JP2611062B2 - Housing for waterproof connector and method of manufacturing the same - Google Patents
Housing for waterproof connector and method of manufacturing the sameInfo
- Publication number
- JP2611062B2 JP2611062B2 JP3204221A JP20422191A JP2611062B2 JP 2611062 B2 JP2611062 B2 JP 2611062B2 JP 3204221 A JP3204221 A JP 3204221A JP 20422191 A JP20422191 A JP 20422191A JP 2611062 B2 JP2611062 B2 JP 2611062B2
- Authority
- JP
- Japan
- Prior art keywords
- housing
- ring
- organopolysiloxane
- primer layer
- silicone rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、雌，雄コネクタ間にリ
ング状パッキンを介在させるいわゆる防水コネクタに使
用される防水コネクタ用ハウジングおよびその製造方法
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a waterproof connector housing used for a so-called waterproof connector in which a ring-shaped packing is interposed between a female connector and a male connector, and a method of manufacturing the same.
【０００２】[0002]
【従来の技術】防水コネクタは雌，雄コネクタの嵌合面
に別部品としてのリング状パッキンを介在させるのが一
般的であるが、パッキンの装着が面倒であり、その作業
時に脱落しやすいなどの欠点がある。これを解消するた
め、図４のように雌コネクタａの嵌合枠ｂの内部にリン
グ状パッキンｃを一体的に形成するか、あるいは図５の
ように雄コネクタｄにおける雌コネクタａ′に対する二
重嵌合枠ｅの内部にリング状パッキンｃ′を一体的に形
成すると共に、ゴム材に接着性のある材料を加えて該パ
ッキンｃ，ｃ′に接着性をもたせて防水シール性をよく
することが知られている（特開昭６３−２２１５６８号
公報）。しかし、ゴム材に接着性をもたせると、金型に
も接着してしまい、これを避けるため金型にフッ素コー
ティング等の表面処理を施しても耐久性がない等の問題
があり、実用化が困難であった。2. Description of the Related Art In general, a ring-shaped packing as a separate component is interposed on a mating surface of a female connector and a male connector in a waterproof connector. However, the mounting of the packing is troublesome, and the connector easily falls off during the work. There are disadvantages. In order to solve this problem, a ring-shaped packing c is integrally formed inside the fitting frame b of the female connector a as shown in FIG. A ring-shaped packing c 'is integrally formed inside the heavy fitting frame e, and an adhesive material is added to a rubber material so that the packings c and c' have an adhesive property to improve waterproof sealing properties. (Japanese Patent Laid-Open No. 63-221568). However, if the rubber material is provided with adhesiveness, it also adheres to the mold, and there is a problem that the mold is not durable even if subjected to a surface treatment such as fluorine coating to avoid this. It was difficult.
【０００３】また、合成樹脂製のコネクタハウジング
（以下、単にハウジングという）は、ＰＢＴ，６ーナイ
ロン，６，６ーナイロンなどの熱可塑性樹脂製で、非強
化樹脂を使用するため、射出圧力、ゴムを加硫する
ための金型温度、加硫時間によってパッキンをハウジ
ングと一体成形する際に、ハウジングが変形したり、或
いはパッキン成形品にバリがでる、などの問題があっ
た。A connector housing made of a synthetic resin (hereinafter simply referred to as a housing) is made of a thermoplastic resin such as PBT, 6-nylon and 6,6-nylon, and uses an unreinforced resin. When the packing is integrally molded with the housing depending on the mold temperature and the vulcanization time for vulcanization, there have been problems such as deformation of the housing or burrs on the molded packing product.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記の問題
点に着目してなされたもので、防水シール性がよく、成
形が容易なリング状パッキンを備えた防水コネクタ用ハ
ウジングおよびその製造方法を提供することを課題とす
る。もう一つの課題は、ハウジングの変形を防止し、成
形精度のすぐれたリング状パッキンを一体的に備えた防
水コネクタ用ハウジングを提供するにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and is provided with a waterproof connector housing having a ring-shaped packing which has good waterproof sealability and is easy to mold, and a method of manufacturing the same. The task is to provide Another object of the present invention is to provide a waterproof connector housing which is integrally provided with a ring-shaped packing which prevents deformation of the housing and has excellent molding accuracy.
【０００５】[0005]
【課題を解決するための手段】前記の課題を達成するた
め、本発明の防水コネクタ用ハウジングは、請求項１に
記載したように、前部に相手方コネクタを受入れる嵌合
枠を有するハウジングであって、該嵌合枠の嵌合面側の
壁面にリング状にオルガノポリシロキサン系プライマー
層を形成させ、該オルガノポリシロキサン系プライマー
層上に付加反応型液状シリコーンゴム層を形成させ、該
シリコーンゴム層のオルガノポリシロキサン系プライマ
ー層への加硫接着によりリング状パッキンをハウジング
と一体的に形成させたことを特徴とする。この防水コネ
クタ用ハウジングの製造は、請求項２に記載したよう
に、次の工程ａ）〜ｅ）： ａ）前部に相手方コネクタを受入れる嵌合枠を有するハ
ウジングの該嵌合枠の少なくとも嵌合面側の壁面にリン
グ状にオルガノポリシロキサン系プライマーを付着させ
る工程、 ｂ）付着したオルガノポリシロキサン系プライマーを乾
燥してリング状のオルガノポリシロキサン系プライマー
層を形成する工程、 ｃ）このオルガノポリシロキサン系プライマー層付のハ
ウジングを雌金型とリング状パッキンに相当する空所を
有する雄金型との間にセットする工程、 ｄ）該空所内に液状シリコーンゴムを注入して加硫接着
によりリング状パッキンを形成する工程、および ｅ）雌，雄の金型をはずしてハウジングと一体的にリン
グ状パッキンが形成された成形品を取り出す工程により
行なわれる。In order to achieve the above object, a waterproof connector housing according to the present invention is a housing having a fitting frame for receiving a mating connector at a front portion. Te, to form an organopolysiloxane-based primer layer on the wall surface of the fitting surface side of the fitting frame in a ring, to form an addition reaction type liquid silicone rubber layer in the organopolysiloxane-based primer layer, the silicone rubber characterized in that to form a ring packing in the housing and integrally by vulcanization bonding to the organopolysiloxane primer <br/> over layers of the layer. The manufacturing of the housing for a waterproof connector includes the following steps a) to e): a) At least fitting of the fitting frame of the housing having a fitting frame for receiving a mating connector at a front portion. step of the wall surface of the mating surface side attaching an organopolysiloxane-based primer in a ring shape, b) forming a organopolysiloxane primer layer by drying an organopolysiloxane-based primer adhering ring, c) the organo Setting a housing with a polysiloxane primer layer between a female mold and a male mold having a space corresponding to a ring-shaped packing; d) pouring liquid silicone rubber into the space and vulcanizing adhesion And e) removing the female and male molds to form a ring-shaped packing integrally with the housing. It carried out by a process taking out the molded article.
【０００６】[0006]
【作用】リング状パッキンは、予めコネクタ用ハウジン
グに設けたオルガノポリシロキサン系プライマー層上に
リング状に付加反応型液状シリコーンゴム層を形成し、
その加硫接着により形成されるから、ハウジングと一体
であり、脱落のおそれがなく、良好な防水シール性が得
られる。The ring-shaped packing is formed by forming an addition-reaction-type liquid silicone rubber layer in a ring shape on an organopolysiloxane-based primer layer previously provided on a connector housing,
Since it is formed by the vulcanization bonding, it is integral with the housing, there is no risk of falling off, and good waterproof sealing properties can be obtained.
【０００７】[0007]
【実施例】図１（Ａ），（Ｂ）において、１は合成樹脂
製の雄コネクタ用ハウジングであって、その外周には図
５に示すような相手方雌コネクタに対する嵌合枠２が設
けられている。このハウジング１は、６，６−ナイロ
ン、６−ナイロン、ＰＢＴなどの熱可塑性樹脂、あるい
はＰＦ，ＰＩ，ＵＰなどの熱硬化性樹脂により、予め所
望の形状に成形されている。また、ハウジング１は、前
述のように予め着色した状態で成形してもよいが、本実
施例では、樹脂材料の有する自然色で成形してある。1A and 1B, reference numeral 1 denotes a synthetic resin housing for a male connector, and a fitting frame 2 for a mating female connector as shown in FIG. ing. The housing 1 is formed in advance into a desired shape using a thermoplastic resin such as 6,6-nylon, 6-nylon, or PBT, or a thermosetting resin such as PF, PI, or UP. Although the housing 1 may be molded in a previously colored state as described above, in the present embodiment, the housing 1 is molded with the natural color of the resin material.
【０００８】ハウジング１の上記嵌合枠２を含めた内外
表面にはオルガノポリシロキサン系プライマー層３が形
成され、嵌合枠２の嵌合面側の壁面、すなわち底部２ａ
と立ち上り基部２ｂとの内面に付加反応型液状シリコー
ンゴムより成るリング状パッキン４がオルガノポリシロ
キサン系プライマー層３に加硫接着されてハウジング１
と一体的に形成されている。なお、１ａおよび１ｂは、
ハウジング１に設けられた後述する液状シリコーンゴム
に対する注入口と溢流口であって、両口１ａ，１ｂ内に
はリング状パッキン４と一体の突起部５が残留してい
る。また、リング状パッキン４の内面には凸部４ａと凹
部４ｂとからなる環状の凹凸面が形成され、相手方コネ
クタに対する嵌合性および密着性をよくしてある。An organopolysiloxane-based primer layer 3 is formed on the inner and outer surfaces of the housing 1 including the fitting frame 2, and a wall surface on the fitting surface side of the fitting frame 2, that is, a bottom 2a.
A ring-shaped gasket 4 made of the addition reaction type liquid silicone rubber to the inner surface of the base portion 2b rises organopolysiloxane white
The housing 1 is vulcanized and adhered to the xane-based primer layer 3.
And are formed integrally with it. 1a and 1b are:
Injection ports and overflow ports for liquid silicone rubber described later provided in the housing 1, and a projection 5 integral with the ring-shaped packing 4 remains in both ports 1 a and 1 b. The inner surface of the ring-shaped packing 4 is formed with an annular concave and convex surface composed of a convex portion 4a and a concave portion 4b, so that the fitting and the close contact with the mating connector are improved.
【０００９】付加反応型液状シリコーンゴムから成るリ
ング状パッキン４は、従来とは異なり防水性向上のため
の接着性を有する材料の添加を要しないので、成形金型
に接着したり、金型のフッ素コーティング処理といった
問題がない。また、ハウジング１と一体的に形成されて
いるから、ハウジング１への装着といった面倒な手間が
かからず、脱落のおそれがないので、確実な防水シール
性が得られる。The ring-shaped packing 4 made of an addition-reaction-type liquid silicone rubber does not require the addition of a material having an adhesive property for improving waterproofness unlike the related art. There is no problem such as fluorine coating. Further, since it is formed integrally with the housing 1, there is no need for troublesome mounting such as mounting on the housing 1, and there is no fear of falling off, so that a reliable waterproof sealing property can be obtained.
【００１０】次に、リング状パッキン４をもつハウジン
グの製造方法について説明する。最初に、成形品である
ハウジング１を付加反応型液状シリコーンゴムに対する
オルガノポリシロキサン系プライマー液の中に浸漬し、
嵌合枠２を含めてその内外全表面にプライマーを付着さ
せ、引き上げ後、常温常湿で４０〜５０時間放置するこ
とにより、前記プライマー層４を形成する。このオルガ
ノポリシロキサン系プライマー層４は、リング状パッキ
ン４のみを形成するためには、図１における嵌合枠２の
嵌合面側壁面である底部２ａと立ち上り基部２ｂの内面
に環状に付着させれば足りる。しかし、付着作業の容易
性および自然色のハウジング１に対する着色の点から、
プライマー液中に浸漬してもよい。Next, a method of manufacturing a housing having the ring-shaped packing 4 will be described. First, the housing 1, which is a molded product, is attached to the addition-reaction-type liquid silicone rubber.
Immerse in an organopolysiloxane primer solution,
The primer is adhered to the entire inner and outer surfaces including the fitting frame 2, pulled up, and left at room temperature and normal humidity for 40 to 50 hours to form the primer layer 4. This Olga
In order to form only the ring-shaped packing 4, the nopolysiloxane- based primer layer 4 is annularly attached to the bottom surface 2a, which is the side wall of the fitting surface of the fitting frame 2, and the inner surface of the rising base 2b in FIG. Is enough. However, from the viewpoint of the easiness of the attaching work and the coloring of the housing 1 having a natural color,
It may be immersed in a primer solution.
【００１１】本発明で使用するオルガノポリシロキサン
系プライマー液は、一般式（１）：The organopolysiloxane used in the present invention
The system primer solution has the general formula (1):
【化１】 （式中、Ｘは炭素数２〜４の不飽和炭化水素、Ｒは炭素
数１〜５のアルキル基を表す。）で示されるオルガノポ
リシロキサンを主成分とし、この主成分と脂肪族炭化水
素例えばｎ−ヘキサン，イソオクタンなどの溶剤および
縮合触媒から構成される混合物であり、ＤＹ３９−０６
７プライマー（東レダウコーニング製）などの市販品を
そのまま使用することができる。そして、ハウジング１
に着色する場合には、前記プライマー液に顔料をミクロ
分散させたものを用いる。顔料としては、例えばベンガ
ラ（茶）、群青（青）が使用される。Embedded image (Wherein, X represents an unsaturated hydrocarbon having 2 to 4 carbon atoms, and R represents an alkyl group having 1 to 5 carbon atoms). For example, DY39-06 is a mixture composed of a solvent such as n-hexane and isooctane and a condensation catalyst.
Commercially available products such as 7 primers (manufactured by Toray Dow Corning) can be used as they are. And the housing 1
In the case where the pigment is colored, a pigment solution micro-dispersed in the primer liquid is used. As the pigment, for example, red iron (brown) and ultramarine (blue) are used.
【００１２】オルガノポリシロキサン系プライマー液に
浸漬したハウジング１は、引上げ後、前記常温常湿での
乾燥処理により、空気中の水分による一般式（１）のポ
リオルガノシロキオサンの加水分解および縮合がはじま
り、強固なオルガノポリシロキサン系プライマー層３が
形成される。また、オルガノポリシロキサン系プライマ
ー液に予め顔料を配合したものは、オルガノポリシロキ
サン系プライマー層形成と同時にハウジング１全体が所
望の色に着色される。この着色は、上記オルガノポリシ
ロキサン系プライマーの縮合により堅牢で、剥離や褐色
のおそれがなく、容易に行うことができる。After the housing 1 immersed in the organopolysiloxane-based primer solution is pulled up, the housing is dried at the ordinary temperature and normal humidity, whereby the hydrolysis and condensation of the polyorganosiloxosan of the general formula (1) by the moisture in the air are performed. Starting, a strong organopolysiloxane-based primer layer 3 is formed. In addition, those in which a pigment is previously blended with an organopolysiloxane-based primer liquid are used as an organopolysiloxane.
At the same time as the formation of the sun-based primer layer, the entire housing 1 is colored in a desired color. This coloring is based on the above-mentioned organopolicy.
It is robust due to the condensation of the oxane-based primer and can be easily carried out without fear of peeling or browning.
【００１３】次に、オルガノポリシロキサン系プライマ
ー層３を形成したハウジング１を図２（Ａ）のように雌
金型６と雄金型７にセットし、型を締める。雄金型７の
先端部にはリング状パッキン４に対応する空所Ｖを形成
するための環状凹部７ａが設けられ、また雌金型６には
前記注入口１ａと溢流口１ｂに連通する位置に液状シリ
コーンゴム（生ゴム）の供給路６ａと溢流路６ｂが設け
られている。金型の温度は８０〜１５０℃、好ましくは
１１０〜１３０℃に予め設定しておく。Next, the housing 1 on which the organopolysiloxane-based primer layer 3 is formed is set in a female mold 6 and a male mold 7 as shown in FIG. 2A, and the mold is closed. An annular concave portion 7a for forming a space V corresponding to the ring-shaped packing 4 is provided at the tip of the male mold 7, and the female mold 6 communicates with the inlet 1a and the overflow 1b. A supply path 6a for liquid silicone rubber (raw rubber) and an overflow path 6b are provided at positions. The temperature of the mold is preset at 80 to 150 ° C, preferably 110 to 130 ° C.
【００１４】次いで、供給路６ａから雌、雄の金型６，
７間に液状シリコーンゴムを注入し、所定の条件で加硫
し、前記オルガノポリシロキサン系プライマー層３への
接着と同時にリング状パッキン４を成形によりハウジン
グ１と一体的に形成する。Next, female and male molds 6 are supplied from the supply path 6a.
Liquid silicone rubber is poured into the gap 7 and vulcanized under predetermined conditions. At the same time as the adhesion to the organopolysiloxane primer layer 3, the ring-shaped packing 4 is formed integrally with the housing 1 by molding.
【００１５】液状シリコーンゴムとしては、付加反応型
シリコーンゴム、好ましくは二液混合型低温高速付加反
応型液状シリコーンゴムであって、かつオイルブリード
タイプのものが使用される。この二液混合型の付加反応
型液状シリコーンゴムは、Ａ液とＢ液の二液から成る。
Ａ液は、一般式（２）：As the liquid silicone rubber, an addition reaction type silicone rubber, preferably a two-component mixed type low temperature and high speed addition reaction type liquid silicone rubber and an oil bleed type are used. The two-component addition-type liquid silicone rubber is composed of two components, a component A and a component B.
The liquid A has the general formula (2):
【化２】 （式中、Ｒはメチル基またはフェニル基を表す。）で示
されるオルガノポリシロキサン（以下、単にビニルポリ
マーともいう）を主成分とする。Ｂ液は、一般式
（３）：Embedded image (In the formula, R represents a methyl group or a phenyl group.) An organopolysiloxane (hereinafter, also simply referred to as a vinyl polymer) represented by the following formula is a main component. The liquid B has the general formula (3):
【化３】 （式中、Ｒは前記と同じ意味をもつ。）で示されるオル
ガノポリシロキサン（以下、単に水素ポリマーともい
う）を主成分とする。Embedded image (Wherein, R has the same meaning as described above) as a main component.
【００１６】また、Ａ液およびＢ液は、それぞれ少量の
フィラーと共に耐熱剤その他の添加剤を含有し、Ａ液に
は前記ビニルポリマーと水素ポリマーの架橋重合のため
の白金触媒が配合されている。The liquids A and B each contain a small amount of filler and a heat-resistant agent and other additives, and the liquid A contains a platinum catalyst for crosslinking polymerization of the vinyl polymer and the hydrogen polymer. .
【００１７】図３は本発明によるハウジングの製造に使
用する装置の一例を示す概略説明図である。図におい
て、８はＡ液の貯槽、９は後述するＣ液の貯槽、１０は
Ｂ液の貯槽を示す。Ａ液とＢ液はポンプＰ1 とＰ3 によ
りラインＲ1 ，Ｒ3 を経て計量装置１１に移送されて個
別に計量した後、射出装置１２の作動により同時に混合
装置１３に送り込まれ、ここで強制的に二液混合した
後、図２（Ａ）に示すように雌．雄の金型６，７に射
出、注入される。FIG. 3 is a schematic explanatory view showing an example of an apparatus used for manufacturing a housing according to the present invention. In the figure, reference numeral 8 denotes a storage tank for the liquid A, 9 denotes a storage tank for the liquid C described later, and 10 denotes a storage tank for the liquid B. A liquid and B liquid was individually weighed is transported to the metering device 11 via line R 1, R 3 by a pump P 1 and P 3, is fed to the mixing device 13 at the same time by the operation of the injection apparatus 12, where After the two liquids were forcibly mixed, as shown in FIG. Injected and injected into male dies 6,7.
【００１８】注入された上記二液混合型液状シリコーン
ゴムの加硫温度は８０〜１５０℃、好ましくは１１０〜
１３０℃である。１５０℃より高温では母体であるハウ
ジング１が熱のため変形し、また、８０℃より低温で加
硫する材料は、常温でも加硫してしまい、熱安定性が悪
い。加硫時間は、上記の加硫温度で、１０〜１２０秒、
好ましいのは３０〜９０秒である。加硫時間が短いもの
は、常温でも加硫し、材料の安定性が悪く、長すぎるも
のはハウジングが変形しやすくなる。さらに、上記Ａ液
とＢ液の粘度は、ともに３００〜８０００ポイズ、好ま
しいのは７００〜５０００ポイズである。粘度が低すぎ
ると、成形時にバリが発生しやすく、逆に高すぎると、
射出圧力によりハウジングが変形するおそれがある。な
お、射出成形圧力は、通常５〜５０Kg/cm2に設定され
る。The vulcanization temperature of the injected two-part liquid silicone rubber is 80 to 150 ° C., preferably 110 to 110 ° C.
130 ° C. If the temperature is higher than 150 ° C., the base body 1 is deformed due to heat, and a material that is vulcanized at a temperature lower than 80 ° C. is vulcanized even at room temperature, and has poor thermal stability. The vulcanization time is 10 to 120 seconds at the above vulcanization temperature,
Preferred is 30 to 90 seconds. If the vulcanization time is short, vulcanization occurs at room temperature, and the stability of the material is poor. If the vulcanization time is too long, the housing is easily deformed. Further, the viscosities of the above-mentioned liquids A and B are both 300 to 8,000 poise, preferably 700 to 5,000 poise. If the viscosity is too low, burrs are likely to occur during molding, and if it is too high,
The housing may be deformed by the injection pressure. The injection molding pressure is usually set at 5 to 50 kg / cm 2 .
【００１９】上記のオルガノポリシロキサン系プライマ
ー乾燥工程および加硫工程により、液状シリコーンゴム
の被着体であるハウジング表面の−ＯＨ基とオルガノポ
リシロキサン系プライマー層上の−ＯＨ基同志の水素結
合により、被着体とプライマー層とが接着し、一方液状
シリコーンゴム中のＳｉＨ基とオルガノポリシロキサン
系プライマー中のビニル基との付加反応により液状シリ
コーンゴムとプライマーが接着する。これにより、図２
（Ｂ）に示すようにリング状パッキン４がハウジング１
に一体的に形成される。The above-mentioned organopolysiloxane-based primer-drying step and vulcanizing step cause --OH groups on the surface of the housing, which is a liquid silicone rubber adherend, to the organopolysiloxane.
The adherend adheres to the primer layer by hydrogen bonds between the -OH groups on the siloxane-based primer layer, while the SiH groups in the liquid silicone rubber and the organopolysiloxane
The liquid silicone rubber and the primer adhere to each other by an addition reaction with a vinyl group in the system primer. As a result, FIG.
As shown in (B), the ring-shaped packing 4 is
Are formed integrally.
【００２０】最後に、雌、雄の金型６，７をはずしてハ
ウジング１と一体的にリング状パッキン４が形成された
成形品を取り出す。このリング状パッキン４は、前述し
た加硫・接着条件により、ハウジング１の変形を伴わ
ず、パッキンのバリがなく、成形しやすくて生産性にす
ぐれ、防水性能の良好なものが得られる。Finally, the female and male dies 6 and 7 are removed, and the molded product on which the ring-shaped packing 4 is formed integrally with the housing 1 is taken out. Due to the above-described vulcanization and bonding conditions, the ring-shaped packing 4 does not involve deformation of the housing 1, has no burr of the packing, is easy to mold, has excellent productivity, and has good waterproof performance.
【００２１】リング状パッキン４に着色する場合には、
前記Ａ液およびＢ液にＣ液を混合して射出成形する。Ｃ
液は着色顔料をシリコーンオイルに分散させたものであ
る。Ａ液またはＢ液にシリコーンオイルを添加すると、
保存中に分離するおそれがあり、成形不良の原因とな
る。しかし、射出成形直前にＡ，Ｂの二液と混合するこ
とにより、上記の問題が解消するうえに、Ａ，Ｂの二液
に対するＣ液の添加量を変えることにより、例えばＡ液
１００容量％およびＢ液１００容量％に対してＣ液を５
〜３０容量％、好ましくは１０〜２０容量％を添加する
ことにより、含油量を簡単に調整し、加硫接着後表面に
油がにじみでた所望の色に着色されたリング状パッキン
が得られる。When coloring the ring-shaped packing 4,
The liquid A and the liquid B are mixed with the liquid C to perform injection molding. C
The liquid is obtained by dispersing a coloring pigment in silicone oil. When silicone oil is added to liquid A or liquid B,
There is a risk of separation during storage, leading to molding failure. However, by mixing the two liquids A and B immediately before injection molding, the above-mentioned problem is solved. In addition, by changing the amount of the liquid C added to the two liquids A and B, for example, 100% by volume of the liquid A 5% of solution C to 100% by volume of solution B
By adding 量 30% by volume, preferably ２０20% by volume, the oil content can be easily adjusted to obtain a ring-shaped packing colored in a desired color with oil oozing on the surface after vulcanization bonding. .
【００２２】Ｃ液の添加混合は、図３において前記Ａ液
およびＢ液と共に貯槽９からＣ液をポンプＰ2 によりラ
インＲ2 を経て計量装置１１に移送し、前記と同様に個
別に計量後、Ａ，Ｂ，Ｃの三液を混合して射出成形すれ
ばよく、前記の加硫条件に従って加硫する。これによ
り、所望の色のリング状パッキンがハウジングと一体的
に形成される。The addition and mixing of the C solution, the solution A and transferred together with the liquid B from the reservoir 9 to C liquid metering device 11 via line R 2 by pump P 2 in FIG. 3, the same manner as described above after individually metered , A, B and C may be mixed and injection molded, and vulcanization is performed according to the above vulcanization conditions. Thereby, a ring-shaped packing of a desired color is formed integrally with the housing.
【００２３】[0023]
【発明の効果】以上説明したように、本発明によれば、
コネクタ用ハウジングの嵌合枠内に設けられるリング状
パッキンは、オルガノポリシロキサン系プライマー層上
に形成した付加反応型液状シリコーンゴム層を加硫接着
することにより形成されるので、パッキンがハウジング
から脱落するおそれがなく、確実な防水シールを行うこ
とができる。成形に際し、接着性のある材料を液状シリ
コーンゴムに別途に添加する必要もないので、従来のよ
うに金型に接着するなどの不具合もなく成形が容易であ
り、生産性も向上する。また、ハウジングの変形やリン
グ状パッキンのバリがなく、熱安定性のよい製品が得ら
れる。As described above, according to the present invention,
The ring-shaped packing provided in the fitting frame of the connector housing is formed by vulcanizing and bonding the addition-reaction-type liquid silicone rubber layer formed on the organopolysiloxane-based primer layer. There is no danger that a waterproof seal can be performed. Since there is no need to separately add an adhesive material to the liquid silicone rubber during molding, molding is easy without problems such as adhesion to a mold as in the conventional art, and productivity is improved. In addition, there is no deformation of the housing and no burr of the ring-shaped packing, and a product having good heat stability can be obtained.
【図１】（Ａ）は本発明の一実施例を示すコネクタ用ハ
ウジングの要部断面図、（Ｂ）はリング状パッキンの部
分拡大断面図である。FIG. 1A is a sectional view of a main part of a connector housing showing one embodiment of the present invention, and FIG. 1B is a partially enlarged sectional view of a ring-shaped packing.
【図２】（Ａ）は本発明の製造方法におけるハウジング
の金型へのセット状態を示す概略断面図、（Ｂ）はリン
グ状パッキンの成形状態を示す概略断面図である。FIG. 2A is a schematic sectional view showing a state in which a housing is set in a mold in the manufacturing method of the present invention, and FIG. 2B is a schematic sectional view showing a state in which a ring-shaped packing is formed.
【図３】本発明を実施する装置の一例を示す概略説明図
である。FIG. 3 is a schematic explanatory view showing an example of an apparatus for implementing the present invention.
【図４】従来の防水コネクタにおける雌コネクタの一例
を示す断面図である。FIG. 4 is a sectional view showing an example of a female connector in a conventional waterproof connector.
【図５】従来の防水コネクタにおける雌，雄のコネクタ
を示す断面図である。FIG. 5 is a sectional view showing female and male connectors in a conventional waterproof connector.
１ 雄コネクタ用ハウジング ２ 嵌合枠 ２ａ 底部 ２ｂ 立ち上り基部 ３ オルガノポリシロキサン系プライマー層 ４ リング状パッキン ６ 雌金型 ７ 雄金型DESCRIPTION OF SYMBOLS 1 Male connector housing 2 Fitting frame 2a Bottom 2b Rise base 3 Organopolysiloxane primer layer 4 Ring packing 6 Female mold 7 Male mold
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ２９Ｌ 31:36 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code Agency reference number FI Technical display location B29L 31:36
Claims (2)
を有するハウジングであって、該嵌合枠の嵌合面側の壁
面にリング状にオルガノポリシロキサン系プライマー層
を形成させ、該オルガノポリシロキサン系プライマー層
上に付加反応型液状シリコーンゴム層を形成させ、該シ
リコーンゴム層のオルガノポリシロキサン系プライマー
層への加硫接着によりリング状パッキンをハウジングと
一体的に形成させたことを特徴とする防水コネクタ用ハ
ウジング。1. A housing having a mating frame for receiving the mating connector to the front, to form an organopolysiloxane-based primer layer on the wall surface of the fitting surface side of the fitting frame in a ring shape, said Oruganopori siloxane to form an addition reaction type liquid silicone rubber layer on the primer layer, and characterized in that to form a ring packing integrally with the housing by vulcanization bonding to the organopolysiloxane-based primer layer of the silicone rubber layer Waterproof connector housing.
ウジングの該嵌合枠の少なくとも嵌合面側の壁面にリン
グ状にオルガノポリシロキサン系プライマーを付着させ
る工程、 ｂ）付着したオルガノポリシロキサン系プライマーを乾
燥してリング状オルガノポリシロキサン系のプライマー
層を形成する工程、 ｃ）このオルガノポリシロキサン系プライマー層付のハ
ウジングを雌金型とリング状パッキンに相当する空所を
有する雄金型との間にセットする工程、 ｄ）該空所内に液状シリコーンゴムを注入して加硫接着
によりリング状パッキンを形成する工程、および ｅ）雌，雄の金型をはずしてハウジングと一体的にリン
グ状パッキンが形成された成形品を取り出す工程を含む
ことを特徴とする防水コネクタ用ハウジングの製造方
法。2. The following steps a) to e): a) a ring-shaped organopolysiloxane-based material on at least a wall surface on a fitting surface side of a fitting frame of a housing having a fitting frame for receiving a mating connector at a front portion. B) drying the attached organopolysiloxane-based primer to form a ring-shaped organopolysiloxane-based primer layer; c) housing the organopolysiloxane-based primer layer with a female mold. A step of setting between a male mold having a space corresponding to a ring-shaped packing, d) a step of injecting liquid silicone rubber into the space to form a ring-shaped packing by vulcanization bonding, and e) a female Removing the molded product having the ring-shaped packing formed integrally with the housing by removing the male mold. Method of manufacturing data for housing.