JP2017223957A - Adhesive polarizing plate and image display device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an adhesive polarizing plate which includes an adhesive layer having an antistatic function and satisfying durability and whose optical properties are hardly degraded.SOLUTION: An adhesive polarizing plate includes: a polarizing plate; and an adhesive layer provided on the polarizing plate. The polarizing plate includes a transparent protective film on only one side of a polarizer. The adhesive layer is provided on the polarizer on a side where the transparent protective film is absent. The adhesive layer is made of an adhesive composition containing a (meth)acryl-based polymer (A) and alkali metal salt (B).SELECTED DRAWING: None

Description

  The present invention relates to a polarizing plate and an adhesive polarizing plate having an adhesive layer provided on the polarizing plate. Furthermore, the present invention relates to an image display device such as a liquid crystal display device, an organic EL display device, and a PDP using the adhesive polarizing plate.

  In a liquid crystal display device or the like, it is indispensable to dispose polarizing elements on both sides of a liquid crystal cell because of its image forming method, and generally a polarizing plate is attached. When sticking the said polarizing plate to a liquid crystal cell, an adhesive is normally used. Further, the adhesion between the polarizing plate and the liquid crystal cell is usually in close contact with each other using an adhesive in order to reduce the loss of light. In such a case, since the adhesive has the merit that a drying step is not required to fix the polarizing plate, the adhesive is an adhesive polarizing plate provided as an adhesive layer in advance on one side of the polarizing plate. Generally used. A release film is usually attached to the pressure-sensitive adhesive layer of the pressure-sensitive adhesive polarizing plate.

  During the production of a liquid crystal display device, when the pressure-sensitive adhesive polarizing plate is attached to a liquid crystal cell, the release film is peeled off from the pressure-sensitive adhesive layer of the pressure-sensitive adhesive polarizing plate, and static electricity is generated by the peeling of the release film. . The static electricity generated in this way affects the orientation of the liquid crystal inside the liquid crystal display device, leading to defects. Further, display unevenness due to static electricity may occur when the liquid crystal display device is used. The generation of static electricity can be suppressed, for example, by forming an antistatic layer on the outer surface of the polarizing plate, but the effect is small and there is a problem that the generation of static electricity cannot be fundamentally prevented. Therefore, in order to suppress the occurrence of static electricity at a fundamental position, it is required to provide an antistatic function to the adhesive layer. As means for imparting an antistatic function to the pressure-sensitive adhesive layer, for example, it has been proposed to blend an ionic compound into the pressure-sensitive adhesive forming the pressure-sensitive adhesive layer (Patent Documents 1 to 4). Patent Document 1 is a lithium salt, Patent Document 2 is at least one of an alkali metal salt and an alkaline earth metal salt, Patent Document 3 is an ionic compound having an organic cation and is solid at room temperature, and Patent Document 4 is an imidazolium cation. And blending an ionic solid containing an inorganic anion into an acrylic pressure-sensitive adhesive used for a polarizing plate. In addition, a method of providing an antistatic layer between a polarizing plate and an adhesive layer using a binder of a conductive polymer such as polythiophene has been proposed (Patent Document 5). Further, the adhesive polarizing plate is required to have durability in an adhesive state.

JP 2010-189489 A JP 2010-065217 A JP 2010-0666756 A JP 2009-251281 A JP 2003-246874 A

  In Patent Documents 1 to 4, an antistatic function is imparted by applying a pressure-sensitive adhesive layer formed of a pressure-sensitive adhesive composition containing an ionic compound to a polarizing plate. As the polarizing plates applied in Patent Documents 1 to 4, those having protective substrates such as transparent protective films on both sides of the polarizer are used.

  On the other hand, as an adhesive polarizing plate, an adhesive polarizing plate provided with an adhesive layer may be used without providing a transparent protective film only on one side of the polarizer and without providing a transparent protective film on the other side. Such an adhesive polarizing plate has a transparent protective film only on one side, so the cost for one layer of the transparent protective film can be reduced compared to the case where the transparent protective film is provided on both sides. In the case where an antistatic function is provided by adding ionic compound, the influence of the ionic compound in the pressure-sensitive adhesive layer on the polarizer is large. For example, when an ionic liquid and an ionic solid are used as the ionic compound However, there is a problem that the optical characteristics are greatly deteriorated after the humidification test by degrading the polarizer.

  Also, as in Patent Document 5, when a layer containing a conductive polymer such as polythiophene is provided on the polarizing plate and the pressure-sensitive adhesive layer, the polarizer is deteriorated and the optical characteristics are lowered.

  An object of the present invention is to provide a pressure-sensitive adhesive polarizing plate having an antistatic function and having a pressure-sensitive adhesive layer satisfying durability and having little deterioration in optical properties.

  Another object of the present invention is to provide an image display device using the pressure-sensitive adhesive polarizing plate.

  As a result of intensive studies to solve the above problems, the present inventors have found the following pressure-sensitive adhesive polarizing plate and have completed the present invention.

That is, the present invention is a pressure-sensitive adhesive polarizing plate having a polarizing plate and a pressure-sensitive adhesive layer provided on the polarizing plate,
The polarizing plate has a transparent protective film only on one side of the polarizer, the adhesive layer is provided on the polarizer on the side not having the transparent protective film, and the adhesive layer is (meta The present invention relates to a pressure-sensitive adhesive polarizing plate characterized by being formed from a pressure-sensitive adhesive composition containing an acrylic polymer (A) and an alkali metal salt (B).

  In the pressure-sensitive adhesive polarizing plate, the alkali metal salt (B) is preferably a lithium salt.

  The pressure-sensitive adhesive polarizing plate preferably contains 0.0001 to 5 parts by weight of the alkali metal salt (B) with respect to 100 parts by weight of the (meth) acrylic polymer (A).

  In the adhesive polarizing plate, a polarizer having a thickness of 10 μm or less can be used. The polarizer having a thickness of 10 μm or less is a continuous web polarizing film made of a polyvinyl alcohol resin in which a dichroic material is oriented, and includes a polyvinyl alcohol resin layer formed on a thermoplastic resin substrate. What was obtained by extending | stretching a laminated body by the two-stage extending | stretching process which consists of an air auxiliary | assistant extending | stretching and boric-acid-water extending | stretching can be used.

  In the pressure-sensitive adhesive polarizing plate, as the (meth) acrylic polymer (A), a monomer unit containing an alkyl (meth) acrylate and a hydroxyl group-containing monomer can be preferably used.

  In the above-mentioned pressure-sensitive adhesive polarizing plate, the (meth) acrylic polymer (A) may preferably be one containing an alkyl (meth) acrylate and a carboxyl group-containing monomer as monomer units.

  In the pressure-sensitive adhesive polarizing plate, the pressure-sensitive adhesive composition may further contain a crosslinking agent. In the pressure-sensitive adhesive composition, the crosslinking agent (C) is preferably contained in an amount of 0.01 to 20 parts by weight with respect to 100 parts by weight of the (meth) acrylic polymer (A). The crosslinking agent (C) is preferably at least one selected from an isocyanate compound and a peroxide.

  In the pressure-sensitive adhesive polarizing plate, 0.001 to 5 parts by weight of the silane coupling agent (D) can be further contained with respect to 100 parts by weight of the (meth) acrylic polymer (A).

  In the pressure-sensitive adhesive polarizing plate, 0.001 to 10 parts by weight of a polyether-modified silicone compound can be further contained with respect to 100 parts by weight of the (meth) acrylic polymer (A).

  In the pressure-sensitive adhesive polarizing plate, the (meth) acrylic polymer (A) preferably has a weight average molecular weight of 500,000 to 3,000,000.

  The said adhesive type polarizing plate can have an easily bonding layer between a polarizing plate and an adhesive layer.

  The present invention also relates to an image display device using at least one of the pressure-sensitive adhesive polarizing plates.

  In an adhesive using an acrylic polymer as a base polymer, an antistatic function can be imparted by adding an ionic compound to the adhesive. In this case, it is considered that the antistatic function is efficiently expressed by bleeding out of the ionic compound on the surface of the pressure-sensitive adhesive layer. On the other hand, when the ionic compound is in contact with the polarizer, optical characteristics such as the degree of polarization may be deteriorated.

  The pressure-sensitive adhesive composition for forming the pressure-sensitive adhesive layer of the pressure-sensitive adhesive polarizing plate of the present invention is an alkali metal salt that can impart an antistatic function in addition to the (meth) acrylic polymer (A) that is a base polymer. The pressure-sensitive adhesive layer containing (B) and formed of the pressure-sensitive adhesive composition is excellent in antistatic function. Moreover, in this invention, it turned out that an antistatic function can be provided by using an alkali metal salt (B), without causing deterioration of a polarizer.

  The pressure-sensitive adhesive composition forming the pressure-sensitive adhesive layer of the pressure-sensitive adhesive polarizing plate of the present invention contains a (meth) acrylic polymer (A) as a base polymer. The (meth) acrylic polymer (A) usually contains an alkyl (meth) acrylate as a main component as a monomer unit. (Meth) acrylate refers to acrylate and / or methacrylate, and (meth) of the present invention has the same meaning.

  Examples of the alkyl (meth) acrylate constituting the main skeleton of the (meth) acrylic polymer (A) include linear or branched alkyl groups having 1 to 18 carbon atoms. For example, the alkyl group includes methyl group, ethyl group, propyl group, isopropyl group, butyl group, isobutyl group, amyl group, hexyl group, cyclohexyl group, heptyl group, 2-ethylhexyl group, isooctyl group, nonyl group, decyl group. Group, isodecyl group, dodecyl group, isomyristyl group, lauryl group, tridecyl group, pentadecyl group, hexadecyl group, heptadecyl group, octadecyl group, and the like. These can be used alone or in combination. The average carbon number of these alkyl groups is preferably 3-9.

  In addition, alkyl (meth) acrylates containing aromatic rings such as phenoxyethyl (meth) acrylate and benzyl (meth) acrylate are used from the viewpoints of adhesive properties, durability, retardation adjustment, refractive index adjustment, and the like. be able to. The alkyl (meth) acrylate containing an aromatic ring can be used by mixing a polymer obtained by polymerizing it with the (meth) acrylic polymer exemplified above, but from the viewpoint of transparency, it contains an aromatic ring. The alkyl (meth) acrylate is preferably copolymerized with the alkyl (meth) acrylate.

  The ratio of the alkyl (meth) acrylate containing the aromatic ring in the (meth) acrylic polymer (A) is 50 in the weight ratio of all the constituent monomers (100 wt%) of the (meth) acrylic polymer (A). It can contain in the ratio of the weight% or less. Furthermore, the content of the alkyl (meth) acrylate containing an aromatic ring is preferably 1 to 35% by weight, more preferably 1 to 20% by weight, further preferably 7 to 18% by weight, and further 10 to 16%. % By weight is preferred.

  The (meth) acrylic polymer (A) has a polymerizable functional group having an unsaturated double bond such as a (meth) acryloyl group or a vinyl group for the purpose of improving adhesiveness and heat resistance. One or more copolymerization monomers can be introduced by copolymerization. Specific examples of such copolymerization monomers include, for example, 2-hydroxyethyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, (meth) acrylic acid 6 Hydroxyl group-containing monomers such as hydroxyhexyl, 8-hydroxyoctyl (meth) acrylate, 10-hydroxydecyl (meth) acrylate, 12-hydroxylauryl (meth) acrylate and (4-hydroxymethylcyclohexyl) -methyl acrylate Carboxyl group-containing monomers such as (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, itaconic acid, maleic acid, fumaric acid and crotonic acid; acid anhydrides such as maleic anhydride and itaconic anhydride Monomer-containing monomer; Caprolac of acrylic acid Adducts such as styrene sulfonic acid, allyl sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid, (meth) acrylamide propane sulfonic acid, sulfopropyl (meth) acrylate, (meth) acryloyloxynaphthalene sulfonic acid, etc. A sulfonic acid group-containing monomer, and a phosphoric acid group-containing monomer such as 2-hydroxyethylacryloyl phosphate.

  In addition, (N-substituted) amides such as (meth) acrylamide, N, N-dimethyl (meth) acrylamide, N-butyl (meth) acrylamide, N-methylol (meth) acrylamide, N-methylolpropane (meth) acrylamide, etc. Monomer; (meth) acrylic acid aminoethyl, (meth) acrylic acid N, N-dimethylaminoethyl, (meth) acrylic acid t-butylaminoethyl and other (meth) acrylic acid alkylaminoalkyl monomers; (meth) acrylic (Meth) acrylic acid alkoxyalkyl monomers such as methoxyethyl acid and ethoxyethyl (meth) acrylate; N- (meth) acryloyloxymethylenesuccinimide, N- (meth) acryloyl-6-oxyhexamethylenesuccinimide, N- ( (Meta) acryloyl- -Succinimide monomers such as oxyoctamethylene succinimide and N-acryloylmorpholine; Maleimide monomers such as N-cyclohexylmaleimide, N-isopropylmaleimide, N-laurylmaleimide and N-phenylmaleimide; N-methylitaconimide, N-ethyl Itaconimide monomers such as itaconimide, N-butylitaconimide, N-octylitaconimide, N-2-ethylhexylitaconimide, N-cyclohexylitaconimide, N-laurylitaconimide, and the like are listed as examples of monomers for modification purposes. It is done.

  Further, as modifying monomers, vinyl acetate, vinyl propionate, N-vinyl pyrrolidone, methyl vinyl pyrrolidone, vinyl pyridine, vinyl piperidone, vinyl pyrimidine, vinyl piperazine, vinyl pyrazine, vinyl pyrrole, vinyl imidazole, vinyl oxazole, vinyl morpholine, N- Vinyl monomers such as vinylcarboxylic acid amides, styrene, α-methylstyrene, N-vinylcaprolactam; cyanoacrylate monomers such as acrylonitrile and methacrylonitrile; epoxy group-containing acrylic monomers such as glycidyl (meth) acrylate; (Meth) acrylic acid polyethylene glycol, (meth) acrylic acid polypropylene glycol, (meth) acrylic acid methoxyethylene glycol, (meth) acrylic acid meth Glycol acrylic ester monomers such as polypropylene glycol; acrylic acid ester monomers such as tetrahydrofurfuryl (meth) acrylate, fluorine (meth) acrylate, silicone (meth) acrylate and 2-methoxyethyl acrylate may also be used. it can. Furthermore, isoprene, butadiene, isobutylene, vinyl ether and the like can be mentioned.

  Furthermore, examples of the copolymerizable monomer other than the above include silane-based monomers containing silicon atoms. Examples of the silane monomer include 3-acryloxypropyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, 4-vinylbutyltrimethoxysilane, 4-vinylbutyltriethoxysilane, and 8-vinyloctyltrimethoxysilane. , 8-vinyloctyltriethoxysilane, 10-methacryloyloxydecyltrimethoxysilane, 10-acryloyloxydecyltrimethoxysilane, 10-methacryloyloxydecyltriethoxysilane, 10-acryloyloxydecyltriethoxysilane, and the like.

  Moreover, as a copolymerization monomer, tripropylene glycol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, bisphenol A diglycidyl ether di (meth) acrylate, neodymium Pentyl glycol di (meth) acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate (Meth) acryloyl such as esterified product of (meth) acrylic acid and polyhydric alcohol such as caprolactone-modified dipentaerythritol hexa (meth) acrylate , Polyfunctional monomers having two or more unsaturated double bonds such as vinyl groups, and unsaturated groups such as (meth) acryloyl groups and vinyl groups as functional groups similar to monomer components in the backbone of polyester, epoxy, urethane, etc. Polyester (meth) acrylate, epoxy (meth) acrylate, urethane (meth) acrylate and the like to which two or more double bonds are added can also be used.

  The (meth) acrylic polymer (A) is mainly composed of alkyl (meth) acrylate in the weight ratio of all constituent monomers, and the proportion of the copolymerized monomer in the (meth) acrylic polymer (A) is particularly limited. However, the ratio of the copolymerization monomer is preferably about 0 to 20%, about 0.1 to 15%, and more preferably about 0.1 to 10% in the weight ratio of all the constituent monomers.

  Among these copolymer monomers, a hydroxyl group-containing monomer and a carboxyl group-containing monomer are preferably used from the viewpoint of adhesiveness and durability. A hydroxyl group-containing monomer and a carboxyl group-containing monomer can be used in combination. These copolymerization monomers serve as reaction points with the crosslinking agent when the pressure-sensitive adhesive composition contains a crosslinking agent. Since a hydroxyl group-containing monomer, a carboxyl group-containing monomer, and the like are rich in reactivity with an intermolecular crosslinking agent, they are preferably used for improving the cohesiveness and heat resistance of the resulting pressure-sensitive adhesive layer. A hydroxyl group-containing monomer is preferable from the viewpoint of reworkability, and a carboxyl group-containing monomer is preferable from the viewpoint of achieving both durability and reworkability.

  When the hydroxyl group-containing monomer is contained as a copolymerization monomer, the proportion is preferably 0.01 to 15% by weight, more preferably 0.03 to 10% by weight, and further preferably 0.05 to 7% by weight. . When a carboxyl group-containing monomer is contained as a copolymerization monomer, the proportion is preferably 0.05 to 10% by weight, more preferably 0.1 to 8% by weight, and further preferably 0.2 to 6% by weight. .

  As the (meth) acrylic polymer (A) of the present invention, those having a weight average molecular weight in the range of 500,000 to 3,000,000 are usually used. In view of durability, particularly heat resistance, it is preferable to use those having a weight average molecular weight of 700,000 to 2,700,000. Furthermore, it is preferable that it is 800,000-2.5 million. A weight average molecular weight of less than 500,000 is not preferable in terms of heat resistance. On the other hand, if the weight average molecular weight is more than 3 million, a large amount of dilution solvent is required to adjust the viscosity for coating, which is not preferable. The weight average molecular weight is a value measured by GPC (gel permeation chromatography) and calculated in terms of polystyrene.

  For the production of such a (meth) acrylic polymer (A), known production methods such as solution polymerization, bulk polymerization, emulsion polymerization, and various radical polymerizations can be appropriately selected. Further, the (meth) acrylic polymer (A) to be obtained may be any of a random copolymer, a block copolymer, a graft copolymer and the like.

  In solution polymerization, for example, ethyl acetate, toluene or the like is used as a polymerization solvent. As a specific example of solution polymerization, the reaction is performed under an inert gas stream such as nitrogen, and a polymerization initiator is added, and the reaction is usually performed at about 50 to 70 ° C. under reaction conditions of about 5 to 30 hours.

  The polymerization initiator, chain transfer agent, emulsifier and the like used for radical polymerization are not particularly limited and can be appropriately selected and used. In addition, the weight average molecular weight of the (meth) acrylic polymer (A) can be controlled by the amount of polymerization initiator, the amount of chain transfer agent used, and the reaction conditions, and the amount used is appropriately adjusted according to these types. The

  Examples of the polymerization initiator include 2,2′-azobisisobutyronitrile, 2,2′-azobis (2-amidinopropane) dihydrochloride, 2,2′-azobis [2- (5-methyl-2). -Imidazolin-2-yl) propane] dihydrochloride, 2,2'-azobis (2-methylpropionamidine) disulfate, 2,2'-azobis (N, N'-dimethyleneisobutylamidine), 2,2 '-Azobis [N- (2-carboxyethyl) -2-methylpropionamidine] hydrate (manufactured by Wako Pure Chemical Industries, VA-057) and other azo initiators, and persulfates such as potassium persulfate and ammonium persulfate , Di (2-ethylhexyl) peroxydicarbonate, di (4-t-butylcyclohexyl) peroxydicarbonate, di-sec-butyl -Oxydicarbonate, t-butylperoxyneodecanoate, t-hexylperoxypivalate, t-butylperoxypivalate, dilauroyl peroxide, di-n-octanoyl peroxide, 1,1,3 , 3-tetramethylbutylperoxy-2-ethylhexanoate, di (4-methylbenzoyl) peroxide, dibenzoyl peroxide, t-butylperoxyisobutyrate, 1,1-di (t-hexylperoxy) ) Peroxides such as cyclohexane, t-butyl hydroperoxide, hydrogen peroxide, peroxides and sodium bisulfite, peroxides and sodium ascorbate Redox initiators combined with Not intended to be.

  The polymerization initiator may be used alone or in combination of two or more, but the total content is 0.005 to 1 part by weight with respect to 100 parts by weight of the monomer. Is preferably about 0.02 to 0.5 parts by weight.

  In order to produce the (meth) acrylic polymer (A) having the weight average molecular weight using, for example, 2,2′-azobisisobutyronitrile as the polymerization initiator, the amount of the polymerization initiator used Is preferably about 0.06 to 0.2 parts by weight, more preferably about 0.08 to 0.175 parts by weight, based on 100 parts by weight of the total amount of monomer components.

  Examples of the chain transfer agent include lauryl mercaptan, glycidyl mercaptan, mercaptoacetic acid, 2-mercaptoethanol, thioglycolic acid, 2-ethylhexyl thioglycolate, and 2,3-dimercapto-1-propanol. The chain transfer agent may be used alone or in combination of two or more, but the total content is 0.1 parts by weight with respect to 100 parts by weight of the total amount of monomer components. Less than or equal to

  Examples of the emulsifier used in emulsion polymerization include anionic emulsifiers such as sodium lauryl sulfate, ammonium lauryl sulfate, sodium dodecylbenzenesulfonate, ammonium polyoxyethylene alkyl ether sulfate, sodium polyoxyethylene alkyl phenyl ether sulfate, and polyoxy Nonionic emulsifiers such as ethylene alkyl ether, polyoxyethylene alkyl phenyl ether, polyoxyethylene fatty acid ester, and polyoxyethylene-polyoxypropylene block polymer are exemplified. These emulsifiers may be used alone or in combination of two or more.

  Further, as reactive emulsifiers, as emulsifiers into which radical polymerizable functional groups such as propenyl groups and allyl ether groups are introduced, specifically, for example, Aqualon HS-10, HS-20, KH-10, BC-05 BC-10, BC-20 (all of which are manufactured by Daiichi Kogyo Seiyaku Co., Ltd.), Adekaria soap SE10N (manufactured by Asahi Denka Kogyo Co., Ltd.), and the like. Reactive emulsifiers are preferable because they are incorporated into the polymer chain after polymerization and thus have improved water resistance. The amount of the emulsifier used is more preferably 0.3 to 5 parts by weight and 0.5 to 1 part by weight from the viewpoint of polymerization stability and mechanical stability with respect to 100 parts by weight of the total amount of monomer components.

  The pressure-sensitive adhesive composition of the present invention contains an alkali metal salt (B) in addition to the (meth) acrylic polymer (A). The alkali metal salt (B) can be used alone or in combination. As the alkali metal salt (B), organic salts and inorganic salts of alkali metals can be used.

  Examples of the alkali metal ions constituting the cation part of the alkali metal salt (B) include lithium, sodium, and potassium ions. Of these alkali metal ions, lithium ions are preferred.

The anion portion of the alkali metal salt (B) may be composed of an organic material or an inorganic material. Examples of the anion part constituting the organic salt include CH ₃ COO ⁻ , CF ₃ COO ⁻ , CH ₃ SO ₃ ⁻ , CF ₃ SO ₃ ⁻ , (CF ₃ SO ₂ ) ₂ N ⁻ , and (CF ₃ SO ₂ ). ^{_{3 C -, C 4 F 9}} SO 3 -, (C 2 F 5 SO 2) 2 N -, C 3 F 7 COO -, (CF 3 SO 2) (CF 3 CO) N -, - O 3 S ( CF ₂ ) ₃ SO ₃ ⁻ , PF ₆ ⁻ , CO ₃ ²⁻ , and the like are used. In particular, an anion moiety containing a fluorine atom is preferably used because an ionic compound having good ion dissociation properties can be obtained. The anion part constituting the inorganic salt includes Cl ⁻ , Br ⁻ , I ⁻ , AlCl ₄ ⁻ , Al ₂ Cl ₇ ⁻ , BF ₄ ⁻ , PF ₆ ⁻ , ClO ₄ ⁻ , NO ₃ ⁻ , AsF ₆ ⁻ , SbF. ₆ ⁻ , NbF ₆ ⁻ , TaF ₆₋ , (CN) ₂ N ⁻ , and the like are used. As the anion moiety, (perfluoroalkylsulfonyl) imide such as (CF ₃ SO ₂ ) ₂ N ⁻ and (C ₂ F ₅ SO ₂ ) ₂ N ^— is preferable, and particularly represented by (CF ₃ SO ₂ ) ₂ N ⁻ . (Trifluoromethanesulfonyl) imide is preferred.

Specific examples of the alkali metal organic salt include sodium acetate, sodium alginate, sodium lignin sulfonate, sodium toluenesulfonate, LiCF ₃ SO ₃ , Li (CF ₃ SO ₂ ) ₂ N, Li (CF ₃ SO ₂ ) ₂ N, Li (C ₂ F ₅ SO ₂ ) ₂ N, Li (C ₄ F ₉ SO ₂ ) ₂ N, Li (CF ₃ SO ₂ ) ₃ C, KO ₃ S (CF ₂ ) ₃ SO ₃ K, _{LiO 3 S (CF 2) 3} SO 3 K , and the like, among these _{LiCF 3 SO 3, Li (CF} 3 SO 2) 2 N, Li (C 2 F 5 SO 2) 2 N, Li (C 4 F ₉ SO ₂ ) ₂ N, Li (CF ₃ SO ₂ ) ₃ C and the like are preferable, and Li (CF ₃ SO ₂ ) ₂ N, Li (C ₂ F ₅ SO ₂ ) ₂ N, Li (C ₄ F ₉ SO _{2) 2} Fluorine-containing lithium imide salt is more preferably equal, particularly (perfluoroalkyl sulfonyl) imide lithium salts are preferred.

  Examples of the alkali metal inorganic salt include lithium perchlorate and lithium iodide.

  As for the ratio of the alkali metal salt (B) in the adhesive composition of this invention, 0.001-5 weight part is preferable with respect to 100 weight part of (meth) acrylic-type polymers (A). When the alkali metal salt (B) is less than 0.001 part by weight, the effect of improving the antistatic performance may not be sufficient. The alkali metal salt (B) is preferably 0.01 parts by weight or more, and more preferably 0.1 parts by weight or more. On the other hand, if the amount of the alkali metal salt (B) is more than 5 parts by weight, the durability may not be sufficient. The alkali metal salt (B) is preferably 3 parts by weight or less, and more preferably 1 part by weight or less. The ratio of the alkali metal salt (B) can be set within a preferable range by adopting the upper limit value or the lower limit value.

  Furthermore, the pressure-sensitive adhesive composition of the present invention can contain a crosslinking agent (C). As the crosslinking agent (C), an organic crosslinking agent or a polyfunctional metal chelate can be used. Examples of the organic crosslinking agent include an isocyanate crosslinking agent, a peroxide crosslinking agent, an epoxy crosslinking agent, and an imine crosslinking agent. A polyfunctional metal chelate is one in which a polyvalent metal is covalently or coordinately bonded to an organic compound. Examples of polyvalent metal atoms include Al, Cr, Zr, Co, Cu, Fe, Ni, V, Zn, In, Ca, Mg, Mn, Y, Ce, Sr, Ba, Mo, La, Sn, Ti, and the like. Can be mentioned. Examples of the atom in the organic compound that is covalently bonded or coordinated include an oxygen atom, and examples of the organic compound include an alkyl ester, an alcohol compound, a carboxylic acid compound, an ether compound, and a ketone compound.

  As the crosslinking agent (C), an isocyanate-based crosslinking agent and / or a peroxide-type crosslinking agent is preferable. Examples of the compounds related to the isocyanate-based crosslinking agent include isocyanate monomers such as tolylene diisocyanate, chlorophenylene diisocyanate, tetramethylene diisocyanate, xylylene diisocyanate, diphenylmethane diisocyanate, hydrogenated diphenylmethane diisocyanate, and these isocyanate monomers. Examples include isocyanate compounds added with trimethylolpropane, isocyanurates, burette compounds, and urethane prepolymer isocyanates such as polyether polyols, polyester polyols, acrylic polyols, polybutadiene polyols, and polyisoprene polyols that have undergone addition reactions. be able to. Particularly preferred is a polyisocyanate compound, which is one or a polyisocyanate compound derived from one selected from the group consisting of hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate. Here, hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, isophorone diisocyanate, polyol-modified is selected from the group consisting of hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate or a polyisocyanate compound derived therefrom. Examples include hexamethylene diisocyanate, polyol-modified hydrogenated xylylene diisocyanate, trimer-type hydrogenated xylylene diisocyanate, and polyol-modified isophorone diisocyanate. The exemplified polyisocyanate compound is preferable because the reaction with a hydroxyl group proceeds rapidly, particularly using an acid or base contained in the polymer as a catalyst, and thus contributes to the speed of crosslinking.

  As the peroxide, any radical active species can be used as long as it generates radical active species by heating or light irradiation to advance the crosslinking of the base polymer of the pressure-sensitive adhesive composition. However, in consideration of workability and stability. It is preferable to use a peroxide having a one-minute half-life temperature of 80 ° C. to 160 ° C., and more preferable to use a peroxide having a 90 ° C. to 140 ° C.

  Examples of peroxides that can be used include di (2-ethylhexyl) peroxydicarbonate (1 minute half-life temperature: 90.6 ° C.), di (4-t-butylcyclohexyl) peroxydicarbonate (1 Minute half-life temperature: 92.1 ° C.), di-sec-butyl peroxydicarbonate (1 minute half-life temperature: 92.4 ° C.), t-butyl peroxyneodecanoate (1 minute half-life temperature: 103 0.5 ° C), t-hexyl peroxypivalate (1 minute half-life temperature: 109.1 ° C), t-butyl peroxypivalate (1 minute half-life temperature: 110.3 ° C), dilauroyl peroxide ( 1 minute half-life temperature: 116.4 ° C.), di-n-octanoyl peroxide (1 minute half-life temperature: 117.4 ° C.), 1,1,3,3-tetramethylbutyl Oxy-2-ethylhexanoate (1 minute half-life temperature: 124.3 ° C), di (4-methylbenzoyl) peroxide (1 minute half-life temperature: 128.2 ° C), dibenzoyl peroxide (half-minute for 1 minute) Period temperature: 130.0 ° C.), t-butyl peroxyisobutyrate (1 minute half-life temperature: 136.1 ° C.), 1,1-di (t-hexylperoxy) cyclohexane (1 minute half-life temperature: 149.2 ° C.). Especially, since the crosslinking reaction efficiency is excellent, di (4-t-butylcyclohexyl) peroxydicarbonate (1 minute half-life temperature: 92.1 ° C.), dilauroyl peroxide (1 minute half-life temperature: 116. 4 ° C), dibenzoyl peroxide (1 minute half-life temperature: 130.0 ° C) and the like are preferably used.

  The peroxide half-life is an index representing the decomposition rate of the peroxide, and means the time until the remaining amount of peroxide is reduced to half. The decomposition temperature for obtaining a half-life at an arbitrary time and the half-life time at an arbitrary temperature are described in the manufacturer catalog, for example, “Organic peroxide catalog 9th edition by Nippon Oil & Fats Co., Ltd.” (May 2003) ".

  The amount of the crosslinking agent (C) used is preferably 0.01 to 20 parts by weight, more preferably 0.03 to 10 parts by weight, with respect to 100 parts by weight of the (meth) acrylic polymer (A). If the crosslinking agent (C) is less than 0.01 parts by weight, the cohesive force of the pressure-sensitive adhesive tends to be insufficient, and foaming may occur during heating. On the other hand, if it exceeds 20 parts by weight, the moisture resistance is sufficient. Instead, peeling easily occurs in a reliability test or the like.

  The isocyanate-based crosslinking agent may be used singly or as a mixture of two or more, but the total content thereof is the (meth) acrylic polymer (A) 100 The polyisocyanate compound crosslinking agent is preferably contained in an amount of 0.01 to 2 parts by weight, more preferably 0.02 to 2 parts by weight, more preferably 0.05 to 1.5 parts by weight. More preferably, it is contained in parts by weight. It can be appropriately contained in consideration of cohesive force and prevention of peeling in a durability test.

  The peroxide may be used alone or as a mixture of two or more, but the total content is 100 weight of the (meth) acrylic polymer (A). The content of the peroxide is 0.01 to 2 parts by weight, preferably 0.04 to 1.5 parts by weight, more preferably 0.05 to 1 part by weight. . In order to adjust processability, reworkability, cross-linking stability, peelability, and the like, it is appropriately selected within this range.

  In addition, as a measuring method of the peroxide decomposition amount which remained after the reaction process, it can measure by HPLC (high performance liquid chromatography), for example.

  More specifically, for example, about 0.2 g of the pressure-sensitive adhesive composition after the reaction treatment is taken out, immersed in 10 ml of ethyl acetate, extracted by shaking at 25 ° C. and 120 rpm for 3 hours with a shaker, and then at room temperature. Leave for 3 days. Next, 10 ml of acetonitrile was added, shaken at 120 rpm at 25 ° C. for 30 minutes, and about 10 μl of the extract obtained by filtration through a membrane filter (0.45 μm) was injected into the HPLC for analysis. The amount of peroxide can be set.

  Furthermore, the pressure-sensitive adhesive composition of the present invention can contain a silane coupling agent (D). The durability can be improved by using the silane coupling agent (D). Specific examples of the silane coupling agent include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropylmethyldiethoxysilane, 2- (3, Epoxy group-containing silane coupling agents such as 4-epoxycyclohexyl) ethyltrimethoxysilane, 3-aminopropyltrimethoxysilane, N-2- (aminoethyl) -3-aminopropylmethyldimethoxysilane, 3-triethoxysilyl- Amino group-containing silane coupling agents such as N- (1,3-dimethylbutylidene) propylamine, N-phenyl-γ-aminopropyltrimethoxysilane, 3-acryloxypropyltrimethoxysilane, 3-methacryloxypropyltri (Meth) a, such as ethoxysilane Lil group-containing silane coupling agents, such as isocyanate group-containing silane coupling agents such as 3-isocyanate propyl triethoxysilane and the like.

  The silane coupling agent (D) may be used alone or as a mixture of two or more, but the total content thereof is the (meth) acrylic polymer (A) 100. The silane coupling agent is preferably 0.001 to 5 parts by weight, more preferably 0.01 to 1 part by weight, still more preferably 0.02 to 1 part by weight, and more preferably 0.05 to part by weight. -0.6 parts by weight are preferred. It is an amount that improves durability and appropriately maintains the adhesive force to an optical member such as a liquid crystal cell.

  Furthermore, a polyether-modified silicone compound can be blended in the pressure-sensitive adhesive composition of the present invention. As the polyether-modified silicone compound, for example, those disclosed in JP 2010-275522 A can be used.

The polyether-modified silicone compound has a polyether skeleton, and at least one terminal has the following general formula (1): -SiR _a M _3-a
(In the formula, R is a monovalent organic group having 1 to 20 carbon atoms which may have a substituent, M is a hydroxyl group or a hydrolyzable group, and a is an integer of 1 to 3. However, when a plurality of R are present, the plurality of R may be the same or different from each other, and when a plurality of M are present, the plurality of M may be the same or different from each other. It has a reactive silyl group represented.

As the polyether-modified silicone compound,
Formula _{(2): R a M 3} -a Si-X-Y- (AO) n -Z
(In the formula, R is a monovalent organic group having 1 to 20 carbon atoms which may have a substituent, M is a hydroxyl group or a hydrolyzable group, and a is an integer of 1 to 3. However, when a plurality of R are present, the plurality of R may be the same or different from each other, and when a plurality of M are present, the plurality of M may be the same or different from each other. Represents a linear or branched oxyalkylene group having 1 to 10 carbon atoms, n is 1 to 1700, and represents an average addition mole number of the oxyalkylene group, X is a linear or branched chain having 1 to 20 carbon atoms, Y represents a branched alkylene group, and Y represents an ether bond, an ester bond, a urethane bond, or a carbonate bond.
Z is a hydrogen atom, a monovalent hydrocarbon group having 1 to 10 carbon atoms,
Formula (2A): —Y ₁ —X—SiR _a M _3-a
(Wherein, R, M, and X are the same as above; Y ¹ represents a single bond, —CO— bond, —CONH— bond, or —COO— bond), or
Formula _{(2B): - Q {-} (OA) n -Y-X-SiR a M 3-a} m
(In the formula, R, M, X and Y are the same as described above. OA is the same as the above AO, n is the same as described above. Q is a divalent or higher valent hydrocarbon group having 1 to 10 carbon atoms. , M is the same as the valence of the hydrocarbon group. ).

  Specific examples of the polyether-modified silicone compound include, for example, Kaneka's MS polymers S203, S303, S810; SILYL EST250, EST280; SAT10, SAT200, SAT220, SAT350, SAT400, EXCESTARS 2410, S2420 or S3430, manufactured by Asahi Glass. Is mentioned.

  Furthermore, the pressure-sensitive adhesive composition of the present invention may contain other known additives, for example, a polyalkylene glycol polyether compound such as polypropylene glycol, a colorant, a powder such as a pigment, a dye, Surfactant, plasticizer, tackifier, surface lubricant, leveling agent, softener, antioxidant, anti-aging agent, light stabilizer, UV absorber, polymerization inhibitor, inorganic or organic filler, metal It can be added as appropriate according to the application in which powder, particles, foil, etc. are used. Moreover, you may employ | adopt the redox system which added a reducing agent within the controllable range.

  The pressure-sensitive adhesive composition forms a pressure-sensitive adhesive layer. In forming the pressure-sensitive adhesive layer, it is necessary to fully consider the influence of the crosslinking treatment temperature and the crosslinking treatment time as well as adjusting the addition amount of the entire crosslinking agent. preferable.

  The crosslinking treatment temperature and the crosslinking treatment time can be adjusted depending on the crosslinking agent used. The crosslinking treatment temperature is preferably 170 ° C. or lower.

  Moreover, this crosslinking process may be performed at the temperature at the time of the drying process of an adhesive layer, and you may carry out by providing a crosslinking process process separately after a drying process.

  The crosslinking treatment time can be set in consideration of productivity and workability, but is usually about 0.2 to 20 minutes, preferably about 0.5 to 10 minutes.

  In the pressure-sensitive adhesive polarizing plate of the present invention, a transparent protective film is provided only on one side of the polarizer, and a pressure-sensitive adhesive layer is formed on the polarizer with the pressure-sensitive adhesive composition without providing a transparent protective film on the other side. Is.

  As a method for forming the pressure-sensitive adhesive layer, for example, a method in which the pressure-sensitive adhesive composition is applied to a release-treated separator, and the polymerization solvent is dried and removed to form a pressure-sensitive adhesive layer, and then transferred to a polarizing plate, or The pressure-sensitive adhesive composition is prepared by applying the pressure-sensitive adhesive composition on a polarizing plate, drying and removing a polymerization solvent, and the like, and forming a pressure-sensitive adhesive layer on the polarizing plate. In applying the pressure-sensitive adhesive, one or more solvents other than the polymerization solvent may be added as appropriate.

  As the release-treated separator, a silicone release liner is preferably used. In the step of applying the adhesive composition of the present invention on such a liner and drying to form a pressure-sensitive adhesive layer, a method for drying the pressure-sensitive adhesive is appropriately employed depending on the purpose. obtain. Preferably, a method of heating and drying the coating film is used. The heat drying temperature is preferably 40 ° C to 200 ° C, more preferably 50 ° C to 180 ° C, and particularly preferably 70 ° C to 170 ° C. By setting the heating temperature within the above range, an adhesive having excellent adhesive properties can be obtained.

  As the drying time, an appropriate time can be adopted as appropriate. The drying time is preferably 5 seconds to 20 minutes, more preferably 5 seconds to 10 minutes, and particularly preferably 10 seconds to 5 minutes.

  In addition, the pressure-sensitive adhesive layer can be formed after forming an anchor layer on the surface of the polarizing plate or performing various easy adhesion treatments such as corona treatment and plasma treatment. Moreover, you may perform an easily bonding process on the surface of an adhesive layer.

  Various methods are used as a method of forming the pressure-sensitive adhesive layer. Specifically, for example, roll coat, kiss roll coat, gravure coat, reverse coat, roll brush, spray coat, dip roll coat, bar coat, knife coat, air knife coat, curtain coat, lip coat, die coater, etc. Examples thereof include an extrusion coating method.

  The thickness in particular of an adhesive layer is not restrict | limited, For example, it is about 1-100 micrometers. Preferably, it is 2-50 micrometers, More preferably, it is 2-40 micrometers, More preferably, it is 5-35 micrometers.

  When the pressure-sensitive adhesive layer is exposed, the pressure-sensitive adhesive layer may be protected with a sheet (separator) that has been subjected to a release treatment until practical use.

  Examples of the constituent material of the separator include, for example, plastic films such as polyethylene, polypropylene, polyethylene terephthalate, and polyester films, porous materials such as paper, cloth, and nonwoven fabric, nets, foam sheets, metal foils, and laminates thereof. Although a thin leaf body etc. can be mentioned, a plastic film is used suitably from the point which is excellent in surface smoothness.

  The plastic film is not particularly limited as long as it can protect the pressure-sensitive adhesive layer. For example, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a polymethylpentene film, a polyvinyl chloride film, and a vinyl chloride co-polymer are used. Examples thereof include a polymer film, a polyethylene terephthalate film, a polybutylene terephthalate film, a polyurethane film, and an ethylene-vinyl acetate copolymer film.

  The thickness of the separator is usually 5 to 200 μm, preferably about 5 to 100 μm. For the separator, if necessary, mold release and antifouling treatment with a silicone type, fluorine type, long chain alkyl type or fatty acid amide type release agent, silica powder, etc., coating type, kneading type, vapor deposition type It is also possible to carry out antistatic treatment such as. In particular, the release property from the pressure-sensitive adhesive layer can be further improved by appropriately performing a release treatment such as silicone treatment, long-chain alkyl treatment, or fluorine treatment on the surface of the separator.

  In addition, the sheet | seat which carried out the peeling process used in preparation of said adhesive type polarizing plate can be used as a separator of an adhesive type polarizing plate as it is, and can simplify in the process surface.

  A polarizing plate having a transparent protective film only on one side of the polarizer is used.

  The polarizer is not particularly limited, and various types can be used. Examples of polarizers include dichroic iodine and dichroic dyes on hydrophilic polymer films such as polyvinyl alcohol films, partially formalized polyvinyl alcohol films, and ethylene / vinyl acetate copolymer partially saponified films. Examples thereof include polyene-based oriented films such as those obtained by adsorbing substances and uniaxially stretched, polyvinyl alcohol dehydrated products and polyvinyl chloride dehydrochlorinated products. Among these, a polarizer composed of a polyvinyl alcohol film and a dichroic material such as iodine is preferable. The thickness of these polarizers is not particularly limited, but is generally about 80 μm or less.

  A polarizer obtained by dyeing a polyvinyl alcohol film with iodine and uniaxially stretching it can be prepared, for example, by immersing polyvinyl alcohol in an aqueous solution of iodine and stretching it 3 to 7 times the original length. If necessary, it can be immersed in an aqueous solution such as potassium iodide which may contain boric acid, zinc sulfate, zinc chloride or the like. Further, if necessary, the polyvinyl alcohol film may be immersed in water and washed before dyeing. In addition to washing the polyvinyl alcohol film surface with dirt and anti-blocking agents by washing the polyvinyl alcohol film with water, it also has the effect of preventing unevenness such as uneven coloring by swelling the polyvinyl alcohol film. is there. Stretching may be performed after dyeing with iodine, may be performed while dyeing, or may be dyed with iodine after stretching. The film can be stretched even in an aqueous solution such as boric acid or potassium iodide or in a water bath.

  As the polarizer, a thin polarizer having a thickness of 10 μm or less can be used. From the viewpoint of thinning, the thickness is preferably 1 to 7 μm. Such a thin polarizer is preferable in that the thickness unevenness is small, the visibility is excellent, the dimensional change is small, the durability is excellent, and the thickness of the polarizing plate can be reduced.

  As the thin polarizer, representatively, JP-A-51-069644, JP-A-2000-338329, WO2010 / 100917 pamphlet, PCT / JP2010 / 001460 specification, or Japanese Patent Application 2010- The thin polarizing film described in 269002 specification and Japanese Patent Application No. 2010-263692 specification can be mentioned. These thin polarizing films can be obtained by a production method including a step of stretching a polyvinyl alcohol-based resin (hereinafter also referred to as PVA-based resin) layer and a stretching resin base material in a laminated state and a step of dyeing. With this manufacturing method, even if the PVA-based resin layer is thin, it can be stretched without problems such as breakage due to stretching by being supported by the stretching resin substrate.

  As the thin polarizing film, among the production methods including the step of stretching in the state of a laminate and the step of dyeing, WO2010 / 100917 pamphlet, PCT / PCT / PCT / JP 2010/001460 specification, or Japanese Patent Application No. 2010-269002 and Japanese Patent Application No. 2010-263692 as described in the manufacturing method including a step of stretching in a boric acid aqueous solution is preferable. What is obtained by the manufacturing method including the process of extending | stretching in the air auxiliary | assistant before extending | stretching in the boric acid aqueous solution as described in Japanese Patent Application No. 2010-269002 and Japanese Patent Application No. 2010-263692 is preferable.

  The thin high-performance polarizing film described in the specification of PCT / JP2010 / 001460 is a thin film having a thickness of 7 μm or less made of a PVA-based resin oriented with a dichroic material, which is integrally formed on a resin base material. It is a high-functional polarizing film, and has optical properties such as a single transmittance of 42.0% or more and a degree of polarization of 99.95% or more.

  The thin high-performance polarizing film generates a PVA-based resin layer by applying and drying a PVA-based resin on a resin substrate having a thickness of at least 20 μm, and the generated PVA-based resin layer is used as a dichroic dyeing solution. So that the dichroic substance is adsorbed on the PVA resin layer, and the PVA resin layer on which the dichroic substance is adsorbed is integrated with the resin base material in the boric acid aqueous solution so that the total draw ratio is the original length. It can manufacture by extending | stretching so that it may become 5 times or more.

  Moreover, it is a method for producing a laminate film including a thin high-performance polarizing film in which a dichroic substance is oriented, and includes a resin base material having a thickness of at least 20 μm and a PVA resin on one side of the resin base material. The said laminated body containing the process of producing | generating the laminated body film containing the PVA-type resin layer formed by apply | coating and drying aqueous solution, and the PVA-type resin layer formed in the single side | surface of the resin base material A step of adsorbing the dichroic substance to the PVA resin layer contained in the laminate film by immersing the film in a dye solution containing the dichroic substance, and a PVA resin adsorbing the dichroic substance A step of stretching the laminate film including a layer in a boric acid aqueous solution so that the total stretching ratio is 5 times or more of the original length, and a PVA resin layer on which a dichroic substance is adsorbed Stretched together with As a result, a thickness of 7 μm or less, a single transmittance of 42.0% or more, and a degree of polarization of 99.95% or more are formed of a PVA resin layer in which a dichroic material is oriented on one side of a resin base material. The thin high-performance polarizing film can be manufactured by including a step of manufacturing a laminate film on which a thin high-performance polarizing film having the above optical characteristics is formed.

  In the present invention, as described above, in the above-mentioned adhesive polarizing plate, as a polarizer having a thickness of 10 μm or less, there is a continuous web polarizing film made of a PVA-based resin in which a dichroic material is oriented, and is a thermoplastic resin. What was obtained by extending | stretching the laminated body containing the polyvinyl-alcohol-type resin layer formed into a base material by the two-stage extending | stretching process which consists of air auxiliary | assistant extending | stretching and boric-acid-water extending | stretching can be used. The thermoplastic resin substrate is preferably an amorphous ester thermoplastic resin substrate or a crystalline ester thermoplastic resin substrate.

The thin polarizing film in the above-mentioned Japanese Patent Application Nos. 2010-269002 and 2010-263692 is a continuous web polarizing film made of a PVA resin in which a dichroic material is oriented, and is amorphous. The laminate including the PVA-based resin layer formed on the ester-based thermoplastic resin base material was stretched in a two-stage stretching process consisting of air-assisted stretching and boric acid-water stretching, so that the thickness was 10 μm or less. Is. Such a thin polarizing film has P> − (10 ^0.929 T ^−42.4 −1) × 100 (where T <42.3) and P ≧, where T is the single transmittance and P is the polarization degree. It is preferable that the optical properties satisfy 99.9 (where T ≧ 42.3).

  Specifically, the thin polarizing film is a stretch intermediate formed of an oriented PVA resin layer by high-temperature stretching in the air with respect to the PVA resin layer formed on the amorphous ester thermoplastic resin substrate of the continuous web. A colored intermediate product comprising a PVA-based resin layer in which a dichroic material (preferably iodine or a mixture of iodine and an organic dye) is oriented by adsorption of the dichroic material to the stretched intermediate product and a step of generating the product. A thin polarizing film comprising: a step of producing a product; and a step of producing a polarizing film having a thickness of 10 μm or less comprising a PVA resin layer in which a dichroic substance is oriented by stretching in a boric acid solution with respect to a colored intermediate product It can manufacture with the manufacturing method of.

In this production method, the total draw ratio of the PVA resin layer formed on the amorphous ester thermoplastic resin base material by high-temperature drawing in air and drawing in boric acid solution should be 5 times or more. desirable. The liquid temperature of the boric acid aqueous solution for boric-acid water extending | stretching can be 60 degreeC or more. Before stretching the colored intermediate product in the aqueous boric acid solution, it is desirable to insolubilize the colored intermediate product. In this case, the colored intermediate product is added to the aqueous boric acid solution whose liquid temperature does not exceed 40 ° C. It is desirable to do so by dipping. The amorphous ester-based thermoplastic resin base material is amorphous polyethylene containing copolymerized polyethylene terephthalate copolymerized with isophthalic acid, copolymerized polyethylene terephthalate copolymerized with cyclohexanedimethanol, or other copolymerized polyethylene terephthalate. It can be terephthalate and is preferably made of a transparent resin, and the thickness thereof can be 7 times or more the thickness of the PVA resin layer to be formed. Moreover, the draw ratio of the high temperature stretching in the air is preferably 3.5 times or less, and the stretching temperature of the high temperature stretching in the air is preferably not less than the glass transition temperature of the PVA resin, specifically in the range of 95 ° C to 150 ° C. When performing high temperature stretching in the air by free end uniaxial stretching, the total stretching ratio of the PVA resin layer formed on the amorphous ester thermoplastic resin base material is preferably 5 to 7.5 times . In addition, when performing high-temperature stretching in the air by uniaxial stretching at the fixed end, the total stretching ratio of the PVA-based resin layer formed on the amorphous ester-based thermoplastic resin base material is 5 times or more and 8.5 times or less. Is preferred.
More specifically, a thin polarizing film can be produced by the following method.

  A base material of a continuous web of isophthalic acid copolymerized polyethylene terephthalate (amorphous PET) in which 6 mol% of isophthalic acid is copolymerized is prepared. The glass transition temperature of amorphous PET is 75 ° C. A laminate comprising a continuous web of amorphous PET substrate and a polyvinyl alcohol (PVA) layer is prepared as follows. Incidentally, the glass transition temperature of PVA is 80 ° C.

  A 200 μm-thick amorphous PET base material and a 4-5% concentration PVA aqueous solution in which PVA powder having a polymerization degree of 1000 or more and a saponification degree of 99% or more are dissolved in water are prepared. Next, a PVA aqueous solution is applied to a 200 μm thick amorphous PET substrate and dried at a temperature of 50 to 60 ° C. to obtain a laminate in which a 7 μm thick PVA layer is formed on the amorphous PET substrate. .

  A laminated body including a PVA layer having a thickness of 7 μm is subjected to the following steps including a two-step stretching process of air-assisted stretching and boric acid water stretching to produce a 3 μm-thick thin high-performance polarizing film. In the first-stage aerial auxiliary stretching step, the laminate including the 7 μm-thick PVA layer is integrally stretched with the amorphous PET substrate to produce a stretched laminate including the 5 μm-thick PVA layer. Specifically, in this stretched laminate, a laminate including a 7 μm-thick PVA layer is subjected to a stretching apparatus disposed in an oven set to a stretching temperature environment of 130 ° C. so that the stretching ratio is 1.8 times. Are stretched uniaxially at the free end. By this stretching treatment, the PVA layer contained in the stretched laminate is changed to a 5 μm thick PVA layer in which PVA molecules are oriented.

  Next, a colored laminate in which iodine is adsorbed on a PVA layer having a thickness of 5 μm in which PVA molecules are oriented is generated by a dyeing process. Specifically, this colored laminate has a single layer transmittance of the PVA layer constituting the high-functional polarizing film that is finally produced by using the stretched laminate in a staining solution containing iodine and potassium iodide at a liquid temperature of 30 ° C. Iodine is adsorbed to the PVA layer contained in the stretched laminate by dipping for an arbitrary period of time so as to be 40 to 44%. In this step, the staining solution uses water as a solvent and an iodine concentration in the range of 0.12 to 0.30% by weight and a potassium iodide concentration in the range of 0.7 to 2.1% by weight. The concentration ratio of iodine and potassium iodide is 1 to 7. Incidentally, potassium iodide is required to dissolve iodine in water. More specifically, by immersing the stretched laminate in a dyeing solution having an iodine concentration of 0.30% by weight and a potassium iodide concentration of 2.1% by weight for 60 seconds, iodine is applied to a 5 μm-thick PVA layer in which PVA molecules are oriented. A colored laminate is adsorbed on the substrate.

  Further, the colored laminated body is further stretched integrally with the amorphous PET base material by the second stage boric acid underwater stretching step to produce an optical film laminate including a PVA layer constituting a highly functional polarizing film having a thickness of 3 μm. To do. Specifically, this optical film laminate is stretched by applying a colored laminate to a stretching apparatus provided in a treatment apparatus set to a boric acid aqueous solution having a liquid temperature range of 60 to 85 ° C. containing boric acid and potassium iodide. It is stretched uniaxially at the free end so that the magnification is 3.3 times. More specifically, the liquid temperature of the boric acid aqueous solution is 65 ° C. It also has a boric acid content of 4 parts by weight with respect to 100 parts by weight of water and a potassium iodide content of 5 parts by weight with respect to 100 parts by weight of water. In this step, the colored laminate with adjusted iodine adsorption amount is first immersed in a boric acid aqueous solution for 5 to 10 seconds. After that, the colored laminate is passed as it is between a plurality of sets of rolls having different peripheral speeds, which is a stretching apparatus provided in the processing apparatus, and the stretching ratio is freely increased to 3.3 times over 30 to 90 seconds. Stretch uniaxially. By this stretching treatment, the PVA layer contained in the colored laminate is changed into a PVA layer having a thickness of 3 μm in which the adsorbed iodine is oriented higher in one direction as a polyiodine ion complex. This PVA layer constitutes a highly functional polarizing film of the optical film laminate.

  Although not an indispensable step for the production of an optical film laminate, the optical film laminate was removed from the boric acid aqueous solution and adhered to the surface of the 3 μm-thick PVA layer formed on the amorphous PET substrate by the washing step. It is preferable to wash boric acid with an aqueous potassium iodide solution. Thereafter, the washed optical film laminate is dried by a drying process using hot air at 60 ° C. The cleaning process is a process for eliminating appearance defects such as boric acid precipitation.

  Similarly, it is not an indispensable process for producing an optical film laminate, but an adhesive is applied to the surface of a 3 μm-thick PVA layer formed on an amorphous PET substrate by a bonding and / or transfer process. However, after bonding the 80 μm thick triacetyl cellulose film, the amorphous PET substrate can be peeled off, and the 3 μm thick PVA layer can be transferred to the 80 μm thick triacetyl cellulose film.

[Other processes]
The manufacturing method of said thin-shaped polarizing film may include another process other than the said process. Examples of other steps include an insolubilization step, a crosslinking step, and a drying (adjustment of moisture content) step. The other steps can be performed at any appropriate timing.
The insolubilization step is typically performed by immersing the PVA resin layer in a boric acid aqueous solution. By performing the insolubilization treatment, water resistance can be imparted to the PVA resin layer. The concentration of the boric acid aqueous solution is preferably 1 to 4 parts by weight with respect to 100 parts by weight of water. The liquid temperature of the insolubilizing bath (boric acid aqueous solution) is preferably 20 ° C to 50 ° C. Preferably, the insolubilization step is performed after the laminate is manufactured and before the dyeing step and the underwater stretching step.
The crosslinking step is typically performed by immersing the PVA resin layer in an aqueous boric acid solution. By performing the crosslinking treatment, water resistance can be imparted to the PVA resin layer. The concentration of the boric acid aqueous solution is preferably 1 to 4 parts by weight with respect to 100 parts by weight of water. Moreover, when performing a bridge | crosslinking process after the said dyeing | staining process, it is preferable to mix | blend iodide further. By blending iodide, elution of iodine adsorbed on the PVA resin layer can be suppressed. The blending amount of iodide is preferably 1 part by weight to 5 parts by weight with respect to 100 parts by weight of water. Specific examples of the iodide are as described above. The liquid temperature of the crosslinking bath (boric acid aqueous solution) is preferably 20 ° C to 50 ° C. Preferably, the crosslinking step is performed before the second boric acid aqueous drawing step. In a preferred embodiment, the dyeing step, the crosslinking step, and the second boric acid aqueous drawing step are performed in this order.

  As a material constituting the transparent protective film, for example, a thermoplastic resin excellent in transparency, mechanical strength, thermal stability, moisture barrier property, isotropy and the like is used. Specific examples of such thermoplastic resins include cellulose resins such as triacetyl cellulose, polyester resins, polyethersulfone resins, polysulfone resins, polycarbonate resins, polyamide resins, polyimide resins, polyolefin resins, (meth) acrylic resins, cyclic Examples thereof include polyolefin resins (norbornene resins), polyarylate resins, polystyrene resins, polyvinyl alcohol resins, and mixtures thereof. One or more kinds of arbitrary appropriate additives may be contained in the transparent protective film. Examples of the additive include an ultraviolet absorber, an antioxidant, a lubricant, a plasticizer, a mold release agent, an anti-coloring agent, a flame retardant, a nucleating agent, an antistatic agent, a pigment, and a coloring agent. The content of the thermoplastic resin in the transparent protective film is preferably 50 to 100% by weight, more preferably 50 to 99% by weight, still more preferably 60 to 98% by weight, and particularly preferably 70 to 97% by weight. . When content of the said thermoplastic resin in a transparent protective film is 50 weight% or less, there exists a possibility that the high transparency etc. which a thermoplastic resin originally has cannot fully be expressed.

  A transparent protective film is bonded to one side of the polarizer with an adhesive layer. An adhesive is used for the adhesion treatment between the polarizer and the transparent protective film. Examples of the adhesive include isocyanate adhesives, polyvinyl alcohol adhesives, gelatin adhesives, vinyl latexes, and water-based polyesters. The said adhesive agent is normally used as an adhesive agent which consists of aqueous solution, and contains 0.5 to 60 weight% of solid content normally. In addition to the above, examples of the adhesive between the polarizer and the transparent protective film include an ultraviolet curable adhesive and an electron beam curable adhesive. The electron beam curable polarizing plate adhesive exhibits suitable adhesion to the various transparent protective films. The adhesive used in the present invention can contain a metal compound filler.

  Moreover, the said polarizing plate can be laminated | stacked with another optical film. Examples of other optical films include the formation of liquid crystal display devices such as reflectors, anti-transmission plates, retardation plates (including wavelength plates such as 1/2 and 1/4), visual compensation films, and brightness enhancement films. The thing used as the optical layer which may be used is mentioned. These may be laminated on the polarizing plate for practical use, and one layer or two or more layers may be used.

  An optical film in which the optical layer is laminated on a polarizing plate can be formed by a method of sequentially laminating separately in the manufacturing process of a liquid crystal display device or the like. There is an advantage that the manufacturing process of a liquid crystal display device or the like can be improved because of excellent stability and assembly work. For the lamination, an appropriate adhesive means such as an adhesive layer can be used. When adhering the polarizing plate and the other optical layer, their optical axes can be set at an appropriate arrangement angle in accordance with the target phase difference characteristic.

  The pressure-sensitive adhesive polarizing plate of the present invention can be preferably used for forming various image display devices such as a liquid crystal display device. The liquid crystal display device can be formed according to the conventional method. That is, the liquid crystal display device is generally formed by appropriately assembling components such as a display panel such as a liquid crystal cell, an adhesive polarizing plate, and an illumination system as necessary, and incorporating a drive circuit. There is no particular limitation except that the pressure-sensitive adhesive polarizing plate according to the present invention is used. As the liquid crystal cell, an arbitrary type such as an arbitrary type such as a TN type, STN type, π type, VA type, or IPS type can be used.

  An appropriate liquid crystal display device such as a liquid crystal display device in which an adhesive polarizing plate is disposed on one side or both sides of a display panel such as a liquid crystal cell, or a lighting system using a backlight or a reflecting plate can be formed. In that case, the adhesive polarizing plate according to the present invention can be installed on one side or both sides of a display panel such as a liquid crystal cell. When optical films are provided on both sides, they may be the same or different. Further, when forming a liquid crystal display device, for example, a single layer or a suitable part such as a diffusing plate, an antiglare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusing plate, a backlight, etc. Two or more layers can be arranged.

  EXAMPLES The present invention will be specifically described below with reference to examples, but the present invention is not limited to these examples. In addition, all the parts and% in each example are based on weight. The room temperature standing conditions not specifically defined below are all 23 ° C. and 65% RH.

<Measurement of weight average molecular weight of (meth) acrylic polymer (A)>
The weight average molecular weight of the (meth) acrylic polymer (A) was measured by GPC (gel permeation chromatography).
・ Analyzer: HLC-8120GPC manufactured by Tosoh Corporation
Column: manufactured by Tosoh Corporation, G7000H _XL + GMH _XL + GMH _XL
・ Column size: 7.8mmφ × 30cm each 90cm in total
-Column temperature: 40 ° C
・ Flow rate: 0.8ml / min
・ Injection volume: 100 μl
・ Eluent: Tetrahydrofuran ・ Detector: Differential refractometer (RI)
Standard sample: polystyrene

<Creation of polarizing plate (1)>
In order to produce a thin polarizing film, first, a laminated body in which a PVA layer having a thickness of 9 μm is formed on an amorphous PET substrate is produced by air-assisted stretching at a stretching temperature of 130 ° C., and then stretched. A colored laminate is produced by dyeing the laminate, and the colored laminate is further stretched integrally with an amorphous PET substrate so that the total draw ratio is 5.94 times by stretching in boric acid water at a stretching temperature of 65 degrees. An optical film laminate including a 4 μm thick PVA layer was produced. The PVA molecules in the PVA layer formed on the amorphous PET substrate by such two-stage stretching are oriented in the higher order, and the iodine adsorbed by the dyeing is oriented in the one direction as the polyiodine ion complex. It was possible to produce an optical film laminate including a PVA layer having a thickness of 4 μm and constituting a highly functional polarizing film. Further, after applying a saponified 40 μm thick triacetyl cellulose film while applying a polyvinyl alcohol-based adhesive on the surface of the polarizing film of the optical film laminate, the amorphous PET substrate was peeled off, A polarizing plate using a thin polarizing film was prepared. Hereinafter, this is referred to as a thin polarizing plate (1).

<Creation of polarizing plate (2)>
A polyvinyl alcohol film having a thickness of 80 μm was stretched up to 3 times while being dyed for 1 minute in an iodine solution of 0.3% concentration at 30 ° C. between rolls having different speed ratios. Thereafter, the total draw ratio was stretched to 6 times while being immersed in an aqueous solution containing 60% at 4% concentration of boric acid and 10% concentration of potassium iodide for 0.5 minutes. Next, after washing by immersing in an aqueous solution containing potassium iodide at 30 ° C. and 1.5% concentration for 10 seconds, drying was performed at 50 ° C. for 4 minutes to obtain a polarizer having a thickness of 20 μm. A saponified 40 μm thick triacetyl cellulose film was bonded to both sides of the polarizer with a polyvinyl alcohol-based adhesive to form a polarizing plate. Hereinafter, this is referred to as a TAC polarizing plate (2).

Production Example 1
<Preparation of acrylic polymer (A1)>
A monomer mixture containing 82 parts of butyl acrylate, 15 parts of benzyl acrylate, and 3 parts of 4-hydroxybutyl acrylate was charged into a four-necked flask equipped with a stirring blade, a thermometer, a nitrogen gas inlet tube, and a condenser. Furthermore, with respect to 100 parts of the monomer mixture (solid content), 0.1 part of 2,2′-azobisisobutyronitrile as a polymerization initiator was charged with ethyl acetate, and nitrogen gas was introduced while gently stirring. Then, the temperature of the liquid in the flask was kept at around 60 ° C., and a polymerization reaction was performed for 7 hours. Then, ethyl acetate was added to the obtained reaction liquid, and the solution of the acrylic polymer (A-1) of the weight average molecular weight 1 million adjusted to solid content concentration 30% was prepared.

Production Example 2
<Preparation of acrylic polymer (A-2)>
In Production Example 1, a monomer mixture containing 76.8 parts of butyl acrylate, 10 parts of benzyl acrylate, 10 parts of phenoxyethyl acrylate, 3 parts of 4-hydroxybutyl acrylate and 0.2 part of acrylic acid was used as the monomer mixture. Except for the above, a solution of an acrylic polymer (A2) having a weight average molecular weight of 1,000,000 was prepared in the same manner as in Production Example 1.

Production Example 3
<Preparation of acrylic polymer (A-3)>
In Production Example 1, Production Example 1 except that a monomer mixture containing 81.9 parts of butyl acrylate, 13 parts of benzyl acrylate, 0.1 part of 2-hydroxyethyl acrylate and 5 parts of acrylic acid was used as the monomer mixture. Similarly, a solution of an acrylic polymer (A2) having a weight average molecular weight of 1 million was prepared.

Example 1
(Preparation of adhesive composition)
To 100 parts of the solid content of the acrylic polymer (A-1) solution obtained in Production Example 1, 0.002 part of lithium bis (trifluoromethanesulfonyl) imide (manufactured by Nippon Carlit) is blended. 0.1 part of methylolpropane xylylene diisocyanate (Mitsui Chemical Co., Ltd .: Takenate D110N), 0.3 part of dibenzoyl peroxide, and γ-glycidoxypropylmethoxysilane (manufactured by Shin-Etsu Chemical Co., Ltd .: KBM-403) 0 0.075 parts was blended to prepare an acrylic pressure-sensitive adhesive solution.

(Preparation of adhesive polarizing plate)
Next, the acrylic pressure-sensitive adhesive solution is uniformly applied to the surface of a polyethylene terephthalate film (separator film) treated with a silicone-based release agent with a fountain coater and dried in an air circulation type thermostatic oven at 155 ° C. for 2 minutes. Then, an adhesive layer having a thickness of 20 μm was formed on the surface of the separator film. Next, the pressure-sensitive adhesive layer formed on the separator film was transferred to the polarizing film side of the polarizer of the thin polarizing plate (1) prepared above to prepare a pressure-sensitive adhesive polarizing plate.

Examples 2-17, Comparative Examples 1-4
In Example 1, the amount of each component used was changed as shown in Table 1 in preparation of the pressure-sensitive adhesive composition, and the type of polarizing plate was changed as shown in Table 1 in preparing the pressure-sensitive adhesive polarizing plate. Except for the above, an adhesive polarizing plate was produced in the same manner as in Example 1.

  The following evaluation was performed about the adhesion type polarizing plate obtained by the said Example and comparative example. The evaluation results are shown in Table 1.

<Surface resistance value: Initial>
After peeling the separator film of the pressure-sensitive adhesive polarizing plate, the surface resistance value (Ω / □) of the pressure-sensitive adhesive surface was measured using MCP-HT450 manufactured by Mitsubishi Chemical Analytech.

<Evaluation of static electricity unevenness>
The produced adhesive polarizing plate was cut into a size of 100 mm × 100 mm and attached to a liquid crystal panel. This panel was placed on a backlight having a luminance of 10,000 cd, and 5 kv of static electricity was generated using ESD (SANKI, ESD-8012A) which is a static electricity generator, thereby causing alignment disorder of the liquid crystal. The display failure recovery time (seconds) due to the alignment failure was measured using an instantaneous multiphotometric detector (manufactured by Otsuka Electronics Co., Ltd., MCPD-3000) and evaluated according to the following criteria.
A: Display failure disappeared in less than 1 second.
○: Display failure disappeared in 1 second or more and less than 10 seconds.
X: Display defect disappeared in 10 seconds or more.

<Durability>
The separator film of the adhesive polarizing plate was peeled off and attached to a non-alkali glass (Corning Corp., 1737) having a thickness of 0.7 mm using a laminator. Subsequently, an autoclave treatment was performed at 50 ° C. and 0.5 MPa for 15 minutes, and the pressure-sensitive adhesive polarizing plate was completely adhered to the acrylic-free glass. Next, this was put in the conditions of a heating oven (heating) at 80 ° C. and a constant temperature and humidity machine (humidification) at 60 ° C./90% RH, respectively, and the presence or absence of peeling of the polarizing plate after 500 hours was determined as follows: Evaluated by criteria.
A: No peeling was observed.
○: Peeling that was not visually confirmed was observed.
(Triangle | delta): The small peeling which can be confirmed visually is recognized.
X: Clear peeling was recognized.

<Measurement of polarization>
The separator film of the adhesive polarizing plate was peeled off and attached to a non-alkali glass (Corning Corp., 1737) having a thickness of 0.7 mm using a laminator. Subsequently, an autoclave treatment was performed at 50 ° C. and 0.5 MPa for 15 minutes, and the pressure-sensitive adhesive polarizing plate was completely adhered to the acrylic-free glass. Subsequently, it was put into a constant temperature and humidity machine of 60 ° C./95% RH for 500 hours. The polarization degree of the polarizing plate before and after the injection was measured using V7100 manufactured by JASCO Corporation, and the amount of change ΔP = (degree of polarization before injection) − (degree of polarization after injection) was determined. .

In Table 1, “B-1” in the alkali metal salt (B) is lithium bis (trifluoromethanesulfonyl) imide manufactured by Nippon Carlit, “B-2” is lithium perchloride manufactured by Nippon Carlit, “3” indicates 1-hexyl-4-methylpyridinium hexafluorophosphate manufactured by Kanto Chemical Co., Inc.
In the crosslinking agent (C), “C-1” is an isocyanate crosslinking agent (Takenate D110N, trimethylolpropane xylylene diisocyanate) manufactured by Mitsui Takeda Chemical Co., and “C-2” is an isocyanate crosslinking agent (manufactured by Nippon Polyurethane Industry Co., Ltd.). Coronate L, adduct body of tolylene diisocyanate of trimethylolpropane), “C-3” indicates benzoyl peroxide (Niper BMT) manufactured by NOF Corporation.
“D-1” in the silane coupling agent (D) indicates KBM403 manufactured by Shin-Etsu Chemical Co., Ltd.
“E-1” in the other compounds (E) represents Silyl SAT10 (number average molecular weight 4000) manufactured by Kaneka Corporation. “E-2” indicates polypropylene glycol (number average molecular weight 5000).

<Creation of polarizing plate (2)>
A polyvinyl alcohol film having a thickness of 80 μm was stretched up to 3 times while being dyed for 1 minute in an iodine solution of 0.3% concentration at 30 ° C. between rolls having different speed ratios. Thereafter, the total draw ratio was stretched to 6 times while being immersed in an aqueous solution containing 60% at 4% concentration of boric acid and 10% concentration of potassium iodide for 0.5 minutes. Next, after washing by immersing in an aqueous solution containing potassium iodide at 30 ° C. and 1.5% concentration for 10 seconds, drying was performed at 50 ° C. for 4 minutes to obtain a polarizer having a thickness of 20 μm. On one surface of the polarizer, a triacetyl cellulose film having a thickness of 40μm was saponified to prepare a polarizing plate bonded by polyvinyl alcohol-based adhesive. Hereinafter, this is referred to as a TAC polarizing plate (2).

Claims (16)

A pressure-sensitive adhesive polarizing plate having a polarizing plate and a pressure-sensitive adhesive layer provided on the polarizing plate,
The polarizing plate has a transparent protective film only on one side of the polarizer, the adhesive layer is provided on the polarizer on the side not having the transparent protective film, and the adhesive layer is (meta ) Formed from a pressure-sensitive adhesive composition containing an acrylic polymer (A) and an alkali metal salt (B),
The pressure-sensitive adhesive-attached polarizing plate is obtained from the degree of polarization measured in a constant temperature and humidity chamber of 60 ° C./95% RH for 500 hours before and after charging. Formula: change amount ΔP (%) = (polarity before charging ( %))-(Adhesive polarizing plate characterized in that the amount of change ΔP (%) expressed by (degree of polarization after introduction (%)) satisfies 0.05 or less.   The pressure-sensitive adhesive polarizing plate according to claim 1, wherein the alkali metal salt (B) is a lithium salt.   The pressure-sensitive adhesive polarizing plate according to claim 1 or 2, comprising 0.0001 to 5 parts by weight of an alkali metal salt (B) with respect to 100 parts by weight of the (meth) acrylic polymer (A).   The pressure-sensitive adhesive polarizing plate according to claim 1, wherein the polarizer has a thickness of 10 μm or less.   The pressure-sensitive adhesive polarizing plate according to claim 1, wherein the (meth) acrylic polymer (A) contains a hydroxyl group-containing monomer as a monomer unit.   The pressure-sensitive adhesive polarizing plate according to claim 1, wherein the (meth) acrylic polymer (A) contains a carboxyl group-containing monomer as a monomer unit.   The pressure-sensitive adhesive composition according to any one of claims 1 to 6, wherein the pressure-sensitive adhesive composition further contains a crosslinking agent (C).   The pressure-sensitive adhesive polarizing plate according to claim 7, wherein the crosslinking agent (C) is contained in an amount of 0.01 to 20 parts by weight with respect to 100 parts by weight of the (meth) acrylic polymer (A).   The pressure-sensitive adhesive polarizing plate according to claim 7 or 8, wherein the crosslinking agent (C) is at least one selected from an isocyanate compound and a peroxide.   The silane coupling agent (D) is further contained in an amount of 0.001 to 5 parts by weight per 100 parts by weight of the (meth) acrylic polymer (A). Adhesive polarizing plate.   The pressure-sensitive adhesive according to any one of claims 1 to 10, further comprising 0.001 to 10 parts by weight of a polyether-modified silicone compound with respect to 100 parts by weight of the (meth) acrylic polymer (A). Type polarizing plate.   The pressure-sensitive adhesive polarizing plate according to any one of claims 1 to 11, wherein the (meth) acrylic polymer (A) has a weight average molecular weight of 500,000 to 3,000,000.   The pressure-sensitive adhesive polarizing plate according to any one of claims 1 to 12, further comprising an easy-adhesion layer between the polarizing plate and the pressure-sensitive adhesive layer.   An image display device comprising at least one pressure-sensitive adhesive polarizing plate according to claim 1. It is a manufacturing method of the adhesion type polarizing plate of Claims 4-13,
A continuous web polarizing film made of a polyvinyl alcohol-based resin in which a dichroic material is oriented, and a laminate including a polyvinyl alcohol-based resin layer formed on a thermoplastic resin base material is formed by aerial auxiliary stretching and boric acid water. A step of preparing a polarizer having a thickness of 10 μm or less obtained by stretching in a two-stage stretching step comprising stretching;
The step of obtaining the polarizing plate by bonding the transparent protective film only to one side of the polarizer, and
The manufacturing method of the adhesion type polarizing plate characterized by including the process of forming the said adhesive layer in the side which does not have the said transparent protective film of the said polarizing plate. Forming the pressure-sensitive adhesive layer,
A method of transferring the pressure-sensitive adhesive layer formed from the pressure-sensitive adhesive composition to the polarizing plate, or