JP2018131614A - Curable resin composition, cured film, and display device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a curable resin composition which contains semiconductor particles and is capable of forming a wavelength conversion film having reduced color unevenness by having small surface roughness, a cured film formed from the curable resin composition, and a display device including the cured film.SOLUTION: There are provided: a curable resin composition containing semiconductor particles (A), a resin (B), a polymerizable compound (C), and an organic solvent (D) which contains a compound having a cycloalkane ring and at least one group selected from the group consisting of -O-, -O-C(=O)-, -C(=O)-O- and -C(=O)- in the molecule; a cured film formed from the curable resin composition; and a display device including the cured film.SELECTED DRAWING: None

Description

  The present invention relates to a curable resin composition, a cured film formed therefrom, and a display device including the cured film.

  As a curable resin composition for forming a cured film such as a wavelength conversion film included in a display device such as an image display device, a material containing semiconductor particles such as semiconductor quantum dots is known [for example, 2015-028139 (patent document 1)]. Japanese Patent Application Laid-Open No. 2005-128539 (Patent Document 2) describes a semiconductor nanocrystal having a surface coordinated compound having a photosensitive functional group and a photosensitive composition containing the semiconductor nanocrystal.

Japanese Unexamined Patent Publication No. 2015-028139 JP 2005-128539 A

  An object of the present invention is a curable resin composition containing semiconductor particles, which has a small surface roughness and thereby can form a cured film with reduced color unevenness, and is formed from the curable resin composition. And a display device including the cured film.

The present invention provides the following curable resin composition, cured film, and display device.
[1] Including semiconductor particles (A), resin (B), polymerizable compound (C) and organic solvent (D),
The organic solvent (D) is composed of a cycloalkane ring, —O—, —O—C (═O) —, —C (═O) —O— and —C (═O) — in the molecule. A curable resin composition comprising a compound having at least one group selected from the group.

[2] A cured film formed from the curable resin composition according to [1].
[3] A display device comprising the cured film according to [2].

  According to the present invention, a curable resin composition containing semiconductor particles, which can form a cured film having a small surface roughness and thereby reduced color unevenness, is formed from the curable resin composition. A cured film and a display device including the cured film can be provided.

<Curable resin composition>
The curable resin composition according to the present invention includes semiconductor particles (A), a resin (B), a polymerizable compound (C), and an organic solvent (D), and the organic solvent (D) contains cycloalkane in the molecule. A compound having a ring and at least one group selected from the group consisting of —O—, —O—C (═O) —, —C (═O) —O— and —C (═O) — Hereinafter, this compound is also referred to as an organic solvent (D1). According to the curable resin composition, a cured film such as a wavelength conversion film having a small surface roughness and thereby reduced color unevenness can be formed. The reduction in color unevenness is advantageous in increasing the in-plane uniformity of the light emission characteristics of a cured film such as a wavelength conversion film. Moreover, this curable resin composition can show favorable patterning property. For example, according to the curable resin composition, it is possible to accurately form a patterned cured film having a desired line width. According to the curable resin composition, it is possible to accurately form a patterned cured film even when the line width is relatively small.

  In addition, unless otherwise indicated, the compound illustrated as each component contained in the curable resin composition in this specification can be used individually or in combination of multiple types.

[1] Semiconductor particles (A)
The curable resin composition contains semiconductor particles (A). The semiconductor particles (A) are preferably luminescent (fluorescent) semiconductor particles. A cured film such as a wavelength conversion film formed from a curable resin composition containing light-emitting semiconductor particles can be excellent in color reproducibility showing fluorescence emission in a desired wavelength range.

  The luminescent semiconductor particles are particles made of a semiconductor crystal, preferably nanoparticles made of a semiconductor crystal. A preferred example of the luminescent semiconductor particles is a semiconductor quantum dot. The average particle diameter of the semiconductor quantum dots is, for example, 0.5 nm or more and 20 nm or less, preferably 1 nm or more and 15 nm or less (for example, 2 nm or more and 15 nm or less). The average particle diameter of the semiconductor quantum dots can be determined using a transmission electron microscope (TEM).

  The semiconductor quantum dot is selected from the group consisting of Group 2 element, Group 11 element, Group 12 element, Group 13 element, Group 14 element, Group 15 element and Group 16 element of the periodic table, for example. It can be composed of a semiconductor material containing one or more elements.

Specific examples of semiconductor materials that can constitute the semiconductor quantum dots include compounds of Group 14 and Group 16 elements such as SnS ₂ , SnS, SnSe, SnTe, PbS, PbSe, and PbTe; GaN, GaP, GaAs, and GaSb , InN, InP, InAs, InSb, InGaN, InGaP and other group 13 elements and group 15 elements; Ga ₂ O ₃ , Ga ₂ S ₃ , Ga ₂ Se ₃ , Ga ₂ Te ₃ , In ₂ O ₃ , Group 13 and Group 16 elements such as In ₂ S ₃ , In ₂ Se ₃ , In ₂ Te ₃ ; ZnO, ZnS, ZnSe, ZnTe, CdO, CdS, CdSe, CdTe, HgO, HgS , HgSe, HgTe, and other group 12 and group 16 elements; As ₂ O ₃ , As ₂ S ₃ , As ₂ Se ₃ , As ₂ Te ₃ , Sb ₂ O ₃ , Sb ₂ S ₃ , Sb ₂ Se ₃ , Sb ₂ Te ₃ , Bi ₂ O ₃ , Bi ₂ S ₃ , Bi ₂ Se ₃ , Bi ₂ Te _3, etc. Compound with element; Compound of Group 2 element such as MgS, MgSe, MgTe, CaS, CaSe, CaTe, SrS, SrSe, SrTe, BaS, BaSe, BaTe etc. and Group 16 element; 14th of Si, Ge, etc. A single element of a group element, a group 15 element or a group 16 element is included.

  The semiconductor quantum dot may have a single layer structure made of a single semiconductor material, or the surface of a core particle (core layer) made of a single semiconductor material may be one or more kinds different from this. A core-shell structure covered with a coating layer (shell layer) made of a semiconductor material may be used. In the latter case, as the semiconductor material constituting the shell layer, a material having a larger band gap energy than that of the semiconductor material constituting the core layer is usually used. The semiconductor quantum dot may have two or more shell layers. The shape of the semiconductor quantum dot is not particularly limited, and may be, for example, spherical or substantially spherical, rod-shaped, disk-shaped, or the like.

The semiconductor particle (A) may be a ligand-containing semiconductor particle containing an organic ligand coordinated to the semiconductor particle. The organic ligand coordinated to the semiconductor particles can be, for example, an organic compound having a polar group that exhibits coordination ability to the semiconductor particles. The organic ligand contained in the ligand-containing semiconductor particles may be an organic ligand added for stabilization due to restrictions in the synthesis of the ligand-containing semiconductor particles. For example, in JP-T-2015-529698, the ligand-containing semiconductor particles contain hexanoic acid as an organic ligand from the viewpoint of particle size control, and the organic ligand is used for stabilization after synthesis. Substitution with DDSA (dodecenyl succinic acid).
The organic ligand can be coordinated to the surface of the semiconductor particle, for example.

  The organic ligand coordinated to the semiconductor particles may be one type of ligand or two or more types of ligand. When the organic ligand is an organic compound having a polar group, the organic ligand is usually coordinated to the semiconductor particles via the polar group. The coordination of the organic ligand is confirmed by the uniform dispersion of the semiconductor particles in a dispersion medium suitable for the organic ligand.

The polar group is preferably at least one group selected from the group consisting of, for example, a thiol group (—SH), a carboxyl group (—COOH), and an amino group (—NH ₂ ). A polar group selected from this group can be advantageous in enhancing the coordination properties to the semiconductor particles. The high coordination property can contribute to improvement in color unevenness of the cured film and / or improvement in patterning property of the curable resin composition. Among these, from the viewpoint of obtaining a cured film (wavelength conversion film or the like) that is superior in light emission characteristics, the polar group is more preferably at least one group selected from the group consisting of a thiol group and a carboxyl group. The organic ligand can have one or more polar groups.

  The molecular weight of the organic ligand coordinated to the semiconductor particles is not particularly limited, but is, for example, 50 or more and 500 or less, and preferably 80 or more and 400 or less. When the molecular weight of the organic ligand is within this range, the ligand-containing semiconductor particles (A) can be prepared with excellent reproducibility.

Examples of the organic ligand include the following formula:
Y-Z
It can be an organic compound represented by: In the formula, Y is the above-mentioned polar group, and Z is a monovalent hydrocarbon group which may contain a hetero atom (N, O, S, halogen atom, etc.). The hydrocarbon group may have one or more unsaturated bonds such as a carbon-carbon double bond. The hydrocarbon group may have a linear, branched or cyclic structure. Carbon number of this hydrocarbon group is 1-40, for example, and may be 1-30. The methylene group contained in the hydrocarbon group includes —O—, —S—, —C (═O) —, —C (═O) —O—, —O—C (═O) —, —C ( ═O) -NH—, —NH— or the like may be substituted. In many cases, the hydrocarbon group usually does not contain a heteroatom because of easy preparation of the ligand-containing semiconductor particles.
The organic ligand represented by YZ is preferably a saturated fatty acid having 5 to 12 carbon atoms or an unsaturated fatty acid having 5 to 12 carbon atoms.

  The group Z may contain a polar group. For specific examples of the polar group, the above description concerning the polar group Y is cited. In general, the group Z often does not contain a polar group because of the ease of preparation of the ligand-containing semiconductor particles.

  Specific examples of the organic ligand having a carboxyl group as the polar group Y include saturated or unsaturated fatty acids in addition to formic acid, acetic acid, and propionic acid. Specific examples of saturated or unsaturated fatty acids include butyric acid, pentanoic acid, caproic acid, caprylic acid, capric acid, lauric acid, myristic acid, pentadecylic acid, palmitic acid, margaric acid, stearic acid, arachidic acid, behenic acid, lignoserine Saturated fatty acids such as acids; monounsaturated fatty acids such as myristoleic acid, palmitoleic acid, oleic acid, icosenoic acid, erucic acid, nervonic acid; linoleic acid, α-linolenic acid, γ-linolenic acid, steadolinic acid, dihomo- It contains polyunsaturated fatty acids such as γ-linolenic acid, arachidonic acid, eicosatetraenoic acid, docosadienoic acid, and adrenic acid (docosatetraenoic acid).

  Specific examples of the organic ligand having a thiol group or an amino group as the polar group Y include an organic ligand in which the carboxyl group of the organic ligand having the carboxyl group as the polar group Y exemplified above is replaced with a thiol group or an amino group. Includes a scale.

  The content of the semiconductor particles (A) is, for example, 0.1 parts by mass or more and 50 parts by mass or less, preferably 1 part by mass or more and 45 parts by mass or less, in 100 parts by mass of the solid content of the curable resin composition. More preferably, they are 5 to 40 mass parts. When the content of the semiconductor particles (A) is within the above range, sufficient light emission intensity is obtained in the cured film (wavelength conversion film or the like) and the patterning property tends to be excellent. In the present specification, the “solid content of the curable resin composition” refers to the total of components other than the organic solvent (D) contained in the curable resin composition.

[2] Resin (B)
The curable resin composition contains a resin (B). The curable resin composition can contain one or more resins as the resin (B). The resin (B) is preferably an alkali-soluble resin. Alkali-soluble refers to the property of being dissolved in a developer which is an aqueous solution of an alkali compound. Examples of the resin (B) include the following resins [K1] to [K6].

Resin [K1]: At least one selected from the group consisting of an unsaturated carboxylic acid and an unsaturated carboxylic acid anhydride (a) [hereinafter also referred to as “(a)”. ] And a monomer (b) having a cyclic ether structure having 2 to 4 carbon atoms and an ethylenically unsaturated bond [hereinafter also referred to as “(b)”. A copolymer with
Resin [K2]: (a) and (b), monomer (c) copolymerizable with (a) (however, different from (a) and (b)) [hereinafter referred to as “(c) " A copolymer with
Resin [K3]: a copolymer of (a) and (c),
Resin [K4]: a resin obtained by reacting (b) with a copolymer of (a) and (c),
Resin [K5]: a resin obtained by reacting (a) with a copolymer of (b) and (c),
Resin [K6]: A resin obtained by reacting (a) with a copolymer of (b) and (c) and further reacting with a carboxylic acid anhydride.

Specifically, as (a),
(Meth) acrylic acid, crotonic acid, o-, m-, p-vinylbenzoic acid, succinic acid mono [2- (meth) acryloyloxyethyl], phthalic acid mono [2- (meth) acryloyloxyethyl], etc. Unsaturated monocarboxylic acids;
Maleic acid, fumaric acid, citraconic acid, mesaconic acid, itaconic acid, 3-vinylphthalic acid, 4-vinylphthalic acid, 3,4,5,6-tetrahydrophthalic acid, 1,2,3,6-tetrahydrophthalic acid, dimethyl Unsaturated dicarboxylic acids such as tetrahydrophthalic acid and 1,4-cyclohexene dicarboxylic acid;
Methyl-5-norbornene-2,3-dicarboxylic acid, 5-carboxybicyclo [2.2.1] hept-2-ene, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene, 5-carboxy-5-methylbicyclo [2.2.1] hept-2-ene, 5-carboxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-carboxy-6-methylbicyclo Bicyclounsaturated compounds containing a carboxy group such as [2.2.1] hept-2-ene, 5-carboxy-6-ethylbicyclo [2.2.1] hept-2-ene;
Maleic anhydride, citraconic anhydride, itaconic anhydride, 3-vinylphthalic anhydride, 4-vinylphthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, 1,2,3,6- Unsaturated dicarboxylic acid anhydrides such as tetrahydrophthalic anhydride, dimethyltetrahydrophthalic anhydride, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene anhydride (hymic acid anhydride);
Examples thereof include unsaturated (meth) acrylic acids containing a hydroxy group and a carboxy group in the same molecule, such as α- (hydroxymethyl) (meth) acrylic acid.

  In this specification, “(meth) acryl” represents at least one selected from the group consisting of acryl and methacryl. The same applies to notations such as “(meth) acryloyl” and “(meth) acrylate”.

  (B) has a cyclic ether structure having 2 to 4 carbon atoms (for example, at least one selected from the group consisting of an oxirane ring, an oxetane ring and a tetrahydrofuran ring (oxolane ring)) and an ethylenically unsaturated bond. It refers to a polymerizable compound. (B) is preferably a monomer having a cyclic ether structure having 2 to 4 carbon atoms and a (meth) acryloyloxy group.

  As (b), for example, a monomer (b1) having an oxiranyl group and an ethylenically unsaturated bond [hereinafter also referred to as “(b1)”. ], A monomer (b2) having an oxetanyl group and an ethylenically unsaturated bond [hereinafter also referred to as “(b2)”]. ] A monomer (b3) having a tetrahydrofuryl group and an ethylenically unsaturated bond [hereinafter also referred to as “(b3)”]. ] Etc. are mentioned.

  As (b1), a monomer (b1-1) having a structure obtained by epoxidizing an unsaturated aliphatic hydrocarbon [hereinafter also referred to as “(b1-1)”. ], Monomer (b1-2) having a structure obtained by epoxidizing unsaturated alicyclic hydrocarbon [hereinafter also referred to as “(b1-2)”. ].

  As (b1-1), glycidyl (meth) acrylate, β-methylglycidyl (meth) acrylate, β-ethylglycidyl (meth) acrylate, glycidyl vinyl ether, o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, p -Vinylbenzyl glycidyl ether, α-methyl-o-vinylbenzyl glycidyl ether, α-methyl-m-vinylbenzyl glycidyl ether, α-methyl-p-vinylbenzyl glycidyl ether, 2,3-bis (glycidyloxymethyl) styrene 2,4-bis (glycidyloxymethyl) styrene, 2,5-bis (glycidyloxymethyl) styrene, 2,6-bis (glycidyloxymethyl) styrene, 2,3,4-tris (glycidyloxymethyl) styrene 2,3,5-tris (glycidyloxymethyl) styrene, 2,3,6-tris (glycidyloxymethyl) styrene, 3,4,5-tris (glycidyloxymethyl) styrene, 2,4,6- Examples include tris (glycidyloxymethyl) styrene.

Examples of (b1-2) include vinylcyclohexene monooxide, 1,2-epoxy 4-vinylcyclohexane (for example, Celoxide 2000; manufactured by Daicel Chemical Industries, Ltd.), 3,4-epoxycyclohexylmethyl (meth) acrylate (for example, , Cyclomer A400; manufactured by Daicel Chemical Industries, Ltd.), 3,4-epoxycyclohexylmethyl (meth) acrylate (for example, Cyclomer M100; manufactured by Daicel Chemical Industries, Ltd.), 3,4-epoxytricyclo [5 .2.1.0 ^2,6 ] decyl (meth) acrylate and the like.

  The monomer (b2) having an oxetanyl group and an ethylenically unsaturated bond is preferably a monomer having an oxetanyl group and a (meth) acryloyloxy group. Preferred examples of (b2) include 3-methyl-3- (meth) acryloyloxymethyl oxetane, 3-ethyl-3- (meth) acryloyloxymethyl oxetane, 3-methyl-3- (meth) acryloyloxyethyl oxetane, 3-ethyl-3- (meth) acryloyloxyethyl oxetane.

  The monomer (b3) having a tetrahydrofuryl group and an ethylenically unsaturated bond is preferably a monomer having a tetrahydrofuryl group and a (meth) acryloyloxy group. Preferable examples of (b3) include tetrahydrofurfuryl acrylate (for example, Biscoat V # 150, manufactured by Osaka Organic Chemical Industry Co., Ltd.), tetrahydrofurfuryl methacrylate and the like.

Specific examples of (c) are:
Methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, sec-butyl (meth) acrylate, tert-butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, dodecyl (meth) acrylate, Lauryl (meth) acrylate, stearyl (meth) acrylate, cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-methylcyclohexyl (meth) acrylate, tricyclo [5.2.1.0 ^2,6 ] decane-8- Ile (meth) acrylate [in this technical field, it is called "dicyclopentanyl (meth) acrylate" as a common name. It may also be called “tricyclodecyl (meth) acrylate”. ], Tricyclo [5.2.1.0 ^2,6 ] decen-8-yl (meth) acrylate [in this technical field, it is called "dicyclopentenyl (meth) acrylate" as a common name. ], Dicyclopentanyloxyethyl (meth) acrylate, isobornyl (meth) acrylate, adamantyl (meth) acrylate, allyl (meth) acrylate, propargyl (meth) acrylate, phenyl (meth) acrylate, naphthyl (meth) acrylate, benzyl (Meth) acrylic acid esters such as (meth) acrylate;
Hydroxy group-containing (meth) acrylic acid esters such as 2-hydroxyethyl (meth) acrylate and 2-hydroxypropyl (meth) acrylate;
Dicarboxylic acid diesters such as diethyl maleate, diethyl fumarate, diethyl itaconate;
Bicyclo [2.2.1] hept-2-ene, 5-methylbicyclo [2.2.1] hept-2-ene, 5-ethylbicyclo [2.2.1] hept-2-ene, 5- Hydroxybicyclo [2.2.1] hept-2-ene, 5-hydroxymethylbicyclo [2.2.1] hept-2-ene, 5- (2′-hydroxyethyl) bicyclo [2.2.1] Hept-2-ene, 5-methoxybicyclo [2.2.1] hept-2-ene, 5-ethoxybicyclo [2.2.1] hept-2-ene, 5,6-dihydroxybicyclo [2.2 .1] Hept-2-ene, 5,6-di (hydroxymethyl) bicyclo [2.2.1] hept-2-ene, 5,6-di (2′-hydroxyethyl) bicyclo [2.2. 1] hept-2-ene, 5,6-dimethoxybicyclo [2.2 1] hept-2-ene, 5,6-diethoxybicyclo [2.2.1] hept-2-ene, 5-hydroxy-5-methylbicyclo [2.2.1] hept-2-ene, 5 -Hydroxy-5-ethylbicyclo [2.2.1] hept-2-ene, 5-hydroxymethyl-5-methylbicyclo [2.2.1] hept-2-ene, 5-tert-butoxycarbonylbicyclo [ 2.2.1] Hept-2-ene, 5-cyclohexyloxycarbonylbicyclo [2.2.1] hept-2-ene, 5-phenoxycarbonylbicyclo [2.2.1] hept-2-ene, 5 , 6-bis (tert-butoxycarbonyl) bicyclo [2.2.1] hept-2-ene, 5,6-bis (cyclohexyloxycarbonyl) bicyclo [2.2.1] hept-2-ene, etc. Bicyclounsaturated compounds;
N-phenylmaleimide, N-cyclohexylmaleimide, N-benzylmaleimide, N-succinimidyl-3-maleimidobenzoate, N-succinimidyl-4-maleimidobutyrate, N-succinimidyl-6-maleimidocaproate, N-succinimidyl-3 -Dicarbonylimide derivatives such as maleimide propionate, N- (9-acridinyl) maleimide;
Styrene, α-methylstyrene, m-methylstyrene, p-methylstyrene, vinyl toluene, p-methoxystyrene, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, acrylamide, methacrylamide, vinyl acetate, 1,3-butadiene , Isoprene, 2,3-dimethyl-1,3-butadiene and the like.

  Among these, from the viewpoint of copolymerization reactivity, heat resistance, developability during patterning, and the like, (c) is methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, benzyl (meth) acrylate. , Tricyclodecyl (meth) acrylate, dicyclopentenyl (meth) acrylate, styrene, N-phenylmaleimide, N-cyclohexylmaleimide, N-benzylmaleimide, bicyclo [2.2.1] hept-2-ene and the like are preferable. .

In the resin [K1], the ratio of the structural units derived from each is preferably in the following range among all the structural units constituting the resin [K1].
A structural unit derived from (a); 2 mol% or more and 50 mol% or less (more preferably 10 mol% or more and 45 mol% or less);
A structural unit derived from (b), particularly a structural unit derived from (b1); 50 mol% or more and 98 mol% or less (more preferably 55 mol% or more and 90 mol% or less).

  When the ratio of the structural unit of the resin [K1] is in the above range, the storage stability, developability, and solvent resistance of the resulting pattern tend to be excellent.

  Resin [K1] is described in the document “Experimental Method for Polymer Synthesis” (Takayuki Otsu, published by Kagaku Dojin Co., Ltd., 1st edition, 1st edition, published on March 1, 1972) and the document. It can be produced with reference to the cited references.

  Specifically, there is a method in which a predetermined amount of (a) and (b) (particularly (b1)), a polymerization initiator, a solvent, and the like are charged into a reaction vessel and stirred, heated, and kept warm in a deoxygenated atmosphere. Can be mentioned. In addition, the polymerization initiator, the solvent, and the like used here are not particularly limited, and any of those usually used in the field can be used. Examples of the polymerization initiator include azo compounds (such as 2,2′-azobisisobutyronitrile and 2,2′-azobis (2,4-dimethylvaleronitrile)) and organic peroxides (such as benzoyl peroxide). It is done. Any solvent may be used as long as it dissolves each monomer, and an organic solvent (D) described later may be used.

  In addition, the obtained copolymer may use the solution after reaction as it is, a concentrated or diluted solution may be used, and it took out as solid (powder) by methods, such as reprecipitation. Things may be used.

In the resin [K2], the ratio of the structural units derived from each is preferably within the following range among all the structural units constituting the resin [K2].
A structural unit derived from (a); 4 mol% or more and 45 mol% or less (more preferably 10 mol% or more and 30 mol% or less);
A structural unit derived from (b), particularly a structural unit derived from (b1); 2 mol% or more and 95 mol% or less (more preferably 5 mol% or more and 80 mol% or less),
Structural unit derived from (c): 1 mol% or more and 65 mol% or less (more preferably 5 mol% or more and 60 mol% or less).

  When the ratio of the structural unit of the resin [K2] is in the above range, the storage stability, developability, solvent resistance of the resulting pattern, heat resistance and mechanical strength tend to be excellent.

  Resin [K2] can be produced in the same manner as described for the production method of resin [K1]. Specifically, a predetermined amount of (a), (b) (particularly (b1)) and (c), a polymerization initiator and a solvent are charged into a reaction vessel, and the mixture is stirred, heated and kept warm in a deoxygenated atmosphere. The method of doing is mentioned. As the obtained copolymer, the solution after the reaction may be used as it is, a concentrated or diluted solution may be used, or a solid (powder) taken out by a method such as reprecipitation. May be used.

In the resin [K3], the ratio of the structural unit derived from each is preferably in the following range among all the structural units constituting the resin [K3].
A structural unit derived from (a); 2 mol% or more and 55 mol% or less (more preferably 10 mol% or more and 50 mol% or less);
Structural unit derived from (c); 45 mol% or more and 98 mol% or less (more preferably 50 mol% or more and 90 mol% or less).

  Resin [K3] can be produced in the same manner as described for the production method of resin [K1].

Resin [K4] obtains a copolymer of (a) and (c), and (b) has a cyclic ether structure having 2 to 4 carbon atoms, particularly (b1) having an oxirane ring (a). Can be produced by adding to a carboxylic acid and / or a carboxylic acid anhydride. Specifically, first, a copolymer of (a) and (c) is produced in the same manner as the method described as the production method of the resin [K1]. In this case, the ratio of the structural units derived from each is preferably in the following range among all the structural units constituting the copolymer of (a) and (c).
A structural unit derived from (a); 5 mol% or more and 50 mol% or less (more preferably 10 mol% or more and 45 mol% or less);
Structural unit derived from (c); 50 mol% or more and 95 mol% or less (more preferably 55 mol% or more and 90 mol% or less).

  Next, in part of the carboxylic acid and / or carboxylic anhydride derived from (a) in the copolymer, a cyclic ether structure having 2 to 4 carbon atoms, particularly (b1), (b) has. The oxirane ring is reacted. Specifically, following the production of the copolymer of (a) and (c), the atmosphere in the flask is replaced with nitrogen to air, and (b) (particularly (b1)), carboxylic acid or carboxylic anhydride And a reaction catalyst (for example, tris (dimethylaminomethyl) phenol) and a polymerization inhibitor (for example, hydroquinone) are placed in a flask and the temperature is 60 ° C. or higher and 130 ° C. or lower and 1 hour or longer and 10 hours or shorter. The resin [K4] can be obtained by reacting with the reaction time of

  The use amount of (b), particularly the use amount of (b1), is preferably 5 mol or more and 80 mol or less, more preferably 10 mol or more and 75 mol or less with respect to 100 mol of (a). By setting it as this range, there exists a tendency for the balance of storage stability, developability, solvent resistance, heat resistance, mechanical strength, and sensitivity to become favorable. Since the reactivity of the cyclic ether structure is high and unreacted (b) hardly remains, (b1) is preferable as (b) used in the resin [K4], and (b1-1) is more preferable.

  The amount of the reaction catalyst used is preferably 0.001% by mass to 5% by mass with respect to the total amount of (a), (b) (particularly (b1)) and (c). The amount of the polymerization inhibitor used is preferably 0.001% by mass or more and 5% by mass or less based on the total amount of (a), (b) and (c).

  The reaction conditions such as the charging method, reaction temperature, and time can be appropriately adjusted in consideration of the production equipment and the amount of heat generated by polymerization. In addition, like the polymerization conditions, the charging method and the reaction temperature can be appropriately adjusted in consideration of the production equipment, the amount of heat generated by the polymerization, and the like.

  Resin [K5] obtains a copolymer of (b) (particularly (b1)) and (c) in the same manner as in the method for producing resin [K1] described above. Similarly to the above, the obtained copolymer may be used as it is after the reaction, or may be a concentrated or diluted solution, or may be solid (powder) by a method such as reprecipitation. You may use what was taken out as.

The ratio of the structural units derived from (b) (particularly (b1)) and (c) is preferably in the following range with respect to the total number of moles of all structural units constituting the copolymer.
A structural unit derived from (b), particularly a structural unit derived from (b1); 5 mol% or more and 95 mol% or less (more preferably 10 mol% or more and 90 mol% or less),
Structural unit derived from (c); 5 mol% or more and 95 mol% or less (more preferably 10 mol% or more and 90 mol% or less).

  Furthermore, under the same conditions as in the production method of the resin [K4], the cyclic ether structure derived from (b) of the copolymer of (b) (particularly (b1)) and (c), The resin [K5] can be obtained by reacting the carboxylic acid or carboxylic anhydride having the resin. The amount of (a) to be reacted with the copolymer is preferably 5 mol or more and 80 mol or less with respect to 100 mol of (b) (particularly (b1)). Since the reactivity of the cyclic ether structure is high and unreacted (b) hardly remains, (b1) is preferable as (b) used in the resin [K5], and (b1-1) is more preferable.

  Resin [K6] is a resin obtained by further reacting carboxylic anhydride with resin [K5]. Carboxylic anhydride is reacted with the hydroxy group generated by the reaction of the cyclic ether structure with carboxylic acid or carboxylic anhydride.

  Carboxylic anhydrides include maleic anhydride, citraconic anhydride, itaconic anhydride, 3-vinylphthalic anhydride, 4-vinylphthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, 1 2,3,6-tetrahydrophthalic anhydride, dimethyltetrahydrophthalic anhydride, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene anhydride (highmic acid anhydride) and the like. It is done.

  Among them, the resin (B) is a carboxyl group (—COOH) and / or a carboxylic anhydride group (—C (═O) —O—C (═O) —) bonded to the molecular main chain via a linking group. It is preferable that resin (B-1) which has this is included. The linking group is a group that is not a direct bond and connects the molecular main chain of the polymer to a carboxyl group and / or a carboxylic anhydride group, for example, a hydrocarbon group having 1 or more carbon atoms. The hydrocarbon group may include a linear, branched and / or cyclic structure. One or more methylene groups contained in the hydrocarbon group are -O-, -S-, -C (= O)-, -C (= O) -O-, -O-C (= O). It may be substituted with —, —C (═O) —NH—, —NH— or the like.

  The linking group may have one bond with the molecular main chain of the polymer, or may have two or more bonds. When the resin (B-1) has a carboxylic anhydride group, the linking group has two bonds with the carboxylic anhydride group.

  The resin (B) containing the resin (B-1) can contribute to enhancing the dispersibility of the semiconductor particles (A) in the curable resin composition. This is because the resin having a polar group can coordinate to the semiconductor particles via the polar group, and the carboxyl group and / or carboxylic anhydride group of the resin (B-1) has a relatively high coordination ability. This is considered to be because the effect of enhancing the dispersibility of the semiconductor particles (A) is further enhanced by the coordination to the semiconductor particles based on this high coordination ability. The high dispersibility of the semiconductor particles (A) contributes to the reduction of the surface roughness of the cured film such as the wavelength conversion film and the resulting color unevenness, as well as the enhancement of the in-plane uniformity of the emission characteristics of the cured film. obtain.

  As the resin (B-1), a carboxyl group and / or a carboxylic acid anhydride group bonded to the molecular main chain via a linking group, and a carboxyl group and / or a carboxylic acid anhydride group directly bonded to the molecular main chain And a resin (B-1b) in which all carboxyl groups and / or carboxylic anhydride groups are bonded to the molecular main chain via a linking group.

  Resin (B-1a) is composed of a structural unit having a carboxyl group and / or a carboxylic acid anhydride group bonded to the molecular main chain through a linking group, and a carboxyl group and / or a carboxylic acid anhydride bonded directly to the molecular main chain. It is preferable that it is a copolymer containing the structural unit which has a physical group. Resin (B-1b) comprises a structural unit having a carboxyl group and / or carboxylic anhydride group bonded to the molecular main chain via a linking group, and a carboxyl group and / or carboxylic acid anhydride bonded directly to the molecular main chain. A copolymer containing a structural unit having no physical group is preferable.

  The resin (B) may contain a resin (B-2) in which all carboxyl groups and / or carboxylic anhydride groups are directly bonded to the molecular main chain.

  Resin (B-1a), Resin (B-1b), and Resin (B-2) are at least one selected from the group consisting of the above unsaturated carboxylic acids and unsaturated carboxylic anhydrides. It can be prepared by using as a monomer. Each of the resin (B-1a), the resin (B-1b), and the resin (B-2) can be prepared by selecting an appropriate monomer as (a). Although the specific example of (a) is as above-mentioned, it is not limited to this specific example.

  In order to introduce a carboxyl group and / or a carboxylic anhydride group bonded to the molecular main chain through a linking group into the resin, (a) is exemplified by vinyl benzoic acid, 1,2,3,6-tetrahydrophthal Acid, 1,2,3,6-tetrahydrophthalic anhydride, methyl-5-norbornene-2,3-dicarboxylic acid, methyl-5-norbornene-2,3-dicarboxylic acid anhydride and the like can be used.

  In order to introduce a carboxyl group and / or a carboxylic acid anhydride group bonded to the molecular main chain through a linking group into the resin, (a) is, for example, 1 of the monomer represented by the following formula (a1) More than seeds can also be used.

［式（ａ１）中、
Ｒ^１は、水素原子又はメチル基を表す。
Ｒ^２は、炭素数２〜６のアルカンジイル基若しくは炭素数５〜１２のシクロアルカンジイル基を表すか、又はＹが水素原子でない場合には該アルカンジイル基から１個の水素原子を引き抜いた３価の基を表す。
Ｒ^３は、炭素数２〜６のアルカンジイル基、炭素数５〜１２のシクロアルカンジイル基若しくは炭素数５〜１２のシクロアルケンジイル基を表すか、又は２価の芳香族基を表す。
Ｙは、水素原子又は炭素数１〜８のアルキル基であり、該アルキル基に含まれるメチレン基は、−Ｏ−、−Ｓ−、−Ｃ（＝Ｏ）−、−Ｃ（＝Ｏ）−Ｏ−、−Ｏ−Ｃ（＝Ｏ）−、−Ｃ（＝Ｏ）−ＮＨ−又は−ＮＨ−で置換されていてもよい。

[In the formula (a1),
R ¹ represents a hydrogen atom or a methyl group.
R ² represents an alkanediyl group having 2 to 6 carbon atoms or a cycloalkanediyl group having 5 to 12 carbon atoms, or when Y is not a hydrogen atom, one hydrogen atom was extracted from the alkanediyl group. Represents a trivalent group.
R ³ represents an alkanediyl group having 2 to 6 carbon atoms, a cycloalkanediyl group having 5 to 12 carbon atoms, a cycloalkenediyl group having 5 to 12 carbon atoms, or a divalent aromatic group.
Y is a hydrogen atom or an alkyl group having 1 to 8 carbon atoms, and the methylene group contained in the alkyl group is -O-, -S-, -C (= O)-, -C (= O)-. O—, —O—C (═O) —, —C (═O) —NH— or —NH— may be substituted.

Examples of the alkanediyl group having 2 to 6 carbon atoms in R ² and R ³ include an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl group, Linear alkanediyl group such as hexane-1,6-diyl group; ethane-1,1-diyl group, propane-1,2-diyl group, butane-1,3-diyl group, 2-methylpropane-1 , 3-diyl group, 2-methylpropane-1,2-diyl group, pentane-1,4-diyl group, 2-methylbutane-1,4-diyl group, and the like.

Examples of the cycloalkanediyl group having 5 to 12 carbon atoms in R ² and R ³ include cyclopentane-1,2-diyl group, cyclopentane-1,3-diyl group, and cyclopentane-1,4-diyl group. , Cyclohexane-1,2-diyl group, cyclohexane-1,3-diyl group, cyclohexane-1,4-diyl group, cycloheptane-1,2-diyl group, cycloheptane-1,3-diyl group, cycloheptane -1,4-diyl group, adamantane-1,2 diyl group, adamantane-1,3 diyl group and the like can be mentioned.

Examples of the cycloalkenediyl group having 5 to 12 carbon atoms in R ³ include groups in which any carbon-carbon single bond in the ring structure of the cycloalkanediyl group is replaced with a carbon-carbon double bond.

Examples of the divalent aromatic group in R ³ include benzene-1,2-diyl group, benzene-1,3-diyl group, benzene-1,4-diyl group, naphthalene-1,2-diyl group, Naphthalene-1,3-diyl group, naphthalene-1,4-diyl group, naphthalene-1,5-diyl group, naphthalene-1,8-diyl group, naphthalene-2,3-diyl group, naphthalene-2,4 -A diyl group, naphthalene-2,6-diyl group, etc. are mentioned.

  Examples of the alkyl group having 1 to 8 carbon atoms in Y include linear or branched alkyl groups such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, a pentyl group, and an octyl group. .

  Examples of the monomer represented by the formula (a1) include monocarboxylic acid mono [2- (meth) acryloyloxyethyl] and phthalic acid mono [2- (meth) acryloyloxyethyl]. [(Meth) acryloyloxyalkyl] esters and the like. Use of the monomer represented by the above formula (a1) such as mono [(meth) acryloyloxyalkyl] esters of dicarboxylic acid is advantageous from the viewpoint of dispersibility of the semiconductor particles (A) in the organic solvent. .

  In order to introduce a carboxyl group and / or a carboxylic anhydride group directly bonded to the molecular main chain into the resin, (a) can be used, for example, (meth) acrylic acid, crotonic acid, maleic acid, fumaric acid, maleic anhydride 3,4,5,6-tetrahydrophthalic acid, 3,4,5,6-tetrahydrophthalic anhydride and the like can be used. (Meth) acrylic acid, maleic anhydride and the like are preferable from the viewpoint of copolymerization reactivity and the solubility of the resulting resin in an alkaline aqueous solution.

Resin (B) includes the following [i] and [ii]:
[I] Resin having a carboxyl group and / or carboxylic anhydride group bonded to the molecular main chain via a linking group and a carboxyl group and / or carboxylic anhydride group directly bonded to the molecular main chain (B- Including 1a),
[Ii] Resin (B-1b) in which all carboxyl groups and / or carboxylic anhydride groups are bonded to the molecular main chain via a linking group, and all carboxyl groups and / or carboxylic anhydride groups Including a resin (B-2) directly bonded to the molecular main chain,
It is preferable to satisfy any of the following.

  Satisfying one or both of the above [i] and [ii] can contribute to enhancing the dispersibility of the semiconductor particles (A) in the curable resin composition, and It can contribute to the improvement of patterning property.

  In the above [i], the resin (B) may contain only the resin (B-1a), may contain the resin (B-1a) and the resin (B-1b), or may contain the resin (B -1a) and resin (B-2) may be included.

  The resin (B) is preferably made of the resin (B-1), more preferably made of the resin (B-1), and more preferably containing the resin (B-1a).

  Among the acid values represented by the resin (B), an acid value X based on a carboxyl group and / or a carboxylic anhydride group directly bonded to the molecular main chain, a carboxyl group bonded to the molecular main chain via a linking group, and / or Alternatively, the ratio X / Y with the acid value Y based on the carboxylic anhydride group is, for example, (0 mg-KOH / g or more and 150 mg-KOH / g or less) / (20 mg-KOH / g or more and 150 mg-KOH / g or less). And preferably (40 mg-KOH / g or more and 100 mg-KOH / g or less) / (40 mg-KOH / g or more and 120 mg-KOH / g or less), more preferably (40 mg-KOH / g or more and 80 mg-KOH or less). / G or less) / (60 mg-KOH / g or more and 90 mg-KOH / g or less). When the ratio X / Y is within the above range, the dispersibility of the resin (B) and the developability (development speed and patternability) of the curable resin composition can be improved. The high dispersibility of the resin (B) also contributes to the reduction of the surface roughness of the cured film such as the wavelength conversion film and the resulting reduction in color unevenness, and thus the in-plane uniformity of the light emission characteristics of the cured film. obtain.

The acid value of the resin (B) is, for example, 20 mg-KOH / g or more and 200 mg-KOH / g or less, preferably 40 mg-KOH / g or more and 170 mg-KOH / g or less, more preferably 60 mg-KOH / g. It is 150 mg-KOH / g or less. When the acid value of the resin (B) is in the above range, both developability and high dispersibility can be achieved.
The acid value is a value measured as the amount (mg) of potassium hydroxide necessary to neutralize 1 g of the resin, and can be determined, for example, by titration using an aqueous potassium hydroxide solution.

The solution acid value of the resin (B) is preferably 5 mg-KOH / g or more and 180 mg-KOH / g or less, more preferably 10 mg-KOH / g or more and 100 mg-KOH / g or less, and further preferably 12 mg- KOH / g or more and 50 mg-KOH / g or less. The solution acid value is a value measured as the amount (mg) of potassium hydroxide necessary to neutralize 1 g of the resin solution, and can be determined by titration using an aqueous potassium hydroxide solution, for example.
The solution acid value is a value measured by dissolving the resin (B) in a predetermined solvent, and the resin concentration of the solution is, for example, 10% by mass or more and 50% by mass or less.
When the solution acid value of the resin (B) is in the above range, both the semiconductor particles and the resin (B) can be mixed without agglomeration.

  The polystyrene equivalent weight average molecular weight of the resin (B) is preferably 3000 or more and 100,000 or less, more preferably 5000 or more and 50000 or less, and further preferably 5000 or more and 30000 or less. When the molecular weight is in the above range, the solubility of the unexposed area in the developer is high, and the residual film ratio and hardness of the resulting pattern tend to be high. The molecular weight distribution [weight average molecular weight (Mw) / number average molecular weight (Mn)] of the resin (B) is preferably 1.1 or more and 6 or less, more preferably 1.2 or more and 4 or less.

  The content of the resin (B) is preferably 5% by mass or more and 70% by mass or less, more preferably 10% by mass or more and 65% by mass or less, in a solid content of 100% by mass of the curable resin composition. Preferably they are 15 mass% or more and 60 mass% or less. When content of resin (B) exists in the said range, there exists a tendency for the solubility with respect to the developing solution of an unexposed part to be high.

[3] Polymerizable compound (C)
The polymerizable compound (C) is not particularly limited as long as it is a compound that can be polymerized by an active radical generated from the polymerization initiator (E) by light irradiation or the like, and a compound having a polymerizable ethylenically unsaturated bond, etc. Is mentioned. The weight average molecular weight of the polymerizable compound (C) is preferably 3000 or less.

  Among these, the polymerizable compound (C) is preferably a photopolymerizable compound having three or more ethylenically unsaturated bonds. Specific examples of the photopolymerizable compound having three or more ethylenically unsaturated bonds include trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) ) Acrylate, dipentaerythritol hexa (meth) acrylate, tripentaerythritol octa (meth) acrylate, tripentaerythritol hepta (meth) acrylate, tetrapentaerythritol deca (meth) acrylate, tetrapentaerythritol nona (meth) acrylate, tris ( 2- (meth) acryloyloxyethyl) isocyanurate, ethylene glycol modified pentaerythritol tetra (meth) acrylate, ethylene glycol modified Dipentaerythritol hexa (meth) acrylate, propylene glycol modified pentaerythritol tetra (meth) acrylate, propylene glycol modified dipentaerythritol hexa (meth) acrylate, caprolactone modified pentaerythritol tetra (meth) acrylate, caprolactone modified dipentaerythritol hexa (meta) ) Acrylate and the like.

  The curable resin composition can contain one or more polymerizable compounds (C). The content of the polymerizable compound (C) is preferably 20 parts by mass or more and 150 parts by mass or less, more preferably 80 parts by mass or more and 120 parts by mass with respect to 100 parts by mass of the resin (B) in the curable resin composition. It is below mass parts.

[4] Organic solvent (D)
The curable resin composition contains an organic solvent (D). The organic solvent (D) includes a cycloalkane ring, an ether group (—O—), an ester group (—C (═O) —O—, —O—C (═O) —) and a carbonyl group (—C ( An organic solvent (D1) which is an organic compound having at least one group selected from the group consisting of = O)-). When the organic solvent (D) contains the organic solvent (D1), it is possible to form a cured film such as a wavelength conversion film having a small surface roughness and thereby reduced color unevenness. Such an organic solvent (D1) is likely to have an affinity for both the resin (B) and the semiconductor particles (A). Therefore, the resin (B) and the semiconductor particles are used in the liquid preparation step and the film forming step. It is considered that aggregation of (A) can be prevented. The curable resin composition can contain one or more organic solvents (D1).

  The organic solvent (D1) is preferably, for example, a compound represented by the following formula (1).

In the above formula (1),
Ring T represents a k-membered cycloalkane ring.
k represents an integer of 3 to 12.
X ¹ and X ² each independently represent —O—, —O—C (═O) —, —C (═O) —O— or —C (═O) —.
A ¹ represents an alkanediyl group having 1 to 12 carbon atoms or a cycloalkanediyl group having 3 to 12 carbon atoms.
A ² and A ⁴ each independently represent a monovalent hydrocarbon group having 1 to 12 carbon atoms.
A ³ represents a single bond, an alkanediyl group having 1 to 12 carbon atoms, or a cycloalkanediyl group having 3 to 12 carbon atoms.
m represents an integer of 1 to 6.
n represents an integer of 0 to 5.
p represents an integer of 0 to 5.
However, m + p is k or less.

  The inclusion of the organic solvent (D1) represented by the above formula (1) can be advantageous from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition.

  K representing the number of carbon atoms constituting the cycloalkane ring T is preferably an integer of 4 to 6 from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition. Specifically, the cycloalkane ring T is preferably a cyclobutane ring, a cycloheptane ring, or a cyclohexane ring.

A ¹ preferably represents an alkanediyl group having 1 to 6 carbon atoms or a cycloalkanediyl group having 3 to 6 carbon atoms from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition, More preferably, it represents an alkanediyl group having 1 to 3 carbon atoms or a cycloalkanediyl group having 4 to 6 carbon atoms. The alkanediyl group may be linear or branched.
Examples of the alkanediyl group having 1 to 6 carbon atoms include methylene group, ethylene group, propane-1,3-diyl group, propane-1,2-diyl group, butane-1,4-diyl group, and pentane-1,5. -Diyl group, hexane-1,6-diyl group, ethane-1,1-diyl group, butane-1,3-diyl group, 2-methylpropane-1,3-diyl group, 2-methylpropane-1, 2-diyl group, pentane-1,4-diyl group, 2-methylbutane-1,4-diyl group and the like can be mentioned.
Examples of the cycloalkanediyl group having 3 to 6 carbon atoms include cyclopropane-1,3-diyl group, cyclobutane-2,2-diyl group, cyclopentane-1,5-diyl group, and cyclohexane-1,6-diyl group. Etc.

The monovalent hydrocarbon group having 1 to 12 carbon atoms in A ² and A ⁴ is a linear or branched monovalent aliphatic hydrocarbon group, monovalent alicyclic hydrocarbon group, monovalent. And aromatic hydrocarbon groups and combinations thereof.
Examples of the linear or branched monovalent aliphatic hydrocarbon group include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, a sec-butyl group, a tert-butyl group, and a pentyl group. , Alkyl groups such as hexyl group, octyl group and 2-ethylhexyl group.
The monovalent alicyclic hydrocarbon group may be monocyclic or polycyclic. Examples of the monocyclic monovalent alicyclic hydrocarbon group include cycloalkyl groups such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, and a cyclodecyl group. Examples of the polycyclic monovalent alicyclic hydrocarbon group include a decahydronaphthyl group, an adamantyl group and a norbornyl group.
Examples of the monovalent aromatic hydrocarbon group include aryl groups such as phenyl group, tolyl group, xylyl group, and naphthyl group.
Examples of the group in which a monovalent aliphatic hydrocarbon group and a monovalent alicyclic hydrocarbon group are combined include a methylcyclohexyl group, a dimethylcyclohexyl group, and a methylnorbornyl group.
The monovalent hydrocarbon group having 1 to 12 carbon atoms is preferably an alkyl group having 1 to 6 carbon atoms from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition.

A ³ is preferably a single bond, an alkanediyl group having 1 to 6 carbon atoms or a cycloalkanediyl group having 3 to 6 carbon atoms from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition. And more preferably a single bond, an alkanediyl group having 1 to 3 carbon atoms, or a cycloalkanediyl group having 4 to 6 carbon atoms. The alkanediyl group may be linear or branched.
Specific examples of the cycloalkane-diyl group having 3 to 6 alkanediyl group and the number of carbon atoms of 1 to 6 carbon atoms are the same as specific examples exemplified for A ^1.

The total number of carbon atoms contained in A ^{1 to} A ⁴ is usually 1 to 24, and preferably 1 to 12 from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition.

m is preferably an integer of 1 to 3, more preferably an integer of 1 to 2, from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition.
n is preferably an integer of 0 to 3, more preferably an integer of 0 to 1, from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition.
From the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition, p preferably represents an integer of 0 to 3.

  The organic solvent (D1) includes two or more of the same groups selected from the group consisting of —O—, —O—C (═O) —, —C (═O) —O—, and —C (═O) —. It may have, and may have two or more different groups selected from the above group.

  Examples of the organic solvent (D1) include ester solvents (solvents containing a cycloalkyl ring and —C (═O) —O—), ether solvents other than ester solvents (solvents containing a cycloalkane ring and —O—), ethers. Ester solvents (solvents containing cycloalkane ring, -O-C (= O)-and / or -C (= O) -O-, and -O-), ketone solvents other than ester solvents (cycloalkane ring) And a solvent containing -C (= O)-).

  Examples of ester solvents include cyclohexyl acetate, 2-methylcyclohexyl acetate, cyclohexyl propionate, cis-3,3,5-trimethylcyclohexyl acetate, 4-tert-butylcyclohexyl acetate, cyclohexyl butyrate, isopropyl cyclohexanecarboxylate, ethyl cyclohexyl acetate, etc. Is mentioned.

  Examples of the ether solvent include methoxycyclohexane, ethoxycyclohexane, propoxycyclohexane, 1-methoxy-4-methylcyclohexane, 1,1-diisopropoxycyclohexane, and the like.

  Examples of the ether ester solvent include ethyl 2-ethoxycyclohexanecarboxylate.

  Examples of the ketone solvent include dicyclohexyl ketone, ethyl 3-cyclohexyl-3-oxopropionate, and cyclohexyl phenyl ketone.

  Among them, the organic solvent (D1) is cis-3,3,5-trimethylcyclohexyl acetate, 4-tert-butylcyclohexyl acetate, from the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition. Selected from the group consisting of cyclohexyl acetate, isopropyl cyclohexanecarboxylate, 1-methoxy-4-methylcyclohexane, 1,1-diisopropoxycyclohexane, dicyclohexyl ketone, ethyl 3-cyclohexyl-3-oxopropionate and cyclohexyl phenyl ketone It is preferable to include at least one organic solvent, and it is more preferable to include at least one selected from the group consisting of cyclohexyl acetate and isopropyl cyclohexanecarboxylate.

  The organic solvent (D) can include an organic solvent (D2) that is an organic solvent other than the organic solvent (D1). The curable resin composition can contain one or more organic solvents (D2). As the organic solvent (D2), ester solvents (solvents containing —C (═O) —O—), ether solvents other than ester solvents (solvents containing —O—), ether ester solvents (—C (═O)) Solvents containing -O- and -O-), ketone solvents other than ester solvents (solvents containing -C (= O)-), alcohol solvents, aromatic hydrocarbon solvents, amide solvents and dimethyl sulfoxide. .

  In the organic solvent (D2), at least one methylene group contained in the cycloalkyl ring is —O—, —S—, —C (═O) —, —C (═O) —O—, —O—C ( It may be a compound having the same structure as the organic solvent (D1) except that it is substituted with a group selected from ═O) —, —C (═O) —NH—, —NH— and the like.

  As ester solvents, methyl lactate, ethyl lactate, butyl lactate, methyl 2-hydroxyisobutanoate, ethyl acetate, n-butyl acetate, isobutyl acetate, pentyl formate, isopentyl acetate, butyl propionate, isopropyl butyrate, ethyl butyrate, butyl butyrate , Methyl pyruvate, ethyl pyruvate, propyl pyruvate, methyl acetoacetate, ethyl acetoacetate and γ-butyrolactone.

  Ether solvents include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether , Propylene glycol monopropyl ether, propylene glycol monobutyl ether, 3-methoxy-1-butanol, 3-methoxy-3-methylbutanol, tetrahydrofuran, tetrahydropyran, 1,4-dioxane, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethyl Glycol methyl ethyl ether, diethylene glycol dipropyl ether, diethylene glycol dibutyl ether, anisole, include phenetol and methyl anisole and the like.

  Examples of ether ester solvents include methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate, ethyl ethoxyacetate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, 3-ethoxy Ethyl propionate, methyl 2-methoxypropionate, ethyl 2-methoxypropionate, propyl 2-methoxypropionate, methyl 2-ethoxypropionate, ethyl 2-ethoxypropionate, methyl 2-methoxy-2-methylpropionate, Ethyl 2-ethoxy-2-methylpropionate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether Acetate, propylene glycol monopropyl ether acetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate and dipropylene glycol methyl ether acetate and the like.

  Examples of ketone solvents include 4-hydroxy-4-methyl-2-pentanone, acetone, 2-butanone, 2-heptanone, 3-heptanone, 4-heptanone, 4-methyl-2-pentanone, cyclopentanone, cyclohexanone and isophorone. Etc.

  Examples of the alcohol solvent include methanol, ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol, propylene glycol, and glycerin. Examples of the aromatic hydrocarbon solvent include benzene, toluene, xylene and mesitylene. Examples of the amide solvent include N, N-dimethylformamide, N, N-dimethylacetamide and N-methylpyrrolidone.

  The organic solvent (D2) is composed of propylene glycol monomethyl ether acetate, ethyl lactate, propylene glycol monomethyl ether, ethyl 3-ethoxypropionate, ethylene glycol monomethyl ether, diethylene glycol monomethyl from the viewpoint of the coating property and drying property of the curable resin composition. At least one selected from the group consisting of ether, diethylene glycol monoethyl ether, 3-methoxybutyl acetate, 3-methoxy-1-butanol, 4-hydroxy-4-methyl-2-pentanone and N, N-dimethylformamide Propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, dipropylene glycol methyl ether acetate, ethyl lactate, 3-metho Shi butyl acetate, and more preferably contains at least one selected from the group consisting of 3-methoxy-1-butanol and ethyl 3-ethoxypropionate.

  The organic solvent (D) may contain only the organic solvent (D1), or may contain the organic solvent (D1) and the organic solvent (D2). From the viewpoint of reducing color unevenness and / or enhancing the patternability of the curable resin composition, the content of the organic solvent (D1) is preferably 100% by mass or more, preferably 20% by mass or more in the organic solvent (D). More preferably, it is 40 mass% or more, More preferably, it is 50 mass% or more.

  The content of the organic solvent (D) is preferably 60% by mass to 95% by mass, more preferably 65% by mass to 92% by mass, in 100% by mass of the curable resin composition. In other words, the solid content of the curable resin composition is preferably 5% by mass or more and 40% by mass or less, more preferably 8% by mass or more and 35% by mass or less. If the content of the organic solvent (D) is in the above range, the coating property of the curable resin composition and the flatness at the time of coating tend to be good, and the light emitting characteristics of a cured film such as a wavelength conversion film are good. Tend to be.

[5] Polymerization initiator (E)
The curable resin composition can contain a polymerization initiator (E). The polymerization initiator (E) is not particularly limited as long as it is a compound that generates an active radical, an acid or the like by the action of light or heat and can initiate polymerization, and a known polymerization initiator can be used.

  Examples of the polymerization initiator (E) include oxime compounds such as O-acyl oxime compounds, alkylphenone compounds, biimidazole compounds, triazine compounds, and acyl phosphine oxide compounds. Two or more kinds of polymerization initiators (E) may be used in consideration of sensitivity and patterning properties. The polymerization initiator (E) is advantageous in precisely creating a pattern shape having sensitivity and a desired line width, and therefore preferably contains an oxime compound such as an O-acyl oxime compound.

  The O-acyl oxime compound is a compound having a structure represented by the following formula (d). Hereinafter, * represents a bond.

  Examples of such O-acyloxime compounds include N-benzoyloxy-1- (4-phenylsulfanylphenyl) butan-1-one-2-imine, N-benzoyloxy-1- (4-phenylsulfanylphenyl) octane. -1-one-2-imine, N-benzoyloxy-1- (4-phenylsulfanylphenyl) -3-cyclopentylpropane-1-one-2-imine, N-acetoxy-1- [9-ethyl-6- (2-Methylbenzoyl) -9H-carbazol-3-yl] ethane-1-imine, N-acetoxy-1- [9-ethyl-6- {2-methyl-4- (3,3-dimethyl-2, 4-Dioxacyclopentanylmethyloxy) benzoyl} -9H-carbazol-3-yl] ethane-1-imine, N-acetoxy-1- [ -Ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] -3-cyclopentylpropane-1-imine, N-benzoyloxy-1- [9-ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl] -3-cyclopentylpropan-1-one-2-imine, N-acetyloxy-1- [4- (2-hydroxyethyloxy) phenylsulfanylphenyl] propan-1-one- 2-imine, N-acetyloxy-1- [4- (1-methyl-2-methoxyethoxy) -2-methylphenyl] -1- (9-ethyl-6-nitro-9H-carbazol-3-yl) And methane-1-imine. Commercial products such as Irgacure (registered trademark) OXE01, OXE02, OXE03 (above, manufactured by BASF), N-1919, NCI-930, NCI-831 (above, made by ADEKA) may be used. These O-acyloxime compounds are advantageous in that the lithography performance can be improved.

  The alkylphenone compound is a compound having a partial structure represented by the following formula (d4) or a partial structure represented by the following formula (d5). In these partial structures, the benzene ring may have a substituent.

  Examples of the compound having a structure represented by the formula (d4) include 2-methyl-2-morpholino-1- (4-methylsulfanylphenyl) propan-1-one, 2-dimethylamino-1- (4-morpholinophenyl) ) -2-benzylbutan-1-one, 2- (dimethylamino) -2-[(4-methylphenyl) methyl] -1- [4- (4-morpholinyl) phenyl] butan-1-one, and the like. It is done. Commercial products such as Irgacure (registered trademark) 369, 907, and 379 (above, manufactured by BASF) may be used.

  Examples of the compound having a structure represented by the formula (d5) include 2-hydroxy-2-methyl-1-phenylpropan-1-one, 2-hydroxy-2-methyl-1- [4- (2-hydroxyethoxy ) Phenyl] propan-1-one, 1-hydroxycyclohexyl phenyl ketone, oligomer of 2-hydroxy-2-methyl-1- (4-isopropenylphenyl) propan-1-one, α, α-diethoxyacetophenone, benzyl Examples thereof include dimethyl ketal.

  In terms of sensitivity, the alkylphenone compound is preferably a compound having a structure represented by the formula (d4).

  Examples of the biimidazole compound include 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole and 2,2′-bis (2,3-dichlorophenyl) -4,4. ', 5,5'-tetraphenylbiimidazole (see, for example, JP-A-6-75372 and JP-A-6-75373), 2,2'-bis (2-chlorophenyl) -4,4' , 5,5′-tetraphenylbiimidazole, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetra (alkoxyphenyl) biimidazole, 2,2′-bis (2- Chlorophenyl) -4,4 ′, 5,5′-tetra (dialkoxyphenyl) biimidazole, 2,2′-bis (2-chlorophenyl) -4,4 ′, 5,5′-tetra (trialkoxypheny ) Biimidazole (for example, see JP-B-48-38403, JP-A-62-174204, etc.), the phenyl group at the 4,4 ′, 5,5′-position is substituted with a carboalkoxy group. Examples thereof include imidazole compounds (for example, see JP-A-7-10913). Among these, a compound represented by the following formula or a mixture thereof is preferable.

  As triazine compounds, 2,4-bis (trichloromethyl) -6- (4-methoxyphenyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxynaphthyl) -1,3,5-triazine, 2,4-bis (trichloromethyl) -6-piperonyl-1,3,5-triazine, 2,4-bis (trichloromethyl) -6- (4-methoxystyryl)- 1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (5-methylfuran-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis ( Trichloromethyl) -6- [2- (furan-2-yl) ethenyl] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (4-diethylamino-2-methyl) Phenyl) etheni ] -1,3,5-triazine, 2,4-bis (trichloromethyl) -6- [2- (3,4-dimethoxyphenyl) ethenyl] -1,3,5-triazine.

  Examples of the acylphosphine oxide compound include 2,4,6-trimethylbenzoyldiphenylphosphine oxide.

  Furthermore, as the polymerization initiator (E), benzoin compounds such as benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether; benzophenone, methyl o-benzoylbenzoate, 4-phenylbenzophenone, 4-benzoyl- Benzophenone compounds such as 4′-methyldiphenyl sulfide, 3,3 ′, 4,4′-tetra (tert-butylperoxycarbonyl) benzophenone, 2,4,6-trimethylbenzophenone; 9,10-phenanthrenequinone, Examples include quinone compounds such as 2-ethylanthraquinone and camphorquinone; 10-butyl-2-chloroacridone, benzyl, methyl phenylglyoxylate, and titanocene compounds. These are preferably used in combination with a polymerization initiation assistant (E1) (particularly amines) described later.

  The polymerization initiator (E) is preferably a polymerization initiator containing at least one selected from the group consisting of alkylphenone compounds, triazine compounds, acylphosphine oxide compounds, O-acyloxime compounds and biimidazole compounds, A polymerization initiator containing an acyloxime compound is more preferable.

  The content of the polymerization initiator (E) is preferably 0.1 parts by mass or more and 30 parts by mass or less, more preferably 100 parts by mass of the total amount of the resin (B) and the polymerizable compound (C). 1 part by mass or more and 25 parts by mass or less, more preferably 1 part by mass or more and 20 parts by mass or less. If the content of the polymerization initiator (E) is within the above range, the sensitivity tends to be increased and the exposure time tends to be shortened, so the productivity of a cured film such as a wavelength conversion film tends to be improved.

[6] Polymerization initiation assistant (E1)
The curable resin composition can contain a polymerization initiation assistant (E1). The polymerization initiation assistant (E1) is a compound or sensitizer used for promoting the polymerization of the polymerizable compound (C) that has been polymerized by the polymerization initiator (E). When the polymerization initiation assistant (E1) is included, it is used in combination with the polymerization initiator (E).

  Examples of the polymerization initiation assistant (E1) include amine compounds, alkoxyanthracene compounds, thioxanthone compounds, and carboxylic acid compounds. Of these, thioxanthone compounds are preferred. Two or more polymerization initiation assistants (E1) may be used in combination.

  Examples of amine compounds include triethanolamine, methyldiethanolamine, triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, isoamyl 4-dimethylaminobenzoate, 2-dimethylaminoethyl benzoate, 4- 2-ethylhexyl dimethylaminobenzoate, N, N-dimethylparatoluidine, 4,4′-bis (dimethylamino) benzophenone (commonly known as Michler's ketone), 4,4′-bis (diethylamino) benzophenone, 4,4′-bis ( Ethylmethylamino) benzophenone and the like, and 4,4′-bis (diethylamino) benzophenone is preferred. Commercial products such as EAB-F (Hodogaya Chemical Co., Ltd.) may be used.

  Examples of the alkoxyanthracene compound include 9,10-dimethoxyanthracene, 2-ethyl-9,10-dimethoxyanthracene, 9,10-diethoxyanthracene, 2-ethyl-9,10-diethoxyanthracene, and 9,10-dibutoxy. Anthracene, 2-ethyl-9,10-dibutoxyanthracene, etc. are mentioned.

  Examples of the thioxanthone compound include 2-isopropylthioxanthone, 4-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 1-chloro-4-propoxythioxanthone and the like.

  Carboxylic acid compounds include phenylsulfanylacetic acid, methylphenylsulfanylacetic acid, ethylphenylsulfanylacetic acid, methylethylphenylsulfanylacetic acid, dimethylphenylsulfanylacetic acid, methoxyphenylsulfanylacetic acid, dimethoxyphenylsulfanylacetic acid, chlorophenylsulfanylacetic acid, dichlorophenylsulfanylacetic acid, N -Phenylglycine, phenoxyacetic acid, naphthylthioacetic acid, N-naphthylglycine, naphthoxyacetic acid and the like.

  The content of the polymerization initiation assistant (E1) is preferably 0.1 parts by mass or more and 30 parts by mass or less, more preferably 1 with respect to 100 parts by mass of the total amount of the resin (B) and the polymerizable compound (C). It is not less than 20 parts by mass. When the content of the polymerization initiation assistant (E1) is within the above range, the productivity of a cured film such as a wavelength conversion film can be further improved.

[7] Leveling agent (F)
The curable resin composition may contain one or more leveling agents (F). Examples of the leveling agent (F) include silicone surfactants, fluorine surfactants, and silicone surfactants having a fluorine atom. These may have a polymerizable group in the side chain.

  Examples of the silicone surfactant include a surfactant having a siloxane bond in the molecule. Specifically, Torre Silicone DC3PA, SH7PA, DC11PA, SH21PA, SH28PA, SH29PA, SH30PA, SH8400 (trade names: manufactured by Toray Dow Corning Co., Ltd.), KP321, KP322, KP323, KP324 , KP326, KP340, KP341 (manufactured by Shin-Etsu Chemical Co., Ltd.), TSF400, TSF401, TSF410, TSF4300, TSF4440, TSF4445, TSF-4446, TSF4452 and TSF4460 (made by Momentive Performance Materials Japan GK) Can be mentioned.

  Examples of the fluorosurfactant include a surfactant having a fluorocarbon chain in the molecule. Specifically, Florard (registered trademark) FC430, FC431 (manufactured by Sumitomo 3M Co., Ltd.), MegaFac (registered trademark) F142D, F171, F172, F173, F177, F183, F183, F554, R30, RS-718-K (manufactured by DIC Corporation), Ftop (registered trademark) EF301, EF303, EF351, EF352 (manufactured by Mitsubishi Materials Electronic Chemicals), Surflon (registered trademark) S381, S382, SC101, SC105 (Asahi Glass Co., Ltd.) and E5844 (Daikin Fine Chemical Laboratory Co., Ltd.).

  Examples of the silicone-based surfactant having a fluorine atom include a surfactant having a siloxane bond and a fluorocarbon chain in the molecule. Specifically, Megafac (registered trademark) R08, BL20, F475, F477, F443 (manufactured by DIC Corporation), and the like can be given.

  The content of the leveling agent (F) is usually 0.001% by mass to 0.2% by mass, preferably 0.002% by mass to 0.1% by mass in 100% by mass of the curable resin composition. More preferably, it is 0.005 mass% or more and 0.05 mass% or less.

[8] Antioxidant (G)
From the viewpoint of improving the heat resistance and light resistance of the curable resin composition, the curable resin composition can contain an antioxidant (G). The antioxidant (G) is not particularly limited as long as it is an antioxidant generally used industrially, and a phenol-based antioxidant, a phosphorus-based antioxidant, a sulfur-based antioxidant, and the like can be used. . Two or more antioxidants (G) may be used in combination.

  As a phenolic antioxidant, Irganox (registered trademark) 1010 (Irganox 1010: pentaerythritol tetrakis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate], manufactured by BASF Corporation) 1076 (Irganox 1076: octadecyl-3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate, manufactured by BASF Corp.), 1330 (Irganox 1330: 3, 3 ′, 3 ″) 5,5 ′, 5 ″ -hexa-t-butyl-a, a ′, a ″-(mesitylene-2,4,6-triyl) tri-p-cresol, manufactured by BASF Corp.), 3114 (Irganox 3114: 1,3,5-tris (3,5-di-tert-butyl-4-hydroxybenzyl) -1,3,5 Triazine-2,4,6 (1H, 3H, 5H) -trione, manufactured by BASF Corp.), 3790 (Irganox 3790: 1,3,5-tris ((4-t-butyl-3-hydroxy-2) , 6-Xylyl) methyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) -trione, manufactured by BASF), 1035 (Irganox 1035: thiodiethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], manufactured by BASF Corp.), 1135 (Irganox 1135: benzenepropanoic acid, 3,5-bis (1,1-dimethylethyl)- 4-hydroxy, C7-C9 side chain alkyl ester, manufactured by BASF), 1520L (Irganox 1520L: 4,6-bis (octyl) Methyl) -o-cresol, manufactured by BASF), 3125 (Irganox 3125, manufactured by BASF), 565 (Irganox 565: 2,4-bis (n-octylthio) -6- (4-hydroxy) 3 ′, 5′-di-t-butylanilino) -1,3,5-triazine (manufactured by BASF Corp.), Adekastab (registered trademark) AO-80 (Adekastab AO-80: 3,9-bis (2- (3- (3-t-butyl-4-hydroxy-5-methylphenyl) propionyloxy) -1,1-dimethylethyl) -2,4,8,10-tetraoxaspiro (5,5) undecane, ADEKA Co., Ltd.), Smither (registered trademark) BHT, GA-80, GS (manufactured by Sumitomo Chemical Co., Ltd.), Sianox (registered trademark) 1790 (Cyan) x 1790, and the like, Ltd. Cytec) and vitamin E (manufactured by Eisai Co.).

  Examples of phosphorus-based antioxidants include Irgaphos (registered trademark) 168 (Irgafos 168: Tris (2,4-di-t-butylphenyl) phosphite, manufactured by BASF Corp.), 12 (Irgafos 12: Tris [2 -[[2,4,8,10-tetra-t-butyldibenzo [d, f] [1,3,2] dioxaphosphin-6-yl] oxy] ethyl] amine, manufactured by BASF Corporation) 38 (Irgafos 38: bis (2,4-bis (1,1-dimethylethyl) -6-methylphenyl) ethyl ester phosphorous acid, manufactured by BASF Corp.), ADK STAB (registered trademark) 329K, PEP36 PEP-8 (above, manufactured by ADEKA Corporation), Sandstab P-EPQ (manufactured by Clariant), Weston (registered trademark) 618, 619 (Above, manufactured by GE), Ultranox 626 (manufactured by GE) and Sumilizer (registered trademark) GP (6- [3- (3-t-butyl-4-hydroxy-5-methylphenyl) propoxy] -2,4, 8,10-tetra-t-butyldibenz [d, f] [1.3.2] dioxaphosphine) (manufactured by Sumitomo Chemical Co., Ltd.) and the like.

  Examples of sulfur-based antioxidants include dialkylthiodipropionate compounds such as dilauryl thiodipropionate, dimyristyl or distearyl, and β-alkyl mercaptopropionate compounds of polyols such as tetrakis [methylene (3-dodecylthio) propionate] methane. Is mentioned.

[9] Other components For the curable resin composition, if necessary, a filler, a polymer compound other than the resin (B), an adhesion promoter, an ultraviolet absorber, an aggregation inhibitor, an organic acid, an organic amine compound 1 type, or 2 or more types of additives, such as a thiol compound, a hardening | curing agent, and a light-scattering agent, can be contained.

  Examples of the filler include glass, silica, and alumina. Examples of the polymer compound other than the resin (B) include polyvinyl alcohol, polyacrylic acid, polyethylene glycol monoalkyl ether, and polyfluoroalkyl acrylate.

  As adhesion promoters, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris (2-methoxyethoxy) silane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, N- (2-aminoethyl) -3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxy Examples include silane, 3-chloropropylmethyldimethoxysilane, 3-chloropropyltrimethoxysilane, 3-methacryloyloxypropyltrimethoxysilane, and 3-mercaptopropyltrimethoxysilane.

  Examples of ultraviolet absorbers include benzotriazole compounds such as 2- (2-hydroxy-3-tert-butyl-5-methylphenyl) -5-chlorobenzotriazole; benzophenone compounds such as 2-hydroxy-4-octyloxybenzophenone Compound; benzoate compounds such as 2,4-di-tert-butylphenyl-3,5-di-tert-butyl-4-hydroxybenzoate; 2- (4,6-diphenyl-1,3,5-triazine- 2-yl) -5-hexyloxyphenol and other triazine compounds; Examples of the aggregation inhibitor include sodium polyacrylate.

  Examples of the curing agent include a compound capable of reacting with a carboxy group in the resin (B) by being heated to crosslink the resin (B), a compound capable of being polymerized and cured alone, and an epoxy compound. And oxetane compounds.

Examples of the light scattering agent include metal or metal oxide particles and glass particles. Examples of the metal oxide include TiO ₂ , SiO ₂ , BaTiO ₃ , ZnO, and the like. The particle diameter of the light scattering agent is, for example, about 0.03 μm to 20 μm, preferably 0.05 μm to 1 μm, and more preferably 0.05 μm to 300 μm. The content of the light scattering agent is usually 0.001% by mass or more and 50% by mass or less, preferably 1% by mass or more and 40% by mass or less, more preferably 5% by mass or more, in 100% by mass of the curable resin composition. 30% by mass or less.

<Method for preparing curable resin composition>
The curable resin composition is prepared by mixing the semiconductor particles (A), the resin (B), the polymerizable compound (C), the organic solvent (D), and other components used as necessary. Can do.

  The ligand-containing semiconductor particle as the semiconductor particle (A) is, for example, prepared or prepared a semiconductor particle coordinated with an organic ligand, and then the coordination amount of the organic ligand with respect to the semiconductor particle. What gave the ligand reduction process to reduce may be used. The ligand reduction treatment can be, for example, a treatment for extracting an organic ligand coordinated to the semiconductor particles into an appropriate solvent.

<Curing film, patterned cured film, wavelength conversion film and display device>
A cured film can be obtained by curing a film (layer) made of the curable resin composition. At this time, a patterned cured film can be obtained by patterning by a method such as a photolithographic method, an ink jet method, or a printing method. The cured film or the patterned cured film can be suitably used as a wavelength conversion film (wavelength conversion filter) that emits light having a wavelength different from the wavelength of incident light. The wavelength conversion film can be suitably used for display devices such as liquid crystal display devices and organic EL devices. The patterning method is preferably a photolithography method. The photolithographic method is a method in which a curable resin composition is applied to a substrate, dried to form a curable resin composition layer, and the curable resin composition layer is exposed through a photomask and developed. is there.

  As a substrate, glass plate such as quartz glass, borosilicate glass, alumina silicate glass, soda lime glass coated with silica on the surface, resin plate such as polycarbonate, polymethyl methacrylate, polyethylene terephthalate, silicon, on the above substrate Further, aluminum, silver, a silver / copper / palladium alloy thin film, or the like can be used.

  Formation of the cured film patterned by the photolithography method can be performed by a known or conventional apparatus or conditions, and for example, can be formed as follows. First, a curable resin composition is applied on a substrate, dried by heating (pre-baking) and / or drying under reduced pressure to remove volatile components such as a solvent and drying to obtain a curable resin composition layer. Examples of the coating method include spin coating, slit coating, and slit and spin coating.

  The temperature for performing heat drying is preferably 30 ° C. or higher and 120 ° C. or lower, and more preferably 50 ° C. or higher and 110 ° C. or lower. The heating time is preferably 10 seconds or longer and 10 minutes or shorter, and more preferably 30 seconds or longer and 5 minutes or shorter. When drying under reduced pressure, it is preferable to carry out under a pressure of 50 Pa or more and 150 Pa or less and a temperature range of 20 ° C. or more and 25 ° C. or less. The film thickness of the curable resin composition layer is not particularly limited, and can be appropriately selected according to the film thickness of a cured film such as a desired wavelength conversion film.

  Next, the curable resin composition layer is exposed through a photomask for forming a desired pattern. The pattern on the photomask is not particularly limited, and a pattern according to the intended use is used. As a light source used for exposure, a light source that generates light having a wavelength of 250 nm to 450 nm is preferable. For example, light less than 350 nm can be cut using a filter that cuts this wavelength range, or light near 436 nm, 408 nm, and 365 nm can be selectively extracted using a bandpass filter that extracts these wavelength ranges. Or you may. Examples of the light source include a mercury lamp, a light emitting diode, a metal halide lamp, and a halogen lamp.

  The exposure can be performed by irradiating the entire exposed surface with parallel light rays or by accurately aligning the photomask and the substrate on which the curable resin composition layer is formed, such as a mask aligner and a stepper. It is preferable to use an exposure apparatus.

  The pattern of the curable resin composition layer is formed on the substrate by bringing the curable resin composition layer after the exposure into contact with the developer and developing. By the development, the unexposed portion of the curable resin composition layer is dissolved in the developer and removed. The developer is preferably an aqueous solution of an alkaline compound such as potassium hydroxide, sodium hydrogen carbonate, sodium carbonate, or tetramethylammonium hydroxide. The concentration of these alkaline compounds in the aqueous solution is preferably 0.01% by mass or more and 10% by mass or less, and more preferably 0.03% by mass or more and 5% by mass or less. The developer may further contain a surfactant. Examples of the developing method include a paddle method, a dipping method, and a spray method. Further, the substrate may be tilted at an arbitrary angle during development. It is preferable to wash with water after development.

  Furthermore, it is preferable that the pattern of the obtained curable resin composition layer is post-baked. The post-bake temperature is preferably 60 ° C. or higher and 250 ° C. or lower, and more preferably 110 ° C. or higher and 240 ° C. or lower. The post-bake time is preferably 1 minute or more and 120 minutes or less, and more preferably 10 minutes or more and 60 minutes or less. The thickness of the cured film after post-baking is, for example, 1 μm or more and 10 μm or less, preferably 3 μm or more and 10 μm or less.

  EXAMPLES Hereinafter, although an Example is shown and this invention is demonstrated further more concretely, this invention is not limited by these examples. In the examples, “%” and “part” representing the content or amount used are based on mass unless otherwise specified.

<Production Examples A to E: Production of Ligand-Containing Semiconductor Particle Dispersions a to e>
(1) Preparation of semiconductor quantum dots Core-shell type semiconductor quantum dots INP530 (manufactured by NN-LABS) having a structure of InP (core) / ZnS (first shell) / ZnS (second shell) are used as semiconductor quantum dots. did. Oleylamine is coordinated on the surface of the semiconductor quantum dot.

(2) Solvent replacement treatment Next, the above-described semiconductor quantum dots (QD) were subjected to a solvent replacement treatment in the following procedure. First, 2 parts by volume of hexane was added to 1 part by volume of the dispersion containing QD of (1) above and diluted. Thereafter, 30 parts by volume of ethanol was added to precipitate QD, and centrifugation was performed. The supernatant was removed and 3 parts by volume of hexane was added to redisperse QD. Such treatment (precipitation by adding ethanol → centrifugation → removing the supernatant liquid → redispersion by adding hexane) was performed three times in total. However, at the time of redispersion for the third time, not the hexane but the solvent shown in the following Table 1 was added so that the concentration of QD (including oleylamine ligand) was 9.5% by mass, respectively. a to e were obtained.

<Production Example F: Preparation of solution containing resin (B)>
A flask equipped with a condenser and a stirrer was charged with 100 parts of propylene glycol monomethyl ether acetate (PGMEA) and purged with nitrogen. While stirring at 70 ° C., 7.6 parts of methyl methacrylate (manufactured by Tokyo Chemical Industry Co., Ltd.), 5.6 parts of dicyclopentanyl methacrylate (“Fancryl FA-513M” manufactured by Hitachi Chemical Co., Ltd.), methacryl 2.7 parts of acid (manufactured by Tokyo Chemical Industry Co., Ltd.), 6.4 parts of succinic acid 1- [2- (methacryloyloxy) ethyl] (manufactured by Sigma Aldrich Japan LLC), 2,2′-azobis (2,4 -Dimethylvaleronitrile) (Wako Pure Chemical Industries, Ltd.) 2.1 parts, Pentaerythritol tetrakis (3-mercaptopropionate) [PEMP] (SC Organic Chemical Co., Ltd.) 1.4 parts by mass and PGMEA 100 parts The mixed solution was added dropwise over 30 minutes, and a polymerization reaction was performed at the same temperature for 2 hours. The reaction solution was gradually cooled to room temperature and then added dropwise to ethanol, and the precipitate was collected by filtration and dried with a vacuum dryer at 40 ° C. 40 parts of the obtained white powder was dissolved in 60 parts of PGMEA to obtain a resin solution-a (resin concentration: 40% by mass). The weight average molecular weight of the obtained resin was 17000 (standard polystyrene conversion value by gel permeation chromatography). Based on the charged amount, the acid value of the obtained resin solid content was calculated as X / Y = 80/70 (mg-KOH / g).

<Examples 1-3, Comparative Examples 1-2>
52.7 parts of the QD dispersion shown in Table 2 and 27.7 parts of the resin solution-a obtained in Production Example F were put in a flask and heated and stirred at 50 ° C. for 12 hours. Then, it stood to cool to room temperature, and obtained the liquid containing QD and resin.

  Next, 3.7 parts of a polymerizable compound (C-1), 3.7 parts of a polymerizable compound (C-2), 0.7 part of a polymerization initiator (E-1), and an antioxidant (G-1) 0 0.7 part, 0.3 part of a PGMEA solution containing a leveling agent (F-1) at a concentration of 10% by mass and 10.5 parts of a solvent (D-1) were mixed. The obtained mixed liquid was added to the liquid containing the above-mentioned QD and resin, and mixed by stirring to obtain a curable resin composition. Solid content concentration of the obtained curable resin composition is 25 mass%. Table 2 summarizes the types of compounding ingredients used and the amounts used. In Table 2, the unit of the amount used is part by mass.

The details of the ingredients shown in Table 2 are as follows.
[1] Polymerizable compound (C-1): propoxylated pentaerythritol triacrylate (“NK ester ATM-4PL” manufactured by Shin-Nakamura Chemical Co., Ltd.),
[2] Polymerizable compound (C-2): Pentaerythritol triacrylate (“NK Ester A-TMM-3LM-N” manufactured by Shin-Nakamura Chemical Co., Ltd.),
[3] Polymerization initiator (E-1): O-acyloxime polymerization initiator “NCI-930” manufactured by ADEKA Corporation,
[4] Solvent (D-1): PGMEA,
[5] Leveling agent (F-1): A polyether-modified silicone oil leveling agent “Toray Silicone SH8400” manufactured by Toray Dow Corning Co., Ltd.
[6] Antioxidant (G-1): A phenol phosphorus antioxidant “Sumilyzer (registered trademark) GP” manufactured by Sumitomo Chemical Co., Ltd.

[Evaluation test]
0.45 mL of the curable resin composition is dropped on a glass substrate, spin-coated at 150 rpm for 20 seconds, and then dried (prebaked) at 100 ° C. for 3 minutes to obtain a curable resin composition layer. Formed. Next, post-baking was performed in an oven at 230 ° C. for 20 minutes to obtain a cured film. The thickness of the cured film was 5 μm or more and 6 μm or less. The following evaluation test was done about the obtained cured film.

(1) Surface roughness The roughness (Sa: arithmetic average height) of the cured film was measured using a laser microscope ("3D Measuring Laser Microscope OLS4100" manufactured by Olympus Corporation) and evaluated according to the following evaluation criteria. The results are shown in Table 2.
○: Sa is 1.0 μm or less,
X: Sa exceeds 1.0 μm.

(2) Color unevenness The surface of the cured film was visually observed and evaluated according to the following evaluation criteria. The results are shown in Table 2.
○: Color unevenness is not visually confirmed.
X: Color unevenness is confirmed visually.

(3) QY retention rate Using an absolute PL quantum yield measuring device “C9920-02G” manufactured by Hamamatsu Photonics Co., Ltd., the quantum yield of the coating film (before curing) of the curable resin composition of Example 1 is measured. did. Moreover, the quantum yield of the cured film (after post-baking) formed from the curable resin composition was measured using the same apparatus. From these measurement results, when the quantum yield of the curable resin composition (before curing) is 100%, the quantum yield (%) of the cured film (after post-baking) formed from the curable resin composition QY retention rate was calculated.
The QY retention was 87%, indicating good wavelength conversion characteristics.

(4) Patterning characteristics 0.45 mL of the curable resin composition prepared in Example 1 was dropped on a glass substrate, spin-coated at 150 rpm for 20 seconds, and then dried at 100 ° C. for 3 minutes ( Pre-baked) to form a curable resin composition layer. Next, using a photomask having a line and space pattern with a line width of 50 μm, pattern exposure was performed in an air atmosphere with an exposure amount of 40 mJ / cm ² (based on 365 nm). The distance between the substrate and the photomask was 120 μm. The curable resin composition layer after pattern exposure is immersed in an aqueous developer having a potassium hydroxide concentration of 0.04 mass% for 70 seconds at 23 ° C., washed with water, and then post-baked in an oven at 230 ° C. for 20 minutes. To obtain a patterned cured film.
The cured film had a thickness of 5 μm and a line width of 54 μm, and showed good patterning characteristics.

Claims (3)

Including semiconductor particles (A), resin (B), polymerizable compound (C) and organic solvent (D),
The organic solvent (D) is composed of a cycloalkane ring, —O—, —O—C (═O) —, —C (═O) —O— and —C (═O) — in the molecule. A curable resin composition comprising a compound having at least one group selected from the group.   A cured film formed from the curable resin composition according to claim 1.   A display device comprising the cured film according to claim 2.