JP2019076925A - Square steel tube - Google Patents
Square steel tube Download PDFInfo
- Publication number
- JP2019076925A JP2019076925A JP2017205161A JP2017205161A JP2019076925A JP 2019076925 A JP2019076925 A JP 2019076925A JP 2017205161 A JP2017205161 A JP 2017205161A JP 2017205161 A JP2017205161 A JP 2017205161A JP 2019076925 A JP2019076925 A JP 2019076925A
- Authority
- JP
- Japan
- Prior art keywords
- steel pipe
- square steel
- ratio
- less
- material metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、断面矩形の角形鋼管に関するものである。 The present invention relates to a square steel pipe having a rectangular cross section.
近年、断面矩形の角形鋼管が様々な用途で使用されている。様々な角形鋼管の中でも、短辺の長さに対する長辺の長さの割合が大きく、周長に対する板厚の割合が小さく、高平坦度(長辺の凹凸量が−0.16〜0.00mm)及び小S値(板厚±0.5mm)を有する幅広薄形の薄肉管については、例えば下記の特許文献1等に示されているように、ダイスとプラグとを使用した引抜成形により製造されている。S値は、角形鋼管の角部の寸法である(図1参照)。
In recent years, square steel pipes having a rectangular cross section are used in various applications. Among various rectangular steel pipes, the ratio of the long side to the short side is large, the ratio of the plate thickness to the circumferential length is small, and the high flatness (the unevenness of the long side is −0.16 to 0. For a wide thin thin-walled tube with 00 mm) and a small S value (plate thickness ± 0.5 mm), for example, as shown in the following
上記のような従来の角形鋼管は、引抜成形により製造されているので、加工硬化のため素材金属よりも伸びが低下し、素材金属が有していたしなやかさが失われてしまう。 Since the conventional square steel tube as described above is manufactured by pultrusion, its elongation is lower than that of the base metal due to work hardening, and the base metal loses its flexibility.
本発明は、上記のような課題を解決するためになされたものであり、その目的は、素材金属のしなやかさを保つことができる角形鋼管を提供することである。 The present invention has been made to solve the above problems, and an object thereof is to provide a square steel pipe capable of maintaining the flexibility of the material metal.
本発明に係る角形鋼管は、長辺及び短辺を有する断面矩形の角形鋼管であって、短辺の長さに対する長辺の長さの割合が2.0以上かつ4.0以下であり、周長に対する板厚の割合が0.003以上かつ0.016以下であり、素材金属の伸びと等しい伸びを有する。 The rectangular steel pipe according to the present invention is a rectangular steel pipe having a rectangular cross section having a long side and a short side, and the ratio of the long side to the short side is 2.0 or more and 4.0 or less, The ratio of the plate thickness to the circumferential length is 0.003 or more and 0.016 or less, and has an elongation equal to that of the material metal.
本発明の角形鋼管によれば、素材金属の伸びと等しい伸びを有するので、素材金属のしなやかさを保つことができる。 According to the square steel pipe of the present invention, since the elongation is equal to that of the material metal, the flexibility of the material metal can be maintained.
以下、本発明を実施するための形態について、図面を参照して説明する。
実施の形態
図2は、本発明の実施の形態による角形鋼管1の断面図である。図2に示すように、角形鋼管1は、長辺1L及び短辺1Sを有する断面矩形のものである。この角形鋼管1は、短辺1Sの長さLSに対する長辺1Lの長さLLの割合(LL/LS)が2.0以上かつ4.0以下の幅広薄形であるとともに、周長Fに対する板厚Tの割合(T/F)が0.003以上かつ0.016以下の薄肉管とされている。
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
Embodiment FIG. 2 is a cross-sectional view of a
なお、図2は、角形鋼管1の延在方向1Dに直交する面で角形鋼管1を切断した際の角形鋼管1の断面図であり、短辺1S及び長辺1Lの長さLS,LLはその断面において測ることができる。周長Fは、その断面における角形鋼管1の外周面の長さによって定義することができる。板厚Tは、任意の位置の断面、例えば短辺側の平板部等において測定できる。
2 is a cross-sectional view of the
角形鋼管1は、ロールフォーミングにより丸形鋼管を変形させることで製造される。ロールフォーミングでは、丸形鋼管を上下から挟む上下ロール対及び丸形鋼管を左右から挟む左右ロール対をそれぞれ含む複数のロールスタンドにより、丸形鋼管が断面矩形に徐々に変形される。丸形鋼管は、両側を互いに突き合わせるように平板状の素材金属を湾曲させて断面C字状のオープンパイプを形成し、それら両側の突合部分を溶接することで製造される。丸形鋼管の製造とロールフォーミングとを連続的に実施できる。
The
上述の丸形鋼管及び角形鋼管1の製造を通して、素材金属が丸形鋼管及び角形鋼管1の長手方向に実質的に引き伸ばされない。このため、丸形鋼管及び角形鋼管1の製造を通して素材金属に加工硬化が生じることを抑えることができ、角形鋼管1は素材金属の伸びと等しい伸びを有する。
Through the manufacture of the above-described round steel pipe and
素材金属とは、角形鋼管1の製造に用いられたものであり、丸形鋼管を製造する前の平板状のものを指す。素材金属及び角形鋼管1の伸びは、日本工業規格Z2241に規定された金属材料引張試験方法に準拠して測定することができる。角形鋼管1の伸びと素材金属の伸びとが等しいとは、これらの伸びが厳密に等しいことのみならず、実質的に等しいことも含む。これらの伸びが実質的に等しいとは、例えば角形鋼管1の伸びをE1とし、素材金属の伸びをE0としたとき、(E0−E1)/E0が0.10以下であることを意味することができる。
The material metal is used to manufacture the
本発明の良好な伸びを有する角形鋼管は、丸形鋼管の成形後に引抜き成形を行うことなく、かつ、ロール成形機により丸形鋼管から角形鋼管に成形する際に用いる絞り率(外周長の変化率)を調整することで得ることができる。例えば、Zn−Al−Mg系合金めっき(片面めっき付着量:90g/m2)が施された材質SS400の鋼板(板厚:1.2mm)を周長が84mmで、短辺の長さに対する長辺の長さの割合が2.0以上かつ4.0以下で、S値が1.0以上かつ1.5以下の角形鋼管を製造する場合は、絞り率を6%以下に調整すれば(E0−E1)/E0を1.0以下とすることができる。なお、絞り率の調整は、ロール成形機の上下成形ロール対および左右成形ロール対の位置を変更することで行うことができる。 The rectangular steel pipe having a favorable elongation according to the present invention is a drawing ratio (change in outer peripheral length) used when forming a round steel pipe into a rectangular steel pipe with a roll forming machine without performing drawing after forming the round steel pipe. Can be obtained by adjusting the rate. For example, a steel plate (plate thickness: 1.2 mm) of material SS400 to which Zn-Al-Mg-based alloy plating (single-side plating adhesion amount: 90 g / m 2 ) has been applied has a circumferential length of 84 mm and a short side length When manufacturing a rectangular steel pipe with a long side ratio of 2.0 or more and 4.0 or less, and an S value of 1.0 or more and 1.5 or less, adjust the reduction ratio to 6% or less (E 0 -E 1 ) / E 0 can be 1.0 or less. The adjustment of the reduction ratio can be performed by changing the positions of the upper and lower forming roll pair and the left and right forming roll pair of the roll forming machine.
このような角形鋼管では、素材金属の伸びと等しい伸びを有するので、素材金属のしなやかさを保つことができる。 In such a square steel pipe, since it has an elongation equal to the elongation of the material metal, the flexibility of the material metal can be maintained.
1 角形鋼管
1S 短辺
1L 長辺
1D 延在方向
1 Square steel pipe 1S short side 1L
Claims (1)
前記短辺の長さに対する前記長辺の長さの割合が2.0以上かつ4.0以下であり、周長に対する板厚の割合が0.003以上かつ0.016以下であり、素材金属の伸びと等しい伸びを有する、
角形鋼管。 A square steel pipe having a rectangular cross section having a long side and a short side,
The ratio of the length of the long side to the length of the short side is 2.0 or more and 4.0 or less, the ratio of the plate thickness to the circumferential length is 0.003 or more and 0.016 or less, and the material metal Have an elongation equal to
Square steel pipe.