JP2915415B2 - Thermal transfer recording media for recording clothing labels - Google Patents
Thermal transfer recording media for recording clothing labelsInfo
- Publication number
- JP2915415B2 JP2915415B2 JP63232651A JP23265188A JP2915415B2 JP 2915415 B2 JP2915415 B2 JP 2915415B2 JP 63232651 A JP63232651 A JP 63232651A JP 23265188 A JP23265188 A JP 23265188A JP 2915415 B2 JP2915415 B2 JP 2915415B2
- Authority
- JP
- Japan
- Prior art keywords
- thermal transfer
- poly
- resin
- transfer recording
- recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明は、熱転写記録用リボン、あるいは衣料ラベル
への印字に有用な衣料ラベル記録用感熱転写記録媒体に
関する。Description: TECHNICAL FIELD The present invention relates to a thermal transfer recording ribbon or a thermal transfer recording medium for clothing labels useful for printing on clothing labels.
［従来の技術］ 従来、樹脂をインク層あるいは保護層に使用した感熱
転写記録媒体は、種々知られている。[Prior Art] Conventionally, various thermal transfer recording media using a resin for an ink layer or a protective layer are known.
たとえば、スチレン／メチルメタクリレート／ブチル
アクリレートを用いたもの（特開昭62−23779号）；ス
チレン／メタクリル酸エステル共重合体、ポリメチルメ
タクリレート、ポリ塩化ビニル系樹脂からなるインク層
にスチレン／メタクリル酸エステル共重合体及びポリ塩
化ビニル系樹脂の混合物からなる透過性保護層を積層し
たもの（特開昭62−179992号）；ガラス転移点40℃以上
の非晶質ポリエステルを用いたもの（特開昭62−13384
号）；アクリル酸又はメタクリル酸エステル重合体から
なるインク層に塩素化ポリオレフィン系樹脂からなる透
過性保護層を積層したもの（特開昭63−42891号）等が
ある。For example, a composition using styrene / methyl methacrylate / butyl acrylate (Japanese Patent Laid-Open No. 23779/1987); styrene / methacrylic acid is added to an ink layer composed of styrene / methacrylic acid ester copolymer, polymethyl methacrylate, and polyvinyl chloride resin. Laminating a permeable protective layer comprising a mixture of an ester copolymer and a polyvinyl chloride resin (Japanese Patent Laid-Open No. 62-17992); Using an amorphous polyester having a glass transition point of 40 ° C. or higher (Japanese Patent Laid-open No. 62-13384
No.); one in which a permeable protective layer made of a chlorinated polyolefin resin is laminated on an ink layer made of an acrylic acid or methacrylic acid ester polymer (JP-A-63-42891).
［発明が解決すべき課題］ しかしながら、上記のものはいずれもインク層に使用
された樹脂と耐熱性が劣り、衣料に縫い付けられる衣料
のサイズ、洗濯性等を表示するラベルに前記表示を熱転
写印字すると、その印字部が衣料とともに熱プレスされ
ると画像にじみや汚れを生じるという問題点があった。[Problems to be Solved by the Invention] However, all of the above are inferior in heat resistance to the resin used for the ink layer, and the above-mentioned indication is thermally transferred to a label indicating the size of the sewn garment, washability, etc. When printing, there is a problem that when the printed portion is hot-pressed together with the clothing, the image is blurred or stained.
本発明は、こうした実情に鑑み耐熱性にすぐれた衣料
ラベル記録用感熱転写記録媒体を提供することを目的と
するものである。An object of the present invention is to provide a thermal transfer recording medium for recording clothing labels which has excellent heat resistance in view of such circumstances.
［課題を解決するための手段］ 本発明者らは、上記課題を解決するため従来より種々
研究を重ねてきたが、インク層に使用する樹脂としてガ
ラス転移温度が100℃以上のものを用いることが有効で
あることを見出し、本発明に至った。[Means for Solving the Problems] The present inventors have been conducting various studies to solve the above problems, but using a resin having a glass transition temperature of 100 ° C. or higher as a resin used for the ink layer. Was found to be effective, leading to the present invention.
すなわち、本発明は基材上に熱溶融性インク層を有
し、該熱溶融性インク層がガラス転移点100℃以上の樹
脂と着色剤を主成分とすることを特徴とする衣料ラベル
記録用感熱転写記録媒体である。That is, the present invention has a heat-fusible ink layer on a base material, and the heat-fusible ink layer is mainly composed of a resin and a colorant having a glass transition point of 100 ° C. or higher, and is used for recording clothing labels. It is a thermal transfer recording medium.
本発明の感熱転写記録媒体は、基材とその上に設けた
インク層から構成されるが、その基材としては、厚み３
〜10μ程度のプラスチックフィルムが用いられる。具体
的にはポリエステルフィルム、ポリカーボネートフィル
ム、ポリイミドフィルム、全芳香族ポリアミドフィル
ム、ポリエーテルエーテルケトンフィルム、ポリサルフ
ォンフィルム等が挙げられる。The thermal transfer recording medium of the present invention is composed of a substrate and an ink layer provided thereon.
A plastic film of about 10 μm is used. Specific examples include a polyester film, a polycarbonate film, a polyimide film, a wholly aromatic polyamide film, a polyetheretherketone film, and a polysulfone film.
また、インク層はガラス転移温度100℃以上の樹脂と
着色剤を主成分とする。The ink layer contains a resin having a glass transition temperature of 100 ° C. or higher and a colorant as main components.
本発明に使用する上記のガラス転移温度100℃以上の
樹脂は、スチレン系、スチレン誘導体系、ビニル系、ア
クリル系、エステル系及び含ふっ素系樹脂からなる群か
ら選ばれた少なくとも１種である。The resin having a glass transition temperature of 100 ° C. or higher used in the present invention is at least one selected from the group consisting of styrene-based, styrene derivative-based, vinyl-based, acrylic-based, ester-based, and fluorine-containing resins.
これをさらに具体的に説明すると、スチレン系樹脂と
しては分子量［Mw］85,000のポリスチレン（Tg 100℃）
等； ポリスチレン誘導体としてはポリＰ−カルボメトキシ
スチレン（Tg 131℃）、ポリＰ−シアノスチレン（Tg 1
20℃）、ポリＯ−メチルスチレン（Tg 115℃）、ポリＰ
−メチルスチレン（Tg 101℃）、ポリ2,4−ジメチルス
チレン（Tg 119℃）、ポリ2,5−ジメチルスチレン（Tg
122℃）、ポリ3,4−ジメチルスチレン（Tg 102℃）、ポ
リＰ−tert−ブチルスチレン（Tg 118℃）、ポリＰ−フ
ェニルスチレン（Tg 138℃）、ポリＰ−フェノキシスチ
レン（Tg 100℃）、ポリ2,5−ジフルオロスチレン（Tg
101℃）、ポリＰ−クロロスチレン（Tg 128℃）、ポリ
2,5−ジクロロスチレン（Tg 130℃）、ポリ3,4−ジクロ
ロスチレン（Tg 138℃）、ポリ2,6−ジクロロスチレン
（Tg 167℃）、ポリα−ビニルナフタレン（Tg 162
℃）、ポリα−メチルナフタレン（Tg 180℃）等、ビニ
ル系樹脂としてはポリジビニルベンゼン（Tg 106℃）、
ポリビニルホルマール（Tg 105℃）、ポリビニルシクロ
ヘキサン（Tg 100℃）、アクリル系樹脂としてはポリメ
チルメタクリレート（Tg 105℃）、アイソタクチックポ
リメチルメタクリレート（Tg 115℃）、ポリtert−ブチ
ルメタクリレート（Tg 107℃）、ポリエチレングリコー
ルメタクリレート（Tg 116℃）、ポリペンタクロロフェ
ニルアクリレート（Tg 145℃）、ポリフェニルメタクリ
レート（Tg 110℃）、ポリＰ−シアノフェニルメタクリ
レート（Tg 155℃）、ポリＰ−カルボメトキシフェニル
メタクリレート（Tg 106℃）、ポリＰ−シアノエチルフ
ェニルメタクリレート（Tg 128℃）、ポリメタクリロニ
トリル（Tg 120℃）等； ポリエステル系としてはポリエチレン−1,4−ナフタ
レート（Tg 119℃）等； 含フッ素系樹脂としてはポリ四フッ化エチレン（Tg 1
30℃）等が挙げられ、これらは単独あるいは２種類以上
の混合で使用できる。To explain this more specifically, polystyrene having a molecular weight [Mw] of 85,000 (Tg 100 ° C.) is used as a styrene resin.
Polystyrene derivatives such as poly-P-carbomethoxystyrene (Tg 131 ° C.) and poly-P-cyanostyrene (Tg 1
20 ° C), poly O-methylstyrene (Tg 115 ° C), poly P
-Methylstyrene (Tg 101 ° C), poly 2,4-dimethylstyrene (Tg 119 ° C), poly2,5-dimethylstyrene (Tg
122 ° C.), poly 3,4-dimethylstyrene (Tg 102 ° C.), poly P-tert-butylstyrene (Tg 118 ° C.), poly P-phenylstyrene (Tg 138 ° C.), poly P-phenoxystyrene (Tg 100 ° C.) ), Poly 2,5-difluorostyrene (Tg
101 ° C), poly P-chlorostyrene (Tg 128 ° C), poly
2,5-dichlorostyrene (Tg 130 ° C.), poly 3,4-dichlorostyrene (Tg 138 ° C.), poly 2,6-dichlorostyrene (Tg 167 ° C.), poly α-vinylnaphthalene (Tg 162
℃), poly-α-methylnaphthalene (Tg 180 ℃) such as polydivinylbenzene (Tg 106 ℃)
Polyvinyl formal (Tg 105 ° C), polyvinylcyclohexane (Tg 100 ° C), polymethyl methacrylate (Tg 105 ° C), isotactic polymethyl methacrylate (Tg 115 ° C), polytert-butyl methacrylate (Tg 107 ° C), polyethylene glycol methacrylate (Tg 116 ° C), polypentachlorophenyl acrylate (Tg 145 ° C), polyphenyl methacrylate (Tg 110 ° C), poly P-cyanophenyl methacrylate (Tg 155 ° C), poly P-carbomethoxyphenyl methacrylate (Tg 106 ° C), poly-P-cyanoethylphenyl methacrylate (Tg 128 ° C), polymethacrylonitrile (Tg 120 ° C), etc .; polyesters such as polyethylene-1,4-naphthalate (Tg 119 ° C); fluorinated Polytetrafluoroethylene (Tg 1
30 ° C.), and these can be used alone or in combination of two or more.
着色剤としてはカーボンブラック、二酸化チタン、ベ
ンガラレーキレッドＣ、ファーストスカイブルー、ベン
ジジンイエロー、フタロシアニングリーン、フタロシア
ニンブルー、直接染料、油性染料、塩基性染料等の顔
料、染料等が挙げられる。Examples of the colorant include pigments and dyes such as carbon black, titanium dioxide, bengara lake red C, fast sky blue, benzidine yellow, phthalocyanine green, phthalocyanine blue, direct dyes, oil dyes, and basic dyes.
尚耐アイロン性をおとさない範囲内でインク層中に活
性剤、滑剤、柔軟剤、ワックス、樹脂を添加しても差し
支えない。An activator, a lubricant, a softener, a wax, and a resin may be added to the ink layer as long as the iron resistance is not lowered.
実施例 樹脂※ 20重量部 カーボンブラック ４重量部 メチルエチルケトン 76重量部 ボールミルで24時間分散後4.5μポリエステルフィル
ム上に塗布し、乾燥塗膜４μｍのインク層を設けた。Example Resin * 20 parts by weight Carbon black 4 parts by weight Methyl ethyl ketone 76 parts by weight After dispersing in a ball mill for 24 hours, the mixture was applied on a 4.5 μm polyester film to form an ink layer having a dry coating of 4 μm.
※上記樹脂としては以下のものを用いた。 * The following resin was used as the above resin.
実施例１ ポリスチレン（Tg 100℃） 〃 ２ ポリＰ−メチルスチレン（Tg 101℃） 〃 ３ ポリビニルホルマール（Tg 105℃） 〃 ４ ポリメチルメタクリレート（Tg 105℃） 〃 ５ ポリエチレン−1,4−ナフタレート（Tg 119
℃） 〃 ６ ポリ四フッ化エチレン（Tg 130℃） 〃 ７ ポリＰフェニルスチレン（Tg 138℃） 10重量部 ポリビニルシクロヘキサノン（Tg 100℃） 10重量部 比較例１ ポリ塩化ビニル（Tg 80℃） 比較例２ ポリtertブチルアクリレート（Tg 43℃） 〃 ３ ポリエチレンテレフタレート（Tg 70℃） 以上のようにして作成した熱転写記録媒体を用いて、
熱転写プリンター（ライン型ヘッド、印加エネルギー20
〜35mj/mm2で合成紙（王子油化合成紙）上に印加し適正
印字エネルギー（感度）を求め、かつ、転写画像を作成
し、以下の試験を行った。Example 1 Polystyrene (Tg 100 ° C.) 〃2 Poly P-methylstyrene (Tg 101 ° C.) 〃3 Polyvinyl formal (Tg 105 ° C.) 〃4 Polymethyl methacrylate (Tg 105 ° C.) 〃5 Polyethylene-1,4-naphthalate ( Tg 119
° C) 〃6 Polytetrafluoroethylene (Tg 130 ° C) ７7 PolyPphenylstyrene (Tg 138 ° C) 10 parts by weight Polyvinylcyclohexanone (Tg 100 ° C) 10 parts by weight Comparative Example 1 Polyvinyl chloride (Tg 80 ° C) Comparison Example 2 Poly-tert-butyl acrylate (Tg 43 ° C.) 〃3 Polyethylene terephthalate (Tg 70 ° C.) Using the thermal transfer recording medium prepared as described above,
Thermal transfer printer (line type head, applied energy 20
Is applied onto the synthetic paper (Oji-Yuka Synthetic Paper) in ~35mj / mm 2 determined the proper printing energy (sensitivity), and to create a transferred image was subjected to the following tests.
なお、ホットプレステストはJIS L0850、100℃で行っ
た。The hot press test was performed at JIS L0850 at 100 ° C.
［発明の効果］ 以上説明したように、本発明の構成による感熱転写記
録媒体により衣料ラベルに記録した印字部は耐熱プレス
性にすぐれている。 [Effects of the Invention] As described above, the printed portion recorded on the clothing label by the thermal transfer recording medium according to the configuration of the present invention has excellent heat press resistance.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平１−120389（ＪＰ，Ａ) 特開 平１−255589（ＪＰ，Ａ) (58)調査した分野(Int.Cl.6，ＤＢ名) B41M 5/38 - 5/40 ────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-1-120389 (JP, A) JP-A-1-255589 (JP, A) (58) Fields investigated (Int.Cl. 6 , DB name) B41M 5/38-5/40
Claims (2)
融性インク層がガラス転移点100℃以上の樹脂と着色剤
を主成分とすることを特徴とする衣料ラベル記録用感熱
転写記録媒体。1. A label for recording clothing labels, comprising a heat-fusible ink layer on a base material, the heat-fusible ink layer being mainly composed of a resin having a glass transition point of 100 ° C. or higher and a colorant. Thermal transfer recording medium.
ン系、スチレン誘導体系、ビニル系、アクリル系、エス
テル系、および含ふっ素系樹脂からなる群から選ばれた
少くとも１種である請求項（１）記載の衣料ラベル記録
用感熱転写記録媒体。2. The resin having a glass transition point of 100 ° C. or higher is at least one selected from the group consisting of styrene-based, styrene derivative-based, vinyl-based, acrylic-based, ester-based, and fluorine-containing resins. Item (1): A thermal transfer recording medium for recording clothing labels according to Item (1).