JP2021010341A - Agricultural mulching film - Google Patents
Agricultural mulching film Download PDFInfo
- Publication number
- JP2021010341A JP2021010341A JP2019127015A JP2019127015A JP2021010341A JP 2021010341 A JP2021010341 A JP 2021010341A JP 2019127015 A JP2019127015 A JP 2019127015A JP 2019127015 A JP2019127015 A JP 2019127015A JP 2021010341 A JP2021010341 A JP 2021010341A
- Authority
- JP
- Japan
- Prior art keywords
- slit
- slits
- film
- group
- parallel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、農作物が栽培される土壌の表面を覆う農業用マルチフィルムに関する。本発明の農業用マルチフィルムは、種子が蒔かれた畝の表面を覆う農業用マルチフィルムとして、特に適する。 The present invention relates to an agricultural mulch film that covers the surface of the soil in which the crop is cultivated. The agricultural mulch film of the present invention is particularly suitable as an agricultural mulch film covering the surface of a ridge on which seeds are sown.
従来、畝に手播きされていた種子が、近年、紐に種を等間隔にまとわせたシーダーテープを用いて、機械的に植え付けられている。シーダーテープは、農業用マルチフィルム（以下、必要に応じ「マルチフィルム」と略称する）の敷設に先立ち、畝に配置する必要があり、マルチフィルムに設けられた穴の位置と、種の発芽位置を合わせることが困難であった。 In recent years, seeds that have been hand-sown in ridges have been mechanically planted in recent years using a seeder tape in which seeds are spread at equal intervals on a string. The seeder tape must be placed in the ridges prior to laying the agricultural mulch film (hereinafter abbreviated as "mulch film" if necessary), and the positions of the holes provided in the mulch film and the germination position of the seeds. It was difficult to match.
特許文献１は、種子が蒔かれた畝の表面を覆うマルチフィルムに関する発明である。該マルチフィルムにはジグザク状のスリットや波状のスリット等が形成されており、発芽有効面積が広い。よって、種の発芽位置とスリットの位置がずれていた場合でも、芽がフィルムの一部を押し開けて成育する為、発芽不良や茎の屈曲が防止される。
しかしながらフィルムの一部が押し開かれると、該押し開かれた部分においてマルチフィルムが大きく開口する為、地温調節機能が著しく低下するという問題があった。また押し開かれた部分から土壌が露出するため、芽の周囲に雑草が生えやすく、また土壌も乾燥しやすい。
Patent Document 1 is an invention relating to a mulch film covering the surface of a ridge on which seeds are sown. The mulch film has zigzag-shaped slits, wavy slits, and the like, and has a large effective germination area. Therefore, even if the germination position of the seed and the position of the slit are deviated from each other, the buds push open a part of the film to grow, so that poor germination and bending of the stem are prevented.
However, when a part of the film is pushed open, the mulch film opens wide in the pushed open part, so that there is a problem that the soil temperature control function is remarkably lowered. In addition, since the soil is exposed from the opened part, weeds easily grow around the buds, and the soil also tends to dry.
特許文献２も、種子が蒔かれた畝の表面を被覆するマルチフィルムに関する発明である。特許文献２には、密度が０．８０〜０．９２８ｇ／ｃｍ３ であり、ＡＳＴＭＤ８２２に準拠して測定したスティフネスが１８０〜２４０ＭＰａであるポリエチレン系樹脂よりなる、厚みが１０〜２９μｍの長尺ポリエチレン系樹脂フィルムに、略平行な多数の直線状スリットが形成されてなる農業用マルチフィルムであって、上記スリットの長さが５０〜１８０ｍｍであり、スリットの角度が長尺ポリエチレン系樹脂フィルムの長手方向に対し４５〜９０度であり、スリットとスリットの間隔が５〜２５ｍｍであることを特徴とする農業用マルチフィルムが開示されている。該マルチフィルムは、地温調整機能、雑草防止機能を低下させることなく、高い種子発芽率を達成することができる。
しかしながらスリットがすべて略平行である為、剥ぎ取り難いという問題があった。地温上昇を目的としたマルチフィルムは気温が高くなると、農作物の収穫前であっても剥ぎ取られる。このときマルチフィルムは、農作物を傷つけないように、農作物の茎を挿通するスリットから引裂かれるのであるが、すべてのスリットが略平行であると、特定の方向以外から引裂くことが困難であった。
Patent Document 2 is also an invention relating to a mulch film that covers the surface of a ridge on which seeds are sown. Patent Document 2 describes a long polyethylene film having a thickness of 10 to 29 μm, which is made of a polyethylene resin having a density of 0.80 to 0.928 g / cm3 and a stiffness of 180 to 240 MPa measured in accordance with ASTMD822. An agricultural multi-film in which a large number of linear slits substantially parallel to each other are formed on the resin film. The length of the slits is 50 to 180 mm, and the angle of the slits is the longitudinal direction of the long polyethylene resin film. Agricultural multi-films characterized in that the temperature is 45 to 90 degrees with respect to the above and the distance between the slits is 5 to 25 mm are disclosed. The mulch film can achieve a high seed germination rate without deteriorating the soil temperature adjusting function and the weed prevention function.
However, since all the slits are substantially parallel, there is a problem that it is difficult to peel off. Mulch films intended to raise soil temperature are stripped off when the temperature rises, even before the crops are harvested. At this time, the mulch film was torn from the slits through which the stems of the crop were inserted so as not to damage the crop, but if all the slits were substantially parallel, it was difficult to tear from any direction other than a specific direction. ..
本発明は、良好な地温調整機能、雑草防止機能を有し、発芽有効面積の広いマルチフィルムであって、農作物を収穫する前であっても剥ぎ取りが容易なマルチフィルムの提供を課題とする。 An object of the present invention is to provide a mulch film having a good soil temperature adjusting function and a weed prevention function and having a wide germination effective area, which can be easily peeled off even before harvesting a crop. ..
本発明によると上記課題を解決するための手段として、互いに平行な複数のスリットａからなる第一スリット群Ａと、互いに平行な複数のスリットｂからなる第二スリット群Ｂと、互いに平行な複数のスリットｃからなる第３スリット群Ｃと、を順に備える農業用マルチフィルムであって、第一スリット群Ａを形成する前記スリットａと、第二スリット群Ｂを形成する前記スリットｂとは平行でなく、前記スリットａの第二スリット群Ｂ側端縁ａ２と、前記スリットｂの第一スリット群Ａ側端縁ｂ１との距離ｄ１が０．２ｍｍ≦ｄ１≦１５ｍｍであり、第二スリット群Ｂを形成する前記スリットｂと、第三スリット群Ｃを形成する前記スリットｃとは平行でなく、前記スリットｂの第三スリット群側端縁ｂ２と、前記スリットｃの第二スリット群Ｂ側端縁ｃ１との距離ｄ２が０．２ｍｍ≦ｄ２≦１５ｍｍであることを特徴とする農業用マルチフィルムが提供される。
また、前記第一スリット群Ａ、前記第二スリット群Ｂおよび前記第三スリット群Ｃはいずれも、フィルムの長手方向に延在することを特徴とする前記農業用マルチフィルムが提供される。
更に、前記スリットａ、前記スリットｂおよび前記スリットｃの少なくとも一つは、直線状であることを特徴とする前記農業用マルチフィルムが提供される。
更にまた、前記スリットａと前記スリットｃと、が平行であることを特徴とする前記農業用マルチフィルムが提供される。
According to the present invention, as means for solving the above problems, a first slit group A composed of a plurality of slits a parallel to each other, a second slit group B composed of a plurality of slits b parallel to each other, and a plurality of slits parallel to each other. Agricultural multi-film having a third slit group C composed of slits c in this order, the slit a forming the first slit group A and the slit b forming the second slit group B are parallel to each other. Instead, the distance d1 between the second slit group B side edge a2 of the slit a and the first slit group A side edge b1 of the slit b is 0.2 mm ≦ d1 ≦ 15 mm, and the second slit group. The slit b forming B and the slit c forming the third slit group C are not parallel to each other, and the third slit group side edge b2 of the slit b and the second slit group B side of the slit c. Provided is an agricultural multi-film characterized in that the distance d2 from the edge c1 is 0.2 mm ≦ d2 ≦ 15 mm.
Further, the agricultural multi-film is provided in which the first slit group A, the second slit group B, and the third slit group C all extend in the longitudinal direction of the film.
Further, the agricultural mulch film characterized in that at least one of the slit a, the slit b and the slit c is linear is provided.
Furthermore, the agricultural mulch film characterized in that the slit a and the slit c are parallel to each other is provided.
また、前記第三スリット群Ｃの、前記第二スリット群Ｂと反対側に、互いに平行な複数のスリットｄからなる第四スリット群Ｄが形成されていることを特徴とする前記農業用マルチフィルムが提供される。
更に、前記スリットｂと、前記スリットｄと、が平行であることを特徴とする前記農業用マルチフィルムが提供される。
更にまた、前記農業用マルチフィルムであって、種子が蒔かれた畝の表面を被覆する用途に用いられることを特徴とする農業用マルチフィルムが提供される。
Further, the agricultural multi-film is characterized in that a fourth slit group D composed of a plurality of slits d parallel to each other is formed on the side of the third slit group C opposite to the second slit group B. Is provided.
Further, the agricultural mulch film characterized in that the slit b and the slit d are parallel to each other is provided.
Furthermore, there is provided an agricultural mulch film, which is the agricultural mulch film, which is used for coating the surface of a ridge on which seeds are sown.
本発明の農業用マルチフィルムは、１つのスリット群を形成するスリットと、隣接するスリット群を形成するスリットが、平行でなく、近接している為、スリットを容易に連結させることができる。よって農作物を収穫する前にマルチフィルムを剥ぎ取る必要が生じた場合であっても、当該剥ぎ取り作業が容易である。
また各スリット群がフィルムの長手方向に延在していると、スリット群が畝に沿うようにマルチフィルムを敷設することができる。
また各スリット群を形成するスリットが直線状であると、スリットから外気や光が侵入し難く、マルチフィルムの持つ地温調整機能、雑草防止機能等が低下しにくい。
更に、複数のスリット群のうち、隣の隣に位置するスリット群を形成するスリット同士が平行であると、マルチフィルムが過剰に強度低下することを防止できる。
本発明の農業用マルチフィルは、地温調整機能に優れ、高い種子発芽率を達成することができるので種子が蒔かれた畝を覆う農業用マルチフィルムとして特に適する。
In the agricultural multi-film of the present invention, the slits forming one slit group and the slits forming adjacent slit groups are not parallel but close to each other, so that the slits can be easily connected. Therefore, even if it becomes necessary to peel off the mulch film before harvesting the crop, the peeling operation is easy.
Further, when each slit group extends in the longitudinal direction of the film, the mulch film can be laid so that the slit group extends along the ridge.
Further, when the slits forming each slit group are linear, it is difficult for outside air and light to enter through the slits, and the soil temperature adjusting function and weed prevention function of the mulch film are not easily deteriorated.
Further, when the slits forming the adjacent slit group among the plurality of slit groups are parallel to each other, it is possible to prevent the multi-film from being excessively lowered in strength.
The agricultural mulch of the present invention is particularly suitable as an agricultural mulch film for covering ridges on which seeds are sown because it has an excellent soil temperature adjusting function and can achieve a high seed germination rate.
以下、本発明を実施するための形態について図面に基づいて説明するが、本発明は以下に限定されるものではなく、同様の効果を奏する範囲において種々の実施形態をとることができる。
図１は本発明の農業用マルチフィルムの一実施形態を表す平面図（Ａ）とその部分拡大図（Ｂ）である。本発明の農業用マルチフィルム１０は、複数のスリット群が形成された基材１１からなる。
Hereinafter, embodiments for carrying out the present invention will be described with reference to the drawings, but the present invention is not limited to the following, and various embodiments can be taken as long as the same effects can be obtained.
FIG. 1 is a plan view (A) and a partially enlarged view (B) showing an embodiment of the agricultural mulch film of the present invention. The
［基材］
基材は、従来、農業用マルチフィルムに用いられていたフィルムを適宜採用することができ、例えば１５〜５０μｍ、好ましくは１８〜３０μｍの熱可塑性樹脂からなるフィルムを採用することができる。該熱可塑性樹脂は、ポリエチレン、ポリプロピレン、エチレン／プロピレン共重合体、ポリブデン、ポリ・４−メチルペンテン等のＣ２〜Ｃ８オレフィン（α−オレフィン）の単独重合体もしくは共重合体、これらオレフィンとジエンとの共重合体、エチレン−アクリレート共重合体、ポリスチレン、ＡＢＳ樹脂、ＡＡＳ樹脂、ＡＳ樹脂、ＭＢＳ樹脂、エチレン−塩化ビニル共重合樹脂、エチレン−酢酸ビニル共重合体、エチレン−塩ビ−酢ビ共重合体、ポリ塩化ビニリデン、ポリ塩化ビニル、塩素化ポリエチレン、塩素化ポリプロピレン、プロピレン−塩化ビニル共重合体、ポリ酢酸ビニル、フェノキシ樹脂、ポリアセタール、ポリアミド、ポリイミド、ポリカーボネート、ポリスルホン、ポリフェニレンオキサイド、ポリフェニレンサルファイド、ポリエチレンテレフタレート、ポリブチレンテレフタレート、メタクリル樹脂等を採用することができる。
[Base material]
As the base material, a film conventionally used for agricultural mulch films can be appropriately adopted, and for example, a film made of a thermoplastic resin having a thickness of 15 to 50 μm, preferably 18 to 30 μm can be adopted. The thermoplastic resin is a homopolymer or copolymer of C2-C8 olefin (α-olefin) such as polyethylene, polypropylene, ethylene / propylene copolymer, polybuden, poly-4-methylpentene, and these olefins and diene. Copolymer, ethylene-acrylate copolymer, polystyrene, ABS resin, AAS resin, AS resin, MBS resin, ethylene-vinyl chloride copolymer resin, ethylene-vinyl acetate copolymer, ethylene-vinyl chloride-vinegar vinyl copolymer Combined, polyvinylidene chloride, polyvinyl chloride, chlorinated polyethylene, chlorinated polypropylene, propylene-vinyl chloride copolymer, polyvinyl acetate, phenoxy resin, polyacetal, polyamide, polyimide, polycarbonate, polysulfone, polyphenylene oxide, polyphenylene sulfide, polyethylene Telephthalate, polybutylene terephthalate, methacrylic resin and the like can be adopted.
熱可塑性樹脂の好ましい例は、ポリオレフィンまたはオレフィン系共重合体であり、特に高密度ポリエチレン、低密度ポリエチレン、直鎖状低密度ポリエチレン、超低密度ポリエチレン、エチレン−酢酸ビニル共重合体等のポリエチレン系樹脂である。
また基材として、ポリ乳酸、ポリ（３−ヒドロキシブチレート−３−ヒドロキシヘキサノエート）、ポリグリコール酸、ポリブチレンサクシネート、ポリブチレンサクシネートアジペート、ポリブチレンアジペートテレフタレート、ポリエチレンテレフタレートサクシネート等からなる生分解性フィルムを採用することもできる。
Preferred examples of the thermoplastic resin are polyolefins or olefin-based copolymers, particularly polyethylene-based such as high-density polyethylene, low-density polyethylene, linear low-density polyethylene, ultra-low-density polyethylene, and ethylene-vinyl acetate copolymer. It is a resin.
Further, as a base material, from polylactic acid, poly (3-hydroxybutyrate-3-hydroxyhexanoate), polyglycolic acid, polybutylene succinate, polybutylene succinate adipate, polybutylene adipate terephthalate, polyethylene terephthalate succinate, etc. It is also possible to use a biodegradable film.
該基材は、本発明の目的を妨げない範囲で脂肪酸エステルや低分子量ポリオレフィン樹脂等の延伸助剤、結晶核剤、安定化剤、酸化防止剤、紫外線吸収剤、難燃剤、滑剤、界面活性剤、顔料などの着色剤等の添加剤を含有してもよい。 The base material is a stretching aid such as a fatty acid ester or a low molecular weight polyolefin resin, a crystal nucleating agent, a stabilizer, an antioxidant, an ultraviolet absorber, a flame retardant, a lubricant, and a surfactant, as long as the object of the present invention is not impaired. Additives such as agents and colorants such as pigments may be contained.
［スリット群］
本発明の農業用マルチフィルムは、互いに平行な複数のスリットからなるスリット群を少なくとも３条備えることを特徴とする。図１の農業用マルチフィルム１は、互いに平行な複数の直線状スリットａからなる第１スリット群Ａと、互いに平行な複数の直線状スリットｂからなる第２スリット群Ｂと、互いに平行な複数の直線状スリットｃからなる第３スリット群Ｃを備える。各スリットａ、ｂ、ｃはいずれも直線状である為、風等の影響によってスリット部分が開口することがなく、マルチフィルムの持つ地温調整機能、雑草防止機能を低下させることがない。
[Slit group]
The agricultural mulch film of the present invention is characterized by including at least three slit groups composed of a plurality of slits parallel to each other. The agricultural multi-film 1 of FIG. 1 has a first slit group A composed of a plurality of linear slits a parallel to each other, a second slit group B composed of a plurality of linear slits b parallel to each other, and a plurality of slits parallel to each other. A third slit group C including the linear slit c of the above is provided. Since each of the slits a, b, and c is linear, the slit portion does not open due to the influence of wind or the like, and the soil temperature adjusting function and the weed prevention function of the mulch film are not deteriorated.
図１のマルチフィルム１０に設けられたスリット群Ａ、Ｂ、Ｃはいずれもフィルムの長手方向（側辺１１に平行な方向）に延在している。これらのスリット群は、０．２〜１５ｍｍの間隔をもって順に配されていれば、例えばフィルムの幅方向に延在してもよい。しかしながら、図１に示すように、フィルム１０の側辺１１付近を残し、スリット群がフィルムの長手方向に延在していると、畝の上部にスリット群が位置するようにマルチフィルムを敷設しやすい。
The slit groups A, B, and C provided in the multi-film 10 of FIG. 1 extend in the longitudinal direction of the film (direction parallel to the side side 11). These slit groups may extend in the width direction of the film, for example, as long as they are arranged in order with an interval of 0.2 to 15 mm. However, as shown in FIG. 1, when the slit group extends in the longitudinal direction of the film while leaving the vicinity of the
本発明のマルチフィルムは、図１に示すように、スリットａとスリットｂとが平行でなく、スリットａとスリットｂの距離ｄ１が０．２〜１５ｍｍである為、スリットａの延在方向と垂直な方向ａｘまたはスリットｂの延在方向と垂直な方向ｂｘにフィルムを引き伸ばすことにより、スリットａまたはスリットｂを引裂き、スリットａとスリットｂとを結合させることができる。
同様に、スリットｂとスリットｃとが平行でなく、スリットｂとスリットｃの距離ｄ２が０．２〜１５ｍｍである為、スリットｂの延在方向と垂直な方向ｂｘ又はスリットｃの延在方向と垂直な方向ｃｘにフィルムを引き伸ばすことにより、スリットｂまたはスリットｃを引裂き、スリットｂとスリットｃとを結合させることができる。
In the multi-film of the present invention, as shown in FIG. 1, the slit a and the slit b are not parallel to each other, and the distance d1 between the slit a and the slit b is 0.2 to 15 mm. By stretching the film in the direction bx perpendicular to the extending direction of the vertical direction ax or the slit b, the slit a or the slit b can be torn and the slit a and the slit b can be joined.
Similarly, since the slit b and the slit c are not parallel and the distance d2 between the slit b and the slit c is 0.2 to 15 mm, the direction bx perpendicular to the extending direction of the slit b or the extending direction of the slit c. By stretching the film in the direction cx perpendicular to, the slit b or the slit c can be torn and the slit b and the slit c can be combined.
距離ｄ１、距離ｄ２が０．２ｍｍ未満であると、スリット加工する際や、マルチフィルムを展張する際に、スリットａとスリットｂ、スリットｂとスリットｃが結合する恐れがある。図２はスリットａとスリットｂの一部が結合したマルチフィルム２０を表す模式図である。スリットの一部が結合すると、該結合部分が捲れ上がり易くなり、マルチフィルムの持つ地温調整機能、雑草防止機能が低下する恐れがある。尚、距離ｄ１、距離ｄ２が１５ｍｍを超えると、マルチフィルムを剥ぎ取る際に隣接するスリットを結合させることが困難となる。距離ｄ１、距離ｄ２はそれぞれ、０．５〜１０ｍｍが好ましく、特に１〜４ｍｍが好ましい。
If the distance d1 and the distance d2 are less than 0.2 mm, the slit a and the slit b, and the slit b and the slit c may be combined when the slit is processed or the multi-film is stretched. FIG. 2 is a schematic view showing a
各スリットの長さＬは特に限定されないが、１０〜５０ｍｍが好ましい。スリットの長さが１０ｍｍ未満の場合、スリット加工が困難となる。またスリットの長さが５０ｍｍを超えると、マルチフィルムが撓んだ際に、スリット部分が開口し、マルチフィルム内に外気や光が侵入する恐れが高まる。スリットＬの長さは１５〜４５ｍｍが好ましく、特に１８〜３０ｍｍが好ましい。
また各スリット群におけるスリットの間隔ｓは５〜５０ｍｍが好ましく、特に１０〜３０ｍｍが好ましい。間隔ｓが５ｍｍ未満の場合は、スリット加工が難しく、加工時にフィルムが裂ける恐れがある。また間隔ｓが５０ｍｍを超えると、発芽不良や茎の屈曲を引き起こす恐れが生じる。
The length L of each slit is not particularly limited, but is preferably 10 to 50 mm. If the length of the slit is less than 10 mm, the slit processing becomes difficult. If the length of the slit exceeds 50 mm, the slit portion opens when the mulch film bends, increasing the risk of outside air or light entering the mulch film. The length of the slit L is preferably 15 to 45 mm, particularly preferably 18 to 30 mm.
The slit spacing s in each slit group is preferably 5 to 50 mm, particularly preferably 10 to 30 mm. If the interval s is less than 5 mm, slitting is difficult and the film may tear during processing. Further, if the interval s exceeds 50 mm, there is a risk of causing poor germination and bending of the stem.
各スリットは、図１に示すように、直線状であることが望ましいが、図３に示すような曲線状であってもよい。しかしながらスリットｓｒの両端ｓｒ１、ｓｒ２を結ぶ直線αと、スリットｓｒとの距離βは、スリットの長さＬの１／５以内であることが望ましく、特に１／１０以内であることが望ましい。距離βがスリットｓｒの長さＬの１／５を超えると、スリット部分が捲れ上がり易くなり、マルチフィルムの地温調整機能、雑草防止機能が低下する。
尚、直線αとスリットｓｒとの距離βは、直線αに垂直な直分であって、一端が直線αに接し、他端がスリットｓｒに接する線分のうち、最も長い線分の長さを意味する。
Each slit is preferably linear as shown in FIG. 1, but may be curved as shown in FIG. However, the distance β between the straight line α connecting both ends sr1 and sr2 of the slit sr and the slit sr is preferably within 1/5 of the length L of the slit, and particularly preferably within 1/10. When the distance β exceeds 1/5 of the length L of the slit sr, the slit portion tends to roll up, and the soil temperature adjusting function and the weed prevention function of the mulch film deteriorate.
The distance β between the straight line α and the slit sr is a straight line segment perpendicular to the straight line α, and is the length of the longest line segment among the line segments having one end in contact with the straight line α and the other end in contact with the slit sr. Means.
図１に示すスリットａ、スリットｃは、いずれもマルチフィルムの左側の側辺１１に対し時計回りに４５°の方向に延在しており、スリットｂは、マルチフィルムの左側の側辺１１に対し時計回りに１３５°の方向に延在している。各スリットの延在方向は特に限定されるものではないが、マルチフィルムの側辺１１に対し２０〜７０°あるいは１１０〜１６０°であることが望ましい。延在方向が７０°〜１１０°の場合、マルチフィルムを展張する際に、フィルムが長さ方向に引っ張られたときに、隣り合うスリット群のスリット同士が結合する恐れがある。また延在方向が２０°未満あるいは１６０°を超える場合は、マルチフィルムを展張する際に、フィルムが幅方向に引っ張られたときに、スリット同士が結合する恐れがある。
また隣接するスリット群の各スリットが形成する角度θは６０〜１２０°が好ましく、特に８０〜１００°が好ましい。角度θが６０°未満あるいは１２０°を超えると、マルチフィルムをスリット部分から引裂く際に、引裂きやすい方向と引裂き難い方向が生じる。
Both the slit a and the slit c shown in FIG. 1 extend clockwise with respect to the
The angle θ formed by each slit of the adjacent slit group is preferably 60 to 120 °, particularly preferably 80 to 100 °. When the angle θ is less than 60 ° or more than 120 °, when the multi-film is torn from the slit portion, a direction in which it is easy to tear and a direction in which it is difficult to tear occur.
図４は本発明の別の実施形態を表す概略平面図である。図４のマルチフィルム４０は４条のスリット群を備える。スリット群の数は特に限定されるものではないが、マルチフィルムの両側の側辺４１から１０〜６０ｃｍの部分にはスリットが設けられていないことが望ましい。側辺から１０〜６０ｃｍの部分は、通常、マルチフィルムを固定する為に用いられるため、該部分にスリット群が形成されていても発芽には寄与せず、フィルムの強度低下を引き起こすだけである。
尚、隣の隣に位置するスリット、即ち図４においては、スリットａとスリットｃ、スリットｂとスリットｄが、それぞれ平行であると、破れやすい方向性がおおむね二方向に定まるため、フィルムのハンドリング性が向上する。
FIG. 4 is a schematic plan view showing another embodiment of the present invention. The multi-film 40 of FIG. 4 includes a group of four slits. The number of slit groups is not particularly limited, but it is desirable that no slits are provided in the portions from the side sides 41 to 10 to 60 cm on both sides of the multi-film. Since the
In addition, in the slits located next to each other, that is, in FIG. 4, if the slits a and c and the slits b and d are parallel to each other, the direction in which the film is easily torn is determined in two directions, so that the film can be handled. Improves sex.
ポリエチレンにカーボンブラックを配合した樹脂組成物から、厚さ２０μｍ、幅９５０ｍｍのフィルムを製造した。フィルムの中央部分に、１辺の長さが２０ｍｍのスリットが１５ｍｍ間隔で形成されたスリット群を６条形成し、図５に示すマルチフィルム５０を得た。尚、第１スリット群Ａ、第３スリット群Ｃ、第５スリット群Ｅとフィルムの左側の側辺５１のなす角θ１は５０°、第２スリット群Ｂ、第４スリット群Ｄ、第６スリット群Ｆとフィルムの左側の側辺５１のなす角θ２は１３０°であった。また各スリットの間隔は２ｍｍとした。
A film having a thickness of 20 μm and a width of 950 mm was produced from a resin composition obtained by blending carbon black with polyethylene. Six slit groups in which slits having a side length of 20 mm were formed at intervals of 15 mm were formed in the central portion of the film to obtain the multi-film 50 shown in FIG. The angle θ1 formed by the first slit group A, the third slit group C, the fifth slit group E and the
大根の種をまいた畝に、上記マルチフィルを敷設した。この時、マルチフィルムの両側辺を人の足で踏みつけながら敷設したが、各スリット先端のつなぎ目は裂けることなく、スリットの連結は見られなかった。
２週間後に、マルチフィルムのスリットの間を通って、芽がマルチフィルムの外に出てきた。目視による発芽率はほぼ１００％であった。更に３か月４週間経過後、マルチフィルムに斜め方向の力をかけたところ、各スリットが結合し、マルチフィルムを容易に引裂くことができた。
The above multifill was laid on the ridges where radish seeds were sown. At this time, both sides of the mulch film were laid while being trampled by human feet, but the joints at the tips of the slits were not torn, and the slits were not connected.
Two weeks later, buds emerged from the mulch film through the slits in the mulch film. The visual germination rate was almost 100%. After 3 months and 4 weeks, when an oblique force was applied to the mulch film, the slits were combined and the mulch film could be easily torn.
以上、本発明の農業用マルチフィルムを、種子が蒔かれた畝を覆うマルチフィルムとして使用する場合を中心に説明したが、本発明のマルチフィルムの用途はこれに限定されるものではない。例えば、苗を植える土壌を覆う際に用いることもできる。当該用途に本発明の農業用マルチフィルムを用いる際は、畝にマルチフィルムを敷設後、苗を植える部分のみスリットを引裂いて結合させ、植え付け用の穴を形成するとよい。 The above description has focused on the case where the agricultural mulch film of the present invention is used as a mulch film for covering the ridges on which seeds are sown, but the application of the mulch film of the present invention is not limited to this. For example, it can be used to cover the soil in which seedlings are planted. When the agricultural mulch film of the present invention is used for this purpose, it is advisable to lay the mulch film on the ridges and then tear and connect only the part where the seedlings are to be planted to form a hole for planting.
１０、２０、４０、５０ マルチフィルム
１１、４１、５１ 側辺
Ａ、Ｂ、Ｃ スリット群
ａ、ｂ、ｃ スリット
10, 20, 40, 50 Multi-film 11, 41, 51 Side sides A, B, C Slit groups a, b, c Slits
Claims (7)
第一スリット群Ａを形成する前記スリットａと、第二スリット群Ｂを形成する前記スリットｂとは平行でなく、前記スリットａの第二スリット群Ｂ側端縁ａ２と、前記スリットｂの第一スリット群Ａ側端縁ｂ１との距離ｄ１が０．２ｍｍ≦ｄ１≦１５ｍｍであり、
第二スリット群Ｂを形成する前記スリットｂと、第三スリット群Ｃを形成する前記スリットｃとは平行でなく、前記スリットｂの第三スリット群側端縁ｂ２と、前記スリットｃの第二スリット群Ｂ側端縁ｃ１との距離ｄ２が０．２ｍｍ≦ｄ２≦１５ｍｍであることを特徴とする農業用マルチフィルム。 A first slit group A composed of a plurality of slits a parallel to each other, a second slit group B composed of a plurality of slits b parallel to each other, and a third slit group C composed of a plurality of slits c parallel to each other are sequentially arranged. Agricultural multi-film to prepare
The slit a forming the first slit group A and the slit b forming the second slit group B are not parallel to each other, and the second slit group B side edge a2 of the slit a and the second slit b. The distance d1 from the one slit group A side edge b1 is 0.2 mm ≦ d1 ≦ 15 mm.
The slit b forming the second slit group B and the slit c forming the third slit group C are not parallel to each other, and the third slit group side edge b2 of the slit b and the second slit c. A multi-film for agriculture, wherein the distance d2 from the slit group B side edge c1 is 0.2 mm ≦ d2 ≦ 15 mm.