と電波吸収特性の両者を
満足するプレキャスト・カーテンウォール電波吸収壁が
得られ、CFRCを用いることで軽量化、薄型化を図る
ことが可能になる。In the case of the second embodiment, since the exterior tile 23 is securely fixed to the CFRC 11 side by the shear connector 23a, the ferrite plate 1 and the exterior tile 23 can be prevented from dropping. Thus, a precast curtain wall radio wave absorption wall satisfying both of the above conditions can be obtained, and the weight and thickness can be reduced by using CFRC.
【0037】図5は本発明の第3実施例であって、フェ
ライト板1の落下防止を兼ねた外装材としてシヤーコネ
クタ付き外装タイル(磁器タイル等)を用いたプレキャ
スト・カーテンウォール電波吸収壁の平断面図である。
この場合、金属反射メッシュ(電波反射体)をなす鉄筋
22の前面にフェライト板1を到来電波の磁界方向に連
続に、電界方向に不連続となるように配置し、シヤーコ
ネクタ付き外装タイル33をフェライト板1の前面に被
せている。ここで、シヤーコネクタ付き外装タイル33
は外装タイル本体の中間部に金属等のシヤーコネクタ3
3aを差し込む等して一体化したものであり、シヤーコ
ネクタ33aは外装タイル33の背後方向に延長してい
る。外装タイル33の電界方向の寸法は、フェライト板
1の電界方向の寸法よりも十分長く、外装タイル33を
目地充填用隙間を残して近接配置したとき、フェライト
板間の電界方向間隙部分が数cm(例えばフェライト板1
の電界方向の長さが10cmのとき電界方向間隙部分が6
cm)残るようにしている。そして、シヤーコネクタ33
aが電界方向間隙部分を通過して後方に延長するように
フェライト板1とシヤーコネクタ付き外装タイル33の
位置関係を設定する。さらに、磁界方向に連続した各フ
ェライト板1の背面及び電界方向間隙部分に臨む両側面
に対接するように発泡コンクリート、軽量コンクリート
等で形成された低誘電率材料の断面コ字状フェライト抑
え部材30が配置され、各フェライト板1の背面及び両
側面に接着固定されている。フェライト抑え部材30は
フェライト板1よりも十分長尺であり、CFRC打設時
にフェライト板1が機械振動等で動いて磁界方向に隙間
が生じるのを防止する。そして、フェライト板1、シヤ
ーコネクタ付き外装タイル33及びフェライト抑え部材
30の背面側にCFRC11を打設することで、フェラ
イト板1、シヤーコネクタ付き外装タイル33、フェラ
イト抑え部材30及び鉄筋22を一体化している。その
際、シヤーコネクタ33aがCFRC11中に埋没して
外装タイル33の落下を防止している。なお、フェライ
ト板1の前面を覆う外装タイル33間の隙間にはタイル
目地材34を充填する。FIG. 5 shows a third embodiment of the present invention, in which a precast curtain wall radio-absorbing wall using an exterior tile (such as a porcelain tile) with a shear connector as an exterior material also serving to prevent the ferrite plate 1 from dropping. It is a plane sectional view.
In this case, the ferrite plate 1 is arranged on the front surface of the reinforcing bar 22 forming a metal reflection mesh (radio wave reflector) so as to be continuous in the magnetic field direction of the incoming radio wave and discontinuous in the electric field direction. It covers the front surface of the ferrite plate 1. Here, the exterior tile 33 with the shear connector
Is a shear connector 3 made of metal or the like in the middle of the exterior tile body
The shear connector 33a extends in the rear direction of the exterior tile 33. The dimension of the exterior tile 33 in the electric field direction is sufficiently longer than the dimension of the ferrite plate 1 in the electric field direction. When the exterior tile 33 is disposed close to the joint filling gap, the gap in the electric field direction between the ferrite plates is several cm. (For example, ferrite plate 1
When the length in the electric field direction is 10 cm, the gap in the electric field direction is 6
cm) to keep it. And the shear connector 33
The positional relationship between the ferrite plate 1 and the exterior tile 33 with a shear connector is set so that a passes through the gap in the electric field direction and extends rearward. Further, a U-shaped ferrite suppressing member 30 made of a low dielectric constant material made of foam concrete, lightweight concrete or the like so as to be in contact with the back surface of each ferrite plate 1 continuous in the magnetic field direction and both side surfaces facing the gap portion in the electric field direction. Are fixed to the back surface and both side surfaces of each ferrite plate 1 by bonding. The ferrite suppressing member 30 is sufficiently longer than the ferrite plate 1, and prevents the ferrite plate 1 from moving due to mechanical vibration or the like at the time of driving the CFRC to form a gap in the magnetic field direction. Then, the ferrite plate 1, the exterior tile 33 with the shear connector, the ferrite suppression member 30, and the reinforcing bar 22 are integrated by placing the CFRC 11 on the back side of the ferrite plate 1, the exterior tile 33 with the shear connector, and the ferrite suppression member 30. ing. At this time, the shear connector 33a is buried in the CFRC 11 to prevent the exterior tile 33 from falling. The gap between the exterior tiles 33 covering the front surface of the ferrite plate 1 is filled with a tile joint material 34.
【0038】この第3実施例によっても前述の第2実施
例と同様の効果を得ることができる。但し、外装タイル
33の落下を防止するためのシヤーコネクタ33aの個
数は第2実施例よりも少なくて済む。According to the third embodiment, the same effect as that of the second embodiment can be obtained. However, the number of shear connectors 33a for preventing the exterior tiles 33 from falling can be smaller than in the second embodiment.
【0039】図6は本発明の第4実施例であって、フェ
ライト板1の落下防止を兼ねた外装材としてシヤーコネ
クタ付き外装タイル(磁器タイル等)を用いたプレキャ
スト・カーテンウォール電波吸収壁の平断面図である。
この場合、フェライト板1、鉄筋22、シヤーコネクタ
付き外装タイル33の配置は前述の第3実施例とほぼ同
様であるが、フェライト抑え部材の形状及び配置が異な
っている。すなわち、第4実施例で用いるフェライト抑
え部材40は発泡コンクリート、軽量コンクリート等の
低誘電率材料で断面略L字状に形成した長尺部材であ
り、フェライト板1の片側のみに取り付けられ、フェラ
イト板1の一端部の背面及び電界方向間隙部分に臨む側
面に接着固定されている。なお、その他の構成は前述の
第3実施例と同様である。FIG. 6 shows a fourth embodiment of the present invention, in which a precast curtain wall radio wave absorbing wall using an exterior tile (such as a porcelain tile) with a shear connector as an exterior material also serving to prevent the ferrite plate 1 from falling. It is a plane sectional view.
In this case, the arrangement of the ferrite plate 1, the reinforcing bar 22, and the exterior tile 33 with the shear connector is almost the same as that of the third embodiment, but the shape and arrangement of the ferrite suppressing member are different. That is, the ferrite suppressing member 40 used in the fourth embodiment is a long member formed of a low dielectric constant material such as foamed concrete or lightweight concrete and having a substantially L-shaped cross section, and is attached to only one side of the ferrite plate 1. It is adhesively fixed to the back surface of one end of the plate 1 and the side surface facing the gap portion in the electric field direction. The other configuration is the same as that of the third embodiment.
【0040】この第4実施例の場合、前述の第3実施例
に比べてフェライト抑え部材40の作製が容易な利点が
ある。その他の効果は第3実施例と同様である。なお、
電波吸収特性を改善するためにはフェライト抑え部材4
0の電界方向間隙部分に延在する部分の肉厚を大きくす
ることが望ましい。The fourth embodiment has an advantage that the ferrite suppressing member 40 can be easily manufactured as compared with the third embodiment. Other effects are the same as those of the third embodiment. In addition,
Ferrite suppressor 4 to improve radio wave absorption characteristics
It is desirable to increase the thickness of the portion extending to the zero electric field direction gap.
【0041】図7は本発明の第5実施例であって、フェ
ライト板1の落下防止を兼ねた外装材として足付き外装
タイル(磁器タイル等)を用いたプレキャスト・カーテ
ンウォール電波吸収壁の平断面図である。この場合、金
属反射メッシュ(電波反射体)をなす鉄筋22の前面に
フェライト板1を到来電波の磁界方向に連続に、電界方
向に不連続となるように配置し、足付き外装タイル53
をフェライト板1の前面に被せている。ここで、足付き
外装タイル53は外装タイル本体の中間部に背後に延長
する足53aを一体に形成したものである。外装タイル
53の電界方向の寸法は、フェライト板1の電界方向の
寸法よりも十分長く、外装タイル53を目地充填用隙間
を残して近接配置したとき、フェライト板間の電界方向
間隙部分が数cm(例えばフェライト板1の電界方向の長
さが10cmのとき電界方向間隙部分が6cm)残るように
している。そして、足53aが電界方向間隙部分を通過
して後方に延長するようにフェライト板1と足付き外装
タイル53の位置関係を設定する。さらに、磁界方向に
連続した各フェライト板1の両端部の背面及び電界方向
間隙部分に臨む側面に対接するように発泡コンクリー
ト、軽量コンクリート等で形成された低誘電率材料の断
面L字状フェライト抑え部材50が配置され、各フェラ
イト板1の背面及び側面に接着固定されている。フェラ
イト抑え部材50はフェライト板1よりも十分長尺であ
り、CFRC打設時にフェライト板1が機械振動等で動
いて磁界方向に隙間が生じるのを防止する。そして、フ
ェライト板1、足付き外装タイル53及びフェライト抑
え部材50の背面側にCFRC11を打設することで、
フェライト板1、足付き外装タイル53、フェライト抑
え部材50及び鉄筋22を一体化している。その際、足
53aがCFRC11中に埋没して外装タイル53の落
下を防止している。なお、フェライト板1の前面を覆う
外装タイル53間の隙間にはタイル目地材34を充填す
る。FIG. 7 shows a fifth embodiment of the present invention, in which a flat cast electromagnetic wave absorbing wall using an exterior tile with a foot (such as a porcelain tile) as an exterior material which also serves to prevent the ferrite plate 1 from dropping. It is sectional drawing. In this case, the ferrite plate 1 is arranged on the front surface of the reinforcing bar 22 forming a metal reflection mesh (radio wave reflector) so as to be continuous in the magnetic field direction of the arriving radio wave and discontinuous in the electric field direction.
On the front surface of the ferrite plate 1. Here, the exterior tile 53 with a foot is formed by integrally forming a foot 53a extending rearward at an intermediate portion of the exterior tile main body. The dimension of the exterior tile 53 in the electric field direction is sufficiently longer than the dimension of the ferrite plate 1 in the electric field direction. When the exterior tile 53 is arranged close to the joint filling gap, the gap in the electric field direction between the ferrite plates is several cm. (For example, when the length of the ferrite plate 1 in the electric field direction is 10 cm, the gap in the electric field direction is 6 cm). Then, the positional relationship between the ferrite plate 1 and the exterior tile 53 with feet is set such that the feet 53a extend rearward through the gaps in the electric field direction. Further, an L-shaped ferrite of low dielectric constant material made of foamed concrete, lightweight concrete, or the like is held so as to be in contact with the back surface of both ends of each ferrite plate 1 continuous in the magnetic field direction and the side surface facing the gap portion in the electric field direction. A member 50 is arranged and fixed to the back and side surfaces of each ferrite plate 1 by bonding. The ferrite suppressing member 50 is sufficiently longer than the ferrite plate 1 and prevents the ferrite plate 1 from moving due to mechanical vibration or the like at the time of driving the CFRC, thereby preventing a gap in the magnetic field direction. Then, the CFRC 11 is cast on the back side of the ferrite plate 1, the exterior tile 53 with feet, and the ferrite suppressing member 50,
The ferrite plate 1, the exterior tile 53 with feet, the ferrite suppressing member 50, and the reinforcing bar 22 are integrated. At this time, the foot 53a is buried in the CFRC 11 to prevent the exterior tile 53 from falling. The gap between the exterior tiles 53 covering the front surface of the ferrite plate 1 is filled with a tile joint material 34.
【0042】この第5実施例によっても前述の第2実施
例と同様の効果を得ることができ、足付き外装タイル5
3を用いることで、シヤーコネクタを省略できる特長が
ある。According to the fifth embodiment, the same effect as in the second embodiment can be obtained.
By using 3, there is an advantage that the shear connector can be omitted.
【0043】図8は本発明の第6実施例であって、フェ
ライト板の落下防止のための外装材として到来電波の磁
界方向にフェライト板を連続させて保持するフェライト
抑え部材をそのまま利用する構造を持つプレキャスト・
カーテンウォール電波吸収壁の平断面図である。この場
合、到来電波の磁界方向にフェライト板1を連続させて
保持するフェライト抑え部材60がフェライト板1の落
下防止のための外装材を兼ねており、該フェライト抑え
部材60は、押し出し成形等により、到来電波の磁界方
向に長く、陶磁器、発泡乃至軽量コンクリート等の低誘
電率材料で断面略コ字状(又は略C字状)に形成され、
両側に足部60aを有するようになっている。そして、
フェライト抑え部材60の内側にフェライト板1が磁界
方向に連続するように接着され、フェライト板1を接着
一体化したしたフェライト抑え部材60は電界方向に一
定間隔で配列されている。そして、フェライト板1及び
フェライト抑え部材60の背面側にCFRC11を打設
することで、フェライト板1、フェライト抑え部材60
及び鉄筋22を一体化している。その際、フェライト抑
え部材60の足部60aがCFRC11中に埋没するこ
とで外装材を兼用したフェライト抑え部材60の落下を
防止している。なお、CFRC11の一部はフェライト
抑え部材60同士の隙間にも充填されている。FIG. 8 shows a sixth embodiment of the present invention, in which a ferrite suppressing member for continuously holding a ferrite plate in the magnetic field direction of an incoming radio wave is used as an exterior material for preventing the ferrite plate from falling. Precast with
It is a plane sectional view of a curtain wall radio wave absorption wall. In this case, the ferrite suppressing member 60 that holds the ferrite plate 1 continuously in the direction of the magnetic field of the arriving radio wave also functions as an exterior material for preventing the ferrite plate 1 from dropping, and the ferrite suppressing member 60 is formed by extrusion molding or the like. Long in the direction of the magnetic field of the arriving radio wave, formed of a low dielectric constant material such as ceramic, foamed or lightweight concrete, and formed in a substantially U-shaped (or substantially C-shaped) cross section;
It has a foot 60a on both sides. And
The ferrite plate 1 is adhered to the inside of the ferrite suppressing member 60 so as to be continuous in the magnetic field direction, and the ferrite suppressing members 60 in which the ferrite plate 1 is bonded and integrated are arranged at regular intervals in the direction of the electric field. Then, the ferrite plate 1 and the ferrite suppressing member 60 are formed by placing the CFRC 11 on the rear side of the ferrite plate 1 and the ferrite suppressing member 60.
And the rebar 22 are integrated. At this time, the foot portion 60a of the ferrite suppressing member 60 is buried in the CFRC 11, thereby preventing the ferrite suppressing member 60 also serving as the exterior material from falling. Note that a part of the CFRC 11 is also filled in the gap between the ferrite suppressing members 60.
【0044】この第6実施例においても、フェライト板
間の電界方向間隙部分に低誘電率のフェライト抑え部材
60の一部が位置することになり、これによって電波吸
収特性を改善することができる。また、フェライト抑え
部材60がフェライト板1の落下防止のための外装材を
兼ねており、構造が簡単になる利点もある。In the sixth embodiment as well, a part of the low dielectric constant ferrite suppressing member 60 is located in the gap between the ferrite plates in the direction of the electric field, whereby the radio wave absorption characteristics can be improved. Further, the ferrite suppressing member 60 also serves as an exterior material for preventing the ferrite plate 1 from dropping, and has an advantage that the structure is simplified.
【0045】なお、上記各実施例では、フェライト抑え
部材の形状として略L字状、略コ字状のものを例示した
が、フェライト板1を磁界方向に連続させて保持可能
で、フェライト板間の電界方向間隙部に少なくとも一部
が配置されればよく、板状を含む多様な形状が可能であ
る。In each of the above embodiments, the shape of the ferrite suppressing member is substantially L-shaped or substantially U-shaped. However, the ferrite plate 1 can be held continuously in the direction of the magnetic field. It is sufficient that at least a portion is disposed in the electric field direction gap, and various shapes including a plate shape are possible.
【0046】また、フェライト抑え部材の材質は、CF
RCとの付着性が良好な低誘電率材料であれば、発泡乃
至軽量コンクリート等の無機材料の他、有機材料の使用
も可能である。The material of the ferrite suppressing member is CF.
As long as it is a low dielectric constant material having good adhesion to RC, it is possible to use an organic material in addition to an inorganic material such as foamed or lightweight concrete.
【0047】さらに、フェライト板1の落下防止機能を
持つ外装材は、陶磁器製タイル等の他、非導電性の非磁
性材であれば、無機、有機の各種材料の使用が可能であ
る。また、外装タイルの落下防止にシヤーコネクタを使
用したとしても電波吸収特性への影響は殆どない。As the exterior material having the function of preventing the ferrite plate 1 from falling, various inorganic and organic materials can be used as long as they are non-conductive non-magnetic materials in addition to ceramic tiles. Even if a shear connector is used to prevent the exterior tile from falling, there is almost no effect on the radio wave absorption characteristics.
【0048】また、第1乃至第2実施例では、フェライ
ト板の電界方向の長さ10cmに対して電界方向のフェラ
イト板間の間隙部分の長さを6cmとしたが、両者の長さ
の比率は、到来電波の電界方向からみたフェライト板と
該フェライト板間の間隙部分の物質からなるフェライト
含有層の実効誘電率が10以下となりかつ当該間隙部分
の長さが過大にならない範囲で適宜変更可能である。In the first and second embodiments, the length of the gap between the ferrite plates in the electric field direction is set to 6 cm with respect to the length of the ferrite plate in the electric field direction of 10 cm. Can be changed as appropriate as long as the effective permittivity of the ferrite plate and the ferrite-containing layer made of the material in the gap between the ferrite plates when viewed from the electric field direction of the arriving radio wave is 10 or less and the length of the gap is not excessive. It is.
【0049】以上本発明の実施例について説明してきた
が、本発明はこれに限定されることなく請求項の記載の
範囲内において各種の変形、変更が可能なことは当業者
には自明であろう。Although the embodiment of the present invention has been described above, it is obvious to those skilled in the art that the present invention is not limited to this and various modifications and changes can be made within the scope of the claims. Would.
【0050】[0050]
【発明の効果】以上説明したように、本発明の電波吸収
壁によれば、到来電波の磁界方向に連続、かつ電界方向
に不連続にフェライト板を配置し、CFRC等の繊維強
化材を混入した高誘電率の繊維強化コンクリートに前記
フェライト板を固定した場合において、前記フェライト
板を前記磁界方向に連続した状態に保持する低誘電率材
料のフェライト抑え部材を前記フェライト板に接着し、
かつ当該フェライト抑え部材の少なくとも一部が前記フ
ェライト板間の電界方向間隙部分に位置するようにした
ので、電界方向からみたフェライト板と該フェライト板
間の物質からなるフェライト含有層の実効誘電率を低く
することができ(例えば、実効誘電率10以下を実現で
き)、電波吸収特性を改善することができ、普通コンク
リートを用いた場合と同等の電波吸収特性とすることが
できる。また、従来の普通コンクリートを用いるコンク
リート一体型の電波吸収壁においても使用しているフェ
ライト抑え板と同様の機能を持つフェライト抑え部材を
利用しており、従来のプレキャスト・コンクリート一体
型の電波吸収壁の製造技術を用いることができ、製造工
程の複雑化や、構造の複雑化を招くことがなく、CFR
Cの特長を生かした軽量、薄型の電波吸収壁が得られ
る。このように、フェライト抑え部材を前記フェライト
含有層の誘電率特性の制御材として利用できることが明
らかになり、この結果、高誘電率特性を示し電波吸収壁
への応用が課題であったCFRC等の繊維強化コンクリ
ートを用いた電波吸収壁の実用化が達成され、軽量建材
の実用化に道を開くことができた。As described above, according to the radio wave absorbing wall of the present invention, the ferrite plate is arranged continuously in the magnetic field direction of the arriving radio wave and discontinuously in the electric field direction and mixed with a fiber reinforced material such as CFRC. When the ferrite plate is fixed to the high dielectric constant fiber reinforced concrete, a ferrite suppressing member made of a low dielectric constant material for holding the ferrite plate in a continuous state in the magnetic field direction is bonded to the ferrite plate.
In addition, since at least a part of the ferrite suppressing member is located in the gap between the ferrite plates in the direction of the electric field, the effective dielectric constant of the ferrite plate and the ferrite-containing layer made of a substance between the ferrite plates as viewed from the direction of the electric field is reduced. It can be lowered (for example, an effective dielectric constant of 10 or less can be realized), the radio wave absorption characteristics can be improved, and the radio wave absorption characteristics can be made equivalent to the case of using ordinary concrete. In addition, the conventional precast / concrete integrated radio wave absorbing wall uses a ferrite suppressing member that has the same function as the ferrite suppressing plate used in the concrete integrated radio wave absorbing wall using the conventional ordinary concrete. Can be used without complicating the manufacturing process or complicating the structure.
A light and thin radio wave absorbing wall utilizing the features of C can be obtained. As described above, it has been clarified that the ferrite suppressing member can be used as a material for controlling the dielectric constant of the ferrite-containing layer. As a result, CFRC and other materials exhibiting high dielectric constant and whose application to a radio wave absorbing wall has been a problem. The practical application of radio wave absorption walls using fiber reinforced concrete has been achieved, paving the way for the practical use of lightweight building materials.
【図1】本発明に係る電波吸収壁の第1実施例を示す平
断面図である。FIG. 1 is a plan sectional view showing a first embodiment of a radio wave absorbing wall according to the present invention.
【図2】第1実施例においてフェライト板を到来電波の
磁界方向に連続配置してフェライト抑え部材で固着する
構造部分の斜視図である。FIG. 2 is a perspective view of a structure in which a ferrite plate is continuously arranged in a magnetic field direction of an incoming radio wave and fixed by a ferrite suppressing member in the first embodiment.
【図3】本発明の第2実施例を示す平断面図である。FIG. 3 is a plan sectional view showing a second embodiment of the present invention.
【図4】第2実施例の場合の反射減衰量の周波数特性を
示すグラフである。FIG. 4 is a graph showing frequency characteristics of return loss in the case of the second embodiment.
【図5】本発明の第3実施例を示す平断面図である。FIG. 5 is a plan sectional view showing a third embodiment of the present invention.
【図6】本発明の第4実施例を示す平断面図である。FIG. 6 is a plan sectional view showing a fourth embodiment of the present invention.
【図7】本発明の第5実施例を示す平断面図である。FIG. 7 is a plan sectional view showing a fifth embodiment of the present invention.
【図8】本発明の第6実施例を示す平断面図である。FIG. 8 is a plan sectional view showing a sixth embodiment of the present invention.
【図9】電波吸収壁の従来例を示す斜視図である。FIG. 9 is a perspective view showing a conventional example of a radio wave absorbing wall.
【図10】同平断面図である。FIG. 10 is a plan sectional view of the same.
【図11】従来例においてフェライト板を到来電波の磁
界方向に連続配置してフェライト抑え板で固着する構造
部分の斜視図である。FIG. 11 is a perspective view of a structure in which a ferrite plate is continuously arranged in a magnetic field direction of an incoming radio wave and fixed by a ferrite suppressing plate in a conventional example.
【図12】CFRCのカーボン繊維量(vol%)と誘電率
(複素誘電率の実数部及び虚数部)との関係を示すグラフ
である。[FIG. 12] Carbon fiber content (vol%) and dielectric constant of CFRC
9 is a graph showing a relationship between the complex dielectric constant (real part and imaginary part).
【図13】コンクリート一体型の電波吸収壁においてコ
ンクリートの誘電率をパラメータとした反射減衰量の周
波数特性を示すグラフである。FIG. 13 is a graph showing a frequency characteristic of return loss using a dielectric constant of concrete as a parameter in a radio wave absorbing wall integrated with concrete.
1 フェライト板 2,22 鉄筋 3,23,33,53 外装タイル 4 コンクリート 5 フェライト抑え板 10,20,30,40,50,60 フェライト抑え
部材 11 CFRC 12 電波反射体 23a,33a シヤーコネクタ 34 目地材 53a 足 60a 足部DESCRIPTION OF SYMBOLS 1 Ferrite plate 2,22 Reinforcing bar 3,23,33,53 Exterior tile 4 Concrete 5 Ferrite holding plate 10,20,30,40,50,60 Ferrite holding member 11 CFRC 12 Radio wave reflector 23a, 33a Shear connector 34 Joint material 53a foot 60a foot
───────────────────────────────────────────────────── フロントページの続き (72)発明者 平井 義人 東京都中央区日本橋一丁目13番1号ティ ーディーケイ株式会社内 (56)参考文献 特開 平1−241898(JP,A) 特開 平5−141021(JP,A) 特開 平8−144392(JP,A) (58)調査した分野(Int.Cl.6,DB名) H05K 9/00 E04B 1/92 ──────────────────────────────────────────────────続 き Continuation of the front page (72) Inventor Yoshito Hirai 1-13-1 Nihonbashi, Chuo-ku, Tokyo Inside TDK Corporation (56) References JP-A 1-241898 (JP, A) JP-A-5 -1410121 (JP, A) JP-A-8-144392 (JP, A) (58) Fields investigated (Int. Cl. 6 , DB name) H05K 9/00 E04B 1/92
Claims (3)
向に不連続にフェライト板を配置し、繊維強化材を混入
した繊維強化コンクリートに前記フェライト板を固定し
てなる電波吸収壁において、前記フェライト板を前記磁
界方向に連続した状態に保持する低誘電率材料のフェラ
イト抑え部材を前記フェライト板に接着し、かつ当該フ
ェライト抑え部材の少なくとも一部を前記フェライト板
間の電界方向間隙部分に位置させたことを特徴とする電
波吸収壁。1. A radio wave absorbing wall comprising: a ferrite plate arranged continuously in a magnetic field direction of an incoming radio wave and discontinuously in an electric field direction; and the ferrite plate fixed to fiber reinforced concrete mixed with a fiber reinforcing material. A ferrite suppressing member made of a low dielectric constant material for holding the ferrite plate in a continuous state in the magnetic field direction is bonded to the ferrite plate, and at least a part of the ferrite suppressing member is located in a gap between the ferrite plates in the electric field direction. A radio wave absorption wall characterized by having been made.
ト板の背面及び前記電界方向間隙部分に臨む側面に対接
するものである請求項1記載の電波吸収壁。2. The radio wave absorbing wall according to claim 1, wherein the ferrite suppressing member is in contact with a back surface of the ferrite plate and a side surface facing the gap portion in the electric field direction.
ト板の前面を覆う外装材を兼ねている請求項1記載の電
波吸収壁。3. The radio wave absorbing wall according to claim 1, wherein said ferrite suppressing member also serves as an exterior material covering a front surface of said ferrite plate.