JP2021181554A - Blocked polyisocyanate composition, resin composition, resin film, and laminate - Google Patents

Abstract

To provide a blocked polyisocyanate composition having good storage stability when used as a resin composition and good curability at a low temperature of about 80°C when formed into a resin film.SOLUTION: The blocked polyisocyanate composition contains a blocked polyisocyanate, which is derived from a polyisocyanate and one or more blocking agents. The blocked polyisocyanate composition has a constitutional unit represented by the general formula (I) and a constitutional unit represented by the general formula (II), where the molar ratio of the constitutional unit represented by the general formula (II) to the constitutional unit represented by the general formula (I) is more than 5/95 and less than 95/5.SELECTED DRAWING: None

Description

The present invention relates to a blocked polyisocyanate composition, a resin composition, a resin film and a laminate.

Conventionally, polyurethane resin paints have very excellent wear resistance, chemical resistance and stain resistance. In particular, polyurethane resin paints using polyisocyanates obtained from aliphatic diisocyanates or alicyclic diisocyanates have further excellent weather resistance, and the demand for them tends to increase. However, since polyurethane resin paints are generally two-component, their use is extremely inconvenient. That is, a normal polyurethane resin paint is composed of two components, a polyol and a polyisocyanate, and it is necessary to store the polyol and the polyisocyanate separately and mix them at the time of painting. Further, once both are mixed, the paint gels in a short time and cannot be used. Since the polyurethane resin paint has such a problem, it is extremely difficult to use it for automatic painting in the field of line painting such as automobile painting or weak electric painting. Moreover, since isocyanate easily reacts with water, it cannot be used in water-based paints such as electrodeposition paints. Further, when a paint containing isocyanate is used, it is necessary to sufficiently clean the coating machine and the coating tank at the end of the work, so that the work efficiency is significantly reduced.

In order to improve the above-mentioned problems, it has been conventionally proposed to use a blocked polyisocyanate in which all active isocyanate groups are blocked with a blocking agent. This blocked polyisocyanate does not react with polyols at room temperature. However, by heating, the blocking agent is dissociated, the active isocyanate group is regenerated, and the reaction with the polyol causes a cross-linking reaction, so that the above-mentioned problems can be improved. Therefore, many blocking agents have been studied, and for example, phenol, methyl ethyl ketooxime and the like can be mentioned as typical blocking agents.

However, when a blocked polyisocyanate using these blocking agents is used, a high baking temperature of 140 ° C. or higher is generally required. The need for baking at a high temperature is not only disadvantageous in terms of energy, but also requires heat resistance of the base material, which is a factor that limits its use.

On the other hand, as a low-temperature baking type block polyisocyanate, research is being conducted on block polyisocyanates using active methylene compounds such as acetoacetic ester and malonic acid diesters. For example, Patent Documents 1 and 2 propose block polyisocyanate compositions that cure at 90 ° C.

Japanese Unexamined Patent Publication No. 2002-322238 Japanese Unexamined Patent Publication No. 2006-335954

However, in recent years, from the viewpoint of protecting the global environment and adaptation to plastics having low heat resistance, there is a strong demand for a block polyisocyanate composition that cures at a temperature lower than 90 ° C. Under such circumstances, it has good dispersibility in water-based polyols (water-dispersed polyols) having hydroxyl groups, does not gel or excessively thicken during storage, and has curability at 80 ° C. or lower. Good things are not yet known.

The present invention has been made in view of the above circumstances, and has good storage stability when made into a resin composition and good curability at a low temperature of about 80 ° C. when made into a resin film. The present invention provides a block polyisocyanate composition, and a resin composition and a resin film using the block polyisocyanate composition.

That is, the present invention includes the following aspects.
The blocked polyisocyanate composition according to the first aspect of the present invention is a blocked polyisocyanate composition containing a blocked polyisocyanate derived from a polyisocyanate and one or more blocking agents.
Including the structural unit represented by the following general formula (I) and the structural unit represented by the following general formula (II).
The molar ratio of the structural unit represented by the following general formula (II) to the structural unit represented by the following general formula (I) is more than 5/95 and less than 95/5.

(In the general formula ^(I), are each R ^{11, R 12} and ^{R 13} independently comprise one or more substituents selected from the group consisting of hydroxy and amino groups are also alkyl groups ^{.R 14} , R ¹⁵ and R ¹⁶ are each independently an alkyl group which may contain one or more substituents selected from the group consisting of a hydrogen atom or a hydroxy group and an amino group. The broken line represents a bond.

(In the general formula (II), R ²¹ , R ²² , R ²³ and R ²⁴ each independently contain a hydrogen atom or one or more substituents selected from the group consisting of hydroxy and amino groups. It is a good alkyl group. The broken line represents the bond.)

The blocked polyisocyanate composition according to the first aspect is a polyisocyanate, a malonic acid ester having one or more tertiary alkyl groups, a malonic acid ester having one or more secondary alkyl groups, or one or more kinds. A blocked polyisocyanate composition containing a malonic acid ester having a primary alkyl group and a blocked polyisocyanate derived from the block polyisocyanate.
The structural unit represented by the general formula (I) is a structural unit derived from a malonic acid ester having a tertiary alkyl group, and the structural unit represented by the general formula (II) is the secondary alkyl group. It may be a structural unit derived from a malonic acid ester having a primary alkyl group or a structural unit derived from the malonic acid ester having a primary alkyl group.

The blocked polyisocyanate composition according to the second aspect of the present invention is derived from a polyisocyanate, a malonic acid ester having one or more tertiary alkyl groups, and a malonic acid ester having one or more secondary alkyl groups. A blocked polyisocyanate composition containing a blocked polyisocyanate, wherein the molar ratio of the structural unit derived from the malonate having a secondary alkyl group to the structural unit derived from the malonate having a tertiary alkyl group is 5. It is more than / 95 and less than 95/5.
In the blocked polyisocyanate composition according to the second aspect, the malonic acid ester having a tertiary alkyl group contains di-tert-butyl malonic acid, and the malonic acid ester having the secondary alkyl group is diisopropyl malonic acid. May include.

In the blocked polyisocyanate composition according to the first aspect or the second aspect, the average number of isocyanate functional groups of the polyisocyanate may be 2 or more.
In the blocked polyisocyanate composition according to the first aspect or the second aspect, the polyisocyanate is a polyisocyanate derived from one or more kinds of diisocyanates selected from the group consisting of an aliphatic diisocyanate and an alicyclic diisocyanate. May be good.
The weight average molecular weight Mw of the first aspect or a blocked polyisocyanate composition according to the second aspect may also be 2.0 × 10 ³ or more.
In the blocked polyisocyanate composition according to the first aspect or the second aspect, the blocked polyisocyanate may have an isocyanurate group.

The resin composition according to the third aspect of the present invention includes the block polyisocyanate composition according to the first or second aspect, and the polyvalent hydroxy compound.

The resin film according to the fourth aspect of the present invention is obtained by curing the resin composition according to the third aspect.
A resin film having a thickness of 40 μm obtained by heating the resin composition at 80 ° C. for 30 minutes and curing it was stored at 23 ° C. for 1 week and then immersed in acetone at 23 ° C. for 24 hours to have a gel fraction of 82% by mass. It may be the above.
The König hardness of a resin film having a film thickness of 40 μm obtained by heating the resin composition on glass at 80 ° C. for 30 minutes at 23 ° C. may be 38 times or more.
A resin film having a film thickness of 40 μm, a width of 10 mm and a length of 40 mm, which is obtained by heating the resin composition at 80 ° C. for 30 minutes and curing it, is set so that the distance between chucks is 20 mm, and the speed is 23 ° C. and 20 mm / min. The maximum stress in the tensile test carried out in 1) may be 5 MPa or more.

The laminate according to the fifth aspect of the present invention is a laminate having two or more layers of the resin film according to the fourth aspect having different compositions.
The thickness of each layer of the laminated body is 1 μm or more and 50 μm or less.

According to the block polyisocyanate composition of the above aspect, the block poly has good storage stability when it is made into a resin composition, and has good curability at a low temperature of about 80 ° C. when it is made into a resin film. An isocyanate composition can be provided. The resin composition of the above embodiment has good storage stability. The resin film of the above aspect has good curability at a low temperature of about 80 ° C.

Hereinafter, embodiments for carrying out the present invention (hereinafter referred to as “the present embodiment”) will be described in detail. The present invention is not limited to the following embodiments. The present invention can be appropriately modified and carried out within the scope of the gist thereof.

In addition, in this specification, a "polyol" means a compound having two or more hydroxy groups (-OH).
As used herein, the term "polyisocyanate" means a reaction product in which a plurality of monomer compounds having one or more isocyanate groups (-NCO) are bonded.

As used herein, the term "constituent unit" means a structure derived from a single molecule in the structure constituting the polyisocyanate or the blocked polyisocyanate. For example, a structural unit derived from a malonic acid ester indicates a structure derived from a single molecule of malonic acid ester in a blocked polyisocyanate. The structural unit may be a unit directly formed by a (co) polymerization reaction of a monomer, or a unit in which a part of the unit is converted into another structure by treating the (co) polymer. There may be.

≪Block polyisocyanate composition≫
The polyisocyanate composition of the present embodiment contains a blocked polyisocyanate derived from the polyisocyanate and one or more blocking agents.
The polyisocyanate composition of the present embodiment has a structural unit represented by the following general formula (I) (hereinafter, may be referred to as “constituent unit (I)”) and a constitution represented by the following general formula (II). The molar ratio of the structural unit represented by the following general formula (II) to the structural unit represented by the following general formula (I) including the unit (hereinafter, may be referred to as “constituent unit (II)”). , "Mole ratio of structural unit (II) / (I)" may be abbreviated) is more than 5/95 and less than 95/5.

(In the general formula ^(I), are each R ^{11, R 12} and ^{R 13} independently comprise one or more substituents selected from the group consisting of hydroxy and amino groups are also alkyl groups ^{.R 14} , R ¹⁵ and R ¹⁶ are each independently an alkyl group which may contain one or more substituents selected from the group consisting of a hydrogen atom or a hydroxy group and an amino group. The broken line represents a bond.

(In the general formula (II), R ²¹ , R ²² , R ²³ and R ²⁴ each independently contain a hydrogen atom or one or more substituents selected from the group consisting of hydroxy and amino groups. It is a good alkyl group. The broken line represents the bond.)

In the polyisocyanate composition of the present embodiment, the molar ratio of the structural unit (II) / (I) is more than 5/95 and less than 95/5, preferably 7/93 or more and 93/7 or less, and 10/90 or more and 93. It is more preferably /7 or less, further preferably 20/80 or more and 93/7 or less, particularly preferably 30/70 or more and 93/7 or less, and most preferably 35/65 or more and 93/7 or less. When the molar ratio is at least the above lower limit value, the storage stability of the resin composition can be improved, and when it is at least the above upper limit value, the low temperature curability when the resin film is formed. Can be made good.
The molar ratio is determined, for example, by removing the solvent and other components from the blocked polyisocyanate composition at 50 ° C. or lower by an evaporator, drying under reduced pressure, and then using ¹ H-NMR and ¹³ C-NMR as a constituent unit with respect to the constituent unit (I). By measuring the composition ratio of (II), the molar ratio of the structural unit (II) to the structural unit (I) can be calculated.

The structural unit (I) is derived from a malonic acid ester having a tertiary alkyl group which is a blocking agent, and the structural unit (II) is a malonic acid ester or a primary alkyl group having a secondary alkyl group which is a blocking agent. It is preferably derived from a malonic acid ester having.
That is, the polyisocyanate composition of the present embodiment includes a polyisocyanate, a malonic acid ester having one or more tertiary alkyl groups, and a malonic acid ester having one or more secondary alkyl groups, or one or more 1s. It preferably contains a blocked polyisocyanate derived from a malonic acid ester having a secondary alkyl group. At this time, it is derived from the molar ratio of the structural unit derived from the malonic acid ester having a secondary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group, and the malonic acid ester having a tertiary alkyl group. The molar ratio of the structural unit derived from the malonic acid ester having a primary alkyl group to the structural unit is in the same range as the molar ratio of the above structural units (II) / (I), respectively. When the molar ratio is at least the above lower limit value, the storage stability of the resin composition can be improved, and when it is at least the above upper limit value, the low temperature curability when the resin film is formed. Can be made good.
The molar ratio can be calculated, for example, from the molar amount of the malonic acid ester having a tertiary alkyl group and the malonic acid ester having a secondary alkyl group and the malonic acid ester having a primary alkyl group used as a blocking agent. Alternatively, the molar ratio is, for example, that the blocked polyisocyanate composition has a tertiary alkyl group by ¹ H-NMR and ¹³ C-NMR after the solvent and other components are removed by an evaporator at 50 ° C. or lower and dried under reduced pressure. It has a composition ratio of a structural unit derived from a malonic acid ester having a secondary alkyl group to a structural unit derived from a malonic acid ester, or a primary alkyl group to a structural unit derived from a malonic acid ester having a tertiary alkyl group. By measuring the composition ratio of the structural unit derived from the malonic acid ester, the molar ratio of the structural unit derived from the malonic acid ester having a secondary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group, Alternatively, the molar ratio of the structural unit derived from the malonic acid ester having a primary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group can be calculated.

As a more preferable embodiment, the blocked polyisocyanate composition of the present embodiment is composed of a polyisocyanate, a malonic acid ester having one or more tertiary alkyl groups, and a malonic acid ester having one or more secondary alkyl groups. Contains induced blocked polyisocyanates.

In the blocked polyisocyanate composition of the present embodiment, the molar ratio of the structural unit derived from the malonic acid ester having the secondary alkyl group to the structural unit derived from the malonic acid ester having the tertiary alkyl group (secondary alkyl group). The structural unit derived from the malonic acid ester having a tertiary alkyl group / the structural unit derived from the malonic acid ester having a tertiary alkyl group) is more than 5/95 and less than 95/5, preferably 7/93 or more and 93/7 or less. It is more preferably 10/90 or more and 93/7 or less, further preferably 20/80 or more and 93/7 or less, particularly preferably 30/70 or more and 93/7 or less, and most preferably 35/65 or more and 93/7 or less. When the molar ratio is at least the above lower limit value, the storage stability of the resin composition can be improved, and when it is at least the above upper limit value, the low temperature curability when the resin film is formed. Can be made good.
The molar ratio can be calculated from, for example, the molar amount of the malonic acid ester having a tertiary alkyl group and the malonic acid ester having a secondary alkyl group used as a blocking agent. Alternatively, the molar ratio is, for example, that the blocked polyisocyanate composition has a tertiary alkyl group by ¹ H-NMR and ¹³ C-NMR after the solvent and other components are blown off at 50 ° C. or lower by an evaporator and dried under reduced pressure. By measuring the composition ratio of the structural unit derived from the malonic acid ester having a secondary alkyl group to the structural unit derived from the malonic acid ester, the secondary alkyl to the structural unit derived from the malonic acid ester having a tertiary alkyl group. The molar ratio of structural units derived from the malonic acid ester having a group can be calculated.

Conventionally, it is known that a blocked polyisocyanate blocked with a malonic acid ester having a tertiary alkyl group has excellent curability at a low temperature of about 80 ° C. However, there is a problem that the reactivity of a polyvalent hydroxy compound such as a polyol to be reacted with a hydroxyl group is high, and when it is stored as a resin composition containing a main agent and a curing agent, a remarkable increase in viscosity and gelation are likely to occur. Therefore, there has been no product that has both curability at a low temperature of about 80 ° C. and storage stability when the resin composition is used. There is also a method of improving the storage stability by adding alcohols to the resin composition, but by adding a large amount of alcohols, the compatibility with the polyol solution and the physical properties of the prepared resin film are also improved. It may affect the composition, it is difficult to achieve both low temperature curability and storage stability, and from the viewpoint of design freedom, a composition without alcohol or with a small amount of addition is desired.

On the other hand, in the blocked polyisocyanate composition of the present embodiment, as a blocking agent, a malonic acid ester having a tertiary alkyl group and a malonic acid ester having a secondary alkyl group or a malonic acid ester having a primary alkyl group are used. Used in combination, the molar ratio of the structural unit derived from the malonic acid ester having a secondary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group, or the malonic acid ester having a tertiary alkyl group. When the molar ratio of the structural unit derived from the malonate having a primary alkyl group to the structural unit derived from is within the above range, the above-mentioned problems can be improved, and the blocked polyisocyanate composition and the polyvalent hydroxy It is possible to effectively suppress the increase in viscosity and gelation during storage of the mixed solution with the compound, and to exhibit good storage stability. At the same time, a resin film having excellent curability at a low temperature of about 80 ° C. can be obtained.

Hereinafter, each constituent component contained in the blocked polyisocyanate composition of the present embodiment will be described in detail.

<Block polyisocyanate>
Blocked polyisocyanate is a reaction product of polyisocyanate and a blocking agent. That is, in the blocked polyisocyanate, at least a part of the isocyanate groups in the polyisocyanate are blocked with a blocking agent.

The polyisocyanate composition of the present embodiment has a structural unit (constituent unit (I)) represented by the following general formula (I) and a structural unit (constituent unit (II)) represented by the following general formula (II). include. That is, in the polyisocyanate composition of the present embodiment, the blocked polyisocyanate may contain both the structural unit (I) and the structural unit (II) in the molecule, and the blocked polyisocyanate containing the structural unit (I). And may be a mixture of blocked polyisocyanates containing the structural unit (II).

(In the general formula ^(I), are each R ^{11, R 12} and ^{R 13} independently comprise one or more substituents selected from the group consisting of hydroxy and amino groups are also alkyl groups ^{.R 14} , R ¹⁵ and R ¹⁶ are each independently an alkyl group which may contain one or more substituents selected from the group consisting of a hydrogen atom or a hydroxy group and an amino group. The broken line represents a bond.

(In the general formula (II), R ²¹ , R ²² , R ²³ and R ²⁴ each independently contain a hydrogen atom or one or more substituents selected from the group consisting of hydroxy and amino groups. It is a good alkyl group. The broken line represents the bond.)

[Structural unit (I)]
In the general formula (I), R ¹¹ , R ¹² and R ¹³ are alkyl groups which may independently contain one or more substituents selected from the group consisting of hydroxy groups and amino groups, respectively. R ¹⁴ , R ¹⁵ and R ¹⁶ are each independently an alkyl group which may contain one or more substituents selected from the group consisting of a hydrogen atom or a hydroxy group and an amino group.

The alkyl group in R ¹¹ , R ¹² , R ¹³ , R ¹⁴ , R ¹⁵ and R ¹⁶ preferably has 1 or more and 30 or less carbon atoms, more preferably 1 or more and 8 or less, and 1 or more and 6 carbon atoms. It is more preferably 1 or more, and particularly preferably 4 or less. Specific examples of the alkyl group having no substituent include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, a tert-butyl group, a sec-butyl group, an isobutyl group, and an n-pentyl group. Isopentyl group, neopentyl group, tert-pentyl group, 1-methylbutyl group, n-hexyl group, 2-methylpentyl group, 3-methylpentyl group, 2,2-dimethylbutyl group, 2,3-dimethylbutyl group, n -Heptyl group, 2-methylhexyl group, 3-methylhexyl group, 2,2-dimethylpentyl group, 2,3-dimethylpentyl group, 2,4-dimethylpentyl group, 3,3-dimethylpentyl group, 3- Examples thereof include ethylpentyl group, 2,2,3-trimethylbutyl group, n-octyl group, isooctyl group, 2-ethylhexyl group, nonyl group, decyl group and the like.

When R ¹¹ , R ¹² , R ¹³ , R ¹⁴ , R ¹⁵ and R ¹⁶ are alkyl groups having a substituent, the substituent is a hydroxy group or an amino group.
Examples of the alkyl group containing a hydroxy group as the substituent include a hydroxymethyl group, a hydroxyethyl group, a hydroxypropyl group and the like.
Examples of the alkyl group containing an amino group as the substituent include an aminomethyl group, an aminoethyl group, an aminopropyl group, an aminobutyl group and the like.
Examples of the alkyl group containing a hydroxy group and an amino group as the substituent include a hydroxyaminomethyl group, a hydroxyaminoethyl group, a hydroxyaminopropyl group and the like.

Among them, the ^{alkyl groups in R 11} , R ¹² , R ¹³ , R ¹⁴ , R ¹⁵ and R ¹⁶ have substituents having 1 or more and 4 or less carbon atoms because they are excellent in low-temperature curability when formed into a resin film. A non-alkyl group is preferable, a methyl group, an ethyl group, or a propyl group is more preferable, and a methyl group is further preferable.
When R ¹¹ , R ¹² , R ¹³ , R ¹⁴ , R ¹⁵ and R ¹⁶ are all methyl groups, the structural unit (I) is a structural unit derived from di-tert-butyl malonic acid. Among them, R ¹¹ , R ¹² , R ¹³ , R ¹⁴ , R ¹⁵ and R ¹⁶ are all methyl groups, that is, the structural unit (I) is a structural unit derived from di-tert-butyl malonic acid. Especially preferable.

[Constituent unit (II)]
In the general formula (II), R ²¹ , R ²² , R ²³ and R ²⁴ may each independently contain a hydrogen atom or one or more substituents selected from the group consisting of hydroxy and amino groups. It is an alkyl group.

Examples of the alkyl group that may contain one or more substituents selected from the group consisting of hydroxy and amino groups in R ²¹ , R ²² , R ²³ and R ^{24 include the above-mentioned "R 11} , R ¹² , R ¹³ and R 11". R ^14, those similar to the ^{R 15} and those exemplified in ^{R 16} ".

Among them, R ²¹ , R ²² , R ²³ and R ²⁴ are excellent in storage stability when used as a resin composition, and thus are hydrogen atoms or alkyl groups having no substituents having 1 or more and 4 or less carbon atoms. Is preferable, a hydrogen atom, a methyl group, or an ethyl group is more preferable, and a methyl group or an ethyl group is further preferable because it is excellent in low-temperature curability.
When R ²¹ , R ²² , R ²³ and R ²⁴ are all methyl groups, the structural unit (II) is a structural unit derived from diisopropyl malonate. A configuration in which one of R ²¹ and R ²² is a hydrogen atom and the other is a methyl group, and one of R ²³ and R ²⁴ is a hydrogen atom and the other is a methyl group. The unit (II) is a structural unit derived from diethyl malonate. Among them, ^{it is particularly preferable that R 21} , R ²² , R ²³ and R ²⁴ are all methyl groups, that is, the structural unit (II) is a structural unit derived from diisopropyl malonic acid.

The blocking agent preferably contains a malonic acid ester having a secondary alkyl group or a malonic acid ester having a primary alkyl group, and a malonic acid ester having a tertiary alkyl group, and a malonic acid ester having a secondary alkyl group. And it is more preferable to contain a malonic acid ester having a tertiary alkyl group. The blocked polyisocyanate contained in the blocked polyisocyanate composition of the present embodiment includes a malonic acid ester in which at least a part of the isocyanate groups have a secondary alkyl group or a malon having a primary alkyl group in the molecule of the blocked polyisocyanate. It may be a blocked polyisocyanate blocked with an acid ester and a malonic acid ester having a tertiary alkyl group. Alternatively, a blocked polyisocyanate in which at least a part of the isocyanate groups in the polyisocyanate is blocked with a malonic acid ester having a secondary alkyl group, or at least a part of the isocyanate groups in the polyisocyanate has a primary alkyl group. It may be a mixture of a blocked polyisocyanate blocked with a malonic acid ester and a blocked polyisocyanate blocked with a malonic acid ester in which at least a part of the isocyanate groups in the polyisocyanate have a tertiary alkyl group.

The blocked polyisocyanate can have one or more functional groups selected from the group consisting of an allophanate group, a uretdione group, an iminooxadiazinedione group, an isocyanurate group, a urethane group and a biuret group. Above all, it is preferable to have an isocyanurate group because it has excellent weather resistance.

[Polyisocyanate]
The polyisocyanate used for producing a blocked polyisocyanate is a reaction product obtained by reacting a plurality of monomer compounds having one or more isocyanate groups (-NCO) (hereinafter, may be referred to as "isocyanate monomer"). Is.
The isocyanate monomer preferably has 4 or more and 30 or less carbon atoms. Specific examples of the isocyanate monomer include the following. These isocyanate monomers may be used alone or in combination of two or more.
(1) Aromatic diisocyanates such as diphenylmethane-4,4'-diisocyanate (MDI), 1,5-naphthalenediocyanate, tolylene diisocyanate (TDI), xylylene diisocyanate, and m-tetramethylxylylene diisocyanate (TMXDI).
(2) 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate (hereinafter, may be referred to as "HDI"), 2,2,4-trimethyl-1,6-diisocyanatohexane, 2, Aliphatic diisocyanates such as 4,4-trimethyl-1,6-hexamethylene diisocyanate, 2-methylpentane-1,5-diisocyanate (MPDI), and lysine diisocyanate (hereinafter, may be referred to as "LDI").
(3) Fats such as isophorone diisocyanate (hereinafter sometimes referred to as "IPDI"), 1,3-bis (diisocyanatemethyl) cyclohexane, 4,4'-dicyclohexylmethane diisocyanate, diisocyanate norbornane, di (isocyanatemethyl) norbornane, etc. Cyclic diisocyanate.
(4) 4-Isocyanate Methyl-1,8-octamethylene diisocyanate (hereinafter, may be referred to as "NTI"), 1,3,6-hexamethylene triisocyanate (hereinafter, may be referred to as "HTI"). , Bis (2-isocyanatoethyl) 2-isocyanatoglutarate (hereinafter, may be referred to as "GTI"), lysine triisocyanate (hereinafter, may be referred to as "LTI") and the like.

Among them, since the weather resistance is excellent, the isocyanate monomer is preferably one or more kinds of diisocyanates selected from the group consisting of aliphatic diisocyanates and alicyclic diisocyanates. Further, the isocyanate monomer is more preferably HDI or IPDI because of its easy industrial availability. Further, the isocyanate monomer is more preferably HDI from the viewpoint of reducing the viscosity of the blocked polyisocyanate component.

Further, as the isocyanate monomer used for producing the polyisocyanate, either an aliphatic diisocyanate or an alicyclic diisocyanate may be used alone, or a combination thereof may be used, but the aliphatic diisocyanate and the alicyclic diisocyanate may be used. It is preferable to use a combination of group diisocyanates, and it is particularly preferable to use HDI and IPDI. By using the aliphatic diisocyanate and the alicyclic diisocyanate, the toughness and hardness of the coating film can be further improved.

In polyisocyanate, from the viewpoint of improving the hardness and strength of the coating film, the mass ratio of the structural unit derived from the aliphatic diisocyanate to the structural unit derived from the alicyclic diisocyanate (constituent unit derived from the aliphatic diisocyanate / alicyclic diisocyanate). The derived structural unit) is preferably 50/50 or more and 95/5 or less, more preferably 55/45 or more and 93/7 or less, further preferably 60/40 or more and 91/9 or less, and 65/35 or more and 90/10 or less. Is even more preferable.
When the mass ratio of the constituent unit derived from the aliphatic diisocyanate to the constituent unit derived from the alicyclic diisocyanate is at least the above lower limit value, it is more effective to suppress the decrease in the flexibility of the coating film. can do. On the other hand, when it is not more than the above upper limit value, the hardness of the coating film can be further improved.
The mass ratio of the structural unit derived from the aliphatic diisocyanate to the structural unit derived from the alicyclic diisocyanate can be calculated by using, for example, the following method. First, the mass of unreacted aliphatic diisocyanate and the unreacted alicyclic diisocyanate are obtained from the mass of unreacted diisocyanate after the reaction and the concentration of aliphatic diisocyanate and the concentration of alicyclic diisocyanate in the unreacted diisocyanate obtained by gas chromatograph measurement. Calculate the mass of. Then, after subtracting the mass of the unreacted aliphatic diisocyanate and the mass of the unreacted aliphatic diisocyanate calculated above from the mass of the charged aliphatic diisocyanate and the mass of the alicyclic diisocyanate, the obtained difference is the fat, respectively. The mass of the constituent unit derived from the group diisocyanate and the mass of the constituent unit derived from the alicyclic diisocyanate. Then, by dividing the mass of the constituent unit derived from the aliphatic diisocyanate by the mass of the constituent unit derived from the alicyclic diisocyanate, the mass of the constituent unit derived from the aliphatic diisocyanate with respect to the constituent unit derived from the alicyclic diisocyanate. The ratio is obtained.

(Polyol)
The polyisocyanate is preferably derived from the above-mentioned diisocyanate monomer and a polyol having an average number of hydroxyl group functional groups of 3.0 or more and 8.0 or less. Thereby, the average number of isocyanate groups of the obtained polyisocyanate can be further increased. In the polyisocyanate, a urethane group is formed by the reaction between the hydroxyl group of the polyol B and the isocyanate group of the diisocyanate monomer.

The average number of hydroxyl group functional groups of the polyol is preferably 3.0 or more and 8.0 or less, more preferably 3 or more and 6 or less, further preferably 3 or more and 5 or less, and particularly preferably 3 or 4. The average number of hydroxyl group functional groups of the polyol referred to here is the number of hydroxyl groups existing in one molecule of the polyol.

The number average molecular weight of the polyol is preferably 100 or more and 1000 or less, preferably 100 or more and 900 or less, more preferably 100 or more and 600 or less, more preferably 100 or more and 570 or less, and 100 or more, from the viewpoint of improving the hardness and strength of the coating film. 500 or less is further preferable, 100 or more and 400 or less is further preferable, 100 or more and 350 or less is particularly preferable, and 100 or more and 250 or less is most preferable.
When the number average molecular weight of the polyol is within the above range, the blocked polyisocyanate composition is excellent in low temperature curability when formed into a coating film, and is particularly excellent in hardness and strength. The number average molecular weight Mn of the polyol is, for example, a polystyrene-based number average molecular weight measured by GPC.

Examples of such polyols include trimethylolpropane, glycerol, polycaprolactone polyols derived from trihydric or higher polyhydric alcohols and ε-caprolactone.
Commercially available products of polycaprolactone polyol include, for example, Daicel's "Plaxel 303" (number average molecular weight 300), "Plaxel 305" (number average molecular weight 550), "Plaxel 308" (number average molecular weight 850), and "Plaxel 309". "(Number average molecular weight 900) and the like.

(Manufacturing method of polyisocyanate)
The method for producing polyisocyanate will be described in detail below.
The polyisocyanate is, for example, an allophanate-forming reaction forming an allophanate group, a uretdione-forming reaction forming a uretdione group, an iminooxadiazidinedione-forming reaction forming an iminooxadiazinedione group, and an isocyanurate-forming reaction forming an isocyanurate group. The reaction, the urethanization reaction forming a urethane group, and the biuretization reaction forming a biuret group can be produced at once in the presence of an excess of isocyanate monomer, and the unreacted isocyanate monomer is removed after the reaction is completed. be able to. That is, the polyisocyanate obtained by the above reaction is a group in which a plurality of the above-mentioned isocyanate monomers are bonded and is composed of an allophanate group, a uretdione group, an iminooxadiazinedione group, an isocyanurate group, a urethane group and a biuret group. It is a reactant having one or more kinds selected from the above.
Further, the above reactions may be carried out separately, and the obtained polyisocyanates may be mixed at a specific ratio.
From the viewpoint of simplicity of production, it is preferable to carry out the above reaction at once to obtain a polyisocyanate, and from the viewpoint of freely adjusting the molar ratio of each functional group, it is preferable to separately produce and then mix.

(1) Method for Producing Alofanate Group-Containing Polyisocyanate An allophanate group-containing polyisocyanate can be obtained by adding an alcohol to an isocyanate monomer and using an allophanate-forming reaction catalyst.
The alcohol used to form the allophanate group is preferably an alcohol formed only of carbon, hydrogen and oxygen.
Specific examples of the alcohol include, but are not limited to, monoalcohol, dialcohol and the like. These alcohols may be used alone or in combination of two or more.
Examples of the monoalcohol include methanol, ethanol, propanol, butanol, pentanol, hexanol, heptanol, octanol, nonanol and the like.
Examples of the dialcohol include ethylene glycol, 1,3-butanediol, neopentyl glycol, 2-ethylhexanediol and the like.
Among them, as the alcohol, monoalcohol is preferable, and monoalcohol having a molecular weight of 200 or less is more preferable.

Examples of the allophanate formation reaction catalyst include, but are not limited to, alkyl carboxylates such as tin, lead, zinc, bismuth, zirconium, and zirconyl.
Examples of the alkyl carboxylate (organic tin compound) of tin include tin 2-ethylhexanoate, dibutyltin dilaurate and the like.
Examples of the lead alkylcarboxylic acid salt (organolead compound) include lead 2-ethylhexanoate.
Examples of the alkylcarboxylic acid salt (organozinc compound) of zinc include zinc 2-ethylhexanoate and the like.
Examples of the alkylcarboxylic acid salt of bismuth include bismuth 2-ethylhexanoate.
Examples of the alkylcarboxylate of zirconium include zirconium 2-ethylhexanoate.
Examples of the alkylcarboxylate of zirconyl include zirconyl 2-ethylhexanoate. These catalysts may be used alone or in combination of two or more.
Further, the isocyanurate-forming reaction catalyst described later can also be an allophanate-forming reaction catalyst. When an allophanate reaction is carried out using an isocyanurate-forming reaction catalyst described later, an isocyanurate group-containing polyisocyanate (hereinafter, may be referred to as "isocyanurate-type polyisocyanate") is naturally produced.
Above all, it is economically preferable to carry out the allophanate formation reaction and the isocyanurate formation reaction using an isocyanurate formation reaction catalyst described later as the allophanate formation reaction catalyst.

The lower limit of the amount of the allophanation reaction catalyst used is preferably 10 mass ppm, more preferably 20 mass ppm, and 40 mass ppm with respect to the mass of the charged isocyanate monomer. It is more preferably 80 mass ppm, and particularly preferably 80 mass ppm.
The upper limit of the amount of the allophanation reaction catalyst used is preferably 1000 mass ppm, more preferably 800 mass ppm, and 600 mass ppm with respect to the mass of the charged isocyanate monomer. It is more preferably 500 mass ppm, and particularly preferably 500 mass ppm.
That is, the amount of the above-mentioned allophanate reaction catalyst used is preferably 10% by mass or more and 1000% by mass or less, and more preferably 20% by mass or more and 800% by mass or less with respect to the mass of the charged isocyanate monomer. It is more preferably 40% by mass or more and 600% by mass or less, and particularly preferably 80% by mass or more and 500% by mass or less.

The lower limit of the allophanate reaction temperature is preferably 40 ° C, more preferably 60 ° C, further preferably 80 ° C, and particularly preferably 100 ° C.
The upper limit of the allophanate reaction temperature is preferably 180 ° C, more preferably 160 ° C, and even more preferably 140 ° C.
That is, the allophanate reaction temperature is preferably 40 ° C. or higher and 180 ° C. or lower, more preferably 60 ° C. or higher and 160 ° C. or lower, further preferably 80 ° C. or higher and 140 ° C. or lower, and 100 ° C. or higher. It is particularly preferable that the temperature is 140 ° C. or lower.
When the allophanate reaction temperature is equal to or higher than the above lower limit, the reaction rate can be further improved. When the allophanate reaction temperature is not more than the above upper limit, coloring of polyisocyanate and the like can be more effectively suppressed.

(2) Method for producing uretdione group-containing polyisocyanate When deriving a polyisocyanate having a uretdione group from an isocyanate monomer, for example, by increasing the amount of the isocyanate monomer using a uretdione reaction catalyst or by heat. Can be manufactured.
The uretdione reaction catalyst is not particularly limited, and examples thereof include trialkylphosphine, tris (dialkylamino) phosphine, third phosphine such as cycloalkylphosphine, and Lewis acid.
Examples of the trialkylphosphine include tri-n-butylphosphine and tri-n-octylphosphine.
Examples of the tris (dialkylamino) phosphine include tris- (dimethylamino) phosphine.
Examples of the cycloalkylphosphine include cyclohexyl-di-n-hexylphosphine.
Examples of Lewis acid include boron trifluoride and zinc hydrochloride.

Many uretdioneization reaction catalysts can also promote isocyanurate-forming reactions at the same time.
When a uretdioneization reaction catalyst is used, a deactivating agent for the uretdioneization reaction catalyst such as phosphoric acid and methyl paratoluenesulfonate may be added to stop the uretdioneization reaction when the desired yield is obtained. preferable.
Further, when one or more diisocyanates selected from the group consisting of the aliphatic diisocyanate and the alicyclic diisocyanate are heated without using a uretdione reaction catalyst to obtain a polyisocyanate having a uretdione group, the heating temperature thereof is set. , 120 ° C. or higher is preferable, and 150 ° C. or higher and 170 ° C. or lower is more preferable. The heating time is preferably 1 hour or more and 4 hours or less.

(3) Method for Producing Iminooxadiazinedione Group-Containing Polyisocyanate When deriving an iminooxadiazinedione group-containing polyisocyanate from an isocyanate monomer, an iminooxadiazinedione formation reaction catalyst is usually used.
Examples of the iminooxadiazine diionization catalyst include those shown in 1) or 2) below.
1) (Poly) hydrogen fluoride represented by the general formula M [F _n ] or the general formula M [F _n (HF) _m ] (in the formula, m and n have a relationship of m / n> 0. It is an integer to be satisfied. M is an n-charged cation (mixture) or one or more radicals having a total n-valence.)
2) the formula _{^{R 1 -CR '2 -C (O}} ) O-, or the general formula ^{R 2 = CR'-C (O} ) with a compound represented by O-, quaternary ammonium cation, or, the A compound consisting of a quaternary phosphonium cation.
(In the formula, R ¹ and R ² are independently linear, branched or cyclic, saturated or unsaturated perfluoroalkyl groups having 1 or more and 30 or less carbon atoms. A plurality of R'are each. It is an alkyl group or an aryl group having 1 to 20 carbon atoms which may independently contain a hydrogen atom or a hetero atom.)

Specific examples of the compound ((poly) hydrogen fluoride) of 1) include tetramethylammonium fluoride hydrate and tetraethylammonium fluoride.
Specifically, as the compound of 2), for example, 3,3,3-trifluorocarboxylic acid, 4,4,4,3,3-pentafluorobutanoic acid, 5,5,5,4,4,3 Examples thereof include 3-heptafluoropentanoic acid and 3,3-difluoropropa-2-enoic acid.
Among them, as the iminooxadiazine diionization reaction catalyst, 1) is preferable from the viewpoint of availability, and 2) is preferable from the viewpoint of safety.

The lower limit of the amount of the iminooxadiazine diionization catalyst used is not particularly limited, but from the viewpoint of reactivity, the mass ratio is preferably 5 ppm and more preferably 10 ppm with respect to the isocyanate monomer such as HDI which is the raw material. , 20 ppm is more preferable.
The upper limit of the amount of the iminooxadiazine diionization catalyst used is preferably 5000 ppm by mass ratio with respect to the isocyanate monomer such as HDI, which is a raw material, from the viewpoint of suppressing coloration and discoloration of the product and controlling the reaction. 2000 ppm is more preferable, and 500 ppm is even more preferable.
That is, the amount of the iminooxadiazine diionization catalyst used is preferably 5 ppm or more and 5000 ppm or less, more preferably 10 ppm or more and 2000 ppm or less, and 20 ppm or more in terms of mass ratio with respect to the isocyanate monomer such as HDI as a raw material. More preferably, it is 500 ppm or less.

The lower limit of the reaction temperature for iminooxadiazinedione formation is not particularly limited, but is preferably 40 ° C, more preferably 50 ° C, and even more preferably 60 ° C from the viewpoint of reaction rate.
The upper limit of the reaction temperature for iminooxadiazine dioneization is preferably 150 ° C., more preferably 120 ° C., and even more preferably 110 ° C. from the viewpoint of suppressing coloration and discoloration of the product.
That is, the reaction temperature for iminooxadiazine dioneization is preferably 40 ° C. or higher and 150 ° C. or lower, more preferably 50 ° C. or higher and 120 ° C. or lower, and even more preferably 60 ° C. or higher and 110 ° C. or lower.

When the iminooxadiazinedioneization reaction reaches the desired iminooxadiazinedione group content, the iminooxadiazinedioneization reaction can be stopped. The iminooxadiazine diionization reaction can be stopped, for example, by adding an acidic compound to the reaction solution. Examples of the acidic compound include phosphoric acid, acidic phosphoric acid ester, sulfuric acid, hydrochloric acid, sulfonic acid compound and the like. This neutralizes the iminooxadiazine diionization reaction catalyst, or inactivates it by thermal decomposition, chemical decomposition, or the like. After stopping the reaction, if necessary, perform filtration.

(4) Method for Producing Isocyanurate Group-Containing Polyisocyanate Examples of the catalyst for deriving the isocyanurate group-containing polyisocyanate from the isocyanate monomer include a commonly used isocyanurate-forming reaction catalyst.

The isocyanurate-forming reaction catalyst is not particularly limited, but is generally preferably one having basicity. Specific examples of the isocyanurate-forming reaction catalyst include those shown below.
1) Hydroxide of tetraalkylammonium such as tetramethylammonium, tetraethylammonium, tetrabutylammonium, and acetate, propionate, octylate, capricate, myristate, and benzoate of the tetraalkylammonium. Organic weak salts such as.
2) Hydroxide of aryltrialkylammonium such as benzyltrimethylammonium and trimethylphenylammonium, acetate of the aryltrialkylammonate, propionate, octylate, capricate, myristate, benzoate and the like. Organic weak acid salt.
3) Hydroxide of hydroxyalkylammonium such as trimethylhydroxyethylammonium, trimethylhydroxypropylammonium, triethylhydroxyethylammonium, triethylhydroxypropylammonium, and acetate, propionate, octylate, capric acid of the hydroxyalkylammonate. Organic weak salts such as salts, myristates and benzoates.
4) Metal salts of alkylcarboxylic acids such as acetic acid, propionic acid, caproic acid, octyl acid, caproic acid and myristic acid such as tin, zinc and lead.
5) Metallic alcoholates such as sodium and potassium.
6) Aminosilyl group-containing compound such as hexamethylene disilazane.
7) Mannich bases.
8) A mixture of tertiary amines and an epoxy compound.
9) Phosphorus compounds such as tributylphosphine.

Above all, from the viewpoint of less likely to generate unnecessary by-products, the quaternary ammonium hydrooxide or the quaternary ammonium organic weak acid salt is preferable as the isocyanurate-forming reaction catalyst, and the tetraalkylammonium hydroxide. More preferably, it is an organic weakened salt of tetraalkylammonium, a hydroxide of aryltrialkylammonium, or an organic weakened salt of aryltrialkylammonium.

The upper limit of the amount of the isocyanurate-forming reaction catalyst used is preferably 1000 mass ppm, more preferably 500 mass ppm, and 100 mass ppm with respect to the mass of the charged isocyanate monomer. Is more preferable.
On the other hand, the lower limit of the amount of the above-mentioned isocyanurate-forming reaction catalyst used is not particularly limited, but may be, for example, 10 mass ppm.

The isocyanurate-forming reaction temperature is preferably 50 ° C. or higher and 120 ° C. or lower, and more preferably 60 ° C. or higher and 90 ° C. or lower. When the isocyanurate-forming reaction temperature is not more than the above upper limit value, coloring of polyisocyanate and the like tend to be more effectively suppressed.

When the desired conversion rate (the ratio of the mass of the polyisocyanate produced in the isocyanurate-forming reaction to the mass of the charged isocyanate monomer) is reached, the isocyanurate-forming reaction is carried out with an acidic compound (for example, phosphoric acid, acidic phosphoric acid). It is stopped by the addition of (ester, etc.).
In order to obtain polyisocyanate, it is necessary to stop the progress of the reaction at an early stage. However, since the initial reaction rate of the isocyanurate-forming reaction is very fast, it is difficult to stop the progress of the reaction at the initial stage, and it is necessary to carefully select the reaction conditions, especially the addition amount and method of the catalyst. be. For example, a method of dividing and adding the catalyst at regular time intervals is recommended as a suitable method.
Therefore, the conversion rate of the isocyanurate-forming reaction for obtaining a polyisocyanate is preferably 10% or more and 60% or less, more preferably 15% or more and 55% or less, and 20% or more and 50% or less. Is even more preferred.
When the conversion rate of the isocyanurate-forming reaction is not more than the above upper limit value, the blocked polyisocyanate component can have a lower viscosity. Further, when the conversion rate of the isocyanurate-forming reaction is at least the above lower limit value, the reaction stop operation can be performed more easily.

Further, when inducing a polyisocyanate containing an isocyanurate group, an alcohol having a valence of 1 or more and a valence of 6 or less can be used in addition to the isocyanate monomer.
Examples of alcohols having a valence of 1 or more and 6 or less that can be used include non-polymerizable alcohols and polymerizable alcohols. The term "non-polymerizable alcohol" as used herein means an alcohol having no polymerizable group. On the other hand, the "polymerizable alcohol" means an alcohol obtained by polymerizing a monomer having a polymerizable group and a hydroxyl group.
Examples of the non-polymerizable alcohol include polyhydric alcohols such as monoalcohols, diols, triols and tetraols.
Examples of monoalcohols include methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, sec-butanol, n-pentanol, n-hexanol, n-octanol, n-nonanol and 2-ethylbutanol. , 2,2-Dimethylhexanol, 2-ethylhexanol, cyclohexanol, methylcyclohexanol, ethylcyclohexanol and the like.
Examples of diols include ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, and 1, 3-butanediol, 1,4-butanediol, 2,3-butanediol, 2-methyl-1,2-propanediol, 1,5-pentanediol, 2-methyl-2,3-butanediol, 1, 6-Hexanediol, 1,2-hexanediol, 2,5-hexanediol, 2-methyl-2,4-pentanediol, 2,3-dimethyl-2,3-butanediol, 2-ethyl-hexanediol, 1,2-octanediol, 1,2-decanediol, 2,2,4-trimethylpentanediol, 2-butyl-2-ethyl-1,3-propanediol, 2,2-diethyl-1,3-propane Examples include diol.
Examples of triols include glycerin, trimethylolpropane and the like.
Examples of tetraols include pentaerythritol and the like.

The polymerizable alcohol is not particularly limited, and examples thereof include polyester polyols, polyether polyols, acrylic polyols, and polyolefin polyols.

The polyester polyols are not particularly limited, and examples thereof include products obtained by a condensation reaction between a dibasic acid alone or a mixture and a polyhydric alcohol alone or a mixture.
The dibasic acid is not particularly limited, but is at least one selected from the group consisting of carboxylic acids such as succinic acid, adipic acid, sebacic acid, dimer acid, maleic anhydride, phthalic acid anhydride, isophthalic acid, and terephthalic acid. Species dibasic acid can be mentioned.
The polyhydric alcohol is not particularly limited, and examples thereof include at least one polyhydric alcohol selected from the group consisting of ethylene glycol, propylene glycol, diethylene glycol, neopentyl glycol, trimethylolpropane, and glycerin.
Examples of polyester polyols include polycaprolactones obtained by ring-opening polymerization of ε-caprolactone using the above polyhydric alcohol.

The polyether polyols are not particularly limited, but for example, an alkali metal hydroxide or a strongly basic catalyst is used to add an alkylene oxide alone or a mixture to a polyhydric alcohol alone or a mixture. Examples thereof include polyether polyols obtained by reacting a polyamine compound with an alkylene oxide, and so-called polymer polyols obtained by polymerizing acrylamide or the like using the above-mentioned polyethers as a medium.
Examples of the alkali metal include lithium, sodium, potassium and the like.
Examples of the strongly basic catalyst include alcoholates, alkylamines and the like.
Examples of the polyhydric alcohol include those similar to those exemplified in the above polyester polyols.
Examples of the alkylene oxide include ethylene oxide, propylene oxide, butylene oxide, cyclohexene oxide, styrene oxide and the like.
Examples of the polyamine compound include ethylenediamines.

The acrylic polyols are not particularly limited, but for example, an ethylenically unsaturated bond-containing monomer having a hydroxyl group alone or a mixture thereof and another ethylenically unsaturated bond-containing monomer copolymerizable therewith are used alone. Alternatively, a copolymer of a mixture may be used.
The ethylenically unsaturated bond-containing monomer having a hydroxyl group is not particularly limited, and for example, hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxybutyl acrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, hydroxy methacrylate. Examples include butyl.
The other ethylenically unsaturated bond-containing monomer copolymerizable with the ethylenically unsaturated bond-containing monomer having a hydroxyl group is not particularly limited, and is, for example, an acrylic acid ester, a methacrylic acid ester, or an unsaturated carboxylic acid. , Unsaturated amides, vinyl monomers, vinyl monomers having a hydrolyzable silyl group.
Examples of the acrylic acid ester include methyl acrylate, ethyl acrylate, propyl acrylate, isopropyl acrylate, -n-butyl acrylate, isobutyl acrylate, -n-hexyl acrylate, cyclohexyl acrylate, and -2 acrylate. -Ethylhexyl, lauryl acrylate, benzyl acrylate, phenyl acrylate and the like can be mentioned.
Examples of the methacrylic acid ester include methyl methacrylate, ethyl methacrylate, propyl methacrylate, isopropyl methacrylate, -n-butyl methacrylate, isobutyl methacrylate, -n-hexyl methacrylate, cyclohexyl methacrylate, and -2 methacrylic acid. -Ethylhexyl, lauryl methacrylate, benzyl methacrylate, phenyl methacrylate and the like can be mentioned.
Examples of unsaturated carboxylic acids include acrylic acid, methacrylic acid, maleic acid, itaconic acid and the like.
Examples of unsaturated amides include acrylamide, methacrylamide, N, N-methylenebisacrylamide, diacetoneacrylamide, diacetonemethacrylamide, maleic acid amide, maleimide and the like.
Examples of the vinyl-based monomer include glycidyl methacrylate, styrene, vinyltoluene, vinyl acetate, acrylonitrile, dibutyl fumarate and the like.
Examples of the vinyl-based monomer having a hydrolyzable silyl group include vinyltrimethoxysilane, vinylmethyldimethoxysilane, γ- (meth) acryloxypropyltrimethoxysilane, and the like.

Examples of the polyolefin polyols include hydroxyl-terminated polybutadiene and hydrogenated products thereof.

(5) Method for Producing Urethane Group-Containing Polyisocyanate When deriving a urethane group-containing polyisocyanate from an isocyanate monomer, for example, an excess isocyanate monomer, the above-mentioned polyol, and, if necessary, an alcohol other than the above-mentioned polyol may be used. Can be produced by mixing and adding a urethanization reaction catalyst as needed.
Examples of the polyol include the same as those exemplified in the above-mentioned "polypoly".
Examples of the alcohol other than the polyol include those exemplified in the above-mentioned "Method for producing an isocyanurate group-containing polyisocyanate", excluding those exemplified in the above-mentioned "polyol".
The urethanization reaction catalyst is not particularly limited, and examples thereof include tin-based compounds, zinc-based compounds, and amine-based compounds.
The urethanization reaction temperature is preferably 50 ° C. or higher and 160 ° C. or lower, and more preferably 60 ° C. or higher and 120 ° C. or lower.
When the urethanization reaction temperature is not more than the above upper limit value, coloring of polyisocyanate and the like can be more effectively suppressed.
The urethanization reaction time is preferably 30 minutes or more and 4 hours or less, more preferably 1 hour or more and 3 hours or less, and further preferably 1 hour or more and 2 hours or less.
The ratio of the molar amount of the isocyanate group of the isocyanate monomer to the molar amount of the hydroxyl group of the polyol (and, if necessary, an alcohol other than the polyol) is preferably 2/1 or more and 50/1 or less. When the molar ratio is at least the above lower limit value, the polyisocyanate can have a lower viscosity. When the molar ratio is not more than the above upper limit, the yield of the urethane group-containing polyisocyanate can be further increased.

(6) Method for Producing Biuret Group-Containing Polyisocyanate The biuret agent for inducing a biuret group-containing polyisocyanate from an isocyanate monomer is not particularly limited, and is, for example, water, a monohydric tertiary alcohol, or an acid acid. , Organic first monoamine, organic first diamine and the like.
The isocyanate group is preferably 6 mol or more, more preferably 10 mol or more, and further preferably 10 mol or more and 80 mol or less with respect to 1 mol of the biuret agent. When the molar amount of the isocyanate group per 1 mol of the biuret agent is at least the above lower limit value, the polyisocyanate has a sufficiently low viscosity, and when it is at least the above upper limit value, the low temperature curability when made into a resin film is further improved. do.

Further, a solvent may be used in the biuret reaction. The solvent may be any one that dissolves an isocyanate monomer and a biuret agent such as water to form a uniform phase under reaction conditions.
Specific examples of the solvent include ethylene glycol-based solvents and phosphoric acid-based solvents.
Examples of the ethylene glycol-based solvent include ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol mono-n-propyl ether acetate, ethylene glycol monoisopropyl ether acetate, ethylene glycol mono-n-butyl ether acetate, and ethylene glycol. Diacetate, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol di-n-propyl ether, ethylene glycol diisopropyl ether, ethylene glycol di-n-butyl ether, ethylene glycol methyl ethyl ether, ethylene glycol methyl isopropyl ether, ethylene glycol methyl- n-butyl ether, ethylene glycol ethyl-n-propyl ether, ethylene glycol ethyl isopropyl ether, ethylene glycol ethyl-n-butyl ether, ethylene glycol-n-propyl-n-butyl ether, ethylene glycol isopropyl-n-butyl ether, diethylene glycol monomethyl ether acetate , Diethylene glycol monoethyl ether acetate, diethylene glycol mono-n-propyl ether acetate, diethylene glycol monoisopropyl ether acetate, diethylene glycol mono-n-butyl ether acetate, diethylene glycol diacetate, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol di-n-propyl ether, diethylene glycol Diisopropyl ether, diethylene glycol di-n-butyl ether, diethylene glycol methyl ethyl ether, diethylene glycol methyl isopropyl ether, diethylene glycol methyl-n-propyl ether, diethylene glycol methyl-n-butyl ether, diethylene glycol ethyl isopropyl ether, diethylene glycol ethyl-n-propyl ether, diethylene glycol ethyl Examples thereof include -n-butyl ether, diethylene glycol-n-propyl-n-butyl ether, diethylene glycol isopropyl-n-butyl ether and the like.
Examples of the phosphoric acid-based solvent include trimethyl phosphate, triethyl phosphate, tripropyl phosphate, tributyl phosphate and the like.
These solvents may be used alone or in combination of two or more.
Among them, as the ethylene glycol solvent, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol diacetate or diethylene glycol dimethyl ether are preferable.
Further, as the phosphoric acid solvent, trimethyl phosphate or triethyl phosphate is preferable.

The biuret reaction temperature is preferably 70 ° C. or higher and 200 ° C. or lower, and more preferably 90 ° C. or higher and 180 ° C. or lower. When it is not more than the above upper limit value, coloring of polyisocyanate or the like tends to be prevented more effectively.

The above-mentioned allophanate-forming reaction, uretdione-forming reaction, iminooxadiazine-izing reaction, isocyanurate-forming reaction, urethanization reaction, and biuret-forming reaction may be carried out sequentially, or some of them may be carried out in parallel. May be good.
The unreacted isocyanate monomer can be removed from the reaction solution after completion of the reaction by thin film distillation, extraction or the like to obtain polyisocyanate.

Further, for the purpose of suppressing coloration during storage, for example, an antioxidant or an ultraviolet absorber may be added to the obtained polyisocyanate.
Examples of the antioxidant include hindered phenols such as 2,6-di-tert-butyl-p-cresol. Examples of the ultraviolet absorber include benzotriazole, benzophenone and the like. These antioxidants and ultraviolet absorbers may be used alone or in combination of two or more. The amount of these additions is preferably 10 mass ppm or more and 500 mass ppm or less with respect to the mass of the polyisocyanate.

(Average number of isocyanate functional groups of polyisocyanate)
The average number of isocyanate functional groups of the polyisocyanate is preferably 2 or more in terms of enhancing the low-temperature curability when the resin film is formed, and both the low-temperature curability when the resin film is used and the compatibility with the polyhydric alcohol compound are compatible. From the viewpoint of the above, 3 or more and 20 or less are more preferable, 3.3 or more and 10 or less are further preferable, 3.8 or more and 9 or less are particularly preferable, and 4.2 or more and 8 or less are most preferable.
The average number of isocyanate functional groups of polyisocyanate can be measured by using the method described in Examples described later.

[Blocking agent]
The blocking agent used for producing the blocked polyisocyanate preferably contains a malonic acid ester having a secondary alkyl group or a malonic acid ester having a primary alkyl group, and a malonic acid ester having a tertiary alkyl group. It is more preferable to contain a malonic acid ester having a tertiary alkyl group and a malonic acid ester having a tertiary alkyl group. The blocking agent may contain one type of malonic acid ester having a secondary alkyl group, a malonic acid ester having a primary alkyl group, and one type of malonic acid ester having a tertiary alkyl group, or may contain two or more types in combination. ..

The malonic acid ester having a primary alkyl group is not particularly limited, and examples thereof include dimethyl malonate, diethyl malonate, dipropyl malonic acid, dibutyl malonate, dicyclohexyl malonic acid, and diphenyl malonic acid. Among them, diethyl malonate is preferable as the malonic acid ester having a primary alkyl group.

The malonic acid ester having a secondary alkyl group is not particularly limited, and examples thereof include di-sec-butyl malonic acid, diisopropyl malonic acid, and isopropylethyl malonic acid. Among them, diisopropyl malonic acid is preferable as the malonic acid ester having a secondary alkyl group.

The malonic acid ester having a tertiary alkyl group is not particularly limited, and examples thereof include di-tert-butyl malonic acid, di-tert-pentyl malonic acid, and tert-butyl ethyl malonic acid. Of these, di-tert-butyl malonic acid is preferred.

Among them, the blocking agent preferably contains diisopropyl malonic acid as a malonic acid ester having a secondary alkyl group and di-tert-butyl malonic acid as a malonic acid ester having a tertiary alkyl group.

(Other blocking agents)
The blocking agent used for the production of the blocked polyisocyanate is not only a malonic acid ester having a secondary alkyl group and a malonic acid ester having a tertiary alkyl group, but also a storage stability when it is made into a resin composition and when it is made into a resin film. Other blocking agents may be further contained as long as the low temperature curability of the ester is not impaired.
The content of the malonic acid ester having a secondary alkyl group and the malonic acid ester having a tertiary alkyl group is 50 mol% or more with respect to the total molar amount of the total blocking agent used for producing the blocked polyisocyanate. It is preferably 70 mol% or more, more preferably 90 mol% or more, particularly preferably 95 mol% or more, and most preferably 100 mol% or more.
When the content of the malonic acid ester having a secondary alkyl group and the malonic acid ester having a tertiary alkyl group is within the above range, the low temperature curability of the resin film can be further improved.

Examples of other blocking agents include 1) alcohol compounds, 2) alkylphenol compounds, 3) phenol compounds, 4) malonic acid esters having a secondary alkyl group, and malonic acid esters having a tertiary alkyl group. Active methylene compounds, 5) mercaptan compounds, 6) acid amide compounds, 7) acidimide compounds, 8) imidazole compounds, 9) urea compounds, 10) oxime compounds, 11) amine compounds, 12 ) Imid-based compounds, 13) heavy sulfites, 14) pyrazole-based compounds, 15) triazole-based compounds and the like. More specific examples of the blocking agent include those shown below.

1) Alcohol-based compounds: Alcohols such as methanol, ethanol, 2-propanol, n-butanol, sec-butanol, 2-ethyl-1-hexanol, 2-methoxyethanol, 2-etokashiethanol, 2-butoxyethanol and the like.
2) Alkylphenol compounds: Monos and dialkylphenols having an alkyl group having 4 or more carbon atoms as a substituent. Specific examples of the alkylphenol compound include n-propylphenol, iso-propylphenol, n-butylphenol, sec-butylphenol, tert-butylphenol, n-hexylphenol, 2-ethylhexylphenol, n-octylphenol, and n-nonylphenol. Monoalkylphenols such as: di-n-propylphenol, diisopropylphenol, isopropylcresol, di-n-butylphenol, di-tert-butylphenol, di-sec-butylphenol, di-n-octylphenol, di-2-ethylhexylphenol, etc. Dialkylphenols such as di-n-nonylphenol.
3) Phenolic compounds: phenol, cresol, ethylphenol, styrenated phenol, hydroxybenzoic acid ester, etc.
4) Active methylene compounds: methyl acetoacetate, ethyl acetoacetate, methyl isobutanoyl acetate, ethyl isobutanoyl acetate, acetylacetone, etc.
5) Mercaptan compounds: Butyl mercaptan, dodecyl mercaptan, etc.
6) Acid amide compounds: acetanilide, acetate amide, ε-caprolactam, δ-valerolactam, γ-butyrolactam and the like.
7) Imide-based compounds: succinimide, maleic acid imide, etc.
8) Imidazole compounds: imidazole, 2-methylimidazole, etc.
9) Urea compounds: urea, thiourea, ethylene urea, etc.
10) Oxime compounds: formaldehyde, acetaldoxime, acetoxime, methylethylketooxime, cyclohexanone oxime and the like.
11) Amine compounds: diphenylamine, aniline, carbazole, din-propylamine, diisopropylamine, isopropylethylamine and the like.
12) Imine-based compounds: ethyleneimine, polyethyleneimine, etc.
13) Sodium bisulfite compound: sodium bisulfite and the like.
14) Pyrazole compounds: pyrazole, 3-methylpyrazole, 3,5-dimethylpyrazole and the like.
15) Triazole compounds: 3,5-dimethyl-1,2,4-triazole and the like.

[Hydrophilic compound]
At least a part of the blocked polyisocyanate may have a structural unit derived from a hydrophilic compound, that is, a hydrophilic group.

The hydrophilic compound is a compound having a hydrophilic group. In addition to the hydrophilic group, the hydrophilic compound preferably has at least one active hydrogen group for reacting with at least one of the isocyanate groups of the polyisocyanate with respect to one molecule of the hydrophilic compound. Specific examples of the active hydrogen group include a hydroxyl group, a mercapto group, a carboxylic acid group, an amino group and a thiol group.

Examples of the hydrophilic compound include a nonionic compound, a cationic compound and an anionic compound. These hydrophilic compounds may be used alone or in combination of two or more. Among them, as the hydrophilic compound, a nonionic compound is preferable from the viewpoint of easy availability and less susceptible to electrical interaction with the compound, from the viewpoint of suppressing a decrease in hardness and strength of the obtained resin film, and from the viewpoint of suppressing a decrease in hardness and strength of the obtained resin film. , Anionic compounds are preferable from the viewpoint of improving emulsifying property.

(Nonionic compound)
Specific examples of the nonionic compound include monoalcohols and compounds in which ethylene oxide is added to the hydroxyl groups of alcohols. Examples of the monoalcohol include methanol, ethanol, butanol and the like. Examples of the compound in which ethylene oxide is added to the hydroxyl group of the alcohol include ethylene glycol, diethylene glycol, polyethylene glycol and the like. These nonionic compounds also have an active hydrogen group that reacts with the isocyanate group.
Among them, as the nonionic compound, polyethylene glycol monoalkyl ether in which ethylene oxide is added to the hydroxyl group of the monoalcohol is preferable because the water dispersibility of the blocked polyisocyanate composition can be improved with a small amount of use.

The number of ethylene oxide additions of the compound to which ethylene oxide is added is preferably 4 or more and 30 or less, and more preferably 4 or more and 25 or less. When the addition number of ethylene oxide is not less than the above lower limit value, the water dispersibility tends to be more effectively imparted to the blocked polyisocyanate composition, and when the addition number of ethylene oxide is not more than the above upper limit value, it tends to be possible to more effectively impart water dispersibility. Precipitates of the blocked polyisocyanate composition tend to be less likely to occur during low temperature storage.

The lower limit of the amount of nonionic hydrophilic groups added to the blocked polyisocyanate (hereinafter, may be referred to as "content of nonionic hydrophilic groups") is from the viewpoint of water dispersion stability of the blocked polyisocyanate composition. Therefore, 0.1% by mass is preferable, 0.15% by mass is more preferable, 0.2% by mass is further preferable, and 0.25% by mass is particularly preferable with respect to the mass of the solid content of the hydrophilic polyisocyanate composition. preferable.
The upper limit of the content of the nonionic hydrophilic group is preferably 55% by mass, preferably 50% by mass, based on the mass of the solid content of the blocked polyisocyanate composition from the viewpoint of the water resistance of the obtained resin film. More preferably, 48% by mass is further preferable, and 44% by mass is particularly preferable.
That is, the content of the nonionic hydrophilic group is preferably 0.1% by mass or more and 55% by mass or less, and 0.15% by mass or more and 50% by mass or less with respect to the mass of the solid content of the blocked polyisocyanate composition. More preferably, it is more preferably 0.20% by mass or more and 48% by mass or less, and particularly preferably 0.25% by mass or more and 44% by mass or less.
When the content of the nonionic hydrophilic group is within the above range, the blocked polyisocyanate composition is more dispersed in water, and a homogeneous film tends to be obtained.

From the viewpoint of suppressing a decrease in the hardness and strength of the obtained resin film, the amount of nonionic hydrophilic groups added to the blocked polyisocyanate is expressed in terms of molar ratio with respect to 100 mol% of isocyanate groups of the raw material polyisocyanate. It is preferably 0.05 mol% or more and 15 mol% or less, more preferably 0.10 mol% or more and 12 mol% or less, further preferably 0.10 mol% or more and 8 mol% or less, and 0.10 mol% or more and 6 mol. % Or less is further preferable, 0.15 mol% or more and 4 mol% or less is further preferable, 0.15 mol% or more and 3 mol% or less is particularly preferable, and 0.15 mol% or more and 2 mol% or less is most preferable.

(Cationic compound)
Specific examples of the cationic compound include compounds having both a cationic hydrophilic group and an active hydrogen group. Further, a compound having an active hydrogen group such as a glycidyl group and a compound having a cationic hydrophilic group such as sulfide and phosphine may be combined to form a hydrophilic compound. In this case, a compound having an isocyanate group and a compound having an active hydrogen group are reacted in advance to add a functional group such as a glycidyl group, and then a compound such as a sulfide or a phosphine is reacted. From the viewpoint of ease of production, a compound having both a cationic hydrophilic group and an active hydrogen group is preferable.

Specific examples of the compound having both a cationic hydrophilic group and an active hydrogen group include dimethylethanolamine, diethylethanolamine, diethanolamine, and methyldiethanolamine. Further, the tertiary amino group added using these compounds can be quaternized with, for example, dimethyl sulfate or diethyl sulfate.

The reaction between the cationic compound and the alicyclic polyisocyanate can be carried out in the presence of a solvent. The solvent in this case preferably does not contain an active hydrogen group, and specific examples thereof include ethyl acetate, propylene glycol monomethyl ether acetate, and dipropylene glycol dimethyl ether.

The cationic hydrophilic group added to the blocked polyisocyanate is preferably neutralized with a compound having an anionic group. Specific examples of the anionic group include a carboxy group, a sulfonic acid group, a phosphoric acid group, a halogen group, a sulfate group and the like.
Specific examples of the compound having a carboxyl group include formic acid, acetic acid, propionic acid, butyric acid, and lactic acid.
Specific examples of the compound having a sulfonic acid group include ethanesulfonic acid and the like.
Specific examples of the compound having a phosphoric acid group include phosphoric acid and acidic phosphoric acid esters.
Specific examples of the compound having a halogen group include hydrochloric acid and the like.
Specific examples of the compound having a sulfuric acid group include sulfuric acid and the like.
Among them, as the compound having an anionic group, a compound having a carboxy group is preferable, and acetic acid, propionic acid or butyric acid is more preferable.

(Anionic compound)
Specific examples of the anionic hydrophilic group include a carboxy group, a sulfonic acid group, a phosphoric acid group, a halogen group and a sulfate group.
Specific examples of the anionic compound include compounds having both an anionic group and an active hydrogen group. More specifically, for example, a carboxy group of a monohydroxycarboxylic acid or a polyhydroxycarboxylic acid is anionic. Examples include compounds having as a group.
Examples of the monohydroxycarboxylic acid include 1-hydroxyacetic acid, 3-hydroxypropanoic acid, 12-hydroxy-9-octadecanoic acid, hydroxypivalic acid (hydroxypivalic acid), lactic acid and the like.
Examples of the compound having a carboxy group of the polyhydroxycarboxylic acid as an anionic group include dimethylol acetic acid, 2,2-dimethylol butyric acid, 2,2-dimethylolpentanoic acid, dihydroxysuccinic acid, dimethylolpropionic acid and the like. ..
Further, a compound having a sulfonic acid group and an active hydrogen group in combination can be mentioned, and more specifically, for example, isethionic acid and the like can be mentioned.
Among them, hydroxypivalic acid or dimethylolpropionic acid is preferable as the compound having both an anionic group and an active hydrogen group.

The anionic hydrophilic group added to the blocked polyisocyanate is preferably neutralized with an amine compound which is a basic substance.
Specific examples of the amine compound include ammonia, a water-soluble amino compound and the like.
Specific examples of the water-soluble amino compound include monoethanolamine, ethylamine, dimethylamine, diethylamine, triethylamine, propylamine, dipropylamine, isopropylamine, diisopropylamine, triethanolamine, butylamine, dibutylamine, 2- Examples thereof include ethylhexylamine, ethylenediamine, propylenediamine, methylethanolamine, dimethylethanolamine, diethylethanolamine, morpholin and the like. Further, tertiary amines such as triethylamine and dimethylethanolamine are also mentioned, and these can also be used. These amine compounds may be used alone or in combination of two or more.

<Other components>
The blocked polyisocyanate composition of the present embodiment may further contain an additive such as a solvent in addition to the above blocked polyisocyanate.

Examples of the solvent include 1-methylpyrrolidone, ethylene glycol monoethyl ether, diethylene glycol monoethyl ether, ethylene glycol monomethyl ether, diethylene glycol monomethyl ether, dipropylene glycol monomethyl ether, propylene glycol monomethyl ether, 3-methoxy-3-methyl-. 1-butanol, ethylene glycol diethyl ether, diethylene glycol diethyl ether, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, dipropylene glycol dimethyl ether (DPDM), propylene glycol dimethyl ether, methyl ethyl ketone, acetone, methyl isobutyl ketone, propylene glycol monomethyl ether acetate, ethanol, methanol, iso-propanol, 1-propanol, iso-butanol, 1-butanol, tert-butanol, 2-ethylhexanol, cyclohexanol, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, 1,4-butanediol , 1,3-Butandiol, ethyl acetate, isopropyl acetate, butyl acetate, toluene, xylene, pentane, iso-pentane, hexane, iso-hexane, cyclohexane, solvent naphtha, mineral spirit and the like. These solvents may be used alone or in combination of two or more. From the viewpoint of dispersibility in water, the solvent preferably has a solubility in water of 5% by mass or more, and specifically, DPDM is preferable.

<Manufacturing method of blocked polyisocyanate composition>
The blocked polyisocyanate composition is not particularly limited, and examples thereof include the following two methods.
1) A method of reacting the polyisocyanate with the malonic acid ester having the tertiary alkyl group and the malonic acid ester having the secondary alkyl group or the malonic acid ester having the primary alkyl group;
2) At least one selected from the group consisting of the polyisocyanate, the malonic acid ester having the tertiary alkyl group, the malonic acid ester having the secondary alkyl group, and the malonic acid ester having the primary alkyl group. An alcohol having a chain alkyl group was added to the obtained reaction product by reacting with a blocking agent, and an alkyl group derived from the alcohol was introduced by ester exchange at the terminal ester moiety of the reaction product. Then, a method of removing the residual alcohol by distillation under reduced pressure or the like.

As the alcohol having a chain alkyl group used in the method 2), a monoalcohol is preferable, and for example, a monoalcohol having a linear alkyl group such as methanol, ethanol, propanol and butanol; isopropanol, isobutanol and tert-. Examples thereof include monoalcohols having a branched chain alkyl group such as butanol. Further, the chain alkyl group contained in the alcohol may have the same chain alkyl group as the blocking agent, or may have a different chain alkyl group. When it has a chain alkyl group different from that of the blocking agent, it is preferable to use a monoalcohol having a chain alkyl group having a different number of alkyl substitutions from the blocking agent. Specifically, for example, when a malonic acid ester having a secondary alkyl group is used alone as a blocking agent, a monoalcohol having a tertiary alkyl group can be used.

Of the above two methods, the method 1) is preferable in consideration of the ease of the process and the ease of controlling the molar ratio of the structural unit (II) / structural unit (I).

The blocking reaction between the polyisocyanate and the blocking agent can be carried out regardless of the presence or absence of a solvent, and a blocked polyisocyanate can be obtained.
As the blocking agent, one type of malonic acid ester having a primary alkyl group, one type of malonic acid ester having a secondary alkyl group, and one type of malonic acid ester having a tertiary alkyl group may be used, respectively, and two or more types may be used in combination. You may.
The amount of the blocking agent added may be usually 80 mol% or more and 200 mol% or less, preferably 90 mol% or more and 150 mol% or less, based on the total molar amount of the isocyanate groups.

Further, in the blocking agent to be added, the molar ratio of the structural unit derived from the malonic acid ester having a secondary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group [(malonic acid having a secondary alkyl). Ester) / (malonic acid ester having a tertiary alkyl)], and the molar ratio of the structural unit derived from the malonic acid ester having a primary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group [ (Malonic acid ester having a primary alkyl group) / (malonic acid ester having a tertiary alkyl group)] is more than 5/95 and less than 95/5, respectively, preferably 7/93 or more and 93/7 or less, 10 /. 90 or more and 93/7 or less are more preferable, 20/80 or more and 93/7 or less are further preferable, 30/70 or more and 93/7 or less are particularly preferable, and 35/65 or more and 93/7 or less are most preferable. When the molar ratio is at least the above lower limit value, the storage stability of the resin composition can be improved, and when it is at least the above upper limit value, the low temperature curability when the resin film is formed. Can be made good.

When a solvent is used, a solvent that is inert to the isocyanate group may be used.
When a solvent is used, the content of the non-volatile content derived from the polyisocyanate and the blocking agent with respect to 100 parts by mass of the blocked polyisocyanate composition may be usually 10 parts by mass or more and 95 parts by mass or less, and 20 parts by mass or more and 80 parts by mass. It is preferably 3 parts by mass or less, and more preferably 30 parts by mass or more and 75 parts by mass or less.

In the blocking reaction, an organic metal salt such as tin, zinc or lead, a tertiary amine compound, an alkali metal alcoholate such as sodium or the like may be used as a catalyst.
The amount of the catalyst added varies depending on the temperature of the blocking reaction and the like, but is usually 0.05 parts by mass or more and 1.5 parts by mass or less with respect to 100 parts by mass of polyisocyanate, and 0.1 parts by mass. It is preferably 1.0 part by mass or less.

The blocking reaction can generally be carried out at −20 ° C. or higher and 150 ° C. or lower, preferably 0 ° C. or higher and 100 ° C. or lower, and more preferably 10 ° C. or higher and 80 ° C. or lower. When the temperature of the blocking reaction is at least the above lower limit value, the reaction rate can be further increased, and when it is at least the above upper limit value, the side reaction can be further suppressed.
After the blocking reaction, a neutralization treatment may be performed by adding an acidic compound or the like.
As the acidic compound, an inorganic acid may be used or an organic acid may be used. Examples of the inorganic acid include hydrochloric acid, phosphoric acid, phosphoric acid and the like. Examples of the organic acid include methanesulfonic acid, p-toluenesulfonic acid, dioctylphthalate, dibutylphthalate and the like.

When a hydrophilic compound is used, it is obtained by reacting the polyisocyanate with the blocking agent and the hydrophilic compound.

The reaction between the polyisocyanate and the hydrophilic compound and the reaction between the polyisocyanate and the blocking agent can be carried out at the same time, or any of the reactions can be carried out in advance and then the second and subsequent reactions can be carried out. Above all, the reaction between the polyisocyanate and the hydrophilic compound is performed first to obtain the hydrophilic compound-modified polyisocyanate modified by the hydrophilic compound, and then the reaction between the obtained hydrophilic compound-modified polyisocyanate and the blocking agent is carried out. It is preferable to do so.

The reaction between the polyisocyanate and the hydrophilic compound may use an organic metal salt, a tertiary amine compound, or an alkali metal alcoholate as a catalyst. Examples of the metal constituting the organometallic salt include tin, zinc, lead and the like. Examples of the alkali metal include sodium and the like.

The reaction temperature between the polyisocyanate and the hydrophilic compound is preferably −20 ° C. or higher and 150 ° C. or lower, and more preferably 30 ° C. or higher and 130 ° C. or lower. When the reaction temperature is equal to or higher than the above lower limit, the reactivity tends to be higher. Further, when the reaction temperature is not more than the above upper limit value, the side reaction tends to be suppressed more effectively.

It is preferable to completely react with polyisocyanate so that the hydrophilic compound does not remain in an unreacted state. Since it does not remain in the unreacted state, it tends to more effectively suppress the deterioration of the water dispersion stability of the blocked polyisocyanate composition and the low temperature curability when it is formed into a resin film.

As the reaction between the hydrophilic compound-modified polyisocyanate and the blocking agent, the method described as the above-mentioned blocking reaction can be used.

<Characteristics of blocked polyisocyanate composition>
[Weight average molecular weight Mw]
The weight average molecular weight Mw of the block polyisocyanate composition of the present embodiment is preferably 2.0 × 10 ³ or more, 2.0 × 10 ³ or more 2.0 × more preferably 10 ⁵ or less, 4.0 × 10 ³ or more more preferably 1.5 × 10 ⁵ or less, particularly preferably 4.0 × 10 ³ or more 1.0 × 10 ⁵ or less, and most preferably 4.0 × 10 ³ or more 7.0 × 10 ⁴ or less. When the weight average molecular weight Mw is within the above range, the viscosity of the blocked polyisocyanate composition can be kept better. The weight average molecular weight Mw can be measured, for example, by gel permeation chromatography (hereinafter, may be abbreviated as "GPC").

≪Resin composition≫
The resin composition of the present embodiment contains the above-mentioned blocked polyisocyanate composition and a multivalent hydroxy compound. The resin composition of the present embodiment can also be said to be a one-component resin composition containing a curing agent component and a main agent component.

The resin composition of the present embodiment has excellent storage stability and a resin film having excellent low temperature curability.
The constituent components of the resin composition of the present embodiment will be described in detail below.

<Multivalent hydroxy compound>
As used herein, the term "polyvalent hydroxy compound" means a compound having at least two hydroxy groups (hydroxyl groups) in one molecule, and is also referred to as a "polyol".
Specific examples of the polyvalent hydroxy compound include aliphatic hydrocarbon polyols, polyether polyols, polyester polyols, epoxy resins, fluorine-containing polyols, acrylic polyols and the like.
Among them, the polyvalent hydroxy compound is preferably polyester polyols, fluorine-containing polyols or acrylic polyols.

[Aliphatic hydrocarbon polyols]
Examples of the aliphatic hydrocarbon polyols include hydroxyl-terminated polybutadiene and hydrogenated products thereof.

[Polyester polyols]
Examples of the polyether polyols include those obtained by using any of the following methods (1) to (3).
(1) Polyether polyols or polytetramethylene glycols obtained by adding an alkylene oxide alone or a mixture to a polyhydric alcohol alone or a mixture.
(2) Polyether polyols obtained by reacting an alkylene oxide with a polyfunctional compound.
(3) So-called polymer polyols obtained by polymerizing acrylamide or the like using the polyether polyols obtained in (1) or (2) as a medium.
Examples of the polyhydric alcohol include glycerin and propylene glycol.
Examples of the alkylene oxide include ethylene oxide and propylene oxide.
Examples of the polyfunctional compound include ethylenediamine and ethanolamines.

[Polyester polyols]
Examples of the polyester polyols include the polyester polyols according to any one of (1) and (2) below.
(1) Polyester polyol resins obtained by a condensation reaction between a dibasic acid alone or a mixture of two or more kinds and a polyhydric alcohol alone or a mixture of two or more kinds.
(2) Polycaprolactones obtained by ring-opening polymerization of ε-caprolactone with a polyhydric alcohol.
Examples of the dibasic acid include carboxylic acids such as succinic acid, adipic acid, dimer acid, maleic anhydride, phthalic acid anhydride, isophthalic acid, terephthalic acid, and 1,4-cyclohexanedicarboxylic acid.
Examples of the polyhydric alcohol include ethylene glycol, propylene glycol, diethylene glycol, 1,4-butanediol, neopentyl glycol, 1,6-hexanediol, trimethylpentanediol, cyclohexanediol, trimethylolpropane, glycerin, and pentaerythritol. , 2-Methylolpropanediol, ethoxylated trimethylolpropane and the like.

[Epoxy resins]
Examples of the epoxy resins include novolak type epoxy resin, β-methylepicro type epoxy resin, cyclic oxylan type epoxy resin, glycidyl ether type epoxy resin, glycol ether type epoxy resin, epoxy type aliphatic unsaturated compound, and epoxidized fatty acid. Epoxy resins such as esters, ester-type polyvalent carboxylic acids, aminoglycidyl-type epoxy resins, halogenated epoxy resins, resorcin-type epoxy resins, and resins obtained by modifying these epoxy resins with amino compounds, polyamide compounds, and the like can be mentioned. Be done.

[Fluorine-containing polyols]
Examples of the fluorine-containing polyols include fluoroolefins, cyclohexyl vinyl ethers, and hydroxys disclosed in Reference 1 (Japanese Patent Laid-Open No. 57-34107) and Reference 2 (Japanese Patent Laid-Open No. 61-275311). Examples thereof include copolymers such as alkyl vinyl ether and monocarboxylic acid vinyl ester.

[Acrylic polyols]
The acrylic polyols are, for example, a polymerizable monomer having one or more active hydrogens in one molecule, or a polymerizable monomer having one or more active hydrogens in one molecule, and if necessary. , Is obtained by copolymerizing the polymerizable monomer with another copolymerizable monomer.

Examples of the polymerizable monomer having one or more active hydrogens in one molecule include those shown in the following (i) to (iii). These may be used alone or in combination of two or more.
(I) Acrylic acid esters having active hydrogen such as -2-hydroxyethyl acrylate, -2-hydroxypropyl acrylate, and -2-hydroxybutyl acrylate.
(Ii) Methacrylic acid esters having active hydrogen such as -2-hydroxyethyl methacrylate, -2-hydroxypropyl methacrylate, and -2-hydroxybutyl methacrylate.
(Iii) (meth) acrylic acid esters having polyvalent active hydrogen such as acrylic acid monoester or methacrylic acid monoester of glycerin, acrylic acid monoester or methacrylic acid monoester of trimethylolpropane.

Examples of other monomers copolymerizable with the polymerizable monomer include those shown in the following (i) to (v). These may be used alone or in combination of two or more.
(I) Acrylic acid esters such as methyl acrylate, ethyl acrylate, isopropyl acrylate, -n-butyl acrylate, and -2-ethylhexyl acrylate.
(Ii) Methacrylic acid esters such as methyl methacrylate, ethyl methacrylate, isopropyl methacrylate, -n-butyl methacrylate, isobutyl methacrylate, -n-hexyl methacrylate, cyclohexyl methacrylate, lauryl methacrylate, and glycidyl methacrylate. ..
(Iii) Unsaturated carboxylic acids such as acrylic acid, methacrylic acid, maleic acid, and itaconic acid.
(Iv) Unsaturated amides such as acrylamide, N-methylolacrylamide, and diacetoneacrylamide.
(V) Styrene, vinyltoluene, vinyl acetate, acrylonitrile, etc.

Further, an acrylic polyol obtained by copolymerizing a polymerizable ultraviolet stable monomer disclosed in Reference 3 (Japanese Patent Laid-Open No. 1-261409) and Reference Document 4 (Japanese Patent Laid-Open No. 3-006273). Kind and the like.

Specifically, as the polymerizable ultraviolet-stable monomer, for example, 4- (meth) acryloyloxy-2, 2,6,6-tetramethylpiperidine, 4- (meth) acryloylamino-2, 2,6 , 6-Tetramethylpiperidine, 1-crotonoyl-4-crotonoyloxy-2, 2,6,6-tetramethylpiperidine, 2-hydroxy-4- (3-methacryloxy-2-hydroxypropoxy) benzophenone and the like. Be done.

For example, the above monomer component is solution-polymerized in the presence of a known radical polymerization initiator such as a peroxide or an azo compound, and if necessary, diluted with an organic solvent or the like to obtain an acrylic polyol. Can be done.

When an aqueous-based base acrylic polyol is obtained, it can be produced by a known method such as a method of solution-polymerizing an olefinically unsaturated compound to convert it into an aqueous layer or an emulsion polymerization. In that case, water solubility or water dispersibility can be imparted by neutralizing an acidic portion such as a carboxylic acid-containing monomer such as acrylic acid or methacrylic acid or a sulfonic acid-containing monomer with an amine or ammonia.

[Hydroxy group value and acid value of multivalent hydroxy compound]
The hydroxyl value of the polyvalent hydroxy compound contained in the resin composition of the present embodiment is preferably 5 mgKOH / g or more and 300 mgKOH / g or less.
When the hydroxyl group of the polyvalent hydroxy compound is at least the above lower limit value, the crosslink density of urethane due to the reaction with polyisocyanate is further increased, and the function of urethane bond is more easily exhibited. On the other hand, when the hydroxyl group of the polyvalent hydroxy compound is not more than the above upper limit value, the crosslink density does not increase too much, and the mechanical properties of the resin film become better.

[NCO / OH]
The molar equivalent ratio (NCO / OH) of the isocyanate group of the blocked polyisocyanate composition to the hydroxyl group of the polyvalent hydroxy compound contained in the resin composition of the present embodiment is determined by the required physical properties of the resin film, but is usually determined. , 0.01 or more and 22.5 or less.

<Other additives>
The resin composition of the present embodiment may further contain other additives.
Other additives include, for example, a curing agent capable of reacting with a crosslinkable functional group in a polyvalent hydroxy compound, a curing catalyst, a solvent, pigments (constituent pigments, coloring pigments, metallic pigments, etc.), ultraviolet absorbers, and photostabilizing agents. Examples thereof include agents, radical stabilizers, anti-yellowing agents that suppress coloring during the baking process, coating surface adjusting agents, flow adjusting agents, pigment dispersants, defoaming agents, thickening agents, and film forming aids.

Examples of the curing agent include melamine resin, urea resin, epoxy group-containing compound or resin, carboxyl group-containing compound or resin, acid anhydride, alkoxysilane group-containing compound or resin, hydrazide compound and the like.

The curing catalyst may be a basic compound or a Lewis acidic compound.
Examples of the basic compound include metal hydroxides, metal alkoxides, metal carboxylates, metal acetyl acetylates, hydroxides of onium salts, onium carboxylates, halides of onium salts, and metal salts of active methylene compounds. Examples thereof include onium salts of active methylene compounds, aminosilanes, amines, phosphines and the like. As the onium salt, an ammonium salt, a phosphonium salt or a sulfonium salt is suitable.
Examples of the Lewis acidic compound include an organic tin compound, an organic zinc compound, an organic titanium compound, and an organic zirconium compound.

Examples of the solvent include those similar to those exemplified in the block polyisocyanate composition.

In addition, pigments (constitution pigments, coloring pigments, metallic pigments, etc.), ultraviolet absorbers, light stabilizers, radical stabilizers, anti-yellowing agents that suppress coloring during the baking process, coating surface adjusting agents, flow adjusting agents, pigments As the dispersant, defoaming agent, thickener and film-forming auxiliary, known ones can be appropriately selected and used.

<Manufacturing method of resin composition>
The resin composition of the present embodiment can be used for both solvent-based and water-based bases, but since no resin composition having good storage stability in water-based base has been known so far, it is water-based. It is suitably used as a resin composition of.

When producing an aqueous-based resin composition (aqueous resin composition), first, a polyvalent hydroxy compound or an aqueous dispersion thereof or a water-soluble substance is added to a crosslinkable functional group in the polyvalent hydroxy compound, if necessary. Curing agents, curing catalysts, solvents, pigments (constituent pigments, coloring pigments, metallic pigments, etc.) that can react with UV absorbers, light stabilizers, radical stabilizers, anti-yellowing agents that suppress coloring during the baking process, Add additives such as coating surface conditioner, flow conditioner, pigment dispersant, defoamer, thickener, and film-forming aid. Next, the blocked polyisocyanate composition or an aqueous dispersion thereof is added as a curing agent, and if necessary, water or a solvent is further added to adjust the viscosity. Then, by forcibly stirring with a stirring device, a water-based resin composition (water-based resin composition) can be obtained.

When producing a solvent-based resin composition, first, a curing agent or a curing catalyst capable of reacting with a polyvalent hydroxy compound or a diluted solution thereof with a crosslinkable functional group in the polyvalent hydroxy compound, if necessary, is used. , Solvents, pigments (constitution pigments, coloring pigments, metallic pigments, etc.), ultraviolet absorbers, light stabilizers, radical stabilizers, anti-yellowing agents that suppress coloring during the baking process, coating surface adjusting agents, flow adjusting agents, Add additives such as pigment dispersants, defoamers, thickeners, and film-forming aids. Then, the block polyisocyanate composition is added as a curing agent, and if necessary, a solvent is further added to adjust the viscosity. Then, the solvent-based resin composition can be obtained by stirring by hand or using a stirring device such as a magella.

≪Resin film≫
The resin film of the present embodiment is obtained by curing the above resin composition. The resin film of the present embodiment has good low-temperature curability.

The resin film of the present embodiment is cured by coating the above resin composition on a base material by a known method such as roll coating, curtain flow coating, spray coating, bell coating, electrostatic coating, and heating. It can be obtained by.

From the viewpoint of energy saving and heat resistance of the base material, the heating temperature is preferably about 70 ° C. or higher and about 120 ° C. or lower, more preferably about 70 ° C. or higher and about 110 ° C. or lower, and further preferably about 75 ° C. or higher and about 100 ° C. or lower.
From the viewpoint of energy saving and heat resistance of the base material, the heating time is preferably about 1 minute or more and about 60 minutes or less, and more preferably about 2 minutes or more and about 40 minutes or less.

The base material is not particularly limited, and is, for example, an outer panel of an automobile body such as a passenger car, a truck, a motorcycle, or a bus; an automobile part such as a bumper; an outer panel of a household electric product such as a mobile phone or an audio device. Part: Various films and the like are mentioned, and among them, the outer panel part of the automobile body or the automobile part is preferable.

The material of the base material is not particularly limited, and is, for example, iron, aluminum, brass, copper, tin, stainless steel, zinc-plated steel, zinc alloy (Zn-Al, Zn-Ni, Zn-Fe, etc.) plating. Metallic materials such as steel; polyethylene resin, polypropylene resin, acrylonitrile-butadiene-styrene (ABS) resin, polyamide resin, acrylic resin, vinylidene chloride resin, polycarbonate resin, polyurethane resin, resins such as epoxy resin, various FRP, etc. Examples thereof include plastic materials; inorganic materials such as glass, cement and concrete; wood; fiber materials such as paper and cloth, and among them, metal materials or plastic materials are preferable.

The base material is obtained by subjecting the surface of the metal material or the metal surface of a vehicle body or the like molded from the metal material to a surface treatment such as a phosphate treatment, a chromate treatment, or a composite oxide treatment. Further, a coating film may be formed on the coating film. The base material on which the coating film is formed may be one in which a surface treatment is applied as necessary and an undercoat coating film is formed on the base material, for example, a vehicle body in which an undercoat coating film is formed by an electrodeposition paint. good. The base material may be a surface of the above-mentioned plastic material or a plastic surface of an automobile part or the like molded from the above-mentioned metal material, which has been subjected to a desired surface treatment. Further, the base material may be a combination of a plastic material and a metal material.

As the resin film of the present embodiment, as shown in Examples described later, a resin film having a thickness of 40 μm obtained by heating and curing the resin composition at 80 ° C. for 30 minutes is stored at 23 ° C. for 1 week and then acetone. The gel content when immersed in 23 ° C. for 24 hours is preferably 82% by mass or more, more preferably 85% by mass or more, still more preferably 86% by mass or more. When the gel fraction is at least the above lower limit value, the low temperature curability can be improved. On the other hand, the upper limit of the gel fraction is not particularly limited, but may be, for example, 100% by mass. As a specific method for measuring the gel fraction, for example, the method shown in Examples described later can be used.

As shown in Examples described later, the resin film of the present embodiment has a König hardness at 23 ° C. of a resin film having a film thickness of 40 μm obtained by heating and curing the resin composition on glass at 80 ° C. for 30 minutes. Is preferably 38 times or more, more preferably 40 times or more, further preferably 50 times or more, and particularly preferably 55 times or more. When the König hardness at 23 ° C. is at least the above lower limit value, a resin film having better hardness can be obtained. On the other hand, the upper limit of the König hardness at 23 ° C. is not particularly limited, but may be, for example, 140 times. As a specific method for measuring the König hardness at 23 ° C., for example, the method shown in Examples described later can be used.

As the resin film of the present embodiment, as shown in Examples described later, a resin film having a film thickness of 40 μm, a width of 10 mm, and a length of 40 mm, which is obtained by heating and curing the resin composition at 80 ° C. for 30 minutes, is formed between chucks. The maximum stress in the tensile test conducted at a speed of 20 mm / min under an environment of 23 ° C. set to a distance of 20 mm is preferably 5 MPa or more, more preferably 10 MPa or more, and more preferably 15 MPa or more. It is more preferable, and it is particularly preferable that it is 20 MPa or more. When the maximum tensile stress is at least the above lower limit value, a resin film having better strength can be obtained. On the other hand, the upper limit of the maximum tensile stress is not particularly limited, but may be, for example, 100 MPa. As a specific method for measuring the maximum tensile stress, for example, the method shown in Examples described later can be used.

Since the resin film of the present embodiment has excellent low-temperature curability, it is suitably used for products in various fields where energy saving is required and as a coating film for a material having low heat resistance.

≪Laminated body≫
The laminate of the present embodiment contains two or more resin films of the above resin films having different compositions. The thickness of one layer of the resin film is 1 μm or more and 50 μm or less. The laminate of the present embodiment is excellent in low temperature curability by containing the above resin film.

The laminate of the present embodiment may include two or more layers of the above resin film having the same composition.

Further, the laminated body of the present embodiment is formed by laminating various coating films including the resin film on the adherend.
The adherend includes, for example, glass, various metals, porous members, various coated members, cured sealing materials, rubbers, leathers, fibers, non-woven fabrics, resin films and plates, and ultraviolet curing. Examples thereof include a mold acrylic resin layer and a layer made of inks. Examples of the various metals include aluminum, iron, galvanized steel sheet, copper, stainless steel and the like. Examples of the porous member include wood, paper, mortar, stone and the like. Examples of the various coatings include fluorine coating, urethane coating, acrylic urethane coating and the like. Examples of the cured sealant include silicone-based, modified silicone-based, urethane-based, and the like. Examples of the rubbers include natural rubber and synthetic rubber. Examples of the leathers include natural leathers and artificial leathers. Examples of the fibers include plant fibers, animal fibers, carbon fibers, glass fibers and the like. Examples of the resins used as raw materials for the films and plates of the resins include polyvinyl chloride, polyester, acrylic, polycarbonate, triacetyl cellulose, and polyolefin. Examples of the inks include printing inks and UV inks.

In the laminate of the present embodiment, the above resin compositions having different compositions are coated on the adherend by a known method such as roll coating, curtain flow coating, spray coating, bell coating, electrostatic coating, etc. It can be obtained by heating and curing each layer, or by heating and curing all the layers together after painting.

In addition to the resin film, the laminate of the present embodiment may include, for example, a layer made of other known components such as a primer layer, an adhesive layer, and a decorative layer.

Hereinafter, the present embodiment will be described in more detail based on Examples and Comparative Examples, but the present embodiment is not limited to the following Examples.

<Test items>
The blocked polyisocyanate compositions obtained in Examples and Comparative Examples were measured and evaluated for their physical properties according to the methods shown below.

[Physical characteristics 1]
(Isocyanate group (NCO) content)
In order to measure the NCO content of polyisocyanate, polyisocyanate before blocking with a blocking agent was used as a measurement sample.

First, 2 g or more and 3 g or less of the measurement sample were precisely weighed in a flask (Wg). Then, 20 mL of toluene was added to dissolve the measurement sample. Then, 20 mL of a toluene solution of 2N-n-butylamine was added, and after mixing, the mixture was allowed to stand at room temperature for 15 minutes. Then 70 mL of isopropyl alcohol was added and mixed. This solution was then titrated into an indicator with a 1N hydrochloric acid solution (Factor F). The obtained titration value was V2 mL. Then, without the polyisocyanate sample, the obtained titration value was set to V1 ml. Next, the isocyanate group (NCO) content (% by mass) of the polyisocyanate was calculated from the following formula.

Isocyanate group (NCO) content (% by mass) = (V1-V2) x F x 42 / (W x 1000) x 100

[Physical characteristics 2]
(Number average molecular weight and weight average molecular weight)
The number average molecular weight and the weight average molecular weight are the polystyrene-based number average molecular weight and the weight average molecular weight measured by gel permeation chromatography (GPC) using the following apparatus. In order to measure the number average molecular weight of polyisocyanate, polyisocyanate before blocking with a blocking agent was used as a measurement sample. As for the weight average molecular weight, the blocked polyisocyanate composition was used as it was as a measurement sample. The measurement conditions are shown below.

(Measurement condition)
Equipment: HLC-802A manufactured by Tosoh Corporation
Column: Made by Tosoh Corporation, G1000HXL x 1
G2000HXL x 1
G3000HXL x 1 Carrier: Tetrahydrofuran Detection method: Differential refractometer

[Physical characteristics 3]
(Average number of isocyanate functional groups)
The average number of isocyanate functional groups (average number of NCOs) of polyisocyanate was calculated by the following formula. In the formula, "Mn" is the number average molecular weight of the polyisocyanate before being blocked by the blocking agent, and the value measured in the above "Physical characteristics 2" was used. The "NCO content" is the isocyanate group content of the polyisocyanate measured before blocking with the blocking agent, and the value calculated in the above "Physical characteristics 1" was used.

Average number of isocyanate functional groups = (Mn x NCO content x 0.01) / 42

[Physical characteristics 4]
(Amount of solid content of blocked polyisocyanate composition)
The solid content of the blocked polyisocyanate composition was determined as follows.
First, an aluminum dish having a bottom diameter of 38 mm was precisely weighed. Then, about 1 g of the block polyisocyanate composition produced in Examples and Comparative Examples was placed on an aluminum dish and weighed precisely (W1). The blocked polyisocyanate composition was then adjusted to a uniform thickness. Then, the blocked polyisocyanate composition on an aluminum dish was held in an oven at 105 ° C. for 1 hour. Then, after the aluminum dish reached room temperature, the blocked polyisocyanate composition remaining on the aluminum dish was precisely weighed (W2). Next, the solid content (mass%) of the blocked polyisocyanate composition was calculated from the following formula.

Solid content (% by mass) of block polyisocyanate composition = W2 / W1 × 100

[Physical characteristics 5]
(Mole ratio of structural unit (II) / structural unit (I))
The molar ratio of the structural unit (II) to the structural unit (I) (molar ratio of (II) / (I)) is such that the blocked polyisocyanate composition is dried under reduced pressure by removing the solvent and other components at 50 ° C. or lower by an evaporator. Then, by ^{measuring the composition ratio of the constituent unit (II) to the constituent unit (I) by 1} H-NMR and ¹³ C-NMR, the molar ratio of the constituent unit (II) to the constituent unit (I) is calculated. bottom.

[Preparation of resin composition]
Acrylic polyol (“Setalux 1152” (trade name) manufactured by Allnex, OH% (on solids) = 4.2, Acid value (mgKOH / g) = 4.8, solid content 61% by mass) and each block polyisocyanate composition. The product was blended so that the ratio of the molar amount of isocyanate groups to the molar amount of hydroxyl groups (isocyanate group / hydroxyl group) was 1, and then butyl acetate was further blended to prepare a solid content of 33% by mass. A resin composition was obtained.

[Evaluation 1]
(Storage stability)
The initial viscosity of 20 g of the obtained resin composition and the viscosity when stored at 23 ° C. for 24 hours in a 20 mL glass bottle were measured (viscosity meter: RE-85R manufactured by Toki Sangyo Co., Ltd.). The ratio of the viscosity after storage to the initial viscosity was calculated. The ratio of the viscosity after storage to the initial viscosity was 5.0 or less, and those without gelation or precipitation were evaluated as good, and the difference in good level was expressed by the following evaluation criteria.

(Evaluation criteria)
⊚: Very good, ratio of viscosity after storage to initial viscosity is 2.0 or less 〇 〇: Good, ratio of viscosity after storage to initial viscosity is more than 2.0 3.0 or less 〇: Generally good, initial viscosity The ratio of viscosity after storage to is more than 3.0 and 5.0 or less.

[Evaluation 2]
(Low temperature curability)
The obtained resin composition was coated on a polypropylene (PP) plate so as to have a dry film thickness of 40 μm, and then heated and dried at 80 ° C. for 30 minutes to obtain a resin film. The obtained resin film was stored at room temperature (23 ° C.) for 1 week, and the gel fraction was measured. The gel fraction was determined as a percentage (% by mass) of the value obtained by dividing the mass of the undissolved portion when the resin membrane was immersed in acetone at 23 ° C. for 24 hours by the mass before immersion. Those having a gel fraction of 82% by mass or more were evaluated as good.

[Evaluation 3]
(König hardness)
A resin film was obtained on a glass plate by the same method as in "Evaluation 2" above. The König hardness (times) of the obtained resin film was measured in a 23 ° C. environment using a König hardness tester (Pendulum hardness tester manufactured by BYK Gardener). Those having a König hardness of 38 times or more were evaluated as good.

[Evaluation 4]
(Maximum tensile stress)
The obtained resin composition was coated on a polypropylene (PP) plate so as to have a dry film thickness of 40 μm, and then heated and dried at 80 ° C. for 30 minutes to obtain a resin film. The obtained resin film was cut into a width of 10 mm and a length of 40 mm, set so that the distance between chucks was 20 mm, and a tensile test was carried out at a speed of 20 mm / min in an environment of 23 ° C. The maximum point stress at that time was taken as the maximum tensile stress. Those having a maximum tensile stress of 5 MPa or more were evaluated as good.

<Synthesis of polyisocyanate>
[Synthesis Example 1]
(Synthesis of polyisocyanate P-1)
In a four-necked flask equipped with a thermometer, agitating blade and a reflux cooling tube, under a nitrogen stream, HDI: 100 parts by mass, and a polyester polyol derived from trihydric alcohol and ε-caprolactone (manufactured by Daicel Chemical Co., Ltd.) , "Praccel 303" (trade name), average number of hydroxyl groups: 3, number average molecular weight: 300): 5.2 parts by mass was charged, and the temperature inside the reactor was maintained at 88 ° C. for 1 hour under stirring to carry out the urethanization reaction. rice field. After that, the temperature inside the reactor was maintained at 62 ° C., tetramethylammonium capriate, an isocyanurate-forming catalyst, was added, and when the yield reached 51% by mass, phosphoric acid was added to terminate the reaction. After filtering the reaction solution, unreacted HDI was removed using a thin film evaporator to obtain an isocyanurate-type polyisocyanate (hereinafter, may be referred to as "polyisocyanate P-1"). The obtained polyisocyanate P-1 had an NCO content of 18.8% by mass, a number average molecular weight of 1180, and an average number of isocyanate groups of 5.3. ^{In addition, 1} H-NMR analysis was performed on the obtained polyisocyanate P-1, and it was confirmed that an isocyanurate group was present.

[Synthesis Example 2]
(Synthesis of polyisocyanate P-2)
In a four-necked flask equipped with a thermometer, stirring blade and reflux cooling tube, HDI: 80 parts by mass, IPDI: 20 parts by mass, and polyester derived from trihydric alcohol and ε-caprolactone under a nitrogen stream. Polycarbonate (manufactured by Daicel Chemical Co., Ltd., "Plaxel 303" (trade name), average number of hydroxyl groups: 3, number average molecular weight: 300): 5.2 parts by mass was charged, and the temperature inside the reactor was maintained at 88 ° C. for 1 hour under stirring. A urethanization reaction was carried out. After that, the temperature inside the reactor was maintained at 62 ° C., tetramethylammonium capriate, an isocyanurate-forming catalyst, was added, and when the yield reached 51% by mass, phosphoric acid was added to terminate the reaction. After filtering the reaction solution, unreacted HDI and IPDI were removed using a thin film evaporator to obtain an isocyanurate-type polyisocyanate (hereinafter, may be referred to as "polyisocyanate P-2"). The obtained polyisocyanate P-2 had an NCO content of 18.0% by mass, a number average molecular weight of 1200, and an average number of isocyanate groups of 5.1. ^{In addition, 1} H-NMR analysis was performed on the obtained polyisocyanate P-2, and it was confirmed that an isocyanurate group was present.

[Synthesis Example 3]
(Synthesis of polyisocyanate P-3)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, HDI: 70 parts by mass, IPDI: 30 parts by mass, and trimethylolpropane (average hydroxyl group functional), which is a trihydric alcohol, under a nitrogen stream. The number of groups: 3 and the molecular weight: 134): 3.2 parts by mass were charged, and the temperature inside the reactor was maintained at 85 ° C. for 1 hour under stirring to carry out the urethanization reaction. After that, the temperature inside the reactor was maintained at 78 ° C., tetramethylammonium capriate: isocyanurate-forming catalyst, 0.012 parts by mass was added, and when the yield reached 45% by mass, phosphoric acid was added to stop the reaction. After filtering the reaction solution, unreacted HDI and IPDI were removed using a thin film evaporator to obtain an isocyanurate-type polyisocyanate (hereinafter, may be referred to as "polyisocyanate P-3"). The obtained polyisocyanate P-3 had an NCO content of 18.9% by mass, a number average molecular weight of 1200, and an average number of isocyanate groups of 5.4. ^{In addition, 1} H-NMR analysis was performed on the obtained polyisocyanate P-3, and it was confirmed that an isocyanurate group was present.

[Synthesis Example 4]
(Synthesis of polyisocyanate P-4)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, HDI: 70 parts by mass, IPDI: 30 parts by mass, and trimethylolpropane (average hydroxyl group functional), which is a trihydric alcohol, under a nitrogen stream. The number of groups: 3 and the molecular weight: 134): 2.6 parts by mass were charged, and the temperature inside the reactor was maintained at 91 ° C. for 1 hour under stirring to carry out the urethanization reaction. After that, the temperature inside the reactor was maintained at 77 ° C., tetramethylammonium caprate, an isocyanurate-forming catalyst: 0.012 parts by mass was added, and when the yield reached 45% by mass, phosphoric acid was added to stop the reaction. After filtering the reaction solution, unreacted HDI and IPDI were removed using a thin film evaporator to obtain an isocyanurate-type polyisocyanate (hereinafter, may be referred to as "polyisocyanate P-4"). The obtained polyisocyanate P-4 had an NCO content of 19.1% by mass, a number average molecular weight of 1070, and an average number of isocyanate groups of 4.9. ^{In addition, 1} H-NMR analysis was performed on the obtained polyisocyanate P-4, and it was confirmed that an isocyanurate group was present.

[Synthesis Example 5]
(Synthesis of polyisocyanate P-5)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, HDI: 69 parts by mass, IPDI: 31 parts by mass, and trimethylolpropane (average hydroxyl group functional), which is a trihydric alcohol, under a nitrogen stream. The number of groups: 3, the molecular weight: 134): 2.56 parts by mass was charged, and the temperature inside the reactor was maintained at 91 ° C. for 1 hour under stirring to carry out the urethanization reaction. After that, the temperature inside the reactor was maintained at 78 ° C., tetramethylammonium capriate of isocyanurate-forming catalyst: 0.0124 parts by mass was added, and when the yield reached 45% by mass, phosphoric acid was added to stop the reaction. After filtering the reaction solution, unreacted HDI and IPDI were removed using a thin film evaporator to obtain an isocyanurate-type polyisocyanate (hereinafter, may be referred to as "polyisocyanate P-5"). The obtained polyisocyanate P-5 had an NCO content of 18.3% by mass, a number average molecular weight of 1420, and an average number of isocyanate groups of 6.2. ^{In addition, 1} H-NMR analysis was performed on the obtained polyisocyanate P-5, and it was confirmed that an isocyanurate group was present.

[Synthesis Example 6]
(Synthesis of polyisocyanate P-6)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, HDI: 80 parts by mass, IPDI: 20 parts by mass, and trimethylolpropane (average hydroxyl group functional), which is a trihydric alcohol, under a nitrogen stream. The number of groups: 3, the molecular weight: 134): 3.5 parts by mass was charged, and the temperature inside the reactor was maintained at 92 ° C. for 1 hour under stirring to carry out the urethanization reaction. After that, the temperature inside the reactor was maintained at 77 ° C., tetramethylammonium caprate, an isocyanurate-forming catalyst: 0.012 parts by mass was added, and when the yield reached 45% by mass, phosphoric acid was added to stop the reaction. After filtering the reaction solution, unreacted HDI and IPDI were removed using a thin film evaporator to obtain an isocyanurate-type polyisocyanate (hereinafter, may be referred to as "polyisocyanate P-6"). The obtained polyisocyanate P-6 had an NCO content of 19.0% by mass, a number average molecular weight of 1240, and an average number of isocyanate groups of 5.6. ^{In addition, 1} H-NMR analysis was performed on the obtained polyisocyanate P-6, and it was confirmed that an isocyanurate group was present.

[Synthesis Example 7]
(Synthesis of polyisocyanate P-7)
In a four-necked flask equipped with a thermometer, stirring blade and reflux cooling tube, polyisocyanate P-1: 100 parts by mass, methoxypolyethylene glycol (MPG-081, ethylene oxide repeating unit: 15 pieces, Japan) under a nitrogen stream. (Manufactured by Embroidery Co., Ltd.): 0.5 mol% with respect to 100 mol% of isocyanate groups of polyisocyanate P-1, 2-ethylhexyl acid phosphate (JP-508T, manufactured by Johoku Chemical Industry Co., Ltd.): 0.08 A part by mass and dipropylene glycol dimethyl ether (DPDM) were mixed and stirred at 120 ° C. for 2 hours to obtain polyisocyanate P-7.

[Synthesis Example 8]
(Synthesis of polyisocyanate P-8)
Polyisocyanate P-4: 100 parts by mass, methoxypolyethylene glycol (MPG-081, ethylene oxide repeating unit: 15 pieces, Japan) in a four-necked flask equipped with a thermometer, stirring blade and reflux cooling tube under a nitrogen stream. (Manufactured by Embroidery Co., Ltd.): 0.5 mol% with respect to 100 mol% of isocyanate groups of polyisocyanate P-4, 2-ethylhexyl acid phosphate (JP-508T, manufactured by Johoku Chemical Industry Co., Ltd.): 0.08 parts by mass, Then, dipropylene glycol dimethyl ether (DPDM) was mixed and stirred at 120 ° C. for 2 hours to obtain polyisocyanate P-8.

[Synthesis Example 9]
(Synthesis of polyisocyanate P-9)
In a four-necked flask equipped with a thermometer, stirring blade and reflux cooling tube, polyisocyanate P-1: 100 parts by mass, methoxypolyethylene glycol (MPG-081, ethylene oxide repeating unit: 15 pieces, Japan) under a nitrogen stream. (Manufactured by Embroidery Co., Ltd.): 6.0 parts by mass (amount of 2.0 mol% with respect to 100 mol% of isocyanate groups of polyisocyanate P-1), 2-ethylhexyl acid phosphate (JP-508T, Johoku Chemical Industry Co., Ltd.) (Manufactured by the company): 0.08 parts by mass and dipropylene glycol dimethyl ether (DPDM) were mixed and stirred at 120 ° C. for 2 hours to obtain polyisocyanate P-9.

<Manufacturing of blocked polyisocyanate composition>
[Example 1]
(Production of Block Polyisocyanate Composition BL-a1)
Polyisocyanate P-1: 100 parts by mass and diisopropyl malate: 6.8 parts by mass obtained in Synthesis Example 1 in a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser under a nitrogen stream. 20 mol% with respect to 100 mol% of NCO group) and di-tert-butyl malonate: 74.9 parts by mass (80 mol% with respect to 100 mol% of NCO group), and further, dipropylene glycol dimethyl ether. (DPDM) was added to prepare the solid content to be 60% by mass. Then, while stirring, 1.0 part by mass of a methanol solution containing sodium methylate (28% by mass with respect to the total mass of the solution) was added dropwise, and then the outer bath was adjusted so that the solution temperature became 55 ° C. The blocking reaction was carried out at 55 ° C. for 5 hours to obtain a blocked polyisocyanate composition BL-a1. The obtained blocked polyisocyanate composition BL-a1, solid content 60.1% by weight, and a weight average molecular weight 5.39 × 10 ^3.

[Examples 2 to 10 and Comparative Examples 1 to 3]
(Production of Block Polyisocyanate Compositions BL-a2-BL-a10 and BL-b1-BL-b3)
Block polyisocyanate compositions BL-a2-BL-a10 and BL-b1-BL-b3 are used in the same manner as in Example 1 except that the types and blending ratios of the blocking agents shown in Tables 1 to 3 are used. Manufactured.

[Example 11]
(Block Polyisocyanate Composition BL-a11)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, the polyisocyanate P-3: 100 parts by mass and diisopropyl malate: 100 mol% of NCO groups obtained in Synthesis Example 3 under a nitrogen stream. 60 mol% and 40 mol% of di-tert-butyl malonate: 100 mol% of NCO groups were added, and dipropylene glycol dimethyl ether (DPDM) was added to solidify the mixture. The minutes were adjusted to be 60% by mass. Then, while stirring, 1.2 parts by mass of a methanol solution containing sodium methylate (28% by mass with respect to the total mass of the solution) was added dropwise, and then the outer bath was adjusted so that the solution temperature became 55 ° C. The blocking reaction was carried out at 53 ° C. for 8 hours or more to obtain a blocked polyisocyanate composition BL-a11. The obtained blocked polyisocyanate composition BL-a11, solid content 60.1% by weight, and a weight average molecular weight 7.94 × 10 ^3.

[Examples 12 to 23]
(Block Polyisocyanate Compositions BL-a12 to BL-a23)
Blocked polyisocyanate compositions BL-a12 to BL-a23 using the same method as in Example 11 except that the types of polyisocyanates, the types of blocking agents and the blending ratios shown in Tables 4 to 6 are used. Manufactured.

[Example 24]
(Block Polyisocyanate Composition BL-a24)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, under a nitrogen stream, the polyisocyanate P-1 obtained in Synthesis Example 1 was added to 100 parts by mass, and diisopropyl malate: 100 mol% of NCO groups. In contrast, an amount of 80 mol% and a di-tert-butyl malonate: an amount of 20 mol% with respect to 100 mol% of NCO groups are charged, and further, dipropylene glycol dimethyl ether (DPDM) is added to solidify. The minutes were adjusted to be 60% by mass. Then, while stirring, 1.0 part by mass of a methanol solution containing sodium methylate (28% by mass with respect to the total mass of the solution) was added dropwise, and then the outer bath was adjusted so that the solution temperature became 53 ° C. The blocking reaction was carried out at 53 ° C. for 6 hours or more, and the disappearance of the peak of the isocyanate group was confirmed by infrared spectroscopy (IR). Then, an amount of 100 mol% was added to 100 mol% of the initial NCO group (NCO group before the blocking reaction) of tert-butanol: polyisocyanate P-1, and the mixture was reacted at 80 ° C. for 2 hours. Then, tert-butanol remaining in the reaction solution and isopropanol produced by the transesterification reaction were removed by distillation under reduced pressure, and dipropylene glycol dimethyl ether (DPDM) removed during distillation under reduced pressure was further added to block polyisocyanate. The composition BL-a24 was obtained. The obtained blocked polyisocyanate composition BL-a24, solid content 60.2% by weight, and a weight average molecular weight 8.31 × 10 ^3.

[Example 25]
(Block Polyisocyanate Composition BL-a25)
In a four-necked flask equipped with a thermometer, a stirring blade and a reflux condenser, 100 parts by mass of the polyisocyanate P-1 obtained in Synthesis Example 1 and 84.2 parts by mass of diisopropyl malonate obtained in Synthesis Example 1 under a nitrogen stream. An amount of 100 mol% with respect to 100 mol% of NCO groups) was charged, and dipropylene glycol dimethyl ether (DPDM) was further added to prepare the solid content to 60% by mass. Then, while stirring, 1.0 part by mass of a methanol solution containing sodium methylate (28% by mass with respect to the total mass of the solution) was added dropwise, and then the outer bath was adjusted so that the solution temperature became 48 ° C. The blocking reaction was carried out at 48 ° C. for 6 hours or more, and the disappearance of the isocyanate group peak was confirmed by the IR method. Then, 66.4 parts by mass of tert-butanol (amount of 200 mol% with respect to 100 mol% of the initial NCO group of polyisocyanate P-1) was added, and the mixture was reacted at 80 ° C. for 4 hours. Then, tert-butanol remaining in the reaction solution and isopropanol produced by the transesterification reaction were removed by distillation under reduced pressure, and dipropylene glycol dimethyl ether (DPDM) removed during distillation under reduced pressure was added to block. A polyisocyanate composition BL-a25 was obtained. The obtained blocked polyisocyanate composition BL-a25, solid content 60.1% by weight, and a weight average molecular weight 6.83 × 10 ^3.

[Example 26]
(Block Polyisocyanate Composition BL-a26)
The blocked polyisocyanate composition BL-a26 was produced by the same method as in Example 1 except that the types of polyisocyanates, the types of blocking agents and the blending ratios shown in Table 6 were used.

For the blocked polyisocyanate composition BL-a26, a resin composition was prepared using the following method.
Aqueous acrylic polyol main agent (manufactured by Nuplex, "Setaqua (registered trademark) 6515" (trade name), OH (%) (on solids) = 3.3, Acid value (mgKOH / g) = 9.9, solid content 45 Mass%) and the blocked polyisocyanate composition BL-a26 were blended so that the ratio of the molar amount of the isocyanate group to the molar amount of the hydroxyl group (isocyanate group / hydroxyl group) was 0.80. Further, ion-exchanged water was added, and a small amount of dimethylaminoethanol was added to prepare the pH so that the pH was 8.0 or more and 8.5 or less and the solid content was 45% by mass. Then, the solution was stirred at 1000 rpm for 15 minutes using a homodisper, and after defoaming, a resin composition was obtained. The low temperature curability of the obtained resin composition was evaluated using the same method as described above.

In addition, the blocked polyisocyanate compositions obtained in Examples and Comparative Examples were evaluated in various ways using the above methods. The results are shown in Tables 1-6 below.

In Tables 1 to 6, the types of blocking agents are as shown below.
(Blocking agent)
B-1: Diisopropyl malonate B-2: Di-tert-butyl malonic acid B-3: Diethyl malonate

From Tables 1 to 6, the block polyisocyanate compositions BL-a1 to BL-a26 having a molar ratio of the structural unit (II) / structural unit (I) of 20/80 or more and 92/8 or less (Examples 1 to 26). The resin composition had good storage stability, and the resin film had good low-temperature curability, König hardness, and maximum tensile stress.
Further, in the blocked polyisocyanate compositions BL-a1 to BL-a9 and BL-a11 to BL-a15 (Examples 1 to 9 and 11 to 15) having different molar ratios of the structural unit (II) / the structural unit (I). The smaller the molar ratio of the structural unit (II) / the structural unit (I), that is, the larger the ratio of B-2, the better the König hardness when the resin film was formed. On the other hand, the larger the molar ratio of the structural unit (II) / the structural unit (I), that is, the larger the ratio of B-1, the better the storage stability of the resin composition tended to be. .. Further, the blocked polyisocyanate compositions BL-a1 to BL-a8 and BL-a11 to BL-a15 (Examples 1 to 8 and) in which the molar ratio of the structural unit (II) / structural unit (I) is 90/10 or less. In 11 to 15), the maximum tensile stress tended to be more excellent when the resin composition was used.
Further, in the blocked polyisocyanate compositions BL-a10 to BL-a18 and BL-a20 (Examples 10 to 18 and 20) using a polyisocyanate containing a structural unit derived from HDI and IPDI, when a resin film is used. The König hardness and maximum tensile stress tended to be particularly excellent.
In BL-a19 (Example 19), a blocked polyisocyanate composition using a polyisocyanate containing a structural unit derived from a hydrophilic compound, a blocked polyisocyanate composition using a polyisocyanate not containing a structural unit derived from a hydrophilic compound. Compared with the compound BL-a6 (Example 6), the low-temperature curability, the König hardness, and the maximum tensile stress tended to be more excellent when the resin film was used.
In the blocked polyisocyanate compositions BL-a2, BL-a4 and BL-a6 in which the combination of the blocking agents used is different, and BL-a21 to BL-a23 (Examples 2, 4, 6 and 21 to 23), 3 In the blocked polyisocyanate compositions BL-a2, BL-a4 and BL-a6 (Examples 2, 4 and 6) using a malonic acid ester having a secondary alkyl group and a malonic acid ester having a secondary alkyl group, a resin film is used. The low temperature curability, König hardness and maximum tensile stress tended to be better.

On the other hand, in the blocked polyisocyanate composition BL-b1 (Comparative Example 1) using diisopropyl malonic acid (B-1) alone, the storage stability of the resin composition could be kept good. The low temperature curability and König hardness when made into a resin film were inferior.
Further, in the block polyisocyanate composition BL-b2 (Comparative Example 2) using di-tert-butyl malonic acid (B-2) alone, low-temperature curability and König hardness when formed as a resin film are maintained well. However, the storage stability of the resin composition was inferior.
In the block polyisocyanate composition BL-b3 (Comparative Example 3) in which the molar ratio of the structural unit (II) / the structural unit (I) is 5/95, the low-temperature curability and the König hardness when the resin film is formed are good. Although it could be maintained, the storage stability of the resin composition was inferior.

According to the block polyisocyanate composition of the present embodiment, the block has good storage stability when made into a resin composition and has good curability at a low temperature of about 80 ° C. when made into a resin film. A polyisocyanate composition can be provided. The resin composition of the present embodiment contains the blocked polyisocyanate composition and has good storage stability. Further, since the resin composition of the present embodiment can obtain a resin film having excellent low-temperature curability, it is suitably used for coating a material having low heat resistance.

Claims (14)

A blocked polyisocyanate composition comprising a blocked polyisocyanate derived from a polyisocyanate and one or more blocking agents.
Including the structural unit represented by the following general formula (I) and the structural unit represented by the following general formula (II).
A blocked polyisocyanate composition in which the molar ratio of the structural unit represented by the following general formula (II) to the structural unit represented by the following general formula (I) is more than 5/95 and less than 95/5.

(In the general formula ^(I), are each R ^{11, R 12} and ^{R 13} independently comprise one or more substituents selected from the group consisting of hydroxy and amino groups are also alkyl groups ^{.R 14} , R ¹⁵ and R ¹⁶ are each independently an alkyl group which may contain one or more substituents selected from the group consisting of a hydrogen atom or a hydroxy group and an amino group. The broken line represents a bond.

(In the general formula (II), R ²¹ , R ²² , R ²³ and R ²⁴ each independently contain a hydrogen atom or one or more substituents selected from the group consisting of hydroxy and amino groups. It is a good alkyl group. The broken line represents the bond.) Derived from a polyisocyanate, a malonic acid ester having one or more tertiary alkyl groups, and a malonic acid ester having one or more secondary alkyl groups or a malonic acid ester having one or more primary alkyl groups. A blocked polyisocyanate composition comprising a blocked polyisocyanate.
The structural unit represented by the general formula (I) is a structural unit derived from a malonic acid ester having a tertiary alkyl group, and the structural unit represented by the general formula (II) is the secondary alkyl group. The blocked polyisocyanate composition according to claim 1, which is a structural unit derived from a malonic acid ester having a primary alkyl group or a structural unit derived from the malonic acid ester having a primary alkyl group. A blocked polyisocyanate composition comprising a blocked polyisocyanate derived from a polyisocyanate, a malonic acid ester having one or more tertiary alkyl groups, and a malonic acid ester having one or more secondary alkyl groups.
Block polyisocyanate composition in which the molar ratio of the structural unit derived from the malonic acid ester having a secondary alkyl group to the structural unit derived from the malonic acid ester having a tertiary alkyl group is more than 5/95 and less than 95/5. thing. The blocked polyisocyanate composition according to claim 3, wherein the malonic acid ester having a tertiary alkyl group contains di-tert-butyl malonic acid, and the malonic acid ester having a secondary alkyl group contains diisopropyl malonic acid. thing. The blocked polyisocyanate composition according to any one of claims 1 to 4, wherein the polyisocyanate has an average number of isocyanate functional groups of 2 or more. The blocked polyisocyanate composition according to any one of claims 1 to 5, wherein the polyisocyanate is a polyisocyanate derived from one or more kinds of diisocyanates selected from the group consisting of an aliphatic diisocyanate and an alicyclic diisocyanate. thing. The weight average molecular weight Mw of the block polyisocyanate composition is 2.0 × 10 ³ or more, a block polyisocyanate composition according to any one of claims 1 to 6. The blocked polyisocyanate composition according to any one of claims 1 to 7, wherein the blocked polyisocyanate has an isocyanurate group. A resin composition comprising the block polyisocyanate composition according to any one of claims 1 to 8 and a multivalent hydroxy compound. A resin film obtained by curing the resin composition according to claim 9. A resin film having a thickness of 40 μm obtained by heating and curing the resin composition at 80 ° C. for 30 minutes was stored at 23 ° C. for 1 week and then immersed in acetone at 23 ° C. for 24 hours to have a gel fraction of 82% by mass. The resin film according to claim 10. The resin film according to claim 10 or 11, wherein the König hardness of a resin film having a thickness of 40 μm obtained by heating the resin composition on glass at 80 ° C. for 30 minutes at 23 ° C. is 38 times or more. .. A resin film having a film thickness of 40 μm, a width of 10 mm and a length of 40 mm, which is obtained by heating the resin composition at 80 ° C. for 30 minutes and curing it, is set so that the distance between chucks is 20 mm, and the speed is 23 ° C. and 20 mm / min. The resin film according to any one of claims 10 to 12, wherein the maximum stress in the tensile test carried out in is 5 MPa or more. A laminate containing two or more resin films of the resin film according to any one of claims 10 to 13 having different compositions.
A laminated body having a thickness of 1 μm or more and 50 μm or less per layer of the laminated body.