JP2583318B2 - Antistatic sheet for floor - Google Patents
Antistatic sheet for floorInfo
- Publication number
- JP2583318B2 JP2583318B2 JP1227144A JP22714489A JP2583318B2 JP 2583318 B2 JP2583318 B2 JP 2583318B2 JP 1227144 A JP1227144 A JP 1227144A JP 22714489 A JP22714489 A JP 22714489A JP 2583318 B2 JP2583318 B2 JP 2583318B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- floor
- antistatic
- sheet
- antistatic effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、床用帯電防止シートに関する。さらに詳細
には、接着性及び剥離性に優れた再剥離性フォームシー
ト層を有する床用帯電防止シートに関する。The present invention relates to an antistatic flooring sheet. More specifically, the present invention relates to an antistatic flooring sheet having a removable foam sheet layer excellent in adhesiveness and releasability.
近年の電子機器の普及から、フリーアクセスタイプの
二重床を設けた建物が増えつつある。そして、この床材
の仕上材の表面を保護する目的で、帯電防止効果を有す
る床用被覆材が開発されている（特開平１−132098
号）。Due to the spread of electronic devices in recent years, buildings with free-access double floors are increasing. For the purpose of protecting the surface of the finishing material of the floor material, a floor covering material having an antistatic effect has been developed (Japanese Patent Laid-Open No. 1-132098).
issue).
この床用被覆材は、従来からの所謂フロアーポリッシ
ュと異なり、パウダリングの問題を生じず、かつ剥離時
に液状の剥離剤を用いる必要がない等の利点を有してい
る。This floor covering material has advantages that, unlike a conventional so-called floor polish, there is no problem of powdering, and there is no need to use a liquid peeling agent at the time of peeling.
しかるに、この床用被覆材は、帯電防止フィルムを床
に固定するための手段として、接着剤を用いており、床
からの剥離が必ずしも容易であったとは言いがたい。However, this floor covering material uses an adhesive as a means for fixing the antistatic film to the floor, and it cannot be said that peeling off the floor was always easy.
そこで本発明の目的は、床からの剥離が容易であり、
かつ使用時には床に強力に密着して、床材の仕上材表面
を保護することができる床用帯電防止シートを提供する
ことにある。Therefore, the object of the present invention is easy to peel from the floor,
Another object of the present invention is to provide an antistatic sheet for floors that can strongly adhere to a floor when used and protect the surface of a finishing material of flooring.
本発明は、帯電防止効果を有するフィルムの一方の面
に１〜100g/3cmの密着力を有する軟質ポリウレタンフォ
ームからなる再剥離性フォームシート層を有する床用帯
電防止シートに関する。The present invention relates to an antistatic flooring sheet having a removable polyurethane foam sheet layer made of a flexible polyurethane foam having an adhesion of 1 to 100 g / 3 cm on one surface of a film having an antistatic effect.
以下本発明について詳細に説明する。 Hereinafter, the present invention will be described in detail.
本発明に用いる「帯電防止効果を有するフィルム」と
は、1012Ω以下の表面抵抗値を有するフィルムである。
このような表面抵抗値を有するフィルムであれば、帯電
によるコンピューター等に対するノズル等が起こり難い
からである。さらに上記フィルムは、108Ω以下の表面
抵抗値を有するものが特に好ましい。また、上記フィル
ムはの内部抵抗は、1013Ω以下であることが好ましい。The “film having an antistatic effect” used in the present invention is a film having a surface resistance of 10 12 Ω or less.
This is because a film having such a surface resistance hardly causes a nozzle or the like to a computer or the like due to charging. Further, it is particularly preferable that the film has a surface resistance of 10 8 Ω or less. The film preferably has an internal resistance of 10 13 Ω or less.
帯電防止効果を有するフィルムとしては、例えば、界
面活性剤、導電性微粒子及び導電性繊維の少なくとも１
種を含有するフィルムを挙げることができる。基体であ
るフィルムの材質には特に制限はなく、有機高分子体で
あればよい。例えば、ポリ塩化ビニル、ポリエチレン、
ポリカーボネート、アクリル樹脂、ポリスチレン、ポリ
エステル、ナイロン、ポリプロピレン、ポリウレタン、
ABS及びこれらの樹脂を構成するモノマーの２種以上か
らなるコポリマーを挙げることができる。さらに、上記
フィルムは、これらの樹脂の２種以上をラミネートした
フィルムでもよい。Examples of the film having an antistatic effect include at least one of a surfactant, conductive fine particles, and conductive fibers.
Mention may be made of seed-containing films. The material of the base film is not particularly limited, and may be any organic polymer. For example, polyvinyl chloride, polyethylene,
Polycarbonate, acrylic resin, polystyrene, polyester, nylon, polypropylene, polyurethane,
ABS and copolymers composed of two or more monomers constituting these resins can be mentioned. Further, the film may be a film obtained by laminating two or more of these resins.
このフィルムは、フィルム状のもの及び織物状のもの
であってもよい。The film may be in the form of a film or a fabric.
本発明で用いる帯電防止効果を有するフィルムは、ヌ
ープ硬度が３〜20KHN、好ましくは８〜15KHNであること
が、床用として用いるという観点から好ましい。ヌープ
硬度を3KHN以上とすることにより、長期間使用すること
が可能となる。即ち、歩行者が歩行時に靴によって床に
与える衝撃によっても本発明のシートが傷付くことがな
く、かつ光沢の低下、汚れのくい込み等により美観が損
なわれることもない。またヌープ硬度を20KHN以下とす
ることにより、歩行者が歩行時に靴によって床に与える
衝撃によっても本発明のシートが割れることがなく、か
つ歩行者の滑りも防止できる。It is preferable that the film having an antistatic effect used in the present invention has a Knoop hardness of 3 to 20 KHN, preferably 8 to 15 KHN from the viewpoint of use for floors. By setting the Knoop hardness to 3 KHN or more, it is possible to use the device for a long time. That is, the sheet of the present invention is not damaged by the impact that the pedestrian gives to the floor with the shoes when walking, and the aesthetic appearance is not impaired due to a decrease in gloss, penetration of dirt, and the like. Further, by setting the Knoop hardness to 20 KHN or less, the sheet of the present invention is not broken even by an impact given to the floor by shoes by a pedestrian during walking, and slippage of the pedestrian can be prevented.
さらに、本発明で用いる帯電防止効果を有するフィル
ムは、テーバー試験方法（荷重1000g、摩耗輪CS−17、
回転数500rpm）で、摩耗減量100mg以下、好ましくは50m
g以下であるものが耐久性の点から好ましい。Furthermore, the film having an antistatic effect used in the present invention, the Taber test method (1000 g load, wear wheel CS-17,
At a rotation speed of 500 rpm), abrasion loss of 100 mg or less, preferably 50 m
Those having g or less are preferred from the viewpoint of durability.
さらに本発明に用いる帯電防止効果を有するフィルム
は、厚さが0.001〜10mm、好ましくは0.1〜2mm、さらに
好ましくは0.5〜1.5mmであるものが耐久性の点で好まし
い。Further, the film having an antistatic effect used in the present invention preferably has a thickness of 0.001 to 10 mm, preferably 0.1 to 2 mm, and more preferably 0.5 to 1.5 mm in terms of durability.
帯電防止効果を有するフィルムに帯電防止効果を付与
するために用いる界面活性剤を以下に例示する。Examples of surfactants used for imparting an antistatic effect to a film having an antistatic effect are shown below.
アニオン系界面活性剤 スルホン酸（脂肪酸スルホン酸塩等） 硫酸エステル型（高級アルコール硫酸エステル塩、高
級アルコールEO付加物硫酸エステル塩等） リン酸エステル型（高級アルコールリン硫酸エステル
塩、高級アルコールEO付加物リン酸エステル塩等） カチオン系界面活性剤 第４級アンモニウム塩型カチオン界面活性剤等 非イオン系界面活性剤 ポリエチレングリコール型（高級アルコールEO付加
物、ポリエチレングリコール脂肪酸エステル等） 多価アルコール型（多価アルコール脂肪酸エステル
等） 両性系界面活性剤 ベタイン型両性界面活性剤等 また、導電性微粒子としては、例えば銀、カーボン、
銅、酸化錫、酸化チタン等を用いることができる。尚、
透明なフィルムを得るためには、導電性微粒子の平均粒
子径は、約0.1ミクロン以下であることが好ましい。Anionic surfactants Sulfonic acid (fatty acid sulfonate, etc.) Sulfate ester type (higher alcohol sulfate ester, higher alcohol EO adduct sulfate ester salt, etc.) Phosphate ester type (higher alcohol phosphorus sulfate ester, higher alcohol EO addition Phosphate ester salt) Cationic surfactant Quaternary ammonium salt type cationic surfactant Nonionic surfactant Polyethylene glycol type (higher alcohol EO adduct, polyethylene glycol fatty acid ester, etc.) Polyhydric alcohol type ( Polyhydric alcohol fatty acid esters, etc.) Amphoteric surfactants, betaine-type amphoteric surfactants, etc. The conductive fine particles include, for example, silver, carbon,
Copper, tin oxide, titanium oxide, or the like can be used. still,
In order to obtain a transparent film, it is preferable that the average particle size of the conductive fine particles is about 0.1 μm or less.
導電性繊維としては、例えば銅等の繊維を用いること
ができる。尚、透明なフィルムを得るためには、導電性
繊維の平均径は、約0.1ミクロン以下であることが好ま
しい。また、繊維の長さには特に制限はないが、少量の
添加量で優れた導電性を付与するという観点から、約0.
5〜100ミンロンであるとが好ましい。As the conductive fiber, for example, a fiber such as copper can be used. Incidentally, in order to obtain a transparent film, the average diameter of the conductive fibers is preferably about 0.1 μm or less. Further, the length of the fiber is not particularly limited, but from the viewpoint of providing excellent conductivity with a small amount of addition, about 0.
Preferably it is 5-100 minron.
界面活性剤を用いた帯電防止効果を有するフィルムに
おいては、フィルムを構成する樹脂100重量部に対し
て、0.01〜10重量部の界面活性剤を含有させることが好
ましい。In a film having an antistatic effect using a surfactant, it is preferable to add 0.01 to 10 parts by weight of a surfactant to 100 parts by weight of a resin constituting the film.
導電性微粒子を用いた帯電防止効果を有するフィルム
においては、フィルムを構成する樹脂100重量部に対し
て、0.05〜100重量部の導電性微粒子を含有させること
が好ましい。In a film having an antistatic effect using conductive fine particles, it is preferable to contain 0.05 to 100 parts by weight of conductive fine particles with respect to 100 parts by weight of the resin constituting the film.
導電性繊維を用いた帯電防止効果を有するフィルムに
おいては、フィルムを構成する樹脂100重量部に対し
て、0.05〜100重量部の導電性繊維を含有させることが
好ましい。In a film having an antistatic effect using conductive fibers, it is preferable to add 0.05 to 100 parts by weight of conductive fibers to 100 parts by weight of the resin constituting the film.
さらに、帯電防止効果を有するフィルムは、アイオノ
マー等の導電性フィルムであってもよい。Further, the film having an antistatic effect may be a conductive film such as an ionomer.
また、帯電防止効果を有するフィルムは、界面活性剤
等以外に、殺菌剤、防虫剤、顔料等を含有することもで
きる。Further, the film having an antistatic effect can contain a bactericide, an insect repellent, a pigment, and the like in addition to the surfactant.
一方、帯電防止効果を有するフィルムを床に着脱自在
に固定するための再剥離性フォームシート層は、多孔性
でかつ軟質のポリウレタンフォームからなり、１〜100g
/3cmの密着力を有する。On the other hand, the removable foam sheet layer for detachably fixing the film having an antistatic effect to the floor is made of a porous and soft polyurethane foam, and is 1 to 100 g.
/ 3cm adhesion.
より具体的には、再剥離性フォームシート層は、発泡
倍率1.5〜８、好ましくは２〜４、より好ましくは2.5〜
3.5の軟質ポリウレタンフォームからなるものである。More specifically, the removable foam sheet layer has an expansion ratio of 1.5 to 8, preferably 2 to 4, more preferably 2.5 to
It consists of flexible polyurethane foam of 3.5.
さらに、このような軟質ポリウレタンフォームは、好
ましくは５〜50g/3cmの密着力を有し、さらに0.1〜1.0k
g/3cm、好ましくは0.2〜0.5kg/3cmのフォーム強度を有
するものであることが好ましい。それにより、本発明の
床用帯電防止シートを床に強力に密着させることがで
き、かつ歩行者よにる踏みつけにも充分に耐え得る。Further, such a flexible polyurethane foam preferably has an adhesion of 5 to 50 g / 3 cm, and more preferably 0.1 to 1.0 k
Preferably it has a foam strength of g / 3 cm, preferably 0.2-0.5 kg / 3 cm. Thereby, the antistatic sheet for floors of the present invention can be strongly adhered to the floor, and can sufficiently withstand pedestrian stepping.
再剥離性フォームシート層の厚さは、用途により種々
選択できるが、例えば0.1〜5mm、好ましくは0.2〜1.5m
m、より好ましくは0.2〜1.0mmとすることが適当であ
る。The thickness of the removable foam sheet layer can be variously selected depending on the application, for example, 0.1 to 5 mm, preferably 0.2 to 1.5 m
m, more preferably 0.2 to 1.0 mm.
上記の如き軟質ポリウレタンフォームを再剥離性フォ
ームシート層として有する本発明の床用帯電防止シート
は、例えば、以下のようにして製造することができる。The floor antistatic sheet of the present invention having the above flexible polyurethane foam as a removable foam sheet layer can be produced, for example, as follows.
ウレタン系ポリマーエマルジョンコンパウンド（不揮
発分50％、pH8〜10、粘度7000〜10000cps）（例えば、
大日本インキ化学工業（株）製DICFOAM Ｆ−520）を起
泡剤、整泡剤、架橋剤、架橋剤用の触媒及び増粘剤等を
室温（例えば15〜30℃）で調合し、得られた混合物をろ
過した後、発泡機を用いて所望の発泡倍率に発泡させ
る。発泡させた混合物は、次いで基体となる樹脂のフィ
ルムに塗布し、予備乾燥の後、例えば100〜120℃で２〜
４分間熱処理することにより硬化させる。熱処理後、冷
却して本発明の床用帯電防止シートを得ることができ
る。Urethane polymer emulsion compound (non-volatile content 50%, pH 8-10, viscosity 7000-10,000 cps) (for example,
DICFOAM F-520 manufactured by Dainippon Ink and Chemicals, Inc. is blended with a foaming agent, a foam stabilizer, a cross-linking agent, a catalyst for the cross-linking agent and a thickener at room temperature (for example, 15 to 30 ° C.). After filtering the obtained mixture, the mixture is foamed to a desired expansion ratio using a foaming machine. The foamed mixture is then applied to a resin film serving as a substrate, and after pre-drying, for example, at 100 to 120 ° C. for 2 to 2 hours.
It is cured by heat treatment for 4 minutes. After the heat treatment, cooling is performed to obtain the antistatic sheet for floors of the present invention.
本発明の床用帯電防止シートは、帯電防止効果に優れ
る。さらに、床への密着性に優れているのみならず、再
剥離性にも優れ、液体の剥離剤を用いることなく容易に
剥離することができる。The floor antistatic sheet of the present invention has an excellent antistatic effect. Furthermore, it is excellent not only in adhesion to the floor but also in removability, and can be easily peeled without using a liquid peeling agent.
以下本発明を実施例によりさらに説明する。 Hereinafter, the present invention will be further described with reference to Examples.
実施例 以下の配合の軟質ポリウレタンフォーム用配合液を室
温で調製した。Example A compounding solution for flexible polyurethane foam having the following formulation was prepared at room temperature.
ウレタン系ポリマーエマルジョンコンパウンド（不揮発
分50％、pH8〜10、粘度7000〜10000cps）（大日本イン
キ化学工業（株）製DICFOAM Ｆ−520） 100重量部 脂肪酸塩素活性剤（Ｆ−１） 10重量部 シリコーン（VONDIC NBA−１） 0.5重量部 水溶性エポキシ（CR−5L） ２重量部 ポリアミン（CATALYST PA−20） 0.5重量部 特殊アクリル系エマルジョン（VONCOAT 3580）１重量部 CMC（第１工業製薬（株）製、セロゲンWSC） ３重量部 上記配合液をろ過した後、発泡機を用いて所定の発泡
倍率で発泡させた。この際の空気と配合液との容積比は
1/1〜3/1の間とした。次いで、基体となる帯電防止効果
を有する樹脂のフィルムに塗布し、予備乾燥の後、100
〜120℃で２〜４分間の条件で熱処理することにより発
泡させた配合液を硬化させた。熱処理終了後、冷却して
本発明の床用帯電防止シートを得た。Urethane-based polymer emulsion compound (non-volatile content: 50%, pH: 8 to 10, viscosity: 7,000 to 10,000 cps) (DICFOAM F-520, manufactured by Dainippon Ink and Chemicals, Inc.) 100 parts by weight Fatty acid chlorine activator (F-1) 10 parts by weight Silicone (VONDIC NBA-1) 0.5 parts by weight Water-soluble epoxy (CR-5L) 2 parts by weight Polyamine (CATALYST PA-20) 0.5 parts by weight Special acrylic emulsion (VONCOAT 3580) 1 part by weight CMC (Daiichi Kogyo Seiyaku Co., Ltd.) ), 3 parts by weight of cellogen WSC) After filtering the above-mentioned mixture, the mixture was foamed at a predetermined foaming ratio using a foaming machine. At this time, the volume ratio between the air and the compounded liquid is
Between 1/1 and 3/1. Next, it is applied to a film of a resin having an antistatic effect as a substrate, and after preliminary drying, 100
The foamed mixture was cured by heat treatment at a temperature of 120 ° C. for 2 to 4 minutes. After the heat treatment, the resultant was cooled to obtain an antistatic sheet for floors of the present invention.
基体として用いた帯電防止効果を有する樹脂のフィル
ムの特性を表１に示す。また、得られた各サンプルの物
性及び性能試験結果を表１に示す。Table 1 shows the characteristics of the resin film having an antistatic effect used as the substrate. In addition, Table 1 shows the physical properties and performance test results of each of the obtained samples.
性能試験方法 １日の通行量が約5000人の通路のビニルアスベストタ
イル床に、300×300mmのシートサンプルを貼り付けて30
日間放置した。Performance test method A 30 x 300 mm sheet sample is stuck on a vinyl asbestos tile floor in a passage where daily traffic is about 5,000.
Left for days.
貼り付け前及び30日間放置後のシートの物性及び剥離
性等について評価した。The sheet was evaluated for physical properties, releasability, etc., before application and after standing for 30 days.
評価基準 （１）表面帯電により表面に付着した綿状のほこりの有
無 A:綿状のほこりが全く付着していない。Evaluation criteria (1) Presence or absence of fluffy dust adhered to the surface due to surface electrification A: No fluffy dust adhered.
B:綿状のほこりが僅かに付着しているが、掃き掃除で容
易に除去できる。B: Cotton-like dust is slightly adhered, but can be easily removed by sweeping.
C:綿状のほこりが多少付着しており、掃き掃除ででは除
去できないが、水掃き掃除で容易に除去できる。C: Some cotton-like dust adheres and cannot be removed by sweeping, but can be easily removed by water sweeping.
D:綿状のほこりが多量に付着しており、水掃き掃除で除
去できるが、すぐに綿状のほこりが付着してくる。D: A large amount of flocculous dust adheres and can be removed by water sweeping cleaning, but flocculous dust adheres immediately.
（２）損傷性 A:摩耗された痕跡もなく、光沢も低下していない。(2) Damage A: No trace of abrasion and no decrease in gloss.
B:多少摩耗されているが、光沢の低下は少ない。B: Although slightly worn, the decrease in gloss is small.
C:摩耗されており、光沢の低下も多少ある。C: Worn, with some decrease in gloss.
D:完全に摩耗され、光沢を失っている。D: Completely worn and lost gloss.
（３）汚染性 A:擦り傷も無く、汚染の形跡もない。(3) Contamination A: There is no abrasion and no evidence of contamination.
B:擦り傷は無いが、僅かに汚染の形跡がある。B: No abrasions, but slight signs of contamination.
C:多少擦り傷が生じ、多少汚染の形跡がある。C: Some abrasions occur, with some evidence of contamination.
D:無数の擦り傷があり、汚染がひどい。D: There are countless scratches and severe contamination.
（４）歩行時の割れ A:全く割れの徴候すらない。(4) Cracks during walking A: No signs of cracking.
B:僅かにクラックの徴候がうかがえる。B: There are slight signs of cracks.
C:僅かにクラックが見える。C: Cracks are slightly visible.
D:無数のクラックが見える。D: Countless cracks are visible.
（５）滑り性（日本工業規格JIS A 1407に準じて行う） A:滑り抵抗係数 0.4以上 B:滑り抵抗係数 0.2〜0.3 C:滑り抵抗係数 0.1〜0.2 D:滑り抵抗係数 0.1以下 （６）床への密着性 A:全く剥がれない。(5) Slip property (performed according to Japanese Industrial Standard JIS A 1407) A: Slip resistance coefficient 0.4 or more B: Slip resistance coefficient 0.2 to 0.3 C: Slip resistance coefficient 0.1 to 0.2 D: Slip resistance coefficient 0.1 or less (6) Adhesion to floor A: No peeling.
B:角がほんの僅か剥がれる。B: The corners are slightly peeled off.
C:廻りが僅かに剥がれる。C: The area is slightly peeled.
D:全体が剥がれてしまう。D: The whole will come off.
（７）床からの剥離性 A:床から容易に剥がれる。(7) Peelability from floor A: Peel easily from floor.
B:床から僅かの力を加えるだけで剥がれる。B: Peel off from the floor with a slight force.
C:床から力を加えてようやく剥がれる。C: It finally peels off from the floor with force.
D:床から力を加えても剥がれない。D: Does not peel off even if force is applied from the floor.
Claims (4)
に１〜100g/3cmの密着力を有する軟質ポリウレタンフォ
ームからなる再剥離性フォームシート層を有する床用帯
電防止シート。1. An antistatic sheet for floors having a removable foam sheet layer made of a flexible polyurethane foam having an adhesion of 1 to 100 g / 3 cm on one surface of a film having an antistatic effect.
の密着力を有する請求項１記載の床用帯電防止シート。2. The flexible polyurethane foam is 5 to 50 g / 3 cm.
The antistatic sheet for floors according to claim 1, which has an adhesion force of:
倍率を有する請求項１または２に記載の床用帯電防止シ
ート。3. The antistatic sheet for floor according to claim 1, wherein the flexible polyurethane foam has an expansion ratio of 2 to 4.
cmのフォーム強度を有する請求項１〜３のいずれか１項
に記載の床用帯電防止シート。4. The flexible polyurethane foam is 0.1 to 1.0 kg / 3.
The antistatic sheet for floors according to any one of claims 1 to 3, which has a foam strength of 5 cm.