JP2769596B2 - Detergent composition - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to a detergent composition containing an inorganic ion exchanger and / or a hydrate thereof. More specifically, it contains an inorganic ion exchanger and / or a hydrate thereof having excellent ion exchange ability and alkali ability and having water resistance, has excellent caking resistance under moisture absorption, and has a powder or granular form having no decrease in bulk density. The present invention relates to a cleaning composition.

[0002]

2. Description of the Related Art Builders to be added to detergents have a large number of chelating agents to date.
Builders, precipitants, dispersants and the like have been reported. recent years,
The use of tripolyphosphate has been reduced due to concerns about eutrophication in closed water bodies such as lakes and marshes, and crystalline aluminosilicates represented by JP-A-50-12381 and JP-A-51-12805 are disclosed. Is often used.

[0003] Sodium silicate has an ion exchange capacity higher than that of zeolite, but its use has been limited because it dissolves in water. As a means for solving the problem, Japanese Unexamined Patent Publication No. Sho 60-239320 discloses a method in which sodium silicate is heated, dehydrated and calcined to obtain a powder. In the same manner, a part of silicon of sodium silicate is isomorphically substituted with aluminum. Although the method is disclosed in JP-A-3-93649,
Both have insufficient water resistance and low ion exchange capacity. Also, a crystalline calcium silicate alkali hydrate obtained by hydrothermal synthesis is disclosed in Japanese Patent Publication No. 61-59245, which has sufficient water resistance, but low ion exchange capacity, and substantially detergent. Not suitable as a builder. Further, since the particle shape is coarse long fiber or mica, the dispersibility in water is poor, and the substantial ion exchange ability is further reduced. In addition, DD-279234A1 discloses a crystalline magnesium-containing silicate obtained by hydrothermal synthesis. However, it is pointed out that the ion-exchange ability is extremely low and cannot be applied practically as a builder for a detergent. I have.

[0004] These crystalline silicates can be classified on the basis of their structure according to the classification by anion form (Friedrich Liebau, "St.
structural Chemistry of Sil
icates "p72, Springer-Verla
g, 1985). That is, for example, the 4A type zeolite represented by the composition of Na ₂ O.Al ₂ O ₃ .2SiO ₂ which is a typical inorganic builder has a tectosilicate structure in which a part of Si is isomorphically substituted with A1. ₂ O ・ 2Si
Dimetasilicate (layered silicate) represented by the composition of O ₂ is classified into a phyllosilicate structure. Furthermore, Ca
Metasilicate (pyroxene, Diopside) and Na ₂ having a composition of O.MgO.2SiO ₂ .nH ₂ O
Metasilicate (sodium metasilicate) represented by the composition of O.SiO ₂ is classified into an inosilicate (polysilicate) structure.

More specifically, it can be classified by the number of cross-linking oxygen (Si-O-Si) of oxygen bonded to Si, and the number of cross-linking oxygen is 4, 3, 2, 1, 0, respectively. _{Q 4, Q 3, Q 2} , Q 1, is classified into Q ₀ units (Y.Tsunawaki, N.Iwamoto, T.
Hattori and A. Mitsubishi,
J. Non-Cryst. Solids, vol44,
p369 (1981)). In the case of the tectosilicate structure, since the number of cross-linking oxygen is 4, only Q ₄ units are used. In the case of the phyllosilicate structure, since the number of cross-linking oxygen is 3, Q _{3 is used.}
The unit only if the Inokei salt structure number crosslinking oxygen is formed from only or Q ₂ units and Q ₃ units Q ₂ units because it is 2.0 to 2.5. Here, silicate consisting of Q ₂ units only, silicate containing at least Q ₂ units as silicate consisting of Q ₂ units and Q ₃ unit is said to be a chain-like structure or band structure. By contrast, silicate consisting of Q ₃ units only are said to be laminar structure, both are structurally clearly distinguished.

According to these classifications, looking at the above-mentioned silicate compounds which are inorganic builders used in detergents,
4A-type zeolite having a tectosilicates structure formed from Q ₄ units, while indicating theoretically high cation exchange capacity, the dispersibility in water is a limited amount of the poor detergents. As the layered silicate with a phyllosilicate structure formed from Q ₃ units, the JP 60-239320 JP like, JP-A-3-936
No. 49, which are excellent in dispersibility in water as described above due to their hydration properties, but conversely, the amount of dissolution in water is large, and the cation exchange capacity is 4A type. It is smaller than zeolite and is insufficient as a builder for detergents.

On the other hand, pyroxene having an inosilicate structure composed of Q ₂ units shows almost no cation exchange ability and is insufficient as an inorganic builder. In addition, a composition (Na ₂ O ·
SiO ₂ ) exists as a crystalline metasilicate,
Since its solubility in water is remarkable and its structure is destroyed,
The actual cation exchange capacity is extremely low and is not suitable as an inorganic builder. As described above, it is difficult to obtain an inorganic builder excellent in both water resistance and ion exchange ability, and the development of an inorganic builder improved in these is required.

On the other hand, in recent years, the concentration of the detergent has been increased in order to pursue the convenience of the user of the detergent, and the builder used for the detergent has only an ion exchange ability such as crystalline aluminosilicate. There is a need in the art for a multifunctional one suitable for concentrating a detergent formulation instead of a single functional one. That is, since the inorganic builder has excellent functions such as an ion exchange ability, an alkalinity adjusting ability, and a buffering effect, it is possible to concentrate the detergent composition containing the inorganic builder.

The present inventors have previously studied a detergent composition suitable for concentration using an inorganic ion exchanger having excellent ion exchange ability and alkali ability and having water resistance. However, when the inorganic ion exchanger was stored under high humidity, there was a tendency that the anti-caking property and the flowability of the detergent powder were reduced, and further the bulk density was lowered, and further improvement was required.

[0010]

Under these circumstances, the present inventors have intensively studied the storage stability of a detergent using an inorganic ion exchanger having excellent ion exchange ability and alkali ability and having water resistance. As a result, the present inventors have found that by suppressing the amount of sodium carbonate or potassium carbonate used as an alkali agent, excellent caking resistance and no reduction in bulk density are obtained even under moisture-absorbing storage, and the present invention has been completed.

That is, the gist of the present invention relates to a detergent composition comprising the following components. (A) a surfactant, 10 to 60 wt% (b) general _{formula, xM 2 O · ySiO 2 ·} zMe m O n ( where, M is a Group Ia element of the hydrogen or the periodic table, Me represents the periodic table IIa , IIb, IIIa, IVa or VIII element, y / x = 0.5-2.0, z / x = 0.005-
1.0, n / m = 0.5 to 2.0. A) a synthetic crystalline silicate having a composition represented by the formula (1), having an ion exchange capacity of at least 100 mg CaCO ₃ / g or more;
0% by weight (c) Na ₂ CO ₃ and / or K ₂ CO ₃ , 5% by weight or less

The surfactant (a) used in the present invention is not particularly limited as long as it is generally used in detergents. Specifically, it is at least one selected from the group consisting of an anionic surfactant, a nonionic surfactant, a cationic surfactant and an amphoteric surfactant exemplified below. For example, the same kind may be selected only when a plurality is selected from anionic surfactants, or various kinds such as when each is selected from an anionic surfactant and a nonionic surfactant. May be selected plurally.

(1) Examples of the anionic surfactant include the following. 1) A linear or branched alkylbenzene sulfonate having an alkyl group having an average of 10 to 16 carbon atoms. 2) having a linear or branched alkyl or alkenyl group having an average of 10 to 20 carbon atoms, and having an average of 0.5 to 8 mol of ethylene oxide, propylene oxide, butylene oxide or ethylene oxide / molecule in one molecule;
Propylene oxide = 0.1 / 9.9-9.9 / 0.1 ratio or ethylene oxide / butylene oxide =
Alkyl or alkenyl ether sulfates added in a ratio of 0.1 / 9.9 to 9.9 / 0.1.

3) An alkyl or alkenyl sulfate having an alkyl or alkenyl group having an average of 10 to 20 carbon atoms. 4) Olefin sulfonic acid salts having an average of 10 to 20 carbon atoms in one molecule. 5) Alkane sulfonates having an average of 10 to 20 carbon atoms in one molecule. 6) A saturated or unsaturated fatty acid salt having an average of 10 to 24 carbon atoms in one molecule. 7) having an alkyl group or alkenyl group having an average of 10 to 20 carbon atoms, and having an average of 0.5 to 8 mol of ethylene oxide, propylene oxide or butylene oxide or ethylene oxide / propylene oxide in a molecule = 0.1 / 9.9 to 9.9 / 0.1 Or ethylene oxide / butylene oxide = 0.1 / 9.9 to 9.9 /
Alkyl or alkenyl ether carboxylate added in a ratio of 0.1. 8) α-Sulfo fatty acid or ester represented by the following formula.

[0015]

Embedded image

(Wherein Y represents an alkyl group or counter ion having 1 to 3 carbon atoms, Z represents a counter ion, and R represents an alkyl group or alkenyl group having 10 to 20 carbon atoms.)

Here, the counter ion of the anionic surfactant is an alkali metal ion such as sodium or potassium,
Alkaline earth metal ions such as calcium and magnesium; ammonium ions; and alkanolamines having 1 to 3 alkanol groups having 2 or 3 carbon atoms (eg, monoethanolamine, diethanolamine, triethanolamine, triisopropanolamine, etc.). Can be.

9) An amino acid type surfactant represented by the following general formula. No. 1

[0019]

Embedded image

(Where R ₁ is an alkyl or alkenyl group having 8 to 24 carbon atoms, R ₂ is hydrogen or an alkyl group having 1 to 2 carbon atoms, R ₃ is an amino acid residue, X is an alkali metal or an alkali metal. No. 1 represents an earth metal ion.) 2

[0021]

Embedded image

(R ₁ , R ₂ and X are as described above, and n is an integer of 1 to 5.) 3

[0023]

Embedded image

(R ₁ and X are as described above. M is 1 to 8)
Indicates an integer. ) No. 4

[0025]

Embedded image

(R ₁ , R ₃ and X are as described above. R ₄
Represents hydrogen or an alkyl or hydroxyalkyl group having 1 to 2 carbon atoms. ) No. 5

[0027]

Embedded image

(R ₂ , R ₃ and X are as described above. R ₅
Represents a β-hydroxyalkyl or β-hydroxyalkenyl group having 6 to 28 carbon atoms. ) No. 6

[0029]

Embedded image

(R ₃ , R ₅ and X are as described above.)

10) Phosphate-based activators. No. 1 Alkyl (or alkenyl) acid phosphates

[0032]

Embedded image

(R ′ is an alkyl group or alkenyl group having 8 to 24 carbon atoms, n ′ + m ′ = 3, n ′ = 1 to 2) 2 Alkyl (or alkenyl) phosphate

[0034]

Embedded image

(R ′ is, as described above, n ″ + m ″ = 3,
n ″ = 1 to 3) No. 3 alkyl (or alkenyl) phosphate ester salt

[0036]

Embedded image

(R ', n "and m" are as described above, and M is N
a, K, Ca)

(2) Examples of the nonionic surfactant include the following. 11) Polyoxide ethylene alkyl or alkenyl ether having an alkyl group or alkenyl group having an average of 10 to 20 carbon atoms and having 1 to 20 mol of ethylene oxide added thereto. 12) Polyoxyethylene alkylphenyl ether having an alkyl group having an average of 6 to 12 carbon atoms and having 1 to 20 mol of ethylene oxide added thereto. 13) Polyoxypropylene alkyl or alkenyl ether having an alkyl or alkenyl group having an average of 10 to 20 carbon atoms and having 1 to 20 mol of propylene oxide added thereto.

14) Polyoxybutylene alkyl or alkenyl ether having an alkyl or alkenyl group having an average of 10 to 20 carbon atoms and having 1 to 20 mol of butylene oxide added thereto. 15) Nonionic activators (ethylene oxide and propylene oxide) having an alkyl group or alkenyl group having an average of 10 to 20 carbon atoms and having a total of 1 to 30 moles of propylene oxide of ethylene oxide or ethylene oxide and butylene oxide added. Or, the ratio to butylene oxide is 0.1 / 9.9 to 9.9 / 0.1).

16) A higher fatty acid alkanolamide represented by the following general formula or an alkylene oxide adduct thereof.

[0041]

Embedded image

[0042] (wherein, R _^'11 is an alkyl group, or an alkenyl group having 10 to 20 carbon atoms, ^R' ₁₂ is H or CH _3, n2 is an integer of 1 to 3, m3 is 0 to 3 Is an integer.)

17) A sucrose fatty acid ester comprising a fatty acid having an average of 10 to 20 carbon atoms and sucrose. 18) Fatty acid glycerin monoester composed of a fatty acid having an average of 10 to 20 carbon atoms and glycerin. 19) An alkylamine oxide represented by the following general formula.

[0044]

Embedded image

Wherein R ^′ ₁₃ is an alkyl or alkenyl group having 10 to 20 carbon atoms, and R ^′ ₁₄ and R ^′ ₁₅ are
3 alkyl groups. Among them, particularly, as a nonionic surfactant, one having 1 carbon atom
It is preferable to use an ethylene oxide adduct of a linear or branched primary or secondary alcohol having 0 to 20 polyoxyethylene alkyl ethers having an average number of added moles of 5 to 15. More preferably 12 to 14 carbon atoms
An ethylene oxide adduct of a linear or branched primary or secondary alcohol having an average number of moles of 6 to 6
It is desirable to use 10 polyoxyethylene alkyl ethers.

(3) Examples of the cationic surfactant include the following. 20) A cationic surfactant represented by the following general formula. No. 1

[0047]

Embedded image

[0048] (wherein ^{_{R '1, R' 2,}} R '3, R' 4
At least one is an alkyl or alkenyl group having 8 to 24 carbon atoms, and the other is an alkyl group having 1 to 5 carbon atoms. X
^' Represents halogen. ) No. 2

[0049]

Embedded image

(Where R ^′ ₁ , R ^′ ₂ , R ^′ ₃ and X
^' Is as described above. ) No. 3

[0051]

Embedded image

(Wherein R ^′ ₁ , R ^′ ₂ and X ^′ are as described above. R ^′ ₅ is an alkylene group having 2 to 3 carbon atoms, n4
Represents an integer of 1 to 20. )

21) An alkyl or alkenylamine represented by the following general formula. No. During _{1 R "1 R" 2 NH} ( wherein, R ₁ is C ₁₂ -C ₂₆ alkyl or alkenyl group, R ₂ is H or C ₁ -C ₇ alkyl or C
A ₁₂ -C ₂₆ alkyl or alkenyl group. ) No. 2

[0054]

Embedded image

Wherein R ₁ and R ″ ₃ may be the same or different and are each a C ₁₂ -C ₂₂ alkyl group, and R ″ ₄ is a methyl or ethyl group or a ─ (R ″
₅ O) a _n5 H, R _"5 represents an alkylene group having 2 to 3 carbon atoms, n5 is an integer of 1-20.)

(4) Examples of the amphoteric surfactant include the following. 22) A sulfonic acid type amphoteric surfactant represented by the following general formula. No. 1

[0057]

Embedded image

(Where R ₁₁ is an alkyl or alkenyl group having 8 to 24 carbon atoms, R ₁₂ is an alkylene group having 1 to 4 carbon atoms,
R ₁₃ is an alkyl group having 1 to 5 carbon atoms, and R ₁₄ is an alkyl group having 1 to 4 carbon atoms.
Represents an alkylene or hydroxyalkylene group. ) No. 2

[0059]

Embedded image

(Where R ₁₁ and R ₁₄ are as described above
_15, R ₁₆ represents an alkyl or alkenyl group having 8 to 24 or 1 to 5 carbon atoms. ) No. 3

[0061]

Embedded image

(Where R ₁₁ and R ₁₄ are n
1 represents an integer of 1 to 20. )

23) Betaine-type amphoteric active agents represented by the following general formula: No. 1

[0064]

Embedded image

(Where R ₂₁ is an alkyl or alkenyl or β-hydroxyalkyl or β-hydroxyalkenyl group having 8 to 24 carbon atoms, R ₂₂ is an alkyl group having 1 to 4 carbon atoms, and R ₂₃ is an alkyl group having 1 to 6 carbon atoms. No. 1). 2

[0066]

Embedded image

(Where R ₂₁ and R ₂₂ represent n
2 represents an integer of 1 to 20. ) No. 3

[0068]

Embedded image

(Where R ₂₁ and R ₂₃ are as described above.
₂₄ represents a carboxyalkyl or hydroxyalkyl group having 2 to 5 carbon atoms. )

In the present invention, the above-mentioned surfactants can be used, but particularly from the viewpoint of concentration,
(1) Anionic surfactants 1), 2), 3), 4),
5), 8), and / or (2) one of the nonionic surfactants
It is preferred to use 1), 12), 15), preferably 11) as the main surfactant. Needless to say, by using other surfactants in combination, more excellent detergency and specific effects can be obtained as in the case of conventional detergents.

The content of the surfactant (a) is as follows:
Preferably, 10 to 60% by weight, more preferably 15 to 50% by weight, of the total composition. If the amount is less than 10% by weight, sufficient detergency cannot be obtained.
Caking due to moisture absorption will occur.

The inorganic ion exchanger of the component (b) used in the present invention refers to an inorganic substance having a cation exchange ability and has a composition represented by the general formula: xM ₂ O.ySiO ₂ .zMe
a synthetic crystalline silicate represented by _m O _n. Here, M is hydrogen or a group Ia element of the periodic table, and Me is II of the periodic table.
a, IIb, IIIa, IVa or VIII element, y / x =
0.5-2.0, z / x = 0.005-1.0, n / m
= 0.5 to 2.0.

Here, M is selected from hydrogen and Group Ia elements of the periodic table, and examples of Group Ia elements include Na and K. These may be used alone or, for example, a mixture of Na ₂ O and K ₂ O to form the M ₂ O component. Me is selected from Group IIa, IIb, IIIa, IVa or VIII elements of the periodic table, and includes, for example, Mg, Ca, Zn, Y, Ti, Zr, Fe and the like. These are not particularly limited, but are preferably Mg and Ca from the viewpoint of resources and safety. Further, it may be mixed alone, or two or more kinds, for example MgO, etc. are mixed CaO Me _{m
An On} component may be included. Further, in the inorganic ion exchanger of the present invention, it may be a hydrate,
In this case, the hydration amount is usually 20 as a molar amount of H ₂ O.
Mol% or less.

In the general formula, y / x is 0.5 to
2.0, and preferably 1.0 to 1.8. y /
If x is less than 0.5, the water resistance is insufficient, and if it exceeds 2.0, the ion exchange capacity is reduced, and the ion exchanger is insufficient. z / x is 0.005 to 1.0,
Preferably it is 0.02-0.9. z / x is 0.00
If it is less than 5, the water resistance will be insufficient, and if it exceeds 1.0, the ion exchange capacity will be low and it will be insufficient as an ion exchanger. x, y, and z are not particularly limited as long as they have the relationship shown in the above y / x and z / x.
As described above, xM ₂ O is, for example, x′Na ₂ O ·
If x ″ K ₂ O, x is x ′ + x ″. This relationship is the same in the z in the case of ZME _m O _n component composed of two or more. Also, n /
m = 0.5 to 2.0 indicates the number of oxygen ions coordinated to the element, and is substantially 0.5, 1.0, 1.5, 2.0
Is selected from the values of

The component (b) in the present invention is preferably one in which M is K and / or Na and Me is Ca and / or Mg. Particularly, the component (b) is aNa ₂ O · bK ₂ O.SiO ₂ .cCaO.dMgO (however, a + b = 0.5 to 2.0, b / a = 0.005
８8.0, c, d ≧ 0, and c + d = 0.005１1.
0. The use of the synthetic crystalline silicate represented by the formula (1) is preferred from the viewpoint of obtaining a better detergency.

Further, the inorganic ion exchanger according to the present invention is classified into an inosilicate structure according to the classification by the form of the anion, and is formed of only the Q ₂ unit or the Q ₂ unit and the Q ₃ unit. Crystalline silicate compound. In other words, the inorganic ion exchanger of the present invention has at least Q ₂ units and has a chain structure.

Specifically, the presence of the Q ₃ and Q ₂ units can be identified by Raman spectroscopy. FIG. 1 shows FT-
Raman spectroscopy (manufactured by JEOL, model: JRS-FT650
0, excitation light: YAG laser, wavelength = 1064 nm, detector: InGaAs).

The inorganic ion exchanger according to the present invention is a crystalline inosilicate compound having the above composition (inorganic ion exchanger G in Examples, see FIG. 1 (a)). And a scattering peak pattern distinctly different from that of the layered silicate having the following formula (crystalline sodium disilicate, see FIG. 1 (b)), 970 ± 20 cm ⁻¹
The main shift peaks derived from Q ₂ units are present at least. Here, the main shift peak is 90
Raman scattering spectrum for the range of 0-1200 cm ^-1 refers to a distinct shift peak that is substantially discernable. On the other hand, the shift peak attributable to Q ₃ units is observed 1070 ± 30 cm ^-1.

Therefore, the inorganic ion exchanger of the present invention is composed of only the Q ₂ unit or the Q ₂ unit and the Q ₃ unit.
In the range of m ⁻¹ , it has shift peaks only at 970 ± 20 cm ⁻¹ , or 970 ± 20 cm ⁻¹ and 1070 ± 30 cm ^−1, and shifts derived from Q ₀ and Q ₁ units due to being crystalline. The peak is substantially absent. Q ₂
When configured by the unit and Q ₃ units are, as scattering peak pattern obtained from the Raman spectrophotometry of the examples below, from the shift peaks and Q ₃ derived from Q ₂ unit shift The peak intensity ratio is 0.1 to 100. Here, the intensity ratio of the shift peak is calculated from the ratio of the height of the peak appearing at 970 ± 20 cm ⁻¹ to the height of the shift peak appearing at 1070 ± 30 cm ⁻¹ .

The reason for exhibiting high structural stability in water despite being formed from a Q ₂ unit structure is that a proper amount of Ca and / or Mg ions is contained in the silica network. This is clear from the measurement results of the cation exchange capacity and the Si elution amount in Examples described later.

As described above, as the component (b), 900 cm
In Raman scattering spectra for the range of ^{-1 ~1200cm -1,} the case of using a crystalline silicate of the synthetic showing a main shift peaks at least 970 ± 20 cm ^-1,
It is more effective for anti-caking properties. In particular, the main shift peak of 970 ± 20 cm ⁻¹ in the Raman scattering spectrum of the component (b) is 0.1 to 100 intensities with respect to the shift peak of 1070 ± 30 cm ^−1. It is preferable to use one having

The inorganic ion exchanger according to the present invention is composed of M ₂ O, SiO ₂ , Me _m O as shown in the above general formula.
_{It consists} of three to five components of _n . Therefore, in order to produce the inorganic ion exchanger of the present invention, each component is required as a raw material. In the present invention, a known compound is appropriately used without any particular limitation. For example, M ₂ O component, the Me _m O _n component, alone or oxides of the composite of each of the elements, hydroxides, salts,
The element-containing mineral is used. Specifically, for example, M
The raw materials of the ₂ O component include NaOH, KOH, Na ₂ C
_{O 3, K 2 CO 3,} Na 2 SO 4 and the like, as a material of Me _m O _{n component, CaCO 3, MgCO 3, Ca} (O
H) ₂ , Mg (OH) ₂ , MgO, ZrO ₂ , dolomite and the like. As the SiO ₂ component, silica stone, kaolin, talc, fused silica, sodium silicate and the like are used.

In the method for preparing an inorganic ion exchanger in the present invention, the above-mentioned raw material components are mixed at a predetermined quantitative ratio so as to obtain the values of x, y, and z of the intended inorganic ion exchanger, and usually 300 to 1500 ° C, preferably 500-1000 ° C,
More preferably, a method of firing at a temperature in the range of 600 to 900 ° C. for crystallization is exemplified. In this case, the heating temperature is 3
If the temperature is lower than 00 ° C., the crystallization is insufficient and the water resistance is poor.
If the temperature is higher than 00 ° C., the particles become coarse and the ion exchange capacity decreases. The heating time is usually 0.1 to 24 hours. Such firing can be usually performed in a heating furnace such as an electric furnace or a gas furnace. After firing, the powder is crushed as necessary to adjust the particle size to a predetermined value. As the pulverizer, for example, a ball mill, a roller mill or the like is used.

The hydrate of the inorganic ion exchanger in the present invention can be easily prepared by a known method, and is not particularly limited. For example, there is a method in which an anhydride of the inorganic ion exchanger obtained as described above is suspended in ion-exchanged water, hydrated, dried, and powdered.

The inorganic ion exchanger or hydrate thereof according to the present invention thus obtained has an ion exchange capacity of at least 100 mg CaCO ₃ / g, preferably 200 to 600 mg CaCO ₃ / g. The amount of Si eluted in water is usually 1 in terms of SiO _2.
It is not more than 00 mg / g and is substantially insoluble in water. In the present invention, the term “substantially insoluble in water” means that the amount of Si eluted when 2 g of a sample is added to 100 g of ion-exchanged water and stirred at 25 ° C. for 30 minutes is usually less than 100 mg / g in terms of SiO _2. A thing. In the present invention, the inorganic ion exchanger is 11% by weight in a dispersion of 0.1% by weight.
It shows the above pH and shows excellent alkalinity. Also, the alkali buffering effect is particularly excellent, and the alkali buffering effect is superior to that of sodium carbonate or ordinary amorphous sodium silicate. Since the inorganic ion exchanger in the present invention has excellent ion trapping ability, alkalinity adjusting ability, and further a buffering effect as described above, the detergent composition of the present invention containing the same has excellent washing performance. Also suitable for concentration.

The content of the inorganic ion exchanger and / or hydrate thereof as the component (b) is from 5 to 50 in the total composition.
% By weight, preferably 7 to 35% by weight. (B)
If the compounding amount of the component is less than 5% by weight, it does not have a sufficient function as an ion exchanger, and if it exceeds 50% by weight, caking tends to occur during storage.

The component (c) used in the present invention, Na ₂ C
O ₃ and K ₂ CO ₃ are generally used as alkaline agents, and it is desirable that the composition does not contain 5% by weight or less, preferably 1% by weight or less, and more preferably does not contain it. 5% by weight
When the amount exceeds the above, the bulk density tends to decrease during storage, and particularly when the amount of component (b) is large, Na ₂ CO ₃ and K ₂ CO
_{When a} large amount of ₃ is blended, the volume becomes 1.5 times or more when severe after long-term storage, and the bulk density decreases.

As a preferred embodiment of the present invention, more preferably, a nonionic surfactant having a melting point of 40 ° C. or less is used as a main base material, and an oil absorbing capacity of 80 ml / 100 g or more is further used as a component (d). 5 to 85% by weight, preferably 10 to 50% by weight of the water-insoluble silica derivative
It is preferred to contain. The nonionic surfactant having a melting point of 40 ° C. or lower is preferably a slurry or a liquid at 40 ° C. Even if the melting point is 40 ° C. or higher, a large amount of other nonionic surfactants may be used. Can be used if it becomes a liquid or a slurry by being mixed with water.

The nonionic surfactants described above can be used, but from the viewpoint of detergency, ethylene oxide is preferably added to an alcohol having 10 to 20 carbon atoms in an average mole number of 5 to 15 as a nonionic surfactant. It is preferable to use a polyoxyethylene alkyl ether obtained by adding the above. Of course, other surfactants are also nonionic surfactants 1
If it is 50 parts or less per 00 parts and does not solidify the nonionic surfactant, it may be used by mixing with the nonionic surfactant.

The silica derivative of the component (d) is other than the component (b) and has an oil absorption capacity of at least 80 ml / 100 g, preferably at least 150 ml / 100 g, as measured by the method described in JIS K6220. However, it has excellent caking resistance. Examples of such silica derivatives include HS.
Z series (manufactured by Tosoh Corporation), TIXOLEX (manufactured by Kofuran Chemical Co., Ltd.), TIXOSIL (manufactured by Kofran Chemical Co., Ltd.), Toksil (manufactured by Tokuyama Soda Co., Ltd.), Nipseal (manufactured by Nippon Silica Co., Ltd.), Carplex (Shionogi & Co., Ltd.) and oil-absorbing carriers marketed under trade names such as SIPERNART (manufactured by Degussa). For example, TIXOLEX 25 (manufactured by Kofran Chemical Company), Toksil AL-1 (manufactured by Tokuyama Soda Co., Ltd.),
Nip Seal NA (manufactured by Nippon Silica Co., Ltd.), Carplex # 100 (manufactured by Shionogi & Co., Ltd.), SIPERNA
RT D10 (manufactured by Degussa) and the like.

As the component (d) used in the present invention, an amorphous component is preferable, and an amorphous aluminosilicate represented by the following formula is particularly preferable in terms of detergency. General formula, αMeO · βM ₂ O · Al ₂ O ₃ · γSiO ₂ (where Me represents an alkaline earth metal, M represents an alkali metal, α = 0 to 0.1, β = 0.2 to 2. 0, γ =
0.5 to 6. )

The amorphous aluminosilicate of the above formula can be produced by a conventional method. For example, SiO ₂ and M ₂ O
(M means an alkali metal) molar ratio of SiO ₂ /
An M ₂ O = 1.0~4.0, the molar ratio of between H ₂ O and M ₂ O is using alkali metal silicate solution is a _{H 2 O / M 2 O =} 12~200, M to The molar ratio of ₂ O to Al ₂ O ₃ is M ₂ O / Al ₂ O ₃ = 1.0 to 2.0;
The molar ratio of ₂ O to M ₂ O is H ₂ O / M ₂ O = 6.0 to 50
The aqueous solution of a low alkali alkali metal aluminate, which is 0, is usually added under a strong stirring at a temperature of 15 to 60 ° C, preferably 30 to 50 ° C.

Next, the formed white precipitate slurry is heated at a temperature of usually 70 to 100 ° C., preferably 90 to 100 ° C.
It can be advantageously obtained by performing a heat treatment usually for 10 minutes or more and 10 hours or less, preferably 5 hours or less, followed by filtration, washing and drying. At this time, the addition method may be a method of adding an aqueous solution of an alkali metal silicate to an aqueous solution of a low alkali alkali metal aluminate. According to this method, the ion exchange capacity is 100 mg CaCO ₃ / g or more and the oil absorption capacity is 150
It is possible to easily obtain an amorphous aluminosilicate oil-absorbing carrier of ml / 100 g or more (see JP-A-62-191417 and JP-A-62-191419).

The content of the silica derivative as the component (d) is from 5 to 85% by weight, preferably from 10 to 5% by weight of the whole composition.
0% by weight is blended. If the amount is less than 5% by weight, the caking resistance is reduced. If the amount exceeds 85% by weight, not only the detergency but also the caking resistance is reduced.

In the present invention, a crystalline aluminosilicate represented by the following formula may be further blended. p (M _'2 O or _{M "O) · Al 2 O} 3 · qSiO 2
• wH ₂ O (wherein, M ′ is an alkali metal atom, M ″ is an alkaline earth metal atom exchangeable with calcium, p, q, and w represent the number of moles of each component, usually 0.7 ≦ p ≦ 1.5, 0.8 ≦
q ≦ 6, w is an arbitrary positive number. Among them, those represented by the following formula are particularly preferred as additives. _{Na 2 O · Al 2 O 3} · rSiO 2 · w'H 2 O ( where r is 1.8 to 3.0, w 'represents a number of 1 to 6.) Such a crystalline aluminosilicate The compounding amount of
The total amount of the component (d) and the silica derivative is 85
Preferably, it does not exceed weight%.

In the present invention, examples of the water-soluble alkaline agent other than the carbonate as the component (c) include various substances such as sodium sulfite, but other than sodium silicate such as water glass can be blended without any problem. The addition of sodium silicate
When a nonionic surfactant is used as a main component, particularly when zeolite is blended, it also causes a decrease in solubility after long-term storage.
It is desirable that the amount is less than 1% by weight, preferably less than 1% by weight.

The detergent composition of the present invention may contain, in addition to the above components, detergent builders, for example, phosphates such as tripolyphosphate and pyrophosphate, aminotri (methylenephosphonic acid), 1-hydroxyethylidene-1,1- Diphosphonic acid, ethylenediaminetetra (methylenephosphonic acid), diethylenetriaminepenta (methylenephosphonic acid), and salts thereof, salts of phosphonocarboxylic acids such as 2-phosphonobutane-1,2-dicarboxylic acid, and amino acids such as aspartic acid and glutamic acid Salts, aminotriacetates such as nitrilotriacetate and ethylenediaminetetraacetate; polyelectrolytes such as polyacrylic acid, acrylic-maleic acid copolymer, and polyaconitic acid; and non-polyesters such as polyethylene glycol, polyvinyl alcohol, and polyvinylpyrrolidone. Dissociated polymer, JP-A-54-5219 JP-A No. 207-216, a polyacetal carboxylic acid polymer, diglycolic acid, builders such as salts of organic acids such as oxycarboxylates, chelating agents and anti-fading agents generally known to be blended in detergents such as carboxymethyl cellulose. And a recontamination inhibitor.

In addition, the cleaning composition of the present invention can also contain the following components. That is, protease,
Enzymes such as lipase, cellulase, paratoluenesulfonate, sulfosuccinate, talc, calcium silicate, etc., antioxidants such as tertiary butylhydroxytoluene, distyrenated cresol, fluorescent dye, bluing agent, Although it may contain a fragrance or the like, these are not particularly limited and may be blended according to the purpose.

The cleaning composition of the present invention contains the above-mentioned components. The method for producing the cleaning composition is not particularly limited, and a conventionally known method can be used. . For example, a method for obtaining a high bulk density detergent is disclosed in JP-A-61-69897 and JP-A-61-69.
899, JP-A-61-69900, EP5
The method described in 13824A can be used. However, when using a spray-dried dough, the inorganic ion exchanger of the present invention is preferably not incorporated into the slurry composition for spraying, and may be blended during granulation or separately.

[0100]

The present invention will be described in more detail with reference to the following Examples, Comparative Examples and Test Examples, but the present invention is not limited to these Examples. In addition, the measured value in this example etc. was measured by the following method.

(1) Cation exchange capacity 0.1 g of a sample was precisely weighed and added to 100 ml of an aqueous calcium chloride solution (concentration: 500 ppm as CaCO ₃ ).
After stirring at 25 ° C. for 60 minutes, filtration was carried out using a membrane filter having a pore size of 0.2 μm (manufactured by Advantech, nitrocellulose), and the amount of Ca contained in 10 ml of the filtrate was measured by EDTA titration. The calcium ion exchange capacity (cation exchange capacity) of the sample was determined from the value. However, in the case of 500 mgCaCO ₃ / g or more,
This is a value measured by setting the amount of the calcium chloride solution to 200 ml.

(2) Si Elution Amount 2 g of a sample was added to 100 g of ion-exchanged water, and 30
Stir for minutes. Thereafter, centrifugation is performed, and the supernatant is filtered using a membrane filter having a pore size of 0.2 μm. Plasma emission spectrometry (ICP) for Si concentration in filtrate
The elution amount of Si was calculated in terms of SiO ₂ .

(3) Raman spectrum intensity ratio Fourier transform Raman spectrophotometer (manufactured by JEOL Ltd., J
SR-FT6500, excitation light: YAG laser, wavelength =
Raman spectroscopy was performed using 1064 nm, detector: InGaAs). In the obtained Raman scattering spectrum, the scattering intensities attributed to Q ₂ and Q ₃ were determined as follows:
The relative intensity ratio of Q ₂ / Q ₃ was determined as the peak top value of the shift peaks appearing at 970 ± 20 cm ⁻¹ and 1070 ± 30 cm ⁻¹ .

Synthesis Example of Inorganic Ion Exchanger No. 2 Sodium Silicate (SiO ₂ / Na ₂ O = 2.5) 100
4.2 parts by weight of sodium hydroxide were added to parts by weight, and the mixture was stirred with a homomixer to dissolve sodium hydroxide. To this, 10 parts by weight of finely ground anhydrous calcium carbonate was added and mixed using a homomixer. An appropriate amount of the mixture was placed in a nickel crucible, fired at 700 ° C. in air for 1 hour, quenched, and the fired body was pulverized to obtain an inorganic ion exchanger powder A of the present invention. The cation exchange capacity of this powder was as high as 243 mg CaCO ₃ / g, and the amount of Si eluted was 19.7 SiO ₂ mg / g, indicating excellent water resistance. Also, the powder X-ray (Cu
Kα) The diffraction pattern was different from that of the mixture before firing, and was a substance showing a novel crystal structure.
In the same manner, inorganic ion exchanger powders B, C, D, E, F and G having the compositions shown in Table 1 were obtained.

[0105]

[Table 1]

Synthesis Example of Amorphous Aluminosilicate (A) Aqueous solution of sodium aluminate (Na ₂ O 1.5
5% by weight, 2.30% by weight of Al ₂ O ₃ , Na ₂ O / Al
₂ O ₃ = 1.11 (molar ratio)) 1010 g was heated at 40 ° C., aqueous sodium silicate solution while stirring at a rotation speed of 1500rpm (Na ₂ O 2.75 wt%, SiO ₂
7.88 _{wt%, SiO 2 / Na 2 O} = 2.96 ( molar ratio)) was added dropwise react 20 minutes 700 g. After the reaction, a heat treatment was further performed for 15 minutes, followed by filtration and washing. The obtained wet cake was heated at 105 ° C. and 300 torr,
After drying for 10 hours and pulverizing, it was confirmed by X-ray diffraction that fine powder of amorphous sodium aluminosilicate A was obtained. The composition of the obtained amorphous aluminosilicate is
As a result of atomic absorption analysis and plasma emission analysis, Al ₂ O ₃
= 21.1% by weight, SiO ₂ = 57.2% by weight, Na ₂
O = 21.7% by weight. Oil absorption capacity is 210ml / 1
00g, Ca exchange capacity was 182 mg CaCO ₃ / g.

(B) Aqueous sodium aluminate solution (Na
_{2 O: Al 2 O 3 =} 20.3: 28.2 as prepared aqueous solution of sodium 100 parts by weight of aluminate further deionized water (weight ratio) was added 2000 parts by weight) 800 parts by weight of No. 3 water glass 100 parts by weight of a solution (prepared by adding 100 parts by weight of a commercially available No. 3 water glass) was dropped in 20 minutes, heat-treated at 60 ° C. for 20 minutes, filtered and washed. The obtained wet cake is dried at 120 ° C. for 12 hours,
It was pulverized with a crusher to obtain amorphous sodium aluminosilicate B. As a result of atomic absorption analysis and plasma emission analysis, the composition of the obtained amorphous aluminosilicate was Al ₂ O ₃ = 2.
7.2% by weight, SiO ₂ = 51.2% by weight, Na ₂ O =
It was 21.8% by weight. Oil absorption capacity 200ml / 100
g, Ca exchange capacity was 192 mgCaCO ₃ / g.

Examples 1 to 18, Comparative Examples 1 to 5 The inorganic ion exchanger powders A to G obtained in the above synthesis examples,
Using crystalline sodium disilicate and amorphous sodium aluminosilicate A, B, detergent compositions having the compositions shown in Tables 2, 3 and 4 (Products 1 to 18 of the present invention and Comparative products 1 to 1)
5) was produced by the following method. That is, in the products 1 to 4 of the present invention and the comparative products 1 and 2, components other than the inorganic ion exchanger are converted into a 60% solid aqueous slurry, which is spray-dried, and the obtained particles are put into a stirring granulator. Further, an inorganic ion exchanger equivalent to the blending amount was further added and granulated. In the present invention products 5 to 18 and comparative products 3 to 5, all the powders (including inorganic ion exchangers) were put into a stirring type tumbling granulator and mixed while gradually adding a liquid nonionic activator. Granulated. Thus, a powdery detergent composition having an average particle size of 200 to 500 μm was obtained. The bulk density of these detergent compositions was measured according to JIS K3362. Tables 2 and 3 show the respective bulk densities.

[0109]

[Table 2]

[0110]

[Table 3]

The abbreviations and the like in Tables 2 and 3 are as follows.
It is as follows. LAS-Na: Sodium linear alkylbenzene sulfonate AS-Na: Sodium alkyl sulfate α-SFE-Na: Sodium salt of α-sulfofatty acid methyl ester EOP: Average number of moles of ethylene oxide added PAS: Sodium polyacrylate (average molecular weight 10,000) Enzyme * 1: Protease (Savinase, NOVO Nordisk Bioi
ndustry) · Cellulase (alkaline cellulase K described in EP 265832) · Lipase (Lipolase, NOVO
Amylase (Termamyl, N) from Nordisk Bioindustry
OVO Nordisk Bioindustry) was added in an amount of 0.4%. Fluorescent dye * 2: 0.25% each of a DM type fluorescent dye (Sumitomo Chemical Co., Ltd.) and Tinopearl CBS-X (Ciba Geigy).

[0112]

[Table 4]

The abbreviations and the like in the table are as follows. EOP: average number of moles of ethylene oxide added PAS: sodium polyacrylate (average molecular weight: 10,000) Enzyme * 1: 0.3% protease (alkali protease K-16 described in JP-A-5-25492). 2% (NOVO Nordisk Bioindustry) · Cellulase 0.8% (alkaline cellulase K described in EP 265832) · Lipase 0.2% (Lipolase, NOVO Nordisk)
Bioindustry) Amylase 0.2% (Termamyl, N
OVO Nordisk Bioindustry). Fluorescent dye * 2: 0.25% each of a DM type fluorescent dye (Sumitomo Chemical Co., Ltd.) and Tinopearl CBS-X (Ciba Geigy).

Test Example 1 (Caking property test) A caking property test was performed on the products 1 to 18 of the present invention and comparative products 1 to 5 by the following method. The results are shown in Tables 2, 3 and 4. (1) Filter paper (Toyo Filter Paper No. 2) 10.2 cm long
Create a 6.2cm wide x 4cm high box without a top. Stapling the four corners. (2) A 50 g sample is put in this box, and an acrylic resin plate and a lead plate (or iron plate) (total weight 250 g + 15
g) is placed. (3) This is left in a thermo-hygrostat at a temperature of 30 ° C. and a humidity of 80%, and the caking state is determined after 7 days.

[0115] The determination of the caking property was carried out by obtaining the transmittance as follows. Passage rate: The sample after the test was tested with a wire mesh (or screen, mesh 5m).
mx 5 mm), weigh the powder that has passed through the wire mesh, and determine the transmittance for the sample after the test. The larger the value, the better the anti-caking properties. Passage rate (%) = [weight of powder passed (g) / weight of entire sample (g)] × 100 As a result, products 1 to 18 of the present invention have better anti-caking properties than comparative products 1 to 4. It was excellent.

Test Example 2 (Powder fluidity test, measurement of bulk density) [0116] The powder fluidity test and bulk density measurement of the present invention products 1 to 13 and comparative products 1 to 4 were performed by the following methods. The results are shown in Tables 2 and 3. (1) Filter paper (Toyo Filter Paper No. 2) 10.2 cm long
Create a 6.2cm wide x 4cm high box without a top. Stapling the four corners. (2) This is left in a thermo-hygrostat at a temperature of 30 ° C. and a humidity of 80%, and after 7 days, a powder fluidity test and a measurement of bulk density are performed. The flowability test of the powder was performed using a stand and a funnel described in JIS K 3362 “Synthetic detergent test method” and AST.
M: Flow Rate of Met specified in B221348
Measure according to the Flow Rate of al Powders. The smaller the value, the better the fluidity. Also,
The bulk density is measured according to JIS K 3362 “Synthetic detergent test method”. As a result, the fluidity of the powder exhibited an effect superior to that of the comparative product. In addition, the bulk densities of the comparative products 1 to 4 were greatly reduced, whereas the bulk products of the present invention 1 to 1 were not.
In No. 3, no decrease in bulk density was observed.

Test Example 3 (detergency test) A blend system using inorganic ion exchangers A, D and G and, as a comparison, crystalline sodium disilicate (Products 14 to 1 of the present invention)
8, the detergency of the comparative product 5) was measured by the following method. The results are shown in Table 4, and it was shown that the product of the present invention has excellent detergency.

Sebum / Carbon Soil Contaminated Cloth (Artificial Contaminated Cloth) (Model Sebum / Carbon Soil Composition) Carbon Black 15% Cottonseed Oil 60% Cholesterol 5% Oleic Acid 5% Palmitic Acid 5% Liquid Paraffin 10% 1 kg of the above composition is 80 After dissolving and dispersing in a liter of perclene, a cloth # 2023 is dipped in the cloth to attach dirt, and then the perchlen is dried and removed.

Washing Conditions Five pieces of 10 cm × 10 cm sebum / carbon stained cloth (artificial stained cloth) were placed in each liter of the detergent aqueous solution for evaluation.
The plate was washed with a tergotometer at 100 rpm under the following washing conditions. Washing time 10 minutes Washing concentration 0.10% Hardness of water 4 ° DH Water temperature 20 ° C Rinse 5 minutes with tap water

Evaluation Method of Cleaning Test The cleaning power was determined by measuring 550 of the original cloth before contamination and the contamination cloth before and after cleaning.
The reflectance in nm was measured using a self-recording colorimeter (manufactured by Shimadzu Corporation), and the cleaning rate (%) was determined by the following equation. Cleaning rate (%) = [(reflectance after cleaning-reflectance before cleaning)
/ (Reflectance of original fabric-reflectance before washing)] x 100

[0121]

The inorganic ion exchanger according to the present invention has excellent cation exchange ability and water resistance,
During storage under high humidity, there are no problems such as excellent caking resistance and reduced fluidity and reduced bulk density of the detergent powder. Therefore, by incorporating this inorganic ion exchanger, it is possible to provide a cleaning composition which is excellent in cleaning effect and has no problem even when stored under high humidity.

[Brief description of the drawings]

FIG. 1 shows a spectrum obtained by Raman spectroscopy. In the figure, (a) is for the crystalline inorganic ion exchanger G obtained in the synthesis example of the inorganic ion exchanger, and (b) is sodium disilicate (Na ₂ Si).
₂ O ₅ ).

────────────────────────────────────────────────── ─── Continued on the front page (58) Field surveyed (Int. Cl. ⁶ , DB name) C11D 3/04-3/14 C01B 33/32 CA (STN)

Claims (12)

(57) [Claims] 1. A cleaning composition comprising the following components: (A) a surfactant, 10 to 60 wt% (b) general _{formula, xM 2 O · ySiO 2 ·} zMe m O n ( where, M is a Group Ia element of the hydrogen or the periodic table, Me represents the periodic table IIa , IIb, IIIa, IVa or VIII element, y / x = 0.5-2.0, z / x = 0.005-
1.0, n / m = 0.5 to 2.0. A) a synthetic crystalline silicate having a composition represented by the formula (1), having an ion exchange capacity of at least 100 mg CaCO ₃ / g or more;
0% by weight (c) Na ₂ CO ₃ and / or K ₂ CO ₃ , 5% by weight or less 2. M in the general formula of component (b) is K and / or
The cleaning composition according to claim 1, wherein Me is Ca and / or Mg. 3. Component (b) is aNa ₂ O.bK ₂ O.S
iO ₂ · cCaO · dMgO (however, a + b = 0.5 to
2.0, b / a = 0.005 to 8.0, c, d ≧ 0, and c + d = 0.005 to 1.0. The cleaning composition according to claim 2, which is a synthetic crystalline silicate represented by the formula: 4. The composition according to claim 1, wherein the component (b) is 900 cm ^{-1 to} 1200.
The cleaning composition according to any one of claims 1 to 3, which is a synthetic crystalline silicate showing a main shift peak at least at 970 ± 20 cm ^-1 in a Raman scattering spectrum in a range of cm ^-1 . 5. The main shift peak at 970 ± 20 cm ⁻¹ in the Raman scattering spectrum of the component (b) is 10
0.1 to ^{1 for} a shift peak of 70 ± 30 cm ⁻¹
The cleaning composition according to claim 4, which has an intensity ratio of 00. 6. The cation exchange capacity of the component (b) is 20.
0~600mgCaCO ₃ / g detergent composition according to any one of claims 1 to 5 is. 7. The cleaning composition according to claim 1, wherein the amount of the component (c) is 1% by weight or less. 8. The surfactant according to claim 1, wherein the surfactant (a) is an anionic surfactant and / or a nonionic surfactant.
A cleaning composition according to any one of claims 1 to 7. 9. The nonionic surfactant has 10 to 2 carbon atoms.
The cleaning composition according to claim 8, which is a polyoxyethylene alkyl ether obtained by adding ethylene oxide to alcohol 0 at an average addition mole number of 5 to 15. 10. The surfactant (a) having a melting point of 40
A nonionic surfactant having a temperature of not more than 0 ° C. and an oil absorbing capacity other than the component (b) of 80 ml / 100 g as the component (d).
The cleaning composition according to any one of claims 1 to 9, wherein the water-insoluble silica derivative is contained in an amount of 5 to 85% by weight. 11. The component (d) has a general formula: αMeO · βM ₂ O · Al ₂ O ₃ · γSiO ₂ (where Me is an alkaline earth metal, M is an alkali metal, and α = 0 to 0. 1, β = 0.2 to 2.0, γ =
0.5 to 6. The cleaning composition according to claim 10, which is an aluminosilicate represented by the formula: 12. The cleaning composition according to claim 10, wherein the silica derivative as the component (d) is amorphous.