JP2018197212A - Cosmetic composition - Google Patents
Cosmetic composition Download PDFInfo
- Publication number
- JP2018197212A JP2018197212A JP2017102719A JP2017102719A JP2018197212A JP 2018197212 A JP2018197212 A JP 2018197212A JP 2017102719 A JP2017102719 A JP 2017102719A JP 2017102719 A JP2017102719 A JP 2017102719A JP 2018197212 A JP2018197212 A JP 2018197212A
- Authority
- JP
- Japan
- Prior art keywords
- hydrogen
- powder
- cosmetic composition
- cosmetic
- silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、水と接触して水素を発生可能な水素発生パウダーを含むシリコーン系化粧用組成物に関する。 The present invention relates to a silicone-based cosmetic composition containing a hydrogen generating powder capable of generating hydrogen upon contact with water.
クリーム等の化粧料に水素を含有することにより、水素の還元作用と化粧料自体の美容作用の相乗効果により、皮膚に生成した活性酸素を分解し、シミやくすみ、しわなどの予防や低減、改善など皮膚の若返り・柔軟性および血行促進等による美容効果が期待できる。 By containing hydrogen in cosmetics such as cream, the active oxygen produced in the skin is decomposed due to the synergistic effect of the hydrogen reducing action and the cosmetic action of the cosmetic itself, preventing and reducing spots, dullness, wrinkles, Beauty effects such as skin rejuvenation / flexibility and blood circulation promotion can be expected.
化粧料に水素を含有させる手法として、水と接触して水素を発生可能な水素発生パウダーを当該化粧料に配合することが可能である。水素発生パウダーを含む化粧料を例えば肌に塗布すると、肌にもともとある水分、並びに、外気に含まれる水蒸気が水素発生パウダーと反応して、当該化粧料中に水素が発生する。これにより、前記化粧料は還元作用を備えることができる。 As a technique for containing hydrogen in cosmetics, it is possible to mix hydrogen generating powder capable of generating hydrogen by contact with water into the cosmetics. When a cosmetic containing hydrogen generating powder is applied to the skin, for example, moisture inherent in the skin and water vapor contained in the outside air react with the hydrogen generating powder to generate hydrogen in the cosmetic. Thereby, the cosmetic can have a reducing action.
特許文献１及び特許文献２には、そのような水素発生パウダーを含有するクリームが開示されている。 Patent Documents 1 and 2 disclose creams containing such a hydrogen generating powder.
しかしながら、水素発生パウダーは水と接触することで水素を発生する仕組みになっているので水素発生パウダーを含む化粧料は非水系である必要がある。化粧料を非水系にするために使用可能な原料（素剤）は限定されており、例えば、グリセリン、ワセリン、スクワラン等の使用が考えられる。しかし、これらの成分をベースとする非水系のクリーム等の化粧料は、使用時にベタツキ、伸びの悪さ、化粧膜が自然でない、水素発生パウダーが均一に分散できないために沈降するといった問題があった。 However, since the hydrogen generating powder has a mechanism for generating hydrogen by contact with water, the cosmetic containing the hydrogen generating powder needs to be non-aqueous. The raw materials (elements) that can be used to make the cosmetics non-aqueous are limited, and for example, use of glycerin, petrolatum, squalane and the like can be considered. However, cosmetics such as non-aqueous creams based on these ingredients have problems such as stickiness during use, poor stretch, cosmetic film is not natural, and hydrogen generation powder does not disperse uniformly and thus settles. .
本発明は、前記課題を解決すべくなされたものであって、使用時にベタツキが無く、伸びが良く、化粧膜が自然で、水素発生パウダーの分散均一性を維持することができる、クリーム等の形態の化粧用組成物を提供しようとするものである。 The present invention has been made to solve the above-mentioned problems, and has no stickiness during use, has good elongation, has a natural decorative film, and can maintain the dispersion uniformity of the hydrogen generating powder, such as a cream. It is intended to provide a cosmetic composition in the form.
本発明の目的は、組成物の全重量を基準として、
（Ａ）部分架橋型オルガノポリシロキサン ０．５〜１０．０重量％、
（Ｂ）ポリエチレングリコール ５．０〜５０．０重量％、
（Ｃ）シリコーンレジン被覆球状シリコーンゴム紛体 ２．０〜１２．０重量％、
（Ｄ）水素還元パウダー ５．０〜１５．０重量％、及び、
（Ｅ）低粘度シリコーン油
を含む化粧用組成物によって達成される。
The purpose of the present invention is based on the total weight of the composition,
(A) 0.5-10.0 wt% of partially crosslinked organopolysiloxane,
(B) Polyethylene glycol 5.0-50.0 wt%,
(C) Silicone resin-coated spherical silicone rubber powder 2.0 to 12.0% by weight,
(D) Hydrogen reduction powder 5.0-15.0 weight%, and
(E) achieved by a cosmetic composition comprising a low viscosity silicone oil.
本発明の化粧用組成物は、好ましくは、
（Ａ）部分架橋型オルガノポリシロキサン ２．４５〜３．８５重量％、
（Ｂ）ポリエチレングリコール １０．０〜３８．０重量％、
（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体 ４．０〜１０．０重量％、
（Ｄ）水素発生パウダー ５．０〜１５．０重量％、及び、
（Ｅ）低粘度シリコーン油
を含む。
The cosmetic composition of the present invention is preferably
(A) partially cross-linked organopolysiloxane 2.45-3.85 wt%,
(B) polyethylene glycol 10.0-38.0 wt%,
(C) Silicone resin-coated spherical silicone rubber powder 4.0 to 10.0% by weight,
(D) Hydrogen generation powder 5.0 to 15.0 wt%, and
(E) Contains a low viscosity silicone oil.
本発明の化粧用組成物は皮膚用化粧料であることが好ましく、クリームの形態であることがより好ましい。本発明の化粧用組成物は水素を発生することが可能であり、且つ、シリコーン系であるので、クリームの形態の本発明の化粧用組成物は、謂わば水素シリコーンクリームである。 The cosmetic composition of the present invention is preferably a skin cosmetic, and more preferably in the form of a cream. Since the cosmetic composition of the present invention can generate hydrogen and is based on silicone, the cosmetic composition of the present invention in the form of cream is a so-called hydrogen silicone cream.
本発明の化粧用組成物は水素発生パウダーを含有しているので、肌に塗布後、肌にもともとある微量の水分、及び／又は、外気の水蒸気と接触して水素を発生させて、還元機能を発揮することができる。したがって、本発明の化粧用組成物は、皮膚に生成した活性酸素を分解し、シミやくすみ、しわなどの予防や低減、改善など皮膚の若返り・柔軟性および血行促進等による美容効果を発揮することができる。 Since the cosmetic composition of the present invention contains a hydrogen generating powder, after applying to the skin, it generates hydrogen by contacting the skin with a very small amount of moisture and / or water vapor in the outside air, thereby reducing the function. Can be demonstrated. Accordingly, the cosmetic composition of the present invention decomposes active oxygen generated in the skin, and exhibits beauty effects such as skin rejuvenation / flexibility and blood circulation promotion, such as prevention, reduction, and improvement of spots, dullness and wrinkles. be able to.
また、本発明の化粧用組成物は、使用時にベタツキが無く、伸びが良く、化粧膜が自然で、水素発生パウダーの分散均一性を維持することができる。 Further, the cosmetic composition of the present invention has no stickiness when used, has good elongation, has a natural cosmetic film, and can maintain the uniformity of dispersion of the hydrogen generating powder.
グリセリン、ワセリン、スクワラン等をベースとする非水系のクリーム等の化粧料は、肌に塗布したときに、塗布面が透明になるため、塗布により形成される化粧膜に被覆力が無く、テカリが目立ち、自然感がないために、きれいに見えない。しかし、本発明の化粧用組成物は半透明のシリコーン系の化粧膜を形成することができるので、自然な外観を長時間もたらすことができる。したがって、本発明の化粧用組成物は、水素による還元作用で美容効果のあらわれた肌を、生き生きとみせることができる。 Cosmetics such as non-aqueous creams based on glycerin, petrolatum, squalane, etc. have a coating surface that is transparent when applied to the skin. Because it is not noticeable and natural, it does not look beautiful. However, since the cosmetic composition of the present invention can form a translucent silicone-based decorative film, it can provide a natural appearance for a long time. Therefore, the cosmetic composition of the present invention can make the skin that has a beauty effect due to the reducing action of hydrogen appear lively.
本発明の化粧用組成物は、組成物の全重量を基準として、
（Ａ）部分架橋型オルガノポリシロキサン ０．５〜１０．０重量％、
（Ｂ）ポリエチレングリコール ５．０〜５０．０重量％、
（Ｃ）シリコーンレジン被覆球状シリコーンゴム紛体 ２．０〜１２．０重量％、
（Ｄ）水素還元パウダー ５．０〜１５．０重量％、及び、
（Ｅ）低粘度シリコーン油
を含む。但し、本発明の化粧用組成物は、上記（Ａ）〜（Ｅ）成分の他に化粧料に汎用の各種の任意成分を含むことができる。
The cosmetic composition of the present invention is based on the total weight of the composition,
(A) 0.5-10.0 wt% of partially crosslinked organopolysiloxane,
(B) Polyethylene glycol 5.0-50.0 wt%,
(C) Silicone resin-coated spherical silicone rubber powder 2.0 to 12.0% by weight,
(D) Hydrogen reduction powder 5.0-15.0 weight%, and
(E) Contains a low viscosity silicone oil. However, the cosmetic composition of the present invention can contain various general-purpose optional components in cosmetics in addition to the components (A) to (E).
（Ａ）部分架橋型オルガノポリシロキサン重合物とは、三次元架橋構造を有するオルガノポリシロキサン重合物で、特公平８−６０３５号公報等に記戴されているものが例示される。部分架橋型オルガノポリシロキサン重合物は、オルガノポリシロキサンを、架橋結合させて得られる重合物であり、一部に三次元架橋構造を有し、Ｒ２ＳｉＯ単位及びＲＳｉＯ１．５単位よりなり、Ｒ３ＳｉＯ０．５単位及び／又はＳｉＯ２単位を含んでもよい。ただし、各構成単位のＲは水素原子、メチル基、エチル基、プロピル基等のアルキル基、フェニル基、トリル基等などのアリール基、およびビニル基等の脂肪族不飽和基などが例示され、同種又は異なった種類であっても良い。市販品としては、部分架橋オルガノポリシロキサン重合物にシリコーン油を配合したものとして、例えば、「ＫＳＧ―１５」、「ＫＳＧ―１６」、「ＫＳＧ−１８」（信越化学工業（（株））製）等が挙げられる。 (A) The partially cross-linked organopolysiloxane polymer is an organopolysiloxane polymer having a three-dimensional cross-linked structure, and examples thereof include those described in Japanese Patent Publication No. 8-6035. The partially cross-linked organopolysiloxane polymer is a polymer obtained by cross-linking organopolysiloxane, partly having a three-dimensional cross-linking structure, consisting of R 2 SiO units and RSiO 1.5 units, R 3 SiO 0.5 units and / or SiO 2 units may be included. However, R of each structural unit is exemplified by a hydrogen atom, an alkyl group such as a methyl group, an ethyl group, and a propyl group, an aryl group such as a phenyl group and a tolyl group, and an aliphatic unsaturated group such as a vinyl group. The same kind or different kind may be sufficient. As a commercially available product, for example, “KSG-15”, “KSG-16”, “KSG-18” (manufactured by Shin-Etsu Chemical Co., Ltd.) as a mixture of a partially crosslinked organopolysiloxane polymer and silicone oil. ) And the like.
（Ａ）の配合目的は、３次元のゲルを形成することで均一なゲルを形成し、固形分の割合が少なくても、（Ｅ）低粘度シリコーン油を多量に包含して、ベタツキのない、いわゆる水系製品でいう瑞々しいゲルを生成することである。 The blending purpose of (A) is to form a uniform gel by forming a three-dimensional gel, and even if the solid content is small, (E) a large amount of low-viscosity silicone oil is included and there is no stickiness It is to produce a refreshing gel in a so-called aqueous product.
（Ｂ）ポリエチレングリコールとしては、水酸基価が１８７〜２２４であるものが好ましく、ポリエチレングリコール１５００（ＰＥＧ−３０）が好ましい。たとえば、市販品としては「トーホーポリエチレングリコール１５００」（東邦化学（（株））社）または「ブラウノンＰＥＧ−１５００」（青木油脂工業製）等があげられる。 (B) As polyethyleneglycol, that whose hydroxyl value is 187-224 is preferable, and polyethyleneglycol 1500 (PEG-30) is preferable. Examples of commercially available products include “Toho Polyethylene Glycol 1500” (Toho Chemical Co., Ltd.) or “Brownon PEG-1500” (Aoki Yushi Kogyo Co., Ltd.).
（Ｂ）の配合目的は、シリコーン系成分だけの非水系の系だと、水と馴染む部分がなく皮膚に塗布後の微量の水と（Ｄ）水素発生パウダーが反応しないため、非水系ではあるが水と馴染む部分を本発明の化粧料にもたせることである。 The blending purpose of (B) is non-aqueous because it is a non-aqueous system containing only silicone components, and there is no part that is compatible with water and a small amount of water after application to the skin does not react with (D) hydrogen generating powder. Is to make the cosmetic of the present invention have a part that is familiar with water.
（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体は、シリコーンゴムの表面をシリコーンレジンで被覆したシリコーン複合パウダーで、市販品としては、「ＫＳＰ−１００」、「ＫＳＰ−１０１」（信越化学工業（株）製）等が挙げられる。 (C) Silicone resin-coated spherical silicone rubber powder is a silicone composite powder in which the surface of silicone rubber is coated with silicone resin, and commercially available products include “KSP-100” and “KSP-101” (Shin-Etsu Chemical Co., Ltd.). )) And the like.
（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体の配合目的は、皮膚に密着し、皮膚上の凹凸を水平にし光の乱反射を防ぐことで、自然な顔色で、生き生きとした肌にみせるためことである。 (C) The purpose of blending the silicone resin-coated spherical silicone rubber powder is to make the skin look natural and lively by sticking to the skin, leveling the unevenness on the skin and preventing irregular reflection of light. is there.
（Ｄ）水素発生パウダーとは、水と接触することにより、酸化されて、水素を発生させる還元性の粉体で、たとえば、特開２０１３−２１２４９８号公報に記載の「還元パウダー」、及び「水素化マグウネシウム」（関東化学（株）製）等が挙げられる。 (D) The hydrogen generating powder is a reducing powder that is oxidized by being brought into contact with water to generate hydrogen. For example, “reducing powder” described in Japanese Patent Application Laid-Open No. 2013-212498, and “ Magnesium hydride "(manufactured by Kanto Chemical Co., Inc.) and the like.
（Ｄ）水素発生パウダーの配合目的は水と接触することで水素を発生させることである。 (D) The purpose of blending the hydrogen generating powder is to generate hydrogen by contact with water.
（Ｅ）低粘度シリコーン油としては特に限定されるものではないが、粘度５０ｃｓ程度以下のものであれば好適に使用できる。たとえば、ジメチルポリシロキサン、メチルフェニルポリシロキサン、環状のオクタメチルシクロテトラポリシロキサン、デカメチルシクロペンタシロキサンなどが挙げられる。揮発性であることが好ましい。これらは、単独でも適宜任意の２種以上組み合わせても使用できる。 (E) Although it does not specifically limit as a low-viscosity silicone oil, If it is a thing below a viscosity of about 50 cs, it can be used conveniently. Examples thereof include dimethylpolysiloxane, methylphenylpolysiloxane, cyclic octamethylcyclotetrapolysiloxane, decamethylcyclopentasiloxane, and the like. It is preferably volatile. These may be used alone or in any combination of two or more.
（Ｅ）低粘度シリコーン油の配合目的は（Ａ）〜（Ｄ）成分を希釈して、均一に保つためである。 (E) The purpose of blending the low-viscosity silicone oil is to dilute the components (A) to (D) and keep them uniform.
本発明における各成分としては、いずれも一般に市販されているものを使用することができる。 As each component in this invention, what is generally marketed can be used.
本発明の化粧用組成物は主にシリコーン成分から構成されるシリコーン系組成物であるので、クリームのような比較的高い粘度を有する形態であっても、ベタツキがなく、皮膚上での伸びを失わない。 Since the cosmetic composition of the present invention is a silicone-based composition mainly composed of a silicone component, even in a form having a relatively high viscosity such as a cream, there is no stickiness and the elongation on the skin is increased. I will not lose.
化粧膜の自然さ、ベタツキの無さ、伸びの良さ、を向上させるためには、（Ａ）部分架橋型オルガノポリシロキサンの配合量を調節することになるが、あまり増やし過ぎると、透明感が増して化粧膜の自然さが悪くなってしまう。また、疎水性が増すために水分が弾かれてしまい水素発生パウダーと水が反応し難くなり水素発生量が落ちてしまう。そこで、本発明者らは、部分架橋型オルガノポリシロキサンを０．５〜１０．０重量％、好ましくは２．４５〜３．８５重量％に調節することで、過度な透明感を減らし、水との馴染みを確保できた。また、非水系の剤型中に親水性の（Ｂ）ポリエチレングリコールを配合することで水素発生パウダーと水との反応性を高めて水素を発生しやすくしているが、ポリエチレングリコールの量を増やし過ぎると親水性が上がるもののシリコーン系成分との相溶性が悪くなり化粧膜の自然さが失われる。一方、ポリエチレングリコールの配合量を下げ過ぎると親水性が下がり水素発生パウダーと水との反応性が下がり水素発生量が減ってしまう。そこで、（Ｂ）ポリエチレングリコールの配合量を５．０〜５０．０重量％、好ましくは１０．０〜３８．０重量％に調節することで目的を達成した。（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体の配合目的は、皮膚に密着し、皮膚上の凹凸を水平にし光の乱反射を防ぐことで、自然な顔色で、生き生きとした肌にみせるためであるが、配合量を上げ過ぎると膜が厚くなり不自然になり、下げ過ぎると肌の被覆力が下がり、効果が下がってしまう。適切な配合量は２．０〜１２重量％で、好ましくは４．０〜１０．０重量％である。（Ｄ）水素発生パウダーの配合目的は水と接触することで水素を発生させることであり、適切な配合量は５．０〜１５．０重量％である。（Ｅ）低粘度シリコーン油の配合量は好ましくは３０〜７０重量％、好ましくは４０〜６０重量％であり、上記（Ａ）〜（Ｄ）成分並びにその他の任意成分以外が（Ｅ）低粘度シリコーン油となるように（すなわち、残部が（Ｅ）低粘度シリコーン油）、配合量を調節することが好ましい。 In order to improve the naturalness of the cosmetic film, no stickiness, and good elongation, the amount of (A) the partially crosslinked organopolysiloxane will be adjusted. In addition, the naturalness of the cosmetic film is worsened. Further, since the hydrophobicity is increased, moisture is repelled, and the hydrogen generating powder and water hardly react with each other, resulting in a decrease in the amount of hydrogen generated. Therefore, the present inventors reduce excessive transparency by adjusting the partially crosslinked organopolysiloxane to 0.5 to 10.0% by weight, preferably 2.45 to 3.85% by weight. We were able to secure familiarity with. In addition, by adding hydrophilic (B) polyethylene glycol in the non-aqueous dosage form, the reactivity between the hydrogen generating powder and water is increased to facilitate hydrogen generation, but the amount of polyethylene glycol is increased. If it is too high, the hydrophilicity will increase, but the compatibility with the silicone-based component will deteriorate and the natural beauty of the cosmetic film will be lost. On the other hand, if the blending amount of polyethylene glycol is too low, the hydrophilicity is lowered and the reactivity between the hydrogen generating powder and water is lowered and the amount of hydrogen generated is reduced. Therefore, the object was achieved by adjusting the blending amount of (B) polyethylene glycol to 5.0 to 50.0% by weight, preferably 10.0 to 38.0% by weight. (C) The compounding purpose of the silicone resin-coated spherical silicone rubber powder is to adhere to the skin, level the unevenness on the skin and prevent diffused reflection of light, and to make it look natural and vivid on the skin. However, if the amount is too high, the film becomes thick and unnatural, and if it is too low, the covering power of the skin is lowered and the effect is reduced. A suitable blending amount is 2.0 to 12% by weight, preferably 4.0 to 10.0% by weight. (D) The compounding purpose of the hydrogen generating powder is to generate hydrogen by contacting with water, and the appropriate compounding amount is 5.0 to 15.0% by weight. The blending amount of the (E) low-viscosity silicone oil is preferably 30 to 70% by weight, preferably 40 to 60% by weight. Other than the above components (A) to (D) and other optional components, (E) the low viscosity It is preferable to adjust the blending amount so that it becomes a silicone oil (that is, the balance is (E) low-viscosity silicone oil).
本発明の化粧用組成物の製造方法は特には限定されるものではなく、上記（Ａ）〜（Ｅ）成分、そして、必要に応じて、その他の任意成分を適宜混合することによって本発明の化粧用組成物を製造することができる。好ましくは、（Ａ）部分架橋型オルガノポリシロキサン、（Ｂ）ポリエチレングリコール、（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体、及び、（Ｄ）水素発生パウダーを混合し、次いで、（Ｅ）低粘度シリコーン油を混合することにより、本発明の化粧用組成物を好適に製造することができる。（Ｅ）低粘度シリコーン油を混合する際に、組成物の１００重量％の残量が（Ｅ）低粘度シリコーン油となるように調整することがより好ましい。 The method for producing the cosmetic composition of the present invention is not particularly limited, and the above-described components (A) to (E) and, if necessary, other optional components are mixed as appropriate. A cosmetic composition can be produced. Preferably, (A) partially crosslinked organopolysiloxane, (B) polyethylene glycol, (C) silicone resin-coated spherical silicone rubber powder, and (D) hydrogen generating powder are mixed, and then (E) low viscosity By mixing silicone oil, the cosmetic composition of the present invention can be suitably produced. (E) When mixing low-viscosity silicone oil, it is more preferable to adjust so that the remaining amount of 100% by weight of the composition becomes (E) low-viscosity silicone oil.
以下、本発明を実施例及び比較例を用いてより具体的に説明するが、本発明の範囲は実施例に限定されるものではない。 EXAMPLES Hereinafter, although this invention is demonstrated more concretely using an Example and a comparative example, the scope of the present invention is not limited to an Example.
表１に示す「実施例１」〜「実施例９」は、本発明者が、（Ａ）部分架橋型オルガノポリシロキサン、（Ｂ）ポリエチレングリコール、（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体、（Ｄ）水素発生パウダー、及び、（Ｅ）低粘度シリコーンの配合量を変えて、本発明が目的とする、水素発生可能なシリコーン系クリームであって、使用時にベタツキが無く、伸びが良く、自然な化粧膜を形成することができ、水素発生パウダーを均一に分散することができ、ひいては、生き生きとした肌にみせることを実現するクリームを製造するのに最適な配合量を見つけ出すためにテストを繰り返した際に採用した配合量を示したものであり、また「比較例」は、本発明と比較するためのものである。なお、番号１の成分（ＫＳＧ−１５）の配合量の直下の括弧は当該成分に含まれるシリコーンゴム粉体（架橋物）の量を示す。 "Example 1" to "Example 9" shown in Table 1 are as follows. The inventors have (A) partially crosslinked organopolysiloxane, (B) polyethylene glycol, (C) silicone resin-coated spherical silicone rubber powder, (D) Hydrogen generating powder, and (E) A silicone-based cream capable of generating hydrogen by changing the blending amount of low-viscosity silicone, having no stickiness at the time of use, and having good elongation. Tested to find the optimum formulation to produce a cream that can form a natural cosmetic film, uniformly disperse the hydrogen generating powder, and thus make it appear vivid on the skin The compounding amount employed when the above is repeated is shown, and the “Comparative Example” is for comparison with the present invention. In addition, the parenthesis just under the compounding quantity of the component (KSG-15) of number 1 shows the quantity of the silicone rubber powder (crosslinked product) contained in the said component.
表１における一番左側の欄には、使用する各原料(素剤) が記載されており、実施例１〜実施例９の欄には、（Ａ）部分架橋型オルガノポリシロキサン、（Ｂ）ポリエチレングリコール、（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体、（Ｄ）水素発生パウダー、及び、（Ｅ）低粘度シリコーン油が記載され、「比較例」の欄には、水素発生パウダー、グリセリン、アルキルポリグリセリル、及び、プロパンジオールが記載されている。 In the leftmost column of Table 1, the raw materials (elements) to be used are described. In the columns of Examples 1 to 9, (A) partially crosslinked organopolysiloxane, (B) Polyethylene glycol, (C) silicone resin-coated spherical silicone rubber powder, (D) hydrogen generating powder, and (E) low-viscosity silicone oil are described. In the column “Comparative Example”, hydrogen generating powder, glycerin, Alkyl polyglyceryl and propanediol are described.
「プロパンジオール」はデュポン社製の「Ｚｅｍｅａ Ｓｅｌｅｃｔ」を、「グリセリン」は阪本薬品工業社製の「化粧品用濃グリセリン」を、「アルキルポリグリセリル」は日清オイリオグループ社製「ノムコートＨＫ−Ｐ」を、それぞれ使用した。 “Propanediol” is “Zeme Select” manufactured by DuPont, “Glycerin” is “Concentrated glycerin for cosmetics” manufactured by Sakamoto Pharmaceutical Co., Ltd., and “Alkylpolyglyceryl” is “NOMCOAT HK-P” manufactured by Nisshin Oillio Group. Were used respectively.
そして、本発明者らは、表１の実施例１〜実施例９の欄に示す配合量（重量％）で各原料を混合してクリームを製造した。具体的には、表１の左端の番号１〜４の原料を混合分散後、番号５の原料を更に添加し均一に混合してクリーム状の組成物を得た。なお、実施例４については番号１の原料に既に低粘度シリコーン油が含まれているので、番号４のシクロペンタシロキサンを使用することは行わなかった。 And the present inventors mixed each raw material with the compounding quantity (weight%) shown in the column of Example 1-Example 9 of Table 1, and manufactured cream. Specifically, after mixing and dispersing the raw materials of Nos. 1 to 4 at the left end of Table 1, the raw material of No. 5 was further added and mixed uniformly to obtain a creamy composition. In Example 4, since the low-viscosity silicone oil was already contained in the raw material No. 1, the use of cyclopentasiloxane No. 4 was not performed.
実施例１〜実施例９において、実施例１、２においては、（Ａ）部分架橋型オルガノポリシロキサンの配合量がそれぞれ異なっている。実施例３、４においては、Ｂ）ポリエチレングリコール１５００の配合量がそれぞれ異なっている。実施例５、６においては、（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体の配合量が異なっている。実施例７、８においては、Ｄ）水素発生パウダーの配合量が異なっている。実施例９においては、最適な配合量を記載した。 In Examples 1 to 9, in Examples 1 and 2, the blending amount of (A) partially crosslinked organopolysiloxane is different. In Examples 3 and 4, the blending amount of B) polyethylene glycol 1500 is different. In Examples 5 and 6, the blending amount of the (C) silicone resin-coated spherical silicone rubber powder is different. In Examples 7 and 8, the blending amount of D) hydrogen generating powder is different. In Example 9, the optimum blending amount was described.
また、本発明者らは、表１の「比較例」に示す配合量（重量％）で各原料を混合してクリームを製造した。具体的には、表１の左端の番号６〜８の原料を混合分散後、番号５の原料を更に添加し均一に混合してクリーム状の組成物を得た。 In addition, the present inventors produced creams by mixing the raw materials in the blending amounts (% by weight) shown in “Comparative Examples” in Table 1. Specifically, after mixing and dispersing the raw materials of Nos. 6 to 8 at the left end of Table 1, the raw material of No. 5 was further added and mixed uniformly to obtain a cream-like composition.
実施例１〜９及び比較例の組成物の特性を評価した。評価項目及び評価法は以下のとおりである。 The characteristics of the compositions of Examples 1 to 9 and Comparative Example were evaluated. Evaluation items and evaluation methods are as follows.
評価項目
（１）官能テストによる使用感（ベタツキがないこと、伸びがよいこと、化粧膜の外観の自然さ、及び、水素発生パウダーの分散均一性）
（２）溶存水素量
Evaluation item (1) Feeling by sensory test (no stickiness, good elongation, natural appearance of cosmetic film, and dispersion uniformity of hydrogen generating powder)
(2) Dissolved hydrogen amount
評価法
（１）専門パネル１０名による使用テスト。使用時の、上記（１）の項目について絶対評価５段階（＊１）で評価した。各パネルに各試料ごとに評点をつけてもらい、平均値を算出した。その平均値により、判定基準４段階（＊２）で判定した。
＊１：絶対評価における評点
５：非常によい
４：良い
３：良いか悪いかどちらとも言えない
２：やや悪い
１：悪い
＊２ 判定基準
４．０〜５．０：非常に良いとして◎印を付した。
３．０〜４．０未満：良いとして○印を付した。
２．０〜３．０未満：どちらとも言えないとして△印を付した。
１．０〜２．０未満：悪いとして×印を付した。
Evaluation method (1) Use test by 10 expert panels. At the time of use, the above item (1) was evaluated in five absolute evaluations (* 1). Each panel was given a score for each sample, and the average value was calculated. Based on the average value, determination was made in four criteria (* 2).
* 1: Score in absolute evaluation 5: Very good 4: Good 3: Not good or bad 2: Slightly bad 1: Bad * 2 Judgment criteria 4.0-5.0: ◎ marked as very good Was attached.
3.0 to less than 4.0: Marked as good.
2.0-less than 3.0: Marked as not being able to say either.
1.0-less than 2.0: Marked as bad.
（２）溶存水素分析計（ＫＭ２１００ＤＨ、共栄電子研究所製）にて、溶存水素量を測定して評価した。各試料１．０ｇを、溶存水素分析計の専用フローセル（内容積：２２０ｍＬ）にイオン交換水２１５ｍＬ中に分散させ、室温で、マグネチックスタラーで２５０ｒｐｍで撹拌しつつ、６０分後までの水素量を５分毎に測定した。その値で、最大値をもって溶存水素量値とした。 (2) The amount of dissolved hydrogen was measured and evaluated with a dissolved hydrogen analyzer (KM2100DH, manufactured by Kyoei Denshi Laboratories). 1.0 g of each sample was dispersed in 215 mL of ion-exchanged water in a dedicated flow cell (internal volume: 220 mL) of a dissolved hydrogen analyzer, and the amount of hydrogen up to 60 minutes after stirring at 250 rpm with a magnetic stirrer at room temperature. Was measured every 5 minutes. The maximum value was taken as the dissolved hydrogen content value.
判定は次のように行った。その値が３００ｐｐｂ以上ならば、非常によく水素が発生しているとして、◎印を付した。その値が１００〜３００ｐｐｂ未満ならば、良く水素が発生しているとして、○印を付した。その値が３０〜１００ｐｐｂ未満ならば一応水素が発生していとして、△印を付した。その値が０〜３０ｐｐｂ未満ならば十分な水素が発生していないとして、×印を付した。 The determination was performed as follows. If the value was 300 ppb or more, it was marked as ◎ because hydrogen was generated very well. If the value was less than 100 to 300 ppb, it was marked as ◯ because hydrogen was generated well. If the value was less than 30 to 100 ppb, it was assumed that hydrogen had been generated, and a Δ mark was given. If the value was less than 0 to 30 ppb, it was marked as x because sufficient hydrogen was not generated.
更に、上記評価の結果に基づき、実施例１〜９及び比較例の総合評価を行った。 Furthermore, based on the results of the above evaluations, comprehensive evaluations of Examples 1 to 9 and Comparative Examples were performed.
結果を表２に示す。
表２に示すように、実施例１〜実施例９のクリームのうち、最も優れていると評価されたものは実施例９のクリームであった。その他の実施例１、２、４、６、７、８のクリームも、優れていると評価され、実施例３、５もある程度は優れていると評価され、水素シリコーンクリームとしては普通に使用することができるという評価であった。 As shown in Table 2, the cream of Example 9 was evaluated as the most excellent among the creams of Example 1 to Example 9. The other creams of Examples 1, 2, 4, 6, 7, and 8 are also evaluated as excellent, and Examples 3 and 5 are also evaluated as excellent to some extent, and are normally used as hydrogen silicone creams. It was evaluation that it was possible.
一方、比較例のクリームは、「溶存水素」の点においては優れた評価結果であったが、「ベタツキの無さ」と「伸びの良さ」「化粧膜の自然さ」、「水素発生パウダーの分散均一性」は最低の評価結果で、総合評価も最低であり、実施例１〜実施例９のいずれのクリームよりも総合評価が低く、実施例１〜実施例９のクリームの総合評価が優れていることを確認することができた。 On the other hand, the cream of the comparative example had an excellent evaluation result in terms of “dissolved hydrogen”, but “no stickiness”, “good elongation”, “naturalness of cosmetic film”, “hydrogen generation powder” “Dispersion uniformity” is the lowest evaluation result, the overall evaluation is also the lowest, the overall evaluation is lower than any of the creams of Examples 1 to 9, and the overall evaluation of the creams of Examples 1 to 9 is excellent. I was able to confirm that.
すなわち、実施例１〜実施例９に示す本発明の化粧用組成物に係るクリームは、所定量の、（Ａ）部分架橋型オルガノポリシロキサン、（Ｂ）ポリエチレングリコール、（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体、及び、（Ｄ）水素発生パウダー、並びに、（Ｅ）低粘度シリコーン油を含むことにより、いずれも「比較例」のクリームよりも、使用時にベタツキが無く、伸びが良く、自然な化粧膜を持ち、水素発生パウダーの分散均一性のある、生き生きとした肌にみせることを実現可能な水素シリコーンクリームである。 That is, the creams according to the cosmetic compositions of the present invention shown in Examples 1 to 9 have a predetermined amount of (A) partially crosslinked organopolysiloxane, (B) polyethylene glycol, and (C) silicone resin-coated spheres. By including silicone rubber powder, (D) hydrogen generating powder, and (E) low viscosity silicone oil, all of them have no stickiness during use, good elongation and naturalness than the cream of “Comparative Example”. Hydrogen silicone cream that has a beautiful makeup film and has a uniform dispersion of the hydrogen generating powder, and can be made to appear on a lively skin.
Claims (1)
（Ａ）部分架橋型オルガノポリシロキサン ０．５〜１０．０重量％、
（Ｂ）ポリエチレングリコール ５．０〜５０．０重量％、
（Ｃ）シリコーンレジン被覆球状シリコーンゴム粉体 ２．０〜１２．０重量％、
（Ｄ）水素発生パウダー５．０〜１５．０重量％、及び、
（Ｅ）低粘度シリコーン油
を含む化粧用組成物。 Based on the total weight of the composition,
(A) 0.5-10.0 wt% of partially crosslinked organopolysiloxane,
(B) Polyethylene glycol 5.0-50.0 wt%,
(C) Silicone resin-coated spherical silicone rubber powder 2.0 to 12.0% by weight,
(D) Hydrogen generation powder 5.0-15.0 wt%, and
(E) A cosmetic composition comprising a low viscosity silicone oil.