JP2017066255A - Manufacturing method of long fiber-reinforced composite material and long fiber-reinforced composite material - Google Patents
Manufacturing method of long fiber-reinforced composite material and long fiber-reinforced composite material Download PDFInfo
- Publication number
- JP2017066255A JP2017066255A JP2015192440A JP2015192440A JP2017066255A JP 2017066255 A JP2017066255 A JP 2017066255A JP 2015192440 A JP2015192440 A JP 2015192440A JP 2015192440 A JP2015192440 A JP 2015192440A JP 2017066255 A JP2017066255 A JP 2017066255A
- Authority
- JP
- Japan
- Prior art keywords
- long fiber
- composite material
- reinforced composite
- fiber reinforced
- metal foil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、長繊維強化複合材料の製造方法および長繊維強化複合材料に関する。 The present invention relates to a method for producing a long fiber reinforced composite material and a long fiber reinforced composite material.
長繊維強化複合材料は、長繊維材料とマトリックス樹脂を組み合わせたもので、軽量で剛性が高いことから、各種産業に、広く用いられている。マトリック ス樹脂としては、熱硬化性樹脂および熱可塑性樹脂のいずれもが用いられている。ここで、マトリックス樹脂として熱可塑性樹脂を利用したものについては、特許文献１〜３に記載がある。 The long fiber reinforced composite material is a combination of a long fiber material and a matrix resin, and is widely used in various industries because it is lightweight and has high rigidity. As the matrix resin, both a thermosetting resin and a thermoplastic resin are used. Here, the thing using a thermoplastic resin as a matrix resin has description in patent documents 1-3.
ここで、ポリアミド樹脂は、靱性・引っ張り強度に優れ、各種プラスチックの中でも融点が高く、耐薬品性や耐衝撃性等に強く、かつ、強化繊維によって強化可能であることから、長繊維強化複合材料として注目されている。しかしながら、マトリックス樹脂として、ポリアミド樹脂を用いた長繊維強化複合材料を用いた成形品は、近年、より高い機械的強度が求められる傾向にある。
本発明は、かかる課題を解決することを目的としたものであって、より高い機械的強度を有する成形品を提供可能な長繊維強化複合材料の製造方法および長繊維強化複合材料を提供することを目的とする。
Here, polyamide resin is excellent in toughness and tensile strength, has a high melting point among various plastics, is strong in chemical resistance, impact resistance, etc., and can be reinforced by reinforcing fibers. It is attracting attention as. However, molded products using a long fiber reinforced composite material using a polyamide resin as a matrix resin have recently been required to have higher mechanical strength.
The present invention is intended to solve such problems, and provides a method for producing a long fiber reinforced composite material and a long fiber reinforced composite material capable of providing a molded article having higher mechanical strength. With the goal.
上記課題のもと、所定のポリアミド樹脂と、長繊維を、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物を表面に有する金属箔で挟んだ状態で、熱プレスして長繊維強化複合材料を製造することにより、さらに高い機械的強度を有する成形品を達成可能であることを見出した。具体的には、下記＜１＞により、好ましくは＜２＞〜＜１４＞により、上記課題を解決しうることを見出した。
＜１＞ポリアミド樹脂と長繊維を、第１の金属箔と第２の金属箔で挟んで熱プレスし、前記熱プレス後、第１の金属箔および第２の金属箔を剥離することを含み、
前記第１の金属箔は、前記ポリアミド樹脂または長繊維と接する側の表面に、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物を有し、前記ポリアミド樹脂は、ジアミン由来の構成単位とジカルボン酸由来の構成単位から構成され、前記ジアミン由来の構成単位の７０モル％以上が、キシリレンジアミンに由来する、長繊維強化複合材料の製造方法。
＜２＞前記ケイ素原子を含む化合物は、シロキサン結合を含む、＜１＞に記載の長繊維強化複合材料の製造方法。
＜３＞前記熱プレスは、２７０〜３２０℃で行う、＜１＞または＜２＞に記載の長繊維強化複合材料の製造方法。
＜４＞前記第２の金属箔の表面に、さらに、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物を有する、＜１＞〜＜３＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜５＞前記熱プレスを、１〜６ＭＰａの圧力で１０秒〜３分間行う、＜１＞〜＜４＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜６＞前記熱プレスは、ポリアミド樹脂フィルムと、シート状の長繊維を、前記第１の金属箔と第２の金属箔で挟んで行う、＜１＞〜＜５＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜７＞前記熱プレスは、２枚以上のポリアミド樹脂フィルムと、２枚以上のシート状の長繊維を交互に積層し、前記第１の金属箔と第２の金属箔で挟んで行う、＜１＞〜＜５＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜８＞前記熱プレスは、ダブルベルトプレス機を用いて行う、＜１＞〜＜７＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜９＞前記長繊維強化複合材料の厚さが、３０μｍ〜３ｍｍである、＜１＞〜＜８＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜１０＞前記ジカルボン酸由来の構成単位の７０モル％以上が、炭素数４〜２０のα,ω−直鎖脂肪族ジカルボン酸に由来する、＜１＞〜＜９＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜１１＞前記ジカルボン酸由来の構成単位の７０モル％以上が、アジピン酸およびセバシン酸の少なくとも一方に由来する、＜１＞〜＜１０＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜１２＞前記長繊維は、炭素繊維およびガラス繊維の少なくとも１種である、＜１＞〜＜１１＞のいずれかに記載の長繊維強化複合材料の製造方法。
＜１３＞ポリアミド樹脂が長繊維に含浸している長繊維強化複合材料であって、前記長繊維強化複合材料の表面に、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物からなるエポキシ樹脂層を有し、前記ジアミン由来の構成単位の７０モル％以上が、キシリレンジアミンに由来し、エポキシ樹脂層の厚さが、５μｍ以下である、長繊維強化複合材料。
＜１４＞＜１＞〜＜１２＞のいずれかに記載の長繊維強化複合材料の製造方法にて、長繊維強化複合材料を製造し、前記長繊維強化複合材料を複数枚積層して、加熱加工することを含む、成形品の製造方法。
Under the above-mentioned problem, in a state where a predetermined polyamide resin and long fibers are sandwiched between metal foils having a composition containing 1 to 30 parts by weight of a compound containing silicon atoms on the surface with respect to 100 parts by weight of epoxy resin, It has been found that a molded article having higher mechanical strength can be achieved by hot pressing to produce a long fiber reinforced composite material. Specifically, it has been found that the above problem can be solved by the following <1>, preferably by <2> to <14>.
<1> including heat-pressing a polyamide resin and long fibers sandwiched between a first metal foil and a second metal foil, and peeling the first metal foil and the second metal foil after the hot pressing ,
The first metal foil has a composition containing 1 to 30 parts by weight of a compound containing a silicon atom with respect to 100 parts by weight of an epoxy resin on a surface in contact with the polyamide resin or long fibers, and the polyamide resin Is a method for producing a long fiber reinforced composite material, which is composed of a structural unit derived from diamine and a structural unit derived from dicarboxylic acid, and 70 mol% or more of the structural unit derived from diamine is derived from xylylenediamine.
<2> The method for producing a long fiber reinforced composite material according to <1>, wherein the compound containing a silicon atom contains a siloxane bond.
<3> The method for producing a long fiber reinforced composite material according to <1> or <2>, wherein the hot pressing is performed at 270 to 320 ° C.
<4> Any one of <1> to <3>, further comprising a composition containing 1 to 30 parts by weight of a compound containing a silicon atom with respect to 100 parts by weight of the epoxy resin on the surface of the second metal foil. A method for producing the long fiber reinforced composite material described in 1.
<5> The method for producing a long fiber reinforced composite material according to any one of <1> to <4>, wherein the hot pressing is performed at a pressure of 1 to 6 MPa for 10 seconds to 3 minutes.
<6> The hot press according to any one of <1> to <5>, in which the polyamide resin film and a sheet-like long fiber are sandwiched between the first metal foil and the second metal foil. A method for producing a long fiber reinforced composite material.
<7> The hot press is performed by alternately laminating two or more polyamide resin films and two or more sheet-like long fibers and sandwiching the first metal foil and the second metal foil. The manufacturing method of the long fiber reinforced composite material in any one of 1>-<5>.
<8> The method for producing a long fiber reinforced composite material according to any one of <1> to <7>, wherein the hot pressing is performed using a double belt press.
<9> The method for producing a long fiber reinforced composite material according to any one of <1> to <8>, wherein the long fiber reinforced composite material has a thickness of 30 μm to 3 mm.
<10> 70% by mole or more of the structural unit derived from the dicarboxylic acid is derived from an α, ω-linear aliphatic dicarboxylic acid having 4 to 20 carbon atoms, according to any one of <1> to <9>. A method for producing a long fiber reinforced composite material.
<11> The method for producing a long fiber reinforced composite material according to any one of <1> to <10>, wherein 70 mol% or more of the structural unit derived from the dicarboxylic acid is derived from at least one of adipic acid and sebacic acid. .
<12> The method for producing a long fiber reinforced composite material according to any one of <1> to <11>, wherein the long fiber is at least one of carbon fiber and glass fiber.
<13> A long fiber reinforced composite material in which a polyamide resin is impregnated in a long fiber, wherein 1 to 30 parts by weight of a compound containing a silicon atom with respect to 100 parts by weight of an epoxy resin on the surface of the long fiber reinforced composite material A long fiber reinforced composite having an epoxy resin layer comprising a composition comprising: 70 mol% or more of the structural unit derived from the diamine is derived from xylylenediamine, and the thickness of the epoxy resin layer is 5 μm or less material.
<14> A method for producing a long fiber reinforced composite material according to any one of <1> to <12>, producing a long fiber reinforced composite material, laminating a plurality of the long fiber reinforced composite materials, and heating The manufacturing method of a molded article including processing.
本発明により、より高い機械的強度を有する成形品を提供可能な長繊維強化複合材料の製造方法および長繊維強化複合材料を提供可能になった。 According to the present invention, it is possible to provide a method for producing a long fiber reinforced composite material and a long fiber reinforced composite material capable of providing a molded article having higher mechanical strength.
以下において、本発明の内容について詳細に説明する。尚、本願明細書において「〜」とはその前後に記載される数値を下限値及び上限値として含む意味で使用される。 Hereinafter, the contents of the present invention will be described in detail. In the present specification, “to” is used to mean that the numerical values described before and after it are included as a lower limit value and an upper limit value.
本発明の長繊維強化複合材料の製造方法は、ポリアミド樹脂と長繊維を、第１の金属箔と第２の金属箔で挟んで熱プレスし、前記熱プレス後、第１の金属箔および第２の金属箔を剥離することを含み、前記第１の金属箔は、前記ポリアミド樹脂または長繊維と接する側の表面に、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物（以下、「エポキシ樹脂組成物」ということがある）を有し、前記ポリアミド樹脂は、ジアミン由来の構成単位とジカルボン酸由来の構成単位から構成され、前記ジアミン由来の構成単位の７０モル％以上が、キシリレンジアミンに由来する（以下、「キシリレン系ポリアミド樹脂という」）ことを特徴とする。
このような製造方法によって、長繊維強化複合材料を製造することにより、より高い機械的強度を有する成形品を提供可能な長繊維強化複合材料が得られる。特に、曲げ弾性率および曲げ強度に優れた成形品を提供可能な長繊維強化複合材料が得られる。このメカニズムは、推定であるが、エポキシ樹脂組成物が熱プレス時に、キシリレン系ポリアミド樹脂と表層部分のみで混合することに寄与していると考えられる。また、本発明における長繊維強化複合材料は、複数枚を積層して成形加工されることが多いが、この場合にも、エポキシ樹脂組成物がそれぞれの長繊維強化複合材料間の層間剥離を抑え、成形品の機械的強度を向上させると推定される。シロキサン結合を含む化合物などの、ケイ素原子を含む化合物は、一般的に離型性があり、層間剥離を引き起こしやすいと考えられていた。しかしながら、本発明では、樹脂として、キシリレン系ポリアミド樹脂を採用することにより、驚くべきことに、高い機械的強度を達成したものである。
特に、後述する実施例で述べるように、代表的なポリアミド樹脂であるポリアミド６を用いても、同様の傾向が認められないことから、本発明の効果は驚くべきものである。
以下、本発明について詳細に説明する。
In the method for producing a long fiber reinforced composite material of the present invention, a polyamide resin and a long fiber are hot-pressed between a first metal foil and a second metal foil, and after the hot pressing, the first metal foil and the
By producing a long fiber reinforced composite material by such a production method, a long fiber reinforced composite material capable of providing a molded article having higher mechanical strength can be obtained. In particular, a long fiber reinforced composite material capable of providing a molded article having excellent bending elastic modulus and bending strength can be obtained. Although this mechanism is presumed, it is considered that the epoxy resin composition contributes to mixing with the xylylene-based polyamide resin only in the surface layer portion during hot pressing. In addition, the long fiber reinforced composite material in the present invention is often formed by laminating a plurality of sheets. In this case as well, the epoxy resin composition suppresses delamination between the long fiber reinforced composite materials. It is estimated that the mechanical strength of the molded product is improved. A compound containing a silicon atom, such as a compound containing a siloxane bond, is generally considered to be releasable and likely to cause delamination. However, in the present invention, surprisingly, a high mechanical strength is achieved by employing a xylylene-based polyamide resin as the resin.
In particular, as will be described later in Examples, even when
Hereinafter, the present invention will be described in detail.
＜熱プレス＞
本発明の製造方法は、キシリレン系ポリアミド樹脂と長繊維を、第１の金属箔と第２の金属箔で挟んで熱プレスすることを含む。熱プレスにより、キシリレン系ポリアミド樹脂が長繊維中に含浸する。熱プレスは、２７０〜３２０℃で行うことが好ましく、２８０〜３１０℃で行うことがより好ましい。このような範囲とすることにより、キシリレン系ポリアミド樹脂が適切に溶融し、長繊維中への含浸性が高まると共に、得られる長繊維強化複合材料の黄色化をより効果的に抑制できる。
熱プレスの圧力は、１〜６ＭＰａが好ましく、２〜５ＭＰａがより好ましく、３〜５ＭＰａがさらに好ましい。このような範囲とすることにより、長繊維のキシリレン系ポリアミド樹脂への含浸が促進され、得られる長繊維強化複合材料中のボイドをより減少させることが可能となる。
また、熱プレスの時間は、１０秒〜３分間が好ましく、３０秒〜２分３０秒間がより好ましい。このような範囲とすることにより、得られる長繊維強化複合材料の黄色化を抑えつつ、キシリレン系ポリアミド樹脂を適切に含浸させることができる。
<Hot press>
The production method of the present invention includes hot pressing a xylylene-based polyamide resin and a long fiber sandwiched between a first metal foil and a second metal foil. The long fiber is impregnated with the xylylene-based polyamide resin by hot pressing. The hot pressing is preferably performed at 270 to 320 ° C, more preferably 280 to 310 ° C. By setting it as such a range, while a xylylene-type polyamide resin fuse | melts appropriately, the impregnation property to a long fiber increases, and yellowing of the obtained long fiber reinforced composite material can be suppressed more effectively.
The pressure of the hot press is preferably 1 to 6 MPa, more preferably 2 to 5 MPa, and further preferably 3 to 5 MPa. By setting it as such a range, the impregnation to the xylylene-type polyamide resin of a long fiber is accelerated | stimulated, and it becomes possible to further reduce the void in the obtained long fiber reinforced composite material.
The hot pressing time is preferably 10 seconds to 3 minutes, more preferably 30 seconds to 2 minutes 30 seconds. By setting it as such a range, a xylylene-type polyamide resin can be impregnated appropriately, suppressing yellowing of the obtained long fiber reinforced composite material.
熱プレスは、キシリレン系ポリアミド樹脂と長繊維を、第１の金属箔と第２の金属箔で挟んで行う。
キシリレン系ポリアミド樹脂は、ポリアミド樹脂フィルムが好ましい。ポリアミド樹脂フィルムの厚さとしては、例えば、２０〜１００μｍが好ましく、２０〜８０μｍがより好ましい。フィルム以外には、ペレットや粉状・繊維状のキシリレン系ポリアミド樹脂などを用いてもよい。
長繊維も、その形態等を特に定めるものではないが、シート状の長繊維が好ましい。
キシリレン系ポリアミド樹脂や長繊維として、フィルムやシート状のものを用いる場合、熱プレスは、複数枚のポリアミド樹脂フィルムとシート状の長繊維を、交互に積層した状態で、第１の金属箔と第２の金属箔で挟んで行うことが好ましい。具体的には、熱プレスは、２枚以上のポリアミド樹脂フィルムと、２枚以上のシート状の長繊維を交互に積層し、第１の金属箔と第２の金属箔で挟んで行うことが例示され、より好ましくは、熱プレスは、３枚以上のポリアミド樹脂フィルムと２枚以上のシート状の長繊維を交互に積層した状態で、第１の金属箔と第２の金属箔で挟んで行うことが挙げられる。ポリアミド樹脂フィルムとシート状の長繊維の積層枚数としては、合計で２〜１３枚が好ましく、２〜１１枚がより好ましく、３〜９枚がさらに好ましい。
本発明では、ポリアミド樹脂フィルムが、第１の金属箔に接するように積層されることが好ましく、第１の金属箔および第２の金属箔の両方に、ポリアミド樹脂フィルムが接するように積層されることがさらに好ましい。このような構成とすることにより、エポキシ樹脂組成物とキシリレン系ポリアミド樹脂が混合しやすくなり、本発明の効果がより効果的に発揮される。
The hot pressing is performed by sandwiching the xylylene-based polyamide resin and the long fibers between the first metal foil and the second metal foil.
The xylylene-based polyamide resin is preferably a polyamide resin film. As thickness of a polyamide resin film, 20-100 micrometers is preferable, for example, and 20-80 micrometers is more preferable. Other than the film, pellets, powdery / fibrous xylylene-based polyamide resins, and the like may be used.
The form of the long fiber is not particularly defined, but a sheet-like long fiber is preferable.
When a film or sheet-like material is used as the xylylene-based polyamide resin or long fiber, the hot press is a state in which a plurality of polyamide resin films and sheet-like long fibers are alternately laminated, It is preferable to sandwich the second metal foil. Specifically, the hot pressing may be performed by alternately laminating two or more polyamide resin films and two or more sheet-like long fibers and sandwiching them between the first metal foil and the second metal foil. More preferably, the hot press is sandwiched between the first metal foil and the second metal foil in a state where three or more polyamide resin films and two or more sheet-like long fibers are alternately laminated. To do. The total number of laminated polyamide resin films and sheet-like long fibers is preferably 2 to 13, more preferably 2 to 11, and even more preferably 3 to 9.
In the present invention, the polyamide resin film is preferably laminated so as to be in contact with the first metal foil, and is laminated so that the polyamide resin film is in contact with both the first metal foil and the second metal foil. More preferably. By setting it as such a structure, it becomes easy to mix an epoxy resin composition and a xylylene-type polyamide resin, and the effect of this invention is exhibited more effectively.
熱プレスは、ダブルベルトプレス機を用いて行うことが好ましい。ダブルベルトプレス機を用いることにより、長繊維複合強化樹脂材料を連続的にかつ、面厚で均一に加温及び加圧することができる。図１は、ダブルベルトプレス機の構成の概略図を示したものである。図１に示す実施形態では、加熱加圧ユニット１を有するベルトタイプのプレス機の間に、第１の金属箔２と、ポリアミド樹脂フィルム３、シート状の長繊維４、ポリアミド樹脂３、第２の金属箔５を搬送させ、加熱しながらプレスし、その後、冷却加熱ユニット６でプレス（冷却プレス）しながら冷却している。すなわち、本発明の製造方法は、熱プレスの後、冷却することが好ましく、冷却プレスにより冷却することがより好ましい。冷却プレスをすることにより、熱プレスした材料が膨らんで強度が落ちることをより効果的に抑制することが可能になる。冷却プレスの温度は、（熱プレスの温度−２００℃）〜（熱プレスの温度−１００℃）が好ましい。冷却プレスの圧力は、１〜６ＭＰａが好ましく、２〜５ＭＰａがより好ましく、３〜５ＭＰａがさらに好ましい。冷却プレスの時間としては、５秒〜１．５分が好ましい。熱プレスの後、そのままの圧力で冷却プレスすることが一実施形態として例示される。
再び図１に戻り、図１では、２枚のポリアミド樹脂フィルムと１枚のシート状の長繊維を積層している。さらに、ポリアミド樹脂フィルムの枚数やシート状の長繊維の枚数を増やしてもよい。
本実施形態において、ポリアミド樹脂と長繊維を含む材料の搬送速度は、０．５〜５ｍ／分であることが好ましく、０．８〜２ｍ／分であることがより好ましい。加熱温度および加熱時間は、上記と同様であり、好ましい範囲も同様である。尚、熱プレスは、加熱と加圧を完全に同時に行う場合の他、加熱と加圧の一部が同時に行われる場合も含む趣旨である。
熱プレス時に与える複合材料の目付あたりの熱量は加熱時間と温度、圧力で調整することができる。その熱量は、５００（ΔＴ・ｔ・ｍ2／ｇ）以下であることが好ましく、４００（ΔＴ・ｔ・ｍ2／ｇ）以下であることがより好ましく、３００（ΔＴ・ｔ・ｍ2／ｇ）以下であることがさらに好ましい。このような範囲にすることで得られる長繊維強化複合材料の黄色化をより効果的に抑えることができる。
ここで複合材料の目付あたりの熱量とは、材料が成形開始から終わりまでの温度変化（ΔＴ）を時間（ｔ）で乗じた値を、目付（ｇ／ｍ2）で除したものである。複合材料の温度変化は、温度センサーをダブルベルトプレス機に通して測定した実測値に基づく。
The hot press is preferably performed using a double belt press. By using a double belt press machine, the long fiber composite reinforced resin material can be continuously heated and pressurized uniformly with a surface thickness. FIG. 1 shows a schematic diagram of the configuration of a double belt press. In the embodiment shown in FIG. 1, a first metal foil 2, a
Returning again to FIG. 1, in FIG. 1, two polyamide resin films and one sheet-like long fiber are laminated. Furthermore, the number of polyamide resin films and the number of sheet-like long fibers may be increased.
In this embodiment, it is preferable that the conveyance speed of the material containing a polyamide resin and a long fiber is 0.5-5 m / min, and it is more preferable that it is 0.8-2 m / min. The heating temperature and heating time are the same as described above, and the preferred ranges are also the same. The hot press is intended to include not only the case where heating and pressurization are performed completely simultaneously but also the case where a part of heating and pressurization is performed simultaneously.
The amount of heat per unit weight of the composite material applied during hot pressing can be adjusted by heating time, temperature, and pressure. The amount of heat is preferably 500 (ΔT · t · m 2 / g) or less, more preferably 400 (ΔT · t · m 2 / g) or less, and 300 (ΔT · t · m 2 / g). g) More preferably, it is the following. Yellowing of the long fiber reinforced composite material obtained by setting it in such a range can be suppressed more effectively.
Here, the amount of heat per unit weight of the composite material is obtained by dividing the value obtained by multiplying the temperature change (ΔT) from the start to the end of molding by time (t) by the basis weight (g / m 2 ). The temperature change of the composite material is based on an actual measurement value measured by passing a temperature sensor through a double belt press.
本発明ではさらに、通常は、熱プレス後、第１の金属箔および第２の金属箔を剥離することを含む。金属箔を剥離後、芯材に巻き取って巻き取り品とすることが好ましい。 The present invention further usually includes peeling the first metal foil and the second metal foil after hot pressing. After peeling off the metal foil, it is preferable to wind it around a core material to obtain a wound product.
＜キシリレン系ポリアミド樹脂＞
本発明で用いるキシリレン系ポリアミド樹脂は、ジアミン由来の構成単位とジカルボン酸由来の構成単位から構成され、ジアミン由来の構成単位の７０モル％以上が、キシリレンジアミンに由来することを特徴とする。すなわち、ジアミンの７０モル％以上がキシリレンジアミンに由来し、ジカルボン酸と重縮合されたキシリレン系ポリアミド樹脂である。
ジアミン由来の構成単位に占めるキシリレンジアミンに由来する構成単位は、８０モル％以上であることが好ましく、９０モル％以上であることがより好ましく、９５モル％以上であることがさらに好ましい。上限については、特に定めるものではないが、例えば、１００モル％とすることもできる。また、ジカルボン酸由来の構成単位の好ましくは５０モル％以上、より好ましくは７０モル％以上、特に好ましくは８０モル％以上、一層好ましくは９０モル％以上、より一層好ましくは９５モル％以上が、炭素原子数が好ましくは４〜２０のα，ω−直鎖脂肪族ジカルボン酸に由来することがさらに好ましい。上限については、特に定めるものではないが、例えば、１００モル％とすることもできる。
キシリレンジアミンはメタキシリレンジアミンおよびパラキシリレンジアミンの少なくとも１種であることが好ましい。
<Xylylene-based polyamide resin>
The xylylene-based polyamide resin used in the present invention is composed of a structural unit derived from diamine and a structural unit derived from dicarboxylic acid, and 70 mol% or more of the structural unit derived from diamine is derived from xylylenediamine. That is, it is a xylylene-based polyamide resin in which 70 mol% or more of the diamine is derived from xylylenediamine and polycondensed with a dicarboxylic acid.
The structural unit derived from xylylenediamine occupying the structural unit derived from diamine is preferably 80 mol% or more, more preferably 90 mol% or more, and further preferably 95 mol% or more. The upper limit is not particularly defined, but may be, for example, 100 mol%. Further, the structural unit derived from dicarboxylic acid is preferably 50 mol% or more, more preferably 70 mol% or more, particularly preferably 80 mol% or more, more preferably 90 mol% or more, still more preferably 95 mol% or more. More preferably, it is derived from an α, ω-linear aliphatic dicarboxylic acid having 4 to 20 carbon atoms. The upper limit is not particularly defined, but may be, for example, 100 mol%.
The xylylenediamine is preferably at least one of metaxylylenediamine and paraxylylenediamine.
キシリレン系ポリアミド樹脂の原料ジアミン成分として用いることが出来るメタキシリレンジアミンおよびパラキシリレンジアミン以外のジアミンとしては、テトラメチレンジアミン、ペンタメチレンジアミン、２−メチルペンタンジアミン、ヘキサメチレンジアミン、ヘプタメチレンジアミン、オクタメチレンジアミン、ノナメチレンジアミン、デカメチレンジアミン、ドデカメチレンジアミン、２，２，４−トリメチル−ヘキサメチレンジアミン、２，４，４−トリメチルヘキサメチレンジアミン等の脂肪族ジアミン、１，３−ビス（アミノメチル）シクロヘキサン、１，４−ビス（アミノメチル）シクロヘキサン、１，３−ジアミノシクロヘキサン、１，４−ジアミノシクロヘキサン、ビス（４−アミノシクロヘキシル）メタン、２，２−ビス（４−アミノシクロヘキシル）プロパン、ビス（アミノメチル）デカリン、ビス（アミノメチル）トリシクロデカン等の脂環式ジアミン、ビス（４−アミノフェニル）エーテル、パラフェニレンジアミン、ビス（アミノメチル）ナフタレン等の芳香環を有するジアミン等を例示することができ、１種または２種以上を混合して使用できる。
ジアミン成分として、キシリレンジアミン以外のジアミンを用いる場合、その割合は、ジアミン由来の構成単位の５０モル％以下であり、３０モル％以下であることが好ましく、より好ましくは１〜２５モル％、特に好ましくは５〜２０モル％である。
Examples of diamines other than metaxylylenediamine and paraxylylenediamine that can be used as raw material diamine components for xylylene-based polyamide resins include tetramethylenediamine, pentamethylenediamine, 2-methylpentanediamine, hexamethylenediamine, heptamethylenediamine, Aliphatic diamines such as octamethylenediamine, nonamethylenediamine, decamethylenediamine, dodecamethylenediamine, 2,2,4-trimethyl-hexamethylenediamine, 2,4,4-trimethylhexamethylenediamine, 1,3-bis ( Aminomethyl) cyclohexane, 1,4-bis (aminomethyl) cyclohexane, 1,3-diaminocyclohexane, 1,4-diaminocyclohexane, bis (4-aminocyclohexyl) methane, 2, -Alicyclic diamines such as bis (4-aminocyclohexyl) propane, bis (aminomethyl) decalin, bis (aminomethyl) tricyclodecane, bis (4-aminophenyl) ether, paraphenylenediamine, bis (aminomethyl) Examples include diamines having an aromatic ring such as naphthalene, and one or two or more of them can be used in combination.
When a diamine other than xylylenediamine is used as the diamine component, the proportion is 50 mol% or less of the structural unit derived from the diamine, preferably 30 mol% or less, more preferably 1 to 25 mol%, Most preferably, it is 5-20 mol%.
ポリアミド樹脂の原料ジカルボン酸成分として用いるのに好ましい炭素原子数４〜２０のα，ω−直鎖脂肪族ジカルボン酸としては、例えばコハク酸、グルタル酸、ピメリン酸、スベリン酸、アゼライン酸、アジピン酸、セバシン酸、ウンデカン二酸、ドデカン二酸等の脂肪族ジカルボン酸が例示でき、１種又は２種以上を混合して使用できるが、これらの中でもポリアミド樹脂の融点が成形加工するのに適切な範囲となることから、アジピン酸またはセバシン酸が好ましい。 Preferred examples of the α, ω-linear aliphatic dicarboxylic acid having 4 to 20 carbon atoms to be used as the raw material dicarboxylic acid component of the polyamide resin include succinic acid, glutaric acid, pimelic acid, suberic acid, azelaic acid, and adipic acid. Examples thereof include aliphatic dicarboxylic acids such as sebacic acid, undecanedioic acid, dodecanedioic acid and the like, and one or a mixture of two or more can be used. Among these, the melting point of the polyamide resin is suitable for molding processing. Since it becomes a range, adipic acid or sebacic acid is preferable.
上記炭素原子数４〜２０のα，ω−直鎖脂肪族ジカルボン酸以外のジカルボン酸成分としては、イソフタル酸、テレフタル酸、オルソフタル酸等のフタル酸化合物、１，２−ナフタレンジカルボン酸、１，３−ナフタレンジカルボン酸、１，４−ナフタレンジカルボン酸、１，５−ナフタレンジカルボン酸、１，６−ナフタレンジカルボン酸、１，７−ナフタレンジカルボン酸、１，８−ナフタレンジカルボン酸、２，３−ナフタレンジカルボン酸、２，６−ナフタレンジカルボン酸、２，７−ナフタレンジカルボン酸といった異性体等のナフタレンジカルボン酸等を例示することができ、１種又は２種以上を混合して使用できる。 Examples of the dicarboxylic acid component other than the α, ω-linear aliphatic dicarboxylic acid having 4 to 20 carbon atoms include phthalic acid compounds such as isophthalic acid, terephthalic acid and orthophthalic acid, 1,2-naphthalenedicarboxylic acid, 3-naphthalenedicarboxylic acid, 1,4-naphthalenedicarboxylic acid, 1,5-naphthalenedicarboxylic acid, 1,6-naphthalenedicarboxylic acid, 1,7-naphthalenedicarboxylic acid, 1,8-naphthalenedicarboxylic acid, 2,3- Examples thereof include naphthalenedicarboxylic acid such as isomers such as naphthalenedicarboxylic acid, 2,6-naphthalenedicarboxylic acid, and 2,7-naphthalenedicarboxylic acid, and one kind or a mixture of two or more kinds can be used.
ジカルボン酸成分として、炭素原子数４〜２０のα，ω−直鎖脂肪族ジカルボン酸以外のジカルボン酸を用いる場合は、成形加工性、バリア性の点から、テレフタル酸、イソフタル酸を用いることが好ましい。テレフタル酸、イソフタル酸を用いる場合、その割合は、好ましくはジカルボン酸由来の構成単位の３０モル％以下であり、より好ましくは１〜３０モル％、特に好ましくは５〜２０モル％の範囲である。 When a dicarboxylic acid other than an α, ω-linear aliphatic dicarboxylic acid having 4 to 20 carbon atoms is used as the dicarboxylic acid component, terephthalic acid or isophthalic acid may be used from the viewpoint of molding processability and barrier properties. preferable. When terephthalic acid or isophthalic acid is used, the proportion thereof is preferably 30 mol% or less, more preferably 1 to 30 mol%, particularly preferably 5 to 20 mol% of the structural unit derived from dicarboxylic acid. .
さらに、ジアミン成分、ジカルボン酸成分以外にも、キシリレン系ポリアミド樹脂を構成する成分として、本発明の効果を損なわない範囲でε−カプロラクタムやラウロラクタム等のラクタム類、アミノカプロン酸、アミノウンデカン酸等の脂肪族アミノカルボン酸類も共重合成分として使用できる。 Furthermore, in addition to the diamine component and the dicarboxylic acid component, as components constituting the xylylene-based polyamide resin, lactams such as ε-caprolactam and laurolactam, aminocaproic acid, aminoundecanoic acid and the like as long as the effects of the present invention are not impaired. Aliphatic aminocarboxylic acids can also be used as copolymerization components.
キシリレン系ポリアミド樹脂として、ポリメタキシリレンアジパミド樹脂、ポリメタキシリレンセバカミド樹脂、ポリパラキシリレンセバカミド樹脂、及び、メタキシリレンジアミンとパラキシリレンジアミンの混合キシリレンジアミンをセバシン酸と重縮合してなるポリメタキシリレン／パラキシリレン混合セバカミド樹脂が好ましく、より好ましいものは、ポリメタキシリレンセバカミド樹脂、ポリパラキシリレンセバカミド樹脂、及び、メタキシリレンジアミンとパラキシリレンジアミンの混合キシリレンジアミンをセバシン酸と重縮合してなるポリメタキシリレン／パラキシリレン混合セバカミド樹脂である。これらのポリアミド樹脂は成形加工性が特に良好となる傾向にある。 As xylylene-based polyamide resin, polymetaxylylene adipamide resin, polymetaxylylene sebacamide resin, polyparaxylylene sebacamide resin, and mixed xylylenediamine of paraxylylenediamine and paraxylylenediamine are sebacic acid A polymetaxylylene / paraxylylene mixed sebacamide resin obtained by polycondensation with poly (xylene) is preferable, and more preferable are polymetaxylylene sebacamide resin, polyparaxylylene sebacamide resin, and metaxylylenediamine and paraxylylenediamine It is a polymetaxylylene / paraxylylene mixed sebacamide resin obtained by polycondensation of the above mixed xylylenediamine with sebacic acid. These polyamide resins tend to have particularly good moldability.
キシリレン系ポリアミド樹脂のガラス転移点は、４０〜１８０℃であることが好ましく、６０〜１３０℃であることがより好ましい。
キシリレン系ポリアミド樹脂の数平均分子量は、５０００〜４５０００であることが好ましく、１００００〜２５０００であることがより好ましい。
キシリレン系ポリアミド樹脂の融点は、１９０〜３４０℃であることが好ましく、２００〜３４０℃であることがより好ましく、２００〜３２０℃であることがさらに好ましい。
融点とは、ＤＳＣ（示差走査熱量測定）法により観測される昇温時の吸熱ピークのピークトップの温度である。また、ガラス転移点とは、試料を一度加熱溶融させ熱履歴による結晶性への影響をなくした後、再度昇温して測定されるガラス転移点をいう。測定には、例えば、島津製作所社（ＳＨＩＭＡＤＺＵ ＣＯＲＰＯＲＡＴＩＯＮ）製「ＤＳＣ−６０」を用い、試料量は約５ｍｇとし、雰囲気ガスとしては窒素を３０ｍｌ／分で流し、昇温速度は１０℃／分の条件で室温から予想される融点以上の温度まで加熱し溶融させた際に観測される吸熱ピークのピークトップの温度から融点を求めることができる。次いで、溶融したポリアミド樹脂を、ドライアイスで急冷し、１０℃／分の速度で融点以上の温度まで再度昇温し、ガラス転移点を求めることができる。
The glass transition point of the xylylene-based polyamide resin is preferably 40 to 180 ° C, and more preferably 60 to 130 ° C.
The number average molecular weight of the xylylene-based polyamide resin is preferably 5,000 to 45,000, and more preferably 10,000 to 25,000.
The melting point of the xylylene-based polyamide resin is preferably 190 to 340 ° C, more preferably 200 to 340 ° C, and further preferably 200 to 320 ° C.
The melting point is the temperature at the top of the endothermic peak at the time of temperature rise observed by the DSC (Differential Scanning Calorimetry) method. The glass transition point refers to a glass transition point measured by heating and melting a sample once to eliminate the influence on crystallinity due to thermal history and then raising the temperature again. For the measurement, for example, “DSC-60” manufactured by Shimadzu Corporation is used, the sample amount is about 5 mg, nitrogen is flowed at 30 ml / min as the atmospheric gas, and the heating rate is 10 ° C./min. Under the conditions, the melting point can be determined from the temperature at the peak top of the endothermic peak observed when the mixture is heated from room temperature to a temperature higher than the expected melting point. Next, the melted polyamide resin is rapidly cooled with dry ice, and the temperature is raised again to a temperature equal to or higher than the melting point at a rate of 10 ° C./min, whereby the glass transition point can be obtained.
キシリレン系ポリアミド樹脂の製造方法は、特開２０１５−０９８６６９号公報の記載を参酌でき、これらの内容は本願明細書に組み込まれる。 Regarding the method for producing the xylylene-based polyamide resin, the description of JP-A-2015-098669 can be referred to, and the contents thereof are incorporated in the present specification.
さらに、本発明の目的・効果を損なわない範囲で、本発明で用いるキシリレン系ポリアミド樹脂には、他のポリアミド樹脂、ポリアミド樹脂以外の樹脂やエラストマー、酸化防止剤、熱安定剤等の安定剤、耐加水分解性改良剤、耐候安定剤、艶消剤、紫外線吸収剤、核剤、可塑剤、分散剤、難燃剤、帯電防止剤、着色防止剤、ゲル化防止剤、着色剤、離型剤等の添加剤等を加えることができる。これらの詳細は、特許第４８９４９８２号公報の段落番号０１３０〜０１５５の記載を参酌でき、これらの内容は本願明細書に組み込まれる。 In addition, the xylylene-based polyamide resin used in the present invention is within a range that does not impair the object and effect of the present invention. Hydrolysis resistance improver, weathering stabilizer, matting agent, UV absorber, nucleating agent, plasticizer, dispersant, flame retardant, antistatic agent, anti-coloring agent, anti-gelling agent, coloring agent, release agent Etc. can be added. For details of these, reference can be made to the description of paragraph numbers 0130 to 0155 of Japanese Patent No. 4894982, the contents of which are incorporated herein.
他のポリアミド樹脂の例としては、ラクタムの重縮合物、ジアミンと炭素数８以下の脂肪族ジカルボン酸との重縮合物、ジアミンと、芳香族ジカルボン酸との重縮合物、ω−アミノカルボン酸の重縮合物等の各種ポリアミド樹脂、または、これらの共重合ポリアミド樹脂が例示される。
本発明で用いるキシリレン系ポリアミド樹脂に、他のポリアミド樹脂を配合する場合、その含有量は、ポリアミド樹脂全量の１０〜５０重量％が好ましく、１０〜２０重量％が好ましい。
一方、本発明で用いるキシリレン系ポリアミド樹脂は、他のポリアミド樹脂を実質的に配合しない構成としてもよく、例えば、他のポリアミド樹脂を、ポリアミド樹脂全量の５重量％以下とすることもできる。
ポリアミド樹脂以外の樹脂としては、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル樹脂、ポリカーボネート樹脂、ポリアセタール樹脂等の熱可塑性樹脂を用いることができる。これらの成分の配合量は、キシリレン系ポリアミド樹脂の５重量％以下であることが好ましい。
Examples of other polyamide resins include lactam polycondensates, diamines and polycondensates of aliphatic dicarboxylic acids having 8 or less carbon atoms, polycondensates of diamines and aromatic dicarboxylic acids, and ω-aminocarboxylic acids. Examples thereof include various polyamide resins such as polycondensates of these, or copolymerized polyamide resins thereof.
When other polyamide resin is mix | blended with the xylylene-type polyamide resin used by this invention, the content is 10-50 weight% of the polyamide resin whole quantity, and 10-20 weight% is preferable.
On the other hand, the xylylene-based polyamide resin used in the present invention may be configured so that other polyamide resins are not substantially blended. For example, the other polyamide resins may be 5% by weight or less of the total amount of the polyamide resins.
As a resin other than the polyamide resin, a thermoplastic resin such as a polyester resin such as polyethylene terephthalate or polybutylene terephthalate, a polycarbonate resin, or a polyacetal resin can be used. The amount of these components is preferably 5% by weight or less of the xylylene-based polyamide resin.
＜長繊維＞
本発明で用いる長繊維は、その形態等特にさだめるものではなく、キシリレン系ポリアミド樹脂と共に熱プレス可能なものであればよい。長繊維とは、長さが０．５ｃｍ以上、好ましくは１ｍ〜１００００ｍの繊維をいう。
<Long fiber>
The long fiber used in the present invention is not particularly limited in its form and the like, and may be any one that can be hot pressed together with the xylylene-based polyamide resin. The long fiber means a fiber having a length of 0.5 cm or more, preferably 1 m to 10000 m.
長繊維の実施形態の一例としては、シート状の長繊維が例示される。
シート状の長繊維の一例として、ロービング状の長繊維を開繊したものが挙げられる。本発明におけるロービング状の長繊維は、ロービング状の長繊維を開繊したものを同一方向に複数並列して引き揃えたものであり、等間隔に隙間なく配列していることが好ましい。用いられる長繊維の繊度は、そのフィラメント数３０００〜６００００であることが好ましく、６０００〜５００００であることがより好ましく、１２０００〜２４０００であることがさらに好ましい。
また、シート状の長繊維の他の一例として、長繊維が一方向または二方向以上に分散・配列等してシートを形成しているものが挙げられる。具体的には、長繊維がシート面内で、不織布のようにランダムに分散しているものや、織物や編み物のように規則的に配列しているものが例示される。
シート状の長繊維は、その目付が１０〜１０００ｇ／ｍ2であることが好ましく、５０〜５００ｇ／ｍ2であることがより好ましく、６０〜４００ｇ／ｍ2であることがさらに好ましく、６０〜１５０ｇ／ｍ2が特に好ましい。また、長繊維は、単層であってもよいし、積層構造であってもよい。
本発明では、ロービング状の長繊維を開繊したもの、および、織物や編み物のように規則的に配列しているものが好ましく、ロービング状の長繊維を開繊したものがさらに好ましい。
シート状の長繊維の厚さは、０．１ｍｍ〜５ｍｍとすることが好ましく、０．１〜３ｍｍがより好ましい。
長繊維としては、植物繊維、炭素繊維、ガラス繊維、アルミナ繊維、ボロン繊維、セラミック繊維、アラミド繊維等が例示され、炭素繊維およびガラス繊維から選択されることが好ましい。炭素繊維はポリアクリロニトリル系炭素繊維、ピッチ系炭素繊維を好ましく用いることができる。また、リグニンやセルロースなど、植物由来原料の炭素繊維も用いることができる。
本発明の一実施形態として、複数枚のシート状の繊維を用いる場合、シート状の炭素繊維とシート状のガラス繊維を併用することが挙げられる。例えば、ポリアミド樹脂フィルム／シート状の炭素繊維／ポリアミド樹脂フィルム／シート状のガラス繊維／ポリアミド樹脂フィルム／シート状の炭素繊維／ポリアミド樹脂フィルムの順に積層して熱プレスすることが例示される。このように、表層に近い層にシート状の炭素繊維を用い、内側にシート状のガラス繊維を用いることにより、高い強度を維持しつつ生産コストを低減することができる。
また、本発明で用いる長繊維は、表面処理剤または集束剤で処理されていてもよい。
本発明では、長繊維強化複合材料のうち、３０体積％以上が長繊維となるように調整されることが好ましく、３５〜６０体積％が長繊維となるように調整されることがさらに好ましい。
A sheet-like long fiber is illustrated as an example of the embodiment of the long fiber.
As an example of the sheet-like long fibers, one obtained by opening roving-like long fibers can be given. The roving-like long fibers according to the present invention are obtained by arranging a plurality of roving-like long fibers opened in parallel in the same direction, and are preferably arranged without gaps at equal intervals. The fineness of the long fibers used is preferably 3000 to 60000 filaments, more preferably 6000 to 50000, and even more preferably 12000 to 24000.
Another example of the sheet-like long fibers is one in which the long fibers are dispersed and arranged in one direction or two or more directions to form a sheet. Specific examples include those in which long fibers are randomly dispersed within the sheet surface, such as a nonwoven fabric, and regularly arranged, such as a woven fabric or a knitted fabric.
Long fiber-like sheet preferably has a basis weight is 10 to 1000 g / m 2, more preferably from 50 to 500 g / m 2, more preferably from 60~400g / m 2, 60~ 150 g / m 2 is particularly preferred. Further, the long fiber may be a single layer or a laminated structure.
In the present invention, those obtained by opening roving-like long fibers and those regularly arranged like woven or knitted fabrics are preferred, and those obtained by opening roving-like long fibers are more preferred.
The thickness of the sheet-like long fibers is preferably 0.1 mm to 5 mm, and more preferably 0.1 to 3 mm.
Examples of the long fibers include plant fibers, carbon fibers, glass fibers, alumina fibers, boron fibers, ceramic fibers, and aramid fibers, and are preferably selected from carbon fibers and glass fibers. As the carbon fiber, polyacrylonitrile-based carbon fiber and pitch-based carbon fiber can be preferably used. Moreover, carbon fibers of plant-derived materials such as lignin and cellulose can also be used.
As one embodiment of the present invention, when a plurality of sheet-like fibers are used, a combination of sheet-like carbon fibers and sheet-like glass fibers can be mentioned. For example, it is exemplified that a polyamide resin film / sheet-like carbon fiber / polyamide resin film / sheet-like glass fiber / polyamide resin film / sheet-like carbon fiber / polyamide resin film are laminated in this order and hot-pressed. Thus, by using a sheet-like carbon fiber for the layer close to the surface layer and using a sheet-like glass fiber on the inside, the production cost can be reduced while maintaining high strength.
Moreover, the long fibers used in the present invention may be treated with a surface treatment agent or a sizing agent.
In this invention, it is preferable to adjust so that 30 volume% or more may become a long fiber among long fiber reinforced composite materials, and it is still more preferable to adjust so that 35-60 volume% may become a long fiber.
＜第１の金属箔と第２の金属箔＞
第１の金属箔と第２の金属箔は、ポリアミド樹脂と長繊維を熱プレスするのに用いられる。第１の金属箔は、前記ポリアミド樹脂および長繊維の少なくとも一方と接する側の表面に、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物を有する。このような組成のエポキシ樹脂組成物を用い、熱プレスすることにより、前記組成物等とポリアミド樹脂の表層での混合をより促進し、組成物とポリアミド樹脂の高い密着性を達成することができる。
金属箔の表面にエポキシ樹脂組成物を有するとは、例えば、エポキシ樹脂組成物が薄層状に、金属箔の表面に存在していることをいう。
尚、上述の図１では、第１の金属箔のダブルベルトプレス機の加熱加圧ユニットと接する側と反対側の表面にエポキシ樹脂組成物を有する。
本発明では、第２の金属箔も、その表面に、さらに、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物を有することが好ましい。このような構成とすることにより、本発明の効果がより効果的に発揮される。第２の金属箔が表面にエポキシ樹脂組成物を有さない場合、第２の金属箔のうち、ポリアミド樹脂と接触する側の表面に、離型剤等を有することが好ましい。このような構成とすることにより、ポリアミド樹脂と第２の金属箔の剥離を容易にすることができる。
第１の金属箔および第２の金属箔は、それぞれ、アルミ箔、ステンレス箔、マグネシウム箔、チタン箔、ニッケル箔、亜鉛箔、銅箔等が挙げられる。本発明で用いる金属箔は、熱収縮率が小さいものが好ましい。
第１の金属箔および第２の金属箔の厚さは、特に定めるものではないが、通常１０〜１００μｍであり、好ましくは１０〜５０μｍである。
<First metal foil and second metal foil>
The first metal foil and the second metal foil are used for hot pressing the polyamide resin and the long fibers. The first metal foil has a composition containing 1 to 30 parts by weight of a compound containing silicon atoms with respect to 100 parts by weight of the epoxy resin on the surface in contact with at least one of the polyamide resin and the long fibers. By using the epoxy resin composition having such a composition and hot pressing, the mixing of the composition and the polyamide resin on the surface layer can be further promoted, and high adhesion between the composition and the polyamide resin can be achieved. .
Having the epoxy resin composition on the surface of the metal foil means, for example, that the epoxy resin composition is present in a thin layer on the surface of the metal foil.
In addition, in above-mentioned FIG. 1, it has an epoxy resin composition on the surface on the opposite side to the side which contacts the heating-pressing unit of the double belt press of a 1st metal foil.
In this invention, it is preferable that the 2nd metal foil also has the composition which contains 1-30 weight part of compounds containing a silicon atom with respect to 100 weight part of epoxy resins on the surface further. By adopting such a configuration, the effect of the present invention is more effectively exhibited. When the second metal foil does not have the epoxy resin composition on the surface, it is preferable to have a release agent or the like on the surface of the second metal foil that is in contact with the polyamide resin. By setting it as such a structure, peeling of a polyamide resin and 2nd metal foil can be made easy.
Examples of the first metal foil and the second metal foil include aluminum foil, stainless steel foil, magnesium foil, titanium foil, nickel foil, zinc foil, and copper foil, respectively. The metal foil used in the present invention preferably has a small heat shrinkage rate.
The thicknesses of the first metal foil and the second metal foil are not particularly defined, but are usually 10 to 100 μm, preferably 10 to 50 μm.
＜＜エポキシ樹脂組成物＞＞
本発明で用いるエポキシ樹脂組成物は、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む。
<< Epoxy resin composition >>
The epoxy resin composition used by this invention contains 1-30 weight part of compounds containing a silicon atom with respect to 100 weight part of epoxy resins.
エポキシ樹脂としては、ビスフェノールＡ型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、ノボラック型エポキシ樹脂、臭素化エポキシ樹脂、アミン型エポキシ樹脂、可撓性エポキシ樹脂、水添ビスフェノールＡ型エポキシ樹脂等が挙げられる。エポキシ樹脂は１種のみでも、２種以上であってもよい。
エポキシ樹脂の数平均分子量は２０００〜３０００であることが好ましい。
本発明で用いるエポキシ樹脂組成物におけるエポキシ樹脂の量は、５０重量％以上が好ましく、６０重量％以上がより好ましい。
Examples of the epoxy resin include bisphenol A type epoxy resin, bisphenol F type epoxy resin, novolac type epoxy resin, brominated epoxy resin, amine type epoxy resin, flexible epoxy resin, hydrogenated bisphenol A type epoxy resin and the like. Only one type of epoxy resin or two or more types of epoxy resins may be used.
The number average molecular weight of the epoxy resin is preferably 2000 to 3000.
The amount of the epoxy resin in the epoxy resin composition used in the present invention is preferably 50% by weight or more, and more preferably 60% by weight or more.
ケイ素原子を含む化合物は、シロキサン結合を含むことが好ましい。ケイ素原子を含む化合物は、低分子であっても、オリゴマーであっても、ポリマーであってもよいが、ポリマー（シリコーン樹脂）が好ましい。また、ケイ素原子を含む化合物中のケイ素原子の割合は、５〜５０重量％であることが好ましい。シリコーン樹脂は、変性剤で変性された、いわゆる、変性シリコーン樹脂であってもよい。 The compound containing a silicon atom preferably contains a siloxane bond. The compound containing a silicon atom may be a low molecule, an oligomer, or a polymer, but a polymer (silicone resin) is preferable. Moreover, it is preferable that the ratio of the silicon atom in the compound containing a silicon atom is 5 to 50 weight%. The silicone resin may be a so-called modified silicone resin modified with a modifier.
シリコーン樹脂としては、メチルフェニルポリシロキサン樹脂、メチルハイドロポリシロキサン樹脂、ジメチルポリシロキサン樹脂、変性ジメチルポリシロキサン樹脂、これらの混合物等が挙げられる。ここで、変性とは、例えば、エポキシ変性、アルキル変性、アミノ変性、カルボキシル変性、アルコール変性、フッ素変性、アルキルアラルキルポリエーテル変性、エポキシポリエーテル変性、ポリエーテル変性、アルキル高級アルコールエステル変性、ポリエステル変性、アシロキシアルキル変性、ハロゲン化アルキルアシロキシアルキル変性、ハロゲン化アルキル変性、アミノグリコール変性、メルカプト変性、水酸基含有ポリエステル変性等が挙げられる。
本発明で用いるエポキシ樹脂組成物における、ケイ素原子を含む化合物の量は、エポキシ樹脂１００重量部に対し、１〜３０重量部含み、１〜１０重量部がより好ましい。
Examples of the silicone resin include methylphenylpolysiloxane resin, methylhydropolysiloxane resin, dimethylpolysiloxane resin, modified dimethylpolysiloxane resin, and mixtures thereof. Here, the modification is, for example, epoxy modification, alkyl modification, amino modification, carboxyl modification, alcohol modification, fluorine modification, alkylaralkyl polyether modification, epoxy polyether modification, polyether modification, alkyl higher alcohol ester modification, polyester modification. And acyloxyalkyl modification, halogenated alkylacyloxyalkyl modification, halogenated alkyl modification, aminoglycol modification, mercapto modification, hydroxyl group-containing polyester modification, and the like.
The amount of the compound containing a silicon atom in the epoxy resin composition used in the present invention is 1 to 30 parts by weight, and more preferably 1 to 10 parts by weight with respect to 100 parts by weight of the epoxy resin.
本発明で用いるエポキシ樹脂組成物には、上記の他、本発明の趣旨を逸脱しない範囲で、他の成分を含んでいてもよい。
他の成分としては、エポキシ樹脂の硬化剤が例示される。
硬化剤としては、メラミン樹脂、イミダゾール類、ＢＦ３錯体、３級アミン類、トリフェニルホスフィン等が挙げられ、メラミン樹脂が好ましい。
メラミン樹脂としては、メチルエーテル化メラミン樹脂、ブチル化尿素メラミン樹脂、ブチル化メラミン樹脂、メチル化メラミン樹脂、ブチルアルコール変性メラミン樹脂等が挙げられる。メラミン樹脂の数平均分子量は５００〜１０００であることが好ましい。
メラミン樹脂を含む場合、エポキシ樹脂組成物におけるその配合量は、エポキシ樹脂１００重量部に対し、３０〜７０重量部であることが好ましく、４０〜６０重量部であることがより好ましい。
In addition to the above, the epoxy resin composition used in the present invention may contain other components without departing from the spirit of the present invention.
Examples of other components include epoxy resin curing agents.
Examples of the curing agent include melamine resins, imidazoles, BF3 complexes, tertiary amines, triphenylphosphine, and the like, and melamine resins are preferable.
Examples of the melamine resin include methyl etherified melamine resin, butylated urea melamine resin, butylated melamine resin, methylated melamine resin, and butyl alcohol-modified melamine resin. The number average molecular weight of the melamine resin is preferably 500 to 1,000.
When the melamine resin is included, the blending amount in the epoxy resin composition is preferably 30 to 70 parts by weight and more preferably 40 to 60 parts by weight with respect to 100 parts by weight of the epoxy resin.
本発明で用いるエポキシ樹脂組成物は、実質的にフッ素原子を含まないことが好ましい。実質的にフッ素原子を含まないとは、エポキシ樹脂組成物中のフッ素原子の割合が、例えば、０．１重量％以下であることをいい、さらには０．０１重量％以下であることをいう。このような構成とすることにより、本発明の製造方法で得られる長繊維強化複合材料を積層して成形する場合に、層間剥離をより引き起こしにくくできる。
また、本発明で用いるエポキシ樹脂組成物は、キシリレン系ポリアミド樹脂よりも第１の金属箔との結合性に優れる基を実質的に含まないことが好ましい。このような構成とすることにより、本発明で用いるエポキシ樹脂組成物を、キシリレン系ポリアミド樹脂の表面に容易に結合させることができる。
It is preferable that the epoxy resin composition used in the present invention does not substantially contain a fluorine atom. “Substantially free of fluorine atoms” means that the proportion of fluorine atoms in the epoxy resin composition is, for example, 0.1% by weight or less, and further 0.01% by weight or less. . By setting it as such a structure, when laminating | stacking and shape | molding the long fiber reinforced composite material obtained with the manufacturing method of this invention, it can make it more difficult to cause delamination.
Moreover, it is preferable that the epoxy resin composition used by this invention does not contain substantially the group which is excellent in bondability with 1st metal foil rather than a xylylene-type polyamide resin. By setting it as such a structure, the epoxy resin composition used by this invention can be easily combined with the surface of a xylylene-type polyamide resin.
＜長繊維強化複合材料＞
本発明では、また、上記長繊維強化複合材料の製造方法によって製造された長繊維強化複合材料を開示する。
また、本発明の長繊維強化複合材料は、ポリアミド樹脂が長繊維に含浸している長繊維強化複合材料であって、前記長繊維強化複合材料の表面に、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物からなるエポキシ樹脂層を有し、前記ジアミン由来の構成単位の７０モル％以上が、キシリレンジアミンに由来し、エポキシ樹脂層の厚さが、５μｍ以下である、長繊維強化複合材料である。下限値は、エポキシ樹脂が存在していれば、すなわち、０μｍを超えればよく、例えば、１ｎｍ以上とすることができる。また、完全に層状をしている必要はなく、長繊維強化複合材料の表面にまだらにエポキシ樹脂が存在している状態でもよい。
本発明の長繊維強化複合材料は厚さが、３０μｍ〜３ｍｍであることが好ましく、５０μｍ〜１ｍｍであることがより好ましく、５０μｍ〜３００μｍがさらに好ましい。
<Long fiber reinforced composite material>
The present invention also discloses a long fiber reinforced composite material produced by the method for producing a long fiber reinforced composite material.
Further, the long fiber reinforced composite material of the present invention is a long fiber reinforced composite material in which a polyamide resin is impregnated in a long fiber, and on the surface of the long fiber reinforced composite material, silicon is added to 100 parts by weight of an epoxy resin. It has an epoxy resin layer composed of a composition containing 1 to 30 parts by weight of a compound containing atoms, 70 mol% or more of the structural unit derived from the diamine is derived from xylylenediamine, and the thickness of the epoxy resin layer is It is a long fiber reinforced composite material of 5 μm or less. If an epoxy resin exists, a lower limit should just exceed 0 micrometer, for example, can be 1 nm or more, for example. Moreover, it is not necessary to be completely layered, and the state where the epoxy resin is present on the surface of the long fiber reinforced composite material may be used.
The long fiber reinforced composite material of the present invention preferably has a thickness of 30 μm to 3 mm, more preferably 50 μm to 1 mm, and even more preferably 50 μm to 300 μm.
＜長繊維強化複合材料の用途＞
本発明の長繊維強化複合材料は、プリプレグとして好ましく用いることができる。また、本発明の長繊維強化複合材料は、そのまま加工成形してもよいし、何層かを積層して、加工成形してもよい。
一例として、本発明の長繊維強化複合材料の製造方法にて、長繊維強化複合材料を製造し、前記長繊維強化複合材料を複数枚積層して、加熱加工することを含む、成形品の製造方法、ならびに、前記成形品の製造方法により得られる成形品が例示される。このような成形品の最薄肉部の厚さとしては、用途等に応じて適宜定めることができるが、例えば、１ｍｍ〜１０ｍｍとすることができる。
本発明の長繊維強化複合材料の利用分野については特に定めるものではなく、自動車等輸送機部品、一般機械部品、精密機械部品、電子・電気機器部品、ＯＡ機器部品、建材・住設関連部品、医療装置、レジャースポーツ用品、遊戯具、医療品、食品包装用フィルム等の日用品、防衛および航空宇宙製品等に広く用いられる。
<Uses of long fiber reinforced composite materials>
The long fiber reinforced composite material of the present invention can be preferably used as a prepreg. Further, the long fiber reinforced composite material of the present invention may be processed and molded as it is, or may be formed by laminating several layers.
As an example, in the method for producing a long fiber reinforced composite material according to the present invention, a long fiber reinforced composite material is produced, and a plurality of the long fiber reinforced composite materials are laminated and heat-processed. Examples of the molded article obtained by the method and the method for producing the molded article are given. The thickness of the thinnest portion of such a molded product can be determined as appropriate depending on the application and the like, and can be, for example, 1 mm to 10 mm.
The field of application of the long fiber reinforced composite material of the present invention is not particularly defined, such as automobile parts such as automobiles, general machine parts, precision machine parts, electronic / electric equipment parts, OA equipment parts, building materials / householding related parts, Widely used in medical equipment, leisure sports equipment, play equipment, medical products, daily goods such as food packaging films, defense and aerospace products.
以下に実施例を挙げて本発明をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り、適宜、変更することができる。従って、本発明の範囲は以下に示す具体例に限定されるものではない。 The present invention will be described more specifically with reference to the following examples. The materials, amounts used, ratios, processing details, processing procedures, and the like shown in the following examples can be changed as appropriate without departing from the spirit of the present invention. Therefore, the scope of the present invention is not limited to the specific examples shown below.
＜キシリレン系ポリアミド樹脂（１）：ポリアミド樹脂ＭＰＸＤ１０の合成＞
撹拌機、分縮器、冷却器、温度計、滴下装置及び窒素導入管、ストランドダイを備えた内容積５０リットルの反応容器に、精秤したセバシン酸８９５０ｇ（４４．２５ｍｏｌ）、次亜リン酸カルシウム１２．５４ｇ（０．０７４ｍｏｌ）、酢酸ナトリウム６．４５ｇ（０．０７９ｍｏｌ）を秤量して仕込んだ。反応容器内を十分に窒素置換した後、窒素で０．４ＭＰａに加圧し、撹拌しながら２０℃から１９０℃に昇温して５５分間でセバシン酸を均一に溶融した。次いでメタキシリレンジアミン４１７２ｇ（３０．６３ｍｏｌ）とパラキシリレンジアミン１７８８ｇ（１３．１３ｍｏｌ）の混合ジアミンを撹拌下で滴下した。この間、反応容器内温は２９３℃まで連続的に上昇させた。滴下工程では圧力を０．４２ＭＰａに制御し、生成水は分縮器及び冷却器を通して系外に除いた。分縮器の温度は１４５〜１４７℃の範囲に制御した。混合ジアミン滴下終了後、反応容器内圧力０．４２ＭＰａにて２０分間重縮合反応を継続した。この間、反応容器内温は２９６℃まで上昇させた。その後、３０分間で反応容器内圧力を０．４２ＭＰａから０．１２ＭＰａまで減圧した。この間に内温は２９８℃まで昇温した。その後０．００２ＭＰａ／分の速度で減圧し、２０分間で０．０８ＭＰａまで減圧し、分子量１，０００以下の成分量を調整した。減圧完了時の反応容器内の温度は３０１℃であった。その後、系内を窒素で加圧し、反応容器内温度３０１℃、樹脂温度３０１℃で、ストランドダイからポリマーをストランド状に取出して２０℃の冷却水にて冷却し、これをペレット化し、約１３ｋｇのポリアミド樹脂を得た。融点は２１３℃であった。
<Synthesis of Xylylene Polyamide Resin (1): Polyamide Resin MPXD10>
In a reaction vessel having an internal volume of 50 liters equipped with a stirrer, a condenser, a cooler, a thermometer, a nitrogen introducing tube, and a strand die, 8950 g (44.25 mol) of sebacic acid precisely measured, calcium hypophosphite 12 .54 g (0.074 mol) and 6.45 g (0.079 mol) of sodium acetate were weighed and charged. After sufficiently purging the inside of the reaction vessel with nitrogen, the pressure was increased to 0.4 MPa with nitrogen, the temperature was raised from 20 ° C. to 190 ° C. with stirring, and sebacic acid was uniformly melted in 55 minutes. Subsequently, a mixed diamine of 4172 g (30.63 mol) of metaxylylenediamine and 1788 g (13.13 mol) of paraxylylenediamine was added dropwise with stirring. During this time, the internal temperature of the reaction vessel was continuously increased to 293 ° C. In the dropping step, the pressure was controlled to 0.42 MPa, and the generated water was removed from the system through a partial condenser and a cooler. The temperature of the partial condenser was controlled in the range of 145 to 147 ° C. After completion of the dropwise addition of the mixed diamine, the polycondensation reaction was continued for 20 minutes at a reaction vessel internal pressure of 0.42 MPa. During this time, the temperature inside the reaction vessel was raised to 296 ° C. Thereafter, the internal pressure of the reaction vessel was reduced from 0.42 MPa to 0.12 MPa over 30 minutes. During this time, the internal temperature rose to 298 ° C. Thereafter, the pressure was reduced at a rate of 0.002 MPa / minute, the pressure was reduced to 0.08 MPa over 20 minutes, and the amount of the component having a molecular weight of 1,000 or less was adjusted. The temperature in the reaction vessel at the time of completion of decompression was 301 ° C. Thereafter, the inside of the system was pressurized with nitrogen, the temperature in the reaction vessel was 301 ° C., the resin temperature was 301 ° C., the polymer was taken out from the strand die into a strand shape, cooled with 20 ° C. cooling water, pelletized, and about 13 kg. A polyamide resin was obtained. The melting point was 213 ° C.
＜その他のポリアミド樹脂＞
キシリレン系ポリアミド樹脂（２）：ポリアミド樹脂ＭＸＤ６、（三菱ガス化学製、ポリメタキシリレンアジパミド樹脂、グレード ＭＸナイロン Ｓ６００１、融点：２３７℃）
ポリアミド６：宇部興産製、グレード１０２２Ｂ、融点：２２４℃
<Other polyamide resins>
Xylylene-based polyamide resin (2): Polyamide resin MXD6 (manufactured by Mitsubishi Gas Chemical Co., Ltd., polymetaxylylene adipamide resin, grade MX nylon S6001, melting point: 237 ° C.)
Polyamide 6: Ube Industries, grade 1022B, melting point: 224 ° C
＜ポリアミド樹脂フィルムの製造＞
上記キシリレン系ポリアミド樹脂（１）、キシリレン系ポリアミド樹脂（２）およびポリアミド６を用いて、それぞれ、以下の方法により、フィルムを製造した。
真空乾燥機により乾燥したポリアミド樹脂を、直径３０ｍｍのスクリューを有する単軸押出機にて溶融押出しし、５００ｍｍ幅のＴダイを介して押出成形し、表面に凹凸状シボを設けたステンレス製の対ロールにより、ロール温度７０℃、ロール圧０．４ＭＰａで加圧し、フィルム表面にシボを有するフィルムを成形した。
得られたキシリレン系ポリアミド樹脂（１）フィルムの平均厚さは５０μｍであった。
得られたキシリレン系ポリアミド樹脂（２）フィルムの平均厚さは３０μｍであった。
得られたポリアミド６フィルムの平均厚さは５０μｍであった。
<Manufacture of polyamide resin film>
Using the xylylene-based polyamide resin (1), the xylylene-based polyamide resin (2), and the
A polyamide resin dried by a vacuum dryer is melt-extruded by a single screw extruder having a screw having a diameter of 30 mm, extruded through a T-die having a width of 500 mm, and a stainless steel pair provided with uneven texture on the surface. A roll having a roll temperature of 70 ° C. and a roll pressure of 0.4 MPa was formed to form a film having a texture on the film surface.
The average thickness of the obtained xylylene-based polyamide resin (1) film was 50 μm.
The average thickness of the obtained xylylene-based polyamide resin (2) film was 30 μm.
The average thickness of the obtained
熱離型樹脂を塗工した金属箔：東洋アルミ千葉製、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部の範囲で含み、そのケイ素原子が主にシロキサン結合を成す熱離型樹脂
シート状の長繊維（１）：炭素繊維（三菱レイヨン製、ＴＲ５０Ｓ、１２Ｋ）を開繊して一方向に引き揃えた巻取体、目付１３０ｇ／ｍ2、一層あたりの厚さ約０．４ｍｍ
シート状の長繊維（２）：炭素繊維織物、三菱レイヨン製、ＴＲ３１１０Ｍ、目付２００ｇ／ｍ2、１枚当たりの厚さ１ｍｍ
シート状の長繊維（３）：ガラス繊維織物、日東紡績製、ＫＳ１２１０ １０８０Ｓ−９３５Ｎ、目付９０ｇ／ｍ2、１枚当たりの厚さ０．０８ｍｍ
Metal foil coated with heat release resin: made of Toyo Aluminum Chiba, 100 parts by weight of epoxy resin, contained in a range of 1 to 30 parts by weight of a compound containing silicon atoms, and the silicon atoms mainly form siloxane bonds Release resin sheet-like long fiber (1): Winding body in which carbon fiber (manufactured by Mitsubishi Rayon, TR50S, 12K) is opened and aligned in one direction, basis weight 130 g / m 2 , thickness per layer about 0.4mm
Sheet-like long fiber (2): Carbon fiber fabric, manufactured by Mitsubishi Rayon, TR3110M, basis weight 200 g / m 2 ,
Sheet-like long fiber (3): Glass fiber fabric, manufactured by Nitto Boseki Co., Ltd., KS1210 1080S-935N, basis weight 90 g / m 2 , thickness per sheet 0.08 mm
＜実施例１＞
＜＜長繊維強化複合材料の製造＞＞
２枚の上記熱離型樹脂を塗工した金属箔の間に、上記キシリレン系ポリアミド樹脂フィルム（１）、上記シート状の長繊維（１）および上記キシリレン系ポリアミド樹脂フィルム（１）を前記順に、かつ、熱離型樹脂が内側となるように挟み、搬送速度１．０分／ｍでＨＥＬＤ社製のダブルベルトプレス機のスチールベルト間に投入し、３００℃、４ＭＰａの圧力で２分間連続熱プレスし、キシリレン系ポリアミド樹脂フィルム（１）をシート状の長繊維（１）に含浸させ、連続して４ＭＰａに加圧したまま１４０℃で１分間冷却した。その後、金属箔を剥がし、長繊維強化複合材料を得た。得られた長繊維強化複合材料の厚さは、１３０μｍであった。
<Example 1>
<< Manufacture of long fiber reinforced composite material >>
Between the two metal foils coated with the thermal release resin, the xylylene-based polyamide resin film (1), the sheet-like long fibers (1), and the xylylene-based polyamide resin film (1) are arranged in the order described above. In addition, it is sandwiched so that the heat-release resin is on the inside, and is fed between steel belts of a double belt press machine manufactured by HELD at a conveyance speed of 1.0 min / m, and continuously for 2 minutes at 300 ° C. and 4 MPa pressure. Heat-pressed, the xylylene-based polyamide resin film (1) was impregnated into the sheet-like long fibers (1), and cooled at 140 ° C. for 1 minute while continuously pressing at 4 MPa. Thereafter, the metal foil was peeled off to obtain a long fiber reinforced composite material. The resulting long fiber reinforced composite material had a thickness of 130 μm.
＜＜曲げ試験＞＞
上記で得られた長繊維強化複合材料を７枚、繊維方向が交互に略０度／９０度になるように積層し、２５０℃、３ＭＰａの圧力で、３分間プレスした。厚さ１．０ｍｍの試験片が得られた。得られた試験片について、ＪＩＳ Ｋ７１７１に従い、曲げ強度および曲げ弾性率を測定した。
また、得られた長繊維強化複合材料の表面をアセトンで洗浄した後、上記と同様に、長繊維強化複合材料７枚を積層して熱プレスし、上記と同様に曲げ強度および曲げ弾性率を測定した。
<< Bending test >>
Seven of the long fiber reinforced composite materials obtained above were laminated so that the fiber directions were alternately 0 ° / 90 °, and pressed at 250 ° C. and a pressure of 3 MPa for 3 minutes. A test piece having a thickness of 1.0 mm was obtained. About the obtained test piece, bending strength and a bending elastic modulus were measured according to JISK7171.
In addition, after washing the surface of the obtained long fiber reinforced composite material with acetone, similarly to the above, 7 sheets of long fiber reinforced composite material were laminated and hot-pressed, and the bending strength and the bending elastic modulus were adjusted in the same manner as described above. It was measured.
＜実施例２＞
シート状の長繊維（１）を上記シート状の長繊維（２）に変え、熱プレス温度を３０５℃に変えて得た厚さ２００μｍの長繊維強化複合材料を、４枚同方向に積層してプレスした他は実施例１と同様に行った。得られた試験片の厚さは、０．８ｍｍであった。
<Example 2>
A sheet-like long fiber (1) is changed to the sheet-like long fiber (2), and a 200 μm-thick long fiber-reinforced composite material obtained by changing the hot press temperature to 305 ° C. is laminated in the same direction. Example 1 was carried out in the same manner as in Example 1 except that pressing was performed. The thickness of the obtained test piece was 0.8 mm.
＜実施例３＞
シート状の長繊維（１）を上記シート状の長繊維（３）に変え、キシリレン系ポリアミド樹脂フィルム（１）を、キシリレン系ポリアミド樹脂フィルム（２）に変え、熱プレス温度を３２０℃に変えて得た厚さ７０μｍの長繊維強化複合材料を、１２枚同方向に積層し、積層体のプレス温度を２６０℃にした他は実施例１と同様に行った。得られた試験片の厚さは、０．８ｍｍであった。
<Example 3>
Change the sheet-like long fiber (1) to the sheet-like long fiber (3), change the xylylene-based polyamide resin film (1) to the xylylene-based polyamide resin film (2), and change the hot press temperature to 320 ° C. The same procedure as in Example 1 was carried out except that 12 long fiber reinforced composite materials having a thickness of 70 μm obtained were laminated in the same direction and the press temperature of the laminate was 260 ° C. The thickness of the obtained test piece was 0.8 mm.
＜比較例１＞
実施例１において、キシリレン系ポリアミド樹脂フィルム（１）をポリアミド６フィルムに変えた他は実施例１と同様に行った。得られた試験片について、実施例１と同様に評価した。得られた試験片の厚さは、１．０ｍｍであった。
<Comparative Example 1>
In Example 1, it carried out similarly to Example 1 except having changed the xylylene-type polyamide resin film (1) into the
＜参考例１＞
上記キシリレン系ポリアミド樹脂フィルム（１）と上記シート状長繊維（１）とを、熱離型樹脂を塗工した金属箔を用いずに、ニップロールで貼り合わせて得た長繊維強化複合材料を用いた他は実施例１と同様に行った。得られた試験片の厚さは、１．０ｍｍであった。
<Reference Example 1>
A long fiber reinforced composite material obtained by bonding the xylylene-based polyamide resin film (1) and the sheet-like long fiber (1) with a nip roll without using a metal foil coated with a heat release resin is used. Otherwise, the same procedure as in Example 1 was performed. The thickness of the obtained test piece was 1.0 mm.
上記実施例１と参考例１の結果から明らかなとおり、本発明の製造方法で得られた長繊維複合強化材料は、従来の方法で製造された長繊維複合強化材料よりも、曲げ弾性率および曲げ強度が向上していることが分かった。
また、実施例１のアセトン洗浄前後の長繊維強化複合材料について、ＦＴ−ＩＲ ＡＴＲ分析により、確認したところ、アセトン洗浄前のものは、離型樹脂を検出した。これに対し、アセトン洗浄後のものは、離型樹脂を検出しなかった。これらの結果から、熱離型樹脂を塗工した金属箔の離型樹脂が、長繊維強化複合材料に転写されていることが確認された。また、離型樹脂の存在が成形品の曲げ弾性率および曲げ強度を向上させていることが分かった。尚、ポリアミド樹脂は耐薬品性に優れた樹脂であり、アセトン洗浄によって、ポリアミド樹脂がダメージを受けることはない。
また、ポリアミド６を用いた場合、金属箔を剥離した際に離型樹脂は転写されず、アセトン洗浄前後で、曲げ弾性率および曲げ強度に違いが認められなかった。
As is clear from the results of Example 1 and Reference Example 1, the long fiber composite reinforcing material obtained by the production method of the present invention has a higher flexural modulus and higher modulus than the long fiber composite reinforcing material produced by the conventional method. It was found that the bending strength was improved.
Moreover, about the long fiber reinforced composite material before and behind acetone washing | cleaning of Example 1, when confirmed by FT-IR ATR analysis, the thing before acetone washing | cleaning detected the mold release resin. On the other hand, the release resin was not detected after washing with acetone. From these results, it was confirmed that the release resin of the metal foil coated with the heat release resin was transferred to the long fiber reinforced composite material. It was also found that the presence of the release resin improves the bending elastic modulus and bending strength of the molded product. The polyamide resin is a resin having excellent chemical resistance, and the polyamide resin is not damaged by washing with acetone.
When
＜実施例４＞
３枚のキシリレン系ポリアミド樹脂フィルム（１）と２枚のシート状の長繊維（１）を交互に積層して、２枚の熱離型樹脂を塗工した金属箔の離型樹脂を塗工した金属箔に、離型樹脂が内側となるように挟んだ。３０５℃、４ＭＰａの圧力で１２０秒間プレスした。その後、金属箔を剥がし、長繊維強化複合材料を得た。
<Example 4>
3 sheets of xylylene-based polyamide resin film (1) and 2 sheets of long fiber (1) are laminated alternately and coated with a metal foil release resin coated with 2 sheets of heat release resin. The release resin was sandwiched between the metal foils. Pressing was performed at 305 ° C. and a pressure of 4 MPa for 120 seconds. Thereafter, the metal foil was peeled off to obtain a long fiber reinforced composite material.
１ 加熱加圧ユニット
２ 第１の金属箔
３ ポリアミド樹脂フィルム
４ シート状の長繊維
５ 第２の金属箔
６ 冷却加圧ユニット
DESCRIPTION OF
Claims (14)
前記第１の金属箔は、前記ポリアミド樹脂または長繊維と接する側の表面に、エポキシ樹脂１００重量部に対し、ケイ素原子を含む化合物１〜３０重量部を含む組成物を有し、前記ポリアミド樹脂は、ジアミン由来の構成単位とジカルボン酸由来の構成単位から構成され、前記ジアミン由来の構成単位の７０モル％以上が、キシリレンジアミンに由来する、長繊維強化複合材料の製造方法。 Heat-pressing the polyamide resin and the long fiber between the first metal foil and the second metal foil, and after the hot pressing, peeling off the first metal foil and the second metal foil,
The first metal foil has a composition containing 1 to 30 parts by weight of a compound containing a silicon atom with respect to 100 parts by weight of an epoxy resin on a surface in contact with the polyamide resin or long fibers, and the polyamide resin Is a method for producing a long fiber reinforced composite material, which is composed of a structural unit derived from diamine and a structural unit derived from dicarboxylic acid, and 70 mol% or more of the structural unit derived from diamine is derived from xylylenediamine.