JP2017144997A - tire - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a tire which suppresses a progress speed till a scratch occurring in a coating resin layer coating a reinforcement cord reaches the reinforcement cord.SOLUTION: A tire 10 includes: an annular tire skeleton member 17 formed of a skeleton resin material; and a coating cord member 26 provided in the tire skeleton member 17 and including a reinforcement cord 32 extending in a tire circumferential direction, a coating resin layer 34 formed of a coating resin material, coating the reinforcement cord 32, and joined to the tire skeleton member 17, and a joint resin layer 36 formed of a joint resin material having an elastic modulus higher than that of the coating resin material, disposed between the reinforcement cord 32 and the coating resin layer 34, joining the reinforcement cord 32 to the coating resin layer 34, and having a layer thickness T1 thicker than a layer thickness T2 of the coating resin layer 34.SELECTED DRAWING: Figure 2

Description

  The present invention relates to a tire, and particularly relates to a tire in which a tire frame member is formed using a resin material.

  In recent years, resin materials (for example, thermoplastic resins, thermoplastic elastomers, and the like) are required to be used as tire materials because of weight reduction, ease of molding, and ease of recycling.

  Patent Document 1 discloses a tire in which a tire frame member is formed of a thermoplastic resin material.

Japanese Patent Laid-Open No. 03-143701

  Incidentally, in the tire disclosed in Patent Document 1, the rubber-coated reinforcing cord is provided on the outer periphery of the tire frame member. However, it is not easy to separate the rubber from the reinforcing cord at the time of recycling. From the viewpoint, a technique for coating a reinforcing cord with a resin has been studied.

  When the reinforcing cord is covered with the covering resin material, it is desirable to firmly bond the reinforcing cord and the covering resin material with an adhesive resin material interposed therebetween. As this coating resin material, a relatively soft resin material tends to be used so that it can follow the tire deformation during rolling of the tire. Although such a soft resin material is excellent in followability to deformation, it tends to be difficult to suppress the progress of the scratch when a scratch or the like occurs.

  The present invention has been made in consideration of the above facts, and it is an object of the present invention to provide a tire capable of suppressing the progress speed until a scratch generated in the coating resin layer covering the reinforcing cord reaches the reinforcing cord. And

  The tire according to the first aspect of the present invention is formed of an annular tire skeleton member formed of a skeleton resin material, a reinforcing cord provided in the tire skeleton member and extending in the tire circumferential direction, and a coating resin material. A coating resin layer covering the reinforcement cord and bonded to the tire frame member, and a bonding resin material having a higher elastic modulus than the coating resin material, and the reinforcement cord and the coating resin layer A covering cord member that is disposed between the reinforcing cord and the covering resin layer and includes a bonding resin layer having a layer thickness larger than that of the covering resin layer. .

  In the tire according to the first aspect, since the layer thickness of the bonding resin layer is larger than the layer thickness of the coating resin layer, for example, the layer thickness of the bonding resin layer is equal to or less than the layer thickness of the coating resin layer. Compared to the above, the bonding resin layer becomes harder. Thereby, for example, even if a flaw occurs in the coating resin layer, the progress speed of the flaw is suppressed by the bonding resin layer. For this reason, the advancing speed until the damage | wound produced in the resin layer for a coating | cover reaches | attains a reinforcement cord is suppressed.

  A tire according to a second aspect of the present invention is the tire according to the first aspect, wherein the tire frame member includes a bead portion, a side portion that is continuous with a tire radial direction outside of the bead portion, and a tire width direction of the side portion. And the covering cord member is spirally wound around the outer periphery of the crown portion.

  In the tire according to the second aspect, since the covering cord member is spirally wound around the outer periphery of the crown portion of the tire frame member, the tire circumferential rigidity of the crown portion is improved.

  A tire according to a third aspect of the present invention is the tire according to the second aspect, wherein the coating resin material has thermoplasticity, and the coating resin layer and the crown portion are joined by thermal welding. .

  In the tire according to the third aspect, since the covering resin layer of the covering cord member and the crown portion of the tire frame member are bonded by thermal welding, the bonding strength between the covering resin layer and the crown portion is improved.

  A tire according to a fourth aspect of the present invention is the tire according to the first aspect, wherein the tire frame member includes a bead portion, a side portion continuous to the tire radial direction outside of the bead portion, and a tire width direction of the side portion. A crown portion connected to the inside, and the covering cord member is embedded in the bead portion.

  In the tire according to the fourth aspect, since the covering cord member is embedded in the bead portion, the circumferential rigidity of the bead portion of the tire frame member is improved.

  In the tire according to the fifth aspect of the present invention, in the tire according to the fourth aspect, the skeleton resin material has thermoplasticity, and the coating resin layer and the bead portion are joined by thermal welding. .

  In the tire of the fifth aspect, since the covering resin layer of the covering cord member and the bead portion of the tire frame member are bonded by thermal welding, the bonding strength between the covering resin layer and the bead portion is improved.

  The tire according to a sixth aspect of the present invention is the tire according to any one of the first aspect to the fifth aspect, wherein the bonding resin layer has a layer thickness of 500 μm to 5 mm.

  In the tire according to the sixth aspect, since the thickness of the bonding resin layer is 500 μm to 5 mm, the bonding resin layer can be further hardened. Thereby, for example, even if a flaw occurs in the coating resin layer, the progress speed of the flaw is further suppressed by the bonding resin layer.

  As described above, according to the tire of the present invention, it is possible to suppress the progress speed until the scratches generated in the coating resin layer covering the reinforcing cord reach the reinforcing cord.

It is sectional drawing along the tire width direction of the tire of 1st Embodiment of this invention. It is an expansion perspective view of the part pointed by the arrow 2 of the tire of FIG. It is sectional drawing along the tire width direction of the bead part of the tire of 2nd Embodiment of this invention. It is sectional drawing along the tire width direction of the covering cord member which shows the 1st modification of the covering cord member of the tire of 1st Embodiment of this invention. It is sectional drawing along the tire width direction of the covering cord member which shows the 2nd modification of the covering cord member of the tire of 1st Embodiment of this invention.

Hereinafter, embodiments will be described and embodiments of the present invention will be described. In the drawings, an arrow TW indicates a tire width direction, an arrow TR indicates a tire radial direction (a direction orthogonal to a tire rotation axis (not shown)), and an arrow TC indicates a tire circumferential direction. In the following, the side close to the tire rotation axis along the tire radial direction is referred to as “tire radial inner side”, and the side far from the tire rotation axis along the tire radial direction is referred to as “tire radial outer side”. On the other hand, the side close to the tire equatorial plane CL along the tire width direction is “inner side in the tire width direction”, and the opposite side, that is, the side far from the tire equatorial plane CL along the tire width direction is “outside in the tire width direction”. ".
In addition, the dimension measuring method of each part is based on the method as described in the 2014 edition YEAR BOOK issued by JATMA (Japan Automobile Tire Association).

<First Embodiment>
As shown in FIG. 1, the tire 10 of the first embodiment is a pneumatic tire that is used by being filled with air, and has substantially the same cross-sectional shape as a conventional general rubber pneumatic tire. .

The tire 10 of this embodiment includes a tire skeleton member 17 that is a skeleton portion of the tire 10. The tire frame member 17 is formed by annularly forming a frame resin material. The tire frame member 17 is connected to a pair of bead portions 12 arranged at intervals in the tire width direction, a side portion 14 connected to the outer side of the bead portion 12 in the tire radial direction, and an inner side of the side portion 14 in the tire width direction. , And a crown portion 16 that connects the outer ends in the tire radial direction of the respective side portions 14.
Note that the circumferential direction, the width direction, and the radial direction of the tire frame member 17 correspond to the tire circumferential direction, the tire width direction, and the tire radial direction, respectively.

  The tire frame member 17 is formed using a frame resin material as a main raw material. This skeleton resin material does not include vulcanized rubber. Examples of the resin material for the skeleton include thermoplastic resins (including thermoplastic elastomers), thermosetting resins, and other general-purpose resins, as well as engineering plastics (including super engineering plastics).

  A thermoplastic resin (including a thermoplastic elastomer) refers to a high molecular compound that softens and flows as the temperature rises and becomes relatively hard and strong when cooled. In the present specification, among these, the material softens and flows with increasing temperature, and becomes relatively hard and strong when cooled, and a high molecular compound having rubber-like elasticity is a thermoplastic elastomer, and the material increases with increasing temperature. Is softened, fluidized, and becomes a relatively hard and strong state when cooled, and a high molecular compound having no rubber-like elasticity is distinguished as a thermoplastic resin that is not an elastomer.

  Thermoplastic resins (including thermoplastic elastomers) include polyolefin-based thermoplastic elastomers (TPO), polystyrene-based thermoplastic elastomers (TPS), polyamide-based thermoplastic elastomers (TPA), polyurethane-based thermoplastic elastomers (TPU), and polyesters. Thermoplastic thermoplastic elastomer (TPC), dynamically crosslinked thermoplastic elastomer (TPV), polyolefin thermoplastic resin, polystyrene thermoplastic resin, polyamide thermoplastic resin, polyester thermoplastic resin, etc. Can be mentioned.

  In addition, as the thermoplastic material, for example, the deflection temperature under load (0.45 MPa load) specified in ISO75-2 or ASTM D648 is 78 ° C. or higher, and the tensile yield strength specified in JIS K7161 is 10 MPa. As described above, the tensile fracture elongation similarly defined in JIS K7161 is 50% or more. What has Vicat softening temperature (A method) prescribed | regulated to JISK7206 of 130 degreeC can be used.

  The thermosetting resin refers to a polymer compound that forms a three-dimensional network structure as the temperature rises and cures. As a thermosetting resin, a phenol resin, an epoxy resin, a melamine resin, a urea resin etc. are mentioned, for example.

  In addition to the aforementioned thermoplastic resins (including thermoplastic elastomers) and thermosetting resins, skeleton resin materials include (meth) acrylic resins, EVA resins, vinyl chloride resins, fluorine resins, silicone resins. A general-purpose resin such as a resin may be used.

  In addition, even if the tire skeleton member 17 is formed of a single skeleton resin material, the tire skeleton member 17 has different characteristics for each part (bead portion 12, side portion 14, crown portion 16 and the like) of the tire skeleton member 17. It may be formed of a resin material. In the present embodiment, the tire frame member 17 is formed of a thermoplastic resin.

  As shown in FIG. 1, the bead portion 12 is a portion that fits into a standard rim (not shown) via a covering rubber 24, and an annular bead core 18 that extends along the tire circumferential direction is embedded therein. Yes. The bead core 18 is configured by a bead cord (not shown) such as a metal cord (for example, a steel cord), an organic fiber cord, a resin-coated organic fiber cord, or a hard resin. The bead core 18 may be omitted if the rigidity of the bead portion 12 can be sufficiently secured.

  The side portion 14 is a portion constituting the side portion of the tire 10 and is gently curved so as to protrude outward from the bead portion 12 toward the crown portion 16 in the tire width direction.

  The crown portion 16 is a portion that supports a tread 30 (described later) disposed on the outer side in the tire radial direction, and has an outer peripheral surface that is substantially flat along the tire width direction.

  A belt layer 28 is disposed outside the crown portion 16 in the tire radial direction. The belt layer 28 is formed by winding the covering cord member 26 spirally in the tire circumferential direction. The details of the covering cord member 26 will be described later.

  A tread 30 is disposed outside the belt layer 28 in the tire radial direction. The tread 30 covers the belt layer 28. Further, the tread 30 is formed with a tread pattern (not shown) on the contact surface with the road surface.

  The tire frame member 17 is provided with a covering rubber 24 extending from the outer surface of the side portion 14 to the inner surface of the bead portion 12. As the rubber material constituting the covering rubber 24, a rubber material having higher weather resistance and sealability with a standard rim than the tire frame member 17 is used. In the present embodiment, the outer surface of the tire frame member 17 is all covered with the tread 30 and the covering rubber 24.

Next, the covering cord member 26 will be described in detail.
As shown in FIG. 2, the covering cord member 26 includes a reinforcing cord 32 extending in the tire circumferential direction, a covering resin layer 34 covering the reinforcing cord 32, and between the reinforcing cord 32 and the covering resin layer 34. And a bonding resin layer 36 for bonding (adhering) the reinforcing cord 32 and the covering resin layer 34 to each other.

  The reinforcing cord 32 is composed of a monofilament (single wire) such as a metal fiber or an organic fiber, or a multifilament (stranded wire) obtained by twisting these fibers. In the present embodiment, the reinforcing cord 32 is a metal cord made of metal fibers.

  The coating resin layer 34 is made of a coating resin material. As the resin material for covering, the same material as the resin material for skeleton forming the tire skeleton member 17 can be used. In this embodiment, a thermoplastic resin is used as the coating resin material, and the coating resin layer 34 is joined to the crown portion 16 by thermal welding.

  Further, in the present embodiment, since the covering resin layer 34 and the crown portion 16 are joined by thermal welding, it is preferable from the viewpoint of joining strength that the covering resin material and the skeleton resin material are the same resin material. The present invention is not limited to this configuration, and the coating resin material and the skeleton resin material may be different resin materials.

  The covering resin layer 34 has a substantially square cross-sectional shape. The cross-sectional shape of the coating resin layer 34 is not limited to a substantially square shape. For example, it may have a circular cross section or a trapezoidal cross section.

  The bonding resin layer 36 is formed of a bonding resin material having a higher elastic modulus than the coating resin material and having excellent adhesion to the reinforcing cord 32. Here, the “elastic modulus” refers to a tensile elastic modulus defined in JIS K7161. The elastic modulus of the bonding resin layer 36 is preferably set to 1 to 5 times the elastic modulus of the covering resin layer 34.

Examples of bonding resin materials include modified olefin resins (modified polyethylene resins, modified polypropylene resins, etc.), polyamide resins, polyurethane resins, polyester resins, ethylene-ethyl acrylate copolymers, ethylene-acetic acid. What contains 1 type, or 2 or more types of thermoplastic resins, such as a vinyl copolymer, as a main component (main ingredient) is mentioned. Among these, from the viewpoint of adhesion to the reinforcing metal cord member and the coating composition, from a modified olefin resin, a polyester resin, an ethylene-ethyl acrylate copolymer, and an ethylene-vinyl acetate copolymer A hot melt adhesive containing at least one selected from the above is preferable, and a modified olefin resin (acid-modified olefin resin) acid-modified with an unsaturated carboxylic acid is more preferable.
Here, “modified olefin resin acid-modified with an unsaturated carboxylic acid” means a modified olefin resin obtained by graft copolymerization of an unsaturated carboxylic acid with a polyolefin.
Moreover, as these olefin type thermoplastic elastomers, those having an elastic modulus of 140 MPa to 950 MPa are preferably used.

  The layer thickness T1 of the bonding resin layer 36 is larger (larger) than the layer thickness T2 of the coating resin layer 34. Here, the “layer thickness” refers to the thinnest portion of the thickness measured along the radial direction of the reinforcing cord 32 from the center of the reinforcing cord 32.

  In the present embodiment, the layer thickness T1 of the bonding resin layer 36 is set in the range of 500 μm to 5 mm.

As shown in FIGS. 1 and 2, the covering cord member 26 is wound around the outer periphery of the crown portion 16 in the tire circumferential direction and joined by thermal welding.
The covering cord member 26 is wound around the outer periphery of the crown portion 16 without a gap in the tire width direction, and adjacent portions in the tire width direction are joined together by heat welding. In addition, this invention is not limited to the said structure, For example, it is good also as a structure by which the covering cord member 26 is wound with a clearance gap in the tire width direction.

  Next, an example of the manufacturing method of the tire 10 of this embodiment is demonstrated.

First, the skeleton formation step will be described.
In the skeleton forming step, a pair of tire skeleton halves (not shown) are formed by injection molding the skeleton resin material and dividing the tire skeleton member 17 in half. In addition, the injection molding of the tire frame half is performed in a state where the bead core 18 formed in advance is arranged at a predetermined position in the mold. For this reason, a bead core 18 is embedded in the bead portion 12 of the molded tire frame half.

  Next, a pair of tire frame halves are joined together by heat welding to form the tire frame member 17.

  Thereafter, an unvulcanized coated rubber to be the coated rubber 24 is pasted from the outer surface of the side portion 14 to the inner surface of the bead portion 12 of the tire frame member 17. Thereby, the tire frame member 17 with unvulcanized coated rubber is formed.

  In the present embodiment, a pair of tire skeleton halves are formed and a pair of tire skeleton halves are joined to form a tire skeleton member. However, the present invention is not limited to this configuration. For example, the tire frame member 17 may be formed by dividing it into three or more parts, and the divided parts may be joined to form the tire frame member 17. Further, the tire frame member 17 may be formed without being divided.

Next, the covering cord member forming step will be described.
In the covering cord member forming step, first, the reinforcing cord 32 is coated with a molten adhesive resin material, and then coated with the molten covering resin material before the adhesive resin material is solidified. When the adhesive resin material and the coating resin material are cooled and solidified, the bonding resin layer 36 and the coating resin layer 34 are formed on the outer periphery of the reinforcing cord 32 to form the coated cord member 26.
The covering cord member forming step is not limited to the above-described configuration, and may be a configuration in which the adhesive resin material covering the reinforcing cord 32 is cooled and solidified and then covered with a molten covering resin material.

The shapes of the coating resin layer 34 and the bonding resin layer 36 can be changed by changing the shape of the extrusion port of an extruder (not shown). Similarly, the thickness of each of the coating resin layer 34 and the bonding resin layer 36 can be adjusted by changing the opening amount of the extrusion port of the extruder.
In this embodiment, the opening amount of the extrusion port of an extruder (not shown) is changed so that the layer thickness T1 of the bonding resin layer 36 is thicker (larger) than the layer thickness T2 of the coating resin layer 34. .

  Next, the belt forming process will be described. In this belt forming step, the belt layer 28 is formed on the outer periphery of the tire frame member 17. Specifically, the belt layer 28 is formed by winding the covering cord member 26 around the crown portion 16 of the tire frame member 17 in a spiral manner. Here, the reinforcing cord 32 is wound around the crown portion 16 while melting the portion of the coating resin layer 34 that contacts the outer surface of the crown portion 16, so that after the cooling and solidification of the coating resin material, the crown portion 16 is heated. It is firmly joined by welding.

  Next, the tread arrangement process will be described. In this tread arrangement step, an unvulcanized tread rubber (not shown) that becomes the tread 30 is arranged on the outer side in the tire radial direction of the belt layer 28. Specifically, a belt-shaped unvulcanized rubber tread for one round of the tire is wound around the outer periphery of the tire frame member 17 and bonded to the outer peripheral surfaces of the belt layer 28 and the tire frame member 17 using an adhesive.

  Next, the vulcanization process will be described. In this vulcanization step, the unvulcanized tread rubber and the unvulcanized coated rubber adhered to the tire frame member 17 are vulcanized. Specifically, the tire frame member 17 is set in a vulcanizer, and the unvulcanized tread rubber and the unvulcanized coated rubber are heated and vulcanized at a predetermined temperature for a predetermined time. Thereby, the unvulcanized coated rubber and the unvulcanized tread are vulcanized to reach the vulcanization degree of the final product.

  Next, the vulcanized tire 10 is taken out from the vulcanizer. Thereby, the tire 10 is completed.

  In addition, the order of each process in the manufacturing method of the tire which concerns on this embodiment can be changed suitably. For example, a belt layer 28 is disposed on the crown portion 16 of the tire frame member 17 and an unvulcanized tread 30 is disposed on the belt layer 28 before the unvulcanized coated rubber is attached to the tire frame member 17. Also good. Moreover, before joining a pair of tire halves, it is good also as a structure which affixes unvulcanized coating rubber to a tire half.

Next, the effect of the tire 10 of this embodiment is demonstrated.
In the tire 10, since the layer thickness T1 of the bonding resin layer 36 is thicker than the layer thickness T2 of the coating resin layer 34, for example, compared with the case where the layer thickness T1 is set to be equal to or less than the layer thickness T2. The resin layer 36 is hardened. Thereby, for example, even if an injury generated in the tread 30 reaches the coating resin layer 34 and the coating resin layer 34 is damaged as a result, the progress speed of the scratch is suppressed by the bonding resin layer 36. . Specifically, since the bonding resin layer 36 is formed of a bonding resin material having a higher elastic modulus than that of the coating resin material, it is possible to make the progress of scratches slower than that of the coating resin layer 34. For this reason, by making the layer thickness T1 of the bonding resin layer 36 thicker than the layer thickness T2 of the coating resin layer 34, the progress speed until the scratches generated in the coating resin layer 34 reach the reinforcing cord 32 is increased. Can be suppressed.

  On the other hand, since the elastic modulus of the coating resin material is lower than the elastic modulus of the bonding resin material, the difference in elastic modulus (stiffness difference) from the reinforcing cord 32, which is a metal cord, to the crown portion 16 can be reduced. Further, it is possible to suppress the peeling and the like between the reinforcing cord 32 and the covering resin layer 34.

  Furthermore, in the tire 10, since the layer thickness T1 of the bonding resin layer 36 is set in the range of 500 μm to 5 mm, the bonding resin layer 36 is further hardened. Thereby, the progress speed of the flaw in the bonding resin layer 36 can be further suppressed (slowed). When the layer thickness T1 is less than 500 μm, the bonding resin layer 36 is insufficient in thickness, and there is a possibility that the effect of suppressing the progress of scratches in the bonding resin layer 36 cannot be sufficiently ensured. On the other hand, when the layer thickness T1 is 5 mm or more, the bonding resin layer 36 becomes too hard, and there is a possibility that peeling between the reinforcing cord 32 and the covering resin layer 34 is likely to occur. Therefore, the layer thickness T1 of the bonding resin layer 36 is preferably set within a range of 500 μm to 5 mm.

  Further, since the covering cord member 26 is spirally wound around the outer periphery of the crown portion 16 of the tire frame member 17, the rigidity in the tire circumferential direction of the crown portion 16 is improved. Further, due to the effect of the belt layer 28 formed by the covering cord member 26, the radial growth of the crown portion 16 (a phenomenon in which the crown portion 16 swells in the radial direction) during tire rolling is suppressed.

  Furthermore, in the tire 10, since the covering resin layer 34 of the covering cord member 26 and the crown portion 16 of the tire frame member 17 are bonded by thermal welding, the bonding strength between the covering resin layer 34 and the crown portion 16 is high. improves. Thereby, the tire circumferential direction rigidity of the crown portion 16 is further improved.

  In the tire 10 according to the first embodiment, one covering cord member 26 is spirally wound and joined to the outer periphery of the crown portion 16 in the tire circumferential direction, but the present invention is not limited to this configuration. A belt-like body in which a plurality of coated cord members 26 are arranged in parallel may be wound and joined to the outer periphery of the crown portion 16 in a spiral manner in the tire circumferential direction.

  Moreover, in 1st Embodiment, although the outer peripheral surface of the crown part 16 is made flat in the tire width direction cross section, this invention is not limited to this structure, The said outer peripheral surface is not made flat in the tire width direction cross section. May be. For example, the outer peripheral surface of the crown portion 16 may have a curved shape (arc shape) inflated outward in the tire radial direction in the cross section in the tire width direction.

  In the manufacturing method of the tire 10 of the first embodiment, the covering resin layer 34 of the covering cord member 26 is in a molten state and the crown portion 16 and the covering cord member 26 are joined by thermal welding. It is not limited to this configuration. For example, the crown portion 16 and the covering cord member 26 may be bonded by heat welding with the outer peripheral surface of the crown portion 16 in a molten state. The covering resin layer 34 of the covering cord member 26 and the outer peripheral surface of the crown portion 16 It is good also as a structure which joins the crown part 16 and the coating | coated code | cord member 26 by thermal welding by making each into a molten state.

Second Embodiment
Next, a tire according to a second embodiment of the present invention will be described with reference to FIG. In addition, the same code | symbol is attached | subjected about the structure similar to 1st Embodiment, and description is abbreviate | omitted suitably.

  As shown in FIG. 3, the tire 40 has the same configuration as that of the tire 10 of the first embodiment, except that a coated cord member 44 is wound to form a bead core 42.

  The bead core 42 is formed by arranging a single coated cord member 44 while being wound in the tire circumferential direction so as to form a plurality of rows and a plurality of columns (4 rows and 4 columns in this embodiment).

The covering cord member 44 is disposed between the reinforcing cord 46 extending in the tire circumferential direction, the covering resin layer 48 covering the reinforcing cord 46, and the reinforcing cord 46 and the covering resin layer 48. A bonding resin layer 50 that bonds (adheres) the coating resin layer 48. In addition, as a material which comprises the reinforcement cord 46 of this embodiment, the material similar to the material which comprises the reinforcement cord 32 of 1st Embodiment may be used, and the resin layer 48 for coating | cover of this embodiment is comprised. As the coating resin material, the same material as the coating resin material constituting the coating resin layer 34 may be used, and as the bonding resin material constituting the bonding resin layer 50 of the present embodiment, the bonding resin material A material similar to the bonding resin material constituting the resin layer 36 may be used.
Further, the layer thickness T1 of the bonding resin layer 50 is larger than the layer thickness T2 of the coating resin layer 48.

  Further, the covering cord member 44 has portions adjacent to at least one of the tire width direction and the tire radial direction joined together by heat welding. A covering resin layer 48 of the covering cord member 44 that constitutes the outer peripheral portion of the bead core 42 is joined to the bead portion 12 by thermal welding. Specifically, in the skeleton molding process, since the injection molding is performed in a state where the preformed bead core 42 is arranged in the mold, the skeleton resin material and the outer periphery of the bead core 42 are configured in the mold. The coating resin layer 48 is bonded by heat welding.

  Next, the effect of the tire 40 of this embodiment is demonstrated. In addition, description is abbreviate | omitted about the effect obtained by the structure similar to the tire 10 of 1st Embodiment.

  In the tire 40, since the layer thickness T1 of the bonding resin layer 50 is thicker than the layer thickness T2 of the coating resin layer 48, for example, compared with a case where the layer thickness T1 is set to be equal to or less than the layer thickness T2. The resin layer 50 is hardened. Thereby, for example, even if an injury generated in the coating rubber 24 reaches the coating resin layer 48 and the coating resin layer 48 is damaged as a result, the progress rate of the scratch is suppressed by the bonding resin layer 50. The Specifically, since the bonding resin layer 50 is formed of a bonding resin material having a higher elastic modulus than that of the coating resin material, it is possible to make the progress of scratches slower than that of the coating resin layer 48. For this reason, by making the layer thickness T1 of the bonding resin layer 50 thicker than the layer thickness T2 of the coating resin layer 48, the progress speed until the scratches generated in the coating resin layer 48 reach the reinforcing cord 46 is increased. Can be suppressed.

  On the other hand, since the elastic modulus of the coating resin material is lower than that of the bonding resin material, the difference in elastic modulus (stiffness difference) from the reinforcing cord 46, which is a metal cord, to the bead portion 12 can be reduced. Further, it is possible to suppress the occurrence of peeling between the reinforcing cord 46 and the coating resin layer 48.

  Furthermore, in the tire 40, since the layer thickness T1 of the bonding resin layer 50 is set in the range of 500 μm to 5 mm, the bonding resin layer 50 is further hardened. Thereby, the progress speed of the damage | wound in the resin layer 50 for joining can further be suppressed (slow down). When the layer thickness T1 is less than 500 μm, the bonding resin layer 50 is insufficient in thickness, and there is a possibility that the effect of suppressing the progress of flaws in the bonding resin layer 50 cannot be sufficiently ensured. On the other hand, when the layer thickness T1 is set to 5 mm or more, the bonding resin layer 50 becomes too hard and the separation between the reinforcing cord 46 and the covering resin layer 48 may easily occur. Therefore, the layer thickness T1 of the bonding resin layer 50 is preferably set in the range of 500 μm to 5 mm.

  Moreover, in the tire 40, since the bead core 42 formed by the covering cord member 44 is embedded in the bead portion 12 and joined by thermal welding, the circumferential rigidity of the bead portion 12 of the tire frame member 17 is improved.

  Furthermore, in the tire 40, since the covering resin layer 48 of the covering cord member 44 and the bead portion 12 of the tire frame member 17 are bonded by thermal welding, the bonding of the covering resin layer 48 and the bead portion 12 is performed. Strength is improved. Thereby, the tire circumferential direction rigidity of the bead part 12 further improves.

  In the tire 40 of the second embodiment, the bead core 42 is configured by winding a single coated cord member 44 in the tire circumferential direction so as to form a plurality of rows and columns, but the present invention is limited to this configuration. Alternatively, the bead core 42 may be formed by winding a plurality of coated cord members 44 in parallel to form a belt-shaped body a plurality of times in the tire circumferential direction.

  In the tire 40 of the second embodiment, the belt layer 28 is formed by the covering cord member 26 and the bead core 42 is formed by the covering cord member 44, but the present invention is not limited to this configuration. As other embodiments, a belt layer is formed with a rubber-coated reinforcing cord while forming the bead core 42 with the covering cord member 44, or an uncoated reinforcing cord is embedded in the outer periphery of the crown portion 16 (partially embedded). The belt layer may be formed by winding the belt layer.

  In the first embodiment, the coating resin layer 34 of the coating cord member 26 is formed of a single coating resin material, but the present invention is not limited to this configuration. For example, the covering resin layer 34 of the covering cord member 26 may be composed of a plurality of covering resin materials having different elastic moduli. Specifically, like the covering cord member 60 shown in FIG. 4, the covering resin layer 62 is a multilayer, and each layer of the covering resin layer 62 is formed of a covering resin material having a different elastic modulus. Here, by lowering the elastic modulus of the outer resin layer 66 than the inner resin layer 64 constituting the coating resin layer 62, delamination due to the difference in elastic modulus can be suppressed. As a result, the durability of the tire is improved. The configuration in which the coating resin layer 62 of the coating cord member 60 is a multilayer may be applied to the coating resin layer 48 of the coating cord member 44 of the second embodiment.

  In the first embodiment, as shown in FIG. 2, the bonding resin layer 36 of the covering cord member 26 has a circular cross section, and the outer periphery thereof is covered with the covering resin layer 34 having a rectangular cross section. The present invention is not limited to this configuration. For example, as in the coated cord member 70 shown in FIG. 5, the bonding resin layer 72 may have a quadrangular cross section and the outer periphery thereof may be covered with the covering resin layer 74 having a quadrangular cross section. The configuration in which the cross-sectional shapes of the bonding resin layer 72 and the covering resin layer 74 of the covering cord member 70 are rectangular is applied to the covering resin layer 48 of the covering cord member 44 of the second embodiment. May be.

  The embodiments of the present invention have been described above with reference to the embodiments. However, these embodiments are merely examples, and various modifications can be made without departing from the scope of the invention, and the order of the manufacturing steps can be changed as appropriate. Is possible. It goes without saying that the scope of rights of the present invention is not limited to these embodiments.

10, 40 Tire 12 Bead portion 14 Side portion 16 Crown portion 17 Tire frame member 26, 44, 60, 70 Cover cord member 32, 46 Reinforcement cord 34, 48, 62, 74 Resin layer 36, 50, 72 for covering Resin layer T1 layer thickness T2 layer thickness

Claims (6)

An annular tire skeleton member formed of a skeleton resin material;
A reinforcing cord provided on the tire frame member and extending in the tire circumferential direction; a coating resin layer formed of a coating resin material, covering the reinforcement cord and bonded to the tire frame member; and the coating resin It is formed of a bonding resin material having a higher elastic modulus than the material, and is disposed between the reinforcing cord and the covering resin layer to bond the reinforcing cord and the covering resin layer, and has a layer thickness of the covering A coated cord member comprising a bonding resin layer thicker than the resin layer for use;
Tire with. The tire skeleton member includes a bead portion, a side portion continuous to the tire radial direction outer side of the bead portion, and a crown portion continuous to the tire width direction inner side of the side portion,
The tire according to claim 1, wherein the covering cord member is spirally wound around an outer periphery of the crown portion. The coating resin material has thermoplasticity,
The tire according to claim 2, wherein the covering resin layer and the crown portion are joined by heat welding. The tire skeleton member includes a bead portion, a side portion continuous to the tire radial direction outer side of the bead portion, and a crown portion continuous to the tire width direction inner side of the side portion,
The tire according to claim 1, wherein the covering cord member is embedded in the bead portion. The skeleton resin material has thermoplasticity,
The tire according to claim 4, wherein the coating resin layer and the bead portion are joined by heat welding.   The tire according to any one of claims 1 to 5, wherein a thickness of the bonding resin layer is 500 µm to 5 mm.