JP2668018B2 - How to remove oil stains - Google Patents
How to remove oil stainsInfo
- Publication number
- JP2668018B2 JP2668018B2 JP5350924A JP35092493A JP2668018B2 JP 2668018 B2 JP2668018 B2 JP 2668018B2 JP 5350924 A JP5350924 A JP 5350924A JP 35092493 A JP35092493 A JP 35092493A JP 2668018 B2 JP2668018 B2 JP 2668018B2
- Authority
- JP
- Japan
- Prior art keywords
- paint
- antifouling
- oil stains
- protective coating
- fiber sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、台所の換気扇や排気口
を覆うフード等に付着した油汚れを除去するための方法
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for removing oil stains adhering to a ventilation fan in a kitchen or a hood covering an exhaust port.
【0002】[0002]
【従来の技術】台所の換気扇や排気口を覆うフード等に
は、油汚れが付着し易く、一旦付着した油汚れは固化し
てなかなか落ちにくいため、除去作業が非常に大変であ
る。このため従来では、合成樹脂製フィルムの表面に粘
着剤を塗布してなる防汚シートを使用し、該防汚シート
を換気扇やフード等の防汚対象物の表面に張り付けてお
いて、その表面にある程度の油汚れが付着したところで
該防汚シートを防汚対象物から剥離することにより、付
着した油汚れを該防汚シートと共に防汚対象物から除去
するといった方法がとられている。2. Description of the Related Art Oil dirt easily adheres to a ventilation fan or a hood covering an exhaust port of a kitchen, and the oil dirt once adhered hardens and hardly falls off. For this reason, conventionally, an antifouling sheet obtained by applying an adhesive to the surface of a synthetic resin film is used, and the antifouling sheet is attached to the surface of an antifouling object such as a ventilation fan or a hood, and the surface thereof is When a certain amount of oil stain adheres to the antifouling sheet, the stainproof sheet is peeled off from the antifouling object to remove the adhered oil stain together with the antifouling sheet from the antifouling object.
【0003】しかしながら、上記従来の防汚シートは、
表面が滑らかな合成樹脂製フィルムに粘着剤を塗布した
ものであることから、該粘着剤がフィルムから剥れ易
く、防汚シートを防汚対象物から剥離する際に、フィル
ムから剥れた粘着剤が防汚対象物の表面に付着したまま
残るため、残存した粘着剤の除去に手間がかかるという
欠点があった。However, the above conventional antifouling sheet is
Since the adhesive is applied to the synthetic resin film having a smooth surface, the adhesive is easily peeled off from the film, and when the antifouling sheet is peeled off from the antifouling target, the adhesive peeled off from the film. Since the agent remains attached to the surface of the antifouling target, it takes a lot of time to remove the remaining adhesive.
【0004】[0004]
【発明が解決しようとする課題】本発明の技術的課題
は、剥離性に勝れた保護被膜を防汚対象物に被設するこ
とにより、油汚れの付着後に該保護被膜を防汚対象物か
ら簡単且つ確実に剥離することができる油汚れの除去方
法を提供することにある。The technical problem of the present invention is to provide a protective film having excellent releasability on an antifouling object, so that after the oil stain adheres, the protective film is applied to the antifouling object. Another object of the present invention is to provide a method for removing oil stains, which can be easily and surely peeled off.
【0005】[0005]
【課題を解決するための手段】上記課題を解決するた
め、本発明の除去方法は、油汚れの付着し易い防汚対象
物の表面に剥離性のある塗料を塗布し、該塗料が乾かな
いうちに繊維シートを被覆してその上から再び塗料を塗
布することにより、繊維シートで補強された塗料による
保護被膜を形成し、油汚れの付着後に該保護被膜を防汚
対象物から剥離することを特徴とするものである。ま
た、本発明の他の方法は、油汚れの付着し易い防汚対象
物の表面に、補強用の繊維を混合した剥離性のある塗料
を塗布することにより、繊維で強化された塗料による保
護被膜を形成し、油汚れの付着後に該保護被膜を防汚対
象物から剥離することを特徴とするものである。In order to solve the above-mentioned problems, a method of the present invention is to apply a releasable paint to the surface of an antifouling object to which oil stains easily adhere, and the paint does not dry. By coating the fiber sheet in the meantime and applying the paint again from above, forming a protective film of the paint reinforced with the fiber sheet, and peeling off the protective film from the antifouling object after the oil stain adheres. It is characterized by the following. Further, another method of the present invention is to apply a releasable paint mixed with reinforcing fibers to the surface of an antifouling object to which oil stains are liable to adhere, thereby providing protection by a fiber-reinforced paint. The invention is characterized in that a coating film is formed, and after the oil stain is attached, the protective coating is peeled off from the stainproof object.
【0006】[0006]
【作用】上記方法によれば、塗料と繊維シート又は繊維
とが一体化することにより、強度が大きく、且つ塗料と
繊維シート又は繊維とが分離しにくく、しかも防汚対象
物からは容易に剥離可能な保護被膜が形成される。従っ
て、油汚れが付着した保護被膜を防汚対象物から剥離す
る際に、塗料が防汚対象物に付着したまま残存したり、
塗料が繊維シート又は繊維から分離して周囲に落下する
ような不都合がなく、保護被膜を簡単且つ確実に剥離す
ることができる。According to the above method, the paint is integrated with the fiber sheet or fiber, so that the strength is large, the paint and the fiber sheet or fiber are hardly separated, and easily peeled off from the antifouling object. A possible protective coating is formed. Therefore, when peeling off the protective coating to which the oil stain adheres from the antifouling object, the paint remains attached to the antifouling object,
There is no inconvenience that the paint separates from the fiber sheet or the fiber and falls to the surroundings, and the protective coating can be easily and reliably peeled off.
【0007】[0007]
【実施例】以下、本発明の除去方法を図面に基づいて詳
細に説明する。図1及び図2は本発明の第1の方法を示
すもので、この方法においては、台所の換気扇や排気口
を覆うフードのような油汚れの付着し易い防汚対象物1
の表面に、その使用に先立ち、あるいは清掃後に、剥離
性のある保護被膜2を次の手順により形成する。即ち、
先ず、適度の粘着性と耐熱性及び安全性を備えた塗料3
aを防汚対象物1の表面に所要の厚さに塗布し、次に、
該塗料3aが乾かないうちにその上に繊維シート4を被
覆して、その上から再び同じ塗料3bを所要の厚さに塗
布することにより、該繊維シート4を塗料3a,3b内
に塗り込む。これにより上記防汚対象物1の表面には、
繊維シート4で補強された塗料による保護被膜2が形成
される。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The removal method of the present invention will be described in detail below with reference to the drawings. FIGS. 1 and 2 show a first method of the present invention. In this method, an antifouling object 1 to which oily dirt easily adheres, such as a kitchen ventilation fan or a hood covering an exhaust port.
Prior to its use or after cleaning, a protective coating 2 having a peeling property is formed on the surface of No. 1 by the following procedure. That is,
First, a paint 3 having moderate adhesiveness, heat resistance and safety
a is applied to the surface of the antifouling object 1 to a required thickness, and then
Before the paint 3a is not dried, the fiber sheet 4 is coated thereon, and the same paint 3b is applied again to a required thickness from above, whereby the fiber sheet 4 is applied to the paints 3a and 3b. . Thereby, on the surface of the antifouling target 1,
The protective coating 2 made of the paint reinforced with the fiber sheet 4 is formed.
【0008】上記塗料としては、防汚対象物1に対する
付着力よりも繊維シート4に対する付着力の方が大きい
ものが使用され、また、該繊維シート4としては、耐熱
性を有する繊維素材からなる織布又は不織布のいずれを
使用することもできるが、織布を使用する場合は織り目
のやや粗いものが好ましい。As the paint, a paint having an adhesive force to the fiber sheet 4 larger than an adhesive force to the antifouling object 1 is used, and the fiber sheet 4 is made of a heat-resistant fiber material. Either a woven cloth or a non-woven cloth can be used, but when a woven cloth is used, a slightly coarse weave is preferable.
【0009】かくして、上述したような付着力を持つ塗
料内に繊維シート4を塗り込むことにより、該塗料が繊
維シート4内に十分浸透して一体化して、強度が大き
く、且つ塗料と繊維シート4とが分離しにくく、しかも
防汚対象物1からは容易に剥離することが可能な保護被
膜2を形成することができる。この場合、上記塗料は、
必ずしも繊維シート4を完全に覆い隠す程度にまで厚く
塗布する必要はなく、繊維シート4内に十分浸透して所
望の保護被膜2を形成し得る程度の厚さに塗布すれば良
い。Thus, by coating the fiber sheet 4 into the paint having the above-mentioned adhesive force, the paint sufficiently penetrates and integrates into the fiber sheet 4 to have high strength, and the paint and the fiber sheet It is possible to form the protective coating 2 which is difficult to separate from the antifouling target 1 and which can be easily peeled off from the antifouling target 1. In this case, the paint is
It is not always necessary to apply the coating so thickly that the fiber sheet 4 is completely covered and hidden, but it is sufficient to apply the coating so as to sufficiently penetrate the fiber sheet 4 to form the desired protective coating 2.
【0010】かくして保護被膜2を形成した防汚対象物
1を適当な期間使用し、保護被膜2の表面に油汚れが付
着すると、図2に示すように、保護被膜2を防汚対象物
1から剥離することにより、油汚れを該保護被膜2と共
に除去する。このとき、上記保護被膜2は、繊維シート
4により補強されて強度が大きく、しかも、塗料が繊維
シート4と強固に付着一体化して分離することなく、防
汚対象物1からは容易に剥離するため、その剥離作業を
容易に行うことができる。When the antifouling object 1 on which the protective film 2 is formed is used for a suitable period of time and oil stains adhere to the surface of the protective film 2, as shown in FIG. The oil stain is removed together with the protective coating 2 by peeling from the protective film 2. At this time, the protective coating 2 is reinforced by the fiber sheet 4 and has a large strength. Further, the coating material is easily separated from the antifouling target object 1 without being firmly integrated with and separated from the fiber sheet 4. Therefore, the peeling work can be easily performed.
【0011】保護被膜2を剥離することにより油汚れが
除去された防汚対象物1には、上述した方法で再び保護
被膜2を形成する。On the antifouling object 1 from which the oil stain has been removed by peeling off the protective film 2, the protective film 2 is formed again by the method described above.
【0012】図3は本発明の第2の方法を示すもので、
この方法においては、適宜長さの補強用短繊維14を混
合した塗料13を使用し、防汚対象物1の表面に該塗料
13を所要の厚さに塗布することにより、繊維14で強
化された塗料13による保護被膜12を形成し、油汚れ
の付着後に該保護被膜12を剥離する。この場合も、防
汚対象物1に対して所要の剥離性を示す塗料13が用い
られることはいうまでもない。FIG. 3 shows the second method of the present invention.
In this method, a paint 13 mixed with an appropriate length of reinforcing short fibers 14 is used, and the paint 13 is applied to the surface of the antifouling object 1 to a required thickness to thereby be reinforced with the fibers 14. The protective coating 12 is formed by the coating material 13 and the protective coating 12 is peeled off after the oil stain is attached. In this case as well, it goes without saying that the coating material 13 showing the required peeling property with respect to the antifouling object 1 is used.
【0013】[0013]
【発明の効果】以上に詳述したように、本発明によれ
ば、剥離性に勝れた保護被膜を防汚対象物に被設するこ
とができると共に、油汚れの付着後に該保護被膜を防汚
対象物から簡単且つ確実に剥離することができる。As described above in detail, according to the present invention, it is possible to provide a protective film excellent in releasability on an antifouling object, and to apply the protective film after adhesion of oil stains. It can be easily and surely peeled from the stainproof object.
【図1】本発明の第1の方法における、防汚対象物の表
面に保護被膜が形成された状態の要部断面図である。FIG. 1 is a cross-sectional view of essential parts in a state in which a protective coating is formed on the surface of an antifouling target in the first method of the present invention.
【図2】油汚れが付着した保護被膜を剥離する過程を示
す要部断面図である。FIG. 2 is a cross-sectional view of a main part showing a process of peeling off a protective film having oil stains attached thereto.
【図3】本発明の第2の方法における、防汚対象物の表
面に保護被膜が形成された状態の要部断面図である。FIG. 3 is a cross-sectional view of essential parts in a state in which a protective coating is formed on the surface of an antifouling object in the second method of the present invention.
1 防汚対象物 2,12 保護被
膜 3a,3b,13 塗料 4 繊維シート 5 油汚れ 14 繊維1 Antifouling target 2,12 Protective coating 3a, 3b, 13 Paint 4 Fiber sheet 5 Oil stain 14 Fiber
Claims (2)
剥離性のある塗料を塗布し、該塗料が乾かないうちに繊
維シートを被覆してその上から再び塗料を塗布すること
により、繊維シートで強化された塗料による保護被膜を
形成し、油汚れの付着後に該保護被膜を防汚対象物から
剥離することを特徴とする油汚れの除去方法。1. A method in which a paint having releasability is applied to the surface of an antifouling object to which oil stains easily adhere, and the fiber sheet is coated before the paint is dried, and the paint is applied again from above. Forming a protective coating made of a paint reinforced with a fiber sheet, and removing the protective coating from an antifouling object after the oily dirt is attached.
に、補強用の繊維を混合した剥離性のある塗料を塗布す
ることにより、繊維で強化された塗料による保護被膜を
形成し、油汚れの付着後に該保護被膜を防汚対象物から
剥離することを特徴とする油汚れの除去方法。2. A protective coating of a fiber-reinforced paint is formed by applying a releasable paint mixed with reinforcing fibers to the surface of an antifouling object to which oil stains easily adhere. A method for removing oil stains, which comprises peeling the protective coating from an object to be soiled after the oil stains are attached.