JP2834615B2 - Antioxidant coating with electrical conductivity for electric furnace electrodes - Google Patents
Antioxidant coating with electrical conductivity for electric furnace electrodesInfo
- Publication number
- JP2834615B2 JP2834615B2 JP4096785A JP9678592A JP2834615B2 JP 2834615 B2 JP2834615 B2 JP 2834615B2 JP 4096785 A JP4096785 A JP 4096785A JP 9678592 A JP9678592 A JP 9678592A JP 2834615 B2 JP2834615 B2 JP 2834615B2
- Authority
- JP
- Japan
- Prior art keywords
- electric furnace
- electrical conductivity
- electrode
- function
- coating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、電気炉電極の高熱によ
る酸化を防止するコーティング剤に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coating agent for preventing oxidation of an electric furnace electrode due to high heat.
【０００２】[0002]
【従来の技術】従来、電気炉の電極としては、棒状に形
成した黒鉛を使用しており、同電極を電極ホルダーを介
して通電することにより放熱させて製鋼するようにして
いるが、同電極が高熱により酸化されるために、この酸
化を防止するために、同電気炉電極の表面にコーティン
グ剤を塗布することが行なわれている。2. Description of the Related Art Conventionally, rod-shaped graphite has been used as an electrode of an electric furnace, and the electrode is energized through an electrode holder to radiate heat to produce steel. Is oxidized by high heat, and to prevent this oxidation, a coating agent is applied to the surface of the electric furnace electrode.
【０００３】そして、かかるコーティング剤としては、
例えば、特開昭60-118762 号公報に記載されたものがあ
る。[0003] As such a coating agent,
For example, there is one described in JP-A-60-118762.
【０００４】すなわち、このコーティング剤は、炭化珪
素と、熱放射助材及びバインダーと、密着性や塗膜間結
合強度を高める添加剤と、金属粉と、焼結助剤混合物
と、融点降下剤とからなるものであり、電気炉電極の表
面に塗布した際には、高い密着性と気密性のある焼成被
覆層を形成して、電気炉電極の酸化を防止することがで
きるものである。That is, this coating agent is composed of silicon carbide, a heat radiation aid and a binder, an additive for improving adhesion and bonding strength between coatings, a metal powder, a sintering aid mixture, and a melting point depressant. When applied to the surface of an electric furnace electrode, a fired coating layer having high adhesion and airtightness can be formed to prevent oxidation of the electric furnace electrode.
【０００５】[0005]
【発明が解決しようとする課題】ところが、上記したコ
ーティング剤の場合、通電性がないために、いまだ次の
ような問題点を有していた。However, the above-mentioned coating agent still has the following problems due to lack of electrical conductivity.
【０００６】すなわち、電気炉電極には、電極ホルダー
を通して通電しているために、前もって電気炉電極の全
周面にコーティング剤を塗布することはできず、そのた
めに、電極ホルダーに電気炉電極を把持させた後にコー
ティング剤を塗布しなければならないが、この場合に
は、電気炉電極の周面に塗布することが困難で、正面側
半面しか塗布できず、確実な酸化防止効果が得られない
という問題があった。That is, since the electric furnace electrode is energized through the electrode holder, it is not possible to apply a coating agent on the entire peripheral surface of the electric furnace electrode in advance. The coating agent must be applied after being gripped, but in this case, it is difficult to apply the coating agent to the peripheral surface of the electric furnace electrode, and only the front half surface can be applied, and a reliable antioxidant effect cannot be obtained. There was a problem.
【０００７】[0007]
【課題を解決するための手段】そこで、本発明では、発
熱抵抗体としての機能と焼結機能とを有する炭化ケイ素
と、通電性を付与するモリブデンと黒鉛との混合物と、
耐水性を付与するコロイダルシリカとを配合してなる電
気炉電極の通電性を有する酸化防止用コーティング剤を
提供せんとするものである。Therefore, according to the present invention, silicon carbide having a function as a heating resistor and a sintering function, a mixture of molybdenum and graphite for providing electrical conductivity,
An object of the present invention is to provide an antioxidant coating agent having electric conductivity for an electric furnace electrode, which is formed by blending with water-resistant colloidal silica.
【０００８】また、さらに、焼結を促進する機能を有す
るガラス粉及び／又は二酸化ケイ素を配合してなること
にも特徴を有する。Further, the present invention is characterized in that glass powder and / or silicon dioxide having a function of accelerating sintering are blended.
【０００９】ここで、(a) 炭化ケイ素は、５〜４０重量
％使用することができ、発熱抵抗体（熱を発散させやす
い）としての機能と、焼結機能とを有する。Here, (a) silicon carbide can be used in an amount of 5 to 40% by weight, and has a function as a heating resistor (dissipating heat easily) and a sintering function.
【００１０】(b) 通電性を付与するモリブデンは、５〜
３０重量％使用することができ、また、通電性を付与す
る黒鉛は、５〜６０重量％使用することができる。(B) Molybdenum for imparting electrical conductivity is 5 to 5.
30% by weight can be used, and 5 to 60% by weight of graphite for imparting electrical conductivity can be used.
【００１１】(c) 耐水性剤を付与するコロイダルシリ
カ、アルミナゾル、又はジルコニアゾルは、それぞれ１
０〜８０重量％使用することができ、これらコロイダル
シリカやアルミナゾルやジルコニアゾルは結合剤として
も機能する。(C) Colloidal silica, alumina sol or zirconia sol for imparting a water-resistant agent is 1
The colloidal silica, alumina sol or zirconia sol can also function as a binder.
【００１２】(d) 焼結を促進するガラス粉５〜５０重量
％と二酸化ケイ素５〜５０重量％とを配合して使用する
ことができ、これらにより酸化防止用コーティング剤自
体を低温（７０〜１７００℃）で結合させて、塗膜間強
度を高めることができる。(D) 5 to 50% by weight of glass powder for promoting sintering and 5 to 50% by weight of silicon dioxide can be blended and used. 1700 ° C.) to increase the intercoat strength.
【００１３】(e) 分散剤としては、メチルセルローズナ
トリウム１〜５重量％とケイ酸アルミニウム２〜１０重
量％とを配合して使用することができる。(E) As a dispersant, 1 to 5% by weight of sodium methylcellulose and 2 to 10% by weight of aluminum silicate can be used in combination.
【００１４】(f) 被覆して酸化防止機能を付与する酸化
亜鉛は、１０〜６０重量％使用することができ、かかる
被覆物により間隙を埋めて隠蔽状態にすることにより、
酸化防止機能を高めることができる。(F) Zinc oxide which is coated to provide an antioxidant function can be used in an amount of 10 to 60% by weight.
The antioxidant function can be enhanced.
【００１５】(g) 通電性を補足する安定化ジルコニア粉
５〜４０重量％とチタン酸バリウム１〜３０重量％とを
配合して使用することができ、これらにより、耐熱性強
度を良好に確保することができる。(G) 5 to 40% by weight of stabilized zirconia powder and 1 to 30% by weight of barium titanate, which are used for supplementing the electrical conductivity, can be used in combination. can do.
【００１６】(h) 耐熱・耐食のための酸化アルミニウム
を５〜５０重量％、又は、酸化ジルコニアを５〜５０重
量％使用することができる。(H) 5 to 50% by weight of aluminum oxide or 5 to 50% by weight of zirconia for heat and corrosion resistance can be used.
【００１７】[0017]
【発明の効果】本発明によれば、次のような効果が得ら
れる。According to the present invention, the following effects can be obtained.
【００１８】 本発明に係る酸化防止用コーティング
剤を電気炉電極の表面に塗布した場合には、同コーティ
ング剤中の炭化ケイ素により、高い密着性と気密性のあ
る焼成被覆層を形成することができて、電気炉電極の酸
化を確実に防止することができると共に、モリブデンと
黒鉛との混合物を配合しているために、上記焼成被覆層
に通電性をもたせることができ、従って、電気炉電極を
電極ホルダーに把持させる前に、かかるコーティング剤
の塗布作業を楽に行なうことができる。When the antioxidant coating agent according to the present invention is applied to the surface of the electrode of an electric furnace, the fired coating layer having high adhesion and airtightness can be formed by silicon carbide in the coating agent. As a result, oxidation of the electric furnace electrode can be reliably prevented, and since the mixture of molybdenum and graphite is blended, the fired coating layer can be provided with electrical conductivity. The coating operation of the coating agent can be easily performed before the electrode holder is held by the electrode holder.
【００１９】そして、コロイダルシリカも配合している
ために、散水を受けた場合にも耐水性を良好に保つこと
ができて、焼成被覆層の破壊を防止することができる。Further, since colloidal silica is also contained, water resistance can be kept good even when water is sprinkled, and breakage of the fired coating layer can be prevented.
【００２０】 ガラス粉及び／又は二酸化ケイ素を配
合した場合には、塗膜間強度を高めることができるため
に、より酸化防止効果を高めることができる。When glass powder and / or silicon dioxide is blended, the strength between the coating films can be increased, so that the antioxidant effect can be further enhanced.
【００２１】[0021]
【実施例】以下、本発明の実施例を説明する。Embodiments of the present invention will be described below.
【００２２】[0022]
【表１】 [Table 1]
【００２３】表１は、本発明の一実施例としての酸化防
止用のコーティング剤の成分配合割合を示している。Table 1 shows the component mixing ratio of the antioxidant coating agent as one embodiment of the present invention.
【００２４】表１で製造した酸化防止用コーティング剤
を２０インチの径を有する電気炉電極の全周面にエアー
スプレーにて800g／ｍ2 の割合で塗布し、常温にて３時
間乾燥後、酸化消耗の激しい層、すなわち、三層ある内
の酸化吹込み側に使用してみた。The antioxidant coating agent prepared in Table 1 was applied to the entire periphery of an electric furnace electrode having a diameter of 20 inches by air spray at a rate of 800 g / m 2 and dried at room temperature for 3 hours. It was used on the layer with high oxidation consumption, that is, on the oxidation blowing side among three layers.
【００２５】なお、電極の消耗度を平均値でみる為、酸
化消耗の激しい層に１０本使用し、電極の原単位を調査
した。In order to determine the average degree of electrode wear, ten electrodes were used in a layer where oxidative consumption was severe, and the basic unit of the electrode was examined.
【００２６】[0026]
【数１】 (Equation 1)
【００２７】１０本の電気炉電極の使用後の電極の原単
位で、約１０％の電極原単位が引き下げられた。After the use of the ten electric furnace electrodes, the basic unit of the electrode was reduced by about 10%.
【００２８】他の電極層についても１１〜１５％の電極
原単位の引き下げ効果が認められた。With respect to the other electrode layers, an effect of reducing the basic unit of the electrode by 11 to 15% was observed.
【００２９】また、電極ホルダーより下方に位置する電
気炉電極の１．６ｍ内では、酸化防止用コーティング剤
による塗膜の剥離はまったく見られず、散水による塗膜
の破壊についても皆無であった。Further, within 1.6 m of the electric furnace electrode located below the electrode holder, no peeling of the coating film due to the antioxidant coating agent was observed at all, and there was no destruction of the coating film due to water spraying. .
フロントページの続き (58)調査した分野(Int.Cl.6，ＤＢ名) C09D 5/24 C09D 1/00 C09D 5/08 C04B 41/87Continuation of front page (58) Field surveyed (Int.Cl. 6 , DB name) C09D 5/24 C09D 1/00 C09D 5/08 C04B 41/87
Claims (2)
有する炭化ケイ素と、 通電性を付与するモリブデンと黒鉛との混合物と、 耐水性を付与するコロイダルシリカとを配合してなる電
気炉電極の通電性を有する酸化防止用コーティング剤。 1. A function as a heating resistor and a sintering function.
Comprising silicon carbide, a mixture of molybdenum and graphite for providing electrical conductivity, and colloidal silica for providing water resistance.
An antioxidant coating agent having electrical conductivity for the furnace electrode.
ラス粉及び／又は二酸化ケイ素を配合してなる請求項１
記載の電気炉電極の通電性を有する酸化防止用コーティ
ング剤。2. A gas having a function of accelerating sintering.
2. A composition comprising a lath powder and / or silicon dioxide.
Oxidation-preventive coating for electric furnace electrodes
Agent .