JP2018060066A - Resist composition, resist pattern forming method, and polymer compound - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a polymer compound useful for a resist composition, a resist composition, and a resist pattern forming method.SOLUTION: The resist composition, which generates an acid upon exposure and whose solubility in a developer changes by the action of an acid, contains a polymer compound having a constituent unit represented by formula (a0-1). In the formula (a0-1), Vais a divalent hydrocarbon group; nis 0-2; Rais an acid-dissociable group represented by formula (a0-r1-1); Raand Raare each a hydrocarbon group; Raand Ramay be bonded to each other to form a ring structure; Yais a quaternary carbon atom; and Ra, Raand Raare each a hydrocarbon group, provided that one or more of them are each a hydrocarbon group having at least a polar group.SELECTED DRAWING: None

Description

  The present invention relates to a resist composition, a resist pattern forming method, and a polymer compound.

A technique (pattern formation technique) in which a fine pattern is formed on a substrate and etching is performed using the fine pattern as a mask to process a lower layer of the pattern (pattern formation technique) is widely adopted in the manufacture of semiconductor elements and liquid crystal display elements. The fine pattern is usually made of an organic material and is formed by a technique such as a lithography method or a nanoimprint method. For example, in a lithography method, a resist film is formed on a support such as a substrate using a resist material containing a base material component such as a resin, and the resist film is selected by radiation such as light or an electron beam. A step of forming a resist pattern having a predetermined shape on the resist film is performed by performing a general exposure and developing. And a semiconductor element etc. are manufactured through the process of processing a board | substrate by an etching using this resist pattern as a mask.
The resist material is classified into a positive type and a negative type. A resist material whose solubility in an exposed portion of a developer increases is called a positive type, and a resist material whose solubility in an exposed portion of a developer decreases is called a negative type. .
As the developer, an alkaline aqueous solution (alkali developer) such as a tetramethylammonium hydroxide (TMAH) aqueous solution is usually used. Developers containing organic solvents such as aromatic organic solvents, aliphatic hydrocarbon organic solvents, ether organic solvents, ketone organic solvents, ester organic solvents, amide organic solvents, alcohol organic solvents, etc. (Organic developer) is also used as a developer.

In recent years, pattern miniaturization has been progressing rapidly due to advances in lithography technology.
As a technique for miniaturization, the exposure light source is generally shortened in wavelength (increased energy). Specifically, conventionally, ultraviolet rays typified by g-line and i-line have been used, but mass production of semiconductor elements using a KrF excimer laser or an ArF excimer laser has been started. Further, studies have been made on EB (electron beam), EUV (extreme ultraviolet), X-rays, and the like having shorter wavelengths (higher energy) than these excimer lasers.

Along with the shortening of the wavelength of the exposure light source, the resist material is required to be improved in lithography characteristics such as sensitivity to the exposure light source and resolution capable of reproducing a pattern with a fine dimension. A chemically amplified resist composition is known as a resist material that satisfies such requirements.
As the chemically amplified resist composition, generally, a resist composition containing a base material component whose solubility in a developing solution is changed by the action of an acid and an acid generator component that generates an acid upon exposure is used. Yes. For example, when the developer is an alkali developer (alkaline development process), a substrate component that has increased solubility in an alkali developer due to the action of an acid is used.

  Conventionally, a resin (base resin) is mainly used as a base material component of a chemically amplified resist composition. At present, as a base resin of a chemically amplified resist composition used in ArF excimer laser lithography and the like, it has a structural unit derived from (meth) acrylic acid ester in its main chain because of its excellent transparency near 193 nm. Resin (acrylic resin) is the mainstream.

  Here, “(meth) acrylic acid” means one or both of acrylic acid having a hydrogen atom bonded to the α-position and methacrylic acid having a methyl group bonded to the α-position. “(Meth) acrylic acid ester” means one or both of an acrylic acid ester having a hydrogen atom bonded to the α-position and a methacrylic acid ester having a methyl group bonded to the α-position. “(Meth) acrylate” means one or both of an acrylate having a hydrogen atom bonded to the α-position and a methacrylate having a methyl group bonded to the α-position.

  The base resin of the chemically amplified resist composition generally has a plurality of types of structural units in order to improve lithography properties and the like. For example, a structural unit having an acid-decomposable group that decomposes by the action of an acid generated from an acid generator to generate an alkali-soluble group, a structural unit having a lactone structure, a structural unit having a polar group such as a hydroxyl group, etc. are used. (For example, refer to Patent Document 1). When the base resin is an acrylic resin, as the acid-decomposable group, generally, a carboxy group in (meth) acrylic acid or the like is protected with an acid-dissociable group such as a tertiary alkyl group or an acetal group. Things are used.

A positive development process that combines a positive chemically amplified resist composition, that is, a chemically amplified resist composition whose solubility in an alkali developer increases upon exposure, and an alkaline developer is a negative chemically amplified type. Compared to a negative development process in which a resist composition and an alkali developer are combined, there are advantages such as a simple photomask structure and excellent pattern characteristics. Therefore, at present, a positive development process in which a positive chemically amplified resist composition and an alkali developer are combined is mainly used for forming a fine pattern.
When the positive development process is applied, when the resist film obtained by coating the positive chemically amplified resist composition on the support is selectively exposed, the exposed portion of the resist film is a base resin. The acid-decomposable groups in the resist film are decomposed by the action of the acid generated from the acid generator, etc., and change from poorly soluble to soluble in an alkaline developer, while the unexposed part of the resist film remains hardly soluble in alkali. Therefore, by developing with an alkali developer, dissolution contrast can be provided between the exposed and unexposed areas, and a positive resist pattern can be formed.

A method of forming a resist pattern (negative resist pattern) by selectively dissolving and removing a region having low optical intensity is also useful for forming a fine pattern. As a method of forming this negative resist pattern, a chemically amplified resist composition used in the positive development process, which is the mainstream, and a developer containing an organic solvent (organic developer) are combined. Negative development processes are known.
In addition, conventionally, for example, an acid-decomposable group having a specific structure (that is, an acid-decomposable group having a tertiary carbon atom bonded to an aliphatic hydrocarbon group having an ether bond) is included to improve lithography properties and the like. A chemically amplified resist composition using a polymer compound having a structural unit as a base resin has been proposed (see Patent Document 2).

JP 2003-241385 A Japanese Patent Laying-Open No. 2015-169843

As electronic devices become more sophisticated and smaller in size, further improvements in lithography characteristics and resist pattern shapes are required for pattern formation when manufacturing semiconductor elements and the like. However, there is still room for improvement in the shape of a resist pattern formed using a conventional resist composition, and there is a demand for further improvement in sensitivity, lithography characteristics, and the like.
The present invention has been made in view of the above circumstances, and includes a novel polymer compound useful as a base component for a resist composition, a resist composition containing the polymer compound, and the resist composition. It is an object to provide a resist pattern forming method used.

In order to solve the above problems, the present invention employs the following configuration.
That is, the first aspect of the present invention is a resist composition that generates an acid upon exposure and changes its solubility in a developer by the action of an acid, and the solubility in the developer changes by the action of an acid. The base material component (A) contains a polymer compound (A1) having a structural unit (a0) represented by the following general formula (a0-1). And a resist composition.

［式中、Ｒは、水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｖａ^０は、エーテル結合を有していてもよい２価の炭化水素基である。ｎ_ａ０は、０〜２の整数である。Ｒａ^００は、一般式（ａ０−ｒ１−１）で表される酸解離性基である。Ｒａ^０１は、置換基を有していてもよい炭化水素基である。Ｒａ^０２は、置換基を有していてもよい炭化水素基である。Ｒａ^０１とＲａ^０２とは相互に結合して、環構造を形成してもよい。Ｙａ^０は、第４級炭素原子である。Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３は、それぞれ独立に、置換基を有していてもよい炭化水素基である。但し、Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３のうちの１つ以上は、少なくとも極性基を有する炭化水素基である。＊は、結合手であることを表す。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ⁰ is a divalent hydrocarbon group which may have an ether bond. n _a0 is an integer of 0-2. Ra ⁰⁰ is an acid dissociable group represented by general formula (a0-r1-1). Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent. However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group. * Represents a bond. ]

  In a second aspect of the present invention, a step of forming a resist film on the support using the resist composition of the first aspect, a step of exposing the resist film, and developing the resist film after the exposure And a resist pattern forming method comprising a step of forming a resist pattern.

  A third aspect of the present invention is a polymer compound having a structural unit (a0) represented by the following general formula (a0-1).

［式中、Ｒは、水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｖａ^０は、エーテル結合を有していてもよい２価の炭化水素基である。ｎ_ａ０は、０〜２の整数である。Ｒａ^００は、一般式（ａ０−ｒ１−１）で表される酸解離性基である。Ｒａ^０１は、置換基を有していてもよい炭化水素基である。Ｒａ^０２は、置換基を有していてもよい炭化水素基である。Ｒａ^０１とＲａ^０２とは相互に結合して、環構造を形成してもよい。Ｙａ^０は、第４級炭素原子である。Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３は、それぞれ独立に、置換基を有していてもよい炭化水素基である。但し、Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３のうちの１つ以上は、少なくとも極性基を有する炭化水素基である。＊は、結合手であることを表す。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ⁰ is a divalent hydrocarbon group which may have an ether bond. n _a0 is an integer of 0-2. Ra ⁰⁰ is an acid dissociable group represented by general formula (a0-r1-1). Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent. However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group. * Represents a bond. ]

According to the resist composition and the resist pattern forming method of the present invention, the sensitivity can be further increased and the resist pattern shape can be further improved.
The polymer compound of the present invention is useful as a resin for a resist composition in that the sensitivity can be further increased in resist pattern formation and the resist pattern shape can be further improved.

In the present specification and claims, “aliphatic” is a relative concept with respect to aromatics, and is defined to mean groups, compounds, etc. that do not have aromaticity.
Unless otherwise specified, the “alkyl group” includes linear, branched and cyclic monovalent saturated hydrocarbon groups. The same applies to the alkyl group in the alkoxy group.
The “alkylene group” includes linear, branched, and cyclic divalent saturated hydrocarbon groups unless otherwise specified.
The “halogenated alkyl group” is a group in which part or all of the hydrogen atoms of the alkyl group are substituted with a halogen atom, and examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
“Fluorinated alkyl group” or “fluorinated alkylene group” refers to a group in which part or all of the hydrogen atoms of an alkyl group or alkylene group are substituted with fluorine atoms.
“Structural unit” means a monomer unit (monomer unit) constituting a polymer compound (resin, polymer, copolymer).
When it is described as “may have a substituent”, when a hydrogen atom (—H) is substituted with a monovalent group, and when a methylene group (—CH ₂ —) is substituted with a divalent group And both.
“Exposure” is a concept including general irradiation of radiation.

“A structural unit derived from an acrylate ester” means a structural unit formed by cleavage of an ethylenic double bond of an acrylate ester.
“Acrylic acid ester” is a compound in which the hydrogen atom at the carboxy group terminal of acrylic acid (CH ₂ ═CH—COOH) is substituted with an organic group.
In the acrylate ester, the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent. The substituent (R ^α0 ) for substituting the hydrogen atom bonded to the α-position carbon atom is an atom or group other than a hydrogen atom, such as an alkyl group having 1 to 5 carbon atoms or a halogenated group having 1 to 5 carbon atoms. An alkyl group etc. are mentioned. In addition, itaconic acid diesters in which the substituent (R ^α0 ) is substituted with a substituent containing an ester bond, and α-hydroxyacrylic esters in which the substituent (R ^α0 ) is substituted with a hydroxyalkyl group or a group with a modified hydroxyl group thereof Shall be included. The α-position carbon atom of the acrylate ester is a carbon atom to which a carbonyl group of acrylic acid is bonded unless otherwise specified.
Hereinafter, an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position is substituted with a substituent may be referred to as an α-substituted acrylate ester. Further, the acrylate ester and the α-substituted acrylate ester may be collectively referred to as “(α-substituted) acrylate ester”.

“Styrene” is a concept including styrene and those in which the α-position hydrogen atom of styrene is substituted with another substituent such as an alkyl group or a halogenated alkyl group.
“Structural unit derived from styrene” and “structural unit derived from styrene derivative” mean a structural unit formed by cleavage of an ethylenic double bond of styrene or a styrene derivative.

The alkyl group as a substituent at the α-position is preferably a linear or branched alkyl group, specifically, an alkyl group having 1 to 5 carbon atoms (methyl group, ethyl group, propyl group, isopropyl group). , N-butyl group, isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group) and the like.
Specific examples of the halogenated alkyl group as the substituent at the α-position include groups in which part or all of the hydrogen atoms of the above-mentioned “alkyl group as the substituent at the α-position” are substituted with a halogen atom. It is done. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
Specific examples of the hydroxyalkyl group as a substituent at the α-position include a group in which part or all of the hydrogen atoms of the “alkyl group as the substituent at the α-position” are substituted with a hydroxyl group. 1-5 are preferable and, as for the number of the hydroxyl groups in this hydroxyalkyl group, 1 is the most preferable.

(Resist composition)
The resist composition of the present embodiment is a resist composition that generates an acid upon exposure and changes its solubility in a developer by the action of an acid, and is a group that changes its solubility in a developer by the action of an acid. Contains a material component (A) (hereinafter also referred to as “component (A)”).
When a resist film is formed using such a resist composition and the resist film is selectively exposed, an acid is generated in the exposed portion of the resist film, and the developer of component (A) is produced by the action of the acid. On the other hand, since the solubility of the component (A) in the developing solution does not change in the unexposed portion of the resist film, there is a difference in solubility in the developing solution between the exposed portion and the unexposed portion. Arise. Therefore, when the resist film is developed, when the resist composition is positive, the exposed portion is dissolved and removed to form a positive resist pattern, and when the resist composition is negative, the unexposed portion is dissolved. This is removed to form a negative resist pattern.
In this specification, a resist composition in which an exposed portion is dissolved and removed to form a positive resist pattern is referred to as a positive resist composition, and an unexposed portion is dissolved and removed to form a negative resist pattern. Is referred to as a negative resist composition.
The resist composition of the present embodiment may be a positive resist composition or a negative resist composition.
In addition, the resist composition of the present embodiment may be used for an alkali development process that uses an alkali developer for the development process at the time of forming a resist pattern, and a developer (organic developer) containing an organic solvent in the development process. It may be for a solvent development process using

The resist composition of the present embodiment has an acid generating ability to generate an acid upon exposure, and the (A) component may generate an acid upon exposure, and is added separately from the (A) component. The agent component may generate an acid upon exposure.
Specifically, the resist composition of the present embodiment is
(1) It may further contain an acid generator component (B) (hereinafter referred to as “component (B)”) that generates an acid upon exposure;
(2) The component (A) may be a component that generates an acid upon exposure;
(3) The component (A) is a component that generates an acid upon exposure, and may further contain a component (B).
That is, in the case of the above (2) and (3), the component (A) is a “base material component that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid”. When the component (A) is a base material component that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid, the component (A1) described later generates an acid upon exposure, and A polymer compound whose solubility in a developing solution is changed by the action of an acid is preferable. As such a polymer compound, a resin having a structural unit that generates an acid upon exposure can be used. A well-known thing can be used as a structural unit which generates an acid by exposure. Among these, the resist composition according to this embodiment is preferably the above (1).

<(A) component>
In the present invention, the “base component” is an organic compound having a film forming ability, and preferably an organic compound having a molecular weight of 500 or more is used. When the molecular weight of the organic compound is 500 or more, the film forming ability is improved, and in addition, a nano-level resist pattern is easily formed.
Organic compounds used as the base material component are roughly classified into non-polymers and polymers.
As the non-polymer, those having a molecular weight of 500 or more and less than 4000 are usually used. Hereinafter, the “low molecular compound” refers to a non-polymer having a molecular weight of 500 or more and less than 4000.
As the polymer, those having a molecular weight of 1000 or more are usually used. Hereinafter, the term “resin” or “polymer compound” refers to a polymer having a molecular weight of 1000 or more.
As the molecular weight of the polymer, a polystyrene-reduced weight average molecular weight by GPC (gel permeation chromatography) is used.

When the resist composition of the present embodiment is a “negative resist composition for an alkali development process” that forms a negative resist pattern in an alkali development process, or a “solvent that forms a positive resist pattern in a solvent development process In the case of the “positive resist composition for development process”, the component (A) is preferably a substrate component (A-2) soluble in an alkali developer (hereinafter referred to as “component (A-2)”). Is used, and a crosslinking agent component is further blended. In such a resist composition, for example, when an acid is generated from the component (B) by exposure, the acid acts to cause crosslinking between the component (A-2) and the crosslinking agent component. The solubility in the liquid is reduced (the solubility in the organic developer is increased). Therefore, in the formation of a resist pattern, when a resist film obtained by coating the resist composition on a support is selectively exposed, the exposed portion is hardly soluble in an alkali developer (to an organic developer). On the other hand, the unexposed area remains soluble (almost insoluble in the organic developer) while remaining undissolved in the alkaline developer, and a negative resist pattern is formed by developing with the alkaline developer. The At this time, a positive resist pattern is formed by developing with an organic developer.
As the component (A-2), a resin that is soluble in an alkali developer (hereinafter referred to as “alkali-soluble resin”) is preferably used.
Examples of the alkali-soluble resin include α- (hydroxyalkyl) acrylic acid or α- (hydroxyalkyl) acrylic acid alkyl ester (preferably having 1 to 5 carbon atoms) disclosed in, for example, JP-A-2000-206694. A resin having a unit derived from at least one selected from alkyl ester); a hydrogen atom bonded to a carbon atom at the α-position having a sulfonamide group, which is disclosed in US Pat. No. 6,949,325, is substituted with a substituent. Acrylic resin or polycycloolefin resin that may be contained; disclosed in US Pat. No. 6,949,325; The hydrogen atom bonded to the atom may be substituted with a substituent. Le resin; Japanese Patent disclosed in 2006-259582, JP-polycycloolefin resins having fluorinated alcohol is preferred because it can form a resist pattern with minimal swelling.
The α- (hydroxyalkyl) acrylic acid is a hydrogen atom bonded to the α-position carbon atom to which the carboxy group is bonded, among the acrylic acid in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent. One or both of acrylic acid having an atom bonded thereto and α-hydroxyalkylacrylic acid having a hydroxyalkyl group (preferably a hydroxyalkyl group having 1 to 5 carbon atoms) bonded to the α-position carbon atom are shown. .
As the crosslinking agent component, for example, it is usually preferable to use an amino crosslinking agent such as glycoluril having a methylol group or an alkoxymethyl group, a melamine crosslinking agent, and the like because a good resist pattern with less swelling can be formed. It is preferable that the compounding quantity of a crosslinking agent component is 1-50 mass parts with respect to 100 mass parts of alkali-soluble resin.

When the resist composition of the present embodiment is a “positive resist composition for an alkali development process” that forms a positive resist pattern in an alkali development process, or a “solvent that forms a negative resist pattern in a solvent development process In the case of a “developing process negative resist composition”, the component (A) is preferably a substrate component (A-1) whose polarity is increased by the action of an acid (hereinafter referred to as “component (A-1)”). .) Is used. By using the component (A-1), since the polarity of the base material component changes before and after exposure, a good development contrast can be obtained not only in the alkali development process but also in the solvent development process.
When the alkali development process is applied, the component (A-1) is hardly soluble in an alkali developer before exposure. For example, when acid is generated from the component (B) by exposure, The polarity increases and the solubility in an alkaline developer increases. Therefore, in the formation of a resist pattern, when a resist film obtained by applying the resist composition on a support is selectively exposed, the exposed portion changes from slightly soluble to soluble in an alkaline developer. Since the unexposed portion remains hardly soluble in alkali and does not change, a positive resist pattern is formed by alkali development.
On the other hand, when a solvent development process is applied, the component (A-1) is highly soluble in an organic developer before exposure. When an acid is generated by exposure, the component (A-1) is highly polar due to the action of the acid. The solubility in an organic developer is reduced. Therefore, in the formation of the resist pattern, when the resist film obtained by applying the resist composition on the support is selectively exposed, the exposed portion changes from soluble to poorly soluble in an organic developer. On the other hand, since the unexposed portion remains soluble and does not change, development with an organic developer can provide a contrast between the exposed portion and the unexposed portion, thereby forming a negative resist pattern.

  In the resist composition of this embodiment, the component (A) is preferably the component (A-1). That is, the resist composition of the present embodiment is a “positive resist composition for an alkali development process” that forms a positive resist pattern in an alkali development process, or a “solvent development” that forms a negative resist pattern in a solvent development process. It is preferably a “negative resist composition for process”.

The component (A) used in the resist composition of this embodiment is a polymer compound (A1) having a structural unit (a0) represented by the general formula (a0-1) (hereinafter referred to as “component (A1)”). )including.
As the component (A), at least the component (A1) is used, and other high molecular compounds and / or low molecular compounds may be used in combination with the component (A1). When the component (A-1) is used as the component (A), the component (A-1) includes the component (A1).

-About (A1) component (A1) component is a high molecular compound which has the structural unit (a0) represented by general formula (a0-1), and another structural unit as needed.

≪Structural unit (a0) ≫
The structural unit (a0) is a structural unit represented by the following general formula (a0-1).

［式中、Ｒは、水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｖａ^０は、エーテル結合を有していてもよい２価の炭化水素基である。ｎ_ａ０は、０〜２の整数である。Ｒａ^００は、一般式（ａ０−ｒ１−１）で表される酸解離性基である。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ⁰ is a divalent hydrocarbon group which may have an ether bond. n _a0 is an integer of 0-2. Ra ⁰⁰ is an acid dissociable group represented by general formula (a0-r1-1). ]

In said formula (a0-1), R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group.
The alkyl group having 1 to 5 carbon atoms in R is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, specifically, methyl group, ethyl group, propyl group, isopropyl group, n- Examples thereof include a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, and a neopentyl group.
The halogenated alkyl group having 1 to 5 carbon atoms in R is a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with a halogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms, more preferably a hydrogen atom or a methyl group, and a methyl group from the viewpoint of industrial availability. Further preferred.

In the formula (a0-1), Va ⁰ is a divalent hydrocarbon group which may have an ether bond.
The divalent hydrocarbon group in Va ⁰ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group.

The aliphatic hydrocarbon group as a divalent hydrocarbon group in Va ⁰ may be saturated or unsaturated, and is usually preferably saturated.
More specific examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like.

The linear aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6, still more preferably 1 to 4, and most preferably 1 to 3.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
The branched aliphatic hydrocarbon group preferably has 2 to 10 carbon atoms, more preferably 3 to 6, still more preferably 3 or 4, and most preferably 3.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

Examples of the aliphatic hydrocarbon group containing a ring in the structure include an alicyclic hydrocarbon group (a group obtained by removing two hydrogen atoms from an aliphatic hydrocarbon ring), and an alicyclic hydrocarbon group that is linear or branched. Examples include a group bonded to the end of a chain-like aliphatic hydrocarbon group and a group in which an alicyclic hydrocarbon group is interposed in the middle of a linear or branched aliphatic hydrocarbon group. Examples of the linear or branched aliphatic hydrocarbon group include those similar to the linear aliphatic hydrocarbon group or the branched aliphatic hydrocarbon group.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be polycyclic or monocyclic. The monocyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a monocycloalkane. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples thereof include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing two hydrogen atoms from a polycycloalkane, and the polycycloalkane preferably has 7 to 12 carbon atoms, specifically adamantane. , Norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

The aromatic hydrocarbon group as a divalent hydrocarbon group in Va ⁰ is a hydrocarbon group having an aromatic ring.
The aromatic hydrocarbon group preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, further preferably 5 to 20 carbon atoms, particularly preferably 6 to 15 carbon atoms, and most preferably 6 to 10 carbon atoms. . However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic ring of the aromatic hydrocarbon group include aromatic hydrocarbon rings such as benzene, biphenyl, fluorene, naphthalene, anthracene, and phenanthrene; a part of carbon atoms constituting the aromatic hydrocarbon ring is hetero Aromatic heterocycles substituted with atoms and the like. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group is a group obtained by removing two hydrogen atoms from the aromatic hydrocarbon ring (arylene group); a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring (aryl group) ) In which one of the hydrogen atoms is substituted with an alkylene group (for example, arylalkyl such as benzyl, phenethyl, 1-naphthylmethyl, 2-naphthylmethyl, 1-naphthylethyl, 2-naphthylethyl, etc.) And a group obtained by further removing one hydrogen atom from the aryl group in the group). The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

In the formula (a0-1), _na0 is an integer of 0 to 2, preferably 0 or 1, and more preferably 0.

In the formula (a0-1), Ra ⁰⁰ is an acid dissociable group represented by the following general formula (a0-r1-1). Such an acid dissociable group is a functional group having a quaternary carbon atom (Ya ⁰ ) and a polar group, and the carbonyloxy group [—C (═O) —O— in the formula (a0-1). ] On the oxy group (—O—) side. The “acid-dissociable group” here has acid-dissociation property that allows the bond between the acid-dissociable group and the oxygen atom (O) adjacent to the acid-dissociable group to be cleaved by the action of an acid. When the acid dissociable group is dissociated by the action of an acid, a polar group having a polarity higher than that of the acid dissociable group is generated, and the polarity is increased. As a result, the polarity of the entire component (A1) increases. As the polarity increases, the solubility in the developer changes relatively. When the developer is an alkaline developer, the solubility increases. When the developer is an organic developer, the solubility increases. Decrease.

［式中、Ｒａ^０１は、置換基を有していてもよい炭化水素基である。Ｒａ^０２は、置換基を有していてもよい炭化水素基である。Ｒａ^０１とＲａ^０２とは相互に結合して、環構造を形成してもよい。Ｙａ^０は、第４級炭素原子である。Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３は、それぞれ独立に、置換基を有していてもよい炭化水素基である。但し、Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３のうちの１つ以上は、少なくとも極性基を有する炭化水素基である。＊は、結合手であることを表す（以下本明細書において同じ）。］

[In the formula, Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent. However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group. * Represents a bond (hereinafter the same in this specification). ]

  In the formula (a0-r1-1), * is a bond that is bonded to the oxy group (—O—) of the carbonyloxy group [—C (═O) —O—] in the formula (a0-1). is there.

In the formula (a0-r1-1), Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure.
Examples of the hydrocarbon group in Ra ⁰¹ and Ra ⁰² include a linear or branched alkyl group, a linear or cyclic alkenyl group, or a cyclic hydrocarbon group.

The linear alkyl group in Ra ⁰¹ and Ra ⁰² preferably has 1 to 5 carbon atoms, more preferably 1 to 4, and still more preferably 1 or 2. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, and an n-pentyl group. Among these, a methyl group, an ethyl group, or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.
The branched alkyl group in Ra ⁰¹ and Ra ⁰² preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include isopropyl group, isobutyl group, tert-butyl group, isopentyl group, neopentyl group, 1,1-diethylpropyl group, 2,2-dimethylbutyl group, and the like is preferably isopropyl group.
The chain or cyclic alkenyl group in Ra ⁰¹ and Ra ⁰² is preferably an alkenyl group having 2 to 10 carbon atoms.

The cyclic hydrocarbon group in Ra ⁰¹ and Ra ⁰² may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group, and may be a polycyclic group or a monocyclic group.
As the aliphatic hydrocarbon group which is a monocyclic group, a group in which one hydrogen atom has been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane.
The aliphatic hydrocarbon group which is a polycyclic group is preferably a group obtained by removing one hydrogen atom from a polycycloalkane, and the polycycloalkane is preferably a group having 7 to 12 carbon atoms, specifically Includes adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

The aromatic hydrocarbon group in Ra ⁰¹ and Ra ⁰² is a hydrocarbon group having at least one aromatic ring. The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n + 2 π electrons, and may be monocyclic or polycyclic. It is preferable that carbon number of an aromatic ring is 5-30, 5-20 are more preferable, 6-15 are more preferable, and 6-12 are especially preferable. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; aromatic heterocycles in which a part of carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms, and the like. Can be mentioned. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom. Specific examples of the aromatic heterocycle include a pyridine ring and a thiophene ring. Specifically, the aromatic hydrocarbon group is a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring or aromatic heterocyclic ring (aryl group or heteroaryl group); an aromatic group containing two or more aromatic rings A group in which one hydrogen atom has been removed from a compound (for example, biphenyl, fluorene, etc.); a group in which one of the hydrogen atoms of the aromatic hydrocarbon ring or aromatic heterocyclic ring is substituted with an alkylene group (for example, a benzyl group, a phenethyl group) 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, arylalkyl groups such as 2-naphthylethyl group, etc.). The alkylene group bonded to the aromatic hydrocarbon ring or aromatic heterocyclic ring preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

When the hydrocarbon group represented by Ra ⁰¹ and Ra ⁰² is substituted, examples of the substituent include a hydroxy group, a carboxy group, a halogen atom (fluorine atom, chlorine atom, bromine atom, etc.), alkoxy Groups (methoxy group, ethoxy group, propoxy group, butoxy group, etc.), alkyloxycarbonyl groups and the like.

In the formula (a0-r1-1), Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure.
Examples of the ring structure formed by Ra ⁰¹ and Ra ⁰² include an alicyclic hydrocarbon group, a condensed ring of an alicyclic hydrocarbon and an aromatic hydrocarbon, and the like. The ring structure formed by Ra ⁰¹ and Ra ⁰² may have a hetero atom.

The alicyclic hydrocarbon group formed by Ra ⁰¹ and Ra ⁰² may be a polycyclic group or a monocyclic group.
As the alicyclic hydrocarbon group which is a monocyclic group, a group in which one hydrogen atom has been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane.
The aliphatic hydrocarbon group which is a polycyclic group is preferably a group obtained by removing one hydrogen atom from a polycycloalkane, and the polycycloalkane is preferably a group having 7 to 12 carbon atoms, specifically Includes adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

In the condensed ring formed by Ra ⁰¹ and Ra ⁰² , the alicyclic hydrocarbon portion may be monocyclic or polycyclic, and the aromatic hydrocarbon portion may be monocyclic or polycyclic.
This condensed ring may have a substituent. Examples of the substituent include methyl group, ethyl group, propyl group, hydroxy group, hydroxyalkyl group, carboxy group, halogen atom (fluorine atom, chlorine atom, bromine atom, etc.), alkoxy group (methoxy group, ethoxy group, Propoxy group, butoxy group, etc.), acyl group, alkyloxycarbonyl group, alkylcarbonyloxy group and the like.
Specific examples of the condensed ring formed by Ra ⁰¹ and Ra ⁰² are shown below.

In the formula (a0-r1-1), Ra ⁰¹ and Ra ⁰² are preferably bonded to each other to form a ring structure because the lithography properties are more likely to be enhanced. It is more preferable to form a formula hydrocarbon group.

In the formula (a0-r1-1), Ya ⁰ is a quaternary carbon atom. That is, there are four adjacent carbon atoms bonded to Ya ⁰ (carbon atom).

In the formula (a0-r1-1), Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent.
The hydrocarbon group which may have a substituent in Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ may have a substituent in Ra ⁰¹ and Ra ⁰² in the formula (a0-r1-1). The thing similar to a good hydrocarbon group is mentioned. Among these, the hydrocarbon group which may have a substituent in Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is preferably a linear or branched alkyl group which may have a substituent. A chain alkyl group is more preferable.

However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group.
The term “hydrocarbon group having a polar group” means that a polar group is interposed between hydrocarbon chains (between carbon atoms), or at least one hydrogen atom constituting the hydrocarbon group is substituted with a polar group. Any of these are included.
The “hydrocarbon group having a polar group” is preferably a functional group represented by the following general formula (a0-p1).

［式中、Ｒａ^０４は、炭素数２〜１２の２価の炭化水素基を表す。Ｒａ^０５は、ヘテロ原子を含む２価の連結基を表す。Ｒａ^０６は、炭素数１〜１２の１価の炭化水素基を表す。ｎ_ｐ０は、１〜６の整数である。］

[In the formula, Ra ⁰⁴ represents a divalent hydrocarbon group having 2 to 12 carbon atoms. Ra ⁰⁵ represents a divalent linking group containing a hetero atom. Ra ⁰⁶ represents a monovalent hydrocarbon group having 1 to 12 carbon atoms. n _p0 is an integer of 1 to 6. ]

In the formula (a0-p1), Ra ⁰⁴ represents a divalent hydrocarbon group having 2 to 12 carbon atoms.
Ra ⁰⁴ has 2 to 12 carbon atoms, preferably 2 to 8 carbon atoms, more preferably 2 to 6 carbon atoms, still more preferably 2 to 4 carbon atoms, and particularly preferably 2 carbon atoms.
The hydrocarbon group in Ra ⁰⁴ is preferably a chain or cyclic aliphatic hydrocarbon group, and more preferably a chain hydrocarbon group.
Examples of Ra ⁰⁴ include ethylene group, propane-1,3-diyl group, butane-1,4-diyl group, pentane-1,5-diyl group, hexane-1,6-diyl group, heptane-1, 7-diyl group, octane-1,8-diyl group, nonane-1,9-diyl group, decane-1,10-diyl group, undecane-1,11-diyl group, dodecane-1,12-diyl group, etc. A linear alkanediyl group of propane-1,2-diyl group, 1-methylbutane-1,3-diyl group, 2-methylpropane-1,3-diyl group, pentane-1,4-diyl group, 2 -Branched chain alkanediyl group such as methylbutane-1,4-diyl group; cyclobutane-1,3-diyl group, cyclopentane-1,3-diyl group, cyclohexane-1,4-diyl group, cyclooctane-1 , 5-Di Cycloalkanediyl groups such as yl groups; polycyclic cyclic groups such as norbornane-1,4-diyl group, norbornane-2,5-diyl group, adamantane-1,5-diyl group, adamantane-2,6-diyl group, etc. And divalent alicyclic hydrocarbon groups.
Among the above, an alkanediyl group is preferable, and a linear alkanediyl group is more preferable.

In the formula (a0-p1), Ra ⁰⁵ represents a divalent linking group containing a hetero atom.
Ra ⁰⁵ is, for example, —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O—, —C (═O) —NH—. , —NH—, —NH—C (═NH) — (H may be substituted with a substituent such as an alkyl group or an acyl group), —S—, —S (═O) ₂ —, — S (= O) ₂ —O— and the like can be mentioned.
Among these, from the viewpoint of solubility in a developer, —O—, —C (═O) —O—, —C (═O) —, —O—C (═O) —O— are preferable. O- and -C (= O)-are particularly preferable.

In the formula (a0-p1), Ra ⁰⁶ represents a monovalent hydrocarbon group having 1 to 12 carbon atoms.
Ra ⁰⁶ has 1 to 12 carbon atoms, preferably 1 to 8 carbon atoms, more preferably 1 to 5 carbon atoms, still more preferably 1 to 3 carbon atoms, from the viewpoint of solubility in a developer. 1 or 2 is particularly preferable, and 1 is most preferable.

Examples of the hydrocarbon group in Ra ⁰⁶ include a chain hydrocarbon group or a cyclic hydrocarbon group, or a hydrocarbon group in which a chain and a ring are combined.
Examples of the chain hydrocarbon group include a methyl group, ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, n-pentyl group, n-hexyl group, n -Heptyl group, 2-ethylhexyl group, n-octyl group, n-nonyl group, n-decyl group, n-undecyl group, n-dodecyl group and the like can be mentioned.

The cyclic hydrocarbon group may be an alicyclic hydrocarbon group or an aromatic hydrocarbon group.
The alicyclic hydrocarbon group may be monocyclic or polycyclic, and examples of the monocyclic alicyclic hydrocarbon group include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, and a methyl group. Examples thereof include cycloalkyl groups such as cyclohexyl group, dimethylcyclohexyl group, cycloheptyl group, cyclooctyl group, cycloheptyl group, and cyclodecyl group. Examples of the polycyclic alicyclic hydrocarbon group include decahydronaphthyl group, adamantyl group, 2-alkyladamantan-2-yl group, 1- (adamantan-1-yl) alkane-1-yl group, and norbornyl. Group, methylnorbornyl group, isobornyl group and the like.
Examples of the aromatic hydrocarbon group include a phenyl group, a naphthyl group, an anthryl group, a p-methylphenyl group, a p-tert-butylphenyl group, a p-adamantylphenyl group, a tolyl group, a xylyl group, a cumenyl group, and a mesityl group. , Biphenyl group, phenanthryl group, 2,6-diethylphenyl group, 2-methyl-6-ethylphenyl group and the like.

Ra ⁰⁶ is preferably a chain hydrocarbon group, more preferably an alkyl group, and still more preferably a linear alkyl group, from the viewpoint of solubility in a developer.

In the formula (a0-p1), n _p0 is an integer of 1 to 6, preferably an integer of 1 to 3, more preferably 1 or 2, and even more preferably 1.

Specific examples of the hydrocarbon group having at least a polar group are shown below.
In the following formula, * is a bond bonded to a quaternary carbon atom (Ya ⁰ ).

In formula (a0-r1-1), among Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ , the number of hydrocarbon groups having at least a polar group is one or more. ^May be appropriately determined in consideration of the solubility of, for example, one or two of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are preferred, and one is particularly preferred.

  The hydrocarbon group having at least a polar group may have a substituent other than the polar group. Examples of the substituent include a halogen atom (fluorine atom, chlorine atom, bromine atom, etc.) and a halogenated alkyl group having 1 to 5 carbon atoms.

In the formula (a0-1), Ra ⁰⁰ is preferably an acid dissociable group represented by the following general formula (a0-r1-10).

［式中、Ｙａａは炭素原子である。Ｘａａは、Ｙａａと共に環状の炭化水素基を形成する基である。Ｙａ^０は、第４級炭素原子である。Ｒａ^０３１１及びＲａ^０３２１は、それぞれ独立に、置換基を有していてもよい鎖状のアルキル基を表す。Ｒａ^０３３１は、上記一般式（ａ０−ｐ１）で表される官能基を表す。］

[Wherein Yaa is a carbon atom. Xaa is a group that forms a cyclic hydrocarbon group together with Yaa. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹¹ and Ra ⁰³²¹ each independently represent a chain-like alkyl group which may have a substituent. Ra ⁰³³¹ represents the functional group represented by the general formula (a0-p1). ]

In the formula (a0-r1-10), examples of the cyclic hydrocarbon group formed by Xaa together with Yaa are exemplified in the description of Ra ⁰¹ and Ra ⁰² in the formula (a0-r1-1). Examples thereof are the same as those obtained by further removing one or more hydrogen atoms from a cyclic hydrocarbon group.
Among these, the alicyclic hydrocarbon group is preferable as the cyclic hydrocarbon group formed by Xaa together with Yaa. Such an alicyclic hydrocarbon group may be a polycyclic group or a monocyclic group, and among them, a monocyclic group is more preferable.

  The cyclic hydrocarbon group formed by Xaa together with Yaa may have a substituent. Examples of the substituent include hydroxy group, carboxy group, halogen atom (fluorine atom, chlorine atom, bromine atom, etc.), alkoxy group (methoxy group, ethoxy group, propoxy group, butoxy group, etc.), alkyloxycarbonyl group, etc. Is mentioned.

In the formula (a0-r1-10), Ra ⁰³¹¹ and Ra ⁰³²¹ each independently represent a chain alkyl group which may have a substituent.
^Examples of the chain alkyl group in Ra ⁰³¹¹ and Ra ⁰³²¹ include the same as the linear or branched alkyl group in Ra ⁰¹ and Ra ⁰² . Among these, a linear alkyl group is preferable, it is preferable that it is C1-C5, a methyl group, an ethyl group, or n-butyl group is more preferable, and a methyl group or an ethyl group is further more preferable.

Specific examples of the structural unit represented by the formula (a0-1) are shown below.
In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

As the structural unit (a0) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
The proportion of the structural unit (a0) in the component (A1) is preferably 10 to 70 mol%, more preferably 20 to 65 mol%, based on the total (100 mol%) of all the structural units constituting the component (A1). Preferably, 25 to 60 mol% is more preferable, and 30 to 50 mol% is particularly preferable.
When the proportion of the structural unit (a0) is not less than the lower limit of the preferable range, a resist pattern can be easily obtained, and sensitivity, in-plane uniformity of pattern dimensions (CDU), and circularity (Circularity) Lithographic properties such as) are also improved. On the other hand, when it is not more than the upper limit value of the preferred range, it becomes easy to balance with other structural units.

≪Other structural units≫
The component (A1) may have other structural units other than the structural unit (a0) described above.
Examples of other structural units include, for example, a structural unit (a1) (excluding the structural unit (a0)) containing an acid-decomposable group whose polarity increases by the action of an acid; a lactone-containing cyclic group, and —SO ₂ — content A structural unit (a2) containing a cyclic group or a carbonate-containing cyclic group; a structural unit (a3) containing a polar group-containing aliphatic hydrocarbon group (however, the structural unit (a0), the structural unit (a1) or the structural unit ( except for those corresponding to a2)); a structural unit (a4) containing a non-acid-dissociable aliphatic cyclic group; a structural unit derived from styrene or a derivative thereof.

About structural unit (a1):
In addition to the structural unit (a0), the component (A1) may further include a structural unit (a1) containing an acid-decomposable group that increases in polarity by the action of an acid.

The “acid-decomposable group” is an acid-decomposable group that can cleave at least part of bonds in the structure of the acid-decomposable group by the action of an acid.
Examples of the acid-decomposable group whose polarity increases by the action of an acid include a group that decomposes by the action of an acid to generate a polar group.
Examples of the polar group include a carboxy group, a hydroxyl group, an amino group, a sulfo group (—SO ₃ H), and the like. Among these, a polar group containing —OH in the structure (hereinafter sometimes referred to as “OH-containing polar group”) is preferable, a carboxy group or a hydroxyl group is more preferable, and a carboxy group is particularly preferable.
More specifically, examples of the acid-decomposable group include groups in which the polar group is protected with an acid-dissociable group (for example, a group in which a hydrogen atom of an OH-containing polar group is protected with an acid-dissociable group).
Here, the “acid-dissociable group” means (i) a group having acid-dissociable properties capable of cleaving a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group by the action of an acid, Alternatively, (ii) after a partial bond is cleaved by the action of an acid, a further decarboxylation reaction occurs, whereby a bond between the acid-dissociable group and an atom adjacent to the acid-dissociable group is cleaved. Both of the resulting groups
The acid-dissociable group constituting the acid-decomposable group must be a group having a lower polarity than the polar group generated by dissociation of the acid-dissociable group. Is dissociated, a polar group having a polarity higher than that of the acid dissociable group is generated to increase the polarity. As a result, the polarity of the entire component (A1) increases. As the polarity increases, the solubility in the developer changes relatively. When the developer is an alkaline developer, the solubility increases. When the developer is an organic developer, the solubility increases. Decrease.

As the acid dissociable group in the structural unit (a1), the acid dissociable group represented by the general formula (a0-r1-1) described above is excluded. What is proposed as an acid dissociable group is mentioned.
Specifically, what is proposed as an acid dissociable group of a base resin for a chemically amplified resist includes an “acetal acid dissociable group” and a “tertiary alkyl ester acid dissociable group” described below. , “Tertiary alkyloxycarbonyl acid dissociable group”.

・ Acetal type acid dissociable group:
Examples of the acid dissociable group that protects a carboxy group or a hydroxyl group among the polar groups include, for example, an acid dissociable group represented by the following general formula (a1-r-1) (hereinafter referred to as “acetal acid dissociable group”). May be included).

［式中、Ｒａ’^１、Ｒａ’^２は水素原子またはアルキル基であり、Ｒａ’^３は炭化水素基であって、Ｒａ’^３は、Ｒａ’^１、Ｒａ’^２のいずれかと結合して環を形成してもよい。］

[Wherein, Ra ′ ¹ and Ra ′ ² are a hydrogen atom or an alkyl group, Ra ′ ³ is a hydrocarbon group, and Ra ′ ³ is bonded to either Ra ′ ¹ or Ra ′ ² to form a ring. May be formed. ]

In formula (a1-r-1), at least one of Ra ′ ¹ and Ra ′ ² is preferably a hydrogen atom, and more preferably both are hydrogen atoms.
In the case where Ra ′ ¹ or Ra ′ ² is an alkyl group, the alkyl group is the alkyl group mentioned as the substituent that may be bonded to the α-position carbon atom in the description of the α-substituted acrylate ester. The same thing is mentioned, A C1-C5 alkyl group is preferable. Specifically, a linear or branched alkyl group is preferable. More specifically, a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, a neopentyl group, and the like can be given. More preferred is a methyl group.

In formula (a1-r-1), examples of the Ra ′ ³ hydrocarbon group include a linear or branched alkyl group and a cyclic hydrocarbon group.
The linear alkyl group preferably has 1 to 5 carbon atoms, more preferably 1 to 4, and still more preferably 1 or 2. Specific examples include a methyl group, an ethyl group, an n-propyl group, an n-butyl group, and an n-pentyl group. Among these, a methyl group, an ethyl group, or an n-butyl group is preferable, and a methyl group or an ethyl group is more preferable.

  The branched alkyl group preferably has 3 to 10 carbon atoms, and more preferably 3 to 5 carbon atoms. Specific examples include isopropyl group, isobutyl group, tert-butyl group, isopentyl group, neopentyl group, 1,1-diethylpropyl group, 2,2-dimethylbutyl group, and the like is preferably isopropyl group.

When Ra ′ ³ is a cyclic hydrocarbon group, the hydrocarbon group may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group, and may be a polycyclic group or a monocyclic group.
As the aliphatic hydrocarbon group which is a monocyclic group, a group in which one hydrogen atom has been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane.
The aliphatic hydrocarbon group which is a polycyclic group is preferably a group obtained by removing one hydrogen atom from a polycycloalkane, and the polycycloalkane is preferably a group having 7 to 12 carbon atoms, specifically Includes adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane and the like.

When the cyclic hydrocarbon group of Ra ′ ³ is an aromatic hydrocarbon group, the aromatic hydrocarbon group is a hydrocarbon group having at least one aromatic ring.
The aromatic ring is not particularly limited as long as it is a cyclic conjugated system having 4n + 2 π electrons, and may be monocyclic or polycyclic. It is preferable that carbon number of an aromatic ring is 5-30, 5-20 are more preferable, 6-15 are more preferable, and 6-12 are especially preferable. Specific examples of the aromatic ring include aromatic hydrocarbon rings such as benzene, naphthalene, anthracene, and phenanthrene; aromatic heterocycles in which a part of carbon atoms constituting the aromatic hydrocarbon ring are substituted with heteroatoms, and the like. Can be mentioned. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom. Specific examples of the aromatic heterocycle include a pyridine ring and a thiophene ring.
Specifically, the aromatic hydrocarbon group in Ra ′ ³ is a group obtained by removing one hydrogen atom from the aromatic hydrocarbon ring or aromatic heterocyclic ring (aryl group or heteroaryl group); A group obtained by removing one hydrogen atom from an aromatic compound (for example, biphenyl, fluorene, etc.); a group in which one of the hydrogen atoms of the aromatic hydrocarbon ring or aromatic heterocyclic ring is substituted with an alkylene group (for example, a benzyl group) Phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, arylalkyl groups such as 2-naphthylethyl group, etc.). The alkylene group bonded to the aromatic hydrocarbon ring or aromatic heterocyclic ring preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

When Ra ′ ³ is bonded to either Ra ′ ¹ or Ra ′ ² to form a ring, the cyclic group is preferably a 4- to 7-membered ring, and more preferably a 4- to 6-membered ring. Specific examples of the cyclic group include a tetrahydropyranyl group and a tetrahydrofuranyl group.

Tertiary alkyl ester type acid dissociable group:
Among the polar groups, examples of the acid dissociable group that protects the carboxy group include an acid dissociable group represented by the following general formula (a1-r-2). In addition, among the acid dissociable groups represented by the following formula (a1-r-2), those composed of an alkyl group may be hereinafter referred to as “tertiary alkyl ester type acid dissociable groups” for convenience. .

［式中、Ｒａ’^４〜Ｒａ’^６はそれぞれ炭化水素基であって、Ｒａ’^５、Ｒａ’^６は互いに結合して環を形成してもよい。］

[Wherein, Ra ′ ^{4 to} Ra ′ ⁶ are each a hydrocarbon group, and Ra ′ ⁵ and Ra ′ ⁶ may be bonded to each other to form a ring. ]

As the hydrocarbon group for Ra ′ ^{4 to} Ra ′ ^6, the same groups as those described above for Ra ′ ³ can be mentioned.
Ra ′ ⁴ is preferably an alkyl group having 1 to 5 carbon atoms. When Ra ′ ⁵ and Ra ′ ⁶ are bonded to each other to form a ring, a group represented by general formula (a1-r2-1) shown below can be given. On the other hand, when Ra ′ ^{4 to} Ra ′ ⁶ are not bonded to each other and are independent hydrocarbon groups, groups represented by the following general formula (a1-r2-2) are exemplified.

［式中、Ｒａ’^１０は炭素数１〜１０のアルキル基、Ｒａ’^１１はＲａ’^１０が結合した炭素原子と共に脂肪族環式基を形成する基、Ｒａ’^１２〜Ｒａ’^１４は、それぞれ独立に炭化水素基を示す。］

[Wherein, Ra ′ ¹⁰ is an alkyl group having 1 to ¹⁰ carbon atoms, Ra ′ ¹¹ is a group that forms an aliphatic cyclic group together with a carbon atom to which Ra ′ ¹⁰ is bonded, and Ra ′ ^{12 to} Ra ′ ¹⁴ are Independently represents a hydrocarbon group. ]

Formula (a1-r2-1) in, Ra 'alkyl group having 1 to 10 carbon atoms ^10, Ra in formula (a1-r-1)' was mentioned as the linear or branched alkyl group of ³ Groups are preferred. In formula (a1-r2-1), the aliphatic cyclic group formed by Ra ′ ¹¹ together with the carbon atom to which Ra ′ ¹⁰ is bonded is a monocyclic group of Ra ′ ³ in formula (a1-r-1) or The groups mentioned as the aliphatic hydrocarbon group which is a polycyclic group are preferred.

In formula (a1-r2-2), Ra ′ ¹² and Ra ′ ¹⁴ are preferably each independently an alkyl group having 1 to 10 carbon atoms, and the alkyl group is represented by Ra in formula (a1-r-1). 'The group mentioned as a linear or branched alkyl group of ³ is more preferable, It is more preferable that it is a C1-C5 linear alkyl group, It is especially preferable that it is a methyl group or an ethyl group .
In formula (a1-r2-2), Ra ′ ¹³ represents a linear or branched alkyl group or monocyclic group exemplified as the hydrocarbon group for Ra ′ ³ in formula (a1-r-1). Or it is preferable that it is an aliphatic hydrocarbon group which is a polycyclic group. Among these, the group mentioned as the aliphatic hydrocarbon group which is a monocyclic group or a polycyclic group of Ra ′ ³ is more preferable.

  Specific examples of the group represented by the formula (a1-r2-1) are given below. * Represents a bond (hereinafter the same in this specification).

  Specific examples of the group represented by the formula (a1-r2-2) are given below.

Tertiary alkyloxycarbonyl acid dissociable group:
Examples of the acid dissociable group for protecting the hydroxyl group among the polar groups include an acid dissociable group represented by the following general formula (a1-r-3) (hereinafter referred to as “tertiary alkyloxycarbonyl acid dissociable group for convenience”). ”).

［式中、Ｒａ’^７〜Ｒａ’^９はそれぞれアルキル基である。］

[Wherein, Ra ′ ^{7 to} Ra ′ ⁹ each represents an alkyl group. ]

In formula (a1-r-3), Ra ′ ^{7 to} Ra ′ ⁹ are each preferably an alkyl group having 1 to 5 carbon atoms, and more preferably an alkyl group having 1 to 3 carbon atoms.
Moreover, it is preferable that the total carbon number of each alkyl group is 3-7, it is more preferable that it is 3-5, and it is most preferable that it is 3-4.

  As the structural unit (a1), a structural unit derived from an acrylate ester in which a hydrogen atom bonded to a carbon atom at the α-position may be substituted with a substituent, a structural unit derived from acrylamide, hydroxystyrene or hydroxy A structural unit in which at least a part of hydrogen atoms in a hydroxyl group of a structural unit derived from a styrene derivative is protected by a substituent containing the acid-decomposable group, a structural unit derived from vinylbenzoic acid or a vinylbenzoic acid derivative; Examples include a structural unit in which at least a part of hydrogen atoms in C (═O) —OH is protected by a substituent containing the acid-decomposable group.

Among the above, the structural unit (a1) is preferably a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the carbon atom at the α-position may be substituted with a substituent.
Preferable specific examples of the structural unit (a1) include structural units represented by the following general formula (a1-1) or (a1-2).

［式中、Ｒは水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｖａ^１はエーテル結合を有していてもよい２価の炭化水素基であり、ｎ_ａ１は０〜２であり、Ｒａ^１は上記式（ａ１−ｒ−１）又は（ａ１−ｒ−２）で表される酸解離性基である。Ｗａ^１はｎ_ａ２＋１価の炭化水素基であり、ｎ_ａ２は１〜３であり、Ｒａ^２は上記式（ａ１−ｒ−１）又は（ａ１−ｒ−３）で表される酸解離性基である。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ¹ is a divalent hydrocarbon group which may have an ether bond, n _a1 is 0 to 2, and Ra ¹ is the above formula (a1-r-1) or (a1-r-2) It is an acid dissociable group represented by. Wa ¹ is a n _a2 +1 valent hydrocarbon group, n _a2 is 1 to 3, and Ra ² is an acid dissociation property represented by the above formula (a1-r-1) or (a1-r-3). It is a group. ]

In the formula (a1-1), the alkyl group having 1 to 5 carbon atoms of R is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, specifically a methyl group or an ethyl group. Propyl group, isopropyl group, n-butyl group, isobutyl group, tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like. The halogenated alkyl group having 1 to 5 carbon atoms is a group in which part or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms are substituted with halogen atoms. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable.
R is preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a fluorinated alkyl group having 1 to 5 carbon atoms, and is most preferably a hydrogen atom or a methyl group in terms of industrial availability.

In the formula (a1-1), the hydrocarbon group which may divalent have an ether bond Va ¹ is, Va ⁰ in formula (a0-1) is have an ether bond as a substituent This is the same as the case where the divalent hydrocarbon group may be used.

In the formula (a1-2), the n _a2 +1 valent hydrocarbon group in Wa ¹ may be an aliphatic hydrocarbon group or an aromatic hydrocarbon group. The aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity, may be saturated or unsaturated, and is usually preferably saturated. Examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group including a ring in the structure, or a linear or branched aliphatic hydrocarbon group. Examples thereof include a combination of an aliphatic hydrocarbon group containing a ring in the structure.
The n _a2 +1 valence is preferably 2 to 4, and more preferably 2 or 3.

Specific examples of the structural unit represented by the formula (a1-1) are shown below. In the following formulas, R ^α represents a hydrogen atom, a methyl group or a trifluoromethyl group.

  Specific examples of the structural unit represented by the formula (a1-2) are shown below.

As the structural unit (a1) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
When the component (A1) has the structural unit (a1), the proportion of the structural unit (a1) in the component (A1) is 1 to 50 mol% with respect to the total of all the structural units constituting the component (A1). Preferably, 5-45 mol% is more preferable, and 5-30 mol% is further more preferable.
By setting the ratio of the structural unit (a1) to the lower limit value or more, a resist pattern can be easily obtained, and lithography properties such as sensitivity, resolution, roughness improvement, or EL margin are improved. In addition, by setting the upper limit value or less, it is possible to balance with other structural units.

Regarding structural unit (a2):
In addition to the structural unit (a0), the component (A1) may further include a structural unit (a2) containing a lactone-containing cyclic group, an —SO ₂ — containing cyclic group, or a carbonate-containing cyclic group. .
The lactone-containing cyclic group, -SO ₂ -containing cyclic group or carbonate-containing cyclic group of the structural unit (a2) can be used to adhere the resist film to the substrate when the component (A1) is used for forming the resist film. It is effective in enhancing the sex. Moreover, by having the structural unit (a2), in the alkali development process, the solubility of the resist film in the alkaline developer is enhanced during development.

The “lactone-containing cyclic group” refers to a cyclic group containing a ring (lactone ring) containing —O—C (═O) — in the ring skeleton. The lactone ring is counted as the first ring. When only the lactone ring is present, it is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The lactone-containing cyclic group may be a monocyclic group or a polycyclic group.
The lactone-containing cyclic group in the structural unit (a2) is not particularly limited, and any lactone-containing cyclic group can be used. Specific examples include groups represented by general formulas (a2-r-1) to (a2-r-7) shown below.

［式中、Ｒａ’^２１は、それぞれ独立に、水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基又はシアノ基であり；Ｒ”は水素原子、アルキル基、ラクトン含有環式基、カーボネート含有環式基、又は−ＳＯ_２−含有環式基である。Ａ”は酸素原子（−Ｏ−）もしくは硫黄原子（−Ｓ−）を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子又は硫黄原子である。ｎ’は０〜２の整数であり、ｍ’は０又は１である。］

[Wherein, Ra ′ ²¹ each independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group, or a cyano group. R ″ is a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group, or an —SO ₂ -containing cyclic group. A ″ is an oxygen atom (—O—) or a sulfur atom. It is a C1-C5 alkylene group, oxygen atom, or sulfur atom which may contain (-S-). n ′ is an integer of 0 to 2, and m ′ is 0 or 1. ]

In the formula (a2-r-1) ~ (a2-r-7), the alkyl group in Ra ^'21, preferably an alkyl group having 1 to 6 carbon atoms. The alkyl group is preferably linear or branched. Specific examples include a methyl group, an ethyl group, a propyl group, an isopropyl group, an n-butyl group, an isobutyl group, a tert-butyl group, a pentyl group, an isopentyl group, a neopentyl group, and a hexyl group. Among these, a methyl group or an ethyl group is preferable, and a methyl group is particularly preferable.
The alkoxy group in the ra ^'21, preferably an alkoxy group having 1 to 6 carbon atoms. The alkoxy group is preferably linear or branched. Specifically, groups of the the Ra 'group and an oxygen atom mentioned as the alkyl group in ²¹ (-O-) are linked and the like.
Examples of the halogen atom in Ra ′ ²¹ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
'As the halogenated alkyl group in ^21, wherein Ra' Ra some or all of the hydrogen atoms of the alkyl group in ²¹ can be given has been substituted with the aforementioned halogen atoms. As the halogenated alkyl group, a fluorinated alkyl group is preferable, and a perfluoroalkyl group is particularly preferable.

In —COOR ″ and —OC (═O) R ″ in Ra ′ ²¹ , R ″ is any hydrogen atom, alkyl group, lactone-containing cyclic group, carbonate-containing cyclic group, or —SO ₂ -containing cyclic group. It is.
The alkyl group for R ″ may be linear, branched or cyclic, and preferably has 1 to 15 carbon atoms.
When R ″ is a linear or branched alkyl group, it preferably has 1 to 10 carbon atoms, more preferably 1 to 5 carbon atoms, and particularly preferably a methyl group or an ethyl group. preferable.
When R ″ is a cyclic alkyl group, it preferably has 3 to 15 carbon atoms, more preferably 4 to 12 carbon atoms, and most preferably 5 to 10 carbon atoms. Specifically, a fluorine atom Or a group obtained by removing one or more hydrogen atoms from a monocycloalkane which may or may not be substituted with a fluorinated alkyl group; a polycycloalkane such as a bicycloalkane, tricycloalkane or tetracycloalkane A group in which one or more hydrogen atoms are removed from a monocycloalkane such as cyclopentane, cyclohexane, etc .; more specifically, a group in which one or more hydrogen atoms are removed; adamantane, norbornane, isobornane, Examples include groups in which one or more hydrogen atoms have been removed from a polycycloalkane such as cyclodecane or tetracyclododecane. That.
Examples of the lactone-containing cyclic group for R ″ include the same groups as those represented by general formulas (a2-r-1) to (a2-r-7).
The carbonate-containing cyclic group for R ″ is the same as the carbonate-containing cyclic group described later, and specifically, groups represented by general formulas (ax3-r-1) to (ax3-r-3), respectively. Is mentioned.
The —SO ₂ — containing cyclic group in R ″ is the same as the later-described —SO ₂ — containing cyclic group, and specifically, is represented by the general formulas (a5-r-1) to (a5-r-4) And groups represented respectively by
As the hydroxyalkyl group in Ra ′ ²¹ , those having 1 to 6 carbon atoms are preferable, and specific examples include a group in which at least one hydrogen atom of the alkyl group in Ra ′ ²¹ is substituted with a hydroxyl group. .

In the general formulas (a2-r-2), (a2-r-3), and (a2-r-5), the alkylene group having 1 to 5 carbon atoms in A ″ is linear or branched. An alkylene group is preferable, and examples include a methylene group, an ethylene group, an n-propylene group, an isopropylene group, etc. When the alkylene group contains an oxygen atom or a sulfur atom, specific examples thereof include a terminal of the alkylene group or a carbon atom. between atoms -O- or -S- can be mentioned a group intervening, for example, _{-O-CH 2 -, - CH} 2 -O-CH 2 -, - S-CH 2 -, - CH 2 -S-CH _As A ″, an alkylene group having 1 to 5 carbon atoms or —O— is preferable, an alkylene group having 1 to 5 carbon atoms is more preferable, and a methylene group is most preferable.

  Specific examples of groups represented by general formulas (a2-r-1) to (a2-r-7) are given below.

The “—SO ₂ -containing cyclic group” refers to a cyclic group containing a ring containing —SO ₂ — in the ring skeleton, specifically, the sulfur atom (S) in —SO ₂ — is It is a cyclic group that forms part of the ring skeleton of the cyclic group. The ring containing —SO ₂ — in the ring skeleton is counted as the first ring, and when it is only the ring, it is a monocyclic group, and when it has another ring structure, it is a polycyclic group regardless of the structure. Called. The —SO ₂ — containing cyclic group may be a monocyclic group or a polycyclic group.
-SO ₂ - containing cyclic group, in particular, -O-SO ₂ - within the ring skeleton cyclic group containing, _{i.e., -O-SO 2 - -O-} S- is part of the ring skeleton of the medium It is preferably a cyclic group containing a sultone ring which forms
More specifically, examples of the —SO ₂ -containing cyclic group include groups represented by general formulas (a5-r-1) to (a5-r-4) shown below.

［式中、Ｒａ’^５１は、それぞれ独立に、水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基又はシアノ基である。Ｒ”は水素原子、アルキル基、ラクトン含有環式基、カーボネート含有環式基、又は−ＳＯ_２−含有環式基である。Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子又は硫黄原子である。ｎ’は０〜２の整数である。］

[In the formula, each of Ra ′ ⁵¹ independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group, or cyano. It is a group. R ″ is a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group, or an —SO ₂ -containing cyclic group. A ″ is a carbon atom that may contain an oxygen atom or a sulfur atom. It is an alkylene group of -5, an oxygen atom, or a sulfur atom. n 'is an integer of 0-2. ]

In general formulas (a5-r-1) to (a5-r-2), A ″ represents the general formulas (a2-r-2), (a2-r-3), and (a2-r-5). Same as A ″ in the middle.
As the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in Ra ′ ⁵¹ , the above general formulas (a2-r-1) to ( a2-r-7) as in the same as those exemplified in the description of the Ra ^'21 of the like.
Specific examples of groups represented by general formulas (a5-r-1) to (a5-r-4) are shown below. “Ac” in the formula represents an acetyl group.

The “carbonate-containing cyclic group” refers to a cyclic group containing a ring (carbonate ring) containing —O—C (═O) —O— in the ring skeleton. When the carbonate ring is counted as the first ring, the carbonate ring alone is called a monocyclic group, and when it has another ring structure, it is called a polycyclic group regardless of the structure. The carbonate-containing cyclic group may be a monocyclic group or a polycyclic group.
Any carbonate ring-containing cyclic group can be used without any particular limitation. Specific examples include groups represented by the following general formulas (ax3-r-1) to (ax3-r-3).

［式中、Ｒａ’^ｘ３１は、それぞれ独立に、水素原子、アルキル基、アルコキシ基、ハロゲン原子、ハロゲン化アルキル基、水酸基、−ＣＯＯＲ”、−ＯＣ（＝Ｏ）Ｒ”、ヒドロキシアルキル基又はシアノ基である。Ｒ”は、水素原子、アルキル基、ラクトン含有環式基、カーボネート含有環式基、又は−ＳＯ_２−含有環式基である。Ａ”は酸素原子もしくは硫黄原子を含んでいてもよい炭素数１〜５のアルキレン基、酸素原子又は硫黄原子である。ｐ’は０〜３の整数であり、ｑ’は０又は１である。］

[ ^Wherein , Ra ′ ^x31 each independently represents a hydrogen atom, an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, —COOR ″, —OC (═O) R ″, a hydroxyalkyl group, or cyano. It is a group. R ″ is a hydrogen atom, an alkyl group, a lactone-containing cyclic group, a carbonate-containing cyclic group, or an —SO ₂ -containing cyclic group. A ″ is a carbon number that may contain an oxygen atom or a sulfur atom. It is a 1-5 alkylene group, an oxygen atom, or a sulfur atom. p ′ is an integer of 0 to 3, and q ′ is 0 or 1. ]

In general formulas (ax3-r-2) to (ax3-r-3), A ″ represents the general formulas (a2-r-2), (a2-r-3), and (a2-r-5). Same as A ″ in the middle.
As the alkyl group, alkoxy group, halogen atom, halogenated alkyl group, —COOR ″, —OC (═O) R ″, and hydroxyalkyl group in Ra ′ ³¹ , the above general formulas (a2-r-1) to ( a2-r-7) as in the same as those exemplified in the description of the Ra ^'21 of the like.
Specific examples of groups represented by general formulas (ax3-r-1) to (ax3-r-3) are given below.

As the structural unit (a2), a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent is preferable.
The structural unit (a2) is preferably a structural unit represented by the following general formula (a2-1).

［式中、Ｒは、水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｙａ^２１は、単結合又は２価の連結基である。Ｌａ^２１は−Ｏ−、−ＣＯＯ−、−ＣＯＮ（Ｒ’）−、−ＯＣＯ−、−ＣＯＮＨＣＯ−又は−ＣＯＮＨＣＳ−であり、Ｒ’は水素原子又はメチル基を示す。但し、Ｌａ^２１が−Ｏ−の場合、Ｙａ^２１は−ＣＯ−にはならない。Ｒａ^２１は、ラクトン含有環式基、−ＳＯ_２−含有環式基又はカーボネート含有環式基である。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Ya ²¹ is a single bond or a divalent linking group. La ²¹ represents —O—, —COO—, —CON (R ′) —, —OCO—, —CONHCO— or —CONHCS—, and R ′ represents a hydrogen atom or a methyl group. However, when La ²¹ is —O—, Ya ²¹ is not —CO—. Ra ²¹ is a lactone-containing cyclic group, a —SO ₂ — containing cyclic group, or a carbonate-containing cyclic group. ]

In the formula (a2-1), R is the same as described above.
As R, a hydrogen atom, an alkyl group having 1 to 5 carbon atoms or a fluorinated alkyl group having 1 to 5 carbon atoms is preferable, and a hydrogen atom or a methyl group is particularly preferable from the viewpoint of industrial availability.

In formula (a2-1), the divalent linking group of Ya ²¹ is not particularly limited, but may be a divalent hydrocarbon group which may have a substituent, or a divalent linking group containing a hetero atom. Etc. are mentioned as suitable.

Examples of the divalent hydrocarbon group for Ya ²¹ include the same groups as those described above for the divalent hydrocarbon group for Va ⁰ in formula (a0-1). Examples of the substituent that the divalent hydrocarbon group in Ya ²¹ may have include an alkyl group having 1 to 5 carbon atoms, an alkoxy group, a halogen atom, a halogenated alkyl group having 1 to 5 carbon atoms, and a hydroxyl group. And a carbonyl group.

Preferred examples of the divalent linking group containing a hetero atom in Ya ²¹ include, for example, —O—, —C (═O) —O—, —C (═O) —, —O—C (═O ) —O—, —C (═O) —NH—, —NH—, —NH—C (═NH) — (H may be substituted with a substituent such as an alkyl group or an acyl group), _{-S -, - S (= O} ) 2 -, - S (= O) 2 -O-, the formula ^{-Y 21 -O-Y 22 -,} - Y 21 -O -, - Y 21 -C (= O) —O—, —C (═O) —O—Y ²¹ —, — [Y ²¹ —C (═O) —O] _{m ″} —Y ²² —, —Y ²¹ —O—C (═O) A group represented by —Y ²² — or —Y ²¹ —S (═O) ₂ —O—Y ²² —, wherein Y ²¹ and Y ²² each independently have a substituent; Valent hydrocarbon group, O is an acid It is an atom, m "is an integer of 0 to 3. ] Etc. are mentioned.
The divalent linking group containing a hetero atom is -C (= O) -NH-, -C (= O) -NH-C (= O)-, -NH-, -NH-C (= NH). In the case of-, the H may be substituted with a substituent such as an alkyl group or acyl. The substituent (alkyl group, acyl group, etc.) preferably has 1 to 10 carbon atoms, more preferably 1 to 8 carbon atoms, and particularly preferably 1 to 5 carbon atoms.
Formula ^{-Y 21 -O-Y 22 -,} - Y 21 -O -, - Y 21 -C (= O) -O -, - C (= O) -O-Y 21 -, - [Y 21 - C (═O) —O] _{m ″} —Y ²² —, —Y ²¹ —O—C (═O) —Y ²² — or —Y ²¹ —S (═O) ₂ —O—Y ²² —, wherein Y ²¹ and Y ²² are each independently a divalent hydrocarbon group which may have a substituent, and the divalent hydrocarbon group is exemplified in the description of the divalent linking group. And (the divalent hydrocarbon group which may have a substituent).
Y ²¹ is preferably a linear aliphatic hydrocarbon group, more preferably a linear alkylene group, still more preferably a linear alkylene group having 1 to 5 carbon atoms, and particularly preferably a methylene group or an ethylene group. preferable.
Y ²² is preferably a linear or branched aliphatic hydrocarbon group, and more preferably a methylene group, an ethylene group or an alkylmethylene group. The alkyl group in the alkylmethylene group is preferably a linear alkyl group having 1 to 5 carbon atoms, more preferably a linear alkyl group having 1 to 3 carbon atoms, and most preferably a methyl group.
In the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ″} —Y ²² —, m ″ is an integer of 0 to 3, preferably an integer of 0 to 2, Or 1 is more preferable, and 1 is particularly preferable. That is, the group represented by the formula — [Y ²¹ —C (═O) —O] _{m ″} —Y ²² — is represented by the formula —Y ²¹ —C (═O) —O—Y ²² —. Especially preferred are groups represented by the formula — (CH ₂ ) _{a ′} —C (═O) —O— (CH ₂ ) _{b ′} —, wherein a ′ is 1 to It is an integer of 10, preferably an integer of 1 to 8, more preferably an integer of 1 to 5, more preferably 1 or 2, and most preferably 1. b ′ is an integer of 1 to 10, and 1 to 8 An integer of 1 is preferable, an integer of 1 to 5 is more preferable, 1 or 2 is more preferable, and 1 is most preferable.

Ya ²¹ is preferably a single bond, an ester bond [—C (═O) —O—], an ether bond (—O—), a linear or branched alkylene group, or a combination thereof. .

In the formula (a2-1), La ²¹ is —O—, —COO—, —CON (R ′) —, —OCO—, —CONHCO—, or —CONHCS—.
R ′ represents a hydrogen atom or a methyl group.
However, when La ²¹ is —O—, Ya ²¹ is not —CO—.

In the formula (a2-1), Ra ²¹ is a lactone-containing cyclic group, an —SO ₂ — containing cyclic group, or a carbonate-containing cyclic group.
The lactone-containing cyclic group, -SO ₂ -containing cyclic group, and carbonate-containing cyclic group in Ra ²¹ are respectively represented by the general formulas (a2-r-1) to (a2-r-7) described above. Groups represented by general formulas (a5-r-1) to (a5-r-4) and general formulas (ax3-r-1) to (ax3-r-3), respectively. A group is preferably mentioned.
Among them, Ra ²¹ is preferably a lactone-containing cyclic group or a —SO ₂ — containing cyclic group, and the general formula (a2-r-1), (a2-r-2), (a2-r-6) or The groups represented by (a5-r-1) are more preferable. Specifically, the chemical formulas (r-lc-1-1) to (r-lc-1-7), (r-lc-2-1) to (r-lc-2-18), (r- Any group represented by lc-6-1), (r-sl-1-1), and (r-sl-1-18) is more preferable.

As the structural unit (a2) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
When the component (A1) has the structural unit (a2), the proportion of the structural unit (a2) is 1 to 70 mol% with respect to the total (100 mol%) of all the structural units constituting the component (A1). It is preferable that it is 3-60 mol%, and it is more preferable that it is 5-50 mol%.
When the proportion of the structural unit (a2) is not less than the lower limit value of the preferable range, the effect of containing the structural unit (a2) can be sufficiently obtained, while it is not more than the upper limit value of the preferable range. And other structural units can be balanced, and various lithography characteristics and pattern shapes are improved.

About structural unit (a3):
In addition to the structural unit (a0), the component (A1) may further have a structural unit (a3) containing a polar group-containing aliphatic hydrocarbon group (however, the structural unit (a0) and the structural unit described above) Excluding those corresponding to either the unit (a1) or the structural unit (a2)).
When the component (A1) has the structural unit (a3), the hydrophilicity of the component (A) increases, which contributes to the improvement of resolution.

Examples of the polar group include a hydroxyl group, a cyano group, a carboxy group, and a hydroxyalkyl group in which a part of hydrogen atoms of an alkyl group is substituted with a fluorine atom. A hydroxyl group is particularly preferable.
Examples of the aliphatic hydrocarbon group include a linear or branched hydrocarbon group having 1 to 10 carbon atoms (preferably an alkylene group) and a cyclic aliphatic hydrocarbon group (cyclic group). The cyclic group may be a monocyclic group or a polycyclic group, and can be appropriately selected and used, for example, from many proposed resins for resist compositions for ArF excimer lasers. The cyclic group is preferably a polycyclic group and more preferably 7 to 30 carbon atoms.
Among them, a structural unit derived from an acrylate ester containing an aliphatic polycyclic group containing a hydroxyalkyl group in which a part of hydrogen atoms of a hydroxyl group, a cyano group, a carboxy group, or an alkyl group is substituted with a fluorine atom Is more preferable. Examples of the polycyclic group include groups in which two or more hydrogen atoms have been removed from bicycloalkane, tricycloalkane, tetracycloalkane and the like. Specific examples include groups in which two or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. Among these polycyclic groups, there are groups in which two or more hydrogen atoms have been removed from adamantane, groups in which two or more hydrogen atoms have been removed from norbornane, and groups in which two or more hydrogen atoms have been removed from tetracyclododecane. Industrially preferable.

The structural unit (a3) is not particularly limited as long as it contains a polar group-containing aliphatic hydrocarbon group, and any structural unit can be used.
The structural unit (a3) is a structural unit derived from an acrylate ester in which the hydrogen atom bonded to the α-position carbon atom may be substituted with a substituent, and includes a polar group-containing aliphatic hydrocarbon group. Containing units are preferred.
The structural unit (a3) is derived from a hydroxyethyl ester of acrylic acid when the hydrocarbon group in the polar group-containing aliphatic hydrocarbon group is a linear or branched hydrocarbon group having 1 to 10 carbon atoms. When the hydrocarbon group is a polycyclic group, the structural unit represented by the following formula (a3-1), the structural unit represented by the formula (a3-2), the formula ( The structural unit represented by a3-3) is preferred.

［式中、Ｒは前記と同じであり、ｊは１〜３の整数であり、ｋは１〜３の整数であり、ｔ’は１〜３の整数であり、ｌは１〜５の整数であり、ｓは１〜３の整数である。］

[Wherein, R is as defined above, j is an integer of 1 to 3, k is an integer of 1 to 3, t ′ is an integer of 1 to 3, and l is an integer of 1 to 5] And s is an integer of 1 to 3. ]

In formula (a3-1), j is preferably 1 or 2, and more preferably 1. When j is 2, it is preferable that the hydroxyl group is bonded to the 3rd and 5th positions of the adamantyl group. When j is 1, it is preferable that the hydroxyl group is bonded to the 3-position of the adamantyl group.
j is preferably 1, and a hydroxyl group bonded to the 3-position of the adamantyl group is particularly preferred.

  In formula (a3-2), k is preferably 1. The cyano group is preferably bonded to the 5th or 6th position of the norbornyl group.

  In formula (a3-3), t ′ is preferably 1. l is preferably 1. s is preferably 1. In these, a 2-norbornyl group or a 3-norbornyl group is preferably bonded to the terminal of the carboxy group of acrylic acid. The fluorinated alkyl alcohol is preferably bonded to the 5th or 6th position of the norbornyl group.

As the structural unit (a3) contained in the component (A1), 1 type of structural unit may be used, or 2 or more types may be used.
When the component (A1) has the structural unit (a3), the proportion of the structural unit (a3) is preferably 1 to 50 mol% with respect to the total of all the structural units constituting the component (A1). It is more preferably 1 to 40 mol%, further preferably 3 to 30 mol%, and particularly preferably 10 to 20 mol%.
By setting the proportion of the structural unit (a3) to a preferable lower limit value or more, the resolution is further improved in resist pattern formation. On the other hand, by setting it to a preferable upper limit value or less, it becomes easy to balance with other structural units.

Regarding structural unit (a4):
In addition to the structural unit (a0), the component (A1) may further have a structural unit (a4) containing an acid non-dissociable aliphatic cyclic group.
When the component (A1) has the structural unit (a4), the dry etching resistance of the formed resist pattern is improved. Moreover, the hydrophobicity of (A) component increases. The improvement in hydrophobicity contributes to improvement in resolution, resist pattern shape, etc., particularly in the case of a solvent development process.
The “acid non-dissociable cyclic group” in the structural unit (a4) is generated when an acid is generated in the resist composition by exposure (for example, an acid is generated from the structural unit or the component (B) that generates acid by exposure). The cyclic group remains in the structural unit as it is without dissociating even when the acid acts.
As the structural unit (a4), for example, a structural unit derived from an acrylate ester containing a non-acid-dissociable aliphatic cyclic group is preferable. As the cyclic group, many conventionally known groups can be used as resin components of resist compositions such as for ArF excimer laser and for KrF excimer laser (preferably for ArF excimer laser). .
In particular, at least one selected from a tricyclodecyl group, an adamantyl group, a tetracyclododecyl group, an isobornyl group, and a norbornyl group is preferable in terms of industrial availability. These polycyclic groups may have a linear or branched alkyl group having 1 to 5 carbon atoms as a substituent.
Specific examples of the structural unit (a4) include structural units represented by general formulas (a4-1) to (a4-7) shown below.

［式中、Ｒ^αは前記と同じである。］

[Wherein, R ^α is the same as defined above. ]

The structural unit (a4) contained in the component (A1) may be one type or two or more types.
When the component (A1) has the structural unit (a4), the proportion of the structural unit (a4) is preferably 1 to 40 mol% with respect to the total of all the structural units constituting the component (A1). More preferably, it is 5-20 mol%.
By setting the proportion of the structural unit (a4) to a preferable lower limit value or more, the effect of containing the structural unit (a4) can be sufficiently obtained. It becomes easy to balance with.

In the resist composition of this embodiment, the component (A) includes the polymer compound (A1) having the structural unit (a0).
Examples of the component (A1) include a polymer compound having the structural unit (a0) and the structural unit (a2), and a polymer having the structural unit (a0), the structural unit (a2), and the structural unit (a3). Compounds.
Specifically, the (A1) component is preferably a copolymer having a repeating structure of the structural unit (a0), the structural unit (a2), and the structural unit (a3).

The weight average molecular weight (Mw) of the component (A1) (polystyrene conversion standard by gel permeation chromatography (GPC)) is not particularly limited, and is preferably about 1000 to 500000, more preferably 2000 to 100000, and 3000. -50,000 is more preferable.
When the Mw of the component (A1) is less than or equal to the upper limit value of the above preferred range, there is sufficient solubility in a resist solvent to be used as a resist, Dry etching resistance and resist pattern cross-sectional shape become better.
The molecular weight dispersity (Mw / Mn) of the component (A1) is not particularly limited, and is preferably about 1.0 to 4.0, more preferably 1.0 to 3.0, and 1.5 to 2.5. Particularly preferred. In addition, Mn shows a number average molecular weight.

As the component (A1), one type may be used alone, or two or more types may be used in combination.
The proportion of the component (A1) in the component (A) is preferably 25% by mass or more, more preferably 50% by mass or more, further preferably 75% by mass or more, and 100% by mass with respect to the total mass of the component (A) It may be.
When the proportion of the component (A1) is not less than the lower limit of the above preferable range, a resist pattern excellent in various lithography properties such as high sensitivity and roughness improvement is easily formed.

-About (A2) component The resist composition of this embodiment does not correspond to the said (A1) component as a (A) component, but is a base-material component (henceforth "(A2) which changes the solubility with respect to a developing solution by the effect | action of an acid. ) Component ”)) may be used in combination.
The component (A2) is not particularly limited, and may be arbitrarily selected from a number of conventionally known substrate components for chemically amplified resist compositions.
As the component (A2), one type may be used alone, or two or more types may be used in combination.

In the resist composition of this embodiment, as the component (A), one type may be used alone, or two or more types may be used in combination.
In the resist composition of this embodiment, the content of the component (A) may be adjusted according to the resist film thickness to be formed.

<Other ingredients>
The resist composition of this embodiment may further contain other components in addition to the component (A) described above, in addition to the component (A). Examples of other components include the following components (B), (D), (E), (F), and (S).

≪Acid generator component (B) ≫
The resist composition of the present embodiment may further contain an acid generator component (hereinafter referred to as “component (B)”) in addition to the component (A).
The component (B) is not particularly limited, and those that have been proposed as acid generators for chemically amplified resists can be used.
Examples of such acid generators include onium salt acid generators such as iodonium salts and sulfonium salts, oxime sulfonate acid generators; diazomethanes such as bisalkyl or bisarylsulfonyldiazomethanes and poly (bissulfonyl) diazomethanes Acid generators: various types such as nitrobenzyl sulfonate acid generators, imino sulfonate acid generators, disulfone acid generators, and the like. Of these, it is preferable to use an onium salt acid generator.

  Examples of the onium salt-based acid generator include a compound represented by the following general formula (b-1) (hereinafter also referred to as “(b-1) component”) and a general formula (b-2). A compound (hereinafter also referred to as “(b-2) component”) or a compound represented by the general formula (b-3) (hereinafter also referred to as “(b-3) component”) can be used.

［式中、Ｒ^１０１、Ｒ^１０４〜Ｒ^１０８はそれぞれ独立に置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、又は置換基を有していてもよい鎖状のアルケニル基である。Ｒ^１０４、Ｒ^１０５は、相互に結合して環を形成していてもよい。Ｒ^１０２はフッ素原子又は炭素数１〜５のフッ素化アルキル基である。Ｙ^１０１は単結合又は酸素原子を含む２価の連結基である。Ｖ^１０１〜Ｖ^１０３はそれぞれ独立に単結合、アルキレン基又はフッ素化アルキレン基である。Ｌ^１０１〜Ｌ^１０２はそれぞれ独立に単結合又は酸素原子である。Ｌ^１０３〜Ｌ^１０５はそれぞれ独立に単結合、−ＣＯ−又は−ＳＯ_２−である。ｍは１以上の整数であって、Ｍ’^ｍ＋はｍ価のオニウムカチオンである。］

[Wherein, R ¹⁰¹ and R ^{104 to} R ¹⁰⁸ each independently have a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. A chain alkenyl group which may be present. R ¹⁰⁴ and R ¹⁰⁵ may be bonded to each other to form a ring. R ¹⁰² represents a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. Y ¹⁰¹ is a single bond or a divalent linking group containing an oxygen atom. V ^{101 to} V ¹⁰³ are each independently a single bond, an alkylene group or a fluorinated alkylene group. L ^{101 to} L ¹⁰² are each independently a single bond or an oxygen atom. L ^{103 to} L ¹⁰⁵ are each independently a single bond, —CO— or —SO ₂ —. m is an integer of 1 or more, and M ′ ^{m +} is an m-valent onium cation. ]

{Anion part}
-Anion moiety of component (b-1) In formula (b-1), R ¹⁰¹ represents a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, Or it is the chain-like alkenyl group which may have a substituent.

Cyclic group which may have a substituent:
The cyclic group is preferably a cyclic hydrocarbon group, and the cyclic hydrocarbon group may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group. An aliphatic hydrocarbon group means a hydrocarbon group having no aromaticity. The aliphatic hydrocarbon group may be saturated or unsaturated, and is usually preferably saturated.

The aromatic hydrocarbon group for R ¹⁰¹ is a hydrocarbon group having an aromatic ring. The aromatic hydrocarbon group preferably has 3 to 30 carbon atoms, more preferably 5 to 30 carbon atoms, further preferably 5 to 20 carbon atoms, particularly preferably 6 to 15 carbon atoms, and most preferably 6 to 10 carbon atoms. However, the carbon number does not include the carbon number in the substituent.
Specific examples of the aromatic ring of the aromatic hydrocarbon group in R ¹⁰¹ include benzene, fluorene, naphthalene, anthracene, phenanthrene, biphenyl, or a part of carbon atoms constituting these aromatic rings substituted with a heteroatom. An aromatic heterocyclic ring is mentioned. Examples of the hetero atom in the aromatic heterocyclic ring include an oxygen atom, a sulfur atom, and a nitrogen atom.
Specifically, the aromatic hydrocarbon group in R ¹⁰¹ is a group obtained by removing one hydrogen atom from the aromatic ring (aryl group: for example, phenyl group, naphthyl group, etc.), and one of the hydrogen atoms of the aromatic ring is alkylene. And a group substituted with a group (for example, arylalkyl groups such as benzyl group, phenethyl group, 1-naphthylmethyl group, 2-naphthylmethyl group, 1-naphthylethyl group, 2-naphthylethyl group, etc.). The alkylene group (alkyl chain in the arylalkyl group) preferably has 1 to 4 carbon atoms, more preferably 1 to 2 carbon atoms, and particularly preferably 1 carbon atom.

Examples of the cyclic aliphatic hydrocarbon group for R ¹⁰¹ include an aliphatic hydrocarbon group containing a ring in the structure.
As the aliphatic hydrocarbon group containing a ring in this structure, an alicyclic hydrocarbon group (a group obtained by removing one hydrogen atom from an aliphatic hydrocarbon ring), an alicyclic hydrocarbon group is linear or branched Examples thereof include a group bonded to the end of a chain aliphatic hydrocarbon group and a group in which an alicyclic hydrocarbon group is interposed in the middle of a linear or branched aliphatic hydrocarbon group.
The alicyclic hydrocarbon group preferably has 3 to 20 carbon atoms, and more preferably 3 to 12 carbon atoms.
The alicyclic hydrocarbon group may be a polycyclic group or a monocyclic group. As the monocyclic alicyclic hydrocarbon group, a group in which one or more hydrogen atoms have been removed from a monocycloalkane is preferable. The monocycloalkane preferably has 3 to 6 carbon atoms, and specific examples include cyclopentane and cyclohexane. The polycyclic alicyclic hydrocarbon group is preferably a group obtained by removing one or more hydrogen atoms from a polycycloalkane, and the polycycloalkane preferably has 7 to 30 carbon atoms. Among these, the polycycloalkane includes polycycloalkanes having a polycyclic skeleton of a bridged ring system such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane; condensed ring systems such as a cyclic group having a steroid skeleton A polycycloalkane having a polycyclic skeleton is more preferable.

Among these, the cyclic aliphatic hydrocarbon group for R ¹⁰¹ is preferably a group obtained by removing one or more hydrogen atoms from a monocycloalkane or polycycloalkane, and more preferably a group obtained by removing one hydrogen atom from a polycycloalkane. An adamantyl group and a norbornyl group are particularly preferable, and an adamantyl group is most preferable.

The linear or branched aliphatic hydrocarbon group that may be bonded to the alicyclic hydrocarbon group preferably has 1 to 10 carbon atoms, more preferably 1 to 6 carbon atoms, and 1 to 4 carbon atoms. Is more preferable, and 1-3 are most preferable.
As the linear aliphatic hydrocarbon group, a linear alkylene group is preferable. Specifically, a methylene group [—CH ₂ —], an ethylene group [— (CH ₂ ) ₂ —], a trimethylene group [ — (CH ₂ ) ₃ —], tetramethylene group [— (CH ₂ ) ₄ —], pentamethylene group [— (CH ₂ ) ₅ —] and the like can be mentioned.
As the branched aliphatic hydrocarbon group, a branched alkylene group is preferred, and specifically, —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as - _{CH (CH 3) CH 2 -} , - CH (CH 3) CH (CH 3) -, - C (CH 3) 2 CH 2 -, - CH (CH 2 CH 3) CH 2 -, - C (CH 2 CH _{3) 2} -CH ₂ - alkyl groups such _{as; -CH (CH 3) CH 2} CH 2 -, - CH 2 CH (CH 3) CH 2 - alkyl trimethylene groups such as; -CH _(CH 3) _{CH 2 CH 2 CH 2 -,} - CH 2 CH (CH 3) CH 2 CH 2 - And the like alkyl alkylene group such as an alkyl tetramethylene group of. The alkyl group in the alkyl alkylene group is preferably a linear alkyl group having 1 to 5 carbon atoms.

In addition, the cyclic hydrocarbon group for R ¹⁰¹ may contain a hetero atom such as a heterocyclic ring. Specifically, the lactone-containing cyclic groups represented by the general formulas (a2-r-1) to (a2-r-7), and the general formulas (a5-r-1) to (a5-r- -SO ₂ respectively represented by 4) - containing cyclic group, other above formula (r-hr-1) include heterocyclic groups respectively represented by ~ (r-hr-16) .

Examples of the substituent in the cyclic group of R ¹⁰¹ include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, and a nitro group.
The alkyl group as a substituent is preferably an alkyl group having 1 to 5 carbon atoms, and most preferably a methyl group, an ethyl group, a propyl group, an n-butyl group, or a tert-butyl group.
The alkoxy group as a substituent is preferably an alkoxy group having 1 to 5 carbon atoms, more preferably a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, or a tert-butoxy group. Most preferred is an ethoxy group.
Examples of the halogen atom as a substituent include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
As the halogenated alkyl group as a substituent, a part or all of hydrogen atoms such as an alkyl group having 1 to 5 carbon atoms, for example, methyl group, ethyl group, propyl group, n-butyl group, tert-butyl group, and the like And a group substituted with a halogen atom.
The carbonyl group as a substituent is a group that substitutes a methylene group (—CH ₂ —) constituting a cyclic hydrocarbon group.

A chain-like alkyl group which may have a substituent:
The chain alkyl group for R ¹⁰¹ may be either linear or branched.
The linear alkyl group preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms, and most preferably 1 to 10 carbon atoms. Specifically, for example, methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, nonyl group, decanyl group, undecyl group, dodecyl group, tridecyl group, isotridecyl group, tetradecyl group Group, pentadecyl group, hexadecyl group, isohexadecyl group, heptadecyl group, octadecyl group, nonadecyl group, icosyl group, henocosyl group, docosyl group and the like.
The branched alkyl group preferably has 3 to 20 carbon atoms, more preferably 3 to 15 carbon atoms, and most preferably 3 to 10 carbon atoms. Specifically, for example, 1-methylethyl group, 1-methylpropyl group, 2-methylpropyl group, 1-methylbutyl group, 2-methylbutyl group, 3-methylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, Examples include 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group and the like.

A chain-like alkenyl group which may have a substituent:
The chain alkenyl group for R ¹⁰¹ may be either linear or branched, preferably has 2 to 10 carbon atoms, more preferably 2 to 5, still more preferably 2 to 4, more preferably 3 Is particularly preferred. Examples of the linear alkenyl group include a vinyl group, a propenyl group (allyl group), and a butynyl group. Examples of the branched alkenyl group include 1-methylvinyl group, 2-methylvinyl group, 1-methylpropenyl group, 2-methylpropenyl group and the like.
Among the above, the chain alkenyl group is preferably a linear alkenyl group, more preferably a vinyl group or propenyl group, and particularly preferably a vinyl group.

Examples of the substituent in the chain alkyl group or alkenyl group of R ¹⁰¹ include an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, a carbonyl group, a nitro group, an amino group, and the cyclic group in R ¹⁰¹ described above. Can be mentioned.

Among these, R ¹⁰¹ is preferably a cyclic group which may have a substituent, and more preferably a cyclic hydrocarbon group which may have a substituent. More specifically, a group obtained by removing one or more hydrogen atoms from a phenyl group, a naphthyl group, or a polycycloalkane; each represented by the general formulas (a2-r-1) to (a2-r-7) Lactone-containing cyclic groups; —SO ₂ -containing cyclic groups represented by general formulas (a5-r-1) to (a5-r-4), respectively, are preferable.

In formula (b-1), Y ¹⁰¹ represents a single bond or a divalent linking group containing an oxygen atom.
When Y ¹⁰¹ is a divalent linking group containing an oxygen atom, Y ¹⁰¹ may contain an atom other than an oxygen atom. Examples of atoms other than oxygen atoms include carbon atoms, hydrogen atoms, sulfur atoms, and nitrogen atoms.
Examples of the divalent linking group containing an oxygen atom include an oxygen atom (ether bond: —O—), an ester bond (—C (═O) —O—), and an oxycarbonyl group (—O—C (═O). )-), Amide bond (—C (═O) —NH—), carbonyl group (—C (═O) —), carbonate bond (—O—C (═O) —O—), etc. A combination of a non-hydrocarbon oxygen atom-containing linking group and an alkylene group; and the like. A sulfonyl group (—SO ₂ —) may be further linked to this combination. Examples of the divalent linking group containing an oxygen atom include linking groups represented by the following general formulas (y-al-1) to (y-al-7), respectively.

［式中、Ｖ’^１０１は単結合または炭素数１〜５のアルキレン基であり、Ｖ’^１０２は炭素数１〜３０の２価の飽和炭化水素基である。］

[Wherein, V ′ ¹⁰¹ is a single bond or an alkylene group having 1 to 5 carbon atoms, and V ′ ¹⁰² is a divalent saturated hydrocarbon group having 1 to 30 carbon atoms. ]

The divalent saturated hydrocarbon group for V ′ ¹⁰² is preferably an alkylene group having 1 to 30 carbon atoms, more preferably an alkylene group having 1 to 10 carbon atoms, and an alkylene group having 1 to 5 carbon atoms. More preferably.

The alkylene group for V ′ ¹⁰¹ and V ′ ¹⁰² may be a linear alkylene group or a branched alkylene group, and a linear alkylene group is preferred.
Specific examples of the alkylene group in V ′ ¹⁰¹ and V ′ ¹⁰² include a methylene group [—CH ₂ —]; —CH (CH ₃ ) —, —CH (CH ₂ CH ₃ ) —, —C (CH ₃ ). _{2 -, - C (CH 3} ) (CH 2 CH 3) -, - C (CH 3) (CH 2 CH 2 CH 3) -, - C (CH 2 CH 3) 2 - ; alkylethylene groups such as ethylene Groups [—CH ₂ CH ₂ —]; —CH (CH ₃ ) CH ₂ —, —CH (CH ₃ ) CH (CH ₃ ) —, —C (CH ₃ ) ₂ CH ₂ —, —CH (CH ₂ CH - ₃₎ CH ₂ alkyl groups such as, trimethylene group (n- propylene _{group) [- CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 -, - CH 2 CH (CH 3) CH ₂ - and the like alkyl trimethylene group; tetramethylene _{[-CH 2 CH 2 CH 2 CH} 2 -]; - CH (CH 3) CH 2 CH 2 CH 2 -, - CH 2 CH (CH 3) CH 2 CH 2 - alkyl tetramethylene group and the like; pentamethylene group _{[-CH 2 CH 2 CH 2 CH} 2 CH 2 -] , and the like.
Moreover, some methylene groups in the alkylene group in V ′ ¹⁰¹ or V ′ ¹⁰² may be substituted with a C 5-10 divalent aliphatic cyclic group. The aliphatic cyclic group is a cyclic aliphatic hydrocarbon group represented by R ¹⁰¹ in the formula (b-1) (monocyclic alicyclic hydrocarbon group, polycyclic alicyclic hydrocarbon group). A divalent group in which one hydrogen atom is further removed is preferable, and a cyclohexylene group, a 1,5-adamantylene group, or a 2,6-adamantylene group is more preferable.

Y ¹⁰¹ is preferably a divalent linking group containing an ester bond or a divalent linking group containing an ether bond, each represented by the above formulas (y-al-1) to (y-al-5). A linking group is more preferred.

In formula (b-1), V ¹⁰¹ represents a single bond, an alkylene group or a fluorinated alkylene group. The alkylene group and fluorinated alkylene group for V ¹⁰¹ preferably have 1 to 4 carbon atoms. ^Examples of the fluorinated alkylene group for V ¹⁰¹ include groups in which some or all of the hydrogen atoms of the alkylene group for V ¹⁰¹ have been substituted with fluorine atoms. Among ^{them, V 101} is preferably a single bond, or a fluorinated alkylene group having 1 to 4 carbon atoms.

In formula (b-1), R ¹⁰² represents a fluorine atom or a fluorinated alkyl group having 1 to 5 carbon atoms. R ¹⁰² is preferably a fluorine atom or a C 1-5 perfluoroalkyl group, and more preferably a fluorine atom.

(B-1) Specific examples of the anion moiety of the component, for example, if the Y ¹⁰¹ is a single bond, fluorinated alkyl sulfonate anions such as trifluoromethane sulfonate anion or perfluorobutane sulfonate anion can be exemplified; Y ¹⁰¹ is In the case of a divalent linking group containing an oxygen atom, anions represented by any one of the following formulas (an-1) to (an-3) can be mentioned.

［式中、Ｒ”^１０１は、置換基を有していてもよい脂肪族環式基、前記式（ｒ−ｈｒ−１）〜（ｒ−ｈｒ−６）でそれぞれ表される基、又は置換基を有していてもよい鎖状のアルキル基であり；Ｒ”^１０２は、置換基を有していてもよい脂肪族環式基、前記一般式（ａ２−ｒ−１）〜（ａ２−ｒ−７）でそれぞれ表されるラクトン含有環式基、又は前記一般式（ａ５−ｒ−１）〜（ａ５−ｒ−４）でそれぞれ表される−ＳＯ_２−含有環式基であり；Ｒ”^１０３は、置換基を有していてもよい芳香族環式基、置換基を有していてもよい脂肪族環式基、又は置換基を有していてもよい鎖状のアルケニル基であり；ｖ”はそれぞれ独立に０〜３の整数であり、ｑ”はそれぞれ独立に１〜２０の整数であり、ｔ”は１〜３の整数であり、ｎ”は０または１である。］

[Wherein R ″ ¹⁰¹ represents an aliphatic cyclic group which may have a substituent, a group represented by each of the above formulas (r-hr-1) to (r-hr-6), or a substituent. A chain-like alkyl group which may have a group; R ″ ¹⁰² represents an aliphatic cyclic group which may have a substituent, the above-mentioned general formulas (a2-r-1) to (a2- a lactone-containing cyclic group represented by each of r-7), or a —SO ₂ -containing cyclic group represented by each of the general formulas (a5-r-1) to (a5-r-4); R ″ ¹⁰³ is an aromatic cyclic group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a chain alkenyl group which may have a substituent. V ″ is independently an integer from 0 to 3, q ″ is independently an integer from 1 to 20, t ″ is an integer from 1 to 3, and n ″ is 0. The other is 1.]

The aliphatic cyclic group which may have a substituent of R ″ ¹⁰¹ , R ″ ¹⁰² and R ″ ¹⁰³ is preferably a group exemplified as the cyclic aliphatic hydrocarbon group in R ¹⁰¹ . Examples of the substituent include the same substituents that may be substituted for the cyclic aliphatic hydrocarbon group in R ¹⁰¹ .

The aromatic cyclic group which may have a substituent in R ″ ¹⁰³ is preferably the group exemplified as the aromatic hydrocarbon group in the cyclic hydrocarbon group in R ¹⁰¹ . , R ¹⁰¹ and the same substituents that may be substituted for the aromatic hydrocarbon group.

The chain alkyl group which may have a substituent in R ″ ¹⁰¹ is preferably the group exemplified as the chain alkyl group in R ^101. The chain in R ″ ¹⁰³ has a substituent. The good chain alkenyl group is preferably the group exemplified as the chain alkenyl group in R ¹⁰¹ .

-Anion part of component (b-2) In formula (b-2), R ¹⁰⁴ and R ¹⁰⁵ may each independently have a cyclic group which may have a substituent or a substituent. Examples thereof include a good chain alkyl group or a chain alkenyl group which may have a substituent, and examples thereof include the same as those described above for R ¹⁰¹ in formula (b-1). However, R ¹⁰⁴ and R ¹⁰⁵ may be bonded to each other to form a ring.
R ¹⁰⁴ and R ¹⁰⁵ are preferably a chain alkyl group which may have a substituent, and are a linear or branched alkyl group, or a linear or branched fluorinated alkyl group. It is more preferable.
The chain alkyl group preferably has 1 to 10 carbon atoms, more preferably 1 to 7 carbon atoms, and still more preferably 1 to 3 carbon atoms. The number of carbon atoms of the chain alkyl group of R ¹⁰⁴ and R ¹⁰⁵ is preferably as small as possible because the solubility in a resist solvent is good within the range of the carbon number. In addition, in the chain alkyl group of R ¹⁰⁴ and R ^105, the greater the number of hydrogen atoms substituted with fluorine atoms, the stronger the acid strength, and against high-energy light and electron beams of 200 nm or less Since transparency improves, it is preferable. The proportion of fluorine atoms in the chain alkyl group, that is, the fluorination rate is preferably 70 to 100%, more preferably 90 to 100%, and most preferably all hydrogen atoms are substituted with fluorine atoms. Perfluoroalkyl group.
In formula (b-2), V ¹⁰² and V ¹⁰³ are each independently a single bond, an alkylene group, or a fluorinated alkylene group, and each of them is the same as V ¹⁰¹ in formula (b-1). Can be mentioned.
In formula (b-2), L ¹⁰¹ and L ¹⁰² each independently represent a single bond or an oxygen atom.

-Anion part of (b-3) component In formula (b-3), R < ¹⁰⁶ > -R < ¹⁰⁸ > may have the cyclic group which may have a substituent, and a substituent each independently. Examples thereof include a good chain alkyl group or a chain alkenyl group which may have a substituent, and examples thereof include those similar to R ¹⁰¹ in formula (b-1).
L ^{103 to} L ¹⁰⁵ are each independently a single bond, —CO— or —SO ₂ —.

{Cation part}
In the formulas (b-1), (b-2), and (b-3), m is an integer of 1 or more, M ′ ^{m +} is an m-valent onium cation, and a sulfonium cation and an iodonium cation are preferable. And organic cations represented by the following general formulas (ca-1) to (ca-5) are particularly preferable.

［式中、Ｒ^２０１〜Ｒ^２０７、およびＲ^２１１〜Ｒ^２１２は、それぞれ独立に置換基を有していてもよいアリール基、アルキル基またはアルケニル基を表し、Ｒ^２０１〜Ｒ^２０３、Ｒ^２０６〜Ｒ^２０７、Ｒ^２１１〜Ｒ^２１２は、相互に結合して式中のイオウ原子と共に環を形成してもよい。Ｒ^２０８〜Ｒ^２０９はそれぞれ独立に水素原子または炭素数１〜５のアルキル基を表し、Ｒ^２１０は置換基を有していてもよいアリール基、置換基を有していてもよいアルキル基、置換基を有していてもよいアルケニル基、又は置換基を有していてもよい−ＳＯ_２−含有環式基であり、Ｌ^２０１は−Ｃ（＝Ｏ）−または−Ｃ（＝Ｏ）−Ｏ−を表し、Ｙ^２０１は、それぞれ独立に、アリーレン基、アルキレン基またはアルケニレン基を表し、ｘは１または２であり、Ｗ^２０１は（ｘ＋１）価の連結基を表す。］

[Wherein, R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² each independently represents an aryl group, an alkyl group or an alkenyl group which may have a substituent, and R ^{201 to} R ²⁰³ , R ²⁰⁶ to R ²⁰⁷ and R ^{211 to} R ²¹² may be bonded to each other to form a ring together with the sulfur atom in the formula. R ^{208 to} R ²⁰⁹ each independently represent a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, R ²¹⁰ is an aryl group which may have a substituent, an alkyl group which may have a substituent, An alkenyl group which may have a substituent, or an —SO ₂ — containing cyclic group which may have a substituent, and L ²⁰¹ represents —C (═O) — or —C (═O). -O- represents that Y ²⁰¹ independently represents an arylene group, an alkylene group or an alkenylene group, x is 1 or 2, and W ²⁰¹ represents a (x + 1) -valent linking group. ]

Examples of the aryl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² include an unsubstituted aryl group having 6 to 20 carbon atoms, and a phenyl group and a naphthyl group are preferable.
The alkyl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² is a chain or cyclic alkyl group and preferably has 1 to 30 carbon atoms.
The alkenyl group in R ^{201 to} R ²⁰⁷ and R ^{211 to} R ²¹² preferably has 2 to 10 carbon atoms.
Examples of the substituent that R ^{201 to} R ²⁰⁷ and R ^{210 to} R ²¹² may have include an alkyl group, a halogen atom, a halogenated alkyl group, a carbonyl group, a cyano group, an amino group, an aryl group, And groups represented by formulas (ca-r-1) to (ca-r-7), respectively.

［式中、Ｒ’^２０１はそれぞれ独立に、水素原子、置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、又は置換基を有していてもよい鎖状のアルケニル基である。］

[Wherein, each R ′ ²⁰¹ independently has a hydrogen atom, a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. It may be a chain alkenyl group. ]

The cyclic group which may have a substituent of R ′ ^201, the chain alkyl group which may have a substituent, or the chain alkenyl group which may have a substituent are the same as those described above. In addition to those similar to R ^{101 in} the formula (b-1), a cyclic group which may have a substituent or a chain alkyl group which may have a substituent may be The same thing as the acid dissociable group represented by the formula (a1-r-2) is also mentioned.

^{R 201 ~R 203, R 206 ~R} 207, R 211 ~R 212 , when bonded to each other to form a ring with the sulfur atom, a sulfur atom, an oxygen atom, or a hetero atom such as nitrogen atom, carbonyl _{group, -SO -, - SO 2 -} , - SO 3 -, - COO -, - CONH- , or -N _(R N) - (. the _{R N} is an alkyl group having 1 to 5 carbon atoms), etc. You may couple | bond through the functional group of. As the ring to be formed, one ring containing a sulfur atom in the ring skeleton in the formula is preferably a 3- to 10-membered ring, particularly a 5- to 7-membered ring, including the sulfur atom. preferable. Specific examples of the ring formed include, for example, thiophene ring, thiazole ring, benzothiophene ring, thianthrene ring, benzothiophene ring, dibenzothiophene ring, 9H-thioxanthene ring, thioxanthone ring, thianthrene ring, phenoxathiin ring, tetrahydro A thiophenium ring, a tetrahydrothiopyranium ring, etc. are mentioned.

R ^{208 to} R ²⁰⁹ each independently represent a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, and a hydrogen atom or an alkyl group having 1 to 3 carbon atoms is preferable. A ring may be formed.

R ²¹⁰ may have an aryl group which may have a substituent, an alkyl group which may have a substituent, an alkenyl group which may have a substituent, or a substituent. -SO ₂ - containing cyclic group.
The aryl group in R ^210, include unsubstituted aryl group having 6 to 20 carbon atoms, a phenyl group, a naphthyl group.
The alkyl group for R ²¹⁰ is preferably a chain or cyclic alkyl group having 1 to 30 carbon atoms.
The alkenyl group for R ²¹⁰ preferably has 2 to 10 carbon atoms.
^Examples of the —SO ₂ — containing cyclic group which may have a substituent in R ²¹⁰ include the above-mentioned “—SO ₂ — containing polycyclic group” or “—SO ₂ — containing monocyclic group”. like can be mentioned, among the _- preferably "-SO 2 containing polycyclic group", the group represented by the general formula (a5-r-1) is more preferable.

In the formulas (ca-4) and (ca-5), Y ²⁰¹ each independently represents an arylene group, an alkylene group, or an alkenylene group.
Examples of the arylene group for Y ²⁰¹ include a group in which one hydrogen atom has been removed from the aryl group exemplified as the aromatic hydrocarbon group for R ¹⁰¹ in the aforementioned formula (b-1).
Examples of the alkylene group and alkenylene group in Y ²⁰¹ include a group in which one hydrogen atom has been removed from the groups exemplified as the chain alkyl group and chain alkenyl group in R ¹⁰¹ in the aforementioned formula (b-1). .

In the above formula (ca-4) and formula (ca-5), x is 1 or 2.
W ²⁰¹ is a (x + 1) valent, that is, a divalent or trivalent linking group.
The divalent linking group in W ²⁰¹ is preferably a divalent hydrocarbon group which may have a substituent, and has the same substituent as Ya ^{21 in} the general formula (a2-1). And a divalent hydrocarbon group which may be used. The divalent linking group in W ²⁰¹ may be linear, branched or cyclic, and is preferably cyclic. Of these, a group in which two carbonyl groups are combined at both ends of the arylene group is preferable. Examples of the arylene group include a phenylene group and a naphthylene group, and a phenylene group is particularly preferable.
^Examples of the trivalent linking group in W ²⁰¹ include a group obtained by removing one hydrogen atom from the divalent linking group in W ²⁰¹ , a group in which the divalent linking group is further bonded to the divalent linking group, and the like. Can be mentioned. The trivalent linking group in W ²⁰¹ is preferably a group in which two carbonyl groups are bonded to an arylene group.

  Specific examples of suitable cations represented by the formula (ca-1) include cations represented by the following formulas (ca-1-1) to (ca-1-67).

［式中、ｇ１、ｇ２、ｇ３は繰返し数を示し、ｇ１は１〜５の整数であり、ｇ２は０〜２０の整数であり、ｇ３は０〜２０の整数である。］

[Wherein, g1, g2, and g3 represent the number of repetitions, g1 is an integer of 1 to 5, g2 is an integer of 0 to 20, and g3 is an integer of 0 to 20. ]

［式中、Ｒ”^２０１は水素原子又は置換基であって、該置換基としては前記Ｒ^２０１〜Ｒ^２０７、およびＲ^２１０〜Ｒ^２１２が有していてもよい置換基として挙げたものと同様である。］

[Wherein, R ″ ²⁰¹ is a hydrogen atom or a substituent, and the substituent is the same as those exemplified as the substituent that R ^{201 to} R ²⁰⁷ and R ^{210 to} R ²¹² may have. Is.]

  Specific examples of suitable cations represented by the formula (ca-2) include diphenyliodonium cation and bis (4-tert-butylphenyl) iodonium cation.

  Specific examples of suitable cations represented by the formula (ca-3) include cations represented by the following formulas (ca-3-1) to (ca-3-6).

  Specific examples of suitable cations represented by the formula (ca-4) include cations represented by the following formulas (ca-4-1) to (ca-4-2).

  Moreover, as a cation represented by the said formula (ca-5), the cation represented by each of the following general formula (ca-5-1)-(ca-5-3) is also preferable.

Among the above, the cation part [(M ′ ^{m +} ) _{1 / m} ] is preferably a cation represented by the general formula (ca-1), represented by the formulas (ca-1-1) to (ca-1-67). Cations represented respectively are more preferred.

As the component (B), one type of acid generator described above may be used alone, or two or more types may be used in combination.
When a resist composition contains (B) component, 0.5-60 mass parts is preferable with respect to 100 mass parts of (A) component, and, as for content of (B) component, 1-50 mass parts is more preferable. 1 to 40 parts by mass is more preferable.
By forming the content of the component (B) within the above range, pattern formation is sufficiently performed. Moreover, when each component of a resist composition is melt | dissolved in the organic solvent, since a uniform solution is easy to be obtained and the storage stability as a resist composition becomes favorable, it is preferable.

≪Acid diffusion controller component (D) ≫
In addition to the component (A) or in addition to the component (A) and the component (B), the resist composition of this embodiment further includes an acid diffusion controller component (hereinafter referred to as “component (D)”). It may contain. The component (D) acts as a quencher (acid diffusion controller) that traps acid generated by exposure in the resist composition.
The component (D) may be a photodegradable base (D1) (hereinafter referred to as “component (D1)”) that is decomposed by exposure and loses acid diffusion controllability. It may be a nitrogen organic compound (D2) (hereinafter referred to as “component (D2)”).

-About (D1) component By forming it as a resist composition containing (D1) component, when forming a resist pattern, the contrast of an exposed part and an unexposed part can be improved.
The component (D1) is not particularly limited as long as it is decomposed by exposure and loses acid diffusion controllability, and is a compound represented by the following general formula (d1-1) (hereinafter referred to as “(d1-1) component”). ), A compound represented by the following general formula (d1-2) (hereinafter referred to as “(d1-2) component”) and a compound represented by the following general formula (d1-3) (hereinafter referred to as “(d1- One or more compounds selected from the group consisting of “3) component”) are preferred.
The components (d1-1) to (d1-3) decompose in the exposed part of the resist film and lose acid diffusion controllability (basicity), and thus do not act as a quencher, and act as a quencher in an unexposed part. To do.

［式中、Ｒｄ^１〜Ｒｄ^４は置換基を有していてもよい環式基、置換基を有していてもよい鎖状のアルキル基、又は置換基を有していてもよい鎖状のアルケニル基である。但し、式（ｄ１−２）中のＲｄ^２における、Ｓ原子に隣接する炭素原子にはフッ素原子は結合していないものとする。Ｙｄ^１は単結合又は２価の連結基である。ｍは１以上の整数であって、Ｍ^ｍ＋はそれぞれ独立にｍ価の有機カチオンである。］

[Wherein Rd ^{1 to} Rd ⁴ are a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a chain which may have a substituent. Of the alkenyl group. However, a fluorine atom is not bonded to a carbon atom adjacent to the S atom in Rd ² in the formula (d1-2). Yd ¹ is a single bond or a divalent linking group. m is an integer of 1 or more, and M ^{m +} is each independently an m-valent organic cation. ]

{(D1-1) component}
.. Anion moiety In formula (d1-1), Rd ¹ has a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. And a chain alkenyl group which may be the same as R ¹⁰¹ in the formula (b-1).
Among these, Rd ¹ may have an aromatic hydrocarbon group which may have a substituent, an aliphatic cyclic group which may have a substituent, or a substituent. A chain alkyl group is preferred. Examples of the substituent that these groups may have include a hydroxyl group, an oxo group, an alkyl group, an aryl group, a fluorine atom, a fluorinated alkyl group, and the above general formulas (a2-r-1) to (a2-r- Examples thereof include lactone-containing cyclic groups represented by 7), ether bonds, ester bonds, or combinations thereof. When an ether bond or an ester bond is included as a substituent, an alkylene group may be interposed. In this case, the substituent is represented by the above formulas (y-al-1) to (y-al-5), respectively. The linking group is preferred.
As the aromatic hydrocarbon group, a phenyl group or a naphthyl group is more preferable.
The aliphatic cyclic group is more preferably a group in which one or more hydrogen atoms have been removed from a polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane or tetracyclododecane.
The chain alkyl group preferably has 1 to 10 carbon atoms, specifically, methyl group, ethyl group, propyl group, butyl group, pentyl group, hexyl group, heptyl group, octyl group, Linear alkyl groups such as nonyl and decyl; 1-methylethyl, 1-methylpropyl, 2-methylpropyl, 1-methylbutyl, 2-methylbutyl, 3-methylbutyl, 1-ethylbutyl A branched alkyl group such as a group, 2-ethylbutyl group, 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4-methylpentyl group.

When the chain alkyl group is a fluorinated alkyl group having a fluorine atom or a fluorinated alkyl group as a substituent, the fluorinated alkyl group preferably has 1 to 11 carbon atoms, more preferably 1 to 8 carbon atoms. ~ 4 is more preferred. The fluorinated alkyl group may contain an atom other than a fluorine atom. Examples of atoms other than fluorine atoms include oxygen atoms, sulfur atoms and nitrogen atoms.
Rd ¹ is preferably a fluorinated alkyl group in which some or all of the hydrogen atoms constituting the linear alkyl group are substituted by fluorine atoms, and the hydrogen atom constituting the linear alkyl group It is particularly preferable that all are fluorinated alkyl groups (linear perfluoroalkyl groups) substituted with fluorine atoms.

  Preferred specific examples of the anion moiety of the component (d1-1) are shown below.

..Cation part In the formula (d1-1), M ^{m +} is an m-valent organic cation.
As the organic cation of M ^{m +} , those similar to the cations represented by the general formulas (ca-1) to (ca-5) are preferably exemplified, and represented by the general formula (ca-1). A cation is more preferable, and a cation represented by each of the formulas (ca-1-1) to (ca-1-67) is more preferable.
As the component (d1-1), one type may be used alone, or two or more types may be used in combination.

{(D1-2) component}
.. Anion moiety In formula (d1-2), Rd ² has a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. A chain alkenyl group that may be present, and examples thereof include the same groups as those described above for R ^{101 in} formula (b-1).
However, a fluorine atom is not bonded to a carbon atom adjacent to the S atom in Rd ² (not fluorine-substituted). Thereby, the anion of (d1-2) component turns into a moderate weak acid anion, and the quenching ability as (D) component improves.
Rd ² is preferably a chain alkyl group which may have a substituent, or an aliphatic cyclic group which may have a substituent. The chain alkyl group preferably has 1 to 10 carbon atoms, and more preferably 3 to 10 carbon atoms. As the aliphatic cyclic group, a group in which one or more hydrogen atoms are removed from adamantane, norbornane, isobornane, tricyclodecane, tetracyclododecane or the like (which may have a substituent); one from camphor or the like A group excluding the above hydrogen atoms is more preferable.
The hydrocarbon group of Rd ² may have a substituent, and examples of the substituent include a hydrocarbon group (aromatic hydrocarbon group, aliphatic cyclic group) in Rd ¹ of the formula (d1-1). Examples thereof include the same substituents that the chain-like alkyl group may have.

  Preferred specific examples of the anion moiety of the component (d1-2) are shown below.

..Cation part In the formula (d1-2), M ^{m +} is an m-valent organic cation, which is the same as M ^{m +} in the formula (d1-1).
As the component (d1-2), one type may be used alone, or two or more types may be used in combination.

{(D1-3) component}
.. Anion moiety In formula (d1-3), Rd ³ has a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. A chain alkenyl group which may be the same as R ^{101 in} formula (b-1), and includes a cyclic group containing a fluorine atom, a chain alkyl group, or a chain alkenyl group. It is preferable that Among them, a fluorinated alkyl group is preferable, and the same as the fluorinated alkyl group for Rd ¹ is more preferable.

In formula (d1-3), Rd ⁴ may have a cyclic group which may have a substituent, a chain alkyl group which may have a substituent, or a substituent. Examples of the chain alkenyl group include those similar to R ¹⁰¹ in the formula (b-1).
Among these, an alkyl group, an alkoxy group, an alkenyl group, or a cyclic group that may have a substituent is preferable.
The alkyl group in Rd ⁴ is preferably a linear or branched alkyl group having 1 to 5 carbon atoms, specifically, methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, isobutyl group. Tert-butyl group, pentyl group, isopentyl group, neopentyl group and the like. A part of the hydrogen atoms of the alkyl group of Rd ⁴ may be substituted with a hydroxyl group, a cyano group, or the like.
The alkoxy group in Rd ⁴ is preferably an alkoxy group having 1 to 5 carbon atoms. Specific examples of the alkoxy group having 1 to 5 carbon atoms include methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n- Examples include butoxy group and tert-butoxy group. Of these, a methoxy group and an ethoxy group are preferable.

Examples of the alkenyl group for Rd ⁴ include the same groups as those for R ¹⁰¹ in the above formula (b-1), and a vinyl group, a propenyl group (allyl group), a 1-methylpropenyl group, and a 2-methylpropenyl group are preferable. These groups may further have, as a substituent, an alkyl group having 1 to 5 carbon atoms or a halogenated alkyl group having 1 to 5 carbon atoms.

Examples of the cyclic group for Rd ⁴ include those similar to R ¹⁰¹ in the above formula (b-1), such as cyclopentane, cyclohexane, adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. An alicyclic group excluding one or more hydrogen atoms, or an aromatic group such as a phenyl group or a naphthyl group is preferred. When Rd ⁴ is an alicyclic group, the resist composition is well dissolved in an organic solvent, whereby the lithography properties are improved. In addition, when Rd ⁴ is an aromatic group, in lithography using EUV or the like as an exposure light source, the resist composition is excellent in light absorption efficiency, and sensitivity and lithography characteristics are good.

In formula (d1-3), Yd ¹ represents a single bond or a divalent linking group.
The divalent linking group in Yd ¹ is not particularly limited, but may be a divalent hydrocarbon group (aliphatic hydrocarbon group or aromatic hydrocarbon group) which may have a substituent, or a hetero atom containing 2 Valent linking groups and the like. Each of these includes a divalent hydrocarbon group which may have a substituent and a hetero atom which are mentioned in the description of the divalent linking group in Ya ²¹ in the above formula (a2-1). The thing similar to a bivalent coupling group is mentioned.
Yd ¹ is preferably a carbonyl group, an ester bond, an amide bond, an alkylene group, or a combination thereof. The alkylene group is preferably a linear or branched alkylene group, and more preferably a methylene group or an ethylene group.

  Preferred specific examples of the anion moiety of the component (d1-3) are shown below.

..Cation part In the formula (d1-3), M ^{m +} is an m-valent organic cation, and is the same as M ^{m +} in the formula (d1-1).
As the component (d1-3), one type may be used alone, or two or more types may be used in combination.

As the component (D1), only one of the above components (d1-1) to (d1-3) may be used, or two or more may be used in combination.
When the resist composition contains the component (D1), the content of the component (D1) is preferably 0.5 to 10 parts by mass with respect to 100 parts by mass of the component (A), and 0.5 to The amount is more preferably 8 parts by mass, and further preferably 1 to 8 parts by mass.
When the content of the component (D1) is equal to or more than the preferable lower limit value, particularly good lithography characteristics and a resist pattern shape are easily obtained. On the other hand, when it is not more than the upper limit value, the sensitivity can be maintained well and the throughput is also excellent.

(D1) Component production method:
The manufacturing method of said (d1-1) component and (d1-2) component is not specifically limited, It can manufacture by a well-known method.
Moreover, the manufacturing method of (d1-3) component is not specifically limited, For example, it manufactures similarly to the method of US2012-0149916 gazette.

-About (D2) component As an acid diffusion controlling agent component, you may contain the nitrogen-containing organic compound component (henceforth "(D2) component") which does not correspond to said (D1) component.
The component (D2) is not particularly limited as long as it functions as an acid diffusion controller and does not correspond to the component (D1), and any known component may be used. Of these, aliphatic amines are preferable, and among these, secondary aliphatic amines and tertiary aliphatic amines are more preferable.
An aliphatic amine is an amine having one or more aliphatic groups, and the aliphatic groups preferably have 1 to 12 carbon atoms.
Examples of the aliphatic amine include an amine (alkyl amine or alkyl alcohol amine) or a cyclic amine in which at least one hydrogen atom of ammonia NH ₃ is substituted with an alkyl group or hydroxyalkyl group having 12 or less carbon atoms.
Specific examples of alkylamines and alkyl alcohol amines include monoalkylamines such as n-hexylamine, n-heptylamine, n-octylamine, n-nonylamine, n-decylamine; diethylamine, di-n-propylamine, di- -Dialkylamines such as n-heptylamine, di-n-octylamine, dicyclohexylamine; trimethylamine, triethylamine, tri-n-propylamine, tri-n-butylamine, tri-n-pentylamine, tri-n-hexylamine , Trialkylamines such as tri-n-heptylamine, tri-n-octylamine, tri-n-nonylamine, tri-n-decylamine, tri-n-dodecylamine; diethanolamine, triethanolamine, diisopropanolamine, Li isopropanolamine, di -n- octanol amines, alkyl alcohol amines tri -n- octanol amine. Among these, a trialkylamine having 5 to 10 carbon atoms is more preferable, and tri-n-pentylamine or tri-n-octylamine is particularly preferable.

Examples of the cyclic amine include heterocyclic compounds containing a nitrogen atom as a hetero atom. The heterocyclic compound may be monocyclic (aliphatic monocyclic amine) or polycyclic (aliphatic polycyclic amine).
Specific examples of the aliphatic monocyclic amine include piperidine and piperazine.
As the aliphatic polycyclic amine, those having 6 to 10 carbon atoms are preferable. Specifically, 1,5-diazabicyclo [4.3.0] -5-nonene, 1,8-diazabicyclo [5. 4.0] -7-undecene, hexamethylenetetramine, 1,4-diazabicyclo [2.2.2] octane, and the like.

  Other aliphatic amines include tris (2-methoxymethoxyethyl) amine, tris {2- (2-methoxyethoxy) ethyl} amine, tris {2- (2-methoxyethoxymethoxy) ethyl} amine, tris {2 -(1-methoxyethoxy) ethyl} amine, tris {2- (1-ethoxyethoxy) ethyl} amine, tris {2- (1-ethoxypropoxy) ethyl} amine, tris [2- {2- (2-hydroxy Ethoxy) ethoxy} ethyl] amine, triethanolamine triacetate and the like, and triethanolamine triacetate is preferable.

As the component (D2), an aromatic amine may be used.
Examples of the aromatic amine include 4-dimethylaminopyridine, pyrrole, indole, pyrazole, imidazole or derivatives thereof, tribenzylamine, 2,6-diisopropylaniline, N-tert-butoxycarbonylpyrrolidine and the like.

(D2) A component may be used independently and may be used in combination of 2 or more type.
When the resist composition contains the component (D2), the component (D2) is usually used in the range of 0.01 to 5 parts by mass with respect to 100 parts by mass of the component (A). By setting the content in the above range, the resist pattern shape, the stability over time, and the like are improved.

<< Organic carboxylic acid, and at least one compound (E) selected from the group consisting of phosphorus oxoacids and derivatives thereof >>
The resist composition of the present embodiment includes, as optional components, organic carboxylic acid, phosphorus oxo acid, and derivatives thereof for the purpose of preventing sensitivity deterioration and improving the resist pattern shape, retention stability over time, and the like. At least one compound (E) (hereinafter referred to as “component (E)”) selected from the group consisting of:
As the organic carboxylic acid, for example, acetic acid, malonic acid, citric acid, malic acid, succinic acid, benzoic acid, salicylic acid and the like are suitable.
Examples of phosphorus oxo acids include phosphoric acid, phosphonic acid, and phosphinic acid. Among these, phosphonic acid is particularly preferable.
Examples of the oxo acid derivative of phosphorus include esters obtained by substituting the hydrogen atom of the oxo acid with a hydrocarbon group, and examples of the hydrocarbon group include an alkyl group having 1 to 5 carbon atoms and 6 to 6 carbon atoms. 15 aryl groups and the like.
Examples of phosphoric acid derivatives include phosphoric acid esters such as di-n-butyl phosphate and diphenyl phosphate.
Examples of phosphonic acid derivatives include phosphonic acid esters such as phosphonic acid dimethyl ester, phosphonic acid-di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester.
Examples of phosphinic acid derivatives include phosphinic acid esters and phenylphosphinic acid.
(E) A component may be used individually by 1 type and may use 2 or more types together.
When a resist composition contains (E) component, (E) component is normally used in 0.01-5 mass parts with respect to 100 mass parts of (A) component.

≪Fluorine additive component (F) ≫
The resist composition of this embodiment may contain a fluorine additive component (hereinafter referred to as “component (F)”) in order to impart water repellency to the resist film.
Examples of the component (F) include those described in JP 2010-002870 A, JP 2010-032994 A, JP 2010-277043 A, JP 2011-13569 A, and JP 2011-128226 A. These fluorine-containing polymer compounds can be used.
More specifically, examples of the component (F) include a polymer having a structural unit (f1) represented by the following formula (f1-1). Examples of the polymer include a polymer (homopolymer) composed only of the structural unit (f1) represented by the following formula (f1-1); a structural unit (a1) containing an acid-decomposable group whose polarity increases by the action of an acid. ) And the structural unit (f1); a copolymer of the structural unit (f1), a structural unit derived from acrylic acid or methacrylic acid, and the structural unit (a1). Is preferred. Here, as the structural unit (a1) copolymerized with the structural unit (f1), a structural unit derived from 1-ethyl-1-cyclooctyl (meth) acrylate, 1-methyl-1-adamantyl ( Structural units derived from (meth) acrylates are preferred.

［式中、Ｒは前記と同様であり、Ｒｆ^１０２およびＲｆ^１０３はそれぞれ独立して水素原子、ハロゲン原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基を表し、Ｒｆ^１０２およびＲｆ^１０３は同じであっても異なっていてもよい。ｎｆ^１は１〜５の整数であり、Ｒｆ^１０１はフッ素原子を含む有機基である。］

[Wherein, R is the same as defined above, and Rf ¹⁰² and Rf ¹⁰³ each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, Rf ¹⁰² and Rf ¹⁰³ may be the same or different. nf ¹ is an integer of ¹ to 5, and Rf ¹⁰¹ is an organic group containing a fluorine atom. ]

In the formula (f1-1), R bonded to the α-position carbon atom is the same as described above. R is preferably a hydrogen atom or a methyl group.
In formula (f1-1), examples of the halogen atom for Rf ¹⁰² and Rf ¹⁰³ include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. Examples of the alkyl group having 1 to 5 carbon atoms of Rf ¹⁰² and Rf ¹⁰³ include the same as the alkyl group having 1 to 5 carbon atoms of R, and a methyl group or an ethyl group is preferable. Specific examples of the halogenated alkyl group having 1 to 5 carbon atoms of Rf ¹⁰² and Rf ¹⁰³ include groups in which some or all of the hydrogen atoms of the alkyl group having 1 to 5 carbon atoms have been substituted with halogen atoms. It is done. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is particularly preferable. The inter alia ^{Rf 102} and ^{Rf 103,} a hydrogen atom, a fluorine atom, or an alkyl group of 1 to 5 carbon atoms is preferable, a hydrogen atom, a fluorine atom, a methyl group or an ethyl group, preferred.
In formula (f1-1), nf ¹ is an integer of ¹ to 5, an integer of 1 to 3 is preferable, and 1 or 2 is more preferable.

In formula (f1-1), Rf ¹⁰¹ is an organic group containing a fluorine atom, and is preferably a hydrocarbon group containing a fluorine atom.
The hydrocarbon group containing a fluorine atom may be linear, branched or cyclic, and preferably has 1 to 20 carbon atoms, more preferably 1 to 15 carbon atoms. The carbon number of 1 to 10 is particularly preferable.
The hydrocarbon group containing a fluorine atom preferably has 25% or more of the hydrogen atoms in the hydrocarbon group fluorinated, more preferably 50% or more fluorinated, and 60% or more. Fluorination is particularly preferred because the hydrophobicity of the resist film during immersion exposure is increased.
Among ^these, as ^{Rf 101,} more preferably a fluorinated hydrocarbon group having 1 to 6 carbon atoms, trifluoromethyl _{group, -CH 2 -CF 3, -CH 2} -CF 2 -CF 3, -CH (CF 3 ) ₂ , —CH ₂ —CH ₂ —CF ₃ , —CH ₂ —CH ₂ —CF ₂ —CF ₂ —CF ₂ —CF ₃ are particularly preferred.

(F) As for the weight average molecular weight (Mw) (polystyrene conversion reference | standard by a gel permeation chromatography), 1000-50000 are preferable, 5000-40000 are more preferable, and 10000-30000 are the most preferable. If it is below the upper limit of this range, it has sufficient solubility in a resist solvent for use as a resist, and if it is above the lower limit of this range, the dry etching resistance and resist pattern cross-sectional shape are good. .
The dispersity (Mw / Mn) of the component (F) is preferably 1.0 to 5.0, more preferably 1.0 to 3.0, and most preferably 1.2 to 2.5.

(F) A component may be used individually by 1 type and may use 2 or more types together.
When a resist composition contains (F) component, (F) component is normally used in the ratio of 0.5-10 mass parts with respect to 100 mass parts of (A) component.

  The resist composition according to the present embodiment further includes, if desired, miscible additives such as an additional resin for improving the performance of the resist film, a dissolution inhibitor, a plasticizer, a stabilizer, a colorant, and an antihalation agent. A dye or the like can be added and contained as appropriate.

≪Organic solvent component (S) ≫
The resist composition of this embodiment can be produced by dissolving a resist material in an organic solvent component (hereinafter sometimes referred to as “(S) component”).
As the component (S), any component can be used as long as it can dissolve each component to be used to form a uniform solution, and any conventionally known solvent for chemically amplified resist compositions can be appropriately selected. It can be selected and used.
For example, lactones such as γ-butyrolactone; ketones such as acetone, methyl ethyl ketone, cyclohexanone, methyl-n-pentyl ketone, methyl isopentyl ketone, and 2-heptanone; many such as ethylene glycol, diethylene glycol, propylene glycol, and dipropylene glycol Monohydric alcohols; compounds having an ester bond, such as ethylene glycol monoacetate, diethylene glycol monoacetate, propylene glycol monoacetate, dipropylene glycol monoacetate, monomethyl ether, monoethyl of the polyhydric alcohols or compound having the ester bond Ethers such as ether, monopropyl ether, monobutyl ether and other monoalkyl ethers and monophenyl ether Derivatives of polyhydric alcohols such as compounds having a combination [in these, propylene glycol monomethyl ether acetate (PGMEA) and propylene glycol monomethyl ether (PGME) are preferred]; cyclic ethers such as dioxane, methyl lactate Esters such as ethyl lactate (EL), methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, ethyl ethoxypropionate; anisole, ethyl benzyl ether, cresyl methyl ether, diphenyl ether , Dibenzyl ether, phenetole, butyl phenyl ether, ethylbenzene, diethylbenzene, pentylbenzene, isopropylbenzene, toluene, xylene, cymene, mesitylene, etc. Examples of the solvent include dimethyl sulfoxide (DMSO).
(S) component may be used independently and may be used as 2 or more types of mixed solvents.
Of these, PGMEA, PGME, γ-butyrolactone, EL, and cyclohexanone are preferable.
Moreover, the mixed solvent which mixed PGMEA and the polar solvent is also preferable. The blending ratio (mass ratio) may be appropriately determined in consideration of the compatibility between PGMEA and the polar solvent, preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. It is preferable to be within the range.
More specifically, when EL or cyclohexanone is blended as the polar solvent, the mass ratio of PGMEA: EL or cyclohexanone is preferably 1: 9 to 9: 1, more preferably 2: 8 to 8: 2. . Moreover, when mix | blending PGME as a polar solvent, the mass ratio of PGMEA: PGME becomes like this. Preferably it is 1: 9-9: 1, More preferably, it is 2: 8-8: 2, More preferably, it is 3: 7-7: 3. Furthermore, a mixed solvent of PGMEA, PGME, and cyclohexanone is also preferable.
In addition, as the component (S), a mixed solvent of at least one selected from PGMEA and EL and γ-butyrolactone is also preferable. In this case, the mixing ratio of the former and the latter is preferably 70:30 to 95: 5.
The amount of the component (S) used is not particularly limited, and is a concentration that can be applied to a substrate or the like, and is appropriately set according to the coating film thickness. Generally, the (S) component is used so that the solid content concentration of the resist composition is in the range of 1 to 20% by mass, preferably 2 to 15% by mass.

According to the resist composition of the present embodiment described above, it is possible to obtain the effects that the sensitivity can be further improved and the resist pattern shape can be further improved in the formation of the resist pattern.
In the resist composition of the embodiment, the polymer compound (A1) having the structural unit (a0) represented by the general formula (a0-1) is used as the base component (A). This structural unit (a0) has an acid dissociable group represented by the general formula (a0-r1-1) at the end of the side chain. Such acid dissociable groups include quaternary carbon atoms (Ya ⁰ ) and polar groups.
When such a acid dissociable group contains a quaternary carbon atom (Ya ⁰ ), compared with the case where a tertiary carbon atom is present in the acid dissociable group, when forming a resist pattern, Acid dissociation by exposure is likely to improve. For this reason, the reactivity is enhanced and the sensitivity is increased. In addition, high dissolution contrast can be obtained by development.
Further, since the acid dissociable group contains a polar group, the solubility in a developer containing an organic solvent can be kept low. For this reason, when the acid-dissociable group remains in the resist film exposed part without being decomposed in the solvent development or when it remains in the resist film as a decomposition product, Since the dissolution rate is less likely to increase, it is possible to suppress film loss at the pattern portion. In addition, partial dissolution of the pattern boundary can be suppressed. Furthermore, since the acid dissociable group contains a polar group, the affinity for an alkali developer is increased. For this reason, at the time of alkali development, since the solubility in an alkali developer increases, the development proceeds more uniformly and smoothly.
Due to the above-described action, in the formation of a resist pattern using the resist composition of the embodiment, lithography characteristics such as in-plane uniformity (CDU) and circularity of pattern dimensions are further improved and good A resist pattern having a proper shape can be formed.

(Resist pattern formation method)
In the resist pattern forming method of the present embodiment, a step of forming a resist film on the support using the above-described (resist composition), a step of exposing the resist film, and developing the resist film after the exposure Forming a resist pattern.
The resist pattern formation method of this embodiment can be performed as follows, for example.

First, the resist composition of the present embodiment described above is applied onto a support with a spinner or the like, and a baking (post-apply bake (PAB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds. The resist film is formed preferably for 60 to 90 seconds.
Next, exposure or a mask pattern is performed on the resist film through a mask (mask pattern) on which a predetermined pattern is formed using an exposure apparatus such as an ArF exposure apparatus, an electron beam drawing apparatus, or an EUV exposure apparatus. After performing selective exposure by drawing or the like by direct irradiation of an electron beam without passing through, baking (post-exposure baking (PEB)) treatment is performed, for example, at a temperature of 80 to 150 ° C. for 40 to 120 seconds, preferably 60 to Apply for 90 seconds.
Next, the resist film is developed. The development treatment is performed using an alkaline developer in the case of an alkali development process, and using a developer (organic developer) containing an organic solvent in the case of a solvent development process.
A rinsing treatment is preferably performed after the development treatment. The rinse treatment is preferably a water rinse using pure water in the case of an alkali development process, and is preferably a rinse solution containing an organic solvent in the case of a solvent development process.
In the case of a solvent development process, after the development process or the rinse process, a process of removing the developer or rinse liquid adhering to the pattern with a supercritical fluid may be performed.
Drying is performed after development or rinsing. In some cases, a baking process (post-bake) may be performed after the development process.
In this way, a resist pattern can be formed.

The support is not particularly limited, and a conventionally known one can be used. Examples thereof include a substrate for electronic parts and a substrate on which a predetermined wiring pattern is formed. More specifically, a silicon substrate, a metal substrate such as copper, chromium, iron, and aluminum, a glass substrate, and the like can be given. As a material for the wiring pattern, for example, copper, aluminum, nickel, gold or the like can be used.
Further, the support may be a substrate in which an inorganic and / or organic film is provided on the above-described substrate. An inorganic antireflection film (inorganic BARC) is an example of the inorganic film. Examples of the organic film include an organic antireflection film (organic BARC) and an organic film such as a lower organic film in a multilayer resist method.
Here, the multilayer resist method is a method in which at least one organic film (lower organic film) and at least one resist film (upper resist film) are provided on a substrate, and the resist pattern formed on the upper resist film is used as a mask. This is a method of patterning a lower organic film, and it is said that a pattern with a high aspect ratio can be formed. That is, according to the multilayer resist method, the required thickness can be secured by the lower organic film, so that the resist film can be thinned and a fine pattern with a high aspect ratio can be formed.
In the multilayer resist method, basically, a method of forming a two-layer structure of an upper resist film and a lower organic film (two-layer resist method), and one or more intermediate layers between the upper resist film and the lower organic film And a method of forming a multilayer structure of three or more layers (metal thin film etc.) (three-layer resist method).

The wavelength used for exposure is not particularly limited, and ArF excimer laser, KrF excimer laser, F ₂ excimer laser, EUV (extreme ultraviolet), VUV (vacuum ultraviolet), EB (electron beam), X-ray, soft X-ray, etc. Can be done using radiation. The resist composition is highly useful for KrF excimer laser, ArF excimer laser, EB or EUV, and is particularly useful for ArF excimer laser, EB or EUV.

The exposure method of the resist film may be normal exposure (dry exposure) performed in an inert gas such as air or nitrogen, or may be immersion exposure (Liquid Immersion Lithography).
In immersion exposure, the space between the resist film and the lens at the lowest position of the exposure apparatus is previously filled with a solvent (immersion medium) having a refractive index larger than that of air, and exposure (immersion exposure) is performed in that state. It is an exposure method.
As the immersion medium, a solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film to be exposed is preferable. The refractive index of such a solvent is not particularly limited as long as it is within the above range.
Examples of the solvent having a refractive index larger than the refractive index of air and smaller than the refractive index of the resist film include water, a fluorine-based inert liquid, a silicon-based solvent, and a hydrocarbon-based solvent.
Specific examples of the fluorine-based inert liquid include a fluorine-based compound such as C ₃ HCl ₂ F ₅ , C ₄ F ₉ OCH ₃ , C ₄ F ₉ OC ₂ H ₅ , and C ₅ H ₃ F ₇ as a main component. Examples thereof include liquids, and those having a boiling point of 70 to 180 ° C are preferable, and those having a boiling point of 80 to 160 ° C are more preferable. It is preferable that the fluorine-based inert liquid has a boiling point in the above range since the medium used for immersion can be removed by a simple method after the exposure is completed.
As the fluorine-based inert liquid, a perfluoroalkyl compound in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms is particularly preferable. Specific examples of the perfluoroalkyl compound include a perfluoroalkyl ether compound and a perfluoroalkylamine compound.
More specifically, examples of the perfluoroalkyl ether compound include perfluoro (2-butyl-tetrahydrofuran) (boiling point: 102 ° C.). Examples of the perfluoroalkylamine compound include perfluorotributylamine ( Boiling point of 174 ° C.).
As the immersion medium, water is preferably used from the viewpoints of cost, safety, environmental problems, versatility, and the like.

Examples of the alkali developer used for the development treatment in the alkali development process include a 0.1 to 10% by mass tetramethylammonium hydroxide (TMAH) aqueous solution.
The organic solvent contained in the organic developer used for the development process in the solvent development process is not particularly limited as long as it can dissolve the component (A) (component (A) before exposure). It can be selected as appropriate. Specific examples include ketone solvents, ester solvents, alcohol solvents, nitrile solvents, amide solvents, ether solvents, and other polar solvents, hydrocarbon solvents, and the like.
The ketone solvent is an organic solvent containing C—C (═O) —C in the structure. The ester solvent is an organic solvent containing C—C (═O) —O—C in the structure. The alcohol solvent is an organic solvent containing an alcoholic hydroxyl group in the structure. “Alcoholic hydroxyl group” means a hydroxyl group bonded to a carbon atom of an aliphatic hydrocarbon group. A nitrile solvent is an organic solvent containing a nitrile group in its structure. The amide solvent is an organic solvent containing an amide group in the structure. The ether solvent is an organic solvent containing C—O—C in the structure.
Among organic solvents, there are organic solvents that contain multiple types of functional groups that characterize each of the above solvents in the structure, but in that case, any of the solvent types that contain the functional groups of the organic solvent is applicable. Shall. For example, diethylene glycol monomethyl ether corresponds to both alcohol solvents and ether solvents in the above classification.
The hydrocarbon solvent is a hydrocarbon solvent made of a hydrocarbon which may be halogenated and having no substituent other than a halogen atom. Examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom, and a fluorine atom is preferable.
Among the above, the organic solvent contained in the organic developer is preferably a polar solvent, and is preferably a ketone solvent, an ester solvent, a nitrile solvent, or the like.

  Examples of ketone solvents include 1-octanone, 2-octanone, 1-nonanone, 2-nonanone, acetone, 4-heptanone, 1-hexanone, 2-hexanone, diisobutyl ketone, cyclohexanone, methylcyclohexanone, phenylacetone, and methyl ethyl ketone. , Methyl isobutyl ketone, acetylacetone, acetonyl acetone, ionone, diacetyl alcohol, acetyl carbinol, acetophenone, methyl naphthyl ketone, isophorone, propylene carbonate, γ-butyrolactone, methyl amyl ketone (2-heptanone) and the like. Among these, as a ketone solvent, methyl amyl ketone (2-heptanone) is preferable.

  Examples of ester solvents include methyl acetate, butyl acetate, ethyl acetate, isopropyl acetate, amyl acetate, isoamyl acetate, ethyl methoxyacetate, ethyl ethoxyacetate, propylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethylene glycol mono Propyl ether acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monophenyl ether acetate, diethylene glycol monomethyl ether acetate, diethylene glycol monopropyl ether acetate, diethylene glycol monoethyl ether acetate, diethylene glycol monophenyl ether acetate, diethylene glycol monobutyl ether acetate, diethylene Recall monoethyl ether acetate, 2-methoxybutyl acetate, 3-methoxybutyl acetate, 4-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, 3-ethyl-3-methoxybutyl acetate, propylene glycol monomethyl ether acetate, Propylene glycol monoethyl ether acetate, propylene glycol monopropyl ether acetate, 2-ethoxybutyl acetate, 4-ethoxybutyl acetate, 4-propoxybutyl acetate, 2-methoxypentyl acetate, 3-methoxypentyl acetate, 4-methoxypentyl acetate, 2-methyl-3-methoxypentyl acetate, 3-methyl-3-methoxypentyl acetate, 3-methyl-4-methoxy Nethyl acetate, 4-methyl-4-methoxypentyl acetate, propylene glycol diacetate, methyl formate, ethyl formate, butyl formate, propyl formate, ethyl lactate, butyl lactate, propyl lactate, ethyl carbonate, propyl carbonate, butyl carbonate, pyrubin Methyl acid, ethyl pyruvate, propyl pyruvate, butyl pyruvate, methyl acetoacetate, ethyl acetoacetate, methyl propionate, ethyl propionate, propyl propionate, isopropyl propionate, methyl 2-hydroxypropionate, 2-hydroxypropionate Examples include ethyl acid, methyl-3-methoxypropionate, ethyl-3-methoxypropionate, ethyl-3-ethoxypropionate, and propyl-3-methoxypropionate. Among these, butyl acetate is preferable as the ester solvent.

  Examples of the nitrile solvent include acetonitrile, propionitryl, valeronitrile, butyronitryl and the like.

A known additive can be blended in the organic developer as required. Examples of the additive include a surfactant. The surfactant is not particularly limited. For example, ionic or nonionic fluorine-based and / or silicon-based surfactants can be used. As the surfactant, a nonionic surfactant is preferable, and a nonionic fluorine-based surfactant or a nonionic silicon-based surfactant is more preferable.
When the surfactant is blended, the blending amount is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and 0.01 to 0. 5 mass% is more preferable.

  The development process can be performed by a known development method. For example, a method in which a support is immersed in a developer for a certain period of time (dip method), a developer is raised on the surface of the support by surface tension, and is left for a certain period of time. (Paddle method), spraying developer on the surface of the support (spray method), coating the developer while scanning the developer coating nozzle at a constant speed on the support rotating at a constant speed The method of continuing (dynamic dispensing method) etc. are mentioned.

As the organic solvent contained in the rinsing liquid used for the rinsing process after the development process in the solvent developing process, for example, an organic solvent that is difficult to dissolve the resist pattern is selected as appropriate from the organic solvents used as the organic solvent used in the organic developer. Can be used. Usually, at least one solvent selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents, amide solvents and ether solvents is used. Among these, at least one selected from hydrocarbon solvents, ketone solvents, ester solvents, alcohol solvents and amide solvents is preferable, and at least one selected from alcohol solvents and ester solvents is preferable. More preferred are alcohol solvents.
The alcohol solvent used in the rinse liquid is preferably a monohydric alcohol having 6 to 8 carbon atoms, and the monohydric alcohol may be linear, branched or cyclic. Specific examples include 1-hexanol, 1-heptanol, 1-octanol, 2-hexanol, 2-heptanol, 2-octanol, 3-hexanol, 3-heptanol, 3-octanol, 4-octanol, and benzyl alcohol. It is done. Among these, 1-hexanol, 2-heptanol, and 2-hexanol are preferable, and 1-hexanol and 2-hexanol are more preferable.
Any one of these organic solvents may be used alone, or two or more thereof may be used in combination. Moreover, you may mix and use the organic solvent and water other than the above. However, in consideration of development characteristics, the amount of water in the rinsing liquid is preferably 30% by mass or less, more preferably 10% by mass or less, further preferably 5% by mass or less, more preferably 3% by mass with respect to the total amount of the rinsing liquid. The following are particularly preferred:
A well-known additive can be mix | blended with a rinse liquid as needed. Examples of the additive include a surfactant. Examples of the surfactant are the same as described above, and a nonionic surfactant is preferable, and a nonionic fluorine-based surfactant or a nonionic silicon-based surfactant is more preferable.
When the surfactant is blended, the blending amount is usually 0.001 to 5% by mass, preferably 0.005 to 2% by mass, and 0.01 to 0.5% by mass with respect to the total amount of the rinse liquid. % Is more preferable.

  The rinse treatment (washing treatment) using the rinse liquid can be performed by a known rinse method. Examples of the rinsing method include a method of continuously applying a rinsing liquid onto a support rotating at a constant speed (rotary coating method), a method of immersing the support in a rinsing liquid for a predetermined time (dip method), The method (spray method) etc. which spray the rinse liquid on the support body surface are mentioned.

  According to the resist pattern forming method of the present embodiment described above, since the above-described (resist composition) is used, the sensitivity can be improved and the lithography characteristics can be improved, and a resist pattern having a better shape can be formed. .

(Polymer compound)
The polymer compound of this embodiment has a structural unit (a0) represented by the following general formula (a0-1).

［式中、Ｒは、水素原子、炭素数１〜５のアルキル基又は炭素数１〜５のハロゲン化アルキル基である。Ｖａ^０は、エーテル結合を有していてもよい２価の炭化水素基である。ｎ_ａ０は、０〜２の整数である。Ｒａ^００は、一般式（ａ０−ｒ１−１）で表される酸解離性基である。Ｒａ^０１は、置換基を有していてもよい炭化水素基である。Ｒａ^０２は、置換基を有していてもよい炭化水素基である。Ｒａ^０１とＲａ^０２とは相互に結合して、環構造を形成してもよい。Ｙａ^０は、第４級炭素原子である。Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３は、それぞれ独立に、置換基を有していてもよい炭化水素基である。但し、Ｒａ^０３１、Ｒａ^０３２及びＲａ^０３３のうちの１つ以上は、少なくとも極性基を有する炭化水素基である。］

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ⁰ is a divalent hydrocarbon group which may have an ether bond. n _a0 is an integer of 0-2. Ra ⁰⁰ is an acid dissociable group represented by general formula (a0-r1-1). Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent. However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group. ]

  In the polymer compound of the embodiment, the proportion of the structural unit (a0) is, for example, 10 to 70 with respect to the total of all the structural units constituting the polymer compound when applied to a base resin for a resist composition. The mol% is preferred, and the content is particularly preferably 20 to 50 mol%.

  The polymer compound of this embodiment is the same as the component (A1) (polymer compound having the structural unit (a0)) in the above description of the (resist composition), and is present in addition to the structural unit (a0). The types of structural units that may be used and the content of each structural unit in the component (A1) are the same as described above.

In the polymer compound of this embodiment, a monomer for deriving the structural unit (a0) and a monomer for deriving a structural unit other than the structural unit (a0), if necessary, are dissolved in a polymerization solvent. It can be produced by adding a radical polymerization initiator such as azobisisobutyronitrile (AIBN) or dimethyl azobisisobutyrate (for example, V-601) for polymerization.
In the polymerization, for example, a chain transfer agent such as HS—CH ₂ —CH ₂ —CH ₂ —C (CF ₃ ) ₂ —OH is used in combination, so that —C (CF ₃ ) is terminally used. _{A 2-} OH group may be introduced. As described above, a copolymer introduced with a hydroxyalkyl group in which a part of hydrogen atoms of the alkyl group is substituted with a fluorine atom reduces development defects and LER (line edge roughness: uneven unevenness of line side walls). It is effective in reducing

  The monomer for deriving the structural unit (a0) can be produced, for example, by a method referring to the synthesis described in paragraphs 0087 and 0090 of International Publication No. 2013/042694.

  The polymer compound of the present embodiment is a novel substance that is useful as a base resin for a resist composition, and the solubility in a developing solution is changed by the action of an acid in addition to a base material component having film-forming ability. It can mix | blend suitably with a resist composition as a resin component ((A1) component).

  EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited by these examples.

<Production example of monomer (a01)>
Synthesis is carried out using methyl 2,2-dimethyl-3-methoxypropionate as a raw material with reference to synthesis examples described in paragraphs 0087 and 0090 of International Publication No. 2013/042694, and the target monomer (a01) That is, 1- (2′-methoxy-1 ′, 1′-dimethylethyl) cyclopentan-1-yl methacrylate having the following NMR characteristics was obtained.

NMR measurement was performed on the obtained monomer (a01), and the structure was identified from the following results.
¹ H-NMR (CDCl ₃ ) δ (ppm) = 6.00 (m, 1H), 5.47 (m, 1H), 3.10 (s, 3H), 3.08 (s, 2H), 2 20-2.12 (m, 2H), 2.05-1.95 (m, 4H), 1.93 (t, 3H), 1.60-1.50 (m, 2H), 1.02 (S, 6H).

<Production example of base material component (polymer compound)>
The polymer compound used in this example was produced as follows (see Patent Document 2: Japanese Patent Application Laid-Open No. 2015-169843).

  26.40 g of methyl ethyl ketone (MEK) was placed in a separable flask connected with a thermometer, a reflux tube, and a nitrogen introduction tube, and heated to 80 ° C. Here, 3.5 g monomer (a21), 1.1 g monomer (a22), 4.59 g monomer (a01), 0.9 g monomer (a31), and 0.79 g as a polymerization initiator. A solution of dimethyl azobisisobutyrate (V-601) in 74.67 g of MEK was added dropwise over 4 hours under a nitrogen atmosphere. After completion of dropping, the reaction solution was heated and stirred for 1 hour, and then the reaction solution was cooled to room temperature. The obtained reaction polymerization solution was dropped into a large amount of n-heptane to precipitate a polymer, and the precipitated white powder was filtered and dried to obtain the desired polymer compound (A1-1) 6 0.7 g was obtained.

About the obtained high molecular compound (A1-1), the weight average molecular weight (Mw) of standard polystyrene conversion calculated | required by GPC measurement was 7900, and molecular weight dispersion degree (Mw / Mn) was 1.61. . ^The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by ¹³ C-NMR was 1 / m / n / o = 3/1/5/1.

<Preparation of resist composition>
(Example 1, Comparative Examples 1-4)
Each component shown in Table 1 was mixed and dissolved to prepare resist compositions (solid content concentration of 3.0% by mass) in each example.

In Table 1, each abbreviation has the following meaning. The numerical value in [] is a compounding amount (part by mass).
(A1) -1: The above-described polymer compound (A1-1).

(A2) -1: a polymer compound represented by the following chemical formula (A2-1). The weight average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement is 7000, and the molecular weight dispersion (Mw / Mn) is 1.50. ^The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by ¹³ C-NMR is 1 / m / n / o = 3/1/5/1.

(A2) -2: a polymer compound represented by the following chemical formula (A2-2). The weight average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement is 7500, and the molecular weight dispersity (Mw / Mn) is 1.48. ^The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by ¹³ C-NMR is 1 / m / n / o = 3/1/5/1.

(A2) -3: a polymer compound represented by the following chemical formula (A2-3). The weight average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement is 5700, and the molecular weight dispersity (Mw / Mn) is 1.49. ^The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by ¹³ C-NMR is 1 / m / n / o = 3/1/5/1.

(A2) -4: a polymer compound represented by the following chemical formula (A2-4). The weight average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement is 6500, and the molecular weight dispersity (Mw / Mn) is 1.52. ^The copolymer composition ratio (ratio of each structural unit in the structural formula (molar ratio)) determined by ¹³ C-NMR is 1 / m / n / o = 3/1/5/1.

(B) -1: Compound (acid generator) represented by the following chemical formula (B-1).
(D) -1: a compound (acid diffusion controller) represented by the following chemical formula (D-1).

(F) -1: A fluorine-containing polymer compound represented by the following chemical formula (F-1). The weight average molecular weight (Mw) in terms of standard polystyrene determined by GPC measurement is 15500, and the molecular weight dispersity (Mw / Mn) is 1.67. ^The copolymer composition ratio (ratio (molar ratio) of each structural unit in the structural formula) determined by ¹³ C-NMR is 1 / m = 5/5.
(S) -1: Mixed solvent of propylene glycol monomethyl ether acetate / propylene glycol monomethyl ether / cyclohexanone = 45/30/25 (mass ratio).

<Formation of resist pattern>
The resist composition of each example was applied onto an 8-inch silicon substrate subjected to hexamethyldisilazane (HMDS) treatment using a spinner, and prebaked (PAB) at a temperature of 110 ° C. for 60 seconds on a hot plate. By performing the treatment, it was dried to form a resist film having a thickness of 90 nm.
Next, using an ArF exposure apparatus S610C (NA 1.20; Annual, 0.90 / 0.70), an ArF excimer laser (193 nm) is applied to the resist film with a target (hole diameter 67 nm / pitch 130 nm). Irradiated selectively through a mask pattern.
Thereafter, a post-exposure heating (PEB) treatment was performed at 80 ° C. for 60 seconds.
Subsequently, the solvent development for 30 seconds was performed at 23 degreeC using butyl acetate, and the rinse process was performed continuously.
As a result, a contact hole (CH) pattern having a hole diameter of 73 nm / pitch of 130 nm was formed.

[Evaluation of optimum exposure (EOP)]
The optimum exposure dose EOP (mJ / cm ² ) at which the target size CH pattern is formed by the above-described <resist pattern formation> was determined. This is shown in Table 2 as “EOP (mJ / cm ² )”.

[Evaluation of in-plane uniformity of pattern dimensions (CDU)]
With respect to the CH pattern formed by the above <resist pattern formation>, the CH pattern was measured by a length measurement SEM (scanning electron microscope, acceleration voltage 300 V, trade name: S-9380, manufactured by Hitachi High-Technologies Corporation). The hole diameter (nm) of 100 holes in the CH pattern was measured. A triple value (3σ) of the standard deviation (σ) calculated from the measurement result was obtained. This is shown in Table 2 as “CDU (nm)”.
3σ obtained in this way means that the smaller the value, the higher the dimension (CD) uniformity of the holes formed in the resist film.

[Evaluation of Circularity]
Twenty-five holes in the CH pattern formed by the above <resist pattern formation> were measured with a length measurement SEM (scanning electron microscope, acceleration voltage 300 V, trade name: S-9380, manufactured by Hitachi High-Technologies Corporation). Observed from above, the distance from the center of each hole to the outer edge was measured in 24 directions. A triple value (3σ) of the standard deviation (σ) calculated from the measurement result was obtained. This is shown in Table 2 as “Circularity (nm)”.
The 3σ obtained in this way means that the smaller the value, the higher the roundness of the hole.

  From the results shown in Table 2, according to the resist composition of Example 1 to which the present invention was applied, higher sensitivity and improved lithographic properties can be achieved compared to the resist compositions of Comparative Examples 1 to 4, which is better. It can be confirmed that a resist pattern having a shape can be formed.

Claims (5)

A resist composition that generates an acid upon exposure and changes its solubility in a developer due to the action of the acid,
Containing a base component (A) whose solubility in a developer is changed by the action of an acid,
The said base material component (A) contains the high molecular compound (A1) which has a structural unit (a0) represented by the following general formula (a0-1), The resist composition characterized by the above-mentioned.

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ⁰ is a divalent hydrocarbon group which may have an ether bond. n _a0 is an integer of 0-2. Ra ⁰⁰ is an acid dissociable group represented by general formula (a0-r1-1). Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent. However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group. * Represents a bond. ]   The resist composition according to claim 1, wherein the proportion of the structural unit (a0) is 10 to 70 mol% with respect to the total of all the structural units constituting the polymer compound (A1).   A step of forming a resist film using the resist composition according to claim 1 on the support, a step of exposing the resist film, and developing the resist film after the exposure to form a resist pattern A resist pattern forming method comprising a step. The high molecular compound which has a structural unit (a0) represented by the following general formula (a0-1).

[In formula, R is a hydrogen atom, a C1-C5 alkyl group, or a C1-C5 halogenated alkyl group. Va ⁰ is a divalent hydrocarbon group which may have an ether bond. n _a0 is an integer of 0-2. Ra ⁰⁰ is an acid dissociable group represented by general formula (a0-r1-1). Ra ⁰¹ is a hydrocarbon group which may have a substituent. Ra ⁰² is a hydrocarbon group that may have a substituent. Ra ⁰¹ and Ra ⁰² may be bonded to each other to form a ring structure. Ya ⁰ is a quaternary carbon atom. Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ are each independently a hydrocarbon group which may have a substituent. However, at least one of Ra ⁰³¹ , Ra ⁰³² and Ra ⁰³³ is a hydrocarbon group having at least a polar group. ]   The polymer compound according to claim 4, wherein the proportion of the structural unit (a0) is 20 to 50 mol% with respect to the total of all the structural units constituting the polymer compound.