JP2019175855A - Carbon nanotube coated wire - Google Patents
Carbon nanotube coated wire Download PDFInfo
- Publication number
- JP2019175855A JP2019175855A JP2019093093A JP2019093093A JP2019175855A JP 2019175855 A JP2019175855 A JP 2019175855A JP 2019093093 A JP2019093093 A JP 2019093093A JP 2019093093 A JP2019093093 A JP 2019093093A JP 2019175855 A JP2019175855 A JP 2019175855A
- Authority
- JP
- Japan
- Prior art keywords
- wire
- cnt
- carbon nanotube
- coating layer
- insulating coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、複数のカーボンナノチューブで構成されるカーボンナノチューブ線材を絶縁材料で被覆したカーボンナノチューブ被覆電線に関するものである。 The present invention relates to a carbon nanotube-coated electric wire in which a carbon nanotube wire composed of a plurality of carbon nanotubes is coated with an insulating material.
カーボンナノチューブ（以下、「ＣＮＴ」ということがある。）は、様々な特性を有する素材であり、多くの分野への応用が期待されている。 Carbon nanotubes (hereinafter sometimes referred to as “CNT”) are materials having various properties, and are expected to be applied in many fields.
例えば、ＣＮＴは、六角形格子の網目構造を有する筒状体の単層、または略同軸で配された多層で構成される３次元網目構造体であり、軽量であると共に、導電性、熱伝導性、機械的強度等の諸特性に優れる。しかし、ＣＮＴを線材化することは容易ではなく、特にメートル単位以上の長いＣＮＴを線材として利用する技術は提案されていない。 For example, the CNT is a single layer of a cylindrical body having a hexagonal lattice network structure, or a three-dimensional network structure composed of multiple layers arranged substantially coaxially, and is lightweight, conductive and thermally conductive. Excellent properties such as properties and mechanical strength. However, it is not easy to turn CNT into a wire, and in particular, no technology has been proposed that uses CNTs longer than a metric unit as a wire.
一方、多層配線構造に形成されるビアホールの埋め込み材料である金属の代替として、ＣＮＴを使用することが検討されている。具体的には、多層配線構造の低抵抗化のために、多層ＣＮＴの成長基点から遠い側の端部へ同心状に伸延した多層ＣＮＴの複数の切り口を導電層にそれぞれ接触させた多層ＣＮＴを、２以上の導線層の層間配線として使用した配線構造が提案されている（特許文献１）。 On the other hand, the use of CNTs as a substitute for metal, which is a filling material for via holes formed in a multilayer wiring structure, has been studied. Specifically, in order to reduce the resistance of the multilayer wiring structure, a multilayer CNT in which a plurality of cut edges of the multilayer CNT concentrically extended to the end far from the growth base point of the multilayer CNT are brought into contact with the conductive layer, respectively. A wiring structure used as an interlayer wiring of two or more conductor layers has been proposed (Patent Document 1).
その他の例として、ＣＮＴ材料の導電性をさらに向上させるために、隣接したＣＮＴ線材の電気的接合点に、金属等からなる導電性堆積物を形成したカーボンナノチューブ材料が提案され、このようなカーボンナノチューブ材料は広汎な用途に適用できることが開示されている（特許文献２）。また、ＣＮＴ線材の有する優れた熱伝導性から、カーボンナノチューブのマトリクスから作られた熱伝導部材を有する加熱器が提案されている（特許文献３）。 As another example, in order to further improve the conductivity of the CNT material, a carbon nanotube material in which a conductive deposit made of metal or the like is formed at an electrical junction of adjacent CNT wires is proposed. It is disclosed that the nanotube material can be applied to a wide range of uses (Patent Document 2). Further, a heater having a heat conducting member made of a carbon nanotube matrix has been proposed due to the excellent heat conductivity of the CNT wire (Patent Document 3).
ところで、自動車や産業機器などの様々な分野における電力線や信号線として、一又は複数の線材からなる芯線と、該芯線を被覆する絶縁被覆とからなる電線が用いられている。芯線を構成する線材の材料としては、通常、電気特性の観点から銅又は銅合金が使用されるが、近年、軽量化の観点からアルミニウム又はアルミニウム合金が提案されている。例えば、アルミニウムの比重は銅の比重の約１／３、アルミニウムの導電率は銅の導電率の約２／３（純銅を１００％ＩＡＣＳの基準とした場合、純アルミニウムは約６６％ＩＡＣＳ）であり、アルミニウム線材に、銅線材と同じ電流を流すためには、アルミニウム線材の断面積を、銅の線材の断面積の約１．５倍と大きくする必要があるが、そのように断面積を大きくしたアルミニウム線材を用いたとしても、アルミニウム線材の質量は、純銅の線材の質量の半分程度であることから、アルミニウム線材を使用することは、軽量化の観点から有利である。 By the way, as a power line and a signal line in various fields such as automobiles and industrial equipment, an electric wire composed of a core wire made of one or a plurality of wires and an insulating coating covering the core wire is used. As the material of the wire constituting the core wire, copper or a copper alloy is usually used from the viewpoint of electrical characteristics, but in recent years, aluminum or an aluminum alloy has been proposed from the viewpoint of weight reduction. For example, the specific gravity of aluminum is about 1/3 of the specific gravity of copper, and the electrical conductivity of aluminum is about 2/3 of the electrical conductivity of copper (pure aluminum is about 66% IACS when pure copper is used as the standard of 100% IACS). Yes, to allow the same current to flow through the aluminum wire as the copper wire, the cross-sectional area of the aluminum wire must be about 1.5 times the cross-sectional area of the copper wire. Even if a large aluminum wire is used, the mass of the aluminum wire is about half of the mass of the pure copper wire, so the use of the aluminum wire is advantageous from the viewpoint of weight reduction.
また、自動車、産業機器等の高性能化・高機能化が進められており、これに伴い、各種電気機器、制御機器などの配設数が増加するとともに、これら機器に使用される電気配線体の配線数と芯線からの発熱も増加する傾向にある。そこで、絶縁被覆による絶縁性を損なうことなく、電線の放熱特性を向上させることが要求されている。また、その一方で、環境対応のために自動車等の移動体の燃費を向上させるため、線材の軽量化も要求されている。 In addition, higher performance and higher functionality of automobiles, industrial equipment, etc. are being promoted. With this increase in the number of various electrical equipment, control equipment, etc., electrical wiring bodies used in these equipment The number of wires and the heat generated from the core wire tend to increase. Therefore, it is required to improve the heat dissipation characteristics of the electric wire without impairing the insulating property by the insulating coating. On the other hand, in order to improve the fuel efficiency of a moving body such as an automobile for environmental reasons, a reduction in the weight of the wire is also required.
本発明は、銅やアルミニウム等からなる線材に匹敵する優れた導電性を有しつつ、軽量化と放熱特性に優れたカーボンナノチューブ被覆電線を提供することを目的とする。 An object of the present invention is to provide a carbon nanotube-coated electric wire that has excellent conductivity comparable to a wire made of copper, aluminum, or the like, and is excellent in weight reduction and heat dissipation characteristics.
本発明の態様は、複数のカーボンナノチューブで構成されるカーボンナノチューブ集合体の単数または複数からなるカーボンナノチューブ線材と、該カーボンナノチューブ線材を被覆する絶縁被覆層と、を備え、前記カーボンナノチューブ線材の径方向の断面積に対する前記絶縁被覆層の径方向の断面積の比率が、０．００１以上１．５以下であるカーボンナノチューブ被覆電線である。 An aspect of the present invention includes a carbon nanotube wire composed of one or a plurality of carbon nanotube aggregates composed of a plurality of carbon nanotubes, and an insulating coating layer that covers the carbon nanotube wire, and the diameter of the carbon nanotube wire The carbon nanotube-coated electric wire has a ratio of a radial sectional area of the insulating coating layer to a sectional area in the direction of 0.001 or more and 1.5 or less.
本発明の態様は、前記カーボンナノチューブ線材の径方向の断面積が、０．０３ｍｍ２以上８０ｍｍ２以下であるカーボンナノチューブ被覆電線である。 Aspect of the present invention, the cross-sectional area of the radial direction of the carbon nanotube wire is a carbon nanotube covered electric wire is 0.03 mm 2 or more 80 mm 2 or less.
本発明の態様は、前記カーボンナノチューブ線材のヤング率に対する前記絶縁被覆層を構成する材料のヤング率の比率が、０．００００１以上０．５以下であるカーボンナノチューブ被覆電線である。 An aspect of the present invention is the carbon nanotube-covered electric wire in which the ratio of the Young's modulus of the material constituting the insulating coating layer to the Young's modulus of the carbon nanotube wire is 0.00001 or more and 0.5 or less.
本発明の態様は、前記カーボンナノチューブ線材のヤング率に対する前記絶縁被覆層を構成する材料のヤング率の比率が、０．０００５以上０．１以下であるカーボンナノチューブ被覆電線である。 An aspect of the present invention is the carbon nanotube-coated electric wire in which the ratio of the Young's modulus of the material constituting the insulating coating layer to the Young's modulus of the carbon nanotube wire is 0.0005 or more and 0.1 or less.
本発明の態様は、前記カーボンナノチューブ線材が、複数の前記カーボンナノチューブ集合体からなり、複数の該カーボンナノチューブ集合体の配向性を示す小角Ｘ線散乱によるアジマスプロットにおけるアジマス角の半値幅Δθが６０°以下であるカーボンナノチューブ被覆電線である。 In an aspect of the present invention, the carbon nanotube wire is composed of a plurality of the carbon nanotube aggregates, and the half width Δθ of the azimuth angle in the azimuth plot by small angle X-ray scattering indicating the orientation of the plurality of carbon nanotube aggregates is 60. It is a carbon nanotube-coated electric wire that is less than or equal to °.
本発明の態様は、複数の前記カーボンナノチューブの密度を示すＸ線散乱による散乱強度の（１０）ピークにおけるピークトップのｑ値が２．０ｎｍ−１以上５．０ｎｍ−１以下であり、且つ半値幅Δｑが０．１ｎｍ−１以上２．０ｎｍ−１以下であるカーボンナノチューブ被覆電線である。 Aspect of the present invention is q value of the peak top in (10) the peak of scattering intensity by X-ray scattering shows a density of the plurality of carbon nanotubes 2.0 nm -1 or 5.0 nm -1 or less, and a half width Δq is a carbon nanotube covered electric wire is 0.1 nm -1 or 2.0 nm -1 or less.
本発明の態様は、前記絶縁被覆層の偏肉率が、５０％以上であるカーボンナノチューブ被覆電線である。 An aspect of the present invention is a carbon nanotube-covered electric wire in which the thickness ratio of the insulating coating layer is 50% or more.
本発明の態様は、前記絶縁被覆層の偏肉率が、８０％以上であるカーボンナノチューブ被覆電線である。 An aspect of the present invention is a carbon nanotube-coated electric wire in which the thickness ratio of the insulating coating layer is 80% or more.
芯線としてカーボンナノチューブを使用したカーボンナノチューブ線材は、金属製の芯線とは異なり、熱伝導に異方性があり、径方向と比較して長手方向に優先的に熱が伝導する。すなわち、カーボンナノチューブ線材には、放熱特性に異方性があるため、金属製の芯線と比較して優れた放熱性を備えている。そのため、カーボンナノチューブを使用した芯線に被覆する絶縁被覆層の設計は、金属製の芯線の絶縁被覆層とは異なる設計とすることが必要になるところ、本発明の態様によれば、カーボンナノチューブ線材の径方向の断面積に対する絶縁被覆層の径方向の断面積の比率が０．００１以上１．５以下であることにより、優れた放熱性を得ることができ、さらに、絶縁被覆層が形成されていても軽量化をすることができる。 Unlike a metal core wire, a carbon nanotube wire using carbon nanotubes as a core wire has anisotropy in heat conduction, and heat is preferentially conducted in the longitudinal direction compared to the radial direction. That is, since the carbon nanotube wire has anisotropy in heat dissipation characteristics, the carbon nanotube wire has excellent heat dissipation compared to a metal core wire. Therefore, the design of the insulating coating layer covering the core wire using carbon nanotubes needs to be different from the design of the insulating coating layer of the metal core wire. According to the aspect of the present invention, the carbon nanotube wire rod When the ratio of the radial cross-sectional area of the insulating coating layer to the radial cross-sectional area is 0.001 or more and 1.5 or less, excellent heat dissipation can be obtained, and further, the insulating coating layer is formed. Even if it is, it can be reduced in weight.
本発明の態様によれば、カーボンナノチューブ線材のヤング率に対する絶縁被覆層を構成する材料のヤング率の比率が０．００００１以上０．５以下であることにより、カーボンナノチューブ被覆電線を繰り返し屈曲させても、カーボンナノチューブ線材から絶縁被覆層が剥離したり、絶縁被覆層に割れが生じることを確実に防止できる。 According to the aspect of the present invention, when the ratio of the Young's modulus of the material constituting the insulating coating layer to the Young's modulus of the carbon nanotube wire is 0.00001 or more and 0.5 or less, the carbon nanotube-coated electric wire is repeatedly bent. In addition, it is possible to reliably prevent the insulating coating layer from peeling from the carbon nanotube wire or cracking in the insulating coating layer.
本発明の態様によれば、カーボンナノチューブ線材におけるカーボンナノチューブ集合体の、小角Ｘ線散乱によるアジマスプロットにおけるアジマス角の半値幅Δθが６０°以下であることにより、カーボンナノチューブ線材においてカーボンナノチューブやカーボンナノチューブ集合体が高い配向性を有するので、カーボンナノチューブ線材の放熱特性がさらに向上する。 According to the aspect of the present invention, the carbon nanotube aggregate in the carbon nanotube wire has a azimuth angle half-value width Δθ in an azimuth plot by small-angle X-ray scattering of 60 ° or less. Since the aggregate has a high orientation, the heat dissipation characteristics of the carbon nanotube wire are further improved.
本発明の態様によれば、配列したカーボンナノチューブのＸ線散乱による散乱強度の（１０）ピークにおけるピークトップのｑ値が２．０ｎｍ−１以上５．０ｎｍ−１以下であり、且つ半値幅Δｑが０．１ｎｍ−１以上２．０ｎｍ−１以下であることにより、カーボンナノチューブが高密度で存在しうるので、カーボンナノチューブ線材の放熱特性がさらに向上する。 According to an aspect of the present invention, q values of the peak top in (10) the peak of scattering intensity by X-ray scattering of aligned carbon nanotubes is at 2.0 nm -1 or 5.0 nm -1 or less, and the half-value width Δq there by is 0.1 nm -1 or 2.0 nm -1 or less, since the carbon nanotubes may be present at a high density, heat radiation properties of the carbon nanotube wire can be further improved.
本発明の態様によれば、絶縁被覆層の偏肉率が５０％以上であることにより、絶縁被覆層の肉厚が均一化されて、カーボンナノチューブ被覆電線の耐摩耗性や屈曲性等の機械的強度がさらに向上する。 According to the aspect of the present invention, the thickness ratio of the insulating coating layer is equalized by 50% or more of the thickness of the insulating coating layer, so that the thickness of the insulating coating layer is uniform, and the carbon nanotube-coated electric wire has a mechanical property such as wear resistance and flexibility. The mechanical strength is further improved.
以下に、本発明の実施形態例に係るカーボンナノチューブ被覆電線について、図面を用いながら説明する。 Below, the carbon nanotube covering electric wire concerning the example of an embodiment of the present invention is explained using a drawing.
図１に示すように、本発明の実施形態例に係るカーボンナノチューブ被覆電線（以下、「ＣＮＴ被覆電線」ということがある。）１は、カーボンナノチューブ線材（以下、「ＣＮＴ線材」ということがある。）１０の外周面に絶縁被覆層２１が被覆された構成となっている。すなわち、ＣＮＴ線材１０の長手方向に沿って絶縁被覆層２１が被覆されている。ＣＮＴ被覆電線１では、ＣＮＴ線材１０の外周面全体が、絶縁被覆層２１によって被覆されている。また、ＣＮＴ被覆電線１では、絶縁被覆層２１はＣＮＴ線材１０の外周面と直接接した態様となっている。図１では、ＣＮＴ線材１０は、１本のＣＮＴ線材１０からなる素線（単線）となっているが、ＣＮＴ線材１０は、複数本のＣＮＴ線材１０を撚り合わせた撚り線の状態でもよい。ＣＮＴ線材１０を撚り線の形態とすることで、ＣＮＴ線材１０の円相当直径や断面積を適宜調節することができる。 As shown in FIG. 1, a carbon nanotube-coated electric wire (hereinafter sometimes referred to as “CNT-coated electric wire”) 1 according to an embodiment of the present invention may be referred to as a carbon nanotube wire (hereinafter referred to as “CNT wire”). .) The outer peripheral surface of 10 is covered with the insulating coating layer 21. That is, the insulating coating layer 21 is coated along the longitudinal direction of the CNT wire 10. In the CNT-coated electric wire 1, the entire outer peripheral surface of the CNT wire 10 is covered with an insulating coating layer 21. Further, in the CNT-coated electric wire 1, the insulating coating layer 21 is in a form in direct contact with the outer peripheral surface of the CNT wire 10. In FIG. 1, the CNT wire 10 is an element wire (single wire) made of one CNT wire 10, but the CNT wire 10 may be in a twisted wire state in which a plurality of CNT wires 10 are twisted together. By making the CNT wire 10 into the form of a stranded wire, the equivalent circle diameter and cross-sectional area of the CNT wire 10 can be adjusted as appropriate.
図２に示すように、ＣＮＴ線材１０は、１層以上の層構造を有する複数のＣＮＴ１１ａ，１１ａ，・・・で構成されるカーボンナノチューブ集合体（以下、「ＣＮＴ集合体」ということがある。）１１の単数から、または複数が束ねられて形成されている。ここで、ＣＮＴ線材とはＣＮＴの割合が９０質量％以上のＣＮＴ線材を意味する。なお、ＣＮＴ線材におけるＣＮＴ割合の算定においては、メッキとドーパントは除かれる。図２では、ＣＮＴ線材１０は、ＣＮＴ集合体１１が、複数、束ねられた構成となっている。ＣＮＴ集合体１１の長手方向が、ＣＮＴ線材１０の長手方向を形成している。従って、ＣＮＴ集合体１１は、線状となっている。ＣＮＴ線材１０における複数のＣＮＴ集合体１１，１１，・・・は、その長軸方向がほぼ揃って配されている。従って、ＣＮＴ線材１０における複数のＣＮＴ集合体１１，１１，・・・は、配向している。素線であるＣＮＴ線材１０の円相当直径は、特に限定されないが、例えば、０．０１ｍｍ以上４．０ｍｍ以下である。また、撚り線としたＣＮＴ線材１０の円相当直径は、特に限定されないが、例えば、０．１ｍｍ以上１５ｍｍ以下である。 As shown in FIG. 2, the CNT wire 10 is sometimes referred to as a carbon nanotube aggregate (hereinafter referred to as “CNT aggregate”) composed of a plurality of CNTs 11 a, 11 a,. ) It is formed from one or a plurality of 11 bundles. Here, the CNT wire means a CNT wire having a CNT ratio of 90% by mass or more. In the calculation of the CNT ratio in the CNT wire, plating and dopant are excluded. In FIG. 2, the CNT wire 10 has a configuration in which a plurality of CNT aggregates 11 are bundled. The longitudinal direction of the CNT aggregate 11 forms the longitudinal direction of the CNT wire 10. Therefore, the CNT aggregate 11 is linear. The plurality of CNT aggregates 11, 11,... In the CNT wire 10 are arranged so that the major axis directions thereof are substantially aligned. Therefore, the plurality of CNT aggregates 11, 11,... In the CNT wire 10 are oriented. Although the circle equivalent diameter of the CNT wire 10 which is a strand is not specifically limited, For example, they are 0.01 mm or more and 4.0 mm or less. Moreover, although the circle equivalent diameter of the CNT wire 10 made into the strand wire is not specifically limited, For example, it is 0.1 mm or more and 15 mm or less.
ＣＮＴ集合体１１は、１層以上の層構造を有するＣＮＴ１１ａの束である。ＣＮＴ１１ａの長手方向が、ＣＮＴ集合体１１の長手方向を形成している。ＣＮＴ集合体１１における複数のＣＮＴ１１ａ，１１ａ，・・・は、その長軸方向がほぼ揃って配されている。従って、ＣＮＴ集合体１１における複数のＣＮＴ１１ａ，１１ａ，・・・は、配向している。ＣＮＴ集合体１１の円相当直径は、例えば、２０ｎｍ以上１０００ｎｍ以下であり、より典型的には、２０ｎｍ以上８０ｎｍ以下である。ＣＮＴ１１ａの最外層の幅寸法は、例えば、１．０ｎｍ以上５．０ｎｍ以下である。 The CNT aggregate 11 is a bundle of CNTs 11a having a layer structure of one or more layers. The longitudinal direction of the CNT 11 a forms the longitudinal direction of the CNT aggregate 11. The plurality of CNTs 11a, 11a,... In the CNT aggregate 11 are arranged so that their major axis directions are substantially aligned. Therefore, the plurality of CNTs 11a, 11a,... In the CNT aggregate 11 are oriented. The equivalent circle diameter of the CNT aggregate 11 is, for example, 20 nm or more and 1000 nm or less, and more typically 20 nm or more and 80 nm or less. The width of the outermost layer of the CNT 11a is, for example, not less than 1.0 nm and not more than 5.0 nm.
ＣＮＴ集合体１１を構成するＣＮＴ１１ａは、単層構造又は複層構造を有する筒状体であり、それぞれ、ＳＷＮＴ（single-walled nanotube）、ＭＷＮＴ（multi-walled nanotube）と呼ばれる。図２では、便宜上、２層構造を有するＣＮＴ１１ａのみを記載しているが、ＣＮＴ集合体１１には、３層構造以上の層構造を有するＣＮＴや単層構造の層構造を有するＣＮＴも含まれていてもよく、３層構造以上の層構造を有するＣＮＴまたは単層構造の層構造を有するＣＮＴから形成されていてもよい。 The CNTs 11a constituting the CNT aggregate 11 are cylindrical bodies having a single-layer structure or a multi-layer structure, and are called SWNT (single-walled nanotube) and MWNT (multi-walled nanotube), respectively. In FIG. 2, only the CNTs 11a having a two-layer structure are shown for convenience, but the CNT aggregate 11 includes CNTs having a layer structure of three or more layers and CNTs having a single-layer structure. It may be formed from CNTs having a layer structure of three or more layers or CNTs having a layer structure of a single layer structure.
２層構造を有するＣＮＴ１１ａでは、六角形格子の網目構造を有する２つの筒状体Ｔ１、Ｔ２が略同軸で配された３次元網目構造体となっており、ＤＷＮＴ（double-walled nanotube）と呼ばれる。構成単位である六角形格子は、その頂点に炭素原子が配された六員環であり、他の六員環と隣接してこれらが連続的に結合している。 The CNT 11a having a two-layer structure is a three-dimensional network structure in which two cylindrical bodies T1 and T2 having a hexagonal lattice network structure are arranged substantially coaxially, which is called DWNT (double-walled nanotube). . The hexagonal lattice, which is a structural unit, is a six-membered ring in which a carbon atom is arranged at the apex, and these are continuously bonded adjacent to another six-membered ring.
ＣＮＴ１１ａの性質は、上記筒状体のカイラリティ（chirality）に依存する。カイラリティは、アームチェア型、ジグザグ型、及びカイラル型に大別され、アームチェア型は金属性、ジグザグ型は半導体性および半金属性、カイラル型は半導体性および半金属性の挙動を示す。従って、ＣＮＴ１１ａの導電性は、筒状体がいずれのカイラリティを有するかによって大きく異なる。ＣＮＴ被覆電線１のＣＮＴ線材１０を構成するＣＮＴ集合体１１では、導電性をさらに向上させる点から、金属性の挙動を示すアームチェア型のＣＮＴ１１ａの割合を増大させることが好ましい。 The properties of the CNT 11a depend on the chirality of the cylindrical body. Chirality is roughly divided into an armchair type, a zigzag type, and a chiral type. The armchair type is metallic, the zigzag type is semiconducting and semimetallic, and the chiral type is semiconducting and semimetallic. Therefore, the conductivity of the CNT 11a varies greatly depending on which chirality the cylindrical body has. In the CNT aggregate 11 constituting the CNT wire 10 of the CNT-covered electric wire 1, it is preferable to increase the ratio of the armchair type CNTs 11a exhibiting metallic behavior from the viewpoint of further improving the conductivity.
一方で、半導体性の挙動を示すカイラル型のＣＮＴ１１ａに電子供与性もしくは電子受容性を持つ物質（異種元素）をドープすることにより、カイラル型のＣＮＴ１１ａが金属性の挙動を示すことが分かっている。また、一般的な金属では、異種元素をドープすることによって金属内部での伝導電子の散乱が起こって導電性が低下するが、これと同様に、金属性の挙動を示すＣＮＴ１１ａに異種元素をドープした場合には、導電性の低下を引き起こす。 On the other hand, it is known that the chiral CNT 11a exhibits a metallic behavior by doping the chiral CNT 11a exhibiting a semiconducting behavior with a substance (a different element) having an electron donating property or an electron accepting property. . In addition, in general metals, doping of different elements causes scattering of conduction electrons inside the metal, resulting in a decrease in conductivity. Similarly, CNTs 11a exhibiting metallic behavior are doped with different elements. In such a case, the conductivity is lowered.
このように、金属性の挙動を示すＣＮＴ１１ａ及び半導体性の挙動を示すＣＮＴ１１ａへのドーピング効果は、導電性の観点からはトレードオフの関係にあることから、理論的には金属性の挙動を示すＣＮＴ１１ａと半導体性の挙動を示すＣＮＴ１１ａとを別個に作製し、半導体性の挙動を示すＣＮＴ１１ａにのみドーピング処理を施した後、これらを組み合わせることが望ましい。金属性の挙動を示すＣＮＴ１１ａと半導体性の挙動を示すＣＮＴ１１ａが混在した状態で作製される場合には、異種元素又は分子によるドーピング処理が効果的となるＣＮＴ１１ａの層構造を選択することが好ましい。これにより、金属性の挙動を示すＣＮＴ１１ａと半導体性の挙動を示すＣＮＴ１１ａの混合物からなるＣＮＴ線材１０の導電性をさらに向上させることができる。 Thus, since the doping effect on the CNT 11a showing the metallic behavior and the CNT 11a showing the semiconductor behavior is in a trade-off relationship from the viewpoint of conductivity, it theoretically shows the metallic behavior. It is desirable that the CNT 11a and the CNT 11a exhibiting the semiconducting behavior are separately manufactured, and only the CNT 11a exhibiting the semiconducting behavior is subjected to the doping treatment and then combined. When the CNTs 11a exhibiting metallic behavior and the CNTs 11a exhibiting semiconducting behavior are mixed, it is preferable to select a layer structure of the CNTs 11a in which doping treatment with different elements or molecules is effective. Thereby, the electroconductivity of the CNT wire 10 which consists of a mixture of CNT11a which shows metallic behavior, and CNT11a which shows semiconducting behavior can be improved further.
例えば、２層構造又は３層構造のような層数が少ないＣＮＴは、それより層数の多いＣＮＴよりも比較的導電性が高く、ドーピング処理を施した際には、２層構造又は３層構造を有するＣＮＴでのドーピング効果が最も高い。従って、ＣＮＴ線材１０の導電性をさらに向上させる点から、２層構造又は３層構造を有するＣＮＴの割合を増大させることが好ましい。具体的には、ＣＮＴ全体に対する２層構造又は３層構造をもつＣＮＴの割合が５０個数％以上が好ましく、７５個数％以上がより好ましい。２層構造又は３層構造をもつＣＮＴの割合は、ＣＮＴ集合体１１の断面を透過型電子顕微鏡（ＴＥＭ）で観察及び解析し、１００個のＣＮＴのそれぞれの層数を測定することで算出することができる。 For example, a CNT with a small number of layers such as a two-layer structure or a three-layer structure has a relatively higher conductivity than a CNT with a larger number of layers, and when subjected to doping treatment, the CNT has a two-layer structure or a three-layer structure. The doping effect in the CNT having a structure is the highest. Therefore, from the viewpoint of further improving the conductivity of the CNT wire 10, it is preferable to increase the proportion of CNTs having a two-layer structure or a three-layer structure. Specifically, the ratio of CNTs having a two-layer structure or a three-layer structure to the entire CNT is preferably 50% by number or more, and more preferably 75% by number or more. The proportion of CNTs having a two-layer structure or a three-layer structure is calculated by observing and analyzing the cross section of the CNT aggregate 11 with a transmission electron microscope (TEM) and measuring the number of layers of 100 CNTs. be able to.
次に、ＣＮＴ線材１０におけるＣＮＴ１１ａ及びＣＮＴ集合体１１の配向性について説明する。 Next, the orientation of the CNT 11a and the CNT aggregate 11 in the CNT wire 10 will be described.
図３（ａ）は、小角Ｘ線散乱（ＳＡＸＳ）による複数のＣＮＴ集合体１１，１１，・・・の散乱ベクトルｑの二次元散乱像の一例を示す図であり、図３（ｂ）は、二次元散乱像において、透過Ｘ線の位置を原点とする任意の散乱ベクトルｑの方位角−散乱強度の関係を示すアジマスプロットの一例を示すグラフである。 3A is a diagram illustrating an example of a two-dimensional scattered image of the scattering vector q of the plurality of CNT aggregates 11, 11,... By small angle X-ray scattering (SAXS), and FIG. In the two-dimensional scattered image, it is a graph showing an example of an azimuth plot showing the relationship between the azimuth angle-scattering intensity of an arbitrary scattering vector q having the transmission X-ray position as the origin.
ＳＡＸＳは、数ｎｍ〜数十ｎｍの大きさの構造等を評価するのに適している。例えば、ＳＡＸＳを用いて、以下の方法でＸ線散乱画像の情報を分析することで、外径が数ｎｍであるＣＮＴ１１ａの配向性及び外径が数十ｎｍであるＣＮＴ集合体１１の配向性を評価することができる。例えば、ＣＮＴ線材１０についてＸ線散乱像を分析すると、図３（ａ）に示すように、ＣＮＴ集合体１１の散乱ベクトルｑ（ｑ＝２π／ｄ、ｄは格子面間隔）のｘ成分であるｑｘよりも、ｙ成分であるｑｙの方が相対的に狭く分布している。また、図３（ａ）と同じＣＮＴ線材１０について、ＳＡＸＳのアジマスプロットを分析した結果、図３（ｂ）に示すアジマスプロットにおけるアジマス角の半値幅Δθは、４８°である。これらの分析結果から、ＣＮＴ線材１０において、複数のＣＮＴ１１ａ，１１ａ，・・・及び複数のＣＮＴ集合体１１，１１，・・・が良好な配向性を有しているといえる。このように、複数のＣＮＴ１１ａ，１１ａ，・・・及び複数のＣＮＴ集合体１１，１１，・・・が良好な配向性を有しているので、ＣＮＴ線材１０の熱は、ＣＮＴ１１ａやＣＮＴ集合体１１の長手方向に沿って円滑に伝達して行きながら放熱されやすくなる。従って、ＣＮＴ線材１０は、上記ＣＮＴ１１ａ及びＣＮＴ集合体１１の配向性を調節することで、放熱ルートを長手方向、径の断面方向にわたり調節できるので、金属製の芯線と比較して優れた放熱特性を発揮する。なお、配向性とは、ＣＮＴを撚り集めて作製した撚り線の長手方向へのベクトルＶに対する内部のＣＮＴ及びＣＮＴ集合体のベクトルの角度差のことを指す。 SAXS is suitable for evaluating a structure having a size of several nanometers to several tens of nanometers. For example, by using SAXS and analyzing the information of the X-ray scattering image by the following method, the orientation of the CNT 11a having an outer diameter of several nanometers and the orientation of the CNT aggregate 11 having an outer diameter of several tens of nanometers Can be evaluated. For example, when an X-ray scattering image is analyzed for the CNT wire 10, as shown in FIG. 3A, it is an x component of the scattering vector q (q = 2π / d, d is the lattice spacing) of the CNT aggregate 11. The y component q y is distributed relatively narrower than q x . As a result of analyzing the SAXS azimuth plot for the same CNT wire 10 as in FIG. 3A, the half-value width Δθ of the azimuth angle in the azimuth plot shown in FIG. 3B is 48 °. From these analysis results, in the CNT wire 10, it can be said that the plurality of CNTs 11a, 11a,... And the plurality of CNT aggregates 11, 11,. As described above, since the plurality of CNTs 11a, 11a,... And the plurality of CNT aggregates 11, 11,. It becomes easy to radiate heat while smoothly transmitting along the longitudinal direction of 11. Therefore, the CNT wire 10 can adjust the heat radiation route in the longitudinal direction and the cross-sectional direction of the diameter by adjusting the orientation of the CNT 11a and the CNT aggregate 11, so that it has excellent heat dissipation characteristics compared to the metal core wire. Demonstrate. The orientation refers to the angle difference between the internal CNT and the CNT aggregate vector with respect to the vector V in the longitudinal direction of the stranded wire produced by twisting together the CNTs.
複数のＣＮＴ集合体１１，１１，・・・の配向性を示す小角Ｘ線散乱（ＳＡＸＳ）のアジマスプロットにおけるアジマス角の半値幅Δθにより示される一定以上の配向性を得ることで、ＣＮＴ線材１０の放熱特性をより向上させる点から、アジマス角の半値幅Δθは６０°以下が好ましく、５０°以下が特に好ましい。 The CNT wire 10 is obtained by obtaining an orientation greater than a certain value indicated by the half-value width Δθ of the azimuth angle in the azimuth plot of small angle X-ray scattering (SAXS) indicating the orientation of the plurality of CNT aggregates 11, 11,. In view of further improving the heat radiation characteristics, the half width Δθ of the azimuth angle is preferably 60 ° or less, and particularly preferably 50 ° or less.
次に、ＣＮＴ集合体１１を構成する複数のＣＮＴ１１ａの配列構造及び密度について説明する。 Next, the arrangement structure and density of the plurality of CNTs 11a constituting the CNT aggregate 11 will be described.
図４は、ＣＮＴ集合体１１を構成する複数のＣＮＴ１１ａ，１１ａ，・・・のＷＡＸＳ（広角Ｘ線散乱）によるｑ値−強度の関係を示すグラフである。 FIG. 4 is a graph showing a q value-intensity relationship by WAXS (wide angle X-ray scattering) of a plurality of CNTs 11a, 11a,... Constituting the CNT aggregate 11.
ＷＡＸＳは、数ｎｍ以下の大きさの物質の構造等を評価するのに適している。例えば、ＷＡＸＳを用いて、以下の方法でＸ線散乱画像の情報を分析することで、外径が数ｎｍ以下であるＣＮＴ１１ａの密度を評価することができる。任意の１つのＣＮＴ集合体１１について散乱ベクトルｑと強度の関係を分析した結果、図４に示すように、ｑ＝３．０ｎｍ−１〜４．０ｎｍ−１付近に見られる（１０）ピークのピークトップのｑ値から見積られる格子定数の値が測定される。この格子定数の測定値とラマン分光法やＴＥＭなどで観測されるＣＮＴ集合体の直径とに基づいて、ＣＮＴ１１ａ，１１ａ，・・・が平面視で六方最密充填構造を形成していることを確認することができる。従って、ＣＮＴ線材１０内で複数のＣＮＴ集合体の直径分布が狭く、複数のＣＮＴ１１ａ，１１ａ，・・・が、規則正しく配列、すなわち、高密度を有することで、六方最密充填構造を形成して高密度で存在しているといえる。このように、複数のＣＮＴ集合体１１，１１，・・・が良好な配向性を有していると共に、更に、ＣＮＴ集合体１１を構成する複数のＣＮＴ１１ａ，１１ａ，・・・が規則正しく配列して高密度で配置されているので、ＣＮＴ線材１０の熱は、ＣＮＴ集合体１１の長手方向に沿って円滑に伝達して行きながら放熱されやすくなる。従って、ＣＮＴ線材１０は、上記ＣＮＴ集合体１１とＣＮＴ１１ａの配列構造や密度を調節することで、放熱ルートを長手方向、径の断面方向にわたり調節できるので、金属製の芯線と比較して優れた放熱特性を発揮する。 WAXS is suitable for evaluating the structure of a substance having a size of several nm or less. For example, using WAXS, the density of the CNT 11a having an outer diameter of several nm or less can be evaluated by analyzing information of the X-ray scattering image by the following method. Any one CNT aggregate 11 Analysis of the relationship between the scattering vector q and strength for, as shown in FIG. 4, observed around q = 3.0nm -1 ~4.0nm -1 (10 ) of the peak The value of the lattice constant estimated from the q value of the peak top is measured. Based on the measured value of the lattice constant and the diameter of the CNT aggregate observed by Raman spectroscopy or TEM, the CNTs 11a, 11a,... Form a hexagonal close-packed structure in plan view. Can be confirmed. Accordingly, the diameter distribution of the plurality of CNT aggregates in the CNT wire 10 is narrow, and the plurality of CNTs 11a, 11a,... Are regularly arranged, that is, having a high density, thereby forming a hexagonal close-packed packing structure. It can be said that it exists at high density. As described above, the plurality of CNT aggregates 11, 11,... Have good orientation, and the plurality of CNTs 11a, 11a,. Therefore, the heat of the CNT wire 10 is easily radiated while being smoothly transmitted along the longitudinal direction of the CNT aggregate 11. Therefore, the CNT wire 10 is superior to the metal core wire because the heat dissipation route can be adjusted in the longitudinal direction and the cross-sectional direction of the diameter by adjusting the arrangement structure and density of the CNT aggregate 11 and CNT 11a. Exhibits heat dissipation characteristics.
高密度を得ることで放熱特性をより向上させる点から、複数のＣＮＴ１１ａ，１１ａ，・・・の密度を示すＸ線散乱による強度の（１０）ピークにおけるピークトップのｑ値が２．０ｎｍ−１以上５．０ｎｍ−１以下であり、且つ半値幅Δｑ（ＦＷＨＭ）が０．１ｎｍ−１以上２．０ｎｍ−１以下であることが好ましい。 From the viewpoint of further improving the heat dissipation characteristics by obtaining a high density, multiple CNT11a, 11a, of intensity by X-ray scattering shows a density of ··· (10) q value of the peak top in the peak 2.0 nm -1 above 5.0 nm -1 or less, and is preferably a half-value width [Delta] q (FWHM) is 0.1 nm -1 or 2.0 nm -1 or less.
ＣＮＴ集合体１１及びＣＮＴ１１の配向性、並びにＣＮＴ１１ａの配列構造及び密度は、後述する、乾式紡糸、湿式紡糸、液晶紡糸等の紡糸方法と該紡糸方法の紡糸条件とを適宜選択することで調節することができる。 The orientation of the CNT aggregate 11 and the CNT 11 and the arrangement structure and density of the CNTs 11a are adjusted by appropriately selecting a spinning method such as dry spinning, wet spinning, and liquid crystal spinning, which will be described later, and spinning conditions of the spinning method. be able to.
次に、ＣＮＴ線材１０の外面を被覆する絶縁被覆層２１について説明する。 Next, the insulating coating layer 21 that covers the outer surface of the CNT wire 10 will be described.
絶縁被覆層２１の材料としては、芯線として金属を用いた被覆電線の絶縁被覆層に用いる材料を使用することができ、例えば、熱可塑性樹脂、熱硬化性樹脂を挙げることができる。熱可塑性樹脂としては、例えば、ポリテトラフルオロエチレン（ＰＴＦＥ）（ヤング率：０．４ＧＰａ）、ポリエチレン（ヤング率：０．１〜１．０ＧＰａ）、ポリプロピレン（ヤング率：１．１〜１．４ＧＰａ）、ポリアセタール（ヤング率：２．８ＧＰａ）、ポリスチレン（ヤング率：２．８〜３．５ＧＰａ）、ポリカーボネート（ヤング率：２．５ＧＰａ）、ポリアミド（ヤング率：１．１〜２．９ＧＰａ）、ポリ塩化ビニル（ヤング率：２．５〜４．２ＧＰａ）、ポリメチルメタクリレート（ヤング率：３．２ＧＰａ）、ポリウレタン（ヤング率：０．０７〜０．７ＧＰａ）等を挙げることができる。熱硬化性樹脂としては、例えば、ポリイミド（２．１〜２．８ＧＰａ）、フェノール樹脂（５．２〜７．０ＧＰａ）等を挙げることができる。これらは、単独で使用してもよく、２種以上を適宜混合して使用してもよい。絶縁被覆層２１のヤング率は、特に限定されないが、例えば、０．０７ＧＰａ以上７ＧＰａ以下が好ましく、０．０７ＧＰａ以上４ＧＰａ以下が特に好ましい。 As a material of the insulating coating layer 21, a material used for an insulating coating layer of a covered electric wire using a metal as a core wire can be used, and examples thereof include a thermoplastic resin and a thermosetting resin. Examples of the thermoplastic resin include polytetrafluoroethylene (PTFE) (Young's modulus: 0.4 GPa), polyethylene (Young's modulus: 0.1-1.0 GPa), and polypropylene (Young's modulus: 1.1-1.4 GPa). ), Polyacetal (Young's modulus: 2.8 GPa), polystyrene (Young's modulus: 2.8 to 3.5 GPa), polycarbonate (Young's modulus: 2.5 GPa), polyamide (Young's modulus: 1.1 to 2.9 GPa), Examples thereof include polyvinyl chloride (Young's modulus: 2.5 to 4.2 GPa), polymethyl methacrylate (Young's modulus: 3.2 GPa), polyurethane (Young's modulus: 0.07 to 0.7 GPa), and the like. Examples of the thermosetting resin include polyimide (2.1 to 2.8 GPa), phenol resin (5.2 to 7.0 GPa), and the like. These may be used alone, or two or more kinds may be appropriately mixed and used. Although the Young's modulus of the insulating coating layer 21 is not particularly limited, for example, 0.07 GPa or more and 7 GPa or less is preferable, and 0.07 GPa or more and 4 GPa or less is particularly preferable.
絶縁被覆層２１は、図１に示すように、一層としてもよく、これに代えて、二層以上としてもよい。また、必要に応じて、ＣＮＴ線材１０の外面と絶縁被覆層２１との間に、さらに、熱硬化性樹脂の層が設けられていてもよい。 As shown in FIG. 1, the insulating coating layer 21 may be a single layer, or alternatively, two or more layers may be used. Further, a thermosetting resin layer may be further provided between the outer surface of the CNT wire 10 and the insulating coating layer 21 as necessary.
ＣＮＴ被覆電線１では、ＣＮＴ線材１０の径方向の断面積に対する絶縁被覆層２１の径方向の断面積の比率は、０．００１以上１．５以下の範囲である。前記断面積の比率が０．００１以上１．５以下の範囲であることにより、芯線が銅やアルミニウム等と比較して軽量であるＣＮＴ線材１０である上に、絶縁被覆層２１の厚さを薄肉化できることから、絶縁被覆層で被覆された電線を軽量化することができ、また、ＣＮＴ線材１０の熱に対して優れた放熱特性を得ることができる。 In the CNT-coated electric wire 1, the ratio of the radial cross-sectional area of the insulating coating layer 21 to the radial cross-sectional area of the CNT wire 10 is in the range of 0.001 to 1.5. When the ratio of the cross-sectional area is in the range of 0.001 to 1.5, the core wire is a CNT wire 10 that is lighter than copper or aluminum, and the thickness of the insulating coating layer 21 is reduced. Since the thickness can be reduced, the electric wire covered with the insulating coating layer can be reduced in weight, and excellent heat dissipation characteristics can be obtained with respect to the heat of the CNT wire 10.
また、ＣＮＴ線材１０単独では、長手方向における形状維持が難しい場合があるところ、前記断面積の比率にて絶縁被覆層２１がＣＮＴ線材１０の外面に被覆されていることにより、ＣＮＴ被覆電線１は、長手方向における形状を維持することができ、また、曲げ加工等の変形加工も容易である。従って、ＣＮＴ被覆電線１は、所望の配線経路に沿った形状に形成することができる。 In addition, when the shape of the CNT wire 10 alone is difficult to maintain in the longitudinal direction, the insulating coating layer 21 is coated on the outer surface of the CNT wire 10 at the ratio of the cross-sectional area. The shape in the longitudinal direction can be maintained, and deformation processing such as bending is easy. Therefore, the CNT-coated electric wire 1 can be formed in a shape along a desired wiring path.
さらに、ＣＮＴ線材１０は、外面に微細な凹凸が形成されていることから、アルミニウムや銅の芯線を用いた被覆電線と比較して、ＣＮＴ線材１０と絶縁被覆層２１との間の接着性が向上し、ＣＮＴ線材１０と絶縁被覆層２１との間の剥離を抑制することができる。 Furthermore, since the CNT wire 10 has fine irregularities formed on the outer surface, the adhesion between the CNT wire 10 and the insulating coating layer 21 is higher than that of a covered electric wire using an aluminum or copper core wire. And the separation between the CNT wire 10 and the insulating coating layer 21 can be suppressed.
前記断面積の比率は０．００１以上１．５以下の範囲であれば、特に限定されないが、前記断面積の比率の上限値は、ＣＮＴ被覆電線１のさらなる軽量化とＣＮＴ線材１０の熱に対する放熱特性をさらに向上させる点から１．０が好ましく、０．８０がより好ましく、０．２７が特に好ましい。 The cross-sectional area ratio is not particularly limited as long as it is in the range of 0.001 to 1.5, but the upper limit value of the cross-sectional area ratio is further reduced in weight of the CNT-coated electric wire 1 and the heat of the CNT wire 10. 1.0 is preferable from the point which further improves a thermal radiation characteristic, 0.80 is more preferable, 0.27 is especially preferable.
前記断面積の比率が０．００１以上１．５以下の範囲である場合、ＣＮＴ線材１０の径方向の断面積は、特に限定されないが、例えば、０．０００５ｍｍ２以上８０ｍｍ２以下が好ましく、０．０１ｍｍ２以上１０ｍｍ２以下がより好ましく、０．０３ｍｍ２以上６．０ｍｍ２以下が特に好ましい。また、絶縁被覆層２１の径方向の断面積は、特に限定されないが、絶縁信頼性と放熱性とのバランスの観点から、例えば、０．００３ｍｍ２以上４０ｍｍ２以下が好ましく、０．０１５ｍｍ２以上５ｍｍ２以下が特に好ましい。 断面積は、例えば、走査型電子顕微鏡（ＳＥＭ）観察の画像から測定することができる。具体的には、ＣＮＴ被覆電線１の径方向断面のＳＥＭ像（１００倍〜１０，０００倍）を得た後に、ＣＮＴ線材１０の外周で囲われた部分の面積からＣＮＴ線材１０内部に入り込んだ絶縁被覆層２１の材料の面積を差し引いた面積、ＣＮＴ線材１０の外周を被覆する絶縁被覆層２１の部分の面積とＣＮＴ線材１０内部に入り込んだ絶縁被覆層２１の材料の面積との合計を、それぞれ、ＣＮＴ線材１０の径方向の断面積、絶縁被覆層２１の径方向の断面積とする。絶縁被覆層２１の径方向の断面積には、ＣＮＴ線材１０間に入り込んだ樹脂も含む。 If the ratio of the cross-sectional area is in the range of 0.001 to 1.5, the cross-sectional area in the radial direction of the CNT wire 10 is not particularly limited, for example, preferably 0.0005 mm 2 or more 80 mm 2 or less, 0 .01Mm 2 or 10 mm 2 and more preferably less, 0.03 mm 2 or more 6.0 mm 2 or less is particularly preferred. Further, the cross-sectional area in the radial direction of the insulating cover layer 21 is not particularly limited, from the viewpoint of the balance between heat dissipation and insulation reliability, for example, preferably 0.003 mm 2 or more 40 mm 2 or less, 0.015 mm 2 or more 5 mm 2 or less is particularly preferable. The cross-sectional area can be measured from an image observed with a scanning electron microscope (SEM), for example. Specifically, after obtaining an SEM image (100 times to 10,000 times) of the radial cross section of the CNT-coated electric wire 1, it entered the CNT wire 10 from the area surrounded by the outer periphery of the CNT wire 10. The total of the area obtained by subtracting the area of the material of the insulating coating layer 21, the area of the portion of the insulating coating layer 21 that covers the outer periphery of the CNT wire 10, and the area of the material of the insulating coating layer 21 that has entered the CNT wire 10, The cross-sectional area in the radial direction of the CNT wire 10 and the cross-sectional area in the radial direction of the insulating coating layer 21 are used respectively. The radial cross-sectional area of the insulating coating layer 21 includes a resin that has entered between the CNT wires 10.
ＣＮＴ線材１０のヤング率は、従来の芯線として使用されるアルミニウムや銅のヤング率よりも高い。アルミニウムのヤング率が７０．３ＧＰａ、銅のヤング率が１２９．８ＧＰａであるのに対し、ＣＮＴ線材１０のヤング率は３００〜１５００ＧＰａと、２倍以上の値を有する。従って、ＣＮＴ被覆電線１では、芯線としてアルミニウムや銅を用いた被覆電線と比較して、絶縁被覆層２１の材料としてヤング率の高い材料（ヤング率の高い熱可塑性樹脂）を使用することができるので、ＣＮＴ被覆電線１の絶縁被覆層２１に優れた耐摩耗性を付与することができ、ひいては、ＣＮＴ被覆電線１は優れた耐久性を発揮する。 The Young's modulus of the CNT wire 10 is higher than the Young's modulus of aluminum or copper used as a conventional core wire. Whereas the Young's modulus of aluminum is 70.3 GPa and the Young's modulus of copper is 129.8 GPa, the Young's modulus of the CNT wire 10 is 300 to 1500 GPa, which is twice or more. Therefore, in the CNT-coated electric wire 1, a material having a high Young's modulus (a thermoplastic resin having a high Young's modulus) can be used as the material of the insulating coating layer 21 as compared with a coated electric wire using aluminum or copper as the core wire. Therefore, it is possible to impart excellent wear resistance to the insulating coating layer 21 of the CNT-coated electric wire 1, and as a result, the CNT-coated electric wire 1 exhibits excellent durability.
上記の通り、ＣＮＴのヤング率は、従来の芯線として使用されるアルミニウムや銅のヤング率よりも高いので、ＣＮＴ被覆電線１では、芯線のヤング率に対する絶縁被覆層を構成する材料のヤング率の比率が、芯線としてアルミニウムや銅を使用した被覆電線の前記ヤング率の比率よりも小さくなる。従って、ＣＮＴ被覆電線１では、芯線としてアルミニウムや銅を使用した被覆電線と比較して、繰り返し屈曲させてもＣＮＴ線材１０と絶縁被覆層２１の剥離や絶縁被覆層２１の割れを抑制できる。 As described above, the Young's modulus of CNT is higher than the Young's modulus of aluminum or copper used as a conventional core wire. Therefore, in the CNT-coated electric wire 1, the Young's modulus of the material constituting the insulating coating layer with respect to the Young's modulus of the core wire is The ratio is smaller than the Young's modulus ratio of the covered electric wire using aluminum or copper as the core wire. Therefore, in the CNT-coated electric wire 1, separation of the CNT wire 10 and the insulating coating layer 21 and cracking of the insulating coating layer 21 can be suppressed even when the CNT-coated electric wire 1 is bent repeatedly as compared with a coated electric wire using aluminum or copper as a core wire.
ＣＮＴ線材１０のヤング率に対する絶縁被覆層２１を構成する材料のヤング率の比率は、特に限定されないが、前記ヤング率の比率の下限値は、ＣＮＴ被覆電線１を繰り返し屈曲させても、ＣＮＴ線材１０に絶縁被覆層２１が追従することでＣＮＴ線材１０から絶縁被覆層２１が剥離するのを防止する点から０．００００１が好ましく、長期にわたりＣＮＴ被覆電線１を屈曲させても、ＣＮＴ線材１０から絶縁被覆層２１が剥離するのを防止する点から０．０００５がより好ましく、０．００１が特に好ましい。一方で、前記ヤング率の比率の上限値は、ＣＮＴ被覆電線１を繰り返し屈曲させても、絶縁被覆層２１に割れが生じるのを防止する点から０．５が好ましく、長期にわたりＣＮＴ被覆電線１を屈曲させても、絶縁被覆層２１に割れが生じるのを防止する点から０．１がより好ましく、０．０１がさらに好ましく、０．００５が特に好ましい。 The ratio of the Young's modulus of the material constituting the insulating coating layer 21 to the Young's modulus of the CNT wire 10 is not particularly limited, but the lower limit of the ratio of the Young's modulus is not limited even if the CNT-coated electric wire 1 is bent repeatedly. 0.00001 is preferable in that the insulation coating layer 21 prevents the insulation coating layer 21 from peeling off from the CNT wire 10 by following the insulation coating layer 21, and even if the CNT-coated electric wire 1 is bent over a long period, From the viewpoint of preventing the insulating coating layer 21 from peeling, 0.0005 is more preferable, and 0.001 is particularly preferable. On the other hand, the upper limit of the Young's modulus ratio is preferably 0.5 from the viewpoint of preventing the insulating coating layer 21 from cracking even when the CNT-coated wire 1 is repeatedly bent. Is preferably 0.1, more preferably 0.01, and particularly preferably 0.005 from the viewpoint of preventing the insulating coating layer 21 from being cracked even if it is bent.
絶縁被覆層２１の長手方向に対し直交方向（すなわち、径方向）の肉厚は、ＣＮＴ被覆電線１の耐摩耗性等の機械的強度を向上させる点から均一化されていることが好ましい。具体的には、絶縁被覆層２１の偏肉率は、例えば、耐摩耗性と屈曲性をより向上させる点から５０％以上が好ましく、８０％以上が特に好ましい。なお、本明細書中、「偏肉率」とは、ＣＮＴ被覆電線１の長手方向中心側の任意の１．０ｍにおいて１０ｃｍごとに、径方向の同一断面について、それぞれ、α＝（絶縁被覆層２１の肉厚の最小値／絶縁被覆層２１の肉厚の最大値）×１００の値を算出し、各断面にて算出したα値を平均した値を意味する。また、絶縁被覆層２１の肉厚は、例えば、ＣＮＴ線材１０を円近似してＳＥＭ観察の画像から測定することができる。ここで、長手方向中心側とは、線の長手方向からみて中心に位置する領域をさす。 The thickness in the direction orthogonal to the longitudinal direction of the insulating coating layer 21 (that is, the radial direction) is preferably uniform from the viewpoint of improving mechanical strength such as wear resistance of the CNT-coated electric wire 1. Specifically, the wall thickness ratio of the insulating coating layer 21 is preferably 50% or more, and particularly preferably 80% or more from the viewpoint of further improving wear resistance and flexibility. In the present specification, the “thickness ratio” refers to α = (insulation coating layer) for the same cross section in the radial direction every 10 cm at an arbitrary 1.0 m on the longitudinal center side of the CNT-coated electric wire 1. 21 is a value obtained by calculating a value of (minimum value of thickness 21 / maximum value of thickness of insulating coating layer 21) × 100 and averaging the α values calculated in each cross section. Further, the thickness of the insulating coating layer 21 can be measured from an image obtained by SEM observation by approximating the CNT wire 10 in a circle, for example. Here, the center side in the longitudinal direction refers to a region located at the center when viewed from the longitudinal direction of the line.
絶縁被覆層２１の偏肉率は、例えば、押出被覆にてＣＮＴ線材１０の外周面に絶縁被覆層２１を形成する場合、押出工程時にダイスへ通すＣＮＴ線材１０の長手方向の張り具合を高めることで向上させることができる。 For example, when the insulating coating layer 21 is formed on the outer peripheral surface of the CNT wire 10 by extrusion coating, the uneven thickness ratio of the insulating coating layer 21 increases the tension in the longitudinal direction of the CNT wire 10 that passes through the die during the extrusion process. Can be improved.
次に、本発明の実施形態例に係るＣＮＴ被覆電線１の製造方法例について説明する。ＣＮＴ被覆電線１は、まず、ＣＮＴ１１ａを製造し、得られた複数のＣＮＴ１１ａからＣＮＴ線材１０を形成し、ＣＮＴ線材１０の外周面に絶縁被覆層２１を被覆することで、製造することができる。また、本発明のＣＮＴ被覆電線１は、ＣＮＴ線材１０に直接絶縁被覆層２１を設けていても、ＣＮＴ線材１０に直接絶縁被覆してから撚り合わせた電線であってもよい。 Next, an example of a method for manufacturing the CNT-covered electric wire 1 according to the embodiment of the present invention will be described. The CNT-covered electric wire 1 can be manufactured by first manufacturing the CNT 11 a, forming the CNT wire 10 from the obtained CNTs 11 a, and covering the outer peripheral surface of the CNT wire 10 with the insulating coating layer 21. In addition, the CNT-coated electric wire 1 of the present invention may be an electric wire in which the insulating coating layer 21 is directly provided on the CNT wire 10 or an electric wire twisted after being directly insulated and coated on the CNT wire 10.
ＣＮＴ１１ａは、浮遊触媒法（特許第5819888号公報）や、基板法（特許第5590603号公報）などの手法で作製することができる。ＣＮＴ線材１０の素線は、乾式紡糸（特許第5819888号公報、特許第5990202号公報、特許第5350635号公報）、湿式紡糸（特許第5135620号公報、特許第5131571号公報、特許第5288359号公報）、液晶紡糸（特表2014-530964号公報）等で作製することができる。 The CNT 11a can be produced by a method such as a floating catalyst method (Japanese Patent No. 5819888) or a substrate method (Japanese Patent No. 5860603). The strands of the CNT wire 10 are dry spinning (Patent No. 5819888, Patent No. 5990202, Patent No. 5350635), wet spinning (Patent No. 5135620, Patent No. 5115771, Patent No. 5288359) ), Liquid crystal spinning (Japanese Patent Publication No. 2014-530964), and the like.
上記のようにして得られたＣＮＴ線材１０の外周面に絶縁被覆層２１を被覆する方法は、アルミニウムや銅の芯線に絶縁被覆層を被覆する方法を使用でき、例えば、絶縁被覆層２１の原料である熱可塑性樹脂を溶融させ、ＣＮＴ線材１０の周りに押し出して被覆する方法を挙げることができる。 As a method of coating the insulating coating layer 21 on the outer peripheral surface of the CNT wire 10 obtained as described above, a method of coating an insulating coating layer on an aluminum or copper core wire can be used. And a method of melting the thermoplastic resin and extruding the CNT wire 10 around the thermoplastic resin.
本発明の実施形態例に係るＣＮＴ被覆電線１は、ワイヤハーネス等の一般電線として使用することができ、また、ＣＮＴ被覆電線１を使用した一般電線からケーブルを作製してもよい。 The CNT-coated electric wire 1 according to the embodiment of the present invention can be used as a general electric wire such as a wire harness, and a cable may be produced from the general electric wire using the CNT-coated electric wire 1.
次に、本発明の実施例を説明するが、本発明の趣旨を超えない限り、下記実施例に限定されるものではない。 Next, examples of the present invention will be described, but the present invention is not limited to the following examples as long as the gist of the present invention is not exceeded.
実施例１〜１３、比較例１〜４について
ＣＮＴ線材の製造方法について
先ず、浮遊触媒法で作製したＣＮＴを直接紡糸する乾式紡糸方法（特許第5819888号公報）または湿式紡糸する方法（特許第5135620号公報、特許第5131571号公報、特許第5288359号公報）で円相当直径０．２ｍｍのＣＮＴ線材の素線（単線）を得た。また、円相当直径０．２ｍｍ超のＣＮＴ線材については、円相当直径０．２ｍｍのＣＮＴ線材の本数を調節して適宜撚り合わせる撚り線とすることで得た。
Examples 1 to 13 and Comparative Examples 1 to 4 CNT Wire Manufacturing Method First, a dry spinning method (Patent No. 5819888) for directly spinning CNTs produced by a floating catalyst method or a wet spinning method (Patent No. 5135620). CNT wire rod (single wire) having a circle equivalent diameter of 0.2 mm was obtained. Further, a CNT wire having an equivalent circle diameter of more than 0.2 mm was obtained by adjusting the number of CNT wires having an equivalent circle diameter of 0.2 mm to be appropriately twisted.
ＣＮＴ線材の外面に絶縁被覆層を被覆する方法について
下記ポリウレタンａを用いて、通常の電線製造用押出成形機を用いて導体周囲に押出被覆することにより絶縁被覆層を形成し、下記表１の実施例と比較例で使用するＣＮＴ被覆電線を作製した。
About the method of coat | covering an insulation coating layer on the outer surface of a CNT wire material Using the following polyurethane a, an insulation coating layer is formed by carrying out extrusion coating around a conductor using the normal extruder for electric wire manufacture. CNT-coated electric wires used in Examples and Comparative Examples were produced.
（ａ）ＣＮＴ線材の断面積の測定
ＣＮＴ線材の径方向の断面をイオンミリング装置（日立ハイテクノロジーズ社製ＩＭ４０００）により切り出した後、走査電子顕微鏡（日立ハイテクノロジーズ社製ＳＵ８０２０、倍率：１００〜１０，０００倍）で得られたＳＥＭ像から、ＣＮＴ線材の径方向の断面積を測定した。ＣＮＴ被覆電線の長手方向中心側の任意の１．０ｍにおいて１０ｃｍごとに同様の測定を繰り返し、その平均値をＣＮＴ線材の径方向の断面積とした。なお、ＣＮＴ線材の断面積として、ＣＮＴ線材内部に入り込んだ樹脂は測定に含めなかった。
(A) Measurement of cross-sectional area of CNT wire After cutting a radial cross section of the CNT wire with an ion milling device (IM4000 manufactured by Hitachi High-Technologies Corporation), a scanning electron microscope (SU8020 manufactured by Hitachi High-Technologies Corporation, magnification: 100 to 10) The cross-sectional area in the radial direction of the CNT wire was measured from the SEM image obtained at (1,000 times). The same measurement was repeated every 10 cm at an arbitrary 1.0 m on the longitudinal center side of the CNT-coated electric wire, and the average value was taken as the cross-sectional area in the radial direction of the CNT wire. In addition, as the cross-sectional area of the CNT wire, the resin that entered the CNT wire was not included in the measurement.
（ｂ）絶縁被覆層の断面積の測定
ＣＮＴ線材の径方向の断面をイオンミリング装置（日立ハイテクノロジーズ社製ＩＭ４０００）により切り出した後、走査電子顕微鏡（日立ハイテクノロジーズ社製ＳＵ８０２０、倍率：１００〜１０，０００倍）で得られたＳＥＭ像から、絶縁被覆層の径方向の断面積を測定した。ＣＮＴ被覆電線の長手方向中心側の任意の１．０ｍにおいて１０ｃｍごとに同様の測定を繰り返し、その平均値を絶縁被覆層の径方向の断面積とした。従って、絶縁被覆層の断面積として、ＣＮＴ線材内部に入り込んだ樹脂も測定に含めた。
(B) Measurement of the cross-sectional area of the insulating coating layer After cutting the radial cross section of the CNT wire with an ion milling device (IM4000 manufactured by Hitachi High-Technologies Corporation), a scanning electron microscope (SU8020 manufactured by Hitachi High-Technologies Corporation, magnification: 100 to 100- The cross-sectional area in the radial direction of the insulating coating layer was measured from the SEM image obtained at 10,000 times. The same measurement was repeated every 10 cm at an arbitrary 1.0 m on the center side in the longitudinal direction of the CNT-coated electric wire, and the average value was taken as the cross-sectional area in the radial direction of the insulating coating layer. Therefore, as the cross-sectional area of the insulating coating layer, the resin that entered the CNT wire was also included in the measurement.
（ｃ）ＳＡＸＳによるアジマス角の半値幅Δθの測定
小角Ｘ線散乱装置（Aichi Synchrotoron製）を用いてＸ線散乱測定を行い、得られたアジマスプロットからアジマス角の半値幅Δθを求めた。
(C) Measurement of half width Δθ of azimuth angle by SAXS X-ray scattering measurement was performed using a small angle X-ray scattering device (manufactured by Aichi Synchrotoron), and the half width Δθ of azimuth angle was obtained from the obtained azimuth plot.
（ｄ）ＷＡＸＳによるピークトップのｑ値及び半値幅Δｑの測定
広角Ｘ線散乱装置（Aichi Synchrotoron製）を用いて広角Ｘ線散乱測定を行い、得られたｑ値−強度グラフから、強度の（１０）ピークにおけるピークトップのｑ値及び半値幅Δｑを求めた。
(D) Measurement of peak top q-value and half-value width Δq by WAXS Wide-angle X-ray scattering measurement was performed using a wide-angle X-ray scattering device (manufactured by Aichi Synchrotoron), and from the obtained q-value-intensity graph, intensity ( 10) The peak-top q value and half-value width Δq of the peak were determined.
（ｅ）偏肉率の測定
ＣＮＴ被覆電線の長手方向中心側の任意の１．０ｍにおいて１０ｃｍごとに径方向の同一断面について、それぞれ、α＝（絶縁被覆層の肉厚の最小値／絶縁被覆層の肉厚の最大値）×１００の値を算出し、各断面にて算出したα値を平均した値として測定した。また、絶縁被覆層２１の肉厚は、例えば、円近似したＣＮＴ線材１０の界面と絶縁被覆層２１の最短距離として、ＳＥＭ観察の画像から測定することができる。
(E) Measurement of thickness deviation rate α = (minimum thickness of insulating coating layer / insulating coating) for the same cross section in the radial direction every 10 cm at an arbitrary 1.0 m on the center side in the longitudinal direction of the CNT-coated electric wire The maximum value of the layer thickness) × 100 was calculated, and the α value calculated in each cross section was measured as an average value. Moreover, the thickness of the insulating coating layer 21 can be measured from the image of SEM observation as the shortest distance between the interface of the CNT wire 10 and the insulating coating layer 21 that are circularly approximated, for example.
（ｆ）絶縁被覆層のヤング率／ＣＮＴ線材のヤング率の測定
１．０ｍのＣＮＴ被覆電線の被覆層を剥離させ、分離した被覆およびＣＮＴ線材のそれぞれについて長手方向２０ｃｍごとに５ｃｍを試験片として採取した。ＪＩＳＫ７１６１−１に準拠した方法で引張試験を実施し、分離した被覆のヤング率およびＣＮＴ線材のヤング率を求めた。被覆のヤング率およびＣＮＴ線材のヤング率を平均した値から、上記ヤング率の比を算出した。
(F) Measurement of Young's modulus of insulating coating layer / Young's modulus of CNT wire material The coating layer of a 1.0 m CNT-coated electric wire was peeled off, and 5 cm for each 20 cm in the longitudinal direction was used as a test piece for each of the separated coating and CNT wire material. Collected. A tensile test was performed by a method based on JISK7161-1, and the Young's modulus of the separated coating and the Young's modulus of the CNT wire were obtained. The ratio of the Young's modulus was calculated from the average value of the Young's modulus of the coating and the Young's modulus of the CNT wire.
ＣＮＴ被覆電線の上記各測定の結果について、下記表１に示す。 The results of the above measurements of the CNT-coated wires are shown in Table 1 below.
上記のようにして作製したＣＮＴ被覆電線について、以下の評価を行った。 The following evaluation was performed about the CNT covering electric wire produced as mentioned above.
（１）放熱性
１００ｃｍのＣＮＴ被覆電線の両端に４本の端子を接続し、四端子法で抵抗測定を行った。この際、印加電流は２０００Ａ／ｃｍ２となるように設定し、抵抗値の時間変化を記録した。測定開始時と１０分間経過後の抵抗値を比較し、その増加率を算出した。ＣＮＴ電線は温度に比例して抵抗が増加するため、抵抗の増加率が小さいものほど放熱性に優れると判断することができる。抵抗の増加率が５％未満のものを〇、５％以上１０％未満のものを△、１０％以上のものを×とした。ただし、導体が異なる場合、温度と抵抗増加の相関係数が異なるため、本評価法ではＣＮＴ電線と銅電線等の比較をすることはできないので、芯線が銅である比較例３、６、芯線がアルミニウムである比較例４、５については、放熱性の評価を行わなかった。
(1) Heat dissipation Four terminals were connected to both ends of a 100 cm CNT-coated electric wire, and resistance measurement was performed by a four-terminal method. At this time, the applied current was set to be 2000 A / cm 2, and the change in resistance value with time was recorded. The resistance values after the start of measurement and after 10 minutes were compared, and the increase rate was calculated. Since the resistance of a CNT electric wire increases in proportion to the temperature, it can be determined that the smaller the rate of increase in resistance, the better the heat dissipation. A resistance increase rate of less than 5% is given as ◯, 5% or more and less than 10% as Δ, and 10% or more as x. However, when the conductors are different, the correlation coefficient between the temperature and the resistance increase is different, so that this evaluation method cannot compare the CNT electric wire and the copper electric wire, so Comparative Examples 3 and 6 in which the core wire is copper, the core wire In Comparative Examples 4 and 5 in which is aluminum, the heat dissipation property was not evaluated.
（２）絶縁信頼性
ＪＩＳＣ３２１５−０−１の箇条１３．３に準拠した方法で行った。試験結果が表９に記載されたグレード３を満たすものを◎、グレード２を満たすものを〇、グレード１を満たすものを△、いずれのグレードにも満たないものを×とした。
(2) Insulation reliability The insulation reliability was measured by a method in accordance with clause 13.3 of JISC3215-0-1. The test results satisfying grade 3 listed in Table 9 were marked as ◎, those satisfying grade 2 as ◯, those satisfying grade 1 as Δ, and those not satisfying any grade as x.
上記評価の結果を下記表１に示す。 The results of the evaluation are shown in Table 1 below.
上記表１に示すように、ＣＮＴ線材の径方向の断面積に対する絶縁被覆層の径方向の断面積の比率が、０．００４１以上１．３以下である実施例１〜１３では、 放熱性が良好なＣＮＴ被覆電線が得られた。また、ＣＮＴ線材の径方向の断面積に対する絶縁被覆層の径方向の断面積の比率が、０．０２１以上０．７１以下である実施例１、２、４〜１０では、更に良好な放熱性のＣＮＴ被覆電線が得られた。また、実施例９、１１、１２から、絶縁被覆層の偏肉が低減されたＣＮＴ被覆電線では、放熱性を損なうことなく、さらに優れた絶縁信頼性が得られた。 As shown in Table 1 above, in Examples 1 to 13, in which the ratio of the radial cross-sectional area of the insulating coating layer to the radial cross-sectional area of the CNT wire is 0.0041 or more and 1.3 or less, the heat dissipation is A good CNT-coated electric wire was obtained. In Examples 1, 2, 4 to 10 in which the ratio of the radial cross-sectional area of the insulating coating layer to the radial cross-sectional area of the CNT wire is 0.021 or more and 0.71 or less, even better heat dissipation A CNT-coated electric wire was obtained. Further, from Examples 9, 11, and 12, in the CNT-coated electric wires in which the uneven thickness of the insulating coating layer was reduced, further superior insulation reliability was obtained without impairing heat dissipation.
さらに、実施例１〜１３では、アジマス角の半値幅Δθは、いずれも６０°以下であった。従って、実施例１〜１３のＣＮＴ線材では、ＣＮＴ集合体は優れた配向性を有していた。さらに、実施例１〜１３では、強度の（１０）ピークにおけるピークトップのｑ値は、いずれも２．０ｎｍ−１以上５．０ｎｍ−１以下であり、半値幅Δｑは、いずれも０．１ｎｍ−１以上２．０ｎｍ−１以下であった。従って、実施例１〜１３のＣＮＴ線材では、ＣＮＴも優れた配向性を有していた。 Furthermore, in Examples 1 to 13, the FWHM Δθ of the azimuth angle was 60 ° or less. Therefore, in the CNT wires of Examples 1 to 13, the CNT aggregate had excellent orientation. Further, in Examples 1 to 13, q values of the peak top in (10) peak intensity are both at 2.0 nm -1 or 5.0 nm -1 or less, the half width Δq are all 0.1nm -1 or more and 2.0 nm -1 or less. Therefore, in the CNT wires of Examples 1 to 13, the CNTs also had excellent orientation.
一方で、ＣＮＴ線材の径方向の断面積に対する絶縁被覆層の径方向の断面積の比率が、それぞれ、１．７、２．１である比較例１、２では、放熱性が得られなかった。 On the other hand, in Comparative Examples 1 and 2 in which the ratio of the radial cross-sectional area of the insulating coating layer to the radial cross-sectional area of the CNT wire was 1.7 and 2.1, respectively, heat dissipation was not obtained. .
実施例１、４、７、１４〜２６、比較例５、６について
次に、絶縁被覆層の樹脂種を下記表２のように変更して、ＣＮＴ被覆電線を作製した。
Examples 1, 4, 7, 14 to 26, and Comparative Examples 5 and 6 Next, the resin type of the insulating coating layer was changed as shown in Table 2 below, and CNT-coated wires were produced.
ポリウレタンａ：東特塗料株式会社製ＴＰＵ３０００ＥＡ
ポリウレタンｂ：東特塗料株式会社製ＴＰＵ５２００
ポリイミド：ユニチカ株式会社製Ｕイミド
ポリプロピレン：日本ポリプロ株式会社製ノバテックＰＰ
Polyurethane a: Toku Paint Co., Ltd. TPU3000EA
Polyurethane b: TPU5200 manufactured by Toku Paint Co., Ltd.
Polyimide: Uimide manufactured by Unitika Ltd. Polypropylene: Novatec PP manufactured by Nippon Polypro Co., Ltd.
ＣＮＴ線材の断面積、絶縁被覆層の断面積、偏肉率は、いずれも、実施例１〜１３と同様の方法にて測定した。 The cross-sectional area of the CNT wire, the cross-sectional area of the insulating coating layer, and the wall thickness ratio were all measured by the same method as in Examples 1-13.
上記のようにして作製したＣＮＴ被覆電線について、以下の評価を行った。 The following evaluation was performed about the CNT covering electric wire produced as mentioned above.
（４）耐摩耗性
ＪＩＳＣ３２１６−３の箇条６に準拠した方法で行った。試験結果がＪＩＳＣ３２１５−４の表１に記載されたグレード２を満たすものを〇、グレード１を満たすものを△、いずれのグレードにも満たないものを×とした。
(4) Abrasion resistance It carried out by the method based on Clause 6 of JISC3216-3. A test result satisfying grade 2 described in Table 1 of JISC3215-4 was marked with ◯, a grade satisfying grade 1 was marked with Δ, and a grade not satisfying any grade was marked with x.
（５）屈曲性
ＩＥＣ６０２２７−２に準拠した方法で、１００ｃｍのＣＮＴ被覆電線に荷重５００ｇｆで９０度の屈曲を１０００回行った。その後、軸方向１０ｃｍごとに断面観察を行い、導体と被覆の間に剥離があるかどうかを確認した。剥離がないものを〇、一部剥離したものを△、導体が断線したものを×とした。
(5) Flexibility By a method based on IEC60227-2, a 100-cm CNT-coated electric wire was bent at 90 degrees with a load of 500 gf 1000 times. Thereafter, a cross-section was observed every 10 cm in the axial direction to confirm whether there was any peeling between the conductor and the coating. “No” indicates that there is no peeling, “Δ” indicates that the peeling is partially, and “×” indicates that the conductor is disconnected.
なお、放熱性、絶縁信頼性は、いずれも、実施例１〜１３と同様の評価方法にて評価した。 In addition, both heat dissipation and insulation reliability were evaluated by the same evaluation method as Examples 1-13.
上記評価の結果を下記表２に示す。 The results of the evaluation are shown in Table 2 below.
上記表２に示すように、ＣＮＴ線材の径方向の断面積に対する絶縁被覆層の径方向の断面積の比率が０．０１以上１．５以下の範囲である実施例１、４、７、１４〜２６では、樹脂種が、ポリウレタンａ、ポリウレタンｂ、ポリスチレン、ポリテトラフルオロエチレンのいずれであっても、放熱性、絶縁信頼性ともに良好なＣＮＴ被覆電線が得られた。さらに、実施例１、４、７、１４〜２６では、耐摩耗性と屈曲性にも優れたＣＮＴ被覆電線が得られた。 As shown in Table 2 above, Examples 1, 4, 7, and 14 in which the ratio of the radial cross-sectional area of the insulating coating layer to the radial cross-sectional area of the CNT wire is in the range of 0.01 to 1.5. In ˜26, a CNT-coated electric wire with good heat dissipation and insulation reliability was obtained regardless of whether the resin type was polyurethane a, polyurethane b, polystyrene, or polytetrafluoroethylene. Furthermore, in Examples 1, 4, 7, and 14 to 26, CNT-coated electric wires excellent in wear resistance and flexibility were obtained.
特に、偏肉率が８０％以上まで絶縁被覆層の偏肉の低減された実施例７、１７、２１では、耐摩耗性と屈曲性とをバランスよく向上させることができた。また、実施例１、４、７、１４〜２６から、ＣＮＴ線材のヤング率に対する絶縁被覆層のヤング率の比率が大きくなると、屈曲性が向上する傾向が得られた。 In particular, in Examples 7, 17, and 21 in which the uneven thickness of the insulating coating layer was reduced to 80% or more, the wear resistance and the flexibility could be improved in a balanced manner. Further, from Examples 1, 4, 7, and 14 to 26, when the ratio of the Young's modulus of the insulating coating layer to the Young's modulus of the CNT wire was increased, the tendency to improve the flexibility was obtained.
一方で、比較例５、６から、芯線として金属線を使用すると、屈曲性を得ることができなかった。 On the other hand, from Comparative Examples 5 and 6, when a metal wire was used as the core wire, the flexibility could not be obtained.
１ カーボンナノチューブ被覆電線
１０ カーボンナノチューブ線材
１１ カーボンナノチューブ集合体
１１ａ カーボンナノチューブ
２１ 絶縁被覆層
DESCRIPTION OF SYMBOLS 1 Carbon nanotube covering electric wire 10 Carbon nanotube wire 11 Carbon nanotube aggregate 11a Carbon nanotube 21 Insulation coating layer
Claims (5)
前記カーボンナノチューブ線材の径方向の断面積に対する前記絶縁被覆層の径方向の断面積の比率が、０．００１以上１．０以下、
前記カーボンナノチューブ線材が、複数の前記カーボンナノチューブ集合体からなり、複数の該カーボンナノチューブ集合体の配向性を示す小角Ｘ線散乱によるアジマスプロットにおけるアジマス角の半値幅Δθが６０°以下、
前記カーボンナノチューブ線材の径方向の断面積が、０．０３ｍｍ２以上６．０ｍｍ２以下であるカーボンナノチューブ被覆電線。 A carbon nanotube wire composed of a plurality of carbon nanotube aggregates composed of a plurality of carbon nanotubes, and an insulating coating layer covering the carbon nanotube wire,
The ratio of the radial cross-sectional area of the insulating coating layer to the radial cross-sectional area of the carbon nanotube wire is 0.001 or more and 1.0 or less,
The carbon nanotube wire is composed of a plurality of the carbon nanotube aggregates, and the azimuth angle half-value width Δθ in the azimuth plot by small angle X-ray scattering indicating the orientation of the plurality of carbon nanotube aggregates is 60 ° or less,
Sectional area of the radial direction of the carbon nanotube wire is, 0.03 mm 2 or more 6.0 mm 2 or less is carbon nanotubes coated electric wire.