JP2017025318A - Coating composition and article produced therefrom - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an aqueous dispersed body, a coating composition, a coating layer and a coated article produced therefrom for delaying or suppressing the corrosion of a metallic can or container.SOLUTION: Provided is an aqueous dispersed body (the dispersed body has a solid content of 10 to 85% to the total weight of the dispersed body) containing: (a) one or more kinds of polyethylene terephthalate resins of 50 to 99 wt.% to the total solid content of the dispersed body (the second polyester has (i) a carboxylic acid group and has an acid value of 15 or more to the solid content of the second polyester, or being (ii) self-dispersion type sulfopolyester); (b)one or more kinds of stabilizers including one or more kinds of the second polyester of 1 to 50 wt.% to the total solid content of the dispersed body; (c) one or more kinds of neutralizers; and (d) a melted blend product of water of 15 to 90 wt.% to the total weight of the dispersed body.SELECTED DRAWING: None

Description

  The present invention relates to coating compositions and articles made therefrom.

In order to retard or inhibit corrosion, it is well established to apply various treatment and pretreatment solutions to the metal. This is particularly true not only in the field of non-food metal containers but also in the field of metal food and beverage cans. A coating is applied to the inner surface of such containers to prevent the contents from contacting the metal parts of the container. Contact between metal and non-food material as well as between metal and food or beverage can lead to corrosion of the metal container, which in turn is food or beverage or non-food content of such metal container. May contaminate things. Corrosion is particularly a problem when food and beverage products are highly acidic and / or have a high salt content such as rhubarb-based products or isotonic beverages. In addition, strongly alkaline contents of non-food substances such as hair dyes are made of metal (for example, aluminum) in containers.
Can react with the moiety. For example, a coating applied to the inner surface of food and beverage cans also helps prevent corrosion in the can headspace (the area between the food filling boundary and the can lid). A coating may be applied to the outer surface of the metal container to provide protection against the external environment or to provide a decorative layer comprising fillers and / or pigments. In addition to protection from corrosion, coatings on food and beverage cans should be non-toxic and inert and adversely affect the taste or appearance, eg color, of the food or beverage in the can when applied to the inner surface. Should not affect or contaminate the contents of the can. "Popping
Resistance to “popping”, “whitening” and / or “blowing” is also desirable. Certain types of coatings are applied on coiled metal materials, such as coiled metal materials from which the end of the can is made, “can end materials”, and valve cups (eg, top end surfaces of aerosol cans). Is particularly suitable for. Since coatings designed for use on can end materials are applied before the end surfaces are cut and stamped from the coiled metal material, they are also usually flexible and / or
Or it is extensible. For example, can end materials are typically coated on both sides. Thereafter, the coated metal material may be stamped, beaded or bent. The coated metal material may be marked for a “pop-top” opening, and then the pop top ring may be attached with a separately manufactured pin. Next, the end face is the edge rolling method (edge
It is attached to the can body by rolling process). Thus, the coating applied to the can end materials typically has some toughness and flexibility in order to be resistant to a wide range of manufacturing methods in addition to some or all of the other desired features described above. Have. Various coatings have been used to coat the inner surface of metal cans to prevent corrosion, such as epoxy based and polyvinyl chloride based, eg, organosol type coatings. However, there is a need for non-food container liners as well as food and beverage can liners that provide improved properties such as having adequate levels of flexibility as well as resistance to degradation in corrosive media.

The present invention provides aqueous dispersions, coating compositions, coating layers, and coated articles made therefrom.

In one embodiment, the present invention provides (a) 50 to 99 weight percent of one or more polyethylene terephthalate resins based on the total solids content of the dispersion; (b) based on the total solids content of the dispersion. 1 containing 1 to 50 weight percent of at least one second polyester
One or more stabilizers (wherein the second polyester has (i) a carboxylic acid group;
(Ii) a self-dispersing sulfopolyester); (c) one or more neutralizing agents;
And (d) an aqueous dispersion comprising 15 to 90 percent by weight of the melt blend product of water relative to the total weight of the dispersion, wherein the dispersion is 10 to 85 percent relative to the total weight of the dispersion Having a solids content of

In an alternative embodiment, the present invention comprises (1) selecting one or more polyethylene terephthalate resins; and (2) at least one second polyester relative to the total solids content of the dispersion. (Wherein the second polyester has (i) a carboxylic acid group and has an acid number of 15 or more, such as 20 or more, relative to the solids content of the second polyester; or (
ii) selecting one or more stabilizers comprising a self-dispersing sulfopolyester); (3) selecting one or more neutralizing agents; (4) water and 1 Melt blending one or more polyethylene terephthalate resins, one or more stabilizers in the presence of one or more neutralizing agents; and (4) thereby adding to the total weight of the dispersion And an aqueous dispersion having a solids content of 10 to 85 percent relative to the aqueous dispersion.

In another alternative embodiment, the present invention provides: (a) an aqueous dispersion of the present invention as described above; (b)
Optionally one or more crosslinking agents; (c) optionally a polyolefin dispersion, acrylic latex, epoxy resin dispersion, polyurethane dispersion, alkyd dispersion, vinyl acetate dispersion and ethylene vinyl acetate dispersion (ethylene vinyl acetate dispersion)
Further provided is a coating composition comprising one or more selected from the group consisting of:

In another alternative embodiment, the present invention further provides a coating layer comprising at least one or more film layers derived from the inventive coating composition described above.

In another alternative embodiment, the present invention is coated, comprising (1) one or more substrates; (2) at least one or more coating layers derived from the coating composition of the present invention described above. Further providing articles.

In another alternative embodiment, the present invention comprises (1) selecting a substrate; (2) selecting a coating composition of the present invention as described above; (3) coating the composition at least on the substrate Applying to one surface; (4) from a coating composition;
Removing at least a portion of the water; (5) thereby forming one or more coating layers associated with the substrate; and (6) thereby coating the coated substrate to the coated article. A method of making a coated article.

In another alternative embodiment, the present invention includes (1) selecting a substrate; (2) molding the substrate into an article; (3) selecting the coating composition described above; (4) ) Applying the coating composition to at least one surface of the article;
(5) removing at least a portion of water from the coating composition; (6) thereby forming one or more coating layers associated with at least one surface of the article; Thereby further providing a method of making a coated article comprising forming the coated article.

In an alternative embodiment, the invention provides that the one or more polyethylene terephthalate resins are at least 30 ° C; such as at least 40 ° C; or alternatively at least 50 ° C.
Or alternatively according to any previous embodiment except having a glass transition temperature (T _g ) in the range of 30 to 130 ° C .; or alternatively at least 60 ° C .; or alternatively at least 70 ° C .; Aqueous dispersion, coating composition, coating layer, coated article,
A method of manufacturing them is provided.

In an alternative embodiment, the present invention provides an aqueous dispersion, coating composition, coating layer, coated article, and their manufacture according to any previous embodiment, except that the substrate is a pre-coated substrate. Provide a way to do it.

In an alternative embodiment, the present invention provides an aqueous dispersion, coating composition, according to any preceding embodiment, except that the substrate is metal, wood, paper, plastic, glass, leather and / or concrete. Coating layers, coated articles, and methods of making them are provided.

In an alternative embodiment, the present invention provides an aqueous dispersion according to any preceding embodiment, except that the dispersion and / or the coating composition derived therefrom further comprises a catalyst,
Coating compositions, coating layers, coated articles and methods for making them are provided.

In an alternative embodiment, the invention is a linear saturated aromatic polyester wherein the one or more polyethylene terephthalate resins have a glass transition temperature greater than 50 ° C. and an acid number less than 5 mg KOH / g, Any preceding embodiment except that the two polyesters are compatible with one or more polyethylene terephthalate resins, thereby producing a dispersion having a volume average particle size of less than 5 microns. In accordance with the present invention, aqueous dispersions, coating compositions, coating layers, coated articles and methods of making them are provided.

In an alternative embodiment, the present invention provides that the aqueous dispersion and / or coating composition derived therefrom is an acrylic latex, vinyl acrylic latex, styrene acrylic latex, vinyl acetate ethylene latex, polyurethane dispersion, alkyd dispersion,
One or more binder compositions such as epoxy dispersions, polyolefin dispersions, and combinations thereof; optionally one or more fillers; optionally catalysts, wetting agents, antifoaming agents, flow agents, Mold release agent, slip agent, anti-blocking agent, sulfide contamination concealer (addit
ives to mask sulfur staining), pigment wetting / dispersing agents, anti-settling agents, UV stabilizers, adhesion promoters and the like; optionally fatty acid ester waxes, silicon-based waxes, fluorine-based additives One or more lubricants such as wax, polyethylene or any other similar polyolefin wax, carnauba wax, lanolin wax; optionally one or more corrosion inhibitors such as aluminum and zinc; Depending on one or more pigments, for example titanium dioxide, barium sulfate, mica, calcium carbonate, silica, zinc oxide, ground glass, aluminum trihydrate, talc, antimony trioxide, fly ash and clay; One or more co-solvents, for example glycols, glycol ethers 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, alcohol, mineral spirits, aromatic solvents and benzoic acid esters and the like; optionally one or more dispersants, such as amino alcohols and A polycarboxylate salt; optionally one or more surfactants;
One or more preservatives such as biocides, fungicides, bactericides, algicides, and combinations thereof; optionally one or more thickeners such as hydroxyethylcellulose Cellulose-based thickeners, hydrophobically modified alkali-soluble emulsions (HASE thickeners such as UCAR POLYPHOBE TR-116) and hydrophobically modified ethoxylated urethane thickeners (HEUR); or optionally One or more additional neutralizing agents such as hydroxides, amines, ammonia and carbonates; optional, except optionally further comprising one or more solvents or coalescing agents Aqueous dispersion, coating composition, coating layer, coated article, according to the preceding embodiment To provide a method for producing a.

The present invention provides aqueous dispersions, coating compositions, coating layers, and coated articles made therefrom.

The coating composition of the present invention has (1) (a) 50 to 9 relative to the total solids content of the dispersion.
9 weight percent of one or more polyethylene terephthalate resins; (b) one or more of at least one second polyester comprising 1 to 50 weight percent based on the total solids content of the dispersion Stabilizer (wherein the second polyester has (i) carboxylic acid groups and has an acid number of 15 or more, such as 20 or more, relative to the solid content of the second polyester; or (ii) self-dispersing (C) one or more neutralizing agents; and (d) a melt blend product of 15 to 90 weight percent water based on the total weight of the dispersion. A dispersion, wherein the dispersion has a solids content of 10 to 85 percent based on the total weight of the dispersion; and (2) optionally comprises one or more crosslinkers

Aqueous Dispersion The aqueous dispersion of the present invention comprises (a) 50 to 99 weight percent of one or more polyethylene terephthalate resins, based on the total solid content of the dispersion; (b) the total solid content of the dispersion. One or more stabilizers comprising 1 to 50 percent by weight of at least one second polyester, wherein the second polyester has (i) a carboxylic acid group and a second
Having an acid number of 15 or more, for example 20 or more, based on the solids content of the polyester; or (
ii) a self-dispersing sulfopolyester); (c) one or more neutralizing agents; and (d) a melt blend product of 15 to 90 weight percent water based on the total weight of the dispersion. Where the dispersion has a solids content of 10 to 85 percent relative to the total weight of the dispersion.

The aqueous dispersion of one or more polyethylene terephthalate resins comprises 50 to 99 weight percent of one or more polyethylene terephthalate resins, based on the total weight of the solid content of the aqueous dispersion. All individual values and subranges from 50 to 99 weight percent are included herein and disclosed herein; for example, weight percent is 50, 55, 60, 65 or 70 It can be from a lower limit of weight percent to an upper limit of 60, 65, 70, 75, 80, 85, 90, 95 or 99 weight percent. For example, the aqueous dispersion may comprise 55 to 95 weight percent of one or more polyethylene terephthalate resins, based on the total weight of the solid content of the aqueous dispersion; or alternatively, the aqueous dispersion May comprise from 60 to 90 weight percent of one or more polyethylene terephthalate resins, based on the total weight of the solids content of the aqueous dispersion; or alternatively, the aqueous dispersion is an aqueous dispersion May comprise from 65 to 90 weight percent of one or more polyethylene terephthalate resins, or alternatively, the aqueous dispersion may comprise the total solid content of the aqueous dispersion. It may contain 75 to 95 percent by weight of one or more polyethylene terephthalate resins. The aqueous dispersion contains at least one or more polyethylene terephthalate resins.

The one or more polyethylene terephthalate resins are polyesters and copolyesters, such as high molecular weight linear thermoplastic polyesters, having at least some intrinsic crystallinity, in which case the dicarboxylic acid monomer component used Is mainly terephthalic acid. Although these thermoplastic polyesters and copolyesters may have hydroxyl or carboxyl end groups, the overall functional group concentration is very low and is not normally reported. It is usually not necessary to cross-link these polyesters in order to improve the excellent physical properties. Polyesters and copolyesters are described in US Pat. No. 2,901,466.
No. 2,465,319 and 3,047,539, which are incorporated herein by reference to the extent they disclose the method, and the like in the art It is usually prepared by a known conventional polycondensation method. Typically, the thermoplastic polyester or copolyester has a glass transition temperature of 50 to 130 ° C. and a heat strain temperature of 60 to 120 ° C. (at ASTM D648, 264 psi (1.82 MPa)). The molecular weight of thermoplastic polyesters and copolyesters is typically expressed in terms of their intrinsic viscosity, which is 0 measured at 25 ° C. in a solvent mixture consisting of 60% by weight phenol and 40% by weight tetrachloroethane. The range is from 0.5 to 1.0 Dl / g.

The dicarboxylic acid component of thermoplastic polyesters and copolyesters is primarily terephthalic acid (at least 50 mole percent based on the total moles of diacids). The thermoplastic polyester or copolyester is preferably composed of at least 80 mole percent terephthalic acid, most preferably at least 90 mole percent terephthalic acid, based on the total moles of diacid. In addition to terephthalic acid, the dicarboxylic acid component can have up to 50 mol% of another modified dicarboxylic acid. Modified dicarboxylic acid comonomers modify properties such as melting point, T _g , gas permeability, transparency, flexibility, impact resistance, crystallization rate, hydrolysis stability, and resistance to solvents and other chemicals Used for. Thermoplastic polyester or copolyester
Preferably it contains less than 20 mol% modified dicarboxylic acid, most preferably less than 10 mol% modified dicarboxylic acid. Suitable modified aromatic dicarboxylic acids include, but are not limited to, isophthalic acid, 4,4′-biphenyldicarboxylic acid, 1,4-, 1,5-, 2,6-, 2,7
-Includes those having up to about 20 carbon atoms, including naphthalenedicarboxylic acid and trans-4,4'-stilbene dicarboxylic acid, and esters thereof.
Suitable modified aliphatic dicarboxylic acids include, but are not limited to, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azaleic acid and dodecanedioic acid. Preferably 10 mol% or less of the aliphatic modified dicarboxylic acid is used. The total mole percent of the dicarboxylic acid component is 100 mole percent.

The glycol component of the thermoplastic polyester and copolyester of the present invention is one or more of the following diols: ethylene glycol, 2,3 butanediol, 1,4 butanediol, 1,3-cyclohexanedimethanol, 1,4 -Cyclohexanedimethanol (
Or a mixture of 1,3 and 1,4 cyclohexanedimethanol, which may be cis or trans), and / or 2,2,4,4-tetramethyl-1,
3-cyclobutanediol (which may be cis, trans, or a mixture thereof).

In an exemplary embodiment, the glycol component is 10 (relative to the total moles of diol).
Contains ~ 100 mol% ethylene glycol. In another exemplary embodiment, the glycol component is 15 to 85 mol% ethylene glycol, and 15 to 85 mol% of one or more of the following diols: 1,4 butanediol, 1,3-cyclohexane. Dimethanol, 1,4-cyclohexanedimethanol (or a mixture of 1,3 and 1,4 cyclohexanedimethanol, which may be cis or trans), and / or 2
2,4,4-tetramethyl-1,3-cyclobutanediol (which may be cis, trans, or a mixture thereof).

In addition, suitable glycol components of the copolyester are from 3 to 40, up to 10 mol%.
It can also be modified with other glycols having 1 carbon atom, preferably less than 5 mol% modified glycols. Modified glycol comonomer is used to modify properties such as melting point, _Tg , gas permeability, transparency, flexibility, impact resistance, crystallization rate, hydrolytic stability, and resistance to solvents and other chemicals. used. Examples of suitable modified glycols include, but are not limited to, 1,2-propanediol, neopentyl glycol, 1,3-propanediol, polyethylene glycol, polytetramethylene glycol, p-xylene glycol, diethylene glycol, Triethylene glycol, dipropylene glycol, tripropylene glycol and higher polypropylene glycol, butanediol, 1,5-
Pentanediol and other pentanediols, hexanediol, decanediol, and dodecanediol, glycerin, dipentaerythritol, 1,3-butylene-ethylpropanediol, 2-methyl-1,3-propanediol, 1,4-benzyl Dimethanol, 2,4-dimethyl-2-ethylhexane-1,3-diol, isopropylidenebis (p-phenylene-oxypropanol-2), and mixtures thereof are included.
In some embodiments, the aliphatic glycol may contain from 2 to about 8 carbon atoms, and mixtures thereof. The total mole percent of the glycol component is 100 mole percent.

Exemplary thermoplastic polyesters are described, for example, in US Pat. No. 2,936,296, US Pat. No. 5,955,565, and US Pat. No. 5,859,116 (such thermoplastic polyesters are described). To the extent that they are incorporated herein by reference). For more details on thermoplastic polyesters, see “Handbook of Thermoplastics
”, Edited by Olagoke Olabisi and published by Marcel Dekker, Inc. (1997), ISBN 0
-8247-9797-3. Can be found in Pages417-490. Suitable thermoplastic polyesters and copolyesters are, for example, the trade names; CADENCE®, EASTAR®, SPECTAR®, PROVISTA®, DURASTA
As R (registered trademark), EMBRACE (registered trademark) and TRITAN (registered trademark),
Available from Eastman Chemical. This group of thermoplastic polyesters provides a range of molecular weights, glass transition temperatures and chemical structures that can provide advantageous properties in the aqueous coating applications of the present invention.

Thermoplastic polyesters and copolyester resins have very limited ambient temperature solubility in conventional solvents suitable for coating formulations. The present invention describes the discovery that aqueous dispersions of such thermoplastic polyesters and copolyesters can be made at high solids and can be successfully applied as liquids in high solids aqueous coating formulations. To do.

Such thermoplastic polyesters and copolyesters include, but are not limited to, for example, PCT, PBT, PCTG, PET, PETG, PCTA, PETA, and PTT.

The stabilizer aqueous dispersion comprising the second polyester further comprises at least one or more stabilizers comprising one or more second polyesters to promote the formation of a stable dispersion. . In one embodiment,
The second polyester (i) has a carboxylic acid group and has an acid value of 15 or more, such as 20 or more, relative to the solid content of the second polyester; or (ii) a self-dispersing sulfopolyester . In one embodiment, the second polyester has carboxylic acid groups and is 15 or more,
For example, it has an acid value greater than 20. The aqueous dispersion is 1 to the total weight of the solid content of the dispersion.
To 50 weight percent of one or more stabilizers. All individual values and subranges from 1 to 50 weight percent are included herein and disclosed herein; for example, weight percent is 1, 3, 5, 10 weight percent From the lower limit of
It can be up to an upper limit of 15, 25, 35, 45 or 50 weight percent. For example, the dispersion is 1 to 25; or alternatively 1 to 35, based on the total weight of the solid content of the dispersion;
Or alternatively 1 to 40; or alternatively 1 to 45 weight percent of one or more stabilizers.

The carboxylated second polyester is a highly acidic, water-dispersible, hydrophilic polyester, which is used as the main stabilizer for dispersing the first polyester resin. The carboxylated second polyester is typically 15 mg KOH / g (
For example, the acid value is in the range of 20 to 80 mg KOH / g (based on the resin solid). The carboxylic acid functionality of the second polyester is critical to the present invention. In making the aqueous dispersion, the acid functionality of the second polyester is neutralized with a suitable inorganic or organic base to provide colloidal stability. Highly acid stabilized polyester
It also has a hydroxyl functionality, but this is not essential. Preferably, the highly acidic stabilized polyester is at least 2 mg KOH / g (based on resin solids), preferably 5 mg KOH
/ G or more, and most preferably has an OH number of 20 mgKOH / g or more. Highly acid stabilized polyesters, for example, Zeno W. Wicks, Jr, Frank N. Jones, S. Peter. Pappas "Organic Coating
s, Science and Technology, "pp 246-257 (John Wiley & Sons, 1999, second edition) and references therein, or Houben-Weyl," Methoden der Organischen Chemie, Band E2.
0, Makromolekulare Soffe, Polyester "pp 1405-1429, (Georg Thieme Verlag, Stuttgart 1
987) and references therein, may be produced by conventional polycondensation techniques.
In one embodiment, the diol or polyol and dicarboxylic acid or polycarboxylic acid are charged into a conventional polymerization vessel and allowed to react between about 150 ° C. and 280 ° C. for several hours. In some cases, an esterification catalyst may be used to shorten the reaction time. It may be preferred to use a two-step method to provide polyesters containing carboxyl functional groups. In one embodiment, a polyester containing OH functionality is first prepared such that there is a small amount, if any, of free carboxylic acid and / or carboxylate functionality, which is then converted to a cyclic dicarboxylic acid in a subsequent step. Reacting with the acid anhydride in a ring-opening and monoester formation reaction, free carboxylic acid and / or carboxylate groups are then formed. The excess amount of the OH functional group in the resin in the first step is such that the final resin after the reaction with the molecule containing a polyacid functional group usually has an acid value of 15 mgKOH / g (based on the resin solid) or more,
Designed in such a way as to provide a carboxyl-terminated polyester resin, for example in the range of 20 to 80 mg KOH / g (relative to the resin solids).

The carboxylic acid component of the highly acidic stabilized polyester comprises one or more aliphatic, cycloaliphatic, aromatic aliphatic and / or aromatic carboxylic acids or anhydrides having at least two COOH functional groups. May be included. Suitable and typical dicarboxylic or polycarboxylic acids, or their corresponding alkyl esters, that can be used to form highly acidic stabilized polyesters include, but are not limited to, saturated and unsaturated Dicarboxylic acids such as, but not limited to, maleic acid, maleic anhydride, malonic acid, fumaric acid, succinic acid, succinic anhydride, glutaric acid, adipic acid, 2-methyl-1,6-
Hexanoic acid, pimelic acid, suberic acid, dodecanedioic acid, phthalic acid, phthalic anhydride, 5-t
ert-Butylisophthalic acid, Tetrahydrophthalic anhydride, Hexahydrophthalic acid, Hexahydrophthalic anhydride, Endomethylenetetrahydrophthalic anhydride, Azelaic acid, Fumaric acid, Sebacic acid, Tetrachlorophthalic anhydride, Chlorendic acid , Isophthalic acid,
Trimellitic anhydride, terephthalic acid, naphthalene dicarboxylic acid, cyclohexane-dicarboxylic acid and the like, and mixtures thereof are included.

The glycol component of the highly acidic stabilized polyester includes ethylene glycol, diethylene glycol, triethylene glycol and / or higher polyethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol and / or higher polypropylene glycol, 1,3-propanediol, , 4-butanediol and other butanediols, 1,5-pentanediol and / or other pentanediols, hexanediol, decanediol, and / or dodecanediol, glycerin, trimethylolpropane, trimethylolethane, neopentylglycol , Pentaerythritol, cyclohexanedimethanol, polyethylene or polypropylene having a molecular weight of about 500 or less Coal, dipentaerythritol, 1,3-butylethyl propanediol, 2-methyl-1,3-propanediol, 1,4-benzyldimethanol, 2,4-dimethyl-2-ethylhexane-1,3- It may be a diol, isopropylidenebis (p-phenylene-oxypropanol-2), and mixtures thereof. In some embodiments, the aliphatic glycol is a 1,3-carbon of 1,3-carbon atoms.
Cyclohexanedimethanol, 1,4-cyclohexanedimethanol (or 1,3
And a mixture of 1,4 cyclohexanedimethanol, which may be cis or trans), 2,2,4,4-tetramethyl-1,3-cyclobutanediol (cis, t
ran, or a mixture thereof), 4,4′-dihydroxy-2,2
It may contain '-diphenylpropane, or a mixture thereof.

The composition of the highly acidic stabilized polyester (second polyester) must be selected to exhibit excellent compatibility with one or more polyethylene terephthalate resins. Insufficient compatibility may not produce an excellent aqueous dispersion with small particle size (typically a volume average particle size of less than about 5 microns) and excellent stability. Furthermore, coatings obtained from such dispersions may have poor appearance due to lack of compatibility and may exhibit poor performance in coating evaluation tests. One method for evaluating compatibility is to melt mix one or more polyethylene terephthalate resins and a second polyester at temperatures above their respective melting points. A blend with good compatibility will usually be a relatively clear or translucent blend, while an incompatible blend will usually be an opaque or turbid white melt blend. Other methods of determining compatibility may be used, such as morphological measurements of the blend by optical or transmission electron microscopy.

In another embodiment, the stabilizer comprising the second polyester is a sulfopolyester that is dispersed directly in hot water without the aid of a neutralizing agent. The sulfopolyester essentially consists of (a) a dicarboxylic acid component comprising one or more sulfomonomers (including, but not limited to, dimethyl-5-sodiosulfoisophthalate, and 5 -Sodiosulfoisophthalic acid is included.The dicarboxylic acid component usually also includes one or more conventional dicarboxylic acids used in the preparation of polyesters, including but not limited to isophthalic acid) (B) a diol component composed of one or a plurality of diols usually used in the production of polyester (the diol component is not limited, but includes diethylene glycol, 1,4-cyclohexanedimethanol (cis or trans)) 1,3
-Cyclohexanedimethanol (cis or trans), and mixtures thereof). Sulfopolyesters usually have a glass transition temperature (Tg) between 20-60 ° C.
Have

The sulfopolyesters useful in the present invention are US Pat. No. 3,546,008; US Pat. No. 4,340,519; US Pat. No. 3,734,874; US Pat. No. 3,779.
, 993; and U.S. Pat. No. 4,233,196, which are incorporated herein by reference to the extent that such sulfopolyesters are disclosed. Useful sulfopolyesters are available from Eastman Chemical, such as, for example, Eastman AQ29, Eastman AQ38, and Eastman AQ55. Such suitable sulfopolyesters are usually pre-neutralized.

The composition of the stabilized polyester (second polyester) must be selected to exhibit excellent compatibility with the first polyester. Insufficient compatibility may not produce an excellent aqueous dispersion with small particle size (typically a volume average particle size of less than about 5 microns) and excellent stability. Furthermore, coatings obtained from such dispersions may have poor appearance due to lack of compatibility and may exhibit poor performance in coating evaluation tests. For example, when an aliphatic strongly acidic polyester (second polyester) is used to disperse the aromatic and hydrophobic first polyester, it usually has a large particle size (typically greater than 5 microns in volume). This results in an insufficient dispersion having an average particle size).
One method for evaluating compatibility is to melt mix the first polyester and the second polyester at temperatures above their respective melting points. A blend with good compatibility will usually be a relatively clear or translucent blend, while an incompatible blend will usually be an opaque or turbid white melt blend. Other methods of determining compatibility may be used, such as morphological measurements of the blend by optical or transmission electron microscopy.

In selected embodiments, the stabilizer may optionally include a surfactant. Other stabilizers that can be used include, but are not limited to, long chain fatty acids, fatty acid salts, or fatty acid alkyl esters having from 12 to 60 carbon atoms.
In other embodiments, the long chain fatty acid or fatty acid salt may have 12 to 40 carbon atoms.

Additional stabilizers that may be useful in the practice of the present invention include, but are not limited to:
Cationic surfactants, anionic surfactants, or nonionic surfactants are included. Examples of anionic surfactants include, but are not limited to, sulfonates, carboxylates and phosphates. Examples of cationic surfactants include, but are not limited to quaternary amines. Examples of nonionic surfactants include, but are not limited to:
Block copolymers containing ethylene oxide and silicone surfactants are included. Stabilizers useful in the practice of the present invention may be either external surfactants or internal surfactants. External surfactants are surfactants that do not penetrate into the base polymer through chemical reaction during dispersion preparation. Examples of external surfactants useful herein include, but are not limited to, dodecylbenzene sulfonate and lauryl sulfonate. An internal surfactant is a surfactant that chemically reacts into the base polymer during dispersion preparation. Examples of internal surfactants useful herein include 2,2-dimethylolpropionic acid and its salts. Additional surfactants that may be useful in the practice of the present invention include cationic surfactants, anionic surfactants, nonionic surfactants, or combinations thereof. In the embodiments disclosed herein, OP-100
(Sodium stearate), OPK-1000 (potassium stearate), and OP
K-181 (potassium oleate) (each available from RTD Hallstar); UNICID 350 (available from Baker Petrolite)
DISPONIL FES 77-IS, DISPONIL TA-430, Disp
onil FES-32 and Diponil FES-993 (Cogni, respectively)
RHODAPEX CO-436, SOPPROHOR 4D
384, 3D-33, and 796 / P, RHODACAL BX-78 and LDS-
22, RHODAFAC RE-610, and RM-710, and SUPRAGIL
MNS / 90 (each available from Rhodia); and TRITON Q
S-15, TRITON W-30, DOWFAX 2A1, DOWFAX 3B2, D
OWFAX 8390, DOWFAX C6L, TRITON X-200, TRITO
N XN-45S, TRITON H-55, TRITON GR-5M, TRITON
BG-10 and TRITON CG-110 (Dow Chemical, respectively)
Available from Company, Midland, Michigan); and ESPERSE grades E-100, E-506, E-328, E-355, and E
A variety of commercially available surfactants may be used including -600 (each available from Ethox Chemicals, LLC).

Further stabilizers that can be used include acrylic acid and / or methacrylic acid, and their (C ₁ -C ₃₀ ) esters or amides; acrylamide / methacrylamide and their N-substituted derivatives; acrylonitrile; styrene and substituted styrene derivatives, etc. A solution or suspension polymer composed of ethylenically unsaturated monomers.

Exemplary polymer stabilizers include, but are not limited to, a copolymer comprising (i) 5 to 95% by weight of one or more hydrophilic monomers and (ii) 5 to 95% by weight of one or more Included are amphiphilic copolymer compositions comprising reaction products with multiple types of copolymerizable ethylenically unsaturated hydrophobic monomers. These materials are water soluble or can be emulsified, especially when neutralized, and can act as colloidal stabilizers. Exemplary stabilizers include, for example, but are not limited to butyl acrylate and lauryl methacrylate.

Representative nonionic, water-soluble monomers that are suitable for making amphiphilic copolymer compositions include, but are not limited to, acrylamide, methacrylamide, N, N-dimethylacrylamide, N, N- Diethylacrylamide, N-isopropylacrylamide, N-vinylformamide, N-vinylmethylacetamide, N-vinylpyrrolidone,
Alkyl (meth) acrylates such as hydroxyethyl methacrylate, hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, t-butyl acrylamide, N methylol acrylamide, methyl (meth) acrylate, butyl acrylate and ethyl acrylate, Vinyl monomers such as ethylene, styrene, divinylbenzene, diisobutylethylene, vinyl acetate and N-vinylpyrrolidone, and allyl monomers such as allyl (meth) acrylate are included.

Representative cationic, water-soluble monomers suitable for producing amphiphilic copolymer compositions include, but are not limited to, acrylamide, methacrylamide, N, N-dimethylacrylamide, N, N-diethyl. Acrylamide, N-isopropylacrylamide, N-vinylformamide, N-vinylmethylacetamide, N-vinylpyrrolidone,
t-butylacrylamide, N-methylolacrylamide, tributylammoniumethyl (meth) acrylate TBAEMA, DMAEMA, DMAPMAM, diallyldimethylammonium chloride (DADMAC), methylacrylamidepropyltrimethylammonium chloride (MAPTAC), acrylamidopropyltrimethylammonium chloride (APTAC), Quaternary ammonium salts of amine functionalized monomers such as N-vinyl pyrrolidone, vinyl imidazole, polyquaternium-11 and polyquaternium-4 are included.

“Anionic” or “acid-containing monomers” suitable for making amphiphilic copolymer compositions include, but are not limited to, carboxylic acid groups, phosphonic acid groups, phosphinic acid groups, sulfinic acid groups and Ethylenically unsaturated monomers containing sulfonic acid groups are included.
Suitable examples include (meth) acrylic acid, maleic acid, succinic acid, itaconic acid, vinyl phosphonic acid and vinyl sulfonic acid.

In an alternative embodiment, the one or more stabilizers can react with an acrylic acid resin or acrylic acid monomer to form a polyester acrylate, polyamide acrylate epoxy resin acrylate, polyester, epoxy resin, polyamide resin. It is also possible to use a resin such as

Polyester acrylates as stabilizers may be formed by in-situ polymerization of copolymerizable ethylenically unsaturated monomers in the presence of polyester. Examples include not only vinyl monomers and vinyl esters, but also ethylenically unsaturated mono- or polyfunctional acids, esters of ethylenically unsaturated mono- or polyfunctional acids, with polyester, in the presence or absence of a reaction fluid, Amides and nitriles are included. The polyester acrylate in the solvent can be dried by any suitable method known to those skilled in the art.

Epoxy resins suitable for making stabilizers may be obtained according to conventional procedures well known to those skilled in the art by reacting a polyepoxide with a suitable multivalent nucleophile. Suitable epoxides include, but are not limited to, glycidyl ether and other molecules containing epoxy groups. Suitable polynucleophiles include, but are not limited to, polyphenols, and polyphenols, polythiols, aliphatic polyhydric alcohols or polybasic acids or polyamines. Exemplary suitable epoxies include, for example, but are not limited to, at least two glycidyl ether groups per polyglycidyl ether molecule at elevated temperatures in the presence of conventional catalysts, with or without solvents. Glycidyl ether containing (for example, at least diglycidyl ether) and polyhydric phenol containing at least two hydroxyl groups in the polyhydric polyphenol (eg, at least dihydric phenol or diphenol). Another class of epoxy resins is, for example, at least 2 per polyglycidyl ether molecule at elevated temperatures in the presence of conventional catalysts, with or without solvents.
Reacting a polyglycidyl ether containing one glycidyl ether group (eg at least diglycidyl ether) with a polybasic acid containing at least two carboxyl groups per polybasic acid molecule (eg at least a dibasic polycarboxylic acid) May be obtained according to conventional procedures well known to those skilled in the art.

The epoxy acrylate for producing the stabilizer may be formed by in-situ polymerization of a copolymerizable ethylenically unsaturated monomer in the presence of an epoxy resin. Examples include, but are not limited to, ethylenically unsaturated mono- or polyfunctional acids, ethylenically unsaturated, as well as vinyl monomers and vinyl esters, with or without an epoxy resin, in the presence or absence of a reaction fluid. Mono- or polyfunctional acid esters, amides, nitriles are included. Alternatively, an acrylic resin containing acid functionality of the polymer can be reacted with the epoxy resin in the presence of a suitable catalyst to form an epoxy acrylate. The epoxy acrylate in the solvent can be dried by any suitable method known to those skilled in the art. In one embodiment, the surfactant may comprise a reaction product of an acid functionalized polyester and an epoxy resin.

In one embodiment, the stabilizer comprises a second polyester that is an acid-functionalized oligomer derived from a PET-based polyester.

The neutralizer stabilizer can be partially or completely neutralized with a neutralizer. In certain embodiments, neutralization of the stabilizer (second polyester) may be from 50 to 250 percent on a molar basis; or alternatively, may be from 50 to 200 percent on a molar basis; or Alternatively, it may be 50 to 150 percent on a molar basis; or alternatively, 50 to 120 percent on a molar basis. For example, the neutralizing agent may be a base such as ammonium hydroxide, sodium hydroxide or potassium hydroxide. Other neutralizing agents can include, for example, lithium hydroxide or sodium hydroxide. In another alternative, the neutralizing agent may be a carbonate, for example. In another alternative, the neutralizing agent may be any amine such as, for example, monoethanolamine or 2-amino-2-methyl-1-propanol (AMP). Useful amines in the embodiments disclosed herein include diethanolamine, triethanolamine, and TRIS AMINO ™ (each A
ngus), NEUTROL ™ TE (available from BASF), and triisopropanolamine, diisopropanolamine, and N, N-dimethylethanolamine (Dow Chemical Company, Midlan, respectively)
d, available from MI). Other useful amines are ammonia, monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, mono-n-propylamine, butylamine, dibutylamine, tributylamine, dimethylbenzylamine, dimethyln-propylamine, N -Methanolamine, N-aminoethylethanolamine, N-methyldiethanolamine, monoisopropanolamine, N, N-dimethylpropanolamine, 2-amino-2-methyl-1-propanol, 1,2-diaminopropane, tris (hydroxy Methyl) aminomethane, ethylenediamine N, N, N′N′-tetrakis (2-hydroxylpropyl) ethylenediamine, N, N, N ′, N′tetramethylpropanediamine, 3-methoxy Cypropylamine, iminobis-propylamine and the like may be included. In some embodiments, a mixture of amines or a mixture of amines and other surfactants may be used. In one embodiment, the neutralizing agent may be a polymeric amine, such as diethylenetriamine. One skilled in the art understands that the selection of a suitable neutralizing agent will depend on the particular composition to be formulated, and such selection is within the knowledge of one of ordinary skill in the art. In one embodiment, an amine having a boiling point of less than 250 ° C. may be used as a neutralizing agent.

The liquid medium aqueous dispersion further includes a liquid medium. The liquid medium may be any medium, for example, the liquid medium may be water. The aqueous dispersion comprises 15 to 90 weight percent water based on the weight of the dispersion; for example, the dispersion is 20 to 85 weight percent water based on the weight of the dispersion; or alternatively the dispersion 30 to 75 weight percent water based on the weight of
Or alternatively, 40 to 75 weight percent water based on the weight of the dispersion; or alternatively 40 to 65 weight percent water based on the weight of the dispersion. The water content of the dispersion is
Preferably, the solids content (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester) is in the range of 10 to 85 weight percent based on the weight of the dispersion. , May be controlled. For example, the dispersion may have a solids content of 20 to 70 weight percent (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester) relative to the weight of the dispersion; A solids content of 25 to 70 percent by weight based on the weight of the dispersion (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester); or alternatively, the dispersion A solids content of 35 to 70 percent by weight relative to the weight of (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester); or alternatively,
A solids content of 35 to 65 percent by weight relative to the weight of the dispersion (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester); or alternatively, the weight of the dispersion A solids content of 40 to 70 percent by weight (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester); or alternatively 40 To 65 weight percent solids (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester)
Or alternatively 45 to 65 weight percent solids content of the dispersion (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester); or Includes a solids content of 50 to 70 weight percent (sum of one or more polyethylene terephthalate resins and a stabilizer comprising a second polyester) based on the weight of the dispersion.

The liquid medium may optionally contain one or more suitable solvents. For example, the one or more optional solvents include, but are not limited to, glycols, glycol ethers, 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, alcohols, Ketones, glycol ether esters, mineral spirits,
Aromatic solvents and / or esters etc. are included; optionally one or more dispersants, for example amino alcohols and / or polycarboxylates.

Additional components The aqueous dispersions of the present invention optionally contain one or more binder compositions, such as
Acrylic latex, vinyl acrylic latex, styrene acrylic latex, vinyl acetate ethylene latex, epoxy dispersion, polyurethane dispersion, alkyd dispersion, polyolefin dispersion, and combinations thereof; optionally one or more fillers; One or more additives such as catalysts, wetting agents, antifoaming agents, flow agents, mold release agents, slipping agents, antiblocking agents, sulfide contamination concealing agents, pigment wetting / dispersing agents, antisettling agents,
UV stabilizers, adhesion promoters; optionally one or more lubricants such as fatty acid ester waxes, silicon-based waxes, fluorine-based waxes, polyethylene or any other similar polyolefin wax, carnauba wax, Lanolin wax and the like; optionally one or more corrosion inhibitors such as aluminum and zinc;
Optionally, one or more pigments such as titanium dioxide, barium sulfate, mica,
Calcium carbonate, silica, zinc oxide, ground glass, aluminum trihydrate, talc, antimony trioxide, fly ash and clay, etc .; optionally one or more co-solvents such as glycols, glycol ethers, 2, 2,4-trimethyl-1,3-pentanediol monoisobutyrate, alcohols, mineral spirits, aromatic solvents and benzoate esters, etc .; optionally one or more dispersants such as amino alcohols and polycarboxylic acids Acid salt; optionally one or more surfactants; optionally one or more preservatives such as biocides, fungicides, fungicides, algicides, and combinations thereof; One or more thickeners, for example celluloses such as hydroxyethylcellulose Thickeners, hydrophobically modified alkali soluble emulsions (HASE thickeners such as UCAR POLYPHOBE TR-116) and hydrophobically modified ethoxylated urethane thickeners (HEUR); or optionally One or more additional neutralizing agents such as hydroxides, amines, ammonia and carbonates; optionally may be blended with one or more solvents or coalescing agents.

Further, the aqueous dispersion can be blended with one or more dispersions, emulsions, suspensions, colloidal suspensions, and the like.

For example, the aqueous dispersions of the present invention can be blended with polyurethane dispersions, alkyd dispersions, epoxy dispersions, polyolefin dispersions, vinyl acetate emulsions, acrylic acid emulsions, vinyl acetate ethylene emulsions, and the like. The addition of additional components described herein can be accomplished as part of the process of making the dispersion, i.e., the additional components are added during the manufacture of the aqueous dispersion; or alternatively , Additional components can be added after the aqueous dispersion is made, i.e., the additional components are added into the aqueous dispersion after the dispersion is made; or alternatively, combinations thereof, i.e. Additional components can be added during the process of making the dispersion, and such additional components are also added after the dispersion is made.

The aqueous crosslinker dispersion optionally further comprises at least one or more crosslinkers and / or optionally one or more catalysts to increase the crosslinking rate to promote crosslinking. May be included. Such catalysts are generally known and the selection of a suitable catalyst usually depends on other factors such as the choice of cross-linking agent and the conditions for such cross-linking. Such catalysts include, but are not limited to, for example, dodecylbenzenesulfonic acid, p-toluenesulfonic acid, dinonylnaphthalenedisulfone, depending on the type of crosslinking agent (strong acid, weak acid or metal-containing compound). Acids, methanesulfonic acid, phosphoric acid, or weak acids such as ammonium or phosphonium salts or chelating compounds of tin, bismuth, zirconium or aluminum are included. Exemplary catalysts include, but are not limited to, NACURE ™, K-Kure ™ and K-Kat ™
(Available from King Industries), CYCAT ™ (Cytec
Industries) and / or FASCAT ™ (Arkema In
c. Made). The aqueous dispersion of the present invention is 0.5% based on the total weight of the solid content of the dispersion.
To 50 weight percent of one or more crosslinking agents. All individual values and subranges from 0.5 to 50 weight percent are included herein and disclosed herein; for example, weight percent is 0.5, 1, 3, From the lower limit of 5, 10.15 or 20 weight percent, 10, 12, 15, 18, 20, 25, 30, 35, 40, 45
Or it can be up to an upper limit of 50 weight percent. For example, the dispersion can be from 1 to 18; or alternatively from 1 to 15; or alternatively 1 from the total weight of the solid content of the dispersion.
Or alternatively 1 to 10; or alternatively 1 to 20; or alternatively 1 to 30; or alternatively 1 to 40; or alternatively 1 to 45; or alternatively 1 to 50. It may contain a weight percent of one or more crosslinkers. In selected embodiments, the cross-linking agent is, for example, a phenol-formaldehyde resin, an amino-formaldehyde resin, including but not limited to urea-formaldehyde resin, melamine formaldehyde resin, benzoguanamine formaldehyde resin, anhydride resin, epoxy resin. ,
A resin containing an epoxy group such as polyester or acrylic resin containing an epoxy group,
And block or non-block isocyanate resins, and combinations of two or more thereof (provided that such a combination of crosslinkers is compatible).

The cross-linking agent can be a compound that reacts with reactive functional groups contained in the dispersion formulation, thereby promoting their cross-linking. Such functional groups can be present in both one or more polyethylene terephthalate resins and stabilizers including the second polyester.

For example, reactive functional groups include, but are not limited to, acid groups such as carboxylic acid groups in free or neutralized form, or separation by other components such as alcohol groups, amino groups, epoxy groups, etc. Any functional group having an active hydrogen of

The crosslinkable functional group in the crosslinker is a group capable of reacting with the reactive functional group of the stabilizer including the first polyester or the second polyester. For example, carbodiimide group, oxazoline group, isocyanate group, epoxy group, methylol group, aldehyde group, acid anhydride group,
Hydroxy groups, aziridinyl groups or silane groups can be used in the crosslinking agent.

Another possibility for crosslinkable acid functional groups is by using polyvalent metal ions by reaction of the aforementioned acid groups with substances containing polyvalent metal ions such as zinc oxide.

Carboxylic acids can also react and crosslink with olefinically unsaturated materials containing polyfunctional groups under the action of strong acids. Carbonates containing polyfunctional groups can also react with carboxylic acids to liberate carbon dioxide and produce ester linkages.

Alternatively, the crosslinking may be carried out by addition of peroxides or free radical crosslinking initiated by radiation, eg electron beam.

With respect to the crosslinkable functional group, one or more kinds may be present in the crosslinking agent. Alternatively,
Two or more crosslinkable functional groups may be present in a single molecule.

The crosslinking agent having a crosslinkable functional group described above may be a water-dispersed or water-dispersible or water-soluble substance. In one embodiment, exemplary crosslinkers include, but are not limited to, aqueous monomeric or polymeric materials, which include two or more oxazoline groups, carbodiimide groups, epoxy groups, isocyanates per molecule. Groups, methylol groups, etc., or some of these.

An exemplary oxazoline crosslinker is an aqueous polymer having two or more oxazoline groups in the molecule, and the material can be obtained by polymerizing oxazoline group-containing monomers, and optionally ethylenically unsaturated monomers. it can. Alternatively, the oxazoline crosslinking agent can be obtained by a reaction between a nitrile group and an aminoethanol group, dehydration of a hydroxylalkylamide group, or the like.

The crosslinking agent having two or more carbodiimide groups can be produced from the diisocyanate compound by a condensation reaction that occurs in association with the decarboxylation reaction of the diisocyanate compound.
Examples of diisocyanate compounds include, but are not limited to, 1,5-naphthylene diisocyanate, 4,4′-diphenylmethane diisocyanate, 4,4′-diphenyldimethylmethane diisocyanate, 1,4 -Phenylene diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, hexanemethylene diisocyanate, cyclohexane-1,4-diisocyanate, xylylene diisocyanate, isophorone diisocyanate, Examples include dicyclohexylmethane-4,4′-diisocyanate, methylcyclohexane diisocyanate, and tetramethylxylylene diisocyanate. These compounds can also be used as a mixture.

Monofunctional isocyanates may be included to control the resin molecule chain length, for example
Phenyl isocyanate, tolyl isocyanate, cyclohexyl isocyanate, dimethylphenyl isocyanate, butyl isocyanate and naphthyl isocyanate are useful.

The diisocyanate material may be partially reacted with an aliphatic compound, alicyclic compound or aromatic compound having a hydroxyl group, an imino group, an amino group, a carboxyl group, a mercapto group, an epoxy group, or the like.

A carbodiimidization catalyst can be used in the condensation reaction that occurs with the decarboxylation of the diisocyanate compound. Suitable for use as such a catalyst is, for example, 1-
Phosphorene oxides such as phenyl-2-phospholene-1-oxide, 3-methyl-2-phospholene-1-oxide, 1-ethyl-2-phospholene-1-oxide, and their 3-phospholene isomers.

In order to convert a carbodiimide group-containing polymer into an aqueous polymer, a hydrophilic moiety is provided in the molecular structure of the carbodiimide group-containing polymer. For example, an aqueous polymer containing a carbodiimide group can be obtained by supplying a hydrophilic portion having a functional group having reactivity with an isocyanate group. Suitable for use as the hydrophilic moiety are quaternary ammonium salts of dialkylaminoalkylamines (eg, quaternary ammonium salts of 2-dimethylaminoethanol); quaternary salts of dialkylaminoalkylamines (eg, 3 −
Dimethylamino-n-propylamine); alkyl sulfonates having at least one reactive hydroxyl group (eg sodium hydroxypropane sulfonate); polyethylene oxide or polyethylene oxide capped with an alkoxy group at the end; , And a mixture with polypropylene oxide (for example, polyethylene oxide capped with a methoxy group or an ethoxy group at the terminal position).

As an aqueous crosslinking agent containing an epoxy group, sorbitol polyglycidyl ether, glycerin triglycidyl ether, polyglycerin polyglycidyl ether trimethylolpropane triglycidyl ether, poly (ethylene glycol) diglycidyl ether,
Examples include poly (propylene glycol) diglycidyl ether, phenol ethylene oxide glycidyl ether, and lauryl alcohol ethylene oxide glycidyl ether. In addition to the above, examples that may be mentioned include carboxy compounds (obtained by reaction between polyoxyethylene polyol compounds and acid anhydride compounds) with epoxy having two or more epoxy groups in the molecule. A water-soluble epoxy resin obtained by reacting with a resin; and a self-emulsifying epoxy resin composition obtained by mixing a water-soluble epoxy resin with an epoxy resin having two or more epoxy groups in its molecule is there. Such resins are, for example, XZ 92533.00, XZ 92598.0.
Dow Chemical Company with trade names of 0 and XZ 92446.00
, Midland, MI. Examples of anhydride compounds include, but are not limited to, preferably aromatic anhydrides such as phthalic anhydride, trimellitic anhydride and pyromellitic anhydride; and maleic anhydride, succinic anhydride, tetrahydro Cyclic aliphatic anhydrides such as phthalic anhydride, methyltetrahydrophthalic anhydride, methyl nadic anhydride, alkenyl succinic anhydride, hexahydrophthalic anhydride and methyl hexahydrophthalic anhydride are included. There is no limitation with respect to epoxy resins having two or more epoxy groups in the molecule, and all known epoxy resins having two or more epoxy functional groups can be used. Examples include epichlorohydrin and polyhydric hydroxyl compounds such as phenol novolac and cresol novolac bisphenol A, bisphenol F, bisphenol S, resorcinol, hydroquinone or catechol; bisphenol A with added alkylene oxide; polypropylene glycol, 1 Polyglycidyl ethers obtained from polyhydric alcohols such as 1,6-hexanediol, trimethylolpropane, glycerin and cyclohexanedimethanol; and polyglycidyl esters and polyglycidyl of polycarboxylic acids such as adipic acid, phthalic acid and dimer acid There is an amine.

Examples of the aqueous crosslinking agent containing an isocyanate group include an isocyanurate group-containing polyisocyanate, a uretdione group-containing polyisocyanate, a uretdione group / isocyanurate group-containing polyisocyanate, a urethane group-containing polyisocyanate, and an allophanate. Group-containing polyisocyanates, biuret group-containing polyisocyanates, carbodiimide group-containing polyisocyanates, and uretdione group-containing polyisocyanates (each of which has 1,6-hexamethylene diisocyanate and / or isophorone diisocyanate as raw materials) A polyisocyanate mainly comprising at least one element selected from the group consisting of: comprising at least one group; and at least one active hydrogen group (which can react with the isocyanate group) The hydrophilic surfactant, or polyethylene ether alcohols containing at least three polyethylene oxide units, fatty acid esters (This is the sum of the number of carbon atoms of fatty acids and hydroxyl-containing compounds as raw materials 8 or more,
There are self-emulsifying polyisocyanates obtained by reacting with at least one active hydrogen group capable of reacting with isocyanate groups. In addition to the above,
6-hexamethylene diisocyanate and / or urethane group-containing polyisocyanate obtained by reaction between isophorone diisocyanate and an active hydrogen group-containing compound, or allophanate reaction, carbodiimidization reaction of these diisocyanate compounds ,
Mention may be made of polyisocyanates obtained by uretdioneation and biuretization reactions.

Examples of suitable cross-linking agents comprising aldehydes are water-dispersed or water-dispersible or water-soluble phenol formaldehyde resins, amino formaldehyde resins or combinations thereof.

Phenol formaldehyde crosslinking agents include, but are not limited to, reaction products of aldehydes and phenols. Preferred aldehydeoids include, but are not limited to formaldehyde and acetaldehyde. Without limitation, phenol, cresol, p-phenylphenol, p-tert-butylphenol, p-
Various phenols can be used, such as tert-amylphenol, cyclopentylphenol, cresolic acid, bisphenol-A, bisphenol-F, and combinations thereof. Phenols containing acid functional groups can also be used to make phenol formaldehyde resins. The crosslinker may be deetherified or etherified with an alcohol or polyol. These phenol formaldehyde resins may be water soluble or self-emulsifying or can be stabilized by the use of colloidal stabilizers such as polyvinyl alcohol.

Amino formaldehyde crosslinkers include, but are not limited to, reaction products of aldehydes with amino or amide group containing molecules. Exemplary aldehydes include, but are not limited to formaldehyde and acetaldehyde. Various amino or amide group-containing molecules can be used, including but not limited to urea, melamine, benzoguanamine, acetoguanamine, glycoluril, and the like. Suitable amino-crosslinked resins include melamine-formaldehyde, urea-formaldehyde, benzoguanamine-formaldehyde, acetoguanamine-formaldehyde, glycoluril-formaldehyde resin. The methylol group of the aminoformaldehyde resin is at least one of the group of monohydric aliphatic alcohols such as methanol and / or n-butanol,
It can also be partially or completely etherified. These aminoformaldehyde resins may be water soluble or self-emulsifying or may be stabilized by the use of a colloidal stabilizer such as polyvinyl alcohol to stabilize the aminoformaldehyde dispersion.

Commercial amino-formaldehyde resins that are water soluble or water dispersible and useful for this purpose include Cymel ™ 301, Cymel ™ 303, Cymel ™ 370, and Cymel ™ 373. (All Cytec Surface S
specialties, Brussels, Belgium).
Other aldehydes used to react with amino compounds to form resin materials include crotonic aldehydes, acrolein, or compounds that produce aldehydes such as hexamethylene-tetraamine, paraaldehyde.

Another type of crosslinker for carboxylic acid groups is a water soluble hydroxyalkylamide crosslinker such as bis (N, N′-dihydroxyethyl) adipamide. Such compounds are traded under the trade name PRIMID ™ crosslinker resin, eg PRIMID ™ XL-522, P
As RIMID ™ SF-4510 and PRIMID ™ QM-1260,
Commercially available from EMS-PRIMID (Switzerland).

One or more cross-linking agents may be added to the aqueous dispersion as part of the aqueous dispersion compounding process; or alternatively, one or more cross-linking agents may be added to the aqueous dispersion after the dispersion compounding process. It may be added to the body.

In one embodiment, depending on the type of food or beverage contained in the coated container and the required coating properties, it may be beneficial to combine several crosslinkers, or some crosslinks Agents may be more suitable than others. Some crosslinkers are
It may not be suitable for all applications. Some crosslinkers may require the addition of a catalyst for proper curing.

The crosslinker helps to form a thermoset network, which is indicated by the higher value of the MEK double rub test compared to the same formulation without the crosslinker.

Dispersion Formation Aqueous dispersions may be formed by several methods recognized by those skilled in the art. The dispersing apparatus can be operated in batch, semi-batch or continuous mode. Examples of mixers include melt kneading devices such as rotors / stators, microfluidizers, high pressure homogenizers, ultrasonic, impinging jets, Cowles ™ blades, planetary mixers, and extruders.

In one embodiment, one or more stabilizers including one or more polyethylene terephthalate resins, a second polyester, water, and optionally one or more types, are formed to form the dispersion. It is melt kneaded in an extruder together with a neutralizing agent such as ammonia, potassium hydroxide, an amine, or a combination of two or more. In another embodiment, one or more stabilizers comprising one or more polyethylene terephthalate resins, a second polyester are mixed, then water, and optionally one or more neutralizations. In the presence of the agent,
Melt and knead in an extruder, thereby forming a dispersion. In some embodiments, the dispersion is first diluted to contain 1 to 20 weight percent, for example 1 to 5 weight percent or 1 to 3 weight percent water based on the weight of the dispersion, followed by 15 to 9
Further dilute to contain 0 weight percent water. In one embodiment, the further dilution is
You may implement by a solvent. In one embodiment, the dispersion does not contain any solvent.

Any melt kneading means known in the art may be used. In some embodiments,
A melt pump coupled to a kneader, a BANBURY® mixer, a single screw extruder, or a multi-screw extruder, such as a twin screw extruder, rotor / stator is used. The method for producing the dispersion of the present invention is not particularly limited. For example, an extruder, in certain embodiments, for example, a twin screw extruder is combined with a back pressure controller, a melt pump or a gear pump. The exemplary embodiment also includes a base reservoir and an initial water reservoir, each of which includes a pump. Desired amounts of base and initial water are supplied from a base reservoir and initial water reservoir, respectively. Although any suitable pump may be used, in some embodiments, a pump that provides a flow of about 150 cc / min at a pressure of 240 bar, for example, to supply base and initial water to the extruder Is used. In other embodiments, the liquid infusion pump is 300 cc / min or 133 at 200 bar.
Provides a flow of 600 cc / min at bar. In some embodiments, the base and initial water are preheated in a preheater.

For example, one or more polyethylene terephthalate resins in the form of pellets, powder or flakes are fed from a feeder to the inlet of the extruder, where the resins are melted or mixed. One or more additional ingredients may be fed into the extruder by a feeder, optionally simultaneously with one or more polyethylene terephthalate resins;
Alternatively, one or more additional components may be mixed into one or more polyethylene terephthalate resins and then fed into the extruder by a feeder. Alternatively, additional one or more additional ingredients may be further metered into a molten mixture comprising one or more polyethylene terephthalate resins, optionally via a previous inlet in the emulsification zone. You may supply. In some embodiments, the stabilizer comprising the second polyester is one or more polyethylene terephthalate resins together with one or more polyethylene terephthalate resins through one or more polyethylene terephthalate resins. As well as in other embodiments, a stabilizer comprising a second polyester is separately fed to the twin screw extruder. The resin melt is then fed from the mixing and transport zone to the emulsification zone of the extruder, where initial amounts of water and base are added from the water and base reservoir through the inlet. In some embodiments, a stabilizer comprising a second polyester may be added additionally or exclusively to the water stream. In some embodiments, additional dilution water may be added from the water reservoir via the water inlet to the dilution and cooling zone of the extruder. Typically, the dispersion is diluted to at least 30 weight percent water in the cooling zone. Further, the diluted mixture may be diluted many times until the desired dilution level is obtained. In some embodiments, the dispersion is further cooled by use of a suitable heat exchanger after being discharged from the extruder. In other embodiments, water is not added into the twin screw extruder, but rather is added to the stream containing the resin melt after the melt is discharged from the extruder. In this way, the increase in water vapor pressure in the extruder is eliminated and the dispersion is formed in an auxiliary mixing device such as a rotor / stator mixer.

In another embodiment, the aqueous dispersion can be formed in a continuous high shear mixer without using a melt kneading extruder. In this embodiment, the first stream comprising one or more liquid or molten polyethylene terephthalate resins is a suitable liquid pump such as a syringe pump, gear pump or single screw pump (progressive cavity pu
mp) to a continuous high shear mixer. The first stream is flowed through a first conduit and is continuously joined with a second stream containing a continuous aqueous phase that is flowed through a second conduit. The first and second streams are combined in a disperser in the presence of a stabilizer comprising a second polyester, along with an optional neutralizing agent. The agent can be added to either the first or second stream or a separate stream. A third stream containing water may be added downstream from the disperser. The flow rate of the stream is adjusted to obtain a dispersion having the desired amount of polymer phase and percent solids. The disperser can be any one of a number of continuous in-line mixers such as an IKA high shear mixer, Oakes rotor / stator mixer, Ross mixer, Silverson mixer or centrifugal pump. The rpm setting of the disperser can be used to help control the particle size of the dispersed hydrophobic phase in the dispersion. The system can be heated to provide polymer and neutralizer components at a viscosity suitable for pumping. Water vapor production is reduced by controlling the pressure by the use of a back pressure controller, gear pump, metering pump, or other suitable device near the process outlet. In some embodiments, the dispersion is further cooled after discharge from the disperser by use of a suitable heat exchanger.

In another embodiment, the aqueous dispersion is in a batch or semi-batch high shear mixer, where the mixer may be placed, for example, in a pressurized tank, for example, to reduce steam production. Can be formed. All or at least a portion of the dispersion is removed from the tank during processing and optionally cooled by use of a suitable heat exchanger.

During the preparation of the aqueous dispersion, optionally one or more fillers; optionally catalysts, wetting agents, antifoaming agents, flow agents, mold release agents, slip agents, antiblocking agents, sulphide contamination masking agents One or more additives such as pigment wetting / dispersing agents, anti-settling agents, UV stabilizers, adhesion promoters; optionally fatty acid ester waxes, silicon-based waxes, fluorine-based waxes, polyethylene or any One or more lubricants such as other similar polyolefin waxes, carnauba waxes, lanolin waxes; optionally one or more corrosion inhibitors such as aluminum and zinc; optionally one or more lubricants Pigments such as titanium dioxide, mica, calcium carbonate, barium sulfate, silica, zinc oxide, crushed glass, aluminum Hydrates, talc, antimony trioxide, fly ash, clays and the like; optionally one or more dyes; optionally one or more cosolvents such as glycols, glycol ethers, 2,2,4- Trimethyl-1,3-pentanediol monoisobutyrate, alcohol, mineral spirits and benzoate esters, etc .; optionally one or more dispersants, such as amino alcohols and polycarboxylates; optionally one or more Species surfactants; optionally one or more antifoam agents; optionally one or more preservatives, for example biocides, fungicides, fungicides, algicides, and combinations thereof Optionally one or more thickeners, for example a cellulose base such as hydroxyethylcellulose Thickeners, alkali soluble emulsions which are hydrophobically modified (UCAR POLYPHOBE TR-116 or the like of the H
ASE thickeners) and hydrophobically modified ethoxylated urethane thickeners (HEUR); or optionally one or more additional neutralizing agents such as hydroxides, amines, ammonia and carbonates May be added to the aqueous dispersion formulation; alternatively, it may be added to the dispersion after the dispersion blending step.

During preparation of the aqueous dispersion, one or more cross-linking agents may be added to the aqueous dispersion formulation; or alternatively, after the dispersion compounding step, it may be added to the dispersion. .

Optionally, another polymer dispersion or emulsion may be used as part of the aqueous phase of the dispersion during the dispersion of one or more polyethylene terephthalate resins. Examples include but are not limited to acrylic acid, epoxy, polyester, polyurethane,
Dispersions, emulsions, suspensions, colloidal suspensions containing polyolefins, polyamides, alkyds and the like are included.

In one embodiment, the method of making the aqueous dispersion of the present invention comprises (1) selecting one or more polyethylene terephthalate resins; and (2) having an acid number greater than or equal to 15, for example greater than 20. (1) selecting one or more stabilizers comprising at least one second polyester; (3) selecting one or more neutralizing agents;
Melt blending one or more first polyesters, one or more stabilizers in the presence of water and one or more neutralizing agents; and (4) a dispersion thereby Producing an aqueous dispersion having a solids content of 10 to 74 percent relative to the total weight of the.

Application of coatings and molded aqueous dispersions of coated containers or sealed devices and / or coating compositions derived therefrom, including but not limited to metals, wood, plastics, leather, glass, concrete, etc. It may be used on any suitable substrate. In one embodiment, the aqueous dispersion and / or coating derived therefrom can be used, for example, for container coating applications such as cans or coating applications for closed devices. These coated container devices include
Non-food cans, non-food cans, eg aerosol containers such as hair sprays, hair dyes or colored spray lacquers; drums; kegs; pales; decorative tins; lids None tray; includes tubes, bottles, monoblocks, etc. Coated articles such as sealing devices include but are not limited to caps, lids such as thin aluminum foil base lids for yogurt and butter containers, or crown corks; for glass jars and bottles such as roll-on closures Closures, vacuum closures, pill fur proof closures, easy peel lids for can closures, and easy-open or conventional end faces for cans. The can may be a two-piece can or a three-piece can. Beverage cans include, but are not limited to, beer cans, carbonated soft drink cans, energy beverage cans, isotonic beverage cans, water cans, juice cans, tea cans, coffee cans, milk cans and the like. Food cans include, but are not limited to, vegetable cans, fruit cans, meat cans, soup cans, ladymeal cans, fish cans, edible oil cans, sauce cans and the like. Such cans can have any shape; for example, such cans can be cylindrical, cubic, spherical, hemispherical, bottle shaped, elongated cubic shaped, shallow or tall shaped. , Circular or rectangular shape,
Or it may have any other suitable shape. The coated articles of the present invention, such as container devices, can be formed by any conventional method. For example, coated container devices can be stamped, drawn, redrawn, wall ironed, bent, beaded, embossed, devoted, flanged, necked, stretched, blow stretched, and any other suitable It may be formed by a conventional method. Such methods are generally known to those skilled in the art. The aqueous dispersion and / or coating composition derived therefrom may be applied to a substrate, such as, for example, a metal sheet or metal foil, and the coated substrate is then coated with a coated container device or coated seal. It may be molded into a device. Alternatively, the substrate may be formed into a container device or a sealed device, and then the container device or sealed device is coated with one or more aqueous dispersions and / or coating compositions derived therefrom. Forming a coated container device or coated closed device. The coating may be applied by any method, for example, roller coating, spray coating, powder coating, dip coating, electrodeposition coating, printing, wash coating, flow coating, curtain coating.

Substrates include, but are not limited to, aluminum and aluminum alloys, electrolytic tin plated cold rolled low carbon mild steel (“ETP”), electrolytic chromium / chromium oxide plated cold rolled low carbon mild steel (ECCS), and any other One or more metals, including pre-treated steels
Alternatively, one or more polyolefins, for example one or more polymers such as polyethylene and / or polypropylene are included. The pretreatment may include, but is not limited to, treatment with phosphoric acid, zirconium phosphate, chromium phosphate, etc., and treatment with silane for reasons such as primary corrosion protection and improved adhesion. The substrate may comprise a sheet, strip or coil. The substrate may comprise one or more layers, each layer having a thickness of 0.01 μm to 2 mm; for example, 0.01 μm to 1.5 mm;
. 01 μm to 1 mm; or alternatively 0.01 μm to 0.5 mm; or alternatively 0.01 μm to 0.2 mm; or alternatively 0.01 μm to 0.1 mm or alternatively 0.01 μm Or alternatively 0.01 μm to 50 μm; or alternatively 1 μm to 50 μm; or alternatively, may have a thickness in the range of 1 μm to 15 μm. The substrate may be precoated with one or more precoating compositions. Such pre-coating compositions are not limited in some cases,
One or more resin binders, one or more resin crosslinking agents, one or more solvents, one or more additives, and one or more pigments. Also good. Exemplary resin binders include, but are not limited to, epoxy, polyester, polyvinyl chloride-containing organosol / vinyl, phenolic, alkyd, oleo resin, acrylic resin, and the like. Exemplary cross-linking agents include, but are not limited to, phenol-formaldehyde resins; amino-formaldehyde resins including but not limited to urea formaldehyde, melamine formaldehyde, benzoguanamine formaldehyde;
Examples include anhydride resins, block isocyanate resins, and, but are not limited to, epoxy resins, epoxy group-containing resins including epoxy group-containing polyesters, acrylic resins, vinyl resins, and the like. Exemplary solvents and thinners include, but are not limited to, glycol ethers, alcohols, aromatics such as aromatic hydrocarbons, white spirits, branched ketones and esters. Exemplary additives include, but are not limited to, catalysts, lubricants, wetting agents, antifoaming agents, flow agents, mold release agents, slipping agents, antiblocking agents, sulfide contamination hiding additives, pigment wetting / Dispersing agents, anti-settling agents, UV stabilizers, adhesion promoters are included. Pigments include, but are not limited to, titanium dioxide, zinc oxide, aluminum oxide, zinc and aluminum. The substrate can also be precoated with one or more precoat laminating compositions. Such compositions include, for example, polyethylene,
Polypropylene or polyester compositions are included and may be applied as a film on a metal surface by either a film lamination process or a melt extrusion coating process.

The one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate may be dried by any conventional drying method. Such conventional drying methods include, but are not limited to, air drying, convection oven drying, hot air drying, and / or infrared oven drying. During the drying process, crosslinking of one or more base polymers, stabilizers, or combinations thereof involving one or more crosslinking agents may occur. Additional curing may occur by radiation curing, for example electron beam curing. The one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate may be dried at any temperature, for example, the melting point of the first polyester It may be dried at a temperature in the range above the temperature, or alternatively at a temperature in the range below the melting point of the stabilizer comprising the second polyester. The one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate are about 60 ° F. (15.5 ° C.) to about 700 ° F. (371 ° C.). ) At a temperature in the range of between about 40 minutes, eg less than 20 minutes, or less than 10 minutes, or less than 5 minutes, or less than 2 minutes, or less than 1 minute, or less than 20 seconds. . All individual values and subranges from about 60 ° F. (15.5 ° C.) to about 700 ° F. (371 ° C.) are included herein and disclosed herein, for example, One or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate from about 60 ° F. (15.5 ° C.) to about 5
May dry at a temperature in the range of 00 ° F. (260 ° C.) for less than about 40 minutes, such as less than 20 minutes, or less than 10 minutes, or less than 5 minutes, or less than 2 minutes, or less than 1 minute; Alternatively, the one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate can be from about 60 ° F. (15.5 ° C.) to about 450 Dry at less than about 40 minutes, such as less than 20 minutes, or less than 10 minutes, or less than 5 minutes, or less than 2 minutes, or less than 1 minute at a temperature in the range of ° F (232.2 ° C.) . The temperature of the one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate is less than about 40 minutes to a temperature in the range above the melting temperature of the base polymer. May be raised during All individual values and subranges less than about 40 minutes are included herein and disclosed herein, for example, one or more applied to at least one surface of a substrate. The temperature of the seed aqueous dispersion and / or coating composition derived therefrom may be raised to a temperature in the range above the melting point temperature of the first polyester for less than about 20 minutes, or alternatively, The temperature of the one or more aqueous dispersions applied and / or the coating composition derived therefrom to at least one surface of the substrate is less than about 5 minutes to a temperature in the range above the melting temperature of the first polyester. Or in another alternative, one or more aqueous dispersions and / or coatings derived therefrom applied to at least one surface of the substrate Temperature of the composition, may be raised during the temperature in the range of from about 0.5 to 300 seconds the melting point temperature or more ranges of the first polyester. In another alternative, the temperature of the one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate is:
The temperature may be raised to a temperature in the range below the melting point temperature of the first polyester for less than 40 minutes. All individual values and subranges less than about 40 minutes are included herein and disclosed herein, for example, one or more applied to at least one surface of a substrate. The temperature of the seed aqueous dispersion and / or coating composition derived therefrom may be raised to a temperature in the range below the melting temperature of the first polyester for less than about 20 minutes, or alternatively, the substrate The temperature of the one or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of the substrate is less than about 5 minutes to a temperature in the range below the melting point temperature of the first polyester. Or in another alternative, one or more aqueous dispersions applied and / or a coating derived therefrom on at least one surface of the substrate Temperature Narubutsu may be raised during the temperature in the range of from about 0.5 to 300 seconds in the range of less than the melting point temperature of the first polyester.

The coated substrate may be further coated with one or more conventional coating compositions, or may be further laminated to one or more other layers. Such conventional coating compositions are generally known to those skilled in the art and include, but are not limited to, epoxy resin coating compositions, acrylate-based coating compositions, and polyester-based coatings. A composition may be included. Lamination processes are generally known and exemplary lamination layers are not limited,
Polyolefin-based laminates such as polyester laminates and polypropylene laminates may be included.

One or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of a substrate, for example a pre-coated substrate, are one or more crosslinked coating layers. As prior to retorting, ASTM-D 33
It may have a cross-cut adhesion of at least 3B measured according to 59-08; for example a 4B or 5B rating. One or more aqueous dispersions and / or coating compositions derived therefrom applied to at least one surface of a substrate can be used as Gardner “COVERALL” Bend T as one or more cross-linked coating layers.
It may have a wedge fold score of at least 50 percent, such as at least 70 percent, or alternatively at least 80 percent, or alternatively at least 90 percent, as measured by the ester IG1125.

The following examples illustrate the invention but do not limit the scope of the invention. Embodiments of the present invention provide that one or more aqueous dispersions applied to at least one surface of a metal substrate can provide improved coating layer flexibility as well as adhesion of the coating layer to the metal substrate. Is also exemplified.

Description of Formulation Components Crylcoat 1510 has a T _{g of} about 58 ° C., a melt viscosity of 8500 poise at 200 C, an acid number of 71 mg KOH / g, and a hydroxyl number of less than 20 mg KOH / g,
It is an aromatic polyester available from ytec Industries.

Cadence GS4 is a polyester of PET type copolyester available from Eastman Chemical having a T _{g of} 80 ° C. and an intrinsic viscosity of about 0.59 Dl / g.

CYMEL 303 crosslinker is> 98% non-volatile liquid form, 2600-5000
Cytec Industrial, supplied as a clear viscous liquid with centipoise viscosity
Commercial grade hexamethoxymethyl melamine available from ries.

NACURE 5925 is an amine-neutralized DDBSA catalyst available from King Industries, which is supplied as a clear pale amber liquid with 25% active material and typical recommended use levels are total resin solids 0.5 to 2.0 in the supply state
%.

Eastman AQ 55s has a T _{g of} about 55 ° C., a melt viscosity of 42000 poise at 200 C, an acid value of <2 mg KOH / g, and a hydroxyl value of <10 mg KOH / g.
A sulfonated polyester available from Eastman Chemical.

Preparation of Aqueous Dispersion Examples A and B of the Invention Aqueous Dispersion Examples A and B were prepared according to the following procedure based on the formulation ingredients listed in Table 1. One or more polyethylene terephthalate resins and stabilizers were fed to a 25 mm diameter twin screw extruder by separate controlled flow rate feeders. In the extruder, one or more polyethylene terephthalate resins and stabilizers were melted, mixed and transferred. The extruder temperature profile was initially set at 150 ° C. prior to the addition of initial water and neutralizing agent. After addition of initial water and neutralizing agent, the temperature was reduced to 120 ° C. across the barrel. In Example A, DMEA, 2-dimethylaminoethanol (100%) (CAS NO. 108-01-0) was used as a neutralizing agent. In Example B, no neutralizer was used. The extruder speed was about 450 rpm. In Example A, the amine base and initial water were mixed and supplied to the extruder at the initial water addition point, and in Example B, only water was supplied to the extruder at the initial water addition point. Dilution water was supplied by a second pump and introduced into the dilution zone of the extruder. The initial water and dilution water streams were optionally preheated to the extruder temperature. A back pressure controller was used to adjust the interior of the extruder barrel to a suitable pressure to prevent water vapor generation at the operating temperature at the extruder outlet.
The resulting dispersion was cooled and filtered through a 200 micron filter. The aqueous dispersion Example A of the present invention was tested for its properties and the results are reported in Table 3.

Comparative Coating Composition Examples 1 and 2
Dynapol L952 was dissolved at 70 ° C. in a 1: 1 (weight) blend of toluene and PM acetate (1-methoxy-2-acetoxypropane) to produce a 40 wt% solid solution. This procedure is carried out under constant stirring with a rod stirrer and heating of the mantle.
Performed in a 5 liter round bottom flask yielded approximately 3500 g of solution. Room temperature (about 25 ° C)
The solution was then cooled to C in a 2 oz glass jar using a tumbler.
ymel ™ 303LF (hexamethoxymethylmelamine resin (Cytec Ind
usures, as a crosslinker), Nacure 5925 (as amine neutralized dodecylbenzenesulfonic acid (King Industries), as catalyst), and PM acetate to reduce solids at room temperature (about 25 ° C.) overnight (about 25 ° C.) 18-24 hours) to obtain a comparative coating composition Example 1. Following the same procedure as described above in Coating Composition Comparative Example 1, a solvent-based solution of Dynapol L952 was added to Cyme.
l 303LF, Crylcoat 1510-0, DMEA (for amine neutralization), Nac
mixed with ure 5925, and PM acetate to form a coating composition comparative example 2. Comparative Coating Composition The coating formulation components of Examples 1 and 2 are listed in Table 3.

Coating Application The aqueous dispersion Example A of the present invention was applied to an aluminum metal panel using a drawdown bar and baked at 120 ° C. for 30 minutes to achieve good chemical resistance and metal as shown in Table 4. A coating having an excellent balance of hardness and flexibility as well as adhesion was obtained.

Coating compositions 1 to 4 of the present invention
In a 2 oz glass jar using a tumbler, the aqueous dispersion A of the present invention is
l ™ 303LF (hexamethoxymethylmelamine resin (Cytec), as a cross-linking agent), and Nacure 5925 (amine-neutralized dodecylbenzenesulfonic acid (
King Industries) as a catalyst) at room temperature (about 25 ° C.) overnight (18-
24 hours) to obtain coating compositions 1 to 4 of the present invention. The ingredients of the coating formulation are listed in Table 5.

Coating compositions 5-7 of the present invention
In a 2 oz glass jar using a tumbler, the aqueous dispersion B of the present invention is
l (trademark) 303LF (hexamethoxymethylmelamine resin (Cytec Indust
rie), as a crosslinker), and Nacure 5925 (amine-neutralized dodecylbenzene sulfonic acid (King Industries) as a catalyst) at room temperature (
Mixing was performed overnight (18 to 24 hours) to obtain coating compositions 5 to 7 of the present invention. The coating formulation ingredients are listed in Table 5.

Application of the coating Tin-plated panel with a size of about 10 cm to 20 cm (Rasselstein)
(Having a standard finish of grade TS-245) was washed with acetone and then dried. About 3 grams of the inventive coating composition 1-4 is added to 35 microns (1.4
Mill # 14) A tin-plated panel was individually applied by a wound-type drawdown bar, thereby coating one surface of the tin-plated panel. Subsequently, the panel was placed in a convection oven and cured at 200 ° C. for 10 minutes. The coated tin plated panels were tested according to the procedure described below for wedge folding, cross-cut adhesion before sterilization, and cross-cut adhesion and brushing after sterilization. An aluminum panel washed with acetone and dried (clean foil raw aluminum with dimensions of 009 × 4 inches × 12 inches from All Foils) was used for coating thickness and MEK DR (methyl ethyl ketone double rub) evaluation. Results are reported in Tables 6-9.

Test methods Test methods include the following:

Particle size measurement The average particle size was measured using a Coulter LS-230 particle size analyzer (Beckman Coulter).
r Corporation).

  The film thickness of the coating was measured according to ASTM D1186.

Impact resistance is measured in accordance with ASTM D5420 Gardner impact tester (Paul
N. (Gardner Co).

The König hardness of the coating film was measured using a pendulum hardness tester according to ASTM-D4366 (1995). Report in seconds.

The pencil hardness of the coating film is 6 according to ASTM D3363 (2005).
Pencil with wick ranging in hardness from B to 4H (Paul N. Gardner Co)
It measured using.

The solvent resistance of the coating film was measured according to ASTM D4752, using methyl ethyl ketone (MEK) as the solvent, and the number of rubs until blistering or breakthrough occurred in the film was reported. Friction was counted as reciprocating friction (ie, one forward friction and one rear friction constitute one reciprocating friction). This test method is used to determine the degree of cure of a coating film and its resistance to a particular solvent.

The specular gloss is measured according to BYK Micro-Tri-Gloss according to ASTM D523.
Measured using s meter.

The acid etch resistance of the coating was measured using a BYK Chemie gradient temperature oven and if a 10% solution of H ₂ SO ₄ was left on the coating for 15 minutes, it would damage the film (early visible defects). Alternatively, it was reported as the minimum temperature (unit: ° C.) for cutting through the substrate (severe defect). The higher the temperature reported, the more resistant the coating is to acid.

Film appearance was also evaluated at 60 and 70 ° C. (1-5 grade, 5 being best in this case).

Resistance to various chemicals was measured by placing 1 ml of chemical drops on the coating and letting it sit for 24 hours (covered to prevent evaporation), after which time the film appearance (Rating of 1-5, where 5 is the best).

Crosscut adhesion before retort treatment Crosscut adhesion according to ASTM-D 3359-02, tape adhesion test,
Measured by Method B and measured using Erichsen crosscut tester EPT 675R. This method uses tape (grade: TESA 4124) on a cut made in the film.
A procedure for evaluating the adhesion of the coating film to the metal substrate by applying and removing (transparent) is provided. The center of the tape strip is placed over the grid and stretched flat in place with a finger in the grid area. Rub the tape strongly to ensure good contact with the film. Within 90 ± 30 seconds after application, the tape is removed by grabbing the free end and pulling it off as quickly as possible (without dragging) at an angle as close to 180 degrees as possible. The area of the grating for coating detachment from the substrate or from the preceding coating is examined using an illumination magnifier. Adhesion is evaluated by the following grading.

Cross-cut adhesion after retort treatment In addition to the cross-cut adhesion test on the dry panel before exposure to the retort treatment, a cross-cut adhesion test is performed within 1 hour after removal from the autoclave, Adhesion is evaluated as described in the section on cross-cut adhesion. Adhesion is evaluated by the following grading.

Retort processing resistance (water)
Coated panels are immersed in water in individual pressurizable glass beakers housed in secondary container trays, and a Chamber with a Tuttnauer diameter of 10 inches x depth of 18 inches.
r Placed in Autoclave Model 1 Z-TUT-EZ-10, where the panel was retorted at 129 ° C. for 30 minutes. The panel was removed and dried. The appearance of the coating was then evaluated on a scale of 1-5 (5-best, 1-worst) as determined by brushing (the whitish appearance of the coating) as shown below.

Retort treatment resistance (lactic acid)
Coated panels are dipped in 2% lactic acid in individual pressurizable glass beakers housed in secondary container trays and Chat having a Tuttnauer diameter of 10 inches x depth of 18 inches.
Placed in mber Autoclave model 1 Z-TUT-EZ-10, where the panel was retorted at 121 ° C. for 30 minutes. The panel was removed and dried. The appearance of the coating was then evaluated on a scale of 1-5 (5-best, 1-worst) as determined by brushing (the whitish appearance of the coating) as shown below.

The round end of a 1.5 pound ball peen hammer was used to perform a MEK reciprocating friction test by applying a force of about 1000-2000 g to the MEK reciprocating friction coating. 4 inches x 4
An inch square cheesecloth is tied to the end of the hammer and immersed in methyl ethyl ketone (MEK). A hammer is brought into contact with the coating and reciprocated over a section measuring approximately 6 inches by 1 inch, where one reciprocating movement over the entire coating is considered one reciprocating friction. Reciprocating friction was performed at a rate of about 1 reciprocating friction per second. No further pressure was applied to the hammer. The fabric was re-immersed after every 25 reciprocations. The reciprocating friction step was repeated until the coating was rubbed off, i.e., at least a portion of the metal substrate was exposed (except for the 1/2 inch section at the edge of the test area). If the reciprocating friction step reached 150 reciprocating friction, the test was terminated and 150+ reciprocating friction was reported as the final result.

Wedge bending Wedge bending Gardner "COVERALL" Bend Tester IG
1125. The equipment used for this test consists of two parts to turn it into a folding machine. Install a steel rod (mandrel) in front of the base. A 100 mm wide coated test panel was folded around a 3 mm rod mandrel. Therefore, the coating appears on the outer surface of the fold. The folded panel was inserted into the wedge mandrel. The impactor, ie the metal weight, was raised to a height of 40 centimeters and then dropped. Collect and fix the impact body during the first rebound. Cylindrical folds in the panel were crushed into cones. The edges of the coated panel were rubbed with a solution of copper sulfate (a mixture of 10 grams copper sulfate, 90 grams water and 3 grams sulfuric acid). If any coating is cracked, dark spots will appear and indicate damage. Along the length of the wedge fold (which is 100 mm), the length of the undamaged area was measured in millimeters and expressed as percent ok.

Coating Thickness The coating thickness was measured using a Byko-Test 8500 coating thickness gauge according to ASTM-D 1186-93 (a non-destructive measurement of the dry film thickness of a non-magnetic coating applied to a non-ferrous substrate). A standard aluminum panel with nothing coated was used for calibration. The coating thickness of the coated panel is reported as a range of 10 measurements, where each measurement of the coating thickness of the coated panel is measured using a nonferrous material probe. I.e. measured relative to zero.
The measured thickness was reported in mils.

The present invention may be embodied in other forms without departing from its spirit and essential attributes, and thus is intended to represent the scope of the invention rather than the foregoing specification, rather than the appended claims. You should refer to the range.

The present invention may be embodied in other forms without departing from its spirit and essential attributes, and thus is intended to represent the scope of the invention rather than the foregoing specification, rather than the appended claims. You should refer to the range.
The present invention includes the following aspects.
[1]
(A) 50 to 99 weight percent of one or more polyethylene terephthalate resins, based on the total solids content of the dispersion;
(B) one or more stabilizers comprising at least one second polyester, from 1 to 50 percent by weight relative to the total solids content of the dispersion, wherein the second polyester is (i) Having a carboxylic acid group and having an acid number of 15 or greater relative to the solids content of the second polyester; or (ii) a self-dispersing sulfopolyester);
(C) optionally one or more neutralizing agents; and
(D) 15 to 90 weight percent water based on the total weight of the dispersion
An aqueous dispersion comprising a melt blend product of:
An aqueous dispersion wherein the dispersion has a solids content of 10 to 85 percent based on the total weight of the dispersion and the volume average particle size of the dispersion is less than 5 microns.
[2]
Selecting one or more polyethylene terephthalate resins;
At least one second polyester, wherein the second polyester has (i) a carboxylic acid group and an acid number of 15 or greater relative to the solids content of the second polyester; or (ii) self Selecting one or more stabilizers comprising a dispersed sulfopolyester);
Optionally selecting one or more neutralizing agents;
Melt blending one or more polyethylene terephthalate resins, one or more stabilizers in the presence of water and optionally one or more neutralizing agents;
Thereby producing an aqueous dispersion having a solids content of 10 to 85 percent relative to the total weight of the dispersion and having a volume average particle size of the dispersion of less than 5 microns. How to manufacture.
[3]
The aqueous dispersion according to the above [1];
Optionally one or more crosslinking agents;
Optionally one or more crosslinking catalysts;
Optionally one or more solvents;
Optionally one or more selected from the group consisting of polyolefin dispersion, acrylic latex, alkyd dispersion, epoxy resin dispersion, polyurethane dispersion, vinyl acetate dispersion and ethylene vinyl acetate dispersion; and
A coating composition optionally comprising one or more additives.
[4]
(A) 50 to 99 weight percent of one or more polyethylene terephthalate resins (wherein the polyethylene terephthalate resin has a glass transition temperature (Tg) of at least 65 ° C.), and a total solids content of the dispersion; Having an intrinsic viscosity of 0.5 to 1.0 Dl / g);
(B) one or more stabilizers comprising at least one second polyester in an amount of 1 to 50 percent by weight relative to the total solids content of the dispersion, wherein the second polyester is a carboxylic acid group And has an acid number of 20 or more with respect to the solids content of the second polyester);
(C) one or more neutralizing agents; and
(D) 15 to 90 weight percent water based on the total weight of the dispersion
An aqueous dispersion comprising a melt blend product of:
An aqueous dispersion wherein the dispersion has a solids content of 10 to 85 percent based on the total weight of the dispersion and the volume average particle size of the dispersion is less than 5 microns.
[5]
A coating layer comprising one or more film layers derived from the dispersion according to [1] above or the coating composition according to [3] above.
[6]
One or more substrates;
A coated article comprising at least one or more coating layers derived from the dispersion according to [1] above or the coating composition according to [3] above.
[7]
Selecting a substrate;
Selecting a coating composition according to [3] above;
Applying the coating composition to at least one surface of the substrate;
Removing at least some of the water from the coating composition;
Thereby forming one or more coating layers associated with the substrate;
Forming a coated substrate into a coated article.
[8]
Selecting a substrate;
Forming a substrate into an article;
Selecting a coating composition according to [3] above;
Applying the coating composition to at least one surface of the article;
Removing at least some of the water from the coating composition;
Thereby forming one or more coating layers associated with at least one surface of the article;
Forming a coated article, thereby forming the coated article.
[9]
The aqueous dispersion or aqueous dispersion according to any one of [1] to [8] above, wherein the one or more polyethylene terephthalate resins have a glass transition temperature (Tg) of at least 30 ° C. A method of making, a coating composition, a coating layer, a coated article, or a coated article.
[10]
The aqueous dispersion according to any one of [1] to [9] above, wherein the substrate is a pre-coated substrate, a method for producing the aqueous dispersion, a coating composition, a coating layer, a coated article, Or a method of making a coated article.
[11]
A can or coil coating composition comprising the coating composition according to [3] above.
[12]
The aqueous dispersion according to [4] above;
Optionally one or more crosslinking agents;
Optionally one or more crosslinking catalysts;
Optionally one or more solvents;
Optionally one or more selected from the group consisting of polyolefin dispersion, acrylic latex, alkyd dispersion, epoxy resin dispersion, polyurethane dispersion, vinyl acetate dispersion and ethylene vinyl acetate dispersion; and
A can or coil coating composition optionally comprising one or more additives.

Claims (12)

(A) 50 to 99 weight percent of one or more polyethylene terephthalate resins, based on the total solids content of the dispersion;
(B) one or more stabilizers comprising at least one second polyester, from 1 to 50 percent by weight relative to the total solids content of the dispersion, wherein the second polyester is (
i) having a carboxylic acid group and having an acid number of 15 or more relative to the solids content of the second polyester; or (ii) a self-dispersing sulfopolyester);
An aqueous dispersion comprising optionally (c) one or more neutralizing agents; and (d) a melt blend product of 15 to 90 weight percent water, based on the total weight of the dispersion,
An aqueous dispersion wherein the dispersion has a solids content of 10 to 85 percent based on the total weight of the dispersion and the volume average particle size of the dispersion is less than 5 microns. Selecting one or more polyethylene terephthalate resins;
At least one second polyester, wherein the second polyester has (i) a carboxylic acid group and an acid number of 15 or greater relative to the solids content of the second polyester; or (
ii) selecting one or more stabilizers comprising a self-dispersing sulfopolyester);
Optionally selecting one or more neutralizing agents;
Melt blending one or more polyethylene terephthalate resins, one or more stabilizers in the presence of water and optionally one or more neutralizing agents;
Thereby producing an aqueous dispersion having a solids content of 10 to 85 percent relative to the total weight of the dispersion and having a volume average particle size of the dispersion of less than 5 microns. How to manufacture. The aqueous dispersion of claim 1;
Optionally one or more crosslinking agents;
Optionally one or more crosslinking catalysts;
Optionally one or more solvents;
Optionally one or more selected from the group consisting of polyolefin dispersion, acrylic latex, alkyd dispersion, epoxy resin dispersion, polyurethane dispersion, vinyl acetate dispersion and ethylene vinyl acetate dispersion; and optionally 1 A coating composition comprising seeds or additives. (A) 50 to 99 weight percent of one or more polyethylene terephthalate resins (wherein the polyethylene terephthalate resin has a glass transition temperature (T _g ) of at least 65 ° C., based on the total solids content of the dispersion; And an intrinsic viscosity of 0.5 to 1.0 Dl / g);
(B) one or more stabilizers comprising at least one second polyester in an amount of 1 to 50 percent by weight relative to the total solids content of the dispersion, wherein the second polyester is a carboxylic acid group And has an acid number of 20 or more with respect to the solids content of the second polyester);
An aqueous dispersion comprising (c) one or more neutralizing agents; and (d) a melt blend product of 15 to 90 weight percent water, based on the total weight of the dispersion,
An aqueous dispersion wherein the dispersion has a solids content of 10 to 85 percent based on the total weight of the dispersion and the volume average particle size of the dispersion is less than 5 microns. 1 derived from the dispersion according to claim 1 or the coating composition according to claim 3.
A coating layer comprising one or more film layers. One or more substrates;
A coated article comprising at least one or more coating layers derived from the dispersion of claim 1 or the coating composition of claim 3. Selecting a substrate;
Selecting a coating composition according to claim 3;
Applying the coating composition to at least one surface of the substrate;
Removing at least some of the water from the coating composition;
Thereby forming one or more coating layers associated with the substrate;
Forming a coated substrate into a coated article. Selecting a substrate;
Forming a substrate into an article;
Selecting a coating composition according to claim 3;
Applying the coating composition to at least one surface of the article;
Removing at least some of the water from the coating composition;
Thereby forming one or more coating layers associated with at least one surface of the article;
Forming a coated article, thereby forming the coated article. The method for producing an aqueous dispersion or an aqueous dispersion according to any one of claims 1 to 8, wherein the one or more polyethylene terephthalate resins have a glass transition temperature ( _Tg ) of at least 30C. , A coating composition, a coating layer, a coated article, or a method of making a coated article. 10. The aqueous dispersion according to any one of claims 1 to 9, the method for producing the aqueous dispersion, the coating composition, the coating layer, the coated article, or the coated substrate, wherein the substrate is a pre-coated substrate. A method of making an article.   A coating composition for cans or coils comprising the coating composition according to claim 3. An aqueous dispersion according to claim 4;
Optionally one or more crosslinking agents;
Optionally one or more crosslinking catalysts;
Optionally one or more solvents;
Optionally one or more selected from the group consisting of polyolefin dispersion, acrylic latex, alkyd dispersion, epoxy resin dispersion, polyurethane dispersion, vinyl acetate dispersion and ethylene vinyl acetate dispersion; and optionally 1 A can or coil coating composition comprising seeds or additives.