Description

《要件（１）》
エチレン系共重合体（Ｌ）は、エチレン［Ａ］に由来する構造単位と、炭素数４～２０のα－オレフィン［Ｂ］に由来する構造単位とのモル比〔［Ａ］／［Ｂ］〕が、４０／６０～９０／１０である。モル比が前記範囲にあるエチレン系共重合体（Ｌ）は、低温でのゴム弾性と常温での引張強度とのバランスに優れる。
［Ａ］／［Ｂ］の下限は、好ましくは４５／５５、より好ましくは５０／５０、特に好ましくは５５／４５である。また、［Ａ］／［Ｂ］の上限は、好ましくは８０／２０、より好ましくは７５／２５、さらに好ましくは７０／３０である。《Requirements (1)》
The ethylene-based copolymer (L) has a molar ratio of structural units derived from ethylene [ A ] to structural units derived from an α-olefin [ B ] having 4 to 20 carbon atoms [[ A ]/[ B ]. ] is between 40/60 and 90/10. The ethylene-based copolymer (L) having a molar ratio within the above range has an excellent balance between rubber elasticity at low temperature and tensile strength at room temperature.
The lower limit of [ A ]/[ B ] is preferably 45/55, more preferably 50/50, and particularly preferably 55/45. Also, the upper limit of [ A ]/[ B ] is preferably 80/20, more preferably 75/25, still more preferably 70/30.

《要件（２）》
エチレン系共重合体（Ｌ）は、非共役ポリエン［Ｃ］に由来する構造単位の含有割合が、前記［Ａ］に由来する構造単位、前記［Ｂ］に由来する構造単位および前記［Ｃ］に由来する構造単位の合計を１００モル％として、０．１～６．０モル％である。この含有割合が前記範囲にあるエチレン系共重合体（Ｌ）は、充分な架橋性および柔軟性を有する。
前記［Ｃ］に由来する構造単位の含有割合の下限は、好ましくは０．５モル％である。前記［Ｃ］に由来する構造単位の含有割合の上限は、好ましくは４．０モル％、より好ましくは３．５モル％、さらに好ましくは３．０モル％である。
非共役ポリエン［Ｃ］に由来する構造単位の含有量が上記範囲にあると、充分な架橋性および柔軟性を有するエチレン系共重合体（Ｌ）が得られる。《Requirement (2)》
In the ethylene copolymer (L), the content ratio of the structural units derived from the non-conjugated polyene [ C ] is the structural units derived from the [ A ], the structural units derived from the [ B ] and the [ C ]. It is 0.1 to 6.0 mol % when the total of structural units derived from is 100 mol %. The ethylene-based copolymer (L) having this content within the above range has sufficient crosslinkability and flexibility.
The lower limit of the content of structural units derived from [ C ] is preferably 0.5 mol%. The upper limit of the content of the structural unit derived from [ C ] is preferably 4.0 mol%, more preferably 3.5 mol%, still more preferably 3.0 mol%.
When the content of structural units derived from the non-conjugated polyene [C] is within the above range, an ethylene copolymer (L) having sufficient crosslinkability and flexibility can be obtained.

〈Ｂ値〉
ｏ－ジクロロベンゼン－ｄ₄／ベンゼン－ｄ₆（４／１［ｖ／ｖ］）を測定溶媒とし、測定温度１２０℃にて、¹³Ｃ－ＮＭＲスペクトル（１００ＭＨｚ、日本電子製ＥＣＸ４００Ｐ）を測定し、下記式（ｉ）に基づき算出した。
Ｂ値＝（［ＥＸ］＋２［Ｙ］）／〔２×［Ｅ］×（［Ｘ］＋［Ｙ］）〕・・・（ｉ）
［ここで［Ｅ］、［Ｘ］および［Ｙ］は、それぞれ、エチレン［Ａ］、炭素数４～２０のα－オレフィン［Ｂ］、および非共役ポリエン［Ｃ］に由来する構造単位のモル分率を示し、［ＥＸ］はエチレン［Ａ］－炭素数４～２０のα－オレフィン［Ｂ］ダイアッド連鎖分率を示す。］ <B value>
Using o-dichlorobenzene-d ₄ /benzene-d ₆ (4/1 [v/v]) as a measurement solvent, ¹³ C-NMR spectrum (100 MHz, JEOL ECX400P) was measured at a measurement temperature of 120°C. , calculated based on the following formula (i).
B value = ([EX] + 2 [Y]) / [2 x [E] x ([X] + [Y])] (i)
[wherein [E], [X] and [Y] are moles of structural units derived from ethylene [ A ], α-olefins having 4 to 20 carbon atoms [ B ], and non-conjugated polyenes [ C ], respectively [EX] indicates the ethylene [ A ]-C4-C20 α-olefin [ B ] diad chain fraction. ]