JP2879848B1 - Insulation gas consisting of fluorinated ketone and insulation material filled with it - Google Patents
Insulation gas consisting of fluorinated ketone and insulation material filled with itInfo
- Publication number
- JP2879848B1 JP2879848B1 JP10103610A JP10361098A JP2879848B1 JP 2879848 B1 JP2879848 B1 JP 2879848B1 JP 10103610 A JP10103610 A JP 10103610A JP 10361098 A JP10361098 A JP 10361098A JP 2879848 B1 JP2879848 B1 JP 2879848B1
- Authority
- JP
- Japan
- Prior art keywords
- insulation
- gas
- material filled
- polyol
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
【要約】
【課題】 地球環境への影響が少なく、より断熱性の高
い断熱ガス及びそれを充填した断熱材を提供する。
【解決手段】 下記一般式（１）
【化１】
（式中、ｎは２〜５の数を示し、ｍは０〜２の数を示
し、ｘは１または２の数を示し、ｙは０〜５の数を示
す）で表される含フッ素ケトンからなる断熱ガス及び前
記断熱ガスを充填した断熱材。An object of the present invention is to provide an insulating gas having less influence on the global environment and having higher insulating properties, and an insulating material filled with the same. SOLUTION: The following general formula (1): (Wherein, n represents a number of 2 to 5, m represents a number of 0 to 2, x represents a number of 1 or 2, and y represents a number of 0 to 5). An insulating gas made of ketone and an insulating material filled with the insulating gas.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、複層硝子、ポリオ
レフィンフォーム、硬質ポリウレタンフォーム等の断熱
材に充填する断熱ガス及びそれを充填した断熱材に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heat insulating gas filled in a heat insulating material such as multilayer glass, polyolefin foam, rigid polyurethane foam and the like, and a heat insulating material filled with the same.
【０００２】[0002]
【従来の技術】冷暖房効率向上、消費電力の低減のため
に断熱材が住宅、電気冷蔵庫等に広く使用されている。
断熱の方法として、真空断熱法が挙げられる。これは、
理論上、最も効率の高い断熱法であるが、真空がブレイ
クされると断熱性能が急激に低下するので、頑丈な設備
を要し、一般に重量が増す。もう一つの方法として、気
体の熱伝導率が低く、不活性なガスを断熱材に充填する
方法が挙げられる。具体的には住宅用サッシの複層硝子
の間に断熱ガスを充填する方法や、発泡剤として断熱ガ
スを用い硬質ポリウレタンフォーム中に封入する方法が
ある。従来、ＣＦＣ（クロロフルオロカーボン）、ＨＣ
ＦＣ（ヒドロクロロフルロカーボン）が断熱ガスとして
使用されてきたが、これらの化合物はオゾン層を破壊す
るだけでなく、その化学的に安定な性質のために、大気
寿命が長く地球温暖化を招く。オゾン層を破壊すること
無い断熱ガスとして、ＨＦＣ（ヒドロフルオロカーボ
ン）、例えばＨＦＣ−２４５ｆａ等が提案されている
が、５０℃におけるＨＦＣ−２４５ｆａの気体の熱伝導
率は１３．９ｍＷ／ｍＫであり、ＣＦＣ−１１（９．６
９ｍＷ／ｍＫ）、ＨＣＦＣ−１４１ｂ（１１．８ｍＷ／
ｍＫ）に比べて断熱性能が低い。本発明者らは含フッ素
ケトン類の気体の熱伝導率を測定し、これらの熱伝導率
は（１３．０９から１３．１２ｍＷ／ｍＫ）であり、Ｈ
ＦＣ−２４５ｆａより断熱性能が高いことを示した。し
かし、より断熱性が高く（より気体の熱伝導率が低く）
かつ、オゾン層を破壊しない断熱ガスが望まれている。2. Description of the Related Art Insulating materials are widely used in houses, electric refrigerators and the like for improving cooling and heating efficiency and reducing power consumption.
As a method of heat insulation, there is a vacuum heat insulation method. this is,
Although theoretically the most efficient method of insulation, a break in the vacuum sharply reduces insulation performance, requiring rugged equipment and generally adding weight. Another method is to fill the heat insulating material with an inert gas having a low thermal conductivity. Specifically, there are a method of filling a heat insulating gas between the multi-layer glass of a residential sash and a method of using a heat insulating gas as a foaming agent and enclosing the same in a rigid polyurethane foam. Conventionally, CFC (chlorofluorocarbon), HC
FC (hydrochlorofluorocarbon) has been used as an insulating gas, but these compounds not only destroy the ozone layer, but also have a long atmospheric life and reduce global warming due to their chemically stable properties. Invite. As a heat insulating gas that does not destroy the ozone layer, HFC (hydrofluorocarbon), for example, HFC-245fa has been proposed. CFC-11 (9.6
9mW / mK), HCFC-141b (11.8mW /
mK). The present inventors measured the thermal conductivity of fluorinated ketone gases and found that their thermal conductivity was (13.09 to 13.12 mW / mK).
It showed that the heat insulation performance was higher than FC-245fa. But more adiabatic (lower gas thermal conductivity)
In addition, a heat insulating gas that does not destroy the ozone layer is desired.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、地球環境へ
の影響が少なく、より断熱性の高い断熱ガス及びそれを
充填した断熱材を提供することをその課題とする。SUMMARY OF THE INVENTION It is an object of the present invention to provide a heat insulating gas which has less influence on the global environment and has a higher heat insulating property, and a heat insulating material filled with the gas.
【０００４】[0004]
【課題を解決するための手段】本発明者らは、前記課題
を解決すべく鋭意検討した結果、特定の含フッ素ケトン
化合物は、既存の化合物に比べて気体の熱伝導率が低い
ことを見出し、本発明を完成するに至った。即ち、本発
明によれば、下記一般式（１）Means for Solving the Problems The present inventors have conducted intensive studies to solve the above-mentioned problems, and as a result, have found that a specific fluorine-containing ketone compound has a lower gas thermal conductivity than existing compounds. Thus, the present invention has been completed. That is, according to the present invention, the following general formula (1)
【化１】 （式中、ｎは２〜５の数を示し、ｍは０〜２の数を示
し、ｘは１または２の数を示し、ｙは０〜５の数を示
す）で表される含フッ素ケトンからなる断熱ガスが提供
される。また、本発明によれば、前記断熱ガスを充填し
た断熱材が提供される。Embedded image (Wherein, n represents a number of 2 to 5, m represents a number of 0 to 2, x represents a number of 1 or 2, and y represents a number of 0 to 5). An insulating gas comprising ketone is provided. Further, according to the present invention, there is provided a heat insulating material filled with the heat insulating gas.
【０００５】[0005]
【発明の実施の形態】本発明の断熱ガスを例示すると、
ＣＦ3ＣＦ2ＣＯＣＨＦ2、ＣＦ3ＣＦ2ＣＯＣＨ2Ｆ、ＣＦ
3ＣＦ2ＣＯＣＦ3、ＣＦ3ＣＦ2ＣＯＣＨ2ＣＨ3、ＣＦ3Ｃ
Ｆ2ＣＯＣＨ2ＣＦ3、ＣＦ3ＣＦ2ＣＯＣＨ2ＣＨＦ2、Ｃ
Ｆ3ＣＦ2ＣＯＣＨ2ＣＨ2Ｆ、ＣＦ3ＣＦ2ＣＯＣＨＦＣＨ
3、ＣＦ3ＣＦ2ＣＯＣＨＦＣＨＦ2、ＣＦ3ＣＦ2ＣＯＣＨ
ＦＣＨ2Ｆ、ＣＦ3ＣＦ2ＣＯＣＦ2ＣＨ3、ＣＦ3ＣＦ2Ｃ
ＯＣＦ2ＣＦ3、ＣＦ3ＣＦ2ＣＯＣＦ2ＣＨＦ2、ＣＦ3Ｃ
Ｆ2ＣＯＣＦ2ＣＨ2Ｆ、（ＣＦ3）2ＣＦＣＯＣＨＦ2、
（ＣＦ3）2ＣＦＣＯＣＨ2Ｆ、（ＣＦ3）2ＣＦＣＯＣ
Ｆ3、ＣＦ3ＣＦ（ＣＨＦ2）ＣＯＣＨＦ2、ＣＦ3ＣＦ
（ＣＨＦ2）ＣＯＣＨ2Ｆ、ＣＦ3ＣＦ（ＣＨＦ2）ＣＯＣ
Ｆ3、ＣＦ3ＣＦ（ＣＨ2Ｆ）ＣＯＣＨＦ2、ＣＦ3ＣＦ
（ＣＨ2Ｆ）ＣＯＣＨ2Ｆ、ＣＦ3ＣＦ（ＣＨ2Ｆ）ＣＯＣ
Ｆ3などの化合物が挙げられるが、好ましくはＣＦ3ＣＦ
2ＣＯＣＨ3または（ＣＦ3）2ＣＦＣＯＣＨ3などが挙げ
られる。これらの２種以上の化合物同士を混合して使用
することも可能である。また、所望により、シクロペン
タン、ｎ−ペンタン、ｉｓｏ−ペンタン等の炭化水素、
ＨＦＣ−２４５ｆａ等のハイドロフルオロカーボンを任
意の割合で混合することも可能である。また、その時の
熱伝導率は、概ねそれらの化合物の熱伝導率の加重平均
に等しくなる。BEST MODE FOR CARRYING OUT THE INVENTION As an example of the heat insulating gas of the present invention,
CF 3 CF 2 COCHF 2 , CF 3 CF 2 COCH 2 F, CF
3 CF 2 COCF 3 , CF 3 CF 2 COCH 2 CH 3 , CF 3 C
F 2 COCH 2 CF 3 , CF 3 CF 2 COCH 2 CHF 2 , C
F 3 CF 2 COCH 2 CH 2 F, CF 3 CF 2 COCHFCH
3 , CF 3 CF 2 COCHFCHF 2 , CF 3 CF 2 COCH
FCH 2 F, CF 3 CF 2 COCF 2 CH 3 , CF 3 CF 2 C
OCF 2 CF 3 , CF 3 CF 2 COCF 2 CHF 2 , CF 3 C
F 2 COCF 2 CH 2 F, (CF 3 ) 2 CFCOCHF 2 ,
(CF 3 ) 2 CFCOCH 2 F, (CF 3 ) 2 CFCOC
F 3 , CF 3 CF (CHF 2 ) COCHF 2 , CF 3 CF
(CHF 2 ) COCH 2 F, CF 3 CF (CHF 2 ) COC
F 3 , CF 3 CF (CH 2 F) COCHF 2 , CF 3 CF
(CH 2 F) COCH 2 F, CF 3 CF (CH 2 F) COC
Compounds such as F 3 are mentioned, and preferably CF 3 CF
2 COCH 3 or (CF 3 ) 2 CFCOCH 3 and the like. It is also possible to use a mixture of two or more of these compounds. Also, if desired, hydrocarbons such as cyclopentane, n-pentane and iso-pentane,
It is also possible to mix a hydrofluorocarbon such as HFC-245fa at an arbitrary ratio. Further, the thermal conductivity at that time is approximately equal to the weighted average of the thermal conductivity of those compounds.
【０００６】これらの断熱ガスの断熱材に対する充填圧
力は当業者の所望の圧力で使用可能であるが、常圧近傍
が好ましい。加圧状態の場合は気体の熱伝導率が上が
り、断熱性が下がる。また、過度の減圧状態では断熱材
の強度により、変形することもありうる。また、本発明
の断熱ガスをポリオレフィンフォーム、またはポリウレ
タンフォーム用発泡剤として使用する場合は、本発明者
らは既にこれ以前の出願して示したようにポリオールと
の相溶性を増すためにフッ素系の界面活性剤を使用する
ことも可能である。また、界面活性剤の使用を好まない
場合は発泡直前にこれらのガスを混合し、硬質ウレタン
フォームを製造することも出来る。本発明の断熱剤を用
いて断熱を目的とした硬質ウレタンフォームの製造は、
本発明の断熱ガスを発泡剤として用い、この断熱ガスと
ポリオール、ポリイソシアネート、触媒、水、界面活性
剤、整泡剤を混合、反応させることによって行うことが
できる。[0006] The pressure at which the insulating gas is charged into the insulating material can be any pressure desired by those skilled in the art, but is preferably around normal pressure. In the case of a pressurized state, the thermal conductivity of the gas increases, and the heat insulating property decreases. In an excessively decompressed state, it may be deformed due to the strength of the heat insulating material. When the insulating gas of the present invention is used as a foaming agent for a polyolefin foam or a polyurethane foam, the present inventors have already used a fluorine-based gas to increase the compatibility with a polyol as shown in the earlier application. It is also possible to use surfactants. If the use of a surfactant is not preferred, these gases can be mixed immediately before foaming to produce a rigid urethane foam. Production of rigid urethane foam for heat insulation using the heat insulating agent of the present invention,
It can be performed by using the heat-insulating gas of the present invention as a foaming agent, and mixing and reacting the heat-insulating gas with a polyol, a polyisocyanate, a catalyst, water, a surfactant, and a foam stabilizer.
【０００７】ポリイソシアネートには、芳香族、環状脂
肪族、鎖状脂肪族系のものが包含され、従来一般に使用
されている２官能のものが用いられる。このようなもの
としては、例えば、トリレンジイソシアネート、ジフェ
ニルメタンジイソシアネート、ポリメチレンポリフェニ
ルポリイソシアネート、トリジンジイソシアネート、ナ
フタリンジイソシアネート、ヘキサメチレンジイソシア
ネート、イソホロンジイソシアネート、キシリレンジイ
ソシアネート、水添キシリレンジイソシアネート、ジシ
クロヘキシルメタンジイソシアネート等が挙げられる。
これらのものは単独又は混合物の形で用いられる。The polyisocyanate includes aromatic, cycloaliphatic and linear aliphatic ones, and bifunctional ones conventionally used are generally used. As such, for example, tolylene diisocyanate, diphenylmethane diisocyanate, polymethylene polyphenyl polyisocyanate, tolidine diisocyanate, naphthalene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, xylylene diisocyanate, hydrogenated xylylene diisocyanate, dicyclohexyl methane diisocyanate, etc. Is mentioned.
These are used alone or in the form of a mixture.
【０００８】ポリオールには、ポリエーテル系ポリオー
ル、ポリエステル系ポリオール、多価アルコール、水酸
基含有ジエチレン系ポリマー等が包含されるが、ポリエ
ーテル系ポリオールの使用が好ましい。また、ポリエー
テル系ポリオールを主成分とし、ポリエステル系ポリオ
ール等の他のポリオールを含むポリオールの使用も可能
である。ポリエーテル系ポリオールとしては、ポリプロ
ピレングリコール、ポリテトラメチレングリコール及び
それら変性体の他、糖、多価アルコール、アルカノール
アミン等の活性水素を含む化合物をイニシエータにし
て、これに、プロピレンオキシド、エチレンオキシド、
エピクロルヒドリン、ブチレンオキシド等の環状エーテ
ルを付加したものが好ましく使用される。ポリエステル
系ポリオールには、縮合系ポリエステルポリオール、ラ
クトン系ポリエステルポリオール、ポリカーボネートポ
リオール等が包含される。ポリオールとしては、通常、
その水酸基価が１００〜１０００のものが使用される。The polyol includes a polyether-based polyol, a polyester-based polyol, a polyhydric alcohol, a hydroxyl group-containing diethylene-based polymer, and the like, and the use of a polyether-based polyol is preferred. It is also possible to use a polyol containing a polyether-based polyol as a main component and other polyols such as a polyester-based polyol. Examples of the polyether polyol include, in addition to polypropylene glycol, polytetramethylene glycol and modified products thereof, sugars, polyhydric alcohols, compounds containing active hydrogen such as alkanolamines as initiators, and propylene oxide, ethylene oxide,
Those to which cyclic ethers such as epichlorohydrin and butylene oxide are added are preferably used. The polyester-based polyol includes a condensation-based polyester polyol, a lactone-based polyester polyol, a polycarbonate polyol, and the like. As a polyol, usually
Those having a hydroxyl value of 100 to 1,000 are used.
【０００９】触媒には、有機金属系触媒と有機アミン系
触媒が包含される。有機金属系触媒としては、有機スズ
化合物が好ましく使用され、スタナスオクトエート、ス
タナスラウレート、ジブチル錫ジラウレート、ジブチル
錫ジマレエート、ジブチル錫ジアセテート、ジオクチル
錫ジアセテート等が挙げられる。有機アミン系触媒とし
ては、第３級アミン、例えば、トリエチレンジアミン、
Ｎ−エチルモルホリン、トリエチルアミン、Ｎ，Ｎ，
Ｎ’，Ｎ’−テトラメチルヘキサメチレンジアミン、ビ
ス（２−ジメチルアミノエチル）エーテル、Ｎ，Ｎ’，
Ｎ’−トリエチルエタノールアミン等が挙げられる。The catalyst includes an organometallic catalyst and an organic amine catalyst. As the organometallic catalyst, an organotin compound is preferably used, and examples thereof include stannasoctoate, stannaslaurate, dibutyltin dilaurate, dibutyltin dimaleate, dibutyltin diacetate, and dioctyltin diacetate. Examples of the organic amine catalyst include tertiary amines such as triethylenediamine,
N-ethylmorpholine, triethylamine, N, N,
N ′, N′-tetramethylhexamethylenediamine, bis (2-dimethylaminoethyl) ether, N, N ′,
N'-triethylethanolamine and the like.
【００１０】本発明においては、前記したように、発泡
剤としての含フッ素ケトン化合物の使用との関連で、界
面活性剤としてパーフルオロアルキル基を有する含フッ
素界面活性剤を好ましく用いることができる。発泡剤と
して使用する含フッ素ケトン化合物の表面張力が低いの
で、含フッ素系界面活性剤を用いることによりポリオー
ルに対する発泡剤の相溶性をコントロールすることがで
きる。含フッ素系界面活性剤の使用量は、含フッ素ケト
ン化合物１００重量部当り、０．００１〜１０重量部、
好ましくは０．０１〜５重量部の割合である。含フッ素
系界面活性剤としては、例えば、下記のものが挙げられ
る。 （１）ＲｆＳＯ2ＮＲ−（Ｃ2Ｈ4Ｏ）ｎＨ （２）ＲｆＳＯ2ＮＲ−ＣＨ2ＣＯＯＫ （３）ＲｆＳＯ3Ｍ 前記式中、Ｒｆはパーフルオロアルキル基を示し、Ｒは
アルキル基を示し、ＭはＮＨ4、Ｋ又はＮａを示し、ｎ
は１０〜２の数を示す。In the present invention, as described above, a fluorine-containing surfactant having a perfluoroalkyl group can be preferably used as the surfactant in connection with the use of the fluorine-containing ketone compound as a foaming agent. Since the surface tension of the fluorinated ketone compound used as the foaming agent is low, the compatibility of the foaming agent with the polyol can be controlled by using a fluorinated surfactant. The amount of the fluorinated surfactant used is 0.001 to 10 parts by weight, per 100 parts by weight of the fluorinated ketone compound,
Preferably it is 0.01 to 5 parts by weight. Examples of the fluorinated surfactant include the following. (1) RfSO 2 NR- (C 2 H 4 O) nH (2) RfSO 2 NR-CH 2 COOK (3) RfSO in 3 M wherein formula, Rf represents a perfluoroalkyl group, R represents an alkyl group , M represents NH 4 , K or Na, n
Indicates a number of 10 to 2.
【００１１】発泡剤として用いる含フッ素ケトン化合物
の使用割合は、ポリオール１００重量部当り、５〜５０
重量部、好ましくは１５〜３０重量部であり、このよう
な量の含フッ素ケトン化合物の使用により、２０ｋｇ／
ｍ3以上、特に、３０〜８０ｋｇ／ｍ3の密度を有する硬
質ポリウレタンフォームを得ることができる。原料混合
物の反応温度は、１５〜９０℃、好ましくは２０〜６０
℃、より好ましくは２０〜３５℃である。硬質ポリウレ
タンフォームの製造方法には、従来公知の各種の方法が
包含され、硬質ポリウレタンフォームは、ワンショット
法やプレポリマー法で製造することができる。また、そ
のフォームを得る際の発泡方式としては、現場発泡、ス
ラブ発泡、注入発泡（充填法、モールド法）、ラミネー
ト発泡、スプレー発泡等の各種の発泡方式を採用するこ
とができる。The proportion of the fluorine-containing ketone compound used as a foaming agent is from 5 to 50 per 100 parts by weight of the polyol.
Parts by weight, preferably 15 to 30 parts by weight, and by using such an amount of the fluorine-containing ketone compound, 20 kg /
A rigid polyurethane foam having a density of at least m 3 , in particular 30 to 80 kg / m 3 can be obtained. The reaction temperature of the raw material mixture is 15 to 90 ° C, preferably 20 to 60 ° C.
° C, more preferably 20-35 ° C. Methods for producing a rigid polyurethane foam include various conventionally known methods, and a rigid polyurethane foam can be produced by a one-shot method or a prepolymer method. Further, as a foaming method for obtaining the foam, various foaming methods such as in-situ foaming, slab foaming, injection foaming (filling method, molding method), laminate foaming, and spray foaming can be adopted.
【００１２】[0012]
【実施例】以下、本発明を実施例により、更に詳しく説
明する。The present invention will be described in more detail with reference to the following examples.
【００１３】実施例１ 硝子製コールドフィンガーの通常ドライアイス−メタノ
ール等の寒剤を入れる部分に５０℃の水を２００ｇを入
れ、発泡スチロール製の断熱材でふたをした。そして、
凝縮部に断熱ガスとしてＣＦ3ＣＦ2ＣＯＣＨ3を７５０
ｔｏｒｒ充填した。１時間後、水の温度を測定した結
果、４１℃であった。また、この間の室温は２６．３℃
であった。Example 1 200 g of water at 50 ° C. was put in a portion of a cold finger made of glass in which a cryogen such as dry ice-methanol was usually put, and the glass was covered with a thermal insulating material made of styrene foam. And
750 of CF 3 CF 2 COCH 3 as adiabatic gas in the condensation section
Torr filled. One hour later, the temperature of the water was measured to be 41 ° C. The room temperature during this period was 26.3 ° C.
Met.
【００１４】比較例１ 凝縮部にＣＦ3ＣＦ2ＣＯＣＨ3の代りに空気を７５０ｔ
ｏｒｒ充填した以外実施例１と同様にして実験行った結
果、試験後の水温は３６℃であった。Comparative Example 1 750 t of air was used instead of CF 3 CF 2 COCH 3 in the condensing section.
As a result of conducting an experiment in the same manner as in Example 1 except that orr was filled, the water temperature after the test was 36 ° C.
【００１５】実施例２ ＣＦ3ＣＦ2ＣＯＣＨ3または（ＣＦ3）2ＣＦＣＯＣＨ3か
らなる断熱ガスを発泡剤として用いてポリウレタンフォ
ームを以下のようにして製造した。旭硝子（株）製ポリ
オール３１５：５０重量部、ポリオール４３０：５０重
量部、シリコーン系整泡剤（信越化学（株）製Ｆ−３３
８）：２部、水：０．５部、三菱マテリアル（株）製非
イオン系含フッ素界面活性剤ＥＦ−８０２：０．１５
部、同ＥＦ−１２２Ａ：０．０５部、ＥＦ−１２２Ｃ：
０．０５部、Ｎ，Ｎ−ジメチルシクロヘキシルアミンを
ゲルタイム４５秒とするための必要量、断熱ガスをコア
密度２７〜３３ｋｇ／ｍ3になるための必要量からなる
混合液とＭＤ化成（株）製ポリメチレンポリフェニルイ
ソシアネートＰＡＩ１３５：１１０部を激しく混合し、
２００×３００×１８０ｍｍの木製の鋳型に投入し、得
られた発泡体の熱伝導率を測定した。その結果を表１に
示す。Example 2 A polyurethane foam was produced as follows using an insulating gas comprising CF 3 CF 2 COCH 3 or (CF 3 ) 2 CFCOCH 3 as a foaming agent. Asahi Glass Co., Ltd. polyol 315: 50 parts by weight, polyol 430: 50 parts by weight, silicone-based foam stabilizer (Shin-Etsu Chemical Co., Ltd. F-33)
8): 2 parts, water: 0.5 part, non-ionic fluorinated surfactant EF-802 manufactured by Mitsubishi Materials Corporation: 0.15
Part, EF-122A: 0.05 part, EF-122C:
A liquid mixture comprising 0.05 parts, a necessary amount of N, N-dimethylcyclohexylamine for a gel time of 45 seconds, and a necessary amount of an adiabatic gas for a core density of 27 to 33 kg / m 3 , and MD Kasei Co., Ltd. Violently mix 110 parts of polymethylene polyphenylisocyanate PAI135 manufactured by
The obtained foam was put into a 200 × 300 × 180 mm wooden mold, and the thermal conductivity of the obtained foam was measured. Table 1 shows the results.
【００１６】[0016]
【表１】 ────────────────────────────── 断熱ガス 発泡体の熱伝導率（ｍＷ／ｍＫ） ────────────────────────────── ＣＦ3ＣＦ2ＣＯＣＨ3 ２１．０９ （ＣＦ3）2ＣＦＣＯＣＨ3 ２１．１２ ──────────────────────────────[Table 1] 断 熱 Thermal insulation foam thermal conductivity (mW / mK) ─── ─────────────────────────── CF 3 CF 2 COCH 3 21.09 (CF 3) 2 CFCOCH 3 21.12 ──── ──────────────────────────
【００１７】[0017]
【発明の効果】本発明の断熱ガスは、高い断熱性を有す
るとともに、その毒性も極めて低く、人体に対する安全
性も非常に高いものである。本発明の断熱性ガスはオゾ
ン層破壊を生じないという大きな特徴を有するものであ
る。The heat-insulating gas of the present invention has high heat-insulating properties, extremely low toxicity, and very high safety to the human body. The heat-insulating gas of the present invention has a great feature that ozone layer destruction does not occur.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 関屋 章 茨城県つくば市東１丁目１番 工業技術 院物質工学工業技術研究所内 審査官 鈴木 恵理子 (58)調査した分野(Int.Cl.6，ＤＢ名) C09K 5/00 C08J 9/14 C08K 5/07 C09K 3/00 C07C 49/167 ＣＡ（ＳＴＮ) ＲＥＧＩＳＴＲＹ（ＳＴＮ)────────────────────────────────────────────────── ─── of the front page continued (72) inventor Akira Sekiya Higashi, Tsukuba, Ibaraki 1 chome industrial technology Institute substance Institute of Advanced industrial Science and technology in the examiner Eriko Suzuki (58) investigated the field (Int.Cl. 6, DB name ) C09K 5/00 C08J 9/14 C08K 5/07 C09K 3/00 C07C 49/167 CA (STN) REGISTRY (STN)
Claims (3)
し、ｘは１または２の数を示し、ｙは０〜５の数を示
す）で表される含フッ素ケトンからなる断熱ガス。[Claim 1] The following general formula (1) (Wherein, n represents a number of 2 to 5, m represents a number of 0 to 2, x represents a number of 1 or 2, and y represents a number of 0 to 5). Insulating gas made of ketone.
Ｈ3及び／又は（ＣＦ3）2ＣＦＣＯＣＨ3である請求項１
の断熱ガス。2. The fluorinated ketone is CF 3 CF 2 COC.
H 3 and / or claim 1 (CF 3) is 2 CFCOCH 3
Insulation gas.
熱材。3. A heat insulating material filled with the heat insulating gas according to claim 1.