JP2021527630A - Macromonomer photocurable dental impression material - Google Patents

Abstract

(A) Formula ^(I): and E- _{(L 1} -Z) polymerizable polysiloxane resin composition comprising a compound of n ^-L 2 -E, and (b) particulate fillers, and (c) a photoinitiator Including photocurable dental impression material.
[Selection diagram] Fig. 1

Description

The present invention relates to a photocurable dental impression material. Furthermore, the present invention relates to the use of the photocurable dental impression material of the present invention for the preparation of dental impressions.

Dental impression materials are known. Dental impression materials are generally available as reactive multi-component materials provided in packages containing two compartments or two separate containers that keep the ingredients isolated from each other during storage. When the ingredients are mixed, a chemical reaction begins in which the mixed composition transforms into a cured mass during the curing time. Moreover, the working and curing times of conventional dental impression materials are limited and depend on the speed of the curing reaction. Therefore, the storage stability of the dental impression material depends on the separation of the reactive components and needs to be done on the chair side just before use so that the dental impression can usually be completed within just a few minutes of working time. Requires pre-use mixing.

Devices for automatic mixing and dispensing of multi-component dental impression materials have been developed to provide high accuracy with respect to the uniformity of the mixture and the ratio of the two components to be mixed. Thus, the components of the dental impression material are simultaneously fed to the mixer from a separate material chamber during application of the dental impression material, mixed and then the mixed paste is distributed. The paste may be fed directly from the mixer onto the dental impression tray for immediate placement in the patient's mouth.

The mixture of materials in the mixing chamber can only be stored for a short period of time because when the material components come into contact with each other in the mixing chamber, the mixed materials will quickly cure in the mixing chamber if not distributed and used. Therefore, the dentist may have to remove and replace the mixer several times a day.

The dental impression material may be a silicone impression material that is curable by an addition reaction or a condensation reaction, of which addition type silicone is most common. Traditional add-on silicone impression materials provide good detail reproduction, excellent dimensional stability and little cure shrinkage, while add-on silicones are hydrophobic in nature and therefore damp for optimal use. Needs control. Finally, add-on silicones have inadequate tear resistance.

Dental impression materials based on crosslinked polysiloxane are known. For example, US-A-5849812 is (a) at least one polyether having at least two optionally substituted vinyl and / or allyl end groups, (b) a SiH component, and (c) at least one platinum catalyst. , (D) optional additives and (e) organopolysiloxanes having at least two alkenyl groups are described as addition-curable polyether dental impression materials.

US-A 5137448 discloses a dental impression composition that is polymerizable by having an initiator that is activated by an active light within the visible light range of 360-600 nanometers, wherein the composition is at least. It contains a compound having two terminal acylate unsaturateds and a skeleton-containing organosilicone.

The object of the present invention is to have adjustable working time and curing time, to provide good detail reproduction without sticking to the core build-up material or composite restoration, and at the same time to have excellent tear resistance, excellent. It is to provide a highly moisture resistant dental impression material which has dimensional stability, reduced curing shrinkage and may be provided as a single composition which does not require pre-use mixing.

Furthermore, an object of the present invention is to provide the use of the dental impression material of the present invention.

の二価の基を表し、式中、
２つ以上のＬ^３が存在する場合、同じであるかまたは異なっていてよいＬ^３は独立して、最大４つの式（ＩＩＩ）：
−Ｌ^１−Ｅ
（ＩＩＩ）
の置換基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）で置換されてよい二価のリンカー基を表し、
２つ以上のＬ^４が存在する場合、同じであるかまたは異なっていてよいＬ^４は独立して、最大４つの式（ＩＩＩ）の置換基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）で置換されてよい二価のリンカー基を表し、
Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、同じであるかまたは異なっていてよく、２つ以上のＸ^１、Ｘ^２、Ｙ^１、またはＹ^２が存在する場合、Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、同じであるかまたは異なっていてよく、独立して、酸素原子、硫黄原子、および基ＮＲ’（式中、Ｒ’は、水素原子もしくはＣ_１〜４アルキル基である）を表し、
ｍは、０、または１〜４０の整数を表し、
Ｚは、ポリシロキサン基および式（ＩＩＩ）の基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）から選択される最大４つの置換基でさらに置換されてよい二価のリンカー基を表し、
Ｌ^２は、単結合または式（ＩＩ）の二価の基（式中、Ｌ^３、Ｌ^４、Ｘ^１、Ｘ^２、Ｙ^１、Ｙ^２、およびｍは独立して、Ｌ^１について定義されるとおりである）を表し、
ｎは、０、または１〜４の整数を表し、
ただし、
−式（Ｉ）の化合物は、重合性炭素−炭素二重結合を有する少なくとも１つの一価の基Ｅを含有し、
−式（Ｉ）の化合物は、少なくとも１つのポリシロキサン基を含有し、
ただし、
ｎが０である場合、Ｌ^２は、式（ＩＩ）の二価の基である、
化合物、を含む重合性ポリシロキサン樹脂組成物と、
（ｂ）微粒子フィラーと、
（ｃ）光開始剤
を含む、光硬化性歯科用印象材を提供する。 The present invention
(A) The following formula (I):
E- (L ^1- Z) _n- L ^2- E
(I)
In the formula,
E, which may be the same or different, is independently a group containing a polymerizable carbon-carbon double bond, a group containing a polysiloxane moiety, a C _2-20 alkoxy group, a C _2-20 thioalkyl group, And represents a monovalent group selected from RNH groups (where R is a C _{2-20 alkyl group).}
If more than one L ¹ is present, may L ¹ which have the same or different, the following formula (II):

Represents the divalent group of
If more than one L ³ there may L ³ that have the same or different is independently up to four of the formula (III):
-L ^1- E
(III)
Substituents (wherein, L ¹ is and E is as defined above) represents which may be substituted bivalent linker group,
If more than one L ⁴ is present may L ⁴ which have the same or different are independently substituents (wherein up to four of the formula (III), L ¹ is and E, above Represents a divalent linker group that may be substituted with (as defined)
X ¹ , X ² , Y ¹ , and Y ² may be the same or different, and if more than one X ¹ , X ² , Y ¹ , or Y ² is present, then X ¹ , X ² , Y ¹ , and Y ² may be the same or different, and independently, an oxygen atom, a sulfur atom, and a group NR'(in the formula, R'is a hydrogen atom or a C _1-4 alkyl group. Represents)
m represents an integer of 0 or 1-40,
Z is a group (wherein, L ¹ is and E is as defined above) of the polysiloxane group and the formula (III) further which may be substituted divalent up to four substituents selected from Represents the linker group of
L ² is a single bond or a divalent group of formula (II) (in the formula, L ³ , L ⁴ , X ¹ , X ² , Y ¹ , Y ² , and m are independently defined for ^{L 1).} As you can see)
n represents an integer of 0 or 1-4,
However,
-The compound of formula (I) contains at least one monovalent group E having a polymerizable carbon-carbon double bond.
-The compound of formula (I) contains at least one polysiloxane group and contains.
However,
When n is 0, L ² is the divalent group of formula (II).
A polymerizable polysiloxane resin composition containing a compound,
(B) Fine particle filler and
(C) A photocurable dental impression material containing a photoinitiator is provided.

が同じであるかまたは異なっていてよいように、Ｌ^３、Ｌ^４、Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は各々独立して、上記で定義されるように同じであるかまたは異なっていてよい。 If m is greater than 1, the repeating unit of the divalent group of formula (II)

L ³ , L ⁴ , X ¹ , X ² , Y ¹ , and Y ² are each independently the same or different, as defined above, so that may be the same or different. You may be.

It should be understood that the divalent group of formula (II) may comprise the same repeating unit oligomer or polymer chain, or different repeating unit alternating oligomer or polymer chain, and / or different repeating unit random polymer chains. Is. In addition, m of formula (II) may include i and j of specific embodiments of compounds of formula (I) as set forth herein.

Furthermore, the present invention provides the use of the photocurable dental impression material of the present invention for making dental impressions.

The present invention is such that the compound has a low viscosity and is cured by a radical polymerization reaction, resulting in a cured material with limited adhesion to hard and soft tooth structures, core build-up materials, or composite restorations. In addition, it is assumed that such a compound contains at least one monovalent group E having a polymerizable carbon-carbon double bond, and at least one polysiloxane group, and the radically polymerizable poly according to the formula (I). Based on the recognition that certain compositions of siloxane compounds may be used in filled photocurable dental impression materials.

Curing by radical polymerization makes it possible to provide a convenient one-component photocurable dental impression material that has high storage stability and does not require mixing before use. Therefore, the photocurable dental impression material may be provided as a ready-to-use dental tray. At the same time, photocurable dental impression materials, when cured, provide excellent tear resistance, good detail reproduction, excellent dimensional stability, and do not provide curing shrinkage.

The scheme of the procedure for synthesizing a compound according to the formula (I) is shown. A scheme of a procedure for synthesizing a macromonomer that may be used in combination with a compound according to formula (I) is shown. The scheme of the reaction route to the high molecular weight cross-linking agent having 3 or more polymerizable groups which may be used in combination with the compound of formula (I) is shown. The scheme of the reaction pathway to the further macromonomer which may be used in combination with the compound of formula (I) is shown. A chart showing the processing effect of Silver / Lot 11801005 on the mechanical properties of the combo resin is shown. The chart which shows the processing effect of Silver / lot 11804022 on the mechanical property of a combo resin is shown.

Detailed Description of Preferred Embodiments The terms "polymerization" and "polymerizable" are covalently linked or linked so that a number of smaller molecules, such as monomers, form larger molecules, i.e. macromolecules or polymers. Regarding ability. The monomers may be bound to form only linear macromolecules or to form three-dimensional macromolecules, commonly referred to as crosslinked polymers. For example, monofunctional monomers form linear polymers, while monomers with at least two functional groups form crosslinked polymers, also known as networks.

_{The term "C 2-20} alkylene group" according to the present invention _{represents a divalent C 2-20} hydrocarbon linker group. Specifically, the linker group may be a hydrocarbon group which may be aliphatic and / or aromatic. In addition, the linker group may be a linear, branched, and / or cyclic hydrocarbon group. The C _2-20 hydrocarbon linker group may contain 1 to 8 heteroatoms selected from oxygen, nitrogen, and sulfur, the divalent organic residue of which is a C _{1 to 4} alkoxy group, hydroxyl group. , A thiol group, and one or more substituents selected from the group consisting of _{C 6-14 aryl groups.} The C _2-20 alkylene group may be a linear or branched group. Hydrocarbon groups may be substituted with _{1 to 6 C 1-4 alkyl groups.} Specific examples of alkyl groups are methylene, ethylene, n-propylene, i-propylene, n-butylene, i-butylene, or tert-butylene. In a preferred embodiment, the hydrocarbon group may contain 1 to 5 oxygen atoms in the hydrocarbon group in the form of an aliphatic or aromatic ether bond, keto group, carboxylic acid group, or hydroxyl group. In the case of an aliphatic group, the C _2-20 alkylene group may be a linear or branched alkylene group or a cycloalkylene group. In the case of aromatic groups, the C _2-20 alkylene group may be an arylene group or a C _3-14 heteroarylene group. Specifically, it is a divalent substituted or unsubstituted C _2-20 alkylene group, a substituted or unsubstituted C _6-14 arylene group, a substituted or unsubstituted C _3-20 cycloalkylene group, a substituted or unsubstituted C _{7 to It may be a 20} arylene alkylene arylene group. Further, the C _2-20 alkylene group may contain 2 to 4 oxygen or nitrogen atoms and _{may be substituted with 1 to 6 C 1 to 4} alkyl groups, saturated aliphatic C _{2 to 20} hydrocarbons. _{The C 2-20} alkylene group, which represents a hydrogen chain, may be a substituted or unsubstituted C _7-20 arylene alkylene arylene group which _{may be substituted with 1 to 6 C 1-4 alkyl groups.}

An "active radiation" is any electromagnetic radiation capable of producing photochemical action and can have wavelengths of at least 150 nm, up to 1250 nm, typically at least 300 nm, up to 750 nm.

As used herein, the term "electron donor" means a compound that can donate electrons during a photochemical process. Suitable examples include organic compounds having heteroatoms with lone electron pairs, such as amine compounds.

The present invention provides a photocurable dental impression material. The photocurable dental impression material is preferably a one-component composition packed in a syringe or provided in a ready-to-use dental impression tray. Alternatively, the photocurable dental impression material of the present invention may also be a two-component composition, especially when formulated as a dual cure composition containing an additional redox initiator system.

When packed in a syringe or provided in a ready-to-use dental impression tray, the composition must be shielded from chemical light during storage.

The photocurable dental impression material of the present invention contains a polymerizable polysiloxane resin composition containing a compound of formula (I) having a polymerizable moiety in combination with the polysiloxane moiety. The polymerizable polysiloxane resin composition contains a compound of formula (I) which is a macromonomer. The macromonomer reacts the first and second reactants at a particular stoichiometric ratio such that there is an excess with respect to the molar amount of reactive groups in the second reactant, and any excess. It may be obtained by using a third reactant in a particular ratio that caps the ends of the reactive end groups.

The reaction between the first reactant and the second reactant is preferably addition polymerization. However, polycondensation is also possible.

The terminal capping reaction between the third reactant and the excess functional group of the second reactant is also preferably addition polymerization. However, polycondensation is also possible.

In the case of a heavy addition reaction, the formation of a urethane bond is preferable. Alternatively, the formation of a urea or S-thiocarbamate bond by the reaction of the first reactant and the second reactant is also possible. Thus, the first reactant may be a diol or diamine or dithiol instead, and the second reactant may be diisocyanate.

In the case of polyfunctional reactants such as trifunctional reactants, branching may be introduced into the macromonomer. According to the present invention, di- or polyalcohol can be used as the first reactant and di- or polyisocyanate can be used as the second reactant, thereby monofunctional such as alcohol as shown in FIG. It forms an isocyanate-terminated polyurethane prepolymer whose ends are capped with a third reactant of sex. Alternatively, the use of di- or polyamines or di- or polythiols as the first reactant and di- or polyisocyanate as the second reactant is monofunctional, such as alcohol, amine, or thiol compounds. A third reactant results in an isocyanate-terminated urea or S-carbamate prepolymer whose ends are capped.

However, according to the present invention, di- or polyisocyanate can be used as the first reactant and di- or polyalcohol can be used as the second reactant, whereby a monofunctional third such as isocyanate can be used. To form a hydroxyl-terminated prepolymer whose ends are capped with the reactants of. Alternatively, di- or polyisocyanate can be used as the first reactant, and di- or polyamine or di- or polythiol can be used as the second reactant, thereby a monofunctional third reaction such as isocyanate. Form an amine or thiol-terminated prepolymer whose ends are capped with material.

The first, second, and third reactants may be a mixture of two or more different compounds. Any of the first, second, and third reactants contains one or more polysiloxane moieties. Preferably, the third component introduces a radically polymerizable moiety into the macromonomer.

According to a preferred embodiment, the photocurable dental impression material of the present invention further comprises an additional polymerizable compound, particularly a compound of formula (I), but without any polysiloxane moiety. Specifically, the photocurable dental impression material of the present invention preferably contains an additional polymerizable macromonomer. The polymerizable macromonomer is an arbitrary stoichiometric ratio in which the fourth and fifth reactants are reacted in a particular stoichiometric ratio such that there is an excess with respect to the molar amount of reactive groups in the fifth reactant. It may be obtained by using a sixth reactant in a particular ratio that caps the ends of the excess reactive end groups.

The reaction between the fourth and fifth reactants is preferably addition polymerization. However, polycondensation is also possible. The terminal capping reaction between the sixth reactant and the excess functional group of the fifth reactant is also preferably addition polymerization. However, polycondensation is also possible.

In the case of a heavy addition reaction, the formation of a urethane bond is preferable. Alternatively, the formation of a urea or S-thiocarbamate bond by the reaction of the fourth and fifth reactants is also possible. Thus, the fourth reactant may be a diol or diamine or dithiol instead, and the second reactant may be diisocyanate.

For polyfunctional reactants, branching may be introduced into the macromonomer. According to the present invention, di- or polyalcohol can be used as the fourth reactant and di- or polyisocyanate can be used as the fifth reactant, thereby monofunctional such as alcohol as shown in FIG. It forms an isocyanate-terminated prepolymer whose ends are capped with a sixth reactant of sex. Alternatively, the use of di- or polyamines or di- or polythiols as the fourth reactant and di- or polyisocyanate as the fifth reactant is monofunctional, such as alcohol, amine, or thiol compounds. A third reactant results in an isocyanate-terminated urea or S-carbamate prepolymer whose ends are capped.

However, according to the present invention, di- or polyisocyanate can also be used as the fourth reactant, and di- or polyalcohol can also be used as the fifth reactant, thereby making a monofunctional sixth such as isocyanate. To form a hydroxyl-terminated polyurethane prepolymer whose ends are capped with the reactants of. Alternatively, di- or polyisocyanate can be used as the fourth reactant, and di- or polyamine or di- or polythiol can be used as the second reactant, thereby a monofunctional third reaction such as isocyanate. It forms an amine or thiol-terminated polyurea or poly-S-thiocarbamate prepolymer whose ends are capped with a substance.

The fourth, fifth, and sixth reactants may be a mixture of two or more different compounds. In the case of addition-polymerizable macromonomers, none of the first, second, and third reactants may contain any polysiloxane moiety. The reactants without any polysiloxane moiety used to prepare the polymerizable polysiloxane resin composition containing the compound of formula (I) may be used to prepare the addition polymerizable macromonomer. Preferably, the sixth component introduces a radically polymerizable moiety into the addition-polymerizable macromonomer.

Polymerizable Polysiloxane Resin Composition The photocurable dental impression material of the present invention has the following formula (I):
E- (L ^1- Z) _n- L ^2- E
(I)
Contains a polymerizable polysiloxane resin composition comprising the above compounds.

According to a preferred embodiment, the polymerizable polysiloxane resin composition has a total siloxane content in the range of 10-40% wt / wt, more preferably in the range of 15-35% wt / wt. The total siloxane content of the polymerizable polysiloxane resin composition may ^{be determined by 29} Si-NMR.

In the compound of formula (I), E, which may be the same or different, is independently a group containing a polymerizable carbon-carbon double bond, a group containing a polysiloxane moiety, and a C _2-20 alkoxy group. , C _2-20 thioalkyl group, and RNH group (in the formula, R is a C _2-20 alkyl group) represents a monovalent group selected.

According to a preferred embodiment, E is a group containing a polymerizable carbon-carbon double bond, preferably a (meth) acryloyl group, a (meth) acrylamide group, or an allyl (meth) acrylamide group, more preferably ( Meta) Acryloyl group.

According to a preferred embodiment, the monovalent group E has a total (meth) acrylate content of 0.25 to 0.50 mmol / g, more preferably 0.25 to 0.45 mmol in the polymerizable polysiloxane resin composition. It contains a (meth) acrylate group so that it is in the range of / g. The total (meth) acrylate content of the polymerizable polysiloxane resin composition is ^{determined by 1 1} H-NMR.

による基であり、式中、
Ｒ^１は、水素原子、またはＣ_１〜１２アルキル基を表し、
Ｘ^３は、酸素原子、硫黄原子、または基ＮＲ^２（式中、Ｒ^２は、水素原子、Ｃ_１〜１２アルキル基、もしくはアリル基である）を表し、
Ｌ^５は、二価の炭化水素リンカー基、またはポリシロキサン含有リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
Ｘ^４は、酸素原子、硫黄原子、または基ＮＲ^３（式中、Ｒ^３は、水素原子、もしくはＣ_１〜１２アルキル基である）を表し、
ａは、１〜２０の整数を表す。 According to a preferred embodiment, E is the following formula (IV):

In the formula,
R ¹ represents a hydrogen atom or a C _1-12 alkyl group.
X ³ represents an oxygen atom, a sulfur atom, or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ⁵ is a divalent hydrocarbon linker group or a polysiloxane-containing linker group, preferably a C _{2 to 20} alkylene group.
X ⁴ represents an oxygen atom, a sulfur atom, or a group NR ³ (in the formula, R ³ is a hydrogen atom or a C _1-12 alkyl group).
a represents an integer of 1 to 20.

Preferably, R ¹ represents a C _1-4 alkyl group, more preferably a methyl group.

According to the first embodiment, X ³ is preferably an oxygen atom or a sulfur atom, more preferably an oxygen atom. According to the second embodiment, X ³ preferably represents the group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).

Preferably, X ⁴ represents an oxygen atom or a sulfur atom, more preferably an oxygen atom.

L ⁵ is a divalent hydrocarbon linker group or a polysiloxane-containing linker group. The polysiloxane-containing linker group may be a polysiloxane group or may contain one or more hydrocarbon fragments in the main chain. Preferably, L ⁵ is a linear or branched C _2-3 alkylene group.

According to a preferred embodiment, the group- [L ^5- X ⁴ ]-is selected from the following groups:

Preferably, a is an integer of 1-10.

のポリシロキサン基であり、式中、
同じであるかまたは異なっていてよいＲ^４は独立して、直鎖、分岐、または環状アルキル基を表し、
Ｌ^６は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
Ｘ^５は、酸素原子、硫黄原子、または基ＮＲ^５（式中、Ｒ^５は、水素原子、もしくはＣ_１〜１２アルキル基である）を表し、
ｂは、０、または１〜１０００の整数であり、
ｃは、０または１である。 According to a preferred embodiment, E is the following formula (V):

Polysiloxane group in the formula,
Or R ⁴ which have the same or different independently represent a linear, branched, or cyclic alkyl group,
L ⁶ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
X ⁵ represents an oxygen atom, a sulfur atom, or a group NR ⁵ (in the formula, R ⁵ is a hydrogen atom or a C _1-12 alkyl group).
b is an integer of 0 or 1-1000,
c is 0 or 1.

According to a preferred embodiment, R ⁴ is a straight-chain C _{1 to 12} alkyl group optionally substituted, is preferably straight-chain C _{1 to 6} alkyl groups optionally substituted.

According to a preferred embodiment, R ⁴ is a branched C _{1 to 12} alkyl group optionally substituted, preferably, branched C _{1 to 6} alkyl group which is optionally substituted.

According to a preferred embodiment, R ⁴ is cyclic C _{1 to 12} alkyl group optionally substituted, preferably, cyclic C _{1 to 6} alkyl groups optionally substituted.

More preferably, ^{R 4} is a methyl group.

Preferably, X ⁵ represents an oxygen atom or a sulfur atom, more preferably an oxygen atom.

Preferably, b is an integer of 1 to 1000, more preferably an integer of 1 to 100, and even more preferably an integer of 1 to 10.

Preferably, c is 1.

According to a preferred embodiment, E is an optionally substituted linear C _2-20 alkoxy group.

According to a preferred embodiment, E is an optionally substituted branched C _2-20 alkoxy group.

Preferably, E is an optionally substituted linear C _2-15 alkoxy group, more preferably an unsubstituted linear C _2-15 alkoxy group, and even more preferably an unsubstituted linear C. _{It is a 12} alkoxy group.

According to a preferred embodiment, E is an optionally substituted linear C _2-20 thioalkyl group.

According to a preferred embodiment, E is an optionally substituted branched C _2-20 thioalkyl group.

Preferably, E is an optionally substituted linear C _2-15 thioalkyl group, more preferably an unsubstituted linear C _2-15 thioalkyl group.

According to a preferred embodiment, E is an RNH group and in the formula, R is a C _2-20 alkyl group.

Preferably, R is a linear C _2-20 alkyl group optionally substituted.

Preferably, R is a branched C _2-20 alkyl group optionally substituted.

Preferably, R is an optionally substituted linear C _2-15 alkyl group, more preferably an unsubstituted linear C _2-15 alkyl group, and even more preferably an unsubstituted linear C. _{It is a 2-5} alkyl group.

の二価の基を表し、式中、
２つ以上のＬ^３が存在する場合、同じであるかまたは異なっていてよいＬ^３は、独立して、最大４つの式（ＩＩＩ）：
−Ｌ^１−Ｅ
（ＩＩＩ）
の置換基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）で置換されてよい二価のリンカー基を表し、
２つ以上のＬ^４が存在する場合、同じであるかまたは異なっていてよいＬ^４は、独立して、最大４つの式（ＩＩＩ）の置換基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）で置換されてよい二価のリンカー基を表し、
Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、同じであるかまたは異なっていてもよく、２つ以上のＸ^１、Ｘ^２、Ｙ^１、またはＹ^２が存在する場合、Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、同じであるかまたは異なっていてよく、独立して、酸素原子、硫黄原子、および基ＮＲ’（式中、Ｒ’は、水素原子もしくはＣ_１〜４アルキル基である）を表し、
ｍは、０、または１〜４０の整数を表す。 In the compound of formula (I), L ¹ is represented by the following formula (II):

Represents the divalent group of
If more than one L ³ there may L ³ that have the same or different, independently, up to four of the formula (III):
-L ^1- E
(III)
Substituents (wherein, L ¹ is and E is as defined above) represents which may be substituted bivalent linker group,
If more than one L ⁴ is present may L ⁴ which have the same or different, are independently a substituent (wherein up to four of the formula (III), L ¹ is and E, the Represents a divalent linker group that may be substituted with (as defined in)
If X ^{1, X} 2, ^{Y 1,} and ^{Y 2} may be the same or different, two or more ^{X 1,} X 2, ^{Y 1} or if ^{Y 2,} is ^{present, X} 1, X ² , Y ¹ , and Y ² may be the same or different, and independently, the oxygen atom, the sulfur atom, and the group NR'(in the formula, R'is a hydrogen atom or C _1-4 alkyl. Represents)
m represents 0, or an integer of 1-40.

が同じであるかまたは異なっていてよいように、Ｌ^３、Ｌ^４、Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、各々独立して、上記で定義されるように同じであるかまたは異なっていてよい。 If m is greater than 1, the repeating unit of the divalent group of formula (II)

L ³ , L ⁴ , X ¹ , X ² , Y ¹ , and Y ² are each independently the same or the same as defined above, so that may be the same or different. It can be different.

It should be understood that the divalent group of formula (II) may comprise the same repeating unit oligomer or polymer chain, or different repeating unit alternating oligomers or polymer chains, and / or different repeating unit random polymer chains. Is. In addition, m of formula (II) may include i and j of specific embodiments of compounds of formula (I) as set forth herein.

According to a preferred embodiment, L ³ may contain heteroatoms up to 10 in the main chain, it represents a C _{2 to 20} alkylene group, as defined above, heteroatom, oxygen, sulfur or, It is selected from NR ^# (where R ^# represents a hydrogen atom or a linear, branched or cyclic C _1-6 alkyl group).

による基を表し、式中、
同じであるかまたは異なっていてよいＲ^ａ１およびＲ^ａ２は、独立して、水素原子、Ｃ_１〜６線状または分岐アルキル基、Ｃ_４〜１０アリール基、重合性二重結合含有有機残基、好ましくは（メタ）アクリラート基含有有機残基、以下の式［−Ｘ’’Ｌ’’］_ｍＲ^ａ３（式中、Ｘ’’はＯ、Ｓ、もしくはＮＲ^ａ４（式中、Ｒ^ａ４は、水素原子、重合性二重結合を含有する有機残基、好ましくは（メタ）アクリラート基を含有する有機残基、線状もしくは分岐Ｃ_１〜６アルキル基、もしくはＣ_４〜１０アリール基を表す）を表し、Ｌ’’は、Ｃ_１〜６線状もしくは分岐アルキル基、Ｃ_４〜１０アリール基、もしくはＳｉＲ^ａ５ _２基（式中、同じであるかもしくは異なっていてよいＲ^ａ５は、独立して、重合性二重結合を含有する有機残基、好ましくは（メタ）アクリラート基を含有する有機残基、もしくはＣ_１〜４アルキル基、好ましくはメチル基を表す）を表し、ｍは、１〜２０の整数であり、Ｒ^ａ３は、重合性二重結合を含有する有機残基、好ましくは（メタ）アクリラート基を含有する有機残基、Ｃ_１〜４アルキル基、もしくはＣ_４〜１０アリール基である）の基を表し、Ｒ^ａ１およびＲ^ａ２は、式（ＩＩＩ）の基を含んでよく、
ｄは、１〜２０の整数、好ましくは１〜１０の整数であり、より好ましくは、ｄは６である。 According to a preferred embodiment, ^{L 3} has the following formula (VI):

Represents the group by
^Ra1 and ^Ra2 , which may be the same or different, are independently hydrogen atoms, C _1-6 linear or branched alkyl groups, C _4-10 aryl groups, polymerizable double bond-containing organic residues. , Preferably (meth) acrylate group-containing organic residue, the following formula [-X''L''] _m R ^a3 (in the formula, X'' is O, S, or NR ^a4 (in the formula, R ^a4 is , Hydrogen atom, organic residue containing polymerizable double bond, preferably organic residue containing (meth) acrylate group, linear or branched C _1-6 alkyl group, or C _4-10 aryl group. ), Where L'' is a C _1-6 linear or branched alkyl group, a C _4-10 aryl group, or _two ^{SiR a5} groups (in the formula, R ^a5 which may be the same or different is independent. Represents an organic residue containing a polymerizable double bond, preferably an organic residue containing a (meth) acrylate group, or a C _1-4 alkyl group, preferably a methyl group), where m represents. An integer of 1 to 20, Ra ³ is an organic residue containing a polymerizable double bond, preferably an organic residue containing a (meth) acrylate group, a C _1-4 alkyl group, or C _4-10. Representing a group (which is an aryl group), ^Ra1 and ^Ra2 may include a group of formula (III).
d is an integer of 1 to 20, preferably an integer of 1 to 10, and more preferably d is 6.

Preferably, L ³ is selected from the following groups:

による基を表し、式中、
同じであるかまたは異なっていてよいＲ^ｂ１、Ｒ^ｂ２、Ｒ^ｂ３、およびＲ^ｂ４は、独立して、水素原子、Ｃ_１〜６線状または分岐アルキル基、Ｃ_４〜１０アリール基、重合性二重結合含有有機残基、好ましくは（メタ）アクリラート基含有有機残基、以下の式［−Ｘ’’’Ｌ’’’］_ｍＲ^ｂ５（式中、Ｘ’’’はＯ、Ｓ、もしくはＮＲ^ｂ６（式中、Ｒ^ｂ６は、水素原子、重合性二重結合を含有する有機残基、好ましくは（メタ）アクリラート基を含有する有機残基、線状もしくは分岐Ｃ_１〜６アルキル基、もしくはＣ_４〜１０アリール基を表す）を表し、Ｌ’’’は、Ｃ_１〜６線状もしくは分岐アルキル基、Ｃ_４〜１０アリール基、もしくはＳｉＲ^ｂ７ _２基（式中、同じであるかもしくは異なっていてよいＲ^ｂ７は、独立して、重合性二重結合を含有する有機残基、好ましくは（メタ）アクリラート基を含有する有機残基、もしくはＣ_１〜４アルキル基、好ましくはメチル基を表す）を表し、ｍは、１〜２０の整数であり、Ｒ^ｂ５は、重合性二重結合を含有する有機残基、好ましくは（メタ）アクリラート基を含有する有機残基、Ｃ_１〜４アルキル基、もしくはＣ_４〜１０アリール基である）の基を表し、Ｒ^ｂ１、Ｒ^ｂ２、Ｒ^ｂ３、およびＲ^ｂ４は、式（ＩＩＩ）の基を含んでよく、
Ｘ^５およびＸ^６は、同じであるかまたは異なっていてよく、２つ以上のＸ^５またはＸ^６が存在する場合、Ｘ^５およびＸ^６は、同じであるかまたは異なっていてよく、独立して、酸素原子、硫黄原子、および基ＮＲ^Ｎ（式中、Ｒ^Ｎは、水素原子もしくはＣ_１〜４アルキル基である）を表し、
Ｌ^６は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
ｅは、１〜１０の整数であり、
ｆは、１〜１００、具体的には、１〜４０または４０〜１００の整数であり、
ｇは、０または１である。 According to a preferred embodiment, ^{L 3} has the following formula (VII):

Represents the group by
^{R b1} , R ^b2 , R ^b3 , and R ^b4 , which may be the same or different, are independently hydrogen atoms, C _1-6 linear or branched alkyl groups, C _4-10 aryl groups, polymerizable. Double bond-containing organic residue, preferably (meth) acrylate group-containing organic residue, the following formula [-X'''L'''] _m R ^b5 (in the formula, X'''is O, S, Alternatively, NR ^b6 (in the formula, R ^b6 is an organic residue containing a hydrogen atom and a polymerizable double bond, preferably an organic residue containing a (meth) acrylate group, a linear or branched C _1-6 alkyl group. , Or _{represents a C 4-10} aryl group), where L'''is a C _1-6 linear or branched alkyl group, a C _4-10 aryl group, or _two ^{SiR b7} groups (the same in the formula). ^{R b7} , which may be different or different, is an independently organic residue containing a polymerizable double bond, preferably an organic residue containing a (meth) acrylate group, or a C _1-4 alkyl group, preferably a C 1-4 alkyl group. Represents a methyl group), m is an integer of 1 to 20, R ^b5 is an organic residue containing a polymerizable double bond, preferably an organic residue containing a (meth) acrylate group, C. _{Representing a group of 1 to 4} alkyl groups, or C4 to ₁₀ aryl groups), R ^b1 , R ^b2 , R ^b3 , and R ^b4 may comprise a group of formula (III).
X ⁵ and X ⁶ may be the same or different, and if two or more X ⁵ or X ⁶ are present, X ⁵ and X ⁶ may be the same or different and are independent. Represents an oxygen atom, a sulfur atom, and a group NR ^N (in the formula, ^RN is a hydrogen atom or a C _1-4 alkyl group).
L ⁶ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
e is an integer from 1 to 10 and
f is an integer from 1 to 100, specifically 1 to 40 or 40 to 100.
g is 0 or 1.

Preferably, L ⁶ is a linear or branched C _2-3 alkylene group.

According to a preferred embodiment, the group- [L ^6- X ⁵ ]-is selected from the following groups:

による基を表し、式中、
同じであるかまたは異なっていてよいＲ^６は、独立して、直鎖、分岐、または環状アルキル基を表し、
Ｘ^７は、酸素原子、硫黄原子、および基ＮＲ^Ｎ１（式中、Ｒ^Ｎ１は、水素原子、もしくはＣ_１〜４アルキル基である）を表し、
Ｌ^７およびＬ^８は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
ｈは、０、または１〜１０００の整数であり、
ｔは、０または１である。 According to a preferred embodiment, ^{L 3} has the following formula (VIII):

Represents the group by
Or R ⁶ which have the same or different, independently represent a linear, branched, or cyclic alkyl group,
X ⁷ represents an oxygen atom, a sulfur atom, and a group NR ^N1 (in the formula, ^RN1 is a hydrogen atom or a C _1-4 alkyl group).
L ⁷ and L ⁸ are divalent hydrocarbon linker groups, preferably C _2-20 alkylene groups.
h is an integer of 0 or 1-1000,
t is 0 or 1.

のポリシロキサン基であってもよく、式中、
Ｒ^１＃は、１〜８つの炭素原子を有するアルキレンであり、
Ｒ^２＃は、１〜４つの炭素原子を有するアルキルであり、
Ｒ^４＃は、アルキル、アルコキシ、またはシクロアルキル基であり、
ｙ^＃は、５〜２０の整数である。 L ³ also has the following formula (VIIIa), (VIIIb), or (VIIIc)

It may be a polysiloxane group of
R ^{1 #} is an alkylene having 1 to 8 carbon atoms.
R ^{2 #} is an alkyl having 1 to 4 carbon atoms.
R ^{4 #} is an alkyl, alkoxy, or cycloalkyl group.
y ^# is an integer of 5 to 20.

According to a preferred embodiment, R ⁶ is an optionally substituted linear C _1-12 alkyl group, preferably an optionally substituted linear C _1-6 alkyl group.

According to a preferred embodiment, R ⁶ is an optionally substituted branched C _1-12 alkyl group, preferably an optionally substituted branched C _1-6 alkyl group.

According to a preferred embodiment, R ⁶ is an optionally substituted cyclic C _1-12 alkyl group, preferably an optionally substituted cyclic C _1-6 alkyl group.

More preferably, ^{R 6} is methyl group.

Preferably, X ⁷ represents an oxygen atom.

^{Preferably, L 7} and L ⁸ , which may be the same or different, independently represent a linear or branched C _2-3 alkylene group.

More preferably, L ⁷ and L ⁸ have the same or different, are independently selected from the following group:

h is an integer of 1 to 40, preferably h is an integer of 1 to 20, and more preferably an integer of 1 to 10.

Preferably t is 1.

According to a preferred embodiment, L ⁴ may represent any group as defined by L ^3.

による基を表し、式中、
ＥおよびＬ^１は、上記のように定義され、
Ｌ^９は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
２つ以上のＸ^９が存在する場合、Ｘ^９基は同じであるかまたは異なっていてよく、独立して、酸素原子、硫黄原子、および基ＮＲ^Ｎ２（式中、Ｒ^Ｎ２は、水素原子、もしくはＣ_１〜４アルキル基である）を表し、
ｕは、１〜４０の整数である。 According to a preferred embodiment, ^{L 4} has the following formula (IX):

Represents the group by
E and L ¹ are defined as above and
L ⁹ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
If more than one X ⁹ is present, the X ⁹ groups may be the same or different, independently of the oxygen atom, the sulfur atom, and the group NR ^N2 (in the formula, ^RN2 is the hydrogen atom, Alternatively, it represents a _{C 1-4 alkyl group).}
u is an integer from 1 to 40.

Preferably, X ⁹ is an oxygen atom or a sulfur atom, more preferably an oxygen atom.

Preferably u is 1 or 2, preferably 2.

According to a preferred embodiment, the group according to formula (IX) is selected from the following groups:

In the group of formula (II), X ¹ and X ² may be the same or different, and if two or more X ¹ and X ² are present, are X ¹ and X ² the same? Alternatively, they may be different and independently represent an oxygen atom, a sulfur atom, and a group NR'(in the formula, R'is a hydrogen atom or a C _1-4 alkyl group). Preferably, X ¹ and X ² represent an oxygen atom.

In the group of formula (II), Y ¹ and Y ² may be the same or different, and if two or more Y ¹ and Y ² are present, are Y ¹ and Y ² the same? Alternatively, they may be different and independently represent an oxygen atom, a sulfur atom, and a group NR'(in the formula, R'is a hydrogen atom or a C _1-4 alkyl group). Preferably, Y ¹ and Y ² represent the group NR'(where R'is a hydrogen atom or a C _1-4 alkyl group). More preferably, Y ¹ and Y ² represent the group NR'(where R'is a hydrogen atom in the formula).

In the group of formula (II), m represents 0 or an integer of 1 to 40.

In a preferred embodiment, m is 0.

In a preferred embodiment, m is an integer of 1-10.

Preferably m is 1 or 2.

In the compounds of formula (I), Z is, represents any group as defined by L ^3.

In a preferred embodiment, Z represents any group as defined by L ^4.

Preferably, Z represents a group according to formula (XI).

In the compound of formula (I), L ² represents any group as defined by L ³ or L ^4. Preferably, L ² represents any group as defined by L ^3.

Preferably, L ² is selected from the following groups:

In a preferred embodiment, L ² represents a single bond.

In the compound of formula (I), n represents 0, or an integer of 1-4.

In a preferred embodiment, n> 0.

In a preferred embodiment, n is 0, L ² is the divalent group of formula (II), and m is 0 in the formula.

In a preferred embodiment, n = 0, where L ² represents the divalent group of formula (II), in the formula.
L ³ is a divalent C _1-12 hydrocarbon group or a polysiloxane group.
If more than one L ⁴ is present may L ⁴ which have the same or different, are independently a substituent (wherein up to four of the formula (III), L ¹ is and E, the Represents a divalent linker group that may be substituted with (as defined in)
X ¹ and X ² are oxygen atoms and
Y ¹ and Y ² are NH groups and are
m is an integer of 1 to 40.

In a preferred embodiment, n> 0, where L ² represents the divalent group of formula (II), in the formula,
L ³ is a divalent C _1-12 hydrocarbon group or a polysiloxane group.
If more than one L ⁴ is present may L ⁴ which have the same or different, are independently a substituent (wherein up to four of the formula (III), L ¹ is and E, the Represents a divalent linker group that may be substituted with (as defined in)
X ¹ and X ² are oxygen atoms and
Y ¹ and Y ² are NH groups and are
m is an integer of 1 to 40.

According to a preferred embodiment, L ¹ and L ² independently represent a divalent group of formula (II), in the formula.
L ³ is a divalent C _1-12 hydrocarbon group or a polysiloxane group.
If more than one L ⁴ is present may L ⁴ which have the same or different, are independently a substituent (wherein up to four of the formula (III), L ¹ is and E, the Represents a divalent linker group that may be substituted with (as defined in)
X ¹ and X ² are oxygen atoms and
Y ¹ and Y ² are NH groups and are
m is an integer from 1 to 40 and
Z is a divalent C _1-12 hydrocarbon group.

が同じであるかまたは異なっていてよいように、Ｌ^３、Ｌ^４、Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、各々独立して、上記で定義されるように同じであるかまたは異なっていてよい。 If m is greater than 1, the repeating unit of the divalent group of formula (II)

L ³ , L ⁴ , X ¹ , X ² , Y ¹ , and Y ² are each independently the same or the same as defined above, so that may be the same or different. It can be different.

It should be understood that the divalent group of formula (II) may comprise the same repeating unit oligomer or polymer chain, or different repeating unit alternating oligomer or polymer chain, and / or different repeating unit random polymer chains. Is. Further, m of formula (II) may include i and j of specific embodiments of the compound of formula (I) as shown below.

のいずれか１つの化合物であり、式中、
Ｂ^＃は、

であり、
Ａ^＃は

であり、
Ｅ^＃は

であり、
Ｒ^＃は、２〜２５の炭素原子を有するアルキレンであり、
Ｒ’^＃は、ＨまたはＣＨ_３であり、
Ｒ’’^＃は、２〜１５の炭素原子を有するアルキレンであり、
Ｒ^１＃は、１〜８つの炭素原子を有するアルキレンであり、
Ｒ^２＃は、１〜４つの炭素原子を有するアルキルであり、
Ｒ^４＃は、アルキル、アルコキシ、またはシクロアルキル基であり、
ｉおよびｊは、独立して、１〜２０の整数であり、
ｘ^＃は、２〜１０の整数であり、
ｙ^＃は、５〜２０の整数であり、
ｂ^＃は、５０〜１００の整数であり、
ｋは、５〜１５の整数である。 According to a particular embodiment, the compound of formula (I) has the following formula:

It is a compound of any one of the above, and in the formula,
B ^# is

And
A ^# is

And
E ^# is

And
R ^# is an alkylene having 2 to 25 carbon atoms.
R'^# is H or CH ₃ and
R''^# is an alkylene having 2 to 15 carbon atoms.
R ^{1 #} is an alkylene having 1 to 8 carbon atoms.
R ^{2 #} is an alkyl having 1 to 4 carbon atoms.
R ^{4 #} is an alkyl, alkoxy, or cycloalkyl group.
i and j are independently integers from 1 to 20 and
x ^# is an integer from 2 to 10 and
y ^# is an integer of 5 to 20
b ^# is an integer from 50 to 100 and
k is an integer of 5 to 15.

According to a preferred embodiment, the compound of formula (I) has a molecular weight of 100-10.000 Da, more preferably 300-2000 Da.

Preferably, the compound of formula (I) has a viscosity in the range of 0.001 to 100 Pas, more preferably 0.1 to 10 Pas. Viscosity is a measure of the fluid's internal resistance to flow. Viscosity can be measured by various types of viscometers and rheometers at a temperature of 25 ° C.

According to a preferred embodiment, -L 1 ^-Z- represents a divalent group of formula (II), which is a diisocyanate compound, a diol compound, and a polyol compound having at least three hydroxyl groups react It can be obtained by letting it.

According to a preferred embodiment, L ² represents a divalent group of formula (II), which can be obtained by reacting a diisocyanate compound with a diol compound.

（式中、
Ｒ^１は、水素原子、またはＣ_１〜１２アルキル基を表し、
Ｘ^３は、酸素原子、硫黄原子、または基ＮＲ^２（式中、Ｒ^２は、水素原子、Ｃ_１〜１２アルキル基、もしくはアリル基である）を表し、
Ｌ^５は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
Ｘ^４は、酸素原子、硫黄原子、または基ＮＲ^３（式中、Ｒ^３は、水素原子、もしくはＣ_１〜１２アルキル基である）を表し、
ａは、１〜２０の整数を表す）
の１つ以上の化合物、
を含む混合物を反応させることによって得ることができ、
０．０５≦ｘ／ｙ≦０．６６、かつ

であり、
ｘ、ｙ、およびｚは、成分（ａ）、（ｂ）、および（ｃ）のモル等量であり、

は、成分（ａ）の平均ヒドロキシル官能価：

であり、
ｌは、式（Ｘ）で定義されるとおりであり、ｘ_ｌ／ｘは、ｌ＋１のヒドロキシル官能価を有する化合物のモル分率である。 According to a preferred embodiment, the polymerizable polysiloxane resin mixture is
(A) The following formula (X) of x equal quantity:
HO-L ⁴ (OH) _l
(X)
(During the ceremony,
L ⁴ is a (l + 1) -valent linker group.
l is an integer from 1 to 5)
With one or more di- or polyol compounds of
(B) The following formula (XI) of y equal quantity:
OCN-L ³ NCO
(XI)
(During the ceremony,
L ³ is a divalent linker group)
With one or more compounds of
(C) The following formula (XII) of z equal quantity:

(During the ceremony,
R ¹ represents a hydrogen atom or a C _1-12 alkyl group.
X ³ represents an oxygen atom, a sulfur atom, or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ⁵ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
X ⁴ represents an oxygen atom, a sulfur atom, or a group NR ³ (in the formula, R ³ is a hydrogen atom or a C _1-12 alkyl group).
a represents an integer of 1 to 20)
One or more compounds of
Can be obtained by reacting a mixture containing
0.05 ≤ x / y ≤ 0.66 and

And
x, y, and z are molar equivalents of the components (a), (b), and (c).

Is the average hydroxyl functional value of component (a):

And
l is as defined by the formula (X), and x _l / x is the mole fraction of the compound having a hydroxyl functional value of l + 1.

The mixture contains an x-mol equivalent component (a), a y-mol equivalent component (b), and a z-mol equivalent component (c).

によって定義される成分（ａ）の平均ヒドロキシル官能価であり、
Ｉは、式（Ｘ）で定義されるとおりであり、ｘ_Ｉ／ｘは、Ｉ＋１のヒドロキシル官能価を有する化合物のモル分率である。 The molar equivalent is adjusted so that 0.05 ≦ x / y ≦ 0.66 and 2y-fx ≦ z ≦ 1.5 (2y-fx), and f is expressed by the following formula:

The average hydroxyl functional value of component (a) as defined by
I is as defined by formula (X) and x _I / x is the mole fraction of the compound having a hydroxyl functional value of I + 1.

Therefore, the molar equivalent x of component (a) depends on the functional value of one or more di- and / or polyhydroxyl compounds contained in component (a). According to a preferred embodiment, I is 1. If I is 1, then f is 2. According to a further preferred embodiment, the mixture contains one compound of formula (I), preferably I is 1. As a result, the compound according to formula (I) is linear.

According to the present invention, the molar equivalent y is larger than the molar equivalent x in that 0.05 ≦ x / y ≦ 0.66. Considering y> x and depending on the molar ratio of r'= x / y, the degree of polymerization (Pa) increases with Pa = (1 + r') / (1-r'). When x / y> 0.66, the viscosity of the polymerizable composition may be excessively high, so that large amounts of solvent or reactive diluent provide the photocurable dental impression material of the present invention. Needed to do. When x / y <0.05, the polymerizable composition contains an excess amount of reaction product between component (b) and component (c), thereby the photocurable dental impression material of the present invention. The mechanical properties of are reduced.

The mixture contains z mol equivalents of one or more chain stop compounds (c). The amount of z is selected according to the present invention such that 2y-fx ≦ z ≦ 1.5 (2y-fx), where f is the average hydroxyl functional value of component (a) as defined above. Preferably, z is 2y-fx. When x <2y-fx, the content of terminal groups in the macromonomer contained in the polymerizable mixture of the present invention may be reduced, which is considered the mechanical properties of the dental composite of the present invention. Is not preferable. When z> 1.5 (2y-fx), the excess amount of the chain stop compound may compete with the reaction of component (a) and component (b) and interfere with macromonomer formation.

は、以下の式に従って推定されてよい：

Average molecular weight of the polymerizable mixture

May be estimated according to the following equation:

は成分（ａ）の平均分子量であり、

は成分（ｂ）の平均分子量であり、

は成分（ｃ）の平均分子量である。 In the above formula

Is the average molecular weight of the component (a),

Is the average molecular weight of component (b),

Is the average molecular weight of the component (c).

（式中、
Ｒ^１’は、水素原子、またはＣ_１〜１２アルキル基を表し、
Ｘ^３’は、酸素原子、硫黄原子、または基ＮＲ^２（式中、Ｒ^２は、水素原子、Ｃ_１〜１２アルキル基、もしくはアリル基である）を表し、
Ｌ^５’は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
ｓは、０、または１〜６の整数を表す）
の１つ以上の化合物、
を含む混合物を反応させることによって得ることができ、
０．０５≦ｘ／ｙ≦０．６６、かつ

であり、
ｘ、ｙ、およびｚは、成分（ａ’）、（ｂ’）、および（ｃ’）のモル等量であり、

は、成分（ａ）の平均イソシアナート官能価：

であり、
ｌは、式（Ｘ’）で定義されるようなｌ’であり、ｘ_ｌ／ｘは、ｌ’＋１のイソシアナート官能価を有する化合物のモル分率である。 According to an alternative embodiment, the polymerizable polysiloxane resin mixture is
The following equation (X') of (a') x equal quantity:
OCN-L ^4' (NCO) _l'
(X')
(During the ceremony,
L ^{4 'is,} (l' a + 1) valent linker group,
l'is an integer from 1 to 5)
With one or more di- or polyisocyanate compounds of
The following equation (XI') of (b') y equal quantity:
HO-L ^{3 'OH}
(XI')
(During the ceremony,
L 3 ^'is a divalent linker group)
With one or more diol compounds
The following formula (XII') of (c') z equal quantity:

(During the ceremony,
R ^{1 'represents} a hydrogen atom or a _{C 1 to 12} alkyl group,
X ^3'represents an oxygen atom, a sulfur atom, or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ^{5 'is} a divalent hydrocarbon linker groups, preferably _{C 2 to 20} alkylene groups,
s represents an integer of 0 or 1-6)
One or more compounds of
Can be obtained by reacting a mixture containing
0.05 ≤ x / y ≤ 0.66 and

And
x, y, and z are molar equivalents of the components (a'), (b'), and (c').

Is the average isocyanate functional value of component (a):

And
l is l'as defined by the formula (X'), and x _l / x is the mole fraction of the compound having an isocyanate functional value of l'+ 1.

The mixture contains an x-mol equivalent component (a'), a y-mol equivalent component (b'), and a z-mol equivalent component (c').

によって定義される成分（ａ）の平均イソシアナート官能価であり、
Ｉは、式（Ｘ）で定義されるとおりであり、ｘ_Ｉ／ｘは、Ｉ＋１のヒドロキシル官能価を有する化合物のモル分率である。 The molar equivalent is adjusted so that 0.05 ≦ x / y ≦ 0.66 and 2y-fx ≦ z ≦ 1.5 (2y-fx), and f is expressed by the following formula:

Isocyanate functional value of component (a) defined by
I is as defined by formula (X) and x _I / x is the mole fraction of the compound having a hydroxyl functional value of I + 1.

Therefore, the molar equivalent x of component (a) depends on the functional value of one or more di- and / or polyhydroxyl compounds contained in component (a). According to a preferred embodiment, I is 1. If I is 1, then f is 2. According to a further preferred embodiment, the mixture contains one compound of formula (I), preferably I is 1. As a result, the compound according to formula (I) is linear.

According to the present invention, the molar equivalent y is larger than the molar equivalent x in that 0.05 ≦ x / y ≦ 0.66. Considering y> x and depending on the molar ratio of r'= x / y, the degree of polymerization (Pa) increases with Pa = (1 + r') / (1-r'). When x / y> 0.66, the viscosity of the polymerizable composition may be excessively high, so that large amounts of solvent or reactive diluent provide the photocurable dental impression material of the present invention. Needed to do. When x / y <0.05, the polymerizable composition contains an excess amount of reaction product between component (b) and component (c), thereby the photocurable dental impression material of the present invention. The mechanical properties of are reduced.

The mixture contains z mol equivalents of one or more chain stop compounds (c). The amount of z is selected according to the present invention such that 2y-fx ≦ z ≦ 1.5 (2y-fx), where f is the average isocyanate functional value of component (a) as defined above. Preferably, z is 2y-fx. When x <2y-fx, the content of terminal groups in the macromonomer contained in the polymerizable mixture of the present invention may be reduced, which is considered the mechanical properties of the dental composite of the present invention. Is not preferable. When z> 1.5 (2y-fx), the excess amount of the chain stop compound may compete with the reaction of component (a) and component (b) and interfere with macromonomer formation.

は、以下の式に従って推定されてよい：

Average molecular weight of the polymerizable mixture

May be estimated according to the following equation:

は成分（ａ’）の平均分子量であり、

は成分（ｂ’）の平均分子量であり、

は成分（ｃ’）の平均分子量である。 In the above formula

Is the average molecular weight of the component (a'),

Is the average molecular weight of the component (b'),

Is the average molecular weight of the component (c').

Preferably, the photocurable dental impression material comprises a polymerizable polysiloxane resin composition comprising a compound of formula (I) in an amount of 2 to 95 weight percent based on the total weight of the photocurable dental impression material. More preferably, the photocurable dental impression material comprises 4 to 20 weight percent of the compound of formula (I) based on the total weight of the photocurable dental impression material.

In addition, the photocurable dental impression material preferably comprises a polymerizable compound of formula (I) without any polysiloxane moiety, up to 75 weight percent based on the total weight of the photocurable dental impression material. good. Preferably, the photocurable dental impression material is a polymerizable compound of formula (I) without any such polysiloxane moiety, which is 10 to 50 weight percent based on the total weight of the photocurable dental impression material. May include.

Coupling agents may be used in the preparation of the polymerizable compound of formula (I). Examples of suitable coupling agents are bismuth compounds such as bismuth 2-ethylhexanoate (K-KAT 348), tin compounds such as dibutyltin dioctanoate, and 1,4-diazabicyclo [2.2.2] octane (DABCO). ) And other tertiary amines.

Filler The photocurable dental impression material of the present invention contains a filler. The filler preferably has an average particle size of 0.05 as measured, for example, by an electron microscope or by using a conventional laser diffraction particle size measurement method as embodied by a MALLVERN Mastersizer S or MALLVERN Mastersizer 3000 device. It is a fine particle filler in the range of ~ 75 μm. The fine particle filler may be a multimodal fine particle filler representing two or more fine particle fractions having different average particle sizes. The fine particle reactive filler may also be a mixture of particles of different chemical compositions.

Preferably, the photocurable dental impression material contains 10 to 60 weight percent, more preferably 20 to 50 weight percent filler, based on the total weight of the dental impression material.

The specific type of filler is not particularly limited. In order to achieve a usable curing depth, a filler having a refractive index comparable to that of one of the polymerizable resin mixtures is preferred. Therefore, toxicologically acceptable inorganic, especially hydrophobic fillers such as silica, alumina, magnesia, titania, inorganic salts, metal oxides, and glass may be employed.

The filler may be a mixture of different fillers, such as crystalline form, specifically fine quartz, amorphous silicon dioxide, specifically diatomaceous earth, and silicon dioxide containing silanated fumed silica.

The viscosity and rock denaturation of the uncured composition, as well as the physical properties of the cured composition, may be controlled by varying the size and surface area of the filler.

The filler may be surface treated with one or more silane treatment agents. Preferred silane treatment agents include those having at least one polymerizable double bond and at least one group that is easily hydrolyzed with water. Examples of such agents are 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropyldimethoxymonochromosilane, 3-methacryloxypropyldichloromonomethoxysilane, methacryloxypropyltrichlorosilane, 3-methacryloxypropyldichloromonomethyl. Included are silanes, 3-methacryloxypropylmonochlorodimethylsilanes, and mixtures thereof.

Preferred fillers are fumed silica, quartz, cristovalite, calcium silicate, diatomaceous soil, montmorillonite such as zirconium silicate, bentonite, zeolite containing molecular sieves such as sodium aluminum silicate, aluminum oxide or zinc oxide or mixed oxides thereof. Metal oxide powders such as barium sulfate, calcium carbonate, plaster, and glass powder.

Preferably, the photocurable dental impression material contains 5 to 50 weight percent of particulate filler based on the total weight of the photocurable dental impression material. More preferably, the filler is contained in an amount of 10 to 45 weight percent based on the total weight of the photocurable dental impression material.

Photoinitiator The photocurable dental impression material of the present invention contains a photoinitiator. Photoinitiators generate free radicals when exposed to chemical light. Free radicals may typically be generated by one of two pathways:
(1) The photoinitiator is excited by energy absorption followed by the compound decomposing into one or more radicals (Norlish type I), or (2) the photoinitiator is excited and excited. Will interact with the second compound by either energy transfer or oxidation-reduction reaction to form free radicals from any of the compounds (Norlish type II).

According to the present invention, any compound or system capable of initiating the polymerization of a mixture of polymerizable silicone compounds according to the present invention may be used.

For example, a suitable photoinitiator system may be in the form of a two-component or three-component system. The two-component system may include a photoinitiator and an electron donor compound, and the three-component system is an iodonium, sulfonium, or phosphonium salt, photoinitiator, and as described, for example, in US 5,545,676. It may contain an electron donor compound.

Suitable photoinitiators are monoketones and diketones that absorb some light in the range of about 400 nm to about 520 nm (preferably about 450 nm to about 500 nm). Particularly suitable compounds include alpha-diketones that absorb some light in the range of about 400 nm to about 520 nm (even more preferably about 450 nm to about 500 nm). Examples include camphorquinone, benzyl, frills, 3,3,6,6-tetramethylcyclohexanedione, phenanthraquinone, 1-phenyl-1,2-propanedione and other 1-aryl-2-alkyl-. 1,2-ethanedione, as well as cyclic alpha-diketone.

In addition, suitable photoinitiators are compounds of formula (III) below, as disclosed in EP 32341413 A1 and EP 3153150 A1:

In the compound of formula (XIII), M is Ge or Si.

In addition, in compounds of formula (XIII), R ⁷ , R ⁸ and R ⁹ may be the same or different and independently represent organic groups. Preferably, R ⁷ and R ⁸ represent a substituted or unsubstituted hydrocarbyl or hydrocarbylcarbonyl group independently of each other, and R ⁹ represents a substituted or unsubstituted hydrocarbyl group. The hydrocarbyl group may be an alkyl group, a cycloalkyl group, a cycloalkylalkyl group, an arylalkyl group, or an aryl group. The alkyl group may be a linear C _1-20 or a branched C _3-20 alkyl group, typically a linear C _1-8 or a branched C _3-8 alkyl group. Examples of C _1-16 alkyl groups include linear or branched alkyl groups having 1 to 6 carbon atoms, preferably 1 to 4 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-. Butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, isopentyl, and n-hexyl can be mentioned. The cycloalkyl group may be a C _3-20 cycloalkyl group, typically a C _3-8 cycloalkyl group. Examples of cycloalkyl groups include those having 3 to 6 carbon atoms, such as cyclopropyl, cyclobutyl, cyclopentyl, and cyclohexyl. Cycloalkylalkyl groups may have 4 to 20 carbon atoms and include a combination of a linear or branched alkyl group having 1 to 6 carbon atoms and a cycloalkyl group having 3 to 14 carbon atoms. good. Examples of cycloalkylalkyl (-) groups include, for example, methylcyclopropyl, methylcyclobutyl, methylcyclopentyl, methylcyclohexyl, ethylcyclopropyl, ethylcyclobutyl, ethylcyclopentyl, ethylcyclohexyl, propylcyclopropyl, propylcyclobutyl, Propylcyclopentyl and propylcyclohexyl can be mentioned. The arylalkyl group may be a combination of a C _7-20 arylalkyl group, typically a linear or branched alkyl group having 1 to 6 carbon atoms and an aryl group having 6 to 10 carbon atoms. .. Specific examples of arylalkyl groups are benzyl groups or phenylethyl groups. Examples of the aryl group include an aryl group having 6 to 10 carbon atoms. Examples of aryl groups are phenyl and naphthyl.

Hydrocarbyl group of R ⁷ and ^{R 8,} an acyl group _{(R org - (C = O} ) -) ( wherein the organic residue _{R org} is a is a hydrocarbyl residue as defined above) represents a ..

Compounds of formula (XIII) may contain one or two hydrocarbyl group, i.e., both of any one of R ⁷ and R ^8, or a hydrocarbyl group, or R ⁷ and R ^8, Is a hydrocarbylcarbonyl group. Preferably, the compound of formula (XIII) contains one hydrocarbylcarbonyl group. Preferably, the hydrocarbylcarbonyl group is an arylcarbonyl group, more preferably a benzoyl group. Preferably, R ⁷ and R ⁸ are independently linear C _1-6 or branched C _3-6 alkyl groups, as well as halogen atoms, nitro groups, C _1-4 alkoxy groups, and -NR ^x R ^y groups. A group consisting of phenyl or benzoyl groups which may be optionally substituted with 1-3 substituents selected from (in the formula, R ^x and R ^y _{represent C 1-4} alkyl groups independently of each other). Selected from, R ⁹ is a linear or branched C _3-6 alkyl group or phenyl group. Most preferably, R ⁷ and R ⁸ are independently linear C _1-4 or branched C ₃ or C ₄ alkyl groups, as well as halogen atoms, nitro groups, C _1-4 alkoxy groups, and -NR ^x R. ^{In the formula, R x} and R ^y are optionally substituted with one substituent selected from the group consisting of those selected from the y groups (in the formula, R _{x and R y represent C 1-4} alkyl groups independently of each other). Selected from the group of good phenyl or benzoyl groups, R ⁹ is a linear C _1-4 or branched C ₃ or C ₄ alkyl group.

Further, in the compound of formula (XIII), R ¹⁰ represents a hydrogen atom, an organic group, or an organic metal group, where R ¹⁰ is a hydrogen atom, the initiator system is light in the range of 300-600 nm. Further contains a sensitizer compound having an absorption maximum.

の基を表し、式中、Ｒ^１１は、
（ｉ）以下の式（ＸＶ）：

（式中、
Ｍ、Ｒ^７、Ｒ^８およびＲ^９は、式（ＸＩＩＩ）について上記で定義されたのと同じ意味を有し、それにより、式（ＸＩＩＩ）の化合物は、対称もしくは非対称であってよい）
の基であるか、または
（ｉｉ）以下の式（ＸＶＩ）：

（式中、
Ｘは、単結合、酸素原子、もしくは基ＮＲ^Ｘ１（式中、Ｒ^Ｘ１は、置換もしくは無置換ヒドロカルビル基を表す）を表し、
Ｒ^＊は、置換もしくは無置換ヒドロカルビル基、トリヒドロカルビルシリル基、モノ（ヒドロカルビルカルボニル）ジヒドロカルビルシリル基、もしくはジ（ヒドロカルビルカルボニル）モノヒドロカルビルシリル基を表す）
の基であるか、または
（ｉｉｉ）ＭがＳｉである場合、Ｒ^１１は、置換もしくは無置換ヒドロカルビル基であってよい。 According to the first preferred embodiment, R ¹⁰ is expressed by the following formula (XIV):

In the formula, R ^{11 represents the group of}
(I) The following equation (XV):

(During the ceremony,
M, R ⁷ , R ⁸ and R ⁹ have the same meaning as defined above for formula (XIII), so that the compound of formula (XIII) may be symmetric or asymmetric).
Is based on, or (ii) the following equation (XVI):

(During the ceremony,
X represents a single bond, an oxygen atom, or a group NR ^X1 (in the formula, ^RX1 represents a substituted or unsubstituted hydrocarbyl group).
R ^* represents a substituted or unsubstituted hydrocarbyl group, a trihydrocarbylsilyl group, a mono (hydrocarbylcarbonyl) dihydrocarbylsilyl group, or a di (hydrocarbylcarbonyl) monohydrocarbylsilyl group)
Or if (iii) M is Si, R ¹¹ may be a substituted or unsubstituted hydrocarbyl group.

^{For R *} of formula (XVI), which is a trihydrocarbylsilyl group, a mono (hydrocarbylcarbonyl) dihydrocarbylsilyl group, or a di (hydrocarbylcarbonyl) monohydrocarbylsilyl group, the hydrocarbyl and hydrocarbylcarbonyl groups are R ⁷ , R, respectively. has the same meaning as ⁸ and was defined for R ^9, is selected therefrom independently.

In formula ^{(XVI), R X1} has the same meaning as defined for ^{R 9,} it is selected therefrom independently.

According to the second preferred embodiment, R ¹⁰ represents a hydrogen atom. Therefore, the initiator system further comprises a sensitizer compound. The sensitizer compound is preferably an alpha-diketone sensitizer compound having a maximum light absorption in the range of 300 to 500 nm. The alpha-diketone sensitizer can absorb visible light and form a photoexcited complex with the hydrogen donor compound of formula (XIII). Alpha-diketone photoinitiator compounds include camphorquinone, 1,2-diphenylethane-1,2-dione (benzyl), 1,2-cyclohexanedione, 2,3-pentanedione, 2,3-hexanedione, 3 , 4-Hexanedione, 2,3-Heptanedione, 3,4-Heptanedione Glyoxal, Biacetyl, 3,3,6,6-Tetramethylcyclohexanedione, 3,3,7,7-Tetramethyl-1,2 -Cycloheptane, 3,3,8,8-tetramethyl-1,2-cyclooctanedione, 3,3,18,18-tetramethyl-1,2-cyclooctadecanedione, dipivaloyl, frills, hydroxybenzyl, It may be selected from 2,3-butanedione, 2,3-octanedione, 4,5-octanedione, and 1-phenyl-1,2-propanedione. Camphorquinone is the most preferred alpha-diketone photoinitiator. According to a preferred embodiment, the photocurable dental impression material contains an alpha-diketone sensitizer in an amount of 0.01-5 weight percent based on the total weight of the composition.

Preferably, in the compound of formula (XIII), M is Si.

For example, ^{a compound of formula (XIII) in which R 11} has formula (XV) and is symmetric may have the following structural formula:

For example, ^{formula (XIII) in which R 11} represents a group of formula (XVI) (wherein X is a bond, oxygen atom, or NR ^X1 group and R ^* represents a substituted or unsubstituted hydrocarbyl group). The compounds of may have the following structural formulas:

For example, a compound of formula (XIII) in which R represents a group of formula (XVI) (wherein R ^* represents a trihydrocarbylsilyl group) has the following structural formula:

For example, a compound of formula (XIII) where M is Si and R ¹¹ represents a substituted or unsubstituted hydrocarbyl group may have the following structural formula:

からなる群から選択され、式中、Ｍ＝Ｓｉである式（ＸＩＩＩ）の化合物が、特に好ましい。 Preferably, the compound of formula (XIII) is:

The compound of formula (XIII), which is selected from the group consisting of, and in which M = Si, is particularly preferable.

からなる群から選択され、式中、Ｍ＝Ｓｉが、特に好ましい。 More preferably, the compounds of formula (XIII) are:

It is selected from the group consisting of, and in the formula, M = Si is particularly preferable.

Most preferably, the compound of formula (XIII) is tert-butyl (tert-butyldimethylsilyl) glyoxylate) (DKSi).

Suitable photoinitiator systems may also include phosphine oxides, which typically have a functional wavelength range of about 380 nm to about 1200 nm. Examples of phosphine oxide-free radical initiators having a functional wavelength range of about 380 nm to about 450 nm are described in US 4,298,738, US 4,324,744, and US 4,385,109, and EP 0 173 567. Examples thereof include acylphosphine oxides and bisacylphosphine oxides. Specific examples of acylphosphine oxides include 2,4,6-trimethylbenzoyldiphenylphosphine oxide, bis (2,4,6-trimethylbenzoyl) phenylphosphine oxide, dibenzoylphenylphosphine oxide, and bis (2,6-dimethoxybenzoyl). ) Phosphine phosphine oxide, tris (2,4-dimethylbenzoyl) phosphine oxide, tris (2-methoxybenzoyl) phosphine oxide, 2,6-dimethoxybenzoyldiphenylphosphine oxide, 2,6-dichlorobenzoyldiphenylphosphine oxide, 2,3 , 5,6-tetramethylbenzoyldiphenylphosphine oxide, benzoyl-bis (2,6-dimethylphenyl) phosphonate, and 2,4,6-trimethylbenzoylethoxyphenylphosphine oxide. As a commercially available phosphine oxide photoinitiator capable of initiating free radicals when irradiated in the wavelength range of more than about 380 nm to about 450 nm, bis (2,4,6-trimethylbenzoyl) phenylphosphine oxide (IRGACURE 819), Bis (2,6-dimethoxybenzoyl)-(2,4,4-trimethylpentyl) phosphenyl oxide (CGI 403), bis (2,6-dimethoxybenzoyl) -2,4,4-trimethyl with a weight ratio of 25:75 A mixture of pentylphosphine oxide and 2-hydroxy-2-methyl-1-phenylpropan-1-one (IRGACURE 1700), bis (2,4,6-trimethylbenzoyl) phenylphosphine oxide with a weight ratio of 1: 1 and 2 Examples include a mixture with −hydroxy-2-methyl-1-phenylpropan-1-one (DAROCUR 4265) and ethyl 2,4,6-trimethylbenzylphenylphosphinate (LUCIRIN LR8883X). Typically, the phosphine oxide initiator is present in the composition in a catalytically effective amount, such as 0.01 weight percent to 5.0 weight percent, based on the total weight of the composition.

Suitable electron donor compounds include substituted amines such as ethyl dimethylaminobenzoate and / or dimethylaminobenzonitrile.

A tertiary amine reducing agent may be used in combination with the acylphosphine oxide. Examples of suitable aromatic tertiary amine reducing agents are N, N-dimethylaniline, N, N-dimethyl-p-toluidine, N, N-dimethyl-m-toluidine, N, N-diethyl-p-toluidine. , N, N-dimethyl-3,5-dimethylaniline, N, N-dimethyl-3,4-dimethylaniline, N, N-dimethyl-4-ethylaniline, N, N-dimethyl-4-isopropylaniline, N , N-dimethyl-4-t-butylaniline, N, N-dimethyl-3,5-di-t-butylaniline, N, N-bis (2-hydroxyethyl) -3,5-dimethylaniline, N, N-bis (2-hydroxyethyl) -p-toluidine, N, N-bis (2-hydroxyethyl) -3,4-dimethylaniline, N, N-bis (2-hydroxyethyl) -4-ethylaniline, N, N-bis (2-hydroxyethyl) -4-isopropylaniline, N, N-bis (2-hydroxyethyl) -4-t-butylaniline, N, N-bis (2-hydroxyethyl) -3, 5-Di-isopropylaniline, N, N-bis (2-hydroxyethyl) -3,5-di-t-butylaniline, 4-N, N-dimethylaminobenzoic acid ethyl ester, 4-N, N-dimethyl Aminobenzoic acid methyl ester, 4-N, N-dimethylaminobenzoic acid n-butoxyethyl ester, 4-N, N-dimethylaminobenzoic acid 2- (methacryloyloxy) ethyl ester, 4-N, N-dimethylaminobenzophenone Included are ethyl 4- (N, N-dimethylamino) benzoate, and N, N-dimethylaminoethyl methacrylate. Examples of aliphatic tertiary amines include trimethylamine, triethylamine, N-methyldiethanolamine, N-ethyldiethanolamine, Nn-butyldiethanolamine, N-lauryldiethanolamine, triethanolamine, 2- (dimethylamino) ethylmethacrylate, Examples thereof include N-methyldiethanolamine dimethacrylate, N-ethyldiethanolamine dimethacrylate, triethanolamine monomethacrylate, triethanolamine dimethacrylate, and triethanolamine trimethacrylate.

One or more amine reducing agents may be present in the composition in an amount of 0.01 weight percent to 5.0 weight percent based on the total weight of the composition.

According to a further preferred embodiment, the photoinitiator is of the formula (XVII):
^{R 12 -I + -R 13 A -} (XVII)
Further contains the iodonium compound of
Independent of each other, R ¹² and R ¹³ , represent organic moieties.
A ⁻ is an anion.

For example, the diallyl iodonium salt is (4-methylphenyl) [4- (2-methylpropyl) phenyl] iodonium hexafluoroantimonate, (4-methylphenyl) [4- (2-methylpropyl) phenyl] iodonium tetrafluoro. Borate, Diphenyliodonium (DPI) Tetrafluoroborate, Di (4-Methylphenyl) Iodonium (Me2-DPI) Tetrafluoroborate, Phenyl-4-methylphenyliodonium Tetrafluoroborate, Di (4-Heptylphenyl) Iodonium tetrafluoroborate, di (3-nitrophenyl) iodonium hexafluorophosphate, di (4-chlorophenyl) iodonium hexafluorophosphate, di (naphthyl) iodonium tetrafluoroborate, di (4-trifluoromethylphenyl) Iodonium tetrafluoroborate, DPI hexafluorophosphate, Me2-DPI hexafluorophosphate, DPI hexafluoroarsenate, di (4-phenoxyphenyl) iodonium tetrafluoroborate, phenyl-2-thienyl iodonium hexafluorophosphate, 3,5-Dimethylpyrazolyl-4-phenyliodonium hexafluorophosphate, DPI hexafluoroantimonate, 2,2'-DPI tetrafluoroborate, di (2,4-dichlorophenyl) iodonium hexafluorophosphate, di (4) -Bromophenyl) iodonium hexafluorophosphate, di (4-methoxyphenyl) iodonium hexafluorophosphate, di (3-carboxyphenyl) iodonium hexafluorophosphate, di (3-methoxycarbonylphenyl) iodonium hexafluorophosphate, Selected from di (3-methoxysulfonylphenyl) iodonium hexafluorophosphate, di (4-acetamidophenyl) iodonium hexafluorophosphate, di (2-benzothienyl) iodonium hexafluorophosphate, and DPI hexafluorophosphate. good.

Particularly preferred iodonium compounds include diphenyliodonium (DPI) hexafluorophosphate, di (4-methylphenyl) iodonium (Me2-DPI) hexafluorophosphate, diaryliodonium hexafluoroantimonate, (4-methylphenyl) [4. -(2-Methylpropyl) Phenyl] Iodonium Hexafluoroantimonate, (4-Methylphenyl) [4- (2-Methylpropyl) Phenyl] Iodium HexafluoroPhenyl (Irgacure® 250, available from BASF SE) Commercial products), (4-methylphenyl) [4- (2-methylpropyl) phenyl] iodonium tetrafluoroborate, 4-octyloxyphenylphenyl iodonium hexafluoroantimonate, 4- (2-hydroxytetradecyloxyphenyl) ) Phenyliodonium hexafluoroantimonate, and 4-isopropyl-4'-methyldiphenyliodonium borate.

According to a particularly preferred embodiment, the iodonium compound is DPI hexafluorophosphate and / or 4-isopropyl-4'-methyldiphenyliodonium tetrakis (pentafluorophenyl) borate.

According to a further preferred embodiment, the photoinitiator is of the formula (XVIII):
^{R 14 R 15 R 16 S +} A - (XVIII)
Further contains the sulfonium compound of
Independent of each other, R ¹⁴ , R ¹⁵ , and R ¹⁶ represent organic moieties, or either two of R ¹⁴ , R ¹⁵ , and R ¹⁶ form a cyclic structure with the sulfur atoms to which they are attached. ,
A ⁻ is an anion.

のＳ−（フェニル）チアントレニウムヘキサフルオロホスファートである。 Preferred triarylsulfonium salts are:

S- (Phenyl) thiantrenium hexafluorophosphate.

According to a further preferred embodiment, the photoinitiator is of the formula (XIX):
^{R 17 R 18 R 19 R 20} P + A - (XIX)
Further comprises the phosphonium compound of
Independent of each other, R ¹⁷ , R ¹⁸ , R ¹⁹ and R ²⁰ represent organic moieties.
A ⁻ is an anion.

Particularly preferred phosphonium salts are tetraalkylphosphonium salts, tetrakis- (hydroxymethyl) -phosphonium (THP) salts, or tetrakis- (hydroxymethyl) -phosphonium hydroxide (THPOH) salts, and the anion of the tetraalkylphosphonium salt is It is selected from the group consisting of formic acid, acetic acid, phosphoric acid, sulfuric acid, fluoride, chloride, bromide, and iodide.

According to a preferred embodiment, the photocurable dental impression material is 0.01-5% by weight, or 0.1 to 5% by weight, more preferably, based on the total weight of the photocurable dental impression material. Contains 1-4 weight percent photoinitiator.

Optional polymerizable (meth) acrylate or (meth) acrylamide The photocurable dental impression material of the present invention is polymerizable (meth) acrylate or (meth) in up to 20% by weight based on the total weight of the composition. It may further contain acrylamide.

(Meta) acrylate compounds include methylacryllate, methylmethacrylate, ethylacryllate, ethylmethacrylate, propylacryllate, propylmethacrylate, isopropylacryllate, isopropylmethacrylate, 2-hydroxyethylacryllate, 2-hydroxyethyl. Methacrylate (HEMA), Hydroxypropyl Acrylate, Hydroxypropyl Methrate, Tetrahydrofurfuryl Acrylate, Tetrahydrofurfuryl Methrate, Glycidyl Acrylate, Glycidyl Methrate, Bisphenol A Glycerolate Dimethacrylate ("bis-GMA", CAS No. 1565-94-2), 4,4,6,16 (or 4,6,6,16) -tetramethyl-10,15-dioxo-11,14-dioxa-2,9-diazaheptadeca-16- 2-[(2-Methyl-1-oxo-2-propen-1-yl) oxy] ethyl ester of enoic acid (CAS number 72869-86-4) _ (UDM), 1,3-glycerol dimethacrylate (GDM) ) Such as glycerol mono-and di-acrylate, glycerol mono- and dimethacrylate, ethylene glycol diacetylate, ethylene glycol dimethacrylate, polyethylene glycol diacrylate (the number of ethylene oxide repeating units varies from 2 to 30). ), Polyethylene glycol dimethacrylate (the number of ethylene oxide repeating units varies from 2 to 30, in particular triethylene glycol dimethacrylate (“TEGDMA”)), neopentyl glycol dimethacrylate, neopentyl glycol dimethacrylate, Trimethylol Propanetriacryllate, Trimethylol Propanetrimethacrylate, Pentaerythritol and Dipentaerythritol Mono, Di, Tri-, and Tetra-Acrylate and Methacrylate, 1,3-Butanediol Diacrylate, 1, 3-Butanediol dimethacrylate, 1,4-butanediol dimethacrylate, 1,4-butanediol dimethacrylate, 1,6-hexanediol dimethacrylate, 1,6-hexanediol dimethacrylate, di- 2-Methacryloxyethyl hexamethylene dicarbamate, di-2-methacryloyloxyethyl trimethylhexaneethylene dicarbamate, di-2-methacryloyl oki Siethyldimethylbenzenedicarbamate, methylene-bis-2-methacryloxyethyl-4-cyclohexylcarbamate, di-2-methacryloxyethyl-dimethylcyclohexanedicarbamate, methylene-bis-2-methacryloxyethyl-4- Cyclohexylcarbamate, di-1-methyl-2-methacryloxyethyl-trimethyl-hexamethylenedicarbamate, di-1-methyl-2-methacryloxyethyl-dimethylbenzenedicarbamate, di-1-methyl-2- Methacryloxyethyl-dimethylcyclohexanedicarbamate, methylene-bis-1-methyl-2-methacryloxyethyl-4-cyclohexylcarbamate, di-1-chloromethyl-2-methacryloxyethyl-hexamethylenedicarbamate, di. -1-Chloromethyl-2-methacryloxyethyl-trimethylhexamethylene dicarbamate, di-1-chloromethyl-2-methacryloxyethyl-dimethylbenzenedicarbamate, di-1-chloromethyl-2-methacryloxyethyl -Dimethylcyclohexanedicarbamate, methylene-bis-2-methacryloxyethyl-4-cyclohexylcarbamate, di-1-methyl-2-methacryloxyethyl-hexamethylenedicarbamate, di-1-methyl-2-methacryl Oxyethyl-trimethylhexamethylene dicarbamate, di-1-methyl-2-methacryloxyethyl-dimethylbenzenedicarbamate, di-1-methyl-2-methacryloxyethyl-dimethylcyclohexanedicarbamate, methylene-bis- 1-Methyl-2-methacryloxyethyl-4-cyclohexylcarbamate, di-1-chloromethyl-2-methacryloxyethyl-hexamethylenedicarbamate, di-1-chloromethyl-2-methacryloxyethyl-trimethylhexa Methylene dicarbamate, di-1-chloromethyl-2-methacryloxyethyl-dimethylbenzenedicarbamate, di-1-chloromethyl-2-methacryloxyethyl-dimethylcyclohexanedicarbamate, methylene-bis-1-chloro Methyl-2-methacryloxyethyl 4-cyclohexylcarbamate, 2,2'-bis (4-methacryloxyphenyl) propane, 2,2'bis (4-acrylicoxyphenyl) propane, 2,2'-bis [4 (2-Hydroxy-3-methac Lyloxy-phenyl)] propane, 2,2'-bis [4 (2-hydroxy-3-acrylicoxy-phenyl) propane, 2,2'-bis (4-methacryloxyethoxyphenyl) propane, 2,2'- Bis (4-acrylicoxyethoxyphenyl) propane, 2,2'-bis (4-methacryloxypropoxyphenyl) propane, 2,2'-bis (4-acrylicoxypropoxyphenyl) propane, 2,2'-bis ( 4-Methacryloxydiethoxyphenyl) propane, 2,2'-bis (4-acrylicoxydiethoxyphenyl) propane, 2,2'-bis [3 (4-phenoxy) -2-hydroxypropane-1-methacrylate ] Propane, as well as 2,2'-bis [3 (4-phenoxy) -2-hydroxypropane-1-acrylate] propane may be selected.

Preferred (meth) acrylamide may be selected from the following compounds.

を有するＮ，Ｎ’−ジアリル−１，４−ビスアクリルアミド−（２Ｅ）−ブタ−２−エン（ＢＡＡＢＥ）、
および
構造式

を有するＮ，Ｎ’−ジエチル−１，３−ビスアクリルアミド−プロパン（ＢＡＤＥＰ）
である。 Most preferred is bis- (meth) acrylamide;
Structural formula

N, N'-diallyl-1,4-bisacrylamide- (2E) -but-2-ene (BAABE),
And structural formula

N, N'-diethyl-1,3-bisacrylamide-propane (BADEP)
Is.

Further Ingredients Optionally, the photocurable dental impression material of the present invention may further include stabilizers (s), plasticizers, dyes / pigments, and / or flavors / sweeteners. Furthermore, the photocurable dental impression material of the present invention may further contain a cationically polymerizable monomer.

As used herein, the term "stabilizer" means any compound that can prevent the polymerizable compound contained in the photocurable dental impression material from spontaneously polymerizing during storage. However, the stabilizer does not interfere with or prevent the intended polymerization cure of the photocurable dental impression material during application.

For example, the stabilizer is conventionally selected from the group consisting of hydroquinone, hydroquinone monomethyl ether, tert-butyl-hydroquinone, tert-butylhydroxyanisole, propyl gallate, and 2,6-di-tert-butyl-p-cresol. It may be a stabilizer of. Of these conventional stabilizers, 2,6-di-tert-butyl-p-cresol is preferred. In addition, anaerobic stabilizers such as TEMPO, phenothiazine, galbinoxyl radicals may be used.

The photocurable dental impression material according to the present invention contains a stabilizer in an amount of 0.001 to 1% by weight, preferably 0.005 to 0.8% by weight, based on the total weight of the composition. good. If the amount of stabilizer is less than the lower limit of 0.001 shown above, the storage stability of the photocurable dental impression material is poor because the amount of stabilizer is too small to provide a stabilizing effect. May be enough. However, if the amount of stabilizer is above the maximum threshold of 1 weight percent, a higher amount of stabilizer will interfere with or substantially cure the intended polymerization cure of the photocurable dental impression material during application. It can even prevent it, which can adversely affect the applicability of photocurable dental impression materials.

The photocurable dental impression material according to the present invention improves the softness of the impression material at the time of curing, reduces the affinity between the cured impression and the dental substrate, and gives an impression from the dental substrate. One or more plasticizers may be included to enhance the clean removal of. Suitable plasticizers are non-toxic in the oral environment and include, for example, mineral oils, vegetable oils, hydrogenated vegetable oils, silicone oils, phthalic acid derivatives such as dibutyl phthalate, diethyl phthalate, and dioctyl phthalate, fatty alcohols, fats. It may contain (meth) acrylate, glycerin, glyceride, and other macromolecules such as polyethylene glycol, polypropylene glycol, poly tetrahydrofuran, polyvinyl alcohol, polyether-modified polysiloxane, xanthan gum, cellulose polyalkylene glycol, and hydrocarbon wax. Includes their halogenated derivatives and / or hydrogenated derivatives.

The photocurable dental impression material is 0.1 to 20 wt. Based on the total weight of the composition. % Plasticizer, optionally 1-10 wt. May contain% plasticizer.

Dyes and pigments are selected to have no or low absorption and scattering of chemical light as measured by, for example, UV-Visible spectroscopy, while coloring the photocurable dental impression material. Suitable dyes and pigments are soluble in the polymerizable resin matrix or measured, for example, by electron microscopy or by using conventional laser diffraction particle size measurement methods, in the range of 0.05-75 μm. Has an average particle size. In some embodiments, thermochromic pigments and thermochromic liquid crystals, including leuco dyes, that change from a high absorbance color to a low absorbance color within the wavelength range of chemical light when heated at physiological temperatures are used. ..

The photocurable dental impression material may contain 1 wt ppm to 10 wt%, optionally 4 ppm to 5 wt% dyes and / or pigments based on the total weight of the composition.

（式中、
Ｋ＝カチオン重合性基、
Ｒ^２１＝有機部分、
ｏ≧１）
による１つ以上のカチオン重合性基を有する化合物を含む、追加のカチオン重合性樹脂を含んでよい。 According to a particular embodiment, the photocurable dental impression material according to the present invention has the following formula (XX):

(During the ceremony,
K = cationically polymerizable group,
R ²¹ = organic part,
o ≧ 1)
Additional cationically polymerizable resins may be included, including compounds having one or more cationically polymerizable groups according to.

Preferably, K represents a vinyl ether group, a vinyl ester group, a vinylsiloxane group, an epoxide group, an oxetane group, and a furan group.

More preferably, K represents a vinyl ether group and a vinyl ester group, and most preferably K represents a vinyl ether group.

Preferably, R ²¹ may contain 1-15 heteroatoms selected from O, S, Si, C _1-4 alkyl groups, C _4-10 aryl groups, C _4-9 heteroaryl groups, _{Represents an o-valent C 1-30} hydrocarbyl group that may be substituted with 1 to 15 substituents selected from halogen atoms, C _1-4 alkoxy groups, ester groups, thioether groups, silyl groups, and siloxane groups.

The hydrocarbyl group may be an alkyl group, a cycloalkyl group, a cycloalkylalkyl group, an arylalkyl group, or an aryl group.

The alkyl group may be a linear or branched C _1-30 alkyl group, typically a C _1-6 alkyl group. Examples of C _1-6 alkyl groups include linear or branched alkyl groups having 1 to 6 carbon atoms, preferably 1 to 4 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-. Butyl, isobutyl, sec-butyl, tert-butyl, n-pentyl, isopentyl, and n-hexyl can be mentioned.

The cycloalkyl group may be a C _3-20 cycloalkyl group, typically a C _3-8 cycloalkyl group. Examples of cycloalkyl groups include those having 3 to 6 carbon atoms, such as cyclopropyl, cyclobutyl, cyclopentyl, and cyclohexyl.

Cycloalkylalkyl groups may have 4 to 20 carbon atoms and include a combination of a linear or branched alkyl group having 1 to 6 carbon atoms and a cycloalkyl group having 3 to 14 carbon atoms. good. Examples of cycloalkylalkyl groups include, for example, methylcyclopropyl, methylcyclobutyl, methylcyclopentyl, methylcyclohexyl, ethylcyclopropyl, ethylcyclobutyl, ethylcyclopentyl, ethylcyclohexyl, propylcyclopropyl, propylcyclobutyl, propylcyclopentyl, Propylcyclohexyl can be mentioned.

The arylalkyl group may be a combination of a C _7-20 arylalkyl group, typically a linear or branched alkyl group having 1 to 6 carbon atoms and an aryl group having 6 to 10 carbon atoms. .. Specific examples of arylalkyl groups are benzyl groups or phenylethyl groups.

Examples of the aryl group include an aryl group having 6 to 10 carbon atoms. Examples of aryl groups are phenyl and naphthyl.

The hydrocarbylcarbonyl group of R ²¹ represents an acyl group (R ²² − (C = O) −) (in the formula, the organic residue R ²² is a hydrocarbyl residue as defined above).

Preferably, the hydrocarbylcarbonyl group is an arylcarbonyl group, more preferably a benzoyl group.

Preferably, R ²¹ is a phenyl or benzoyl group optionally substituted with a linear or branched C _1-6 alkyl group and 1-3 substituents selected from halogen atoms, C _{1-4 alkoxy groups.} Selected from the group consisting of.

Preferably o is 1-4, more preferably o is 2.

の化合物であり、式中、
同じであるかまたは異なっていてよいＲ^２３およびＲ^２６は、独立して、水素原子、Ｃ_１〜４アルキル基、ビニル基、ビニルシリル基、エポキシド基、オキセタン基、フラン基を表し、
同じであるかまたは異なっていてよいＲ^２４およびＲ^２５は、独立して、水素原子、Ｃ_１〜４アルキル基、またはビニルエーテル基、ビニルエステル基、ビニルシロキサン基、エポキシド基、オキセタン基、フラン基を表し、
Ｘ’は、酸素、硫黄、または炭素原子を表し、
ｐは、１〜１０の整数を表し、
ただし、少なくとも１つのカチオン重合性基が、式（ＸＸＩ）の化合物中に存在する。 More preferably, the reactive diluent is of formula (XXI).

In the formula,
^{R 23} and R ²⁶ , which may be the same or different, independently represent a hydrogen atom, a C _1-4 alkyl group, a vinyl group, a vinylsilyl group, an epoxide group, an oxetane group, a furan group.
^{R 24} and R ²⁵ , which may be the same or different, are independently hydrogen atoms, C _1-4 alkyl groups, or vinyl ether groups, vinyl ester groups, vinyl siloxane groups, epoxide groups, oxetane groups, furan groups. Represents
X'represents an oxygen, sulfur, or carbon atom
p represents an integer from 1 to 10 and represents
However, at least one cationically polymerizable group is present in the compound of formula (XXI).

In a preferred embodiment, X'represents an oxygen atom, R ²⁴ represents a hydrogen atom or a methyl group, R ²⁵ represents a hydrogen atom, R ²³ and R ²⁶ represent a vinyl group, and more preferably X'represents. R ²⁴ and R ²⁵ represent a hydrogen atom, and R ²³ and R ²⁶ represent a vinyl group.

A particularly suitable reactive diluent is ethylene glycol vinyl ether.

The present invention also provides the use of photocurable dental impression materials according to the invention for the production of dental impressions.

It has been found that the acid residues in the raw material Silver OH Di-10 (hydroxyl-terminated siloxane) have a significant adverse effect on the performance of the composition formulated from the polymerizable resin B derived from the hydroxyl-terminated siloxane. Due to the inconsistent quality of ready-made / impure hydroxyl-terminated siloxanes from the same manufacturer and / or different manufacturers, efforts to identify the root cause of the inconsistent quality of such off-the-shelf / impure raw materials. It has been made. Once the active impurities have been identified, their activity is to ensure the performance of the compositions formulated from good quality hydroxyl-terminated siloxanes and the polymerizable resin B derived from such treated hydroxyl-terminated siloxanes. An effective process for removing / cleaning impurities has been developed.

"Off-the-shelf" and "impure" are used interchangeably.

The identified active impurities include alcohols, aldehydes, and acids, along with additional unidentified compounds. Generally, a high acid value of 0.25 to 0.55 mgKOH / g was found in such off-the-shelf hydroxyl-terminated siloxanes (Silmer OH Di-10 from Silkech, or DMS-C16 from Gelest), which Designated as low quality hydroxyl-terminated siloxane. It has also been found that some off-the-shelf raw materials can easily transform into low quality hydroxyl-terminated siloxanes with increasing acid value due to normal aging at room temperature.

To ensure good quality hydroxyl-terminated siloxanes, solid acid-absorbing materials were used to treat low-quality hydroxyl-terminated siloxanes.

のポリシロキサン基であって、式中、
Ｒ^１＃は、１〜８つの炭素原子を有するアルキレンであり、
Ｒ^２＃は、１〜４つの炭素原子を有するアルキルであり、
ｙ^＃は、５〜２０の整数である）
の純粋でないジオール化合物を、固体酸吸収材料で処理して精製された式（Ｘａ）の化合物を得るステップと、
（ｂ）以下の：
（ｉ）ｘ等量の、精製された式（Ｘａ）の化合物、および以下の式
ＨＯ−Ｌ^４’’（ＯＨ）_ｌ’’
（Ｘａ’）
（式中、
Ｌ^４’’は、（ｌ^’’＋１）価のリンカー基であり、
ｌ^’’は、１〜５の整数である）
の１つ以上のジ−またはポリオール化合物と、
（ｉｉ）ｙ等量の、以下の式（ＸＩ）：
ＯＣＮ−Ｌ^３ＮＣＯ
（ＸＩ）
（式中、Ｌ^３は、式（ＶＩ）

の二価のリンカー基であって、式中、
同じであるかまたは異なっていてよいＲ^ａ１およびＲ^ａ２は、独立して、水素原子、Ｃ_１〜６線状または分岐アルキル基、Ｃ_４〜１０アリール基、重合性二重結合含有有機残基、以下の式［−Ｘ’’Ｌ’’］_ｍＲ^ａ３（式中、Ｘ’’はＯ、Ｓ、もしくはＮＲ^ａ４（式中、Ｒ^ａ４は、水素原子、重合性二重結合を含有する有機残基、線状もしくは分岐Ｃ_１〜６アルキル基、もしくはＣ_４〜１０アリール基を表す）を表し、Ｌ’’は、Ｃ_１〜６線状もしくは分岐アルキル基、Ｃ_４〜１０アリール基、もしくはＳｉＲ^ａ５ _２基（式中、同じであるかもしくは異なっていてよいＲ^ａ５は、独立して、重合性二重結合を含有する有機残基、もしくはＣ_１〜４アルキル基、好ましくはメチル基を表す）を表し、ｍは、１〜２０の整数であり、Ｒ^ａ３は、重合性二重結合を含有する有機残基、Ｃ_１〜４アルキル基、もしくはＣ_４〜１０アリール基である）の基を表す）
の１つ以上の化合物と、
（ｉｉｉ）ｚ等量の、以下の式（ＸＩＩ）：

（式中、
Ｒ^１は、水素原子、またはＣ_１〜１２アルキル基を表し、
Ｘ^３は、酸素原子、硫黄原子、または基ＮＲ^２（式中、Ｒ^２は、水素原子、Ｃ_１〜１２アルキル基、もしくはアリル基である）を表し、
Ｌ^５は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
Ｘ^４は、酸素原子、硫黄原子、または基ＮＲ^３（式中、Ｒ^３は、水素原子、もしくはＣ_１〜１２アルキル基である）を表し、
ａは、１〜２０の整数を表し、
０．０５≦ｘ／ｙ≦０．６６であり、
ｘ、ｙ、およびｚは、成分（ａ）、（ｂ）、および（ｃ）のモル等量である）
の１つ以上の化合物、
を含む混合物を反応させて重合性ポリシロキサン樹脂混合物を形成するステップ、
を含むプロセスにより得られる重合性ポリシロキサン樹脂混合物を含む。 In embodiments, photocurable dental impression materials with improved shore hardness and improved tear strength may be provided. Impression material is
(A) Equation (Xa)
HO-L ⁴ (OH) _l
(Xa)
(In the formula, L ⁴ is the formula (VIIIa).

Polysiloxane group in the formula,
R ^{1 #} is an alkylene having 1 to 8 carbon atoms.
R ^{2 #} is an alkyl having 1 to 4 carbon atoms.
y ^# is an integer from 5 to 20)
To obtain a purified compound of formula (Xa) by treating an impure diol compound of
(B) The following:
(I) x equal amounts of the purified compound of formula (Xa) and the following formula HO-L ^4'' (OH) _l''
(Xa')
(During the ceremony,
L ^4'' is a (l ^'' + 1) -valent linker group.
l ^'' is an integer from 1 to 5)
With one or more di- or polyol compounds of
The following equation (XI): of (ii) y equal amount:
OCN-L ³ NCO
(XI)
(In the formula, L ³ is the formula (VI).

It is a divalent linker group of
^{R a1} and R ^a2 , which may be the same or different, are independently hydrogen atoms, C _1-6 linear or branched alkyl groups, C _4-10 aryl groups, polymerizable double bond containing organic residues. , The following formula [-X''L''] _m R ^a3 (in the formula, X'' is O, S, or NR ^a4 (in the formula, R ^a4 contains a hydrogen atom, a polymerizable double bond). Represents an organic residue, linear or branched C _1-6 alkyl group, or C _4-10 aryl group), where L ″ represents C _1-6 linear or branched alkyl group, C _4-10 aryl group. , Or SiR ^a5 ₂ groups (in the formula, R ^a5 which may be the same or different is an organic residue containing a polymerizable double bond independently, or a C _1-4 alkyl group, preferably methyl. Represents a group), m is an integer of 1 to 20, and ^Ra3 is an organic residue containing a polymerizable double bond, a C _1-4 alkyl group, or a C _4-10 aryl group. ) Represents the group)
With one or more compounds of
The following formula (XII) of (iii) z equal quantity:

(During the ceremony,
R ¹ represents a hydrogen atom or a C _1-12 alkyl group.
X ³ represents an oxygen atom, a sulfur atom, or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ⁵ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
X ⁴ represents an oxygen atom, a sulfur atom, or a group NR ³ (in the formula, R ³ is a hydrogen atom or a C _1-12 alkyl group).
a represents an integer of 1 to 20 and represents
0.05 ≦ x / y ≦ 0.66,
x, y, and z are molar equivalents of the components (a), (b), and (c))
One or more compounds of
To form a polymerizable polysiloxane resin mixture by reacting the mixture containing
Contains a polymerizable polysiloxane resin mixture obtained by a process comprising.

の二価の基を表し、式中、
２つ以上のＬ^３が存在する場合、同じであるかまたは異なっていてよいＬ^３は、独立して、最大４つの式（ＩＩＩ）：
−Ｌ^１−Ｅ
（ＩＩＩ）
の置換基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）で置換されてよい二価のリンカー基を表し、
２つ以上のＬ^４が存在する場合、同じであるかまたは異なっていてよいＬ^４は、独立して、最大４つの式（ＩＩＩ）の置換基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）で置換されてよい二価のリンカー基を表し、
Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、同じであるかまたは異なっていてよく、２つ以上のＸ^１、Ｘ^２、Ｙ^１、またはＹ^２が存在する場合、Ｘ^１、Ｘ^２、Ｙ^１、およびＹ^２は、同じであるかまたは異なっていてよく、独立して、酸素原子、硫黄原子、および基ＮＲ’（式中、Ｒ’は、水素原子もしくはＣ_１〜４アルキル基である）を表し、
ｍは、０、または１〜４０の整数を表し、
Ｚは、ポリシロキサン基および式（ＩＩＩ）の基（式中、Ｌ^１はおよびＥは、上記で定義されるとおりである）から選択される最大４つの置換基でさらに置換されてよい二価のリンカー基を表し、
Ｌ^２は、単結合または式（ＩＩ）の二価の基（式中、Ｌ^３、Ｌ^４、Ｘ^１、Ｘ^２、Ｙ^１、Ｙ^２、およびｍは、独立して、Ｌ^１について定義されるとおりである）を表し、
ｎは、０、または１〜４の整数を表し、
ただし、
−式（Ｉ）の化合物は、重合性炭素−炭素二重結合を有する少なくとも１つの一価の基Ｅを含有し、
−式（Ｉ）の化合物は、少なくとも１つのポリシロキサン基を含有し、
ただし、
ｎが０である場合、Ｌ^２は、式（ＩＩ）の二価の基である。 In one embodiment of the photocurable dental impression material, the polymerizable polysiloxane resin composition is of the following formula (I):
E- (L ^1- Z) _n- L ^2- E
(I)
In the formula,
E, which may be the same or different, is independently a group containing a polymerizable carbon-carbon double bond, a group containing a polysiloxane moiety, a C _2-20 alkoxy group, and a C _2-20 thioalkyl group. , And RNH groups (in the formula, R is a C _2-20 alkyl group), representing a monovalent group.
If more than one L ¹ is present, may L ¹ which have the same or different, the following formula (II):

Represents the divalent group of
If more than one L ³ there may L ³ that have the same or different, independently, up to four of the formula (III):
-L ^1- E
(III)
Substituents (wherein, L ¹ is and E is as defined above) represents which may be substituted bivalent linker group,
If more than one L ⁴ is present may L ⁴ which have the same or different, are independently a substituent (wherein up to four of the formula (III), L ¹ is and E, the Represents a divalent linker group that may be substituted with (as defined in)
X ¹ , X ² , Y ¹ , and Y ² may be the same or different, and if more than one X ¹ , X ² , Y ¹ , or Y ² is present, then X ¹ , X ² , Y ¹ , and Y ² may be the same or different, and independently, an oxygen atom, a sulfur atom, and a group NR'(in the formula, R'is a hydrogen atom or a C _1-4 alkyl group. Represents)
m represents an integer of 0 or 1-40,
Z is a group (wherein, L ¹ is and E is as defined above) of the polysiloxane group and the formula (III) further which may be substituted divalent up to four substituents selected from Represents the linker group of
L ² is a single bond or a divalent group of formula (II) (in the formula, L ³ , L ⁴ , X ¹ , X ² , Y ¹ , Y ² , and m are independently defined for ^{L 1).} As it is done),
n represents an integer of 0 or 1-4,
However,
-The compound of formula (I) contains at least one monovalent group E having a polymerizable carbon-carbon double bond.
-The compound of formula (I) contains at least one polysiloxane group and contains.
However,
If n is 0, then L ² is the divalent group of formula (II).

（式中、
Ｒ^１＃は、１〜８つの炭素原子を有するアルキレンであり、
Ｒ^２＃は、１〜４つの炭素原子を有するアルキルであり、
ｙ^＃は、５〜２０の整数である）
のポリシロキサン基を表す。 In some embodiments of photocurable dental impression material, L ² , and / or L ³ , and / or L ⁴ independently formulate the following formula (VIIIa):

(During the ceremony,
R ^{1 #} is an alkylene having 1 to 8 carbon atoms.
R ^{2 #} is an alkyl having 1 to 4 carbon atoms.
y ^# is an integer from 5 to 20)
Represents the polysiloxane group of.

の基であり、式中、
同じであるかまたは異なるＲ^ｂ１、Ｒ^ｂ２、Ｒ^ｂ３、およびＲ^ｂ４は、独立して、水素原子、Ｃ_１〜６線状または分岐アルキル基、Ｃ_４〜１０アリール基、重合性二重結合含有有機残基、以下の式［−Ｘ’’’Ｌ’’’］_ｍＲ^ｂ５（式中、Ｘ’’’はＯ、Ｓ、もしくはＮＲ^ｂ６（式中、Ｒ^ｂ６は、水素原子、重合性二重結合を含有する有機残基、線状もしくは分岐Ｃ_１〜６アルキル基、もしくはＣ_４〜１０アリール基を表す）を表し、Ｌ’’’は、Ｃ_１〜６線状もしくは分岐アルキル基、Ｃ_４〜１０アリール基、もしくはＳｉＲ^ｂ７ _２基（式中、同じであるかもしくは異なるＲ^ｂ７は、独立して、重合性二重結合を含有する有機残基、もしくはＣ_１〜４アルキル基を表す）を表し、ｍは、１〜２０の整数であり、Ｒ^ｂ５は、重合性二重結合を含有する有機残基、Ｃ_１〜４アルキル基、もしくはＣ_４〜１０アリール基である）の基を表し、
Ｘ^５およびＸ^６は、同じであるかまたは異なり、２つ以上のＸ^５またはＸ^６が存在する場合、Ｘ^５およびＸ^６は、同じであるかまたは異なり、独立して、酸素原子、硫黄原子、および基ＮＲ^Ｎ（式中、Ｒ^Ｎは、水素原子もしくはＣ_１〜４アルキル基である）を表し、
Ｌ^６は、二価の炭化水素リンカー基であり、
ｅは、１〜１０の整数であり、
ｆは、１〜１００の整数であり、
ｇは、０または１である。 In one embodiment of the photocurable dental impression material, L ^{4 ″} is of formula (VII) :.

In the formula,
The same or different R ^b1 , R ^b2 , R ^b3 , and R ^b4 are independently hydrogen atoms, C _1-6 linear or branched alkyl groups, C _4-10 aryl groups, polymerizable double bonds. Containing organic residues, the following formula [-X'''L'''] _m R ^b5 (in the formula, X''' is O, S, or NR ^b6 (in the formula, R ^b6 is a hydrogen atom, polymerization Represents an organic residue containing a sex double bond, a linear or branched C _1-6 alkyl group, or a C _4-10 aryl group), where L'''represents a C _1-6 linear or branched alkyl. Group, C _4-10 aryl group, or SiR ^b7 ₂ groups (in the formula, the same or different R ^b7 are independently organic residues containing a polymerizable double bond, or C _1-4 alkyl. Represents a group), m is an integer of 1 to 20, and R ^b5 is an organic residue containing a polymerizable double bond, a C _1-4 alkyl group, or a C _4-10 aryl group. ) Represents the group
X ⁵ and X ⁶ are the same or different, and if two or more X ⁵ or X ⁶ are present, then X ⁵ and X ⁶ are the same or different, independently of the oxygen atom, sulfur. atom, and a group NR ^N (wherein, ^{R N} represents a hydrogen atom or a _{C 1 to 4} alkyl group) represents,
L ⁶ is a divalent hydrocarbon linker group and
e is an integer from 1 to 10 and
f is an integer from 1 to 100 and
g is 0 or 1.

According to a preferred embodiment, the group- [L ^6- X ⁵ ]-is selected from the following groups:

In embodiments of the photocurable dental impression materials, L ³ is selected from the following groups:

のポリシロキサン基であって、式中、
Ｒ^１＃は、１〜８つの炭素原子を有するアルキレンであり、
Ｒ^２＃は、１〜４つの炭素原子を有するアルキルであり、
ｙ^＃は、５〜２０の整数である）
の純粋でないジオール化合物を、固体酸吸収材料で処理して精製された式（Ｘａ）の化合物を得るステップと、
（ｂ）以下の：
（ｉ）ｘ等量の、精製された式（Ｘａ）の化合物、および以下の式
ＨＯ−Ｌ^４’’（ＯＨ）_ｌ’’
（Ｘ）
（式中、
Ｌ^４’’は、（ｌ^’’＋１）価のリンカー基であり、
ｌ^’’は、１〜５の整数である）
の１つ以上のジ−またはポリオール化合物と、
（ｉｉ）ｙ等量の、以下の式（ＸＩ）：
ＯＣＮ−Ｌ^３ＮＣＯ
（ＸＩ）
（式中、Ｌ^３は、式（ＶＩ）

の二価のリンカー基であって、式中、
同じであるかまたは異なっていてよいＲ^ａ１およびＲ^ａ２は、独立して、水素原子、Ｃ_１〜６線状または分岐アルキル基、Ｃ_４〜１０アリール基、重合性二重結合含有有機残基、以下の式［−Ｘ’’Ｌ’’］_ｍＲ^ａ３（式中、Ｘ’’はＯ、Ｓ、もしくはＮＲ^ａ４（式中、Ｒ^ａ４は、水素原子、重合性二重結合を含有する有機残基、線状もしくは分岐Ｃ_１〜６アルキル基、もしくはＣ_４〜１０アリール基を表す）を表し、Ｌ’’は、Ｃ_１〜６線状もしくは分岐アルキル基、Ｃ_４〜１０アリール基、もしくはＳｉＲ^ａ５ _２基（式中、同じであるかもしくは異なっていてよいＲ^ａ５は、独立して、重合性二重結合を含有する有機残基、もしくはＣ_１〜４アルキル基、好ましくはメチル基を表す）を表し、ｍは、１〜２０の整数であり、Ｒ^ａ３は、重合性二重結合を含有する有機残基、Ｃ_１〜４アルキル基、もしくはＣ_４〜１０アリール基である）の基を表す）
の１つ以上の化合物と、
（ｉｉｉ）ｚ等量の、以下の式（ＸＩＩ）：

（式中、
Ｒ^１は、水素原子、またはＣ_１〜１２アルキル基を表し、
Ｘ^３は、酸素原子、硫黄原子、または基ＮＲ^２（式中、Ｒ^２は、水素原子、Ｃ_１〜１２アルキル基、もしくはアリル基である）を表し、
Ｌ^５は、二価の炭化水素リンカー基、好ましくはＣ_２〜２０アルキレン基であり、
Ｘ^４は、酸素原子、硫黄原子、または基ＮＲ^３（式中、Ｒ^３は、水素原子、もしくはＣ_１〜１２アルキル基である）を表し、
ａは、１〜２０の整数を表し、
０．０５≦ｘ／ｙ≦０．６６であり、
ｘ、ｙ、およびｚは、成分（ａ）、（ｂ）、および（ｃ）のモル等量である）
の１つ以上の化合物、
を含む混合物を反応させて重合性ポリシロキサン樹脂混合物を形成するステップ、
を含む。 In one aspect, a process for preparing a polymerizable polysiloxane resin mixture is provided. The process is the following steps:
(A) Equation (Xa)
HO-L ⁴ (OH) _l
(Xa)
(In the formula, L ⁴ is the formula (VIIIa).

Polysiloxane group in the formula,
R ^{1 #} is an alkylene having 1 to 8 carbon atoms.
R ^{2 #} is an alkyl having 1 to 4 carbon atoms.
y ^# is an integer from 5 to 20)
To obtain a purified compound of formula (Xa) by treating an impure diol compound of
(B) The following:
(I) x equal amounts of the purified compound of formula (Xa) and the following formula HO-L ^4'' (OH) _l''
(X)
(During the ceremony,
L ^4'' is a (l ^'' + 1) -valent linker group.
l ^'' is an integer from 1 to 5)
With one or more di- or polyol compounds of
The following equation (XI): of (ii) y equal amount:
OCN-L ³ NCO
(XI)
(In the formula, L ³ is the formula (VI).

It is a divalent linker group of
^{R a1} and R ^a2 , which may be the same or different, are independently hydrogen atoms, C _1-6 linear or branched alkyl groups, C _4-10 aryl groups, polymerizable double bond containing organic residues. , The following formula [-X''L''] _m R ^a3 (in the formula, X'' is O, S, or NR ^a4 (in the formula, R ^a4 contains a hydrogen atom, a polymerizable double bond). Represents an organic residue, linear or branched C _1-6 alkyl group, or C _4-10 aryl group), where L ″ represents C _1-6 linear or branched alkyl group, C _4-10 aryl group. , Or SiR ^a5 ₂ groups (in the formula, R ^a5 which may be the same or different is an organic residue containing a polymerizable double bond independently, or a C _1-4 alkyl group, preferably methyl. Represents a group), m is an integer of 1 to 20, and ^Ra3 is an organic residue containing a polymerizable double bond, a C _1-4 alkyl group, or a C _4-10 aryl group. ) Represents the group)
With one or more compounds of
The following formula (XII) of (iii) z equal quantity:

(During the ceremony,
R ¹ represents a hydrogen atom or a C _1-12 alkyl group.
X ³ represents an oxygen atom, a sulfur atom, or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ⁵ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
X ⁴ represents an oxygen atom, a sulfur atom, or a group NR ³ (in the formula, R ³ is a hydrogen atom or a C _1-12 alkyl group).
a represents an integer of 1 to 20 and represents
0.05 ≦ x / y ≦ 0.66,
x, y, and z are molar equivalents of the components (a), (b), and (c))
One or more compounds of
To form a polymerizable polysiloxane resin mixture by reacting the mixture containing
including.

Examples of the solid acid absorbing material may include _{weakly basic ion exchange resins such as active basic alumina oxide (Al 2} O ₃ ), molecular sieve (MS), and Amberlyst A21, or a combination thereof. Low quality hydroxyl ends such as silmer monomers (lot # 11801005 and lot # 11804022) in which active basic alumina oxide (Al ₂ O _{3) and molecular sieve (MS) have an acid value of 0.234 to 0.297 mgKOH / g.} Used to treat siloxane. Not only was the total acid value significantly reduced from 0.234 to 0.297 mgKOH / g to 0.056 mgKOH / g, but the pH also increased (as is apparent from Tables 15, 16 and 17). More importantly, the polymerizable urethane-polyester-siloxane copolymer was able to present significant enhancements in mechanical properties such as Shore A hardness and tear strength in each of its blended compositions (FIG. 5). And as shown in 6). The composition was blended as a paste with a 15% wt / wt filler mixture and cured with an LED curing pad. Tear strength was tested using the old test method (see the test method description for details).

The solid acid absorbing material is added in an amount of 1-10% wt / wt based on the total weight of the ready-made / impure hydroxyl-terminated siloxane, or 1-5% based on the total weight of the ready-made hydroxyl-terminated siloxane. rice field. It has been found _{that such basic Al 2} O _{3 at} 5-10% wt / wt works well. Molecular sieves are optional to reduce total water content during such treatments. The weakly basic ion exchange resin, Amberlyst A21, has also been demonstrated to work well to remove acidic impurities from low quality hydroxyl-terminated siloxanes and restore good mechanical properties. Such effectiveness includes reduced low acid value (<0.06 mgKOH / g) to achieve higher pH (> 4.0), complete removal of allyl alcohol, recovery of urethane reaction with elevated exothermic temperature. It is evident from the consistent results of the high reactivity that has been achieved and the good mechanical properties of the TRON paste formulated from the resin B derived from such pretreated Simmer monomers.

Next, the present invention will be further described based on the following examples.

Examples Typical Compositions and Processes for Siloxane-Modified Origin Resins (Figure 1) and PEGMA Modified Origin Resins:
Preparation Example 1
Siloxane-modified origin resin (Fig. 1):
The following raw materials were used.

Dry air was purged through a 1000 mL resin reaction kiln and the jacket temperature was set to 50 ° C. Trimethylhexamethylene diisocyanate (TMDI) (121.7 g, 0.58 mol) was added to the reaction kiln, followed by Volanol-220-028 (466.8 g, 0.12 mol), followed by the Simmer monomer (284.0 g, 0). .29 mol) and 0.31 g of urethane catalyst (K-Kat® 348, bismuth carboxylate from King Industries) were added to the reaction system. The reaction was maintained for an additional 2-3 hours. Samples were then taken for analysis by FTIR and NMR to confirm that all hydroxyl groups had reacted before proceeding to the next step. PEGMA (116.6 g, 0.32 mol) was added slowly to the reaction system for 30 minutes. The reaction was maintained at 50 ° C. for an additional 2 hours. 1-Dodecanol (118.2 g, 0.10 mol) was then slowly added to the system. The reaction was maintained at 50 ° C. overnight and then butylated hydroxytoluene (BHT) (0.4 g) was added to the system prior to removal. Samples for FTIR and NMR were taken. The resin was placed at 45 ° C. to expel all trapped air bubbles. A viscosity of 11 Pa · s was obtained at 25 ° C. with an MA content of 0.32 mmol / g and a siloxane content of 28.2% wt / wt.

Examples 2-14
Further siloxane-modified polyether-urethane dimethacrylate macromonomers were prepared in the same manner as described in Preparation Example 1.

The compositions and properties of the macromonomers of Preparation Examples 1-14 are as shown in Tables 1 and 2 below.

Example 15 (reference)
PEGMA modified origin resin as additional polymerizable macromonomer (Fig. 2):
The following raw materials were used.

Dry air was purged through a 1000 mL resin reaction kiln and the jacket temperature was set to 50 ° C. Trimethylhexamethylene diisocyanate (TMDI) (105.35 g, 0.50 mol) was added to the reaction kiln, followed by Volanol 220-056 (400.4 g, 0.20 mol, Volanol 220-028 (400.6 g, 0. 10 mol) and 0.304 g of urethane catalyst (K-Kat® 348, bismuth carboxylate from King Industries) were added to the reaction system. The reaction was maintained for an additional 2-3 hours. Collected for analysis by FTIR and NMR, it was confirmed that all hydroxyl groups had reacted before proceeding to the next step. PEGMA (161.9 g, 0.45 mol) was added to the reaction system for 60 minutes. Add slowly. The reaction was maintained at 50 ° C. overnight, then 0.4 g of BHT was added to the system prior to removal. Sampling for FTIR and NMR was performed. Resin was placed at 45 ° C. All trapped air bubbles were expelled. With an MA content of 0.42 mmol / g, the result was a viscosity of 24 Pa · s at 25 ° C.

Reference examples 16-39
Further PEGMA-modified polyether-urethane dimethacrylate macromonomers were prepared in the same manner as described in Reference Example 15.

The compositions and properties of the macromonomers of Reference Examples 15-39 are as shown in Tables 3 and 4 below.

Examples 40-50
The effect of the molecular weight of carbinol on the appearance of the siloxane-modified macromonomer was investigated. The results are summarized in Table 5.

Examples 51 to 53 (reference)
Additional polymerizable macromonomers in the form of trimethacrylylated polyethers derived from Carpol triol were prepared as high molecular weight crosslinkers according to the scheme shown in FIG. The composition and properties of the additional polymerizable macromonomers are summarized in Table 6.

Reference Examples 54 to 85 (Figs. 2 and 4)
Standard origin resin with T-9 via the process of adding TMDI to Voranol (T2V):
Dry air was purged through a 1000 mL resin reaction kiln and the jacket temperature was set to 50 ° C. Voranol-220-056 (545.01 g, 0.2726 mol) and urethane catalyst (T-9) (0.12 g) were added to the reaction kiln. Then, trimethylhexamethylene diisocyanate (TMDI) (114.22 g, 0.5431 mol) was placed in an additional funnel and slowly started to be added to the reaction system over 2 hours. Samples were then taken for analysis by FTIR and NMR. HEMA (28.6 g) was added to the reaction system in 30 minutes, and then 34.47 g of 1,4-butanediol (BDO) was also added to the system in 30 minutes. The reaction was maintained at 50 ° C. for 1 hour, TIM preblend (ICEM) (65.01 g) was added in 30 minutes, the reaction was further maintained at 50 ° C. overnight, and finally an additional 13.7 g of HEMA was added to the system. added. The reaction was continued to mix overnight at 50 ° C. BHT (0.4 g) was added to the system prior to removal. Samples for FTIR and NMR were taken. The resin was placed at 45 ° C. to expel all trapped air bubbles. A result with a viscosity of 55 Pa · s was obtained at 25 ° C.

Standard origin resin with K-KAT via the process of adding TMDI to Voranol (T2V):
Dry air was purged through a 1000 mL resin reaction kiln and the jacket temperature was set to 50 ° C. Voranol-220-056 (546.27 g, 0.2732 mol) and 0.14 g of urethane catalyst (K-Kat® 348, bismuth carboxylate from King Industries) were added to the reaction kiln. Then, trimethylhexamethylene diisocyanate (TMDI) (114.65 g, 0.5452 mol) was placed in an addition funnel and slowly started to be added to the reaction system over 2 hours. Samples were then taken for analysis by FTIR and NMR. HEMA (26.6 g) was added to the reaction system in 30 minutes, and then 34.47 g of 1,4-butanediol (BDO) was also added to the system in 30 minutes. The reaction was maintained at 50 ° C. for 1 hour. TIM preblend (ICEM) (64.86 g) was added in 30 minutes and the reaction was further maintained at 50 ° C. overnight, and finally an additional 13.06 g of HEMA was added to the system. The reaction was continued to mix overnight at 50 ° C. Prior to removal, 0.4 g of BHT was added to the system. Samples for FTIR and NMR were taken. The resin was placed at 45 ° C. to expel all trapped air bubbles. A result with a viscosity of 120 Pa · s was obtained at 25 ° C.

Denatured origin resin with K-KAT via the process of adding Voranol to TMDI (V2T):
Dry air was purged through a 1000 mL resin reaction kiln and the jacket temperature was set to 50 ° C. Trimethylhexamethylene diisocyanate (TMDI) (154.73 g (0.7358 mol)) and 0.15 g urethane catalyst (K-Kat® 348, bismuth carboxylate from King Industries) were added to the reaction kiln. Then Volanol-220-056 (545.77 g, 0.273 mol) was placed in an addition funnel and slowly started to be added to the reaction system over 2 hours. Then samples were taken for analysis by FTIR and NMR. HEMA (39.04 g, 0.300 mol) was added to the reaction system in 30 minutes, and then 31.5 (0.35 mol) of 1,4-butanediol (BDO) was also added to the system in 30 minutes. The reaction continued to mix overnight at 50 ° C., then 0.4 g of BHT was added to the system prior to removal. Sampling for FTIR and NMR was performed. The resin was placed at 45 ° C. All trapped bubbles were expelled. Results were obtained with a viscosity of 90 Pa · s at 25 ° C.

Denatured origin resin using K-KAT via all-in-one process (all-in-one):
Dry air was purged through a 1000 mL resin reaction kiln and the jacket temperature was set to 50 ° C. Trimethylhexamethylene diisocyanate (TMDI) (154.73 g (0.7358 mol), Voranal-220-056 (545.95 g, 0.273 mol), HEMA (64.71 g, 0.497 mol), 1,4-butane Diol (BDO) (34.77, 0.3858 mol) and 0.27 g of urethane catalyst (K-Kat® 348, bismuth carboxylate from King Industries) were added to the reaction kiln. Continued mixing at 50 ° C. in the evening, then 0.4 g of BHT was added to the system prior to removal. Sampling for FTIR and NMR was performed. All captured air bubbles were placed at 45 ° C. Was expelled. The result was that the viscosity was 15 Pa · s at 25 ° C.

The composition and properties of the addition-polymerizable macromonomer are summarized in Tables 7-10.

Example 86
By adding a certain amount (10-30% wt / wt) of Resin B to Resin A, from such pastes formulated for impression materials for both light and heavy bodies, the mechanical properties (Shore A). It was unexpectedly discovered that (hardness and tear strength) can be effectively improved (see Table 14A). Further increases in the amount of resin B added in the mixture could not present any such performance enhancement.

A 90/10 or 80/20 combo resin of resin A containing a compound of formula (I) having no polysiloxane group and resin B containing a compound of formula (I) according to the present invention is also a hydroxyl-terminated siloxane monomer. It was prepared by mixing all the components of Resin A and Resin B in a feed composition (see Table 11) as part of a composition technique that further reduces the reaction rate involved. In fact, in such direct synthesis of 90/10 or 80/20 compositions of Resin A and Resin B, 5 with 80/20 combo resin (ZZ2-4) compared to 12 ° C. with Resin B alone. A moderate temperature rise of 9 ° C. was found at ° C. and 90/10 combo resin (ZZ1-208).

Further, such a combo resin was blended (see Table 12) to prepare a paste (Table 13), which was evaluated according to the following test method (Table 14B).

Explanation of test method 1. Curing Depth and Shore A Hardness The impression material is extruded into a cylindrical mold with a height of 20 mm and an inner diameter of 12 mm, and is 30 from one side using a blue LED light source with an intensity of 60 ± 5 mW / cm2 and a peak wavelength of 460 ± 10 nm. Allow to cure for seconds. The curing depth is determined by measuring the height of the cured sample after removing the uncured portion. Shore A hardness is measured with a durometer on a cross section of a cured sample having a curing depth of 10 mm.

2. Old method of compression set (recovery) Impression material is extruded into a cylindrical mold with a height of 10 mm and an inner diameter of 8 mm, and from one side using a blue LED light source with an intensity of 1000 ± 100 mW / cm2 and a peak wavelength of 460 ± 10 nm. Allow to cure for 20 seconds. Measure the height of the cured sample at 0'55 "counting from the time the photocuring was completed (recorded as A). At 1'00", 30% (height 7 mm) of the cured sample for 5 seconds. Compress (up to) and then recover under no load. At 3'00, measure the height of the sample again (recorded as B). Recovery is calculated as (1- (AB) / 10) x 100%.

3. 3. New method of compression set (recovery) Impression material is extruded into a cylindrical mold with a height of 20 mm and an inner diameter of 12.5 mm, using a blue LED light source with an intensity of 60 ± 5 mW / cm2 and a peak wavelength of 460 ± 10 nm. Allow to cure for 90 seconds (45 seconds on each side) from both sides. Measure the height of the cured sample at 0'55 "counting from the time the photocuring was completed (recorded as A). At 1'00", 30% (height) of the cured sample within 1 second. Compress (up to 14 mm) and slowly release the deforming force for 5 seconds, after which the cured sample is restored under no load. At 3'00, measure the height of the sample again (recorded as B). Recovery is calculated as (1- (AB) / 20) x 100%.

4. Old method of tear strength Extrude impression material into a dogbone-shaped mold. The material is cured either in a halogen light oven such as Triad 2000 (Dentsply Sirona) for 30 seconds or for 45 seconds using a blue LED light source with an intensity of 60 ± 5 mW / cm2 and a peak wavelength of 460 ± 10 nm. Within 2 hours after completion of curing, the sample is subjected to tensile elongation at a crosshead speed of 100 mm / min. The tear strength is determined as the tensile stress at break of the sample.

5. New method of tear strength Extrude into a die C compliant mold of ATSM D624- "Standard test method of tear strength of conventional vulcanized rubber and thermoplastic elastomer". The material is cured for 45 seconds using a blue LED light source with an intensity of 60 ± 5 mW / cm2 and a peak wavelength of 460 ± 10 nm. Within 2 hours after completion of curing, the sample is subjected to tensile elongation at a crosshead speed of 500 mm / min. The tear strength is determined as the ratio between the force at break and the thickness of the sample at the notch.

注：上の表に列挙されたペーストは、２５．３％ｗｔ／ｗｔのフィラー混合物とともに配合され、試料は、ＬＥＤ硬化パッドで硬化された。引裂強さは、新試験方法を使用することによって試験された（詳細は、試験方法の説明を参照）。

注：上の表に列挙されたペーストは、１５％ｗｔ／ｗｔのフィラー混合物とともに配合され、試料は、TRIADハロゲン光で硬化された。引裂強さは、旧試験方法を使用することによって試験された（詳細は、試験方法の説明を参照）。

The compositions of the corresponding active resins (AL02-170-2) and KR2-11, and the compositions of their blended pastes (AL02-171 and AL02-172, respectively) are shown below. The paste from the 90/10 combo resin (ZZ2-208) was able to exhibit excellent tear strength, but Shore A compared to pastes based on Resin A and Resin B physically blended with the same composition. Hardness decreased (AL02-171 vs. AL02-132 in Table 14B).

Note: The pastes listed in the table above were blended with a 25.3% wt / wt filler mixture and the samples were cured with LED curing pads. Tear strength was tested by using a new test method (see the test method description for details).

Note: The pastes listed in the table above were formulated with a 15% wt / wt filler mixture and the samples were cured with TRIAD halogen light. Tear strength was tested by using the old test method (see the test method description for details).

Example: 87
To a 2000 mL flask equipped with a mechanical stirrer, add 1625 g of hydroxyl-terminated siloxane, Silver OH Di-10 (total acid value 0.297 mgKOH / g), followed by 168 g of active basic alumina oxide (~ 60 mesh). rice field. The contents were mixed at room temperature for 4-8 hours and then precipitated overnight before decanting the supernatant for further vacuum filtration to remove any solid particles. All 1476 g of the clarified solution was recovered (yield 91%). Samples were analyzed for total acid value and total water content analysis. Results were obtained with a total acid value of 0.056 mgKOH / g and a water content of 1006 ppm.

Additional GC / MS was performed on the similarly treated samples, revealing that allyl alcohol could not be detected (see Table 15 for detailed compositions before and after pretreatment).

As shown in Table 15, treatment with only the Molecular / Lot 11804022 or DMS / Lot 3A-2388 / Aging molecular sieves could reduce the total water content, but could not remove those acidic impurities, such It was not possible to achieve good mechanical performance of the composition compounded from the resin obtained from the molecular sieved Simmer monomer. Therefore, removal of acidic impurities is important to ensure proper free radical polymerization to build the crosslinked network. Active basic alumina oxide has been found to be effective in achieving this goal. Other weakly basic solid materials should function similarly in the removal of acidic impurities. As shown in Table 15, this was confirmed using a microporous ion exchange resin (Amberlyst A21) having a weakly basic group. Amberlyst A21 was used to achieve an easy filtration process compared to the use of basic alumina oxide in the Silver treatment.

Although the present disclosure has been described with reference to one or more embodiments, it is possible to make various modifications and replace those elements with equivalents without departing from the scope of the present disclosure. Will be understood by those skilled in the art. Also, many modifications can be made to adapt a particular situation or material to the teachings of the present disclosure without departing from its essential scope. Accordingly, the present disclosure is not limited to the particular embodiments disclosed as the best embodiments intended for carrying out the present disclosure, and the present disclosure includes all embodiments within the scope of the appended claims. Intended to include. Also, all numbers specified in the detailed description shall be construed as if both exact and approximate values were explicitly specified.

Claims (18)

(A) The following formula (I):
E- (L ^1- Z) _n- L ^2- E
(I)
In the formula,
E, which may be the same or different, is independently a group containing a polymerizable carbon-carbon double bond, a group containing a polysiloxane moiety, a C _2-20 alkoxy group, and a C _2-20 thioalkyl group. , And RNH groups (in the formula, R is a C _2-20 alkyl group), representing a monovalent group.
Or L ^1, which have the same or different if more than one L ¹ is present, following formula (II):

Represents the divalent group of
Two or more L ³ may L ³ that have the same or different when present is independently up to four of the formula (III):
-L ^1- E
(III)
Substituents (wherein, L ¹ is and E is as defined above) represents which may be substituted bivalent linker group,
Two or more L ⁴ may L ⁴ that have if the same or different which are present, is independently a substituent (wherein up to four of the formula (III), L ¹ is and E, above Represents a divalent linker group that may be substituted with (as defined)
X ¹ , X ² , Y ¹ , and Y ² may be the same or different, and if more than one X ¹ , X ² , Y ¹ , or Y ² is present, then X ¹ , X ² , Y ¹ , and Y ² may be the same or different, independently of an oxygen atom, a sulfur atom and a group NR'(where R'is a hydrogen atom or a C _1-4 alkyl group. Represents)
m represents an integer of 0 or 1-40,
Z is a group (wherein, L ¹ is and E is as defined above) of the polysiloxane group and the formula (III) further which may be substituted divalent up to four substituents selected from Represents the linker group of
L ² is a single bond or a divalent group of formula (II) (in the formula, L ³ , L ⁴ , X ¹ , X ² , Y ¹ , Y ² , and m are independently defined for ^{L 1).} As you can see)
n represents an integer of 0 or 1-4
However,
-The compound of formula (I) contains at least one monovalent group E having a polymerizable carbon-carbon double bond.
-The compound of formula (I) contains at least one polysiloxane group and contains.
However,
When n is 0, L ² is the divalent group of formula (II).
A polymerizable polysiloxane resin composition containing a compound,
(B) Fine particle filler and
(C) Photocurable dental impression material containing a photoinitiator. Claimed that the monovalent group E contains a (meth) acrylate group so that the total (meth) acrylate content of the polymerizable polysiloxane resin composition is in the range of 0.25 to 0.50 mmol / g. Item 1. The photocurable dental impression material according to Item 1. The photocurable dental impression material according to claim 1 or 2, wherein the polymerizable polysiloxane resin composition has a total siloxane content in the range of 10 to 40% wt / wt. The photocurable dental impression material according to any one of claims 1 to 3, wherein n is 0. L ² represents a divalent group of formula (II), and in the formula,
L ³ is a divalent C _1-12 hydrocarbon group or polysiloxane group.
Two or more L ⁴ may L ⁴ that have if the same or different which are present, is independently a substituent (wherein up to four of the formula (III), L ¹ is and E, above Represents a divalent linker group that may be substituted with (as defined)
X ¹ and X ² are oxygen atoms and
Y ¹ and Y ² are NH groups and are
m is an integer from 1 to 40,
The photocurable dental impression material according to any one of claims 1 to 4. The photocurable dental impression material according to any one of claims 1 to 3, wherein n> 0. L ¹ and L ² independently represent the divalent group of formula (II), and in the formula,
L ³ is a divalent C _1-12 hydrocarbon group or polysiloxane group.
Two or more L ⁴ may L ⁴ that have if the same or different which are present, is independently a substituent (wherein up to four of the formula (III), L ¹ is and E, above Represents a divalent linker group that may be substituted with (as defined)
X ¹ and X ² are oxygen atoms and
Y ¹ and Y ² are NH groups and are
m is an integer from 1 to 40 and
Z is a divalent C _1-12 hydrocarbon group,
The photocurable dental impression material according to any one of claims 1 to 6. E is the following equation (IV):

Represents a monovalent end group, in the formula,
R ¹ represents a hydrogen atom or a C _1-12 alkyl group.
X ³ represents an oxygen atom, a sulfur atom or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ⁵ is a divalent hydrocarbon linker group or a polysiloxane-containing linker group, preferably a C _{2 to 20} alkylene group.
X ⁴ represents an oxygen atom, a sulfur atom or a group NR ³ (in the formula, R ³ is a hydrogen atom or a C _1-12 alkyl group).
a represents an integer of 1 to 20
The photocurable dental impression material according to any one of claims 1 to 7. The photocurable dental impression material according to any one of claims 1 to 8, which contains a polymerizable group selected from a (meth) acryloyl group, a (meth) acrylamide group or an allyl (meth) acrylamide group. E is the following formula (V):

Represents the polysiloxane group of
Or R ⁴ which have the same or different, independently represent a linear, branched or cyclic alkyl group,
L ⁶ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
X ⁵ represents an oxygen atom, a sulfur atom or a group NR ⁵ (in the formula, R ⁵ is a hydrogen atom or a C _1-12 alkyl group).
b is an integer of 0 or 1-1000 and
c is 0 or 1,
The photocurable dental impression material according to any one of claims 1 to 9. L ² , and / or L ³ , and / or L ⁴ independently have the following equation (VIII):

(During the ceremony,
Or R ⁶ which have or different are the same, independently represents a linear, branched or cyclic alkyl group, and linear, branched or cyclic alkoxy group,
L ⁷ and L ⁸ are divalent hydrocarbon linker groups, preferably C _2-20 alkylene groups.
X ⁷ represents an oxygen atom, a sulfur atom, or a group NR ⁷ (in the formula, R ⁷ is a hydrogen atom or a C _1-12 alkyl group).
h is an integer of 0 or 1-1000,
t is 0 or 1)
Polysiloxane group of, or the following formulas (VIIIa), (VIIIb), or (VIIIc)

(During the ceremony,
R ^{1 #} is an alkylene having 1 to 8 carbon atoms.
R ^{2 #} is an alkyl having 1 to 4 carbon atoms.
R ^{4 #} is an alkyl, alkoxy or cycloalkyl group
y ^# is an integer from 5 to 20)
The dental material according to any one of claims 1 to 10, which represents the polysiloxane group of the above. The photocurable dental impression material according to any one of claims 1 to 11, wherein the compound of the formula (I) has a molecular weight of 100 to 10,000 Da. Claim ^1- Z-represents a divalent group of formula (II), which can be obtained by reacting a diisocyanate compound, a diol compound, and a polyol compound having at least three hydroxyl groups. The photocurable dental impression material according to any one of 1 to 12. The photocurable dentistry according to any one of claims 1 to 13, wherein L ² represents a divalent group of the formula (II), which can be obtained by reacting a diisocyanate compound and a diol compound. Impression material for. The polymerizable polysiloxane resin mixture is
(A) The following equation (Xs) of x equal quantity:
HO-L ⁴ (OH) _l
(X)
(During the ceremony,
L ⁴ is a (l + 1) -valent linker group.
l is an integer from 1 to 5)
With one or more di- or polyol compounds of
(B) The following equation (XI) of y equal quantity:
OCN-L ³ NCO
(XI)
(During the ceremony,
L ³ is a divalent linker group)
With one or more compounds of
(C) The following formula (XII) of z equal quantity:

(During the ceremony,
R ¹ represents a hydrogen atom or a C _1-12 alkyl group.
X ³ represents an oxygen atom, a sulfur atom or a group NR ² (in the formula, R ² is a hydrogen atom, a C _1-12 alkyl group, or an allyl group).
L ⁵ is a divalent hydrocarbon linker group, preferably a C _2-20 alkylene group.
X ⁴ represents an oxygen atom, a sulfur atom or a group NR ³ (in the formula, R ³ is a hydrogen atom or a C _1-12 alkyl group).
a represents an integer of 1 to 20)
One or more compounds of
Can be obtained by reacting a mixture containing
0.05 ≤ x / y ≤ 0.66 and

And
x, y, and z are molar equivalents of the components (a), (b), and (c).

However, the average hydroxyl functional value of the component (a):

And
l is as defined in formula (X) and x _l / x is the mole fraction of the compound having a hydroxyl functional value of l + 1.
The photocurable dental impression material according to any one of claims 1 to 14. (I) Containing a polymerizable polysiloxane resin composition comprising a compound of formula (I) in an amount of 2 to 95 weight percent based on the total weight of the photocurable dental impression material.
(Ii) 5 to 50 weight percent based on the total weight of the photocurable dental impression material, and (iii) 0.1 based on the total weight of the photocurable dental impression material. The photocurable dental impression material according to any one of claims 1 to 15, which comprises ~ 5 weight percent of a photoinitiator. The photocurable dental impression material according to any one of the preceding claims, further comprising a compound of formula (I) that does not contain any polysiloxane group. Use of the photocurable dental impression material according to any one of claims 1 to 17 for making a dental impression.

Images