JP2888501B2 - Articles made of magnetically transformed metal - Google Patents
Articles made of magnetically transformed metalInfo
- Publication number
- JP2888501B2 JP2888501B2 JP3201499A JP20149991A JP2888501B2 JP 2888501 B2 JP2888501 B2 JP 2888501B2 JP 3201499 A JP3201499 A JP 3201499A JP 20149991 A JP20149991 A JP 20149991A JP 2888501 B2 JP2888501 B2 JP 2888501B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- ferromagnetic
- metal
- transformation
- cash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】この発明は、パチンコ店、ゲーム
店等で顧客に渡す換金用特殊景品やメダル或いは有名ブ
ランド商品など、偽造や改ざん又は模造に対してセキュ
リティを要求される物品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to articles requiring security against counterfeiting, falsification, or imitation, such as special prizes for cash, medals, or famous brand goods to be passed on to customers in pachinko parlors, game stores, and the like.
【０００２】[0002]
【従来の技術】一般に、パチンコ店、ゲーム店等の遊技
場では顧客が獲得したパチンコ玉、メダルを景品（商
品）に交換しているが、その景品の内、現金と交換でき
る特殊景品を希望する顧客も多い。この現金交換用景品
は、例えばプラスチックケースに入った万年筆，プラス
チックケース入りの文鎮（薄い金属）等、種々の品物が
店毎あるいは、ある一定の地域毎に統一して使用されて
おり、顧客はこの現金交換用特殊景品を別途交換場へ持
っていき、所定の比率の現金に交換してもらっている。2. Description of the Related Art In general, pachinko balls and medals are exchanged for prizes (goods) at amusement arcades such as pachinko parlors and game stores. Of these prizes, special prizes that can be exchanged for cash are desired. Many customers do. The cash exchange prize includes various items such as a fountain pen in a plastic case, a paperweight (thin metal) in a plastic case, and the like, which are used in each store or in a certain area. The special prize for cash exchange is separately brought to an exchange, where the prize is exchanged for a predetermined ratio of cash.
【０００３】最近ではパチンコ玉等を計数して、その計
数値に応じた現金交換用特殊景品を顧客に対して自動的
に払い出すようにした景品交換装置も出現している。[0003] Recently, a prize exchange apparatus has been developed which counts pachinko balls and the like and automatically pays out special prizes for cash exchange to customers according to the counted value.
【０００４】[0004]
【発明が解決しようとする課題】現金交換用特殊景品の
現金への交換は、景品交換場の係員が目で見て判断して
おり、一度に多数持ち込まれた場合には数え間違いを生
じたり、価値（金額）が異なる多種の現金交換用特殊景
品が使用されているときは、換金金額の計算間違いを生
じていた。また、外のケースはそのままで中身の商品が
すり換えられた偽造景品が持ち込まれても確実に発見で
きないこともあった。The exchange of special prizes for cash exchange into cash is visually judged by a staff at the prize exchange hall, and if a large number are brought in at once, counting errors may occur. When various kinds of special gifts for cash exchange having different values (amounts) are used, the calculation of the cash amount has occurred. In addition, in some cases, counterfeit prizes in which the contents of the product have been replaced with the outer case cannot be reliably detected.
【０００５】さらに、換金を自動的に行ない得るように
したシステムが特開平１−１１５３８１号公報に開示さ
れているが、これは特殊景品に磁気テープを貼付してお
き、景品払い出し時にこの磁気テープに金額等を記録
し、現金交換機にて磁気テープの金額を読取って現金を
払い出している為、磁気テープの情報を解析することに
よりデータの改ざんが容易になされてしまうという問題
点がある。また改ざんはしなくても、磁気テープの情報
をコピーして別の磁気テープに写し、偽の特殊景品に貼
付されて使用されても発見できないという問題点もあ
る。[0005] Further, Japanese Patent Laid-Open Publication No. HEI 1-1115381 discloses a system which can automatically exchange money, but this system has a magnetic tape affixed to a special prize, and the magnetic tape is used when the prize is paid out. The amount of money and the like are recorded in the data and the cash exchange reads the amount of the magnetic tape and pays out the cash. Therefore, there is a problem that the data is easily falsified by analyzing the information of the magnetic tape. Further, there is a problem that even if the information is not falsified, the information on the magnetic tape is copied and copied onto another magnetic tape, and the information cannot be found even if the information is attached to a fake special gift and used.
【０００６】また、遊技用メダルでは、大きさ（直径）
だけで判別しているため偽造が容易であり、他店のメダ
ルが混入することも多かった。[0006] The size (diameter) of a gaming medal is
Forgery was easy because it was determined only by the medals, and medals from other stores were often mixed.
【０００７】その他、有名ブランド品のベルトのバック
ル、ネクタイピン、カフスボタンなどの装身具やバッグ
類の金具等にはメーカ名や商標が記入されているが、し
ばしば模造品が出回っており、それらは外観的に精巧に
出来ているので、目視だけで見分けることは困難であっ
た。[0007] In addition, manufacturers' names and trademarks are written on accessories such as belt buckles, tie pins, cufflinks and the like of famous brands and metal fittings of bags. It was difficult to distinguish them only by visual inspection because they were so sophisticated.
【０００８】この発明は上述のような事情に鑑みてなさ
れたものであり、この発明の目的は、偽造や改ざんがで
きず、セキュリティの高い記録機能を持った物品を提供
することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and an object of the present invention is to provide an article which cannot be forged or tampered with and has a highly secure recording function.
【０００９】[0009]
【課題を解決するための手段】この発明は偽造に対して
セキュリティを有する記録媒体から成る物品に関するも
ので、この発明の上記目的は、機械的変形によって非磁
性から強磁性に磁性変態を生じる金属を用いて、部分的
に強磁性への磁性変態を生ぜしめ、記録を行なうように
した磁性変態金属でなる物品によって達成される。SUMMARY OF THE INVENTION The present invention relates to an article comprising a recording medium having security against forgery, and an object of the present invention is to provide a metal which undergoes a magnetic transformation from non-magnetic to ferromagnetic by mechanical deformation. This is achieved by means of an article made of a magnetically transformed metal, which partially causes a magnetic transformation to ferromagnetism and performs recording.
【００１０】[0010]
【作用】鋼をオーステナイト域から臨界冷却速度以上で
焼入れすると、マルテンサイトが得られる。このマルテ
ンサイトの発生温度をＭｓ点といい、鋼の化学成分に依
存する。しかし、マルテンサイトは不安定なオーステナ
イトを加工しても誘発されることがあり、加工度によっ
てその発生温度はＭｓ点より高温にずれるが、Ｍｓ点よ
り余り高くなると、加工によるマルテンサイト化が生じ
なくなる。この点をＭｄ点といい、加工によって生じる
マルテンサイト化を加工誘発変態という。この場合、オ
ーステナイトを加工するために応力が負荷されていて、
この加工ひずみによってマルテンサイト変態が誘発・進
行する。マルテンサイト変態の進行に伴って大きな塑性
が生じるが、これは変態誘起塑性（ｔｒａｎｓｆｏｒｍ
ａｔｉｏｎ−ｉｎｄｕｃｅｄ ｐｌａｓｔｉｃｉｔｙ，
略称ＴＲＩＰ）と名付けられており、この変態誘起塑性
は超塑性の一種である。すなわち、加工によってオース
テナイト→マルテンサイト変態が発生し、加工誘発変態
の起因となった応力集中が変態の発生によって緩和さ
れ、かなり大きい延性を示すことになる。When the steel is quenched from the austenite region at a critical cooling rate or higher, martensite is obtained. The temperature at which martensite is generated is called the Ms point, and depends on the chemical composition of the steel. However, martensite may be induced also by processing the unstable austenite, but its occurrence temperature by working ratio is shifted to a higher temperature than the M s point and becomes higher too than M s point, martensite due to processing Will not occur. This point is called the Md point, and the formation of martensite caused by processing is called processing-induced transformation. In this case, stress is applied to process austenite,
The martensitic transformation is induced and proceeds by this processing strain. Large plasticity occurs with the progress of martensitic transformation, which is caused by transformation-induced plasticity (transformation).
ation-induced plasticity,
Transformation-induced plasticity is a type of superplasticity. That is, austenite-> martensite transformation occurs due to the working, and the stress concentration that caused the working-induced transformation is alleviated by the occurrence of the transformation, thereby exhibiting considerably large ductility.
【００１１】この発明は上述のような加工誘発変態があ
り、機械的変形によって非磁性から強磁性に磁性変態を
生じる金属をセキュリティを要する物品又はその一部と
して用いるものである。尚、ここで言う「金属」とは合
金も含むものとする。According to the present invention, a metal which undergoes the above-described process-induced transformation and undergoes a magnetic transformation from non-magnetic to ferromagnetic by mechanical deformation is used as an article requiring security or a part thereof. It is to be noted that the “metal” mentioned here includes an alloy.
【００１２】ところで、ステンレス鋼は次の表１のよう
に分類される。Incidentally, stainless steel is classified as shown in Table 1 below.
【００１３】[0013]
【表１】 また、オーステナイトステンレスはＳＵＳ３０１，３０
４，３１６，３２１の如く種々に分かれており、この発
明に用いるステンレスは準安定なオーステナイト相を室
温で有するステンレス鋼、つまりＭｄ点は室温以上であ
り、Ｍｓ点は室温以下のオーステナイトステンレス鋼で
ある。そして、室温において圧延，エンボス，パンチ穴
等の機械的変形を上記オーステナイトステンレス鋼に与
えることにより、非磁性のオーステナイトが強磁性のマ
ルテンサイトに変態する。これは、数百°Ｃ以上に加熱
しない限り非可逆性である。[Table 1] Austenitic stainless steel is SUS301, 30
4,316,321 as is divided into various stainless steel having a stainless steel metastable austenite phase used in the present invention at room temperature, i.e. M d point is above room temperature, M s point below room temperature Austenitic Stainless It is steel. Then, non-magnetic austenite is transformed into ferromagnetic martensite by applying mechanical deformation such as rolling, embossing and punching holes to the austenitic stainless steel at room temperature. It is irreversible unless heated above a few hundred degrees Celsius.
【００１４】図１０は、一例としてプレス又はエンボス
によってオーステナイトステンレス鋼１の凹部２が強磁
性化された様子を示している。このようにしてセキュリ
ティが必要な物品上の任意の部分に強磁性部分を形成す
ることにより、偽造が不可能な情報記録を行なう。FIG. 10 shows a state in which the recess 2 of the austenitic stainless steel 1 is made ferromagnetic by pressing or embossing as an example. By forming a ferromagnetic portion on an arbitrary portion of the article requiring security in this manner, information recording that cannot be counterfeited is performed.
【００１５】[0015]
【実施例】図１はこの発明の１実施例として、現金交換
用特殊景品１０の外観を透明ケース１１に収納した状態
で示しており、パチンコ店では顧客の獲得したパチンコ
球数に応じて上記ケース１１に入った現金交換用特殊景
品１０を顧客に渡すことになる。ここに、現金交換用特
殊景品１０は底部に樹脂，布１２等を敷設された透明ケ
ース１１内に収容されており、現金交換用特殊景品１０
に記録されている球数データ又は金額データは、ケース
１１の外側より非接触センサで磁気的に読取られる。
尚、強磁性，非磁性のパターンは景品の価値により変え
る（例えば２００円，５００円，１０００円等）。この
とき、顧客が目で見て分るように表面に数字を明示する
こともできる。また、現金交換用特殊景品１０は必ずし
も透明ケース１１に収容されてなくても良い。FIG. 1 shows an embodiment of the present invention in which a special gift 10 for cash exchange is housed in a transparent case 11, and in a pachinko parlor, the number of pachinko balls obtained by a customer is determined. The special gift 10 for cash exchange in the case 11 will be given to the customer. Here, the special prize 10 for cash exchange is accommodated in a transparent case 11 having a resin, cloth 12 or the like laid on the bottom thereof.
The ball number data or the amount data recorded in the case 11 are magnetically read from the outside of the case 11 by a non-contact sensor.
The ferromagnetic and non-magnetic patterns are changed according to the value of the premium (for example, 200 yen, 500 yen, 1000 yen, etc.). At this time, a number can be clearly indicated on the surface so that the customer can see it. Further, the special gift 10 for cash exchange does not necessarily have to be accommodated in the transparent case 11.
【００１６】次に、現金交換用特殊景品１０の製造工程
を図２を参照して説明すると、上述したようなオーステ
ナイトステンレス鋼を機械加工して同図（Ａ）の如き景
品部材２０を得る。この場合、凸部２０Ａの位置によっ
て最終的な強磁性の位置が決まり、凸部２０Ａの高さの
違い、つまり機械加工における圧延率の違いによって最
終的に磁性（磁気的強度）の違いが生じる。凸部２０Ａ
が高いほど圧延率が大きくなって磁性が強くなる。図２
（Ａ）の機械加工が終了した時点では、機械加工のため
に景品部材２０の表面全体或は一部が強磁性化されてい
るので、熱処理によって非磁性化、つまりオーステナイ
ト単相にする（図２（Ｂ）の状態）。熱処理によって非
磁性化された景品部材２１に対して、凸部のみ圧延を行
なうことによって、その部分のみを強磁性化させた図２
（Ｃ）の如き景品部材２２を得る。図の斜線部が強磁性
化された部分を示している。そして、かかる図２（Ｃ）
の景品部材２２に対して表面研磨して汚れ（油，酸化膜
等），凹凸等を取り除き、最終的には電解研磨，化学研
磨等の残留ひずみが残らない研磨で仕上げることが望ま
しい。その後に表面装飾して、図２（Ｄ）の如き現金交
換用特殊景品10を得る。Next, the manufacturing process of the special gift 10 for cash exchange will be described with reference to FIG. 2. The austenitic stainless steel as described above is machined to obtain a premium member 20 as shown in FIG. In this case, the final ferromagnetic position is determined by the position of the projection 20A, and the difference in magnetism (magnetic strength) finally occurs due to the difference in height of the projection 20A, that is, the difference in the rolling ratio in machining. . Protrusion 20A
The higher the value, the higher the rolling ratio and the stronger the magnetism. FIG.
At the time when the machining of (A) is completed, the whole or a part of the surface of the prize member 20 is ferromagnetic due to the machining, so that it is demagnetized by heat treatment, that is, turned into an austenitic single phase (FIG. 2 (B) state). FIG. 2 shows that the prize member 21 that has been demagnetized by the heat treatment is subjected to rolling only the protruding portion to make only that portion ferromagnetic.
A premium member 22 as shown in FIG. The hatched portions in the figure indicate the ferromagnetic portions. Then, FIG. 2 (C)
It is desirable that the surface of the prize member 22 is polished to remove dirt (oil, oxide film, etc.), irregularities, and the like, and finally finished by polishing such as electrolytic polishing, chemical polishing or the like that does not leave residual strain. Thereafter, the surface is decorated to obtain a special gift 10 for cash exchange as shown in FIG.
【００１７】ここで、表面研磨は砥石，研磨紙等によっ
て研磨したい面を擦り、機械的に削って行くもので、数
μｍの変形ダメージ層（変質層）が生じる。また、電解
研磨は研磨を行ないたい材料を正極として、正負両極を
同時に電解液に浸して電圧を印加するものである。この
場合、正極からは電子が奪われるため、材料表面の原子
はイオン化して電解液中に溶け出す。機械的ダメージが
ないため変質相が生じることはなく、この電解研磨は機
械研磨によって生じた変質相を取り除くために行な
う。、更に化学研磨は特定の腐食液（塩酸，硫酸，王水
等）に材料を浸し、表面を溶かして行くもので、目的は
電解研磨と同一である。従って、電解研磨又は化学研磨
のいずれか一方を行なえば良い。表面装飾は、例えば金
メッキ等のように表面に高級感のあるものを成膜した
り、表面彫刻又は表面塗装でも良い。なお、表面彫刻に
よって生じた強磁性は、電解研磨等により取り除いても
良い。最終的に得られた図２（Ｄ）の如き現金交換用特
殊景品１０のＸ−Ｘ断面構造は、図３のようになってい
る。Here, the surface polishing is performed by rubbing the surface to be polished with a grindstone, abrasive paper or the like and mechanically shaving the surface, and a deformation damage layer (denatured layer) of several μm is generated. In the electropolishing, a material to be polished is used as a positive electrode, and both positive and negative electrodes are simultaneously immersed in an electrolytic solution to apply a voltage. In this case, electrons are deprived from the positive electrode, and atoms on the material surface are ionized and dissolved in the electrolytic solution. Since there is no mechanical damage, no altered phase occurs, and this electropolishing is performed to remove the altered phase caused by mechanical polishing. In addition, chemical polishing involves immersing a material in a specific corrosive liquid (hydrochloric acid, sulfuric acid, aqua regia, etc.) and dissolving the surface, and the purpose is the same as electrolytic polishing. Therefore, either one of electrolytic polishing or chemical polishing may be performed. The surface decoration may be, for example, a film having a high-grade appearance such as gold plating or the like, or may be surface engraving or surface painting. The ferromagnetism generated by the surface engraving may be removed by electrolytic polishing or the like. The XX cross-sectional structure of the finally obtained special prize 10 for cash exchange as shown in FIG. 2 (D) is as shown in FIG.
【００１８】尚、上述の実施例では現金交換用特殊景品
の長手方向に対して直交するように強磁性体化部を形成
しているが、図４に示すように長手方向に沿って強磁性
体化部を形成してコード化しても良い。In the above-described embodiment, the ferromagnetic portion is formed so as to be orthogonal to the longitudinal direction of the special prize for cash exchange. However, as shown in FIG. The embodied portion may be formed and encoded.
【００１９】この発明の現金交換用特殊景品１０に記録
されている情報は、図５（Ａ）に示す如く現金交換用特
殊景品１０の上方（又は側面）に金属の強磁性部を磁化
させ得る磁化力を持つバイアス磁石を備えた磁気抵抗
（ＭＲ）センサ３０を設置し、相対的にいずれかを移動
することによって磁気出力を検出し、信号処理すると同
図（Ｂ）のような磁気抵抗信号ＭＳが得られるので、こ
の磁気抵抗信号ＭＳを所定のスレッショルドＴＨｏで２
値化して計数等することによって読取ることができる。
実際には図６に示すように景品１０の入ったケース１１
を複数個立てて搬送させ、ＭＲセンサアレイ３１で同時
に読取るようにする。その際、景品１０の強磁性，非磁
性のパターンを図６に示すように左右上下対称にしてお
けば、ケース１１の向きがどの方向であっても読取を容
易に行なうことができる。The information recorded on the special prize for cash exchange 10 of the present invention can magnetize a metal ferromagnetic portion above (or on the side of) the special prize for cash exchange 10 as shown in FIG. A magnetoresistive (MR) sensor 30 provided with a bias magnet having a magnetizing force is installed, a magnetic output is detected by relatively moving any one, and a signal processing is performed. As shown in FIG. Since MS is obtained, the magnetoresistive signal MS is set at 2 at a predetermined threshold THo.
It can be read by converting to a value and counting.
Actually, as shown in FIG.
Are transported upright and read by the MR sensor array 31 simultaneously. At this time, if the ferromagnetic and non-magnetic patterns of the prize 10 are symmetrical left and right as shown in FIG. 6, reading can be easily performed regardless of the direction of the case 11.
【００２０】ところで、上述したように圧延率の大小に
よって磁性に大小が生じるが、この現象は図７に示され
ている（日本金属学会会報 Ｖｏ１．２４（１９８５）
年参照）。このことから上記金属に対して多値情報記録
が可能であり、図８で示すように複数のスレッショルド
ＴＨ１及びＴＨ２で多値情報を読取ることができる。な
お、読取はホールセンサによっても可能である。As described above, the magnitude of the magnetism varies depending on the magnitude of the rolling reduction, and this phenomenon is shown in FIG. 7 (Journal of the Japan Institute of Metals, Vol 1.24 (1985)).
Year). From this, multi-valued information can be recorded on the metal, and as shown in FIG. 8, multi-valued information can be read at a plurality of thresholds TH1 and TH2. Note that reading is also possible with a hall sensor.
【００２１】また、この発明の現金交換用特殊景品の製
造工程は、図９（Ａ）に示すように先ずオーステナイト
ステンレス鋼で成る平板４を切り出し、熱処理を施して
非磁性化した後にプレスで加工し、図９（Ｂ）のように
加工部のみを強磁性化するようにしても良い。この場合
もその後、研磨によって表面を平面化，装飾する。As shown in FIG. 9 (A), the process of manufacturing the special prize for cash exchange of the present invention is as follows. First, the flat plate 4 made of austenitic stainless steel is cut out, heat-treated to make it non-magnetic, and then processed by a press. Alternatively, only the processed portion may be made ferromagnetic as shown in FIG. Also in this case, the surface is flattened and decorated by polishing.
【００２２】尚、熱により強磁性から非磁性に磁性変態
を生じる金属を用いて、レーザー等により非磁性の部分
を形成した特殊景品を作成しても良い。A special prize having a non-magnetic portion formed by a laser or the like may be produced by using a metal which undergoes magnetic transformation from ferromagnetic to non-magnetic by heat.
【００２３】次に、この発明の他の実施例として遊技用
メダルの概要構成を図１１に示す。すなわち、非磁性の
メダルに同心円のリング状強磁性部を形成したもので、
リングの径及び数によって情報を記録することができ
る。製造方法は前述の現金交換用特殊景品と同じ工程を
用いることができ、図１２によって示される。オーステ
ナイトステンレス鋼を機械加工して同図（Ａ）のような
メダル部材を得る。機械加工によって強磁性化された部
分は熱処理によって非磁性化し、図１２（Ｂ）のように
オーステナイト単相とする。更に凸部のみ圧延を行なう
ことによって部分的に強磁性化させ、図１２（Ｃ）のご
ときメダル部材を得る。図の斜線部は強磁性化された部
分を示している。その表面を機械研磨及び電解乃至化学
研磨して仕上げを行なったあと、表面装飾して図２
（Ｄ）の如き遊技用メダル４０を得る。あるいは非磁性
化したステンレス円板から図１２（Ａ）の形状をプレス
加工で作れば凹部が強磁性化するので、これを研磨、装
飾してもよい。この場合には図１２（Ｃ）の白抜き部が
強磁性となる。FIG. 11 shows a schematic configuration of a gaming medal as another embodiment of the present invention. In other words, a concentric ring-shaped ferromagnetic portion is formed on a non-magnetic medal,
Information can be recorded by the diameter and number of rings. The manufacturing method can use the same process as the above-mentioned special gift for cash exchange, and is shown by FIG. An austenitic stainless steel is machined to obtain a medal member as shown in FIG. The portion that has been made ferromagnetic by mechanical processing is demagnetized by heat treatment to form an austenitic single phase as shown in FIG. Further, only the protrusions are rolled to partially ferromagnetically obtain a medal member as shown in FIG. The hatched portion in the figure indicates a ferromagnetic portion. After finishing the surface by mechanical polishing and electrolytic or chemical polishing, the surface is decorated and FIG.
A gaming medal 40 as shown in (D) is obtained. Alternatively, if the shape shown in FIG. 12A is made by pressing from a non-magnetized stainless steel disk, the concave portion becomes ferromagnetic, and this may be polished and decorated. In this case, the white portion in FIG. 12C becomes ferromagnetic.
【００２４】メダルに記録された情報の読取り方法を図
１３に示す。メダルＡ及びＢが傾斜した搬送路４１を転
動しながら搬送される時、ＭＲセンサー又はホールセン
サ等磁気センサ４２の検出位置をメダル中心の軌跡４３
上におくようにすれば、メダルＡ及びＢに対してそれぞ
れ図１４（Ａ），（Ｂ）のような出力変化が得られる。
図において、メダルの中心位置から見た強磁性部分の数
及び位置でメダルの種類，真偽が判別できる。FIG. 13 shows a method of reading information recorded on a medal. When the medals A and B are conveyed while rolling on the inclined conveyance path 41, the detection position of the magnetic sensor 42 such as an MR sensor or a hall sensor is set to the locus 43 of the medal center.
By doing so, output changes as shown in FIGS. 14A and 14B are obtained for medals A and B, respectively.
In the figure, the type and authenticity of the medal can be determined based on the number and position of the ferromagnetic portions viewed from the center position of the medal.
【００２５】更に他の実施例として、ブランド品の金具
類に適用する例を挙げる。図１５は本発明による金具を
用いたハンドバッグを示したものである。非磁性オース
テイナイトステンレス鋼の金具５０に記録した強磁性部
の位置によって本物と偽物とを識別できる。また金具を
使わないハンドバッグの場合でも図１６のように表皮の
内側に部分的に強磁性化したステンレス箔５１を添付す
ることにより、磁気センサを用いて真偽の判定ができ
る。As still another embodiment, an example in which the present invention is applied to metal fittings of a brand product will be described. FIG. 15 shows a handbag using the metal fitting according to the present invention. The genuine product and the fake product can be distinguished by the position of the ferromagnetic portion recorded on the nonmagnetic austenitic stainless steel fitting 50. Even in the case of a handbag that does not use metal fittings, authenticity can be determined using a magnetic sensor by attaching a partially ferromagnetic stainless steel foil 51 inside the skin as shown in FIG.
【００２６】ブランド品識別のための磁気センサとして
は、図１７に示すようなハンディタイプの検知器を用い
ると便利である。検知器はホール素子から成るプローブ
５２，バイアス磁石５３，駆動用電池５４，出力表示部
５５及びスイッチ５６から構成されており、プローブ５
２を当てるとバイアス磁石５３により磁化された金具の
磁気出力をホール素子が検出し、その点のホール素子出
力が表示部５５に示されるようになっている。プローブ
を移動すれば、金具上の強磁性部の分布状態がわかる。It is convenient to use a handy-type detector as shown in FIG. 17 as a magnetic sensor for identifying a brand product. The detector comprises a probe 52 composed of a Hall element, a bias magnet 53, a driving battery 54, an output display unit 55, and a switch 56.
When 2 is applied, the Hall element detects the magnetic output of the bracket magnetized by the bias magnet 53, and the output of the Hall element at that point is displayed on the display unit 55. By moving the probe, the distribution state of the ferromagnetic portions on the metal fitting can be determined.
【００２７】その他、紙幣を収納する金箱の一部に金種
を示すコードとして使用してもよい。Alternatively, a code indicating a denomination may be used in a part of a gold box for storing bills.
【００２８】[0028]
【発明の効果】以上のようにこの発明の物品によれば、
機械的変形により非磁性から強磁性に磁性変態を生じる
金属を用いており、部分的に強磁性に磁性変態させてい
るので、表面から見ても磁性変態は見やぶることはでき
ず、磁気ヘッド等によってはエンコードできない為セキ
ュリティが極めて高い。また、景品にエンコードする磁
気量を加工度，加工温度により調整するようにすれば、
偽造を完全に防止できる物品を提供することができる。As described above, according to the article of the present invention,
A metal that undergoes magnetic transformation from non-magnetic to ferromagnetic due to mechanical deformation is used, and the magnetic transformation is partially ferromagnetic, so the magnetic transformation cannot be seen from the surface, and the magnetic head In some cases, encoding is not possible, so security is extremely high. Also, if the amount of magnetism to be encoded in the prize is adjusted by the processing degree and processing temperature,
An article that can completely prevent forgery can be provided.
【図１】現金交換用特殊景品の外観図である。FIG. 1 is an external view of a special gift for cash exchange.
【図２】現金交換用特殊景品の製造工程示す図である。FIG. 2 is a diagram showing a manufacturing process of a special gift for cash exchange.
【図３】図２（Ｄ）のＸ−Ｘ断面構成図である。FIG. 3 is a sectional view taken along the line XX of FIG. 2 (D).
【図４】現金交換用特殊景品の他の形態を示す外観図で
ある。FIG. 4 is an external view showing another form of a special gift for cash exchange.
【図５】この発明の情報読出の例を示す図である。FIG. 5 is a diagram showing an example of information reading according to the present invention.
【図６】ＭＲセンサアレイを用いて複数の景品のデータ
を読取る例を示す図である。FIG. 6 is a diagram illustrating an example of reading data of a plurality of premiums using an MR sensor array.
【図７】Ｎｉ当量に対する透磁率の変化を示す図であ
る。7 is a diagram showing a change in magnetic permeability with respect to N i eq.
【図８】多値情報の読出を説明するための図である。FIG. 8 is a diagram for explaining reading of multi-value information.
【図９】現金交換用特殊景品の他の製造工程を示す図で
ある。FIG. 9 is a diagram showing another manufacturing process of the special gift for cash exchange.
【図１０】機械的変形によって局部的な磁性変態を生じ
た様子を示す図である。FIG. 10 is a diagram showing a state where local magnetic transformation is caused by mechanical deformation.
【図１１】遊技用メダルの概要構成を示す図である。FIG. 11 is a diagram showing a schematic configuration of a gaming medal.
【図１２】遊技用メダルの製造工程を示す図である。FIG. 12 is a view illustrating a manufacturing process of a gaming medal.
【図１３】遊技用メダルの情報読取方法を示す図であ
る。FIG. 13 is a diagram showing a method of reading information on gaming medals.
【図１４】磁気センサ出力のタイムチャートである。FIG. 14 is a time chart of the output of the magnetic sensor.
【図１５】この発明の金具を用いたハンドバッグを示す
図である。FIG. 15 is a view showing a handbag using the fitting of the present invention.
【図１６】この発明の物品を用いたハンドバッグを示す
図である。FIG. 16 is a view showing a handbag using the article of the present invention.
【図１７】ハンディタイプの検知器の外観図である。FIG. 17 is an external view of a handy type detector.
１ オーステナイトステンレス綱 ２ 凹部 ４ 平板 １０ 現金交換用特殊景品 １１ 透明ケース １２ 布 ２０ 景品部材 ２１ 景品部材 ２２ 景品部材 ３０ ＭＲセンサ ３１ ＭＲセンサアレイ ４１ 搬送路 ４２ 磁気センサ ４３ メダル中心の軌跡 ５０ 金具 ５１ ステンレス箔 ５２ プローブ ５３ バイアス磁石 ５４ 電池 ５５ 表示部 ５６ スイッチ DESCRIPTION OF SYMBOLS 1 Austenitic stainless steel rope 2 Concave 4 Flat plate 10 Special prize for cash exchange 11 Transparent case 12 Cloth 20 Premium member 21 Premium member 22 Premium member 30 MR sensor 31 MR sensor array 41 Transport path 42 Magnetic sensor 43 Medal center locus 50 Metal fitting 51 Stainless steel Foil 52 Probe 53 Bias magnet 54 Battery 55 Display 56 Switch
Claims (5)
磁性変態を生じる金属を用いて、部分的に強磁性への磁
性変態を生ぜしめ記録を行なうようにしたことを特徴と
する磁性変態金属でなる物品。1. A magnetic transformation metal characterized in that a magnetic transformation from non-magnetic to ferromagnetic due to mechanical deformation is used to perform recording by partially causing a magnetic transformation to ferromagnetism. Article consisting of.
現金交換用特殊景品。2. A special gift for cash exchange using the magnetically transformed metal according to claim 1.
遊技用メダル。3. A game medal using the magnetically transformed metal according to claim 1.
ブランド商品の金具。4. A metal fitting for a brand product using the magnetically transformed metal according to claim 1.
性変態を生じる金属を用いて、部分的に非磁性への磁性
変態を生ぜしめ記録を行なうようにしたことを特徴とす
る磁性変態金属でなる物品5. A magnetic transformation metal, characterized in that a magnetic transformation from ferromagnetic to nonmagnetic by a heat treatment is used to perform recording by partially causing a magnetic transformation to nonmagnetic. Goods