JP2020041344A - tatami - Google Patents
tatami Download PDFInfo
- Publication number
- JP2020041344A JP2020041344A JP2018170110A JP2018170110A JP2020041344A JP 2020041344 A JP2020041344 A JP 2020041344A JP 2018170110 A JP2018170110 A JP 2018170110A JP 2018170110 A JP2018170110 A JP 2018170110A JP 2020041344 A JP2020041344 A JP 2020041344A
- Authority
- JP
- Japan
- Prior art keywords
- tatami
- tatami mat
- cushion
- cushion material
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、畳に関し、特に複数の板状部材を積層してなる畳に関する。 The present invention relates to a tatami mat, and more particularly to a tatami mat formed by stacking a plurality of plate members.
従来、複数の板状部材を積層してなる畳が知られている（例えば、特許文献１〜５）。 2. Description of the Related Art Conventionally, tatami mats formed by stacking a plurality of plate members are known (for example, Patent Documents 1 to 5).
従来の畳は、複数の板状部材を積層することで、クッション性と圧縮強度を確保している。以下、特許文献１〜５の特徴を示す。
（１）特許文献１に示す畳床は、芯材（Ａ）と畳表（Ｃ）の間にクッションシート（Ｂ）が設けられる。
（２）特許文献２に示す防炎防水畳１は、プラスチックダンボール２と防炎防水畳表６の間にクッション材４が設けられる。
（３）特許文献３に示す畳は、床基材１２と畳表２２の間にクッション材１７が設けられる。
（４）特許文献４に示す畳床１は、ハニカム構造ボード５と消臭シート７の間に低発泡ポリプロピレンボード６が設けられる。
（５）特許文献５に示す畳９は、畳芯材１と畳表７の間にクッション層４が設けられる。
この様に特許文献１〜５に示す畳は、芯材と畳表の間に１種類のクッション材が設けられる構成であるため、クッション材の材質や厚みのみを工夫することで使用者が心地良いと感じるクッション性を実現しなければならないという問題があった。
Conventional tatami mats ensure cushioning and compressive strength by laminating a plurality of plate members. Hereinafter, features of Patent Documents 1 to 5 will be described.
(1) In the tatami floor disclosed in Patent Document 1, a cushion sheet (B) is provided between a core material (A) and a tatami mat (C).
(2) In the flameproof and waterproof tatami mat 1 shown in Patent Document 2, a cushion material 4 is provided between the plastic cardboard 2 and the flameproof and waterproof tatami mat 6.
(3) In the tatami disclosed in Patent Document 3, a cushion material 17 is provided between the floor base material 12 and the tatami mat table 22.
(4) In the tatami floor 1 disclosed in Patent Document 4, a low-foam polypropylene board 6 is provided between a honeycomb structure board 5 and a deodorant sheet 7.
(5) In the tatami 9 shown in Patent Document 5, the cushion layer 4 is provided between the tatami mat core 1 and the tatami mat 7.
As described above, the tatami disclosed in Patent Literatures 1 to 5 has a configuration in which one kind of cushion material is provided between the core material and the tatami mat surface. Therefore, the user is comfortable by devising only the material and thickness of the cushion material. There was a problem that it was necessary to realize the cushioning property that felt.
本発明の目的は、使用者が心地良いと感じるクッション性を実現した畳を提供することである。 An object of the present invention is to provide a tatami mat that realizes cushioning properties that a user feels comfortable.
上記目的は、複数の板状部材を積層してなる畳（１０）であって、
前記複数の板状部材の中で最も硬い芯材（１）と該芯材よりも柔らかい第一のクッション材（２ａ）と該芯材よりも柔らかい第二のクッション材（２ｂ）と畳表シート（４ａ）を有し、
上から下に向けて、前記畳表シート（４ａ）、前記第一のクッション材（２ａ）、前記第二のクッション材（２ｂ）、前記芯材（１）の順番に積層される、畳（１０）によって達成される。
The above object is a tatami (10) formed by stacking a plurality of plate members,
Among the plurality of plate members, the hardest core material (1), a first cushion material (2a) softer than the core material, a second cushion material (2b) softer than the core material, and a tatami mat sheet ( 4a),
From top to bottom, the tatami mat (10a) is laminated in the order of the tatami mat sheet (4a), the first cushion material (2a), the second cushion material (2b), and the core material (1). ).
上記目的は、上記の畳（１０）であって、
前記第一のクッション材（２ａ）と前記第二のクッション材（２ｂ）は、硬さが異なる、畳（１０）によっても達成される。
The object is the tatami (10) described above,
The first cushion material (2a) and the second cushion material (2b) are also achieved by a tatami (10) having different hardness.
上記目的は、上記の畳（１０）であって、前記第二のクッション材（２ｂ）は、前記第一のクッション材（２ａ）よりも硬い、畳（１０）によっても達成される。 The above object is also achieved by the tatami mat (10), wherein the second cushion material (2b) is harder than the first cushion material (2a).
上記目的は、上記の畳（１０）であって、前記第一のクッション材（２ａ）の厚みは、前記芯材（１）の厚みよりも厚い、畳（１０）によっても達成される。 The above object is also achieved by the tatami (10) described above, wherein the thickness of the first cushion material (2a) is larger than the thickness of the core material (1).
上記目的は、上記の畳（１０）であって、前記複数の板状部材は、接着剤で固着されている、畳（１０）によっても達成される。 The above object is also achieved by the tatami mat (10), wherein the plurality of plate members are fixed with an adhesive.
本発明によれば、使用者が心地良いと感じるクッション性を実現した畳を提供できる。 ADVANTAGE OF THE INVENTION According to this invention, the tatami mat which realized the cushioning property which a user feels comfortable can be provided.
以下、図１乃至図２を用いて、本発明の実施形態による畳を説明する。なお、以下の全ての図面においては、理解を容易にするため、各構成要素の寸法や比率などは適宜異ならせて図示している。 Hereinafter, a tatami mat according to an embodiment of the present invention will be described with reference to FIGS. In all the drawings, the dimensions, ratios, and the like of each component are appropriately changed for easy understanding.
［第１の実施形態］
図１を用いて、本発明の第１の実施形態による畳１０を説明する。図１は、畳１０の断面図の一部を示している。図１に示すように、畳１０は、上から下に向けて、畳表シート４ａ、クッション材２ａ、２ｂ、芯材１、断熱材３、畳裏シート４ｂの順番に積層されている。なお、これらは接着剤で固着されてもよいし、縫着されてもよい。また、接着剤で固着する場合には、畳表シート４ａ及び畳裏シート４ｂを防水性のある合成樹脂等を用い、かつ畳１０の側面を防水性のある合成樹脂で被う。このようにすることで、畳１０を丸ごと水洗いすることが可能になる。また、縫着により固着する場合は、針穴から水が進入するため、防水性は劣ることになる。また、クッション材２ａ、２ｂ、芯材１、断熱材３は、板状部材で構成される。
[First Embodiment]
A tatami 10 according to a first embodiment of the present invention will be described with reference to FIG. FIG. 1 shows a part of a sectional view of the tatami mat 10. As shown in FIG. 1, the tatami mat 10 is laminated from the top to the bottom in the order of a tatami mat front sheet 4a, cushion materials 2a and 2b, a core material 1, a heat insulating material 3, and a tatami mat back sheet 4b. These may be fixed with an adhesive or sewn. When fixing with an adhesive, the tatami mat front sheet 4a and the tatami mat back sheet 4b are made of a waterproof synthetic resin, and the side surfaces of the tatami mat 10 are covered with a waterproof synthetic resin. This makes it possible to wash the entire tatami 10 with water. Further, in the case of fixing by sewing, water enters through the needle hole, so that the waterproofness is inferior. In addition, the cushion members 2a and 2b, the core member 1, and the heat insulating material 3 are configured by plate members.
畳表シート４ａ及び／または畳裏シート４ｂには、例えば、天然い草を用いた畳表や、麻、木綿、絹等の、食物繊維や動物繊維、若しくは、再生繊維、半合成繊維、合成繊維、またはこれらの繊維のうちのいずれかを配合した繊維を用いてもよい。また、防水性の観点において、畳表シート４ａ及び／または畳裏シート４ｂには、ポリエチレンやポリプロピレン等の合成樹脂シートを用いるのが好適である。本実施形態においては、畳表シート４ａ及び畳裏シート４ｂの厚みを２ｍｍ〜３ｍｍ程度としている。 The tatami mat sheet 4a and / or the tatami mat back sheet 4b include, for example, tatami mats made of natural rush, dietary fibers and animal fibers such as hemp, cotton, and silk, or regenerated fibers, semi-synthetic fibers, synthetic fibers, or Fibers containing any of these fibers may be used. From the viewpoint of waterproofness, it is preferable to use a synthetic resin sheet such as polyethylene or polypropylene for the tatami mat front sheet 4a and / or the tatami mat back sheet 4b. In the present embodiment, the thickness of the tatami mat front sheet 4a and the tatami mat back sheet 4b is about 2 mm to 3 mm.
クッション材２ａは、厚みを芯材１と同等若しくは厚くし、かつ、クッション材２ｂよりも柔らかい材質で構成する。また、クッション材２ａは、例えば、ポリエチレン繊維、ポリプロピレン繊維、ウレタン繊維、ポリアクリル繊維、ポリスチレン樹脂発泡シート、ポリエチレン樹脂発泡シート、ポリプロピレン樹脂発泡体、ウレタン発泡体、ゴム発泡体；クラフト紙、板紙、厚紙、ダンボール等を用いてもよいし、好ましくは、ポリオレフィン発泡体やポリエチレン発泡体を用いるのがよい。また、クッション材２ａの厚みは、クッション材２ｂの厚みよりも薄くするのが好適であるが、クッション材２ｂの厚みと同等あるいは厚くしてもよい。芯材１の厚みを１とした場合にクッション材２ａの厚みを０．５〜３の範囲（好ましくは、０．８〜３の範囲）とし、クッション材２ｂの厚みを０．５〜６の範囲（好ましくは、０．８〜６の範囲）とするのがよい。また、本実施形態においては、クッション材２ａの厚みを１０ｍｍ程度としている。 The cushion material 2a is made of a material which is equal to or thicker than the core material 1 and which is softer than the cushion material 2b. The cushion material 2a is made of, for example, polyethylene fiber, polypropylene fiber, urethane fiber, polyacryl fiber, polystyrene resin foam sheet, polyethylene resin foam sheet, polypropylene resin foam, urethane foam, rubber foam; kraft paper, paperboard, Cardboard, cardboard, or the like may be used, and preferably, a polyolefin foam or a polyethylene foam is used. The thickness of the cushion 2a is preferably smaller than the thickness of the cushion 2b, but may be equal to or greater than the thickness of the cushion 2b. When the thickness of the core material 1 is 1, the thickness of the cushion material 2a is in the range of 0.5 to 3 (preferably in the range of 0.8 to 3), and the thickness of the cushion material 2b is 0.5 to 6. It is good to make it range (preferably, the range of 0.8-6). In the present embodiment, the thickness of the cushion material 2a is set to about 10 mm.
クッション材２ｂは、厚みを芯材１よりも厚くし、かつ、芯材１よりも柔らかい材質で構成する。また、クッション材２ｂは、例えば、ポリエチレン繊維、ポリプロピレン繊維、ウレタン繊維、ポリアクリル繊維、ポリスチレン樹脂発泡体、ポリエチレン樹脂発泡体、ポリプロピレン樹脂発泡体、ウレタン発泡体、ゴム発泡体、クラフト紙、板紙、厚紙、ダンボール等を用いてもよいし、好ましくは、ポリプロピレン発泡体やポリエチレン発泡体を用いるのがよい。また、本実施形態においては、クッション材２ａの厚みを１５ｍｍ程度としている。 The cushion material 2 b is made of a material that is thicker than the core material 1 and is softer than the core material 1. The cushion material 2b is made of, for example, polyethylene fiber, polypropylene fiber, urethane fiber, polyacryl fiber, polystyrene resin foam, polyethylene resin foam, polypropylene resin foam, urethane foam, rubber foam, kraft paper, paperboard, Cardboard, cardboard, or the like may be used, and a polypropylene foam or a polyethylene foam is preferably used. In the present embodiment, the thickness of the cushion material 2a is set to about 15 mm.
芯材１は、表シート４ａ、クッション材２ａ、２ｂ、断熱材３、畳裏シート４ｂのいずれよりも最も硬い材質を用いている。例えば、木質ボード、木質のファイバーボード、グラスファイバーボード、またはウレタン等の樹脂系材料が用いられてもよい。また、芯材１の厚みを薄くすることで、クッション材２ａ、２ｂの厚みの幅が広がるため、使用者が心地良いと感じるクッション性を実現するために、クッション材２ａ、２ｂの選択性（材料の選択性や厚みの選択性）を高めることが可能となる。また、本実施形態においては、心材１に木質のファイバーボードやグラスファイバーボードを用い、厚みを５ｍｍ程度としている。 The core material 1 is made of the hardest material than any of the front sheet 4a, the cushion materials 2a and 2b, the heat insulating material 3, and the tatami back sheet 4b. For example, a resin material such as a wood board, a wood fiber board, a glass fiber board, or urethane may be used. Further, by reducing the thickness of the core 1, the width of the thickness of the cushions 2 a and 2 b is widened, and the selectivity of the cushions 2 a and 2 b ( Material selectivity and thickness selectivity). In the present embodiment, a wood fiber board or a glass fiber board is used as the core 1 and the thickness is about 5 mm.
断熱材３は、断熱性の高い材質で構成される。例えば、ウレタンフォーム、フェノールフォム、ポリスエチレンフォーム等の発泡体が用いられてもよいし、クラフト紙、板紙、厚紙、ダンボール等を用いてもよい。また、芯材１で充分な強度を確保している場合には、重量の軽い発泡体を用いるのが好適である。また、本実施形態においては、断熱材３の厚みを２０ｍｍ程度としている。また、本実施の形態の畳１０は、上記の材料を積層し、全体の厚みが５０ｍｍ程度になるよう圧縮することで構成される。 The heat insulating material 3 is made of a material having high heat insulating properties. For example, foams such as urethane foam, phenol foam, and polyethylene foam may be used, and kraft paper, paperboard, cardboard, cardboard, and the like may be used. If the core material 1 has sufficient strength, it is preferable to use a lightweight foam. In the present embodiment, the thickness of the heat insulating material 3 is set to about 20 mm. Further, the tatami mat 10 of the present embodiment is formed by laminating the above-mentioned materials and compressing them so that the overall thickness becomes about 50 mm.
このように、本実施の形態による畳１０は、芯材１と畳表４ａの間に２種類のクッション材を設けている。２種類のクッション材を設けることで、使用者が心地良いと感じるクッション性の実現が容易になる。例えば、使用者が最初に畳に触れる際の柔らかさを畳表４ａの直下に設けられるクッション材１により実現し、使用者がぐっと押しこんだ時の心地良い反発を芯材１の直上に設けられるクッション材２により実現することができる。なお、本実施の形態の畳１０は、芯材１と畳表４ａの間に２種類のクッション材を設ける構成であるが、３種類以上のクッション材を設ける構成であってもよい。なお、上記の２種類、３種類のクッション材とは、これらのクッション材が同じ材料で構成されても内部形状や外形が異なることで、厚みや硬さや応力が異なる場合には、２種類、３種類のクッション材であるものとする。また、本実施の形態による畳１０は、各層の厚みを薄くすることで、１０ｍｍ〜３０ｍｍ程度の厚みの薄畳として用いてもよいし、断熱材３を設けないことで、１０ｍｍ〜３０ｍｍ程度の厚みの薄畳として用いてもよい。 As described above, the tatami mat 10 according to the present embodiment has two types of cushion members between the core member 1 and the tatami mat table 4a. By providing two types of cushioning materials, it is easy to realize cushioning properties that the user feels comfortable. For example, the softness when the user first touches the tatami mat is realized by the cushion material 1 provided directly below the tatami mat table 4a, and the comfortable rebound when the user pushes the mat is provided directly above the core material 1. This can be realized by the cushion material 2. Although the tatami mat 10 of the present embodiment has a configuration in which two types of cushioning materials are provided between the core material 1 and the tatami mat table 4a, a configuration in which three or more types of cushioning materials are provided may be employed. The above two types and three types of cushioning materials are different in internal shape and outer shape even if these cushioning materials are made of the same material. It is assumed that there are three types of cushion materials. In addition, the tatami 10 according to the present embodiment may be used as a thin tatami mat having a thickness of about 10 mm to 30 mm by reducing the thickness of each layer, or about 10 mm to 30 mm by not providing the heat insulating material 3. It may be used as a thin tatami mat.
以下、本発明の第１の実施形態による畳１０の性能試験の結果を記す。
［歩行時を代表とする各種動作時の床のかたさの能試験］
１Ａ．試験方法
かたさを測定するために研究開発された装置（床のかたさ測定装置）において、重量４０ｋｇの重錘をゴムばねに接触させたまま、落下させたときの床の動的変形挙動を測定するものである。得られる床の動的挙動から、ＵＦ１，ＤＲ，ＴＲを算出して、かたさを表示する物理量ｌｏｇ（ＵＦ１−８×ＤＲ×ＤＲ・１／ＴＲ）を求め、かたさの評価指標より当該試料のかたさを評価するものである。
２Ａ．試験結果
最大変形量（３回平均）：０．６６８［ｃｍ］
ＵＦ１（３回平均）：２５．７４９［ｋｇｆ・ｃｍ］
ＤＲ（３回平均）：０．２４８［ｃｍ］
ＴＲ（３回平均）：０．１３５［ｋｇｆ・ｃｍ］
ｌｏｇ（ＵＦ１−８×ＤＲ×ＤＲ・１／ＴＲ）（３回平均）：１．３４５
［転倒衝突時の床のかたさ試験］（関連規格：ＪＩＳ Ａ ６５１９）
１Ｂ．試験方法
転倒衝突時の床のかたさを測定するために研究開発された装置（転倒衝突時の床のかたさ測定装置）において、人間の頭部に近似したヘッドモデルを高さ２０ｃｍからゴム板を敷いた床上に自由落下させたときに、加速度計（４）に発生する最大加速度（Ｇｓ）により、転倒衝突時の安全性からみた床のかたさを評価するものである。
安全性の観点から、最大加速度は１００Ｇ以下が望ましく、ＪＩＳ Ａ ６５１９では以下のように恕限値を決めている。
体育館床：１００Ｇ以下 柔道場床： ６５Ｇ以下
２Ｂ．試験結果
Ｇｓ（３回平均）：３２．０９（Ｇ）
Hereinafter, the results of the performance test of the tatami mat 10 according to the first embodiment of the present invention will be described.
[Performance test of the hardness of the floor during various movements such as walking]
1A. Test method In a device developed to measure hardness (floor hardness measuring device), the dynamic deformation behavior of a floor when a weight of 40 kg is dropped while being in contact with a rubber spring is measured. Things. From the obtained dynamic behavior of the floor, UF1, DR, TR are calculated, a physical quantity log (UF1-8 × DR × DR · 1 / TR) indicating hardness is obtained, and the hardness of the sample is calculated from the hardness evaluation index. Is evaluated.
2A. Test result Maximum deformation (average of 3 times): 0.668 [cm]
UF1 (average of 3 times): 25.749 [kgf · cm]
DR (average of 3 times): 0.248 [cm]
TR (average of 3 times): 0.135 [kgf · cm]
log (UF1-8 × DR × DR · 1 / TR) (average of 3 times): 1.345
[Hardness test of floor at falling collision] (Related standard: JIS A 6519)
1B. Test method In a device developed to measure the hardness of the floor at the time of a falling collision (a device for measuring the hardness of the floor at the time of a falling collision), a head model approximating a human head is covered with a rubber plate from a height of 20 cm. The maximum hardness (Gs) generated by the accelerometer (4) when freely dropped on the floor is used to evaluate the hardness of the floor from the viewpoint of safety at the time of a fall collision.
From the viewpoint of safety, the maximum acceleration is desirably 100 G or less, and JIS A 6519 determines the limit value as follows.
Gymnasium floor: 100G or less Judo hall floor: 65G or less 2B. Test result Gs (average of 3 times): 32.09 (G)
以上より、本発明の第１の実施形態による畳１０により、優れたクッション性が確認できた。 As described above, the tatami mat 10 according to the first embodiment of the present invention has confirmed excellent cushioning properties.
［第２の実施形態］
図２を用いて、本発明の第２の実施形態による畳２０を説明する。なお、第１の実施形態による畳１０と同じ構成については符号を同一にすることでその説明を省略する場合がある。図２は、畳２０の断面図の一部を示している。図２に示すように、畳２０は、上から下に向けて、畳表シート４ａ、クッション材２ｂ、芯材１、畳裏シート４ｂの順番に積層されている。なお、これらは接着剤で固着されてもよいし、縫着されてもよい。また、接着剤で固着する場合には、畳表シート４ａ及び畳裏シート４ｂを防水性のある合成樹脂等を用い、かつ畳２０の側面を防水性のある合成樹脂で被う。このようにすることで、畳１０を丸ごと水洗いすることが可能になる。
[Second embodiment]
A tatami mat 20 according to a second embodiment of the present invention will be described with reference to FIG. In addition, about the structure same as the tatami 10 by 1st Embodiment, the code | symbol is made the same and the description may be abbreviate | omitted. FIG. 2 shows a part of a cross-sectional view of the tatami mat 20. As shown in FIG. 2, the tatami mats 20 are stacked in the order of a tatami mat front sheet 4a, a cushion material 2b, a core material 1, and a tatami mat back sheet 4b from top to bottom. These may be fixed with an adhesive or sewn. When fixing with an adhesive, the tatami mat front sheet 4a and the tatami mat back sheet 4b are made of a waterproof synthetic resin, and the side surfaces of the tatami mat 20 are covered with a waterproof synthetic resin. This makes it possible to wash the entire tatami 10 with water.
本実施の形態による畳２０は、厚みが１０ｍｍ〜３０ｍｍ程度の薄畳として用いるのが好適である。本実施の形態による畳２０の芯材１は、３〜５ｍｍ程度の厚みを有し、クッション材２ｂは、５ｍｍ〜２０ｍｍ程度の厚みを有する。このように、薄畳であっても、クッション材２ｂの厚みを芯材１の厚みよりも厚くすることで優れたクッション性を実現することが可能となる。 The tatami mat 20 according to the present embodiment is preferably used as a thin tatami mat having a thickness of about 10 mm to 30 mm. The core 1 of the tatami 20 according to the present embodiment has a thickness of about 3 to 5 mm, and the cushion 2b has a thickness of about 5 to 20 mm. As described above, even in the case of a thin tatami mat, it is possible to realize excellent cushioning properties by making the thickness of the cushion material 2b larger than the thickness of the core material 1.
本発明は、和室等の部屋に設けることを目的とした畳以外の畳（例えば、椅子等の家具に用いることを目的とした畳）においても適用できる。また、上述の実施形態は、本発明の好適な一例であるので、技術的に好ましい種々の限定が付されているが、本発明の範囲は、上述の説明によって不当に限定されるものではない。また、上述の実施形態で説明される構成の全てが本発明の必須の構成要件ではない。 The present invention can be applied to tatami mats other than tatami mats intended to be provided in a room such as a Japanese-style room (for example, tatami mats intended to be used for furniture such as chairs). In addition, the above-described embodiment is a preferred example of the present invention, and thus various technically preferable limitations are added. However, the scope of the present invention is not unduly limited by the above description. . Further, all of the configurations described in the above embodiments are not essential configuration requirements of the present invention.
本発明は、畳において広く利用可能である。 The present invention is widely available in tatami.
１０、２０ 畳
１ 芯材
２ａ、２ｂ クッション材
３ 断熱材
４ａ 畳表シート
４ｂ 畳裏シート
10, 20 tatami 1 core material 2a, 2b cushion material 3 heat insulating material 4a tatami front sheet 4b tatami back sheet
Claims (5)
前記複数の板状部材の中で最も硬い芯材と該芯材よりも柔らかい第一のクッション材と該芯材よりも柔らかい第二のクッション材と畳表シートを有し、
上から下に向けて、前記畳表シート、前記第一のクッション材、前記第二のクッション材、前記芯材の順番に積層される、畳。 A tatami mat formed by laminating a plurality of plate members,
Among the plurality of plate-like members, a hardest core material, a first cushion material softer than the core material, a second cushion material softer than the core material, and a tatami mat sheet,
A tatami mat which is laminated from the top to the bottom in the order of the tatami front sheet, the first cushion material, the second cushion material, and the core material.
前記第一のクッション材の厚みは、前記芯材の厚みよりも厚い、畳。 The tatami mat according to any one of claims 1 to 3,
The tatami mat, wherein the thickness of the first cushion material is greater than the thickness of the core material.
前記複数の板状部材は、接着剤で固着されている、畳。 The tatami mat according to any one of claims 1 to 4,
The tatami mat, wherein the plurality of plate members are fixed with an adhesive.