JP2822301B2 - Simulated bait made of konjac and method for producing the same - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a konjac artificial bait used for fishing and a method for producing the same.

[0002]

2. Description of the Related Art The inventor of the present invention has previously filed a patent application for the same kind of artificial bait and a method for producing the same. (Japanese Patent Application No. 4-287031) Since this invention is an improvement of the above-mentioned invention, the above-mentioned invention will be described first.

The artificial konjac bait is described by mixing a predetermined amount of gelatin as a reinforcing material into konjac mannan and pressing the mixture into a mold such as an insect to form a pseudo bait. The artificial bait formed in this way can eliminate the danger of death if a bird or the like accidentally eats it by leaving it on a riverbank or seaside when it is no longer needed. For this reason, for synthetic resin artificial bait,
Can solve problems raised by bird conservation groups. Also, when left on a riverbank, a seaside, or the like, it corrodes and returns to the soil, so that there is an effect that the fear of pollution can be eliminated.

[0004]

However, the artificial bait according to the present invention has the following disadvantages. That is, when this artificial bait is attached to a needle, and the fishing rod is thrown toward the surface of the water with a fishing rod as usual, the artificial bait is broken in the air and scatters away from the needle.

[0005] This is because the artificial bait breaks in the air from the portion where the needle is put, and the rift immediately spreads throughout,
They are torn apart and scatter. The present invention has been made in order to solve the above-mentioned problems, and its purpose is to attach a fishing hook, shake a rod and throw it toward the surface of the water, and the konjac will not be torn away from the needle. And a method of producing the same.

[0006]

Means for Solving the Problems In order to achieve the above object, the present invention first describes a konjac artificial bait, which is composed of konjac mannan, an edible paste material and
It is composed of an edible alkaline agent , is formed in the shape of a living thing , and
It is formed by releasing water in a dry state.
When shaking the rod and throwing it toward the surface of the water,
Formed to a tear strength that is not broken by shearing forces
It is a fake bait made of konjac characterized by that.

Next, the production method will be described. The konjac mannan, the edible paste material and water are mixed and stirred, an edible alkali agent is added to the mixture, and the mixture is solidified. Formed into a shape , then this shape
The growth was allowed to syneresis semi dry form, by該離water, which the hook
Attach the fishing rod to the surface of the water
Shaped to tear strength that is not broken by the shear force generated by the needle
A method for producing konjac-made lure, characterized in that the formed. Separation is a method for producing the artificial konjac bait, which is performed by freezing.

[0008]

The artificial bait of the present invention is constituted as described above, and contains edible sizing material in konjac mannan and is given a semi-dry state of water to give appropriate elasticity and sufficient tear strength. As a result, even if the artificial bait is attached to the needle, and the rod is shaken and thrown onto the water surface, the dummy bait is not torn apart from the needle and splattered as in the conventional case, and can be thrown into the water with the needle attached.

Next, the operation of the manufacturing method will be described.
Mix and stir konjac mannan, edible sizing material and water. In this case, mixing is performed well. Then, an edible alkali agent, for example, an aqueous solution of calcium hydroxide is added thereto to coagulate.

Next, the solidified mixture is molded using a mold such as an aquatic insect or a frog, and then, as an example of water separation, the mixture is frozen and thawed. Then the above
Konjac mannan has a strong tear strength by separating water in a semi-dry state and containing an edible glue to the extent that it retains appropriate elasticity, and this artificial bait has elasticity as a dummy bait. A tear strength is obtained that is not broken by a fishhook moving rapidly in the air.

[0011]

[Example] Konjac mannan (konjac fine powder) 1 k
g and edible sizing material 1 kg to 20 kg and water about 10 kg to 5 g
0 kg and stirred. In this case, as the edible paste material, starch paste, gluten, vegetable protein, arabic gum, or any other suitable material may be used, but starch paste was used as an example.

Next, as an example of an edible alkaline agent, a 2% aqueous solution of calcium hydroxide 0.1% is added to the above mixed solution. 1 kg ~
0. 5 kg are added, whereby the mixture solidifies. The edible alkaline agent may be appropriately replaced with other edible alkaline agents such as sodium bicarbonate or the like.

Next, the mixed solution solidified as described above is put into a mold simulating the shape of an insect or other living thing, and molded. In this case, as an example, a worm and frog shape was formed.
And what was formed in this way was -10 ° C to -2.
Freeze in a freezer at 0 ° C and thaw. Then the konjac mannan releases water and separates in a semi-dry state,
Having appropriate elasticity and sufficient tear strength by the edible glue material, it can be stuck on a fishing hook and attached, and even if the rod is shaken and thrown from the air to the surface of the water, it will be broken off on the way and separated from the needle A fake bait was obtained.

The water separation may be carried out by drying. That is, water is separated by forced drying. However
In terms of the elasticity of konjac mannan, it is preferable to use water separation by freezing because it does not cause unnecessary water separation.

The konjac artificial bait produced as described above is very similar in elasticity and hardness to the actual target insect, and can be made close to the real insect. Next, the above-mentioned artificial bait was manufactured by the following prescription as another example. First, 17.5 kg of potato starch is added to 3.5 kg of konjac fine powder, and 100 liters of water is added thereto, followed by mixing and stirring. Next, in advance, 175 g of calcium hydroxide (5% of konjac fine powder in 10 liters of water,
This advance to form an aqueous solution by adding it may) Re der about 3-10%, was coagulated by adding to a mixture of the refined Konjac flour and potato starch and water. Subsequent steps are the same as in the above method.

[0016]

The artificial konjac bait according to the present invention is constituted as described above, and is formed in a semi-dry state by separating water.
The pulling strength was urged by swinging the fishing rod
The strength of the fishhook to prevent it from breaking
Therefore , when the fishing rod is shaken, it can be prevented from being separated from the hook and scattered .

Moreover, even if the artificial bait is left on the riverside, on the beach, etc., it rots and returns to the soil.
It can also solve the problems raised by bird protection groups.

Claims (3)

(57) [Claims] (1) Konjac mannan and edible paste material and
It is composed of an edible alkaline agent , is formed into the shape of a living thing, and
Formed by water separation in a semi-dry form, by該離water, dipped in hook
When the fishing rod is thrown toward the surface of the water
Formed to a tear strength that is not broken by shearing forces
A konjac artificial bait that is characterized by being used . 2. A mixture of konjac mannan, an edible paste material, and water , which are mixed and stirred, an edible alkali agent is added to the mixture, and the mixture is solidified. The solidified mixture is formed into an appropriate organism.
Later to syneresis the formation semi dry form, by該離water, this
Attach it to the hook and shake the fishing rod and throw it toward the surface of the water
A tear which is not broken by the shear force generated in the fishhook.
A method for producing a simulated bait made of konjac, characterized in that it is formed with high strength . 3. The method according to claim 2, wherein the water separation is performed by freezing.