JP2019065435A - Yarn, fabric and textile product - Google Patents

Abstract

To provide a yarn including an ultrafine filament that is excellent in handlability and stretchability and capable of producing a high-grade fabric and a high-grade textile product, to provide a fabric produced using the yarn, and to provide a textile product produced using the yarn or the fabric.SOLUTION: A fabric and a textile product are produced by adding a sizing agent and wax to a yarn including a filament A-1 having a single fiber diameter of 10 to 3,000 nm and a fiber A-2 having a larger single fiber diameter than that of the filament A-1 and using the yarn as needed.SELECTED DRAWING: None

Description

  The present invention is a yarn comprising ultrafine filaments, which is excellent in handleability and stretchability, and is capable of obtaining a high quality fabric or fiber product, and a fabric using the yarn. And a textile product using the yarn or fabric.

  Conventionally, in order to obtain excellent anti-slip performance, wiping performance, and soft texture, a fabric using ultra-fine filaments has been proposed (e.g., Patent Document 1).

  However, in such a fabric, after obtaining a fabric using a sea-island type composite fiber, the sea component of the sea-island type composite fiber is dissolved and removed with alkali, so there is a restriction on equipment and the process becomes complicated. was there. Furthermore, there is a problem that it is difficult to cross weave or cross knit with other fibers that have a weak point in alkali resistance such as wool.

  Further, Patent Document 2 proposes an ultra-fine filament, but when a fabric or fiber product is produced using such an ultra-fine filament, the filament surface is abraded away by a production facility to cause thread breakage and the like. There was a problem that it was inferior to stability and it was not possible to obtain high quality fabrics and fiber products.

  Further, as Patent Document 3, a yarn is proposed which is excellent in handleability and capable of obtaining high-quality fabrics and fiber products by applying a focusing agent to yarns containing ultrafine filaments. However, such yarns have a problem in knitability, and there is still room for improvement in stably producing fabrics and fiber products.

  On the other hand, as socks, various socks such as socks in which the water absorbability is improved by using ultra-fine fibers, socks in which a plate-like material is provided on the sole, and the like have been proposed (for example, patent documents 4 and 5 ).

  However, socks that do not have a plate-like material and prevent slippage between the shoe and the sock by the effect of the component fibers of the sock have not been proposed so far, thus improving wear comfort.

International Publication No. 05/095686 Pamphlet JP, 2012-193476, A JP 2014-210986 A Japanese Utility Model Publication No. 58-7721 JP, 2006-249623, A

  The present invention has been made in view of the above background, and an object thereof is a yarn including ultrafine filaments, which is excellent in handleability and stretchability, and can obtain high quality fabrics and fiber products. It is an object of the present invention to provide a yarn, a fabric using the yarn, and a fiber product using the yarn or the fabric.

  As a result of intensive studies to achieve the above-mentioned problems, the inventors of the present invention have excellent handling and stretchability by applying a bundling agent to yarns containing ultra-fine filaments and fibers whose fiber diameter is larger than the filaments. And it discovers that the thread which can obtain a high grade cloth and textiles is obtained, and came to complete the present invention by repeating and earnestly examining.

  Thus, according to the present invention, "a yarn comprising a filament A-1 having a single fiber diameter of 10 to 3000 nm and a fiber A-2 having a single fiber diameter larger than that of the filament A-1, and A yarn characterized in that a sizing agent and wax are applied.

  At that time, it is preferable that the sizing agent contains a sizing agent and / or an oil agent. It is preferable that the adhesion amount of the sizing agent is 0.1 to 15% by weight with respect to the weight of the yarn, and the adhesion amount of wax is 0.1 to 10% by weight with respect to the weight of the yarn. Moreover, it is preferable that the number of filaments of said filament A-1 contained in a yarn is 500 or more. Moreover, it is preferable that the said filament A-1 is a filament obtained by dissolving and removing the sea component of the sea-island type composite fiber which consists of a sea component and an island component. Further, a filament obtained by dissolving and removing the sea component of the sea-island type composite fiber after combining the sea-island type composite fiber in which the filament A-1 comprises the sea component and the island component with the fiber A-2 Is preferred. Moreover, it is preferable that the said filament A-1 consists of polyester fibers. The fiber A-2 is preferably a crimped fiber having a single fiber diameter of 5 μm or more and an apparent crimp rate of 2% or more. At that time, it is preferable that the crimped fiber is a composite fiber in which two components are bonded in a side-by-side type or an eccentric core-sheath type, or a false twist crimped yarn. Moreover, it is preferable that the total fineness of a yarn exists in the range of 50-1400 dtex. Further, it is preferable that the yarn is subjected to a dyeing process.

Further, according to the present invention, a fabric obtained by using the above-mentioned yarn is provided. At that time, it is preferable that the fabric further include a yarn B containing elastic fibers. It is preferable that weight ratio (A-1 + A-2): B of the total weight of the said filament A-1 and the fiber A-2 and the said thread B exists in the range of 95: 5-30: 70. In addition, the coefficient of friction is preferably in the range of 0.4 to 2.5 on the front surface or the back surface of the fabric.
Further, according to the present invention, there is provided any textile product selected from the group consisting of socks, gloves, supporters, clothes, woven and knitted tapes, and cords obtained using the above-mentioned yarn or fabric. .

  According to the present invention, a yarn comprising ultrafine filaments, which is excellent in handleability and capable of obtaining a high-quality fabric or fiber product, and a fabric comprising the yarn, A textile product comprising the yarn or fabric is obtained.

  Hereinafter, embodiments of the present invention will be described in detail. In the yarn of the present invention (hereinafter sometimes referred to as "yarn A"), a filament A-1 having a single fiber diameter of 10 to 3,000 nm and a fiber A having a single fiber diameter larger than that of the filament A-1 -2 is included.

  Here, in the filament A-1 (hereinafter sometimes referred to as "nanofiber"), the single fiber diameter (diameter of single fiber) is 10 to 3000 nm (preferably 250 to 1500 nm, particularly preferably 400 to 400). It is important to be within the range of 800 nm). If the single fiber diameter is smaller than 10 nm, the fiber strength is unfavorably reduced. On the other hand, when the single fiber diameter is larger than 3000 nm, there is a possibility that the anti-slip performance, the wiping performance, the soft texture and the like may not be obtained, which is not preferable. Here, when the cross-sectional shape of the single fiber is a modified cross-section other than a round cross-section, the diameter of the circumscribed circle is taken as the diameter of the single fiber. The single fiber diameter can be measured by photographing the cross section of the fiber with a transmission electron microscope.

  The number of filaments in the filament A-1 is not particularly limited, but is preferably 500 or more (more preferably 2000 to 60000) in order to obtain anti-slip performance, wiping performance, soft texture and the like.

  The fiber form of the filament A-1 is not particularly limited, and may be a spun yarn or a long fiber (multifilament yarn). In particular, long fibers (multifilament yarns) are preferred. The cross-sectional shape of the single fiber is not particularly limited, and may be a known cross-sectional shape such as round, triangular, flat or hollow. In addition, air processing such as interlacing processing or Taslan (registered trademark) processing or false twist crimp processing may be applied.

  The fiber type of the filament A-1 is preferably polyester fiber, polyphenylene sulfide (PPS) fiber, polyolefin fiber or nylon (Ny) fiber.

  Examples of polyesters that form polyester fibers include polyethylene terephthalate (PET), polytrimethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, and aromatics such as isophthalic acid and metal salt of 5-sulfoisophthalic acid containing these as main repeating units. Aliphatic dicarboxylic acids such as dicarboxylic acids, adipic acid and sebacic acid, hydroxycarboxylic acid condensates such as ε-caprolactone, and copolymers with glycol components such as diethylene glycol, trimethylene glycol, tetramethylene glycol, hexamethylene glycol, etc. preferable. The material may be polyester recycled by material recycling or chemical recycling, or polyethylene terephthalate as described in JP-A-2009-091694, which uses a monomer component obtained by using a biomass, that is, a substance of biological origin as a raw material. Furthermore, polyesters obtained using a catalyst containing a specific phosphorus compound and a titanium compound as described in JP-A-2004-270097 and JP-A-2004-211268 may be used.

  Any polyarylene sulfide resin forming a polyphenylene sulfide (PPS) fiber may be used as long as it belongs to a category called polyarylene sulfide resin. As a polyarylene sulfide resin, as its constituent unit, for example, p-phenylene sulfide unit, m-phenylene sulfide unit, o-phenylene sulfide unit, phenylene sulfide sulfone unit, phenylene sulfide ketone unit, phenylene sulfide ether unit, diphenylene sulfide unit And those containing a substituent-containing phenylene sulfide unit, a branched structure-containing phenylene sulfide unit, and the like. Among them, those containing 70 mol% or more, particularly 90 mol% or more of p-phenylene sulfide units are preferable, and poly (p-phenylene sulfide) is more preferable.

Polyolefin fibers also include polypropylene fibers and polyethylene fibers.
Also, nylon fibers include nylon 6 fibers and nylon 66 fibers.

  In the polymer forming the filament A-1, if necessary, a micropore forming agent, a cationic dye dyeable agent, a coloring inhibitor, a heat stabilizer, a fluorescent whitening agent, as long as the object of the present invention is not impaired. The agent, the matting agent, the coloring agent, the hygroscopic agent, and the inorganic fine particles may be contained alone or in combination of two or more.

  The method for producing the filament A-1 is not particularly limited, and examples thereof include a method of dissolving and removing the sea component of the sea-island composite fiber consisting of the sea component and the island component, an electrospinning method, and a spinning and drawing method of a conventional method. .

  Next, in the fiber A-2, the fiber form is not particularly limited, and may be a spun yarn or a long fiber (multifilament yarn). In particular, long fibers (multifilament yarns) are preferable in order to obtain excellent stretchability. The cross-sectional shape of the single fiber is not particularly limited, and may be a known cross-sectional shape such as round, triangular, flat or hollow. In addition, normal air processing and false twist crimping may be applied.

  Examples of the fiber type of the fiber A-2 include polyester fiber, polyphenylene sulfide (PPS) fiber, polyolefin fiber, nylon (Ny) fiber, cotton, acrylic fiber, rayon, acetate fiber and the like.

  The total fineness and the single fiber fineness of the fiber A-2 are appropriately selected according to the application, and it is preferable that the total fineness 20 to 200 dtex and the single fiber fineness 0.5 to 10.0 dtex. The number of filaments is preferably in the range of 1 to 300. The single fiber diameter is preferably in the range of 5 to 20 μm. If the single fiber diameter is less than 5 μm, the shape retention of the yarn may be impaired. On the contrary, when the diameter of the single fiber is larger than 20 μm, soft texture may not be obtained. Here, when the cross-sectional shape of the single fiber is a modified cross-section other than a round cross-section, the diameter of the circumscribed circle is taken as the diameter of the single fiber. The single fiber diameter can be measured by photographing the cross section of the fiber with a transmission electron microscope as described above.

  Moreover, it is preferable that the said fiber A-2 is a crimped fiber. In particular, a crimped fiber having a single fiber diameter of 5 μm or more (more preferably 5 to 20 μm) and an apparent crimp rate of 2% or more (more preferably 2 to 40%) is preferable. The crimped fiber is preferably a composite fiber in which two components are bonded to a side-by-side type or an eccentric core-sheath type, or a false twist crimped yarn.

  A composite fiber is a composite fiber in which two components are bonded to a side-by-side type or an eccentric core-sheath type. When the yarn of the present invention contains not only the filament A-1 but also such a composite fiber, the composite fiber takes the form of a three-dimensional coil crimp in the heat treatment step, and the yarn is provided with elasticity. As a result, stretchability is also imparted to the fabric.

  Here, as a two component which forms the said composite fiber, the combination of polyester and polyester, the combination of polyester and nylon, etc. are illustrated. More specifically, a combination of polytrimethylene terephthalate and polytrimethylene terephthalate, a combination of polytrimethylene terephthalate and polyethylene terephthalate, a combination of polyethylene terephthalate and polyethylene terephthalate, and the like are preferable. At that time, it is preferable to make the intrinsic viscosities different from one another. Moreover, you may contain additives, such as antioxidant, a ultraviolet absorber, a heat stabilizer, a flame retardant, a titanium oxide, a coloring agent, inactive microparticles | fine-particles.

  The polyester may be material recycled or chemically recycled polyester. Furthermore, polyesters, polylactic acids and stereocomplex polys obtained using a catalyst containing a specific phosphorus compound and titanium compound as described in JP-A-2004-270097 and JP-A-2004-211268. Although lactic acid may be used, an elastic resin such as polyether ester or polyurethane is preferable in the case of further pursuing the anti-slip effect. In the polymer, as necessary, within the range not impairing the object of the present invention, a micropore forming agent, a cationic dye dyeable agent, a coloring inhibitor, a heat stabilizer, a brightening agent, a matting agent, coloring The agent, the hygroscopic agent, and the inorganic fine particles may be contained alone or in combination of two or more.

  The yarn of the present invention comprises the above-mentioned filament A-1 and the above-mentioned fiber A-2. At that time, as the weight ratio of the fiber A-2 contained in the yarn, the weight ratio of the fiber A-2 is 2 to 40 wt. % (More preferably 4 to 30% by weight, particularly preferably 4 to 20% by weight) is preferable.

  In the yarn of the present invention, the method of combining the filament A-1 and the fiber A-2 is not particularly limited, but a composite false twist method, an air mixing method, a combining method, a covering method and the like are preferably exemplified.

  In the yarn of the present invention, in addition to the filaments A-1 and the fibers A-2, for example, elastic fibers such as polyurethane fibers and polyether ester fibers may be further contained.

  The total fineness (the product of the single fiber fineness and the number of filaments) of the yarn of the present invention is preferably in the range of 50 to 1400 dtex (more preferably 65 to 800 dtex, particularly preferably 65 to 400 dtex). If the total fineness is less than 50 dtex, the yarn strength may be reduced. On the other hand, when the total fineness is larger than 1400 dtex, when obtaining a fiber product using yarn, it may be difficult to set the yarn to a manufacturing facility.

  When the yarn of the present invention is subjected to a dyeing process, it is not necessary to dye the fabric, the fiber product, etc. after obtaining a fabric or a textile product using the yarn, which is preferable. Here, in the yarn after dyeing processing, the lightness index is preferably in the range of 10 to 90.

  A sizing agent is applied to the yarn of the present invention. As such a bundling agent, what is necessary is just to have a bundling property which can visually determine that the single yarn is aggregated in a free (non-tensioned) state of the yarn. If no bundling agent is applied, the handleability of the yarn may be reduced, and a high quality fabric or fiber product may not be obtained, which is not preferable.

  Here, at least one of a sizing agent (sometimes referred to as a sizing agent) and an oil agent (sometimes referred to as an oiling agent) in order to obtain excellent bundling properties as a sizing agent. Is preferably included. It may consist of only one of the sizing agent and the oil, or it may consist of both.

  Examples of such a sizing agent include PVA (polyvinyl alcohol), polyacrylic acid ester, polyacrylic acid, polymethacrylic acid ester, polymethacrylic acid, and acrylic type sizing agent such as polymethacrylic acid and so forth.

  On the other hand, as the oil agent, for example, an oil agent as described in JP-A-10-158939, or a lubricating oil (mineral oil) may be used. Among commercially available products, those referred to as corning oil such as "LAN-401" (product name) manufactured by Nicha Chemical Co., Ltd., "Brian C-1840-1" (product name) manufactured by Matsumoto Yushi-Seiyaku Co., Ltd. It is preferably exemplified.

The yarn of the present invention needs to contain wax. By providing the above-described sizing agent and wax to the yarn, slippage of the yarn is improved at the time of twisting yarn, weaving or knitting, and high-quality fabrics and fiber products can be obtained. Examples of such waxes include natural waxes such as carnauba wax, candelilla wax and montan wax, and synthetic waxes such as polyethylene waxes and glycol based glycols such as polyethylene glycol (PEG).
In addition, the sizing agent and the wax may contain a surfactant.

  In the yarn of the present invention, the adhesion amount of the sizing agent is in the range of 0.1 to 15% by weight (preferably 0.1 to 10% by weight) by solid weight with respect to the yarn weight. preferable. If no glue is attached to the surface of the yarn, or if the amount of adhesion is less than 0.1% by weight, the yarn contains ultra-fine filaments, so a fabric or textile product is produced using the yarn. When doing so, fluff etc. may occur and there may be problems with the quality. On the other hand, when the adhesion amount is larger than 15% by weight, the yarn becomes rigid, which may make it difficult to produce a fabric or a fiber product.

  In the yarn of the present invention, the adhesion amount of the wax is preferably in the range of 0.1 to 10% by weight (preferably 0.1 to 5% by weight) based on the solid weight with respect to the yarn weight. When wax does not adhere to the yarn surface, or when the adhesion amount is less than 0.1% by weight, since the yarn contains ultrafine filaments, a fabric or a textile product is produced using the yarn. At the time, a yarn may be caught by a guide of a weaving machine or a knitting machine, and a yarn breakage may occur, resulting in quality problems. On the other hand, when the adhesion amount is larger than 10% by weight, the yarn becomes rigid, which may make it difficult to produce a fabric or a fiber product, or may decrease the color fastness.

  Since the wax adheres to the yarn of the present invention, the slip of the yarn is improved, the friction with the guide of the weaving machine or the knitting machine is reduced, and a high quality fabric and fiber product can be obtained. This is particularly noticeable in weft knitting machines represented by WHOLEGARMENT.

  The yarn of the present invention can be produced, for example, by the following production method. First, a sea-island composite fiber (fiber for filament A-1) formed of a sea component and an island component is prepared. As such a sea-island composite fiber, a sea-island composite fiber multifilament (number of islands 100 to 1500) disclosed in Japanese Patent Application Laid-Open No. 2007-2364 is preferably used.

  That is, as the sea component polymer, polyester, polyamide, polystyrene, polyethylene and the like having a good fiber forming property are preferable. For example, as an alkaline aqueous solution-soluble polymer, polylactic acid, ultrahigh molecular weight polyalkylene oxide condensation polymer, polyethylene glycol compound copolymer polyester, polyethylene glycol compound and 5-sodium sulfonic acid isophthalic acid copolymer polyester It is suitable. Among them, a polyethylene terephthalate copolymer polyester having an intrinsic viscosity of 0.4 to 0.6 obtained by copolymerizing 6 to 12% by mole of 5-sodium sulfoisophthalic acid and 3 to 10% by weight of polyethylene glycol having a molecular weight of 4,000 to 12,000. Is preferred.

  On the other hand, the island component polymer is preferably a polyester such as fiber-forming polyethylene terephthalate, polytrimethylene terephthalate, polybutylene terephthalate, polylactic acid or polyester obtained by copolymerizing the third component. In the polymer, as necessary, within the range not impairing the object of the present invention, a micropore forming agent, a cationic dye dyeable agent, a coloring inhibitor, a heat stabilizer, a brightening agent, a matting agent, coloring The agent, the hygroscopic agent, and the inorganic fine particles may be contained alone or in combination of two or more.

  In the sea-island composite fiber comprising the above sea component polymer and island component polymer, it is preferable that the melt viscosity of the sea component at the time of melt spinning is larger than the melt viscosity of the island component polymer. Further, the diameter of the island component needs to be in the range of 10 to 3000 nm. At this time, if the shape of the island component is not a perfect circle, the diameter of the circumscribed circle is obtained. In the sea-island composite fiber, the sea-island composite weight ratio (sea: island) is preferably in the range of 40:60 to 5:95, and particularly preferably in the range of 30:70 to 10:90.

  Such sea-island composite fiber can be easily manufactured, for example, by the following method. That is, melt spinning is performed using the above-mentioned sea component polymer and island component polymer. As a spinneret used for melt spinning, it is possible to use an arbitrary one such as one having a hollow pin group or a micropore group for forming an island component. The discharged sea-island cross-section composite fiber is solidified by a cooling air, preferably melt spun at 400 to 6000 m / min and wound up. The obtained undrawn yarn is made into a composite fiber (drawn yarn) having desired strength, elongation, and heat shrinkage properties through a separate drawing process, or is taken up by a roller at a constant speed without being wound up once. It may be any method of winding after passing through the stretching step. In this sea-island composite fiber, the single fiber fineness, the number of filaments, and the total fineness are preferably within the ranges of single fiber fineness 0.5 to 10.0 dtex, filament number 5 to 75, and total fineness 30 to 170 dtex, respectively. .

  Then, a yarn is produced using the islands-in-sea type composite fiber, the fiber A-2, and optionally, other fibers (A-3, A-4, ...). Here, a method of arranging the sea-island composite fiber as the outermost layer and arranging other fibers in the middle layer by making the yarn into a three-layer structure so that the sea-island composite fiber is easily exposed to the surface of the yarn; It is preferable to manufacture a core-sheath composite yarn in which the sea-island composite fiber is disposed in the sheath and the fiber A-2 is disposed in the core. At that time, a machine to be used is not limited, and a conventionally known air mixing machine, a false twist crimper or a covering machine may be used. Moreover, when making the obtained composite yarn into fiber products, such as a woven and knitted fabric, you may give twist 500 times / m or less.

  Next, the yarn is treated with an aqueous alkali solution, and the sea component of the sea-island composite fiber is dissolved and removed with an aqueous alkali solution to make the sea-island composite fiber a filament A-1 having a single fiber diameter of 10 to 3000 nm. At that time, as a condition of the alkaline aqueous solution treatment, it is preferable to treat at a temperature of 55 to 98 ° C. using an aqueous solution of NaOH having a concentration of 1 to 4%.

  In addition, the yarn may be subjected to a dyeing process before and / or after the dissolution and removal with the alkaline aqueous solution. In addition, various methods for imparting functions such as conventional brushing treatment, water repellent treatment, UV shielding or antistatic agent, antibacterial agent, deodorant, insect repellent, luminous agent, retroreflecting agent, negative ion generating agent, etc. Processing may be additionally applied.

  A sea component of the sea-island composite fiber is dissolved and removed with an aqueous alkali solution to obtain a yarn containing filaments A-1 and fibers A-2 having a single fiber diameter of 10 to 3000 nm, and a bundling agent is then applied to the yarn. The yarn of the present invention can be obtained by drying if necessary. At this time, a processing machine to be used may be a conventionally known sizing machine without any limitation.

  The step of dissolving and removing the sea component of the sea-island composite fiber with an aqueous alkali solution may be performed before or after combining the sea-island composite fiber with the fiber A-2.

  The yarn thus obtained is a yarn containing ultrafine filaments, and is a yarn excellent in handleability and stretchability and capable of obtaining high-quality fabrics and fiber products.

  Next, the fabric of the present invention is a fabric woven or knitted or braided using the yarn. Such a fabric may be composed of only the yarn (yarn A), but may be composed of the yarn (yarn A) and other yarns. As such another yarn, a yarn containing an elastic fiber (yarn B) is preferable. At that time, the yarn (yarn A) and the yarn B may be combined to be contained in the fabric as a composite yarn, or the yarn (yarn A) and the yarn B may be cross-woven or crossed. It may be knitted and contained in the fabric.

  Here, the yarn B may be composed only of elastic fibers, or may be composed of elastic fibers and non-elastic fibers.

  For example, a core-sheath composite yarn in which elastic fibers are disposed in the core and inelastic fibers are disposed in the sheath may be used. For example, core-sheath type composite yarn called FTY (Filament Twisted Yarn) in which elastic fibers such as polyamide, polyurethane and polyester are arranged in the core and covered with polyester fiber or nylon fiber on the sheath side is more preferable. If the fabric does not contain elastic fibers, the stretchability of the fabric may be reduced, and the comfort as a sock may be reduced. In addition, cotton may be used as the yarn B in order to prevent stuffiness in shoes.

  The total fineness of the yarn B is preferably in the range of 10 to 800 dtex (preferably 20 to 500 dtex). If the total fineness is less than 10 dtex, sufficient stretchability can not be obtained, and there is a possibility that comfort as a sock can not be obtained. When the total fineness exceeds 800 dtex, the stretchability is too large, and there is a possibility that the form as a fabric can not be stably maintained.

  In the present invention, the weight ratio of the total weight of the filament A-1 and the fiber A-2 (the weight of the yarn A) to the yarn B (A-1 + A-2): B is 30:70 to 95. Preferably within the range of 5 :. When the ratio of (A-1 + A-2) is smaller than the above range, there is a possibility that a sufficient antislip effect can not be obtained. On the other hand, when the ratio of the yarn B is smaller than the above range, the stretchability of the woven or knitted fabric is insufficient, and when a sock is obtained using a fabric, the comfort as a sock may be reduced.

  In the above-mentioned textile, it is preferred that the above-mentioned thread A is exposed to both sides of the front and back of a textile. By exposing the yarn A (filament A-1) to the skin, an excellent frictional force with the skin is obtained, so that the socks are less likely to shift, and the wearing comfort is improved. Further, by exposing the yarn A (filament A-1) to the outside air side, an excellent frictional force with a shoe or the like is obtained, it becomes difficult to slip, and the wearing comfort is improved.

  In the above-described fabric, the woven structure and the knitted structure of the fabric are not particularly limited. Examples of the weft knitting structure include Tendon knitting, rubber knitting, double-sided knitting, pearl knitting, tack knitting, float knitting, single-knit knitting, lace knitting, plied knitting and the like. The warp knitting structure is exemplified by single denby knitting, single atlas knitting, double cord knitting, half knitting, half base knitting, satin knitting, half tricot knitting, fleece knitting, jacquard knitting and the like. Examples of the woven fabric include Mihara tissue such as plain weave, twill weave and satin weave, modified tissue, single double weave such as vertical double weave, weft double weave, and vertical velvet. It is not limited to these. The number of layers may be a single layer or a multilayer of two or more layers.

  Moreover, it is preferable that a friction coefficient is 0.4-2.5 (preferably 0.5-2.3) in the surface or back surface of a fabric. If the coefficient of friction is less than 0.4, there is a possibility that a sufficient non-slip can not be obtained. Also, if the coefficient of friction exceeds 2.5, it may be difficult to put on and take off the shoes because the frictional resistance is too large. In addition, a coefficient of friction shall measure a coefficient of static friction by the method of ASTMD1894-95.

  Such a fabric is removed by soaping (refining) to remove the sizing agent and wax attached to the yarn A, and exhibits excellent anti-slip performance, wiping performance, soft texture, stretchability and the like. Furthermore, since it manufactures using said yarn, it is excellent in processability, and is high grade.

  Next, the textile product of the present invention is any textile product selected from the group consisting of socks, gloves, supporters, clothing, woven and knitted tapes, and cords obtained using the above-mentioned yarn A or fabric. is there.

  Moreover, in the sock, it is preferable that the yarn A be disposed on the heel, the sole, part or all of the toes, and the like. The shape of the sock is not particularly limited, and it may be any of men's socks, women's socks, infant socks, pumps-in-type socks called foot covers, and stockings.

  Such fiber products remove the sizing agent and wax attached to the yarn by soaping (refining), and exhibit excellent anti-slip performance, wiping performance, soft texture, stretchability and the like. Furthermore, since it is manufactured using the above-mentioned yarn, it is excellent in the processability at the time of knitting and weaving, and it is high grade.

EXAMPLES The present invention will next be described in detail by way of Examples and Comparative Examples, which should not be construed as limiting the invention thereto. In addition, each measurement item in an Example was measured by the following method.
Melt viscosity
After drying, the polymer is set in an orifice set at the luder melting temperature for spinning and held for 5 minutes, then it is extruded under several levels of load, and the shear rate and the melt viscosity at that time are plotted. By connecting the plots gently, a shear rate-melt viscosity curve was created, and the melt viscosity was observed at a shear rate of 1000 sec-1.
<Dissolution rate>
Take up the yarn at a spinning speed of 1000 to 2000 m / min with a nozzle of 0.3φ-0.6 L x 24 H for each of sea and island components, and further stretch so that the residual elongation is in the range of 30 to 60%. Then, a multifilament having a total fineness of 84 dtex / 24 fil was produced. The weight loss rate was calculated from the dissolution time and the dissolution amount at a bath ratio of 100 at the temperature at which this is to be dissolved in each solvent.
<Single fiber diameter>
After the cloth was photographed with an electron microscope, the single fiber diameter was measured at n number 5 and the average value was determined.
<Actual crimp rate>
Take only crimped fiber A-2 from the yarn and measure the length under a load of 0.222 gr / dtex (L0) and the length after 1 minute with a load of 2 mg / dtex (L1) next Calculated by the equation.
Explicit crimp rate (%) = [(L0−L1) / L0] × 100
<Attachment amount of focusing agent>
About 2 g of the yarn was removed by a rolling mill, completely dried at 105 ° C. for 2 hours, and allowed to cool for 2 hours in a silica gel-containing desiccator. Thereafter, the yarn was treated in an aqueous solution of 98 ° C. to which 4 gr / L of soda ash and 2 gr / L of surfactant and 2 gr / L of tripolyphosphate were added for 1 hour. The treated yarn was completely dried at 105 ° C. for 2 hours, allowed to cool for 2 hours in a silica gel-containing desiccator, and the weight (W2) was measured. From the following formula, it was calculated as the adhesion amount of the sizing agent.
Glue adhesion amount (%) = (W1-W2) / W1 x 100
<Handling of yarns>
The processability at the time of knitting a weft knitted fabric using yarn was evaluated in three levels of "excellent.", "Normal" and "poor are generated and inferior."
Coefficient of friction
The coefficient of static friction was measured by the method of ASTM D1894-95. The value of the coefficient of static friction was taken as the coefficient of friction.

Example 1
Polyethylene terephthalate as an island component (melt viscosity at 280 ° C 1200 poise, content of matting agent: 0% by weight), sea component 6 mol% of 5-sodium sulfoisophthalic acid and 6% by weight of polyethylene glycol having a number average molecular weight of 4000 A sea-island composite undrawn fiber of (polyester ratio (sea / island) = 230), sea: island = 30: 70, number of islands = (polyurethane viscosity 1750 poise at 280 ° C) copolymerized with Were melt spun at a spinning temperature of 280 ° C. and a spinning speed of 1500 m / min and wound up once.

  The obtained undrawn yarn was subjected to roller drawing at a drawing temperature of 80 ° C. and a drawing ratio of 2.5, and then was heat set at 150 ° C. and wound up. The obtained islands-in-sea composite fibers (fibers for filament A-1 and drawn yarns) have a total fineness of 56 dtex / 10 fil, and when the fiber cross section is observed with a transmission electron microscope TEM, the island has a round shape and is an island. The diameter of was 700 nm.

  Side-by-side type composite fiber multifilament (total fineness 56 dtex / 36 fil; single fiber diameter 12 μm, two obtained islands-in-sea type composite fibers and one component constituting single fibers is polytrimethylene terephthalate and the other component is polyethylene terephthalate) Fibers A-2) were aligned with each other to obtain mixed yarns by interlacing.

  Subsequently, in order to remove the sea component of the sea-island type composite fiber contained in the mixed fiber, the weight was decreased by 20% (alkali loss) at 70 ° C. with a 2.0% aqueous NaOH solution. Then, it dye | stained in gray color by the dyeing process of a conventional method.

  Thereafter, PVA (molecular weight 500) 5% sol. And polyacrylate 1% sol. , As wax, PEG 1000 (molecular weight 1000) 2% sol. An aqueous solution containing the above was prepared, and the yarn was continuously immersed in a sizing agent aqueous solution while unwinding the above-mentioned yarn, and then wound while being dried at a temperature of 80.degree.

  The obtained yarn is composed of a filament A-1 having a single fiber diameter of 700 nm and a side-by-side type composite fiber multifilament (fiber A-2) having a single fiber diameter of 12 μm and an apparent crimp rate of 5.2%. The total fineness of the yarn was 157 dtex, the adhesion amount of the sizing agent (pasting agent) was 7.2% by weight, and the adhesion amount of wax was 1% by weight.

  The obtained yarn is used to manufacture a woven fabric having a smooth texture using MACH 2 SIR (14 gauge) manufactured by Shima Seiki Co., Ltd., since the yarn has stretchability and slipperiness. Stabilized knitting was possible, thread breakage due to fluff and the like did not occur, and the handleability was excellent.

  The obtained weft knit was soda ash 4% sol. And surfactant 2% sol. As a result of soaping with an aqueous solution at 60 ° C. containing the above, the sizing agent (pasting agent) and wax were completely removed, and the filament A-1 with a single fiber diameter of 700 nm was exposed, and it was very difficult to slip. The coefficient of friction showed a very high value of 2.2. In addition, no knitting defects such as yarn breakage due to fuzz were observed, and the product was of high quality. Next, a sock was obtained using the weft knit and was of high quality.

Example 2
Two sea-island composite fibers obtained in the same manner as in Example 1 and one polyethylene terephthalate multifilament total fineness of 56 dtex / 48 fil (single fiber diameter 10.5 μm, fiber for fiber A-2) are aligned and composited A composite yarn was obtained by false twist crimping.

  Subsequently, in order to remove the sea component of the sea-island type composite fiber contained in the composite yarn, the weight was decreased by 20% (alkali loss) at 70 ° C. with a 2.0% aqueous NaOH solution. Then, it dye | stained in gray color by the dyeing process of a conventional method.

  Thereafter, PVA (molecular weight 500) 5% sol. And polyacrylate 1% sol. , As wax, PEG 1000 (molecular weight 1000) 2% sol. An aqueous solution containing the above was prepared, and the yarn was continuously immersed in a sizing agent aqueous solution while unwinding the above-mentioned yarn, and then wound while being dried at 80.degree.

  The obtained yarn is a polyester multifilament comprising a filament A-1 having a single fiber diameter of 700 nm and a false twist crimped yarn having a single fiber diameter of 10.5 μm and an apparent crimp rate of 7.8% (Fiber A-2 The total fineness of the yarn was 162 dtex, the adhesion amount of the sizing agent (pasting agent) was 9.6% by weight, and the adhesion amount of wax was 1.5% by weight.

  As a result of the soaping process in the same manner as in Example 1, the sizing agent (pasting agent) and the wax were completely removed, and the filament A-1 having a single fiber diameter of 700 nm was exposed and it was very difficult to slip. The coefficient of friction showed a very high value of 2.0. In addition, knitting defects such as yarn breakage due to fuzz were not observed, and high quality. Next, a glove was obtained using the weft knit and was of high quality.

[Example 3]
In Example 1, instead of using a sizing agent as the sizing agent, an oil agent (“Brian C-1840-1” (product name) manufactured by Matsumoto Yushi Seiyaku Co., Ltd.) was used, and the adhesion amount of the oil agent (sizing agent) was 5.5 The same procedure as in Example 1 was repeated except that it was changed to% by weight. As a result of the soaping process, the oil agent (binder) and the wax were completely removed, and the filament A-1 having a single fiber diameter of 700 nm was exposed, which was very difficult to slip. The coefficient of friction showed a very high value of 2.2. In addition, knitting defects such as yarn breakage due to fuzz were not observed, and high quality. Next, a sock was obtained using the weft knit and was of high quality.

Comparative Example 1
In Example 1, PVA (molecular weight 500) 5% sol. And polyacrylate 1% sol. Prepared in the same manner as in Example 1 except that an aqueous solution containing no wax (containing no wax component) was immersed in the sizing agent aqueous solution continuously while unwinding the above yarn, and then wound while being dried at a temperature of 80 ° C. , A yarn with only a sizing agent (paste agent) was obtained.

    When a woven fabric having a smooth structure is produced by using the obtained yarn and the same weft knitting machine as in Example 1, since the yarn lacks slipperiness, the fluff and the broken yarn become It was not possible to generate a knit.

Comparative Example 2
A composite yarn is obtained in the same manner as in Example 1, and after obtaining an alkali-reduced yarn, as a wax, PEG 1000 (molecular weight: 1000) 5% sol. An aqueous solution containing only the solution was prepared, immersed in the sizing agent aqueous solution continuously while unwinding the above-mentioned yarn, and then wound while being dried at 80 ° C. The obtained yarn was used to make a weave of a weft knit fabric having a smooth texture using MACH2SIR (14 gauge) manufactured by Shima Seiki Co., Ltd. The yarn convergence was poor and the yarn was used as a guide or the like. Was rubbed to generate fuzz, and frequent threading occurred. Such composite yarn was inferior in handleability. The coefficient of friction showed a high value of 1.9, but the obtained woven fabric was of poor quality.

Example 4
Composite false twisting by aligning two sea-island composite fibers obtained in the same manner as in Example 1 and one polyethylene terephthalate multifilament total fineness of 56 dtex / 48 fil (single fiber diameter 10.5 μm, fiber A-2) The composite yarn was obtained by crimping. Two composite yarns thus obtained were mixed and twisted by a twining machine with Z twist 120 times / m.

  Subsequently, in order to remove the sea component of the sea-island type composite fiber contained in the combined twisted yarn, the weight loss (alkali loss) was reduced by 20% at 70 ° C. with a 2.0% aqueous NaOH solution. Thereafter, it was dyed in a beige color by a conventional dyeing process.

  Thereafter, PVA (molecular weight 500) 5% sol. And polyacrylate 1% sol. , As wax, PEG 1000 (molecular weight 1000) 2% sol. An aqueous solution containing the above was prepared, and the yarn was continuously immersed in a sizing agent aqueous solution while unwinding the above-mentioned yarn, and then it was taken up while being dried at a temperature of 80 ° C. to obtain a combined twisting yarn consisting of two composite yarns.

  In the obtained plied yarn, a filament A-1 having a single fiber diameter of 700 nm is disposed in the sheath portion, and a polyethylene terephthalate multifilament (fiber A-2) having a single fiber diameter of 10.5 μm and an apparent crimp rate of 7.8% It was disposed in the core, and the total fineness of the yarn was 320 dtex, the adhesion amount of a sizing agent (pasting agent) was 9.0% by weight, and the adhesion amount of wax was 1.4% by weight.

  The obtained double-twisted yarn (yarn A) and covering yarn FTY 70 T / 2 (yarn B) in which polyurethane fibers are disposed in the core and nylon fibers are disposed in the sheath are obtained with S twist 350 times / m After twisting with a twining machine according to the number of times of twisting, twist prevention was performed at a temperature of 70 ° C. The sock was knitted using the same weft knitting machine as in Example 1 using the obtained plied yarn for the heel, sole and toe portion, and using polyester and cotton mixed yarn and nylon yarn except the above.

  The yarn A has stretchability and slipperiness, and since the yarn B has stretchability, the yarn can be stably knitted, no thread breakage due to fluff etc. occurs, and the handleability is excellent. The obtained weft knit was soda ash 4% sol. And surfactant 2% sol. As a result of soaping with an aqueous solution at 60 ° C containing a binder, the sizing agent (pasting agent) and wax are completely removed, and filament A-1 with a single fiber diameter of 700 nm is exposed on both sides of the fabric and very slip resistant The The coefficient of friction was 0.6.

[Example 5]
Side-by-side type composite fiber multifilament (total fineness 56 dtex / 36 fil) in which two islands-in-sea type composite fibers obtained in the same manner as in Example 4 and polytrimethylene terephthalate and polyethylene terephthalate are joined side by side to form single fibers. A mixed fiber was obtained by interlacing with a single fiber diameter of 12 μm and for one of the fibers A-2.

  Subsequently, in order to remove the sea component of the sea-island type composite fiber contained in the mixed fiber, the weight was decreased by 20% (alkali loss) at 70 ° C. with a 2.0% aqueous NaOH solution. Thereafter, it was dyed in a beige color by a conventional dyeing process.

  Thereafter, PVA (molecular weight 500) 5% sol. And polyacrylate 1% sol. , As wax, PEG 1000 (molecular weight 1000) 2% sol. An aqueous solution containing the above was prepared, and continuously dipped in a sizing agent aqueous solution while unwinding the above-mentioned yarn, and then wound and dried at a temperature of 80 ° C. to obtain a composite yarn (Yarn A).

  In the obtained composite yarn (filament A), a filament A-1 having a single fiber diameter of 700 nm and a side-by-side-type composite fiber multifilament (fiber A-2) having a single fiber diameter of 12 μm and an apparent crimp of 5.2% It had a total fineness of 310 dtex, an adhesion amount of a sizing agent (pasting agent) of 7.0% by weight, and an adhesion amount of wax of 0.9% by weight.

  Using the obtained twisting yarn (yarn A) and covering yarn FTY 70 T / 2 (yarn B) in which polyurethane fibers are disposed in the core and nylon fibers are disposed in the sheath After twisting with S twist 350 times / m, twist stop setting was performed at a temperature of 70 ° C. The obtained double-twisted yarn was used for the heel, sole and toe, and a sock was knitted using the same weft knitting machine as in Example 1 except that polyester fiber and cotton blended yarn and nylon yarn were used otherwise. .

  At that time, the yarn A was stretchable and slippery, and the yarn B was stretchable so that stable knitting could be made, and no thread breakage due to fluff etc. was generated, and the handleability was excellent. The obtained circular knit was soda ash 4% sol. And surfactant 2% sol. Soaking with an aqueous solution containing 60 ° C results in complete removal of the sizing agent (pasting agent) and wax, and exposure of filament A-1 with a single fiber diameter of 700 nm on both sides of the fabric, making it extremely slip resistant there were. The coefficient of friction was 0.65.

[Example 6]
Except that three composite yarns (yarn A) obtained in the same manner as in Example 4 are combined and twisted, the process is the same as Example 4.
At that time, the yarn A was stretchable and slippery, and the yarn B was stretchable so that stable knitting could be made, and no thread breakage due to fluff etc. was generated, and the handleability was excellent. The obtained weft knit was soda ash 4% sol. And surfactant 2% sol. As a result of soaping with an aqueous solution at 60 ° C containing a binder, the sizing agent (pasting agent) and wax are completely removed, and filament A-1 with a single fiber diameter of 700 nm is exposed on both sides of the fabric and very slip resistant The The coefficient of friction was 0.55.

[Example 7]
Except that three composite yarns (yarn A) obtained in the same manner as in Example 5 are combined and twisted in the same manner as in Example 5.
At that time, the yarn A was stretchable and slippery, and the yarn B was stretchable so that stable knitting could be made, and no thread breakage due to fluff etc. was generated, and the handleability was excellent. The obtained weft knit was soda ash 4% sol. And surfactant 2% sol. Soaking with an aqueous solution containing 60 ° C results in complete removal of the sizing agent (pasting agent) and wax, and exposure of filament A-1 with a single fiber diameter of 700 nm on both sides of the fabric, making it extremely slip resistant there were. The coefficient of friction was 0.6.

According to the present invention, a yarn containing ultrafine filaments, which is excellent in handleability and stretchability, and is capable of obtaining a high quality fabric or fiber product, and using the yarn There is provided a fabric and a textile product using the yarn or fabric, the industrial value of which is extremely large.

Claims (16)

  A filament comprising a filament A-1 having a single fiber diameter of 10 to 3,000 nm and a fiber A-2 having a single filament diameter larger than that of the filament A-1, wherein a bundling agent and wax are applied Yarns characterized by   The yarn according to claim 1, wherein the sizing agent comprises a sizing agent and / or an oil agent.   The adhesion amount of the sizing agent is 0.1 to 15% by weight with respect to the weight of the yarn, and the adhesion amount of wax is 0.1 to 10% by weight with respect to the weight of the yarn. The yarn described in 2.   The yarn according to any one of claims 1 to 3, wherein the number of filaments of the filament A-1 contained in the yarn is 500 or more.   The yarn according to any one of claims 1 to 4, wherein the filament A-1 is a filament obtained by dissolving and removing the sea component of a sea-island composite fiber consisting of a sea component and an island component.   The filament A-1 is a filament obtained by dissolving the sea component of the sea-island type composite fiber after dissolving the sea-island type composite fiber comprising the sea component and the island component with the fiber A-2 The yarn according to any one of claims 1 to 4.   The yarn according to any one of claims 1 to 6, wherein the filament A-1 is made of polyester fiber.   The yarn according to any one of claims 1 to 7, wherein the fiber A-2 is a crimped fiber having a single fiber diameter of 5 μm or more and an apparent crimp rate of 2% or more.   The yarn according to claim 8, wherein the crimped fiber is a composite fiber in which two components are bonded to a side-by-side type or an eccentric core-sheath type, or a false twist crimped yarn.   The yarn according to any one of claims 1 to 9, wherein the total fineness of the yarn is in the range of 50 to 1400 dtex.   The yarn according to any one of claims 1 to 10, wherein the yarn is subjected to a dyeing process.   A fabric obtained by using the yarn according to any one of claims 1 to 11.   The fabric according to claim 12, wherein the fabric further comprises yarns B comprising elastic fibers.   The weight ratio of the total weight of the filament A-1 and the fiber A-2 to the yarn B (A-1 + A-2): B is in the range of 95: 5 to 30:70. The fabric of description.   The fabric according to claim 13 or 14, wherein the coefficient of friction is in the range of 0.4 to 2.5 on the front surface or the back surface of the fabric. From the group consisting of socks, gloves, supporters, clothing, woven and knitted tapes, and cords obtained using the yarn according to any of claims 1 to 10 or the fabric according to any of claims 12 to 15. Any textile product chosen.